RU2005136214A - Способ и устройство для упрочнения стекла - Google Patents
Способ и устройство для упрочнения стекла Download PDFInfo
- Publication number
- RU2005136214A RU2005136214A RU2005136214/03A RU2005136214A RU2005136214A RU 2005136214 A RU2005136214 A RU 2005136214A RU 2005136214/03 A RU2005136214/03 A RU 2005136214/03A RU 2005136214 A RU2005136214 A RU 2005136214A RU 2005136214 A RU2005136214 A RU 2005136214A
- Authority
- RU
- Russia
- Prior art keywords
- glass
- temperature
- glass product
- salt bath
- deformation
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C21/00—Treatment of glass, not in the form of fibres or filaments, by diffusing ions or metals in the surface
- C03C21/001—Treatment of glass, not in the form of fibres or filaments, by diffusing ions or metals in the surface in liquid phase, e.g. molten salts, solutions
- C03C21/002—Treatment of glass, not in the form of fibres or filaments, by diffusing ions or metals in the surface in liquid phase, e.g. molten salts, solutions to perform ion-exchange between alkali ions
Landscapes
- Chemical & Material Sciences (AREA)
- Life Sciences & Earth Sciences (AREA)
- Engineering & Computer Science (AREA)
- Chemical Kinetics & Catalysis (AREA)
- General Chemical & Material Sciences (AREA)
- Geochemistry & Mineralogy (AREA)
- Materials Engineering (AREA)
- Organic Chemistry (AREA)
- Surface Treatment Of Glass (AREA)
Claims (1)
1. Способ упрочнения стеклянных изделий, содержащий шаги формование стеклянного изделия из расплавленного стекла, причем стекло имеет температуру отжига, погружение формованного стеклянного изделия в ванну солевого расплава, причем солевая ванна содержит ионы калия, а температура поверхности стеклянного изделия во время шага погружения равна по меньшей мере температуре отжига стекла, и выдерживание стеклянного изделия при температуре в диапазоне от точки деформирования стекла до температуры, приблизительно на 150°С ниже точки деформирования стекла, в течение по меньшей мере приблизительно пяти минут, причем стекло остается при температуре выше температуры отжига стекла после операции формования и до операции погружения.
2. Способ по п.1, в котором температура поверхности стеклянного изделия по меньшей мере на 25°С превышает температуру отжига стекла.
3. Способ по п.1, в котором стеклянное изделие погружают в солевую ванну приблизительно на 10 с или менее.
4. Способ по п.1, в котором стеклянное изделие погружают в солевую ванну на время от приблизительно 0,5 до приблизительно 30 с.
5. Способ по п.1, в котором солевая ванна содержит сочетание по меньшей мере двух из числа нитрата калия, хлорида калия и сульфата калия.
6. Способ по п.1, в котором солевая ванна содержит сочетание по меньшей мере двух из числа нитрата калия, хлорида калия и сульфата калия, причем сочетание имеет температуру плавления не ниже 550°С.
7. Способ по п.1, в котором солевая ванна имеет температуру от 550 до 750°С.
8. Способ по п.1, в котором выдерживание стеклянного изделия происходит при температуре в диапазоне от температуры деформирования до температуры, приблизительно на 130°С ниже температуры деформирования.
9. Способ по п.1, который содержит также после операции выдерживания, охлаждение стеклянного изделия, удаление остатков соли со стеклянного изделия и нанесение на поверхность стеклянного изделия защитного слоя, устойчивого к образованию царапин.
10. Устройство для упрочнения стеклянных изделий, которое содержит накопительный участок, средство перемещения стеклянных изделий для перемещения стеклянных изделий после формования стеклянного изделия и перед охлаждением стеклянного изделия до температуры ниже температуры отжига стеклянного изделия, солевую ванну, причем солевая ванна содержит солевой расплав, и средство перемещения стеклянных изделий сконфигурировано для перемещения стеклянных изделий с накопительного участка и погружения стеклянных изделий в солевую ванну, причем средство перемещения стеклянных изделий сконфигурировано для погружения стеклянных изделий, имеющих температуру поверхности, равную по меньшей мере температуре отжига стекла, а стеклянное изделие сконфигурировано так, чтобы оставаться в солевой ванне в течение менее, чем приблизительно одной минуты, и упрочнительный лер, причем упрочнительный лер сконфигурирован для выдерживания стеклянного изделия при температуре между температурой деформирования стекла и температурой приблизительно на 150°С ниже температуры деформирования стекла в течение по меньшей мере приблизительно пяти минут.
11. Устройство по п.10, в котором средство перемещения стеклянного изделия сконфигурировано для погружения стеклянного изделия в солевую ванну на период от приблизительно 0,5 с до приблизительно 30 с.
12. Устройство по п.10, в котором средство перемещения стеклянного изделия сконфигурировано для погружения стеклянного изделия в солевую ванну на период от приблизительно 3 с до приблизительно 5 с.
13. Устройство по п.10, в котором солевая ванна содержит нитрат калия в диапазоне 40-60 мол.% и хлорид калия в диапазоне 40-60 мол.%.
14. Устройства по п.10, в котором солевая ванна содержит сочетание по меньшей мере двух из числа нитрата калия, хлорида калия и сульфата калия.
15. Устройство по п.10, в котором солевая ванна содержит сочетание по меньшей мере двух из числа нитрата калия, хлорида калия и сульфата калия, причем сочетание имеет температуру плавления не ниже 550°С.
16. Устройство по п.10, в котором упрочнительный лер сконфигурирован для выдерживания стеклянного изделия при температуре в диапазоне от температуры деформирования до температуры, приблизительно на 130°С ниже температуры деформирования.
17. Устройство по п.10, в котором температура деформирования составляет около 530°С.
18. Устройство по п.10, которое содержит также:
средство огневого полирования, причем средство огневого полирования сконфигурировано для огневого полирования стеклянных изделий.
19. Устройство по п.18, в котором средство огневого полирования является первым средством огневого полирования, сконфигурированным для огневого полирования сторон стеклянного изделия, а устройство дополнительно содержит второе средство огневого полирования, сконфигурированное для полирования донышек стеклянных изделий.
20. Устройство по п.10, которое содержит также механизм нанесения покрытий, сконфигурированный для нанесения на поверхность стеклянного изделия защитного слоя, устойчивого к образованию царапин, после извлечения стеклянного изделия из упрочнительного лера.
21. Способ упрочнения стеклянных изделий, который содержит формование стеклянного изделия из расплавленного стекла, причем стекло имеет температуру отжига, применение ионов калия к поверхности стеклянного изделия, причем температура поверхности стеклянного изделия во время операции применения равна по меньшей мере температуре отжига стекла, и выдерживание стеклянного изделия при температуре в диапазоне от точки деформирования стекла до температуры приблизительно на 150°С ниже точки деформирования стекла в течение по меньшей мере приблизительно пяти минут.
22. Способ по п.21, в котором стеклянное изделие погружают в солевую ванну на время от приблизительно 0,5 до приблизительно 30 с.
23. Способ по п.21, в котором операция применения ионов калия к поверхности стеклянного изделия выполняется путем погружения стеклянного изделия в солевую ванну на время от приблизительно 3 до приблизительно 5 с.
24. Способ по п.21, в котором операция применения ионов калия к поверхности стеклянного изделия выполняется путем напыления ионов калия на поверхность стеклянного изделия.
25. Способ по п.24, в котором операция напыления содержит по меньшей мере одну операцию из числа порошкового напыления, электростатического напыления и газопламенного напыления.
26. Способ по п.21, в котором операция применения ионов калия к поверхности стеклянного изделия выполняется путем химического осаждения из паровой фазы (CVD).
27. Способ по п.21, в котором стеклянное изделие имеет температуру, которая во время операции применения по меньшей мере приблизительно на 25°С превышает температуру отжига стекла.
28. Способ по п.21, в котором стеклянное изделие имеет температуру, которая во время операции применения по меньшей мере приблизительно на 50°С превышает температуру отжига стекла.
29. Способ по п.21, в котором стеклянное изделие имеет температуру, которая во время операции применения по меньшей мере приблизительно на 80°С превышает температуру отжига стекла.
31. Способ по п.21, в котором выдерживание стеклянного изделия происходит при температуре в диапазоне от температуры деформирования до температуры, приблизительно на 130°С ниже температуры деформирования.
31. Способ по п.21, при котором температура деформирования составляет около 530°С.
32. Способ по п.21, который содержит также после операции выдерживания нанесение на поверхность стеклянного изделия защитного слоя, устойчивого к образованию царапин.
33. Способ упрочнения стеклянных изделий, который содержит формование стеклянного изделия из расплавленного стекла, погружение формованного стеклянного изделия в солевую ванну, перед тем, как стеклянное изделие после формирования стеклянного изделия охладится до температуры ниже температуры отжига стекла, причем солевая ванна содержит ионы калия, а стеклянные изделия погружают менее, чем приблизительно на 30 с, и выдерживание стеклянного изделия при температуре в диапазоне от точки деформирования стекла до температуры приблизительно на 150°С ниже точки деформирования стекла в течение по меньшей мере приблизительно 5 мин.
34. Способ по п.33, в котором стеклянное изделие погружают в солевую ванну на время приблизительно 20 с или менее.
35. Способ по п.33, в котором стеклянное изделие погружают в солевую ванну приблизительно на 10 с или менее.
36. Способ по п.33, в котором стеклянное изделие погружают в солевую ванну на время от приблизительно 3 до приблизительно 5 с.
37. Способ по п.33, в котором солевая ванна содержит нитрат калия в диапазоне 40-60 мол.% и хлорид калия в диапазоне 40-60 мол.%.
38. Способ по п.33, в котором солевая ванна содержит сульфат калия и хлорид калия.
39. Способ по п.33, который содержит также огневое полирование перед погружением стеклянного изделия в солевую ванну.
40. Способ по п.33, который содержит также после операции выдерживания нанесение на поверхность стеклянного изделия защитного слоя, устойчивого к образованию царапин.
41. Способ по п.33, в котором солевая ванна имеет температуру от 550 до 750°С.
42. Способ по п.33, в котором выдерживание стеклянного изделия происходит при температуре в диапазоне от температуры деформирования до температуры, приблизительно на 130°С ниже температуры деформирования.
43. Способ по п.33, в котором температура деформирования составляет около 530°С.