KR20160082424A - Lightweight concrete panel having finishing material composition for building and finishing panel comprising the same - Google Patents

Lightweight concrete panel having finishing material composition for building and finishing panel comprising the same Download PDF

Info

Publication number
KR20160082424A
KR20160082424A KR1020140193038A KR20140193038A KR20160082424A KR 20160082424 A KR20160082424 A KR 20160082424A KR 1020140193038 A KR1020140193038 A KR 1020140193038A KR 20140193038 A KR20140193038 A KR 20140193038A KR 20160082424 A KR20160082424 A KR 20160082424A
Authority
KR
South Korea
Prior art keywords
weight
cement board
inorganic pigment
lightweight concrete
clay
Prior art date
Application number
KR1020140193038A
Other languages
Korean (ko)
Other versions
KR101641998B1 (en
Inventor
정영
윤영훈
Original Assignee
평택대학교 산학협력단
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 평택대학교 산학협력단 filed Critical 평택대학교 산학협력단
Priority to KR1020140193038A priority Critical patent/KR101641998B1/en
Publication of KR20160082424A publication Critical patent/KR20160082424A/en
Application granted granted Critical
Publication of KR101641998B1 publication Critical patent/KR101641998B1/en

Abstract

Disclosed is a lightweight concrete panel equipped with an eco-friendly functional finishing material composition which prevent harmful substances released from a concrete panel and has excellent sound insulation properties. To disclose the same, provided is a lightweight concrete panel comprising: a first cement board; a concrete layer arranged on an upper portion of the first cement board and equipped with Styrofoam; a second cement board arranged on an upper portion of the concrete layer; and a finishing material composition consisting of 10-20 wt% of water, 10-30 wt% of a binder, 20-40 wt% of a first pigment, and 10-30 wt% of a second pigment. According to the present invention, the surface of the lightweight concrete panel is finished with the finishing material composition, so release of harmful substances is prevented and sound insulation performance is enhanced.

Description

친환경 기능성 건축마감재 조성물이 구비된 경량 콘크리트패널, 및 상기 경량 콘크리트패널이 이중으로 배치된 마감패널{LIGHTWEIGHT CONCRETE PANEL HAVING FINISHING MATERIAL COMPOSITION FOR BUILDING AND FINISHING PANEL COMPRISING THE SAME}BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a lightweight concrete panel having an environmentally friendly functional building finishing composition, and a lightweight concrete panel having a double-

본 발명은 친환경 성능을 갖는 기능성 건축마감재 조성물이 구비된 경량 콘크리트패널, 및 상기 경량 콘크리트패널이 이중으로 배치된 마감패널에 관한 것으로, 보다 상세하게는 콘크리트로부터 방출되는 유해물질을 차단하고 우수한 차음성을 가지는 친환경 기능성 건축마감재 조성물이 구비된 경량 콘크리트패널, 및 상기 경량 콘크리트패널이 이중으로 배치된 마감패널에 관한 것이다.
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a lightweight concrete panel having a functional building finishing material composition having an environmentally friendly performance and a finishing panel in which the lightweight concrete panel is disposed in a double manner. And a finishing panel in which the lightweight concrete panel is disposed in a double-sided manner. The present invention relates to a lightweight concrete panel having an eco-friendly functional building finishing material composition.

현대식 건물은 대부분 시멘트가 주성분으로 된 콘크리트 및 벽돌로 건설되어져 인체에 해로운 물질이 방출됨과 동시에 내장재로 합성수지를 주재료로 하기 때문에 내장재로부터 방출되는 미량의 휘발성 유기화합물질이 실내 공기를 오염시키고 나아가 인체에 나쁜 영향을 미쳐 두통, 천식, 아토피성 피부염 등의 알레르기성 질환을 일으키는 문제점이 있다.Modern buildings are mostly made of concrete and brick made mainly of cement, which releases harmful substances to human body. At the same time, since synthetic resin is used as the main material, a small amount of volatile organic compounds released from the interior material pollutes indoor air, It has a problem that allergic diseases such as headache, asthma and atopic dermatitis are caused.

종래의 건축용 내외장재로는 EPS(Expanded Poly Styrene)패널, 우레탄, 그라스울(glass wool), 경량기포콘크리트(Autoclaved Lightweight Concrete), 콘크리트 PC(Prestressed Concrete) 등이다. 이러한 건축용 내외장재들은 화재에 대해 취약하며, 무게가 무거워 운반 및 시공과 가공성이 떨어져 건축 자재로서는 사용이 부적절하다. 또한, 상기 건축용 내외장재들은 단열 및 보온성이 좋을 경우 인화성이 약하고 내습성이 좋으면 통풍성이 약해서 건축용 내외장재로서의 조건을 충족시키지 못하고 있는 실정이다. Conventional architectural interior and exterior materials include EPS (Expanded Poly Styrene) panel, urethane, glass wool, lightweight foamed concrete, and concrete PC (Prestressed Concrete). These building interior and exterior materials are vulnerable to fire, and they are heavy in weight, which makes transportation, construction and workability difficult and is inadequate for construction materials. In addition, the interior and exterior materials for buildings are poor in flammability when heat insulation and warmth are good, and have poor air permeability when they are good in moisture resistance, failing to satisfy the conditions as interior and exterior materials for construction.

이러한 단점을 해결하고자, 내장재 조성물로 광촉매 및 천연물질 중에서 원적외선이 방사되거나, 흡착 및 탈취 효과가 높은 숯, 황토 등과 같은 재질을 사용하여 유해성물질을 차단하고 기능성을 향상시킨 내장재가 개발되어 왔다.In order to solve such a disadvantage, an interior material has been developed in which a far infrared ray is emitted from a photocatalyst and a natural substance by using an interior material composition, and a material such as charcoal, loess or the like having a high adsorption and deodorizing effect is used to block harmful substances and improve functionality.

예를 들면, 대한민국 공개특허 제10-2006-81158호에는 수성도료, 유성도료와, 수정, 제올라이트, 토르말린, 자수정, 생광석, 죽탄, 흑요석, 귀양석, 의왕석, 광명석, 귀신석으로 된 세라믹파우더와, 금강토 파우더로 조성된 원적외선 및 음이온을 방출하는 세라믹과 금강토를 포함하는 건축물 마감재용 조성물이 공개되어 있다. For example, Korean Patent Laid-Open No. 10-2006-81158 discloses a water-based paint, a oil-based paint, and a water-based paint comprising a crystal, zeolite, tourmaline, amethyst, ore, bamboo, obsidian, There is disclosed a composition for a building finishing material comprising a ceramic powder and a ceramic powder which emits far-infrared rays and anions, which is made of a manganese soil powder.

그리고 대한민국 공개특허 제10-2005-123039호에는 수지에멀젼과 탄산칼슘, 안료, 사문옥석, 귀양석, 경옥, 연옥으로 혼합된 사문옥석이 포함된 마감재가 공개되어 있다.Korean Patent Laid-Open No. 10-2005-123039 discloses a finishing material containing a resin emulsion, a calcium carbonate, a pigment, a sawn jade stone, a jadeite stone, a jadeite, and a silk jade mixed with nephrite.

그러나, 전술한 종래의 기술들은 수성 및 유성 도료나 수지에멀젼과 같은 재료들에 의해 유해 물질들이 방출될 수 있으며, 차음성능이 낮다는 문제점이 있다.
However, the conventional techniques described above have a problem that harmful substances can be released by materials such as water-based and oil-based paints and resin emulsions, and the sound insulation performance is low.

대한민국 공개특허 제10-2010-0017003호(2010.02.16 공개)Korean Patent Publication No. 10-2010-0017003 (published Feb. 16, 2010) 대한민국 등록특허 제10-0244170호(2000.02.01 공고)Korean Patent No. 10-0244170 (published on Mar. 2, 2000) 대한민국 공개특허 제10-2012-0126202호(2012.11.21 공개)Korean Patent Publication No. 10-2012-0126202 (published on November 21, 2012)

따라서, 본 발명의 제1 목적은 유해 물질을 방출하는 단점을 해소하여 사용 안전성을 높이며, 신규 건축물에 요구되는 차음성을 확보할 수 있는 경량 콘크리트패널을 제공하는데 있다.Accordingly, it is a first object of the present invention to provide a lightweight concrete panel capable of solving the disadvantage of releasing harmful substances to enhance safety of use, and securing a car sound required for a new building.

또한, 본 발명의 제2 목적은 유해 물질을 방출하는 단점을 해소하여 사용 안전성을 높이며, 신규 건축물에 요구되는 차음성을 확보할 수 있는 경량 콘크리트패널이 이중으로 배치된 마감패널을 제공하는데 있다.
A second object of the present invention is to provide a finishing panel in which a lightweight concrete panel capable of securing a car sound required for a new building is disposed in a double manner by eliminating the disadvantages of releasing harmful substances.

상술한 본 발명의 제1 목적을 달성하기 위하여, 본 발명의 일 실시예에서는 제1 시멘트보드와, 상기 제1 시멘트보드의 상부에 구비되며 스티로폼이 내장된 콘크리트층과, 상기 콘코리트의 상부에 구비된 제2 시멘트보드, 및 상기 제2 시멘트보드의 상부에 도포되며, 물 10 내지 20 중량%와 바인더 10 내지 30 중량%와 제1 무기안료 20 내지 40 중량%와 제2 무기안료 10 내지 30 중량%로 구성된 건축마감재 조성물을 포함하는 경량 콘크리트패널을 제공한다.In order to attain the first object of the present invention, in one embodiment of the present invention, there is provided a cement board comprising a first cement board, a concrete layer provided on the first cement board and containing styrofoam, A second cement board, and a second cement board, wherein the first cement board comprises 10 to 20% by weight of water, 10 to 30% by weight of a binder, 20 to 40% by weight of a first inorganic pigment and 10 to 30% % ≪ / RTI > by weight of a building finishing composition.

또한, 본 발명의 제2 목적을 달성하기 위하여, 본 발명의 일 실시예에서는 제1 시멘트보드와, 상기 제1 시멘트보드의 좌측에 도포되며 물 10 내지 20 중량%와 바인더 10 내지 30 중량%와 제1 무기안료 20 내지 40 중량%와 제2 무기안료 10 내지 30 중량%로 구성된 제1 건축마감재 조성물과, 상기 제1 시멘트보드의 우측에 구비되며 스티로폼이 내장된 제1 콘크리트층, 및 상기 제1 콘크리트층의 우측에 구비된 제2 시멘트보드로 구성된 제1 경량 콘크리트패널과, 상기 제1 경량 콘크리트패널의 우측에 구비된 단열재와, 상기 단열재의 우측에 형성된 중공층, 및 상기 중공층의 우측에 구비되되, 제3 시멘트보드와, 상기 제3 시멘트보드의 우측에 구비되며 스티로폼이 내장된 제2 콘크리트층, 상기 제2 콘크리트층의 우측에 구비된 제4 시멘트보드, 및 상기 제4 시멘트보드의 우측에 도포되며 물 10 내지 20 중량%와 바인더 10 내지 30 중량%와 제1 무기안료 20 내지 40 중량%와 제2 무기안료 10 내지 30 중량%로 구성된 제2 건축마감재 조성물로 구성된 제2 경량 콘크리트패널을 포함하는 마감패널을 제공한다.In order to accomplish the second object of the present invention, in an embodiment of the present invention, the first cement board and the first cement board are coated with 10 to 20% by weight of water and 10 to 30% by weight of binder, A first concrete finish composition comprising 20 to 40% by weight of a first inorganic pigment and 10 to 30% by weight of a second inorganic pigment; a first concrete layer provided on the right side of the first cement board and containing styrofoam; A first lightweight concrete panel composed of a second cement board disposed on the right side of the first concrete layer, a heat insulating material provided on the right side of the first lightweight concrete panel, a hollow layer formed on the right side of the heat insulating material, A second concrete layer provided on the right side of the third cement board and containing styrofoam, a fourth cement board disposed on the right side of the second concrete layer, and a second cement board disposed on the right side of the third cement board, And a second lightweight concrete layer composed of a second building finish composition composed of 10 to 20 wt% of water, 10 to 30 wt% of a binder, 20 to 40 wt% of a first inorganic pigment and 10 to 30 wt% of a second inorganic pigment, Thereby providing a finish panel comprising the panel.

본 발명에 의한 건축마감재 조성물이 코팅된 경량 콘크리트패널은 콘크리트로부터 방출된 유해 물질을 차단할 수 있다.The lightweight concrete panel coated with the building finishing composition according to the present invention can block the harmful substances emitted from the concrete.

또한, 본 발명은 아파트나 공동주택 건설에 사용되면 건축물의 차음성능을 향상시켜 층간 소음 및 세대 간 소음 문제를 예방할 수 있다.
Further, the present invention improves the sound insulation performance of a building when used in an apartment or a residential building, thereby preventing interlayer noise and intergenerational noise problems.

도 1은 본 발명의 일실시예에 따른 마감패널을 설명하기 위한 부분 단면도이다.
도 2는 본 발명의 일 실시예에 의한 제1 무기안료의 제조방법을 설명하기 위한 순서도이다.
도 3은 본 발명의 일 실시예에 의한 제2 무기안료의 제조방법을 설명하기 위한 순서도이다.
도 4는 유해 화학물질 방출량의 시험결과를 나타내는 인증기관 시험성적서이다.
도 5는 건축마감재 조성물의 유무에 따른 차음성능 변화 결과를 나타내는 인증기관 시험성적서이다.
1 is a partial cross-sectional view illustrating a finishing panel according to an embodiment of the present invention.
2 is a flowchart illustrating a method of manufacturing a first inorganic pigment according to an embodiment of the present invention.
3 is a flowchart illustrating a method of manufacturing a second inorganic pigment according to an embodiment of the present invention.
Fig. 4 is a certificate of the certification body test report showing the test result of the amount of the toxic chemical substance.
FIG. 5 is a certificate report of the certification body showing the result of changing the sound insulation performance depending on the presence or absence of the building finish material composition.

이하, 첨부도면을 참조하여 본 발명의 바람직한 실시예들에 의한 친환경 기능성 건축마감재 조성물이 구비된 경량 콘크리트패널(이하, '경량 콘크리트패널'이라 약칭함)을 상세하게 설명한다.
Hereinafter, a lightweight concrete panel (hereinafter abbreviated as 'lightweight concrete panel') provided with an eco-friendly functional building finishing composition according to preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

본 발명은 차폐성 및 차음성을 가지는 건축마감재(이와 같이 건축용 패널을 마감처리 하는데 사용하는 것을 시중에서는 '탄성코트'라고 칭하기도 한다) 조성물이 도포된 경량 콘크리트패널을 제공한다. The present invention provides a lightweight concrete panel coated with a construction finish material having a shielding property and a sound insulation (also referred to as " elastic coat " in this case, which is used for finishing a building panel).

상기 경량 콘크리트패널은 건축마감재 조성물과 제1 시멘트보드와 콘크리트층 및 제2 시멘트보드를 포함한다. 이하, 각 구성요소별로 구체적으로 살펴본다.
The lightweight concrete panel comprises a building finish composition, a first cement board, a concrete layer and a second cement board. Hereinafter, each component will be described in detail.

본 발명에 따른 경량 콘크리트패널은 제1 시멘트보드를 포함한다. The lightweight concrete panel according to the present invention includes a first cement board.

상기 제1 시멘트보드는 내하력을 제공하는 압축 부재 및 내화 부재로서 작용하는 것으로, 3.2㎜ 이상의 두께를 갖는 것이 바람직하다.The first cement board functions as a compression member and a refractory member for providing a load-bearing capacity, and preferably has a thickness of 3.2 mm or more.

예를 들면, 제1 시멘트보드는 포틀랜트 시멘트와 모래가 주성분으로 구성되고 셀룰로오즈 화이버(섬유소)가 보강되어 오토클레이브 양생된 고밀도 화이버 시멘트 판재로서, 평활하고 매끄러운 표면을 가져 페인트 마감이 용이하며 내수성, 내화성, 내연성을 가진 것이 바람직하다,
For example, the first cement board is a high-density fiber cement board composed of portland cement and sand as main components and reinforced with cellulose fibers (fiber) and is autoclaved. It has a smooth and smooth surface, It is preferable that it has fire resistance and flame resistance.

본 발명에 따른 경량 콘크리트패널은 콘크리트층을 포함한다. The lightweight concrete panel according to the present invention includes a concrete layer.

상기 콘크리트층은 제1 시멘트보드의 상부에 구비되는 것으로, 43.6㎜ 이상의 두께를 갖는 것이 바람직하다. 이러한 콘크리트층은 시멘트와 폴링(스티로폼 알갱이)혼합물을 배합하여 양생시킨 기포콘크리트로, 스티로폼이 내장되며 기포에 의해 흡음성이 향상된다.
The concrete layer is provided on the first cement board and preferably has a thickness of 43.6 mm or more. This concrete layer is foamed concrete cured by mixing a mixture of cement and poling (styrofoam granules). Styrofoam is built in and the sound absorption is improved by bubbles.

본 발명에 따른 경량 콘크리트패널은 제2 시멘트보드를 포함한다. The lightweight concrete panel according to the present invention includes a second cement board.

상기 제2 시멘트보드는 상기 콘크리트층의 상부에 구비된 것으로, 제1 시멘트보드와 동일한 시멘트보드가 사용될 수 있으며, 3.2㎜ 이상의 두께를 갖는 것이 바람직하다.
The second cement board is provided on the concrete layer. The second cement board may be the same cement board as the first cement board, and preferably has a thickness of 3.2 mm or more.

본 발명에 따른 경량 콘크리트패널은 건축물마감재 조성물을 포함한다.The lightweight concrete panel according to the present invention comprises a building finishing material composition.

상기 건축물마감재 조성물은 건축마감재 조성물은 물, 바인더, 제1 무기안료, 제2 무기안료를 포함한다.The building finish composition includes a building finish composition comprising water, a binder, a first inorganic pigment, and a second inorganic pigment.

보다 구체적으로, 상기 물은 건축물마감재 조성물 100 중량%를 기준으로 10 내지 20 중량%를 포함한다.More specifically, the water comprises 10 to 20 wt% based on 100 wt% of the building finish composition.

그리고 바인더는 유기 또는 무기 바인더를 사용할 수 있으며, 건축물마감재 조성물 100 중량%를 기준으로 10 내지 30 중량%를 포함한다. 보다 구체적으로, 상기 바인더로는 아크릴계 고분자, 실리콘계 고분자, 수성 우레탄계 및 아크릴-실리콘 공중합 고분자물질로 이루어지는 군에서 하나 이상 선택되는 고분자 합성 에멀전을 사용할 수 있다. 상기 바인더를 10 중량% 미만의 양으로 사용하는 경우, 본 발명에 의한 건축마감재 조성물(110)의 접착력과 내수성 및 내구성이 저하되고, 30 중량%를 초과하여 사용하는 경우 제1 무기안료 및 제2 무기안료의 기능이 저하되어 차폐 및 차음 등의 기능성을 저하시킨다. The binder can be an organic or inorganic binder and comprises 10 to 30% by weight based on 100% by weight of the building finish composition. More specifically, the binder may be at least one polymer synthetic emulsion selected from the group consisting of an acrylic polymer, a silicone polymer, an aqueous urethane polymer, and an acrylic-silicone copolymer polymer material. When the binder is used in an amount of less than 10% by weight, the adhesive strength, water resistance and durability of the building finishing composition 110 according to the present invention are lowered. When the binder is used in an amount exceeding 30% by weight, The function of the inorganic pigment is deteriorated and the functionality such as shielding and sound insulation is lowered.

또한, 상기 제1 무기안료는 건축물마감재 조성물 100 중량%를 기준으로 20 내지 40 중량%를 포함한다. Also, the first inorganic pigment includes 20 to 40% by weight based on 100% by weight of the building finishing composition.

구체적으로, 제1 무기안료는 다공질 분상체 100 중량부를 기준으로 소다장석 100 내지 120 중량부, 내화점토 110 내지 130 중량부, 도석 100 내지 120 중량부, 토르말린 100 내지 120 중량부, 그리고 흑활석 12 내지 18 중량부를 포함한다. Specifically, the first inorganic pigment comprises 100 to 120 parts by weight of soda feldspar, 110 to 130 parts by weight of refractory clay, 100 to 120 parts by weight of tourmaline, 100 to 120 parts by weight of tourmaline and 100 to 120 parts by weight of black talc 12 To 18 parts by weight.

먼저, 상기 다공질 분상체는 각 성분들을 미세입자로 가공하여 다공질 표면적을 증대시켜 혼합 사용하는 것으로, 규조토, 백토, 황토, 차점토, 알로펜, 패분, 이산화규소, 산화칼슘, 수산화칼슘, 탄산칼슘, 숯, 활성탄, 벤토나이트, 버미큘라이트, 세피올라이트, 제올라이트, 포졸란 및 마크로시멘트로 이루어진 군에서 하나 이상이 선택되어 사용될 수 있다. First, the porous particles are prepared by processing each of the components into fine particles to increase the surface area of the porous particles to be mixed and used. Examples of the porous particles include diatomaceous earth, clay, loess, tea clay, allopen, peat, silicon dioxide, calcium oxide, calcium hydroxide, At least one selected from the group consisting of coal, activated carbon, bentonite, vermiculite, sepiolite, zeolite, pozzolan and macrocement can be selected and used.

상기 규조토는 천연광물점토를 구성하는 주성분으로서, 다공질의 미세한 입자들로 구성되어 있으며, 새집증후군의 원인인 포름알데히드의 저감 기능이 뛰어나다. 특히, 일본에서는 실내공기 중의 휘발성 유기화합물(Volatile Organic Compounds; VOCs)에 따른 오염을 저감시키는 건축재로 인증을 받았을 정도이다. The diatomaceous earth is a main constituent of natural mineral clay, and is composed of porous fine particles, and has excellent function of reducing formaldehyde which is a cause of sick house syndrome. Especially, in Japan, it has been certified as a building material that reduces pollution caused by Volatile Organic Compounds (VOCs) in indoor air.

상기 백토, 황토, 차점토는 다공질 미세한 입자들로 뛰어난 습도조절기능을 지니고 있는 천연광물이다. 상기 세피올라이트와 제올라이트는 연구기관의 실험 결과, 냄새의 제거와 경감 효과가 단순한 규조토벽 및 다른 제품들보다도 뛰어난 것으로 확인되고 있다. The clay, loess, and tea clay are porous fine particles, which are natural minerals having excellent humidity control. The above-mentioned sepiolite and zeolite have been found to be superior to simple diatomaceous earth walls and other products as a result of the research institute's experiments.

상기 알로펜은 화산재의 천연광물점토를 구성하는 주성분으로서, 다공질의 미세한 입자들로 구성되어 있으며, 새집증후군의 원인인 포름알데히드의 저감 기능이 뛰어나다는 장점을 가지고 있는 것으로 알려져 있다. 그리고 알로펜은 다공질의 미세한 입자들로 뛰어난 습도조절기능을 지니고 있는 화산재를 주재료로 만들어져 규조토의 4내지 5배, 조습벽지의 15배에 이르는 흡, 방습 능력을 지닌 것으로 알려져 있다. 또한 알로펜은 실내의 습도가 높을 경우 습기를 흡수해 습도를 낮추고, 습도가 낮을 때는 반대로 습기를 방출한다. 때문에 생활공간의 최적습도(50% 내지 60%)를 유지, 잡균의 번식억제를 통한 알레르기, 아토피 질환 등을 예방할 수 있다. 한편 한국연구기관의 실험 결과 악취의 주성분인 암모니아, 트리메칠아민 등의 알카리성 냄새와 석화수소, 메틸머캡탄 등의 산성 냄새 성분에도 효과를 갖고 있다. 냄새의 제거와 경감 효과가 규조토벽 및 다른 제품들보다도 뛰어난 것으로 입증되고 있다.  Allopen is a major component of natural mineral clay of volcanic ash, and it is known that it has the advantage of being excellent in the function of reducing formaldehyde, which is a cause of sick house syndrome, composed of porous fine particles. And allopen is porous fine particles, which is made of volcanic ash, which has excellent humidity control function, and is known to have absorption and desorptive ability of 4 to 5 times of diatomaceous earth and 15 times of humidity wall paper. Alopen also absorbs moisture when the humidity is high in the room and lowers the humidity when the humidity is low. Therefore, it is possible to maintain the optimum humidity (50% to 60%) of the living space, to prevent the allergy and the atopic disease by suppressing the propagation of the germs. On the other hand, the results of experiments conducted by Korean research institutes have shown that they have an effect on alkaline odors such as ammonia and trimethylamine, which are major components of odor, and acid odor components such as hydrogen sulfide and methylmercaptan. Odor removal and mitigation effects have been demonstrated to be superior to diatomite walls and other products.

상기 패분, 이산화규소, 산화칼슘, 수산화칼슘, 탄산칼슘, 숯, 활성탄, 벤토나이트, 버미큘라이트, 포졸란 등은 유기바인더 또는 무기바인더와 혼합하여 사용 할 수 있는 것이다. The above-mentioned powder, silicon dioxide, calcium oxide, calcium hydroxide, calcium carbonate, charcoal, activated carbon, bentonite, vermiculite and pozzolan can be mixed with an organic binder or an inorganic binder.

상기 마이크로시멘트는 자체의 수화작용으로 인하여 물과의 혼합에 의해 단단한 강도를 구성하며, 역시 수화작용에 의해 다양한 형상으로 성형할 수 있다. 이러한 마이크로시멘트는 무기질계 지반주입재와 각종 보수용재 또는 보강용재에 적합하도록 개발된 미립자 시멘트로서, 일반적인 미립자 시멘트의 특성인 조강성, 고강도, 고내구성은 물론 균일한 입경 크기가 요구되는 지반주입재와 보수보강재에 탁월한 성능을 발휘한다. Due to the hydration of the microcement, the microcement constitutes a rigid strength by mixing with water, and can be formed into various shapes by hydration. These micro cements are particulate cements that are developed to be suitable for inorganic ground fillers and various repair or reinforcement materials. They are widely used as ground fillers and maintenance materials that require uniform grain size as well as roughness, high strength and high durability, Excellent performance for stiffeners.

상기 마이크로시멘트의 특성으로는 미 분말이므로 활성화가 빠르게 진행하여 조기강도가 우수하고, 치밀한 매트릭스를 조직하므로 강도 발현율이 우수하고, 입경이 고르고 최대입경 크기가 작아 침투성이 우수하고, 염과 산 등의 유해물에 대한 내화학성이 탁월하여 우수한 내구성을 가진다. Since micro-cement has a fine powder, the micro-cement is rapidly activated and its early strength is excellent. Since a dense matrix is formed, the microcement is excellent in strength development rate, excellent in permeability because of its uniform particle size and small maximum particle size, Excellent chemical resistance against harmful substances and excellent durability.

상기 소다장석은 건축마감재 조성물(110)에 100 중량부 미만으로 사용되면 내오염성 및 부착력이 저하되며, 120 중량부를 초과의 양으로 사용되면 건축마감재의 도막 내오염성이 떨어지는 문제가 발생한다.If the soda feldspar is used in an amount less than 100 parts by weight, the stain resistance and adhesion of the soda feldspar may be decreased. If the soda feldspar is used in an amount exceeding 120 parts by weight, the stain resistance of the building finishing material may deteriorate.

또한, 상기 내화점토는 상술한 차점토와 달리 난연성능을 개선하기 위한 내화 성분이 있는 점토이다. 상기 내화점토를 110 중량부 미만으로 사용되면 내화성능이 저하되며, 130 중량부를 초과하여 사용되면 건축마감재의 내오염성이 저하되는 문제점이 있다. The refractory clay is a clay having refractory components for improving the flame retardancy, unlike the above-mentioned clay. When the refractory clay is used in an amount of less than 110 parts by weight, the fire resistance is deteriorated. When the refractory clay is used in an amount exceeding 130 parts by weight, the stain resistance of the building finishing material is deteriorated.

또한, 상기 도석은 본 조성물을 경량 콘크리트 패널에 도포되는 경우 적은 횟수의 칠 작업으로도 일정한 두께를 형성하는 역할을 수행한다. 상기 도석의 사용량이 100 중량부 미만이면 건축마감재의 최적의 도막 두께를 나타낼 수 없으며, 120 중량부를 초과하면 건축마감재의 내구성, 내수성이 떨어져 본 발명의 목적을 달성하기 어렵다. In addition, when the composition is applied to a lightweight concrete panel, the stones serve to form a constant thickness even with a few times of firing. If the amount of stones used is less than 100 parts by weight, the optimum coating film thickness of the building finish material can not be exhibited. If the amount of the stones is more than 120 parts by weight, durability and water resistance of the building finish material are difficult to achieve the object of the present invention.

상기 토르말린과 흑활석의 사용량이 각각 40 중량부와 12 중량부 미만이면, 건축마감재의 물리적 특성 중 결로방지 성능이 저하된다. 그리고 토르말린과 흑활석의 사용량이 각각 50 중량부와 18 중량부를 초과하면, 건축마감재의 내오염성이 열화되는 문제가 발생한다. If the amount of the tourmaline and the amount of the black talc used is less than 40 parts by weight and less than 12 parts by weight, the dew condensation preventing performance among the physical properties of the building finishing material is lowered. When the amounts of tourmaline and black talc used are more than 50 parts by weight and 18 parts by weight, respectively, the stain resistance of the building finish material deteriorates.

한편, 상기 제2 무기안료는 건축물마감재 조성물 100 중량%를 기준으로 10 내지 30 중량%를 포함한다. 이러한 제2 무기안료는 다공질 분상체와 내화점토를 포함한다.On the other hand, the second inorganic pigment includes 10 to 30% by weight based on 100% by weight of the building finishing composition. The second inorganic pigment includes a porous particulate and refractory clay.

구체적으로, 제2 무가안료는 다공질 분상체 70 내지 80 중량%를 포함한다. 이러한 다공질 분상체로는 규조토, 백토, 황토, 차점토, 알로펜, 패분, 이산화규소, 산화칼슘, 수산화칼슘, 탄산칼슘, 숯, 활성탄, 벤토나이트, 버미큘라이트, 세피올라이트, 제올라이트, 포졸란 및 마크로시멘트로 이루어진 군에서 하나 이상 선택되는 것이 사용될 수 있다. Specifically, the second unbranched pigment comprises 70 to 80% by weight of the porous particulate. Examples of such a porous powder include porous materials such as diatomaceous earth, clay, loess, tea clay, alopen, peat, silicon dioxide, calcium oxide, calcium hydroxide, calcium carbonate, charcoal, activated carbon, bentonite, vermiculite, sepiolite, zeolite, pozzolan, May be used.

이때, 다공질 분상재료의 사용량이 70중량% 미만인 경우 본 발명의 기능성 특성인 차폐성 및 차음성이 저하되며, 80 중량%를 초과하면 건축마감재의 수축력이 높아져 표면 크랙이 발생하는 원인이 된다.If the amount of the porous polymeric material is less than 70% by weight, the functional characteristics of the present invention, such as shielding ability and sound insulation, are lowered. If the amount is more than 80% by weight, shrinkage of the building finish material is increased.

그리고 본 발명의 제2 무기안료는 내화점토 20 내지 30 중량%를 포함한다. 이때, 내화점토의 사용량이 20 중량% 미만이면 내화성능이 저하되며, 30 중량%를 초과하면 건축마감재의 내오염성이 저하된다.
And the second inorganic pigment of the present invention comprises 20 to 30% by weight of refractory clay. If the amount of the refractory clay is less than 20 wt%, the refractory performance is deteriorated. If the amount is more than 30 wt%, the stain resistance of the building finish material is deteriorated.

본 발명에서는 상기 두 종류의 무기안료가 구별되어 사용되고 있다. In the present invention, the two kinds of inorganic pigments are used separately.

먼저 제1 무기안료는 다공질 분상재료의 배합구성비를 적게 구성하고 기타 광물의 배합비를 높게 분산시킨 것으로, 본 건축마감재 조성물(110)의 기본적인 물리적 특성(내오염성, 부착력, 내수성, 내후성, 결로방지 등) 및 기능성(차폐성 및 차음성)을 구현하는 구성성분이다. First, the first inorganic pigment is a composition in which the blending ratio of the porous particulate material is small and the mixing ratio of the other minerals is high. The basic inorganic particulate material of the present architectural finishing composition 110 (basic stain resistance, adhesion, water resistance, weather resistance, ) And functionality (shielding and car audio).

반면 제2 무기안료는 다공질 분상재료의 배합구성비를 높게 하여 본 기술의 기능적의 특성(차폐성 및 차음성)을 극대화시켜 제공하는 것을 목적으로 한다. On the other hand, the second inorganic pigment is intended to maximize the functional characteristics (shielding property and sound insulation) of the present invention by increasing the composition ratio of the porous polymeric material.

필요에 따라, 본 발명에 따른 건축마감재 조성물(110)은 그 점도를 증가시키기 위하여 증점제 0.1 내지 0.8 중량%와 첨가제 2 내지 3.0 중량%를 더 포함할 수 있다. If desired, the building finish composition 110 according to the present invention may further comprise 0.1 to 0.8% by weight of a thickener and 2 to 3.0% by weight of an additive to increase its viscosity.

상기 증점제는 셀루로오스 유도체와 폴리아크릴산 중합체를 포함하는 알카리계 증점제를 사용하며, 틱소트로피 인덱스(thixotropy index) 값이 1이하인 것을 사용하는 것이 바람직하다.The thickener is preferably an alkaline thickener containing a cellulose derivative and a polyacrylic acid polymer, and preferably has a thixotropy index of 1 or less.

상기 첨가제로는 분산제, 동결방지제, 소포제, pH조절제 등을 예시할 수 있다. 구체적으로, 분산제로는 나프탈렌 술폰산염 포르말린 축합물, 멜라민 술폰산염 포르말린 축합물, 폴리카르복산 화합물, 폴리카르복산 에테르, 방향족 아미노술폰산 폴리머 및 리그닌 술폰산의 금속염으로 이루어진 그룹으로부터 선택된 하나 이상의 물질이 사용될 수 있으며, 동결방지제로는 프로필렌글리콜, 에틸렌글리콜을 사용할 수 있다. 또한, 소포제로는 미네랄 오일계, 실리콘계 또는 기타 계열의 소포제가 사용될 수 있으며 pH 조절제는 2-아미노-2-메틸-1-프로페놀을 사용할 수 있다.
Examples of the additives include a dispersing agent, a cryoprotectant, a defoaming agent, a pH adjusting agent, and the like. Specifically, as the dispersing agent, at least one material selected from the group consisting of a naphthalenesulfonate-formalin condensate, a melamine sulfonate-formalin condensate, a polycarboxylic acid compound, a polycarboxylic acid ether, an aromatic aminosulfonic acid polymer and a metal salt of ligninsulfonic acid may be used Propylene glycol and ethylene glycol may be used as the anti-freezing agent. The antifoaming agent may be mineral oil type, silicone type or other antifoaming agent. The pH adjusting agent may be 2-amino-2-methyl-1-propanol.

도 1은 본 발명에 따른 마감패널을 설명하기 위한 부분 단면도이다. 1 is a partial cross-sectional view illustrating a finishing panel according to the present invention.

도 1을 참조하면, 본 발명에 따른 마감패널은 제1 경량 콘크리트패널(100)과, 단열재(200)와, 중공층(300), 제2 경량 콘크리트패널(200)을 포함한다. Referring to FIG. 1, a finishing panel according to the present invention includes a first lightweight concrete panel 100, a heat insulating material 200, a hollow layer 300, and a second lightweight concrete panel 200.

상기 제1 경량 콘크리트패널(100)은 제1 시멘트보드와, 상기 제1 시멘트보드의 좌측에 도포되며 물 10 내지 20 중량%와 바인더 10 내지 30 중량%와 제1 무기안료 20 내지 40 중량%와 제2 무기안료 10 내지 30 중량%로 구성된 제1 건축마감재 조성물(110)과, 상기 제1 시멘트보드의 우측에 구비되며 스티로폼이 내장된 제1 콘크리트층, 및 상기 제1 콘크리트층의 우측에 구비된 제2 시멘트보드로 구성된다. 여기서, 상기 제1 콘크리트층은 전술한 콘크리트층과 동일한 구성이다.The first lightweight concrete panel 100 comprises a first cement board and a second cement board, which is applied on the left side of the first cement board and comprises 10 to 20 wt% of water, 10 to 30 wt% of a binder, 20 to 40 wt% A first concrete finishing layer 110 formed on the right side of the first cement board and containing styrofoam, and a second concrete finishing layer 110 disposed on the right side of the first concrete layer. And a second cement board. Here, the first concrete layer has the same structure as the above-described concrete layer.

상기 단열재(200)는 상기 제1 경량 콘크리트패널(100)의 우측에 구비된 것으로, 유리면보온재(glass wool), 암면판, 화이바보드, 셀룰로우즈단열재, 미네랄울보온재, 퍼라이트판, 폴리에스터 섬유단열재, 와이어 단열보드, 발포폴리스티렌판, 하이폴, 스티로폼, 발포폴리에틸렌보온재, 폴리우레탄보드 중 어느 하나가 사용될 수 있으나, 유리면보온재를 사용하는 것이 바람직하다. 이는, 유리면보온재가 셀 형태(충분한 공기층과 단섬유의 특성) 영향과 소음의 고주파수 대역(2,000Hz이상)의 소음을 흡음하여 차음성능 개선에 효과적이기 때문이다.The heat insulating material 200 is provided on the right side of the first lightweight concrete panel 100 and includes a glass wool, a rock wool board, a fiber board, a cellulose heat insulator, a mineral wool insulating material, Any one of a heat insulating material, a wire insulating board, a foamed polystyrene plate, a high pole, a styrofoam, a foamed polyethylene insulating material and a polyurethane board may be used, but a glass surface insulating material is preferably used. This is because the glass surface insulating material is effective in improving the sound insulation performance by absorbing the influence of the cell shape (characteristics of the sufficient air layer and the short fiber) and the noise of the high frequency band (over 2,000 Hz) of the noise.

상기 중공층(300)은 마감패널의 차음성 및 단열성을 극대화시키기 위해 단열재(200)의 우측에 형성된 것으로, 마감패널의 외형을 제공하며 제1 경량 콘크리트패널(100)과 단열재(200)와 제2 경량 콘크리트패널(400)을 일열로 내삽시키는 하우징(미도시)에 의해 형성된다. 특히, 중공층에 형성된 공기층은 중.고주파수 대역(500~4,000Hz)의 소음을 흡음하여 차음성능 개선에 효과적이다.The hollow layer 300 is formed on the right side of the heat insulating material 200 in order to maximize the sound insulation and heat insulation of the finished panel. The hollow layer 300 provides a contour of the finished panel and includes the first lightweight concrete panel 100, the heat insulating material 200, (Not shown) for inserting two lightweight concrete panels 400 in a row. Particularly, the air layer formed in the hollow layer absorbs noise in the middle and high frequency band (500 to 4,000 Hz), and is effective in improving sound insulation performance.

상기 제2 경량 콘크리트패널(400)은 상기 중공층(300)의 우측에 구비되는 것으로, 제3 시멘트보드와, 상기 제3 시멘트보드의 우측에 구비되며 스티로폼이 내장된 제2 콘크리트층, 상기 제2 콘크리트층의 우측에 구비된 제4 시멘트보드, 및 상기 제4 시멘트보드의 우측에 도포되며 물 10 내지 20 중량%와 바인더 10 내지 30 중량%와 제1 무기안료 20 내지 40 중량%와 제2 무기안료 10 내지 30 중량%로 구성된 제2 건축마감재 조성물(410)로 구성된다.The second lightweight concrete panel 400 is provided on the right side of the hollow layer 300 and includes a third cement board, a second concrete layer provided on the right side of the third cement board and having styrofoam, 2 concrete layer and a fourth cement board provided on the right side of the fourth cement board and comprising 10 to 20% by weight of water, 10 to 30% by weight of a binder, 20 to 40% by weight of a first inorganic pigment, And a second building finish material composition 410 composed of 10 to 30% by weight of an inorganic pigment.

이러한 제1 경량 콘크리트패널(100)과 제2 경량 콘크리트패널(400)은 전술한 경량 콘크리트패널과 동일한 구성이므로, 보다 구체적인 설명은 생략한다.
Since the first lightweight concrete panel 100 and the second lightweight concrete panel 400 have the same configuration as the lightweight concrete panel described above, a detailed description thereof will be omitted.

본 발명은 차폐성 및 차음성을 가지는 건축마감재 조성물의 제조방법을 제공한다. 본 발명에 의한 기능성 건축마감재 조성물의 제조방법은 제1 무기 안료를 제조하는 단계, 제2 무기 안료를 제조하는 단계, 및 물 10 내지 20 중량%와 바인더 10 내지 30 중량%와 상기 제1 무기안료 20 내지 40 중량% 및 상기 제2 무기안료 10 내지 30 중량%를 혼합하는 단계를 포함한다. SUMMARY OF THE INVENTION The present invention provides a method of making a building finishing composition having shielding and car audio. The process for producing a functional building finishing composition according to the present invention comprises the steps of preparing a first inorganic pigment, preparing a second inorganic pigment, and mixing 10 to 20% by weight of water, 10 to 30% 20 to 40% by weight of the first inorganic pigment and 10 to 30% by weight of the second inorganic pigment.

여기서, 상기 제1 무기안료는 다음의 방법으로 제조된다. 도 2는 본 발명의 일 실시예에 의한 제1 무기안료의 제조방법을 설명하기 위한 순서도이다. Here, the first inorganic pigment is prepared by the following method. 2 is a flowchart illustrating a method of manufacturing a first inorganic pigment according to an embodiment of the present invention.

먼저, 규조토, 백토, 황토, 차점토, 알로펜, 패분, 이산화규소, 산화칼슘, 수산화칼슘, 탄산칼슘, 숯, 활성탄, 벤토나이트, 버미큘라이트, 세피올라이트, 제올라이트, 포졸란 및 마크로시멘트로 이루어진 군에서 하나 이상 선택되는 다공질 분상체 100 중량부, 소다장석 100 내지 120 중량부, 내화점토 110 내지 130 중량부, 도석 100 내지 120 중량부, 토르말린 40 내지 50 중량부, 및 흑활석 12 내지 18 중량부를 혼합하여 혼합물을 수득한다(S110). First, one of the group consisting of diatomaceous earth, clay, loess, tea clay, alopen, peat, silicon dioxide, calcium oxide, calcium hydroxide, calcium carbonate, charcoal, activated carbon, bentonite, vermiculite, sepiolite, zeolite, pozzolan and macrocement 100 to 120 parts by weight of soda feldspar, 110 to 130 parts by weight of refractory clay, 100 to 120 parts by weight of stones, 40 to 50 parts by weight of tourmaline and 12 to 18 parts by weight of talc are mixed A mixture is obtained (Sl 10).

이어서, 상기 혼합물에 물을 넣어 반죽하여 반죽물을 얻는다(S120).Subsequently, water is added to the mixture and kneaded to obtain a kneaded product (S120).

그 다음, 상기 반죽물을 습식 분쇄하여 습식분쇄물을 얻는다(S130). 구체적으로 알루미나 볼로 구성된 통상의 볼밀로 12 내지 15시간 동안 분쇄하여 직경이 75 내지 95 ㎛로 습식분쇄 한다. Then, the kneaded product is subjected to wet pulverization to obtain a wet pulverized product (S130). Specifically, the mixture is pulverized for 12 to 15 hours with a conventional ball mill composed of alumina balls and wet-milled to a diameter of 75 to 95 mu m.

여기서, 볼밀의 분쇄시간을 12 시간미만으로 할 경우 목표로 하는 평균적인 입경의 크기(75 내지 95 ㎛)보다 크게 분쇄되어 다공질 미세입자들의 표면적이 적게 되므로 차폐 및 차음기능이 저하되는 원인이 된다. 반대로 15시간을 초과하여 분쇄하는 경우 목표의 입경의 크기(95 ㎛)로 보다 작은 입경의 광물들로 분쇄되어 미세입자들의 다공질 특성이 저하되어 차폐 및 차음 기능이 저하되는 원인이 되며, 건축마감재의 제조 시 혼합 및 분산시간의 증가로 열이 발생되어 물리적 특성의 변화 원인이 된다. If the grinding time of the ball mill is less than 12 hours, the grinding time of the ball mill is larger than the target average particle size (75 to 95 탆), and the surface area of the porous fine particles becomes small, which causes the shielding and sound insulating functions to deteriorate. On the other hand, when crushing for more than 15 hours, the target particle size (95 탆) is crushed into minerals having a smaller particle size, and the porous properties of the fine particles are lowered, thereby lowering the shielding and sound insulating function. Heat is generated by the increase of mixing and dispersing time during manufacture, which causes the change of physical properties.

계속하여, 상기 습식분쇄물을 건조하여 건조파우더를 얻는다(S140). Subsequently, the wet pulverized product is dried to obtain a dry powder (S140).

구체적으로 설명하면, 고압 분사 건조기(spray dryer)에 이송시켜, 분무 건조하여 파우더의 수분이 약 4.5 내지 5.5중량% 되도록 건조 파우더를 제조한다. 여기서 파우더의 수분이 4.5 중량% 미만이면 물질에 있는 무해한 미생물들이 활동이 저하되며, 건축마감재 조성물(110)의 제조 시 바인더의 고형분외 수분을 흡수하여 표면의 미세 크랙을 발생시키는 원인이 된다. 그리고 파우더의 수분이 5.5 중량%를 초과하면 물질의 미세한 입자들의 다공질 특성을 저하시켜 차음기능을 저하시키는 문제가 발생된다. Specifically, the powder is transferred to a high-pressure spray dryer and spray-dried to produce a dry powder such that the moisture content of the powder is about 4.5 to 5.5 wt%. If the moisture content of the powder is less than 4.5% by weight, the harmless microorganisms in the material may be deteriorated in activity and absorb moisture outside the solid content of the binder during the production of the building finishing material composition 110, causing microcracks on the surface. If the water content of the powder exceeds 5.5% by weight, the porous property of the fine particles of the material is lowered, thereby deteriorating the sound insulating function.

연속하여, 상기 건조파우더를 숙성시킨다(S150). 예를 들면, 상기 건조파우더를 사일로(silo)로 이송시켜, 사일로안에서 약 24시간 동안 숙성 시킬 수 있다. Subsequently, the dry powder is aged (S150). For example, the dried powder can be transferred to a silo and aged in a silo for about 24 hours.

마지막으로, 상기 숙성파우더를 성형하여 안료를 제작한다(S160). 이 단계에서는 숙성된 건조 파우더를 건식 성형기(press)에 투입하여 상기 제1 무기안료를 제조한다.
Finally, the aged powder is molded to produce a pigment (S160). In this step, the aged dry powder is put into a dry press to produce the first inorganic pigment.

그리고 상기 제2 무기안료는 다음의 방법으로 제조된다. 상기 제2 무기안료의 제조방법은 사용되는 원재료나 일부 공정조건 등을 제외하면, 상기 제1 무기안료의 제조방법과 유사한다. 도 3은 본 발명의 일 실시예에 의한 제2 무기안료의 제조방법을 설명하기 위한 순서도이다. The second inorganic pigment is prepared in the following manner. The method for producing the second inorganic pigment is similar to the method for producing the first inorganic pigment except for the raw materials to be used and some process conditions. 3 is a flowchart illustrating a method of manufacturing a second inorganic pigment according to an embodiment of the present invention.

도 3을 참조하면, 먼저, 규조토, 백토, 황토, 차점토, 알로펜, 패분, 이산화규소, 산화칼슘, 수산화칼슘, 탄산칼슘, 숯, 활성탄, 벤토나이트, 버미큘라이트, 세피올라이트, 제올라이트, 포졸란 및 마크로시멘트로 이루어진 군에서 하나 이상 선택되는 다공질 분상체 70 내지 80 중량%, 내화점토 20 내지 30 중량%를 혼합하여 혼합물을 수득한다(S210). Referring to FIG. 3, at first, the diatomaceous earth, clay, loess, tea clay, alopen, peat, silicon dioxide, calcium oxide, calcium hydroxide, calcium carbonate, char, activated carbon, bentonite, vermiculite, sepiolite, zeolite, 70 to 80% by weight of a porous particle selected from the group consisting of cement, and 20 to 30% by weight of refractory clay are mixed to obtain a mixture (S210).

이어서, 상기 혼합물에 물을 넣어 반죽하여 반죽물을 얻는다(S220).Subsequently, water is added to the mixture and kneaded to obtain a kneaded product (S220).

그 다음, 상기 반죽물을 습식 분쇄하여 습식분쇄물을 얻는다(S230). 구체적으로 알루미나 볼로 구성된 통상의 볼밀로 12 내지 15시간 동안 분쇄하여 직경이 75 내지 95 ㎛로 습식분쇄한다. Next, the kneaded product is wet-milled to obtain a wet milled product (S230). Specifically, the mixture is pulverized for 12 to 15 hours with a conventional ball mill composed of alumina balls and wet-milled to a diameter of 75 to 95 mu m.

여기서, 볼밀의 분쇄시간을 12 시간미만으로 할 경우 목표로 하는 평균적인 입경의 크기(75 내지 95 ㎛)보다 크게 분쇄되어 다공질 미세입자들의 표면적이 적게 되므로 차폐 및 차음기능이 저하되는 원인이 된다. 반대로 15시간을 초과하여 분쇄하는 경우 목표의 입경의 크기(95 ㎛)로 보다 작은 입경의 광물들로 분쇄되어 미세입자들의 다공질 특성이 저하되어 차폐 및 차음기능이 저하되는 원인이 되며, 건축마감재의 제조 시 혼합 및 분산시간의 증가로 열이 발생되어 물리적 특성의 변화 원인이 된다. If the grinding time of the ball mill is less than 12 hours, the grinding time of the ball mill is larger than the target average particle size (75 to 95 탆), and the surface area of the porous fine particles becomes small, which causes the shielding and sound insulating functions to deteriorate. On the other hand, when crushing for more than 15 hours, the target particle size (95 탆) is crushed into minerals having a smaller particle size, and the porous properties of the fine particles are lowered, thereby lowering the shielding and sound insulating function. Heat is generated by the increase of mixing and dispersing time during manufacture, which causes the change of physical properties.

계속하여, 상기 습식분쇄물을 건조하여 건조파우더를 얻는다(S240). Subsequently, the wet pulverized product is dried to obtain a dry powder (S240).

구체적으로 설명하면, 고압 분사 건조기(spray dryer)에 이송시켜, 분무 건조하여 파우더의 수분이 약 5.5∼6.5 중량% 되도록 건조 파우더를 제조한다. 여기서 파우더의 수분이 5.5 중량% 미만이면 물질에 있는 무해한 미생물들이 활동이 저하되며, 건축마감재 조성물(110)의 제조 시 바인더의 고형분외 수분을 흡수하여 표면의 미세 크랙을 발생시키는 원인이 된다. 그리고 파우더 수분이 6.5 중량%를 초과하면 물질의 미세한 입자들의 다공질 특성을 저하시켜 차음기능을 저하시키는 문제가 발생된다. Specifically, the powder is transferred to a high-pressure spray dryer and spray-dried to produce a dry powder such that the moisture content of the powder is about 5.5 to 6.5 wt%. If the moisture content of the powder is less than 5.5% by weight, the harmless microorganisms in the material may be deteriorated in activity and absorb moisture outside the solid content of the binder during the production of the building finishing material composition 110, causing microcracks on the surface. If the powder water content exceeds 6.5% by weight, the porous property of the fine particles of the material is lowered and the sound insulating function is deteriorated.

연속하여, 상기 건조파우더를 숙성시킨다(S250). 예를 들면, 상기 건조파우더를 사일로(silo)로 이송시켜, 사일로안에서 약 24시간 동안 숙성 시킬 수 있다. Subsequently, the dry powder is aged (S250). For example, the dried powder can be transferred to a silo and aged in a silo for about 24 hours.

마지막으로, 상기 숙성파우더를 성형하여 안료를 제작한다(S260). 이 단계에서는 숙성된 건조 파우더를 건식 성형기(press)에 투입하여 상기 제2 무기안료를 제조한다.
Finally, the aged powder is molded to produce a pigment (S260). In this step, the aged dry powder is put into a dry press to produce the second inorganic pigment.

이하, 본 발명을 구체적인 실시예를 통하여 보다 구체적으로 설명한다. 다만, 하기 실시예 및 실험예는 예시적인 것으로 본 발명의 권리범위 등이 제한되는 것으로 해석되어서는 아니된다.Hereinafter, the present invention will be described more specifically with reference to specific examples. However, the following examples and experimental examples are illustrative and should not be construed as limiting the scope of the present invention.

가. 제1 무기안료 제조end. Preparation of the First Inorganic Pigment

규조토, 차점토, 알로펜, 패분, 수산화칼슘, 탄산칼슘, 숯, 활성탄, 벤토나이트, 제올라이트, 포졸란 또는 마이크로시멘트를 균일한 무게로 혼합하여 준비한 다공질 분상체 20g, 소다장석 22g, 내화점토 24g, 도석 22g, 토르말린 9g, 흑활석 3g을 혼합하였다. 20 g of porous particles prepared by mixing diatomaceous earth, tea clay, alopenes, peat, calcium hydroxide, calcium carbonate, charcoal, activated carbon, bentonite, zeolite, pozzolan or micro cement in a uniform weight, 22 g of soda feldspar, 24 g of refractory clay, , 9 g of tourmaline and 3 g of talc.

이어서, 물 50g을 넣어 반죽한 다음, 알루미나 볼로 구성된 통상의 볼밀로 15시간 동안 분쇄하여 직경크기가 90 ㎛로 습식분쇄 하였다.Subsequently, 50 g of water was kneaded, kneaded for 15 hours in a conventional ball mill composed of alumina balls, and wet pulverized to a diameter of 90 탆.

계속하여, 고압 분사 건조기에 이송시켜, 분무 건조하여 파우더의 수분이 약 4.8중량(%) 되게 건조 파우더를 제조하였다.Subsequently, the mixture was transferred to a high-pressure spray dryer, and spray-dried to prepare a dry powder in which the water content of the powder was about 4.8 wt%.

그 다음 사일로로 이송시켜, 사일로안에서 24시간 동안 숙성 시킨 후에, 숙성된 건조 파우더를 건식 성형기(PRESS)에 투입하여 제1 무기안료를 제조하였다.
The mixture was then transferred to a silo and aged in a silo for 24 hours. Then, the aged dry powder was put into a dry press (PRESS) to prepare a first inorganic pigment.

나. 제2 무기안료 제조 I. Preparation of Second Inorganic Pigment

규조토, 차점토, 알로펜, 패분, 수산화칼슘, 탄산칼슘, 숯, 활성탄, 벤토나이트, 제올라이트, 포졸란 또는 마이크로시멘트를 균일한 무게로 혼합하여 준비한 다공질 분상체 76g, 내화점토 24g을 혼합하였다. 76 g of porous particles prepared by mixing diatomaceous earth, tea clay, alopenes, peat, calcium hydroxide, calcium carbonate, charcoal, activated carbon, bentonite, zeolite, pozzolan or microcement at a uniform weight and 24 g of refractory clay were mixed.

이어서, 물 50g을 넣어 반죽한 다음, 알루미나 볼로 구성된 통상의 볼밀로 15시간 동안 분쇄하여 직경크기가 90 ㎛로 습식분쇄 하였다.Subsequently, 50 g of water was kneaded, kneaded for 15 hours in a conventional ball mill composed of alumina balls, and wet pulverized to a diameter of 90 탆.

계속하여, 고압 분사 건조기에 이송시켜, 분무 건조하여 파우더의 수분이 약 5.2중량(%) 되도록 건조 파우더를 제조하였다.Subsequently, the mixture was transferred to a high-pressure spray dryer, and spray-dried to prepare a dry powder such that the water content of the powder was about 5.2% by weight.

그 다음 사일로로 이송시켜, 사일로 안에서 24시간 동안 숙성 시킨 후에, 숙성된 건조 파우더를 건식 성형기(PRESS)에 투입하여 제1 무기안료를 제조하였다.
The mixture was then transferred to a silo and aged in a silo for 24 hours. Then, the aged dry powder was put into a dry press (PRESS) to prepare a first inorganic pigment.

다. 건축마감재 조성물의 제조All. Manufacture of architectural finish composition

상기 제1 무기안료 80g, 상기 제2 무기안료 50g, 물 40g, 바인더인 천일워터텍스8000/9000 60g을 투입하여 건축마감재 조성물을 제조하였다. 이때 측정된 기능성 건축마감재 조성물의 함수율은 14%이었다.
80 g of the first inorganic pigment, 50 g of the second inorganic pigment, 40 g of water, and 60 g of a binder, Chunil Watertex 8000/9000, were added to prepare a finish material composition. The water content of the functional building finish composition measured was 14%.

[실시예][Example]

1. 3.2㎜ 두께의 제1 시멘트보드의 우측에 스티로폼이 내장된 43.6㎜ 두께의 콘크리트층을 배치하고, 상기 콘크리트층의 우측에 3.2㎜ 두께의 제2 시멘트보드를 배치한 후, 제1 시멘트보드의 좌측에 건축마감재 조성물을 2㎜ 두께로 도포하고 건조시켜 제1 경량 콘크리트패널을 제작하였다.1. A 43.6 mm thick concrete layer with styrofoam embedded was placed on the right side of a first cement board having a thickness of 3.2 mm and a second cement board having a thickness of 3.2 mm was placed on the right side of the concrete layer, And the first lightweight concrete panel was manufactured by drying the composition.

2. 3.2㎜ 두께의 제3 시멘트보드의 우측에 스티로폼이 내장된 43.6㎜ 두께의 콘크리트층을 배치하고, 상기 콘크리트층의 우측에 3.2㎜ 두께의 제4 시멘트보드를 배치한 후, 제4 시멘트보드의 우측에 건축마감재 조성물을 2㎜ 두께로 도포하고 건조시켜 제2 경량 콘크리트패널을 제작하였다.2. A 43.6 mm thick concrete layer containing styrofoam was placed on the right side of a third cement board having a thickness of 3.2 mm and a fourth cement board having a thickness of 3.2 mm was placed on the right side of the concrete layer, A second finishing concrete panel was prepared by applying a composition of construction finishing composition to a thickness of 2 mm on the right side and drying it.

2. 제1 경량 콘크리트패널의 우측에 50㎜ 두께의 유리면보온재(밀도 32㎏/㎥)를 배치하였다.2. On the right side of the first lightweight concrete panel, a 50 mm thick glass surface insulating material (density 32 kg / m3) was placed.

3. 상기 유리면보온재의 우측에 50㎜ 두께의 중공층을 형성하고, 상기 중공층의 우측에 상기 제2 경량 콘크리트패널을 배치하여 마감패널을 제작하였다.
3. A 50 mm thick hollow layer was formed on the right side of the glass surface insulating material, and the second lightweight concrete panel was disposed on the right side of the hollow layer to prepare a finished panel.

[비교예][Comparative Example]

실시예와 동일한 방법으로 마감패널을 제작하되, 제1 시멘트보드와 제4 시멘트보드 모두에 건축마감재 조성물이 구비되지 않도록 마감패널을 제작하였다.
A finished panel was produced in the same manner as in Example 1 except that the first cement board and the fourth cement board were not provided with the construction finishing composition.

[실험예 1][Experimental Example 1]

한국산업기술시험원을 통해 실내공기질 공정시험기준 ES 02131.1(실험 규격 및 방법)로 실시예를 통해 제작된 마감패널의 차폐성능을 실험하였다. 그 결과는 [도 4]로 나타내었다.The shielding performance of the finished panels manufactured through the examples was tested with the indoor air quality process test standard ES 02131.1 (experimental specification and method) through Korea Industrial Technology Development Center. The results are shown in Fig.

측정결과 본 발명에 따른 마감패널은 포름알데하이드의 방출량(㎎/㎡h)이 0.001이며 아세트알데하이드, 벤젠, 톨루엔, 자일렌, 스틸렌 등의 방출량은 0.000으로, 콘크리트에 의한 유해 물질 방출의 차단이 탁월하게 이루어지고 있음을 확인할 수 있었다.
As a result, the release amount of formaldehyde (0.001) and the amount of acetaldehyde, benzene, toluene, xylene, styrene and the like were 0.000, and the release of harmful substances by concrete was excellent In the case of

[실험예 2][Experimental Example 2]

한국건설생활환경시험연구원을 통해 실시예와 비교예를 통해 제작된 마감패널의 음향감쇠계수를 측정하였다. 그 결과는 [표 1]과 [도 5]로 나타내었다.The acoustic attenuation coefficients of the finished panels fabricated through the examples and comparative examples were measured through Korea Institute of Construction & Living Environment Test. The results are shown in [Table 1] and [Figure 5].

[표 1][Table 1]

Figure pat00001

Figure pat00001

측정결과 본 발명에 따른 마감패널은 차음감쇠계수가 43으로, 건축마감재 조성물이 적용되지 않는 마감패널(차음감쇠계수 36)에 비해 음의 전달에 대한 차단이 탁월하게 이루어지고 있음을 확인할 수 있었다.
As a result of the measurement, it was confirmed that the finish panel according to the present invention had a sound attenuation coefficient of 43, which is superior to the finishing panel (sound attenuation coefficient 36) to which the building finish material composition is not applied.

이상에서 본 발명의 바람직한 실시예를 참조하여 설명하였지만, 해당 기술분야의 숙련된 당업자는 하기의 특허청구범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다.
It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit and scope of the invention as defined in the appended claims. It can be understood that it is possible.

110 : 건축마감재 조성물 120 : 제1 시멘트보드
130 : 콘크리트층 140 : 제2 시멘트보드
200 : 단열재 300 : 중공층
410 : 건축마감재 조성물 420 : 제3 시멘트보드
430 : 제2 콘크리트층 440 : 제4 시멘트보드
110: building finish composition 120: first cement board
130: Concrete layer 140: Second cement board
200: Insulation material 300: Hollow layer
410: building finish composition 420: third cement board
430: second concrete layer 440: fourth cement board

Claims (5)

제1 시멘트보드;
상기 제1 시멘트보드의 상부에 구비되며 스티로폼이 내장된 콘크리트층;
상기 콘코리트층의 상부에 구비된 제2 시멘트보드; 및
상기 제2 시멘트보드의 상부에 도포되며, 물 10 내지 20 중량%와 바인더 10 내지 30 중량%와 제1 무기안료 20 내지 40 중량%와 제2 무기안료 10 내지 30 중량%로 구성된 건축마감재 조성물을 포함하는 경량 콘크리트패널.
A first cement board;
A concrete layer provided on the first cement board and having a built-in styrofoam;
A second cement board provided on an upper portion of the concollet layer; And
A composition of a building finish comprising 10 to 20% by weight of water, 10 to 30% by weight of a binder, 20 to 40% by weight of a first inorganic pigment and 10 to 30% by weight of a second inorganic pigment, applied on top of the second cement board, Contains lightweight concrete panels.
제 1 항에 있어서, 상기 건축마감재 조성물은
증점제 0.1 내지 0.8 중량%; 및
첨가제 2 내지 3 중량%를 더 포함하는 것을 특징으로 하는 경량 콘크리트패널.
2. The composition of claim 1, wherein the architectural finish composition comprises
0.1 to 0.8 wt% of a thickener; And
And 2 to 3% by weight of an additive.
제 1 항에 있어서, 상기 제1 무기안료는
규조토, 백토, 황토, 점토, 알로펜, 패분, 이산화규소, 산화칼슘, 수산화칼슘, 탄산칼슘, 숯, 활성탄, 벤토나이트, 버미큘라이트, 세피올라이트, 제올라이트, 포졸란, 마이크로시멘트로 이루어진 군에서 하나 이상 선택되는 다공질 분상체 100 중량부;
소다장석 100 내지 120 중량부;
내화점토 110 내지 130 중량부;
도석 100 내지 120 중량부;
토르말린 40 내지 50 중량부; 및
흑활석 12 내지 18 중량부를 포함하는 것을 특징으로 하는 경량 콘크리트패널.
The method according to claim 1, wherein the first inorganic pigment is
At least one member selected from the group consisting of diatomaceous earth, clay, loess, clay, alopen, peat, silicon dioxide, calcium oxide, calcium hydroxide, calcium carbonate, charcoal, activated carbon, bentonite, vermiculite, sepiolite, zeolite, pozzolan, 100 parts by weight of a porous particulate material;
100 to 120 parts by weight of soda feldspar;
110 to 130 parts by weight of refractory clay;
100 to 120 parts by weight of stones;
40 to 50 parts by weight of tourmaline; And
And 12 to 18 parts by weight of black talc.
제 1 항에 있어서, 상기 제2 무기안료는
규조토, 백토, 황토, 차점토, 알로펜, 패분, 이산화규소, 산화칼슘, 수산화칼슘, 탄산칼슘, 숯, 활성탄, 벤토나이트, 버미큘라이트, 세피올라이트, 제올라이트, 포졸란 및 마크로시멘트로 이루어진 군에서 하나 이상 선택되는 다공질 분상체 70 내지 80 중량%; 및
내화점토 20 내지 30 중량%로 구성된 것을 특징으로 하는 경량 콘크리트패널.
The method according to claim 1, wherein the second inorganic pigment is
At least one selected from the group consisting of diatomaceous earth, clay, loess, tea clay, alopen, peat, silicon dioxide, calcium oxide, calcium hydroxide, calcium carbonate, charcoal, activated carbon, bentonite, vermiculite, sepiolite, zeolite, pozzolan and macrocement 70 to 80% by weight of the porous particles; And
And 20 to 30% by weight of refractory clay.
제1 시멘트보드와, 상기 제1 시멘트보드의 좌측에 도포되며 물 10 내지 20 중량%와 바인더 10 내지 30 중량%와 제1 무기안료 20 내지 40 중량%와 제2 무기안료 10 내지 30 중량%로 구성된 제1 건축마감재 조성물과, 상기 제1 시멘트보드의 우측에 구비되며 스티로폼이 내장된 제1 콘크리트층, 및 상기 제1 콘크리트층의 우측에 구비된 제2 시멘트보드로 구성된 제1 경량 콘크리트패널;
상기 제1 경량 콘크리트패널의 우측에 구비된 단열재;
상기 단열재의 우측에 형성된 중공층; 및
상기 중공층의 우측에 구비되되, 제3 시멘트보드와, 상기 제3 시멘트보드의 우측에 구비되며 스티로폼이 내장된 제2 콘크리트층, 상기 제2 콘크리트층의 우측에 구비된 제4 시멘트보드, 및 상기 제4 시멘트보드의 우측에 도포되며 물 10 내지 20 중량%와 바인더 10 내지 30 중량%와 제1 무기안료 20 내지 40 중량%와 제2 무기안료 10 내지 30 중량%로 구성된 제2 건축마감재 조성물로 구성된 제2 경량 콘크리트패널을 포함하는 마감패널.
A first cement board, a first cement board, a second cement board, and a second cement board, wherein the first cement board comprises 10 to 20% by weight of water, 10 to 30% by weight of a binder, 20 to 40% by weight of a first inorganic pigment and 10 to 30% A first lightweight concrete panel composed of a first building finish material composition, a first concrete layer provided on the right side of the first cement board and containing styrofoam, and a second cement board disposed on the right side of the first concrete layer;
A heat insulating material provided on the right side of the first lightweight concrete panel;
A hollow layer formed on the right side of the heat insulating material; And
A third cement board provided on the right side of the hollow layer, a second concrete layer provided on the right side of the third cement board and containing styrofoam, a fourth cement board disposed on the right side of the second concrete layer, A second building finishing material composition applied on the right side of the fourth cement board and consisting of 10 to 20% by weight of water, 10 to 30% by weight of a binder, 20 to 40% by weight of a first inorganic pigment and 10 to 30% And a second lightweight concrete panel constructed of a second lightweight concrete panel.
KR1020140193038A 2014-12-30 2014-12-30 Lightweight concrete panel having finishing material composition for building and finishing panel comprising the same KR101641998B1 (en)