KR20210010064A - Aqueous urethane foam containing mugwort extract and its preparation method - Google Patents

Aqueous urethane foam containing mugwort extract and its preparation method Download PDF

Info

Publication number
KR20210010064A
KR20210010064A KR1020190087456A KR20190087456A KR20210010064A KR 20210010064 A KR20210010064 A KR 20210010064A KR 1020190087456 A KR1020190087456 A KR 1020190087456A KR 20190087456 A KR20190087456 A KR 20190087456A KR 20210010064 A KR20210010064 A KR 20210010064A
Authority
KR
South Korea
Prior art keywords
mugwort extract
urethane foam
weight
parts
polyol
Prior art date
Application number
KR1020190087456A
Other languages
Korean (ko)
Inventor
김두화
Original Assignee
(주)엔나노텍
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)엔나노텍 filed Critical (주)엔나노텍
Priority to KR1020190087456A priority Critical patent/KR20210010064A/en
Publication of KR20210010064A publication Critical patent/KR20210010064A/en

Abstract

The present invention relates to an aqueous urethane foam comprising a mugwort extract and a preparation method thereof and, more particularly, to an aqueous urethane foam containing a mugwort extract which includes polyols, foam stabilizers, catalysts, flame retardants, and mugwort extract so as to provide a low density and an effect on reduced separation of the system, and a preparation method thereof. The present invention provides an aqueous urethane foam containing a mugwort extract and a preparation method thereof, thereby securing liquid stability of a polyol system containing the mugwort extract and increasing an amount of water added. In addition, when preparing an aqueous rigid spray foam including the mugwort extract, a unit price can be lowered by lowering a density, and the VOC can be reduced by using an eco-friendly material, along with an excellent effect of increasing the strength and dimensional stability of urethane foam prepared by the mugwort extract serving as a surfactant.

Description

쑥 추출물 함유 수성 우레탄폼 및 그 제조방법 {Aqueous urethane foam containing mugwort extract and its preparation method}Aqueous urethane foam containing mugwort extract and its preparation method}

본 발명은 쑥 추출물 함유 수성 우레탄폼 및 그 제조방법에 관한 것으로, 보다 상세하게는 폴리올, 정포제, 촉매, 난연제, 및 쑥 추출물을 포함함으로써 낮은 밀도를 가지고 시스템의 분리가 감소된 효과를 나타내는 쑥 추출물 함유 수성 우레탄폼 및 그 제조방법에 관한 것이다.The present invention relates to an aqueous urethane foam containing mugwort extract and a method for producing the same, and more particularly, by including a polyol, a foam stabilizer, a catalyst, a flame retardant, and a mugwort extract, a mugwort having a low density and reduced separation of the system It relates to an extract-containing aqueous urethane foam and a method for producing the same.

폴리우레탄은 이소시아네이트와 하이드록실 화합물 반응을 통해 제조되는 것으로서 사용되는 용도에 따라 자동차, 소파와 침대의 쿠션재로 사용되는 연질폼 및 냉장고와 건축물의 단열재로 사용되는 경질폼으로 사용되고 있으며, 도료와 접착제, 스판덱스 섬유, 열가소성 폴리우레탄 등의 형태로 이용되고 있다.Polyurethane is manufactured through the reaction of isocyanate and hydroxyl compounds, and is used as a soft foam used as a cushioning material for automobiles, sofas and beds, and a hard foam used as an insulation material for refrigerators and buildings, depending on the intended use. Paints and adhesives, It is used in the form of spandex fiber and thermoplastic polyurethane.

단열재로는 경질우레탄폼이 사용되는데 이는 발포형식에 따라 보드폼, 스프레이 폼으로 나뉜다. 스프레이 폼은 공간을 채우기 어렵거나 곤란한 경우를 포함하여 모든 종류의 지역에 다양한 방법과 효과적인 비용으로 단열을 할 수 있다. 가령, 경사진 지붕, 천정, 바닥 등 폭 넓은 영역에서 사용이 가능하며 방수와 단열을 제공한다. 구조체에 직접 분사하는 것으로써 틈새가 없으며 열교가 만들어지지 않는 장점이 있다.Rigid urethane foam is used as an insulating material, which is divided into board foam and spray foam depending on the foam type. Spray foam can insulate all types of areas in a variety of ways and cost-effectively, including difficult or difficult to fill spaces. For example, it can be used in a wide range of areas such as sloped roofs, ceilings, and floors, and provides waterproofing and insulation. By spraying directly on the structure, there is no gap and no thermal bridge is created.

우레탄폼을 발포시키기 위해서는 발포제가 필요한데 발포제는 화학적 발포제, 물리적 발포제가 있으며 발포제의 양에 따라 밀도의 변화를 줄 수 있다. 물리적 발포제는 비점이 낮아 우레탄 반응 시에 발열반응으로 인하여 내부온도가 증가될 때 휘발되면서 폼을 부풀게 만들며 정도에 따라 밀도를 결정하게 된다.In order to foam the urethane foam, a foaming agent is required. The foaming agent has a chemical foaming agent and a physical foaming agent, and the density can be changed according to the amount of the foaming agent. The physical foaming agent has a low boiling point and volatilizes when the internal temperature increases due to an exothermic reaction during the urethane reaction, causing the foam to swell, and the density is determined according to the degree.

하지만 물리적 발포제는 오존층을 파괴하는 물질로 사용함에 있어 제약이 있다. 오존층을 보호하기 위해 오존층 파괴물질의 사용을 금지하고 선진국에서 대체물질을 개발하여 후진국으로 그 기술을 이전하는 것에 관하여 규정하는 UN이 주관하고 있는 국제협약인 몬트리올 의성서에 의하면 향후 2030년 이내에는 사용이 전면 금지될 것이기 때문에 대체 발포체 원료의 연구가 시급한 실정이다.However, the physical foaming agent has limitations in its use as a material that destroys the ozone layer. In order to protect the ozone layer, the use of ozone-depleting substances is prohibited, and according to the Montreal Protocol, an international agreement governed by the UN that regulates the development of alternative substances in developed countries and transfer of the technology to developed countries, use within the next 2030. Since this will be banned altogether, research on alternative foam materials is urgent.

대체 발포제로는 ODP와 GWP가 낮은 펜탄류가 제안되어 적용되고 있으나 이는 폭발하는 특성이 있어 폭발 방지를 위한 막대한 시설투자비가 발생한다. 이러한 이유로 화학적 발포제인 물만을 이용하여 제조되는 수발포 우레탄폼이 꾸준히 개발되고 있는 실정이다.As an alternative foaming agent, pentanes with low ODP and GWP have been proposed and applied, but this has an explosive property, which incurs a huge facility investment to prevent explosion. For this reason, water-foaming urethane foams manufactured using only water, which is a chemical foaming agent, are being developed steadily.

이에 따라 '대한민국 등록특허 제 10-0549161호'는 건축물의 층간 충격음 저감을 위한 연질 폴리우레탄조성물, 및 이를 이용한 스프레이 시공방법, 그리고 그연질 폴리우레탄 스프레이폼 구조체를 제공하고 있으며, 이러한 우레탄은 수발포 우레탄폼으로만을 이용하고 있으나, 수발포 우레탄폼은 상대적으로 유연성이 있는 우레탄 결합이 적고 비교적 딱딱한 우레아 결합이 상당히 증가되어 접착력이 열악해지는 경향이 있다. 또한 생성되는 우레아 그룹은 우레탄 반응시 점도를 상승시켜 균일한 폼을 형성시키기도 어려운 부분이 있어 열전도율, 강도, 치수안정성 등의 물성이 저하될 수 있으며, 스프레이 폼 특성상 빠른 경화가 필요하기 때문에 촉매를 다량 투입하게 되어 VOC가 발생하는 문제점이 있다.Accordingly,'Korean Patent Registration No. 10-0549161' provides a soft polyurethane composition for reducing the impact sound between floors of a building, a spray construction method using the same, and a soft polyurethane spray foam structure. Such urethane is water-foamed. Although only using urethane foam, water-foamed urethane foam tends to have poor adhesion due to relatively few flexible urethane bonds and relatively hard urea bonds. In addition, the resulting urea group has a part where it is difficult to form a uniform foam by increasing the viscosity during urethane reaction, so physical properties such as thermal conductivity, strength, and dimensional stability may be deteriorated. Due to the nature of the spray foam, a large amount of catalyst is required because rapid curing is required. There is a problem that VOC is generated due to input.

따라서 본 발명은 이러한 문제점을 해결하기 위하여 친환경적인 천연물이면서 계면활성제 역할을 할 수 있는 플라보노이드와 폴리페놀 등의 성분으로 이루어진 쑥 추출물을 포함하는 수성 우레탄폼을 제공하고자 한다.Therefore, in order to solve this problem, the present invention is to provide a water-based urethane foam comprising a mugwort extract composed of components such as flavonoids and polyphenols, which are environmentally friendly natural products and can act as surfactants.

KR 10-0549161 B1KR 10-0549161 B1 KR 10-0729826 B1KR 10-0729826 B1

상기 문제점을 해결하기 위하여 본 발명은 쑥 추출물 함유 수성 우레탄폼을 제공하는 것을 목적으로 한다.In order to solve the above problem, the present invention aims to provide an aqueous urethane foam containing mugwort extract.

또한, 쑥 추출물 함유 수성 우레탄폼의 제조방법을 제공하는 것을 목적으로 한다.In addition, it is an object of the invention to provide a method for producing an aqueous urethane foam containing mugwort extract.

또한, 쑥 추출물 함유 수성 우레탄폼을 포함하는 단열재를 제공하는 것을 목적으로 한다.In addition, it is an object of the present invention to provide a heat insulating material comprising an aqueous urethane foam containing mugwort extract.

상기 목적을 해결하기 위하여 본 발명은,In order to solve the above object, the present invention,

폴리올 100 중량부에 대하여, 정포제 0.1 내지 5 중량부, 촉매 0.1 내지 5 중량부, 난연제 5 내지 40 중량부, 및 쑥 추출물 0.1 내지 20 중량부를 포함하는 시스템 폴리올; 및System polyol comprising 0.1 to 5 parts by weight of a foaming agent, 0.1 to 5 parts by weight of a catalyst, 5 to 40 parts by weight of a flame retardant, and 0.1 to 20 parts by weight of a mugwort extract based on 100 parts by weight of the polyol; And

방향족 디이소시아네이트(aromatic diisocyanate)을 포함하되,Including aromatic diisocyanate (aromatic diisocyanate),

상기 시스템 폴리올과 방향족 디이소시아네이트의 중량비는 1 : 0.5 - 3.0인 것을 특징으로 하는 쑥 추출물 함유 수성 우레탄폼을 제공한다.It provides an aqueous urethane foam containing mugwort extract, characterized in that the weight ratio of the system polyol and the aromatic diisocyanate is 1: 0.5-3.0.

폴리올은 1 내지 10종의 폴리올을 혼합하는 것을 특징으로 하며, 촉매는 아민촉매, 금속촉매, 및 삼량화 촉매 중에서 선택된 하나 이상인 것을 특징으로 한다.The polyol is characterized by mixing 1 to 10 types of polyols, and the catalyst is characterized in that at least one selected from an amine catalyst, a metal catalyst, and a trimerization catalyst.

또한, 쑥 추출물은 물, 에탄올, 및 메탄올로 이루어진 군으로부터 선택된 하나 이상의 용매로 추출하는 것을 특징으로 하며, 방향족 디이소시아네이트는 메틸렌 디페닐 디이소시아네이트(MDI, Methylene Diphenyl Diisocyanate)인 것을 특징으로 한다.In addition, the mugwort extract is characterized in that it is extracted with one or more solvents selected from the group consisting of water, ethanol, and methanol, and the aromatic diisocyanate is methylene diphenyl diisocyanate (MDI).

상기 다른 목적을 해결하기 위하여 본 발명은,In order to solve the above other object, the present invention,

쑥을 추출하여 쑥 추출물을 형성하는 제 1 단계;A first step of extracting the mugwort to form a mugwort extract;

상기 쑥 추출물과 폴리올, 정포제, 촉매, 및 난연제를 혼합하여 시스템 폴리올을 형성하는 제 2 단계; 및A second step of forming a system polyol by mixing the mugwort extract and a polyol, a foam stabilizer, a catalyst, and a flame retardant; And

상기 시스템 폴리올과 방향족 디이소시아네이트를 반응시키는 제 3 단계;를 포함하는 것을 특징으로 하는 쑥 추출물 함유 수성 우레탄폼의 제조방법을 제공한다.It provides a method for producing an aqueous urethane foam containing mugwort extract comprising; a third step of reacting the system polyol with an aromatic diisocyanate.

제 1 단계는 쑥을 추출하여 형성된 고상의 슬러지를 제거하는 과정을 포함하는 것을 특징으로 하며, 제 3 단계는 30 내지 90 ℃의 온도에서 이루어지는 것을 특징으로 한다.The first step is characterized in that it includes a process of removing the solid sludge formed by extracting the mugwort, and the third step is characterized in that it is performed at a temperature of 30 to 90 ℃.

상기 또 다른 목적을 해결하기 위하여 본 발명은,In order to solve the another object, the present invention,

쑥 추출물 함유 수성 우레탄폼을 포함하는 단열재를 제공한다.It provides a heat insulating material comprising an aqueous urethane foam containing mugwort extract.

본 발명은 쑥 추출물 함유 수성 우레탄폼 및 그 제조방법을 제공함으로써, 쑥 추출물이 첨가된 폴리올 시스템의 액 안정성을 확보하고 물의 투입량을 증대시킬 수 있는 효과가 있다. 또한, 쑥 추출물을 포함하여 수성 경질 스프레이 폼을 제조 시 밀도를 낮추어 단가를 낮출 수 있고 친환경 물질을 사용함으로써 VOC를 저감할 수 있으며, 쑥 추출물의 계면활성제 역할에 의해 제조되는 우레탄폼의 강도와 치수안정성이 우수해지는 효과가 있다.The present invention provides an aqueous urethane foam containing mugwort extract and a method for producing the same, thereby securing liquid stability of the polyol system to which the mugwort extract is added and increasing the amount of water input. In addition, when manufacturing an aqueous hard spray foam including mugwort extract, the unit cost can be lowered by lowering the density, and VOC can be reduced by using an eco-friendly material, and the strength and dimensions of the urethane foam produced by the role of a surfactant of the mugwort extract There is an effect of excellent stability.

도 1은 본 발명의 일 실시예에 따른 쑥 추출물 함유 수성 경질 스프레이폼을 제조하는 과정을 나타낸 것이다.
도 2는 본 발명의 일 실시예 및 일 비교예에 따라 제조된 시스템 폴리올의 분산 정도를 비교한 사진이다.
1 shows a process for producing an aqueous hard spray foam containing mugwort extract according to an embodiment of the present invention.
2 is a photograph comparing the degree of dispersion of system polyols prepared according to an embodiment and a comparative example of the present invention.

본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 상세하게 후술되어 있는 실시예들을 참조하면 명확해질 것이다. 그러나 본 발명은 이하 개시되는 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 본 실시예들은 본 발명의 개시가 완전하도록 하며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이다. 본 명세서에서 사용된 용어는 실시예들을 설명하기 위한 것으로 본 발명을 제한하고자 하는 것이 아니며, 본 명세서에서 단수형은 문구에서 특별히 언급하지 않는 한 복수형도 포함한다.Advantages and features of the present invention, and a method of achieving them will become apparent with reference to embodiments described below in detail. However, the present invention is not limited to the embodiments disclosed below, but will be implemented in various forms different from each other, and only these embodiments make the disclosure of the present invention complete, and those skilled in the art to which the present invention pertains. It is provided to fully inform the person of the scope of the invention. The terms used in the present specification are for explaining embodiments and are not intended to limit the present invention, and the singular form in the present specification includes the plural form unless specifically stated in the text.

이하, 본 발명의 바람직한 실시예에 대해 상세히 설명하기로 한다. 한편, 해당 기술분야의 통상적인 지식을 가진자로부터 용이하게 알 수 있는 구성과 그에 대한 작용 및 효과에 대한 도시 및 상세한 설명은 간략히 하거나 생략하고 본 발명과 관련된 부분들을 중심으로 상세히 설명하도록 한다.Hereinafter, a preferred embodiment of the present invention will be described in detail. On the other hand, the illustrations and detailed descriptions of configurations, actions and effects thereof that can be easily recognized by those of ordinary skill in the art will be simplified or omitted, and will be described in detail centering on parts related to the present invention.

본 발명은 쑥 추출물 함유 수성 우레탄폼 및 그 제조방법에 관한 것이다.The present invention relates to an aqueous urethane foam containing mugwort extract and a method for producing the same.

일 측면에 따르면, 본 발명은 폴리올 100 중량부에 대하여, 정포제 0.1 내지 5 중량부, 촉매 0.1 내지 5 중량부, 난연제 5 내지 40 중량부, 및 쑥 추출물 0.1 내지 20 중량부를 포함하는 시스템 폴리올; 및 방향족 디이소시아네이트(aromatic diisocyanate)을 포함하되, 상기 시스템 폴리올과 방향족 디이소시아네이트의 중량비는 1 : 0.5 - 3.0인 것을 특징으로 하는 쑥 추출물 함유 수성 우레탄폼을 제공한다.According to one aspect, the present invention, based on 100 parts by weight of the polyol, 0.1 to 5 parts by weight of a foaming agent, 0.1 to 5 parts by weight of a catalyst, 5 to 40 parts by weight of a flame retardant, and a system polyol comprising 0.1 to 20 parts by weight of mugwort extract; And it includes an aromatic diisocyanate (aromatic diisocyanate), wherein the weight ratio of the system polyol and the aromatic diisocyanate is 1: 0.5-Provides an aqueous urethane foam containing wormwood extract, characterized in that the weight ratio is 3.0.

본 발명의 쑥 추출물 함유 수성 우레탄폼에서 폴리올은 경질용 폴리올로써 수산기가는 200~600 mgKOH/g이며 작용기는 3 이상인 것을 사용할 수 있다. 바람직하게는 수산기는 250-500인 것을 사용할 수 있으며, 작용기는 글리세롤(Glycerol), 펜타에리트리톨(Pentaerythritol), 솔비톨(sorbitol), 수크로오즈(sucrose) 등 작용기가 높은 것에 EO(ethylene oxide), PO(propylene oxide) 등이 부가된 것을 혼합하여 사용할 수 있다. 종류에 따라 1종 내지 10종의 폴리올을 혼합하여 사용할 수 있으며, 바람직하게는 2종 내지 8종, 더욱 바람직하게는 3종 내지 6종을 혼합하여 사용할 수 있다.In the aqueous urethane foam containing mugwort extract of the present invention, the polyol is a hard polyol with a hydroxyl value of 200 to 600 mgKOH/g and a functional group of 3 or more. Preferably, those having a hydroxyl group of 250-500 may be used, and the functional groups are those having high functional groups such as glycerol, pentaerythritol, sorbitol, and sucrose, and EO (ethylene oxide), It can be used by mixing the addition of PO (propylene oxide) or the like. Depending on the type, 1 to 10 types of polyols may be mixed and used, preferably 2 to 8 types, and more preferably 3 to 6 types may be used by mixing.

정포제는 원료의 혼합을 용이하게 하는 역할을 할 수 있으며, 셀 성장과 셀막의 안정화와 폼의 유동성과 제품밀도의 균일함을 위하여 사용할 수 있다. 본 발명의 쑥 추출물 함유 수성 우레탄폼에서 정포제는 폴리올 100 중량부에 대하여 0.1 내지 5 중량부를 사용할 수 있으며, 바람직하게는 0.3 내지 3.0 중량부를 포함할 수 있다. 이러한 정포제가 0.1 중량부 보다 적을 경우, 첨가제 간의 혼합성이 떨어지고 우레탄 폼의 셀이 단단하지 못하여 터질 수 있으며 이로 인해 물성이 저하될 수 있고, 5 중량부 보다 많을 경우 셀 벽이 무너져 물성이 저하될 수 있다.The foaming agent can play a role of facilitating mixing of raw materials, and can be used for cell growth, stabilization of cell membranes, fluidity of foam and uniform product density. In the aqueous urethane foam containing mugwort extract of the present invention, the foaming agent may be used in an amount of 0.1 to 5 parts by weight, and preferably, 0.3 to 3.0 parts by weight, based on 100 parts by weight of polyol. If the foaming agent is less than 0.1 parts by weight, the mixing property between the additives is poor, and the cell of the urethane foam is not hard and may burst, resulting in a decrease in physical properties, and if it is more than 5 parts by weight, the cell wall collapses and the physical properties decrease. I can.

우레탄폼을 제조하는데 있어서 촉매는 발포촉매와 수지화 촉매, 삼량화 촉매로 나뉠 수 있으며, 이러한 촉매를 이소시아네이트 반응과의 속도를 조절하면서 첨가하여 물성에 맞는 폼을 제조할 수 있다. 본 발명에서 촉매는 폴리올 100 중량부에 대하여 0.1 내지 5 중량부를 사용할 수 있으며, 바람직하게는 0.5 내지 3.0 중량부, 더 바람직하게는 1 내지 3 중량부를 포함하여 우레탄폼을 제조할 수 있다. 촉매는 반응속도를 조절할 수 있으며, 스프레이 폼의 특성상 반응속도가 느리면 폼의 형성에 영향을 줄 수 있다. 이러한 촉매가 0.1 중량부 미만으로 포함될 경우 반응속도가 느려질 수 있어 밀도를 높이거나 벽에 분사하였을 시 폼이 흘러내리며 원활한 폼의 생성이 어려울 수 있으며, 5 중량부를 초과하여 포함될 경우 반응속도가 너무 빨라 분사가 시작됨과 동시에 발포가 되어 폼의 형상이 무너질 수 있으며, 시스템 폴리올과 방향족 디이소시사네이트의 혼합이 어려울 수 있다.In preparing urethane foams, catalysts can be divided into foaming catalysts, resinization catalysts, and trimerization catalysts, and these catalysts can be added while controlling the rate of the isocyanate reaction to prepare a foam suitable for physical properties. In the present invention, the catalyst may be 0.1 to 5 parts by weight based on 100 parts by weight of the polyol, preferably 0.5 to 3.0 parts by weight, more preferably 1 to 3 parts by weight to prepare a urethane foam. The catalyst can control the reaction rate, and if the reaction rate is slow due to the nature of the spray foam, it may affect the formation of the foam. If less than 0.1 parts by weight of such a catalyst is included, the reaction rate may be slow, so when the density is increased or sprayed on the wall, the foam flows down and it may be difficult to produce a smooth foam.If it contains more than 5 parts by weight, the reaction rate is too fast. Foaming may occur as soon as spraying begins, and the shape of the foam may collapse, and it may be difficult to mix the system polyol and the aromatic diisocyanate.

또한, 본 발명의 쑥 추출물 함유 수성 우레탄폼에서 촉매는 아민촉매, 금속촉매, 및 삼량화 촉매 중에서 선택된 하나 이상일 수 있다. 아민 촉매로는 TEDA, PC-5, PC-8, PC-9, PC-77, BL-19, DMEA 등이 있으며, 유기금속 촉매로는 반응성을 극대화시킬 수 있는 주석촉매가 있고, 삼량화 촉매로는 TMR-2, TMR-30, PC-41, PC-46, K-15 등이 있다.In addition, in the aqueous urethane foam containing mugwort extract of the present invention, the catalyst may be at least one selected from an amine catalyst, a metal catalyst, and a trimerization catalyst. Amine catalysts include TEDA, PC-5, PC-8, PC-9, PC-77, BL-19, and DMEA, and organometallic catalysts include tin catalysts that can maximize reactivity, and trimerization catalysts Examples include TMR-2, TMR-30, PC-41, PC-46, and K-15.

본 발명의 쑥 추출물 함유 수성 우레탄폼에서 난연제는 할로겐계 난연제, 인계 난연제 또는 무기계 난연제를 사용할 수 있다. 할로겐계 난연제는 근본적으로 기체상에서 발생하는 라디칼을 안정화시켜 난연효과를 가질 수 있으며, 인계 난연제는 연소할 때 인화합물이 열분해에 의하여 폴리메타인산을 생성하고 탈수작용에 의해서 생성되는 탄소피막의 형성이 산소를 차단하여 연소를 막을 수 있다. 무기계 난연제는 표면에서 흡열반응을 통하여 냉각 및 열분해 생성물의 생성을 감소시킬 수 있다. 바람직하게는 인계 난연제를 사용할 수 있으며, Trioctyl phosphate, Dimethyl phosphate, penthaerythritol phosphate, Triphenyl phosphate, Triethyl phosphate, Tris(1-chloro-2-Propyl)phosphate), Tris(2-carboxyethyl)phosphine, Tris 2-chloroethyl phosphate 중에서 선택된 하나 이상일 수 있다. 이러한 난연제는 폴리올 100 중량부에 대하여 5 내지 40 중량부를 사용할 수 있으며, 바람직하게는 5 내지 30 중량부를 포함하여 우레탄폼을 제조할 수 있다. 이러한 난연제가 5 중량부 미만으로 투입될 경우 난연성이 저하될 수 있으며, 40 중량부를 초과하여 투입될 경우 폼 셀의 크기와 셀 벽에 영향을 줌으로써 물성이 떨어지면서 난연성이 함께 저하될 수 있다.In the aqueous urethane foam containing mugwort extract of the present invention, the flame retardant may be a halogen-based flame retardant, a phosphorus-based flame retardant, or an inorganic flame retardant. Halogen-based flame retardants can have a flame-retardant effect by stabilizing radicals generated in the gaseous phase fundamentally, and phosphorus-based flame retardants generate polymetaphosphoric acid by pyrolysis of phosphorus compounds when combusted, and the formation of a carbon film produced by dehydration is difficult. Blocking oxygen can prevent combustion. The inorganic flame retardant can reduce the generation of cooling and pyrolysis products through endothermic reactions on the surface. Preferably, a phosphorus-based flame retardant may be used, and Trioctyl phosphate, Dimethyl phosphate, penthaerythritol phosphate, Triphenyl phosphate, Triethyl phosphate, Tris(1-chloro-2-Propyl)phosphate), Tris(2-carboxyethyl)phosphine, Tris 2-chloroethyl It may be one or more selected from phosphate. These flame retardants may be used in an amount of 5 to 40 parts by weight based on 100 parts by weight of polyol, and preferably 5 to 30 parts by weight to prepare a urethane foam. If the flame retardant is added in an amount of less than 5 parts by weight, flame retardancy may be deteriorated, and if it is added in an amount exceeding 40 parts by weight, it affects the size of the foam cell and the cell wall, thereby deteriorating the physical properties and lowering the flame retardancy.

본 발명에서 쑥 추출물은 어떤 것이든 한정하지 않고 사용할 수 있으나, 바람직하게는 물, 에탄올, 및 메탄올로 이루어진 군으로부터 선택된 하나 이상의 용매로 추출한 것일 수 있으며, 쑥속(Artemisia)에 속하는 약쑥, 사재발쑥, 모기태쑥 등의 쌍떡잎식물 초롱꽃목 국화과의 여러해살이풀을 추출한 것일 수 있다. 더욱 바람직하게 쑥 추출물은 물 또는 메탄올을 용매로 하여 추출한 것일 수 있으며, 물과 메탄올을 함께 사용하여 추출한 것일 수 있다.In the present invention, the mugwort extract may be used without any limitation, but preferably, it may be extracted with one or more solvents selected from the group consisting of water, ethanol, and methanol, and wormwood belonging to the Artemisia genus, Mugwort, mosquito It may be an extract of the perennial plant of the Asteraceae family of dicotyledons, such as tarex. More preferably, the mugwort extract may be extracted using water or methanol as a solvent, and may be extracted using water and methanol together.

이러한 쑥 추출물은 본 발명의 수성 우레탄폼을 제조하는데 있어서, 발포제로서 사용될 수 있으며, 폴리올 100 중량부에 대하여 0.1 내지 20 중량부를 사용할 수 있으며, 바람직하게는 2 내지 15 중량부를 포함하여 우레탄폼을 제조할 수 있다. 이러한 쑥 추출물이 0.1 중량부 미만으로 포함될 경우 폼의 밀도를 맞추기가 어려우며, 20 중량부를 초과하여 포함될 경우 셀 내부에서 가스가 터져 나오면서 셀이 무너질 수 있다.Such mugwort extract may be used as a foaming agent in preparing the aqueous urethane foam of the present invention, and 0.1 to 20 parts by weight may be used based on 100 parts by weight of polyol, and preferably 2 to 15 parts by weight to prepare a urethane foam. can do. If the mugwort extract is contained in an amount of less than 0.1 parts by weight, it is difficult to match the density of the foam, and if it is included in an amount exceeding 20 parts by weight, gas may burst out of the cell and the cell may collapse.

본 발명의 쑥 추출물 함유 수성 우레탄폼에서 시스템 폴리올과 방향족 디이소시아네이트의 중량비는 1 : 0.5 - 3.0일 수 있으며, 바람직하게는 1 : 1 - 1.5일 수 있으며, 방향족 디이소시아네이트는 바람직하게 메틸렌 디페닐 디이소시아네이트(MDI, Methylene Diphenyl Diisocyanate)일 수 있다. 이러한 시스템 폴리올과 방향족 디이소시아네이트의 중량비가 1 : 0.5 - 3.0의 범위를 벗어나 포함될 경우, 폼이 경화되지 않거나 폼이 부러지거나 불안정(brittle)해질 수 있다.In the aqueous urethane foam containing mugwort extract of the present invention, the weight ratio of the system polyol and the aromatic diisocyanate may be 1: 0.5-3.0, preferably 1: 1-1.5, and the aromatic diisocyanate is preferably methylene diphenyl diisocyanate. It may be an isocyanate (MDI, Methylene Diphenyl Diisocyanate). If the weight ratio of the system polyol and the aromatic diisocyanate is included outside the range of 1: 0.5-3.0, the foam may not be cured or the foam may be broken or brittle.

다른 측면에 따르면, 본 발명은 쑥을 추출하여 쑥 추출물을 형성하는 제 1 단계; 상기 쑥 추출물과 폴리올, 정포제, 촉매, 및 난연제를 혼합하여 시스템 폴리올을 형성하는 제 2 단계; 및 상기 시스템 폴리올과 방향족 디이소시아네이트를 반응시키는 제 3 단계;를 포함하는 것을 특징으로 하는 쑥 추출물 함유 수성 우레탄폼의 제조방법을 제공한다.According to another aspect, the present invention comprises a first step of extracting mugwort to form a mugwort extract; A second step of forming a system polyol by mixing the mugwort extract and a polyol, a foam stabilizer, a catalyst, and a flame retardant; And a third step of reacting the system polyol with an aromatic diisocyanate; it provides a method for producing an aqueous urethane foam containing mugwort extract.

쑥 추출물을 형성하는 제 1 단계는 반응기에 쑥, 물, 및 메탄올을 투입하고 온도를 올려 추출하는 과정 및 추출 후 메탄올을 증류시키고 쑥 고상 찌꺼기를 분리하기 위하여 필터를 사용하여 필터시키는 과정을 포함할 수 있으며, 보다 상세하게는 쑥 100 중량부에 대하여 물 100내지 500 중량부 및 메탄올 50 내지 300 중량부를 투입하고 온도를 약 60℃로 하여 쑥을 추출하고 투입된 메탄올 및 고상의 슬러지(찌꺼기)를 필터시키는 과정을 포함할 수 있다. 이때 메탄올이 휘발되는 것을방지하기 위하여 반응기에 콘덴서를 연결하여 지속적으로 환류될 수 있도록 하여 쑥을 추출할 수 있으며, 슬러지를 필터시키는 과정에서 메탄올을 제거할 수 있다.The first step of forming the mugwort extract includes a process of adding mugwort, water, and methanol to the reactor and raising the temperature for extraction, and the process of distilling methanol after extraction and filtering using a filter to separate the mugwort solid residue. In more detail, 100 to 500 parts by weight of water and 50 to 300 parts by weight of methanol are added to 100 parts by weight of mugwort, and the mugwort is extracted at a temperature of about 60°C, and the methanol and solid sludge (debris) are filtered. It may include a process of ordering. At this time, in order to prevent volatilization of methanol, a condenser can be connected to the reactor so that it can be continuously refluxed to extract mugwort, and methanol can be removed in the process of filtering the sludge.

메탄올은 1가 알코올로 방향족 디이소시아네이트인 메틸렌 디페닐 디이소시아네이트(MDI, Methylene Diphenyl Diisocyanate)와 반응하여 우레탄폼의 물성을 저하시키기 때문에 쑥 추출 이후 제거해주어야 하며, 원활한 제거를 위해 먼저 고상 슬러지를 필터를 통해 분리한다. 필터의 크기는 200mesh 이하의 것을 사용하며 이는 미세 찌꺼기로 인하여 스프레이 폼의 기기에 노즐을 막을 수 있기 때문에 미세한 필터지를 이용하여 필터한다. 필터한 액은 반응기에 다시 투입하여 메탄올의 비점 이상의 온도로 올려 제거하며 반응기는 밀폐 반응기를 사용하여 다른 부분으로 메탄올이 손실되지 않도록 해야한다.Methanol is a monohydric alcohol that reacts with methylene diphenyl diisocyanate (MDI), an aromatic diisocyanate, and degrades the properties of the urethane foam, so it must be removed after extraction of mugwort. For smooth removal, filter the solid sludge first. Separate through. The filter size is less than 200 mesh, which can block the nozzle in the spray foam device due to fine debris, so it is filtered using fine filter paper. The filtered liquid is re-introduced to the reactor and removed by raising it to a temperature above the boiling point of methanol, and the reactor must use a closed reactor to prevent loss of methanol to other parts.

본 발명의 쑥 추출물 함유 수성 우레탄폼의 제조방법에서 쑥 100 중량부에 대하여 물은 150-400 중량부일 수 있고, 바람직하게는 200-400 중량부일 수 있으며, 메탄올은 100-250 중량부일 수 있고, 바람직하게는 100-200 중량부일 수 있다.In the method for producing an aqueous urethane foam containing mugwort extract of the present invention, water may be 150-400 parts by weight, preferably 200-400 parts by weight, and methanol may be 100-250 parts by weight, based on 100 parts by weight of mugwort, Preferably it may be 100-200 parts by weight.

시스템 폴리올을 형성하는 제 2 단계는 밀폐 반응기에 폴리올 100 중량부에 대하여 난연제 5 내지 40 중량부, 촉매 0.1 내지 5 중량부, 정포제 0.1 내지 5 중량부, 및 쑥 추출물 0.1 내지 20 중량부를 투입하고 혼합하는 과정을 포함할 수 있다. 시스템 폴리올은 폴리올, 촉매, 정포제, 난연제, 발포제로 구성되어 있으며, 이는 필요시에 각 성분을 단일 또는 여러종을 혼합하여 사용이 가능하다. 본 발명에서는 발포제로서 쑥 추출물을 사용할 수 있다.In the second step of forming the system polyol, 5 to 40 parts by weight of a flame retardant, 0.1 to 5 parts by weight of a catalyst, 0.1 to 5 parts by weight of a foaming agent, and 0.1 to 20 parts by weight of a mugwort extract are added to the closed reactor, and It may include a process of mixing. The system polyol is composed of a polyol, a catalyst, a foaming agent, a flame retardant, and a blowing agent, and it is possible to use a single component or a mixture of several types of each component when necessary. In the present invention, mugwort extract can be used as a foaming agent.

시스템 폴리올과 방향족 디이소시아네이트를 반응시키는 제 3 단계는 30 내지 90 ℃의 온도에서 이루어질 수 있다. 수발포 우레탄폼은 물리적 발포제를 사용하였을 때 보다 점도가 높은 편이며, 이 때문에 액상의 온도를 30 내지 90℃, 바람직하게는 40 내지 80℃로 히팅하여 최종적으로 우레탄폼을 제조할 수 있다. 또한, 상기 제 2 단계에서 형성된 시스템 폴리올은 스프레이 폼 장치에 투입할 수 있으며, 여기에 방향족 디이소시아네이트를 첨가하여 수발포 경질 스프레이 폼을 제조할 수 있다.The third step of reacting the system polyol and the aromatic diisocyanate may be performed at a temperature of 30 to 90°C. The water-foamed urethane foam tends to have a higher viscosity than when a physical foaming agent is used, and for this reason, the temperature of the liquid phase is heated to 30 to 90°C, preferably 40 to 80°C, thereby finally producing a urethane foam. In addition, the system polyol formed in the second step may be introduced into a spray foam device, and an aromatic diisocyanate may be added thereto to prepare a water-foaming rigid spray foam.

시스템 폴리올과 방향족 디이소시아네이트의 중량비는 1 : 0.5 - 3.0일 수 있으며, 바람직하게는 1 : 1 - 1.5일 수 있으며, 방향족 디이소시아네이트는 바람직하게 메틸렌 디페닐 디이소시아네이트(MDI, Methylene Diphenyl Diisocyanate)일 수 있다. 이러한 시스템 폴리올과 방향족 디이소시아네이트의 중량비가 1 : 0.5 - 3.0의 범위를 벗어나 포함될 경우, 폼이 경화되지 않거나 폼이 부러지거나 불안정(brittle)해질 수 있다.The weight ratio of the system polyol and the aromatic diisocyanate may be 1: 0.5-3.0, preferably 1: 1-1.5, and the aromatic diisocyanate may be preferably methylene diphenyl diisocyanate (MDI, Methylene Diphenyl Diisocyanate). have. If the weight ratio of the system polyol and the aromatic diisocyanate is included outside the range of 1: 0.5-3.0, the foam may not be cured or the foam may be broken or brittle.

하기 실시예에 의하여 본 발명을 더욱 상세하게 설명하고자 한다. 단 하기 실시예는 본 발명을 예시하기 위한 것으로 본 발명의 범위가 실시예에 의해 한정되는 것은 아니다. 본 발명의 개시가 완전하도록 하며, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이다.The present invention will be described in more detail by the following examples. However, the following examples are intended to illustrate the present invention, and the scope of the present invention is not limited by the examples. The disclosure of the present invention is provided to be complete, and to fully inform the scope of the invention to those of ordinary skill in the art to which the present invention pertains.

<실시예><Example>

실시예 1 - 쑥 추출물 함유 수성 우레탄폼 제조Example 1-Preparation of aqueous urethane foam containing mugwort extract

반응기에 쑥 100 중량부에 물 400g, 메탄올 200g을 투입하고 콘덴서를 연결한 후 온도 60℃로 6시간을 반응시켰다. 이후 고상 슬러지를 제거하기 위하여 200mesh 필터에 필터링을 진행하였으며, 액상은 밀폐 반응기에 투입하고 온도를 70℃로 올려 메탄올을 제거하였다. 시스템 폴리올을 제조하기 위하여 반응기를 준비하여 수신기가 560 mgKOH/g(Glycerol+Sucrose 개시), 430 mgKOH/g(Glycerol 개시), 350 mgKOH/g (sorbitol 개시)인 폴리올을 각각 40g, 30g, 30g을 투입하였으며, 정포제는 evonik사의 B-8455를 0.8g, 촉매로는 TEDA(in DPG), 및 BL-19를 1g씩 투입 하고, 난연제로는 Tris 2-chloroethyl phosphate를 5g 투입하였으며, 쑥 추출물을 10g 투입한 후 30℃의 온도에서 약 3시간 동안 혼합하였다. 이렇게 완성된 시스템 폴리올과 MDI를 각각 통(스프레이 기기)에 투입하여 온도를 70℃로 셋팅하고 비율은 1:1.2로 분사하여 우레탄폼을 제조하였다.400 g of water and 200 g of methanol were added to 100 parts by weight of mugwort in the reactor, and a condenser was connected, followed by reaction at a temperature of 60° C. for 6 hours. Thereafter, filtering was performed on a 200 mesh filter to remove solid sludge, and the liquid phase was introduced into a closed reactor and the temperature was raised to 70°C to remove methanol. To prepare a system polyol, a reactor was prepared, and the receiver prepared a polyol of 560 mgKOH/g (initiated Glycerol + Sucrose), 430 mgKOH/g (initiated Glycerol), and 350 mgKOH/g (initiated sorbitol), respectively. 0.8g of evonik's B-8455 was added as a foaming agent, 1g of TEDA (in DPG), and 1g of BL-19 were added as a catalyst, and 5g of Tris 2-chloroethyl phosphate was added as a flame retardant. After 10g was added, the mixture was mixed for about 3 hours at a temperature of 30°C. The thus-completed system polyol and MDI were added to each barrel (spray machine), the temperature was set at 70°C, and the ratio was sprayed at 1:1.2 to prepare urethane foam.

실시예 2 - 쑥 추출물 함유 수성 우레탄폼 제조Example 2-Preparation of aqueous urethane foam containing mugwort extract

반응기에 쑥 100 중량부에 물 400g, 메탄올 200g을 투입하고 콘덴서를 연결한 후 온도 60℃로 6시간을 반응시켰다. 이후 고상 슬러지를 제거하기 위하여 200mesh 필터에 필터링을 진행하였으며, 액상은 밀폐 반응기에 투입하고 온도를 70℃로 올려 메탄올을 제거하였다. 시스템 폴리올을 제조하기 위하여 반응기를 준비하여 수신기가 560 mgKOH/g(Glycerol+Sucrose 개시), 430 mgKOH/g(Glycerol 개시), 350 mgKOH/g (sorbitol 개시)인 폴리올을 각각 40g, 30g, 30g을 투입하였으며, 정포제는 evonik사의 B-8455를 0.8g, 촉매로는 TEDA(in DPG), 및 BL-19를 1g씩 투입 하고, 난연제로는 Tris 2-chloroethyl phosphate를 5g 투입하였으며, 쑥 추출물을 15g 투입한 후 30℃의 온도에서 약 3시간 동안 혼합하였다. 이렇게 완성된 시스템 폴리올과 MDI를 각각 통(스프레이 기기)에 투입하여 온도를 70℃로 셋팅하고 비율은 1:1.2로 분사하여 우레탄폼을 제조하였다.400 g of water and 200 g of methanol were added to 100 parts by weight of mugwort in the reactor, and a condenser was connected, followed by reaction at a temperature of 60° C. for 6 hours. Thereafter, filtering was performed on a 200 mesh filter to remove solid sludge, and the liquid phase was introduced into a closed reactor and the temperature was raised to 70°C to remove methanol. To prepare a system polyol, a reactor was prepared, and the receiver prepared a polyol of 560 mgKOH/g (initiated Glycerol + Sucrose), 430 mgKOH/g (initiated Glycerol), and 350 mgKOH/g (initiated sorbitol), respectively. 0.8g of evonik's B-8455 was added as a foaming agent, 1g of TEDA (in DPG), and 1g of BL-19 were added as a catalyst, and 5g of Tris 2-chloroethyl phosphate was added as a flame retardant. After 15g was added, the mixture was mixed for about 3 hours at a temperature of 30°C. The thus-completed system polyol and MDI were added to each barrel (spray machine), the temperature was set at 70°C, and the ratio was sprayed at 1:1.2 to prepare urethane foam.

비교예 1 - 수성 우레탄폼 제조Comparative Example 1-Preparation of aqueous urethane foam

쑥 추출물이 포함된 물 대신 일반 증류수를 사용한 것을 제외하고는 상기 실시예 2와 동일한 방법으로 재생폴리올을 제조하였다.A regenerated polyol was prepared in the same manner as in Example 2, except that ordinary distilled water was used instead of water containing the mugwort extract.

<실험예><Experimental Example>

실험예 1 - 물성 분석 시험Experimental Example 1-Physical Property Analysis Test

상기 실시예 및 비교예에 따른 우레탄폼의 밀도와 치수안정성을 확인하기 위하여 각각의 우레탄폼을 동일한 크기로 잘라 부피와 질량을 확인하고 밀도를 측정하였으며, 수축여부를 확인하기 위하여 하루가 지난 후 밀도를 재측정하였다.In order to check the density and dimensional stability of the urethane foams according to the above Examples and Comparative Examples, each urethane foam was cut into the same size to check the volume and mass, and the density was measured. Was measured again.

실험예 2 - 액 안정성 시험Experimental Example 2-Liquid stability test

상기 실시예 및 비교예에 따른 시스템 폴리올의 액 안정성을 확인하기 위하여 각각의 우레탄폼의 제조 후 층 분리 및 분산 정도를 육안으로 관찰하였다.In order to confirm the liquid stability of the system polyols according to the above Examples and Comparative Examples, the degree of separation and dispersion of layers after each urethane foam was prepared was observed with the naked eye.

실험예 3 - VOC 확인 시험Experimental Example 3-VOC confirmation test

상기 실시예 2 및 비교예에 따른 우레탄폼의 VOC 발생량을 확인하기 위하여 각각의 우레탄폼에 대하여 MS300-57 분석을 실시하였다.MS300-57 analysis was performed on each urethane foam to confirm the amount of VOC generated in the urethane foam according to Example 2 and Comparative Example.

<평가 및 결과> <Evaluation and results>

결과 1 - 우레탄폼 물성 분석Result 1-Analysis of urethane foam properties

상기 실시예 및 비교예에 따른 우레탄폼의 밀도와 치수안정성을 확인하여 하기 표 1에 나타내었다.The density and dimensional stability of the urethane foam according to the Examples and Comparative Examples were confirmed, and are shown in Table 1 below.

그 결과, 상기 실시예 1 및 2에 따른 우레탄폼에서는 하루가 지난 후에도 처음과 밀도가 동일하였으나 비교예에서는 밀도가 증가한 것으로 나타났으며, 이는 수축에 의한 것임을 알 수 있었다. 따라서 쑥 추출물을 적용한 실시예 1 및 2의 우레탄폼은 셀이 안정화되면서 폼의 치수안정성이 확보될 수 있음을 확인할 수 있었다.As a result, in the urethane foams according to Examples 1 and 2, the density was the same as that of the beginning even after one day passed, but in the comparative example, the density was found to increase, which was found to be due to shrinkage. Therefore, it was confirmed that the urethane foam of Examples 1 and 2 to which the mugwort extract was applied can secure the dimensional stability of the foam while the cell is stabilized.

밀도(kg/mDensity (kg/m 33 )) 1day 후 밀도(kg/mDensity after 1 day (kg/m 33 )) 실시예 1Example 1 3636 3636 실시예 2Example 2 2222 2222 비교예Comparative example 2323 2626

결과 2 - 액 안정성 확인Result 2-liquid stability check

상기 실시예 및 비교예에 따른 시스템 폴리올의 액 안정성을 확인하여 하기 표 2에 나타내었다.The liquid stability of the system polyols according to the Examples and Comparative Examples was confirmed and shown in Table 2 below.

그 결과, 실시예 1 및 2에 따른 시스템 폴리올에서는 쑥 추출물이 계면활성제의 역할을 함에 따라 층 분리이 없이 전체적으로 액이 분산되어 있음을 확인할 수 있었다. 물이 증가함에도 물만이 아니라 쑥이 추출된 쑥 추출물이 증대되기 때문에 이 또한 분산이 잘 되는 것을 확인할 수 있었다. 반면, 비교예의 시스템 폴리올은 수발포 특성상 물이 많음으로 인해 친유성에 가까운 물질은 침전되는 것으로 나타났다.As a result, in the system polyols according to Examples 1 and 2, it was confirmed that the solution was dispersed as a whole without layer separation as the mugwort extract served as a surfactant. It was confirmed that even when the water was increased, not only the water but also the mugwort extract from which the mugwort was extracted increased, so that it was also well dispersed. On the other hand, the system polyol of the comparative example was found to precipitate a material close to lipophilicity due to the large amount of water due to water-foaming properties.

불순물(슬러지) 상태Impurity (sludge) state 실시예 1Example 1 분산Dispersion 실시예 2Example 2 분산Dispersion 비교예Comparative example 침전Sedimentation

결과 3 - VOC 확인Result 3-VOC confirmation

상기 실시예 2 및 비교예에 따른 우레탄폼의 VOC 발생량을 확인하여 하기 표 3에 나타내었다. 그 결과, 실시예 2에 따른 쑥 추출물을 이용한 우레탄폼의 T-VOC가 감소함을 확인할 수 있다.The VOC generation amount of the urethane foam according to Example 2 and Comparative Example was confirmed and shown in Table 3 below. As a result, it can be seen that the T-VOC of the urethane foam using the mugwort extract according to Example 2 is reduced.

T-VOC 발생량(μg/mT-VOC generation amount (μg/m 33 )) 실시예 2Example 2 2,5002,500 비교예Comparative example 5,7005,700

Claims (9)

폴리올 100 중량부에 대하여, 정포제 0.1 내지 5 중량부, 촉매 0.1 내지 5 중량부, 난연제 5 내지 40 중량부, 및 쑥 추출물 0.1 내지 20 중량부를 포함하는 시스템 폴리올; 및
방향족 디이소시아네이트(aromatic diisocyanate)을 포함하되,
상기 시스템 폴리올과 방향족 디이소시아네이트의 중량비는 1 : 0.5 - 3.0인 것을 특징으로 하는 쑥 추출물 함유 수성 우레탄폼.
System polyol comprising 0.1 to 5 parts by weight of a foaming agent, 0.1 to 5 parts by weight of a catalyst, 5 to 40 parts by weight of a flame retardant, and 0.1 to 20 parts by weight of a mugwort extract based on 100 parts by weight of the polyol; And
Including aromatic diisocyanate (aromatic diisocyanate),
The water-based urethane foam containing mugwort extract, characterized in that the weight ratio of the system polyol and the aromatic diisocyanate is 1: 0.5-3.0.
제 1 항에 있어서,
상기 폴리올은 1 내지 10종의 폴리올을 혼합하는 것을 특징으로 하는 쑥 추출물 함유 수성 우레탄폼.
The method of claim 1,
The polyol is an aqueous urethane foam containing mugwort extract, characterized in that mixing 1 to 10 polyols.
제 1 항에 있어서,
상기 촉매는 아민촉매, 금속촉매, 및 삼량화 촉매 중에서 선택된 하나 이상인 것을 특징으로 하는 쑥 추출물 함유 수성 우레탄폼.
The method of claim 1,
The catalyst is an aqueous urethane foam containing mugwort extract, characterized in that at least one selected from an amine catalyst, a metal catalyst, and a trimerization catalyst.
제 1 항에 있어서,
상기 쑥 추출물은 물, 에탄올, 및 메탄올로 이루어진 군으로부터 선택된 하나 이상의 용매로 추출하는 것을 특징으로 하는 쑥 추출물 함유 수성 우레탄폼.
The method of claim 1,
The mugwort extract is an aqueous urethane foam containing mugwort extract, characterized in that extracted with one or more solvents selected from the group consisting of water, ethanol, and methanol.
제 1 항에 있어서,
상기 방향족 디이소시아네이트는 메틸렌 디페닐 디이소시아네이트(MDI, Methylene Diphenyl Diisocyanate)인 것을 특징으로 하는 쑥 추출물 함유 수성 우레탄폼.
The method of claim 1,
The aromatic diisocyanate is a water-based urethane foam containing mugwort extract, characterized in that methylene diphenyl diisocyanate (MDI, Methylene Diphenyl Diisocyanate).
쑥을 추출하여 쑥 추출물을 형성하는 제 1 단계;
상기 쑥 추출물과 폴리올, 정포제, 촉매, 및 난연제를 혼합하여 시스템 폴리올을 형성하는 제 2 단계; 및
상기 시스템 폴리올과 방향족 디이소시아네이트를 반응시키는 제 3 단계;를 포함하는 것을 특징으로 하는 쑥 추출물 함유 수성 우레탄폼의 제조방법.
A first step of extracting the mugwort to form a mugwort extract;
A second step of forming a system polyol by mixing the mugwort extract and a polyol, a foam stabilizer, a catalyst, and a flame retardant; And
A method for producing an aqueous urethane foam containing mugwort extract comprising a; a third step of reacting the system polyol with an aromatic diisocyanate.
제 6 항에 있어서,
상기 제 1 단계는 쑥을 추출하여 형성된 고상의 슬러지를 제거하는 과정을 포함하는 것을 특징으로 하는 쑥 추출물 함유 수성 우레탄폼의 제조방법.
The method of claim 6,
The first step is a method for producing an aqueous urethane foam containing mugwort extract, characterized in that it comprises a process of removing the solid sludge formed by extracting the mugwort.
제 6 항에 있어서,
상기 제 3 단계는 30 내지 90 ℃의 온도에서 이루어지는 것을 특징으로 하는 쑥 추출물 함유 수성 우레탄폼의 제조방법.
The method of claim 6,
The third step is a method of producing an aqueous urethane foam containing mugwort extract, characterized in that made at a temperature of 30 to 90 ℃.
제 1 항 내지 제 5 항 중 어느 한 항에 따른 수성 우레탄폼을 포함하는 단열재.Insulation material comprising the water-based urethane foam according to any one of claims 1 to 5.
KR1020190087456A 2019-07-19 2019-07-19 Aqueous urethane foam containing mugwort extract and its preparation method KR20210010064A (en)