KR20210057421A - wallpaper system - Google Patents

wallpaper system Download PDF

Info

Publication number
KR20210057421A
KR20210057421A KR1020190144166A KR20190144166A KR20210057421A KR 20210057421 A KR20210057421 A KR 20210057421A KR 1020190144166 A KR1020190144166 A KR 1020190144166A KR 20190144166 A KR20190144166 A KR 20190144166A KR 20210057421 A KR20210057421 A KR 20210057421A
Authority
KR
South Korea
Prior art keywords
wallpaper
insulating
paper
insulation
foaming
Prior art date
Application number
KR1020190144166A
Other languages
Korean (ko)
Inventor
정근수
이시영
김웅길
이봄
Original Assignee
(주)엘지하우시스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)엘지하우시스 filed Critical (주)엘지하우시스
Priority to KR1020190144166A priority Critical patent/KR20210057421A/en
Publication of KR20210057421A publication Critical patent/KR20210057421A/en

Abstract

본 발명은 벽지 시스템에 관한 것으로, 보다 자세하게는 융점이 상이한 2종의 섬유를 포함하는 부직포로 형성된 단열 초배지(110); 및 상기 단열 초배지(110) 일면에 형성되는, 하부에서 상부로 기재층(131), 상기 기재층(131)의 상부에 전면 도포된 제1발포수지층(133)을 포함하고, 열전도율이 150mW/m·k 미만인 단열벽지(130); 를 포함하는 벽지 시스템(100)에 관한 것이다.The present invention relates to a wallpaper system, and more specifically, a heat insulating super medium 110 formed of a non-woven fabric including two kinds of fibers having different melting points; And a base layer 131 from the bottom to the top, and a first foaming resin layer 133 applied entirely on the top of the base layer 131, which is formed on one surface of the heat insulating super medium 110, and has a thermal conductivity of 150 mW/ insulation wallpaper 130 of less than m·k; It relates to a wallpaper system 100 comprising a.

Description

벽지 시스템 {wallpaper system}Wallpaper system {wallpaper system}
본 발명은 벽지 시스템에 관한 것으로, 보다 자세하게는 단열 초배지 및 단열벽지를 포함함으로써, 열 관류율을 저감한 단열성이 우수한 벽지 시스템에 관한 것이다.The present invention relates to a wallpaper system, and more particularly, to a wallpaper system having excellent thermal insulation properties by reducing the heat transmission rate by including a thermal insulation paper and a thermal insulation wallpaper.
벽지는 다양한 문양 또는 입체적 형태를 포함하고 있어 벽에 장식적 미를 부여하는 인테리어 수단이다.Wallpaper contains various patterns or three-dimensional forms, and is an interior means that gives a decorative beauty to the wall.
과거에는 초배지를 시공하지 않고 콘크리트 벽면에 바로 벽지를 도배함으로써 실내 인테리어를 마감하였으나, 이러한 시공방법은 벽면의 불균일성이 그대로 드러나 실내 미적인 문제가 발생하였고, 벽지 자체의 인장강도 등이 약해 쉽게 찢어져 콘크리트의 표면이 그대로 드러나는 문제점이 발생하였다. 이에 따라 초배지를 먼저 벽면에 붙이고 벽지 등을 붙이는 방법이 널리 쓰이게 되었다.In the past, the interior of the room was finished by painting wallpaper directly on the concrete wall without installing super-badge, but this construction method revealed the unevenness of the wall as it was, resulting in interior aesthetic problems, and the tensile strength of the wallpaper itself was weak, causing it to be easily torn. There was a problem that the surface was revealed as it is. As a result, the method of attaching top badges to the wall first and then attaching wallpaper etc. has become widely used.
최근 벽지의 찢김을 방지하여 미관상의 문제점을 방지함과 동시에, 건축물의 단열 시공의 미흡에 따른 냉기 및 외풍을 차단하는 단열 초배지가 선호되고 있으며, 일 예로 대한민국 공개특허공보 10-2009-0125862호(공고일: 2009. 12. 08.)는 스펀본드 부직포 사이에 핫멜트 접착필름을 도포하고, 폴리에틸렌 필름을 라미네이팅 처리한 투습 단열 초배지를 개시하고 있다.In recent years, an insulating superbag that blocks cold air and drafts due to insufficient insulation construction of buildings is preferred, while preventing aesthetic problems by preventing tearing of the wallpaper, for example, Korean Patent Laid-Open No. 10-2009-0125862 ( Announcement Date: 2009. 12. 08.) discloses a moisture-permeable insulating super medium in which a hot melt adhesive film is applied between spunbond nonwoven fabrics and a polyethylene film is laminated.
그러나, 상기 투습 단열 초배지는 평량이 상이한 스펀본드 부직포를 제조하며, 상기 스펀본드 부직포 사이에 핫멜트 접착제 도포 및 폴리에틸렌 필름 적층 등 복잡한 제조과정을 거쳐야 하는 문제점 및 투습 단열 초배지의 두께가 매우 얇아 단열벽지를 제대로 지지할 수 없는 문제점이 있으며, 0.5mm의 얇은 두께로 쿠션감이 없으며 벽면의 요철 형상을 보완하는데 어려움이 있다.However, the moisture-permeable and heat-insulating super-badge fabricates spunbond nonwoven fabrics with different basis weights, and requires a complicated manufacturing process such as applying a hot melt adhesive and laminating a polyethylene film between the spun-bonded non-woven fabrics, and the thickness of the moisture-permeable and heat-insulating super media is very thin. There is a problem that it cannot be properly supported, there is no cushioning feeling due to its thin thickness of 0.5mm, and it is difficult to compensate for the uneven shape of the wall.
또한, 종래의 초배지는 벽면에 부분 부착 시공되는 것인 바, 부분 부착된 초배지 상에 단열벽지를 시공할 경우 상기 단열벽지를 단단하게 지지하기 어려워 상기 단열벽지가 쉽게 찢어질 수 있다. In addition, since the conventional paperboard is partially attached to the wall surface, when the insulating wallpaper is installed on the partially attached paperboard, it is difficult to firmly support the insulating wallpaper, and the insulating wallpaper may be easily torn.
한편, 최근에는 표면질감이 실크처럼 부드럽고 엠보싱 효과가 뛰어나 입체적인 느낌을 잘 표현할 수 있는 실크 벽지가 선호되고 있다. 이러한 실크 벽지는 그 재질이 통상 PVC로서, 이러한 PVC 벽지의 일 예로, 대한민국 등록특허공보 제10-0467775호(공고일: 2005. 01. 24.)는 아래에서부터 순차적으로 원지, PVC 발포층, 인쇄층 및 표면처리층을 포함하는 PVC 벽지를 개시하고 있다.On the other hand, in recent years, silk wallpaper, which has a smooth surface texture like silk and has excellent embossing effect, is preferred to express a three-dimensional feeling well. Such silk wallpaper is usually made of PVC, and as an example of such a PVC wallpaper, Republic of Korea Patent Publication No. 10-0467775 (announced date: January 24, 2005) sequentially from the bottom of the base paper, PVC foam layer, printing layer. And it discloses a PVC wallpaper comprising a surface treatment layer.
그러나, 상기 PVC 벽지는 통상 충전제로 열전도율이 높은 탄산칼슘(900 mW/m·K)을 이용하고 있어 단열성이 좋지 못한 문제점이 있다. However, since the PVC wallpaper uses calcium carbonate (900 mW/m·K) having a high thermal conductivity as a filler, there is a problem of poor insulation.
또한, 상기 탄산칼슘은 밀도가 커서 입체효과를 더욱 향상시키기 위해 추가적으로 PVC 발포층 조성물의 코팅량을 증가시킬 경우 벽지 중량이 무거워짐과 아울러, 시공 후 벽지 간 이음매가 벌어지는 등의 시공이 어려워지고(통상, 벽지 중량이 460g/m2 이상인 경우 시공이 어려움) 또한, 벽지의 접힘 자국이 발생하여 시공 품질에 문제가 있었다.In addition, when the amount of coating of the PVC foam layer composition is additionally increased to further improve the three-dimensional effect due to the high density of the calcium carbonate, the weight of the wallpaper becomes heavier, and it is difficult to construct a joint between the wallpaper after construction ( In general, construction is difficult when the wallpaper weight is 460 g/m 2 or more) In addition, there is a problem in construction quality due to the occurrence of fold marks of the wallpaper.
한편, 종래의 PVC 벽지(200)는 외관 효과를 위해 엠보롤로 가압하는 엠보 공정을 수행 시, 상기 원지(210) 상부의 상기 PVC 발포층(220) 내 발포 셀이 눌리면서 공기층이 파괴되어 벽지의 단열성을 저하시키는 주요 원인이 되었다. On the other hand, when performing an embossing process in which the conventional PVC wallpaper 200 is pressed with an emboss roll for an appearance effect, the air layer is destroyed as the foam cells in the PVC foam layer 220 on the top of the base paper 210 are pressed, resulting in the thermal insulation of the wallpaper. It was a major cause of lowering the problem.
따라서, 단열성 및 쿠션감을 향상시키면서도 벽면의 요철 형상을 보완할 수 있고, 단열벽지를 지지할 수 있으며, 입체효과를 가질 수 있으면서도 시공성 및 시공 품질을 확보할 수 있는 벽지 시스템의 개발이 요구되는 실정이다.Therefore, there is a need to develop a wallpaper system that can improve the insulation and cushioning while complementing the uneven shape of the wall, support the insulation wallpaper, have a three-dimensional effect, and secure workability and construction quality. .
KR 10-2009-0125862 (공고일: 2009. 12. 08.)KR 10-2009-0125862 (Announcement date: 2009. 12. 08.) KR 10-0467775B (공고일: 2005. 01. 24.)KR 10-0467775B (announcement date: 2005. 01. 24.)
상기와 같은 종래기술의 문제점을 해결하고자, 본 발명은 우수한 단열성 및 쿠션감을 가지며, 벽면의 요철 형상을 보완할 수 있으며, 열 관류율이 저감된 벽지 시스템을 제공하는 것을 목적으로 한다.In order to solve the problems of the prior art as described above, the present invention has an excellent heat insulation and cushioning, it is possible to supplement the uneven shape of the wall surface, it is an object of the present invention to provide a wallpaper system with a reduced heat permeation rate.
상기 목적을 달성하기 위하여,To achieve the above object,
본 발명은 융점이 상이한 2종의 섬유를 포함하는 부직포로 형성된 단열 초배지; 및The present invention is a thermal insulation paper formed of a non-woven fabric containing two kinds of fibers having different melting points; And
상기 단열 초배지 일면에 형성되는, It is formed on one side of the insulating super medium,
하부에서 상부로 기재층, 상기 기재층의 상부에 전면 도포된 제1발포수지층을 포함하고, 열전도율이 150mW/m·K 미만인 단열벽지; 를 포함하는 벽지 시스템을 제공한다.An insulating wallpaper comprising a base layer from bottom to top and a first foaming resin layer applied entirely on the top of the base layer, and having a thermal conductivity of less than 150 mW/m·K; It provides a wallpaper system comprising a.
본 발명은 벽지 시스템에 관한 것으로, 상기 벽지 시스템은 단열 초배지 및 단열벽지를 포함함으로써, 열 관류율이 낮아 단열성이 우수하고, 단열벽지의 찢김을 방지하여 미관상의 문제점을 방지하고, 쿠션감을 가지면서 건축물의 벽면을 매끈하게 만들어주는 효과가 있다.The present invention relates to a wallpaper system, wherein the wallpaper system includes a heat-insulating super paper and a heat-insulating wallpaper, so that the heat permeation rate is low, and thus the heat-insulating property is excellent, and by preventing the tearing of the insulating wallpaper, aesthetic problems are prevented, and the building has a feeling of cushioning. It has the effect of making the wall of the wall smooth.
도 1은 본 발명의 단열 초배지의 구조를 개략적으로 도시한 측단면도이다.
도 2는 본 발명의 단열벽지의 적층구조를 개략적으로 도시한 측단면도이다.
도 3은 본 발명의 벽지 시스템의 적층구조를 개략적으로 도시한 측단면도이다.
Figure 1 is a side cross-sectional view schematically showing the structure of the heat insulating paper substrate of the present invention.
Figure 2 is a side cross-sectional view schematically showing the laminated structure of the insulation wallpaper of the present invention.
3 is a side cross-sectional view schematically showing a laminated structure of the wallpaper system of the present invention.
이하 첨부한 도면을 참조하여 본 발명의 바람직한 실시예에 대한 구성 및 작용을 상세히 설명하면 다음과 같다.Hereinafter, the configuration and operation of a preferred embodiment of the present invention will be described in detail with reference to the accompanying drawings.
여기서, 각 도면의 구성요소들에 대해 참조부호를 부가함에 있어서, 동일한 구성요소들에 한해서는 비록 다른 도면상에 표시되더라도, 가능한 한 동일한 부호로 표기되었음에 유의하여야 한다.Here, in adding reference numerals to elements of each drawing, it should be noted that, even though they are indicated on different drawings, only the same elements are denoted by the same numerals as much as possible.
본 발명에서 사용한 용어는 단지 특정한 실시 예를 설명하기 위해 사용된 것으로서, 본 발명을 한정하려는 의도가 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. The terms used in the present invention are used only to describe specific embodiments, and are not intended to limit the present invention. Singular expressions include plural expressions unless the context clearly indicates otherwise.
본 발명에서, "포함하다" 또는 "가지다" 등의 용어는 명세서 상에 기재된 특징, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.In the present invention, terms such as "comprise" or "have" are intended to designate the presence of features, steps, actions, components, parts, or combinations thereof described in the specification, but one or more other features or steps. It is to be understood that it does not preclude the possibility of addition or presence of, operations, components, parts, or combinations thereof.
다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해, 일반적으로 이해되는 것과 동일한 의미를 가지고 있다.Unless otherwise defined, all terms, including technical or scientific terms, used herein have the same meaning as commonly understood by one of ordinary skill in the art to which the present invention belongs.
일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은, 관련 기술의 문맥 상 가지는 의미와 일치하는 의미를 가지는 것으로 해석되어야 하며, 본 발명에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.Terms as defined in a commonly used dictionary should be interpreted as having a meaning consistent with the meaning in the context of the related technology, and should be interpreted as an ideal or excessively formal meaning unless explicitly defined in the present invention. It doesn't work.
본 발명은 융점이 상이한 2종의 섬유를 포함하는 부직포로 형성된 단열 초배지(110); 및The present invention is a thermal insulation paper (110) formed of a non-woven fabric containing two kinds of fibers having different melting points; And
상기 단열 초배지(110) 일면에 형성되는, Formed on one side of the heat insulating paper (110),
하부에서 상부로 기재층(131), 상기 기재층(131)의 상부에 전면 도포된 제1발포수지층(133)을 포함하고, 열전도율이 150mW/m·K 미만인 단열벽지(130);를 포함하는 벽지 시스템(100)에 관한 것이다(도 3 참조).Including: a base layer 131 from the bottom to the top, a first foaming resin layer 133 applied entirely on the top of the base layer 131, and a thermal conductivity of less than 150mW/m·K, an insulating wallpaper 130; including It relates to the wallpaper system 100 (see Fig. 3).
구체적으로, 본 발명의 벽지 시스템(100)은 열 관류율이 15W/m2·K 이하, 12W/m2·K 이하 또는 10W/m2·K 이하일 수 있으며, 열 관류율이 상기 범위를 초과할 경우, 벽지 시스템의 단열성이 저하되므로 상기 범위 내의 열 관류율을 가질 수 있다.Specifically, wallpaper system 100 of the present invention may be up to heat gwanryuyul is 15W / m 2 · K or less, 12W / m 2 · K or less, or 10W / m 2 · K, if a column gwanryuyul exceeds the above range, , Since the thermal insulation property of the wallpaper system is deteriorated, it may have a heat permeation rate within the above range.
상기 벽지 시스템의 열 관류율의 하한치는 특별히 제한하지 않으며, 일 예로 1.0 W/m2·K 일 수 있다.The lower limit of the thermal permeation rate of the wallpaper system is not particularly limited, and may be, for example, 1.0 W/m 2 ·K.
상기 열 관류율은 벽지 시스템을 약 1600×1200mm (가로×세로)의 시편으로 제조한 후 석고보드 사이에 상기 시편을 위치시켜 샘플을 준비한 후, 단열성 측정방법(KS F 2273)을 이용하여 온도가 0℃로 유지되는 저온실과 온도가 20℃로 유지되는 상온실 사이에 상기 샘플을 위치시켜 30-60분 동안 온도 흐름의 안정화 과정을 거친 샘플의 열 저항 값을 측정한 후, 샘플의 열 저항 값과 석고보드의 열 저항 값을 뺀 시편의 열 저항 값의 역수를 계산하여 열 관류율을 계산할 수 있으며, 상기 열 관류율이 낮을수록 단열성이 우수한 것이다. The heat permeation rate is determined by preparing a wallpaper system as a specimen of about 1600 x 1200 mm (width x length), and then placing the specimen between gypsum boards to prepare a sample, and then using a thermal insulation measurement method (KS F 2273) at a temperature of 0. After measuring the thermal resistance value of the sample that has undergone a process of stabilizing the temperature flow for 30-60 minutes by placing the sample between the low temperature room maintained at °C and the room temperature room maintained at 20 °C, the thermal resistance value of the sample and The thermal permeation rate can be calculated by calculating the reciprocal of the thermal resistance value of the specimen by subtracting the thermal resistance value of the gypsum board, and the lower the thermal permeation rate, the better the thermal insulation property.
또한, 본 발명의 벽지 시스템(100)은 보온율이 60% 이상, 65%이상일 수 있으며, 보온율이 상기 범위 미만일 경우, 벽지 시스템의 보온성이 저하되어 단열성이 저하될 수 있으므로 상기 범위 내의 보온율을 가질 수 있다.In addition, the wallpaper system 100 of the present invention may have a thermal insulation rate of 60% or more and 65% or more, and if the thermal insulation rate is less than the above range, the thermal insulation property of the wallpaper system may decrease, so that the thermal insulation rate within the above range Can have.
상기 벽지 시스템(100)의 보온율의 상한치는 특별히 제한하지 않으며, 일 예로 99%이하일 수 있다.The upper limit of the thermal insulation rate of the wallpaper system 100 is not particularly limited, and may be, for example, 99% or less.
상기 보온율은 벽지 시스템을 약 500mm×500mm×4mm (가로×세로×두께)인 시편으로 제조한 후, 보온율 측정법(KS K 0560)을 이용하여 발열체에 시편을 부착하지 않았을 때의 발열량과 발열체에 시편을 부착하였을 때의 발열량을 이용하여 하기 [식 1]로 나타내는 수식을 이용하여 상기 시편의 보온율을 계산할 수 있으며 보온율이 높을수록 보온성이 우수한 것이다.The heat retention rate is the amount of heat generated when the wallpaper system is not attached to the heating element and the heating element after manufacturing the wallpaper system into a specimen of about 500 mm × 500 mm × 4 mm (width × height × thickness), and then using the thermal insulation rate measurement method (KS K 0560). The heat retention rate of the specimen can be calculated using the formula represented by the following [Equation 1] by using the calorific value when the specimen is attached to, and the higher the heat retention rate, the better the heat retention property.
[식 1] [Equation 1]
Figure pat00001
Figure pat00001
이하, 본 발명의 벽지 시스템(100)의 각 구성을 구체적으로 설명하도록 한다.Hereinafter, each configuration of the wallpaper system 100 of the present invention will be described in detail.
단열 초배지(110)Insulation paper (110)
상기 단열 초배지(110)는 본 발명의 벽지 시스템(100)에 쿠션감 및 단열성을 부여하는 역할을 하는 것으로, 융점이 상이한 2종의 섬유가 혼섬된 동일한 열가소성 수지 재질인 부직포로 형성된 것일 수 있으며, 상기 부직포는 쿠션감 및 단열성이 우수한 효과가 있다(도 1 참조).The insulating paper sheet 110 serves to impart cushioning and heat insulating properties to the wallpaper system 100 of the present invention, and may be formed of a nonwoven fabric made of the same thermoplastic resin material in which two kinds of fibers having different melting points are mixed, The nonwoven fabric has excellent cushioning and thermal insulation properties (see FIG. 1).
본 발명에서 잡물(雜物)은 벽면(즉, 콘크리트 벽면)의 자갈, 모래 등의 이물질을 의미하고, 크랙(crack)은 벽면의 갈라진 틈새를 의미하며, 크랙 웨이브(crack wave)란, 벽면의 크랙으로부터 방출되는 공기로 인하여 시공되는 벽지 표면에 발생되는 물결 무늬를 의미한다.In the present invention, miscellaneous objects mean foreign substances such as gravel and sand on a wall surface (that is, a concrete wall surface), and a crack means a crack in the wall surface, and a crack wave means a foreign substance on the wall surface (that is, a concrete wall surface). It refers to the wave pattern generated on the surface of the wallpaper being constructed by the air emitted from the crack.
상기 부직포는 방적, 제직, 편성과 같은 직포 공정 없이 섬유 집합체를 화학적 작용이나, 기계적 작용 또는 적당한 수분과 열처리에 의해 섬유 상호간을 결합한 포 형상을 의미한다.The non-woven fabric refers to a fabric shape in which fibers are bonded to each other by chemical action, mechanical action, or heat treatment with appropriate moisture without a woven process such as spinning, weaving, or knitting.
상기 열가소성 수지는 일 예로, 습기 침투가 쉬운 콘크리트 벽면의 수분 흡수를 방지할 수 있는 소수성 특성을 가지는 폴리에스테르 섬유일 수 있다.The thermoplastic resin may be, for example, a polyester fiber having hydrophobic properties capable of preventing moisture absorption on a concrete wall surface, which is easily penetrated.
상기 폴리에스테르 섬유는 본 발명의 기술분야에서 공지된 일반적인 폴리에스테르 섬유를 이용할 수 있으며, 상기 폴리에스테르 섬유는 단면이 원형 또는 타원형으로 방사되는 것일 수 있고, 섬유의 굵기는 2-10 데니어, 3-8 데니어 일 수 있다.The polyester fiber may be a general polyester fiber known in the technical field of the present invention, and the polyester fiber may be spun in a circular or elliptical cross section, and the thickness of the fiber is 2-10 denier, 3- It can be 8 denier.
상기 폴리에스테르 섬유의 굵기가 상기 범위 미만인 경우 섬유의 굵기가 얇아 초배지의 평량이 낮아져 시공성이 떨어질 수 있으며, 상기 범위 초과인 경우 초배지 내에 포획되는 공기층 함량이 정정수준보다 낮아 단열 보온성이 떨어질 수 있다.If the thickness of the polyester fiber is less than the above range, the thickness of the fiber is thin, so the basis weight of the super medium may be lowered, resulting in poor workability, and if it exceeds the above range, the amount of the air layer trapped in the super medium may be lower than the correction level, resulting in poor thermal insulation insulation.
보다 구체적으로, 본 발명의 일 실시예에서 상기 폴리에스테르 섬유의 굵기는 6데니어 일 수 있다. More specifically, in an embodiment of the present invention, the thickness of the polyester fiber may be 6 denier.
상기 융점이 상이한 2종의 섬유는 융점이 250-280℃인 고융점 폴리에스테르 섬유 및 융점이 110-150℃인 저융점 폴리에스테르 섬유일 일 수 있으며, 본 발명의 부직포는 고융점 폴리에스테르 섬유 및 저융점 폴리에스테르 섬유가 혼섬된 부직포로써 접착성, 성형성 및 형태 안정성이 우수한 특징을 가진다.The two kinds of fibers having different melting points may be a high melting point polyester fiber having a melting point of 250-280° C. and a low melting point polyester fiber having a melting point of 110-150° C., and the nonwoven fabric of the present invention is a high melting point polyester fiber and As a nonwoven fabric mixed with low-melting polyester fibers, it has excellent characteristics of adhesion, moldability, and shape stability.
상기 고융점 폴리에스테르 섬유 및 저융점 폴리에스테르 섬유가 혼합되는 경우, 단열 초배지(110) 제조 시, 상기 저융점 폴리에스테르 섬유가 고융점 폴리에스테르 섬유 사이에서 용융되어 고융점 폴리에스테르 섬유 사이를 용융 접착시킴으로써 상기 고융점 폴리에스테르 섬유의 유동을 방지하여 형태 안정성이 우수하고 상기 단열 초배지(110)의 강도가 높아질 수 있다.When the high-melting-point polyester fiber and the low-melting-point polyester fiber are mixed, the low-melting-point polyester fiber is melted between the high-melting-point polyester fiber and melt-adhesive between the high-melting-point polyester fiber when manufacturing the insulating paper 110 By doing so, it is possible to prevent the flow of the high-melting-point polyester fiber, thereby exhibiting excellent shape stability and increasing the strength of the insulating super media 110.
또한, 본 발명의 단열 초배지(110)는 일면이 매끄럽고 평평한 면으로 형성되어 상기 단열 초배지(110) 일면에 시공되는 단열벽지(130)와의 접착력을 향상시킬 수 있고 상기 단열 초배지(110) 표면의 요철을 보완할 수 있다.In addition, the insulating paper substrate 110 of the present invention has a smooth and flat surface to improve adhesion to the insulating wallpaper 130 installed on one surface of the insulating paper plate 110, and the surface irregularities of the insulating paper plate 110 Can be supplemented.
본 발명에서 상기 단열 초배지(110) 일면은 시공 시 벽지가 접착되는 부분으로, 용융 압착을 통하여 매끄럽고 평평하게 형성되는 면을 말한다.In the present invention, one surface of the insulating paper 110 is a part to which wallpaper is adhered during construction, and refers to a surface formed smoothly and flatly through melt compression.
구체적으로, 상기 부직포는 고융점 폴리에스테르 섬유 40-60중량% 및 저융점 폴리에스테르 섬유 60-40중량%로 혼합된 혼합섬유일 수 있다.Specifically, the nonwoven fabric may be a mixed fiber mixed with 40-60% by weight of high melting point polyester fibers and 60-40% by weight of low melting point polyester fibers.
상기 혼합섬유의 고융점 폴리에스테르 섬유가 60중량% 초과일 경우 저융점 폴리에스테르 섬유의 함량이 낮아져, 단열 초배지(110) 일면을 매끄럽고 평평한 면으로 제조하기 어려울 수 있고, 40중량% 미만일 경우 상기 단열 초배지(110) 제조 시, 용융되는 저융점 폴리에스테르 섬유의 함량이 매우 높아 단열 초배지(110)의 가공성 및 사용이 용이하지 않은 문제점이 있으므로, 상기 범위 내의 함량을 가질 수 있다.When the high melting point polyester fiber of the mixed fiber is more than 60% by weight, the content of the low melting point polyester fiber is lowered, so it may be difficult to manufacture one side of the insulating super medium 110 as a smooth and flat side, and when it is less than 40% by weight, the insulation When the super medium 110 is manufactured, the content of the low-melting polyester fiber to be melted is very high, so that the processability and use of the insulating super medium 110 are not easy, and thus the content within the above range may be obtained.
상기 매끄럽고 평평한 면이 형성된 단열 초배지(110) 일면의 평균마찰계수는 0.2-1.2, 바람직하게는 0.4-1.0, 보다 바람직하게는 0.5-0.8일 수 있다. 상기 단열 초배지(110) 일면의 평균마찰계수가 0.5 미만일 경우 향후 서술되는 단열 초배지(110) 시공 시, 접착제 또는 도배용 풀의 침투가 용이하지 않고, 0.8 초과일 경우, 단열 초배지(110)의 표면에 보풀이 일어나고, 부직포의 섬유 엉킴이 풀어져 단열벽지(130)의 시공이 용이하지 않은 문제점이 있으므로 상기 범위 내의 평균마찰계수를 가질 수 있다.The average coefficient of friction of one side of the insulating super medium 110 on which the smooth and flat surface is formed may be 0.2-1.2, preferably 0.4-1.0, and more preferably 0.5-0.8. When the average friction coefficient of one side of the insulating paper 110 is less than 0.5, the penetration of the adhesive or paper paste is not easy when constructing the insulating paper 110 to be described later, and if it exceeds 0.8, the surface of the insulating paper 110 There is a problem in that fluffing occurs in the nonwoven fabric, and the entanglement of the fibers of the nonwoven fabric is unraveled, so that the construction of the insulating wallpaper 130 is not easy, and thus the average coefficient of friction may be within the above range.
상기 평균마찰계수는 상기 단열 초배지(110)를 63mm×63mm (가로×세로)의 시편으로 제조한 후, 평균마찰계수 측정법(ASTM D 1894)를 이용하여 평판에 250mm×130mm (가로×세로)의 피마찰재를 측정하고자 하는 면이 노출되도록 장착하고, 상기 제조된 시편편을 측정하고자 하는 면이 노출되도록 밑면에 부착한 후, 나일론 줄과 시험편을 미끄럼판에 연결하고 하중센서를 부착하여, 29N의 로드셀, 1.96N의 수직하중, 150mm/min의 속도로 정마찰계수를 측정하고, 이를 5번 반복하여 상기 정마찰계수의 평균값을 계산하여 평균마찰계수를 측정할 수 있다.The average coefficient of friction was prepared as a specimen of 63 mm×63 mm (width×length) of the insulating super media 110, and then 250 mm×130 mm (width×length) on a plate by using an average coefficient of friction measurement (ASTM D 1894). Mount the friction material to be measured so that the surface to be measured is exposed, and the prepared specimen piece is attached to the bottom surface so that the surface to be measured is exposed, and then the nylon string and the test piece are connected to the sliding plate, and a load sensor is attached. The load cell, a vertical load of 1.96N, a static friction coefficient is measured at a speed of 150 mm/min, and the average friction coefficient can be measured by calculating the average value of the static friction coefficient by repeating this five times.
또한, 상기 단열 초배지(110)는 니들펀칭 부직포일 수 있다. In addition, the thermal insulation paper substrate 110 may be a needle punched nonwoven fabric.
구체적으로, 본 발명의 단열 초배지(110) 제조 시, 상기 고융점 폴리에스테르 섬유 및 저융점 폴리에스테르 섬유가 서로 불규칙하게 배열되어 엉켜지는 니들펀칭 공정을 수행하여 섬유 사이에 수많은 공기층을 형성함으로써 열기나 냉기의 이동을 차단할 수 있는 효과가 있어 월등히 우수한 단열성을 나타낼 수 있다.Specifically, in the manufacture of the insulating paper 110 of the present invention, the high melting point polyester fiber and the low melting point polyester fiber are irregularly arranged and entangled with each other by performing a needle punching process to form a number of air layers between the fibers. As it has the effect of blocking the movement of cold air, it can exhibit remarkably excellent thermal insulation properties.
상기 단열 초배지(110) 내의 공기층 함량은 85% 이상, 바람직하게는 90% 이상, 보다 바람직하게는 94% 이상일 수 있으며, 상기 범위 내에서 15W/m2·K 이하의 열 관류율을 가지며 우수한 단열성을 구현할 수 있는 효과를 가질 수 있다. The air layer content in the adiabatic super medium 110 may be 85% or more, preferably 90% or more, more preferably 94% or more, and has a heat permeation rate of 15W/m 2 ·K or less within the above range, and has excellent thermal insulation properties. It can have an effect that can be implemented.
상기 단열 초배지(110) 내의 공기층 함량의 상한치는 특별히 한정하지 않으나, 일 예로 99%일 수 있다.The upper limit of the content of the air layer in the adiabatic paper 110 is not particularly limited, but may be 99%, for example.
상기 단열 초배지(110) 내의 공기층의 함량이 85% 미만일 경우 열 관류율이 상승되어 단열성능이 우수하지 못한 문제점이 있어 상기 범위 내의 공기층 함량을 가질 수 있다.When the content of the air layer in the adiabatic super medium 110 is less than 85%, there is a problem in that the thermal permeation rate is increased and the thermal insulation performance is not excellent, and thus the air layer content within the above range may be obtained.
상기 단열 초배지(110) 내의 공기층 함량은 상기 단열 초배지(110)를 약 5cm×5cm (가로×세로)의 시편으로 제조한 후, 상기 시편의 부피 및 무게를 측정하고, 고융점 및 저융점 폴리에스테르만의 비중(ALFA MIRAGE社, SD-200L) 및 부피를 측정하여 상기 단열 초배지(110) 내 공기층의 ?t량을 %로 나타내어 구할 수 있다. The content of the air layer in the insulating super medium 110 is obtained by preparing the insulating super medium 110 as a specimen of about 5 cm × 5 cm (width × length), and then measuring the volume and weight of the specimen, and high melting point and low melting point polyester By measuring the specific gravity of the bay (ALFA MIRAGE, SD-200L) and the volume, ?t amount of the air layer in the adiabatic super medium 110 can be calculated as %.
보다 구체적으로, 상기 단열 초배지(110)를 5cm×5cm (가로×세로)의 시편으로 제조한 후, 상기 시편의 높이를 자로 측정하여 상기 시편의 부피를 구할 수 있고, ALFA MIRAGE社의 SD-200L를 이용하여 상기 고융점 및 저융점 폴리에스테르 만의 비중을 측정할 수 있고, 이를 이용하여 고융점 및 저융점 폴리에스테르 만의 부피 구함으로써, 상기 단열 초배지(110) 내 공기층의 ?t량을 %로 나타내어 구할 수 있다.More specifically, after the heat-insulating paper 110 is prepared as a specimen of 5 cm x 5 cm (width x length), the volume of the specimen can be obtained by measuring the height of the specimen with a ruler, and SD-200L of ALFA MIRAGE By using the specific gravity of only the high-melting point and low-melting point polyester can be measured, and by using this to obtain the volume of only the high-melting point and low-melting point polyester, the ?t amount of the air layer in the insulating super medium 110 is expressed in %. You can get it.
본 발명의 단열 초배지(110)의 두께는 3.0-5.0mm 또는 3.5-4.5mm일 수 있으며, 상기 범위 내에서 우수한 쿠션감 및 단열성을 가지며, 상기 쿠션감에 의해 벽면의 요철을 보완할 수 있으며, 상기 단열벽지(130)를 지지할 수 있다. 상기 단열 초배지(110)의 두께가 상기 범위 미만일 경우 단열성이 떨어지고 쿠션감이 저하되며 벽면의 요철 형상이 두드러짐과 동시에 상기 단열벽지(130)를 지지할 수 없으며, 상기 범위 초과일 경우 가공성이 용이하지 않고 시공의 어려움이 있어 상기 범위 내의 두께를 가질 수 있다.The thickness of the heat insulation superbadge 110 of the present invention may be 3.0-5.0mm or 3.5-4.5mm, has excellent cushioning feeling and heat insulation within the above range, and the unevenness of the wall surface can be supplemented by the cushioning feeling, The insulating wallpaper 130 may be supported. If the thickness of the insulating superbadge 110 is less than the above range, the insulating property is deteriorated, the cushioning feeling is deteriorated, the uneven shape of the wall surface is remarkable, and at the same time, the insulating wallpaper 130 cannot be supported, and if it exceeds the above range, the processability is not easy. There is a difficulty in construction and may have a thickness within the above range.
또한, 상기 단열 초배지(110)의 평량은 200-400g/m2, 200-350g/m2 또는 200-300g/m2 일 수 있으며, 상기 범위 내에서 충분한 공기층을 확보할 수 있고 우수한 단열성을 가지며 상기 단열벽지(130)가 찢어지지 않도록 지지할 수 있으며 우수한 쿠션감을 가진다. 상기 단열 초배지(110)의 평량이 200g/m2 미만일 경우 충분한 공기층을 확보하지 못해 경량성 및 단열 성능이 저하되며 시공 시 단열벽지(130)가 찢어질 수 있고, 400g/m2 초과일 경우 단열성은 향상될 수 있으나, 평량이 너무 무거워 초배지 시공 시, 벽면에서 이탈이 발생할 수 있으므로 상기 범위 내의 평량을 가질 수 있다.In addition, the basis weight of the insulating super medium 110 may be 200-400g/m 2 , 200-350g/m 2 or 200-300g/m 2 , and it is possible to secure a sufficient air layer within the above range and have excellent thermal insulation properties. The insulating wallpaper 130 can be supported so as not to be torn, and has an excellent cushioning feeling. If the basis weight of the insulating super media 110 is less than 200 g/m 2 , it is not possible to secure a sufficient air layer, resulting in reduced light weight and thermal insulation performance, and the thermal insulation wallpaper 130 may be torn during construction, and thermal insulation when it exceeds 400 g/m 2 Although can be improved, the basis weight may be too heavy, so that separation may occur from the wall surface when the super culture is constructed, so that the basis weight may be within the above range.
본 발명의 단열 초배지(110)는 열 관류율이 15W/m2·K 이하, 10W/m2·K 이하, 또는 9.2W/m2·K 이하일 수 있으며, 열 관류율이 상기 범위를 초과할 경우 단열 초배지(110)의 단열성이 저하되므로 상기 범위 내의 열 관류율을 가질 수 있다.Chobaeji insulation 110 of the present invention can be less than the heat gwanryuyul 15W / m 2 · K or less, 10W / m 2 · K or less, or 9.2W / m 2 · K, the heat insulating case to heat gwanryuyul exceeds the above range, Since the thermal insulation properties of the super medium 110 are deteriorated, it may have a heat permeation rate within the above range.
상기 단열 초배지(110)의 열 관류율의 하한치는 특별히 한정하지 않으나, 일 예로 1.0 W/m2·K 이상일 수 있다.The lower limit of the heat permeation rate of the adiabatic paper 110 is not particularly limited, but may be, for example, 1.0 W/m 2 ·K or more.
상기 열 관류율을 계산하는 방법은 위에서 서술한 바와 동일하므로 중복된 기재는 생략하도록 한다.Since the method of calculating the heat transmission rate is the same as described above, duplicate descriptions will be omitted.
또한, 상기 단열 초배지(110)는 보온율이 50%이상, 55%이상, 60%이상일 수 있으며, 보온율이 상기 범위 미만일 경우 단열 초배지(110)의 보온성이 저하되므로 상기 범위 내의 보온율을 가질 수 있다.In addition, the thermal insulation super medium 110 may have a thermal insulation rate of 50% or more, 55% or more, and 60% or more, and if the thermal insulation rate is less than the above range, the thermal insulation property of the thermal insulation super media 110 is lowered, so that the thermal insulation rate may be within the above range. I can.
상기 단열 초배지(110)의 보온율의 상한치는 특별히 한정하지 않으나, 일 예로 99% 이하일 수 있다.The upper limit of the thermal insulation rate of the insulating paper 110 is not particularly limited, but may be, for example, 99% or less.
상기 보온율을 계산하는 방법은 위에서 서술한 바와 동일하므로 중복된 기재는 생략하도록 한다.Since the method of calculating the heat retention rate is the same as described above, duplicate descriptions will be omitted.
또한, 본 발명의 단열 초배지(110)는 열전도율이 50mW/m·K 미만, 바람직하게는 40mW/m·K 미만, 보다 바람직하게는 35mW/m·K 미만일 수 있으며, 열전도율이 상기 범위를 초과할 경우 단열 초배지(110)의 단열성이 저하되므로 상기 범위 내의 열전도율을 가질 수 있다.In addition, the thermal insulation super medium 110 of the present invention may have a thermal conductivity of less than 50mW/m·K, preferably less than 40mW/m·K, more preferably less than 35mW/m·K, and the thermal conductivity may exceed the above range. In this case, since the thermal insulation properties of the adiabatic super medium 110 are deteriorated, it may have a thermal conductivity within the above range.
상기 단열 초배지(110)의 열전도율의 하한치는 특별히 한정하지 않으나, 일 예로 10 mW/m·K 이상일 수 있다.The lower limit of the thermal conductivity of the adiabatic super medium 110 is not particularly limited, but may be, for example, 10 mW/m·K or more.
상기 열전도율은 단열 초배지(110)를 약 200mm×200mm×1mm (가로×세로×두께)의 시편으로 제작한 후, 평판 열전도율 측정법(KS L ISO 8301)을 이용하여 시편의 상측의 온도를 0℃, 하측의 온도를 20℃로 설정하고, 10-20분 후 온도 흐름이 안정된 시편의 온도 평형 값을 측정하여 상기 시편의 열전도율을 측정할 수 있다. For the thermal conductivity, after making a specimen of about 200mm×200mm×1mm (width×length×thickness), the temperature of the upper side of the sample was adjusted to 0°C using a flat plate thermal conductivity measurement method (KS L ISO 8301), The temperature of the lower side is set to 20° C., and after 10-20 minutes, the thermal conductivity of the specimen can be measured by measuring the temperature equilibrium value of the specimen in which the temperature flow is stable.
한편, 본 발명의 단열 초배지(110)는 시공 시 벽면 전면에 부착되는 것일 수 있다. 상기 단열 초배지(110)를 벽면 전면에 부착할 경우, 상기 단열벽지(130)를 단단하게 지지할 수 있어 상기 단열벽지(130)가 찢어지는 문제점을 방지할 수 있다.On the other hand, the insulation paper 110 of the present invention may be attached to the entire wall surface during construction. When the insulation paper 110 is attached to the entire wall surface, the insulation wallpaper 130 can be firmly supported, thereby preventing the insulation wallpaper 130 from being torn.
종래의 초배지는 벽면에 부분 부착 시공되는 것인 바, 초배지를 부분 부착할 경우 본 발명과 같은 단열성능을 구현하기 어려우며, 종래의 초배지에 본 발명의 단열벽지(130)를 시공할 경우 상기 단열벽지(130)를 단단하게 지지하기 어려워 상기 단열벽지(130)가 쉽게 찢어질 수 있는 문제점이 있으나, 본 발명의 단열 초배지(110)는 벽면에 전면 부착됨으로써 상기의 문제점을 해결할 수 있다.The conventional super badge is partially attached to the wall, and it is difficult to implement the insulation performance as in the present invention when the super badge is partially attached, and when the insulating wallpaper 130 of the present invention is constructed on the conventional super badge, the insulating wallpaper Although it is difficult to firmly support 130, there is a problem in that the insulating wallpaper 130 can be easily torn. However, the insulating paper substrate 110 of the present invention can solve the above problem by attaching it to the wall.
한편, 본 발명의 단열 초배지(110) 상에 전면 초배지(미도시) 및 운용지(미도시)를 더 포함할 수 있다.On the other hand, it may further include a front chobaeji (not shown) and an operating site (not shown) on the insulating paperboard 110 of the present invention.
상기 전면 초배지는 단열 초배지(110) 상부에 위치하여 상기 단열 초배지(110) 및 단열벽지(130)의 이음매가 벌어지는 것을 보완하고, 단열벽지(130)의 수축률을 낮추는 역할을 할 수 있다.The front panel is positioned above the thermal insulation panel 110 to compensate for the opening of the thermal insulation panel 110 and the thermal insulation wallpaper 130, and may serve to lower the shrinkage rate of the thermal insulation wallpaper 130.
상기 전면 초배지는 두께가 20-40㎛이고 평량이 30-50g/m2인 스펀본드 부직포로 형성된 것일 수 있다.The front super medium may be formed of a spunbond nonwoven fabric having a thickness of 20-40 μm and a basis weight of 30-50 g/m 2.
상기 부직포에 대한 구체적인 설명은 위에서 서술한 바, 중복된 기재는 생략하도록 한다.A detailed description of the nonwoven fabric has been described above, and redundant descriptions will be omitted.
상기 전면 초배지는 종래의 초배지와 동일한 스펀본드 부직포로써, 상기 전면 초배지만 시공하여 단열벽지(130)를 부착할 경우, 상기 전면 초배지가 단열벽지(130)를 지지하지 못하여 벽면 이탈 현상이나, 벽지 찢어짐 현상이 발생하는 문제점이 있었으나, 본 발명의 단열 초배지(110)를 시공 벽면에 시공 후, 상기 전면 초배지를 부착함으로써, 하기에서 시공되는 단열벽지(130)의 수축률을 낮출 수 있고, 단열 초배지(110) 및 단열벽지(130)의 이음매가 벌어지는 현상을 방지할 수 있으며, 단열성이 더욱 향상되고, 단열벽지(130)의 벽면 이탈 현상 또는 벽지 찢어짐 현상을 방지할 수 있다.The front super-badge is the same spunbond nonwoven fabric as the conventional super-badge, and when only the front super-badge is constructed and the insulation wallpaper 130 is attached, the front super-badge cannot support the heat-insulating wallpaper 130 and thus the wall surface is separated or the wallpaper is torn. Although there was a problem that the phenomenon occurs, by attaching the front super badge after installing the thermal insulation paper 110 of the present invention on the construction wall, it is possible to lower the shrinkage rate of the thermal insulation wallpaper 130 to be constructed below, and the insulation super medium 110 ) And the opening of the joint of the insulating wallpaper 130 may be prevented, insulating properties may be further improved, and separation of the wall surface of the insulating wallpaper 130 or tearing of the wallpaper may be prevented.
상기 운용지는 상기 전면 초배지 상부에 위치하는 것으로, 상기 전면 초배지와 더불어 단열벽지(130)의 수축률을 낮출 수 있고 상기 단열벽지(130)의 이음매가 위치하는 부위에 부분적으로 형성되어 단열벽지(130)의 이음매가 벌어지는 현상을 방지할 수 있다.The operating paper is located above the front paper, and it is possible to reduce the shrinkage rate of the insulating wallpaper 130 together with the front paper, and is partially formed in a portion where the joint of the insulating wallpaper 130 is located, so that the insulating wallpaper 130 It is possible to prevent the phenomenon that the seam of the joints from spreading out.
상기 운용지는 당업계에서 통상적으로 사용하는 재질을 사용할 수 있으며, 일 예로, 종이를 사용할 수 있다.The operating paper may be made of a material commonly used in the art, and as an example, paper may be used.
단열벽지(130)Insulation Wallpaper(130)
상기 단열벽지(130)는 아래에서부터 순차적으로, 기재층(131), 상기 기재층(131) 상부에 전면 도포된 제1발포수지층(133)을 포함하는 열전도율이 150mW/m·K미만인 단열벽지(130)이다(도 2 참조).The insulating wallpaper 130 is an insulating wallpaper having a thermal conductivity of less than 150mW/m·K including a base layer 131 and a first foaming resin layer 133 applied entirely on top of the base layer 131 sequentially from the bottom. (130) (see Fig. 2).
구체적으로, 상기 단열벽지(130)는 열전도율이 150mW/m·K미만, 100mW/m·K 미만 또는 70mW/m·K 미만일 수 있으며, 열전도율이 상기 범위 이상일 경우, 벽지의 단열성이 저하되므로 상기 범위 내의 열전도율을 가질 수 있다.Specifically, the thermal insulation wallpaper 130 may have a thermal conductivity of less than 150mW/m·K, less than 100mW/m·K, or less than 70mW/m·K, and when the thermal conductivity is more than the above range, the insulation property of the wallpaper decreases. It can have a thermal conductivity within.
상기 단열벽지(130)의 열전도율의 하한치는 특별히 한정하지 않으나, 일 예로 10mW/m·K 이상일 수 있다.The lower limit of the thermal conductivity of the insulating wallpaper 130 is not particularly limited, but may be, for example, 10 mW/m·K or more.
상기 열전도율을 측정하는 방법은 위에서 서술한 바와 동일하므로 중복된 기재는 생략하도록 한다.Since the method of measuring the thermal conductivity is the same as described above, redundant descriptions will be omitted.
이하, 상기 단열벽지(130)의 각 층을 구체적으로 설명하도록 한다.Hereinafter, each layer of the insulating wallpaper 130 will be described in detail.
기재층(131)Base layer 131
상기 기재층(131)은 본 발명의 기술분야에서 공지된 일반적인 벽지용 원지를 사용할 수 있으며, 예를 들면, 모조지 또는 부직포(예: 폴리에스테르/펄프 복합 부직포) 등을 들 수 있으나, 이에 제한되는 것은 아니다. The base layer 131 may use a general base paper for wallpaper known in the technical field of the present invention, for example, imitation paper or non-woven fabric (eg, polyester/pulp composite non-woven fabric), etc., but is limited thereto. It is not.
상기 기재층(131)은 평량이 80-200g/㎡일 수 있다. 상기 기재층(131)의 평량이 상기 범위 미만인 경우 시공 또는 사용과정에서 벽지의 찢어짐 등의 손상이 발생할 우려가 있고, 상기 범위를 초과는 경우 벽지 중량이 너무 무거워, 틈벌어짐 및 컬링 등 시공성 문제를 야기할 우려가 있어 상기 범위 내일 수 있다.The base layer 131 may have a basis weight of 80-200g/m2. If the basis weight of the base layer 131 is less than the above range, there is a concern that damage such as tearing of the wallpaper may occur during construction or use, and if it exceeds the above range, the wallpaper weight is too heavy, causing workability problems such as gaps and curling. It may be within the above range because there is a risk of causing.
상기 기재층(131)의 두께는 일례로 0.1-0.3mm일 수 있으나 반드시 이로 제한되는 것은 아니다. The thickness of the base layer 131 may be 0.1-0.3mm, for example, but is not limited thereto.
제1발포수지층(133)First foaming resin layer (133)
상기 제1발포수지층(133)은 상기 기재층(131) 상부에 전면 도포되어 형성되는 발포 수지층으로, 본 발명의 단열벽지(130)에 쿠션감 및 단열성을 부여하면서, 충전제로서 밀도 및 열전도율이 낮은 글라스 버블을 특정 함량 포함하여 벽지에 경량화를 부여하면서도, 단열성을 더욱 향상시키는 역할을 하는 것으로, 열가소성 수지 100중량부에 대해 글라스 버블 5-20중량부를 포함할 수 있다.The first foaming resin layer 133 is a foamed resin layer formed by being entirely coated on the top of the base layer 131, imparting a cushioning feeling and heat insulation to the insulating wallpaper 130 of the present invention, and density and thermal conductivity as a filler. This low glass bubble is included in a specific content to provide weight reduction to the wallpaper and further improves heat insulation, and may include 5 to 20 parts by weight of glass bubbles based on 100 parts by weight of the thermoplastic resin.
구체적으로, 상기 제1발포수지층(133)은 열가소성 수지 100중량부에 대해 글라스 버블 5-20중량부를 포함하는 졸(sol) 상태의 제1발포수지층(133) 형성용 조성물을 이용하여 형성된 것일 수 있다.Specifically, the first foaming resin layer 133 is formed using a composition for forming the first foaming resin layer 133 in a sol state including 5 to 20 parts by weight of glass bubbles with respect to 100 parts by weight of a thermoplastic resin. Can be.
상기 열가소성 수지는 폴리염화비닐(Poly vinyl chloride, PVC) 수지, 폴리스티렌(Poly styrene, PS) 수지, 아크릴로니트릴부타디엔스티렌(Acrylonitrile butadiene styrene, ABS) 수지, 폴리유산(Poly lactic acid, PLA) 수지, 폴리에틸렌테레프탈레이트(Polyethylene terephthalate, PET) 수지, 폴리올레핀(Poly olefin, PO) 수지 및 아크릴(Acrylic) 수지로 이루어진 군으로부터 선택된 1종 이상의 수지일 수 있고, 본 발명의 구제적인 일 예로, 폴리염화비닐(Poly vinyl chloride, PVC) 수지일 수 있다.The thermoplastic resin is polyvinyl chloride (PVC) resin, polystyrene (PS) resin, acrylonitrile butadiene styrene (ABS) resin, polylactic acid (PLA) resin, It may be one or more resins selected from the group consisting of polyethylene terephthalate (PET) resin, polyolefin (PO) resin, and acrylic resin, and as a specific example of the present invention, polyvinyl chloride ( Poly vinyl chloride, PVC) resin.
상기 제1발포수지층(133)에 포함되는 폴리염화비닐 수지는 중합도가 800-1100 또는 850-1000일 수 있으며, 상기 범위 미만일 경우 졸(sol)을 형성하기 어렵거나 또는 기재층(131) 상부에 코팅이 어려울 수 있고, 상기 범위를 초과할 경우 발포배율을 높이는데 한계가 있으므로 상기 범위 내의 중합도를 갖는 폴리염화비닐 수지를 사용할 수 있다. The polyvinyl chloride resin included in the first foaming resin layer 133 may have a degree of polymerization of 800-1100 or 850-1000, and if it is less than the above range, it is difficult to form a sol or the upper part of the base layer 131 Coating may be difficult, and if the above range is exceeded, there is a limit to increasing the expansion ratio, and thus a polyvinyl chloride resin having a polymerization degree within the above range may be used.
상기 글라스 버블은 종래 벽지에 충전제로서 사용되는 탄산칼슘의 대체용으로 사용될 수 있는 중공의 입자로서, 내부에 공기층을 포함하고 있어 밀도 및 열전도율이 낮아 본 발명의 벽지에 경량화 및 단열성을 부여할 수 있다. The glass bubble is a hollow particle that can be used as a substitute for calcium carbonate used as a filler in the conventional wallpaper, and includes an air layer therein, so its density and thermal conductivity are low, so that it can give the wallpaper of the present invention light weight and heat insulation. .
구체적으로, 상기 글라스 버블은 소다-라임-보로실리케이트 유리(soda-lime-borosilicate glass)를 적어도 90중량% 이상, 94중량% 이상 또는 97중량% 이상 포함하는 것일 수 있다. 상기 소다-라임-보로실리케이트 유리는 50-90중량%의 SiO2, 2-20중량%의 알칼리금속 산화물, 1-30중량%의 2가 금속 산화물, 1-30중량%의 B2O3, 0.005-1.5중량%의 황 또는 황산화물을 포함할 수 있다. 상기 소다-라임-보로실리케이트 유리의 구체적 일예로 70-80중량%의 SiO2, 3-8중량%의 Na2O, 8-15중량%의 CaO, 2-6중량%의 B2O3, 0.125%-1.5%의 SO3를 포함하는 것을 예시할 수 있으나, 반드시 이로 제한되는 것은 아니다. Specifically, the glass bubble may contain at least 90% by weight, 94% by weight or more, or 97% by weight or more of soda-lime-borosilicate glass. The soda-lime-borosilicate glass is 50-90% by weight of SiO 2 , 2-20% by weight of alkali metal oxide, 1-30% by weight of divalent metal oxide, 1-30% by weight of B 2 O 3 , It may contain 0.005-1.5% by weight of sulfur or sulfur oxides. As a specific example of the soda-lime-borosilicate glass, 70-80% by weight of SiO 2 , 3-8% by weight of Na 2 O, 8-15% by weight of CaO, 2-6% by weight of B 2 O 3 , It may be exemplified that 0.125%-1.5% of SO 3 is included, but is not necessarily limited thereto.
또한, 상기 글라스 버블은 평균 진밀도(ture density)가 0.15-0.3g/cc 또는 0.17-0.25g/cc일 수 있다. 상기 범위 미만인 경우 상기 제1 발포 수지층(133) 내에 글라스 버블의 분산성이 저하될 수 있어 생산성에 문제가 있을 수 있고, 상기 범위를 초과할 경우 벽지 경량화를 구현하기 곤란할 수 있고, 공기층의 부피가 줄어들어 단열성 개선 효과가 미미할 수 있어 상기 범위 내의 평균 진밀도를 가질 수 있다.In addition, the glass bubbles may have an average true density of 0.15-0.3g/cc or 0.17-0.25g/cc. If it is less than the above range, the dispersibility of the glass bubbles in the first foamed resin layer 133 may be lowered, so that there may be a problem in productivity, and if it exceeds the above range, it may be difficult to implement the weight reduction of the wallpaper, and the volume of the air layer As is reduced, the effect of improving insulation properties may be insignificant, and thus the average true density may be within the above range.
본 발명에서 평균 진밀도란 상기 글라스 버블의 샘플의 질량을 기체 비중병에 의해 측정된 그 질량의 글라스 버블의 진부피(true volume)로 나눔으로써 얻어진 몫(quotient)을 의미한다.In the present invention, the average true density means a quotient obtained by dividing the mass of the sample of the glass bubble by the true volume of the glass bubble of the mass measured by the gas pycnometer.
구체적으로, 평균 진밀도는 ASTM D2840-69("중공 미소구체의 평균 입자 진밀도"(Average True Particle Density of Hollow Microspheres))에 의거하여 비중병(구체적 일례로, 마이크로메리틱스로부터의 AccuPcy 1330)을 이용하여 측정할 수 있다.Specifically, the average true density is based on ASTM D2840-69 ("Average True Particle Density of Hollow Microspheres"). It can be measured using.
또한, 상기 글라스 버블은 입자크기(particle size)가 25-105㎛, 또는 30-95㎛일 수 있다. 상기 범위 미만인 경우 글라스 버블의 평균 진밀도가 커져 벽지 경량화 및 단열성 개선 효과가 미미할 수 있고, 상기 범위를 초과하는 경우 상기 기재층(131) 상부에 코팅작업이 원활하지 않고 발포 후 제1발포수지층(133)의 표면상태가 좋지 않을 수 있어 상기 범위 내의 입자크기를 가질 수 있다. In addition, the glass bubble may have a particle size of 25-105 μm, or 30-95 μm. If it is less than the above range, the average true density of the glass bubbles increases, so that the effect of reducing the weight of the wallpaper and improving the insulation properties may be insignificant. If it exceeds the above range, the coating operation on the top of the base layer 131 is not smooth and the first foaming resin layer after foaming The surface condition of (133) may be poor, and thus may have a particle size within the above range.
본 발명에서 입자크기란 상기 글라스 버블이 구 형상인 경우는 지름의 평균을 의미하고, 구 형상 외의 다른 형상인 경우는 장축과 단축으로 구분 시 장축의 평균 길이를 의미하는 것일 수 있다. In the present invention, when the glass bubble has a spherical shape, the particle size may mean an average of diameter, and when the glass bubble has a shape other than the spherical shape, it may mean an average length of the long axis when divided into a long axis and a short axis.
상기 글라스 버블의 입자 크기는 입도분석기(S3500, Microtrac社)를 이용하여 측정할 수 있다.The particle size of the glass bubble can be measured using a particle size analyzer (S3500, Microtrac).
또한, 상기 글라스 버블은 20-23℃에서 열전도율이 0.06-0.10W/m·K 또는 0.065-0.08W/m·K일 수 있다. 상기 글라스 버블이 상기 범위 내의 열전도율을 가짐으로써 충진제로 탄산칼슘을 사용한 종래의 벽지에 비해 열전도율이 낮아 단열성을 더욱 개선할 수 있다.In addition, the glass bubble may have a thermal conductivity of 0.06-0.10W/m·K or 0.065-0.08W/m·K at 20-23°C. Since the glass bubble has a thermal conductivity within the above range, the thermal conductivity is lower than that of a conventional wallpaper using calcium carbonate as a filler, so that the thermal insulation properties can be further improved.
상기 글라스 버블은 상기 열가소성 수지 100중량부에 대해 5-20중량부, 또는 7-17중량부로 포함될 수 있다. 상기 범위 미만인 경우 단열벽지(130)의 단열성 개선 효과가 미미할 수 있고 아울러, 물성이 저하되며 입체효과를 향상시키기 위해 기재층(131) 상부에 제1발포수지층(133) 형성용 조성물의 코팅량을 증가시킬 수 없어 입체효과가 제한적이고, 상기 범위를 초과할 경우 제1발포수지층(133)의 발포 시, 발포 셀 형성이 저하됨에 따라 발포배율이 낮으며 표면상태가 매끄럽지 않고, 가격 대비 경량화 및 단열성 개선 효과가 미미할 수 있으며, 제1발포수지층(133) 형성용 조성물의 점도가 상승하여 필요로 하는 가소제 함량이 증가하여 바람직하지 못하므로 상기 범위 내로 포함될 수 있다.The glass bubble may be included in an amount of 5-20 parts by weight, or 7-17 parts by weight based on 100 parts by weight of the thermoplastic resin. If it is less than the above range, the effect of improving the thermal insulation of the thermal insulation wallpaper 130 may be insignificant, and the amount of coating of the composition for forming the first foaming resin layer 133 on the top of the base layer 131 in order to improve the three-dimensional effect and lower physical properties. When the first foaming resin layer 133 is foamed when it exceeds the above range, the foaming ratio is low and the surface condition is not smooth, as the foaming cell formation is lowered, and the weight is reduced compared to the price. And the heat insulation improvement effect may be insignificant, and the viscosity of the composition for forming the first foaming resin layer 133 increases, and thus the required plasticizer content increases, which is not preferable, and thus may be included within the above range.
또한, 상기 제1발포수지층(133)은 가소제 및 발포제 중 선택된 1종 이상을 더 포함할 수 있다. In addition, the first foaming resin layer 133 may further include at least one selected from a plasticizer and a foaming agent.
상기 가소제는 상기 열가소성 수지를 가소화하여 기재층(131) 상부에 제1발포수지층(133)의 형성용 조성물의 코팅이 용이하도록 하기 위해 포함되는 것으로, 테레프탈레이트계 가소제, 벤조에이트계 가소제, 시트레이트계 가소제 및 포스페이트계 가소제로 이루어진 군으로부터 선택되는 1종 이상일 수 있다.The plasticizer is included to plasticize the thermoplastic resin to facilitate the coating of the composition for forming the first foaming resin layer 133 on the base layer 131, and a terephthalate-based plasticizer, a benzoate-based plasticizer, It may be one or more selected from the group consisting of citrate-based plasticizers and phosphate-based plasticizers.
상기 가소제는 상기 열가소성 수지 100중량부에 대해 50-90중량부 또는 60-80중량부로 포함될 수 있다. 상기 범위 미만일 경우 제1발포수지층(133) 형성용 조성물의 점도가 높아 기재층(131) 상부에 형성 시 코팅성이 저하될 수 있고, 상기 범위를 초과할 경우 코팅 후의 겔링(gelling)성이 저하됨과 아울러, 가소제 이행(Migration)으로 인해 물성이 저하될 수 있어 상기 함량 범위 내로 포함할 수 있다.The plasticizer may be included in an amount of 50 to 90 parts by weight or 60 to 80 parts by weight based on 100 parts by weight of the thermoplastic resin. If it is less than the above range, the viscosity of the composition for forming the first foaming resin layer 133 is high, so that when it is formed on the base layer 131, the coating property may be deteriorated. In addition to being lowered, physical properties may be lowered due to plasticizer migration, and thus may be included within the above content range.
상기 발포제는 상기 열가소성 수지 100중량부에 대해 2-10중량부로 포함될 수 있다. The foaming agent may be included in an amount of 2-10 parts by weight based on 100 parts by weight of the thermoplastic resin.
상기 발포제로 화학 발포제를 단독 사용하거나 또는 화학 발포제와 캡슐 발포제를 혼합하여 사용할 수 있다.As the foaming agent, a chemical foaming agent may be used alone, or a chemical foaming agent and a capsule foaming agent may be mixed and used.
상기 화학 발포제의 종류는 상기 열가소성 수지에 사용될 수 있는 것이면 그 종류를 한정하지 않으나 본 발명의 구체적 일 예로, 아조디카본아마이드(azodicarbonamide), p,p'-옥시비스벤젠설포닐하이드라지드(p,p'-oxybisbenzene sulfonyl hydrazide), p-톨루엔설포닐하이드라지드(p-toluene sulfonyl hydrazide) 및 벤젠설포닐하이드라지드(benzene sulfonyl hydarazide)로 이루어진 군으로부터 선택된 1종 이상일 수 있다.The type of the chemical blowing agent is not limited as long as it can be used for the thermoplastic resin, but specific examples of the present invention include azodicarbonamide, p,p'-oxybisbenzenesulfonylhydrazide (p ,p'-oxybisbenzene sulfonyl hydrazide), p-toluene sulfonyl hydrazide, and benzene sulfonyl hydrazide.
상기 화학 발포제는 160-180℃에서 분해되어 200-300ml/gr의 가스량을 생성하는 것을 사용할 수 있다. 상기 온도 범위 미만일 경우 발포성형 단계 전에서 미리 발포되어 충분한 발포성형 효과를 구현하기 어려울 수 있고 상기 온도 범위를 초과할 경우 발포제가 분해되지 않아 많은 공기층을 확보하지 못해 벽지의 단열성 개선 효과가 미미할 수 있어 상기 온도 범위 내에서 분해되는 화학 발포제를 사용할 수 있다.The chemical blowing agent may be decomposed at 160-180°C to generate a gas amount of 200-300ml/gr. If the temperature is less than the above temperature range, it may be difficult to achieve sufficient foaming and molding effects due to pre-foaming before the foaming step, and if the temperature exceeds the above temperature range, the foaming agent is not decomposed and thus many air layers cannot be secured, so the effect of improving the insulation properties of the wallpaper may be insignificant. It is possible to use a chemical blowing agent that decomposes within the above temperature range.
발포제로서, 상기 화학 발포제를 단독으로 사용할 경우 상기 화학 발포제는 상기 열가소성 수지 100중량부에 대해 2-8중량부 또는 3-6중량부로 포함될 수 있다. 상기 범위 미만일 경우 발포 효과가 미미할 수 있어 경량성 및 단열성 개선 효과가 미미함과 아울러, 쿠션감이 저하될 수 있고, 상기 범위를 초과할 경우 과도한 발포로 인해 벽지의 강도 등의 물성이 저하될 수 있어 상기 범위 내로 포함될 수 있다.As a foaming agent, when the chemical foaming agent is used alone, the chemical foaming agent may be included in an amount of 2-8 parts by weight or 3-6 parts by weight based on 100 parts by weight of the thermoplastic resin. If it is less than the above range, the foaming effect may be insignificant, so the effect of improving light weight and heat insulation may be insignificant, and the cushioning feeling may be deteriorated.If it exceeds the above range, physical properties such as the strength of the wallpaper may be deteriorated due to excessive foaming. It may be included within the above range.
또한, 상기 캡슐 발포제는 수지 재질의 캡슐 레이어와, 상기 캡슐 레이어에 내포되며 상기 캡슐 레이어에 사용되는 수지의 연화점 이하에서 비등점을 갖는 팽창제를 포함하는 열팽창성 마이크로 캡슐일 수 있다. In addition, the capsule foaming agent may be a thermally expandable microcapsule including a capsule layer made of a resin material and an expanding agent that is contained in the capsule layer and has a boiling point below the softening point of the resin used in the capsule layer.
보다 구체적으로, 상기 캡슐 발포제는 적정 온도의 열이 가해지면, 상기 캡슐 레이어의 연화가 시작됨과 동시에 캡슐 레이어에 내포되는 팽창제가 기화되면서 내압이 높아지며 화학 발포제의 발포로 형성된 발포 셀의 내, 외부에 발포될 수 있다. 캡슐 발포제는 화학 발포제와 달리 캡슐 레이어를 포함하는 것이어서 외부의 압력이나 충격에 대해서 저항성을 가져 발포 셀의 손상, 파손을 방지할 수 있다. More specifically, when heat of an appropriate temperature is applied to the capsule foaming agent, the capsule layer starts to soften and the expanding agent contained in the capsule layer evaporates, thereby increasing the internal pressure, and inside and outside the foaming cell formed by the foaming of the chemical foaming agent. Can be foamed. Unlike the chemical foaming agent, the capsule foaming agent contains a capsule layer, so it has resistance to external pressure or impact, and thus can prevent damage and breakage of the foaming cell.
상기 캡슐 레이어는 아크릴로니트릴 공중합체, 염화비닐리덴 공중합체, 폴리에틸렌, 폴리프로필렌 및 폴리스티렌으로 이루어진 군에서 선택되는 1종 이상의 폴리염화비닐 수지일 수 있으나 반드시 이로 제한되는 것은 아니다. The capsule layer may be one or more polyvinyl chloride resins selected from the group consisting of acrylonitrile copolymer, vinylidene chloride copolymer, polyethylene, polypropylene, and polystyrene, but is not limited thereto.
상기 팽창제는 프로판, 프로필렌, 부텐, 부탄, 이소부탄, 이소펜탄, 네오펜탄, 노르말펜탄, 노르말헥산, 이소헥산, 헵탄, 옥탄, 노난 및 데칸으로 이루어진 군에서 선택되는 1종 이상의 액상의 탄화수소일 수 있다. The expanding agent may be one or more liquid hydrocarbons selected from the group consisting of propane, propylene, butene, butane, isobutane, isopentane, neopentane, normal pentane, normal hexane, isohexane, heptane, octane, nonane and decane. have.
상기 캡슐 발포제는 발포 전 평균 입경이 10-40㎛, 또는 15-35㎛일 수 있다. 상기 범위 미만일 경우 충분한 발포효과를 얻지 못할 수 있어 많은 공기층을 확보하지 못해 단열벽지(130)의 단열성 개선 효과가 미미할 수 있고, 상기 범위를 초과하면 형성되는 발포 셀의 크기가 커져 벽지로서 요구되는 강도가 저하될 수 있어 상기 범위 내의 평균 입경을 가질 수 있다.The capsule foaming agent may have an average particle diameter before foaming of 10-40 μm, or 15-35 μm. If it is less than the above range, sufficient foaming effect may not be obtained, and thus a large number of air layers may not be secured, so that the effect of improving the heat insulating property of the insulating wallpaper 130 may be insignificant. If it exceeds the above range, the size of the foamed cell formed increases, and the strength required as a wallpaper May be lowered to have an average particle diameter within the above range.
상기 입경은 주사전자현미경(Scanning electron microscope,SEM)을 이용하여 측정할 수 있다.The particle diameter can be measured using a scanning electron microscope (SEM).
또한, 상기 캡슐 발포제는 열팽창 개시온도가 일례로, 110-140℃, 또는 120-130℃일 수 있다. 상기 범위 미만일 경우 조기 발포로 인해 캡슐 발포제가 터져 벽지의 단열성 개선 효과가 미미할 수 있고, 상기 범위를 초과할 경우 충분한 발포를 얻지 못할 수 있어 상기 범위 내의 열팽창 개시온도를 가질 수 있다.In addition, the capsule foaming agent may have a thermal expansion initiation temperature, for example, 110-140°C, or 120-130°C. If it is less than the above range, the capsule foaming agent may burst due to early foaming, so that the effect of improving the insulation properties of the wallpaper may be insignificant, and if it exceeds the above range, sufficient foaming may not be obtained, and thus the thermal expansion start temperature within the above range may be obtained.
상기 열팽창 개시온도란 열 기계 분석 장치(Thermomechanical Analysis, 이하 'TMA')로 상기 캡슐 발포제를 가열했을 때, 높이 방향의 변위가 플러스로 변했을 때의 온도를 의미한다.When in the thermal expansion-starting temperature is thermal mechanical analysis device (Thermomechanical Analysis, hereinafter 'TMA') when heating the capsule blowing agent, it means the temperature at which the displacement in the vertical direction byeonhaeteul positively.
또한, 상기 캡슐 발포제는 열팽창 최대온도가 150-180℃, 또는 160-170℃일 수 있다. 상기 범위 미만일 경우 캡슐 레이어가 터질 수 있어 발포 셀의 손상이 있을 수 있고, 상기 범위를 초과할 경우 발포성형 단계 시 충분한 발포가 일어나지 않을 수 있어 상기 범위 내의 열팽창 최대온도를 가질 수 있다.In addition, the capsule foaming agent may have a maximum thermal expansion temperature of 150-180°C, or 160-170°C. If it is less than the above range, the capsule layer may burst and the foaming cell may be damaged, and if it exceeds the above range, sufficient foaming may not occur during the foam molding step, and thus the maximum thermal expansion temperature may be within the above range.
상기 열팽창 최대온도는 열 기계 분석 장치(TMA)로 상기 캡슐 발포제를 상온으로부터 가열하면서 그 직경을 측정했을 때에, 캡슐 발포제가 최대 변위량이 되었을 때의 온도를 의미한다.The maximum thermal expansion temperature refers to the temperature at which the capsule foaming agent reaches the maximum displacement amount when the diameter of the capsule foaming agent is measured while heating the capsule foaming agent from room temperature with a thermomechanical analysis device (TMA).
또한, 발포제로서, 상기 화학 발포제 및 캡슐 발포제를 혼합하여 사용할 경우, 상기 열가소성 수지 100중량부에 대하여, 화학 발포제는 1-5중량부 또는 2-4중량부, 캡슐 발포제는 1-5중량부, 또는 2-4중량부로 포함될 수 있다.In addition, as a foaming agent, when using a mixture of the chemical foaming agent and the capsule foaming agent, based on 100 parts by weight of the thermoplastic resin, the chemical foaming agent is 1-5 parts by weight or 2-4 parts by weight, the capsule blowing agent is 1-5 parts by weight, Or it may be included in 2-4 parts by weight.
상기 제1발포수지층(133) 형성용 조성물은 선택적으로, 무기안료 및 유기안료로 이루어진 군으로부터 선택되는 1종 이상의 안료, 열안정제 및 점도조절제를 더 포함할 수 있으며, 이들의 종류 및 함량은 특별히 제한하지 않는다.The composition for forming the first foaming resin layer 133 may optionally further include one or more pigments selected from the group consisting of inorganic pigments and organic pigments, thermal stabilizers and viscosity modifiers, and the types and contents thereof There is no particular limitation.
또한, 상기 제1발포수지층(133) 형성용 조성물은 필요에 따라 공지의 첨가제를 더 포함할 수 있고, 이의 종류와 함량은 벽지의 물성에 영향을 미치지 않는 한에서는 한정하지 않는다.In addition, the composition for forming the first foaming resin layer 133 may further include a known additive as necessary, and the type and content thereof are not limited as long as they do not affect the physical properties of the wallpaper.
상기 제1발포수지층(133)의 발포배율은 230-380% 또는 250-300%일 수 있으며, 상기 범위 미만일 경우 공기층을 확보하지 못해 경량성 및 단열성 개선 효과가 미미함과 아울러, 쿠션감이 저하될 수 있고, 상기 범위를 초과할 경우 벽지의 내구성이 저하됨과 아울러, 발포 셀의 크기가 너무 커서 벽지의 이음매가 벌어지는 등 시공성이 저하될 수 있어 상기 범위 내의 발포배율을 가질 수 있다.The foaming ratio of the first foaming resin layer 133 may be 230-380% or 250-300%, and if it is less than the above range, the air layer cannot be secured, so that the effect of improving light weight and insulation is insignificant, and the cushioning feeling is It may be degraded, and if it exceeds the above range, the durability of the wallpaper may be deteriorated, and the workability may be deteriorated, such as a joint of the wallpaper being opened due to the size of the foam cell being too large.
상기 제1발포수지층(133) 형성용 조성물은 점도가 20-25℃에서 2000-4000cps 또는 2500-3500cps일 수 있다. 상기 범위 미만일 경우 점도가 너무 낮아 기재층(131) 상부에 코팅 시 원하는 두께 형성이 어려울 수 있고 건조 후 크랙 발생율이 높을 수 있으며, 상기 범위를 초과할 경우 점도가 너무 높아 코팅성이 저하될 수 있어 상기 범위 내의 점도를 가질 수 있다.The composition for forming the first foaming resin layer 133 may have a viscosity of 2000-4000 cps or 2500-3500 cps at 20-25°C. If the viscosity is less than the above range, the viscosity may be too low to form a desired thickness when coating on the top of the substrate layer 131, and the crack generation rate may be high after drying.If the viscosity is exceeded, the viscosity may be too high and the coating property may be reduced. It may have a viscosity within the above range.
상기 제1발포수지층(133)의 발포 전의 두께는 일례로 0.1-0.7mm 또는 0.2-0.5mm일 수 있다. 상기 범위 미만일 경우 단열성 개선 효과가 미미할 수 있고, 상기 범위를 초과할 경우 벽지의 중량이 무거울 수 있고, 아울러 벽지가 접히는 등의 시공에 어려움이 있을 수 있어 상기 범위 내의 두께를 가질 수 있다.The thickness of the first foaming resin layer 133 before foaming may be 0.1-0.7mm or 0.2-0.5mm, for example. If it is less than the above range, the effect of improving thermal insulation may be insignificant, and if it exceeds the above range, the weight of the wallpaper may be heavy, and there may be difficulties in construction such as folding the wallpaper, and thus the thickness within the above range may be obtained.
본 발명의 단열벽지(130)는 상기 예시한 층들 이외에도 추가적인 층을 더 포함할 수 있다.The insulating wallpaper 130 of the present invention may further include an additional layer in addition to the above-described layers.
일 예로, 본 발명의 단열벽지(130)에 다양한 무늬 및/또는 색상을 부여하여 미관 효과를 개선하기 위하여 상기 제1발포수지층(133) 상부에 부분적으로 도포되는 제2발포수지층(135)을 더 포함할 수 있으며, 별도의 엠보 공정 없이 상기 제1발포수지층(133) 및 제2발포수지층(135)의 발포성형 공정만으로 엠보 무늬를 형성할 수 있어 종래 엠보롤로 가압 시 PVC 발포층의 눌림에 따라 발생하는 단열성능 저하와 같은 문제를 해결할 수 있다. For example, the second foaming resin layer 135 partially applied on the first foaming resin layer 133 to improve the aesthetic effect by giving various patterns and/or colors to the insulating wallpaper 130 of the present invention. It may further include, and the first foaming resin layer 133 and the second foaming resin layer 135 without a separate embossing process can form an embossed pattern only by the foam molding process, when pressing with a conventional embossing roll PVC foam layer Problems such as deterioration of insulation performance caused by pressing of can be solved.
상기 제2발포수지층(135)은 열가소성 수지 100중량부에 대해 캡슐 발포제 1-7중량부를 포함할 수 있다.The second foaming resin layer 135 may include 1 to 7 parts by weight of a capsule foaming agent based on 100 parts by weight of the thermoplastic resin.
구체적으로, 상기 제2발포수지층(135)은 상기 열가소성 수지 100중량부에 대해 캡슐 발포제 1-7중량부를 포함하는 졸(sol) 상태의 제2발포수지층(135) 형성용 조성물을 이용하여 형성된 것일 수 있다.Specifically, the second foaming resin layer 135 is made of a composition for forming the second foaming resin layer 135 in a sol state including 1 to 7 parts by weight of a capsule foaming agent based on 100 parts by weight of the thermoplastic resin. It may be formed.
상기 열가소성 수지 및 캡슐 발포제의 종류는 위에서 서술한 제1발포수지층(133)에 포함되는 열가소성 수지 및 캡슐 발포제와 동일하므로 중복된 기재는 생략하도록 한다.Since the types of the thermoplastic resin and the capsule foaming agent are the same as the thermoplastic resin and the capsule foaming agent included in the first foaming resin layer 133 described above, duplicate descriptions will be omitted.
상기 캡슐 발포제는 상기 열가소성 수지 100중량부에 대해 1-7중량부 또는 2-5중량부로 포함될 수 있다. 상기 범위 미만일 경우 벽지의 접힘자국 방지 효과가 미미하고, 상기 범위를 초과한 경우 과도한 발포(퍼짐)로 인해 의도한 엠보 효과 구현이 어려우므로 상기 함량 범위 내의 캡슐 발포제를 포함할 수 있다.The capsule foaming agent may be included in an amount of 1-7 parts by weight or 2-5 parts by weight based on 100 parts by weight of the thermoplastic resin. If it is less than the above range, the effect of preventing the fold marks of the wallpaper is insignificant, and if it exceeds the above range, it is difficult to implement the intended embossing effect due to excessive foaming (spreading), and thus a capsule foaming agent within the above content range may be included.
또한, 상기 제2발포수지층(135)은 충전제, 화학 발포제 및 가소제 중 선택된 1종 이상을 더 포함할 수 있다. In addition, the second foaming resin layer 135 may further include at least one selected from a filler, a chemical foaming agent, and a plasticizer.
상기 충전제는 글라스 버블 및 탄산칼슘 중 선택되는 1종 이상일 수 있다.The filler may be at least one selected from glass bubbles and calcium carbonate.
상기 충전제로 글라스 버블 단독으로 사용하는 경우, 상기 글라스 버블은 상기 열가소성 수지 100중량부에 대해 1-20중량부 또는 5-17중량부로 포함될 수 있다. 상기 범위를 초과할 경우 제2발포수지층(135)의 발포배율이 낮고 표면상태가 매끄럽지 않을 수 있고, 가격 대비 경량화 및 단열성 개선 효과가 미미할 수 있으며, 제2발포수지층(135) 형성용 조성물의 점도가 상승하여 필요로 하는 가소제 함량이 증가하여 바람직하지 못할 수 있어 상기 범위 내로 포함될 수 있다.When using the glass bubble alone as the filler, the glass bubble may be included in an amount of 1-20 parts by weight or 5-17 parts by weight based on 100 parts by weight of the thermoplastic resin. If it exceeds the above range, the foaming ratio of the second foaming resin layer 135 may be low and the surface condition may not be smooth, and the effect of reducing weight and insulating properties may be insignificant compared to the price, and the composition for forming the second foaming resin layer 135 The viscosity of the plasticizer may increase and thus the required plasticizer content may be increased, which may be undesirable, and thus may be included within the above range.
상기 글라스 버블의 특성은 위에서 서술한 제1발포수지층(133)에 포함되는 글라스 버블과 동일하므로 중복된 기재는 생략하도록 한다.Since the characteristics of the glass bubbles are the same as those of the glass bubbles included in the first foaming resin layer 133 described above, overlapping descriptions will be omitted.
상기 충전제로 상기 탄산칼슘을 단독으로 사용하는 경우, 상기 탄산칼슘은 상기 열가소성 수지 100중량부에 대해 50-90중량부 또는 60-80중량부일 수 있다. 상기 범위 미만일 경우 제2발포수지층(135) 형성용 조성물의 원재료 가격이 상승할 수 있고 치수안정성이 저하될 수 있으며, 상기 범위를 초과할 경우 단열벽지(130)의 경량화 및 단열성 개선 효과가 미미할 수 있어 상기 범위 내로 포함될 수 있다.When the calcium carbonate is used alone as the filler, the calcium carbonate may be 50-90 parts by weight or 60-80 parts by weight based on 100 parts by weight of the thermoplastic resin. If it is less than the above range, the cost of raw materials of the composition for forming the second foaming resin layer 135 may increase and dimensional stability may decrease, and if it exceeds the above range, the effect of reducing the weight of the insulation wallpaper 130 and improving the insulation properties will be insignificant. It can be included within the above range.
상기 충전제로 글라스 버블 및 탄산칼슘을 혼합하여 사용할 경우 상기 글라스 버블은 상기 열가소성 수지 100중량부에 대해 5-15중량부 또는 7-13중량부일 수 있고, 상기 탄산칼슘은 열가소성 수지 100중량부에 대해 50-90중량부 또는 60-80중량부일 수 있다.When using a mixture of glass bubbles and calcium carbonate as the filler, the glass bubbles may be 5-15 parts by weight or 7-13 parts by weight based on 100 parts by weight of the thermoplastic resin, and the calcium carbonate is based on 100 parts by weight of the thermoplastic resin. It may be 50-90 parts by weight or 60-80 parts by weight.
상기 화학 발포제는 상기 열가소성 수지 100중량부에 대해 1-6중량부 또는 2-5중량부로 포함될 수 있다. 상기 범위 미만일 경우 발포가 충분하지 않아 엠보 효과의 구현이 미미할 수 있고, 상기 범위를 초과한 경우 과도한 발포(퍼짐)로 인해 의도한 엠보 효과 구현이 어려울 수 있어 상기 함량 범위 내의 화학 발포제를 포함할 수 있다.The chemical foaming agent may be included in an amount of 1-6 parts by weight or 2-5 parts by weight based on 100 parts by weight of the thermoplastic resin. If it is less than the above range, the embossing effect may be insignificant due to insufficient foaming, and if it exceeds the above range, it may be difficult to implement the intended embossing effect due to excessive foaming (spreading), and a chemical foaming agent within the above content range may be included. have.
상기 가소제는 상기 열가소성 수지 100중량부에 대해 50-90중량부 또는 60-80중량부로 포함될 수 있다. 상기 범위 미만일 경우 제2발포수지층(135) 형성용 조성물의 점도가 높아 코팅성이 저하될 수 있고, 상기 범위를 초과할 경우 제2발포수지층(135) 형성용 조성물의 점도가 낮아 제1발포수지층(133) 상부에 도포 시 원하는 두께 형성이 어려울 수 있어 상기 함량 범위 내로 포함할 수 있다.The plasticizer may be included in an amount of 50 to 90 parts by weight or 60 to 80 parts by weight based on 100 parts by weight of the thermoplastic resin. If it is less than the above range, the viscosity of the composition for forming the second foaming resin layer 135 may be high, so that the coating property may be lowered, and if it exceeds the above range, the viscosity of the composition for forming the second foaming resin layer 135 is low. When it is applied on the foamed resin layer 133, it may be difficult to form a desired thickness, and thus may be included within the above content range.
상기 화학 발포제 및 가소제의 종류는 위에서 서술한 제1발포수지층(133)에 포함되는 화학 발포제 및 가소제와 동일하므로 중복된 기재는 생략하도록 한다.Since the types of the chemical foaming agent and the plasticizer are the same as the chemical foaming agent and the plasticizer included in the first foaming resin layer 133 described above, overlapping descriptions will be omitted.
상기 제2발포수지층(135)은 선택적으로 무기안료 및 유기안료로 이루어진 군으로부터 선택되는 1종 이상의 안료, 열안정제 및 점도조절제를 더 포함할 수 있으며, 이들의 종류 및 함량은 특별히 제한하지 않는다.The second foaming resin layer 135 may optionally further include one or more pigments selected from the group consisting of inorganic pigments and organic pigments, heat stabilizers, and viscosity modifiers, and the types and contents thereof are not particularly limited. .
또한, 상기 제2발포수지층(135) 형성용 조성물은 필요에 따라 공지의 첨가제를 더 포함할 수 있고, 이의 종류와 함량은 벽지의 물성에 영향을 미치지 않는 한에서는 한정하지 않는다.In addition, the composition for forming the second foaming resin layer 135 may further include known additives as necessary, and the type and content thereof are not limited as long as they do not affect the physical properties of the wallpaper.
상기 제2발포수지층(135)의 발포배율은 100-220% 또는 100-200%일 수 있으며, 상기 범위 미만일 경우 벽지에 입체 효과를 부여하기 어려울 수 있고, 상기 범위를 초과할 경우 과도한 발포(발포 셀 형상이 옆으로 퍼짐)로 이 역시 입체 효과가 저하될 수 있으므로 상기 범위 내의 발포배율을 가질 수 있다.The foaming ratio of the second foaming resin layer 135 may be 100-220% or 100-200%, and if it is less than the above range, it may be difficult to impart a three-dimensional effect to the wallpaper, and if it exceeds the above range, excessive foaming ( The foamed cell shape spreads sideways), so that the three-dimensional effect may be deteriorated, and thus the foaming ratio may be within the above range.
또한, 상기 제2발포수지층(135) 형성용 조성물은 점도가 20-25℃에서 2000-4000cps 또는 2500-3500cps일 수 있다. 상기 범위 미만일 경우 점도가 너무 낮아 제1발포수지층(133) 상부에 도포 시 원하는 두께 형성이 어려울 수 있고 건조 후 크랙 발생율이 높을 수 있으며, 상기 범위를 초과할 경우 점도가 너무 높아 코팅성이 저하될 수 있어 상기 범위 내의 점도를 가질 수 있다.In addition, the composition for forming the second foaming resin layer 135 may have a viscosity of 2000-4000 cps or 2500-3500 cps at 20-25°C. If it is less than the above range, the viscosity is too low, so it may be difficult to form the desired thickness when applied to the top of the first foaming resin layer 133, and the crack generation rate after drying may be high.If it exceeds the above range, the viscosity is too high and the coating property decreases. Can have a viscosity within the above range.
상기 제2발포수지층(135)의 발포 전의 두께는 일례로 0.05-0.4mm 또는 0.1-0.3mm일 수 있다. 상기 범위 미만일 경우 발포되더라도 엠보 효과의 구현이 미미할 수 있고, 상기 범위를 초과할 경우 벽지의 중량이 무거울 수 있고, 아울러 제2발포수지층(135)의 과도한 발포(퍼짐)으로 인해 벽지의 접힘성 방지 효과가 저하될 수 있어 상기 범위 내의 두께를 가질 수 있다.The thickness of the second foaming resin layer 135 before foaming may be, for example, 0.05-0.4mm or 0.1-0.3mm. If it is less than the above range, the embossing effect may be insignificant even if it is foamed, and if it exceeds the above range, the weight of the wallpaper may be heavy, and also the foldability of the wallpaper due to excessive foaming (spreading) of the second foaming resin layer 135 The prevention effect may be reduced, and thus may have a thickness within the above range.
또한, 본 발명의 단열벽지(130)의 단열성을 더욱 향상시키기 위하여 상기 기재층(131) 상부에 부분 도포되는 발포 수지층(미도시)를 더 포함할 수 있다.In addition, a foamed resin layer (not shown) partially coated on the base layer 131 may be further included in order to further improve the thermal insulation properties of the insulating wallpaper 130 of the present invention.
상기 발포 수지층(미도시)은 선택적으로 상기 기재층(131) 상부에 코팅된 후 발포되어 공기층을 형성함으로써 벽지에 단열성을 부여하는 역할을 하는 것으로, 상기 기재층(131) 상부에 부분적으로 형성되어 일정한 패턴을 가질 수 있다.The foamed resin layer (not shown) is selectively coated on the base layer 131 and then foamed to form an air layer, thereby providing heat insulation to the wallpaper, and is partially formed on the base layer 131 And can have a certain pattern.
상기 패턴은 원형 패턴, 또는 다각형 패턴일 수 있고, 구체적 일 실시예로 직경이 0.3-0.7mm인 원이 0.3-0.7mm의 간격으로 형성된 원형 패턴일 수 있으며 이 경우 고배율 발포에 의한 벽지의 시공성 저하를 방지할 수 있다.The pattern may be a circular pattern or a polygonal pattern, and in a specific embodiment, a circle having a diameter of 0.3-0.7mm may be a circular pattern formed at intervals of 0.3-0.7mm, and in this case, the workability of the wallpaper is reduced due to high magnification foaming. Can be prevented.
더욱 구체적으로 상기 원형 패턴은 직경이 0.4-0.6mm인 원이 0.4-0.6mm의 간격으로 형성된 패턴일 수 있다.More specifically, the circular pattern may be a pattern in which circles having a diameter of 0.4-0.6mm are formed at intervals of 0.4-0.6mm.
본 발명에서 상기 원은 구 형상일 수 있으며, 이 경우 직경은 지름을 의미하며, 상기 원이 구 형상 외의 다른 형상인 경우 직경은 장축과 단축으로 구분시 장축의 길이를 의미하는 것일 수 있다. In the present invention, the circle may have a spherical shape, and in this case, the diameter means a diameter, and if the circle has a shape other than a spherical shape, the diameter may mean the length of the long axis when divided into a long axis and a short axis.
상기 원의 직경이 상기 범위보다 크고, 간격이 상기 범위보다 좁으면 상기 원(즉, 발포 셀)이 합쳐짐으로 인해 기재층(131)으로부터 제1발포수지층(133) 및 제2발포수지층(135)이 들뜨는 현상이 발생해 벽지가 찢어지거나 벽지 시공 시 기재층(131)의 수축, 팽창 차이에 의한 이음매가 벌어지는 등 시공성이 저하될 수 있고, 상기 원의 직경이 상기 범위보다 작고, 간격이 상기 범위보다 넓으면 벽지에 단열성을 부여할 수 없을 수 있어 상기 범위 내의 원형 직경 및 간격을 가질 수 있다.When the diameter of the circle is larger than the range and the interval is narrower than the range, the circle (i.e., foaming cell) is combined, and thus the first foaming resin layer 133 and the second foaming resin layer from the base layer 131 are combined. The workability may be deteriorated, such as tearing of the wallpaper due to the excitation of 135, or the opening of the joint due to the difference in contraction and expansion of the base layer 131 during wallpaper construction, and the diameter of the circle is smaller than the above range, and the gap If it is wider than the above range, it may not be possible to impart thermal insulation properties to the wallpaper, and thus may have a circular diameter and spacing within the above range.
본 발명에서 상기 원형 패턴의 구체적 일 실시예로 직경이 0.5mm인 원이 0.5mm의 간격으로 형성된 패턴일 수 있으며, 이 경우 벽지의 단열성 및 시공성이 우수할 수 있다.In the present invention, as a specific embodiment of the circular pattern, a circle having a diameter of 0.5 mm may be a pattern formed at intervals of 0.5 mm, and in this case, the insulation and workability of the wallpaper may be excellent.
한편, 상기 발포 수지층은 열가소성 수지 100중량부에 대해 발포제 4-20중량부 및 가소제 50-100중량부를 포함하는 졸(sol) 상태의 발포 수지층 형성용 조성물을 이용하여 형성된 것일 수 있다.Meanwhile, the foamed resin layer may be formed using a composition for forming a foamed resin layer in a sol state including 4-20 parts by weight of a foaming agent and 50-100 parts by weight of a plasticizer based on 100 parts by weight of a thermoplastic resin.
상기 열가소성 수지는 위에서 서술한 상기 제1발포수지층(133)에 포함되는 열가소성 수지와 동일하므로 중복된 기재는 생략하도록 한다.Since the thermoplastic resin is the same as the thermoplastic resin included in the first foaming resin layer 133 described above, a duplicate description will be omitted.
상기 발포제는 화학 발포제를 단독 사용하거나 또는 화학발포제와 캡슐 발포제를 혼합하여 사용할 수 있다.The foaming agent may be used alone or in combination with a chemical foaming agent and a capsule foaming agent.
상기 화학 발포제 및 캡슐 발포제는 위에서 서술한 상기 제1발포수지층(133)에 포함되는 화학 발포제 및 캡슐 발포제와 동일하므로 중복된 기재는 생략하도록 한다.Since the chemical foaming agent and the capsule foaming agent are the same as the chemical foaming agent and the capsule foaming agent included in the first foaming resin layer 133 described above, overlapping descriptions will be omitted.
발포제로서, 상기 화학 발포제를 단독으로 사용할 경우, 상기 화학 발포제는 열가소성 수지 100중량부에 대해 4-15중량부 또는 5-10중량부로 사용될 수 있다. 상기 범위 미만인 경우 발포 배율이 저하되어 많은 공기층을 확보하지 못해 단열벽지(130)의 단열성 개선 효과가 미미할 수 있고, 상기 범위를 초과할 경우 고배율 발포로 인해 벽지 시공 시, 단열벽지(130)가 벽면으로부터 들뜨거나 단열벽지 간 이음매가 표시가 나는 등 시공성이 저하될 수 있어 상기 범위 내로 사용할 수 있다.As the foaming agent, when the chemical foaming agent is used alone, the chemical foaming agent may be used in an amount of 4-15 parts by weight or 5-10 parts by weight based on 100 parts by weight of the thermoplastic resin. If it is less than the above range, the foaming ratio is lowered, so that many air layers cannot be secured, so that the effect of improving the insulation properties of the insulating wallpaper 130 may be insignificant. It can be used within the above range because workability may be deteriorated, such as a display of a joint between the insulating wallpaper and the like.
발포제로서, 상기 화학 발포제 및 캡슐 발포제를 혼합하여 사용할 경우, 상기 열가소성 수지 100중량부에 대하여, 화학 발포제는 3.5-10중량부 또는 4-8중량부, 캡슐 발포제는 0.5-5중량부, 또는 1-4중량부로 포함될 수 있다. 캡슐 발포제가 상기 범위 미만으로 포함될 경우 단열성 개선 효과가 미미할 수 있고 상기 범위를 초과하여 포함할 경우 발포 수지층의 표면 굴곡이 심하여 상기 발포 수지층 상부에 제1발포수지층(133)의 형성이 어려울 수 있어 상기 함량 범위 내의 캡슐 발포제를 포함할 수 있다.As a foaming agent, when using a mixture of the chemical foaming agent and the capsule foaming agent, with respect to 100 parts by weight of the thermoplastic resin, the chemical foaming agent is 3.5-10 parts by weight or 4-8 parts by weight, the capsule blowing agent 0.5-5 parts by weight, or 1 It may be included in -4 parts by weight. If the capsule foaming agent is included below the above range, the effect of improving thermal insulation may be insignificant, and If the content exceeds the above range, it may be difficult to form the first foaming resin layer 133 on the foamed resin layer due to severe surface curvature of the foamed resin layer, and thus a capsule foaming agent within the above content range may be included.
상기 발포 수지층의 발포 배율은 300%이상, 300-600% 또는 400-500%일 수 있다. 상기 범위 미만일 경우 많은 공기층을 확보하지 못해 벽지의 단열성 개선 효과가 미미할 수 있고, 상기 범위를 초과할 경우 고배율 발포로 인해 벽지의 시공성이 저하될 수 있어 상기 범위 내의 발포배율을 가질 수 있다.The foaming ratio of the foamed resin layer may be 300% or more, 300-600%, or 400-500%. If it is less than the above range, the effect of improving the insulation properties of the wallpaper may be insignificant because many air layers cannot be secured, and if it exceeds the above range, the workability of the wallpaper may be deteriorated due to high-magnification foaming, so that the expansion ratio within the above range may be achieved.
상기 가소제는 위에서 서술한 상기 제1발포수지층(133)에 포함되는 가소제와 동일하므로 중복된 기재는 생략하도록 한다.Since the plasticizer is the same as the plasticizer included in the first foaming resin layer 133 described above, overlapping descriptions will be omitted.
상기 가소제는 상기 열가소성 수지 100중량부에 대해 50-100중량부 또는 50-80중량부로 포함될 수 있다. 상기 범위 미만일 경우 발포 수지층 형성용 조성물의 점도가 높아 기재층(131) 상부에 형성 시 코팅성이 저하될 수 있고, 상기 범위를 초과할 경우 코팅 후의 겔링(gelling)성이 저하됨과 아울러, 가소제 이행(Migration)으로 인해 물성이 저하될 수 있어 상기 함량 범위 내로 포함할 수 있다.The plasticizer may be included in an amount of 50 to 100 parts by weight or 50 to 80 parts by weight based on 100 parts by weight of the thermoplastic resin. If it is less than the above range, the viscosity of the composition for forming the foamed resin layer is high, so that when it is formed on the base layer 131, the coating property may decrease. If it exceeds the above range, the gelling property after coating decreases, as well as a plasticizer. Physical properties may be deteriorated due to migration, and thus may be included within the above content range.
상기 발포 수지층 형성용 조성물은 점도가 20-25℃에서 900-3000cps 또는 1000-2000cps일 수 있다. 상기 범위 미만일 경우 점도가 너무 낮아 기재층(131) 상부에 부분적으로 도포하기 어려울 수 있으며, 상기 범위를 초과할 경우 점도가 너무 높아 코팅성이 저하될 수 있어 상기 범위 내의 점도를 가질 수 있다.The composition for forming the foamed resin layer may have a viscosity of 900-3000cps or 1000-2000cps at 20-25°C. If the viscosity is less than the above range, the viscosity may be too low to be partially applied on the top of the substrate layer 131, and if the viscosity is exceeded, the viscosity may be too high and the coating property may be deteriorated, and thus the viscosity may be within the above range.
상기 발포 수지층의 발포 전의 두께는 일례로 0.05-0.5mm 또는 0.1-0.3mm일 수 있다. 상기 범위 미만일 경우 많은 공기층을 확보하지 못해 단열성 개선 효과가 미미할 수 있고, 상기 범위를 초과할 경우 단열벽지(130)의 중량이 무거울 수 있고, 아울러 벽지가 접히는 등의 시공에 어려움이 있을 수 있어 상기 범위 내의 두께를 가질 수 있다.The thickness of the foamed resin layer before foaming may be, for example, 0.05-0.5mm or 0.1-0.3mm. If it is less than the above range, the effect of improving insulation properties may be insignificant because many air layers cannot be secured.If the above range is exceeded, the weight of the insulation wallpaper 130 may be heavy, and there may be difficulties in construction such as folding the wallpaper. It can have a thickness within a range.
또한, 본 발명의 단열 벽지는 상기 제2발포수지층(135) 상부에 오염방지를 위해 표면처리제를 도포하여 형성된 표면처리층(미도시)를 더 포함할 수 있으나, 이에 한정하지 않는다.In addition, the heat insulating wallpaper of the present invention may further include a surface treatment layer (not shown) formed by applying a surface treatment agent to prevent contamination on the second foaming resin layer 135, but is not limited thereto.
상기 표면처리제는 아크릴 수지 또는 PLA(Polylactic acid) 수지를 물에 분산시켜 제조한 에멀젼 상태의 것이나 아크릴 수지 또는 PLA 수지를 물, 알코올계 또는 MEK(Methyl Ethyl Ketone) 등의 용제에 녹인 것을 이용할 수 있다.The surface treatment agent may be an emulsion prepared by dispersing an acrylic resin or a polylactic acid (PLA) resin in water, or an acrylic resin or a PLA resin dissolved in a solvent such as water, alcohol or MEK (Methyl Ethyl Ketone). .
본 발명의 단열벽지(130)는 평량이 250-455g/m2 또는 300-450g/m2일 수 있으며, 상기 범위 미만일 경우 충분한 공기층을 확보하지 못해 경량성 및 단열성 개선 효과가 미미할 수 있고, 상기 범위를 초과할 경우 벽지의 평량이 무거워 시공성이 저하될 수 있으므로 상기 범위 내의 평량을 가질 수 있다.The insulating wallpaper 130 of the present invention may have a basis weight of 250-455g/m 2 or 300-450g/m 2 , and if it is less than the above range, a sufficient air layer may not be secured, and thus the effect of improving light weight and heat insulation may be insignificant. If it exceeds the range, the basis weight of the wallpaper may be heavy and thus workability may be deteriorated, and thus the basis weight may be within the above range.
또한, 본 발명의 단열벽지(130)는 발포 후 벽지의 두께가 0.7-2.3mm, 바람직하게는 0.8-2.0mm, 보다 바람직하게는 0.8-1.5mm일 수 있으며, 상기 범위 내에서 단열성 및 쿠션감이 우수한 효과가 있다.In addition, the thermal insulation wallpaper 130 of the present invention may have a thickness of 0.7-2.3mm, preferably 0.8-2.0mm, more preferably 0.8-1.5mm, after foaming, and heat insulation and cushioning within the above range. This has an excellent effect.
본 발명의 벽지 시스템(100)은 단열 초배지(110); 및 기재층(131), 제1발포수지층(133)을 포함하는 단열벽지(130)를 포함하여, 열 관류율이 낮고 단열성이 우수하고, 쿠션감을 가져 벽면의 요철을 보완해 줄 수 있는 벽지 시스템(100)를 제공할 수 있는 효과가 있다.The wallpaper system 100 of the present invention includes a thermal insulation paper substrate 110; And a wallpaper system that includes a base layer 131 and an insulating wallpaper 130 including the first foaming resin layer 133, which has a low heat permeation rate, excellent insulation, and has a cushioning feeling to compensate for irregularities on the wall surface. There is an effect that can provide (100).
이하, 단열 초배지 및 단열벽지의 제조방법에 대하여 상세하게 설명하도록 한다.Hereinafter, a detailed description will be given of a method of manufacturing an insulating superpaper and an insulating wallpaper.
<단열 초배지 제조><Manufacture of insulating super medium>
상기 단열 초배지 제조는 융점이 상이한 2종의 섬유가 혼합된 혼합섬유를 카딩(carding)공정 및 니들펀칭 공정 후, 용융 압착하는 단계를 포함할 수 있다.The manufacturing of the insulating super medium may include a step of melt-pressing a mixed fiber in which two kinds of fibers having different melting points are mixed after a carding process and a needle punching process.
상기 혼합섬유는 고융점 폴리에스테르 섬유 및 저융점 폴리에스테르 섬유일 수 있으며, 구체적으로 고융점 폴리에스테르 섬유 40-60중량%, 저융점 폴리에스테르 섬유 60-40중량%로 혼합된 혼합섬유일 수 있다.The mixed fiber may be a high melting point polyester fiber and a low melting point polyester fiber, and specifically, may be a mixed fiber mixed with 40 to 60% by weight of high melting point polyester fiber and 60 to 40% by weight of low melting point polyester fiber. .
상기 고융점 폴리에스테르 섬유 및 저융점 폴리에스테르 섬유는 위에서 서술한 바와 동일한 바, 중복된 기재는 생략하도록 한다. The high-melting-point polyester fiber and the low-melting-point polyester fiber are the same as described above, and overlapping descriptions are omitted.
본 발명에서 니들펀칭이란 표면에 돌기가 있는 스틸(steel)제의 바늘(needle)을 이용하여, 상기 혼합된 고융점 폴리에스테르 섬유 및 저융점 폴리에스테르 섬유에 상하로 왕복 운동시키면, 니들 표면의 돌기에 의해 상기 섬유들이 교락되는 것을 말한다.In the present invention, needle punching refers to the protrusion of the needle surface by reciprocating up and down the mixed high-melting-point polyester fiber and low-melting-point polyester fiber by using a needle made of steel with projections on the surface. It means that the fibers are entangled by.
상기 니들펀칭 공정 이후 수행되는 용융 압착 단계는 상기 니들펀칭 된 부직포를 용융 압착하는 단계일 수 있으며, 상기 용융 압착 단계를 통해 저융점 폴리에스테르 섬유가 용융될 수 있으며 단열 초배지 일면을 매끄럽고 평평한 면으로 형성할 수 있다.The melt-pressing step performed after the needle punching process may be a step of melt-pressing the needle-punched nonwoven fabric, and the low-melting-point polyester fiber may be melted through the melt-pressing step, and one side of the insulating super media is formed into a smooth and flat side. can do.
구체적으로, 상기 용융 압착 단계를 통해 상기 니들펀칭 된 부직포의 저융점 폴리에스테르가 용융되어 고융점 폴리에스테르 섬유의 유동을 방지함으로써 상기 단열 초배지의 형태 안정성 및 강도를 향상시킬 수 있으며, 또한 상기 저융점 폴리에스테르 섬유가 용융된 단열 초배지 일면을 매끄럽고 평평한 면으로 형성하여 단열벽지 시공 시, 단열벽지와의 접착력이 향상되고, 단열 초배지 표면의 요철 형상을 보완할 수 있다.Specifically, the low melting point polyester of the needle-punched nonwoven fabric is melted through the melt-pressing step to prevent the flow of high melting point polyester fibers, thereby improving the shape stability and strength of the insulating super media, and the low melting point By forming one side of the thermal insulation super-paper in which the polyester fiber is melted into a smooth and flat surface, when the thermal insulation wallpaper is constructed, the adhesion to the thermal insulation wallpaper is improved, and the uneven shape of the surface of the thermal insulation super media can be supplemented.
또한, 선택적으로 상기 단열 초배지는 일면 뿐만 아니라 양면이 매끄럽고 평평한 면으로 형성될 수 있다.In addition, optionally, the heat-insulating superbadge may be formed not only on one side but also on both sides of a smooth and flat surface.
상기 용융 압착 단계는 150-200℃에서 수행될 수 있으며, 용융 압착 단계의 온도가 150℃ 미만일 경우 상기 저융점 폴리에스테르가 용융되지 않아 고융점 폴리에스테르 섬유의 유동이 방지되지 않으므로 단열 초배지의 형태 안정성 및 강도가 저하되고 시공이 용이하지 않으며 단열벽지를 지지하지 못할 수 있고, 200℃ 초과일 경우 저융점 폴리에스테르 섬유와 고융점 폴리에스테르 섬유가 함께 용융될 수 있으므로 상기 범위 내의 온도에서 수행될 수 있다.The melt-pressing step may be performed at 150-200°C, and when the temperature of the melt-pressing step is less than 150°C, the low-melting-point polyester is not melted and the flow of the high-melting-point polyester fiber is not prevented. And the strength is lowered, construction is not easy, and the insulation wallpaper may not be supported. If it exceeds 200°C, the low-melting-point polyester fiber and the high-melting-point polyester fiber may be melted together, so it can be performed at a temperature within the above range. .
상기 용융 압착 단계는 일 예로 히팅 드럼을 사용할 수 있으나, 이에 한정하지 않는다.The melt-pressing step may use a heating drum as an example, but is not limited thereto.
단열 초배지에 대한 특성은 위에서 서술한 바와 동일하므로 중복된 기재를 생략하도록 한다.Since the characteristics of the thermal insulation paper are the same as described above, duplicate descriptions are omitted.
<단열벽지 제조><Manufacture of insulation wallpaper>
이하, 단열벽지의 각 층의 제조단계에 대하여 설명하도록 한다.Hereinafter, the manufacturing steps of each layer of the insulating wallpaper will be described.
(1) 기재층 준비단계(1) Base layer preparation step
상기 기재층 준비단계에서 상기 기재층에 대한 특성은 위에서 서술한 기재층과 동일하므로 중복된 기재는 생략하도록 한다.Since the properties of the base layer in the base layer preparation step are the same as those of the base layer described above, duplicate descriptions are omitted.
(2) 제1발포수지층 형성용 조성물 도포 단계(2) Step of applying the composition for forming the first foaming resin layer
상기 제1발포수지층 형성용 조성물 도포 단계는 위에서 서술한 제1발포수지층 형성용 조성물을 상기 기재층의 상부에 전면 도포한 후에 겔링(gelling)한 것일 수 있다.In the step of applying the composition for forming the first foaming resin layer, the composition for forming the first foaming resin layer described above may be applied to the top of the base layer and then gelled.
상기 제1발포수지층 형성용 조성물은 위에서 서술한 제1발포수지층의 각 조성을 믹서에 첨가한 후 상온에서 혼련하여 제조한 것일 수 있다.The composition for forming the first foaming resin layer may be prepared by adding each composition of the first foaming resin layer described above to a mixer and then kneading at room temperature.
상기 제1발포수지층 형성용 조성물을 상기 기재층의 상부에 전면 도포하는 방식은 공지된 코팅 방식일 수 있고, 본 발명의 구체적 일 실시예로 바(bar) 코팅 또는 나이프(knife) 코팅일 수 있으나 이에 한정되는 것은 아니다.The method of fully applying the composition for forming the first foaming resin layer on the top of the base layer may be a known coating method, and as a specific embodiment of the present invention, a bar coating or a knife coating may be used. However, it is not limited thereto.
상기 겔링(gelling)은 150-180℃에서 10-20초 동안 행해진 것일 수 있다.The gelling may be performed at 150-180°C for 10-20 seconds.
(3) 발포 단계(3) foaming step
상기 발포 단계는 제1발포수지층 형성용 조성물을 발포시키는 단계로, 180-220℃ 또는 190-210℃에서 30-70초 또는 40-60초의 조건 하에서 발포되는 것일 수 있다. 상기 온도 및 시간 범위 미만일 경우 발포가 미미하여 벽지의 경량성, 쿠션감 및 단열성 개선 효과가 미미함과 아울러 충분한 엠보 효과를 구현할 수 없고, 상기 온도 및 시간 범위를 초과할 경우 발포 셀이 과도하게 커져 내구성이 저하됨과 아울러 벽지 시공에 어려움이 있으므로 상기 온도 및 시간 범위에서 발포시킬 수 있다.The foaming step is a step of foaming the composition for forming the first foaming resin layer, and may be foamed at 180-220°C or 190-210°C for 30-70 seconds or 40-60 seconds. If it is less than the above temperature and time range, foaming is insignificant, so the effect of improving the light weight, cushioning, and insulation of the wallpaper is insignificant, and sufficient embossing effect cannot be implemented.If the temperature and time range is exceeded, the foaming cell becomes excessively large and durable. In addition to this decrease, it is difficult to construct wallpaper, so it can be foamed in the above temperature and time range.
또한, 본 발명은 선택적으로, 상기 제1발포수지층 형성용 조성물 도포 단계이후 제2발포수지층 형성용 조성물 도포 단계를 더 포함할 수 있다.In addition, the present invention may optionally further include a step of applying the composition for forming the second foaming resin layer after the step of applying the composition for forming the first foaming resin layer.
상기 제2발포수지층 형성용 조성물 도포 단계는 위에서 서술한 제2발포수지층 형성용 조성물을 상기 제1발포수지층의 상부에 부분적으로 도포한 후에 겔링(gelling)한 것일 수 있다.In the step of applying the composition for forming the second foaming resin layer, the composition for forming the second foaming resin layer described above may be partially coated on the top of the first foaming resin layer, followed by gelling.
상기 제2발포수지층 형성용 조성물은 위에서 서술한 제2발포수지층의 각 조성을 믹서에 첨가한 후 상온에서 혼련하여 제조한 것일 수 있다.The composition for forming the second foaming resin layer may be prepared by adding each composition of the second foaming resin layer described above to a mixer and then kneading at room temperature.
상기 제2발포수지층 형성용 조성물을 상기 제1발포수지층의 상부에 부분적으로 도포하는 방식은 로터리 스크린 코팅 방식일 수 있다. A method of partially applying the composition for forming the second foaming resin layer on the first foaming resin layer may be a rotary screen coating method.
또한, 상기 제2발포수지층 형성용 조성물을 상기 제1발포수지층의 상부에 부분적으로 도포 시, 패턴 구현을 위해 여러 번에 나누어 도포할 수 있고 구체적 일 예로 3-5번으로 나누어 도포할 수 있다.In addition, when the composition for forming the second foaming resin layer is partially applied on the top of the first foaming resin layer, it may be applied several times to implement a pattern, and as a specific example, it may be applied by dividing it into 3-5 times. have.
상기 겔링(gelling)은 150-180℃에서 10-20초 동안 행해진 것일 수 있다.The gelling may be performed at 150-180°C for 10-20 seconds.
또한, 본 발명은 선택적으로, 상기 기재층 준비 단계 이후 발포 수지층 형성용 조성물 도포 단계를 더 포함할 수 있다.In addition, the present invention may optionally further include a step of applying the composition for forming a foamed resin layer after the base layer preparation step.
상기 발포 수지층 형성용 조성물 도포 단계는 위에서 서술한 발포 수지층 형성용 조성물을 상기 기재층 상부에 부분적으로 도포한 후에 겔링(gelling)하는 단계일 수 있다.The step of applying the composition for forming the foamed resin layer may be a step of partially applying the composition for forming the foamed resin layer described above on the upper portion of the base layer, followed by gelling.
상기 발포 수지층 형성용 조성물은 위에서 서술한 발포 수지층의 각 조성을 믹서에 첨가한 후 상온에서 혼련하여 제조한 것일 수 있다.The composition for forming the foamed resin layer may be prepared by adding each composition of the foamed resin layer described above to a mixer and then kneading at room temperature.
상기 발포 수지층 형성용 조성물을 부분적으로 도포하는 방식은 로터리 스크린 코팅 방식일 수 있으며, 더욱 구체적으로 상기 제 1수지층 형성용 조성물은 원형 패턴으로 도포될 수 있다.The method of partially applying the composition for forming the foamed resin layer may be a rotary screen coating method, and more specifically, the composition for forming the first resin layer may be applied in a circular pattern.
상기 원형 패턴은 위에서 서술한 바와 동일하므로 중복된 기재는 생략하도록 한다.Since the circular pattern is the same as described above, overlapping descriptions will be omitted.
상기 겔링(gelling)은 150-180℃에서 10-20초 동안 행해진 것일 수 있다.The gelling may be performed at 150-180°C for 10-20 seconds.
종래 벽지는 입체 및 미적 효과를 부여하기 위해 엠보롤로 가압하여 엠보 무늬를 형성하는데 이러한 엠보 공정 시, PVC 발포층 내 발포 셀에 압력이 가해져 단열층 역할을 하는 공기층이 파괴되어 벽지의 단열 성능을 저하시키는 문제점이 있었다. Conventional wallpaper is pressurized with an embossing roll to give a three-dimensional and aesthetic effect to form an embossed pattern.In this embossing process, pressure is applied to the foam cells in the PVC foam layer, destroying the air layer serving as the heat insulating layer, reducing the heat insulation performance of the wallpaper. There was a problem.
그러나, 본 발명의 단열벽지는 상기한 바와 같이 제2발포수지층이 제1발포수지층 상부에 로터리 스크린 방식으로 부분적으로 형성되고, 발포됨으로써 입체 효과를 구현할 수 있어, 발포단계 이후 종래와 같이 입체 및 미적 효과를 부여하기 위해 엠보롤로 가압하는 가압 공정(엠보 공정)을 포함하지 않을 수 있다. However, as described above, the heat insulating wallpaper of the present invention can realize a three-dimensional effect by partially forming a second foaming resin layer on top of the first foaming resin layer in a rotary screen method and being foamed, so that it is three-dimensional as in the prior art after the foaming step. And a pressing process (embossing process) of pressing with an emboss roll to impart an aesthetic effect.
이로 인해 본 발명의 단열벽지는 제조 시 공정의 단순화가 가능해지고, 제조된 벽지의 단열 성능이 저하되지 않는 효과가 있다.For this reason, it is possible to simplify the process during manufacture of the thermal insulation wallpaper of the present invention, and there is an effect that the thermal insulation performance of the manufactured wallpaper does not deteriorate.
이하, 상기 단열 초배지 및 단열벽지를 포함하는 벽지 시스템 시공방법에 대하여 설명하도록 한다.Hereinafter, a method of constructing a wallpaper system including the insulating super-paper and the insulating wallpaper will be described.
< 벽지 시공방법><wallpaper construction method>
상기 벽지 시공방법은 단열 초배지 및 단열벽지를 준비하는 단계; 상기 단열 초배지 및 단열벽지를 시공 벽면의 크기에 맞게 재단하는 단계; 상기 시공 벽면을 평탄화 하는 평탄 작업 단계; 상기 평탄화 된 벽면 상에 접착제를 도포하여 상기 단열 초배지를 부착하는 단열 초배지 시공단계; 상기 단열벽지의 하부에 접착제를 도포하여 말음 숙성하는 말음 숙성단계; 상기 말음 숙성된 단열벽지를 상기 단열 초배지 상에 교차시공하는 단열벽지 시공단계; 및 상기 시공된 단열 초배지 및 단열벽지를 건조시키는 단계를 포함한다.The wallpaper construction method comprises the steps of: preparing a thermal insulation paper and a thermal insulation wallpaper; Cutting the insulation super-paper and the insulation wallpaper according to the size of the construction wall; A flattening operation step of flattening the construction wall surface; Insulating super-paper construction step of applying an adhesive on the flattened wall surface to attach the insulated super-badge; A roll aging step of aging the roll by applying an adhesive to the lower part of the insulating wallpaper; Insulation wallpaper construction step of cross-installing the heat-insulating wallpaper on the heat-insulating material; And it includes the step of drying the constructed insulating paper and the insulating wallpaper.
상기 단열 초배지 및 단열벽지를 준비하는 단계; 및 상기 단열 초배지 및 단열벽지를 시공 벽면의 크기에 맞게 재단하는 단계;와 평탄 작업 단계;는 독립적으로 수행될 수 있으며, 상기 평탄 작업 단계 이후 단열 초배지 및 단열벽지를 준비하는 단계 및 상기 단열 초배지 및 단열벽지를 시공 벽면의 크기에 맞게 재단하는 단계를 수행하여도 무방하다.Preparing the heat-insulating paper and heat-insulating wallpaper; And cutting the insulating paper and the insulating wallpaper according to the size of the construction wall; and the flattening operation step; can be performed independently, and the step of preparing the insulating paper and the insulating wallpaper after the flattening operation step, and the insulating paper and It is okay to perform the step of cutting the insulation wallpaper according to the size of the construction wall.
상기 단열 초배지 시공 단계에서 상기 벽면과 단열 초배지를 접착하는 접착제는 본 발명의 기술분야에서 공지에 기술된 벽면 및 초배지의 접착에 이용되는 접착제를 이용할 수 있으며 일 예로 비닐아세테이트계 수지를 포함하는 친환경 수성 접착제를 이용할 수 있다.The adhesive for adhering the wall surface and the insulating super medium in the step of constructing the insulating super medium may be an adhesive used for bonding the wall surface and the super medium known in the technical field of the present invention, and as an example, an eco-friendly aqueous solution including vinyl acetate-based resin. Adhesives can be used.
보다 구체적으로, 상기 친환경 수성 접착제는 물 100중량부에 대해 비닐아세테이트계 수지 40-50 중량부를 혼합한 것일 수 있다.More specifically, the eco-friendly water-based adhesive may be a mixture of 40-50 parts by weight of a vinyl acetate-based resin with respect to 100 parts by weight of water.
상기 비닐아세테이트계 수지는 비닐아세테이트 단량체 또는 상기 비닐아세테이트 단량체와 모노머의 공중합체일 수 있다.The vinyl acetate-based resin may be a vinyl acetate monomer or a copolymer of the vinyl acetate monomer and the monomer.
상기 비닐아세테이트 단량체와 공중합 가능한 모노머는 아크릴산 에스테르(ester acrylate), 아크릴산(acrylic acid, CH2=CHCOOH), 에틸렌, 스티렌, 아크릴레이트, 또는 메타크릴레이트 등일 수 있으며, 특히 아크릴산 에스테르 또는 아크릴산을 사용하는 것이 바람직하다. 구체적으로, 상기 아크릴산 에스테르는 부틸 아크릴레이트 모노머(butyl acrylate monomer), 에틸 아크릴레이트 모노머(ethyl acrylate monomer), 에틸헥실 아크릴레이트 모노머(ethylhexyl acrylate monomer), 또는 메틸 아크릴레이트 모노머(methyl acrylate monomer) 등을 사용할 수 있다.The monomer copolymerizable with the vinyl acetate monomer may be an acrylic acid ester (ester acrylate), acrylic acid (acrylic acid, CH2 = CHCOOH), ethylene, styrene, acrylate, or methacrylate, and in particular, acrylic acid ester or acrylic acid is used. desirable. Specifically, the acrylic acid ester includes butyl acrylate monomer, ethyl acrylate monomer, ethylhexyl acrylate monomer, or methyl acrylate monomer. Can be used.
상기 모노머는 비닐아세테이트계 단량체 100중량부에 대하여 0.1-20 중량부 포함될 수 있으며, 상기 범위 내에서 우수한 접착력을 구현할 수 있다.The monomer may be included in an amount of 0.1 to 20 parts by weight based on 100 parts by weight of the vinyl acetate-based monomer, and excellent adhesion may be implemented within the above range.
또한, 상기 친환경 수성 접착제는 필요에 따라 통상의 기능성 충진제, 분산제, 소포제, 안정제, 레벨링제, 점착부여제, 또는 촉매 등의 첨가제를 추가로 포함할 수 있다.In addition, the eco-friendly water-based adhesive may further include additives such as a conventional functional filler, a dispersant, an antifoam, a stabilizer, a leveling agent, a tackifier, or a catalyst, if necessary.
상기 친환경 수성 접착제를 도포하는 방법은 특별히 한정하지 않으나, 일 예로, 접착제 접촉부 단부에 골이 형성되어 있는 헤라를 이용할 수 있다.The method of applying the eco-friendly water-based adhesive is not particularly limited, but as an example, a hera having a valley formed at the end of the adhesive contact portion may be used.
또한, 상기 단열 초배지는 용융 압착 단계를 통해 형성된 단열 초배지 표면의 매끄럽고 평평한 부분(즉, 단열 초배지의 일면)이 단열벽지가 시공되는 방향을 향하도록 시공될 수 있으며, 벽면에 따라 가로 또는 세로 방향으로 시공될 수 있다.In addition, the thermal insulation paper may be constructed so that a smooth and flat portion of the surface of the insulation paper formed through the melt-pressing step (i.e., one side of the insulation paper) faces the direction in which the insulation wallpaper is installed, and may be constructed in a horizontal or vertical direction depending on the wall surface. Can be constructed.
한편, 상기 단열 초배지를 시공하기 전에 벽면 가장자리에 실리콘 처리를 추가로 수행할 수 있다. 상기 실리콘 처리를 수행할 경우, 상기 단열 초배지를 보다 안정적이고 효과적으로 시공할 수 있는 효과가 있다.Meanwhile, silicon treatment may be additionally performed on the edge of the wall surface prior to the construction of the insulating super medium. When performing the silicon treatment, there is an effect that the insulating super medium can be more stably and effectively constructed.
이후, 상기 단열벽지의 기재층의 하부에 상기 도배용 풀을 도포한 후 말음 숙성을 할 수 있다.Thereafter, after applying the paper paste to the lower portion of the base layer of the insulating wallpaper, the roll may be aged.
상기 말음 숙성은 1-2시간 진행할 수 있으며, 상기 말음 숙성을 진행할 경우 풀이 단열벽지에 스며들어 부드럽게 늘어나 상기 단열벽지 시공 및 건조 후 벽지의 접힘이 방지되고 벽지가 수축하더라도 주름 또는 기포방울이 생기지 않는 효과가 있다.The rolled aging can be carried out for 1-2 hours, and when the rolled aging is performed, the paste soaks into the insulating wallpaper and stretches smoothly to prevent the wallpaper from folding after the construction and drying of the insulating wallpaper, and wrinkles or bubbles do not occur even if the wallpaper shrinks. There is.
종래의 일반 벽지 또는 실크 벽지는 풀칠된 면이 맞닿도록 맞접어 벽지간 적층하여 숙성을 하여, 특히 실크벽지지의 경우 벽지에 접힘자국이 남는 문제점이 있었다. 그러나, 본 발명의 단열멱지는 말아서 숙성되는 바, 단열벽지 표면에 접힘자국이 남는 것을 방지할 수 있다. Conventional wallpaper or silk wallpaper has a problem in that a folded surface remains on the wallpaper, especially in the case of a silk wall support, by folding and stacking the wallpaper so that the pasted surfaces come into contact with each other. However, since the heat insulating paper of the present invention is aged by rolling, it is possible to prevent the fold marks from remaining on the surface of the insulating wallpaper.
한편, 단열벽지의 양쪽 가장자리에 도포된 풀이 마르지 않도록 일부 접을 수 있다.On the other hand, it can be partially folded so that the glue applied to both edges of the insulating wallpaper does not dry out.
상기 도배용 풀은 당업계에서 이용되는 통상의 도배용 풀일 수 있으며, 일 예로, 전분(식용용 밀가루) : 물이 65-75: 35-25의 중량비로 혼합된 것일 수 있다.The paper paste may be a conventional paper paste used in the art, for example, starch (edible flour): water may be mixed in a weight ratio of 65-75: 35-25.
이때, 상기 단열 초배지 및 단열벽지 재단단계; 평탄 작업 단계; 및 단열 초배지를 시공하는 단계와 상기 말음 숙성 단계는 순서에 상관없이 독립적으로 진행될 수 있다.At this time, the insulation super-badge and the insulation wallpaper cutting step; Leveling work steps; And the step of constructing the insulating paper medium and the step of maturing the horses may be independently performed regardless of the order.
이어서, 상기 벽면 전면에 부착된 단열 초배지 상부에 말음 숙성된 단열벽지를 시공하고 건조시킴으로써 본 발명의 단열 초배지 및 단열벽지를 시공할 수 있다.Subsequently, by constructing and drying the rolled-aged insulating wallpaper on the top of the insulating paper attached to the front of the wall, it is possible to construct the insulating paper and the insulating wallpaper of the present invention.
구체적으로, 상기 단열벽지는 길이방향의 일부가 교차되도록 교차시공하고, 벽지의 무늬 및 이음매를 맞춰 시공하는 것이 외관이 좋을 수 있다.Specifically, the heat insulating wallpaper may have a good appearance by cross-construction so that part of the lengthwise direction crosses, and to match the pattern and seam of the wallpaper.
상기 단열벽지는 헤라 또는 롤러를 이용하여 시공하되, 시공 장비는 이에 한정하지 않는다.The insulating wallpaper is constructed using a spatula or a roller, but construction equipment is not limited thereto.
또한, 상기 단열벽지를 시공하기 전에 벽면 가장자리에 실리콘 처리를 추가로 수행할 수 있다.In addition, silicon treatment may be additionally performed on the edge of the wall surface prior to the construction of the insulating wallpaper.
상기 실리콘 처리를 할 경우 상기 단열벽지를 보다 안정적이고 효과적으로 시공할 수 있는 효과가 있다.When the silicon treatment is performed, there is an effect that the insulating wallpaper can be more stably and effectively constructed.
한편, 단열 초배지 및 단열벽지의 이음매가 벌어지는 현상을 방지하고 단열벽지의 수축률을 낮추기 위해 상기 단열 초배지 상부에 전면 초배지를 시공하는 단계를 더 포함할 수 있다.On the other hand, in order to prevent the phenomenon that the joint of the insulating paper and the insulating wallpaper from spreading out, and to lower the shrinkage rate of the insulating wallpaper, the step of constructing a front paper on the top of the insulating paper may be further included.
상기 전면 초배지의 구체적인 설명은 위에서 기재한 바, 중복된 기재는 생략하도록 한다.The detailed description of the front chobadge has been described above, and redundant descriptions will be omitted.
상기 전면 초배지는 벽면 가장자리에서 일정 간격을 띄우고 시공되는 것일 수 있으며, 일 예로 벽면 가장자리로부터 5-10cm 간격을 띄우고 시공될 수 있다.The front super-badge may be constructed with a predetermined distance from the edge of the wall, for example, it may be constructed with a distance of 5-10 cm from the edge of the wall.
상기 전면 초배지는 일정 간격을 띄우고 시공됨으로써 일정 간격 노출된 단열 초배지 일면과 단열벽지가 직접 접착될 수 있으며, 간격을 띄우지 않거나 5cm 미만의 간격을 띄우고 전면 초배지를 시공할 경우 일정 간격 노출된 단열 초배지 일면에 단열벽지가 직접 접착되는 면적이 매우 적어 단열벽지가 단열 초배지로부터 이탈하여 시공성이 저하될 수 있는 문제점이 있으므로 바람직하게 5-10cm 간격을 띄우고 시공될 수 있다.The front super-badge is installed at a certain interval, so that one side of the heat-insulating super-badge exposed at certain intervals and the heat-insulating wallpaper can be directly bonded. Since the area to which the insulating wallpaper is directly adhered to is very small, there is a problem that the insulating wallpaper may be separated from the insulating super media and thus workability may be deteriorated. Therefore, it may be constructed with an interval of 5-10cm.
상기 전면 초배지를 시공할 때 사용되는 접착제는 위에서 설명한 바, 중복된 기재는 생략하도록 한다.The adhesive used when constructing the front super badge is described above, and overlapping descriptions will be omitted.
또한, 상기 단열벽지의 수축률을 더욱 낯추고 단열벽지 사이의 이음매 벌어짐을 더욱 방지하기 위하여 상기 전면 초배지 상부에 운용지(미도시)를 더 포함할 수 있다. 상기 운용지는 본 발명의 기술분야에서 공지된 운용지를 이용할 수 있다.In addition, in order to make the shrinkage of the insulating wallpaper more unfamiliar and to further prevent the joints between the insulating wallpapers from spreading, a management paper (not shown) may be further included on the front super-badge. The operation site may be used well known in the technical field of the present invention.
상기 운용지를 시공할 때 사용되는 도배용 풀은 당업계에서 이용되는 통상의 도배용 풀일 수 있으며, 일 예로, 전분(식용용 밀가루) : 물이 50-60: 40-50의 중량비로 혼합된 것일 수 있다.The paper paste used when constructing the operation site may be a conventional paper paste used in the art, for example, starch (edible flour): water mixed in a weight ratio of 50-60: 40-50 I can.
상기 도배용 풀을 도포하는 방법은 위에서 서술한 바, 중복된 기재는 생략하도록 한다.The method of applying the wallpaper paste is described above, and overlapping descriptions will be omitted.
이상에서 설명한 바와 같은 본 발명은 상기한 실시예에 한정되지 아니하므로 청구범위에서 청구하는 본 발명의 요지를 벗어나지 않는 범위 내에서 변경 가능하며, 그와 같은 변경은 이하 청구범위 기재에 의하여 정의되는 본 발명의 보호범위 내에 있게 된다.The present invention as described above is not limited to the above-described embodiments, and thus can be changed within the scope not departing from the gist of the present invention claimed in the claims, and such changes are defined by the following claims. It is within the scope of the invention.
이하, 실시예 및 비교예에서 사용한 조성은 다음과 같다.Hereinafter, the compositions used in Examples and Comparative Examples are as follows.
- 고융점 폴리에스테르섬유: 융점이 250-280℃이고 두께가 6데니어인 폴리에스테르섬유를 사용하였다.-High melting point polyester fiber: Polyester fiber with a melting point of 250-280℃ and a thickness of 6 denier was used.
- 저융점 폴리에스테르섬유: 융점이 110-150℃이고 두께가 6데니어인 폴리에스테르섬유를 사용하였다. -Low melting point polyester fiber: Polyester fiber with a melting point of 110-150℃ and a thickness of 6 denier was used.
- 폴리염화비닐 수지: 제1발포수지층 및 제2발포수지층에 포함되는 폴리염화비닐 수지는 중합도가 900±50인 LG화학社의 PB900을 사용하였다.-Polyvinyl chloride resin: LG Chem's PB900 with a polymerization degree of 900±50 was used for the polyvinyl chloride resin included in the first and second foaming resin layers.
- 글라스 버블1): 평균 진밀도가 0.2g/cc, 입자크기가 55㎛, 21℃에서 열전도율이 0.07W/m·K인 3M社의 K20을 사용하였다.-Glass Bubble 1) : 3M's K20 with an average true density of 0.2g/cc, a particle size of 55㎛, and a thermal conductivity of 0.07W/m·K at 21℃ was used.
- 글라스 버블2): 평균 진밀도가 0.60g/cc, 입자크기가 30㎛, 21℃에서 열전도율이 0.20W/m·K인 3M社의 S60을 사용하였다.-Glass bubble 2) : 3M's S60 with an average true density of 0.60g/cc, a particle size of 30㎛, and a thermal conductivity of 0.20W/m·K at 21℃ was used.
- 글라스 버블3): 평균 진밀도가 0.125g/cc, 입자크기가 65㎛, 21℃에서 열전도율이 0.047W/m·K인 3M社의 K1을 사용하였다.-Glass Bubble 3) : 3M's K1 with an average true density of 0.125g/cc, a particle size of 65㎛, and a thermal conductivity of 0.047W/m·K at 21℃ was used.
- 가소제: LG화학의 디옥틸테레프탈레이트(DOTP)를 사용하였다.-Plasticizer: LG Chem's dioctyl terephthalate (DOTP) was used.
- 화학 발포제: 분해개시온도가 160-180℃, 가스량이 200-260ml/gr인 동진쎄미캠社의 DWPX03인 ADCA를 사용하였다.-Chemical foaming agent: ADCA, DWPX03 of Dongjin Semicam, with a decomposition initiation temperature of 160-180℃ and a gas volume of 200-260ml/gr was used.
- 캡슐 발포제: 발포 전 평균 입자크기가 18-24㎛, 열팽창 개시온도가 120-130℃, 열팽창 최대온도가 160-170℃인 동진쎄미캠社의 MS2001을 사용하였다.-Capsule foaming agent: MS2001 of Dongjin Semicam with an average particle size of 18-24㎛ before foaming, a thermal expansion initiation temperature of 120-130℃, and a maximum thermal expansion temperature of 160-170℃ was used.
- 접착제1): 비닐아세테이트계 수지가 함유된 수성 접착제인 주식회사 오공社의 205을 사용하였다.-Adhesive 1) : 205 of Wukong Co., Ltd., a water-based adhesive containing vinyl acetate-based resin, was used.
- 접착제2): 비닐아세테이트계 수지가 함유된 수성 접착제인 주식회사 오공社의 200을 사용하였다.-Adhesive 2) : 200 of Ogong Co., Ltd., a water-based adhesive containing vinyl acetate-based resin, was used.
<실시예 1><Example 1>
1. 단열 초배지 제조1. Manufacture of insulation paper
고융점 폴리에스테르 섬유 55중량% 및 저융점 폴리에스테르 섬유 45중량%가 혼합된 혼합섬유를 믹서기를 이용하여 혼합하고, 카딩기(carding machine)를 통해 상기 혼합섬유를 컨베이어 벨트 상부에 방사하여 웹(web)을 형성하였다.A blended fiber in which 55% by weight of high melting point polyester fiber and 45% by weight of low melting point polyester fiber are mixed is mixed using a blender, and the blended fiber is spun on the top of a conveyor belt through a carding machine, and the web ( web) was formed.
이어서, 표면에 돌기가 있는 스틸(steel)제의 바늘(needle)을 이용하여 니들펀칭 부직포를 제조한 후, 상기 부직포를 170℃의 히팅 드럼으로 용융 압착하여 저융점 폴리에스테르 섬유를 용융 시켜 고융점 폴리에스테르 섬유 사이가 접착되고 부직포 일면이 매끄럽고 평평한 면으로 형성된 평량이 245g/m2이고, 두께가 4.0mm인 실시예 1의 단열 초배지를 제조하였다.Subsequently, after manufacturing a needle punched nonwoven fabric using a steel needle with projections on the surface, the nonwoven fabric is melt-pressed with a heating drum at 170°C to melt the low-melting polyester fiber to have a high melting point. The heat insulating super medium of Example 1 was prepared in which the polyester fibers were bonded, and the nonwoven fabric had a smooth and flat surface with a basis weight of 245 g/m 2 and a thickness of 4.0 mm.
2. 단열벽지 제조2. Manufacture of insulation wallpaper
(1) 기재층 준비단계(1) Base layer preparation step
평량이 100g/m2, 두께가 0.15mm인 종이를 준비하였다.Paper having a basis weight of 100 g/m 2 and a thickness of 0.15 mm was prepared.
(2) 제1발포수지층 형성용 조성물 도포 단계(2) Step of applying the composition for forming the first foaming resin layer
폴리염화비닐 수지 100중량부에 대해 글라스 버블1) 10중량부, 가소제 70중량부, 화학 발포제 3.5중량부 및 열안정제 2중량부를 믹서에 넣고 상온에서 혼련하여 점도가 4000cps(25℃)의 졸 상태의 제1발포수지층 형성용 조성물을 제조하였다.Glass bubbles per 100 parts by weight of polyvinyl chloride resin 1) 10 parts by weight, 70 parts by weight of plasticizer, 3.5 parts by weight of chemical foaming agent, and 2 parts by weight of heat stabilizer are put in a mixer and kneaded at room temperature to have a viscosity of 4000 cps (25°C). A composition for forming the first foaming resin layer was prepared.
이어서, 상기 기재층 상부에 제1발포수지층 형성용 조성물을 0.3mm의 두께로 바(bar) 코팅방식으로 도포한 후 160℃에서 15초간 겔링하였다.Subsequently, the composition for forming the first foaming resin layer was applied on the top of the base layer to a thickness of 0.3 mm by a bar coating method and then gelled at 160° C. for 15 seconds.
(3) 발포 단계(3) foaming step
상기 아래에서부터 순차적으로 적층된 기재층; 제1발포수지층 형성용 조성물;을 200℃에서 50초간 발포하여 아래에서부터 순차적으로 기재층(두께: 0.15mm); 제1발포수지층(두께: 0.75mm)을 포함하는 평량이 350g/m2이고, 두께가 0.9mm의 실시예 1의 단열벽지를 제조하였다.A base layer sequentially stacked from below; A composition for forming a first foaming resin layer; the base layer (thickness: 0.15 mm) sequentially from the bottom by foaming at 200° C. for 50 seconds; The insulating wallpaper of Example 1 having a basis weight of 350 g/m 2 including the first foaming resin layer (thickness: 0.75 mm) and a thickness of 0.9 mm was prepared.
상기 제1발포수지층의 발포배율은 250%이었다.The expansion ratio of the first foaming resin layer was 250%.
3. 벽지 시공3. Wallpaper construction
상기에서 제조된 실시예 1의 단열 초배지 및 단열벽지를 시공 벽면의 크기에 맞게 재단한 후, 상기 시공 벽면을 석고처리 및 샌딩(sanding) 작업하여 평탄화 시키고, 단열 초배지의 테두리가 부착될 부분의 벽면에 접착제1)를 도포하고, 벽면의 가장자리에 통상의 실리콘을 도포한 후, 상기 재단된 단열 초배지의 일면(즉, 매끄럽고 평평한 면)이 단열벽지가 시공되는 방향으로 향하도록 벽면에 세로로 전면 부착하고, 상기 단열 초배지 상부에 접착제2)를 이용하여 30㎛의 전면 초배지를 시공하였다. 이때 상기 전면 초배지는 벽면에서 8cm 간격을 띄우고 시공하였다.After cutting the insulating paper and the insulating wallpaper of Example 1 prepared above according to the size of the construction wall, the construction wall was flattened by plastering and sanding the construction wall, and the wall surface of the portion to which the edge of the insulating paper was attached. Adhesive 1) is applied to the wall surface, and normal silicone is applied to the edge of the wall, and then vertically attached to the wall so that one side of the cut insulation paper (i.e., smooth and flat side) faces in the direction in which the insulation wallpaper is installed. And, on the top of the insulating paper, a front paper of 30 μm was constructed using an adhesive 2). At this time, the front panel was constructed with an interval of 8 cm from the wall.
이어서, 향후 시공되는 단열벽지의 이음매 사이에 전분 60중량% 및 물 40중량%가 혼합된 풀을 이용하여 운용지를 부착하였다.Subsequently, the operating paper was attached using a glue mixed with 60% by weight of starch and 40% by weight of water between the joints of the insulating wallpaper to be constructed in the future.
이어서, 전분 70중량% 및 물 30중량%를 혼합하여 벽지 도배용 풀을 제조하여 상기 재단된 단열벽지의 기재층의 하부에 도포한 후 말음 숙성을 위하여 1시간의 말음 숙성 시간을 거쳤다.Subsequently, 70% by weight of starch and 30% by weight of water were mixed to prepare a paste for wallpapering, applied to the lower part of the base layer of the cut insulating wallpaper, and then subjected to a roll aging time of 1 hour for roll aging.
이후, 상기 운용지 상에 상기 단열벽지를 부착하여 실시예 1의 벽지 시스템을 시공하였다.Thereafter, the wallpaper system of Example 1 was constructed by attaching the insulating wallpaper on the operating site.
<실시예 2> <Example 2>
1. 단열 초배지 제조1. Manufacture of insulation paper
실시예 1과 동일한 방법으로 평량이 245g/m2이고 두께가 4.0mm인 실시예 2의 단열 초배지를 제조하였다.In the same manner as in Example 1, a basis weight of 245 g/m 2 and a thickness of 4.0 mm were prepared in the insulating super medium of Example 2.
2. 단열벽지 제조2. Manufacture of insulation wallpaper
(2) 제1발포수지층 형성용 조성물 도포 단계 이후 제2발포수지층 형성용 조성물 도포 단계를 추가한 것을 제외하고는 실시예 1과 동일한 방법으로 평량이 380g/m2이고, 두께가 1.0mm인 실시예 2의 단열벽지를 제조하였다.(2) In the same manner as in Example 1, except that the step of applying the composition for forming the second foaming resin layer was added after the step of applying the composition for forming the first foaming resin layer, the basis weight was 380 g/m 2 and the thickness was 1.0 mm. The insulating wallpaper of Example 2 was prepared.
(제2발포수지층 형성용 조성물 도포 단계)(Step of applying the composition for forming the second foaming resin layer)
폴리염화비닐 수지 100중량부에 대해 탄산칼슘 70중량부, 가소제 70중량부, 화학 발포제 3중량부, 캡슐 발포제 3중량부 및 열안정제 2중량부를 믹서에 넣고 상온에서 혼련하여 점도가 4000cps(25℃)의 졸 상태의 제2발포수지층의 형성용 조성물을 제조하였다.With respect to 100 parts by weight of polyvinyl chloride resin, 70 parts by weight of calcium carbonate, 70 parts by weight of plasticizer, 3 parts by weight of chemical foaming agent, 3 parts by weight of capsule foaming agent, and 2 parts by weight of heat stabilizer are put into a mixer and kneaded at room temperature to obtain a viscosity of 4000 cps (25°C). ) To prepare a composition for forming the second foaming resin layer in a sol state.
이어서, 상기 겔링된 제1발포수지층 형성용 조성물 상부에 제2발포수지층 형성용 조성물을 로터리 스크린 코팅 방식으로 0.1mm의 두께로 부분적으로 도포한 후 160℃에서 15초간 겔링하였다.Subsequently, the composition for forming a second foaming resin layer was partially coated on the gelled composition for forming a first foaming resin layer to a thickness of 0.1 mm by a rotary screen coating method, followed by gelling at 160° C. for 15 seconds.
이어서, 발포 후, 제2발포수지층의 두께는 0.2mm였고, 발포배율은 200% 이었다.Subsequently, after foaming, the thickness of the second foaming resin layer was 0.2 mm, and the foaming magnification was 200%.
평량이 380g/m2이고, 두께가 1.0mm인 실시예 2의 단열벽지를 제조하였다.The insulation wallpaper of Example 2 having a basis weight of 380 g/m 2 and a thickness of 1.0 mm was prepared.
3. 벽지 시스템 시공3. Wallpaper system construction
실시예 1과 동일한 방법으로 실시예 2의 벽지 시스템을 시공하였다.The wallpaper system of Example 2 was constructed in the same manner as in Example 1.
<비교예 1> <Comparative Example 1>
1. 초배지 제조1. Manufacture of super medium
고융점 폴리에스테르를 연속필라멘트로 직접 방사하면서 임의로 배열하고 적층하여 단일 폴리에스테르 섬유 웹(web)을 형성하여 이를 170℃의 캘린더 롤을 이용하여 스펀본드 부직포를 제조함으로써 평량이 0.03g/m2이고, 두께가 0.03mm인 비교예 1의 초배지를 제조하였다.The high melting point polyester is directly spun into continuous filament, randomly arranged and laminated to form a single polyester fiber web, which is produced using a 170°C calender roll to produce a spunbond nonwoven fabric with a basis weight of 0.03 g/m 2 . , A super medium of Comparative Example 1 having a thickness of 0.03 mm was prepared.
2. 단열벽지 제조2. Manufacture of insulation wallpaper
실시예 1과 동일한 방법으로 평량이 350g/m2이고, 두께가 0.9mm인 비교예 1의 단열벽지를 제조하였다.In the same manner as in Example 1, the insulation wallpaper of Comparative Example 1 having a basis weight of 350 g/m 2 and a thickness of 0.9 mm was prepared.
3. 벽지 시스템 시공3. Wallpaper system construction
실시예 1과 동일한 방법으로 비교예 1의 벽지 시스템을 시공하였다.The wallpaper system of Comparative Example 1 was constructed in the same manner as in Example 1.
<비교예 2><Comparative Example 2>
1. 단열 초배지 제조1. Manufacture of insulation paper
실시예 1과 동일한 방법으로 평량이 245g/m2이고, 두께가 2.0mm인 비교예 2의 단열 초배지를 제조하였다.In the same manner as in Example 1, a basis weight of 245 g/m 2 and a thickness of 2.0 mm were prepared in the insulating super medium of Comparative Example 2.
2. 단열벽지 제조2. Manufacture of insulation wallpaper
실시예 2와 동일한 방법으로 평량이 380g/m2이고, 두께가 1.0mm인 비교예 2의 단열벽지를 제조하였다.In the same manner as in Example 2, the insulation wallpaper of Comparative Example 2 having a basis weight of 380 g/m 2 and a thickness of 1.0 mm was prepared.
3. 벽지 시스템 시공3. Wallpaper system construction
실시예 1과 동일한 방법으로 비교예 2의 벽지 시스템을 시공하였다.The wallpaper system of Comparative Example 2 was constructed in the same manner as in Example 1.
<비교예 3> <Comparative Example 3>
1. 단열 초배지 제조1. Manufacture of insulation paper
실시예 1과 동일한 방법으로 평량이 245g/m2이고, 두께가 6.0mm인 비교예 3의 단열 초배지를 제조하였다.In the same manner as in Example 1, a basis weight of 245 g/m 2 and a thickness of 6.0 mm were prepared in the insulating super medium of Comparative Example 3.
2. 단열벽지 제조2. Manufacture of insulation wallpaper
실시예 2와 동일한 방법으로 평량이 380g/m2이고, 두께가 1.0mm인 비교예 3의 단열벽지를 제조하였다.In the same manner as in Example 2, the insulation wallpaper of Comparative Example 3 having a basis weight of 380 g/m 2 and a thickness of 1.0 mm was prepared.
3. 벽지 시스템 시공3. Wallpaper system construction
실시예 1과 동일한 방법으로 비교예 3의 벽지 시스템을 제조하였다.The wallpaper system of Comparative Example 3 was manufactured in the same manner as in Example 1.
<비교예 4><Comparative Example 4>
1. 단열 초배지 제조1. Manufacture of insulation paper
실시예 1과 동일한 방법으로 평량이 100g/m2이고, 두께가 4.0mm인 비교예 4의 단열 초배지를 제조하였다.In the same manner as in Example 1, a basis weight of 100 g/m 2 and a thickness of 4.0 mm were prepared in the insulating super medium of Comparative Example 4.
2. 단열벽지 제조2. Manufacture of insulation wallpaper
실시예 2와 동일한 방법으로 평량이 380g/m2이고, 두께가 1.0mm인 비교예 4의 단열벽지를 제조하였다.In the same manner as in Example 2, the insulation wallpaper of Comparative Example 4 having a basis weight of 380 g/m 2 and a thickness of 1.0 mm was prepared.
3. 벽지 시스템 시공3. Wallpaper system construction
실시예 1과 동일한 방법으로 비교예 4의 벽지 시스템을 시공하였다.The wallpaper system of Comparative Example 4 was constructed in the same manner as in Example 1.
<비교예 5><Comparative Example 5>
1. 단열 초배지 제조1. Manufacture of insulation paper
실시예 1과 동일한 방법으로 평량이 500g/m2이고, 두께가 4.0mm인 비교예 5의 단열 초배지를 제조하였다.In the same manner as in Example 1, a basis weight of 500 g/m 2 and a thickness of 4.0 mm were prepared in the adiabatic super medium of Comparative Example 5.
2. 단열벽지 제조2. Manufacture of insulation wallpaper
실시예 2와 동일한 방법으로 평량이 380g/m2이고, 두께가 1.0mm인 비교예 5의 단열벽지를 제조하였다.In the same manner as in Example 2, the insulation wallpaper of Comparative Example 5 having a basis weight of 380 g/m 2 and a thickness of 1.0 mm was prepared.
3. 벽지 시스템 시공3. Wallpaper system construction
실시예 1과 동일한 방법으로 비교예 5의 벽지 시스템을 시공하였다.The wallpaper system of Comparative Example 5 was constructed in the same manner as in Example 1.
<물성 측정><Measurement of physical properties>
상기에서 제조한 실시예 1 및 2, 비교예 1-5의 단열 초배지의 평균마찰계수, 열 관류율, 보온율 및 공기층의 함량과 단열벽지의 열전도율 및 접힘자국과 벽지 시스템의 열 관류율, 시공성 및 쿠션감을 측정 또는 계산하여 이의 결과를 하기 표 1에 나타내었다.The average friction coefficient, heat permeation rate, heat retention rate, and air layer content of the insulating super media prepared above in Examples 1 and 2 and Comparative Examples 1-5, thermal conductivity of the insulating wallpaper, fold marks and thermal permeability of the wallpaper system, workability, and cushioning Persimmons were measured or calculated, and the results are shown in Table 1 below.
- 단열 초배지의 매끄럽고 평평한 면의 평균마찰계수는 상기에서 제조된 단열 초배지를 63mm×63mm (가로×세로)의 시편으로 제조한 후, 평균마찰계수 측정법(ASTM D 1894)를 이용하여 평판에 250mm×130mm (가로×세로)의 피마찰재를 측정하고자 하는 면이 노출되도록 장착하고, 상기 제조된 시편을 측정하고자 하는 면(매끄러운 면)이 노출되도록 밑면에 부착한 후, 나일론 줄과 시험편을 미끄럼판에 연결하고 하중센서를 부착하여, 29N의 로드셀, 1.96N의 수직하중, 150mm/min의 속도로 정마찰계수를 측정하고, 이를 5번 반복하여 상기 정마찰계수의 평균값을 계산하여 평균마찰계수를 측정하였다.-The average coefficient of friction of the smooth and flat surface of the insulated super medium is 250 mm × on the flat plate using the method of measuring the average coefficient of friction (ASTM D 1894) after preparing the prepared insulated super medium as a sample of 63 mm × 63 mm (width × length). 130mm (width x length) of the friction target material is mounted so that the surface to be measured is exposed, and the prepared specimen is attached to the bottom surface so that the surface to be measured (smooth surface) is exposed, and then the nylon string and the test piece are attached to the sliding plate. After connecting and attaching a load sensor, measure the static friction coefficient at a load cell of 29N, a vertical load of 1.96N, and a speed of 150mm/min, and repeat this five times to calculate the average value of the static friction coefficient to measure the average friction coefficient. I did.
평균마찰계수가 1.2 이하일 경우 표면이 매끄러운 것이다.If the average coefficient of friction is less than 1.2, the surface is smooth.
- 단열 초배지 및 벽지 시스템의 열 관류율은 상기에서 제조된 단열 초배지 및 벽지 시스템을 약 1600×1200mm (가로×세로)의 시편으로 제조한 후 석고보드 사이에 상기 시편을 위치시켜 샘플을 준비한 후, 단열성 측정방법(KS F 2273)을 이용하여 온도가 0℃로 유지되는 저온실과 온도가 20℃로 유지되는 상온실 사이에 상기 샘플을 위치시켜 30-60분 동안 온도 흐름의 안정화 과정을 거친 샘플의 열 저항 값을 측정한 후, 샘플의 열 저항 값과 석고보드의 열 저항 값을 뺀 시편의 열 저항 값의 역수를 계산하여 열 관류율을 계산하였다.-The heat permeation rate of the insulating paper and wallpaper system is determined by preparing the sample by placing the specimen between gypsum boards after preparing the insulating paper and wallpaper system as a specimen of about 1600 × 1200 mm (width × length). Heat of the sample that has undergone a stabilization process of temperature flow for 30-60 minutes by placing the sample between a low temperature room where the temperature is maintained at 0°C and a room temperature room where the temperature is maintained at 20°C using the measurement method (KS F 2273). After measuring the resistance value, the thermal permeation rate was calculated by calculating the reciprocal of the thermal resistance value of the specimen by subtracting the thermal resistance value of the sample and the thermal resistance value of the gypsum board.
상기 열 관류율이 낮을수록 단열성이 우수한 것이다. The lower the heat transmission rate, the better the heat insulation property.
- 단열 초배지의 보온율은 상기에서 제조된 단열 초배지를 약 500mm×500mm×4mm (가로×세로×두께)인 시편으로 제조한 후, 보온율 측정법(KS K 0560)을 이용하여 발열체에 시편을 부착하지 않았을 때의 발열량과 발열체에 시편을 부착하였을 때의 발열량을 이용하여 하기 [식 1]로 나타내는 수식을 이용하여 상기 시편의 보온율을 계산하였다.-For the thermal insulation rate of the thermal insulation super medium, the thermal insulation super medium prepared above was prepared as a specimen of about 500 mm × 500 mm × 4 mm (width × height × thickness) and then attached to the heating element using the thermal insulation rate measurement method (KS K 0560). The heat retention rate of the specimen was calculated using an equation represented by the following [Equation 1] using the calorific value when not not performed and the calorific value when the specimen is attached to the heating element.
보온율이 높을수록 보온성이 우수한 것이다.The higher the heat retention rate, the better the heat retention property.
[식 1][Equation 1]
Figure pat00002
Figure pat00002
- 단열 초배지의 공기층의 함량은 상기에서 제조된 단열 초배지를 약 5cm×5cm (가로×세로)의 시편으로 제조한 후, 상기 시편의 높이를 자로 측정하여 시편의 부피를 계산하고 무게를 측정한다.-The content of the air layer of the insulating paper is prepared as a specimen of about 5 cm × 5 cm (width × length) of the insulating paper prepared above, and then the height of the specimen is measured with a ruler to calculate the volume of the specimen and measure the weight.
이후, 상기 단열 초배지의 고융점 및 저융점 폴리에스테르만의 비중을 ALFA MIRAGE社의 SD-200L를 이용하여 측정하고, 부피를 계산하여, 상기 단열 초배지 내 공기층의 함량을 %로 나타내었다.Thereafter, the specific gravity of only the high-melting point and low-melting-point polyester of the insulating paper medium was measured using SD-200L of ALFA MIRAGE, and the volume was calculated, and the content of the air layer in the insulating paper medium was expressed in %.
- 단열벽지의 열전도율은 상기에서 제조된 단열벽지를 약 200mm×200mm×1mm (가로×세로×두께)의 시편으로 제작한 후, 평판 열전도율 측정법(KS L ISO 8301)을 이용하여 시편의 상측의 온도를 0℃, 하측의 온도를 20℃로 설정하고, 10-20분 후 온도 흐름이 안정된 시편의 온도 평형 값을 측정하여 상기 시편의 열전도율을 측정할 수 있다. -The thermal conductivity of the insulating wallpaper is the temperature of the upper side of the specimen after making the insulating wallpaper prepared above into a specimen of about 200mm×200mm×1mm (width×length×thickness), and then using a flat plate thermal conductivity measurement method (KS L ISO 8301). The thermal conductivity of the specimen can be measured by measuring the temperature equilibrium value of the specimen in which the temperature flow is stable after 10-20 minutes, and the temperature at the lower side is set to 0°C and 20°C.
- 단열벽지의 접힘 자국은 벽지를 접은 후 다시 펼쳤을 때 접힘 부분의 자국이 남는지를 육안으로 측정하였다.-The fold marks on the insulating wallpaper were visually measured to see if the fold marks remained when the wallpaper was folded and then opened again.
(X: 벽지의 접힘 부분의 자국이 있음, ○: 벽지의 접힘 부분의 자국이 없음)(X: There are marks on the folds of the wallpaper, ○: There are no marks on the folds of the wallpaper)
- 벽지 시스템의 시공성은 상기에서 제조된 벽지 시스템을 벽면에 시공 시, 벽지가 들뜨거나 벽지 간 이음매가 표시가 나는 지 여부를 육안으로 측정하였다.-The constructability of the wallpaper system was visually measured whether the wallpaper was lifted or the seam between the wallpaper was marked when the wallpaper system manufactured above was installed on the wall.
(X: 들뜨거나 벽지 간 이음매가 표시가 남, ○: 들뜨거나 벽지 간 이음매가 표시가 나지 않음)(X: Raised or displayed seams between wallpapers, ○: Raised or not indicated seams between wallpapers)
- 벽지 시스템의 쿠션감은 5인의 실험자가 시공된 벽지 시스템을 손바닥으로 눌러 쿠션감이 좋으면 ◎, 보통이면 △, 좋지 않으면 X로 표기하였다.-As for the cushioning feeling of the wallpaper system, five experimenters pressed the installed wallpaper system with their palms and marked ◎ if the cushioning feel is good, △ if it is normal, and X if it is not good.
실시예 1Example 1 실시예 2Example 2 비교예 1Comparative Example 1 비교예 2Comparative Example 2 비교예 3Comparative Example 3 비교예 4Comparative Example 4 비교예 5Comparative Example 5
단열초배지Adiabatic medium
부직포 종류Type of non-woven fabric PET+LMPET(니들펀칭)PET+LMPET (needle punching) PET+LMPET(니들펀칭)PET+LMPET (needle punching) 스펀본드PETSpunbond PET PET+LMPET(니들펀칭)PET+LMPET (needle punching) PET+LMPET(니들펀칭)PET+LMPET (needle punching) PET+LMPET(니들펀칭)PET+LMPET (needle punching) PET+LMPET(니들펀칭)PET+LMPET (needle punching)
평량(g/m2)Basis weight (g/m 2 ) 245245 245245 0.030.03 245245 245245 100100 500500
두께(mm)Thickness(mm) 4.04.0 4.04.0 0.030.03 2.02.0 6.06.0 4.04.0 4.04.0
매끄러운 면의 평균마찰계수Average coefficient of friction of smooth surface 0.70.7 0.70.7 1.41.4 0.60.6 0.920.92 0.930.93 0.40.4
열 관류율(W/m2·K)Heat transmittance rate (W/m 2 ·K) 8.08.0 8.08.0 36.536.5 17.217.2 7.87.8 7.77.7 23.423.4
보온율(%)Insulation rate (%) 6767 6767 1717 5252 7373 6868 4747
공기층 함량(%)Air layer content (%) 96.796.7 96.796.7 7373 6060 97.797.7 9090 6161
단열벽지Insulation wallpaper
제1발포수지층First foaming resin layer 글라스 버블 1)Glass Bubble 1) 1010 1010 1010 1010 1010 1010 1010
글라스 버블 2)Glass Bubble 2) -- -- -- -- -- -- --
글라스 버블 3)Glass Bubble 3) -- -- -- -- -- -- --
탄산 칼슘Calcium carbonate -- -- -- -- -- -- --
캡슐 발포제Capsule blowing agent -- -- -- -- -- -- --
제2발포수지층2nd foaming resin layer 글라스 버블 1)Glass Bubble 1) -- -- -- -- -- -- --
탄산 칼슘Calcium carbonate -- 7070 -- 7070 7070 7070 7070
캡슐 발포제Capsule blowing agent -- 33 -- 33 33 33 33
두께(mm)Thickness(mm) 0.90.9 1.01.0 0.90.9 1.01.0 1.01.0 1.01.0 1.01.0
평량(g/m2)Basis weight (g/m 2 ) 350350 380380 350350 380380 380380 380380 380380
열전도율(mW/m·k)Thermal conductivity (mW/m·k) 5050 8080 5050 8080 8080 8080 8080
접힘자국Fold marks
벽지 시스템 물성Wallpaper system properties
열 관류율(W/m2·K)Heat transmittance rate (W/m 2 ·K) 6.86.8 7.67.6 32.132.1 15.915.9 7.57.5 7.27.2 22.422.4
시공성Constructability X X X X
쿠션감Cushion X X X
상기 표 1에서 확인된 바와 같이, 본 발명에 따른 실시예 1 및 2의 벽지 시스템은, 비교예 1 내지 5와 비교하여 단열 초배지의 열 관류율이 15 W/m2·K 이하이고, 보온율이 50%이상이고, 공기층의 함량이 85%이상이고, 단열벽지의 열전도율이 150 mW/m·k 미만으로, 벽지 시스템의 열 관류율이 저감되어 단열성이 우수하고 경량화를 구현할 수 있음과 아울러, 쿠션감이 우수하고, 단열 초배지 일면이 매끄럽고 평평하여 단열 초배지 표면의 요철 형상이 보완됨과 아울러 단열벽지와의 접착성이 우수하여 단열벽지의 시공성이 우수하면서도 벽지의 접힘 부분의 자국이 없어 시공품질이 우수한 것을 확인할 수 있었다.As confirmed in Table 1, the wallpaper systems of Examples 1 and 2 according to the present invention have a thermal permeation rate of 15 W/m 2 ·K or less, and a heat retention rate of the insulating super medium compared to Comparative Examples 1 to 5 It is more than 50%, the content of the air layer is more than 85%, and the thermal conductivity of the insulation wallpaper is less than 150 mW/m·k, and the heat permeation rate of the wallpaper system is reduced, so that it is possible to realize excellent insulation and light weight, and a feeling of cushioning. It is excellent in terms of its excellent workability and excellent construction quality due to the excellent adhesiveness to the insulation wallpaper as well as the unevenness shape of the surface of the insulation paper is complemented by the smooth and flat one side of the insulation paper, and there are no marks on the folds of the wallpaper. I could confirm.
한편, 스펀본드 부직포를 이용한 초배지를 벽면에 부분 시공한 비교예 1은 벽지의 접힘 부분의 자국은 없으나, 실시예 1 및 2의 단열 초배지의 두께에 비하여 비교예 1의 스펀본드 부직포의 두께가 매우 얇아, 공기층을 많이 포함하지 못하여 열 관류율이 높고 보온율이 낮아 단열성이 우수하지 않으며, 쿠션감이 저하되고 저융점 폴리에스테르 섬유를 포함하지 않는 바, 단열 초배지의 표면 일면이 매끄럽지 못하여 단열 초배지 표면의 요철 형상이 두드러져 외관이 미려하지 못하였고, 단열벽지를 지지하지 못하여 단열벽지가 벽면에서 이탈하거나 찢어져 시공성이 용이하지 않은 것을 확인할 수 있었다.On the other hand, Comparative Example 1 in which the super badge using spunbond nonwoven fabric was partially constructed on the wall surface did not have marks on the folded portion of the wallpaper, but the thickness of the spunbond nonwoven fabric of Comparative Example 1 was very As it is thin, it does not contain a lot of air layer, so it has high heat permeation rate and low thermal insulation rate, so it does not have excellent thermal insulation properties, and the cushioning feel is lowered and does not contain low-melting polyester fiber. It was confirmed that the uneven shape was remarkable, and the appearance was not beautiful, and the insulation wallpaper was not easily constructed because it was not able to support the insulation wallpaper and was torn or separated from the wall.
또한, 단열 초배지의 두께가 3mm 미만인 비교예 2는 단열 초배지 일면이 매끄럽고 평평하지만, 단열 초배지의 두께가 매우 얇아 쿠션감이 저하되어 벽면의 요철 형상을 방지할 수 없었고, 단열 초배지의 공기층 함량이 낮아 열 관류율 및 보온율이 우수하지 않았고, 따라서 벽지 시스템의 열 관류율이 높아져 단열성 및 시공성이 저하된 것을 확인할 수 있었다.In addition, in Comparative Example 2, in which the thickness of the insulating super medium is less than 3 mm, one side of the insulating super medium is smooth and flat, but the cushioning feeling is lowered due to the very thin thickness of the insulating super medium, so that the uneven shape of the wall surface could not be prevented, and the air layer content of the insulating super medium was low. It was confirmed that the thermal permeation rate and the thermal insulation rate were not excellent, and thus the thermal permeation rate of the wallpaper system was increased, resulting in a decrease in thermal insulation and workability.
또한, 단열 초배지의 두께가 5mm 초과인 비교예 3은 단열 초배지 일면이 매끄러워 단열 초배지 표면의 요철을 보완할 수 있었고, 단열 초배지의 두께가 두꺼워 벽지 시스템의 쿠션감이 매우 우수하여 벽면의 요철 형상을 보완할 수 있었으며, 단열 초배지의 공기층의 함량이 높아 벽지 시스템의 열 관류율이 낮아 단열성이 우수하나, 단열 초배지의 두께가 너무 두꺼워 시공성이 좋지 않으며 벽지 시스템으로 사용이 용이하지 않은 것을 확인할 수 있었다.In addition, in Comparative Example 3, in which the thickness of the insulation paper was more than 5mm, one side of the insulation paper was smooth to compensate for the irregularities on the surface of the insulation paper, and the thickness of the insulation paper was very thick, so that the cushioning feeling of the wallpaper system was very excellent, and the shape of the irregularities on the wall surface. It was confirmed that the heat-transmission rate of the wallpaper system was low due to the high content of the air layer in the insulated paper, and the insulation was excellent, but the thickness of the insulated paper was too thick, so the workability was not good and it was not easy to use as a wallpaper system.
또한, 단열 초배지의 평량이 200g/m2 미만인 비교예 4는 단열 초배지 일면이 매끄럽고 평평하여 단열 초배지 표면의 요철을 보완할 수 있고, 평량이 가벼워 공기층의 함량이 높고 열 관류율이 우수하였으나, 쿠션감이 우수하지 않아 벽면의 요철 형상이 보완되지 않았으며 단열벽지를 지지하지 못하여 시공성이 매우 용이하지 않았다.In addition, in Comparative Example 4, in which the basis weight of the insulating super medium is less than 200 g/m 2, one side of the insulating super medium is smooth and flat to compensate for the irregularities on the surface of the insulating super medium, and the basis weight is light, so the content of the air layer is high and the heat permeation rate is excellent, but the cushioning feeling As this was not excellent, the uneven shape of the wall was not complemented, and the workability was not very easy because the insulation wallpaper could not be supported.
또한, 단열 초배지의 평량이 400g/m2 초과인 비교예 5는 단열 초배지 일면이 매끄럽고, 쿠션감이 우수하여 단열 초배지 표면과 벽면의 요철 형상을 보완하였으나, 공기층의 함량이 낮고 열 관류율이 높아 단열성이 저하되었고, 평량이 너무 무거워 단열 초배지가 벽면에서 이탈하여 시공성이 용이하지 않은 것을 확인할 수 있었다. In addition, Comparative Example 5, in which the basis weight of the insulating super medium is more than 400 g/m 2 , supplemented the uneven shape of the surface and the wall of the insulating super medium by smoothing one side of the insulating super medium and having excellent cushioning feeling, but the content of the air layer is low and the heat permeation rate is high. This decreased, and the basis weight was too heavy, and it was confirmed that the insulation super media was separated from the wall surface, and thus the workability was not easy.
100: 벽지 시스템 110: 단열 초배지
130: 단열벽지 131: 기재층
133: 제1발포수지층 135: 제2발포수지층
100: wallpaper system 110: thermal insulation paper
130: insulation wallpaper 131: base layer
133: first foaming resin layer 135: second foaming resin layer

Claims (24)

  1. 융점이 상이한 2종의 섬유를 포함하는 부직포로 형성된 단열 초배지(110); 및
    상기 단열 초배지(110) 일면에 형성되는,
    하부에서 상부로 기재층(131), 상기 기재층(131)의 상부에 전면 도포된 제1발포수지층(133)을 포함하고, 열전도율이 150mW/m·K 미만인 단열벽지(130); 를 포함하는 벽지 시스템.
    Insulating paper (110) formed of a non-woven fabric containing two kinds of fibers having different melting points; And
    Formed on one side of the heat insulating paper (110),
    An insulating wallpaper 130 including a base layer 131 from the bottom to the top, and a first foaming resin layer 133 applied entirely on the top of the base layer 131 and having a thermal conductivity of less than 150mW/m·K; Wallpaper system comprising a.
  2. 제1항에 있어서,
    상기 단열 초배지(110)는 일면에 매끄러운 면이 형성된 것인 벽지 시스템.
    The method of claim 1,
    The insulating paper paper 110 is a wallpaper system that has a smooth surface formed on one surface.
  3. 제2항에 있어서,
    상기 단열 초배지(110) 일면은 평균마찰계수가 0.2-1.2인 것인 벽지 시스템.
    The method of claim 2,
    One side of the insulation paper (110) is a wallpaper system that has an average coefficient of friction of 0.2-1.2.
  4. 제1항에 있어서,
    상기 2종의 섬유는 동일한 열가소성 수지 재질인 것인 벽지 시스템.
    The method of claim 1,
    The wallpaper system that the two kinds of fibers are made of the same thermoplastic resin material.
  5. 제1항에 있어서,
    상기 섬유는 폴리에스테르 섬유인 것인 벽지 시스템.
    The method of claim 1,
    The wallpaper system that the fibers are polyester fibers.
  6. 제1항에 있어서,
    상기 2종의 섬유는 융점이 250-280℃인 고융점 폴리에스테르 섬유 및 융점이 110-150℃인 저융점 폴리에스테르 섬유인 것인 벽지 시스템.
    The method of claim 1,
    The two kinds of fibers are a high-melting polyester fiber having a melting point of 250-280°C and a low-melting polyester fiber having a melting point of 110-150°C.
  7. 제1항에 있어서,
    상기 단열 초배지(110)는 평량이 200-400g/m2 인 것인 벽지 시스템.
    The method of claim 1,
    The insulation paper (110) is a wallpaper system that has a basis weight of 200-400g/m 2.
  8. 제1항에 있어서,
    상기 단열 초배지(110)는 평량이 200-350g/m2 인 것인 벽지 시스템.
    The method of claim 1,
    The insulation paper (110) is a wallpaper system that has a basis weight of 200-350g/m 2.
  9. 제1항에 있어서,
    상기 단열 초배지(110)는 두께가 3.0-5.0mm인 것인 벽지 시스템.
    The method of claim 1,
    The thermal insulation paper (110) is a wallpaper system that has a thickness of 3.0-5.0mm.
  10. 제1항에 있어서,
    상기 단열 초배지(110)는 두께가 3.5-4.5mm인 것인 벽지 시스템.
    The method of claim 1,
    The thermal insulation paper (110) is a wallpaper system that has a thickness of 3.5-4.5mm.
  11. 제1항에 있어서,
    상기 단열 초배지(110)는 열 관류율이 15W/m2·K 이하인 것인 벽지 시스템.
    The method of claim 1,
    The thermal insulation paper substrate 110 is a wallpaper system that has a heat transmission rate of 15W/m 2 ·K or less.
  12. 제1항에 있어서,
    상기 단열 초배지(110)의 공기층 함량은 85% 이상인 것인 벽지 시스템.
    The method of claim 1,
    The wallpaper system that the air layer content of the insulating paper (110) is 85% or more.
  13. 제1항에 있어서,
    상기 단열벽지(130)는 열전도율이 100mW/m·k 미만인 것인 벽지 시스템.
    The method of claim 1,
    The thermal insulation wallpaper 130 is a wallpaper system that has a thermal conductivity of less than 100mW/m·k.
  14. 제1항에 있어서,
    상기 단열벽지(130)는 열전도율이 70mW/m·k 미만인 것인 벽지 시스템.
    The method of claim 1,
    The thermal insulation wallpaper 130 is a wallpaper system that has a thermal conductivity of less than 70mW/m·k.
  15. 제1항에 있어서,
    상기 단열벽지(130)는 상기 기재층(131) 상부에 부분 도포되는 발포 수지층을 더 포함하는 것인 벽지 시스템
    The method of claim 1,
    The insulating wallpaper 130 is a wallpaper system that further comprises a foamed resin layer partially coated on the base layer 131
  16. 제1항에 있어서,
    상기 단열벽지(130)는 상기 제1발포수지층(133) 상부에 부분 도포되는 제2발포수지층(135)을 더 포함하는 것인 벽지 시스템.
    The method of claim 1,
    The insulating wallpaper 130 further comprises a second foaming resin layer 135 partially coated on the first foaming resin layer 133.
  17. 제1항에 있어서,
    상기 제1발포수지층(133)은 글라스 버블을 포함하는 것인 벽지 시스템.
    The method of claim 1,
    The first foaming resin layer 133 is a wallpaper system comprising glass bubbles.
  18. 제16항에 있어서,
    상기 제2발포수지층(135)은 캡슐 발포제를 포함하는 것인 벽지 시스템.
    The method of claim 16,
    The second foaming resin layer 135 is a wallpaper system containing a capsule foaming agent.
  19. 제1항에 있어서,
    상기 벽지 시스템은 열 관류율이 15W/m2·K 이하인 것인 벽지 시스템.
    The method of claim 1,
    The wallpaper system is a wallpaper system that has a heat transmission rate of 15W/m 2 ·K or less.
  20. 제1항에 있어서,
    상기 벽지 시스템은 열 관류율이 12W/m2·K 이하인 것인 벽지 시스템.
    The method of claim 1,
    The wallpaper system is a wallpaper system that has a heat permeation rate of 12W/m 2 ·K or less.
  21. 제1항에 있어서,
    상기 벽지 시스템은 보온율이 60%이상인 것인 벽지 시스템.
    The method of claim 1,
    The wallpaper system is a wallpaper system that has a thermal insulation rate of 60% or more.
  22. 제1항에 있어서,
    상기 벽지 시스템은 단열 초배지(110)와 단열벽지(130) 사이에 전면 초배지를 더 포함하는 것인 벽지 시스템.
    The method of claim 1,
    The wallpaper system is a wallpaper system that further comprises a front panel between the thermal insulation paper (110) and the insulation wallpaper (130).
  23. 제22항에 있어서,
    상기 전면 초배지는 벽면 가장자리에서 일정 간격을 두고 형성되는 것이며,
    일정 간격 노출된 단열 초배지 일면과 단열벽지가 직접 접착되는 것인 벽지 시스템.
    The method of claim 22,
    The front super badge is formed at regular intervals at the edge of the wall,
    A wallpaper system in which the one side of the thermal insulation super media exposed at regular intervals and the thermal insulation wallpaper are directly bonded.
  24. 제23항에 있어서,
    상기 전면 초배지는 벽면 가장자리에서 5-10cm 간격을 두고 형성되는 것인 벽지 시스템.

    The method of claim 23,
    The front wall paper system is formed at intervals of 5-10cm from the edge of the wall.

KR1020190144166A 2019-11-12 2019-11-12 wallpaper system KR20210057421A (en)