KR20030046120A - Multilayer films and resin composition for multilayer films - Google Patents

Multilayer films and resin composition for multilayer films Download PDF

Info

Publication number
KR20030046120A
KR20030046120A KR20010076525A KR20010076525A KR20030046120A KR 20030046120 A KR20030046120 A KR 20030046120A KR 20010076525 A KR20010076525 A KR 20010076525A KR 20010076525 A KR20010076525 A KR 20010076525A KR 20030046120 A KR20030046120 A KR 20030046120A
Authority
KR
Grant status
Application
Patent type
Prior art keywords
layer
weight
parts
styrene
ethylene
Prior art date
Application number
KR20010076525A
Other languages
Korean (ko)
Other versions
KR100422761B1 (en )
Inventor
이동우
윤성택
신양재
이상진
Original Assignee
호남석유화학 주식회사
주식회사 이생
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

PURPOSE: Provided are a multi-layered film which has properties required for a medical injection container, such as thermal resistance, transparency, softness and formability and a resin composition for multi-layered film. CONSTITUTION: The multi-layered film has an outer layer, a middle layer and an inner layer. The outer layer comprises 50 to 100 weight parts of propylene homopolymer or an alpha-olefin copolymer of propylene and a blend thereof, and 1 to 50 weight parts of terpolymer of styrene-ethylene-butylene-styrene. The middle layer comprises 30 to 80 weight parts of alpha-olefin copolymer of propylene and 20 to 70 weight parts of terpolymer of styrene-ethylene-butylene-styrene. The inner layer comprises 50 to 100 weight parts of alpha-olefin copolymer of propylene and 50 to 100 weight parts of terpolymer of styrene-ethylene-butylene-styrene.

Description

다층 필름 및 다층 필름용 수지 조성물{Multilayer films and resin composition for multilayer films} The resin composition for a multilayer film and multilayer film {Multilayer films and resin composition for multilayer films}

본 발명은 내열성, 투명성, 유연성, 내충격성 및 열접착성이 우수한 의료용 다층필름 및 이를 이루는 내열성, 투명성, 유연성 및 성형성이 우수한 수지조성물에 관한 것이다. The present invention relates to a heat resistance, transparency, flexibility, impact resistance and an excellent heat-adhesive medical multilayer film and forming it in heat resistance, transparency, flexibility and good moldability resin composition.

종래 의료용 수액용기는 유리병으로 깨지기 쉽고 사용시 내용물이 감소함에 따른 진공공간의 발생으로 유량을 주기적으로 조절해야 하는 불편을 극복하기 위해 PVC계 수액용기가 등장하게 되었다. Conventional medical fluid containers was a PVC-based fluid container appeared to overcome the inconvenience that must be periodically adjusted to a flow rate generated by the vacuum space resulting from the fragile and when using a reduced content of a glass bottle. 그러나, PVC계 수액용기의 경우 내분비계 교란물질(환경호르몬)의 발생 및 소각시 다량의 다이옥신 발생으로 인해 Non-PVC계 수액용기 개발의 필요성이 대두하게 되었다. However, there is a need for PVC-based fluid endocrine disrupting chemicals (environmental hormones) generation and development due to a large amount of dioxin Non-PVC-based fluid container at the time of incineration in the case of the container was soybeans.

그러나, 상기 Non-PVC계 수액용기의 경우 폴리올레핀계 다층 용기의 개발이 많이 이루어졌으나, 대부분의 경우 살균시 내열성이 낮아 백화현상(투명도 저하) 발생 및 유연성 부족, 성형성 문제 등으로 실용화에 한계가 발생하였다. However, the Non-PVC type for the receiver vessel been made a lot of development in the polyolefin multi-layer container, a limit to the practical use in many cases, sterilization during the low bleaching (transparency decreases) generation and lack of flexibility in heat resistance, moldability and problems It occurred.

미국특허 출원 제 408,668호는 에틸렌/알파올레핀 공중합체를 포함하는 내부층, 폴리프로필렌계 또는 고밀도 폴리에틸렌 및 코폴리에스테르로 구성되는 제 1외부층, 폴리아미드 등으로 구성되는 제 2외부층을 포함하는 다중층 필름을 개시하고 있는데, 상기 필름은 유연성이 우수하나 121℃ 살균시 백화현상 발생으로 투명성이 저하된다. U.S. Patent Application No. 408 668 discloses a second outer layer consisting of an ethylene / an inner layer comprising an alpha-olefin copolymer, a first outer layer consisting of polypropylene or high density polyethylene, and co-polyester, polyamide, etc. There discloses a multilayer film, the film transparency is deteriorated with bleaching occurs when the flexibility is excellent in a 121 ℃ sterilization.

일본특개평 제 3-277365호에는 밀도 0.920g/㎤이상의 직쇄상 저밀도 폴리에틸렌으로 구성된 외부층, 밀도 0.915g/㎤이하의 직쇄상 저밀도 폴리에틸렌으로 구성된 중앙층, 밀도 0.918g/㎤이상의 측쇄상 저밀도 폴리에틸렌으로 구성된 내부층을 포함하는 3층 필름을 개시하고 있는데, 상기 필름은 유연성이 우수하나 121℃ 살균시 투명성이 저하된다. Japanese Patent Application Laid-Open No. 3-277365 discloses a density of 0.920g / ㎤ or more linear low-density outer layer consisting of polyethylene, density 0.915g / ㎤ than the linear low-density central layer consisting of a polyethylene, density 0.918g / ㎤ or more branched the low density polyethylene as there discloses a three-layer film comprising an inner layer made, the film has excellent flexibility, the transparency when a 121 ℃ sterilization is lowered.

일본특개평 제 9-52328호에는 신디오택틱폴리프로필렌과 프로필렌-에틸렌 공중합체로 이루어진 폴리프로필렌계 수지층과 메탈로센 촉매를 사용한 에틸렌-알파올레핀 공중합체로 이루어지는 폴리에틸렌계 수지층을 적층시켜 투명성, 유연성, 내열성을 향상시켰으나, 121℃ 살균시 백화현상 발생으로 투명성이 저하된다. Japanese Patent Application Laid-Open No. 9-52328 discloses a syndiotactic polypropylene and propylene-ethylene using a metallocene catalyst as a propylene-based polyester resin layer and a metal consisting of an ethylene copolymer by laminating a polyethylene-based resin layer is made of an alpha olefin copolymer Transparency , flexibility, sikyeoteuna improve the heat resistance, the transparency is degraded by bleaching occurs when 121 ℃ sterilization.

일본특개평 제 9-59455호는 프로필렌을 주성분으로 한 프로필렌-알파올레핀 공중합체와 수소첨가 스티렌부티렌고무 및 핵제로 이루어진 의료용 백용 조성물을 개시하고 있는데, 상기 조성물은 투명성, 내충격성이 우수하고 살균 후 백화현상은 없으나, 투명성과 유연성이 다소 떨어진다. Japanese Patent Application Laid-Open No. 9-59455 discloses a propylene as a major component, propylene - there discloses an alpha-olefin copolymer and hydrogenated styrene-butylene baekyong medical composition comprising rubber and a nucleating agent, the composition in transparency, impact resistance, and excellent sterilizing after bleaching, but is, rather, the transparency and the flexibility inferior.

미국특허 출원 제 6,017,598호는 폴리프로필렌계 수지를 포함하는 외부층, VLDPE 및 폴리프로필렌계 수지로 이루어진 조성물을 포함하는 중앙층, 및 폴리프로필렌계 수지 및 스티렌-에틸렌-부틸렌-스티렌 3원 공중합체 등을 포함하는 내부층으로 이루어지는 수지 조성물로 구성되는 3층 필름을 개시하고 있는데, 상기 필름은 열봉합성, 성형성 및 유연성은 우수하나 121℃ 살균시 투명성이 저하된다. U.S. Patent Application No. 6,017,598 discloses a polyester outer layer comprising a propylene resin, VLDPE and poly center layer comprising a composition consisting of a propylene-based resin, and polypropylene-based resins and styrene-ethylene-butylene-styrene terpolymer There discloses a three-layer film consisting of a resin composition composed of an inner layer comprising the like, the film has heat sealing properties, formability and flexibility are excellent in transparency when a 121 ℃ sterilization is lowered.

본 발명은 상기의 문제점을 개선하고, 의료용 수액용기에 요구되는 물성인 내열성, 투명성, 유연성, 성형성, 내충격성 및 열접착성이 우수한 의료용 다층 필름 및 이를 이루는 내열성, 투명성, 유연성 및 성형성이 우수한 수지 조성물을 개발하고자 한다. The present invention is to improve the above problem, and the medical fluid physical properties of heat resistance and transparency required for the container, flexibility, moldability, impact resistance and heat adhesion is excellent medical multilayer film and forming this heat resistance, transparency, flexibility and moldability and to develop an excellent resin composition.

본 발명은 외부층, 중앙층 및 내부층을 포함하는 다층필름으로 외부층은 A: 폴리프로필렌 단독중합체, 프로필렌을 주성분으로 하는 알파올레핀 공중합체 또는 이들의 블랜드 50~99중량부 및 B: 스티렌-에틸렌-부틸렌-스티렌 삼원 공중합체 1~50중량부로 이루어진 수지 조성물로 구성되고, 중앙층은 A′: 프로필렌을 주성분으로 하는 알파올레핀 공중합체의 30~80중량부 및 B의 20~70중량부로 이루어진 수지 조성물로 제조된 것이며, 내부층은 상기 A′의 50~99중량부 및 B의 1~50중량부로 이루어진 수지 조성물로 구성된다. The present invention is a multi-layer film comprising an outer layer, middle layer and inner layer outer layer A: polypropylene homopolymers, alpha-olefin copolymer or a blend mainly composed of a polypropylene 50 to 99 parts by weight, and B: a styrene- ethylene-butylene-styrene terpolymer consists of a 1 to 50 parts by weight of resin composition, the center layer is a ': 30 ~ 80 parts by weight of alpha olefin copolymer as a main component, propylene unit, and parts 20 to 70 parts by weight of B are manufactured with a resin composition consisting of, the inner layer is made of a resin composition comprising an amount of 1 to 50 parts by weight of 50 to 99 parts by weight, and B of the a '. 한편, 상기 각 층은 각 층의 성분 100중량부에 대하여 C: 에틸렌을 주성분으로 하는 알파올레핀 공중합체 1~20중량부를 더 함유할 수 있다. On the other hand, the layers are based on 100 parts by weight of the components of each layer C: may further contain alpha olefin copolymer composed mainly of ethylene of 1 to 20 parts by weight.

상기 외부층은 열봉합시 표면불량없이 열전달에 의해 내면층을 접착시켜야 하므로, 프로필렌 성분의 함량이 높아야 하며, 내부층 및 중앙층 수지 조성물보다 융점이 높아야 한다. It said outer layer is heat sealed so When need to adhere the inner layer by means of heat transfer surfaces without defects, the higher the content of the propylene component, the higher melting point than the inner layer and the central layer resin composition. 또한, 외부층은 용융지수(230℃, 2.16kg)가 0.5~7.0g/10min인 것이 바람직하며, 이는 열접착시 내면의 접착성을 높이면서 표면을 보호하기 위해서이다. Further, the outer layer is a melt index (230 ℃, 2.16kg), and is preferably from 0.5 ~ 7.0g / 10min, which is to protect the surface while increasing the adhesion of the inner surface during thermal bonding.

그리고, 상기 중앙층은 투명성, 유연성이 가장 중요한 요소이므로, 스티렌-에틸렌-부틸렌-스티렌 삼원 공중합체의 함량을 높이는 것이 효과적이다. Further, the center layer had an in transparency, flexibility, the most important factor, a styrene-it is effective to increase the content of styrene terpolymer - ethylene-butylene. 또한, 중앙층을 구성하는 수지조성물의 용융지수(230℃, 2.16kg)가 1.0~8.0g/10min이 바람직하며, 이는 필름의 성형시 용융지수가 높으면 성형이 불가능하기 때문이다. In addition, the melt index of the resin composition constituting the middle layer (230 ℃, 2.16kg) is 1.0 ~ 8.0g / 10min is preferred, because the melt index of the molding of the film to high molding is not possible.

의료용 수액용기에 보관된 약물이 적절한 타입의 종류이고, 약물이 변질되거나 오염되어 있는지 여부를 육안으로 용이하게 확인하기 위해서는 의료용 수액용기는 투명성이 좋아야 한다. And the drug has been the type of suitable types stored in the medical fluid container, in order to confirm that the drug is easily deteriorated or whether with the naked eye that the contaminated medical fluid containers shall be good in transparency. 따라서, 투명도는 적어도 80%이상, 바람직하게는 85%이상이 양호하다. Thus, the transparency is good for at least 80%, preferably 85% or more.

또한, 상기 내부층은 의약품이 접촉하는 부분이면서 용기 밀봉시 서로간의 접착이 일어나는 부분으로 융점이 다른 층에 비해 낮은 것이 사용되며, 내부층은 용융지수(230℃, 2.16kg)가 2.0~9.0g/10min인 것이 바람직하다. Further, the inner layer portion and having a melting point of use, yet it is lower than the other layer as a part of the adhesive between each other taking place during the sealing container of the drug contact with, the inner layer has a melt index (230 ℃, 2.16kg) is 2.0 ~ 9.0g that the / 10min is preferred.

본 발명에서 각층을 구성하는 수지의 융점은 외부층:148~170℃, 중앙층: 135~155℃ 및 내부층: 130~150℃인 것을 특징으로 하는 다층 필름을 제공한다. The melting point of the resin constituting the respective layers in the present invention is outer layer: providing a multi-layer film, characterized in that 130 ~ 150 ℃: 148 ~ 170 ℃, the center layer: 135 ~ 155 ℃ and the inner layer. 외부층, 중앙층 및 내부층이 상기와 같은 온도범위를 갖는 것은 의료용 수액용기는 내용물을 충진한 후 121℃에서 살균을 하도록 되어 있으며, 이때 변형이나 용출되는 물질이 규정치 이하이어야 하기 때문에 내열성이 좋아야 한다. The outer layer, the center layer and the inner layer has a temperature range as described above, and is adapted to the sterilization at 121 ℃ after the medical fluid container is filled with the contents, the case deformation or eluted material to be heat resistance in good because it must be higher than the predetermined do. 외부층은 살균시 먼저 접촉하는 부분으로 내열성이 더 우수한 수지가 필요하며, 내부층은 용기를 접착시킬 때 실링온도를 낮추면서 접착이 용이하도록 용융온도가 낮은 수지가 필요하다. The outer layer is a need to better heat resistance to the resin portion in contact first during sterilization, the inner layer has a lower melting temperature resin to facilitate bonding the need while reducing the sealing temperature when bonding the container. 이때, 외부층은 내부층의 실링온도보다 녹는점이 높아 변화발생이 없어야 한다. At this time, the outer layer is higher than the melting point temperature of the inner sealing layer should be no change occurs. 중앙층은 전체 다층필름의 유연성 및 투명성을 향상시키면서 내열성을 갖는 수지층이 필요하다. The middle layer while improving the flexibility and transparency of the entire multi-layer film having a heat-resistant resin is required.

의료용 수액용기는 사용시 수액이 공급되는 속도가 일정하기 위해서는 공급되는 속도와 거의 일정하게 용기가 쭈그러들 수 있어야 하므로, 유연성이 좋아야 한다. Because the medical fluid container needs to be able to use the receiver the feed rate, the speed and the container jjugeureo substantially constant to be supplied in order to schedule, and require good flexibility. 따라서 본 발명의 다층필름의 굴곡탄성률은 5000kg/㎠이하가 바람직하다. Thus the flexural modulus of the multilayer film of the present invention is preferably less than 5000kg / ㎠.

본 발명에 따라 제조된 필름(film)은 용기로서 적절한 열가소성물질로서 하나 이상의 고분자 물질층을 갖는 것을 의미하며, 상기 고분자 물질들은 당업계에 잘 알려진 방법에 의해 결합될 수 있다. Means having at least one high molecular material layer as a suitable thermoplastic film (film) produced in accordance with the present invention provides a container, and the polymer material can be joined by methods well known in the art. 본 발명의 다층 필름은 외부층, 중앙층 및 내부층으로 구성될 수 있고 특수 기능성 부여를 위해 층의 추가가 가능하나 경제성 문제가 발생할 수 있다. Multilayer films of the present invention may be composed of an outer layer, middle layer and inner layer can cause an additional problem of the economics one can layer for imparting specialized functionality.

나아가, 본 발명에 따른 다층필름은 약물을 투여하는 의료용 수액용기로 사용될 뿐만 아니라, 소변 또는 기타 환자의 배설물을 수집하는데도 사용될 수 있다. Further, the multi-layer film according to the present invention is not only used as a medical fluid container of administering a drug, it can also be used to collect the excreta of urine, or other patients. 또한, 본 발명에 따른 다층필름은 환경호르몬의 영향이 없고, 접착성 수지층 없이 3층의 구성만으로 수액용기 성형이 가능하다. Further, there is no multi-layer film has effects of environmental hormones according to the present invention, the fluid container may be formed with only the configuration of the third layer without adhesive resin layer.

이하 실시예를 들어 본 발명을 상세히 설명하지만, 본 발명이 이들 예로만 한정되는 것은 아니다. Detailed description of the present invention, for following examples, but the present invention is not limited only to these examples.

[실시예 1] Example 1

A2) 용융지수(230℃, 2.16㎏) 5.0g/10min이고 에틸렌 및 부텐-1의 함량이 각각 3%이상인 프로필렌 삼원 공중합체 70중량부, B1) 용융지수(230℃, 2.16㎏) 1.0g/10min이고 스티렌 함량이 30%인 스티렌-에틸렌-부티렌-스티렌 삼원 공중합체30중량부를 헨셀믹서에서 3분간 혼합한 후, L/D가 32이고 직경이 53㎜인 이축압출기로 190~220℃에서 압출하여 펠렛상의 조성물을 얻어 이를 3층 시트의 중앙층으로 하였다. A2) a melt index (230 ℃, 2.16㎏) 5.0g / 10min and an ethylene and butene-1, 70 parts by weight of 3% or more propylene content of the terpolymer, respectively, B1) a melt index (230 ℃, 2.16㎏) 1.0g / 10min and a styrene content of 30% styrene-ethylene-butylene-styrene terpolymer and 30 parts by weight were mixed for 3 minutes in a Henschel mixer, L / D is 32, and at 190 ~ 220 ℃ in a twin-screw extruder having a diameter 53㎜ obtained by extruding the composition on the pellets were them into the middle layer of the three-layer sheet. 한편, A3) 용융지수(230℃, 2.16㎏) 3.0g/10min인 프로필렌 단독중합체 80중량부 및 B1)의 20중량부를 헨셀믹서에서 3분간 혼합한 후, L/D가 32이고 직경이 53㎜인 이축압출기로 190~220℃에서 압출하여 펠렛상의 조성물을 얻어 이를 3층 시트의 외부층으로 하였다. On the other hand, A3) a melt index (230 ℃, 2.16㎏) 3.0g / 10min, propylene homopolymer and 80 parts by weight of B1) is 20 parts by weight, for 3 minutes in a Henschel mixer and mixed, L / D is 32 and the diameter of 53㎜ in a twin-screw extruder and extruded at 190 ~ 220 ℃ takes the composition on the pellets were it to the outer layer of the three-layer sheet. 다음, A2의 90중량부에 B1의 10중량부를 헨셀믹서에서 3분간 혼합한 후, L/D가 32이고 직경이 53㎜인 이축압출기로 190~220℃에서 압출하여 펠렛상의 조성물을 얻어 이를 3층 시트의 내부층으로 하여, 3층 필름성형기를 이용하여 외부층/중앙층/내부층의 두께가 30㎛/140㎛/30㎛인 3층필름을 성형하였다. And then, after mixing for 3 minutes in a Henschel mixer 90 parts by weight 10 parts by weight of B1 to A2, L / D is 32, and in a twin-screw extruder and extruded at 190 ~ 220 ℃ takes the composition on the pellet diameter 53㎜ this 3 Due to the inner layer of the layer sheet, the thickness of the three-layer film molding machine, the outer layer / middle layer / inner layer was formed by using the 30㎛ / 140㎛ / 30㎛ the three-layer film. 그리고, 살균전 투명도, 내열성(121℃, 30분간 증기살균 후의 투명도), 중앙층 수지의 굴곡탄성률, 열접착성, 필름성형성 및 충격강도를 측정하여 그 결과를 표 1에 나타내었다. Then, the transparency before sterilization, the heat resistance (121 ℃, transparency after steam sterilization 30 minutes), the flexural modulus of the middle layer resin, a heat-adhesive, to measure the film formability and impact strength. The results are shown in Table 1.

상기에서 투명성은 ASTM D-746에 의하여 측정한 것으로, 이는 200㎛의 필름을 성형하여 Haze meter를 사용하여 측정한 것이다. That is transparent at said measured by ASTM D-746, which was measured by molding using a Haze meter a film of 200㎛.

굴곡탄성률은 ASTM D-790법에 의하여 측정한 것으로, 12.7㎜(폭)×127㎜(길이)×6㎜두께의 시편을 성형하여 굴곡탄성률 측정기를 사용해 측정하였다. Flexural modulus was measured using that measured by ASTM D-790 method, 12.7㎜ (width) × 127㎜ (length) × 6㎜ flexural modulus measuring instrument by molding a specimen having a thickness of.

열접착성은 135~140℃, 2KG압력에서 2초간 접착 후 외관을 검사하였다. Heat adhesion was tested for 135 ~ 140 ℃, appearance after 2 seconds from bonding 2KG pressure. 의료용 수액용기는 다층필름 간의 내부층의 접착으로 봉지형태로 만들어지는데, 열원이 외부층에 먼저 가해져서 내부로 전달되고, 이 때 내부층이 접착되기 위한 열로인해 외부층의 변형이 일어나지 않은지 여부를 열접착성으로 판단하였다. Whether a medical fluid container which is produced by a bag shape by bonding of the inner layer between the multi-layer film, the heat source is so, first applied to the outer layer being transmitted to the interior, at this time due to the heat to be the inner layer adhesive sure that the deformation of the outer layer occur It was determined by thermal adhesion.

충격강도는 500㎖의료용 용기를 성형하여 물을 주입한 후, 상온의 2m높이에서 배면낙하시켜 누설여부를 관찰하였다. Impact strength 500㎖ by molding the medical container after pouring of water, followed by a back-fall from 2m height of the room temperature was observed for leaks.

한편, 용융지수는 ASTM D-1238법으로 230℃에서 측정하였다. On the other hand, the melt index was measured at 230 ℃ to ASTM D-1238 method. 용융지수는 특정압력(2.16㎏) 및 온도(230℃)에서 10분내 지름 2.09㎜의 구멍(orifice)을 통과할 수 있는 열가소성 수지의 양(g)을 의미하는 것이다. Melt Index is intended to mean the amount (g) of the thermoplastic resin that can pass through a certain pressure (2.16㎏) and temperature (230 ℃) 10 minutes hole (orifice) of diameter in 2.09㎜.

용융온도는 ASTM D-2117법에 의하여 DSC를 사용하여 측정하였다. The melting temperature was measured using DSC, by ASTM D-2117 method.

[실시예 2] Example 2

A2의 40중량부, B1의 40중량부 및 B2) 용융지수(230℃, 2.16㎏) 3.0g/10min이고 스티렌 함량이 10%인 스티렌-에틸렌-부틸렌-스티렌 삼원 공중합체 20중량부를 헨셀믹서에서 3분간 혼합한 후, L/D가 32이고 직경이 53㎜인 이축압출기로 190~220℃에서 압출하여 펠렛상의 조성물을 얻어 이를 3층 시트의 중앙층으로 제조하는 것을 제외하고는 실시예 1과 동일한 방법으로 실험하여 그 결과를 표 1에 나타내었다. 40 parts by weight of A2, B1 of 40 parts by weight, and B2) a melt index (230 ℃, 2.16㎏) 3.0g / 10min, and a styrene content of 10% of styrene-ethylene-butylene-styrene terpolymer of 20 parts by weight of a Henschel mixer in the mix for 3 minutes and then, L / D is 32, and is carried out, and except that in the twin-screw extruder and extruded at 190 ~ 220 ℃ takes the composition on the pellet diameter 53㎜ manufacturing them into the middle layer of the three-layer sheet in example 1 by the experiments in the same manner. the results are shown in Table 1.

[실시예 3] Example 3

상기 실시예 2에서 내부층 수지를 A2의 100중량부로 변화시킨 것을 제외하고는 실시예 2와 동일한 방법으로 실험하여 그 결과를 표 1에 나타내었다. By experiment, and it is in the same manner as in Example 2 except that in Example 2 was changed to 100 parts by weight of the inner layer resin A2. The results are shown in Table 1.

[실시예 4] Example 4

실시예 1에서 중앙층을 A1) 용융지수(230℃, 2.16㎏) 2.0g/10min인 에틸렌 함량이 3%인 폴리프로필렌 랜덤공중합체 수지 20중량부, A2의 20중량부, B1의 40중량부 및 B2의 20중량부로 변화시키고, 외부층을 A3의 80중량부 및 A2의 20중량부로변화시킨 것을 제외하고는 상기 실시예 1과 동일한 방법으로 실험하여 그 결과를 표 1에 나타내었다. A1 embodiment the middle layer in Example 1) a melt index (230 ℃, 2.16㎏) 2.0g / 10min in an ethylene content of 3% of polypropylene random copolymer resin 20 parts by weight, 20 parts by weight of A2, 40 parts by weight of B1 and the weight change was 20 parts of B2, the outer layer and the experiment in the same manner as example 1 except for change amount 80 parts by weight and 20 parts by weight of A2 A3 of the results are shown in Table 1.

[실시예 5] Example 5

내부층 수지를 A2의 50중량부 및 B1의 50중량부로 변화시키는 것을 제외하고는 상기 실시예 1과 동일한 방법으로 실험하여 그 결과를 표 1에 나타내었다. Except for varying the inner layer resin 50 parts by weight of A2 and B1 and 50 parts by weight of the experiments in the same manner as in Example 1 The results are shown in Table 1.

[실시예 6] Example 6

외부층 수지를 A3의 70중량부 및 B1의 30중량부로 변화시키는 것을 제외하고는 상기 실시예 1과 동일한 방법으로 실험하여 그 결과를 표 1에 나타내었다. Except that changing the outer layer resin 30 parts by weight of the A3 of 70 parts by weight of B1 to experiment in the same manner as in Example 1 The results are shown in Table 1.

[실시예 7] Example 7

중앙층 수지를 A2의 60중량부, B1의 30중량부 및 C) 용융지수(190℃, 2.16㎏) 1.1g/10min인 에틸렌 옥텐 공중합체 10중량부로 변화시킨 것을 제외하고는 상기 실시예 1과 동일한 방법으로 실험하여 그 결과를 표 1에 나타내었다. The middle layer resin 60 parts by weight of A2, 30 parts by weight, and C) a melt index (190 ℃ of B1, 2.16㎏) and 1.1g / 10min ethylene-octene copolymer and is the embodiment except for parts 10 change in weight Example 1 the experiment in the same manner. the results are shown in Table 1.

[실시예 8] Example 8

중앙층 수지를 A2의 60중량부, B1의 30중량부 및 C의 10중량부로 변화시키고, 내부층 수지를 A2의 80중량부, B1의 10중량부, C의 10중량부로 변화시키며, 외부층 수지를 A3의 70중량부, B1의 20중량부, C의 10중량부로 변화시키는 것을 제외하고는 상기 실시예 1과 동일한 방법으로 실험하여 그 결과를 표 1에 나타내었다. 60 parts by weight of the middle layer resin A2, and 30 change parts 10 by weight of parts by weight and C in the B1, 80 parts by weight of the inner layer resin A2, 10 parts by weight of B1, sikimyeo changing part 10 by weight of C, the outside layer 70 parts by weight of the resin A3, 20 parts by weight of B1, except that 10 parts by weight of a C to change to the experiment in the same manner as in example 1. the results are shown in Table 1.

[비교예 1] Comparative Example 1

중앙층 수지를 A2의 20중량부 및 B1의 80중량부로 변화시키는 것을 제외하고는 상기 실시예 1과 동일한 방법으로 실험하여 그 결과를 표 1에 나타내었다. Except for changing the central layer resin amount 80 parts by weight of 20 parts by weight of A2 and B1 The experiment as Example 1. The results are shown in Table 1.

[비교예 2] Comparative Example 2

외부층 수지를 A3의 40중량부 및 B1의 60중량부로 변화시키는 것을 제외하고는 상기 실시예 1과 동일한 방법으로 실험하여 그 결과를 표 1에 나타내었다. Except that changing the outer layer resin 60 parts by weight of the A3 of 40 parts by weight of B1 to experiment in the same manner as in Example 1 The results are shown in Table 1.

[비교예 3] [Comparative Example 3]

내부층 수지를 A2의 30중량부 및 B1의 70중량부로 변화시키는 것을 제외하고는 상기 실시예 1과 동일한 방법으로 실험하여 그 결과를 표 1에 나타내었다. Except for varying the inner layer resin 70 parts by weight of 30 parts by weight of A2 and B1 The experiment as Example 1. The results are shown in Table 1.

[비교예 4] Comparative Example 4

외부층 수지를 A3의 100중량부로 변화시키고, 내부층 수지를 A2의 100중량부로 변화시키는 것을 제외하고는 상기 실시예 1과 동일한 방법으로 실험하여 그 결과를 표 1에 나타내었다. Changing the outer layer resin is 100 parts by weight of A3 and, with the exception that varying the inner layer resin is 100 parts by weight of A2 to the same experimental procedure as in Example 1. The results are shown in Table 1.

[비교예 5] Comparative Example 5

중앙층 수지를 A2의 50중량부, B1의 20중량부 및 C의 30중량부로 변화시키는 것을 제외하고는 상기 실시예 1과 동일한 방법으로 실험하여 그 결과를 표 1에 나타내었다. 50 parts by weight of the middle layer resin A2, and to the test in the same manner as Example 1 except for changing 30 parts by weight of B1, 20 parts by weight of C and the results are shown in Table 1.

조성(중량부) Composition (parts by weight) 실시예 Example 비교예 Comparative Example
1 One 2 2 3 3 4 4 5 5 6 6 7 7 8 8 1 One 2 2 3 3 4 4 5 5
중 앙 층 The central layer 수 지 조 성 Resins Division St. A1 A1 20 20
A2 A2 70 70 40 40 40 40 20 20 70 70 70 70 60 60 60 60 20 20 70 70 70 70 70 70 50 50
C C 10 10 10 10 30 30
B1 B1 30 30 40 40 40 40 40 40 30 30 30 30 30 30 30 30 80 80 30 30 30 30 30 30 20 20
B2 B2 20 20 20 20 20 20
용융지수(230℃, 2.16㎏) A melt index (230 ℃, 2.16㎏) 4.0 4.0 3.7 3.7 3.7 3.7 3.4 3.4 4.0 4.0 4.0 4.0 3.9 3.9 3.9 3.9 2.8 2.8 4.0 4.0 4.0 4.0 4.0 4.0 3.6 3.6
외 부 층 The external layer 수 지 조 성 Resins Division St. A2 A2 20 20
A3 A3 80 80 80 80 80 80 80 80 80 80 70 70 80 80 70 70 80 80 40 40 80 80 100 100 80 80
B1 B1 20 20 20 20 20 20 20 20 30 30 20 20 20 20 20 20 60 60 20 20 20 20
C C 10 10
용융지수(230℃, 2.16㎏) A melt index (230 ℃, 2.16㎏) 2.8 2.8 2.8 2.8 2.8 2.8 3.5 3.5 2.8 2.8 2.5 2.5 2.8 2.8 2.7 2.7 2.8 2.8 2.3 2.3 2.8 2.8 3.0 3.0 2.8 2.8
내 부 층 The internal layer 수지 조성 Resin composition A2 A2 90 90 90 90 100 100 90 90 50 50 90 90 90 90 80 80 90 90 90 90 30 30 100 100 90 90
B1 B1 10 10 10 10 10 10 50 50 10 10 10 10 10 10 10 10 10 10 70 70 10 10
C C 10 10
용융지수(230℃, 2.16㎏) A melt index (230 ℃, 2.16㎏) 4.5 4.5 4.5 4.5 5.0 5.0 4.5 4.5 3.7 3.7 4.5 4.5 4.5 4.5 4.3 4.3 4.5 4.5 4.5 4.5 2.5 2.5 5.0 5.0 4.5 4.5
살균전 투명도(%) Before sterilization transparency (%) 90 90 91 91 91 91 90 90 91 91 90 90 88 88 87 87 93 93 91 91 91 91 88 88 83 83
살균후 투명도(%) After sterilization transparency (%) 91 91 93 93 93 93 92 92 92 92 91 91 90 90 88 88 94 94 93 93 93 93 87 87 80 80
중앙층수지의 굴곡탄성율(㎏/㎠) The flexural modulus of the middle layer resin (㎏ / ㎠) 4500 4500 2000 2000 2000 2000 2200 2200 4500 4500 4500 4500 2700 2700 2600 2600 1500 1500 4500 4500 4500 4500 4500 4500 3600 3600
필름성형성 Film formability × × × ×
열접착성 Thermal Adhesive - - × ×
충격강도 Impact strength - - - - × ×
* A1:에틸렌 함량이 2%인 폴리프로필렌 랜덤공중합체 수지, 용융지수(230℃, 2.16㎏): 2.0g/10min, Tm; * A1: ethylene content of 2% polypropylene random copolymer resin, a melt index (230 ℃, 2.16㎏): 2.0g / 10min, Tm; 150℃* A2:에틸렌 및 부텐-1 함량이 각각 3%이상인 프로필렌계 삼원공중합체 수지, 용융지수 (230℃, 2.16㎏):5.0g/10min, Tm; 150 ℃ * A2: ethylene-butene and propylene-based terpolymer resin, a melt index -1 content of less than 3%, respectively (230 ℃, 2.16㎏): 5.0g / 10min, Tm; 135℃* A3:폴리프로필렌 단독중합체, 용융지수(230℃, 2.16㎏):3.0g/10min, Tm; 135 ℃ * A3: polypropylene homopolymer, melt index (230 ℃, 2.16㎏): 3.0g / 10min, Tm; 165℃* B1:스티렌-에틸렌-부틸렌-스티렌 삼원공중합체,용융지수(230℃,2.16㎏):1.0g/10min,스티렌 함량 30%* B2:스티렌-에틸렌-부틸렌-스티렌 삼원공중합체,용융지수(230℃,2.16㎏):3.5g/10min,스티렌 함량 10%* C:에틸렌 옥텐 공중합체, 용융지수(190℃, 2.16㎏): 1.1g/10min 165 ℃ * B1: styrene-ethylene-butylene-styrene terpolymer, a melt index (230 ℃, 2.16㎏): 1.0g / 10min, 30% styrene content * B2: styrene-ethylene-butylene-styrene terpolymer , a melt index (230 ℃, 2.16㎏): 3.5g / 10min, 10% styrene content * C: ethylene-octene copolymer, melt index (190 ℃, 2.16㎏): 1.1g / 10min

이상에서 설명한 바와 같이, 본 발명은 폴리프로필렌계 수지, 스티렌-에틸렌-부틸렌-스틸렌 삼원공중합체 및 에틸렌을 주성분으로하는 알파올레핀 공중합체 수지를 사용하여 의료용 수액용기에 요구되는 물성인 내열성, 투명성, 유연성, 성형성, 내충격성 및 열접착성이 우수한 의료용 다층필름 구성 및 이를 이루는 내열성, 투명성, 유연성 및 성형성이 우수한 수지 조성물을 얻을 수 있다. As described above, the present invention provides a polypropylene-based resin, styrene-ethylene-butylene-styrene terpolymer, and the physical properties of heat resistance using the alpha olefin copolymer resins composed mainly of ethylene required for the medical fluid container, transparency , it is possible to obtain the flexibility, moldability, impact resistance and an excellent heat-adhesive medical multilayer film configuration and excellent resin composition constituting this heat resistance, transparency, flexibility and moldability.

Claims (6)

  1. 외부층, 중앙층 및 내부층을 포함하는 다층필름에 있어서, In the outer layer, the multilayer film comprising a center layer and an inner layer,
    외부층은 A: 프로필렌 단독중합체 또는 프로필렌을 주성분으로 하는 알파올레핀 공중합체 및 이들의 블렌드 50~100중량부, B: 스티렌-에틸렌 -부틸렌-스티렌 삼원 공중합체 1~50중량부로 구성되고, The outer layer A: a propylene homopolymer or propylene-alpha olefin copolymers containing as a main component and blends thereof 50 to 100 parts by weight, B: a styrene-styrene terpolymer consists amount of 1 to 50 parts by weight, ethylene-butylene
    중앙층은 A′: 프로필렌을 주성분으로 하는 알파올레핀 공중합체 30~80중량부 및 B: 스티렌-에틸렌-부틸렌-스티렌 삼원 공중합체 20~70 중량부로 제조된 것이며, Central layer A ': 30 ~ 80 parts by weight alpha-olefin copolymer as a main component, propylene unit, and B: a styrene-styrene terpolymers are manufactured parts 20 to 70 by weight, ethylene-butylene
    내부층은 A′: 프로필렌을 주성분으로 하는 알파올레핀 공중합체 50~100중량부 및 B: 스티렌-에틸렌-부틸렌-스티렌 삼원 공중합체 1~50 중량부로 이루어진 것을 특징으로 하는 다층필름. The inner layer A ': alpha-olefin copolymer composed mainly of propylene, and 50 to 100 parts by weight B: styrene-ethylene-butylene-styrene terpolymer 1 to the multi-layer film, characterized in that consisting of 50 parts by weight.
  2. 제 1항에 있어서, 각 층은 상기 각층 성분 100중량부에 대하여 C: 에틸렌을 주성분으로 하는 알파올레핀 공중합체 1~20중량부를 더 포함하는 것을 특징으로 하는 다층필름. The method of claim 1 wherein each layer based on 100 parts by weight of the respective layers component C: a multi-layer film according to claim 1, further comprising an alpha-olefin copolymer composed mainly of ethylene of 1 to 20 parts by weight.
  3. 제 1항에 있어서, 각 층을 구성하는 수지의 융점이 외부층 : 148~170℃, 중앙층 : 135~155℃ 및 내부층 : 130~150℃인 것을 특징으로 하는 다층필름. According to claim 1, wherein the melting point of the resin constituting each layer is outer layer: 148 ~ 170 ℃, the center layer: 135 ~ 155 ℃ and an inner layer: a multilayer film which is characterized in that the 130 ~ 150 ℃.
  4. 제 1항에 있어서, 상기 외부층의 용융지수(230℃, 2.16kg)가 0.5~7.0g/10min인 것을 특징으로 하는 다층필름. The method of claim 1 wherein the melt index of the outer layer (230 ℃, 2.16kg) is a multi-layer film, characterized in that 0.5 ~ 7.0g / 10min.
  5. 제 1항에 있어서, 상기 중앙층의 용융지수(230℃, 2.16kg)가 1.0~8.0g/10min인 것을 특징으로 하는 다층필름. The method of claim 1 wherein the melt index of the central layer (230 ℃, 2.16kg) is a multi-layer film, characterized in that 1.0 ~ 8.0g / 10min.
  6. 제 1항에 있어서, 상기 내부층의 용융지수(230℃, 2.16kg)가 2.0~9.0g/10min인 것을 특징으로 하는 다층필름. The method of claim 1 wherein the melt index of the inner layer (230 ℃, 2.16kg) is a multi-layer film, characterized in that 2.0 ~ 9.0g / 10min.
KR20010076525A 2001-12-05 2001-12-05 Multilayer films and resin composition for multilayer films KR100422761B1 (en)