KR20190019138A - Formulation of organic functional material - Google Patents

Abstract

The present invention relates to a formulation comprising at least one organic functional material and at least a first organic solvent, wherein said first organic solvent is a 1,1-diphenylethylene derivative, and to an electronic device manufactured using such a formulation will be.

Description

Formulation of organic functional material

The present invention relates to a formulation containing a 1,1-diphenylethylene derivative as a first solvent, and to an electroluminescent device manufactured using such a formulation.

Organic light emitting devices (OLEDs) have been produced for a long time by a vacuum deposition process. Other techniques such as inkjet printing have been scrutinized in recent years due to their advantages such as cost savings and scale-up possibilities. One of the major challenges in multi-layer printing is to identify the relevant parameters in order to obtain a homogeneous deposition of the ink on the substrate. In order to trigger such parameters, such as surface tension, viscosity or boiling point, some additives may be added to the formulation.

TECHNICAL PROBLEMS AND OBJECTS OF THE INVENTION

A number of solvents have been proposed for organic electronic devices for inkjet printing. However, the number of critical parameters that play a role during the deposition and drying process makes the choice of solvent very difficult. Therefore, formulations containing organic semiconductors used for deposition by inkjet printing still require improvement. It is an object of the present invention to provide a formulation of an organic semiconductor that enables controlled deposition to form an organic semiconductor layer with good layer properties and efficiency performance. It is a further object of the present invention to provide a formulation of an organic semiconductor which, when used, for example, in an inkjet printing process, allows for uniform application of ink droplets onto a substrate, thereby providing good layer properties and efficiency performance .

The above object of the present invention is solved by providing a formulation comprising a 1,1-diphenylethylene derivative as a first solvent.

The present inventors have surprisingly found that the use of an organic solvent containing a 1,1-diphenylethylene derivative as a first solvent enables complete control of surface tension and induces effective ink deposition, To form a highly uniform and well defined organic layer of functional material.

BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a schematic diagram of a device including an ITO anode, a hole injection layer (HIL), a hole transport layer (HTL), a green light emitting layer (G-EML), a hole blocking layer (HBL), an electron transport layer Represent a typical layer structure.
Fig. 2 shows the device performance of an OLED manufactured according to Working Example 1. Fig.

DETAILED DESCRIPTION OF IMPLEMENTATIONS

The present invention relates to formulations containing a 1,1-diphenylethylene derivative as a first solvent and at least one organic functional material.

Preferred embodiment

In a first preferred embodiment, the first organic solvent is a 1,1-diphenylethylene derivative according to formula (I): < EMI ID =

[Wherein,

R ¹ and R ² are the same or different and are each independently selected from the group consisting of F, Cl, Br, I, NO ₂ , CN, a straight chain alkyl or alkoxy group having 1 to 20 carbon atoms or a branched or cyclic Alkyl or alkoxy group wherein one or more non-adjacent CH ₂ groups are optionally replaced by -O-, -S-, -NR ⁵ -, -CONR ⁵ -, -CO-O-, -C = O-, - or -C? C-, and at least one hydrogen atom may be replaced by F, or an aryl or heteroaryl group having from 4 to 14 carbon atoms, which may be substituted with one or more non-aromatic R ⁵ radicals may be substituted, and a plurality of substituents R ^5, together result on the same ring or two different rings, mono-substituted with a plurality of substituents R ⁵ - forming the or polycyclic, aliphatic, aromatic or heteroaromatic ring system, Lt; / RTI >

R ³ and R ⁴ are the same or different and are each independently selected from the group consisting of H, F, Cl, Br, I, NO ₂ , CN, a straight chain alkyl or alkoxy group having 1 to 20 carbon atoms, A cyclic alkyl or alkoxy group wherein one or more non-adjacent CH ₂ groups are replaced by -O-, -S-, -NR ⁵ -, -CONR ⁵ -, -CO-O-, -C = O-, Or -C≡C-, and one or more hydrogen atoms may be replaced by F), or an aryl or heteroaryl group having from 4 to 14 carbon atoms which may be substituted by one or more nonaromatic R ⁵ radicals may form or polycyclic, aliphatic, aromatic or heteroaromatic ring system), in the same ring or a 2, with a plurality of substituents R ⁵ on the two different rings as a result, the mono substituted with a plurality of substituents R ⁵ ego;

R ⁵ is in each case the same or different and is a straight chain alkyl or alkoxy group of 1 to 20 carbon atoms or a branched or cyclic alkyl or alkoxy group of 3 to 20 carbon atoms in which one or more non-adjacent CH ₂ groups are replaced by -O-, -O-, -CO-O-, -C = O-, -CH = CH- or -C? C-, and at least one hydrogen atom may be replaced by F, 14 < / RTI > aryl or heteroaryl group which may be substituted with one or more nonaromatic R < ⁵ &

m and n Are each the same or different and are 0, 1, 2 or 3, preferably 0 or 1, and more preferably 0.

In a first more preferred embodiment, the first organic solvent is a 1,1-diphenylethylene derivative according to formula (I)

Wherein,

R ¹ and R ^2, wherein each the same or different from the case, the number of carbon atoms straight-chain alkyl or alkoxy group of from 1 to 20, or a branched or cyclic having 3 to 20 alkyl or alkoxy group (wherein one or more non-adjacent CH ₂ groups ^{-O-, -S-, -NR 5 -,} -CONR 5 -, -CO-O-, -C = O-, may be replaced by -CH = CH- or -C≡C-) and;

R ³ and R ⁴ are each the same or different and are H, a linear alkyl or alkoxy group having 1 to 20 carbon atoms, or a branched or cyclic alkyl or alkoxy group having 3 to 20 carbon atoms, ₂ groups ^{-O-, -S-, -NR 5 -,} -CONR 5 -, -CO-O-, -C = O- available, can be replaced by -CH = CH- or -C≡C-) and ;

R ⁵ is in each case the same or different and is a straight chain alkyl or alkoxy group of 1 to 20 carbon atoms or a branched or cyclic alkyl or alkoxy group of 3 to 20 carbon atoms in which one or more non-adjacent CH ₂ groups are replaced by -O-, -S-, -CO-O-, -C = O-, -CH = CH- or -C? C-,

m and n Lt; / RTI > are each the same or different from zero or one and preferably zero.

In a second more preferred embodiment, the first organic solvent is a 1,1-diphenylethylene derivative according to formula (I) as follows:

Wherein,

R ¹ and R ² are the same or different in each case, the number of carbon atoms straight-chain alkyl or alkoxy group of from 1 to 20, or a branched or cyclic having 3 to 20 alkyl or alkoxy group (wherein one or more non-adjacent CH ₂ groups - ^{O-, -S-, -NR 5 -,} -CONR 5 -, -CO-O-, -C = O-, may be replaced by -CH = CH- or -C≡C-) and;

R ³ and R ⁴ are H;

R ⁵ is in each case the same or different and is a straight chain alkyl or alkoxy group of 1 to 20 carbon atoms or a branched or cyclic alkyl or alkoxy group of 3 to 20 carbon atoms in which one or more non-adjacent CH ₂ groups are replaced by -O-, -S-, -CO-O-, -C = O-, -CH = CH- or -C? C-;

m and n are each the same or different from 0 or 1, and preferably 0.

In a first most preferred embodiment, the first organic solvent is a 1,1-diphenylethylene derivative according to formula (I) as follows:

Wherein,

R ¹ and R ² are the same or different in each case and are a straight chain alkyl group having 1 to 20 carbon atoms or a branched or cyclic alkyl group having 3 to 20 carbon atoms;

R ³ and R ⁴ are H;

m and n Are the same or different in each case 0 or 1 and preferably 0,

In a second most preferred embodiment, the first organic solvent is 1,1-diphenylethylene according to formula (II) as follows:

.

.

Examples of most preferred 1,1-diphenylethylene derivatives and their boiling points (BP) are shown in Table 1 below.

Table 1: Preferred 1,1-diphenylethylene derivatives and their boiling points (BP).

Preferably, the first solvent has a surface tension of? 20 mN / m. More preferably, the surface tension of the first solvent is in the range of 25 to 40 mN / m, and most preferably in the range of 28 to 37.5 mN / m.

The content of the first solvent is preferably in the range of 50 to 100% by volume, more preferably in the range of 75 to 100% by volume, and most preferably in the range of 90 to 100% by volume, based on the total amount of the solvent in the formulation.

As a result, the content of the second solvent is preferably in the range of 0 to 50% by volume, more preferably in the range of 0 to 25% by volume, and most preferably in the range of 0 to 10% by volume, based on the total amount of the solvent in the formulation to be.

Preferably, the first solvent has a boiling point in the range of 100 to 400 占 폚, more preferably in the range of 150 to 350 占 폚.

In one embodiment, the formulation according to the invention comprises at least a first solvent and a second solvent. A second solvent is used with the first solvent.

Suitable second solvents are preferably, in particular, alcohols, such as alcohols, aldehydes, ketones, ethers, esters, amides such as di-C _1-2 -alkylformamides, sulfur compounds, nitro compounds, hydrocarbons, halogenated hydrocarbons Hydrocarbons), aromatic or heteroaromatic hydrocarbons, and halogenated aromatic or heteroaromatic hydrocarbons.

Preferably, the second solvent may be selected from one of the following groups: substituted and unsubstituted aromatic or linear esters such as ethyl benzoate, butyl benzoate; Substituted and unsubstituted aromatic or linear ethers such as 3-phenoxy toluene or anisole; Substituted or unsubstituted arene derivatives such as xylene; Indane derivatives such as hexamethylindane; Substituted and unsubstituted aromatic or linear ketones; Substituted and unsubstituted heterocycles such as pyrrolidinone, pyridine, pyrazine; Other fluorinated or chlorinated aromatic hydrocarbons.

Particularly preferred second organic solvents are, for example, 1,2,3,4-tetramethylbenzene, 1,2,3,5-tetramethylbenzene, 1,2,3-trimethylbenzene, 1,2,4, 1,2,4-trichlorobenzene, 1,2,4-trimethylbenzene, 1,2-dihydronaphthalene, 1,2-dimethylnaphthalene, 1,3-benzodioxolane, Diisopropylbenzene, 1,3-dimethylnaphthalene, 1,4-benzodioxane, 1,4-diisopropylbenzene, 1,4-dimethylnaphthalene, 1,5-dimethyltetralin, Thiophene, thianaphthalene, 1-bromonaphthalene, 1-chloromethylnaphthalene, 1-ethylnaphthalene, 1-methoxynaphthalene, 1-methylnaphthalene, Dihydrobenzofuran, 2,3-dimethyl anisole, 2,4-dimethyl anisole, 2,5-dimethyl anisole, 2,6-dimethyl anisole, 2,6-dimethyl naphthalene, - bromomethylnaphthalene, 2-bromomethylnaphthalene, 2-bromonaphthalene, 2-ethoxynaphthalene, 2-ethylnaphthalene, 2- 2-methylindole, 3,4-dimethyl anisole, 3,5-dimethyl anisole, 3-bromoquinoline, 3-methyl anisole, 4-methyl anisole, , 5-methoxyindole, 5-tert-butyl-m-xylene, 6-methylquinoline, 8-methylquinoline, acetophenone, anisole, benzonitrile, benzothiazole, benzyl acetate, But are not limited to, bromobenzene, butylbenzoate, butylphenyl ether, cyclohexylbenzene, decahydronaphthol, dimethoxy toluene, 3-phenoxy toluene, diphenyl ether, propiophenone, ethyl benzene, ethyl benzoate, But are not limited to, hexamethylindane, indene, isochromane, cumene, m-cymene, mesitylene, methylbenzoate, o-, m-, p- xylene, propylbenzoate, propylbenzene, o- But are not limited to, benzene, ethoxybenzene, phenylacetate, p-cymene, propiophenone, sec-butylbenzene, t-butylbenzene, thiophene, toluene, veratrol, Pyrazine, pyrimidine, pyrrolidinone, morpholine, dimethylacetamide, dimethylsulfoxide, decalin, and / or mixtures of such compounds.

These solvents may be used individually or as a mixture of two, three or more solvents to form a second solvent.

Preferably, the second solvent has a boiling point in the range of 100 to 400 占 폚, more preferably in the range of 150 to 350 占 폚.

The at least one organic functional material preferably has a solubility in the range of 1 to 250 g / l and more preferably in the range of 1 to 50 g / l in the first and second solvents.

The content of the at least one organofunctional material in the formulation is in the range of 0.001 to 20% by weight, preferably in the range of 0.01 to 15% by weight, more preferably in the range of 0.1 to 10% by weight, By weight is in the range of 0.3 to 10% by weight.

The formulations according to the invention preferably have a surface tension in the range of 10 to 50 mN / m and more preferably in the range of 25 to 40 mN / m.

Moreover, the formulations according to the invention is preferably from 1 to 50 ^mPa. s, more preferably from 2 to 40 mPa ^. s, and most preferably from 2 to 20 mPa ^. s < / RTI >

Preferably, the organic solvent blend comprises a surface tension in the range of 15 to 80 mN / m, more preferably in the range of 20 to 60 mN / m and most preferably in the range of 25 to 40 mN / m. The surface tension was measured at 20 캜 Can be measured using a FTA (First Ten Angstrom) 1000 contact angle goniometer. Details of the method are described in Roger P. Woodward, Ph.D. &Quot; Surface Tension Measurements Using the Drop Shape Method ", available from First Ten Angstrom. Preferably, a pendant drop method can be used to measure the surface tension. This measurement technique dispenses a drop from the needle on a bulk liquid or gas phase. The shape of the drop is obtained from the relationship between surface tension, gravity and density difference. When using the pendant drop method, the surface tension is calculated from the shadow image of the pendant drop using http://www.kruss.de/services/education-theory/glossary/drop-shape-analysis. All surface tension measurements were performed using a commercially available and commercially available high precision drop shape analysis tool, FTA 1000 from First Ten Angstrom. The surface tension is measured by software FTA1000. All measurements were carried out at room temperature ranging from 20 캜 to 22 캜. Standard work procedures include the measurement of the surface tension of each formulation using a new disposable drop dispensing system (syringe and needle). Each drop is measured in 60 measurements over a one minute duration, which is then averaged out. For each formulation, three drops are measured. The final value is averaged over the measurement. The tool is periodically cross-checked against various liquids having well-known surface tension.

The formulations of the examples and the viscosity of the solvent were measured using a TA instruments ARG2 rheometer over shear rates ranging from 10 to 1000 s < ^-1 > using a 40 mm parallel plate geometry. The measurements were taken on average at 200 to 800 s < ^-1 > where the temperature and shear rate are precisely controlled. The viscosity given in Table 3 is the viscosity of each formulation measured at a temperature of 25 DEG C and a shear rate of 500 s < ^-1 >. Each solvent is measured three times. The viscosity values shown are averaged over the measurements.

The formulations of the present invention comprise at least one organofunctional material that can be used in the production of a functional layer of an electronic device. The functional material is generally an organic material introduced between the anode and the cathode of the electronic device.

The term organofunctional material is used in particular for organic conductors, organic semiconductors, organic fluorescent compounds, organic phosphorescent compounds, organic light absorbing compounds, organic light-sensitive compounds, organic photosensitisation agents, Lt; / RTI > Thus, the term organofunctional material includes organometallic complexes of transition metals, rare earths, lanthanides and actinides.

The organic functional material may be a fluorescent material such as a fluorescent light emitter, a phosphorescent light emitting material, a host material, a matrix material, an exciton blocking material, an electron transporting material, an electron injecting material, a hole conduction material, a hole injecting material, an n-dopant, a wide-band-gap material, an electron blocking material, and a hole blocking material.

A preferred embodiment of an organofunctional material is disclosed in detail in WO 2011/076314 A1, the contents of which are incorporated herein by reference.

In a preferred embodiment, the organic functional material is an organic semiconductor selected from the group consisting of hole injection, hole transport, luminescence, electron transport and electron injection materials.

More preferably, the organic functional material is an organic semiconductor selected from the group consisting of hole injection and hole transport materials.

The organic functional material may be a compound having a low molecular weight polymer, oligomer or dendrimer, wherein the organic functional material may also be in the form of a mixture. Thus, formulations according to the invention may comprise two different compounds of low molecular weight, one low molecular weight compound and one polymer or two polymers (blends).

Organo-functional materials are often described through the properties of the frontier orbitals, which are described in more detail below. A material molecular orbital, in particular also of the top level occupied molecular orbital (HOMO) and the lowest level unoccupied molecular orbital (LUMO), its energy level and the lowest triplet state T ₁ or the lowest singlet state S ₁ excitation energy, Quantitative chemical calculations. For the calculation of metal-free organic materials, optimization of the geometry is first performed using the "Ground State / Semi-empirical / Default Spin / AM1 / Charge 0 / Spin Singlet" method. Energy calculations are then performed based on the optimized geometry. Here, the "TD-SCF / DFT / Default Spin / B3PW91" method using the "6-31G (d)" base set (charge 0, spin center) is used. For metal-containing compounds, the geometry is optimized through the "Ground State / Hatree-Fock / Default Spin / LanL2MB / Charge 0 / Spin Singlet" method. The energy calculation is performed similarly to the method described above for the organic material, except for the difference that a "LanL2DZ" base set is used for the metal atom and a "6-31G (d)" base set is used for the ligand. The energy calculation provides the HOMO energy level HEh or the LUMO energy level LEh in units of Hartree. The HOMO and LUMO energy levels to the electron volt, calibrated with reference to the cyclic voltammetry measurement, are then measured as follows:

HOMO (eV) = ((HEh * 27.212) -0.9899) /1.1206

LUMO (eV) = ((LEh * 27.212) -2.0041) / 1.385

For purposes of this application, these values should be considered as the HOMO and LUMO energy levels of each of the materials.

The lowest triplet state T ₁ is defined as the energy of the triplet state with the lowest energy resulting from the quantum chemical calculations described.

The lowest excited singlet state S ₁ is defined as the energy of the excited singlet state with the lowest energy resulting from the quantum chemical calculations described.

The methods described herein are independent of the software package used and always provide the same result. For this purpose, examples of commonly used programs are " Gaussian 09W " (Gaussian Inc.) and Q-Chem 4.1 (Q-Chem, Inc.).

A compound having hole injecting properties, also referred to herein as a hole injecting material, simplifies or facilitates the transport of holes from the anode to the organic layer, that is, a positive charge. In general, the hole injection material has an HOMO level at or above the anode level region, i.e., at least -5.3 eV in general.

A compound having hole transporting characteristics, and also a so-called hole transporting material in this application, can transport holes, that is, positive charges, which are generally injected from an anode or an adjacent layer, for example, a hole injection layer. The hole transporting material generally has a high HOMO level of preferably -5.4 eV or higher. Depending on the structure of the electronic device, a hole transporting material may also be used as the hole injecting material.

Preferred compounds having hole injection and / or hole transporting properties include, for example, triarylamine, benzidine, tetraaryl-para-phenylenediamine, triarylphosphine, phenothiazine, phenoxazine, dihydrophenazine, Further O-, S-, and S-containing compounds having a high HOMO (HOMO = highest level occupied molecular orbital), such as dibenzo-para-dioxine, phenoxathiine, carbazole, azulene, thiophene, pyrrole and furan derivatives, - or an N-containing heterocycle.

(US Pat. No. 3,615,404), arylamine derivatives (US 3567450), amino-substituted chalcone derivatives (US 3526501), styryl anthracene derivatives (JP-A- (JP-A-54-110837), hydrazone derivatives (US 3717462), acylhydrazones, stilbenes, and the like. (JP-A-2-282263), thiophene oligomer (JP Heisei (JP-A-2-282263) 1 (1989) 211399), polythiophenes, poly (N-vinylcarbazole) (PVK), polypyrroles, polyanilines and other electronically conductive macromolecules, porphyrin compounds (JP-A-63-2956965, US 4720432) Lidene-type compounds, carbazole compounds such as CDBP, CBP, mCP, aromatic tertiary amines and styrylamine compounds (US 4127412), for example Jidin type triphenylamine, styrylamine type triphenylamine triphenyl amine and a diamine type may be particularly mentioned. It is also possible to use arylamine dendrimers (JP Heisei 8 (1996) 193191), monomeric triarylamines (US 3180730), triarylamines containing at least one vinyl radical and / or at least one active hydrogen-containing functional group (US 3567450 and US 3658520), or tetraaryldiamine (two tertiary amine units linked through an aryl group) can be used. In addition, more triarylamino groups may be present in the molecule. Also suitable are phthalocyanine derivatives, naphthalocyanine derivatives, butadiene derivatives and quinoline derivatives such as dipyridino [2,3-f: 2 ', 3'-h] -quinoxaline hexacarbonitrile.

NPD (? -NPD = 4,4'-bis [N- (1-naphthyl)] naphthalene, which contains at least two tertiary amine units (US 2008/0102311 A1, US 4720432 and US 5061569) (N, N'-diphenyl-4-aminophenyl) -N, N-diphenyl-4,4'- , 4'-diamino-1,1'-biphenyl) or MTDATA (MTDATA or m-MTDATA = 4,4 ', 4 "-tris [(3- methylphenyl) phenylamino] triphenylamine (4-di-p-tolylamino) -4-hydroxybenzophenone), TBDB (= N, N, N ', N'- ) cyclohexane), TAPPP (= 1,1- bis (4-di - p - tolyl-aminophenyl) -3-phenylpropane), BDTAPVB (= 1,4- bis [2- [4- [N, N (= N, N ', N'-tetra- p -tolyl-4,4'-diaminobiphenyl), TPD , 4'-bis [N-3-methylphenyl] -N-phenylamino) biphenyl), N, N, N ', N'-tetraphenyl- Quot ;, 1 ", 4 ", 1 "'- quaterphenyl, (9H-carbazol-9-yl) phenyl] benzenamine) is reacted with a tertiary amine containing, for example, (H ₂ Pc, CuPc (= copper phthalocyanine), CoPc, NiPc, ZnPc, PdPc, FePc, MnPc, ClAlPc, ClGaPc, and ClgPc in accordance with US 2007/0092755 A1, the _{ClInPc, ClSnPc, Cl 2 SiPc,} (HO) AlPc, (HO) GaPc, VOPc, TiOPc, MoOPc, GaPc-O-GaPc) are preferred as well.

Particularly preferred are triarylamine compounds of the formulas (TA-1) to (TA-12), which are described in EP 1162193 B1, EP 650 955 B1, Synth. Metals 1997 , 91 (1-3), 209, DE 19646119 A1, WO 2006/122630 A1, EP 1 860 097 A1, EP 1834945 A1, JP 08053397 A, US 6251531 B1, US 2005/0221124, JP 08292586 A, US 7399537 B2, US 2006/0061265 A1, EP 1 661 888 and WO 2009/041635. The above compounds of formulas (TA-1) to (TA-12) may also be substituted:

.

.

Additional compounds that may be used as hole injecting materials are disclosed in EP 0891121 Al and EP 1029909 A1, and injection layers generally disclosed in US 2004/0174116 A1.

These aryl amines and heterocycles, which are generally used as hole injecting and / or hole transporting materials, preferably cause a HOMO in the polymer (relative to the vacuum level) of greater than -5.8 eV, particularly preferably greater than -5.5 eV .

Examples of the compound having electron injection and / or electron transporting property include pyridine, pyrimidine, pyridazine, pyrazine, oxadiazole, quinoline, quinoxaline, anthracene, benzanthracene, pyrene, perylene, benzimidazole, tri S- or N-containing heterocycles having triarylborane and a low LUMO (LUMO = lowest level non occupancy molecular orbital) as well as azine, ketone, phosphine oxide and phenazine derivatives.

The electron transport and electron injection layer, particularly suitable compounds include 8-hydroxyquinoline of metal chelates (e.g. _{LiQ, AlQ 3, GaQ 3,} MgQ 2, ZnQ 2, InQ 3, ZrQ 4), BAlQ, Ga oxinoid (US Pat. No. 5,529,853 A, ET-1), butadiene derivatives (US 4356429), heterocyclic optical brighteners (US 4539507), benzimides Triazines such as spirobifluorenyl thiazine derivatives (e.g., DE (US Pat. No. 5,982,753), US Pat. (For example, rubrene derivatives), 1,10-phenanthroline derivatives (JP 2003-115387, JP 2004-311184 (corresponding to JP-A No. 102008064200), pyrene, anthracene, tetracene, fluorene, spirofluorene, dendrimer, (EP 1480280, EP 1478032, EP 1469533), borane derivatives such as Si-containing triarylphosphoric acid derivatives (for example, JP-A-2001-267080, WO 02/043449), silacyclopentadiene derivatives Phenanthroline, especially 1,10-phenanthroline derivatives such as BCP and Bphen, and also biphenyl or derivatives thereof (see US 2007/0087219 Al, formula ET-3), pyridine derivatives (JP 2004-200162) Several phenanthrolines connected through other aromatic groups (US-2007-0252517 A1) or phenanthrolines linked to anthracene (US 2007-0122656 A1, see formulas ET-4 and ET-5).

Heterocyclic organic compounds, such as thiopyran dioxide, oxazole, triazole, imidazole or oxadiazole, are likewise suitable. N-containing 5-membered rings, for example oxazoles, preferably 1,3,4-oxadiazoles, for example the compounds of the formulas ET-6, ET-7, ET-8 and ET- 2007/0273272 A1); (See, for example, US 2008/0102311 A1 and [YA Levin, MS Skorobogatova, Khimiya Geterotsiklicheskikh Soedinenii 1967 (2), 339-341]), preferably the compound represented by the formula ET-10 , Examples of the use of silacyclopentadiene derivatives. Preferred compounds are of the formulas (ET-6) to (ET-10)

Further, organic compounds such as derivatives of fluorenone, fluorenylidenemethane, perylene tetracarboxylic acid, anthraquinone dimethane, diphenoquinone, anthrone and anthraquinone diethylenediamine can be used.

(See US 2008/0193796 Al, formula ET-11) containing 2,9,10-substituted anthracene or two anthracene units (with 1- or 2-naphthyl and 4- or 3-biphenyl) . It is also very advantageous that 9,10-substituted anthracene units are linked to benzimidazole derivatives (see US 2006/147747 A and EP 1551206 A1, Formulas ET-12 and ET-13).

Compounds capable of producing electron injection and / or electron transport properties preferably cause LUMO (relative to the vacuum level) of less than -2.5 eV, particularly preferably less than -2.7 eV.

The formulations of the present invention may comprise an emitter. The term luminous body refers to a material which, after excitation which may be caused by any type of energy transfer, allows for a radiative transition to a ground state with emission. In general, two classes of luminaries, namely fluorescence and phosphorescent luminous bodies, are known. The term fluorescent luminescent material refers to a material or compound that undergoes a radioactive transition from an excited singlet state to a ground state. The term phosphorescent emitter preferably represents a light emitting material or compound containing a transition metal.

An emitter is often referred to as a dopant when the dopant causes the properties described above in the system. In a system comprising a matrix material and a dopant, it is understood that the dopant means a constituent having a lower proportion in the mixture. Correspondingly, in a system comprising a matrix material and a dopant, it is understood that the matrix material means a larger proportion of the composition in the mixture. Thus, the term phosphorescent emitter may also be understood to mean, for example, a phosphorescent dopant.

The compound capable of emitting light includes, in particular, a fluorescent light-emitting substance and a phosphorescent light-emitting substance. These include, but are not limited to, stilbene, stilbeneamine, styrylamine, coumarin, rubrene, rhodamine, thiazole, thiadiazole, cyanine, thiophene, paraphenylene, perylene, phthalocyanine, porphyrin, ketone, quinoline, Imine, anthracene and / or pyrene structures. Particularly preferred are compounds which exhibit electrophosphorescence instead of electrofluorescence, which can emit at high efficiency from the triplet state at room temperature, i. E. Often causing an increase in energy efficiency. For this purpose, compounds containing heavy atoms with an atomic number greater than 36 are preferred. Preference is given to compounds containing d- or f-transition metals which meet the conditions mentioned above. Particularly preferred are the corresponding compounds containing elements 8 to 10 (Ru, Os, Rh, Ir, Pd, Pt). Suitable functional compounds here are, for example, various complexes as described in WO 02/068435 A1, WO 02/081488 A1, EP 1239526 A2 and WO 2004/026886 A2.

Preferred compounds which can act as fluorescence emitters are described as the following examples. Preferred fluorescent emitters are selected from the group of monostyrylamines, distyrylamines, tristyrylamines, tetrastyrylamines, styrylphosphines, styrylethers and arylamines.

Monostyryl amines are understood to mean compounds containing one substituted or unsubstituted styryl group and at least one, preferably aromatic amine. Distyrylamine is understood to mean a compound containing two substituted or unsubstituted styryl groups and at least one, preferably aromatic amine. Tristyrylamine is understood to mean a compound containing three substituted or unsubstituted styryl groups and at least one, preferably aromatic amine. Tetrastyrylamine is understood to mean a compound containing four substituted or unsubstituted styryl groups and at least one, preferably aromatic amine. The styryl group is particularly preferably stilbene, which may also be further substituted. Corresponding phosphines and ethers are defined analogously to amines. In the sense of the present invention, an arylamine or an aromatic amine is understood to mean a compound containing three substituted or unsubstituted aromatic or heteroaromatic ring systems directly bonded to nitrogen. At least one of these aromatic or heteroaromatic ring systems is preferably a fused ring system, preferably having at least 14 aromatic ring atoms. Preferred examples thereof include aromatic anthracene amines, aromatic anthracene diamines, aromatic pyrene amines, aromatic pyrene diamines, aromatic chrysene amines or aromatic chrysene diamines. An aromatic anthracene amine is understood to mean a compound in which one diarylamino group is preferably bonded directly to the anthracene group at the 9-position. An aromatic anthracene diamine is understood to mean a compound in which two diarylamino groups are bonded directly to the anthracene group, preferably at the 2,6- or 9,10-position. Aromatic pyrene amines, pyrene diamines, chrysene amines and chrysene diamines are similarly defined, wherein the diarylamino group is preferably bonded to the pyrene at the 1-position or the 1,6-position.

More preferred fluorescent emitters are indenofluorenamine or indenofluorenediamine (especially described in WO 2006/122630); Benzoindenofluorenamine or benzoindenofluorenediamine (especially described in WO 2008/006449); And dibenzoindenofluorenediamine (especially described in WO 2007/140847).

Examples of styrylamine classes of compounds that can be used as fluorescent emitters include substituted or unsubstituted tristilbutylamines, or compounds described in WO 2006/000388, WO 2006/058737, WO 2006/000389, WO 2007/065549 and WO 2007 / 115610. Distyrylbenzene and distyrylbiphenyl derivatives are described in US 5121029. Additional styrylamines can be found in US 2007/0122656 A1.

Particularly preferred styrylamine compounds are compounds of the formula EM-1 as described in US 7250532 B2 and compounds of the formula EM-2 as described in DE 10 2005 058557 A1:

.

.

Particularly preferred triarylamine compounds are the compounds of the formula EM- < RTI ID = 0.0 > 1 < / RTI > disclosed in CN 1583691 A, JP 08/053397 A and US 6251531 B1, EP 1957606 A1, US 2008/0113101 A1, US 2006/210830 A, WO 2008/006449 and DE 102008035413, 3 to EM-15, and derivatives thereof:

.

.

More preferred compounds that can be used as fluorescent luminescent materials are naphthalene, anthracene, tetracene, benzanthracene, benzophenanthrene (DE 10 2009 005746), fluorene, fluoranthene, periflactene, indenopherylene, phenanthrene, Perylene (US 2007/0252517 A1), pyrene, chrysene, decacyclene, coronene, tetraphenylcyclopentadiene, pentaphenylcyclopentadiene, fluorene, spirofluorene, rubrene, coumarin (US 4769292, US 6020078, US 2007/0252517 A1), pyran, oxazole, benzoxazole, benzothiazole, benzimidazole, pyrazine, cinnamic acid ester, diketopyrrolopyrrole, acridone and quinacridone (US 2007/0252517 A1 ). ≪ / RTI >

Of the anthracene compounds, 9,10-substituted anthracenes such as 9,10-diphenylanthracene and 9,10-bis (phenylethynyl) anthracene are particularly preferred. 1,4-bis (9'-ethynyl anthracenyl) benzene is also a preferred dopant.

(= N, N'-dimethyl quinacridone), dicyanomethylenepyran, for example DCM (= 4- (dicyanoethylene) -6- (4-dimethylaminostyryl-2-methyl) -4H-pyran), thiopyran, polymethine, pyrylium and thiapyrylium salts, periflactene and indenoprenylene derivatives are likewise preferred.

The blue fluorescent light emitter is preferably a polyaromatic compound such as 9,10-di (2-naphthylanthracene) and other anthracene derivatives, tetracene, xanthene, perylene, for example 2,5,8,11 -Tetra- t -butylperylene, phenylene, for example 4,4'-bis (9-ethyl-3-carbazovinylene) -1,1'-biphenyl, fluorene, fluoranthene, aryl Pyrene (US 2006/0222886 A1), arylene vinylene (US 5121029, US 5130603), bis (azinyl) imine-boron compounds (US 2007/0092753 A1), bis (azinyl) ≪ / RTI >

A more preferable blue fluorescent luminescent material is [C.H. Chen et al .: " Recent developments in organic electroluminescent materials ", Macromol. Symp. 125, (1997) 1-48] and [" Recent progress of molecular organic electroluminescent materials and devices ", Mat. Sci. and Eng. R, 39 (2002), 143-222.

A more preferred blue fluorescent luminescent material is the hydrocarbon disclosed in DE 102008035413.

Preferred compounds which can act as phosphorescent emitters are described below by way of example.

Examples of phosphorescent emitters are disclosed in WO 00/70655, WO 01/41512, WO 02/02714, WO 02/15645, EP 1191613, EP 1191612, EP 1191614 and WO 2005/033244. In general, all phosphorescent complexes used in accordance with the prior art for phosphor OLED and known to those skilled in the art of organic electroluminescence are suitable, and those skilled in the art will be able to use additional phosphorescent complexes without an inventive step.

The phosphorescent metal complex preferably contains Ir, Ru, Pd, Pt, Os or Re, more preferably Ir.

Preferred ligands include 2-phenylpyridine derivatives, 7,8-benzoquinoline derivatives, 2- (2-thienyl) pyridine derivatives, 2- (1-naphthyl) pyridine derivatives, 1-phenylisoquinoline derivatives, Isoquinoline derivatives or 2-phenylquinoline derivatives. All such compounds may be substituted, for example, with fluoro, cyano and / or trifluoromethyl substituents for the blue color. The auxiliary ligand is preferably acetylacetonate or picolinic acid.

In particular, a complex of Pt or Pd with a four-terminal ligand of the formula EM-16 is suitable.

The compounds of formula EM-16 are described in more detail in US 2007/0087219 A1, the disclosure of which is incorporated herein by reference in its description of substituents and indices in the above formulas. Furthermore, Pt-porphyrin complexes (US 2009/0061681 Al) with extended ring systems and Ir complexes such as 2,3,7,8,12,13,17,18-octaethyl-21H, 23H-porphyrin -Pt (II), tetraphenyl -Pt (II) porphyrin tetra benzo (US 2009/0061681 A1), cis-bis (2-phenyl-pyrido Dina sat ^{-N, C 2 ') Pt (} II), cis-bis ( 2- (2'-thienyl) pyrimidin Dina sat ^{-N, C 3 ') Pt (} II), cis-bis (2- (2'-thienyl) quinolinato ^{-N, C 5') Pt (} II ), (2-phenyl (4,6-difluorophenyl) pyrimidin Dina sat -N, C ^{2 '),} Pt (II) (acetylacetonate), or tris (2-phenyl-pyrido Dina sat -N, C ^2' ), Ir (III) (= Ir (ppy) _3, green), and bis (2-phenyl-pyrido Dina sat -N, C ^2), Ir (III) (acetylacetonate) (= Ir (ppy) ₂ acetylacetonate, Green, US 2001/0053462 A1, Baldo, Thompson et al. Nature 403, (2000), 750-753), bis (1-phenylisoquinolinato-N, C ^{2 '} Dina sat -N, C ^{2 ')} iridium (III), bis (2-phenyl-pyrido Dina sat -N, C ^2') (1- phenylisothiazol quinolinato -N, C ^{2 ')} iridium (III), Bis (2- (2'-benzothienyl) pyridnato-N, C ^{3 '} ) iridium (III) (acetylacetonate), bis (2- (4', 6'-difluorophenyl) Sat -N, C ^{2 ')} iridium (III) (picolinate) (FIrpic, blue), bis (2- (4', 6'-difluorophenyl) pyrimidin Dina sat -N, C ^{2 ')} Ir (III) (tetrakis (l-pyrazolyl) borate), tris (2- (biphenyl-3-yl) -4-tert- butyl) iridium (III), (ppz) ₂ Ir (5phdpym) (US _{2009/0061681 A1), (45ooppz) 2} -Ir (5phdpym) (US 2009/0061681 A1), 2- phenylpyridine derivative of -Ir complexes, for example, PQIr (= iridium (III) bis (2-phenyl quinolyl (2-benzo [4,5-a] pyridin-2-yl) -N, C ^{2 '} ) acetylacetonate), tris (2-phenylisoquinolinato- thienyl) pyrimidin Dina sat -N, ³ C), Ir _{(acetylacetonate) ([Btp 2 Ir (acac} )], red, [Adachi et al. Appl. Phys. Lett . 78 (2001), 1622-1624).

3 is a lanthanide, for example, Tb ³⁺ and complexes of ^{Eu 3+ ([J. Kido et al} . Appl. Phys. Lett. 65 (1994), 2124], [Kido et al. Chem. Lett. 657, (Johnson et al., JACS 105, 1983, 1795) of Pt (II), Ir (I), Rh (I) and maleononyldithiolate , , Os (II) complexes with Re (I) tricarbonyl-diimine complexes (especially [Wrighton, JACS 96, 1974, 998]), cyano ligands and bipyridyl or phenanthroline ligands al., Synth. Metals 94, 1998, 245).

Additional phosphorescent phosphors with three-terminal ligands are described in US 6824895 and US 10/729238. Red luminous phosphorescent complexes are identified in US 6835469 and US 6830828.

Particularly preferred compounds used as phosphorescent dopants are in particular the compounds of the formula EM-17 (in particular in US 2001/0053462 Al and [ Inorg. Chem. 2001, 40 (7), 1704-1711], [JACS 2001, 123 , ≪ / RTI > 4304-4312) and derivatives thereof.

Derivatives are described in US 7378162 B2, US 6835469 B2 and JP 2003/253145 A.

Furthermore, the compounds of the formulas EM-18 to EM-21 (described in US 7238437 B2, US 2009/008607 A1 and EP 1348711) and derivatives thereof can be used as light emitting materials.

Quantum dots can likewise be used as emitters, and these materials are described in detail in WO 2011/076314 A1.

Particularly, a compound used as a host material together with a luminescent compound includes a material from various classes of materials.

The host material has a larger bandgap between HOMO and LUMO than a commonly used luminous material. Further, a preferable host material exhibits the properties of a hole or an electron transporting material. Further, the host material may have both electron and hole transport properties.

Host materials are sometimes referred to as so-called matrix materials, in particular when host materials are used in combination with phosphorescent emitters in OLEDs.

A preferred host material or co-host material, particularly used with a fluorescent dopant, is a class of oligoarylene (for example 2,2 ', 7,7'-tetraphenyl spirobias according to EP 676461 Fluorene or dinaphthylanthracene), in particular oligoarylenes containing condensed aromatic groups, such as anthracene, benzanthracene, benzophenanthrene (DE 10 2009 005746, WO 2009/069566), phenanthrene, tetracene, (For example, DPVBi = 4,4 ', N'-tetramethylpiperidine according to EP 676461), chrysene, fluorene, spirofluorene, perylene, phthaloperylene, naphthaloperylene, decacyclene, rubrene, Bis (2,2-diphenylethenyl) -1,1'-biphenyl or spiro-DPVBi), polypodal metal complexes (for example according to WO 04/081017), especially 8- metal complexes of quinoline, such as AlQ ₃ (= aluminum (III) tris (8-hydroxyquinoline)), or bis (2-methyl-8-quinolinyl Metal complexes, benzoquinoline-metal complexes, hole-conducting compounds (e. G., ≪ RTI ID = 0.0 > WO 2004/058911), electron conducting compounds, especially ketones, phosphine oxides, sulfoxides, etc. (for example according to WO 2005/084081 and WO 2005/084082), atropisomers (for example WO 2006/048268), boronic acid derivatives (for example according to WO 2006/117052) or benzanthracene (for example according to WO 2008/145239).

Particularly preferred compounds which may serve as the host material or co-host material are selected from the oligoarylene classes, including anthracene, benzanthracene and / or pyrene, or the atropisomers of such compounds. In the sense of the present invention, oligo- arylene is understood to mean a compound in which at least three aryl or arylene groups are bonded together.

Preferred host materials are selected from the compounds of formula (H-1) in particular:

Ar ⁴ - (Ar ⁵ ) _p -Ar ⁶ (H-1)

Wherein Ar ⁴ , Ar ⁵ and Ar ⁶ are each independently an optionally substituted aryl or heteroaryl group having 5 to 30 aromatic ring atoms, and p is in the range of 1 to 5 ≪ / RTI > The sum of the pi electrons in Ar ⁴ , Ar ⁵ and Ar ⁶ is at least 30 for p = 1, at least 36 for p = 2 and at least 42 for p = 3.

In the compounds of formula (H-1), the group Ar ⁵ particularly preferably represents anthracene, the groups Ar ⁴ and Ar ⁶ being bonded at the 9- and 10-positions, wherein these groups may optionally be substituted. Very particularly preferably, at least one of the groups Ar ⁴ and / or Ar ⁶ is 1- or 2-naphthyl, 2-, 3- or 9-phenanthrenyl, or 2-, 3-, , 6- or 7-benzanthracenyl. Anthracene-based compounds are described in US 2007/0092753 A1 and US 2007/0252517 A1, for example 2- (4-methylphenyl) -9,10-di- (2-naphthyl) anthracene, 9- Naphthyl) -10- (1,1'-biphenyl) anthracene and 9,10-bis [4- (2,2- diphenylethenyl) phenyl] anthracene, 9,10- -Bis (phenylethynyl) anthracene and 1,4-bis (9'-ethynyl anthracenyl) benzene. A compound containing two anthracene units (US 2008/0193796 A1), such as 10,10'-bis [1,1 ', 4', 1 "] terphenyl-2-yl-9,9'-bis Anthracenyl is preferred.

More preferred compounds are those selected from the group consisting of arylamine, styrylamine, fluororesin, diphenylbutadiene, tetraphenylbutadiene, cyclopentadiene, tetraphenylcyclopentadiene, pentaphenylcyclopentadiene, coumarin, oxadiazole, bisbenzoxazoline (US 2007/0092753 A1), for example 2,2 ', 2 " - (1,3,5-phenyl) benzoquinoline, derivatives of benzoimidazole, oxazole, pyridine, pyrazine, imine, benzothiazole, Phenyl] -1H-benzimidazole], aldazine, stilbene, styrylarylene derivatives such as 9,10-bis [4- (2,2- diphenylethenyl) phenyl] Anthracene and distyrylarylene derivatives (US 5121029), diphenylethylene, vinyl anthracene, diaminocarbazole, pyran, thiopyran, diketopyrrolopyrrole, polymethine, cinnamic ester and fluorescent dyes.

Particularly preferred are derivatives of arylamine and styrylamine, for example TNB (= 4,4'-bis [N- (1-naphthyl) -N- (2-naphthyl) amino] biphenyl). Metal-oxinoid complexes such as LiQ AlQ ₃ or the ball may be used as a host.

Preferred compounds having oligoarylene as the matrix are disclosed in US 2003/0027016 A1, US 7326371 B2, US 2006/043858 A, WO 2007/114358, WO 2008/145239, JP 3148176 B2, EP 1009044, US 2004/018383, WO 2005/061656 A1, EP 0681019 B1, WO 2004/013073 A1, US 5077142, WO 2007/065678 and DE 102009005746, wherein particularly preferred compounds are represented by the formulas H-2 to H-8.

Further, the compound which can be used as a host or a matrix includes a material used together with a phosphorescent emitter.

Such compounds that may also be utilized as structural elements in polymers include, but are not limited to, CBP (N, N-biscarbazolylbiphenyl), carbazole derivatives (e.g., WO 2005/039246, US 2005/0069729, JP 2004/288381, According to EP 1205527 or WO 2008/086851), azacarbazole (for example according to EP 1617710, EP 1617711, EP 1731584 or JP 2005/347160), ketone (for example according to WO 2004/093207 or DE 102008033943) (For example according to WO 2005/003253), oligophenylene, aromatic amines (for example according to US 2005/0069729), bipolar matrix materials (for example WO 2007/0069729), phosphine oxides, sulfoxides and sulfones (According to WO 2005/111172), 9,9-diarylfluorene derivatives (for example according to DE 102008017591), azaborol or boronic acid esters (for example according to WO 2006/0137725), silanes (for example according to WO 2005/111172) 117052), triazine derivatives (for example according to DE 102008036982), indolocarbazole derivatives (For example according to WO 2007/063754 or WO 2008/056746), indenocarbazole derivatives (for example according to DE 102009023155 and DE 102009031021), diazappor derivatives (for example according to DE 102009022858) Wherein the aromatic amine compound is at least one selected from the group consisting of triazole derivatives, oxazole and oxazole derivatives, imidazole derivatives, polyarylalkane derivatives, pyrazoline derivatives, pyrazolone derivatives, distyrylpyrazine derivatives, thiopyran dioxide derivatives, A metal complex of an 8-hydroxyquinoline derivative, for example, a metal complex such as AlQ ₃ ((AlQ ₃ ) ₂₎ , a metal complex of an allyl amine, an amino-substituted chalcone derivative, an indole, a hydrazone derivative, a stilbene derivative, a silazane derivative, an aromatic dimethylidene compound, a carbodiimide derivative, Which may also contain triarylaminophenol ligands (US 2007/0134514 Al), metal complexes / polysilane compounds, and thiophene, benzothiophene and dibenzothiophene derivatives, It is hereinafter.

An example of a preferable carbazole derivative is mCP (= 1,3-N, N-dicarbazolylbenzene (= 9,9 '- (1,3-phenylene) bis-9H-carbazole) 9), CDBP (= 9,9 '- (2,2'-dimethyl [1,1'-biphenyl] -4,4'-diyl) (N, N'-dicarbazolyl) benzene (= 1,3-bis (carbazol-9-yl) benzene), PVK (polyvinylcarbazole), 3,5- Biphenyl and CMTTP (formula H-10). Particularly preferred compounds are disclosed in US 2007/0128467 A1 and US 2005/0249976 A1 (Formulas H-11 and H-13).

Preferred tetraaryl-Si compounds are described, for example, in US 2004/0209115, US 2004/0209116, US 2007/0087219 A1 and [H. Gilman, E.A. Zuech, Chemistry & Industry (London, United Kingdom), 1960,120.

Especially preferred tetraaryl-Si compounds are represented by the formulas H-14 to H-21.

Particularly preferred compounds of group 4 for the preparation of matrices for phosphorescent dopants are described in particular in DE 102009022858, DE 102009023155, EP 652273 B1, WO 2007/063754 and WO 2008/056746, To H-25.

Particularly preferred is a material containing at least one nitrogen atom for the functional compound which can be used according to the invention and which can act as a host material. This preferably includes aromatic amines, triazine derivatives and carbazole derivatives. Thus, carbazole derivatives exhibit surprisingly high efficiency. Triazine derivatives lead to unexpectedly long lifetimes of electronic devices.

It may also be desirable to use as the mixture a plurality of different matrix materials, especially at least one electron conductive matrix material and at least one hole conductive matrix material. It is likewise preferable to use a mixture of charge transport matrix material and, if present, electrically inert matrix material which does not participate to a significant degree of charge transport, for example as described in WO 2010/108579.

Furthermore, compounds that improve the transition from singlet state to triplet state and improve the phosphorescent properties of such compounds by being used in the support of functional compounds with luminescent properties can be used. For this purpose, in particular carbazole and bridged carbazolyl dimer units (for example as described in WO 2004/070772 A2 and WO 2004/113468 A1) are suitable. For this purpose, ketones, phosphine oxides, sulfoxides, sulfones, silane derivatives and similar compounds (for example as described in WO 2005/040302 A1) are also suitable.

The n-dopant is understood herein to mean a reducing agent, i. E. An electron donor. Preferred examples of n-dopants are W (hpp) ₄ and other electron-rich metal complexes (according to WO 2005/086251 A2), P = N compounds (for example WO 2012/175535 A1, WO 2012/175219 A1) , Free radicals and di-radicals (e.g., EP 1837926 A1, WO 2007/107306 A1), naphthylene carbodiimide (e.g. WO 2012/168358 A1), fluorene (E.g., US 2007/145355 A1) as well as pyridine (e.g., EP 2452946 A1, EP 2463927 A1), N-heterocyclic compounds (e.g. WO 2009/000237 A1) and acridines .

Further, the formulation may comprise a wide bandgap material as a functional material. The wide bandgap material is understood to mean the material in the sense of the disclosure of US 7,294,849. Such a system exhibits performance data particularly advantageous in electroluminescent devices.

The compound used as the wide bandgap material may have a bandgap of 2.5 eV or more, preferably 3.0 eV or more, particularly preferably 3.5 eV or more. The bandgap can be calculated, in particular, by using the energy levels of the highest order occupied molecular orbital (HOMO) and the lowest order non occupied molecular orbital (LUMO).

Further, the formulation may include a hole blocking material (HBM) as a functional material. The hole blocking material represents a material which prevents or minimizes the transfer of holes (positive charges) in a multilayer system, particularly when such a material is disposed in the form of a layer adjacent to the light emitting layer or hole transporting layer. In general, the hole blocking material has a lower HOMO level than the hole transporting material in the adjacent layer. The hole blocking layer is often disposed between the light emitting layer and the electron transporting layer in the OLED.

Basically any known hole blocking material can be used. In addition to other hole blocking materials described elsewhere herein, advantageous hole blocking materials include metal complexes (US 2003/0068528) such as bis (2-methyl-8-quinolinolato) (4-phenylphenolato) aluminum (III) (BAlQ). For this purpose, Fac-tris (1-phenylpyrazolato-N, C2) -Iridium (III) (Ir (ppz) ₃ ) (US 2003/0175553 A1) is also used. Phenanthroline derivatives, such as BCP, or phthalimides, such as TMPP, may likewise be used.

Further advantageous hole blocking materials are described in WO 00/70655 A2, WO 01/41512 and WO 01/93642 A1.

Further, the formulation may comprise an electron blocking material (EBM) as a functional material. The electron blocking material represents a material that prevents or minimizes the transfer of electrons in a multilayer system, especially when such material is disposed in the form of a layer adjacent to the light emitting layer or the electron conducting layer. Generally, the electron blocking material has a higher LUMO level than the electron transporting material in the adjacent layer.

Basically any known electron blocking material can be used. In addition to other electron blocking materials described elsewhere in this application, advantageous electron blocking materials are transition-metal complexes such as Ir (ppz) ₃ (US 2003/0175553).

The electron blocking material may preferably be selected from amines, tri-arylamines and derivatives thereof.

Furthermore, the functional compounds which can be used as organofunctional materials in the formulations are preferably ≤ 3,000 g / mol, more preferably ≤ 2,000 g / mol and most preferably ≤ 1,000 g / mol, when these are low molecular weight compounds. mol. < / RTI >

In particular, functional compounds that are distinguished by a high glass transition temperature are also important. In this connection, particularly preferred functional compounds which can be used as organofunctional materials in formulations are those having a melting point of ≥ 70 캜, preferably ≥ 100 캜, more preferably ≥ 125 캜, and most preferably of ≥100 캜, as measured according to DIN 51005 Gt; < RTI ID = 0.0 > 150 C. < / RTI >

The formulations may also include polymers as organic functional materials. The compounds described above as organic functional materials, often of relatively low molecular weight, can also be mixed with the polymer. Likewise, such compounds may be incorporated into the polymer as covalent bonds. This is especially possible with the use of compounds substituted with reactive leaving groups such as bromine, iodine, chlorine, boronic acid or boronic acid esters, or with reactive polymerizable groups such as olefins or oxetanes. Which can be used as monomers for the preparation of corresponding oligomers, dendrimers or polymers. Wherein the oligomerization or polymerization takes place preferably via a halogen or boronic acid functional group, or via a polymerizable group. It is also possible to crosslink the polymer through this type of group. The compounds and polymers according to the present invention can be used as crosslinked or non-crosslinked layers.

Polymers which may be used as organofunctional materials often include units or structural elements described in the context of the above described compounds, especially those listed and extended in WO 02/077060 A1, WO 2005/014689 A2 and WO 2011/076314 Al do. Such documents are incorporated herein by reference. Functional materials may be derived, for example, from the following classes:

Group 1: a structural element capable of generating hole injection and / or hole transporting characteristics;

Group 2: structural elements capable of generating electron injection and / or electron transport properties;

Group 3: a structural element that combines the characteristics described in Groups 1 and 2;

Group 4: structural elements having light-emitting properties, in particular phosphors;

Group 5: a structural element that improves the transition from so-called singlet state to triplet state;

Group 6: a structural element that affects the morphology of the resulting polymer or also the emission color;

Group 7: A structural element typically used as a backbone.

Here, since the structural element can also have various functions, definite designation is not advantageous. For example, the structural element of group 1 may also act as a backbone.

The polymer having the hole transporting or hole injecting property used as the organic functional material containing the structural element of Group 1 may preferably contain units corresponding to the hole transporting or hole injecting materials described above.

More preferred structural elements of group 1 are, for example, triarylamines, benzidine, tetraaryl-para-phenylenediamine, carbazole, azulene, thiophene, pyrrole and furan derivatives, and further O- , S- or N-containing heterocycle. These aryl amines and heterocycles preferably have a HOMO (relative to the vacuum level) of greater than -5.8 eV, particularly preferably greater than -5.5 eV.

Particularly, a polymer having hole transporting or hole injecting properties, which contains at least one repeating unit of the following formula: ???????? HTP-1 ?????

Wherein the symbols have the following meanings:

Ar ¹ is a monocyclic or polycyclic aryl group, which may be the same or different, in each case, a single bond or an optionally substituted, for different repeating units;

Ar ² is a monocyclic or polycyclic aryl group which may be optionally substituted, in each case, the same or different, for different repeating units;

Ar ³ is a monocyclic or polycyclic aryl group which may be optionally substituted, in each case, the same or different, for different repeating units;

m Is 1, 2 or 3;

Particularly preferred are repeating units of the formula HTP-1 selected from the group consisting of units of the formulas HTP-1A to HTP-1C:

Wherein the symbols have the following meanings:

R ^a is in each case the same or different and is selected from H, a substituted or unsubstituted aromatic or heteroaromatic group, an alkyl, a cycloalkyl, an alkoxy, an aralkyl, an aryloxy, an arylthio, an alkoxycarbonyl, a silyl or a carboxyl, An atom, a cyano group, a nitro group or a hydroxyl group;

r Is 0, 1, 2, 3 or 4;

s Is 0, 1, 2, 3, 4 or 5].

Particularly, polymers having hole transporting or hole-injecting properties, which contain at least one repeating unit of the formula HTP-2, are preferred:

Wherein the symbols have the following meanings:

T ¹ and T ² is optionally substituted with one or more radicals R ^b, thiophene, celecoxib nopen, thieno [2,3-b] thiophene, thieno [3,2-b] thiophene, a dithiol phenothiazine ≪ / RTI > unsubstituted or substituted with one or more substituents selected from fluorine, chlorine, bromine,

R ^b is in each case halogen, -CN, -NC, -NCO, -NCS, -OCN, -SCN, -C (= O) NR ⁰ R ⁰⁰ , -C O) R ⁰ , -NH ₂ , -NR ⁰ R ⁰⁰ , -SH, -SR ⁰ , -SO ₃ H, -SO ₂ R ⁰ , -OH, -NO ₂ , -CF ₃ , -SF ₅ , To 40, optionally substituted silyl, carbyl or hydrocarbyl groups which may optionally be substituted and optionally contain one or more heteroatoms;

R ⁰ and R ⁰⁰ are each independently H or an optionally substituted carbyl or hydrocarbyl group having from 1 to 40 carbon atoms which may optionally be substituted and optionally contain one or more heteroatoms;

Ar ⁷ and Ar ⁸ are, independently of each other, a monocyclic or polycyclic aryl or heteroaryl group which may optionally be substituted and which is optionally substituted at the 2,3-position of one or both of the adjacent thiophene or selenophene groups Lt; / RTI >

c and e independently of one another are 0, 1, 2, 3 or 4, where 1 < c + e &lt;

d and f are independently of each other 0, 1, 2, 3 or 4;

Preferred examples of polymers having hole transport or hole injection properties are described in particular in WO 2007/131582 A1 and WO 2008/009343 A1.

The polymer having the electron-injecting and / or electron-transporting properties, which is used as the organic functional material containing the structural element of Group 2, may preferably contain units corresponding to the electron-injecting and / or electron-transporting materials described above .

More preferred structural elements of group 2 having electron injection and / or electron transport properties include, for example, pyridine, pyrimidine, pyridazine, pyrazine, oxadiazole, quinoline, quinoxaline and phenazine as well as triarylborane Or an additional O-, S- or N-containing heterocycle having a low LUMO level. This structural element of group 2 preferably has a LUMO (relative to the vacuum level) of less than -2.7 eV, particularly preferably less than -2.8 eV.

The organofunctional material may preferably be a polymer containing structural elements of group 3, wherein the structural elements that improve hole and electron mobility (i.e., the structural elements of groups 1 and 2) are directly connected to each other. Some of these structural elements can act as illuminants here, where the emission color can be changed to, for example, green, red or yellow. Thus, its use is advantageous, for example, in the production of other luminescent hues or broadband luminescence by the polymer which originally emitted blue light.

The polymer having the luminescence property, which is used as the organic functional material containing the structural element of group 4, may preferably contain units corresponding to the luminous material described above. Preferred are the above-described luminescent metal complexes containing corresponding units containing a polymer containing a phosphorescent group, particularly an element of the group 8 to 10 (Ru, Os, Rh, Ir, Pd, Pt).

The polymer used as the organofunctional material, containing the units of group 5, which improves the transition from the so-called singlet state to the triplet state, preferably comprises the phosphorescent compound, preferably the structural element of group 4 described above Lt; / RTI &gt; can be used for the support of polymers. A polymeric triplet matrix may be used herein.

For this purpose, in particular carbazole and linked carbazole dimer units (for example as described in DE 10304819 Al and DE 10328627 Al) are suitable. For this purpose, ketones, phosphine oxides, sulfoxide, sulfone and silane derivatives and similar compounds as described for example in DE 10349033 A1 are also suitable. Further, preferred structural units may be derived from the compounds described above in connection with the matrix material used with the phosphorescent compound.

The additional organic functional material is preferably a polymer containing units of group 6 that affect the morphology and / or emission color of the polymer. This is in addition to the above-mentioned polymers, those having at least one additional aromatic or another conjugated structure not considered among the above-mentioned groups. Thus, such groups do not affect charge-carrier mobility, non-organometallic complexes or singlet-triplet transition, or have little effect.

Structural units of this type can affect the morphology and / or emission color of the resulting polymer. Thus, depending on the structural unit, such polymers may also be used as emitters.

Thus, in the case of fluorescent OLEDs, aromatic structural elements of 6 to 40 carbon atoms or also tolane, stilbene or bistyrylarylene derivative units are preferred, each of which may be substituted with one or more radicals. Wherein 1,4-phenylene, 1,4-naphthylene, 1,4- or 9,10-anthrylene, 1,6-, 2,7- or 4,9-pyrrenylene, Or 3,10-perylenylene, 4,4'-biphenylene, 4,4'-terphenylrylene, 4,4'-bya-1,1'-naphthylene, 4,4'-tolanylene , 4,4'-stilbenylene or 4,4'-bistyrylarylene derivatives are preferably used.

The polymer used as the organic functional material preferably contains a unit of group 7 containing an aromatic structure having 6 to 40 carbon atoms, which is often used as a backbone.

These include, in particular, 4,5-dihydropylylene derivatives, 4,5,9,10-tetrahydropylylene derivatives, fluorene derivatives (such as those described in US Pat. No. 5,962,631, WO 2006/052457 A2 and WO 2006 / 118345A1) , 9,9-spirobifluorene derivatives (such as those disclosed in WO 2003/020790 A1), 9,10-phenanthrene derivatives (such as those disclosed in WO 2005/104264 A1), 9,10-di Dihydrodibenzene derivatives, and cis- and trans-indenofluorene derivatives (see, for example, WO 2004/041901 A1 and WO 2005/014689 A2), 5,7- WO 2005/056633 A1, EP 1344788 A1, WO 2007/045330 A2), and binaphthylene derivatives (for example as described in WO 2006/063852 A1), and further units 043495 A1, WO 2005/033174 A1, WO 2003/099901 A1 and DE 102006003710).

Fluorene derivatives (such as those disclosed in US 5,962,631, WO 2006/052457 A2 and WO 2006/118345 A1), spirobifluorene derivatives (such as those disclosed in WO 2003/020790 A1), benzofluorene, di The structural units of group 7 selected from benzofluorene, benzothiophene and dibenzofluorene groups, and derivatives thereof (for example as disclosed in WO 2005/056633 A1, EP 1344788 A1 and WO 2007/043495 A1) Particularly preferred.

Particularly preferred structural elements of group 7 are represented by the formula PB-1:

Wherein the symbols and indices have the following meanings:

A, B and B ', respectively, for the different repeating units are the same or different, preferably -CR ^c R ^d -, -NR ^c -, -PR ^c -, -O-, -S-, _{SO-, -SO 2 -, -CO-,} -CS-, -CSe-, -P (= O) R c -, -P (= S) R c - and -SiR ^c R ^d - is selected from 2 Lt; / RTI &gt;

R ^c and R ^d are each instance, independently, H, halogen, -CN, -NC, -NCO, -NCS , -OCN, -SCN, -C (= O) NR 0 R 00, -C (= O) X, -C (= O ) R 0, -NH 2, -NR 0 R 00, -SH, -SR 0, -SO 3 H, -SO 2 R 0, -OH, -NO 2, -CF ₃ , -SF ₅ , an optionally substituted silyl, carbyl or hydrocarbyl group having 1 to 40 carbon atoms which may optionally be substituted and optionally contain one or more heteroatoms, wherein the groups R ^c and R ^d may optionally form a spiro group with the fluorene radical bonded thereto;

X is halogen;

R ⁰ and R ⁰⁰ are each independently H, or an optionally substituted carbyl or hydrocarbyl group having from 1 to 40 carbon atoms which may optionally be substituted and optionally contain one or more heteroatoms;

g for each occurrence is independently 0 or 1 and h for each occurrence is independently 0 or 1 wherein the sum of g and h in the lower unit is preferably 1;

m is an integer of &gt; = 1;

Ar ¹ and Ar ² are, independently of each other, a monocyclic or polycyclic aryl or heteroaryl group which may optionally be substituted and which is optionally substituted at the 7,8-position or the 8,9-position of the indenofluorene group Lt; / RTI &gt;

a and b are, independently of each other, 0 or 1;

When the groups R ^c and R ^d together with the fluorene group to which these groups are attached form a spiro group, this group preferably represents spirobifluorene.

Particularly preferred are repeating units of the formula (PB-1) selected from the group consisting of units of the formulas PB-1A to PB-1E:

.

.

Wherein R ^c has the meaning described above for the formula PB-1, r is 0, 1, 2, 3 or 4 and R ^e has the same meaning as the radical R ^c .

R ^e is preferably -F, -Cl, -Br, -I, -CN, -NO 2, -NCO, -NCS, -OCN, -SCN, -C (= O) NR 0 R 00, -C (= O) X, -C (= O) R ⁰ , -NR ⁰ R ⁰⁰ , an optionally substituted silyl, aryl or heteroaryl group having 4 to 40, preferably 6 to 20, Alkoxy, alkylcarbonyl, alkoxycarbonyl, alkylcarbonyloxy or alkoxycarbonyloxy group, wherein at least one hydrogen atom is optionally substituted with F or Cl, And the radicals R ⁰ , R ⁰⁰ and X have the meanings given above for formula PB-1.

Particularly preferred are repeating units of the formula (PB-1) selected from the group consisting of units of the formulas PB-1F to PB-1I:

Wherein the symbols have the following meanings:

L is H, halogen, or optionally fluorinated, linear or branched alkyl or alkoxy group of 1 to 12 carbon atoms, preferably H, F, methyl, i-propyl, t-butyl, n-pentoxy or tri Fluoromethyl;

L 'is an optionally fluorinated, linear or branched alkyl or alkoxy group of 1 to 12 carbon atoms, preferably n-octyl or n-octyloxy.

For carrying out the invention, polymers containing more than one of the structural elements of Groups 1 to 7 described above are preferred. Further, polymers may be provided that contain more than one of the structural elements from one group described above, i. E., A mixture of structural elements selected from one group.

In particular, in addition to at least one structural element (group 4) having luminescent properties, preferably in addition to at least one phosphor, additionally selected from Groups 1 to 3, 5 or 6, preferably from Groups 1 to 3 described above Lt; RTI ID = 0.0 &gt; structural &lt; / RTI &gt;

When present in the polymer, the proportions of the various classes of groups may be in a wide range known to those skilled in the art. In each case, the proportion of one class present in the polymer, selected from the structural elements of groups 1 to 7 described above, is preferably ≥ 5 mol% in each case, particularly preferably ≥ 10 mol% in each case , An amazing advantage can be achieved.

The preparation of white luminescent copolymers is described in detail in DE 10343606 A1 in particular.

In order to improve the solubility, the polymer may contain the corresponding groups. Preferably, it is provided that the polymer contains substituents such that on average at least two non-aromatic carbon atoms per repeating unit, particularly preferably at least 4 and particularly preferably at least 8 non-aromatic carbon atoms are present (Where the mean is the number average). Here, the individual carbon atoms may be replaced by, for example, O or S. [ However, in certain ratios, optionally all repeating units may contain no substituent containing a non-aromatic carbon atom. Here, short-chain substituents are preferable because long-chain substituents can negatively affect the layer that can be obtained by using an organic functional material. The substituent preferably contains at most 12 carbon atoms, preferably at most 8 carbon atoms and particularly preferably at most 6 carbon atoms in the linear chain.

The polymers used according to the invention as organic functional materials may be random, alternating or regioregular copolymers, block copolymers or combinations of these copolymer forms.

In further embodiments, the polymer used as the organic functional material may be a non-conjugated polymer having a side chain, wherein such embodiments are particularly important in polymer-based phosphorescent OLEDs. In general, phosphorescent polymers can be obtained by free-radical copolymerization of vinyl compounds, which contain at least one unit having a phosphorescent emitter and / or at least one charge transport unit (especially in US 7250226 B2 Lt; / RTI &gt; Additional phosphorescent polymers are described in particular in JP 2007/211243 A2, JP 2007/197574 A2, US 7250226 B2 and JP 2007/059939 A.

In a more preferred embodiment, the non-conjugated polymer contains backbone units linked together by a spacer unit. Examples of such triplet light emitters based on nonconjugated polymers based on backbone units are disclosed, for example, in DE 102009023154.

In a more preferred embodiment, the non-conjugated polymer may be designed as a fluorescent light emitter. Preferred fluorescent emitters based on non-conjugated polymers having side chains contain anthracene or benzanthracene groups or derivatives of these groups in the side chain and such polymers are disclosed, for example, in JP 2005/108556, JP 2005/285661 and JP 2003/338375.

Such polymers can often be used as electron or hole transport materials, wherein such polymers are preferably designed as non-conjugated polymers.

Furthermore, the functional compounds used as organofunctional materials in the formulations preferably have a molecular weight of ≥ 10,000 g / mol, particularly preferably ≥ 20,000 g / mol and particularly preferably ≥ 50,000 g / mol for polymeric compounds M _w .

Here, the molecular weight M _w of the polymer is preferably in the range of 10,000 to 2,000,000 g / mol, particularly preferably in the range of 20,000 to 1,000,000 g / mol and very particularly preferably in the range of 50,000 to 300,000 g / mol. The molecular weight M _w is measured using GPC (= gel permeation chromatography) for internal polystyrene standards.

The above cited documents for the description of functional compounds are incorporated herein by reference for purposes of disclosure.

The formulations according to the invention may comprise all organic functional materials which are essential for the production of the respective functional layers of the electronic component. For example, when hole transport, hole injection, electron transport, or electron injection layers are constructed from exactly one functional compound, the formulation includes precisely these compounds as organic functional materials. When the light-emitting layer comprises a light-emitting body, for example in combination with a matrix or host material, the formulation can be a mixture of a matrix or a host material and a light-emitting body, as described in more detail elsewhere in the present application, .

In addition to the above components, the formulations according to the invention may comprise further additives and processing aids. These include, in particular, surface-active substances (surfactants), lubricants and greases, additives for modifying viscosity, additives for increasing conductivity, dispersants, hydrophobing agents, adhesion promoters, flow improvers, defoamers, Diluents, fillers, adjuvants, processing aids, dyes, pigments, stabilizers, sensitizers, nanoparticles and inhibitors which may be non-reactive.

The present invention further relates to a process for the production of a formulation according to the invention which comprises mixing at least one organic functional material which can be used in the production of at least a first organic solvent, a 1,1-diphenylethylene derivative, Lt; / RTI &gt;

The formulations according to the present invention can be used in the manufacture of layers or multilayer structures in which organic functional materials are present in the layer, as required for the production of the desired electronic or optoelectronic components, such as OLEDs.

The formulations of the present invention may preferably be used for the formation of a functional layer on one of the layers or on a substrate. The substrate may or may not have a bank structure.

The invention also relates to a process for the production of electronic devices, in which the formulations according to the invention are applied to a substrate and dried.

The functional layer may be formed by any suitable technique known in the art, such as, for example, flood coating, dip coating, spray coating, spin coating, screen printing, relief printing, gravure printing, rotary printing, roller coating, Or by nozzle printing, preferably by ink jet printing, either on one of the layers applied to the substrate or on the substrate.

After the formulation according to the invention is applied to the substrate or to the functional layer already applied, a drying step can be carried out to remove the solvent from the continuous phase described above. The drying can be carried out preferably at a relatively low temperature and for a relatively long period of time in order to prevent bubble formation and obtain a uniform coating. The drying may preferably be carried out at a temperature ranging from 80 to 300 캜, more preferably from 150 to 250 캜 and most preferably from 160 to 200 캜. Drying in this context may preferably be carried out at a pressure in the range of 10 ^-6 mbar to 2 bar, more preferably in the range of 10 ^-2 mbar to 1 bar and most preferably in the range of 10 ^-1 mbar to 100 mbar. During the drying process, the temperature of the substrate may vary from -15 [deg.] C to 250 [deg.] C. The duration of the drying depends on the degree of drying to be achieved, wherein a small amount of water can be removed at relatively high temperatures, and preferably in combination with the sintering to be performed.

Furthermore, the process can be provided with several different iterations, together with the formation of the same functional layer. Here, for example, as disclosed in EP 0 637 899 A1, crosslinking of the formed functional layer takes place and its dissolution can be prevented.

The present invention also relates to an electronic device obtainable by a method of manufacturing an electronic device.

The present invention further relates to an electronic device having at least one functional layer comprising at least one organic functional material obtainable by the above-mentioned method of manufacturing an electronic device.

An electronic device is understood to mean an device comprising an anode, a cathode and at least one functional layer therebetween, wherein the functional layer comprises at least one organic or organometallic compound.

The organic electronic device is preferably an organic electroluminescent device OLED, a polymeric electroluminescent device PLED, an organic integrated circuit O-IC, an organic field effect transistor O-FET, an organic thin film transistor O (O-FQD), Organic Photovoltaic (OPV) Cell, Organic Photodetector, Organic Photodetector, Organic Photovoltaic Cell (O-FQD) A light emitting electrochemical cell (LEC) or an organic laser diode (O-laser), more preferably an organic electroluminescent device (OLED) or a polymeric electroluminescent device (PLED).

The active component is generally an organic or inorganic material that is introduced between the anode and the cathode where such active components influence, maintain and / or maintain the characteristics of the electronic device, such as its performance and / For example charge injection, charge transport or charge blocking materials, especially light emitting materials and matrix materials. Thus, the organic functional material that can be used in the production of the functional layer of the electronic device preferably comprises the active component of the electronic device.

The organic electroluminescent device is a preferred embodiment of the present invention. The organic electroluminescent device includes a cathode, an anode, and at least one light-emitting layer.

Further, it is preferred to use a mixture of matrices with two or more triplet emitters. A triplet light emitting device having a shorter wavelength luminescence spectrum serves as a co-matrix for a triplet light emitting device having a longer wavelength luminescence spectrum.

In this case, the proportion of the matrix material in the light emitting layer is preferably 50 to 99.9% by volume, more preferably 80 to 99.5% by volume, and most preferably 92 to 99.5% by volume in the fluorescent light emitting layer, and 85% To 97% by volume.

Therefore, the proportion of the dopant is preferably 0.1 to 50% by volume, more preferably 0.5 to 20% by volume and most preferably 0.5 to 8% by volume in the fluorescent light-emitting layer, and 3 to 15% to be.

The light emitting layer of the organic electroluminescent device may also include a system comprising a plurality of matrix materials (mixed-matrix system) and / or a plurality of dopants. In this case as well, the dopant is generally a material with a lower proportion in the system, and the matrix material is a material with a higher proportion in the system. However, in each case, the ratio of the individual matrix materials in the system may be less than the ratio of the individual dopants.

The mixed-matrix system preferably comprises two or three different matrix materials, more preferably two different matrix materials. Here, one of the two materials is preferably a material having a hole transporting property, and the other material is a material having an electron transporting property. However, the desired electron transport and hole transport properties of the mixed-matrix component may also be combined primarily or entirely into a single mixed-matrix component wherein the additional mixed-matrix component (s) fulfills the other function . The two different matrix materials have a weight ratio of 1:50 to 1: 1, preferably 1:20 to 1: 1, more preferably 1:10 to 1: 1 and most preferably 1: 4 to 1: 1 Can be present. The mixed-matrix system is preferably used in phosphorescent organic electroluminescent devices. More detailed information on the mixed-matrix system can be found, for example, in WO 2010/108579.

In addition to these layers, the organic electroluminescent device may also include additional layers such as, in each case, at least one hole injection layer, a hole transport layer, a hole blocking layer, an electron transport layer, an electron injection layer, an exciton blocking layer, (IDMC 2003, Taiwan; Session 21 OLED (5), T. Matsumoto, T. Nakada, J. Endo, K. Mori, N. Kawamura, A. Yokoi and J. Kido, Multiphoton Organic EL Device Having Charge Generation Layer ) And / or organic or inorganic p / n junctions. Here, one or more hole transporting layers may be p-doped with, for example, metal oxides such as MoO ₃ or WO ₃ , or (per) fluorinated electron deficient aromatic compounds and / or one or more electron transporting layers may be n- . In addition, for example, an intermediate layer having an exciton blocking function in the electroluminescent element and / or controlling the charge balance can be introduced between two light emitting layers. However, it should be pointed out that these layers do not have to all exist. These layers may also be present in the use of the formulations according to the invention, as defined above.

In a further embodiment of the invention, the element comprises a plurality of layers. Here, the formulation according to the present invention can be preferably used for hole transport, hole injection, electron transport, electron injection and / or light emitting layer production.

Thus, the present invention also relates to an electronic device comprising at least three layers, but in a preferred embodiment all of said layers from hole injection, hole transport, luminescence, electron transport, electron injection, charge blocking and / Wherein at least one layer is obtained through a formulation utilized in accordance with the present invention. The thickness of the layer, for example the hole transport and / or hole injection layer, may preferably be in the range of 1 to 500 nm, more preferably in the range of 2 to 200 nm.

The device may further comprise a layer constructed of additional low molecular weight compounds or polymers that are not applied by use of the formulations according to the invention. It can also be prepared by evaporation of low molecular weight compounds in high vacuum.

It may also be desirable to use a compound that is used as a blend (blend) with any desired type of additional polymeric, oligomeric, dendritic or low molecular weight material, rather than as a pure material. This can, for example, improve the electronic properties or emit itself.

In a preferred embodiment of the present invention, the formulation according to the present invention comprises an organofunctional material used as a host material or a matrix material in the light emitting layer. Where the formulation may comprise the illuminants described above, in addition to the host material or matrix material. Here, the organic electroluminescent device may include one or more light emitting layers. When a plurality of luminescent layers are present, it is preferable that various luminescent compounds having a plurality of luminescent maximum values at 380 nm to 750 nm, i.e., fluorescence or phosphorescence, are used in the luminescent layer, so that white luminescence is wholly obtained as a whole. A three-layer system (where three layers represent blue, green and orange or red luminescence) (for the basic structure, for example WO 2005/011013) is very particularly preferred. The white luminescent device is suitable, for example, for backlighting of LCD displays or for general illumination applications.

Further, by arranging the plurality of OLEDs one over the other, efficiency can be further increased in the light yield to be achieved.

In order to improve the coupling-out of light, the final organic layer on the light-exit side of the OLED may be, for example, a nanofoam that can reduce the ratio of total reflection, Lt; / RTI &gt;

Further, one or more layers are applied by a sublimation process in which the material is deposited in a vacuum sublimation apparatus at a pressure of less than 10 ^-5 mbar, preferably less than 10 ^-6 mbar, more preferably less than 10 ^-7 mbar An organic electroluminescent device is preferable.

Further, one or more layers of the electronic device according to the invention are applied by OVPD (organic vapor phase deposition) process or with the aid of carrier-gas sublimation, wherein the material is applied at a pressure of 10 ^-5 mbar to 1 bar Can be provided.

Furthermore, one or more layers of electronic devices according to the present invention may be formed from a solution, for example by spin coating, or by any desired printing process, such as screen printing, flexographic printing or offset printing, For example, those produced by LITI (light-induced thermal imaging, thermal transfer printing) or ink-jet printing.

This layer may also be applied by a process in which the compounds of formulas (I), (II), (IIa), (III) or (IIIa) are not used. Here, preferably, an orthogonal solvent can be used which dissolves the functional material of the layer to be applied, but does not dissolve the layer to which the functional material is applied.

The device typically includes a cathode and an anode (electrode). The electrode (cathode, anode) is selected for the purposes of the present invention so that its band energy corresponds as closely as possible to the band energy of the adjacent organic layer to ensure highly efficient electron or hole injection.

The cathode preferably comprises a metal complex, a metal having a low work function, a metal alloy or a multi-layered structure (for example, an alkaline earth metal, an alkali metal, a rare metal or a lanthanoid such as Ca, Ba, Mg, Mg, Yb, Sm, and the like). In the case of a multi-layer structure, in addition to the above metals, additional metals having a relatively high work function, such as Ag and Ag nanowires (Ag NW) can also be used and in this case a combination of metals, for example Ca / Ag Or Ba / Ag is generally used. It may also be desirable to introduce a thin intermediate layer of material having a high dielectric constant between the metal cathode and the organic semiconductor. As well as alkali metal or alkaline earth metal fluoride, the corresponding oxides (e.g., LiF, Li ₂ O, BaF _2, MgO, NaF, etc.), is suitable for this purpose. The layer thickness of such a layer is preferably from 0.1 to 10 nm, more preferably from 0.2 to 8 nm, and most preferably from 0.5 to 5 nm.

The anode preferably comprises a material having a high work function. The anode preferably has a potential of greater than 4.5 eV relative to the vacuum. On the other hand, a metal having a high redox potential, such as Ag, Pt or Au, is suitable for this purpose. On the other hand, metal / metal oxide electrodes (e.g. Al / Ni / NiO _x , Al / PtO _x ) may also be preferred. In some applications, at least one of the electrodes must be transparent to facilitate the irradiation of organic materials (O-SC) or coupling out of light (OLED / PLED, O-laser). A preferred structure uses a transparent anode. Here, the preferred anode material is a conductive mixed metal oxide. Indium tin oxide (ITO) or indium zinc oxide (IZO) is particularly preferable. Furthermore, conductive doped organic materials, particularly conductive doped polymers such as poly (ethylene dioxythiophene) (PEDOT) and polyaniline (PANI), or derivatives of such polymers, are preferred. It is more preferable that the p-doped hole transporting material is applied to the anode as a hole injecting layer, wherein the suitable p-dopant is a metal oxide such as MoO ₃ or WO ₃ , or a (per) fluorinated electron deficient aromatic compound to be. A more suitable p-dopant is HAT-CN (hexacyanohexaazatriphenylene) or Novaled's compound NPD9. This type of layer facilitates hole injection into materials with low HOMO, i.e., large HOMO values.

In general, all materials used in the layer according to the prior art can be used in additional layers, and those skilled in the art can combine each of these materials with the material according to the invention in an electronic device without an inventive step.

Since the lifetime of the device is dramatically shortened in the presence of water and / or air, the device is correspondingly structured, contacted and finally hermetically sealed in a manner known per se according to the application.

The formulations according to the invention and the electronic devices obtainable therefrom, in particular organic electroluminescent devices, are distinguished by one or more of the following surprising advantages over the prior art:

One. The electronic devices obtainable using the formulations according to the invention exhibit very high stability and very long lifetimes when compared with electronic devices obtained using conventional methods.

2. Since the formulations according to the invention can be processed using conventional methods, the cost advantages thereof can also be achieved.

3. The organic functional material used in the formulations according to the present invention does not apply to any particular limitation, so that the method of the present invention can be used comprehensively.

4. The coatings obtainable using the formulations of the present invention exhibit excellent quality, especially in the uniformity of the coating.

These advantages mentioned above do not accompany degradation of other electronic properties.

It should be pointed out that variations of the embodiments described in the present invention are included in the scope of the present invention. Each feature disclosed in the present invention may be replaced with alternative features that serve the same, equivalent, or similar purpose, unless explicitly excluded. Accordingly, each feature disclosed in the present invention should be considered as an example of a general series, or an equivalent or similar feature, unless stated otherwise.

All features of the invention may be combined with one another in any manner, so long as the particular features and / or steps are not mutually exclusive. This applies in particular to the preferred features of the invention. Likewise, features of non-essential combinations may be used separately (and not as a combination).

It should also be pointed out that the many features of the invention and the features of particularly preferred embodiments are themselves inventions and should not be construed merely as part of the embodiments of the invention. With respect to this feature, protection may be pursued as an alternative to, or additionally independent of, each presently claimed invention.

The teachings of the technical acts disclosed in the present invention can be combined with extraction and other examples.

The present invention is illustrated in greater detail below with reference to working examples, but is not intended to be limiting thereof.

Those of ordinary skill in the art will be able to make additional electronic elements in accordance with the present invention without departing from the scope of the invention, and using the detailed description, thus making it possible to practice the invention throughout its claimed scope.

Example of work

All of the work examples given below were made using the device structure shown in Fig. The hole injecting layer (HIL) and the hole transporting layer (HTL) of all Examples were prepared by an inkjet printing process to achieve the desired thickness. For the luminescent layer, the individual solvents used in Examples 1 and 2 are listed in Table 2 below:

Table 2: List of solvents used in Examples 1 and 2

The viscosity of the formulation and solvent was measured using a TA instruments ARG2 rheometer over a shear rate ranging from 10 to 1000 s &lt; ^-1 &gt; using a 40 mm parallel plate geometry. Measurements were taken as an average at 200 to 800 s &lt; ^{-1 &} gt ;, where the temperature and shear rate were precisely controlled. The viscosities shown in Table 3 are the viscosities of the respective formulations measured at a temperature of 25 DEG C and a shear rate of 500 s &lt; ^-1 &gt;. Each solvent was measured three times. The viscosity values shown are averaged over the measurements.

Preferably, the organic solvent blend may have a surface tension in the range of 15 to 80 mN / m, more preferably in the range of 20 to 60 mN / m and most preferably in the range of 25 to 40 mN / m. The surface tension was measured at 20 캜 FTA (First Ten Angstrom) 1000 can be measured using a contact angle goniometer. Details of the method are described in Roger P. Woodward, Ph.D. &Quot; Surface Tension Measurements Using the Drop Shape Method &quot;, available from First Ten Angstrom. Preferably, the surface tension can be measured using a pendant drop method. All measurements were performed at room temperature ranging from 20 ° C to 25 ° C. For each formulation, three drops were measured. The final value is averaged over the measurement. The tool periodically cross checked for various liquids with well known surface tension.

Example 1 was made using the same structure in which HIL and HTL were ink jet printed to achieve the same thickness. The solvent (s) used in the EML are different and the details are listed in Table 3.

Table 3: Details of the formulations used in Example 1

Explanation of production process

The glass substrate covered with the pre-structured ITO and bank material was washed with isopropanol and then with ultrasonic in deionized water, then dried using an air gun and dried on a hot plate at 230 DEG C for 2 hours Followed by annealing.

A hole injection layer (HIL) using PEDOT-PSS (Clevios Al4083, Heraeus) was inkjet printed onto the substrate and dried in vacuum. The HIL was then annealed in air at 185 占 폚 for 30 minutes.

At the top of the HIL, a hole transport layer (HTL) was inkjet printed, dried in vacuum and annealed at 210 캜 for 30 minutes under a nitrogen atmosphere. Polymer HTM-1 was used as the material for the hole transport layer. The structure of the polymer HTM-1 is as follows:

.

.

The green light emitting layer (G-EML) was also inkjet printed, vacuum dried, and annealed at 160 DEG C for 10 minutes under a nitrogen atmosphere. The ink for the green luminescent layer contained, in all working examples, one triplet emitter (EM-1) as well as two host materials (i.e. HM-1 and HM-2). HM-2: EM-1 = 40: 40: 20. As can be seen in Table 3, only the solvent (s) differ between the examples. The structure of this material is as follows:

.

.

All inkjet printing processes were performed under yellow light and under ambient conditions.

The device was then transferred to a vacuum deposition chamber where deposition of a hole blocking layer (HBL), an electron transport layer (ETL) and a cathode (Al) was performed using thermal evaporation. The device was then characterized in a glove box.

ETM-1 was used as the hole blocking material for the hole blocking layer. The material has the following structure:

.

.

In the electron transport layer (ETL), a 50:50 mixture of ETM-1 and LiQ was used. LiQ is lithium 8-hydroxyquinolinate.

To measure OLED performance with current density-luminance-voltage performance, the device was driven with a sweeping voltage of -5 V to 25 V provided by a Keithley 2400 source measure unit. The current through the OLED device as well as the voltage for the OLED device was recorded with a Keithley 2400 SMU. The brightness of the device was measured with a calibrated photodiode. The photocurrent was measured with a Keithley 6485 / E picoammeter. For the spectrum, the brightness sensor was replaced by a glass fiber connected to the Ocean Optics USB2000 + spectrometer.

Results and discussion

Example 1

An ink jet printed OLED device was prepared with the layer printed with 1,1-diphenylethylene as the solvent for the light emitting layer. The structure of the pixelated OLED device is glass / ITO / HIL (40 nm) / HTM (20 nm) / EML (60 nm) / HBL (10 nm) / ETL (40 nm) / Al, Were pre-fabricated on a substrate to form pixelated devices. In this case, the green luminescent material was dissolved in 1,1-diphenylethylene at a concentration of 14 mg / ml.

The luminous efficiency at 1000 cd / m ² was 39.2 cd / A. The efficiency of such an OLED device is very good, and the voltage at 1000 cd / m ² is 7.05 V.

The resulting film exhibits extremely good uniform film-forming properties, as can be seen from Fig.

Comparative Example 1

An ink-jet printed OLED device is prepared with a layer printed with 3-phenoxy-toluene as a solvent for the light emitting layer. The structure of the pixelated OLED device is a glass / ITO / HIL (40 nm) / HTM (20 nm) / EML (60 nm) / HBL (10 nm) / ETL To form a pixelated device. In this case, the green luminescent material was dissolved in 1,1-diphenylethylene at a concentration of 14 mg / ml.

The luminous efficiency at 1000 cd / m ² was 47.51 cd / A. The efficiency of such an OLED device is very good and the voltage at 1000 cd / m &lt; ² &gt;

The resulting film exhibits inferior film-forming properties as compared to 1,1-diphenylethylene, as can be seen from Fig.

Claims (22)

A formulation comprising at least one organic functional material and a 1,1-diphenylethylene derivative as a first solvent. The formulation of claim 1, wherein the first organic solvent is a 1,1-diphenylethylene derivative according to formula (I):

[Wherein,
R ¹ and R ² are the same or different and are each independently selected from the group consisting of F, Cl, Br, I, NO ₂ , CN, a straight chain alkyl or alkoxy group having 1 to 20 carbon atoms or a branched or cyclic Alkyl or alkoxy group wherein one or more non-adjacent CH ₂ groups are optionally replaced by -O-, -S-, -NR ⁵ -, -CONR ⁵ -, -CO-O-, -C = O-, - or -C? C-, and at least one hydrogen atom may be replaced by F, or an aryl or heteroaryl group having from 4 to 14 carbon atoms, which may be substituted with one or more non-aromatic R ⁵ radicals may be substituted, and a plurality of substituents R ^5, together result on the same ring or two different rings, mono-substituted with a plurality of substituents R ⁵ - forming the or polycyclic, aliphatic, aromatic or heteroaromatic ring system, Lt; / RTI &gt;
R ³ and R ⁴ are the same or different and are each independently selected from the group consisting of H, F, Cl, Br, I, NO ₂ , CN, a straight chain alkyl or alkoxy group having 1 to 20 carbon atoms, A cyclic alkyl or alkoxy group wherein one or more non-adjacent CH ₂ groups are replaced by -O-, -S-, -NR ⁵ -, -CONR ⁵ -, -CO-O-, -C = O-, Or -C≡C-, and one or more hydrogen atoms may be replaced by F), or an aryl or heteroaryl group having from 4 to 14 carbon atoms which may be substituted by one or more nonaromatic R ⁵ radicals may form or polycyclic, aliphatic, aromatic or heteroaromatic ring system), in the same ring or a 2, with a plurality of substituents R ⁵ on the two different rings as a result, the mono substituted with a plurality of substituents R ⁵ ego;
R ⁵ is in each case the same or different and is a straight chain alkyl or alkoxy group of 1 to 20 carbon atoms or a branched or cyclic alkyl or alkoxy group of 3 to 20 carbon atoms in which one or more non-adjacent CH ₂ groups are replaced by -O-, -O-, -CO-O-, -C = O-, -CH = CH- or -C? C-, and at least one hydrogen atom may be replaced by F, 14 &lt; / RTI &gt; aryl or heteroaryl group, which may be substituted with one or more nonaromatic R &lt; ³ &
m and n are each the same or different and are 0, 1, 2 or 3, preferably 0 or 1, and more preferably 0. The formulation according to claim 2, wherein the first organic solvent is a 1,1-diphenylethylene derivative according to formula (I)
Wherein,
R ¹ and R ^2, wherein each the same or different from the case, the number of carbon atoms straight-chain alkyl or alkoxy group of from 1 to 20, or a branched or cyclic having 3 to 20 alkyl or alkoxy group (wherein one or more non-adjacent CH ₂ groups ^{-O-, -S-, -NR 5 -,} -CONR 5 -, -CO-O-, -C = O-, may be replaced by -CH = CH- or -C≡C-) and;
R ³ and R ⁴ are each the same or different and are H, a linear alkyl or alkoxy group having 1 to 20 carbon atoms, or a branched or cyclic alkyl or alkoxy group having 3 to 20 carbon atoms, ₂ groups ^{-O-, -S-, -NR 5 -,} -CONR 5 -, -CO-O-, -C = O- available, can be replaced by -CH = CH- or -C≡C-) and ;
R ⁵ is in each case the same or different and is a straight chain alkyl or alkoxy group of 1 to 20 carbon atoms or a branched or cyclic alkyl or alkoxy group of 3 to 20 carbon atoms in which one or more non-adjacent CH ₂ groups are replaced by -O-, -S-, -CO-O-, -C = O-, -CH = CH- or -C? C-,
m and n are each the same or different from 0 or 1, and preferably 0. The formulation according to claim 2 or 3, wherein the first organic solvent is a 1,1-diphenylethylene derivative according to formula (I)
Wherein,
R ¹ and R ² are the same or different in each case and are a straight chain alkyl group having 1 to 20 carbon atoms or a branched or cyclic alkyl group having 3 to 20 carbon atoms;
R ³ and R ⁴ are H;
m and n are each the same or different from 0 or 1, and preferably 0. 5. Formulation according to any one of claims 2 to 4, wherein the first organic solvent is 1,1-diphenylethylene according to the formula (II)

. 6. A formulation according to any one of claims 1 to 5 wherein the first solvent has a surface tension of &gt; 25 mN / m. 7. A formulation according to any one of claims 1 to 6, wherein the content of the first solvent is in the range of 50 to 100% by volume based on the total amount of the solvent in the formulation. 8. A formulation according to any one of claims 1 to 7, wherein the first solvent has a boiling point in the range from 100 to 400 &lt; 0 &gt; C. 9. A formulation according to any one of claims 1 to 8 comprising at least one second solvent different from the first solvent. 10. A formulation as claimed in any one of claims 1 to 9 wherein the second solvent has a boiling point in the range of from 100 to 400 &lt; 0 &gt; C. 11. Formulation according to any one of claims 1 to 10, wherein the at least one organic functional material has a solubility in the range of 1 to 250 g / l in the first solvent as well as in the second solvent. 12. A formulation according to any one of claims 1 to 11 having a surface tension in the range from 1 to 70 mN / m. 13. A formulation according to any one of claims 1 to 12 having a viscosity in the range of 1 to 50 mPa.s. 14. Formulation according to any one of claims 1 to 13, wherein the content of at least one organofunctional material in the formulation ranges from 0.001 to 20% by weight, based on the total weight of the formulation. The method of any one of claims 1 to 14, wherein at least one organic functional material is selected from the group consisting of an organic conductor, an organic semiconductor, an organic fluorescent compound, an organic phosphorescent compound, an organic light-absorbing compound, an organic light-sensitive compound ), Organic photosensitizing agents, and other organic photoactive compounds such as transition metal, rare earth, organometallic complexes of lanthanide and actinide. The organic electroluminescent device according to claim 15, wherein the at least one organic functional material is at least one selected from the group consisting of a fluorescent emitter, a phosphorescent emitter, a host material, a matrix material, an exciton blocking material, an electron transporting material, A formulation selected from the group consisting of a dopant, a p-dopant, a wide-band-gap material, an electron blocking material and a hole blocking material. 16. The formulation according to claim 15, wherein the at least one organic functional material is an organic semiconductor selected from the group consisting of hole injection, hole transport, light emitting, electron transport and electron injection materials. 18. The formulation according to claim 17, wherein at least one organic semiconductor is selected from the group consisting of hole injection, hole transport and light emitting materials. 19. The formulation of claim 18, wherein the hole injection and hole transport material is a polymeric compound, or a blend of a polymeric compound and a non-polymeric compound. The method of any one of claims 1 to 19, wherein at least one organic functional material and at least a first solvent are mixed. 19. A method of manufacturing an electroluminescent device, comprising: preparing at least one layer of an electroluminescent device by depositing, preferably printing, and then drying it on a surface according to one or more of claims 1 to 19. Wherein at least one layer is prepared by depositing, preferably printing, and then drying the formulation according to one or more of claims 1 to 19 on the surface.