KR20200042592A - Glace Composition for Ceramic Ware Comprising Ashes from Hawthorn-like raspberry and Preparation Method thereof - Google Patents

Glace Composition for Ceramic Ware Comprising Ashes from Hawthorn-like raspberry and Preparation Method thereof Download PDF

Info

Publication number
KR20200042592A
KR20200042592A KR1020180122879A KR20180122879A KR20200042592A KR 20200042592 A KR20200042592 A KR 20200042592A KR 1020180122879 A KR1020180122879 A KR 1020180122879A KR 20180122879 A KR20180122879 A KR 20180122879A KR 20200042592 A KR20200042592 A KR 20200042592A
Authority
KR
South Korea
Prior art keywords
weight
glaze
raspberry
ash
composition
Prior art date
Application number
KR1020180122879A
Other languages
Korean (ko)
Other versions
KR102138702B1 (en
Inventor
김용득
김진욱
Original Assignee
김진욱
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김진욱 filed Critical 김진욱
Priority to KR1020180122879A priority Critical patent/KR102138702B1/en
Publication of KR20200042592A publication Critical patent/KR20200042592A/en
Application granted granted Critical
Publication of KR102138702B1 publication Critical patent/KR102138702B1/en

Abstract

The present invention relates to a glaze composition for porcelain, which comprises: ashes from Hawthorn-like raspberry which is powder of the ashes burning the Hawthorn-like raspberry; and common glaze raw materials including feldspar, white kaolin, and silica. The glaze composition can be used in the production of various color glazes.

Description

산딸기나무재를 포함하는 도자기용 유약 조성물 및 이의 제조방법{Glace Composition for Ceramic Ware Comprising Ashes from Hawthorn-like raspberry and Preparation Method thereof}Glaze composition for Ceramic Ware Comprising Ashes from Hawthorn-like raspberry and Preparation Method thereof
본 발명은 산딸기나무재를 포함하는 도자기용 유약 조성물 및 이의 제조방법에 관한 것이다.The present invention relates to a glaze composition for porcelain containing raspberry wood and a method for manufacturing the same.
이 부분에 기술된 내용은 단순히 본 발명에 대한 배경정보를 제공할 뿐 종래기술을 구성하는 것은 아니다.The content described in this section merely provides background information for the present invention and does not constitute a prior art.
일반적으로 유약이란, 도자기의 표면에 점착되는 얇은 유리층으로서 도자기의 흡수성을 저하시키고 심미감을 표출시키며 도자기를 튼튼하게 하는 역할을 한다. In general, a glaze is a thin glass layer adhered to the surface of ceramics, which reduces the absorbency of ceramics, expresses an aesthetic sense, and serves to strengthen ceramics.
즉, 유약은 도자기나 옹기류 등의 표면에 칠해지고 열처리 융착되어 그 표면에 광택 또는 무광택의 표면층을 형성시키기 위하여 사용되는 제제로서 투수성을 없애고 미적 효과를 증가시키며 도자기의 강도를 향상시킬 수 있다.That is, the glaze is a preparation used to form a glossy or matte surface layer on the surface of a ceramic or pottery, etc. by being heat-treated and fused, thereby eliminating water permeability, increasing the aesthetic effect, and improving the strength of the ceramic. .
도자기에 표면에 칠해져서 소성에 의해 광택을 띄게 하는 유약은 통상 장석, 규석, 고령토, 석회석, 활석, 형석, 골분을 주성분으로 구성될 수 있다. Glazes that are painted on the surface of ceramics to make them shine by firing can usually consist of feldspar, silica, kaolin, limestone, talc, fluorspar, and bone powder as the main components.
이와 같이 종래의 도자기용 유약은 흙이나 돌가루만을 사용하여 유약을 만들기 때문에 나무재를 사용하였던 과거 고려, 조선 시대의 청자나 백자와 같은 고급스러운 자연미를 살리지 못하는 한계가 있었다.As described above, since the traditional glaze for ceramics makes glaze using only soil or stone powder, there was a limitation that it could not take advantage of luxurious natural beauty such as celadon or white porcelain in the past Goryeo and Joseon Dynasty, where wood was used.
종래기술인 등록특허 제 10-1079706호의 솔잎, 콩깍지재, 장석, 대합조개 껍질 등을 사용한 유약 조성물, 등록특허 제 10-0387920호의 산화철, 코발트 등을 사용한 유약 조성물 등은 발색력이 좋지 못해 역시 고급스러운 자연미를 살리지 못하는 단점이 있었다.The glaze composition using pine needle, soybean pod, feldspar, clamshell, etc. of the registered patent No. 10-1079706, the glaze composition using iron oxide, cobalt, etc. of the registered patent No. 10-0387920 have poor color development, and are also luxurious natural beauty There was a disadvantage that could not save.
이에 본 발명자는 따뜻하고 부드러운 느낌을 주는 고급스러운 자연미를 살릴 수 있는 도자기용 유약을 개발하고자 예의 연구를 거듭하였고, 그 결과 산딸기나무의 재가 첨가된 유약을 도자기에 적용하는 경우, 부드럽고 따뜻한 느낌을 발현할 수 있다는 것을 알게 되어 본 발명을 완성하기에 이르렀다.Accordingly, the present inventor has conducted extensive studies to develop a glaze for porcelain that can take advantage of a luxurious natural beauty that gives a warm and soft feeling, and as a result, when applying glaze with ash from a raspberry tree to porcelain, express a soft and warm feeling. It has been realized that the present invention can be reached to complete the present invention.
본 발명의 일 목적은 따뜻하고 부드러운 느낌을 발현시켜 고급스러운 자연미를 살릴 수 있는 환경 친화적인 도자기용 유약 및 이의 제조방법을 제공하는 것이다.One object of the present invention is to provide an environmentally friendly glaze for ceramics and a method for manufacturing the same, which can express a warm and soft feeling and utilize a luxurious natural beauty.
본 발명의 일 목적을 달성하기 위해, 본 발명은 산딸기나무를 태운 재의 분말인 산딸기나무 재 및 통상의 유약 원료를 포함하는 유약 조성물을 제공한다.In order to achieve one object of the present invention, the present invention provides a glaze composition comprising a raspberry ash, which is a powder of ash-burned ash, and common glaze raw materials.
본 발명에서 산딸기나무의 재는 산딸기나무의 가지, 뿌리 등을 한 데 모아 태우고 남은 재의 분말을 사용할 수 있다. 이러한 산딸기나무 재를 도자기용 유약의 원료로 사용하는 경우, 환경 친화적이고 고급스러운 자연미를 나타내는 도자기를 제공할 수 있다.In the present invention, the ash of the raspberry tree can be used to collect the powder of the ash remaining after collecting and burning the branches and roots of the raspberry tree together. When such a raspberry ash is used as a raw material for glazes for ceramics, it is possible to provide ceramics that are environmentally friendly and exhibit high-quality natural beauty.
산딸기나무 재는 산화칼슘(CaO)을 함유할 수 있다. 산화칼슘(CaO)은 유약 혼합물의 용융온도를 낮출 수 있고 이에 의해 유약 조성물의 용융도가 높아질 수 있다. 즉, 산화칼슘(CaO)이 많이 함유되면 유약 조성물이 비교적 낮은 온도에서 용융되기 시작하므로 잘 녹는 도자기용 유약을 제조할 수 있는 것이다. 도자기용 유약의 용융온도가 높아 잘 녹지 않으면, 더 높은 온도와 더 긴 소성시간이 요구되므로, 산화칼슘(CaO)의 역할이 중요할 수 있다. 또한, 산화칼슘(CaO)은 유약 조성물에 포함된 원료들을 서로 잘 섞이도록 하는 매용제의 역할을 할 수 있다. Raspberry ash may contain calcium oxide (CaO). Calcium oxide (CaO) can lower the melting temperature of the glaze mixture, thereby increasing the meltability of the glaze composition. That is, if a large amount of calcium oxide (CaO) is contained, the glaze composition begins to melt at a relatively low temperature, so that it is possible to manufacture a glaze for porcelain that melts well. If the melting temperature of the ceramic glaze is high and does not melt well, a higher temperature and longer firing time are required, so the role of calcium oxide (CaO) may be important. In addition, calcium oxide (CaO) may serve as a solvent for mixing the ingredients contained in the glaze composition well with each other.
또한, 산화칼슘(CaO)은 유약의 색을 부드럽게 하는 역할을 할 수 있다. 또한, 산화칼슘(CaO)은 유약의 표면 광택도를 높일 수 있다. 즉, 도자기의 외면에 적용되어 도자기의 표면의 광택도를 높일 수 있는 것이다. 다만, 과량 함유되면, 그 유약의 표면은, 갈라진 틈, 내부에서 터져 형성되는 분화구와 같은 형상의 홈 등을 포함하도록 형성될 수 있고, 매끄럽지 않고 울퉁불퉁한 표면으로 형성될 수 있다. In addition, calcium oxide (CaO) may serve to soften the color of the glaze. In addition, calcium oxide (CaO) can increase the surface glossiness of the glaze. That is, it can be applied to the outer surface of the ceramic to increase the glossiness of the surface of the ceramic. However, if it is excessively contained, the surface of the glaze may be formed to include grooves of a shape such as a crack, a crater formed by bursting from the inside, and may be formed as a smooth and uneven surface.
또한, 산딸기나무 재는 산화마그네슘(MgO)을 함유할 수 있다. 산화마그네슘(MgO)은 위에서 언급한 산화칼슘(CaO)과 유사한 역할을 할 수 있다.In addition, the raspberry ash may contain magnesium oxide (MgO). Magnesium oxide (MgO) may play a role similar to the calcium oxide (CaO) mentioned above.
또한, 산딸기나무 재는 실리카(SiO2) 성분을 함유할 수 있다. 실리카(SiO2) 성분에 의하면 유약의 점성을 높일 수 있고, 따라서 산딸기나무 재를 이용하여 유약을 제조하는 경우 별도로 규석(점성을 높일 수 있는 성분)을 첨가하지 않을 수 있다In addition, the raspberry ash may contain a silica (SiO2) component. According to the silica (SiO2) component, the viscosity of the glaze can be increased, and thus, when preparing the glaze using raspberry ash, silica (component that can increase the viscosity) may not be added separately.
또한, 산딸기나무 재는 산화인(P2O5)을 함유할 수 있다. 이를 이용하여 도자기용 유약을 제조하는 경우 부드러운 유백색이 발현되므로, 맑고 따뜻한 느낌을 발현할 수 있다. 산딸기나무 재를 도자기용 유약에 첨가하는 경우 유백 유약, 투명 유약에 적용할 수 있으며, 특히 유백 유약에 적용하는 것이 바람직하다. 다만, 반드시 이에 한정되는 것은 아니고 공지의 어떠한 유약에도 적용될 수 있다.In addition, the raspberry ash may contain phosphorus oxide (P 2 O 5 ). When manufacturing a glaze for ceramics using this, a soft milky white color is expressed, so that a clear and warm feeling can be expressed. When the raspberry ash is added to the glaze for porcelain, it can be applied to a glaze and a transparent glaze, and is particularly preferably applied to a glaze. However, it is not necessarily limited to this and can be applied to any known glaze.
통상의 도자기용 유약 원료에는 이 기술분야에서 널리 사용되는 도자기 유약 원료 성분이 모두 포함될 수 있으며, 구체적으로 장석과 도석, 백운석, 석회석, 규석, 고령토 및 이들의 혼합물로 이루어진 군으로부터 선택된 것을 포함할 수 있으나, 반드시 이에 제한되는 것은 아니다.Common glaze raw materials for porcelain may include all of the ingredients of porcelain glaze widely used in this technical field, and may specifically include those selected from the group consisting of feldspar, pottery, dolomite, limestone, silica, kaolin and mixtures thereof. However, it is not necessarily limited thereto.
통상의 유약 원료의 성분 중 장석이나 도석의 알카리 성분은 유약 원료 중 규석 성분과 반응하며 유리질을 만드는 융제 역할을 하며, 석회석과 석회석의 일종인 백운석은 유약을 더 잘 녹게 하며 경도를 높게 하는 역할을 한다. 이들의 혼합 비율은 본 발명의 속하는 기술분야의 통상의 지식을 가진 자에게 자명한 것이다.Among the ingredients of ordinary glaze raw materials, the alkali component of feldspar or porcelain reacts with the siliceous components of the glaze raw materials and acts as a flux to make the glass. Limestone and dolomite, a type of limestone, play a role in melting glaze better and increasing hardness. do. These mixing ratios are apparent to those skilled in the art to which the present invention pertains.
본 발명의 일 실시예에 따른 도자기용 유약 조성물은 산딸기나무 재 40∼70 중량% 및 통상의 유약 원료 30∼60중량%를 포함할 수 있다.The glaze composition for porcelain according to an embodiment of the present invention may include 40 to 70% by weight of raspberry ash and 30 to 60% by weight of conventional glaze raw materials.
또한, 본 발명의 일 실시예에 따른 도자기용 유약 조성물은 고령토, 점토, 탄산바륨, 도석, 활석, 백운석, 골회, 황토, 벤토 나이트, 산화동, 산화코발트, 산화망간, 산화니켈, 산화티타늄, 산화주석, 산화아연 등을 제조하고자 하는 유약의 종류에 따라 더 포함할 수 있다. 본 발명의 일 실시예에 따른 도자기용 유약 조성물은 도자기에 적용되는 경우 산화동, 산화코발트, 산화망간, 산화니켈, 산화티타늄, 산화주석 등의 발색 원료를 첨가하여 비취색, 올리브 그린색, 브라운 색 등을 나타낼 수 있다. In addition, the glaze composition for ceramics according to an embodiment of the present invention is kaolin, clay, barium carbonate, pottery, talc, dolomite, bone ash, ocher, bentonite, copper oxide, cobalt oxide, manganese oxide, nickel oxide, titanium oxide, oxidation Tin, zinc oxide, etc. may be further included according to the type of glaze to be produced. The glaze composition for porcelain according to an embodiment of the present invention, when applied to porcelain, adds color-producing materials such as copper oxide, cobalt oxide, manganese oxide, nickel oxide, titanium oxide, tin oxide, etc., jade, olive green, brown, etc. Can represent
또한, 본 발명은 산딸기나무 재를 포함하는 도자기용 유약 조성물의 제조방법을 제공할 수 있다. 도자기용 유약 조성물의 제조방법은 산딸기나무 재를 준비하는 단계 및 산딸기나무 재와 통상의 유약 원료를 혼합하는 단계를 포함할 수 있다.In addition, the present invention can provide a method of manufacturing a glaze composition for porcelain comprising raspberry ash. The method of manufacturing a glaze composition for ceramics may include preparing a raspberry ash and mixing a raspberry ash and common glaze raw materials.
산딸기나무 재를 준비하는 단계는, 이 기술분야에서 이용되는 일반적인 방법으로 얻어질 수 있다. 예를 들면, 산딸기나무가 타고 남은 재를 물과 섞고 분쇄 과정을 거친 다음 체를 이용하여 재 이외의 이물질을 걸러 준다. 체로 걸러 낸 산딸기나무의 재가 침전되어 가라앉으면 침전된 재로부터 잿물을 분리해 내고(여러번 반복), 남아 있는 재를 건조시켜 분말 상태로 만들어 사용할 수 있다.The step of preparing the raspberry ash can be obtained by general methods used in the art. For example, a raspberry tree burns, mixes the remaining ash with water, goes through a crushing process, and sifts out foreign matter other than ash. When the ash of the raspberry tree filtered through a sieve precipitates and sinks, the lye is separated from the precipitated ash (repeated several times), and the remaining ash can be dried to form a powder.
이와 같이 제조된 산딸기나무 재를 통상의 유약 원료와 혼합하여 본 발명의 일 실시예에 따른 도자기용 유약 조성물을 제조할 수 있다.The resulting raspberry ash can be mixed with conventional glaze raw materials to produce a glaze composition for porcelain according to an embodiment of the present invention.
본 발명의 추가적인 해결수단은 아래에서 이어지는 설명에서 일부 설명될 것이고, 그 설명으로부터 부분적으로 용이하게 확인할 수 있게 되거나, 또는 본 발명의 실시에 의해 지득될 수 있다.Additional solutions of the present invention will be described in part in the description that follows, and may be readily identifiable in part from the description, or may be learned by practice of the present invention.
전술한 일반적인 설명 및 다음의 상세한 설명 모두는 단지 예시적이고 설명을 위한 것이며 청구범위에 기재된 본 발명을 제한하지 않는다.Both the foregoing general description and the following detailed description are illustrative and illustrative only and do not limit the invention described in the claims.
본 발명에 따른 산딸기나무 재를 포함하는 도자기용 유약 조성물은 고급스러운 자연미를 살릴 수 있으며, 청자 유약, 분청 투명 유약, 매트 유약, 이라보 유약, 천목 유약 등 각종 색 유약의 제조에 사용될 수 있다.The glaze composition for porcelain containing raspberry ash according to the present invention can make use of a luxurious natural beauty, and can be used in the manufacture of various color glazes such as celadon glaze, transparent clear glaze, matt glaze, irabo glaze, celestial glaze.
도 1은 본 발명의 실시예1에 따라 환원분위기로 제조된 도자기 시험편이다.
도 2는 본 발명의 실시예2에 따라 환원분위기로 제조된 도자기 시험편이다.
1 is a porcelain test piece manufactured in a reducing atmosphere according to Example 1 of the present invention.
Figure 2 is a porcelain test piece produced in a reducing atmosphere according to Example 2 of the present invention.
이하, 첨부된 도면을 참조하여 본 발명의 구체적인 실시형태에 대하여 상세하게 서술하도록 한다. Hereinafter, specific embodiments of the present invention will be described in detail with reference to the accompanying drawings.
다만, 본 발명의 구체적 일 실시 형태를 설명함에 있어, 관련된 공지 기능 또는 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략한다.However, in describing a specific embodiment of the present invention, when it is determined that a detailed description of a related known function or configuration may unnecessarily obscure the subject matter of the present invention, the detailed description will be omitted.
시험예: 산딸기나무 재 성분 분석Test Example: Analysis of raspberry ash ingredients
아래의 표 1은 XRF로 분석한 산딸기나무 재의 성분분석표이다. 표 1을 참조하면, 산딸기나무 재를 XRF를 사용하여 성분 분석한 결과를 파악할 수 있다. Table 1 below is a component analysis table of raspberry ash analyzed by XRF. Referring to Table 1, it is possible to grasp the results of the component analysis of the raspberry ash using XRF.
산딸기나무 재는 산화칼슘(CaO) 및 산화마그네슘(MgO)을 포함할 수 있다. 산딸기나무재는 산화칼슘(CaO)을 56.98중량%, 산화마그네슘(MgO)을 22.37중량 % 포함할 수 있다. 산화칼슘(CaO)및 산화마그네슘(MgO)은 앞서 언급했듯이 유약의 조성물의 용융온도를 낮출 수 있고, 유약 조성물에 혼합된 여러 성분을 잘 혼합되게 하는 매용제의 역할을 할 수 있다.Raspberry ash may include calcium oxide (CaO) and magnesium oxide (MgO). The raspberry wood material may include calcium oxide (CaO) of 56.98% by weight and magnesium oxide (MgO) of 22.37% by weight. Calcium oxide (CaO) and magnesium oxide (MgO), as mentioned above, can lower the melting temperature of the composition of the glaze, and can serve as a solvent for mixing various components well mixed in the glaze composition.
또한, 산딸기나무 재는 산화인(P2O5)을 포함할 수 있다. 산딸기나무재는 산화인(P2O5)을 약 8.89중량% 함유할 수 있다. 산화인(P2O5)은 앞서 언급했듯이, 유약을 맑고 따뜻한 느낌이 발현되도록 할 수 있고, 유약의 느낌을 부드럽게 할 수 있다. In addition, the raspberry ash may include phosphorus oxide (P 2 O 5 ). Raspberry wood material may contain about 8.89% by weight of phosphorus oxide (P 2 O 5 ). As mentioned above, phosphorus oxide (P 2 O 5 ) can make the glaze develop a clear and warm feeling, and soften the feel of the glaze.
또한, 산딸기나무 재는 산화규소(SiO2)를 포함할 수 있다. 산딸기나무재는 산화규소(SiO2)를 5.17중량% 함유할 수 있다.In addition, the raspberry ash may include silicon oxide (SiO 2 ). Raspberry wood may contain 5.17% by weight of silicon oxide (SiO 2 ).
또한, 산딸기나무 재는 기타 성분을 1.5중량% 함유할 수 있다. 기타 성분은 그 성분 함량이 작아 유약의 특징에 큰 영향을 미치지 않는 요소를 '기타'라는 하나의 카테고리로 묶은 것으로, MnO, BaO, TiO2, ZnO, SO3, Na2O, CuO, Pm2O3 를 포함할 수 있다.In addition, raspberry ash may contain other components by 1.5% by weight. Other ingredients are those that have a small content and do not significantly affect the characteristics of the glaze, and are grouped into one category called 'other'. MnO , BaO, TiO 2 , ZnO, SO 3 , Na 2 O, CuO, Pm 2 O 3 .
성분ingredient CaO CaO MgO MgO P2O5 P 2 O 5 SiO2 SiO 2 K2OK 2 O Al2O3 Al 2 O 3 SrOSrO Fe2O3 Fe 2 O 3 기타Other
단위(w t%)Unit (w t%) 56.9856.98 22.3722.37 8.898.89 5.175.17 2.32.3 1.421.42 0.760.76 0.610.61 1.51.5
실시예 1Example 1
산딸기나무 재를 장석, 흰색고령토 및 규석과 혼합하되, 아래 표 2에 나타난 성분들의 조성비(유약 조성물 전체중량을 기준으로 한 중량비율)에 따라 혼합하여 10가지 종류의 유약을 제조하였다. 도 1에 첨부된 시험편은 실시예 1에 따라 제조된 10가지의 유약을 10개의 초벌구이한 시험편들에 시유한 후 가마에 넣어 환원분위기로 1230℃ 내지 1250℃에서 8 시간 내지 10시간 동안 소성하는 과정을 거쳐 제조된다. Raspberry ash was mixed with feldspar, white kaolin, and silica, but mixed according to the composition ratio (weight ratio based on the total weight of the glaze composition) of the components shown in Table 2 below to prepare 10 types of glaze. The test piece attached to FIG. 1 is a process of firing for 8 hours to 10 hours at 1230 ° C to 1250 ° C in a reducing atmosphere after applying 10 glazes prepared according to Example 1 to 10 super-baked test pieces and putting them in a kiln. It is manufactured through.
구분division 산딸기나무재Raspberry wood 장석feldspar 흰색고령토White kaolin 규석burr
1One 7070 1010 1010 1010
22 6060 1010 2020 1010
33 6060 2020 1010 1010
44 5050 1010 3030 1010
55 5050 2020 2020 1010
66 5050 3030 1010 1010
77 4040 1010 4040 1010
88 4040 2020 3030 1010
99 4040 3030 2020 1010
1010 4040 4040 1010 1010
도 1은 본 발명의 실시예1에 따라 환원분위기로 제조된 도자기 시험편이다. 1번에서 10번으로 갈수록 산딸기나무재의 함량은 점점 감소될 수 있다. 도 1의 1번 내지 10번의 도자기 시험편을 참조하여 산딸기나무 재의 함량비율 감소됨에 따른 유약의 색상 및 표면의 변화를 관찰해보면, 산딸기나무 재의 함량비율이 감소될수록 유약의 색상은 광택이 있는 밝은 녹색에서 광택이 점점 약해지고 녹색 또한 점점 옅어지는 것을 파악할 수 있다. 1 is a porcelain test piece manufactured in a reducing atmosphere according to Example 1 of the present invention. From 1 to 10, the content of raspberry wood may decrease gradually. Referring to the porcelain test pieces 1 to 10 of Figure 1 to observe the change in the color and surface of the glaze as the content ratio of the raspberry ash is reduced, as the content ratio of the raspberry ash decreases, the color of the glaze is bright green with a gloss You can see that the gloss is getting weaker and the green is getting weaker.
또한, 시험편 7번을 참조하면, 다른 시험편과는 다른 황색 빛깔이 섞인 녹색인 것을 파악할 수 있다. 이는 후술하는 실시예2와 같이, 천목유와 혼합되어 진하고 어두운 가지색의 광택을 내는 유약이 될 수 있다.In addition, referring to Test No. 7, it can be seen that the yellow color is different from other test pieces. This may be a glaze that produces a dark, dark-colored gloss that is mixed with celestial oil, as in Example 2 described later.
실시예 2Example 2
실시예2는 실시예1의 7번 조성물과 종래의 천목유약을 절반씩 혼합한 유약을 10개의 초벌구이한 시험편들에 시유한 후 가마에 넣어 환원분위기로 1230℃ 내지 1250℃에서 8 시간 내지 10시간 동안 소성하는 과정을 거쳐 제조된다. 여기서, 실시예1과 다른 점은, 실시예1은 10개의 시험편이 모두 조성이 조금씩 다른 유약이 적용된 것이고, 실시예2는 10개의 시험편이 모두 같은 조성이다. In Example 2, the glaze obtained by mixing the composition 7 of Example 1 and the conventional celestial glaze in half was applied to 10 pre-baked test pieces and put into a kiln for 8 hours to 10 hours at 1230 ° C to 1250 ° C in a reducing atmosphere. It is manufactured through the process of firing during. Here, the difference from Example 1, Example 1 is that all 10 test pieces have a slightly different glaze composition, and Example 2 has the same composition of all 10 test pieces.
도 2를 참조하면, 10개의 시험편이 서로 다른 색깔을 내는 것을 알 수 있다. 실시예2의 10개의 시험편은 각 시험편에 적용되는 온도의 차이에 의해 색깔 및 빛깔의 차이가 발생할 수 있다. 4번, 5번, 7번 및 8번은 가해지는 온도가 다른 것에 비해 높기 때문에, 진하고 어두운 푸른 빛깔의 가지색이 발현될 수 있다. 이 외 1번 내지 3번, 6번, 9번 및 10번은 가해지는 온도가 다른 것에 비해 낮기 때문에, 비교적 상기 푸른 빛깔의 가지색이 덜 발현될 수 있다.Referring to FIG. 2, it can be seen that ten test pieces emit different colors. In the ten test pieces of Example 2, a difference in color and color may occur due to a difference in temperature applied to each test piece. Since 4, 5, 7, and 8 have higher temperatures than others, dark and dark blue-colored branches may be expressed. In addition, since 1 to 3, 6, 9, and 10 have a lower applied temperature than others, the blue color may be less expressed.
가해지는 온도가 다른 이유는, 가마에 시편을 투입하여 소성할 때, 열원과의 거리 차이 때문일 수 있다. 4번, 5번, 7번 및 8번 시험편은 열원과의 거리가 가까워 1250℃ 내지 1300℃의 온도가 가해질 수 있고, 특히 7번 시험편의 경우 1300℃ 내지 1350℃의 온도가 가해질 수 있다. 도 2를 참조하면 높은 온도에서 소성될수록 진하고 어두운 푸른 빛깔의 가지색이 발현됨을 파악할 수 있다.The reason that the applied temperature is different may be due to a difference in the distance from the heat source when firing with the specimen in the kiln. Test pieces 4, 5, 7 and 8 may be applied at a temperature of 1250 ° C to 1300 ° C because the distance from the heat source is close, and in particular, for the test piece 7, a temperature of 1300 ° C to 1350 ° C may be applied. Referring to FIG. 2, it can be understood that dark and dark blue colored branches are expressed as they are fired at a high temperature.
여기서, 종래의 천목유약은 천목유약 전체 중량을 기준으로 장석 50중량%, 카오린 10 내지 15중량%, 규석 10중량%, 활석 5중량%, 참나무재 10중량% 및 철(Fe) 10 내지 15중량%를 함유할 수 있다. Here, the conventional cheonmok glaze is based on the total weight of cheonmok glaze 50% by weight of feldspar, 10 to 15% by weight of kaolin, 10% by weight of silica, 5% by weight of talc, 10% by weight of oak wood, and 10 to 15% by weight of iron (Fe) %.
즉, 실시예2 조성물은 실시예2조성물 전체 중량을 기준으로 실시예1 7번 조성물 50중량% 및 천목유약 50중량%를 포함할 수 있다. 결과적으로, 산딸기나무재 20중량%, 장석 5중량%, 흰색고령토 20중량%, 규석 5중량% 및 장석 25중량%, 카오린 5내지 7.5중량%, 규석 5중량%, 활석 2.5중량%, 참나무재 5중량%, 철 5내지 7.5중량%를 함유할 수 있다. That is, the composition of Example 2 may include 50% by weight of the composition of Example 1, composition 7, and 50% by weight of a cloth glaze, based on the total weight of the composition of Example 2. As a result, 20% by weight of raspberry wood, 5% by weight of feldspar, 20% by weight of white kaolin, 5% by weight of quartzite and 25% by weight of feldspar, 5 to 7.5% by weight of kaolin, 5% by weight of silica, 2.5% by weight of talc, oak wood It can contain 5% by weight and 5 to 7.5% by weight of iron.
정리하면, 산딸기나무재 20중량%, 장석 5중량%, 흰색고령토 20중량%, 규석 10중량% 및 장석 25중량%, 카오린 5내지 7.5중량%, 활석 2.5중량%, 참나무재 5중량%, 철 5내지 7.5중량%를 함유할 수 있다.In summary, 20% by weight of raspberry wood, 5% by weight of feldspar, 20% by weight of white kaolin, 10% by weight of silica, and 25% by weight of feldspar, 5 to 7.5% by weight of kaolin, 2.5% by weight of talc, 5% by weight of oak, iron 5 to 7.5% by weight.
이와 같이, 진하고 어두운 푸른 빛깔의 가지색을 띠는 고급스러운 느낌을 발현하고자 할 때 본 발명의 실시예2에 따른 유약 조성물을 사용할 수 있고, 목표하는 느낌에 따라 열원과의 거리를 적절히 조절하여 소성할 수 있다.As described above, the glaze composition according to Example 2 of the present invention can be used to express a luxurious feeling with a dark dark blue color, and can be fired by appropriately adjusting the distance to the heat source according to the desired feeling. You can.
본 실시예는 본 발명의 기술적 사상을 예시적으로 설명한 것에 불과하고, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 본 실시예의 다양한 수정 및 변형이 가능할 것이다. 본 실시예는 본 발명의 기술적 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 따라서 본 실시예에 의하여 본 발명의 권리범위가 한정되는 것은 아니다. 본 발명의 보호범위는 청구범위에 의하여 해석되어야 하며, 그와 동등하거나 균등하다고 인정되는 모든 기술적 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 한다.This embodiment is merely illustrative of the technical idea of the present invention, and those skilled in the art to which the present invention pertains may have various modifications and variations of this embodiment without departing from the essential characteristics of the present invention. It will be possible. This embodiment is not intended to limit the technical spirit of the present invention but to explain it, and accordingly, the scope of the present invention is not limited by the present embodiment. The scope of protection of the present invention should be interpreted by the claims, and all technical ideas recognized as equivalent or equivalent should be interpreted as being included in the scope of the present invention.

Claims (6)

  1. 산딸기나무를 태운 재의 분말인 산딸기나무 재; 및
    장석, 흰색고령토 및 규석을 포함하는 통상의 유약원료
    를 포함하는 산딸기나무 재를 포함하는 도자기용 유약 조성물.
    Raspberry ash, which is a powder of ashes that have been burned; And
    Normal glaze raw materials including feldspar, white kaolin and silica
    Glaze composition for porcelain containing raspberry ash comprising a.
  2. 제1항에 있어서,
    유약 조성물 전체 중량을 기준으로 상기 산딸기나무재는 40~70중량%, 상기 통상의 유약원료는 30~60중량%인 것
    을 특징으로 하는 산딸기나무 재를 포함하는 도자기용 유약 조성물.
    According to claim 1,
    The raspberry wood based on the total weight of the glaze composition is 40 to 70% by weight, the conventional glaze raw material is 30 to 60% by weight
    Glaze composition for porcelain comprising raspberry ash characterized in that.
  3. 제2항에 있어서,
    유약 조성물 전체 중량을 기준으로 상기 산딸기나무 재는 40중량%, 및 상기 장석은 10중량%, 상기 흰색고령토는 40중량% 및 상기 규석은 10중량%인 것
    을 특징으로 하는 산딸기나무 재를 포함하는 도자기용 유약 조성물.
    According to claim 2,
    Based on the total weight of the glaze composition, the raspberry ash is 40% by weight, and the feldspar is 10% by weight, the white kaolin is 40% by weight, and the silica is 10% by weight
    Glaze composition for porcelain comprising raspberry ash characterized in that.
  4. 제3항에 있어서,
    유약 조성물 전체 중량을 기준으로 산딸기나무재 20중량%, 장석 5중량%, 흰색고령토 20중량%, 규석 5중량% 및 종래의 천목유약 50중량%
    을 포함하는 산딸기나무 재를 포함하는 도자기용 유약 조성물.
    According to claim 3,
    20% by weight of raspberry wood, 5% by weight of feldspar, 20% by weight of white kaolin, 5% by weight of silica, and 50% by weight of conventional cloth
    Glaze composition for porcelain comprising a raspberry ash comprising a.
  5. 제4항에 있어서,
    상기 종래의 천목유약은
    상기 종래의 천목유약 전체 중량을 기준으로 장석 50중량%, 카오린 10 내지 15중량%, 규석 10중량%, 활석 5중량%, 참나무재 10중량% 및 철(Fe) 10 내지 15중량%
    을 포함하는 산딸기나무 재를 포함하는 도자기용 유약 조성물.
    According to claim 4,
    The conventional cheonmok glaze
    50% by weight of feldspar, 10 to 15% by weight of kaolin, 10% by weight of silica, 5% by weight of talc, 10% by weight of oak wood, and 10 to 15% by weight of iron (Fe)
    Glaze composition for porcelain comprising a raspberry ash comprising a.
  6. 산딸기나무 재를 준비하는 단계; 및
    장석, 흰색고령토 및 규석을 포함하는 통상의 유약원료와 상기 산딸기나무 재를 혼합하는 단계
    를 포함하는 산딸기나무 재를 포함하는 도자기용 유약 조성물의 제조방법.
    Preparing a raspberry ash; And
    Mixing the common raspberry raw materials including feldspar, white kaolin and silica stone and the wild strawberry ash
    Method of manufacturing a glaze composition for porcelain comprising raspberry ash comprising a.
KR1020180122879A 2018-10-16 2018-10-16 Glace Composition for Ceramic Ware Comprising Ashes from Hawthorn-like raspberry and Preparation Method thereof KR102138702B1 (en)