KR20120015273A - Multi-layered article and method of fabricating the same - Google Patents

Multi-layered article and method of fabricating the same Download PDF

Info

Publication number
KR20120015273A
KR20120015273A KR1020110078718A KR20110078718A KR20120015273A KR 20120015273 A KR20120015273 A KR 20120015273A KR 1020110078718 A KR1020110078718 A KR 1020110078718A KR 20110078718 A KR20110078718 A KR 20110078718A KR 20120015273 A KR20120015273 A KR 20120015273A
Authority
KR
South Korea
Prior art keywords
coating layer
laminate
thin film
layer
laminated
Prior art date
Application number
KR1020110078718A
Other languages
Korean (ko)
Inventor
김호우
안진수
오정홍
이재홍
이종균
Original Assignee
삼성코닝정밀소재 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to KR20100077332 priority Critical
Priority to KR1020100077332 priority
Application filed by 삼성코닝정밀소재 주식회사 filed Critical 삼성코닝정밀소재 주식회사
Priority claimed from DE102011052540.8A external-priority patent/DE102011052540B4/en
Publication of KR20120015273A publication Critical patent/KR20120015273A/en

Abstract

PURPOSE: A laminate having a base, a resin pattern layer, and thin film coating layer laminated in order is provided to ensure rich color. CONSTITUTION: A laminate comprises: a base(10); a resin pattern layer(20); and a thin film coating layer(40). A primer coating layer is laminated between the resin pattern layer and thin coating layer. The primer coating layer contains Ti, Nb, Si, TiOx, NbOx or SiOx. The thickness of the primer coating layer is 5-500 nm. The thin film coating layer is formed with metal, oxide, nitride, oxynitride, thermal chromic material, photochromic material, or electro chromic material in a monolayer or multilayer.

Description

적층체 및 적층체 제조방법{Multi-layered article and method of fabricating the same}Multi-layered article and method of fabricating the same
본 발명은 적층체 및 그 제조방법에 관한 것으로, 더욱 상세하게는 박막코팅층을 갖는 적층체 및 그 제조방법에 관한 것이다.The present invention relates to a laminate and a method of manufacturing the same, and more particularly, to a laminate having a thin film coating layer and a method of manufacturing the same.
최근 제품의 디자인 경쟁력이 제품 경쟁력의 주요한 요소로 자리매김하고 있다. 예컨대, 가전 제품(냉장고, 에어컨, 디스플레이 장치), 등에 있어, 디자인 차별화를 통하여 시장 경쟁력을 확보하려는 노력이 집중되고 있다. 가전 제품의 디자인 차별화를 위하여 데코레이션 적층체를 가전 제품의 바디에 접착하여 제품 경쟁력을 높이고 있다. Recently, the design competitiveness of products has become a major factor of product competitiveness. For example, in home appliances (refrigerators, air conditioners, display devices), etc., efforts to secure market competitiveness through design differentiation have been concentrated. In order to differentiate the design of home appliances, decoration laminates are bonded to the body of home appliances to enhance product competitiveness.
도 1은 종래의 적층체의 적층 구조를 보여주는 도면이다. 1 is a view showing a laminated structure of a conventional laminate.
도시한 바와 같이, 종래의 적층체는 기재(10), 패턴층(20') 및 인쇄층(30)을 포함한다. 패턴층(20')은 기재(10)의 배면에 형성된다. 인쇄층(30)은 패턴층(20')의 배면에 형성된다. 상기 인쇄층(30)으로는, 전형적으로 미러 잉크의 인쇄층(30)이 사용되는데, 이러한 인쇄층(30)으로는 풍부한 색감 및 깊이감, 특히 풍부한 금속색의 색감 및 질감을 나타내는데 한계가 있었다. 또한, 미러 잉크가 고가여서, 적층체의 단가를 상승시키는 요인이 되었다.As shown, the conventional laminate includes a substrate 10, a pattern layer 20 ′, and a printed layer 30. The pattern layer 20 'is formed on the back surface of the substrate 10. The print layer 30 is formed on the back side of the pattern layer 20 '. As the printing layer 30, a printing layer 30 of mirror ink is typically used, and the printing layer 30 has a limitation in showing rich color and depth, particularly rich metal color and texture. . In addition, the mirror ink was expensive, which caused the unit cost of the laminate to increase.
본 발명은 상기한 문제점을 해결하기 위하여 안출된 것으로서, 본 발명의 목적은 적층체에 풍부한 색감 및 깊이감을 부여함으로써, 제품 경쟁력을 높이는데 있다.The present invention has been made to solve the above problems, an object of the present invention is to enhance the product competitiveness by providing a rich color and depth to the laminate.
상기한 목적을 달성하기 위하여, 본 발명은, 기재; 수지 패턴층; 및 박막코팅층이 순차적으로 적층되어 이루어지는 것을 특징으로 하는 적층체를 제공한다. In order to achieve the above object, the present invention, the base; Resin pattern layer; And a thin film coating layer is sequentially laminated.
수지 패턴층의 반대쪽에서 박막코팅층에는 보호필름 또는 제1보호코팅층이 적층될 수 있다. 더 나아가 박막코팅층과 보호필름 또는 제1보호코팅층의 사이에는 제2보호코팅층이 적층될 수 있다. On the opposite side of the resin pattern layer, a protective film or a first protective coating layer may be laminated on the thin film coating layer. Furthermore, a second protective coating layer may be stacked between the thin film coating layer and the protective film or the first protective coating layer.
바람직하게는 상기 수지 패턴층과 박막코팅층의 사이에는 프라이머코팅층이 적층될 수 있다. Preferably, a primer coating layer may be laminated between the resin pattern layer and the thin film coating layer.
상기한 구성에 따르면, 본 발명은 적층체가 풍부한 색감 및 깊이감을 뚜렷하게 나타내도록 하여, 세련미를 더 한층 살릴 수 있도록 하는 효과가 있다.
According to the above-described configuration, the present invention has an effect of making the laminate clearly show a rich color and a sense of depth, to further enhance the sophistication.
도 1은 종래의 적층체의 적층 구조를 보여주는 단면도이다.
도 2는 본 발명의 제1실시예에 따른 적층체의 적층 구조를 보여주는 단면도이다.
도 3은 도 2의 적층체의 형성 공정의 일 예를 보여주는 도면이다.
도 4는 본 발명의 제2실시예에 따른 적층체의 적층 구조를 보여주는 단면도이다.
도 5는 도 4의 적층체에서 발생할 수 있는 결함을 보여주는 도면이다.
도 6은 본 발명의 제3실시예에 따른 적층체의 적층 구조를 보여주는 단면도이다.
도 7은 본 발명의 제4실시예에 따른 적층체의 적층 구조를 보여주는 단면도이다.
도 8은 도 7의 적층체에서 발생할 수 있는 결함을 보여주는 도면이다.
도 9는 본 발명의 제5실시예에 따른 적층체의 적층 구조를 보여주는 단면도이다.
도 10은 본 발명의 제6실시예에 따른 적층체의 적층 구조를 보여주는 단면도이다.
도 11 및 도 12는 도 4의 적층체가 가전 제품에 부착되어 사용되는 형태를 보여주는 단면도 및 정면도이다.
1 is a cross-sectional view showing a laminated structure of a conventional laminate.
2 is a cross-sectional view showing a laminated structure of a laminate according to a first embodiment of the present invention.
3 is a view illustrating an example of a process of forming the laminate of FIG. 2.
4 is a cross-sectional view showing a laminated structure of a laminate according to a second embodiment of the present invention.
5 is a view showing a defect that may occur in the laminate of FIG.
6 is a cross-sectional view showing a laminated structure of a laminate according to a third embodiment of the present invention.
7 is a cross-sectional view showing a laminated structure of a laminate according to a fourth embodiment of the present invention.
8 is a view showing a defect that may occur in the laminate of FIG.
9 is a cross-sectional view showing a laminated structure of a laminate according to a fifth embodiment of the present invention.
10 is a cross-sectional view showing a laminated structure of a laminate according to a sixth embodiment of the present invention.
11 and 12 are cross-sectional views and front views showing a form in which the laminate of FIG. 4 is attached to and used in home appliances.
이하, 첨부 도면을 참조하여 본 발명의 바람직한 실시예를 상세히 설명한다. Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.
본 명세서에서, "코팅"은 코팅 물질의 타겟을 스퍼터링하여 얻는 증착층이나 액상 코팅 물질을 도포하여 얻는 인쇄층을 포함하나, 접착제를 개재하여 접착된 필름은 제외한다. 접착(Adhesion)은 PSA(Pressure Sensitive Adhesive)를 이용한 접착을 포함한다. As used herein, "coating" includes a deposition layer obtained by sputtering a target of a coating material or a printing layer obtained by applying a liquid coating material, but excludes a film adhered through an adhesive. Adhesion includes adhesion using a pressure sensitive adhesive (PSA).
도 2는 본 발명의 제1실시예에 따른 적층체의 적층 구조를 보여주는 단면도이다. 2 is a cross-sectional view showing a laminated structure of a laminate according to a first embodiment of the present invention.
도시한 바와 같이, 제1실시예의 적층체는 기재(10), 수지 패턴층(20) 및 박막코팅층(40)을 포함한다. 전형적으로, 수지 패턴층은 기재와 반대쪽의 면에 패턴을 갖고, 이 패턴은 기재를 통하여 가시된다. 즉, 전형적으로, 수지 패턴층의 패턴은 기재의 전방의 관찰자에게 가시된다. As shown, the laminate of the first embodiment includes a substrate 10, a resin pattern layer 20, and a thin film coating layer 40. Typically, the resin pattern layer has a pattern on the side opposite to the substrate, which pattern is visible through the substrate. That is, typically, the pattern of the resin pattern layer is visible to the observer in front of the substrate.
기재(10)는 유리 또는 고분자 필름과 같은 비금속 기재일 수 있다. 유리는 강화 유리가 사용될 수 있다. The substrate 10 may be a nonmetallic substrate such as glass or a polymer film. As the glass, tempered glass may be used.
수지 패턴층(20)은 기재(10)의 배면에 형성된다. 수지 패턴층(20)은 요철 패턴을 갖는다. 여기서, 요철 패턴은, 선형 라인, 비선형 라인, 헤어스핀, 헤어라인, 스크래치, 크로스해칭, 텍스춰(texture), 엠보(emboss), 프리즘, 그루브, 렌즈, 기둥(pillar), 원뿔, 다각뿔, 구멍과 같은 다양한 패턴을 포함한다. 요철 패턴은 다양한 방식으로 형성될 수 있는데, 전형적으로는 도 3과 같은 임프린팅에 의하여 형성된다. 실시예에 따라서는, 수지 패턴층 및 박막코팅층이 기재의 일부 면적에만 형성되는 것도 가능하다. 예컨대, 휴대폰 표시창의 경우, 수지 패턴층 및 박막코팅층은 기재의 테두리에만 형성되어 데코레이션 효과를 부여하고, 기재의 중심부는 디스플레이 화면이 투과될 수 있는 단순 투과창의 기능을 수행하는 것이다.
The resin pattern layer 20 is formed on the back surface of the substrate 10. The resin pattern layer 20 has an uneven pattern. Here, the uneven pattern may include linear lines, nonlinear lines, hairspins, hairlines, scratches, crosshatching, textures, embosses, prisms, grooves, lenses, pillars, cones, polygons, holes and holes. Includes various patterns such as The uneven pattern may be formed in various ways, typically by imprinting as shown in FIG. 3. According to the embodiment, it is also possible that the resin pattern layer and the thin film coating layer are formed only on a partial area of the substrate. For example, in the case of a mobile phone display window, the resin pattern layer and the thin film coating layer are formed only at the edge of the substrate to give a decoration effect, and the center of the substrate serves as a simple transmission window through which the display screen can be transmitted.
도 3은 도 2의 적층체의 형성 공정의 일 예를 보여주는 도면이다. 3 is a view illustrating an example of a process of forming the laminate of FIG. 2.
도시한 바와 같이, 기재(10)와 몰드(M) 사이에 UV 경화 수지를 개재시킨 상태에서 UV를 조사하여 UV 경화 수지를 경화시킨다. 이때 기재(10)는 UV를 투과시키는 재질로 이루어지는 것이 바람직하다. 기재(10)가 UV 투과성이 없는 재질로 이루어지는 경우, 몰드(M)가 UV를 투과시키는 재질로 이루어져야 한다. As shown, UV is irradiated in the state which interposed the UV curable resin between the base material 10 and the mold M to harden the UV curable resin. At this time, the substrate 10 is preferably made of a material that transmits UV. When the substrate 10 is made of a material having no UV transmittance, the mold M should be made of a material transmitting UV.
UV 경화 수지를 임프린팅하여 수지 패턴층(20)을 형성하는 것 외에도 다양한 방식으로 수지 패턴층(20)을 형성할 수 있음은 전술하였다. 예컨대, 열 경화 수지를 임프린팅하여 수지 패턴층(20)을 형성하는 것도 가능하다. 또한, 기재를 에칭하여 수지 패턴층을 형성하거나, 기재에 컬러 수지 물질, 등을 인쇄하여 수지 패턴층을 형성할 수 있다. In addition to forming the resin pattern layer 20 by imprinting the UV curable resin, the resin pattern layer 20 may be formed in various ways. For example, it is also possible to form the resin pattern layer 20 by imprinting a thermosetting resin. In addition, the substrate may be etched to form a resin pattern layer, or a resin pattern layer may be formed by printing a color resin material or the like on the substrate.
수지 패턴층(20)은 3D 입체 패턴을 가질 수 있다. 예컨대, 요부의 깊이 및 철부의 높이가 일정하지 않은 요철 패턴을 가질 수 있다. 이를 위하여, 3D 입체 패턴의 역상을 갖는 몰드를 이용하여 임프린팅 방식으로 수지 패턴층(20)을 형성할 수 있다. 또한, 다층 코팅을 통하여 수지 패턴층(20)을 형성하되, 각 층의 2D 패턴을 달리하여 3D 입체 패턴을 갖는 수지 패턴층(20)을 형성할 수도 있을 것이다. 또한, 기재(10)를 에칭하여 수지 패턴층(20)을 형성하되, 각 위치마다 에칭 깊이를 달리하여 3D 입체 패턴을 갖는 수지 패턴층(20)을 형성할 수도 있을 것이다. The resin pattern layer 20 may have a 3D three-dimensional pattern. For example, the depth of the recess and the height of the convex portion may have an irregular pattern. To this end, the resin pattern layer 20 may be formed by an imprinting method using a mold having a reversed phase of a 3D three-dimensional pattern. In addition, the resin pattern layer 20 may be formed through the multilayer coating, and the resin pattern layer 20 having the 3D three-dimensional pattern may be formed by changing the 2D pattern of each layer. In addition, although the resin pattern layer 20 is formed by etching the substrate 10, the resin pattern layer 20 having a 3D three-dimensional pattern may be formed by varying the etching depth at each position.
수지 패턴층은 안료와 같은 색소를 포함할 수 있다. The resin pattern layer may contain a pigment such as a pigment.
박막코팅층(40)은 수지 패턴층(20)의 배면에 형성될 수 있다. 전형적으로, 본 발명의 적층체에 있어서, 박막코팅층의 색상은 외관에 드러나, 적층체에 색감 및 질감을 부여한다. The thin film coating layer 40 may be formed on the rear surface of the resin pattern layer 20. Typically, in the laminate of the present invention, the color of the thin film coating layer is visible in appearance, giving color and texture to the laminate.
박막코팅층(40)은 금속, 산화물, 질화물, 산질화물(oxy-nitride), 서말크로믹(thermalchromic) 물질, 포토크로믹(photochromic) 물질 및 일렉트로크로믹(electrochromic) 물질 중 적어도 어느 하나가 단층 또는 다층으로 코팅된다. 여기서, 금속은 금속합금을 포함한다. 서말크로믹 물질, 포토크로믹(photochromic) 물질 및 일렉트로크로믹(electrochromic) 물질은 각각 열, 광 및 전기가 인가되면 색상이 변화하는 특성을 갖는다. The thin film coating layer 40 may include at least one of a metal, an oxide, a nitride, an oxy-nitride, a thermalchromic material, a photochromic material, and an electrochromic material. Coated in multiple layers. Here, the metal includes a metal alloy. The thermal chromic material, photochromic material and electrochromic material each have a characteristic of changing color when heat, light and electricity are applied.
예컨대, 수지 패턴층(20)의 배면에 금속층이 단층으로 코팅되거나, 금속층이 다층으로 코팅되거나, 산화물층이 단층으로 코팅되거나, 산화물층이 다층으로 코팅될 수 있다. For example, a metal layer may be coated with a single layer, a metal layer may be coated with a multilayer, an oxide layer may be coated with a single layer, or an oxide layer may be coated with a multilayer on the back surface of the resin pattern layer 20.
또한, 수지 패턴층(20)의 배면에 금속층 및 산화물층이 다층으로 코팅될 수 있다. 금속층 및 산화물층을 포함하는 박막코팅층(40)의 예로서, NbOX 코팅층/AZO(Aluminum doped Zinc Oxide) 코팅층/Ag 코팅층/AZO 코팅층/NbOX 코팅층이 1 회 이상, 예컨대 1회~4회 반복하여 형성될 수 있다.In addition, a metal layer and an oxide layer may be coated in multiple layers on the back surface of the resin pattern layer 20. As an example of the thin film coating layer 40 including the metal layer and the oxide layer, the NbO X coating layer / Aluminum doped Zinc Oxide (AZO) coating layer / Ag coating layer / AZO coating layer / NbO X coating layer is repeated one or more times, for example, once to four times. Can be formed.
또한, 상기 서말크로믹 물질로는 VO2가 사용될 수 있는데, 박막코팅층은 VO2 박막 및 TiO2 박막이 적어도 1회 이상 반복되어 형성될 수 있다. In addition, VO 2 may be used as the thermal chromic material, and the thin film coating layer may be formed by repeating the VO 2 thin film and the TiO 2 thin film at least one or more times.
상기 금속으로는, 예컨대, 스테인레스스틸(SUS 316L, 등), Cu, Al, Ni, Ti, Nb, Si, Cr, 등이 사용될 수 있고, 상기 산화물로는 상기 금속의 산화물, TiO2, SiO2, Ta2O5, 등이 사용될 수 있다. 상기 질화물로는, 상기 금속의 질화물이 사용될 수 있다. 상기 산질화물로는, 상기 금속의 산질화물이 사용될 수 있다. As the metal, for example, stainless steel (SUS 316L, etc.), Cu, Al, Ni, Ti, Nb, Si, Cr, etc. may be used, and the oxide may be an oxide of the metal, TiO 2 , SiO 2 , Ta 2 O 5 , and the like can be used. As the nitride, a nitride of the metal may be used. As the oxynitride, an oxynitride of the metal may be used.
박막코팅층(40)은 전체 두께가 3nm~10㎛인 것이 바람직하다. 더욱 바람직하게는, 박막코팅층은 전체 두께가 10~500nm이다. The thin film coating layer 40 preferably has a total thickness of 3nm ~ 10㎛. More preferably, the thin film coating layer has a total thickness of 10 to 500 nm.
박막코팅층(40)은 스퍼터링에 의하여 코팅되는 것이 바람직하고, 이 밖에, E-beam evaporation 및 저항 가열에 의하여 코팅될 수 있다. 스퍼터링하는 경우, 다양한 가스(산소, 질소 등)를 주입하여, 그 주입량에 따라 박막코팅층의 색상을 조절할 수 있어 바람직하다.
The thin film coating layer 40 is preferably coated by sputtering, in addition, it may be coated by E-beam evaporation and resistance heating. In the case of sputtering, various gases (oxygen, nitrogen, etc.) may be injected, and thus the color of the thin film coating layer may be adjusted according to the injection amount thereof.
아래 표 1은 스퍼터링 조건을 나타낸다. Table 1 below shows the sputtering conditions.
기재 히팅 온도Substrate heating temperature 100℃ (10분)100 ℃ (10 minutes)
공정 압력Process pressure 2.0~3.0 mtorr2.0 ~ 3.0 mtorr
ArAr 100 sccm100 sccm
캐리어 속도Carrier speed 33/65/130 cm/min33/65/130 cm / min
막두께Thickness 30/60/120 nm30/60/120 nm
도 4는 본 발명의 제2실시예에 따른 적층체의 적층 구조를 보여주는 단면도이다. 4 is a cross-sectional view showing a laminated structure of a laminate according to a second embodiment of the present invention.
도시한 바와 같이, 본 발명의 적층체는 박막코팅층(40)의 배면에 보호필름(60)이 적층된다. 보호필름(60)은 박막코팅층(40)의 스크래치를 방지하는 등, 물리적 내구성을 확보하는 것에 그치는 것이 아니라, 박막코팅층(40)의 화학적 내구성을 유지할 수 있도록 하는 효과를 갖는다. 적층체는, 도 11 및 도 12에 도시한 바와 같이 전형적으로 가전제품에 부착되는데, 이때 폴리우레탄 접착제가 사용될 수 있다. 따라서, 보호필름(60)은 폴리우레탄 접착제와 박막코팅층(40)의 화학적 반응을 차단하여 화학적 내구성을 향상시키는 기능을 수행할 수 있다. As shown, in the laminate of the present invention, the protective film 60 is laminated on the back surface of the thin film coating layer 40. The protective film 60 not only secures physical durability, such as preventing scratches of the thin film coating layer 40, but also has an effect of maintaining chemical durability of the thin film coating layer 40. The laminate is typically attached to a household appliance, as shown in FIGS. 11 and 12, wherein a polyurethane adhesive may be used. Therefore, the protective film 60 may perform a function of improving chemical durability by blocking a chemical reaction between the polyurethane adhesive and the thin film coating layer 40.
보호필름(60)은 투명하거나 무채색 또는 유채색 색상을 가질 수 있다. 예컨대, 실시예에 따라 보호필름의 배면의 접착제의 색상이 적층체의 전면에 노출될 우려가 있는 경우, 보호필름(60)에 화이트색을 부여하여 접착제의 색상이 전면에 노출되지 않도록 할 수 있다.
The protective film 60 may have a transparent, achromatic or chromatic color. For example, when the color of the adhesive on the back of the protective film according to the embodiment may be exposed on the front of the laminate, the color of the adhesive may be given to the protective film 60 so that the color of the adhesive is not exposed on the front. .
도 6은 본 발명의 제3실시예에 따른 적층체의 적층 구조를 보여주는 단면도이다. 6 is a cross-sectional view showing a laminated structure of a laminate according to a third embodiment of the present invention.
본 실시예의 적층체는 도 4의 보호필름(60)을 대신하여 제1보호코팅층(70)을 가진다. 상기 제1보호코팅층은 인쇄층일 수 있다. 또한, 상기 제1보호코팅층은, Si3N4, SiC, NbOx, TiN, Ti 및 DLC중 적어도 어느 하나의 물질의 코팅층으로서, 예컨대 CVD, 스퍼터링, 등에 의하여 코팅할 수 있다.
The laminate of this embodiment has a first protective coating layer 70 in place of the protective film 60 of FIG. The first protective coating layer may be a printed layer. In addition, the first protective coating layer is a coating layer of at least one of Si 3 N 4 , SiC, NbOx, TiN, Ti, and DLC, and may be coated by, for example, CVD, sputtering, or the like.
도 7은 본 발명의 제4실시예에 따른 적층체의 적층 구조를 보여주는 단면도이다. 7 is a cross-sectional view showing a laminated structure of a laminate according to a fourth embodiment of the present invention.
도시한 바와 같이, 본 발명의 적층체는 박막코팅층(40)과 보호필름(60)의 사이에 제2보호코팅층(50)이 더 형성될 수 있다. As shown, in the laminate of the present invention, a second protective coating layer 50 may be further formed between the thin film coating layer 40 and the protective film 60.
유사하게, 도 6의 실시예의 박막코팅층과 제1보호코팅층(70) 사이에 제2보호코팅층(50)이 개재될 수 있다. Similarly, the second protective coating layer 50 may be interposed between the thin film coating layer and the first protective coating layer 70 of the embodiment of FIG. 6.
도 4의 적층체에 대한 내열 테스트(65℃, 상대습도 90%, 72시간) 및 내습 테스트(상대습도 90%, 48 시간)를 실시한 결과, 도 5에 도시한 바와 같이 레인보우(rainbow) 무늬의 결함이 발생할 수 있음을 보여주었다. 레인보우 무늬는 UV 수지의 수지 패턴층에 수분이 침투하여 굴절률 차이가 발생한 결과로 판단되었다. 따라서, 도 7에서와 같이, 제2보호코팅층(50), 예컨대 NbOx의 제2보호코팅층을 적층하여 레인보우 무늬의 발생을 막을 수 있었다.
As a result of performing the heat resistance test (65 ° C., relative humidity 90%, 72 hours) and the humidity resistance test (relative humidity 90%, 48 hours) for the laminate of FIG. 4, as shown in FIG. It has been shown that defects can occur. The rainbow pattern was determined to be a result of difference in refractive index due to the penetration of moisture into the resin pattern layer of the UV resin. Therefore, as shown in FIG. 7, the second protective coating layer 50, for example, the second protective coating layer of NbOx, may be stacked to prevent the occurrence of the rainbow pattern.
도 9는 본 발명의 제5실시예에 따른 적층체의 적층 구조를 보여주는 단면도이다. 9 is a cross-sectional view showing a laminated structure of a laminate according to a fifth embodiment of the present invention.
도시한 바와 같이, 도 9의 적층체는 기재(10), 수지 패턴층(20), 프라이머코팅층(90), 박막코팅층(40) 및 보호필름(60)을 포한다. 실시예에 따라서, 보호필름(60)은 제외될 수 있다. 도 9의 적층체도 보호필름을 대신하여 제1보호코팅층을 가질 수 있고, 더 나아가 제2보호코팅층도 가질 수 있다. As illustrated, the laminate of FIG. 9 includes a substrate 10, a resin pattern layer 20, a primer coating layer 90, a thin film coating layer 40, and a protective film 60. According to an embodiment, the protective film 60 may be excluded. The laminate of FIG. 9 may also have a first protective coating layer in place of the protective film, and may further have a second protective coating layer.
프라이머코팅층(90)은 Ti, Nb, Si, TiOx, NbOx 및 SiOx 중 적어도 하나를 포함할 수 있다.The primer coating layer 90 may include at least one of Ti, Nb, Si, TiOx, NbOx, and SiOx.
프라이머코팅층의 두께는 바람직하게는, 5~500nm이다. The thickness of the primer coating layer is preferably 5 to 500 nm.
프라이머코팅층은 예컨대, 스퍼터링을 통한 증착층이 바람직하고, 인쇄층은 바람직하지 않을 수 있다. 후자의 방법은, 프라이머코팅층을 바람직한 두께로 코팅하는 것이 어렵기 때문이다. The primer coating layer is preferably a deposition layer through sputtering, for example, and the printing layer may not be desirable. The latter method is because it is difficult to coat the primer coating layer to a desired thickness.
도 7의 적층체에 대한 내열 테스트 및 내습 테스트를 실시한 결과, 레인보우 무늬의 결함을 억제할 수 있으나, 도 8에 도시한 바와 같이, 적층체에 국부적 색상차의 결함이 발생할 수 있음을 보여주었다. 이는 박막코팅층, 특히 산소 주입 조건에서 스퍼터링된 박막코팅층(40)이 UV 수지의 수지 패턴층(20)과 화학 반응을 야기하여 색상차가 발생되는 것으로 판단되었다. 또한, 박막코팅층(40)의 형성 전에 수지 패턴층(20) 자체가 가지는 오염은 이러한 색상차 결함을 심화시키는 것으로 조사되었다. 따라서, 본 발명에서는 도 9에서와 같이 프라이머코팅층(90)을 형성하여 이 같은 결함을 억제할 수 있었다.
As a result of the heat resistance test and the moisture resistance test of the laminate of FIG. 7, it is possible to suppress defects in the rainbow pattern, but as illustrated in FIG. 8, it was shown that a defect of a local color difference may occur in the laminate. It was determined that the thin film coating layer, in particular, the thin film coating layer 40 sputtered under oxygen injection conditions caused a chemical reaction with the resin pattern layer 20 of the UV resin to generate a color difference. In addition, contamination of the resin pattern layer 20 itself before the formation of the thin film coating layer 40 has been investigated to deepen such color difference defects. Therefore, in the present invention, such a defect could be suppressed by forming the primer coating layer 90 as shown in FIG.
도 10은 본 발명의 제6실시예에 따른 적층체의 적층 구조를 보여주는 단면도이다. 10 is a cross-sectional view showing a laminated structure of a laminate according to a sixth embodiment of the present invention.
본 발명의 적층체는 전면에 방오코팅층(80)을 가질 수 있다. 방오코팅층(80)은, 플루오린계인 MgF2, 플루오린계인 PTFE(polytetrafluroethylene), DLC(Diamond Like Carbon) 및 TiO2 중 적어도 어느 하나를 포함할 수 있다. 또한, 이들에 불순물을 소량 도핑하여 그 성능을 높일 수 있다. 방오코팅층은 친수 기능, 광촉매 기능, 등을 수행하여 적층체의 오염을 방지한다. The laminate of the present invention may have an antifouling coating layer 80 on the front surface. The antifouling coating layer 80 may include at least one of fluorine-based MgF 2 , fluorine-based PTFE (polytetrafluroethylene), DLC (Diamond Like Carbon), and TiO 2 . In addition, a small amount of impurities may be doped into these to increase its performance. The antifouling coating layer performs a hydrophilic function, a photocatalytic function, and the like to prevent contamination of the laminate.
실시예에 따라서, 보호필름(60)은 제외될 수 있다. 도 10의 적층체도 보호필름을 대신하여 제1보호코팅층을 가질 수 있고, 더 나아가 제2보호코팅층도 가질 수 있다.
According to an embodiment, the protective film 60 may be excluded. The laminate of FIG. 10 may also have a first protective coating layer in place of the protective film, and may further have a second protective coating layer.
도 11 및 도 12는 도 4의 적층체가 가전 제품에 부착되어 사용되는 형태를 보여주는 단면도 및 정면도이다. 11 and 12 are cross-sectional views and front views showing a form in which the laminate of FIG. 4 is attached to and used in home appliances.
도 11 및 도 12에서는 본 발명의 적층체가 냉장고(100)에 부착되어 사용되는 실시예를 보여준다. 이러한 실시예에서는, 수지 패턴층(20)의 패턴이 사용자에게 가시될 수 있어야 하므로, 적어도, 기재 및 수지 패턴층은 불투명하지 않아야 할 것이다. 11 and 12 show an embodiment in which the laminate of the present invention is attached to the refrigerator 100 and used. In this embodiment, since the pattern of the resin pattern layer 20 should be visible to the user, at least the substrate and the resin pattern layer should not be opaque.
본 발명의 적층체는 예컨대, 가전 제품, 등의 외벽면에 부착되는 형태가 전형적일 것이나, 반드시 이에 한정되는 것은 아니다. 예컨대 냉장고의 실내 벽면에 부착되어 실내 디자인의 일부를 이룰 수도 있을 것이다. 또한, 지금까지는 본 발명의 적층체가 가전 제품에 부착되는 것을 주요 실시예로 설명하였으나, 이에 한정되는 것이 아님은 물론이다. 예컨대, 본 발명의 적층체의 적용분야는 휴대폰, 가정용품, 가구, 건물용 윈도우, 자동차 등 다양한 분야를 망라한다. The laminate of the present invention will typically be in the form of being attached to an outer wall surface of a home appliance, for example, but is not necessarily limited thereto. For example, it may be attached to the interior wall of the refrigerator to form part of the interior design. In addition, it has been described so far as the main embodiment that the laminate of the present invention is attached to the home appliance, of course, it is not limited thereto. For example, the field of application of the laminate of the present invention covers various fields such as mobile phones, home appliances, furniture, building windows, automobiles, and the like.
10: 기재, 20: 수지 패턴층,
40: 박막코팅층, 50: 제2보호코팅층,
60: 보호필름, 70: 제1보호코팅층,
90: 프라이머코팅층
10: base material, 20: resin pattern layer,
40: a thin film coating layer, 50: a second protective coating layer,
60: protective film, 70: the first protective coating layer,
90: primer coating layer

Claims (25)

  1. 기재;
    수지 패턴층; 및
    박막코팅층이 순차적으로 적층되어 이루어지는 것을 특징으로 하는 적층체.
    materials;
    Resin pattern layer; And
    A laminate comprising a thin film coating layer sequentially laminated.
  2. 제1항에 있어서,
    상기 수지 패턴층과 박막코팅층의 사이에 프라이머코팅층이 적층되는 것을 특징으로 하는 적층체.
    The method of claim 1,
    A laminate, characterized in that the primer coating layer is laminated between the resin pattern layer and the thin film coating layer.
  3. 제2항에 있어서,
    상기 프라이머코팅층은 Ti, Nb, Si, TiOx, NbOx 및 SiOx 중 적어도 하나를 포함하는 것을 특징으로 하는 적층체.
    The method of claim 2,
    The primer coating layer is a laminate comprising at least one of Ti, Nb, Si, TiOx, NbOx and SiOx.
  4. 제2항에 있어서,
    상기 프라이머코팅층의 두께는 5~500nm인 것을 특징으로 하는 적층체.
    The method of claim 2,
    The thickness of the primer coating layer is a laminate, characterized in that 5 ~ 500nm.
  5. 제1항에 있어서,
    상기 박막코팅층은 금속, 산화물, 질화물, 산질화물, 서말크로믹(thermalchromic) 물질, 포토크로믹(photochromic) 물질 및 일렉트로크로믹(electrochromic) 물질 중 적어도 하나의 박막이 단층 또는 다층으로 형성되는 것을 특징으로 하는 적층체.
    The method of claim 1,
    The thin film coating layer is characterized in that at least one thin film of metal, oxide, nitride, oxynitride, thermalchromic material, photochromic material and electrochromic material is formed in a single layer or multiple layers. Laminate.
  6. 제5항에 있어서,
    상기 금속은 스테인레스스틸, Cu, Al, Ni, Ti, Nb, Si 및 Cr 중 적어도 하나이고,
    상기 산화물은 상기 금속의 산화물, TiO2, SiO2 및 Ta2O5 중 적어도 하나이고,
    상기 질화물은 상기 금속의 질화물이고,
    상기 산질화물은 상기 금속의 산질화물이고,
    상기 서말크로믹 물질은 V02인 것을 특징으로 하는 적층체.
    The method of claim 5,
    The metal is at least one of stainless steel, Cu, Al, Ni, Ti, Nb, Si and Cr,
    The oxide is at least one of an oxide of the metal, TiO 2 , SiO 2 and Ta 2 O 5 ,
    The nitride is a nitride of the metal,
    The oxynitride is an oxynitride of the metal,
    The thermochromic material is a laminate, characterized in that V0 2 .
  7. 제1항에 있어서,
    상기 박막코팅층은 NbOx 박막, AZO 박막, Ag 박막, AZO 박막 및 NbOx 박막이 적어도 1회 이상 반복되는 것을 특징으로 하는 적층체.
    The method of claim 1,
    The thin film coating layer is a laminate, characterized in that the repeated NbO x thin film, AZO thin films, Ag thin film, AZO thin film and NbO x thin film is at least more than once.
  8. 제1항에 있어서,
    상기 박막코팅층은 VO2 박막 및 TiO2 박막이 적어도 1회 이상 반복되는 것을 특징으로 하는 적층체.
    The method of claim 1,
    The thin film coating layer is a laminate, characterized in that the VO 2 thin film and the TiO 2 thin film is repeated at least one or more times.
  9. 제1항에 있어서,
    상기 박막코팅층은 두께가 3nm~10㎛인 것을 특징으로 하는 적층체.
    The method of claim 1,
    The thin film coating layer is a laminate, characterized in that the thickness of 3nm ~ 10㎛.
  10. 제9항에 있어서,
    상기 박막코팅층은 두께가 10~500nm인 것을 특징으로 하는 적층체.
    10. The method of claim 9,
    The thin film coating layer is a laminate, characterized in that the thickness of 10 ~ 500nm.
  11. 제1항에 있어서,
    상기 수지 패턴층은 UV 경화 수지 또는 열 경화 수지에 요철 패턴이 형성되어 이루어진 것을 특징으로 하는 적층체.
    The method of claim 1,
    The resin pattern layer is a laminate, characterized in that the concave-convex pattern is formed on the UV curable resin or thermosetting resin.
  12. 제1항에 있어서,
    상기 수지 패턴층은 상기 기재가 에칭되어 이루어진 것을 특징으로 하는 적층체.
    The method of claim 1,
    The said resin pattern layer is a laminated body characterized by the said base material being etched.
  13. 제1항에 있어서,
    상기 수지 패턴층은 컬러 수지 물질이 인쇄되어 이루어진 것을 특징으로 하는 적층체.
    The method of claim 1,
    The resin pattern layer is a laminate, characterized in that the color resin material is printed.
  14. 제1항에 있어서,
    상기 수지 패턴층은 색소를 포함하는 것을 특징으로 하는 적층체.
    The method of claim 1,
    The said resin pattern layer contains a pigment | dye, The laminated body characterized by the above-mentioned.
  15. 제1항에 있어서,
    상기 수지 패턴층은 3D 입체 패턴을 갖는 것을 특징으로 하는 적층체.
    The method of claim 1,
    The said resin pattern layer has a 3D three-dimensional pattern, The laminated body characterized by the above-mentioned.
  16. 제1항에 있어서,
    상기 수지 패턴층과는 반대쪽에서 상기 박막코팅층에 보호필름이 접착되거나 제1보호코팅층이 적층되는 것을 특징으로 하는 적층체.
    The method of claim 1,
    A laminate, characterized in that the protective film is bonded to the thin film coating layer or the first protective coating layer is laminated on the opposite side to the resin pattern layer.
  17. 제16항에 있어서,
    상기 제1보호코팅층은 인쇄층인 것을 특징으로 하는 적층체.
    The method of claim 16,
    The first protective coating layer is a laminate, characterized in that the printing layer.
  18. 제16항에 있어서,
    상기 제1보호코팅층은 Si3N4, SiC, NbOx, TiN, Ti 및 DLC중 적어도 하나를 포함하는 것을 특징으로 하는 적층체.
    The method of claim 16,
    The first protective coating layer is a laminate comprising at least one of Si 3 N 4 , SiC, NbOx, TiN, Ti and DLC.
  19. 제16항에 있어서,
    상기 박막코팅층과 보호필름 또는 제1보호코팅층의 사이에 제2보호코팅층이 적층되는 것을 특징으로 하는 적층체.
    The method of claim 16,
    And a second protective coating layer is laminated between the thin film coating layer and the protective film or the first protective coating layer.
  20. 제19항에 있어서,
    상기 제2보호코팅층은 Ti, TiO2, Si, SiO2, Ta2O5, Nb 및 NbOx 중 적어도 하나를 포함하는 것을 특징으로 하는 적층체.
    20. The method of claim 19,
    The second protective coating layer is a laminate comprising at least one of Ti, TiO 2 , Si, SiO 2, Ta 2 O 5 , Nb and NbO x .
  21. 제1항에 있어서,
    상기 수지 패턴층의 반대쪽에서 상기 기재에 방오코팅층이 적층되는 것을 특징으로 하는 적층체.
    The method of claim 1,
    An antifouling coating layer is laminated on the base material on the opposite side of the resin pattern layer.
  22. 제21항에 있어서,
    상기 방오코팅층은, MgF2, PTFE, DLC 및 TiO2 중 적어도 하나를 포함하는 것을 특징으로 하는 적층체.
    The method of claim 21,
    The antifouling coating layer, the laminate comprising at least one of MgF 2 , PTFE, DLC and TiO 2 .
  23. 제1항에 있어서,
    상기 기재를 통하여 상기 수지 패턴층의 패턴이 가시되는 것을 특징으로 하는 적층체.
    The method of claim 1,
    The laminated body characterized by the pattern of the said resin pattern layer being visible through the said base material.
  24. 제1항에 있어서,
    상기 수지 패턴층은 상기 기재와 반대쪽의 면에 패턴을 갖는 것을 특징으로 하는 적층체.
    The method of claim 1,
    The said resin pattern layer has a pattern in the surface on the opposite side to the said base material, The laminated body characterized by the above-mentioned.
  25. 제1항 내지 제24항 중 어느 한 항의 적층체를 제조하는 방법으로서,
    상기 박막코팅층을 스퍼터링, E-빔 이베퍼레이션(E-beam evaporation) 또는 저항 가열에 의하여 코팅하는 것을 특징으로 하는 적층체 제조방법.
    As a method of manufacturing the laminate of any one of claims 1 to 24,
    The thin film coating layer is a laminate manufacturing method characterized in that the coating by sputtering, E-beam evaporation (E-beam evaporation) or resistance heating.
KR1020110078718A 2010-08-11 2011-08-08 Multi-layered article and method of fabricating the same KR20120015273A (en)