KR20130067396A - Capply for radial tire enhancing adhesion with belt using daul compounds - Google Patents
Capply for radial tire enhancing adhesion with belt using daul compounds Download PDFInfo
- Publication number
- KR20130067396A KR20130067396A KR1020110134437A KR20110134437A KR20130067396A KR 20130067396 A KR20130067396 A KR 20130067396A KR 1020110134437 A KR1020110134437 A KR 1020110134437A KR 20110134437 A KR20110134437 A KR 20110134437A KR 20130067396 A KR20130067396 A KR 20130067396A
- Authority
- KR
- South Korea
- Prior art keywords
- rubber
- belt
- cap
- cap ply
- tire
- Prior art date
Abstract
Description
본 발명은 벨트부와의 접착력이 향상된 이종의 고무를 사용한 캡플라이에 관한 것으로, 더욱 상세하게는 벨트층에 부착되는 캡플라이 고무는 스틸 코드와의 접착력이 높은 검 에지 부 컴파운드를 사용하고 캡플라이 상층 고무에는 기존에 캡플라이 고무를 사용하여 벨트 층과의 접착력이 향상된 캡플라이에 관한 것이다.
The present invention relates to a cap ply using different types of rubber with improved adhesion to a belt portion, and more particularly, to a cap ply attached to a belt layer using a rubber edge compound having high adhesion to a steel cord, The present invention relates to a cap ply having improved adhesion to a belt layer using a cap ply rubber as an upper layer rubber.
자동차용 공기입 타이어는 크게 인너라이너(InnerLiner), 카카스(Carcass), 벨트(Belt) 및 벨트 보강층, 트래드부가 있다.Pneumatic tires for automobiles include InnerLiner, Carcass, Belt, Belt reinforcing layer, and Tread part.
벨트층은 트래드와 카카스 사이에 위치하는 코드층으로서 트래드부의 강성을 높이는 역할 및 타이어에 가하지는 힘을 카카스 층에 전달하여 내구성능에 중요한 역활을 수행한다. 그러나, 타이어가 주행하는 중에 발생하는 지속적인 굴신운동으로 인해 벨트 끝단에 마찰열과 전단응력이 집중되어 벨트 세퍼레이션(Belt Seperation)이 발생하는 문제점이 있어 캡플라이, 1벨트와 2벨트 사이에 벨트 쿠션(Belt Cusion), 벨트 양끝단에 검에지(Gum edge) 등을 적용하여 벨트부의 내구성능을 보강하고 있다.The belt layer is a cord layer positioned between the tread and the carcass, and plays a role in enhancing the rigidity of the tread portion and transmitting the force applied to the tire to the carcass layer to play an important role in durability performance. However, there is a problem that the friction heat and the shearing stress are concentrated on the end of the belt due to the continuous bending motion generated during the running of the tire, so that there is a problem that the belt separation occurs. Accordingly, the cap fly, the belt cushion Belt Cusion, and Gum edge on both ends of the belt to reinforce the durability of the belt.
캡플라이는 타이어의 하중을 지지하며, 벨트의 움직임을 최소화시키고, 주행 시 발생하는 굴신운동에 대한 내 피로성, 내열성을 견디는 역할을 하며 타이어의 내구성능에 중요한 역할을 한다. 그러나 섬유 코드 압연물로 이루어진 캡플라이는 벨트 끝단에 있는 스틸 코드와의 접착력이 떨어져 벨트 끝단에 발생하는 세퍼레이션 현상을 막는데 한계가 있다.The cap fly supports the load of the tire, minimizes the movement of the belt, and endures fatigue and heat resistance against the bending motion generated during driving, and plays an important role in tire durability. However, the cap ply made of the fiber cord rolled material has a limitation in preventing separation phenomenon occurring at the end of the belt due to the adhering force to the steel cord at the end of the belt.
일반적으로 사용하는 벨트 에지에 적용되는 검 에지는 길이는 약 15~25㎜, 두께는 5~15㎜를 가지며 벨트 부의 재단공정 중에 부착된다.The gum edge applied to a commonly used belt edge has a length of about 15 to 25 mm and a thickness of 5 to 15 mm and is attached during the cutting process of the belt portion.
그러나, 검에지에 의해 보강되는 벨트 끝단에 비해 벨트 중앙부의 10~50% 두께가 얇아짐에 따른 벨트 중앙부 함몰에 의해 팽이 권취현상 및 재단 공정이 용이하지 않고 공정이 복잡하여 많은 공정비가 발생하는 문제점이 있다.
However, as the thickness of 10 ~ 50% of the center of the belt is thinner than the belt edge reinforced by the gum edge, the top winding phenomenon and the cutting process are not easy due to depression of the center of the belt, .
종래기술은 벨트 세퍼레이션을 막기 위해 적용된 벨트 검에지는 벨트 중앙부와 벨트 끝단의 두께 차에 의해 벨트 중앙부가 함몰되어 팽이 권취현상 및 재단 성형 공정에서 작업성의 문제점이 있다. 또한 캡플라이의 적용한 경우에는 벨트 부에 사용되는 스틸코드와의 접착력이 떨어져 벨트 세퍼레이션 현상을 막는데 한계가 있다In the prior art, there is a problem in that the center portion of the belt is recessed due to the thickness difference between the center portion of the belt and the end portion of the belt, which is applied to prevent belt separation. In addition, when the cap ply is applied, the adhesive strength to the steel cord used in the belt portion is reduced, which limits the belt separating phenomenon
상기의 문제점을 해결하기 위해 안출된 본 발명의 목적은, 벨트층에 부착되는 캡플라이 고무는 스틸 코드와의 접착력이 높은 검 에지 부 컴파운드를 사용하고 캡플라이 상층 고무에는 기존에 캡플라이 고무를 사용하여 벨트 층과의 접착력이 향상된 캡플라이가 적용된 공기입 타이어를 제공하는 데에 있다.
SUMMARY OF THE INVENTION It is an object of the present invention, which is devised to solve the above-described problems, to provide a rubber composition for a cap ply rubber, which uses a rubber edge compound having high adhesion to a steel cord, And a pneumatic tire to which a cap ply having improved adhesion to the belt layer is applied.
상기의 목적을 달성하기 위한 본 발명은, 공기입 타이어에서 벨트부의 양단부를 덮는 캡플라이에 있어서, 상기 캡플라이는, 상기 벨트부와 접하는 하부고무와, 상기 하부고무에 배치되는 코드와, 상기 코드 상에 설치되는 상부고무를 포함하고, 상기 하부고무는 검엣지 고무로 이루어지는 것을 특징으로 한다.In order to achieve the above object, the present invention provides a cap ply covering both ends of a belt portion in an air-inlet tire, wherein the cap ply includes a lower rubber contacting the belt portion, And the lower rubber is made of gum edge rubber.
또, 상기 하부고무와 상기 상부고무의 비율이 50~140%인 것을 특징으로 한다.
The ratio of the lower rubber to the upper rubber is 50 to 140%.
본 발명은 공기입 타이어의 벨트 층 분리현상이나 유동성 성능이 개선됨에 따라 타이어의 내구성능이 향상되는 효과가 있다.The present invention has the effect of enhancing the durability of the tire as the belt layer separation phenomenon and fluidity performance of the pneumatic tire are improved.
특히, 종래에 사용되는 검에지 대비 공정성 및 경제성이 뛰어나며, 캡플라이의 문제점인 벨트와의 접착력이 향상되어 벨트 세퍼레이션을 효과적으로 예방할 수 있다.
Particularly, it is excellent in fairness and economical efficiency compared to a conventional gum edge, and the adhesive force to the belt, which is a problem of the cap ply, is improved, so that belt separation can be effectively prevented.
도 1은 본 발명에 따른 캡플라이가 적용된 공기입 타이어의 단면도이다.1 is a sectional view of a pneumatic tire to which a cap ply according to the present invention is applied.
이하, 본 발명을 바람직한 실시예를 첨부한 도면을 참조하여 설명하기로 한다. 또, 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 공지 기능 및 구성에 대한 상세한 설명은 생략한다. 따라서, 도 1에 도시된 공기입 타이어(100)를 구성하는 트레드부(102), 인너라이너(104), 벨트부(106), 및 비드부(110)에 대한 상세한 설명은 생략한다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, preferred embodiments of the present invention will be described with reference to the accompanying drawings. In the following description, well-known functions or constructions are not described in detail since they would unnecessarily obscure the gist of the present invention. Therefore, detailed description of the
본 발명에서는, 캡플라이 제조에 있어 벨트부(106)과 만나는 캡플라이(108) 하부에 위치하는 하부고무(114)에는 스틸코드 및 벨트고무와의 접착력이 높은 검에지 고무를 사용하고, 캡플라이(108)의 상부에 위치하는 상부고무(116)에는 기존의 캡플라이 고무를 사용하여 상기의 문제를 해결하고자 한다.In the present invention, gum edge rubber having high adhesion to the steel cord and the belt rubber is used for the
이 때, 사용되는 캡플라이 고무는 공지의 기술을 사용할 수 있다. 일예로써, 이러한 타이어 캡플라이용 고무조성물의 원료고무로서 천연고무와 합성고무를 각각 단독으로 사용하거나 또는 천연고무와 합성고무가 1:9∼9:1의 비로 혼합된 혼합고무를 사용하거나 또는 두 개 이상의 합성고무를 혼합한 혼합고무를 사용할 수 있으며, 이러한 원료고무에 아라미드 펄프를 원료고무 100중량부에 대하여 0.5∼3.0중량부 포함할 수 있다.At this time, a known technique can be used for the cap ply rubber used. For example, natural rubber and synthetic rubber may be used alone as raw material rubbers for the rubber composition for use in tire caps, or mixed rubbers mixed at a ratio of 1: 9 to 9: 1 may be used for natural rubber and synthetic rubbers, Mixed rubber obtained by mixing at least one synthetic rubber may be used. The raw rubber may contain 0.5 to 3.0 parts by weight of aramid pulp relative to 100 parts by weight of the raw rubber.
상기에서 합성고무는 스티렌 부타디엔 고무(SBR), 부타디엔 고무(BR), 이소프렌 고무(IR), 클로로프렌 고무(CR), 니트릴고무(NBR), 부틸고무 중에서 선택된 어느 하나 이상을 사용할 수 있다. The synthetic rubber may be at least one selected from the group consisting of styrene butadiene rubber (SBR), butadiene rubber (BR), isoprene rubber (IR), chloroprene rubber (CR), nitrile rubber (NBR) and butyl rubber.
또, 검에지 고무 역시 공지의 기술을 사용할 수 있다. 일예로, 상기의 목적을 달성하기 위한 본 발명의 스트립 고무조성물은 코발트 염을 포함하는 스트립 고무조성물에 있어서, 원료고무 100phr에 대하여 보강성 수지 1.5∼2.0phr, 경화제 2.5∼3.0phr 포함할 수 있다.A known technique can also be used for the gum edge rubber. For example, the strip rubber composition of the present invention may comprise 1.5 to 2.0 phr of a reinforcing resin and 2.5 to 3.0 phr of a curing agent, based on 100 phr of raw rubber, in a strip rubber composition comprising a cobalt salt .
원료고무는 종래 타이어용 스트립 고무조성물의 원료고무로서 사용할 수 있는 것이라면 어떠한 것이라도 사용할 수 있으며, 이러한 원료고무로는 천연고무나 스티렌 부타디엔 고무, 부타디엔 고무, 이소프렌이함유된 스티렌 부타디엔 고무, 니트릴을 포함하는 스티렌 부타디엔 고무, 네오프렌 고무와 같은 합성고무를 각각 단독으로 사용하거나 또는 둘 이상의 합성고무가 동일한 비로 혼합된 혼합고무를 사용할 수 있다. 또한 상기의 천연고무와 합성고무가 1:9∼9:1의 비로 혼합된 혼합고무를 사용할 수 있다.Any raw rubber that can be used as raw material rubber for a strip rubber composition for a conventional tire can be used. Examples of the raw rubber include natural rubber, styrene butadiene rubber, butadiene rubber, styrene butadiene rubber containing isoprene, nitrile And synthetic rubbers such as styrene-butadiene rubber and neoprene rubber may be used alone, or a mixed rubber in which two or more synthetic rubbers are mixed at the same ratio may be used. Further, a mixed rubber in which the natural rubber and the synthetic rubber are mixed at a ratio of 1: 9 to 9: 1 can be used.
또, 검에지 고무의 고무조성물은 벨트 및/또는 카카스에 포함되어 있는 스틸코드 및/또는 패브릭코드와 같은 보강성 재료와 의 모듈러스 차이를 감소시키기 위해 보강성 수지로서 페놀기를 함유하는 수지를 원료고무 100phr에 대하여 1.5∼2.0phr를 첨가할 수 있다.In addition, the rubber composition of gum edge rubbers is preferably used as a reinforcement resin to reduce the difference in modulus with reinforcing materials such as steel cord and / or fabric cord contained in the belt and / or carcass, 1.5 to 2.0 phr can be added to 100 phr of the rubber.
그리고, 상기 상부고무(116)와 상기 하부고무(114) 사이에 설치되는 코드(112) 공지의 기술이며, 나일론6,6, 폴리에스터(Polyester), 아라미드(Aramid), 하이브리드(Hybrid), PEN 코드 등을 사용할 수 있다. 상기 코드(112)의 두께는 0.8㎜~1.8㎜ 두께를 사용하는 것이 좋다. 1.8㎜이상의 두께를 가진 캡플라이를 벨트 끝단에 경우, 타이어 주행 시 편마모 현상 등 내구성능이 떨어질 수 있다. A
상기 캡플라이는 벨트 층 형성 전 후에 엔드리스 방식으로 적층되는 엣지 캡플라이로서 벨트 엣지부의 형상이나 폭이나 캡플라이 코드 재질 등의 특성은 크게 중요하지 않으나 상기 벨트 층의 양 가장자리 끝지점에서 타이어 안쪽으로 20㎜~50㎜ 폭으로 형성시키는 것이 좋다. 그러나, PCR의 경우 오버랩 폭은 40㎜, 단부 폭은 50㎜로 한다.The cap ply is an edge cap ply which is laminated in an endless manner before and after the formation of the belt layer. The shape and width of the edge portion of the cap, the material of the cap ply cord and the like are not important. However, Mm to 50 mm in width. However, in the case of PCR, the overlap width is 40 mm and the end width is 50 mm.
또, 상기 코드(120)를 중심으로 하부고무(114)와 상부고무(116)의 두께 차는 크게 중요하지는 않으나 하단 고무 대비 상단의 고무가 1~1.5배 두꺼운 것이 좋다.The difference in thickness between the
그리고, 상기 하부고무(114)가 상기 상부고무(116)에 비해 50% 이하인 경우 검에지 고무가 부족하여 벨트 내 스틸코드와의 접착력 향상 기능이 떨어지며, 140% 이상으로 검에지 고무가 사용된 경우 캡플라이 내 사용되는 섬유코드와의 접착력에 문제가 있어 오히려 타이어 내구성능이 떨어진다.If the
따라서, 벨트 끝단과 만나는 상기 하부고무(114)는 검엣지 고무를 사용하여 벨트부에 사용되는 스틸 코드 및 벨트 고무와의 접착력을 높일 수 있으며, 상기 상부고무(116)는 기존의 캡플라이 고무를 사용하여 캡플라이에 사용되는 섬유코드와의 접착력을 유지할 수 있다.Therefore, the
아래의 비교표는 상부고무(116)와 하부고무(114)의 두께 비율의 변화를 준 캡플라이가 적용된 공기입 타이어의 내구성능 및 주행시험 결과이다.The comparison chart below shows the durability test and the running test results of the pneumatic tire to which the cap ply applied to change the thickness ratio of the
이때 사용한 캡플라이 코드는 나일론 6,6이며, 섬유코드의 기본 물성, 캡플라이 총 두께, 벨트 부, 오버랩은 상기와 겉아 동일하게 사용하였다.
The cap fly cord used here was nylon 6,6, and the basic properties of the fiber cord, the total thickness of the cap fly, the belt portion, and the overlap were the same as above.
/하단(검엣지고무)두께 비율Top (cap fly rubber)
/ Bottom (rubber edge) thickness ratio
0.70.3
0.7
0.50.5
0.5
0.250.75
0.25
파괴양상Driving test
Destruction aspect
벨트 엣지
세파1:35
Belt Edge
Sefa
트래트 패턴 세파1:38
Trat pattern Sepah
트래드 패턴
세파1:45
Tread pattern
Sefa
벨트 엣지
세파1:40
Belt Edge
Sefa
박리 접착력Belt - Cap Fly
Peel adhesion
상기 평가 결과, 상단의 캡플라이 고무와 하단의 검엣지 고무를 일정비율로 적용한 캡플라이를 사용한 공기입 타이어의 경우 타이어 내구성능을 향상시킬 수 있다.
As a result of the evaluation, it is possible to improve the tire durability in the case of the pneumatic tire using the cap ply having the upper cap rubber rubber and the lower end gum rubber applied at a certain ratio.
상기와 같이, 본 발명의 바람직한 실시예를 참조하여 설명하였지만 해당 기술 분야의 숙련된 당업자라면 하기의 특허청구범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다.
While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it will be understood by those skilled in the art that various changes and modifications may be made without departing from the spirit and scope of the invention as defined in the appended claims. It can be understood that
100: 공기입 타이어 102: 트레드부
104: 인너라이너 106: 벨트부
108: 캡플라이 110: 비드부
112: 코드 114: 하부고무
116: 상부고무100: pneumatic tire 102: tread portion
104: Inner liner 106: Belt portion
108: cap fly 110: bead portion
112: Code 114: Lower rubber
116: Upper rubber
Claims (2)
상기 캡플라이는, 상기 벨트부와 접하는 하부고무와, 상기 하부고무에 배치되는 코드와, 상기 코드 상에 설치되는 상부고무를 포함하고,
상기 하부고무는 검엣지 고무로 이루어지는 것을 특징으로 하는 벨트부와의 접착력이 향상된 이종의 고무를 사용한 캡플라이.
1. A cap ply which covers both ends of a belt portion in a pneumatic tire,
Wherein the cap ply includes a lower rubber contacting the belt portion, a cord disposed on the lower rubber, and an upper rubber disposed on the cord,
Characterized in that the lower rubber is made of gum edge rubber.