KR20060100645A - Waterproof sheet using ethylene-vinylacetate copolymer and its manufacturing method - Google Patents

Waterproof sheet using ethylene-vinylacetate copolymer and its manufacturing method Download PDF

Info

Publication number
KR20060100645A
KR20060100645A KR1020050022340A KR20050022340A KR20060100645A KR 20060100645 A KR20060100645 A KR 20060100645A KR 1020050022340 A KR1020050022340 A KR 1020050022340A KR 20050022340 A KR20050022340 A KR 20050022340A KR 20060100645 A KR20060100645 A KR 20060100645A
Authority
KR
South Korea
Prior art keywords
waterproof sheet
waterproof
vinyl acetate
sheet
eva resin
Prior art date
Application number
KR1020050022340A
Other languages
Korean (ko)
Other versions
KR100655032B1 (en
Inventor
양우정
Original Assignee
주식회사 대흥산업
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 대흥산업 filed Critical 주식회사 대흥산업
Priority to KR1020050022340A priority Critical patent/KR100655032B1/en
Publication of KR20060100645A publication Critical patent/KR20060100645A/en
Application granted granted Critical
Publication of KR100655032B1 publication Critical patent/KR100655032B1/en

Abstract

본 발명은 건축 구조물의 옥상이나 지하외벽 및 지하 주차장 등에 사용되는 비노출 방수용 방수시트로서, 고함량의 초산비닐을 함유하는 에틸렌초산비닐공중합체 수지층 사이로 유리섬유를 함침시키고 상기 수지층 위아래로 부직포를 접착시킴으로써 제조되는 방수시트 및 그 제조방법에 관한 것이다. 본 발명의 방수시트는 에틸렌 50-60중량% 및 초산비닐 50-40중량%로 구성되는 2개의 EVA 수지층; 상기 EVA 수지층 사이에 제공되는 유리섬유층; 및 상기 2개의 EVA 수지층 상하 표면으로 함침된 부직포층으로 구성된다. The present invention is a non-exposed waterproof waterproof sheet used on a rooftop or basement outer wall of a building structure, underground parking lot, etc., impregnating glass fibers between a resin layer of ethylene vinyl acetate copolymer containing a high content of vinyl acetate and disposing the nonwoven fabric above and below the resin layer. It relates to a waterproof sheet produced by bonding and a method of manufacturing the same. Waterproof sheet of the present invention comprises two EVA resin layers composed of 50-60% by weight of ethylene and 50-40% by weight of vinyl acetate; A glass fiber layer provided between the EVA resin layers; And a nonwoven fabric layer impregnated with the upper and lower surfaces of the two EVA resin layers.

방수시트, 에틸렌초산비닐공중합체 Waterproof Sheet, Ethylene Vinyl Acetate Copolymer

Description

에틸렌초산비닐공중합체를 이용한 방수시트 및 그 제조방법{Waterproof sheet using ethylene-vinylacetate copolymer and its manufacturing method}Waterproof sheet using ethylene-vinylacetate copolymer and its manufacturing method

도1은 본 발명의 방수시트 단면도 및 A-A' 선을 따른 단면 확대도.1 is a cross-sectional enlarged view along the line A-A 'and waterproof sheet of the present invention.

도2는 본 발명의 일 실시예에 따라 인접하는 두개의 방수시트가 연결되는 구조를 보여주는 단면도.Figure 2 is a cross-sectional view showing a structure in which two adjacent waterproof sheet is connected according to an embodiment of the present invention.

본 발명은 일반 건축물이나 옥상바닥 등의 건축 구조물 및 지하외벽, 터널, 발전소, 지하 주차장 등의 지하 구조물 방수에 사용되는 비노출 방수용 방수시트 및 그 제조방법에 관한 것으로, 좀 더 구체적으로는 고함량의 초산비닐을 함유하는 에틸렌초산비닐공중합체 수지층 사이로 유리섬유를 함침시키고 상기 수지층 위아래로 부직포를 접착시켜 전체 방수시트가 일체 결합되어 수밀성이 뛰어나고 치수안정성 및 작업성이 우수한 방수시트 및 그것의 제조방법에 관한 것이다.The present invention relates to a non-exposed waterproof waterproof sheet and a method for manufacturing the same, which are used for waterproofing a building structure such as a general building or a rooftop, and an underground structure such as an underground exterior wall, a tunnel, a power plant, and an underground parking lot. Impregnating glass fibers between ethylene-vinyl acetate copolymer resin layers containing vinyl acetate and adhering the nonwoven fabric above and below the resin layer to form a waterproof sheet with excellent watertightness, excellent dimensional stability and workability by integrally bonding the entire waterproof sheet. It is about a method.

건축 구조물에 대한 방수방법으로서 종래 알려진 우레탄 방수, 아스팔트 방 수 및 도막방수 외에, 외부의 변화하는 기후조건에 잘 적응하며 현장에서 간편하게 시공될 수 있다는 장점을 갖는 시트방수는, 합성고무나 합성수지와 같은 합성고분자계 또는 고무화아스팔트 등을 주원료로 하여 보통 0.8 내지 3.0mm 두께의 일정 폭과 길이를 갖는 방수시트를 연달아 배치함으로써 방수 효과를 얻도록 한다. In addition to urethane waterproofing, asphalt waterproofing, and waterproofing of coatings as a waterproofing method for building structures, sheet waterproofing has advantages of being well adapted to external weather conditions and being easily constructed on site, such as synthetic rubber or synthetic resin. Synthetic polymer or rubberized asphalt is used as a main raw material to obtain a waterproof effect by successively disposing a waterproof sheet having a predetermined width and length of 0.8 to 3.0 mm in thickness.

합성고분자계 방수시트는 주요 성분에 따라 가황고무계, 비가황고무계, 염화비닐수지계, 에틸렌아세트산비닐수지계로 구분되고 형태에 따라 균질시트와 복합시트로 구분되는데, 최근에는 시트의 치수안정성이나 강도 및 역학적 물성을 개선하기 위해 섬유포나 보강포를 부착한 복합시트가 폭넓게 적용된다. Synthetic polymer waterproof sheet is divided into vulcanized rubber system, unvulcanized rubber system, vinyl chloride resin system, ethylene vinyl acetate resin system according to the main components, and homogeneous sheet and composite sheet according to the form. Recently, the dimensional stability, strength and mechanical properties of the sheet In order to improve physical properties, a composite sheet with fiber cloth or reinforcement cloth is widely applied.

종래 개발된 복합시트 방수방법들은 주로, 건축 구조물에 대한 지속적인 외부 충격이나 환경 조건의 변화 등으로 방수층에 균열이 발생한다거나 누수가 발생하여 구조물이 열화되는 것을 방지하고 시공상의 경제성과 편의성을 증진시키고자, 방수시트 원료 자체에 대한 물성 개선은 물론, 복합방수시트를 이루는 각 구성요소들의 결합 구조를 개선하는 것에 관한 것이었다. Conventionally developed composite sheet waterproofing methods are mainly to prevent the structure from deteriorating due to cracks or leaks in the waterproofing layer due to continuous external impact on the building structure or changes in environmental conditions, and to improve construction economy and convenience. In addition to improving the physical properties of the waterproof sheet raw material itself, as well as improving the bonding structure of each component of the composite waterproof sheet.

이와 관련한 종래 기술로서 공지된 것으로는 국내 특허 제412935호(2003. 12. 13 등록) "복합시트 방수재와 그 방수재를 이용한 방수방법" 및 특허 제354191호(2002. 9. 12 등록) "방수공사용 시트 제조방법"을 예로 들 수 있다.Known as a related art in this regard is the Korean Patent No. 412935 (registered on Dec. 13, 2003) "Compound sheet waterproofing method and waterproofing method using the waterproofing material" and Patent No. 354191 (Registered on Sep. 12, 2002) "Waterproof use Sheet production method ".

먼저 전자는 내구성과 치수안정성이 우수하고 시공이 간편한 복합시트 방수재로서, 아스팔트, SBS 열가소성 고무, 첨가제 및 충진제를 포함하는 하부 아스팔트시트; EVA를 포함한 에틸렌아세트산 비닐수지계 또는 EPDM을 포함한 고무계 시트로 된 상부시트; 및 상기 하부시트와 상부시트 사이에서 양시트를 일체로 결합시켜 유지하도록 배치되는 보강용 시트(부직포 또는 유리섬유로 구성됨)로 구성되며, 동일 구성의 인접 복합시트와의 일체 결합을 위해 상기 상부시트는 일단이 연장된 이음부를 갖는 것을 특징으로 하는 복합시트 방수재를 개시하였다. 상기에서 인접한 복합시트들의 이음부 접합은, 인접한 다른 복합시트의 상면에 이음부가 포개어지도록 배치하고 열융착기를 사용하여 300-600℃의 열풍으로 가열하여 대향된 시트들의 표면을 용융된 상태로 적층 가압함으로써 이루어진다. First, the former is a composite sheet waterproofing material having excellent durability and dimensional stability and easy construction, comprising: a lower asphalt sheet including asphalt, SBS thermoplastic rubber, additives, and fillers; An upper sheet made of an ethylene vinyl acetate resin system including EVA or a rubber sheet including EPDM; And a reinforcing sheet (consisting of nonwoven fabric or fiberglass) arranged to hold both sheets integrally between the lower sheet and the upper sheet, and the upper sheet for integral bonding with adjacent composite sheets of the same configuration. Discloses a composite sheet waterproofing material characterized in that one end has an extended joint. The joints of the adjacent composite sheets in the above are arranged so that the joints are stacked on the upper surface of another adjacent composite sheet and heated with a hot air at 300-600 ° C. using a heat welding machine to press the surface of the facing sheets in a molten state. By doing so.

이는 복합시트의 상부 재질로서 에틸렌아세트산 비닐수지 또는 EPDM 고무계 를 선택하고, 그 아래로는 부직포 또는 유리섬유 보강시트를 매개로 하여 하부의 아스팔트시트와 일체 결합되도록 함으로써, 터널내 방수에 있어 해결방안이 없었던 에틸렌아세트산 비닐수지계의 방수구간과 아스팔트 시트방수 구간의 연결부위와 같이 다른 재질의 연결부위에 대한 연결시공을 가능케 한다는 점에서 의미가 있는 것이었다. Ethylene vinyl acetate resin or EPDM rubber is selected as the upper material of the composite sheet, and underneath it is combined with the lower asphalt sheet through the nonwoven fabric or glass fiber reinforcement sheet. It was meaningful in that it was possible to connect the connection parts of other materials such as the connection section of the waterproof section and the asphalt sheet waterproof section of the ethylene vinyl acetate resin system, which were not available.

한편, 특허 제354191호는 호퍼에 분말 형태인 폴리에틸렌 80-85중량%와 아세트산 15-20중량%를 투입한 후 열을 가하여 혼합하는 단계; 호퍼의 일측면 하단에 형성된 배출구를 통하여 배출된 겔상태의 EVA를 일정한 형상을 갖도록 가열기에 의한 지속적인 가열 및 이송하는 단계; 부직포, 유리섬유, EVA, 부직포를 이송부로 이송시키면서, EVA의 상면에 그물형의 형상을 갖는 유리섬유를 얹혀놓고, 상기 유리섬유의 상면과 EVA의 저면에는 부직포를 위치시켜 놓은 다음 상기 압착부에 의해 열을 가하여 함침하는 단계; 및 함침공정을 거쳐 부직포, 유리섬유, EVA, 부직포 순으로 압착되어 제조된 시트의 열기를 공랭식을 이용한 냉각부에 의해 냉각하여, 방수공사용으로 사용될 수 있도록 시트가 생성되는 단계로 이루어지는 것을 특징으로 하는 방수공사용 시트의 제조방법을 개시하였다.On the other hand, Patent No. 354191 is a 80-85% by weight of polyethylene and 15-20% by weight of acetic acid in the form of a powder in the hopper mixing step by applying heat; Continuously heating and transferring the gel EVA discharged through the outlet formed at the bottom of one side of the hopper by a heater to have a predetermined shape; While transferring the nonwoven fabric, glass fiber, EVA, and nonwoven fabric to the conveying part, a glass fiber having a mesh shape is placed on the upper surface of the EVA, and a nonwoven fabric is placed on the upper surface of the glass fiber and the bottom of the EVA, and then the crimping portion Impregnating by applying heat; And through the impregnation process non-woven fabric, glass fiber, EVA, the non-woven fabric is compressed in order to the heat of the sheet is cooled by a cooling unit using an air cooling method, the step of producing a sheet to be used for waterproof construction Disclosed is a method for manufacturing a waterproofing sheet.

이는 종래의 시트방수가 갖는 문제점들, 즉 기온차에 의한 수축 변형 및 시트 사이의 틈으로 인한 누수, 침수 현상과 같은 단점을 개선하고, 고무재 방수의 경우 태양열 및 자외선에 노출되어 수축과 팽창을 반복함으로써 틈과 균열이 발생하였던 문제점을 해결하기 위하여, EVA를 방수시트의 기본 재료로 채택하되, 방수용으로 안정적인 강도를 제공하기 위해 폴리에틸렌과 아세트산의 함량비를 80-85중량% : 15-20중량%로 한정하고, EVA가 열변형되는 것을 방지하기 위해 유리섬유를 부착시키며, 유리섬유 및 EVA와의 친밀도 향상을 위해 이들 구조 위아래로 부직포를 제공하는 것으로, EVA 수지층과 부직포, 유리섬유 상호간의 결합을 위해서는 열을 가하도록 하였다.This improves the problems of the conventional sheet waterproofing, that is, the disadvantages such as shrinkage deformation due to the temperature difference and leakage between the sheets and immersion, and in the case of waterproofing rubber material, it is exposed to solar heat and ultraviolet rays to repeat shrinkage and expansion. In order to solve the problem of cracks and cracks, EVA is used as the base material of the waterproof sheet, but the content ratio of polyethylene and acetic acid is 80-85% by weight: 15-20% by weight to provide stable strength for waterproofing. It is limited to, to attach the glass fibers to prevent the thermal deformation of the EVA, and to provide a non-woven fabric up and down these structures to improve the intimacy with the glass fiber and EVA, the bonding between the EVA resin layer and the non-woven fabric, glass fibers In order to apply heat.

그러나, 상기 방법에 의할 경우 유리섬유 위로 부직포를 제공함에 있어 단지 겔상태의 EVA를 가열하기 위한 가열기에 의해 제공되는 열을 이용함으로써 유리섬유와 부직포 사이의 접착력이 약화되어 수로를 형성할 가능성이 있었고, 이로 인해 방수층의 일체 결합력은 물론 방수층의 수밀성이 저하될 우려가 있었다. 또한 폴리에틸렌과 아세트산의 비율이 80-85:15-20에 불과하여 원가절감 효과는 기대할 수 있을지라도 인장강도 및 신장률, 저온굴곡성과 같은 물성 면에서 유연성이 떨어져 작업성이 떨어진다는 문제점도 있었다. However, in the above method, in providing the nonwoven fabric over the glass fibers, the possibility of forming a channel by weakening the adhesive force between the glass fibers and the nonwoven fabric by using only the heat provided by the heater for heating the gel EVA. As a result, there was a fear that the watertightness of the waterproof layer was lowered as well as the integral bonding force of the waterproof layer. In addition, although the ratio of polyethylene and acetic acid is only 80-85: 15-20, the cost reduction effect can be expected, but there is also a problem that the workability is inferior in flexibility in terms of physical properties such as tensile strength, elongation and low temperature bendability.

따라서 본 발명자는 상술된 시트를 이용한 종래 방수방법상의 문제점을 극복하고자 개선된 방수재질 및 방수구조에 관한 연구를 거듭한 결과 본 발명의 방수시 트 및 그 제조방법을 완성하게 되었다.Therefore, the present inventors have completed the study on the improved waterproofing material and waterproof structure to overcome the problems in the conventional waterproofing method using the above-described sheet was completed the waterproof sheet and the manufacturing method of the present invention.

본 발명의 목적은 고함량의 초산비닐을 함유하는 에틸렌초산비닐공중합체 수지(EVA)를 방수시트의 주원료로 채택함으로써 물성 및 작업성이 현저히 개선되고 방수 수밀성이 우수한 방수시트 및 그 제조방법을 제공하는 것이다.SUMMARY OF THE INVENTION An object of the present invention is to adopt an ethylene vinyl acetate copolymer resin (EVA) containing a high content of vinyl acetate as the main raw material of a waterproof sheet, thereby providing a waterproof sheet excellent in water properties and workability and excellent in watertight water tightness and a manufacturing method thereof. It is.

본 발명의 또 다른 목적은 에틸렌초산비닐공중합체 수지층 사이로 유리섬유를 함침시키고 상기 수지층 위아래로 부직포를 접착시켜 전체 방수시트가 일체 결합되어 방수 수밀성과 치수안정성이 우수한 방수시트 및 그 제조방법을 제공하는 것이다. Another object of the present invention is to impregnate the glass fiber between the ethylene vinyl acetate copolymer resin layer and to adhere the non-woven fabric to the resin layer above and below the entire waterproof sheet is integrally combined waterproof waterproof and dimensional stability excellent waterproof sheet and its manufacturing method To provide.

상기 목적을 달성하기 위하여 본 발명의 방수시트는, 상기 특허 제354191호에서 EVA 제조를 위해 폴리에틸렌 80-85중량%와 아세트산 15-20중량%를 가열 혼합하였던 것과는 달리, 방수층의 주원료 물질로서 에틸렌과 초산비닐을 채택하고 이들을 각각 50-60중량% 및 50-40중량% 준비하여 혼합한 후 가열기로 가열하면서 용융압출시켜 EVA 수지층을 얻으며, 2개의 상기 EVA 수지층 사이로 유리섬유를 공급하는 동시에, 상기 EVA 수지층의 상하 표면으로 부직포를 제공하여 함침시킴으로써 얻어진다. In order to achieve the above object, the waterproof sheet of the present invention is different from 80-85% by weight of polyethylene and 15-20% by weight of acetic acid for EVA production in Patent No. 354191, unlike ethylene and water as the main raw material of the waterproof layer. Adopting vinyl acetate and preparing 50-60% by weight and 50-40% by weight, respectively, and mixing and melt-extruded while heating with a heater to obtain an EVA resin layer, while feeding the glass fiber between the two EVA resin layer, It is obtained by impregnating a nonwoven fabric on the upper and lower surfaces of the EVA resin layer.

즉, 본 발명에 따른 방수시트는 에틸렌 50-60중량% 및 초산비닐 50-40중량% 로 구성되는 2개의 EVA 수지층; 상기 EVA 수지층 사이에 제공되는 유리섬유층; 및 상기 2개의 EVA 수지층 상하 표면으로 제공되는 부직포층으로 구성된다. That is, the waterproof sheet according to the present invention comprises two EVA resin layers composed of 50-60% by weight of ethylene and 50-40% by weight of vinyl acetate; A glass fiber layer provided between the EVA resin layers; And a nonwoven fabric layer provided on the upper and lower surfaces of the two EVA resin layers.

본 발명에 따른 방수시트의 제조방법은, 에틸렌 50-60중량% 및 초산비닐 50-40중량%를 혼합한 후 가열된 압출성형기를 통해 EVA 수지를 용융압출시키고, 가열되는 2개의 다이스를 통해 공급되는 2개의 상기 EVA 수지층 사이로 유리섬유를 공급하는 동시에, 상기 2개의 EVA 수지층의 상하 바깥쪽 표면으로 부직포를 제공하여 함침시키는 것으로 구성된다.Method for producing a waterproof sheet according to the present invention, by mixing 50-60% by weight of ethylene and 50-40% by weight of vinyl acetate, melt-extruded EVA resin through a heated extruder, and supplied through two dies heated It is composed of supplying glass fibers between the two EVA resin layers to be impregnated, while providing a nonwoven fabric to the upper and lower outer surfaces of the two EVA resin layers.

본 발명의 방수시트의 주원료인 EVA는 에틸렌과 초산비닐을 공중합시켜 얻어지는 폴리머로서 저온 열봉합성과 가교특성이 우수하여 신발용 스폰지, 일용잡화나 완구 등의 일반 성형품은 물론, 농업용 및 식품포장용 필름, 핫멜트 접착제의 원료, 왁스, 개질제, 도료 등 다양한 용도로 이용되며, 그 성상은 일반적으로 분자량과 초산비닐의 함량에 따라 다르다. 즉 초산비닐 함량이 증가하면 밀도, 고무탄성, 유연성, 다른 폴리머나 가소제와의 상용성이 향상되고 경화온도는 저하된다. 구체적으로 초산비닐이 10-20% 정도의 것은 PVC 등과 배합하여 성형성, 저온 유연성을 향상시키는데 이용되고, 25-30%의 초산비닐을 함유하는 것은 왁스에 첨가해서 취약(脆弱)성과 열접착성 등을 개량하는데 이용된다. EVA, which is the main raw material of the waterproof sheet of the present invention, is a polymer obtained by copolymerizing ethylene and vinyl acetate, and has excellent low-temperature heat sealing properties and crosslinking properties, so that it is not only general molded articles such as shoe sponges, daily necessities or toys, but also agricultural and food packaging films, It is used for various purposes such as raw materials of hot melt adhesives, waxes, modifiers, paints and the like, and its properties generally depend on the molecular weight and the content of vinyl acetate. In other words, increasing the vinyl acetate content improves density, rubber elasticity, flexibility, compatibility with other polymers and plasticizers, and lowers the curing temperature. Specifically, vinyl acetate containing 10-20% is used to improve moldability and low temperature flexibility by mixing with PVC and the like, and 25-30% of vinyl acetate is added to wax to be fragile and heat-adhesive. It is used to improve the back.

또한 EVA는 내환경응력균열저항(ESCR) 뿐만 아니라 휨, 균열저항이 우수하고, 넓은 온도범위에서 탄성 및 반발력이 뛰어나며, 물리적 물성의 열화를 일으키지 않으면서 충진제와의 혼용성이 우수하여, 본 발명의 방수시트의 주원료로서 사용하기에 적합하다. In addition, EVA is excellent in bending stress and crack resistance as well as environmental stress cracking resistance (ESCR), excellent elasticity and repulsive force over a wide temperature range, excellent compatibility with the filler without causing deterioration of physical properties, the present invention It is suitable for use as the main raw material of waterproof sheet.

다만, 방수시트는 시트의 상하 균형 및 열등한 외부 환경에 따라 시트가 뒤틀리거나 휘어져서는 아니되며, EVA 수지층 사이 및 수지층 상하에 제공되는 보강재층과 일체 결합되어 보강재층의 결합력 약화로 수로가 형성되는 등의 문제가 발생하여서는 아니되므로, 본 발명은 우수한 치수안정성과 인장강도, 수밀성을 확보하기 위하여 방수시트를 형성하는 구성 원료비를 에틸렌 50-60중량% 및 초산비닐 50-40중량%와 같이 초산비닐의 함량을 대폭 증가시켜 이용한다. However, the waterproof sheet should not be twisted or bent according to the top and bottom balance of the sheet and inferior external environment, and the channel is formed by weakening the bonding strength of the reinforcement layer by being integrally combined with the reinforcement layer provided between the EVA resin layers and above and below the resin layer. In order to ensure excellent dimensional stability, tensile strength, and watertightness, the present invention uses acetic acid, such as 50-60% by weight of ethylene and 50-40% by weight of vinyl acetate, to form a waterproof sheet to ensure excellent dimensional stability, tensile strength, and watertightness. The vinyl content is greatly increased.

이렇게 초산비닐의 함량이 40-50% 정도 되면 EVA의 인장강도 등 물성이 개선되고 EVA 수지층과 결합되는 보강재층과의 결합력도 증대되며 작업성 또한 현저히 증가한다. When the content of vinyl acetate is about 40-50%, the physical properties such as the tensile strength of EVA are improved, the bonding strength with the reinforcement layer combined with the EVA resin layer is increased, and the workability is also significantly increased.

또한 본 발명은 EVA 수지층 사이에 보강재로서 유리섬유를 제공하고 상기 수지층 위아래로 부직포를 포함하는 다층시트 형태를 취하는데, 이는 종래 기술에 의할 경우(예를 들어 상기 국내특허 제354191호) 하나의 EVA 수지층 위로 유리섬유를 제공하고 유리섬유 상부와 EVA 하부 각각에 부직포를 제공하여 시트를 구성함으로써, 수분에 노출될 경우 보강재를 타고 수분이 유입되어 수로가 형성되고 보강재와EVA 수지층이 쉽게 박리되며 내구성이나 기계적 물성이 저하되는 문제점이 있었던 것을 개선하기 위한 것이다.In another aspect, the present invention provides a glass fiber as a reinforcing material between the EVA resin layer and takes the form of a multi-layer sheet comprising a nonwoven fabric up and down the resin layer, which is according to the prior art (for example, the domestic patent No. 354191). By providing a glass fiber over one EVA resin layer and providing a nonwoven fabric on each of the glass fiber upper part and the EVA lower part to form a sheet, when exposed to moisture, water enters through a reinforcement material and a water channel is formed. Easily peeled off and to improve the problem that the durability and mechanical properties are deteriorated.

즉, 압출성형기의 스크류를 통해 고온에서 압출되어 나오는 EVA 수지층을 2개의 다이스로부터 제공받아 2개의 EVA 수지층 사이로 유리섬유를 제공하고, 이와 동시에 EVA 수지층의 바깥쪽 상하로 부직포를 함침시켜 EVA 수지층과 보강재가 일체결합됨으로써, 시트가 수분에 노출되더라도 보강재를 타고 수분이 유입되어 수로 가 형성될 가능성이 없고 보강재의 상하를 EVA 수지가 감싸고 있어 박리나 이탈 현상이 발생할 여지가 없게 되는 것이다. That is, the EVA resin layer extruded at a high temperature through the screw of the extruder is provided from two dies to provide glass fibers between the two EVA resin layers, and at the same time, the impregnated nonwoven fabric up and down the outer side of the EVA resin layer Since the resin layer and the reinforcing material are integrally bonded, even if the sheet is exposed to moisture, there is no possibility that water flows through the reinforcing material to form a water channel, and EVA resin is wrapped around the upper and lower parts of the reinforcing material so that there is no room for peeling or leaving.

이하 첨부된 도면을 참고로 본 발명을 보다 구체적으로 살펴보도록 하겠다. Hereinafter, the present invention will be described in more detail with reference to the accompanying drawings.

도 1은 본 발명의 방수시트의 일부 단면도 및 A-A'선을 따른 확대 단면도이고, 도 2는 본 발명에 따라 인접하는 두개의 방수시트가 연결되는 구조를 보여주는 단면도이다.1 is a partial cross-sectional view of the waterproof sheet of the present invention and an enlarged cross-sectional view along line A-A ', and FIG. 2 is a cross-sectional view showing a structure in which two adjacent waterproof sheets are connected according to the present invention.

상기 도면으로부터 본 발명의 방수시트는 에틸렌과 초산비닐을 공중합하여 얻어지는 EVA 수지층(10); 상기 EVA 수지층(10) 중심에 제공되는 유리섬유층(12); 및 상기 EVA 수지층(10) 상하 표면으로 제공된 부직포층(20 및 30)으로 구성됨을 알 수 있다. Waterproofing sheet of the present invention from the drawings is an EVA resin layer 10 obtained by copolymerizing ethylene and vinyl acetate; A glass fiber layer 12 provided at the center of the EVA resin layer 10; And it can be seen that the non-woven fabric layer 20 and 30 provided to the upper and lower surfaces of the EVA resin layer 10.

이러한 방수시트는, 에틸렌 50-60중량% 및 초산비닐 50-40중량%를 혼합기에 넣어 혼합한 후 호퍼로 이송하고, 이를 가열기로 가열되는 압출성형기의 스크류를 통해 용융압출시켜 EVA 수지(11)를 2개의 다이스를 통해 공급하고, 다이스를 가열하면서 상기 2개의 EVA 수지(11) 사이로 유리섬유(12)를 공급하는 동시에, 상기 2개의 EVA 수지(11)의 상하 바깥쪽 표면으로 부직포(20 및 30)를 접착시킴으로써 제조된다.The waterproof sheet is mixed with 50 to 60% by weight of ethylene and 50 to 40% by weight of vinyl acetate, and then transferred to a hopper, and melt-extruded through a screw of an extruder heated by a heater to EVA resin (11). Is supplied through two dies, and the glass fiber 12 is supplied between the two EVA resins 11 while heating the dies, and the nonwoven fabric 20 and the upper and lower outer surfaces of the two EVA resins 11 are supplied. 30) by adhering.

본 발명의 방수시트를 이용하여 방수공사를 함에 있어서는, 도 1의 구성을 갖는 방수시트를 방수 바탕면에 연속하여 인접 배치하여야 한다. 이에 관한 실시예는 도 2에 도시되어 있다. 여기서 상기 도 1의 방수시트와 동일한 구성을 갖는 인접 방수시트의 구성요소들은 해당 도면부호에 '를 부기하였다.In the waterproof construction using the waterproof sheet of the present invention, the waterproof sheet having the configuration of FIG. 1 should be continuously adjacent to the waterproof base surface. An embodiment of this is shown in FIG. 2. Here, the components of the adjacent waterproof sheet having the same configuration as the waterproof sheet of FIG. 1 are denoted by the reference numeral.

도 2에 도시된 바와 같이 인접하는 동일 구성의 방수시트들을 긴밀하게 연결하기 위해서는, EVA 수지층(10)의 상하로 제공되는 부직포(20 및 30)를 인접하는 방수시트와의 이음부 길이만큼 모자라게 재단하여 접착되도록 하여야 한다. 즉, 인접하는 시트 각각의 EVA 수지층(10 및 10')의 상부에 접착되는 부직포(20 및 20')는 예를 들어, EVA 수지층(10 및 10')의 우측 상단으로 이음부 길이만큼 모자라게 재단하여 접착하고, EVA 수지층(10 및 10')의 하부로 제공되는 부직포(30 및 30')는 EVA 수지층(10 및 10')의 좌측 하단으로 이음부 길이만큼 모자라게 재단하여 접착하여, 인접하는 방수시트들은 이음부에서 동질의 EVA 수지층(10 및 10')끼리 접하게 됨으로써 인접부에서 일체결합을 도모할 수 있게 되며, 방수의 수밀성을 확보되어 인접부에서의 누수 현상이나 박리현상을 발생할 여지가 없게 되는 것이다.In order to closely connect the adjacent waterproof sheets of the same configuration as shown in FIG. 2, the nonwoven fabrics 20 and 30 provided above and below the EVA resin layer 10 are shortened by the length of the joint with the adjacent waterproof sheets. It should be cut and bonded. That is, the nonwoven fabrics 20 and 20 'adhered to the upper portions of the EVA resin layers 10 and 10' of each of the adjacent sheets are, for example, the length of the joint to the upper right side of the EVA resin layers 10 and 10 '. Insufficiently cut and bonded, and the nonwoven fabrics 30 and 30 'provided as the lower portions of the EVA resin layers 10 and 10' are cut and adhered to the lower left of the EVA resin layers 10 and 10 'by the length of the joints. Adjacent waterproof sheets are in contact with the homogeneous EVA resin layers 10 and 10 'at the joints, thereby enabling integral bonding at adjacent portions, ensuring watertightness of waterproofing, and water leakage or peeling at adjacent portions. There is no room for it.

이러한 방법으로 본 발명의 방수시트들을 연속적으로 배치하여 건축 구조물의 방수 바탕면에 대한 시트방수가 마무리되면, 부직포 상면(20 및 20') 또는 이음부 위로 방수도막재를 도포하거나 또는 그 위로 누름 콘크리트를 도포하여 방수공사를 완성한다. In this way, when the waterproof sheet of the present invention is continuously disposed and the sheet waterproof to the waterproof base surface of the building structure is finished, the waterproof coating material is applied or pressed onto the upper surfaces of the nonwoven fabrics 20 and 20 'or the joints. Apply waterproofing finish.

상기한 바와 같이 본 발명에 따르면, 고함량의 초산비닐을 함유하는 EVA 수지를 방수시트의 주원료로 채택함으로써 물성 및 작업성이 현저히 개선되고 방수 수밀성이 우수한 방수시트 및 그 제조방법이 제공된다.As described above, according to the present invention, by adopting the EVA resin containing a high content of vinyl acetate as the main raw material of the waterproof sheet, the physical properties and workability is remarkably improved, and the waterproof sheet excellent in waterproof and watertightness, and a manufacturing method thereof.

또한 본 발명에 따르면 EVA 수지층 중심에 유리섬유를 함침시키고 상기 수지 층 위아래로 부직포를 접착시켜 전체 방수시트가 일체 결합되어 방수 수밀성과 치수안정성이 우수한 방수시트 및 그 제조방법을 제공할 수 있게 된다.In addition, according to the present invention by impregnating the glass fiber in the center of the EVA resin layer and by adhering the non-woven fabric on the resin layer up and down, the entire waterproof sheet is integrally combined to provide a waterproof sheet and a manufacturing method excellent in waterproof watertightness and dimensional stability. .

Claims (2)

에틸렌 50-60중량% 및 초산비닐 50-40중량%로 구성되는 2개의 EVA 수지층; 상기 EVA 수지층 사이에 제공되는 유리섬유층; 및 상기 2개의 EVA 수지층 상하 표면으로 제공된 부직포층으로 구성되는 방수시트. Two EVA resin layers composed of 50-60 wt% ethylene and 50-40 wt% vinyl acetate; A glass fiber layer provided between the EVA resin layers; And a nonwoven layer provided on upper and lower surfaces of the two EVA resin layers. 에틸렌 50-60중량% 및 초산비닐 50-40중량%를 혼합한 후 가열된 압출성형기를 통해 EVA 수지를 용융압출시키고, 가열되는 2개의 다이스를 통해 공급되는 2개의 상기 EVA 수지층 사이로 유리섬유를 공급하는 동시에, 상기 2개의 EVA 수지층의 상하 바깥쪽 표면으로 부직포를 제공하여 함침시키는 것으로 구성되는 방수시트의 제조방법.After mixing 50-60% by weight of ethylene and 50-40% by weight of vinyl acetate, melt-extruding the EVA resin through a heated extruder, and feeding the glass fibers between the two layers of EVA resin supplied through two heated dice. At the same time supplying, the manufacturing method of the waterproof sheet consisting of impregnating the non-woven fabric to the upper and lower outer surfaces of the two EVA resin layers.
KR1020050022340A 2005-03-17 2005-03-17 Waterproof sheet using ethylene-vinylacetate copolymer and its manufacturing method KR100655032B1 (en)