KR20060024476A - An end construction of procedure using of yellow soil and white soil - Google Patents

An end construction of procedure using of yellow soil and white soil Download PDF

Info

Publication number
KR20060024476A
KR20060024476A KR1020040072918A KR20040072918A KR20060024476A KR 20060024476 A KR20060024476 A KR 20060024476A KR 1020040072918 A KR1020040072918 A KR 1020040072918A KR 20040072918 A KR20040072918 A KR 20040072918A KR 20060024476 A KR20060024476 A KR 20060024476A
Authority
KR
South Korea
Prior art keywords
loess
clay
construction
ocher
white clay
Prior art date
Application number
KR1020040072918A
Other languages
Korean (ko)
Inventor
송용도
Original Assignee
송용도
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 송용도 filed Critical 송용도
Priority to KR1020040072918A priority Critical patent/KR20060024476A/en
Publication of KR20060024476A publication Critical patent/KR20060024476A/en

Abstract

본 발명은 황토 및 백토를 이용한 건축마감 시공방법 및 건축마감재에 관한 것으로서 보다 구체적으로는 황토 및 백토, 톱밥, 물, 수용성접착제를 섞은 황토조성물 내지 백토조성물을 건축마감으로 시공하는 방법에 관한 것이다.The present invention relates to a construction finishing method and construction finishing material using loess and clay, and more particularly, to a method of constructing a loess composition or a clay composition mixed with loess and white clay, sawdust, water, and a water-soluble adhesive as a construction finish.
본 발명에 따른 황토 및 백토를 이용한 건축마감 시공방법 및 건축마감재를 사용하는 경우에는 건물마감시공 시에 장판을 깔거나 벽지를 바르거나 페인트를 칠하지 않아도 되며, 건물의 시공 시에 황토 또는 백토 자체의 기능과 색감, 질감 등을 증대시켜 주거 인테리어의 새로운 문화를 제시한다.In the case of using the building finishing construction method and building finishing material using loess and clay according to the present invention, it is not necessary to lay the floor covering, wallpaper or paint at the time of building finishing construction, It suggests a new culture of residential interiors by increasing functions, colors and textures.
또한, 본 발명에 따른 황토 및 백토를 이용한 건축마감 시공방법 및 건축마감재를 사용하는 경우에는 화재예방과 유독성가스가 발생되지 않으며, 일정한 온도를 유지시켜 주는 방온기능이 뛰어나고, 일정한 습도를 유지시키는 방습능력이 우수하며, 해충이나 박테리아 등이 서식하지 못하게 하는 방물성이 현저하며, 소음을 차단하는 방음성이 뛰어나며, 에너지 효율성이 막대하다.In addition, when using the building finishing construction method and building finishing material using loess and white clay according to the present invention, fire prevention and toxic gas is not generated, and excellent temperature protection function to maintain a constant temperature, moistureproof to maintain a constant humidity Excellent ability, excellent waterproofing to prevent pests and bacteria from inhabiting, excellent soundproofing to block noise, and enormous energy efficiency.
황토, 백토, 톱밥, 접착제, 보일러Ocher, clay, sawdust, glue, boiler

Description

황토 및 백토를 이용한 건축마감 시공방법 {An end construction of procedure using of yellow soil and white soil}{An end construction of procedure using of yellow soil and white soil}
도 1은 종래의 시멘트 몰탈 공법에 의한 건축마감 시공방법에 따른 시멘트 층의 일부확대도.1 is an enlarged view of a part of the cement layer according to the construction finishing construction method by the conventional cement mortar method.
도 2는 종래의 황토를 이용한 건축마감 시공방법에 따른 황토구성층의 일부확대도.Figure 2 is an enlarged view of a part of the ocher constituent layer according to the construction finishing method using the conventional loess.
도 3은 본 발명의 일실시예에 따른 황토 및 백토를 이용한 건축마감 시공방법을 나타낸 공정도.Figure 3 is a process diagram showing the construction finish construction method using loess and white clay according to an embodiment of the present invention.
도 4는 본 발명에 따른 황토 및 백토를 이용한 건축마감 시공방법에 의한 건축마감재의 일부분해사시도.Figure 4 is a partial perspective view of the building finishing material by the building construction method using the loess and clay according to the present invention.
도 5는 본 발명의 일실시예에 따른 황토 및 백토를 이용한 건축마감 시공방법에 따른 황토 내지 백토조성물층의 일부확대도.Figure 5 is an enlarged view of a part of the loess to white clay composition layer according to the construction finishing method using the loess and clay in accordance with an embodiment of the present invention.
< 도면의 주요 부분에 대한 부호의 설명 ><Description of Symbols for Main Parts of Drawings>
100: 황토 및 백토마감재 10: 황토 및 백토조성물층100: loess and white clay finishing material 10: loess and white clay composition layer
12: 톱밥 14: 메쉬12: sawdust 14: mesh
20: 황토 및 백토층 30: 코팅층20: loess and clay layer 30: coating layer
본 발명은 황토 및 백토를 이용한 건축마감 시공방법 및 건축마감재에 관한 것으로서 보다 구체적으로는 황토 및 백토에 톱밥, 물, 수용성접착제를 섞은 황토조성물 및 백토조성물을 건축마감으로 시공하는 방법 및 이에 의해 생산된 건축마감재에 관한 것이다.The present invention relates to a construction finishing method and construction finishing materials using loess and clay, and more specifically, a method of constructing a loess composition and a clay composition mixed with sawdust, water, and a water-soluble adhesive in loess and white soil as a construction finish and thereby producing It is about finished building materials.
현대의 건물들은 건물벽이나 바닥 천정에 몰탈 미장 작업을 하고 보온기능과 소음을 차단하기 위해 스티로폴이나 석고보드 합판 등을 이용하여 목작업을 마치고 벽지 장판 페인트 등으로 마감하여 건설되어 진다.Modern buildings are constructed by finishing mortar plastering on building walls and floor ceilings, and finishing with woodwork using styropol or gypsum board plywood to block insulation and noise.
이러한 건축형태는 시멘트가 주재료로 사용되고 있으며, 시멘트의 주재료인 시멘트 몰탈 공법은 석회석을 분쇄 미세입자로 만들어 화학물질과 접착제를 첨가시켜 만들며, 도1에서 보는 바와 같이 상기 성분들이 화학적 반응을 일으켜 수분은 증발되며 딱딱한 고체로 되어진다.In this type of construction, cement is used as the main material, and cement mortar process, which is the main material of cement, is made by adding lime and chemicals to make fine particles and adding chemicals and adhesives, as shown in FIG. It evaporates to a hard solid.
상기의 석회석을 이용한 건축물은 모래와 시멘트입자의 결합으로 인하여 견고하지만 열전도율이 외부의 온도변화가 직접 건물에 영향을 미쳐 겨울에는 춥고 여름에는 덥다.The building using limestone is solid due to the combination of sand and cement particles, but its thermal conductivity is cold in winter and hot in summer because the external temperature change directly affects the building.
또한 이러한 건축방법의 마감처리시에 석고보드, 스티로폴, 합판 등으로 처리후 바닥에 장판을 깔거나 벽이나 천정에 벽지나 페인트를 다시 칠하여야 하므로 부수적인 자재와 비용이 들며, 상기의 벽지나 페인트 등의 건축자재를 노출시키므 로 인체에 유해하였다.In addition, the finishing method of this building method is to add plasterboard, styropol, plywood, etc. and then repaint the wall or ceiling, or wallpaper or paint on the walls or ceiling, so it is an additional material and cost. It was harmful to human body by exposing building materials.
이러한 문제점을 해결하기 위하여 황토 및 백토를 건축자재로 사용하여 방습력, 압축강도, 열전도율, 공극율의 향상시키기 위하여 맥반석, 마사토, 옥석 등을 섞어서 방습효과를 높이는 건축마감방법이 공지되어 있으나 상기의 공지된 기술은 기존의 시멘트를 사용하여 건축물을 마감하는 방법과 마찬가지로 화학물질과 접착제를 사용하기 때문에 도 2에서 보는 바와 같이 황토입자와 맥반석, 마사토, 옥석 등의 입자 사이에 화학적 반응을 일으켜 수분이 증발하면 시멘트와 같이 딱딱한 고체로 형성된다.In order to solve this problem, the building finishing method is known to increase the moisture-proof effect by mixing the ganban, masato, jade stone to improve the moisture-proof, compressive strength, thermal conductivity, porosity by using the loess and white clay as a building material As the conventional technology uses chemicals and adhesives, similar to the method of finishing a building using conventional cement, as shown in FIG. 2, a chemical reaction occurs between the ocher particles and the particles of macban, masato, jade, and water to evaporate. It is formed of a hard solid like cement.
상기의 황토와 맥반석, 마사토, 옥석 등을 사용하는 건축마감시공방법 내지 건축마감재는 표면이 매끄럽지 못하며, 황토가 가지는 보온 방습 방음 방물 기능이 현저히 떨어져서 기존의 시멘트와 별반 다를 게 없다고 하겠다.The building finishing construction method or building finishing material using the ocher and elvan, masato, jade and the like is not smooth surface, the thermal insulation and soundproof soundproofing of the loess is markedly apart from the existing cement.
또한, 상기 향토에 맥반석, 마사토, 옥석 등을 섞어서 만든 건축자재는 맥반석, 마사토, 옥석 등을 사용함으로서, 따로 맥반석, 마사토, 옥석 등을 공급받아야 하는 번거로움과 맥반석, 마사토, 옥석이 생산단가에 포함되어 제품단가가 높다는 문제점과 황토입자와 맥반석, 마사토, 옥석 등의 입자 사이에 화학적 반응으로 향토가 인체에 좋은 영향을 미치는 효과가 감쇄되는 문제점이 있었다.In addition, the building materials made by mixing ganban stone, masato, jade stone and the like in the local area by using banban stone, masato, jade stone, etc., the hassle of having to be supplied with ganban stone, masato, jade stone, etc. There is a problem that the product cost is high, and the effect that the local effect on the human body is attenuated by the chemical reaction between the loess particles and the particles of elvan, masato, jade stone.
이에 본 발명은 상기와 같은 문제점들을 해결하기 위하여 발명한 것으로서 본 발명의 목적은 주변에서 쉽게 구할 수 있는 황토, 백토, 톱밥, 수용성접착제 만 을 사용하여 건축물의 마감처리를 함으로서 황토 및 백토가 가지는 인체에 좋은 장점을 직접 영향을 미치도록 함에 있다.Therefore, the present invention has been invented to solve the above problems, the object of the present invention by using only ocher, white clay, sawdust, water-soluble adhesives that can be easily obtained from the surroundings of the building by the finishing treatment of the loess and the clay body To have a direct impact on the good.
또한 황토, 백토, 톱밥, 수용성접착제만을 사용함으로써 건축물을 친환경적으로 시공될 수 있도록 하며, 건물의 노후 등으로 건물을 철거할 때에 건축물 쓰레기의 배출을 적게 하며, 황토 및 백토 성분만을 쉽게 분리하여 재활용을 가능할 수 있게 함에 있다.
In addition, by using only loess, clay, sawdust, and water-soluble adhesives, the building can be constructed in an environmentally friendly manner. When dismantling the building due to the deterioration of the building, the emission of building waste is reduced. To make it possible.
본 발명은 황토 및 백토를 이용한 건축마감 시공방법 및 건축마감재에 관한 것으로서 더욱 상세하게는 건물의 벽 내지 천정에 황토 내지 백토7.8 ~ 8.2중량부, 톱밥 1.9 ~ 2.1중량부, 물 5.8 ~ 6.2중량부, 수용성접착제 1중량부로 만든 황토조성물 내지 백토조성물을 2~5cm로 도포하고; 상기 황토 내지 백토조성물 위에 메쉬를 덮어 일정부분 황토의 작은 입자가 메쉬 표면을 덮게 하고; 상기 메쉬를 덮은 상기 황토 내지 백토조성물을 건조시키고; 상기 건조된 황토 내지 백토조성물에 황토 내지 백토를 정제한 황토 내지 백토도료를 1 내지 2번 칠하는 것을 특징으로 하는 황토 및 백토를 이용한 건물벽 내지 천정의 건축마감시공방법에 관한 것이다.The present invention relates to a construction finishing method and construction finishing material using loess and clay, more specifically loess to clay 7.8 to 8.2 parts by weight, sawdust 1.9 to 2.1 parts by weight, water 5.8 to 6.2 parts by weight on the wall or ceiling of the building. Applying the ocher composition made from 1 part by weight of the water-soluble adhesive to the clay composition 2 ~ 5cm; Covering the mesh on the loess to the clay composition so that a small portion of the loess covers the surface of the mesh; Drying the ocher to white clay composition covering the mesh; It relates to a building finishing construction method of the building wall or ceiling using ocher and white clay, characterized in that the dried ocher to white clay composition to paint the loess to white clay purified from ocher to white clay.
또한, 건물의 바닥 위에 황토 내지 백토 6.8 ~ 7.2중량부, 톱밥 1.4~1.6중량부, 물 5.8 ~ 6.2중량부, 수용성접착제 1중량부로 만든 황토 내지 백토조성물을 2~5cm로 도포하고; 상기 황토 내지 백토조성물 위에 메쉬를 덮어 일정부분 황토 내 지 백토의 작은 입자가 메쉬표면을 덮게 하고; 상기 메쉬를 덮은 황토 내지 백토조성물을 건조시키고; 상기 건조된 향토 내지 백토조성물에 황토 내지 백토를 정제한 황토 내지 백토도료를 1 내지 2번 칠하는 것을 특징으로 하는 황토 및 백토를 이용한 바닥의 건축마감 시공방법에 관한 것이다.In addition, ocher to white clay composition made of 6.8 to 7.2 parts by weight of ocher to clay, 1.4 to 1.6 parts by weight of sawdust, 5.8 to 6.2 parts by weight of water and 1 part by weight of water-soluble adhesive is applied on the floor of the building at 2 to 5 cm; Covering the mesh on the loess to the clay composition so that small particles of the loess to the loess cover the mesh surface; Drying the ocher to white clay composition covering the mesh; It relates to a construction finishing method of the floor using loess and white clay, characterized in that the dried loess to the clay composition to paint the loess to white clay purified from loess to white clay.
또한, 상기의 건물의 벽, 천정 및 바닥의 건축마감 시공방법에 있어서, 상기 황토 내지 백토도료를 칠한 표면에 코팅 처리하는 것을 특징으로 하는 황토 및 백토를 이용한 건물벽, 천정 및 바닥의 건축마감 시공방법에 관한 것이다.In addition, in the building finishing construction method of the wall, the ceiling and the floor of the building, the building finishing construction of the building wall, ceiling and floor using ocher and white clay, characterized in that the coating treatment on the surface coated with ocher to white clay paint It is about a method.
또한, 건물의 벽 내지 천정의 건축시공방법에 사용되는 황토 내지 백토조성물에 방수제를 1 ~ 2 중량부을 첨가하는 것을 특징으로 하는 황토 및 백토를 이용한 건물 외벽의 건축마감 시공방법에 관한 것이다.In addition, the present invention relates to a construction finishing method for building exterior walls using loess and white clay, which comprises adding 1 to 2 parts by weight of a waterproofing agent to the loess to clay composition used in the building construction method of the wall or ceiling of a building.
또한, 상기 건물의 바닥의 시공방법에 있어서 전열기를 연결한 코일 위에 황토조성물을 도포하고, 메쉬를 덮은 후 보일러를 가동하여 황토 내지 백토조성물을 빠른 시간에 건조시키는 황토 및 백토를 이용한 건물바닥의 건축마감 시공방법에 관한 것이다.In addition, in the construction method of the floor of the building, the ocher composition is coated on the coil connecting the heaters, the mesh is covered, and the boiler is operated to quickly dry the ocher to clay composition by drying the boiler. It is about finish construction method.
이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예에 따른 황토 및 백토를 이용한 건축마감 시공방법 및 건축마감재에 대하여 상세히 설명한다.Hereinafter, with reference to the accompanying drawings will be described in detail with respect to the building construction method and building finishing material using the loess and clay in accordance with a preferred embodiment of the present invention.
도 3은 본 고안의 일실시예에 따른 황토 및 백토를 이용한 건축마감 시공방법을 나타낸 공정도이며, 도 4는 본 발명에 따른 황토 및 백토를 이용한 건축마감 시공방법에 의한 건축마감재의 일부분해사시도이며, 도 5는 본 고안의 일실시예에 따른 황토 및 백토를 이용한 건축마감 시공방법에 따른 황토 내지 백토조성물층의 일부확대도이다.Figure 3 is a process diagram showing the construction of the construction finish using loess and clay in accordance with an embodiment of the present invention, Figure 4 is a partial exploded view of the building finish material by the construction finishing construction method using loess and clay in accordance with the present invention , Figure 5 is a partially enlarged view of the loess to white clay composition layer according to the construction finishing method using the loess and clay in accordance with an embodiment of the present invention.
<실시예1>Example 1
건물의 벽 내지 천정에 황토 내지 백토조성물을 1~3cm을 도포한다.Apply 1 ~ 3cm of ocher to clay composition on the wall or ceiling of the building.
상기 황토 내지 백토조성물은 황토 내지 백토 7.8 ~ 8.2중량부, 톱밥 1.9 ~ 2.1중량부, 물 5.8 ~ 6.2중량부, 수용성접착제 1중량부로 만든다.The loess to white clay composition is made of 7.8 to 8.2 parts by weight of loess to white clay, 1.9 to 2.1 parts by weight of sawdust, 5.8 to 6.2 parts by weight of water and 1 part by weight of water-soluble adhesive.
상기 황토 및 백토조성물은 사용상태에 따라 아로마 요법으로서 향기가 나는 성분을 가미하여 인체에 유익한 향이 자연스럽게 새어 나가도록 할 수 있다.The ocher and white clay composition may be added to the fragrance as an aromatherapy according to the use state so that the fragrance beneficial to the human body naturally leaks.
상기 황토 및 백토는 잔존 생물 내지 다른 물질이 섞어있어 메쉬(메쉬의 눈은 사각형으로 가로세로 3~5mm의 크기)로 걸러주고 상기 톱밥도 같은 크기의 메쉬로 2 내지 3회 걸려주는 것이 바람직하겠다.The ocher and the clay is mixed with the remaining organisms or other substances, it is desirable to filter the mesh (mesh eyes are square, 3 to 5 mm in size) and the sawdust also to be hung 2-3 times in the same size mesh.
상기 톱밥은 황토 내지 백토와 섞여서 황토 내지 백토입자와 톱밥 입자의 간격이 좁아지므로 공극율이 낮아져 황토 내지 백토의 건조 시에 갈라짐을 방지한다.The sawdust is mixed with loess to white clay, so the gap between the loess to white clay particles and the sawdust particles is narrowed, the porosity is lowered to prevent cracking during drying of the loess to white clay.
또한 톱밥은 수분함유 보유율과 축열성이 뛰어나 건축물 마감시공시에 건물내부에 습도를 일정하게 유지시키며 보온력을 상승시키는 기포층 역할을 한다.In addition, the sawdust has excellent moisture content and heat storage ability, so it acts as a bubble layer to maintain the constant humidity inside the building and increase the thermal insulation during construction.
다음 단계로 상기 도포된 황토 내지 백토조성물에 메쉬를 얹혀 표면에 보이 지 않을 정도로 황토 내지 백토조성물 사이로 넣는 메쉬도포과정을 거친다.As a next step, the mesh is placed on the coated loess to white clay composition, and then the mesh coating process is placed between the loess to white clay composition so as not to be seen on the surface.
상기 메쉬도포과정은 건물건축시에 사용되는 미장 칼로 메쉬를 밀어 내리면 황토 내지 백토의 작은 입자들이 메쉬표면을 덮게 된다.In the mesh coating process, when the mesh is pushed down with a plastering knife used in building construction, small particles of yellow clay or white clay cover the mesh surface.
상기 메쉬는 합성수지재의 재질로서 메쉬의 눈은 사각형으로 가로세로 3~5mm가 바람직하며, 황토 내지 백토조성물이 흘러내리지 않게 하며 황토 내지 백토조성물의 건조 시에 황토 내지 백토조성물이 갈라지는 것을 방지하는 역할을 한다.The mesh is a material of a synthetic resin material, the eyes of the mesh is preferably a square 3 to 5mm in width, prevents the ocher to clay composition flows and prevents the ocher to clay cracking when drying the ocher to clay composition. do.
메쉬도포과정 처리후 황토 내지 백토를 정제한 황토 내지 백토에 수용성접착제를 섞은 황토 내지 백토도료를 황토 내지 백토조성물층에 1~2회 도포한다.After the mesh coating process, the ocher-white clay paint mixed with the water-soluble adhesive to the ocher-white clay purified ocher-white clay is applied to the ocher-white clay composition layer once or twice.
황토 내지 백토도료는 아주 미세한 황토 내지 백토입자로서 황토 내지 백토를 물에 풀었을 때 물과 함께 가라앉지 않는 순수 황토 내지 백토입자를 수용성접착제와 배합한 것이다.Loess to white clay paint is a very fine loess to white clay particles, which is a combination of pure loess to white clay particles with water-soluble adhesive that does not sink with water when the loess to white clay is dissolved in water.
상기 황토 내지 백토도료를 처리하는 것은 황토 내지 조성물이 건조 시에 부드러운 질감과 표면을 매끄럽게 하는 역할을 한다.Treatment of the ocher to white clay paint serves to smooth the texture and surface when the ocher to dry the composition.
상기 황토 내지 백토도료의 처리 과정이 끝난 다음 니스 등으로 코팅처리하며, 니스 대신 다른 코팅제를 사용하여 코팅처리 할 수 있다.After the treatment process of the loess to white clay paint is coated with a varnish, etc., it can be coated using another coating agent instead of varnish.
<실시예2>Example 2
건물 바닥의 경우 건축마감 시공방법은 황토 내지 백토조성물의 비율이 다르 며 황토 내지 백토조성물의 성분비는 황토 내지 백토6.8 ~ 7.2중량부, 톱밥 1.4~1.6중량부, 물 5.8 ~ 6.2중량부, 수용성접착제 1중량부로 만든 황토 내지 백토조성물을 1~3cm로 도포한다.In the case of building floors, the construction finishing method differs in the ratio of ocher to clay composition, and the component ratio of ocher to clay is 6.8 to 7.2 parts by weight of clay, 1.4 to 1.6 parts by weight of sawdust, 5.8 to 6.2 parts by weight of water, and water-soluble adhesive. 1 to 3 cm of loess to white clay composition is applied.
상기 황토 내지 백토조성물은 사용상태에 따라 아로마 요법으로서 향기가 나는 성분을 가미하여 인체에 유익한 향이 자연스럽게 새어 나가도록 할 수 있다.The ocher to white clay composition may be added to the fragrance as an aromatherapy according to the use state to naturally leak the fragrance beneficial to the human body.
상기 황토 내지 백토는 잔존 생물 내지 다른 물질이 섞어있어 메쉬(메쉬의 눈은 사각형으로 가로세로 3~5mm의 크기)로 걸러주고 상기 톱밥도 같은 크기의 메쉬로 1 내지 2회 걸려주는 것이 바람직하겠다.The ocher to white clay is a mixture of the remaining organisms and other substances, it is preferable to filter the mesh (mesh eyes are square 3 to 5 mm in size) and the sawdust also to be hung once or twice in the same size mesh.
다음 단계로 상기 도포된 황토 내지 백토조성물에 메쉬를 얹혀 표면에 보이지 않을 정도로 황토 내지 백토조성물 사이로 넣는 메쉬도포과정을 거친다.As a next step, the mesh is placed on the coated loess to white clay composition, and then the mesh coating process is placed between the loess to white clay composition so as not to be seen on the surface.
상기 메쉬는 합성수지재의 재질로서 메쉬의 눈은 사각형으로 가로세로 3~5mm가 바람직하며, 황토 내지 백토조성물이 흘러내리지 않게 하며 황토 내지 백토조성물의 건조 시에 황토 내지 백토조성물이 갈라지는 것을 방지하는 역할을 한다.The mesh is a material of a synthetic resin material, the eyes of the mesh is preferably a square 3 to 5mm in width, prevents the ocher to clay composition flows and prevents the ocher to clay cracking when drying the ocher to clay composition. do.
메쉬도포과정 처리후 황토 내지 백토를 정제한 황토 내지 백토에 수용성접착제를 섞은 황토 내지 백토도료를 황토 내지 백토조성물층에 1~2회 도포한다.After the mesh coating process, the ocher-white clay paint mixed with the water-soluble adhesive to the ocher-white clay purified ocher-white clay is applied to the ocher-white clay composition layer once or twice.
상기 황토 내지 백토도료의 처리 과정이 끝난 다음 니스 등으로 코팅처리하 며, 니스 대신 다른 코팅제를 사용하여 코팅처리 할 수 있다.After the treatment process of the loess to white clay paint is finished with a varnish, etc., it can be coated using another coating agent instead of varnish.
황토 내지 백토조성물에 사용되는 황토, 백토, 톱밥, 물, 수용성접착제의 혼합비율만 다르고 건물의 벽이나 천정의 건축마감시공 방법과 동일하며 수용성 락카, 니스 등을 바닥 표면에 코팅하면 장판 마루판처럼 사용이 가능하며 견고성이나 탄력성이 일반 장판 기능보다 월등하며 유지보수가 가능하다.Only the mixing ratio of ocher, white clay, sawdust, water, and water-soluble adhesive used in ocher to clay composition is the same as the construction finishing method of wall or ceiling of the building, and when water-soluble lacquer and varnish are coated on the floor surface, it is used as floorboard floorboard. Durability and resilience are superior to that of general floorboards and can be maintained.
황토 내지 백토조성물은 화학적 반응을 일으켜 건조되지 않아 외부의 열을 전달시켜 건조시키는 것이 바람직함으로 건물에 전열기를 연결한 코일을 5 ~ 10cm 간격으로 배선 설치후 황토 내지 백토조성물을 도포하고 상기 황토 내지 백토조성물층에 메쉬를 도포 처리 후 전열기를 가동하여 빠른 시간 내에 건조시킬 수 있다.The ocher to clay composition does not dry due to chemical reactions, and is preferably dried by transferring external heat, so that the coils connecting the heaters to the building are installed at intervals of 5 to 10 cm, and then the ocher to clay composition is applied. After applying the mesh to the composition layer, the heater can be dried and dried quickly.
상기 전열기는 가정용으로 110V 내지 220V로 사용 가능한 것이 바람직하겠다.It is preferable that the heater can be used at home 110V to 220V.
건물의 벽이나 천정의 경우 황토조성물에 함유된 수분은 중력에 의해 수분이 하부로 내려가 쉽게 잘 마르는 편이나 바닥의 경우 보일러를 가동하지 않거나 보일러의 열선이 전 바닥에 고루 퍼지게 설치되지 않은 경우에는 상기의 전열기를 연결한 코일을 깔아 황토 내지 백토조성물을 빠른 시간 내에 건조시키는 것이 바람직하겠다.In the case of walls or ceilings of buildings, the moisture contained in the ocher composition is easily lowered by gravity due to gravity and dries easily.In the case of floors, the boiler is not operated or the heating wire of the boiler is not spread evenly over the entire floor. It is desirable to dry the ocher to white clay composition in a short time by laying a coil connected to the heater.
<실시예3>Example 3
건물의 외벽인 경우 건물의 벽 내지 천정의 시공방법과 마찬가지이며, 방수 제를 1 ~ 2 중량부를 첨가하여 황토 내지 백토조성물을 만들어서 시공한다.In the case of the outer wall of the building is the same as the construction method of the wall or ceiling of the building, by adding 1 to 2 parts by weight of the waterproofing agent to be made by constructing a loess to white clay composition.
상기 황토 내지 백토는 잔존 생물 내지 다른 물질이 섞어있어 메쉬(메쉬의 눈은 사각형으로 가로세로 3~5mm의 크기)로 걸러주고 상기 톱밥도 같은 크기의 메쉬로 1 내지 2회 걸려주는 것이 바람직하겠다.The ocher to white clay is a mixture of the remaining organisms and other substances, it is preferable to filter the mesh (mesh eyes are square 3 to 5 mm in size) and the sawdust also to be hung once or twice in the same size mesh.
다음 단계로 상기 도포된 황토조성물에 메쉬를 얹혀 표면에 보이지 않을 정도로 황토조성물 사이로 넣는 메쉬도포과정을 거친다.Next, the mesh is placed on the coated ocher composition and subjected to a mesh coating process that is placed between the ocher composition so that it is not visible on the surface.
상기 메쉬도포과정은 건물건축시에 사용되는 미장 칼로 메쉬를 밀어 내리면 황토의 작은 입자들이 메쉬표면을 덮게 된다.In the mesh coating process, when the mesh is pushed down with a plastering knife used in building construction, small particles of ocher cover the mesh surface.
상기 메쉬는 합성수지재의 재질로서 메쉬의 눈은 사각형으로 가로세로 3~5mm가 바람직하며, 황토조성물이 흘러내리지 않게 하며 황토조성물의 건조 시에 황토조성물이 갈라지는 것을 방지하는 역할을 한다.The mesh is a material of the synthetic resin material, the eyes of the mesh is preferably a square 3 to 5mm in width, prevents the ocher composition from flowing and prevents the ocher composition from cracking when the ocher composition is dried.
메쉬도포과정 처리후 황토 내지 백토를 정제한 황토 내지 백토에 수용성접착제를 섞은 황토 내지 백토도료를 황토 내지 백토조성물층에 1~2회 도포한다.After the mesh coating process, the ocher-white clay paint mixed with the water-soluble adhesive to the ocher-white clay purified ocher-white clay is applied to the ocher-white clay composition layer once or twice.
황토 내지 백토도료는 아주 미세한 황토 내지 백토입자로서 황토 내지 백토를 물에 풀었을 때 물과 함께 가라앉지 않는 순수 황토 내지 백토입자를 수용성접착제와 배합한 것이다.Loess to white clay paint is a very fine loess to white clay particles, which is a combination of pure loess to white clay particles with water-soluble adhesive that does not sink with water when the loess to white clay is dissolved in water.
외부로 노출되어 있어서 건조시 햇빛이나 바람을 통해 건조되며, 건물의 바닥과 달리 열선을 처리하지 않아도 된다.As it is exposed to the outside, it is dried by sunlight or wind when drying, and unlike the floor of the building, it does not need to be treated with heat rays.
도 4에서 보는 바와 같이 상기의 건축마감 시공방법으로 제조된 건축마감재(100)는 황토 내지 백토, 톱밥(12), 물, 접착제로 구성된 황토 내지 백토조성물(10)로 구성된 층 사이에 메쉬(14)가 들어있으며, 상기 황토 내지 백토조성물층 상부에 황토 내지 백토를 정제하고 이에 수용성접착제를 섞어서 도포한 황토 내지 백토도료층이 형성되며, 상기 황토 내지 백토도료층(20)에 코팅처리된 코팅층(30)이 형성되어 진다.As shown in FIG. 4, the building finishing material 100 manufactured by the above-described building finishing construction method has a mesh 14 between layers composed of loess to white clay composition 10 composed of loess to white clay, sawdust 12, water, and adhesive. ), The loess to white clay on the top of the loess to the clay composition layer and the ocher to white clay coating layer is formed by mixing and applying a water-soluble adhesive is formed, the coating layer coated on the loess to white clay coating layer (20) 30) is formed.
본 발명에 사용되는 황토, 백토, 톱밥은 우리의 주변에서 쉽게 구입가능하며, 황토의 효능은 파장이 6~15㎛인 원적외선을 발생시키고 해충이나 곤충 등에 대하여도 방충성을 가지며, 축열성이 뛰어나고, 방취효과 등이 양호하며, 인체의 건강에도 여러가지 긍정적인 효과를 가지고 있는 것으로 밝혀지고 있으며, 톱밥은 수분보유율이 높아 건축재료로 사용될 경우 습도를 조절하여 준다.Loess, white clay, sawdust used in the present invention can be easily purchased around us, the efficacy of the loess generates far infrared rays with a wavelength of 6 ~ 15㎛ and has insect repellent against pests and insects, and excellent heat storage It has been found to have good deodorizing effects, and has various positive effects on human health. Sawdust has a high moisture retention rate and controls humidity when used as a building material.
또한, 도 5에서 도시한 바와 같이 화학적 반응을 일으키는 접착제 첨가물을 사용하지 않고 수용성 접착제를 사용하기 때문에 그 양이 현저히 작고 인체에 무해하며 수분이 증발된 곳에 공기층이 형성되어 향토가 가지고 있는 모든 인체에 유익한 기능들이 활성화되고, 마감표면이 매끄럽고 질감이 부드러우며, 미관이 뛰어나다.In addition, since the water-soluble adhesive is used instead of the adhesive additive causing the chemical reaction as shown in FIG. The beneficial functions are activated, the finish surface is smooth, the texture is smooth, and the aesthetics are excellent.
이상에서 설명한 바와 같이, 본 발명에 따른 황토 및 백토를 이용한 건축마감 시공방법 및 건축마감재를 사용하는 경우에는 건물마감 시공 시에 장판을 깔거나 벽지를 바르거나 페인트를 칠하지 않아도 되며, 건물의 시공 시에 황토 내지 백토 자체의 기능과 색감, 질감 등을 증대시켜 주거 인테리어의 새로운 문화를 제시한다.As described above, in the case of using the building finishing construction method and building finishing material using loess and white clay according to the present invention, it is not necessary to lay a floor covering, wallpaper or paint during the construction of the building, The new culture of the residential interior is presented by increasing the function, color, and texture of the loess or white clay itself.
또한, 본 발명에 따른 황토 및 백토를 이용한 건축마감 시공방법에 의해 시공된 경우에는 화재예방과 유독성가스가 발생되지 않으며, 일정한 온도를 유지시키는 주는 방온기능이 뛰어나고, 일정한 습도를 유지시키는 방습능력이 우수하며, 해충이나 박테리아 등이 서식하지 못하게 하는 방물성이 현저하며, 소음을 차단하는 방음성이 뛰어나다.
In addition, when constructed by the construction finishing construction method using loess and white clay according to the present invention, fire prevention and toxic gas is not generated, and it is excellent in the temperature protection function to maintain a constant temperature, and moisture-proof ability to maintain a constant humidity It is excellent, has excellent waterproofing property that prevents pests and bacteria from inhabiting, and has excellent soundproofing to block noise.
본 발명을 상기한 실시예를 들어 구체적으로 설명하였지만, 본 발명은 이에 제한되는 것이 아니고, 해당 기술 분야의 숙련된 당업자의 통상의 지식의 범위 내에서 치환, 변경, 개량이 가능하다.Although the present invention has been described in detail with reference to the embodiments described above, the present invention is not limited thereto, and the present invention may be substituted, changed, and improved within the ordinary knowledge of a person skilled in the art.

Claims (5)

  1. 건물의 벽 내지 천정에 황토 내지 백토 7.8 ~ 8.2중량부, 톱밥 1.9 ~ 2.1중량부, 물 5.8 ~ 6.2중량부, 수용성접착제 1중량부로 만든 황토 내지 백토조성물을 2~5cm로 도포하고;To the wall or ceiling of the building is applied to the loess to white clay composition made of 7.8 to 8.2 parts by weight, 1.9 to 2.1 parts by weight of sawdust, 5.8 to 6.2 parts by weight of water, 1 part by weight of water-soluble adhesive 2 to 5 cm;
    상기 황토 내지 백토조성물 위에 메쉬를 덮어 일정부분 황토 내지 백토의 작은 입자가 메쉬 표면을 덮게 하고;Covering the mesh on the loess to white clay composition such that small particles of loess to white clay cover the mesh surface;
    상기 메쉬를 덮은 상기 황토 내지 백토조성물을 건조시키고;Drying the ocher to white clay composition covering the mesh;
    상기 건조된 황토 내지 백토조성물에 황토 내지 백토를 정제한 황토 내지 백토도료를 1 내지 2번 칠하는 것을 특징으로 하는 황토 및 백토를 이용한 건물벽 내지 천정의 건축마감시공방법.A building finishing method for building walls and ceilings using ocher and clay, wherein the dried ocher to clay composition is coated 1 to 2 times of ocher to clay.
  2. 건물의 바닥 위에 황토 내지 백토 6.8 ~ 7.2중량부, 톱밥 1.4~1.6중량부, 물 5.8 ~ 6.2중량부, 수용성접착제 1중량부로 만든 황토 내지 백토조성물을 2~5cm로 도포하고;On the floor of the building is applied ocher to white clay composition made of 6.8 to 7.2 parts by weight of clay, 1.4 to 1.6 parts by weight of sawdust, 5.8 to 6.2 parts by weight of water and 1 part by weight of water-soluble adhesive, 2 to 5 cm;
    상기 황토 내지 백토조성물 위에 메쉬를 덮어 일정부분 황토의 작은 입자가 메쉬표면을 덮게 하고;Covering the mesh on the loess to the clay composition so that a small portion of the loess covers the mesh surface;
    상기 메쉬를 덮은 황토 내지 백토조성물을 건조시키고;Drying the ocher to white clay composition covering the mesh;
    상기 건조된 향토 내지 백토조성물에 황토 내지 백토를 정제한 황토 내지 백 토도료를 1 내지 2번 칠하는 것을 특징으로 하는 황토 및 백토를 이용한 바닥의 건축마감 시공방법.A construction method for finishing the construction of a floor using loess and white clay, wherein the dried loess to white clay composition is coated with ocher to white clay purified from loess to white clay.
    상기 황토 내지 백토도료를 칠한 표면에 코팅 처리하는 것을 특징으로 하는 황토 및 백토를 이용한 건물바닥의 건축마감 시공방법.Building finishing construction method of the building floor using the loess and white clay, characterized in that the coating treatment on the surface coated with ocher to white clay paint.
  3. 제 1항 또는 제 2항에 있어서,The method according to claim 1 or 2,
    상기 황토 내지 백토도료를 칠한 표면에 코팅 처리하는 것을 특징으로 하는 황토 및 백토를 이용한 건물벽, 천정 및 바닥의 건축마감 시공방법.Building finishing construction method of building walls, ceilings and floors using loess and white clay, characterized in that the coating treatment on the surface covered with ocher to white clay paint.
  4. 제 1항에 있어서,The method of claim 1,
    황토 내지 백토조성물에 방수제를 1 ~ 2 중량부를 첨가하는 것을 특징으로 하는 황토 및 백토를 이용한 건물 외벽의 건축마감 시공방법.Construction finish construction method of the outer wall of the building using ocher and clay, characterized in that to add 1 to 2 parts by weight of a waterproofing agent to the loess to clay composition.
  5. 제 2항에 있어서,The method of claim 2,
    전열기를 연결한 코일 위에 상기 황토 내지 백토조성물을 도포하고, 메쉬를 덮은 후 전열기를 가동하여 황토 내지 백토조성물을 빠른 시간에 건조시키는 황토 및 백토를 이용한 건물바닥의 건축마감 시공방법.A method of constructing and finishing a building floor using loess and white clay by coating the loess to white clay composition on a coil connected to a heater and operating the heater after covering the mesh.
KR1020040072918A 2004-09-13 2004-09-13 An end construction of procedure using of yellow soil and white soil KR20060024476A (en)