KR20200057606A - Waterproof sheet with excellent radon blocking effect - Google Patents
Waterproof sheet with excellent radon blocking effect Download PDFInfo
- Publication number
- KR20200057606A KR20200057606A KR1020190102968A KR20190102968A KR20200057606A KR 20200057606 A KR20200057606 A KR 20200057606A KR 1020190102968 A KR1020190102968 A KR 1020190102968A KR 20190102968 A KR20190102968 A KR 20190102968A KR 20200057606 A KR20200057606 A KR 20200057606A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- layer
- styrene
- waterproof sheet
- Prior art date
Abstract
Description
본 발명은 라돈 차단 효과가 우수한 방수시트에 관한 것이다.The present invention relates to a waterproof sheet having an excellent radon blocking effect.
최근 도시 생태계 및 도시 환경을 개선하기 위하여 건물의 옥상녹화 또는 실내정원을 조성하는 사업을 많이 하고 있는데, 이는 옥상녹화 및 실내정원을 가꾸는 것은 토양 생태계의 복원, 냉난방 에너지 절약, 도시 열섬화 현상 완화, 도시 홍수 예방, 공기 정화, 수질 정화, 소음 경감, 도시 경관 향상, 건축물의 내구성 향상 등 환경적 측면과 경제적 측면 등에서 여러 가지 이점이 있기 때문이다.Recently, in order to improve the urban ecosystem and urban environment, many projects have been done to create rooftop greening or indoor gardening of buildings, which is to restore rooftop greening and indoor gardening, restore soil ecosystems, save energy in heating and cooling, and mitigate urban heat islanding. This is because it has several advantages in environmental and economical aspects such as flood prevention, air purification, water purification, noise reduction, urban landscape improvement, and building durability improvement.
그러나, 이와 같은 옥상녹화의 많은 이점에도 불구하고 옥상녹화가 활성화되지 못하고 있는 이유 중 하나는 식물의 뿌리가 바닥면으로 침투하면서 방수층의 파손으로 건축물의 방수에 문제가 발생한다는 것이다. 즉, 옥상 또는 실내에 심은 식물의 뿌리가 방수시트를 뚫고 들어가서 그 하부에 있는 방수층까지 파손시켜 방수에 문제가 발생하는 것이 큰 문제이다.However, in spite of the many advantages of rooftop greening, one of the reasons why rooftop greening is not activated is that the root of the plant penetrates to the bottom surface, causing damage to the waterproofing of the building due to the breakage of the waterproofing layer. That is, it is a big problem that the roots of plants planted on the rooftop or indoors penetrate through the waterproof sheet and break down to the waterproof layer at the bottom, thereby causing a problem in waterproofing.
상기와 같은 문제를 해결하기 위하여 많은 연구 개발이 시행되는 중이며 하기 특허문헌1인 "방수시트와 방수시트를 이용한 복합방수, 복합방수 구조의 시공방법"(등록특허 제 10-0872127 호)과 같이 방수 및 방수를 위한 복합시트가 발명되었으나 시간이 지남에 따라 시트의 겹침부에 생기는 틈새 또는 방수시트의 접합부에서 들뜸이나 박리현상이 일어고 식물 뿌리가 그러한 틈새나 접합부 사이로 침투하여 여전히 방수 및 방수층이 훼손되는 문제가 발생하고 있다.In order to solve the above problems, many research and development are being carried out, and waterproofing as in Patent Document 1, "Compound waterproofing using waterproof sheet and waterproof sheet, construction method of complex waterproof structure" (Registration Patent No. 10-0872127) And a composite sheet for waterproofing has been invented, but over time, a gap or delamination occurs at the junction of the sheet or the junction of the waterproof sheet, and the plant roots penetrate between such crevices or junctions, and the waterproof and waterproof layer are still damaged. Is becoming a problem.
한편, 라돈은 자연방사능 물질로 지구상 어디에나 존재하는 무색, 무취, 무미의 기체이다. 세계보건기구(WHO)는 전 세계 폐암발생의 3~14%가 라돈에 기인하는 것으로 평가했으며, 폐암 발병 주요 원인 물질로 규정하고 있다.On the other hand, radon is a natural radioactive material, and is a colorless, odorless, tasteless gas that exists everywhere on the planet. The World Health Organization (WHO) estimates that 3 to 14% of the world's lung cancer is caused by radon, and is defined as a major cause of lung cancer.
본 발명은 방수용 도막재 및 투명한 필름을 적층하여 라돈 차단 효과가 우수한 방수시트를 제공하는 것을 목적으로 한다.An object of the present invention is to provide a waterproof sheet having an excellent radon blocking effect by laminating a waterproof coating material and a transparent film.
한편, 본 발명에서 이루고자 하는 기술적 과제들은 이상에서 언급한 기술적 과제들로 제한되지 않으며, 언급하지 않은 또 다른 기술적 과제들은 아래의 기재로부터 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 명확하게 이해될 수 있을 것이다.On the other hand, the technical problems to be achieved in the present invention are not limited to the technical problems mentioned above, and other technical problems not mentioned are clearly understood by a person having ordinary knowledge in the technical field to which the present invention belongs from the following description. Will be understandable.
본 발명에 따른 라돈차단 효과가 우수한 방수시트는 이형필름; 상기 이형필름에 적층되는 도막재층; 및 상기 도막재층에 적층되는 투명 필름층; 을 포함하고, 상기 도막재층은, 수산화 알루미늄을 건조시켜 얻은 알루미늄 분말 100 중량부에 대해 아스팔트 64 내지 110 중량부, 스틸렌 부타디엔 스틸렌 고무 0.92 내지 3.8 중량부, 감광수지 30 내지 50 중량부, 증점 안정화제 2.4 내지 5 중량부, 경화촉진제 1.6 내지 2 중량부, 폴리프로필렌 섬유 0.3 내지 0.44 중량부, 실리카메탈 0.24 내지 0.36 중량부, 돌로마이트 3 내지 4.6 중량부, 탄산칼슘 70 내지 90 중량부 및 충진재 70 내지 120 중량부를 포함한다.A waterproof sheet having an excellent radon blocking effect according to the present invention includes a release film; A coating material layer laminated on the release film; And a transparent film layer laminated on the coating material layer. Containing, and the coating layer, 64 to 110 parts by weight of asphalt, based on 100 parts by weight of aluminum powder obtained by drying aluminum hydroxide, styrene butadiene styrene rubber 0.92 to 3.8 parts by weight, photosensitive resin 30 to 50 parts by weight, thickening stabilizer 2.4 to 5 parts by weight, curing accelerator 1.6 to 2 parts by weight, polypropylene fiber 0.3 to 0.44 parts by weight, silica metal 0.24 to 0.36 parts by weight, dolomite 3 to 4.6 parts by weight, calcium carbonate 70 to 90 parts by weight, and filler 70 to 120 parts Includes parts by weight.
상기 투명 필름층은, 폴리에틸렌테레프탈레이트(PET), 폴리에틸렌 나프탈레이트(PEN) 및 폴리부틸렌테레프탈레이트(PBT)를 포함하는 폴리에스테르계 수지, 폴리프로필렌(PP) 및 폴리스티렌(PS)를 포함하는 폴리올레핀계 수지, 나일론-6 및 나일론-66를 포함하는 폴리아미드(PA), 폴리카보네이트(PC), 폴리아크릴로니트릴(PAN), 폴리이미드(PI), 코팅된 폴리에틸렌테레프탈레이트(PVA-PET, PVDC-PET, EVOH-PET), 에틸렌비닐알코올(EVOH) 및 폴리염화비니리덴(PVDC) 중 적어도 하나를 포함하는 투명한 필름; 을 포함할 수 있다.The transparent film layer is a polyolefin comprising a polyester resin, polypropylene (PP) and polystyrene (PS), including polyethylene terephthalate (PET), polyethylene naphthalate (PEN) and polybutylene terephthalate (PBT). Polyamide (PA), polycarbonate (PC), polyacrylonitrile (PAN), polyimide (PI), coated polyethylene terephthalate (PVA-PET, PVDC) including nylon resin and nylon-6 and nylon-66 -PET, EVOH-PET), a transparent film comprising at least one of ethylene vinyl alcohol (EVOH) and polyvinylidene chloride (PVDC); It may include.
상기 도막재층은, 상기 이형필름에 적층되고, 구리 분말을 포함하는 점착층, 상기 점착층에 적층되는 중심재층, 상기 중심재층에 적층되고, 수산화 알루미늄을 건조시켜 얻은 알루미늄 분말 100 중량부에 대해 아스팔트 64 내지 110 중량부, 스틸렌 부타디엔 스틸렌 고무 0.92 내지 3.8 중량부, 감광수지 30 내지 50 중량부, 증점 안정화제 2.4 내지 5 중량부, 경화촉진제 1.6 내지 2 중량부, 폴리프로필렌 섬유 0.3 내지 0.44 중량부, 실리카메탈 0.24 내지 0.36 중량부, 돌로마이트 3 내지 4.6 중량부, 탄산칼슘 70 내지 90 중량부 및 충진재 70 내지 120 중량부를 포함하는 방수층 및 상기 방수층에 적층되는 강도보강층을 포함할 수 있다.The coating material layer is laminated on the release film, an adhesive layer comprising copper powder, a core material layer laminated on the pressure sensitive adhesive layer, and a core material layer laminated on the core material layer, the aluminum hydroxide obtained by drying aluminum hydroxide 100 parts by weight of asphalt 64 to 110 parts by weight, styrene butadiene styrene rubber 0.92 to 3.8 parts by weight, photosensitive resin 30 to 50 parts by weight, thickening stabilizer 2.4 to 5 parts by weight, curing accelerator 1.6 to 2 parts by weight, polypropylene fiber 0.3 to 0.44 parts by weight, It may include a waterproof layer comprising 0.24 to 0.36 parts by weight of silica metal, 3 to 4.6 parts by weight of dolomite, 70 to 90 parts by weight of calcium carbonate and 70 to 120 parts by weight of a filler, and a strength reinforcement layer laminated on the waterproof layer.
상기 방수층은 알루미늄 분말 100 중량부에 대해 흡착제 10 내지 60 중량부를 더 포함할 수 있다.The waterproof layer may further include 10 to 60 parts by weight of the adsorbent relative to 100 parts by weight of the aluminum powder.
상기 흡착제는 활성탄 및 제올라이트 중에서 선택되는 1종 이상인 것을 특징으로 할 수 있다.The adsorbent may be characterized by at least one selected from activated carbon and zeolite.
상기 점착층은, 프로세스 오일, 개질재, 접착력 보강제, 내열성 보강제, 상용화제 및 구리 분말을 포함하는 점착 조성물로 제조되고, 상기 개질재는, SBS(Styrene-Butadiene-Styrene), SIS(Styrene-Isoprene-Styrene), SB(StyreneButadiene), SBR(Styrene- Butadiene Rubber), SEBS(Styrene ethylene butadiene styrene) 및 EVA(Ethylene vinyl acetate)로 이루어진 그룹에서 선택된 적어도 어느 하나일 수 있다.The adhesive layer is made of an adhesive composition comprising a process oil, a modifier, an adhesion reinforcing agent, a heat resistant reinforcing agent, a compatibilizer, and a copper powder, and the modifier is Styrene-Butadiene-Styrene (SBS), Styrene-Isoprene-SIS (SIS) Styrene), SB (StyreneButadiene), SBR (Styrene-Butadiene Rubber), SEBS (Styrene ethylene butadiene styrene) and EVA (Ethylene vinyl acetate) may be at least one selected from the group consisting of.
상기 중심재층은, 폴리에틸렌(PE) 직포, 폴리프로필렌(PP) 직포, 폴리프로필렌(PP) 부직포, 고밀도 폴리에틸렌(HDPE) 직포, 고밀도 폴리에틸렌(HDPE) 부직포 및 폴리에스터 부직포로 이루어진 그룹에서 선택된 적어도 어느 하나일 수 있다.The core material layer is at least one selected from the group consisting of polyethylene (PE) woven fabric, polypropylene (PP) woven fabric, polypropylene (PP) nonwoven fabric, high density polyethylene (HDPE) woven fabric, high density polyethylene (HDPE) nonwoven fabric, and polyester nonwoven fabric. Can be
본 발명의 실시예에 따르면, 구조물의 표면을 코팅하여 근본적으로 오염물질이 방출되는 것을 방지하는 기술로 라돈 차폐 및 방수기능을 동시에 구현 가능하며, 라돈 기준치가 초과되는 국내 주택의 환경개선으로 거주자의 폐암 발생률을 저감하여 삶의 질을 향상시킬 수 있다.According to an embodiment of the present invention, a radon shielding and waterproofing function can be implemented simultaneously by coating a surface of a structure to fundamentally prevent the release of contaminants, and by improving the environment of a domestic house that exceeds a radon standard, residents It is possible to improve the quality of life by reducing the incidence of lung cancer.
한편, 본 발명에서 얻을 수 있는 효과는 이상에서 언급한 효과들로 제한되지 않으며, 언급하지 않은 또 다른 효과들은 아래의 기재로부터 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 명확하게 이해될 수 있을 것이다.On the other hand, the effects that can be obtained in the present invention are not limited to the above-mentioned effects, and other effects that are not mentioned will be clearly understood by those skilled in the art from the following description. Will be able to.
이하, 본 발명의 실시 예를 첨부된 도면들을 참조하여 더욱 상세하게 설명한다. 본 발명의 실시 예는 여러 가지 형태로 변형할 수 있으며, 본 발명의 범위가 아래의 실시 예들로 한정되는 것으로 해석되어서는 안 된다. 본 실시 예는 당업계에서 평균적인 지식을 가진 자에게 본 발명을 더욱 완전하게 설명하기 위해 제공되는 것이다. 따라서 도면에서의 요소의 형상은 보다 명확한 설명을 강조하기 위해 과장되었다.Hereinafter, embodiments of the present invention will be described in more detail with reference to the accompanying drawings. The embodiments of the present invention can be modified in various forms, and the scope of the present invention should not be interpreted as being limited to the following embodiments. This embodiment is provided to more fully describe the present invention to those skilled in the art. Therefore, the shape of the elements in the drawings has been exaggerated to emphasize a clearer explanation.
본 발명이 해결하고자 하는 과제의 해결 방안을 명확하게 하기 위한 발명의 구성을 본 발명의 바람직한 실시 예에 근거하여 첨부 도면을 참조하여 상세히 설명하되, 도면의 구성요소들에 참조번호를 부여함에 있어서 동일 구성요소에 대해서는 비록 다른 도면상에 있더라도 동일 참조번호를 부여하였으며 당해 도면에 대한 설명 시 필요한 경우 다른 도면의 구성요소를 인용할 수 있음을 미리 밝혀둔다.The configuration of the invention for clarifying the solution to the problem to be solved by the present invention will be described in detail with reference to the accompanying drawings based on preferred embodiments of the present invention, but the same is used in assigning reference numbers to components of the drawings. The same reference numbers are assigned to the components even though they are on other drawings, and it is revealed in advance that components of other drawings may be cited when necessary for the description of the drawings.
본 발명의 일 실시예에 따른 라돈 차단 효과가 우수한 방수시트는 상기 이형필름에 적층되는 도막재층; 및 상기 도막재층에 적층되는 투명 필름층; 을 포함하고, 상기 도막재층은, 수산화 알루미늄을 건조시켜 얻은 알루미늄 분말 100 중량부에 대해 아스팔트 64 내지 110 중량부, 스틸렌 부타디엔 스틸렌 고무 0.92 내지 3.8 중량부, 감광수지 30 내지 50 중량부, 증점 안정화제 2.4 내지 5 중량부, 경화촉진제 1.6 내지 2 중량부, 폴리프로필렌 섬유 0.3 내지 0.44 중량부, 실리카메탈 0.24 내지 0.36 중량부, 돌로마이트 3 내지 4.6 중량부, 탄산칼슘 70 내지 90 중량부 및 충진재 70 내지 120 중량부를 포함할 수 있다.A waterproof sheet having excellent radon blocking effect according to an embodiment of the present invention includes a coating material layer laminated on the release film; And a transparent film layer laminated on the coating material layer. Containing, and the coating layer, 64 to 110 parts by weight of asphalt, based on 100 parts by weight of aluminum powder obtained by drying aluminum hydroxide, styrene butadiene styrene rubber 0.92 to 3.8 parts by weight, photosensitive resin 30 to 50 parts by weight, thickening stabilizer 2.4 to 5 parts by weight, curing accelerator 1.6 to 2 parts by weight, polypropylene fiber 0.3 to 0.44 parts by weight, silica metal 0.24 to 0.36 parts by weight, dolomite 3 to 4.6 parts by weight, calcium carbonate 70 to 90 parts by weight, and filler 70 to 120 parts It may include parts by weight.
또한, 도막재층은, 상기 이형필름에 적층되고, 구리 분말을 포함하는 점착층; 상기 점착층에 적층되는 중심재층; 상기 중심재층에 적층되는 방수층; 상기 방수층에 적층되는 강도보강층; 을 포함한다. In addition, the coating material layer is laminated on the release film, an adhesive layer containing copper powder; A core material layer laminated on the adhesive layer; A waterproof layer laminated on the core material layer; A strength reinforcement layer laminated on the waterproof layer; It includes.
이형필름은 점착층을 보호하는 것으로서 폴리프로필렌(PE) 필름, 실리콘(Silicon) 필름, 이피디엠 에틸렌 프로필렌 다이엔 모노머(EPDM ethylene propylene diene Monomer, M-class)필름 등 다양한 이형필름을 사용할 수 있다.As the release film to protect the adhesive layer, various release films such as polypropylene (PE) film, silicone film, EPDM ethylene propylene diene Monomer (M-class) film can be used.
점착층은 이형필름의 상부에 적층되고, 방수층으로 기능함과 동시에 구리 분말을 포함하고 있어 방근 효과도 발휘할 수 있는 것으로서, 이형필름이 제거된 후, 시공장소에 부착될 수 있다. 점착층은 프로세스 오일, 개질재, 접착력 보강제, 내열성 보강제, 상용화제 및 구리 분말을 포함하는 점착 조성물로 제조될 수 있다.The adhesive layer is laminated on the top of the release film, and functions as a waterproofing layer and also contains copper powder, so that the effect of rooting can also be exhibited. After the release film is removed, it can be attached to a factory. The adhesive layer can be made of an adhesive composition comprising a process oil, a modifier, an adhesion reinforcing agent, a heat resistant reinforcing agent, a compatibilizer and a copper powder.
프로세스 오일은 석유계, 석탄계, 식물성계 오일 모두를 사용할 수 있으며, 석유계 및 석탄계 오일로는 아로마틱계, 나프텐계, 파라핀계 등을 사용할 수 있고 식물성 오일로는 아마인유, 대두유, 린씨드 오일, 미강유 등을 이용할 수 있으며 위에서 명시한 프로세스 오일 중에 선택된 1종 또는 2종 이상이 사용될 수 있다.Process oil can be petroleum-based, coal-based, or vegetable-based oils. Aromatic-based, naphthenic-based, and paraffin-based oils can be used as petroleum-based and coal-based oils. Flaxseed oil, soybean oil, linseed oil, Rice bran oil or the like may be used, and one or two or more selected from the process oils specified above may be used.
프로세스 오일은 점착 조성물 전체 100 중량%에 대해서 40~60 중량% 포함되는 것이 바람직하다. 프로세스 오일이 40 중량% 미만이면 방수층의 점도가 너무 높아져 시공성이 불편해지고 유동성이 떨어지게 되며, 60 중량%를 초과하면 점도가 낮아지고 다른 성분들의 효과가 떨어져 제품의 물성을 충분히 확보할 수 없고 내열 흐름 안정성 및 접착력 또한 약해져 방수재로서의 사용이 어렵기 때문이다.The process oil is preferably included 40 to 60% by weight relative to the total 100% by weight of the adhesive composition. If the process oil is less than 40% by weight, the viscosity of the waterproof layer becomes too high, resulting in inconvenient workability and poor fluidity. If it exceeds 60% by weight, the viscosity is lowered and the effects of other components fall, so that the physical properties of the product cannot be sufficiently secured and heat-resistant flow This is because stability and adhesion are also weak, making it difficult to use as a waterproofing material.
개질재는 고무, 열가소성 엘라스토머 또는 이들의 혼합물이 사용될 수 있으며, 구체적으로, SBS(Styrene-Butadiene-Styrene), SIS(Styrene-isoprene-Styrene), SB(StyreneButadiene), SBR(Styrene-Butadiene Rubber), SEBS(Styrene ethylene butadiene styrene), EVA(Ethylene vinyl acetate), APP 등을 단독 또는 2종 이상 혼합하여 사용할 수 있다.As the modifier, rubber, a thermoplastic elastomer, or a mixture thereof may be used. Specifically, Styrene-Butadiene-Styrene (SBS), Styrene-isoprene-Styrene (SIS), StyreneButadiene (SB), Styrene-Butadiene Rubber (SBR), SEBS (Styrene ethylene butadiene styrene), EVA (Ethylene vinyl acetate), APP, etc. can be used alone or in combination of two or more.
개질재는 점착 조성물 전체 100 중량%에 대해서 5~15 중량% 포함되는 것이 바람직하다. 개질재의 함량이 5 중량% 미만이면, 탄성 및 내구성, 내유동성을 충분히 발휘하지 못하게 되고, 15 중량%를 초과하면 전체적인 방수층의 점도가 높아져 시공성의 불편함을 야기하고, 단가 상승의 결과를 불러 일으켜 결과적으로 제품 경쟁력이 떨어지는 결과를 가져오게 된다.The modifier is preferably included 5 to 15% by weight relative to the total 100% by weight of the adhesive composition. When the content of the modifier is less than 5% by weight, elasticity, durability, and fluid resistance are not sufficiently exhibited, and when it exceeds 15% by weight, the viscosity of the entire waterproof layer is increased, causing discomfort in workability, and causing a result of cost increase. As a result, product competitiveness is degraded.
접착력 보강제는 점착층의 접착력을 보강하면서 인장강도 및 도막강도를 증가시키기 위한 것으로, 석유수지(C5, C9, C5-C9 공중합, 수첨계), 천연수지(로진 에스테르), 쿠마론 수지, 폴리부텐 중 선택된 1종 또는 2종 이상의 것이 사용될 수 있다. 접착력 보강제는 점착 조성물 전체 100 중량%에 대해서 20~40 중량% 포함되는 것이 바람직하다. 20 중량% 미만인 경우, 피착면 및 중심재층과의 접착력이 떨어지게 되어 방수시공 하자의 원인이 될 수 있고, 40 중량%를 초과하면 강도가 높아 고온에서 물성이 딱딱해지고 탄성이 낮아져서 점착층이 뚝뚝 끊어지며 크랙이 발생하는 등의 문제점이 생기게 된다.The adhesion reinforcing agent is intended to increase the tensile strength and coating film strength while reinforcing the adhesive strength of the adhesive layer, petroleum resin (C5, C9, C5-C9 copolymerization, hydrogenation system), natural resin (rosin ester), coumarone resin, polybutene One or two or more selected from the above may be used. It is preferable that the adhesive strength reinforcing agent is included in an amount of 20 to 40% by weight based on 100% by weight of the entire adhesive composition. If the content is less than 20% by weight, the adhesion between the adherend and the core material layer may drop, which may cause a defect in waterproof construction. If the content exceeds 40% by weight, the strength is high and the physical properties become hard at high temperatures and the elasticity decreases, causing the adhesive layer to break. This causes problems such as cracking.
내열성 보강제는 점착층의 내열성을 향상시키기 위한 것으로서, 파라핀 왁스, 아마이드 왁스, 폴리프로필렌 왁스, 폴리에틸렌 왁스, 산화 왁스, 천연 왁스 등을 단독 또는 2종 이상 혼합하여 사용할 수 있다. 내열성 보강제는 점착 조성물 전체 100 중량%에 대해서 5~10 중량% 포함되는 것이 바람직하다. 5 중량% 미만인 경우, 내열성 보강제로서의 기능을 발휘할 수 없으며, 10 중량%를 초과하면 제품 표면에 막이 형성되어 피착면과의 접착 및 점착 성능이 저하되는 결과를 초래하게 된다.The heat-resistant reinforcing agent is for improving the heat resistance of the adhesive layer, and may be used alone or in combination of two or more of paraffin wax, amide wax, polypropylene wax, polyethylene wax, oxide wax, and natural wax. The heat-resistant reinforcing agent is preferably included in 5 to 10% by weight based on 100% by weight of the total adhesive composition. If it is less than 5% by weight, it cannot exhibit the function as a heat-resistant reinforcement, and if it exceeds 10% by weight, a film is formed on the surface of the product, resulting in deterioration of adhesion and adhesion performance with the adherend.
상용화제는 점착층 내의 물질 결합을 원활하게 이루어지게 하여 점착층의 강도를 증진시키는 역할을 한다. 상용화제는 산(acid)계 물질 등 공지의 상용화제를 사용할 수 있고, 점착 조성물 전체 100 중량%에 대해서 0.1~3 중량% 포함되는 것이 바람직하다. 0.1 중량% 미만이면, 물질간의 가교 역할로서의 성능을 발휘할 수 없으며, 3 중량% 초과하면 원가가 상승하게 되는 요인이 된다.The compatibilizer serves to enhance the strength of the adhesive layer by smoothly bonding the substances in the adhesive layer. As the compatibilizer, a known compatibilizer such as an acid-based material may be used, and it is preferable that 0.1 to 3 wt% is included with respect to 100 wt% of the total pressure-sensitive adhesive composition. If it is less than 0.1% by weight, the performance as a crosslinking role between materials cannot be exhibited, and if it exceeds 3% by weight, the cost increases.
구리 분말은 뿌리 분열 조직의 생육을 제어할 수 있어 점착층에 방근 효과를 부여할 수 있다. 방근 효과를 위하여 구리층을 하나의 독립된 층으로 적층할 수도 있으나, 본 발명과 같이 구리 분말 형태로 첨가하는 것이 바람직하다. 즉, 구리층을 외부에 적층하면, 파손 또는 부식되거나 복합시트로부터 이탈(떼어짐)할 수 있고, 이 경우 복합시트가 방근 효과를 전혀 발휘할 수 없게 되므로, 구리 분말을 점착층 내부에 첨가하는 것이 방근 효과 발휘 측면에서 바람직하다. 구리 분말은 점착 조성물 전체 100 중량%에 대해서 1~3 중량% 포함되는 것이 바람직하다. 1 중량% 미만이면, 방근 효과를 달성하기 힘들고, 3 중량%를 초과하면, 점착 조성물 전체의 조성비에 변화를 가져와 점착 조성물의 분산성 등을 떨어뜨려 점착층의 기계적 물성을 저하시킬 우려가 있다.The copper powder can control the growth of the root-split tissue, thereby providing a rooting effect to the adhesive layer. For the rooting effect, the copper layer may be stacked as one independent layer, but it is preferable to add it in the form of copper powder as in the present invention. That is, if the copper layer is laminated on the outside, it may be damaged or corroded or detached (separated) from the composite sheet, and in this case, it is impossible to add the copper powder to the inside of the adhesive layer because the composite sheet cannot exert a rooting effect at all. It is preferable from the standpoint of exerting a rooting effect. The copper powder is preferably included in 1 to 3% by weight relative to the total 100% by weight of the adhesive composition. If it is less than 1% by weight, it is difficult to achieve a rooting effect, and if it exceeds 3% by weight, the composition ratio of the entire pressure-sensitive adhesive composition is changed, and the dispersibility and the like of the pressure-sensitive adhesive composition are lowered, thereby deteriorating the mechanical properties of the pressure-sensitive adhesive layer.
중심재층은 점착층의 상부에 적층되고, 복합시트의 내구성과 재료의 결집력을 높이기 위한 것으로, 폴리에틸렌(PE) 직포, 폴리프로필렌(PP) 직포, 폴리프로필렌(PP) 부직포, 고밀도 폴리에틸렌(HDPE) 직포, 고밀도 폴리에틸렌(HDPE) 부직포 및 폴리에스터 부직포로 이루어진 그룹에서 선택된 적어도 어느 하나를 사용할 수 있다.The core material layer is laminated on the top of the adhesive layer, and is intended to increase the durability of the composite sheet and the binding power of the material. Polyethylene (PE) woven fabric, polypropylene (PP) woven fabric, polypropylene (PP) nonwoven fabric, high density polyethylene (HDPE) woven fabric , At least one selected from the group consisting of high-density polyethylene (HDPE) non-woven fabric and polyester non-woven fabric can be used.
여기서, 방수층은 중심재층에 적층되고, 수산화 알루미늄을 건조시켜 얻은 알루미늄 분말 100 중량부에 대해 아스팔트 64 내지 110 중량부, 스틸렌 부타디엔 스틸렌 고무 0.92 내지 3.8 중량부, 감광수지 30 내지 50 중량부, 증점 안정화제 2.4 내지 5 중량부, 경화촉진제 1.6 내지 2 중량부, 폴리프로필렌 섬유 0.3 내지 0.44 중량부, 실리카메탈 0.24 내지 0.36 중량부, 돌로마이트 3 내지 4.6 중량부, 탄산칼슘 70 내지 90 중량부 및 충진재 70 내지 120 중량부를 포함할 수 있다.Here, the waterproof layer is laminated on the core material layer, 64 to 110 parts by weight of asphalt, 1002 parts by weight of styrene butadiene styrene rubber, 0.92 to 3.8 parts by weight of styrene rubber, 30 to 50 parts by weight of photosensitive resin, and thickening stability 2.4 to 5 parts by weight of the agent, 1.6 to 2 parts by weight of the curing accelerator, 0.3 to 0.44 parts by weight of polypropylene fiber, 0.24 to 0.36 parts by weight of silica metal, 3 to 4.6 parts by weight of dolomite, 70 to 90 parts by weight of calcium carbonate and 70 to 70 parts by weight of filler It may include 120 parts by weight.
또한, 방수층은 알루미늄 분말 100 중량부에 대해 흡착제 10 내지 60 중량부를 더 포함할 수 있다.In addition, the waterproof layer may further include 10 to 60 parts by weight of the adsorbent relative to 100 parts by weight of the aluminum powder.
흡착제는 탈크, 탄산칼슘, 펜질, 흄드 실리카 중에서 선택되는 1종 이상으로 포함될 수 있다. The adsorbent may be included in at least one selected from talc, calcium carbonate, fensil, and fumed silica.
또한, 방수층은 중심재층의 상부에 적층되고, 에스비에스(SBS, Styrene-Butadiene-Styrene) 컴파운드와 구리 분말을 혼합하여 제조할 수 있는 것으로, 시트의 신축성을 향상시키고 내투수성의 효율을 증진시키는 용도로 사용된다. SBS 컴파운드는 리니어 타입의 SBS(Linear Type SBS) 또는 레이디얼 타입의 SBS(Radial Type SBS) 등을 사용할 수 있다. 구리 분말은 전술한 점착층에서와 마찬가지로, 방근 효과를 발휘하기 위해 사용될 수 있다.In addition, the waterproof layer is laminated on top of the core material layer, and can be prepared by mixing SBS (Styrene-Butadiene-Styrene) compound and copper powder, and improves the elasticity of the sheet and improves the water permeability efficiency. Is used. The SBS compound may use a linear type SBS (linear type SBS) or a radial type SBS (radial type SBS). Copper powder can be used to exert a rooting effect, as in the above-mentioned adhesive layer.
강도보강층은 방수층의 상부에 적층되어 강도를 보강하는 용도로 사용되는 것으로서, 알루미늄층을 사용할 수 있다. 구체적으로, 강도보강층은 복합시트의 파단을 방지하고 복합시트의 인장강도 및 저항성을 증가시킨다. 또한, 계절 변화 등의 온도 변화에 따른 복합시트의 수축율 변화를 방지할 수 있다.The strength reinforcing layer is stacked on top of the waterproof layer and used for reinforcing the strength, and an aluminum layer can be used. Specifically, the strength reinforcement layer prevents the fracture of the composite sheet and increases the tensile strength and resistance of the composite sheet. In addition, it is possible to prevent the change in shrinkage of the composite sheet due to temperature changes such as seasonal changes.
일 실시예에 있어서, 강도보강층은 알루미늄에 구리를 첨가하여 제조한 알루미늄합금층을 사용할 수도 있다. 강도보강층으로 구리를 포함하는 알루미늄합금층을 사용하면, 구리를 포함하는 층을 3단계로 구축(강도보강층, 방수층, 점착층)할 수 있게 되어 구리에 의한 우수한 방근 효과를 달성할 수 있을 뿐만 아니라 알루미늄에 훨씬 강도를 높여 복합시트를 보호할 수 있는 효과도 가질 수 있다. 알루미늄에 구리를 첨가한 알루미늄합금은 고온(500~510
또한, 알루미늄합금은 복합시트의 시공 장소 등에 따라 일부 물성에 변화를 주기 위하여 소량의 마그네슘 등을 더 첨가할 수도 있다. 즉, 알루미늄합금 전체 100 중량%에 대해서 마그네슘 0.5~2.5 중량%를 더 포함하면 강도가 더욱 개선된 알루미늄합금을 제조할 수 있다.In addition, a small amount of magnesium or the like may be further added to the aluminum alloy in order to change some properties according to the construction site of the composite sheet. That is, when 0.5 to 2.5% by weight of magnesium is further included with respect to 100% by weight of the entire aluminum alloy, an aluminum alloy with improved strength can be manufactured.
투명 필름층은 강도보강층의 상부에 적층되는 것으로, 폴리에틸렌테레프탈레이트(PET), 폴리에틸렌(PE), 고밀도 폴리에틸렌(HDPE), 선형 저밀도 폴리에틸렌(LLDPE), 에틸렌 비닐 아세테이트(EVA), 폴리염화비닐(PVC) 및 올레핀계 열가소성 엘라스토머(TPO)로 이루어진 그룹에서 선택된 적어도 어느 하나를 사용할 수 있다.The transparent film layer is laminated on top of the strength reinforcement layer, polyethylene terephthalate (PET), polyethylene (PE), high density polyethylene (HDPE), linear low density polyethylene (LLDPE), ethylene vinyl acetate (EVA), polyvinyl chloride (PVC) ) And olefin-based thermoplastic elastomers (TPO).
다음으로, 라돈 차단 효과가 우수한 방수시트 제조방법에 대해 설명한다. 이를 설명하는 데 있어 설명의 편의를 위하여 상술한 라돈 차단 효과가 우수한 방수시트를 예로 들어 설명하나, 이에 국한되는 것은 아니다. 또한, 상술하여 중복된 부분에 대해서는 그 설명을 생략하도록 한다.Next, a method of manufacturing a waterproof sheet having an excellent radon blocking effect will be described. For convenience of explanation, a waterproof sheet having an excellent radon blocking effect is described as an example, but the present invention is not limited thereto. In addition, the description of the overlapped portion will be omitted.
도 2는 본 발명의 일 실시예에 따른 라돈 차단 효과가 우수한 방수시트 제조방법을 개략적으로 나타낸 순서도이다. 도 2를 참조하여 설명하면, 본 발명의 일 실시예에 따른 라돈 차단 효과가 우수한 방수시트 제조방법은 이형필름에 구리 분말을 포함하는 점착층을 적층하는 제1단계; 상기 점착층에 중심재층을 적층하는 제2단계; 상기 중심재층에 구리 분말을 포함하는 방수층을 적층하는 제3단계; 상기 방수층에 강도보강층을 적층하는 제4단계; 및 상기 강도보강층에 투명 필름층을 적층하는 제5단계;를 포함한다. 이 건2 is a flowchart schematically showing a method of manufacturing a waterproof sheet having excellent radon blocking effect according to an embodiment of the present invention. Referring to Figure 2, a method for manufacturing a waterproof sheet having excellent radon blocking effect according to an embodiment of the present invention comprises a first step of laminating an adhesive layer containing copper powder on a release film; A second step of laminating a core material layer on the adhesive layer; A third step of laminating a waterproof layer containing copper powder on the core material layer; A fourth step of stacking a strength reinforcement layer on the waterproof layer; And a fifth step of laminating a transparent film layer on the strength reinforcement layer. This
발명은 물(빗물, 지하수 등)에 의한 침투를 효과적으로 차단할 수 있을 뿐만 아니라 구리 분말을 포함하는 방수층과 점착층을 구비하여 인공녹화시 식재되는 식물의 뿌리가 활착하는 것을 방지할 수 있어 구조물이 파손되는 현상을 방지할 수 있는 효과를 가진다.The invention not only can effectively prevent penetration by water (rainwater, groundwater, etc.), but also has a waterproof layer and an adhesive layer containing copper powder to prevent the roots of plants planted during artificial recording from breaking down, so the structure is damaged. It has the effect of preventing the phenomenon.
제1단계는 이형필름에 구리 분말을 포함하는 점착층을 형성하는 단계로, 점착층은 프로세스 오일에 개질재를 투입하여 용해시키는 제1-1단계, 개질재가 용해된 프로세스 오일에 접착력 보강제, 내열성 보강제 및 구리 분말을 투입하여 용해 및 분산시켜 분산물을 제조하는 제1-2단계, 상기 분산물에 상용화제를 투입하여 용해 및 분산시키는 제1-3단계 및 상용화제가 분산된 분산물을 이형필름에 코팅하는 제1-4단계를 포함할 수 있다. 구체적으로, 140~200
이때, 이형필름에 분산물을 코팅하는 제1-4단계는 슬롯 분사 방식, 스프레이 방식, 롤러 코팅 방식 및 커튼-플로우 코팅방식 중 적어도 어느 하나의 방식에 의하여 수행될 수 있다.At this time, steps 1-4 of coating the dispersion on the release film may be performed by at least one of a slot spray method, a spray method, a roller coating method and a curtain-flow coating method.
슬롯 분사 방식은 기어펌프, 핫 멜트 호스, 슬롯 헤드, 슬롯 노즐, 서플라이와 컨트롤 시스템 등으로 구성된 특수 기계 장비를 이용하는 것이다. 이 방식은 기어펌프를 이용 화합물을 핫 멜트 호스로 이동시킨 후 슬롯 헤드에 모인 화합물을 파워 서플라이와 컨트롤 시스템으로 조정한 후 슬롯 노즐에 의해 분사, 도포하는 방식이다.The slot injection method uses special mechanical equipment consisting of a gear pump, hot melt hose, slot head, slot nozzle, supply and control system. This method uses a gear pump to move the compound to a hot melt hose, adjusts the compound collected in the slot head with a power supply and a control system, and then sprays and applies it with a slot nozzle.
서플라이와 컨트롤 시스템은 피도물의 커버리지와 품질을 최적화하기 위한 세팅 값과 변수를 조절할 수 있으며, 이때 슬롯 노즐과 이형필름과의 거리는 100㎛ 이하로 도포면과 접촉되는 방법으로 코팅된다. 슬롯 분사 방식은 균일한 도포가 가능함은 물론 분사 중에 손실이 발생되지 않는다.The supply and control system can adjust setting values and parameters for optimizing the coverage and quality of the object to be coated. At this time, the distance between the slot nozzle and the release film is 100 μm or less, and is coated by contacting the coated surface. The slot spraying method allows uniform application and does not cause loss during spraying.
스프레이 방식은 가장 널리 알려진 코팅방법의 하나로서 그 구성은 대표적으로 부쓰(BOOTH), 스프레이(Spray) 노즐, 에어 호스, 에어트랜스, 콤프레셔 등으로 이루어져 있다. 히팅기에 의해 저점도로 낮춰진 물질은 압송탱크나 펌프 등의 압력공급 장치를 통해 스프레이 노즐로 공급된 후 고압력 콤프레셔를 이용 각 각의 노즐 팁의 작은 구멍으로 분사시켜 코팅하는 방법이다. 압력조절장치를 이용하여 패턴 크기나 분사속도를 조절할 수 있어 오버스프레이(Overspray)를 최소화할 수 있으며 코팅 속도가 빨라 생산성 향상이 높아지고 균일 도포가 가능하여 도착효율이 높은 장점이 있다.The spray method is one of the most widely known coating methods, and its composition is typically composed of a booth, a spray nozzle, an air hose, an air transformer, and a compressor. The material, which has been lowered to a low viscosity by the heater, is supplied to a spray nozzle through a pressure supply device such as a pressure tank or pump, and then sprayed through a small hole in each nozzle tip using a high pressure compressor to coat it. The pattern size or spray speed can be adjusted using a pressure control device to minimize overspray, and the coating speed is fast, resulting in higher productivity and uniform application, resulting in high arrival efficiency.
롤러 코팅 방식은 롤러(Roller) 사이로 시트가 이동하여 코팅되는 방법으로 편평한 판에 적합한 코팅 방법이며 화합물이 2개의 롤러(Roller) 사이에 놓아져 회전에 의해 롤러(Roller)에 도장되고 그 내용물질이 이형필름에 부착된다. 이때 이형필름의 속도나 물질의 점도 및 롤러(Roller)와 이형필름의 간격에 따라 도막의 두께가 두꺼워지거나 얇아진다. 이 방식의 장점은 물질의 낭비가 적고 코팅속도가 빠른 것이다.The roller coating method is a method in which a sheet is moved and coated between rollers, which is a suitable coating method for flat plates, and a compound is placed between two rollers to be coated on a roller by rotation and its contents It is attached to the release film. At this time, the thickness of the coating film is thickened or thinned according to the speed of the release film or the viscosity of the material and the distance between the roller and the release film. The advantage of this method is that less material is wasted and the coating speed is fast.
커튼-플로우 코팅(Curtain-Flow Coating) 방식의 구성은 콘베어, 가압밸브, 펌프, 필터, 탱크 등으로 이루어져 있다. 가압시킨 물질을 일정한 폭의 엷은 필름형태로 슬릿 상태의 틈새를 통해 여러 개의 노즐에서 커튼 모양으로 끊임없이 위쪽에서 흘러내리게 하여 그 아래 콘베이어(Conveyor)로 피도체가 통과하도록 함으로써 코팅한다.The curtain-flow coating method consists of a conveyor, a pressure valve, a pump, a filter, and a tank. The pressurized material is coated by continuously flowing from the top of the curtain in the form of a thin film of a certain width through a slit-like gap, and passing through the object with a conveyor below it.
피도물에 부착되면서 흘러내린 잔량 물질은 모두 회수되어 자동적으로 용기에서 펌프헤드(Pump Head)로 순환 사용된다. 이 방식의 장점은 재료의 손실이 대단히 적고 코팅 속도가 빠르며 도장막의 두께가 균일하다는 것이다.Any remaining material that has flowed down as it adheres to the object is recovered and automatically recycled from the container to the pump head. The advantages of this method are that the material loss is very small, the coating speed is fast, and the thickness of the coating film is uniform.
제2단계 내지 제5단계는 상술한 중심재층, 구리 분말을 포함하는 방수층, 강도보강층 및 투명 필름층을 이형필름에 코팅된 점착층에 순차적으로 적층하는 단계이다.Steps 2 to 5 are steps of sequentially laminating the above-described core material layer, a waterproof layer including copper powder, a strength reinforcing layer, and a transparent film layer on an adhesive layer coated on a release film.
이상의 상세한 설명은 본 발명을 예시하는 것이다. 또한 전술한 내용은 본 발명의 바람직한 실시 형태를 나타내어 설명하는 것이며, 본 발명은 다양한 다른 조합, 변경 및 환경에서 사용할 수 있다. 즉 본 명세서에 개시된 발명의 개념의 범위, 저술한 개시 내용과 균등한 범위 및/또는 당업계의 기술 또는 지식의 범위내에서 변경 또는 수정이 가능하다. 저술한 실시예는 본 발명의 기술적 사상을 구현하기 위한 최선의 상태를 설명하는 것이며, 본 발명의 구체적인 적용 분야 및 용도에서 요구되는 다양한 변경도 가능하다. 따라서 이상의 발명의 상세한 설명은 개시된 실시 상태로 본 발명을 제한하려는 의도가 아니다. 또한 첨부된 청구범위는 다른 실시 상태도 포함하는 것으로 해석되어야 한다.The above detailed description is to illustrate the present invention. In addition, the above-described content is to describe and describe preferred embodiments of the present invention, and the present invention can be used in various other combinations, modifications and environments. That is, it is possible to change or modify the scope of the concept of the invention disclosed herein, the scope equivalent to the disclosed contents, and / or the scope of the art or knowledge in the art. The embodiments described describe the best conditions for implementing the technical spirit of the present invention, and various changes required in specific application fields and uses of the present invention are possible. Therefore, the detailed description of the above invention is not intended to limit the present invention to the disclosed embodiments. In addition, the appended claims should be construed to include other embodiments.
Claims (6)
상기 이형필름에 적층되는 도막재층; 및
상기 도막재층에 적층되는 투명 필름층; 을 포함하고,
상기 도막재층은,
수산화 알루미늄을 건조시켜 얻은 알루미늄 분말 100 중량부에 대해 아스팔트 64 내지 110 중량부, 스틸렌 부타디엔 스틸렌 고무 0.92 내지 3.8 중량부, 감광수지 30 내지 50 중량부, 증점 안정화제 2.4 내지 5 중량부, 경화촉진제 1.6 내지 2 중량부, 폴리프로필렌 섬유 0.3 내지 0.44 중량부, 실리카메탈 0.24 내지 0.36 중량부, 돌로마이트 3 내지 4.6 중량부, 탄산칼슘 70 내지 90 중량부 및 충진재 70 내지 120 중량부를 포함하는 라돈 차단 효과가 우수한 방수시트.
Release film;
A coating material layer laminated on the release film; And
A transparent film layer laminated on the coating layer; Including,
The coating layer,
64 to 110 parts by weight of asphalt relative to 100 parts by weight of aluminum powder obtained by drying aluminum hydroxide, 0.92 to 3.8 parts by weight of styrene butadiene styrene rubber, 30 to 50 parts by weight of photosensitive resin, 2.4 to 5 parts by weight of thickening stabilizer, and curing accelerator 1.6 Excellent radon blocking effect including 2 to 2 parts by weight, 0.3 to 0.44 parts by weight of polypropylene fiber, 0.24 to 0.36 parts by weight of silica metal, 3 to 4.6 parts by weight of dolomite, 70 to 90 parts by weight of calcium carbonate and 70 to 120 parts by weight of filler Waterproof sheet.
상기 투명 필름층은,
폴리에틸렌테레프탈레이트(PET), 폴리에틸렌 나프탈레이트(PEN) 및 폴리부틸렌테레프탈레이트(PBT)를 포함하는 폴리에스테르계 수지, 폴리프로필렌(PP) 및 폴리스티렌(PS)를 포함하는 폴리올레핀계 수지, 나일론-6 및 나일론-66를 포함하는 폴리아미드(PA), 폴리카보네이트(PC), 폴리아크릴로니트릴(PAN), 폴리이미드(PI), 코팅된 폴리에틸렌테레프탈레이트(PVA-PET, PVDC-PET, EVOH-PET), 에틸렌비닐알코올(EVOH) 및 폴리염화비니리덴(PVDC) 중 적어도 하나를 포함하는 투명한 필름; 을 포함하는 라돈 차단 효과가 우수한 방수시트.
According to claim 1,
The transparent film layer,
Polyester resins including polyethylene terephthalate (PET), polyethylene naphthalate (PEN) and polybutylene terephthalate (PBT), polyolefin resins including polypropylene (PP) and polystyrene (PS), nylon-6 And polyamide (PA), polycarbonate (PC), polyacrylonitrile (PAN), polyimide (PI), and coated polyethylene terephthalate (PVA-PET, PVDC-PET, EVOH-PET) including nylon-66. ), A transparent film comprising at least one of ethylene vinyl alcohol (EVOH) and polyvinylidene chloride (PVDC); A waterproof sheet having an excellent radon blocking effect.
상기 도막재층은,
상기 이형필름에 적층되고, 구리 분말을 포함하는 점착층,
상기 점착층에 적층되는 중심재층,
상기 중심재층에 적층되고, 수산화 알루미늄을 건조시켜 얻은 알루미늄 분말 100 중량부에 대해 아스팔트 64 내지 110 중량부, 스틸렌 부타디엔 스틸렌 고무 0.92 내지 3.8 중량부, 감광수지 30 내지 50 중량부, 증점 안정화제 2.4 내지 5 중량부, 경화촉진제 1.6 내지 2 중량부, 폴리프로필렌 섬유 0.3 내지 0.44 중량부, 실리카메탈 0.24 내지 0.36 중량부, 돌로마이트 3 내지 4.6 중량부, 탄산칼슘 70 내지 90 중량부 및 충진재 70 내지 120 중량부를 포함하는 방수층 및
상기 방수층에 적층되는 강도보강층을 포함하는 라돈 차단 효과가 우수한 방수시트.
According to claim 2,
The coating layer,
An adhesive layer laminated on the release film and comprising copper powder,
The core material layer laminated on the adhesive layer,
Laminated on the core material layer, 64 to 110 parts by weight of asphalt relative to 100 parts by weight of aluminum powder obtained by drying aluminum hydroxide, 0.92 to 3.8 parts by weight of styrene butadiene styrene rubber, 30 to 50 parts by weight of photosensitive resin, and 2.4 to thickening agent 5 parts by weight, curing accelerator 1.6 to 2 parts by weight, polypropylene fiber 0.3 to 0.44 parts by weight, silica metal 0.24 to 0.36 parts by weight, dolomite 3 to 4.6 parts by weight, calcium carbonate 70 to 90 parts by weight, and filler 70 to 120 parts by weight Waterproof layer comprising and
A waterproof sheet having an excellent radon blocking effect including a strength reinforcement layer laminated on the waterproof layer.
상기 방수층은
알루미늄 분말 100 중량부에 대해 흡착제 10 내지 60 중량부를 더 포함하는 라돈 차단 효과가 우수한 방수시트.
According to claim 3,
The waterproof layer
A waterproof sheet having an excellent radon blocking effect further comprising 10 to 60 parts by weight of the adsorbent relative to 100 parts by weight of the aluminum powder.
상기 흡착제는 활성탄 및 제올라이트 중에서 선택되는 1종 이상인 것을 특징으로 하는 라돈 차단 효과가 우수한 방수시트.
The method of claim 4,
The adsorbent is a waterproof sheet having excellent radon blocking effect, characterized in that at least one selected from activated carbon and zeolite.
상기 점착층은,
프로세스 오일, 개질재, 접착력 보강제, 내열성 보강제, 상용화제 및 구리 분말을 포함하는 점착 조성물로 제조되고,
상기 개질재는,
SBS(Styrene-Butadiene-Styrene), SIS(Styrene-Isoprene-Styrene), SB(StyreneButadiene), SBR(Styrene- Butadiene Rubber), SEBS(Styrene ethylene butadiene styrene) 및 EVA(Ethylene vinyl acetate)로 이루어진 그룹에서 선택된 적어도 어느 하나인 라돈 차단 효과가 우수한 방수시트.
상기 중심재층은,
폴리에틸렌(PE) 직포, 폴리프로필렌(PP) 직포, 폴리프로필렌(PP) 부직포, 고밀도 폴리에틸렌(HDPE) 직포, 고밀도 폴리에틸렌(HDPE) 부직포 및 폴리에스터 부직포로 이루어진 그룹에서 선택된 적어도 어느 하나인 라돈 차단 효과가 우수한 방수시트.According to claim 2,
The adhesive layer,
It is made of an adhesive composition comprising process oil, modifier, adhesion reinforcing agent, heat resistant reinforcing agent, compatibilizer and copper powder,
The modifier,
Styrene-Butadiene-Styrene (SBS), Styrene-Isoprene-Styrene (SIS), StyreneButadiene (SB), Styrene-Butadiene Rubber (SBR), Styrene ethylene butadiene styrene (SEBS) and Ethylene vinyl acetate (EVA) A waterproof sheet with at least one radon barrier.
The core material layer,
Polyethylene (PE) woven fabric, polypropylene (PP) woven fabric, polypropylene (PP) nonwoven fabric, high density polyethylene (HDPE) woven fabric, high density polyethylene (HDPE) nonwoven fabric and at least one selected from the group consisting of polyester nonwoven fabric has a radon blocking effect Excellent waterproof sheet.