KR20040027632A - Waterproofing using epoxy or acrylic epoxy cement mortar - Google Patents
Waterproofing using epoxy or acrylic epoxy cement mortar Download PDFInfo
- Publication number
- KR20040027632A KR20040027632A KR1020040010828A KR20040010828A KR20040027632A KR 20040027632 A KR20040027632 A KR 20040027632A KR 1020040010828 A KR1020040010828 A KR 1020040010828A KR 20040010828 A KR20040010828 A KR 20040010828A KR 20040027632 A KR20040027632 A KR 20040027632A
- Authority
- KR
- South Korea
- Prior art keywords
- epoxy
- mortar
- waterproof
- cement mortar
- waterproofing
- Prior art date
Abstract
Description
본 발명은 정수장 계통, 하수처리장 계열의 각종 콘크리트 구조물에 강력한 인장력을 지닌 균열방지장치의 부재를 사용하여 콘크리트 보호용 피복처리 방수, 방식 작업을 행하기 위한 에폭시 또는 아크릴 에폭시 시멘트 몰탈(RC- TECH 및 RC- HITECH)을 이용한 방수, 방식 공법에 관한 것으로서, 본 출원인이 선 출원 등록한 특허 제0271283호의 중방식 내력 수지몰탈 방수·방식 공법에 있어서 재료 및 공법을 개선 보완하고 방수층의 두께 적용범위로 확대코자 한 것이다.The present invention is the epoxy or acrylic epoxy cement mortar for waterproofing the protective coating for concrete protection, anticorrosive work by using a member of a crack prevention device having a strong tensile force in various concrete structures of water purification plant system, sewage treatment plant series (RC- TECH and RC -HITECH), which relates to waterproofing and anticorrosive method, and to improve and supplement materials and methods in the medium-load proof resin mortar waterproofing and anticorrosive method of Patent No. 081283, which the applicant has previously applied for will be.
통상 방수, 방식 공정을 시행함에 있어 하자의 가장 큰 원인은 콘크리트 바탕처리의 불량(레이탄스 제거, 핀홀 확대불량)과 사용자재의 콘크리트와의 친화성 결여이며, 보다 결정적인 요인은 방수, 방식 처리된 시공물의 완성품이 콘크리트의 강력한 수축 팽창에 따른 균열과 방수완성물의 자체 구열로 외부 침투수가 콘크리트 내부에 깊숙이 침투하여 콘크리트 중성화로 인한 열화를 촉진시키는 것이다.In performing waterproof and anticorrosive processes, the main causes of defects are poor concrete ground treatment (removal of tartans, poor pinhole expansion) and lack of affinity with concrete of user materials. As the finished product is cracked by strong shrinkage expansion of concrete and self-organization of waterproof finished product, external infiltration water penetrates deeply into concrete and promotes deterioration due to concrete neutralization.
종래에 시공되어온 시멘트 계열의 액체방수, 액체 침투성 방수, 모체 침투성방수와 유기용제계의 도막방수 등은 시공시에 완벽한 하지처리(바탕처리)가 결여되어 하자발생의 원천적 결함을 제거하는 데 미흡하며, 시멘트 계열의 몰탈 방수류에는 방수 완성물의 자체 구열과 콘크리트의 수축팽창에 따른 균열방지장치가 원천적으로 결여되어 있다.Cement-based liquid waterproofing, liquid-permeable waterproofing, mother-permeable waterproofing, and organic solvent-based coating waterproofing are lacking in perfect base treatment (base treatment) during construction, and are insufficient to remove the source defects of defects. In the cement-based mortar waterproofing system, there is a natural lack of a crack prevention device due to the self-organization of the waterproofing finished material and shrinkage expansion of concrete.
시멘트와 혼합시에는 발열온도의 증가라는 단순화학적 반응에 의한 염화칼슘, 규산소다계의 액체방수는 두꺼운 보호몰탈층이 있음에도 불구하고 적용자재의 화학적 반응(산화현상)에 의하여 콘크리트 구체의 침식과 내부 철근의 산화부식을 초래하며 두꺼운 보호몰탈층도 강력한 균열방지의 결여로 인한 균열로 침투수의 반응으로 콘크리트의 열화(성능저하)와 탈락을 촉진시킨다.When mixed with cement, the liquid waterproofing of calcium chloride and sodium silicate due to the simplistic reaction of increasing the exothermic temperature, despite the thick protective mortar layer, erosion of the concrete sphere and internal reinforcement due to chemical reaction (oxidation) of the applied materials. The thick protective mortar layer also promotes deterioration (deterioration of performance) and dropping of concrete due to the reaction of infiltration water due to the lack of strong crack protection.
이의 개선방법으로 개발된 액체 침투성 방수 역시 주성분으로 혼합하는 아크릴수지의 불투수성, 내습성, 내수성 등 방수제로서의 우수한 기능을 지님에도 불구하고 균열방지장치의 결여로 외적 요인에 의한 균열, 자체 양생과정에서 발생하는 구열 등에 의한 대비는 불가능하다.Liquid permeable waterproofing developed as a method of improvement also occurs in cracking due to external factors and self-curing process due to lack of crack preventing device, despite its excellent function as waterproofing agent such as impermeability, moisture resistance, water resistance, etc. It is impossible to prepare by the heat and so on.
이러한 몰탈방수가 갖는 한계성 등으로 개발된 모체침투성 역시 얇은 피막으로 외수압에 의해 지속적으로 침투하는 수화현상으로 콘크리트 심층부까지 침투하는 장점으로 지하 구조물의 내부 시공(외수압에 대해 강한 반발력)재료로서 탁월한 우수성을 지니고 있으나 균열방지재와 겸용 시공의 불능으로 콘크리트 구체의 균열과 외적 요인에 의한 방수도막층의 충격에 의한 구열 등을 방지하는데는 한계성이 있다.Maternal penetrability, developed due to the limitations of mortar waterproofing, is also a hydration phenomenon that continuously penetrates by external water pressure as a thin film, and it penetrates into the deep concrete part. Although it has superiority, there is a limit in preventing cracking of concrete spheres and cracking due to impact of waterproof coating layer due to external factors due to the inability to combine and prevent cracking materials.
이러한 요인 등에 의하여 강인한 인장력에 의한 균열방지장치의 부재 적용이 없이는 방수몰탈 완성품의 균열방지는 불가능하다.Due to these factors, it is impossible to prevent cracking of the waterproof mortar finished product without the application of the crack preventing device due to the strong tensile force.
정수장, 하수처리장 등 기타 콘크리트 구조물은 공기 중에 존재하는 탄산가스(CO2), 질산화물(NOx), 산소유황으로부터 생기는 산성비가 알카리성 콘크리트에 침투하여 이로 인한 중성화로 콘크리트가 열화되고 균열이 진행되며 물 속의 염소성분으로 콘크리트의 알카리와 반응하여 알카리 실리카겔이 형성된다.In other concrete structures such as water purification plants and sewage treatment plants, acid rain from carbon dioxide (CO 2 ), nitrous oxide (NO x ), and oxygen sulfur in the air penetrates the alkaline concrete, resulting in deterioration of concrete and cracking. Alkali silica gel is formed by reacting with alkali of concrete as chlorine in the genus.
이 알카리 실리카겔이 물을 흡수함에 따라 콘크리트가 팽창 열화되어 작은 파편이 생기고 균열로 인하여 물이 침투하여 내부 철근에서 생긴 녹의 팽창 압력으로 콘크리트가 탈락, 박리되고 콘크리트와 분리된 철근은 급속도로 산화부식이 촉진되어 콘크리트 구조물이 파괴되는 것이다.As the alkali silica gel absorbs water, the concrete expands and deteriorates to form small fragments, and water penetrates due to cracks, causing the concrete to fall off and exfoliate due to rust expansion pressure generated from the internal reinforcing bars. It is accelerated and the concrete structure is destroyed.
이와 함께 하수처리장 계열의 콘크리트 구조물은 황산염이나 황을 포함한 유기물이 다량 혼합된 부식성이 강한 하수나 하수슬러지 등 악질 폐수를 저장하므로 산화부식속도가 빨리 진행된다.In addition, the concrete structure of the sewage treatment plant series stores the corrosive sewage or sewage sludge, which contains a large amount of organic matter including sulfates and sulfur, and thus accelerates oxidation corrosion.
수분은 콘크리트 화합물의 열화를 촉진시킨다. 콘크리트의 열화, 균열, 탈락은 외부에서 침투하는 물과 직접적인 관계가 있으므로 이 침투하는 물을 원천적으로 차단시켜야 하고, 낮은 흡수율로 물의 침투를 항상 배제할 수 있는 내수성을 지녀야 하며, 콘크리트와 유사한 열팽창 계수로 온도 차이에 대한 방수층의 파손 및 박리가 발생치 않아야 되고, 콘크리트 내부에 잔존하는 습기는 오랜 양생기간에 완전 방출되어야 한다.Moisture promotes deterioration of concrete compounds. Since deterioration, cracking, and dropping of concrete are directly related to water penetrating from the outside, it is necessary to block the infiltrating water at the source, and to have water resistance to always exclude water ingress with low absorption rate, and similar coefficient of thermal expansion to concrete. The breakdown and peeling of the waterproof layer against the furnace temperature difference should not occur, and the moisture remaining in the concrete should be completely released during the long curing period.
콘크리트 구조물에는 콘크리트와 친화성이 있는 동질의 재료를 적용하여 포화온도가 충분히 낮아서 저온의 수중에서도 응력이나, 진동 및 충격에도 손상되지 않는 강력한 접착력을 유지하며 상기한 바와 같은 중성화로 인한 열화 균열 누수 부식 등의 하자 발생을 원천적으로 봉쇄하여 콘크리트 구조물을 영구히 유지관리할 수 있는 장기적인 대책을 강구하여야 한다.By applying homogeneous materials that are compatible with concrete, concrete materials have a low saturation temperature to maintain a strong adhesive force that is not damaged by stress, vibration, or impact even in low temperature water, and deterioration crack leakage corrosion due to neutralization as described above. Long-term measures should be taken to permanently maintain the concrete structure by blocking the occurrence of defects.
이에 본 발명자는 부실 부분의 보수보강과 강력한 불순물 제거의 바탕처리가 완료된 콘크리트 구체 표층에 수지몰탈(Resin CRETE PRIMER, Resin CRETE PASTE+R.F.G CLOTH, ResinCRETE)로 마감하여 형성된 강력한 균열방지 방수, 방식층이 투과성 물질을 거의 완벽에 가깝게 차단하여 콘크리트 구조물의 안정성을 영구히 도모함으로서 생산성 증대와 균열, 누수, 부식 등 하자로 인한 경제적 손실을 미연에 방지하며 아울러 부속공정으로 다양한 방식공법을 겸용 대처하게 되어 정수장, 하수처리장 등의 각종 구조물에 대한 방수, 방식공사의 효율성을 개선할 수 있도록 한 중방식 내력수지몰탈 방수, 방식 공법을 선출원 등록(특허 제0271283호)한 바 있으나, 상기에서 제시한 중방식 내력수지몰탈 방수, 방식 공법은 사용 재료 및 방수층의 두께 적용범위서 개선될 부분이 발생하였는바, 본 발명에서는 이러한 부분을 중점적으로 보완코자 한 것이다.Therefore, the present inventors have a strong crack prevention waterproof, anticorrosive layer formed by finishing with concrete mortar (Resin CRETE PRIMER, Resin CRETE PASTE + R.FG CLOTH, ResinCRETE) on the surface of concrete concrete where rehabilitation of poor parts and strong impurities are removed. By blocking permeable materials to near perfect perfection, the stability of concrete structures is permanently prevented, thereby preventing economic losses due to increased productivity, cracks, leaks, corrosion, etc., and coping with various anticorrosion methods as an accessory process. Registered a patent application (Patent No. 081283) for the heavy water proofing resin mortar waterproofing and anticorrosive method to improve the efficiency of waterproofing and anticorrosive construction for various structures such as sewage treatment plant. Mortar waterproofing, anticorrosive method, can be used to improve the thickness of the material and waterproof layer. Bar, in the present invention will hayeotneun one wishes to make up for these parts as focus.
따라서 본 발명에서는 합성고분자 수지와 극성 모노머, 에폭시수지 등의 공중합(Copolymers)에 의하여 만들어진 아크릴 에폭시 수지에다 무기질파우더를 배합한 아크릴 에폭시 시멘트 몰탈 방수제(RCH-200)와, 에폭시수지 에다 무기질파우더를 배합한 에폭시 시멘트 몰탈 방수제(RCT-200)사용하여 정수장 계통, 하수처리장 계열의 콘크리트 구조물을 청정수 보존과 부식으로부터 보호하는 방수, 방식공법을 새롭게 제공하고자 하는 것으로서,Therefore, in the present invention, an acrylic epoxy resin made by copolymerization of a synthetic polymer resin, a polar monomer, an epoxy resin, etc., an acrylic epoxy cement mortar waterproofing agent (RCH-200) incorporating an inorganic powder, and an inorganic powder are added to the epoxy resin. To use a new epoxy cement mortar waterproofing agent (RCT-200) to provide a new waterproof and anticorrosive method that protects water purification system and sewage treatment plant concrete structure from clean water and corrosion protection.
1차적으로 구체의 표면관찰을 철저히 하여First, observe the surface of the sphere thoroughly
①콘크리트의 벌집상태 균열, 누수 및 용수부분 등의 부실부분을 보강하고① Reinforce the poor part of concrete such as honeycomb crack, water leakage and water part.
②콘크리트 표층의 레이탄스, 핀홀피막 등을 강력 분사장치에 의한 습식 샌딩기(Sanding기) 등으로 제거(레이탄스), 확대(핀홀공극)하고 강력한 접착력과 자체탄성을 지닌 결함부 충진재인 RC-60[RC-60A(모세관, 세공, 핀홀, 미세 균열부 등에 강력 침투 접착되는 비결정질 시리카를 혼입한 액체 수지화합물로서 강력한 방수성과 자체 탄성이 우수하며 강력한 접착력을 지닌 활성 화합물수지)와, 수밀성과 내화학성이 우수한 무기질파우더인 RC-60M(포틀랜트 시멘트 + 1∼7㎛의 미립자 플라이애쉬 + 활성화합물 + 규사(시리카) 등)을 배합한 혼합물]을 사용하여 바탕처리가 완료된 평활한 구체의 표층에,(2) RC-, which is a defect filling material with strong adhesion and self-elasticity, is removed (ratans) and enlarged (pinhole voids) by using a wet sanding machine (sanding machine) by a strong injection device. 60 [RC-60A (Liquid resin compound that contains amorphous silica which is strongly penetrated and adhered to capillary tube, pores, pinholes, micro cracks, etc.), and has excellent water resistance, high elasticity and strong adhesion. RC-60M (a mixture of Portland Cement + Particulate Fly Ash + Active Compound + Silica (Silica), etc.), which is an excellent chemical powder, is used on the surface of a smooth sphere finished with ground treatment. ,
③침투성 프라이머인 아크릴 에폭시 폴리머 프라이머 RCH-100 및 에폭시 프라이머 RCT-100으로서 프라이머 바르기를 하여 모세관 차단과 세공과 공극에 침투 접착하여 1차 적인 침투접착의 바탕을 형성시킨 후(3) After applying primer with acrylic epoxy polymer primer RCH-100 and epoxy primer RCT-100 which are permeable primers, penetrate and adhere to capillary blocking and pores and pores to form the basis of primary penetration adhesion.
④아크릴 에폭시 시멘트 몰탈(RCH-200) 또는 에폭시 시멘트 몰탈 (RCT-200)를 레이탄스가 제거된 요철부와 확대된 핀홀공극에 완벽하게 충진되어 방수막이 형성될 수 있도록 정밀하게 도포(붓, 나무 흙손 겸용)하여 방수1차 층을 형성시킨 후,④ Accurately apply acrylic epoxy cement mortar (RCH-200) or epoxy cement mortar (RCT-200) to fill the uneven parts and the enlarged pinhole voids with the elimination of tartans to form a waterproof film (brush, wood) Combined with a trowel) to form a waterproof primary layer,
⑤이 방수1차 층위에 R.F.G Cloth를 적층하여 초기 방수층의 안전성을 구축하며,⑤ Lay R.F.G Cloth on this waterproof primary layer to build safety of initial waterproof layer.
⑥이 R.F.G Cloth층 위에 아크릴 에폭시 시멘트 몰탈(RCH-200) 또는 에폭시 시멘트 몰탈(RCT-200)을 균일하게 압착 미장하여 완벽한 방수층을 형성하여 구체와의 강력한 접착력을 갖는 방수층과 R.F.G CLOTH의 강인한 인장력에 의한 균열방지 장치와 자체탄성을 갖는 내약품성 수지몰탈이 구체와의 일체감을 형성하여 CON'C 표층에 투과성 물질을 완벽히 차단하여 콘크리트 구조물의 안전성을 반영구적으로 하는 에폭시 또는 아크릴 에폭시 시멘트 몰탈(RC- TECH 및 RC- HITECH)을 이용한 방수, 방식 공법을 제공하고자 한다.⑥ Evenly compress and plaster acrylic epoxy cement mortar (RCH-200) or epoxy cement mortar (RCT-200) on this RFG cloth layer to form a perfect waterproof layer, and the strong tensile strength of the waterproof layer and RFG CLOTH with the sphere. Epoxy or acrylic epoxy cement mortar that semi-permanent safety of concrete structure by completely preventing permeable material on the surface of CON'C by forming cracking device and self-elastic chemical-resistant resin mortar. And to provide a waterproof, anticorrosive method using RC-HITECH).
도 1은 본 발명의 바람직한 제 1 실시예를 보인 구성도1 is a configuration diagram showing a first preferred embodiment of the present invention
도 2는 본 발명의 바람직한 제 2 실시예를 보인 구성도2 is a configuration diagram showing a second preferred embodiment of the present invention
도 3은 본 발명의 바람직한 제 3 실시예를 보인 구성도3 is a configuration diagram showing a third preferred embodiment of the present invention
도 4는 본 발명의 바람직한 제 4 실시예를 보인 구성도4 is a configuration diagram showing a fourth preferred embodiment of the present invention
도 5는 본 발명의 바람직한 제 5 실시예를 보인 구성도5 is a configuration diagram showing a fifth preferred embodiment of the present invention
도 6은 본 발명의 바람직한 제 6 실시예를 보인 구성도6 is a configuration diagram showing a sixth preferred embodiment of the present invention
도 7a~7i는 본 발명 중 바탕처리(하자처리) 공정도7a to 7i is a background treatment (defect treatment) process diagram of the present invention
■도면의 주요부분에 사용된 부호의 설명■Explanation of symbols used in main part of drawing
1:바탕처리1: based treatment
2, 4:방수몰탈층2, 4: waterproof mortar layer
3:보강직포3: reinforced fabric
6, 6', 6":무용제형 및 용제형 또는 수계형 에폭시6, 6 ', 6 ": solventless and solvent or water based epoxy
7, 7', 7":에폭시 수지7, 7 ', 7 ": epoxy resin
8, 8':글래스 클로스8, 8 ': glass cloth
9, 9', 9":내오존성 수지9, 9 ', 9 ": ozone resistant resin
이하, 본 발명에 대하여 구체적으로 살펴보면 다음과 같다.Hereinafter, the present invention will be described in detail.
본 발명은 강력한 균열방지장치와 수밀성 혼화제와 방수성과 내약품성을 지닌 수지를 적용하여 균열로 인한 누수, 부식으로부터 하자의 발생을 원천적으로 방지하고자 하는 것으로, 합성고분자 수지와 극성 모노머, 에폭시수지 등의 공중합(Copolymers)에 의하여 만들어진 아크릴 에폭시 수지에다 무기질파우더를 배합한 아크릴 에폭시 시멘트 몰탈 방수제(RCH-200)와, 에폭시수지 에다 무기질파우더를 배합한 에폭시 시멘트 몰탈 방수제(RCT-200)와, 강력한 인장력을 지닌 균열방지용 보강직포(R.F.G cloth)를 사용하여 정수장 계통, 하수처리장 계열의 콘크리트 구조물을 청정수 보존과 부식으로부터 보호하는 방수, 방식공법에 특징이 있는 것이다.The present invention is to prevent the occurrence of defects from leakage and corrosion due to cracks by applying a strong crack prevention device, water-tight admixtures and waterproof and chemical resistance, synthetic polymer resins, polar monomers, epoxy resins, etc. Acrylic Epoxy Cement Mortar Repellent (RCH-200) that contains inorganic powders and Acrylic Powder made of Copolymers, Epoxy Cement Mortar Repellent (RCT-200) that contains inorganic powder and epoxy resin, and strong tensile force It is characterized by waterproofing and anticorrosive method that uses RFG cloth for crack prevention to protect clean water system and concrete structure of sewage treatment plant.
이하 본 발명을 첨부된 도면과 함께 상세히 살펴보면 다음과 같다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.
실시예 1Example 1
도 1과 같이 1차적으로 구체의 표면관찰을 철저히 하여 콘크리트 표층의 레이탄스, 핀홀의 피막 등을 강력 분사장치에 의한 습식 샌딩기 등으로 제거(레이탄스) 확대(핀홀공극)하고, 콘크리트의 벌집 상태 균열, 누수 및 용수부분 등의 부실부분을 보강하여 고압 살수기로 청소하는 바탕처리를 행한 표면에 결함부 충진재( RC-60)를 사용하여 표면요철, 단차 등의 결함부를 충진하여 평활한 구체표면을 형성시킨 후 침투성 프라이머인 아크릴 에폭시 폴리머 프라이머(RCH-100) 및 에폭시 프라이머(RCT-100)로서 프라이머 바르기를 하여 모세관 차단과 세공과 공극에 침투 접착하여 1차적인 침투접착의 바탕을 강화시키는 바탕처리(1)를 하는 공정과,First, as shown in FIG. 1, the surface observation of the sphere is thoroughly performed, and the surface of the concrete surface layer, the pinhole coating, and the like are removed by a wet sanding machine using a powerful spraying device (Raytans) and expanded (pinhole voids), and the honeycomb of concrete Smooth concrete surface by filling defects such as surface irregularities and steps by using the defect filler (RC-60) on the surface of the surface treated by reinforcing cracks, leaks, and water parts, and cleaning with a high pressure sprayer. After forming, the primer is applied with acrylic epoxy polymer primer (RCH-100) and epoxy primer (RCT-100) as permeable primers to infiltrate capillary blocking and pores and pores to strengthen the base of primary penetration adhesion. A process of treating (1),
아크릴 에폭시 시멘트 몰탈(RCH-200) 또는 에폭시 시멘트 몰탈(RCT-200)을 레이탄스가 제거된 요철부와 확대된 핀홀공극에 완벽하게 충진되어 방수막이 형성될 수 있도록 정밀하게 도포(붓, 나무 흙손 겸용)하는 방수몰탈층(2)을 형성하는 공정과,Acrylic Epoxy Cement Mortar (RCH-200) or Epoxy Cement Mortar (RCT-200) is perfectly filled in the recesses and the enlarged pinhole voids with the removal of leitans so that the waterproof film can be formed precisely (brush, wooden trowel) Forming a waterproof mortar layer (2);
강력한 인장력을 지닌 균열방지용 보강직포(3;R.F.G cloth)를 적층하여 초기 방수층의 안전성을 구축하는 공정과,Laminating a crack-resistant reinforcing fabric (3; R.F.G cloth) with a strong tensile force to build the safety of the initial waterproof layer;
그리고, 이 보강직포(3;R.F.G Cloth)층 위에 아크릴 에폭시 시멘트 몰탈(RCH-200) 또는 에폭시 시멘트 몰탈(RCT-200)을 균일하게 압착 미장하여 완벽한 방수층을 형성하여 구체와의 강력한 접착력을 갖는 2차 방수몰탈층(4)을 약 2~7mm 두께로 형성하는 공정으로 된 것으로 종전의 공법을 보완, 개선한 방수·방식 공법이다.Then, the acrylic epoxy cement mortar (RCH-200) or the epoxy cement mortar (RCT-200) is uniformly compressed and plastered on the reinforcing fabric (3; RFG Cloth) layer to form a perfect waterproof layer, which has a strong adhesion to the sphere. It is a process of forming the car waterproof mortar layer 4 to a thickness of about 2 to 7 mm, and is a waterproof and anticorrosive method that supplements and improves the conventional method.
상기 바탕정리(1) 작업에 대하여 살펴보면;Looking at the ground clearance (1) operation;
수지 몰탈을 할 바탕에는 먼지, 기름, 녹 등의 불순물이 없도록 깨끗이 청소되어야 하며, 콘크리트 타설시 발생되는 거푸집의 이음부, 시공조인트, 요철부, 벌집상태 부위에는 파치하고, 콘크리트 표층의 박리층을 형성하는 레이탄스 흡착부위는 습식 샌딩기의 강력 분사장치로 핀홀(Pinhole) 부위의 공극 확대와 흡착된 레이탄스를 제거하여 샌드페이퍼(Sandpaper)형태의 요철형성으로 1차 방수접착제의 침투용이 및 방수층 접착이 완벽하도록 처리한 후 고압 살수기로 청소하여 이물질 제거를 철저히 한다.The base of resin mortar should be cleaned to be free from impurities such as dust, oil, rust, etc., and it shall be installed at the joints, construction joints, uneven parts, and honeycomb parts of the formwork generated during concrete pouring, and the peeling layer of the concrete surface layer may be removed. The latans adsorption site to be formed is a strong sandblasting device of a wet sanding machine, which enlarges the pores of the pinhole area and removes the adsorbed leitans to form sandpaper-type irregularities to facilitate penetration of the first waterproof adhesive and adhesion of the waterproof layer. After this treatment, clean it with a high pressure sprayer to thoroughly remove foreign substances.
그리고 균열부, 누수균열부에는 수지 그라우팅, 용수부위에는 지수처리 등 필요한 모든 공법을 적용하여 하자의 원천적 요인을 제거하도록 도 7a∼7i와 같은 과정을 수행한다.Then, the process as shown in FIGS. 7A to 7I is performed to remove the source of the defect by applying all necessary methods such as resin grouting to the crack and the leak crack, and water treatment to the water.
즉, 레이탄스 제거 및 핀홀부위 공극확대(도 7a)→벌집부위 수지몰탈 충진(도 7b)→누수부분 용수부분 지수처리(도 7c, 7d)→균열부 및 누수균열부 수지 그라우팅(도 7e, 7f)→이음누수 및 절연이음부 보완처리(7g)→코너부위 보강처리(7h)→파이프주위 보강처리(7i)의 과정을 수행한다.That is, the removal of latans and the expansion of the pinhole region (FIG. 7a) → filling the honeycomb resin mortar (FIG. 7b) → water leakage treatment of the leaked portion (FIGS. 7c and 7d) → resin grouting of the crack and the leaked crack (FIG. 7e, 7f) → joint leakage and insulation joint complementary treatment (7g) → corner portion reinforcement treatment (7h) → pipe periphery reinforcement treatment (7i).
이하 수지 몰탈의 시공전 파악사항에 대하여 살펴보면 다음과 같다.Hereinafter, the matters before the construction of the resin mortar will be described.
1). 현장배합에 앞서 소량의 재료를 시험 배합하여 재료의 적정 첨가량을 확정한다.One). A small amount of material should be tested and formulated prior to field formulation to determine the appropriate amount of material to add.
이때, 외기 온도 등 외적환경 변화로 인한 급속 경화로 작업성이 저하될 시에는 적정량의 첨가제를 첨가하여 작업성을 향상시킨다.At this time, when workability is degraded due to rapid curing due to external environmental changes such as external temperature, an appropriate amount of additive is added to improve workability.
2). 몰탈 배합2). Mortar
지정된 배합비율에 의하여 혼합된 골재에 수지몰탈 방수제를 골고루 충분히 혼합하여 수지 몰탈을 만든다.The resin mortar is mixed by sufficiently mixing the resin mortar waterproofing agent to the aggregate mixed by the designated blending ratio.
이하, 상기한 본 발명의 시공방법에 대하여 살펴보면 다음과 같다.Hereinafter, the construction method of the present invention described above is as follows.
1)바탕강화(프라이머 바르기)1) Strengthen the base (apply primer)
상기한 바탕정리공정(1)이 끝나면 침투성 프라이머인 아크릴 에폭시 폴리머 프라이머(RCH-100) 및 에폭시 프라이머(RCT-100)를 압송 분무기 또는 솔이나 로라로서 바탕처리가 완료된 바탕에 바르기를 한다.When the background cleaning process (1) is completed, the permeable primer acrylic epoxy polymer primer (RCH-100) and the epoxy primer (RCT-100) is applied to the ground on which the background treatment is completed with a pressure sprayer or a brush or a roller.
이때, 균일하게 충분히 함침될 수 있게 도포한다.At this time, the coating is applied so as to be uniformly sufficiently impregnated.
2)방수 1차2) waterproofing primary
아크릴 에폭시 시멘트 몰탈(RCH-200) 또는 에폭시 시멘트 몰탈(RCT-200)을 레이탄스가 제거된 요철부와 확대된 핀홀공극에 완벽하게 충진되어 방수막이 형성될 수 있도록 정밀하게 도포(붓, 나무 흙손 겸용)하여 방수1차 층을 형성시킨 후,Acrylic Epoxy Cement Mortar (RCH-200) or Epoxy Cement Mortar (RCT-200) is perfectly filled in the recesses and the enlarged pinhole voids with the removal of leitans so that the waterproof film can be formed precisely (brush, wooden trowel) Combined) to form a waterproof primary layer,
3)보강직포(R.F.G CLOTH)3) Reinforcing fabric (R.F.G CLOTH)
이 방수1차 층위에 보강직포(R.F.G Cloth)를 적층하여 초기 방수층의 안전성을 구축하며,Lay reinforcing fabric (R.F.G Cloth) on this waterproof primary layer to build the safety of the initial waterproof layer,
4) 방수2차4) waterproof secondary
이 보강직포(R.F.G Cloth)층 위에 아크릴 에폭시 시멘트 몰탈(RCH-200) 또는 에폭시 시멘트 몰탈(RCT-200)을 균일하게 압착 미장하여 완벽한 방수층을 형성하여 구체와의 강력한 접착력을 갖는 방수층과 보강직포의 강인한 인장력에 의한 균열방지 장치와 자체탄성을 갖는 내약품성 수지몰탈이 구체와의 일체감을 형성하여 CON'C 표층에 투과성 물질을 완벽히 차단하여 콘크리트 구조물의 안전성을 반영구적으로 하는 에폭시 또는 아크릴 에폭시 시멘트 몰탈(RC- TECH 및 RC- HITECH)을 이용한 방수, 방식 공법이다.Acrylic epoxy cement mortar (RCH-200) or epoxy cement mortar (RCT-200) is uniformly compressed and plastered on the RFG cloth layer to form a perfect waterproof layer. Epoxy or acrylic epoxy cement mortar that semi-permanent stability of concrete structure by preventing cracks by strong tensile force and chemically resistant resin mortar having self-elasticity form a unity with sphere and completely block permeable material on CON'C surface layer. RC-TECH and RC-HITECH) are waterproof and anticorrosive methods.
이하, 상기 결함부 충진재(RC-60)와, 바탕강화 프라이머인 아크릴 에폭시 폴리머 프라이머(RCH-100) 및 에폭시 프라이머(RCT-100), 수지몰탈 방수제 인 아크릴 에폭시 시멘트 몰탈(RCH-200) 및 에폭시 시멘트 몰탈(RCT-200), 균열방지용 보강직포(R.F.G CLOTH)에 대하여 살펴보면 다음과 같다.Hereinafter, the defect filler (RC-60), an acrylic epoxy polymer primer (RCH-100) and an epoxy primer (RCT-100), which are base reinforcing primers, an acrylic epoxy cement mortar (RCH-200) and an epoxy resin mortar waterproofing agent The cement mortar (RCT-200) and crack-proof reinforcing woven fabric (RFG CLOTH) are as follows.
1)결함부 충진재(RC-60)1) Defective filler (RC-60)
RC-60A(모세관, 세공, 핀홀, 미세 균열부 등에 강력침투 접착되는 비결정질 시리카를 혼입한 액체 수지화합물로서 강력한 방수성과 자체 탄성이 우수하며 강력한 접착력을 지닌 활성 화합물수지)와, 수밀성과 내화학성이 우수한 무기질파우더인 RC-60M(포틀랜트 시멘트 + 1∼7㎛의 미립자 플라이애쉬 + 활성화합물 + 규사(시리카) 등)을 배합한 혼합물로서,RC-60A (a liquid resin compound containing amorphous silica, which is strongly penetrated and adhered to capillaries, pores, pinholes, and micro cracks, is an active compound resin with excellent water resistance, excellent elasticity, and strong adhesion), and water resistance and chemical resistance. RC-60M (Portland Cement + Particulate Fly Ash + Active Compound + Silica (Silica), etc.), which is an excellent inorganic powder, is blended.
이 재료는 물에 불용성의 방수·방식층을 형성하는 특성을 가진 재료로서 콘크리트와의 강력한 접착력이 생기며, 종래 몰탈의 결함인 충격 또는 수축에 의한구열을 방지하고 이 충진재가 갖는 강인한 방수막은 시멘트 몰탈과의 결합으로 연행 공기층의 모세관을 막아주고 자체가 갖는 화학적인 내약품성과 내마모성의 특성은 콘크리트 표층 보호에서, 구체와의 강력한 접착은 콘크리트의 균열보수에 이르는 광범위한 용도에 응용된다.This material has the property of forming an insoluble waterproof and anticorrosive layer in water. It has strong adhesive strength with concrete. It prevents cracking due to impact or shrinkage, which is a defect of conventional mortar, and the tough waterproof membrane of this filler is cement mortar. In combination with, it prevents the capillary of entrained air layers and its chemical and abrasion resistance characteristics are applied to a wide range of applications, from concrete surface protection to strong adhesion to concrete crack repair.
2)바탕강화 프라이머(RCH-100, RCT-100)2) Base reinforced primer (RCH-100, RCT-100)
RCH-100은 합성고분자 수지와 극성 모노머, 에폭시수지 등의 공중합(Copolymers)에 의하여 만들어진 아크릴 에폭시 수지를 저점도화 하여 구체표면에서부터 단시간에 습윤되면서 내부 깊숙이 침투하여 공극을 메우며 치밀한 표면을 갖추도록 하는 1차적인 침투접착의 바탕면을 형성하는 프라이머이며, RCH-100 is a low viscosity acrylic polymer made by copolymerization of copolymers such as synthetic polymers, polar monomers, epoxy resins, etc. It is a primer forming the base surface of the primary penetration bonding,
RCT-100은 2액형의 에폭시 수지로서 폴리아마이드 등의 상온 경화제를 사용하여 특수 제조한 열경화성 수지이며 수지몰탈층과의 강력한 접착력과 내산, 내알카리, 내유, 내약품성, 수밀성, 기계적 강도를 겸비하여 몰탈 표층에 흡착하여 1차적인 침투접착의 바탕면을 형성하는 프라이머이다. RCT-100 is a two-component epoxy resin that is specially manufactured using a room temperature curing agent such as polyamide, and combines strong adhesion with the resin mortar layer, acid resistance, alkali resistance, oil resistance, chemical resistance, water tightness, and mechanical strength. It is a primer that adsorbs on the mortar surface layer and forms the base surface of primary penetration adhesion.
3)방수1, 2차용 수지몰탈(RCH-200, RCT-200)3) Waterproofing mortar for secondary and secondary resins (RCH-200, RCT-200)
RCH-200은 합성고분자 수지와 극성 모노머, 에폭시수지 등의 공중합(Copolymers)에 의하여 만들어진 아크릴 에폭시 수지에 무기질파우더(Portland Cement의 알카리성과 친화적 혼합성이 있는 알카리성 미세분말(1∼7㎛)의 플라이애쉬와 특수활성제와 다수의 활성화합물질이 복합된 재질에 규사(시리카)를 혼합한 재질)를 혼합한 수지몰탈 방수재로서 몰탈의 파괴인성의 증가와 인장강도의 증대 및 수지몰탈의 고강도화로 구열방지와 충격,수축에 강하며,화학적인 내약품성과 몰탈 결합체의 탄성형성으로 방수·방식성과 콘크리트 구체와의 강력한 접착력을 발휘하는 재료이며, RCH-200 is a ply of alkaline fine powder (1 ~ 7㎛) that has an alkaline and friendly blend of inorganic powders in acrylic epoxy resin made by copolymerization of synthetic polymer resin, polar monomer, epoxy resin, etc. It is a resin mortar waterproofing material that is mixed with ash, special active material and a number of activated compounds, and silica sand (silica) is mixed). It prevents heat by increasing the fracture toughness of mortar, increasing tensile strength and increasing the strength of resin mortar. Resistant to impact, shrinkage, and chemical resistance and mortar bond elasticity, it is a material that exhibits strong waterproofing, corrosion resistance, and strong adhesion to concrete spheres.
RCT-200은 2액형의 에폭시 수지로서 폴리아마이드 등의 상온 경화제를 사용하여 특수 제조한 열경화성 수지에 무기질파우더(Portland Cement의 알카리성과 친화적 혼합성이 있는 알카리성 미세분말(1∼7㎛)의 플라이애쉬와 특수활성제와 다수의 활성화합물질이 복합된 재질에 규사(시리카)를 혼합한 재질)를 혼합한 수지몰탈 방수재로서 몰탈의 파괴인성의 증가와 인장강도의 증대 및 수지몰탈의 고강도화로 구열방지와 충격, 수축에 강하며, 화학적인 내약품성과 몰탈 결합체의 탄성형성으로 방수·방식성과 콘크리트 구체와의 강력한 접착력을 발휘하는 재료이다 RCT-200 is a two-component epoxy resin, a fly ash of an alkaline fine powder (1 ~ 7㎛) that has an inorganic powder (also known as Portland Cement's alkalinity and friendly mixing) in a thermosetting resin specially manufactured using a room temperature curing agent such as polyamide. And resin mortar waterproofing material mixed with special active material and a number of activated compound materials (silica mixed with silica)), increase the fracture toughness of mortar, increase tensile strength and increase the strength of resin mortar It is resistant to impact and shrinkage and exhibits strong waterproofing, corrosion resistance and strong adhesion to concrete spheres by chemical resistance and elasticity of mortar binder.
4) 보강직포(R.F.G CLOTH)4) Reinforcing Fabric (R.F.G CLOTH)
정선된 글래스(Glass) 원료를 천 수백도의 고온하에서 대단히 미세한 (5,6,7,9ㅅ) 필라멘트 (Filament)로 용융 방사하여 50∼800개를 전분 유기집속제로 집속한 스트랜드(Strand)를 연사시킨 것이나, 합연시킨 것 혹은 특수가공 한 실 상태의 제품군(Yarn)을 일정간격의 경사, 위사로 직조하여 제작되는 것으로, 아크릴 에멀젼수지에 함침, 압착시켜 특유의 강인한 인장력을 발휘하는 것이며, 수지몰탈 사이에 적층시켜 강인한 인장력으로 수지 몰탈의 외부의 충격이나 온도변화에 따른 구열을 방지시켜 주는 것이다.Selected glass raw materials are melt spun at very high temperatures (thousands of hundreds of degrees) into very fine (5,6,7,9) filaments, and strands containing 50 to 800 strands of starch organic binder are collected. It is produced by weaving yarns, joints or specially processed yarns with a certain interval of warp and weft, and impregnating and compressing the acrylic emulsion resin to show its unique strength. By laminating between mortars, the tensile strength of the resin prevents the impact of the resin mortars from external impact or temperature change.
실시예 2Example 2
도 2와 같이 전술한 바탕정리(1)와 방수1,2차 공정을 수행한 수지몰탈 방수층위에 배수지나 정수지의 청정수보호의 목적 또는 하수처리장 계열의 각종구조물의 구체를 오,폐수와 유화수소에 의한 부식방지 및 처리수의 심미적 청결효과, 표면윤활로 사후유지관리(청소) 효율성 등의 목적으로 각 구조물의 용도에 적합하게 무용제형 및 용제형 또는 수계형 에폭시를 3회(6)(6')(6") 도포한 것이다.As shown in FIG. 2, the concrete mortar of various types of sewage treatment plant or the various structures of sewage treatment plant or the sewage treatment plant is disposed on the resin mortar waterproofing layer which has performed the above-described ground cleaning (1) and waterproofing primary and secondary processes. 3 times (6) (6 ') of non-solvent type, solvent type or water type epoxy suitable for the purpose of each structure for the purpose of prevention of corrosion and aesthetic clean effect of treated water and efficiency of post maintenance by surface lubrication. (6 ") applied.
실시예 3Example 3
도 3과 같이 전술한 바탕정리(1)와 방수1,2차 공정을 수행한 수지몰탈 방수층 위에 정수장, 하수처리장 계열의 각종 콘크리트 구조물 내부의 기둥, 천정, 도류벽에 청정수보호 및 부식방지를 목적으로 각 구조물의 용도에 적합하게 무용제형 및 용제형 또는 수계형 에폭시를 3회(6)(6')(6") 도포한 것이다.As shown in FIG. 3, on the resin mortar waterproofing layer having the above-described ground clearance (1) and waterproofing primary and secondary processes, clean water protection and corrosion prevention are performed on columns, ceilings, and walls of various concrete structures in the water purification plant and sewage treatment plant series. Solvent-type and solvent- or water-based epoxy are applied three times (6) (6 ') (6 ") to suit the purpose of each structure.
실시예 4Example 4
도 4와 같이 전술한 바탕정리(1)와 방수1,2차 공정을 수행한 수지몰탈 방수층 위에 대단위 아파트 단지의 옥상 물탱크의 청정수 수질보호와 각종 약품 탱크의 화공약품에 의한 부식 방지 및 하수처리장의 소화조 내부에 부식방지, 가스누출방지, 기밀유지를 목적으로 강판과 같은 인장력을 지닌 에폭시 수지(F.R.P)(7)(7')(7")와 글래스 클로스(Glass Cloth)(8)(8')를 적층한 다음 각 구조물의 용도에 적합하게 무용제형 및 용제형 또는 수계형 에폭시를 2회(6)(6') 도포한 것이다.Clean water quality protection of roof water tanks of large-scale apartment complexes and the chemicals of various chemical tanks and sewage treatment plants on the resin mortar waterproofing layer having the above-described ground clearance (1) and waterproofing primary and secondary processes as shown in FIG. 4. Epoxy resin (FRP) (7) (7 ') (7 ") and glass cloth (8) (8) with the same tensile strength as steel sheet for corrosion protection, gas leak prevention and airtightness ') Is laminated and then applied twice (6) (6') of solvent-free and solvent- or epoxy-based epoxy to suit the purpose of each structure.
즉, 에폭시 수지(7), 글래스 클로스(8), 다시 에폭시 수지(7'), 글래스 클로스(8')를 차례로 적층한 다음 다시 에폭시 수지를 2회(6)(6') 도포한 것이다.That is, the epoxy resin 7, the glass cloth 8, the epoxy resin 7 'and the glass cloth 8' are sequentially laminated, and then the epoxy resin is applied twice (6) (6 ').
※ 본 실시예 4의 약품탱크의 부식방지공에 있어서 글래스 클로스(8)(8')를 적층한 다음 다시 에폭시 수지 2회(6)(6')를 도포함에 있어 본 수지도포는 내산성이 강력한 내약품성 에폭시 수지를 도포한다.※ This resin coating cloth has strong acid resistance when laminating glass cloth (8) (8 ') in the anticorrosion hole of the chemical tank of Example 4 and then applying the epoxy resin twice (6) (6'). A chemical resistant epoxy resin is applied.
실시예 5Example 5
도 5와 같이 전술한 바탕정리(1)와 방수1,2차 공정을 수행한 수지몰탈 방수층 위에 정수장의 전오존, 후오존, 활성탄여과지, 오존체류조 등의 고도 정수처리 구조물의 방식을 목적으로 아크릴수지와 불소수지의 공중합(Copolymers)에 의하여 만들어진 내오존성 수지를 3회(9)(9')(9") 도포한 것이다.As shown in FIG. 5, the above-described ground cleaning 1 and the resin mortar waterproofing layer having undergone the first and second waterproofing processes are used for the purpose of the advanced water treatment structure such as ozone, ozone, activated carbon filter, ozone retention tank, etc. The ozone resistant resin produced by copolymerization of acrylic resin and fluororesin is applied three times (9) (9 ') (9 ").
이상에서 살펴본 바와 같이 본 발명의 에폭시 또는 아크릴 에폭시 시멘트 몰탈(RC- TECH 및 RC- HITECH)을 이용한 방수, 방식 공법은 부실 부분의 보수보강과 강력한 불순물 제거의 바탕처리가 완료된 콘크리트 구체 표층에 아크릴 에폭시 시멘트 몰탈 또는 에폭시 시멘트 몰탈로 마감하여 형성된 강력한 균열방지 방수, 방식층이 투과성 물질을 거의 완벽에 가깝게 차단하여 콘크리트 구조물의 안정성을 영구히 도모함으로서 생산성 증대와 균열, 누수, 부식 등 하자로 인한 경제적 손실을 미연에 방지하고자 하며 아울러 부속공정으로 다양한 방식공법을 겸용 대처하게 되어 정수장, 하수처리장 등의 각종 구조물에 대한 방수, 방식 공사의 효율성을 개선하게 되는 것으로서, 본 발명은 상기 언급한 바 외에도 많은 경제적 이점과 효과를 도모할 수 있는 등, 그 기대되는 효과가 매우 우수한 발명이다.As described above, the waterproofing and anticorrosive method using the epoxy or acrylic epoxy cement mortar of the present invention (RC-TECH and RC-HITECH) is an acrylic epoxy on the surface of concrete spheres where the reinforcement of the defective part and the ground treatment of strong impurities are completed. Strong crack-proof waterproofing and anticorrosive layer formed by finishing with cement mortar or epoxy cement mortar block the permeable material to near perfect perfection to ensure the stability of concrete structure, thereby increasing productivity and economic loss due to defects such as cracks, leaks and corrosion. In order to prevent in advance and to cope with various anticorrosion methods as an accessory process to improve the efficiency of waterproofing, anticorrosion construction for various structures, such as water purification plant, sewage treatment plant, the present invention has many economic advantages in addition to the above-mentioned. And can plan the effect The expected effect is a very excellent invention.
Claims (8)