KR940005690A - 부타디엔계 공중합체 - Google Patents
부타디엔계 공중합체 Download PDFInfo
- Publication number
- KR940005690A KR940005690A KR1019930010304A KR930010304A KR940005690A KR 940005690 A KR940005690 A KR 940005690A KR 1019930010304 A KR1019930010304 A KR 1019930010304A KR 930010304 A KR930010304 A KR 930010304A KR 940005690 A KR940005690 A KR 940005690A
- Authority
- KR
- South Korea
- Prior art keywords
- butadiene
- copolymer
- molecular weight
- compound
- polyvinyl aromatic
- Prior art date
Abstract
본 발명은 탄화수소 용매 속에서 유기 리늄 화합물을 중합 개시제로서 사용하여 부타디엔 및 폴리비닐 방향족 화합물 또는 부타디엔, 스티렌 및 폴리비닐 방향족 화합물을 공중합시켜 공중합체 말단에 리튬을 갖는 공중합체를 수득하고, 이어서 3 내지 4관능성 커플링제를 첨가하여 커플링 반응시켜 수득한 부타디엔계 공중합체로서, 하기 (a) 내지 (d)의 조건을 만족시키는 부타디엔계 공중합체에 관한 것이다; (a) 스티렌 함유향이 50중량% 이하이고, (b) 부타디엔 부분의 비닐 결합 함유량이 10 내지 90%이며, (c) 고속 액체 크로마토그래피에 의해 수득 된 분자량 분포 곡선이 셋 이상의 피크를 가지며 가장 저분자량측에 위치하는 피크에 상당하는 표준 폴리스티렌 환산 분자량의 5배 이상의 분자량을 갖는 고분자량 분자쇄의 공중합체 전체에 대한 중합 비율이 5 내지 60%이고, (d)무니 점도(ML1+47100℃)가 30 내지 200이다. 가공성이 우수하다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (23)
- 탄화수소 용매 속에서 유기 리튬 화합물을 중합 개시제로서 사용하여 부타디엔 및 폴리비닐 방향족 화합물 또는 부타디엔, 스티렌 및 폴리비닐 방향족 화합물을 공중합시켜 공중합체 말단에 리늄을 갖는 공중합체를 수득하고, 이어서 3 내지 4관능성 커플링제를 첨가하여 커플링 반응시켜 수득한 부타디엔게 공중합체로서, 하기 (a) 내지 (d)의 조건을 만족시키는 부타디엔계 공중합체; (a) 스티렌 함유량이 50중량% 이하이고, (b) 부타디엔 부분의 비닐 결합 함유량이 10 내지 90%이며, (c) 고속 액체 크로마토그래피에 의해 수득된 분자량 분포곡석이 셋 이상의 피크를 가지며 가장 저분자량측에 위치하는 피크에 상당하는 표준 폴리스티렌 환산 분자량의 5배 이상의 분자량을 갖는 고분자량 분자쇄의 공중합체 전체에 대한 중합 비율이 5 내지 60%이고, (d) 무니 점도 (ML1+47100℃)가 30 내지 200이다.
- 제1항에 있어서, (c) 고속 액체 크로마토그래피에 의해 수득된 분자량 분포곡선이 셋 이상의 피크를 가지며 가장 저분자량측에 위치하는 피크에 상당하는 표준 폴리스티렌 환산 분자량의 5배 이상의 분자량을 갖는 고분자량 분자쇄의 공중합체 전체에 대한 중합 비율이 10 내지 40%인 부타디엔계 공중합체.
- 제1항에 있어서, 탄화수소 용매가 벤젠, 톨루엔, 크실렌, 에틸벤젠, 헥산, 헵탄, 사이클로펜탄, 사이클로헥산 또는 메틸사이클로헥산인 부타디엔계 공중합체.
- 제1항에 있어서, 유기 리튬, 화합물이 에틸리튬, 프로필리튬, 부틸리튬, 아밀리튬, 트리메틸렌디리튬, 테트라메틸렌리튬, 헥실리튬, 사이클로헥실리튬, 페닐리튬, 톨릴리튬 또는 나프틸리튬인 부타디엔계 공중합체.
- 제1항에 있어서, 플릴비닐 방향족 화합물이 디비닐벤젠, 1,2,4-트리비닐벤젠, 13-디비닐나프탈렌, 1,8-디비닐나프탈렌, 1,2-디비닐-3,4-디메틸벤젠, 2,4-디비닐비페닐, 3,5,4'-트리비닐비페닐 또는 1,3,5-트리비닐벤젠인 부타디엔계 공중합체.
- 제1항에 있어서, 3 내지 4관능성 커플링제가 사염화규소, 사브롬화규소, 사요오드화규소, 사염화게르마늄, 사염화주석, 메틸트리클로로실란, 부틸트리클로로실란, 부틸트리클로로주석, 비스트리클로로실릴에탄 또는 비스트리클로로에탄인 부타디엔계 공중합체.
- 제1항에 있어서, 부타디엔계 공중합체의 부타디엔 부분의 비닐 결합 함유량이 20 내지 70%인 부타디엔계 공중합체.
- 제1항에 있어서, 부타디엔계 공중합체의 무니 점도(ML1+47100℃)가 50 내지 150인 부타디엔계 공중합체.
- 제1항에 따른 부타디엔계 공중합체 100중량부당 신장유 100중량부 이하를 함유하는 오일 신장 부타디엔계 공중합체.
- 탄화수소 용매 속에서 유기 리튬 화합물을 중합 개시제로서 사용하여 부타디엔 및 폴리비닐 방향족 화합물 또는 부타디엔, 스티렌 및 폴리비닐 방향족 화합물을 공중합시켜 공중합체 말단에 리튬을 갖는 공중합체를 수득하고, 이어서 3 내지 4관능성 커플링제를 첨가하여 커플링 반응시킴을 특징으로 하여, 제1항에 따른 부타디엔계 공중합체를 제조하는 방법.
- 제10항에 있어서, 탄화수소 용매가 벤젠, 톨루엔, 크실렌, 에텔벤젠, 헥산, 헵탄, 사이클로펜탄, 사이클로 헥산 또는 메틸사이클로헥산인 방법.
- 제10항에 있어서, 유기 리튬 화합물이 에틸리튬, 프로필리튬, 부틸리튬, 아밀리튬, 트리메틸렌디리늄, 테트라메틸렌리튬, 핵실리튬, 사이크로헥실리튬, 페닐리튬 또는 나프틸리늄인 방법.
- 제10항에 있어서, 폴리비닐 방향족 화합물이 디비닐벤젠, 1,2,4-트리비닐벤젠, 1,3-디비닐나프탈렌, 1,8-디비닐나프타렌, 1,2-디비닐03,4-디메틸베벤젠, 2,4-디비닐비페닐, 3,5,4'-트리비닐비페닐 또는 1,3,5-트리비닐벤젠인 방법.
- 제10항에 있어서, 3 내지 4관능성 커플링제가 사염화규소, 사브롬화규소, 사요오드화규소, 사염화게르마늄, 사염화주석, 메틸트리클로로실란, 부틸트리클로로주석, 비스트리클로로실릴에탄 또는 비스트리클로로에탄인 방법.
- 제10항에 있어서, 부타디엔 부분의 비닐 결합 함유량 조절제로서 루이스 염기성 화합물을 사용하는 방법.
- 제15항에 있어서, 루이스 염기성 화합물이 에테르 화합물 또는 3급 아민인 방법.
- 제16항에 있어서, 에테르 화합물이 테트라하이드로푸란, 테트라하이드로피란, 1,4-디옥산, 디에틸 에테르, 디부틸 에테르, 에틸렌 글리콜 디부틸 에테르, 디에틸렌 글리콜 디에틸 에테르, 디에틸렌 글리콜 디부틸 에테르, 디페닐 에테르 또는 아니솔이고, 3급 아민 화합물이 트리에틸아민, 트리프로필아민, 트리부틸아민, N, N, N', N'-테트라메틸에틸렌디아민, N-디에틸아닐린, 피리딘 또는 퀴놀린인 방법.
- 제10항에 있어서, 중합온도가 0 내지 150℃인 방법.
- 제10항에 있어서, 중합온도가 30 내지 80℃인 방법.
- 제10항에 있어서, 폴리비닐 방향족 화합물의 사용량이 중합 개시제인 유기 리튬 화합물에 대하여 0.05 내지 1.0배 몰인 방법.
- 제10항에 있어서, 폴리비닐 방향족 화합물의 사용량이 중합 개시제인 유기 리튬 화합물에 대하여 0.1 내지 0.6배 몰인 방법.
- 제10항에 있어서, 3 내지 4관능성 커플링제의 사용량이 중합 개시제인 유기 리튬 화합물에 대하여 0.03 내지 0.3배 몰인 방법.
- 제10항에 있어서, 3 내지 4관능성 커플링제의 사용량이 중합 개시제인 유기 리튬 화합물에 대하여 0.05 내지 0.2배 몰인 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.