KR20030003973A - Flexible patches for teeth whitening - Google Patents

Flexible patches for teeth whitening Download PDF

Info

Publication number
KR20030003973A
KR20030003973A KR1020010039851A KR20010039851A KR20030003973A KR 20030003973 A KR20030003973 A KR 20030003973A KR 1020010039851 A KR1020010039851 A KR 1020010039851A KR 20010039851 A KR20010039851 A KR 20010039851A KR 20030003973 A KR20030003973 A KR 20030003973A
Authority
KR
South Korea
Prior art keywords
peroxide
patch
sodium
thickness
characterized
Prior art date
Application number
KR1020010039851A
Other languages
Korean (ko)
Other versions
KR100471919B1 (en
Inventor
김지영
김종호
장석윤
윤세영
Original Assignee
주식회사 엘지생활건강
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 엘지생활건강 filed Critical 주식회사 엘지생활건강
Priority to KR20010039851A priority Critical patent/KR100471919B1/en
Publication of KR20030003973A publication Critical patent/KR20030003973A/en
Application granted granted Critical
Publication of KR100471919B1 publication Critical patent/KR100471919B1/en

Abstract

PURPOSE: A patch for whitening teeth in which the thickness of the patch is classified into an upper part and another part, or the upper, medium and lower part and relatively controlled is provided. The patch is more safe because of low content of peroxide and conveniently inserted into the rear part of teeth after folding. CONSTITUTION: The patch for whitening teeth contains peroxide and a peroxide stabilizer as a whitening agent and is characterized by comprising an upper part having a relatively thin thickness and intermediate and lower part having a thick thickness. The peroxide is one or more selected from the group consisting of hydrogen peroxide, carbamide peroxide, calcium peroxide, sodium percarbonate, sodium perborate and tetrasodium pyrophosphate peroxide and the peroxide stabilizer is one or more selected from the group consisting of alkyl aryl sulfonate, alkyl sulfonate, alkyl carboxylate, alkyl diphenyl oxide disulfonate and Span(Span 60; sorbitan stearate, Span 80; sorbitan oleate, Span 85; sorbitan trioleate).

Description

유연한 치아 미백 용 패취{FLEXIBLE PATCHES FOR TEETH WHITENING} Patch {FLEXIBLE PATCHES FOR TEETH WHITENING} for flexible tooth whitening

본 발명은 치아에 부착하는 것만으로도 치아의 stain을 제거해주고 치아를하얗게 만들어 주는 치아 미백 용 패취에 관한 것이다. The present invention simply by attaching to the teeth also remove the stain of the tooth haejugo about the tooth whitening patch to make the teeth whiter. 더욱 상세하게는 패취의 두께가 부위에 따라 차이가 있고, 특히 가운데 부분이 상대적으로 두꺼워서 착용 시 보다 유연하여 편리할 뿐 아니라, 잇몸에 닿는 부위에 미백제의 양이 상대적으로 적어서 안전하며, 치아의 뒷부분에 접어 넣는 부분도 얇아서 사용감이 좋고, 이물감이 적은 치아 미백 용 패취이다. More specifically, there are differences in the thickness of the patch according to the site, in particular the center portion is relatively thick as well as convenient to more flexible when worn, the amount of the whitening agent and relatively write down safety to where they lie in the gum, the back of the teeth FIG into thin good feeling to the folded portion, this discomfort is a patch for tooth whitening less.

최근 단기간에 미백 효과를 볼 수 있으면서도 비용 면에서나 사용이 편리한 non-tray type의 치아 부착제에 대한 신제형 특허들이 많이 출원 되고 있다. Yet to see the latest whitening effect in the short term use all cost a lot sinjehyeong are being filed patents for teeth attached to the convenience of non-tray type. 특히 피엔지(Procter & Gamble) 사에서는 미국 특허 제 5,879,691, 제 5,891,453호, 제 5,989,569, WO 98/55044에서 마우스트레이를 사용하는 대신에 얇고 투명하며 유연성이 좋은 폴리에틸렌 스트립(Polyethylene Strip)에 치아 미백제로 프로페셔날 화이트닝 겔이나 이와 비슷한 처방을 pre-coating 시키거나 사용 전에 치아나 스트립에 직접 도포한 후 부착하는 치아 미백제 전달 시스템(delivery system)을 제시하고 있다. In particular pienji (Procter & Gamble) Inc. U.S. Patent No. 5,879,691, No. 5,891,453, 1 - 5,989,569, a transparent thin, instead of using the mouse tray in WO 98/55044 and in professional tooth whitening agent in the Good polyethylene strip (Strip Polyethylene) Flexibility the page syeonal whitening gel or something similar prior to prescribing pre-coating or used directly after application to the teeth or tooth whitening strips attached to the delivery system (delivery system) has been proposed. 마우스트레이를 사용하지 않아서 사용상의 간편성은 개선되었고, 착용 시 투명하고 얇아서 일상 생활에 지장이 없는 것이 큰 장점이지만, 실시 예 등에서 볼 수 있듯이 주요 gelling agent로 카보폴을 다량 사용한 점도(viscosity)가 높은 겔(Gel)을 flexible한 폴리에틸렌 스트립에 균일한 두께로 얇게 pre-coating 시킨 것으로 치아 뒷부분에 접어 넣어서 고정시키는 과정에서 불편하고 이물감이 크며, 잇몸에 자극을 줄 수 있는 문제점을 안고 있다. Because they do not use a mouse tray usage simplicity has been improved and transparent when worn and thin, but it is a big advantage not interfere with daily life, performed as can be seen in for example the main gelling agent with high viscosity (viscosity) with a large amount of Carbopol in the large gel process in which foreign body sensation and discomfort (gel) fixed put aside to the rear teeth to be thin at a uniform thickness on a flexible polyethylene strip having a pre-coating, it suffers the problem that may cause irritation to the gums.

WO 00/54699 에서는 스트립과 미백제를 치아에 더 잘 접촉시키기 위한 스트립의 더 나은 형태에 대해 특허를 출원하였다. In WO 00/54699 a patent was filed for the better in the form of a strip for better contact with the strip and the whitening agent to the teeth. 가장 큰 특징은 치아의 경우 4개의앞니와 2개의 송곳니를 가지고 있는 데 스트립이 양 옆의 송곳니의 끝부분을 덮지는 않는 것을 특징으로 한다. The biggest feature is characterized in that it does not cover the four incisors and canines of the two ends of the strips on each side of having a case of canine teeth. 스트립이 송곳니의 끝부분을 덮을 경우 사용자가 스트립을 쉽게 치아에 굴곡에 따라 붙이기 힘들고, 스트립이 충분한 시간 동안 치아에 붙어 있지 못하는 단점이 있기 때문이라고 한다. If the strip covering the tip of the canine user hard paste, depending on the curvature of the strip to the teeth easily, and that is a disadvantage because the strip does not stick to the teeth for a sufficient period of time. 그러나 아래 치아의 경우 이 특허에서와 같이 스트립을 사다리꼴 모양으로 만들어서 치아의 뒷부분에 접어 붙이면, 혀가 쉽게 닿게 되어 착용 시 이물감이 클 수 있다. However, the teeth down by making the strip as shown in the patent in a trapezoidal shape at the end of stick folding tooth, the tongue is easily to touch the foreign body sensation may be greater when worn. 사용감면에서는 이렇게 모양에 의해 접착 시간을 확보하는 것보다는 제형의 부위에 따른 두께를 조절하여 주거나 제형에 충분한 접착력과 유연성을 부가하여, 사다리꼴 형태나 송곳니의 끝부분이 덮이지 않도록 형태를 만들지 않더라도 더 편하게 부착할 수 있게 하는 것이 더 바람직하다고 생각된다. Use reduction in even create a form not more so than to secure the bonding time by the appearance jugeona by adjusting the thickness of the portion of the formulation adding a sufficient adhesive strength and flexibility in the formulation, not the end of the trapezoidal shape or canine cover more it is considered that it is better to be able to comfortably attached.

본 발명은 치아 미백 패취의 부위별 두께를 조절하여 충분한 유연성을 가져서 사용감을 개선시키고, 특히 잇몸에 닿을 수 있는 윗부분의 두께를 상대적으로 얇게 하여 잇몸이 고농도의 과산화물과 접촉하는 것을 막고, 충분한 접착력을 주어 패취를 접지 않아도 탈착의 문제는 없지만, 크기가 본인의 치아와 맞지 않아서 치아 뒷부분에 접어 넣어야 할 경우 밑부분을 상대적으로 얇게 하여 쉽게 접히고 이물감을 줄여 주어 보다 편리하게 사용할 수 있는 치아 미백 용 패취를 제공하는 것이다. The present invention is to improve a feeling gajyeoseo sufficient flexibility to adjust the area by the thickness of the teeth whitening patch, especially relatively thin in the upper part of the thickness of which may reach the gum prevents the gum is brought into contact with a high concentration of peroxide, sufficient adhesion given not need to ground the patch is a matter of desorption, size easily folded to a thin bottom relative If you put aside the back teeth did not fit with my teeth patch for that it can be conveniently used more by reducing the discomfort tooth whitening to provide.

도 1은 dry type의 triple layer 구조를 갖는 본 발명의 일 실시 예로 가운데가 두껍고 위 아래 부분이 상대적으로 얇은 경우를 나타낸 것이다. 1 illustrates a case in which the upper and lower portions of the thick and relatively thin, for example of one embodiment of the invention having a triple layer structure of the dry type.

도 2는 dry type의 triple layer 구조를 갖는 본 발명의 일 실시 예로 가운데 부분과 아래 부분이 두껍고 윗부분이 상대적으로 얇은 경우를 나타낸 것이다. 2 illustrates a case in which the upper part of the center of the bottom of a thick example of one embodiment of the invention having a triple layer structure of the dry type is relatively thin.

도 3은 dry type의 double layer 구조를 갖는 본 발명의 일 실시 예로 가운데 부분과 아래 부분이 두껍고 윗부분이 상대적으로 얇은 경우를 나타낸 것이다. 3 illustrates a case in which the upper part of the center of the bottom of a thick example of one embodiment of the invention having a double layer structure of the dry type is relatively thin.

도 4는 dry type의 double layer 구조를 갖는 본 발명의 일 실시 예로 가운데가 두껍고 위 아래 부분이 상대적으로 얇은 경우를 나타낸 것이다. 4 illustrates a case in which the upper and lower portions of the thick and relatively thin, for example of one embodiment of the invention having a double layer structure of the dry type.

도 5는 dry type의 multiple layer 구조를 갖는 본 발명의 일 실시 예로 가운데 부분과 아래 부분이 두껍고 윗부분이 상대적으로 얇은 경우를 나타낸 것이다. 5 illustrates a case in which the upper part of the center of the bottom of a thick example of one embodiment of the invention having a multiple layer structure of the dry type is relatively thin.

도 6은 dry type의 multiple layer 구조를 갖는 본 발명의 일 실시 예로 가운데가 두껍고 위 아래 부분이 상대적으로 얇은 경우를 나타낸 것이다. 6 illustrates a case in which the upper and lower portions of the thick and relatively thin, for example of one embodiment of the invention having a multiple layer structure of the dry type.

본 발명은 치아 미백제로 과산화물을 함유하는 치아 미백용 패취에 있어서패취의 두께를 부위별로 조절하여 미백 효과는 우수하면서, 효율성이 높아 사용감이 개선된 것이다. The present invention, while excellent by controlling the thickness of the patch for each region according to the whitening effect for the tooth whitening patch which contains a peroxide as a tooth whitening agent, but the feeling is improved more efficient. 보다 자세히 설명하면, 위, 가운데, 아래가 동일한 두께의 제형과는 달리, 윗부분에 특히 두께를 상대적으로 얇게 하여 보다 유연해서 굴곡이 심한 치아에도 굴곡에 따라 잘 붙고, 잇몸에 닿는 부위가 상대적으로 얇아서 보다 안전하고 이물감이 적은 것이 특징이다. Than In more detail, upper, center, and otherwise is the and of the same thickness formulations below, by a more flexible and relatively thin, particularly the thickness at the top catch up well in accordance with the bending even under bending teeth, the portion touching the gum relatively thin it is characterized less safe and discomfort.

본 발명의 제품은 dry type이나 wet type 모두 가능하나, 사용감 면에서나 과산화물 안정화 면에서는 dry type이 더욱 바람직하다. One possible product is both dry type or a wet type of the present invention, it is more preferably a dry type in the peroxide stabilizing surface eseona surface feeling. Dry type은, adhesive 층에 친수성 글라스 폴리머를 사용하여 수화 되기 전에는 묻어 나는 것이 없기 때문에 제품의 size가 본인의 것과 맞지 않을 때 손쉽게 위생적인 칼이나 가위로 맞는 size로 조절하여 사용할 수도 있지만, 갖고 다니면서 아무데나 편하게 사용하기 위해서는 패취가 충분한 접착력만 있다면, 조금 작은 것은 문제 없고 조금 클 경우도 치아 뒷부분으로 접어 넣을 수 있다. Dry type will bury until hydrated by using a hydrophilic glass polymer in the adhesive layer I, because it may be used to adjust the size easily fits in a hygienic knife or scissors when the size of the products do not match those of you, but go around having no Anywhere there is a small but sufficient adhesion, a little patch can also put the tooth back in the fold, if not a little larger issues in order to use comfortably. 그러나 이 때 패취의 유연성이 떨어지거나 두께가 두꺼우면 이물감이 클 수 있다. However, the poor flexibility of the patch or the thick, this surface may be larger when the foreign body sensation. 따라서 본 발명은 윗부분만 두께가 상대적으로 얇은 것에 한정되지 않고, 필요에 따라서는 패취의 밑부분도 윗부분과 같이 두께를 얇게 도포하여 쉽게 접어 넣을 수 있게 할 수 있다. Thus, the present invention is not limited to only a relatively thin-walled upper part, if necessary, it is possible to thin the thickness of the coating as shown in the upper part also the bottom of the patch to be able to easily put aside.

패취의 윗부분만 얇고 가운데와 아래 부분이 두꺼운 패취는 윗부분의 두께가 1~300㎛, 바람직하기는 5~100㎛인 것이 본 발명의 목적에 부합하였으며, 가운데와 아래 부분은 두께가 30~500㎛, 바람직하기는 50~200㎛인 것이 본 발명의 목적에 부합하였다. Thin and thick, only the upper part of the patch is the middle and the bottom patch is 300㎛ the thickness of the upper part 1 and, preferably is 5 - 100㎛ of it was consistent with the objective of the present invention, the middle and the bottom has a thickness of 30 ~ 500㎛ to, and preferably in line with the object of the invention that the 50 ~ 200㎛ present.

패취의 윗부분과 아래 부분이 얇고 가운데 부분이 두꺼운 경우는, 반드시 위와 아래의 두께가 동일할 필요는 없지만 윗부분과 아래 부분은 두께가 1~200㎛, 바람직하기는 5~100㎛인 것이 본 발명의 목적에 부합하였으며, 가운데 부분은 두께가 30~400㎛, 바람직하기는 50~200㎛인 것이 본 발명의 목적에 부합하였다. If the top and bottom of the patch is thin, the center of a thick, be above and not have to be the same as the thickness upper part and lower part and below that of the present invention having a thickness of 1 ~ 200㎛, preferably to the 5 ~ 100㎛ was consistent with the objective, the center part was consistent with the objective of the present invention that the 50 ~ 30 ~ 400㎛ 200㎛ preferably, the thickness.

본 발명에서와 같이 dry type으로 할 경우 치아 미백제로 사용하는 과산화물의 경시 안정성이 문제가 되는 데 본 발명에서는 double layer를 갖는 matrix type에 adhesive 층에 접착력과 함께 과산화물을 함유한 제형에서는 과산화물 안정화제를 첨가함으로써 이 문제를 해결하였으며, 더욱 고온에서의 높은 경시 안정성을 갖기 위해서는 triple layer를 갖는 matrix type의 adhesive 층에 접착력을 줄 수 있는 친수성 글라스 폴리머를 과산화물을 첨가하지 않고 함유하고, 그 밑의 약물 층에 과산화물 단독 또는 과산화물 안정화제를 함께 첨가함으로써 이 문제를 해결하였다. When the dry type, as in the invention according to the present invention having the stability with time of peroxide used in the tooth whitening agent is an issue in the formulation containing a peroxide with the adhesion to adhesive layer on a matrix type having a double layer a peroxide stabilizer added by solved this problem, in order to have a high stability with time in the further high temperature and containing no addition of a hydrophilic glass polymer to give adhesion to the adhesive layer of the matrix type having a triple layer peroxide, and the base of the drug layer by the addition of the peroxide alone, or with a peroxide stabilizer it was around this problem.

한편 미백 효과 면에서 볼 때 미백제로 과산화물만 사용 시 자극 때문에 무조건 높은 농도를 사용할 수 없고, 적정 농도 사용 시 tray를 사용하는 전문가용 미백 제품이나 치아에 부착하는 strip 제품의 경우 자연적으로 발생한 stain의 경우는 비교적 단기간인 2주 만에도 미백 효과가 있는 것으로 알려져 있지만, 약물에 의한 형성된 stain이나 흡연에 의해 발생한 것은 6달 정도 사용 시 효과가 있는 것으로 알려져 있다. On the other hand, when viewed in terms of the whitening effect can not be unconditionally high concentrations because of irritation when using peroxide only as a whitening agent, in the case of stain naturally occurring case of strip products that adhere to professional whitening products or teeth that use the tray when using the proper concentration but is known to have whitening effect in a relatively short period of time of two weeks, it is caused by a stain or the smoke formed by drugs known to be effective when used for six months. 본 발명에서는 과산화물만 사용했을 때보다 미백 효과의 증진을 위하여 치아 미백제로 과산화물과 함께 축합 인산염(polyphosphates)을 첨가하여 사용할 수 있다. In the present invention, it may be added to the condensed phosphates (polyphosphates) with a peroxide tooth whitening agent to promote the whitening effect than when using only the peroxide. 그러나 축합 인산염 추가만으로도 원하는 수준의 빠른 미백 반응을 얻을 수 없을 때는 multiple layer로 과산화물 활성화제만 함유하거나, 경우에따라서는 과산화물과 상용성이 떨어지는 축합 인산염을 단독 또는 과산화물 활성화제와 함께 함유하고, 사이에 보호 층을 두고 그 다음 약물 층에 과산화물을 과산화물 활성화제와 함께 또 경우에 따라서 비교적 과산화물과 상용성이 좋은 축합 인산염을 같이 함유하는 것을 특징으로 하는 치아 미백 패취가 더 바람직하다. Between However, in some cases when you can not get the level of the fast whitening response you want just add the condensed phosphate containing only a multiple layer peroxide activator, or contain with sole or peroxide activator peroxide compatible with the falling condensed phosphates, and to leave a protective layer, then the drug layer is a peroxide according to a further case with a peroxide activator and relatively peroxide is more preferably teeth whitening patch, characterized in that the compatibility is contained as a good condensed phosphate.

패취의 경우 크게 wet type과 dry type으로 구별할 수 있는 데, 전자에 해당하는 것이 하이드로겔(hydrogel) 제형이나 부착층에 겔(Gel)이나 용액을 도포나 함침시킨 것으로 제형 내 물이나 습윤제(humectant)의 함량이 높아서 제형의 초기 상태가 wet한 것이 특징이고, 후자는 제형 내 물이나 습윤제(humectant)의 함량이 낮아서 제형의 초기 상태가 dry한 것이 특징이다. For patch significantly wet type and dry type used to distinguish, within the formulation to which is corresponding to the electronic hydrogel (hydrogel) coating or impregnating the gel (Gel) or a solution in the formulation, and the attaching layer was washed with water and a wetting agent (humectant ), and is characterized by a high content of the initial state of the formulation of the wet, the latter are characterized by the initial state of the low content of the formulations in water or wetting agent (humectant) dry formulation. 건조한 피부에 보습이나 기타 약용 성분 전달을 위해서는 유연성이 좋고 수분 함량이 높은 wet type이 바람직하지만, wet type의 경우 일반적으로 접착력이 부족하고, 초기 상태부터 끈적임이 많아서 손으로 원하는 부위에 부착 시 약물이 묻을 수 있다. For a moisturizing and other medicinal ingredients delivered dry skin is good and the moisture content is high wet type is preferably flexible, but adhesion is low in general, if the wet type, and the drug when attached to many this early state sticky hand desired area there can be transferred. 또한 처방에 따라서 지지체 층을 통과해 반대 방향으로 약물이나 미백제가 들어있는 겔이 방출될 수도 있는 문제점이 있다. In addition, there is a problem in that the gel which passes through the support layer contains a drug or a whitening agent in the opposite direction may be emitted in accordance with the prescription. 특히 고농도의 과산화물을 다량의 습윤제를 넣은 겔(Gel)로 도포 시켰을 때 치아의 크기와 굴곡에 맞게 조정하며 부착 시 원하지 않는 부위인 손이나 입술, 잇몸 등에 묻어서 자극을 일으킬 수 있다. Particularly adapted to the size and curvature of the teeth when applied sikyeoteul a high concentration of peroxide in the gel (Gel) into a quantity of wetting agent and muteoseo undesirable when mounting portion of a hand or lips, gums, or the like may cause irritation. 또한 다량의 습윤제가 혀에 묻어서 맛이 없어 사용 시 이물감을 크게 느끼게 된다. Also, I do not have much of a taste on the tongue wetting muteoseo largely feel discomfort during use. 그러나 이러한 wet type의 문제도 패취의 부위별 두께를 다르게 함에 따라 많이 개선될 수 있었다. However, the problem of such a wet type also could be much improved as different cuts of the thickness of the patch. 즉 잇몸에 닿는 부위는 가능한 얇게 하여, 잇몸 자극 정도를 줄이고, 치아의 뒷면에 접어 넣는 부위인 아랫 부분도 얇게 하여 접어 넣을 때 보다 편리하고 이물감이 적게 할 수있다. That is where they lie on the gums is possible to thin, reduce the degree of gum irritation can put aside part of the lower part of the back of the teeth it is also more convenient when you thin by folding and to reduce the discomfort.

더욱 바람직하기는 wet type의 단점도 해결한 dry type을 선택하였다. Further preferably selected the dry type which addresses the disadvantages of the wet type. 본 발명의 dry type 패취는 습한 구강 내에서 충분한 접착력을 가지면서도 dry 하여 착용 시 손이나 기타 여러 곳에 미백제가 묻지 않고 잇몸이나 혀에도 묻지 않아 사용 시 이물감이 적은 것이 큰 장점이 될 수 있다. dry type patch of the present invention is sufficient while maintaining adhesion to dry hands and many other places whitening equip be a great advantage to less discomfort when using do not even ask the gums or tongue in my wet mouth without asking.

이러한 dry type의 패취를 만들기 위해 dry 상태에서는 접착력이 없거나 강도가 약하다가 미백제가 작용하기 원하는 부위에서 적은 양의 물에 의해 수화 되면서 접착력이 생기거나 강해지고 원하는 성분의 방출이 시작되는 폴리머가 필수적으로 필요하다. In the dry state to create a patch of such a dry type, or the adhesive force is weak, the strength as the whitening agent is a polymer that is the release of ingredients is the advent of adhesion or strong desired starting essentially as hydrated by a small amount of water at the desired site to act need. 본 발명에서는 친수성 글라스 폴리머(glass polymer)가 이러한 물성을 갖는 다는 것을 알게 되어 매트릭스 형태의 패취에 접착층(Adhesive)에 주요 폴리머로 친수성 글라스 폴리머(glass polymer)를 사용하였다. In the present invention, it was used as a hydrophilic glass polymer (glass polymer) The hydrophilic polymer-glass (glass polymer) as the main polymer in the patch of a matrix is ​​found that the adhesive (Adhesive) having such physical properties.

Backing은 water-insoluble 하고 water-impermeable한 폴리머를 film former로 사용한 sheet로 치아에 부착 시 잇몸이나 혀에 붙지 않고 침에 의해 패취의 형태가 변형되거나 탈착 되는 것을 막아 주는 역할을 한다. Backing should serve to prevent the deformation in the form of a patch or desorbed by the water-insoluble and water-impermeable needle does not stick to the the gums or tongue, when attached to the tooth with a polymer sheet used as a film former.

치아 미백 패취는 앞에서 언급한 것과 같이 패취의 부위별 두께를 조절함에 따라 사용감 개선 등의 효과 외에 전반적인 두께나 약물을 조절함에 의해 미백 효과를 control 할 수 있으며, 착용 시 과산화물의 산소 방울도 관찰할 수 있어서 사용자가 감성적으로도 미백 효과를 인지할 수 있다. Teeth whitening patch may control the whitening effect by adjusting the overall thickness and the drug in addition to effects such as improved feeling as to adjust the area by the thickness of the patch, as mentioned earlier, can be observed of oxygen drops of wear during peroxide in user it can recognize the degree whitening effect emotionally. 또한 착용 중 표가 나지 않기 때문에 일상 생활에 지장 받지 않을 수 있다. It can also do not interfere with daily life because it is born of the table wear.

본 발명은 Matrix Type 패취로 피부나 점막에 부착하는 것이 아니라 치아의에나멜 층에 부착하여 치아 표면에 미백제를 충분한 시간 동안 공급해 주는 것이 특징이다. The invention is characterized in that, rather than adhering to the skin or mucous membranes in Type Matrix patch adhering to the enamel layer of the tooth for a sufficient time to supply the whitening agent to the tooth surface. 본 발명에서 패취가 치아에 부착되고, Matrix 안의 미백제를 치아의 표면에 방출 할 수 있는 원리는 다음과 같다. The principle being that the patch attached to the teeth by the present invention, can release the whitening agent in the Matrix to the surfaces of the teeth are as follows. 약물 송달학 분야에서, 시간적 경과(time lag)가 있는 경피 송달을 위하여 사용되는 방법 중에 붙인 뒤 일정 시간이 지나 약물이 방출 하게 만든 경피 제제의 예로서 피부에서 발산되는 수분을 이용한 아이디어가 있다. In the field of drug delivery studies, the elapsed time as an example of a transdermal formulation after a certain period of time through the drug is made to emit in the attached method that is used for transdermal delivery with the (time lag) the idea using the moisture emanating from the skin. 즉, 피부 부착면과 약물 저장고 사이에 약물 불투과성 장벽(barrier)를 설치해 놓고 제제를 부착한 후에 피부에서 침입한 수분에 의해 장벽이 수화 되는 것을 이용하여 시간이 경과함에 따라 약물의 투과성을 증가 시킨 것이다. That is, the place to install the drug-impermeable barrier (barrier) between the skin attachment surface and the drug reservoir that increases the permeability of the drug, as used to be the barrier hydrated by the moisture intrusion from the skin after adhesion of the agent over time will be. 이 때 장벽 물질로 사용되는 것은 친수성의 글라스 폴리머(glass polymer)이다. It is used as the barrier material, when the glass polymer (glass polymer) having hydrophilic properties. 본 발명에서는 이러한 기술을 사용하여 Matrix Type의 패취의 Adhesive 층에 친수성 글라스 폴리머를 사용하여 보관 중이나 치아에 부착하기 위해 손으로 만질 때는 미백제의 방출이 일어나지 않다가 치아 표면의 수분에 의해 수화 되기 시작하면서 부착력과 미백제의 방출이 일어나는 것을 특징으로 한다. In the present invention, and starting to use this technology when handling hand to attach to the tooth during storage using a hydrophilic glass polymer in Adhesive layer of the patch of Matrix Type hydration by water in a dental surface emission does not occur in the whitening agent It characterized in that the adhesion and release of the whitening agent occurs. 이러한 글라스 폴리머의 경우 대부분 친수성인 치아 표면과도 접착력이 우수하기 때문에 치아에 충분한 접촉 시간을 확보하기 위해 치아의 뒷부분까지 패취를 접어 넣을 필요도 없다. For these polymers the glass because it is excellent in adhesive strength even with most hydrophilic tooth surface to ensure a sufficient contact time to the tooth it does not need to put aside the patch to the back of the tooth. 또한 잇몸의 경우 닿아도 미량의 미백제를 사용하여 큰 자극은 우려되지 않지만, 원하면 치아에만 닿게 패취를 부착 시 잇몸에는 미백제의 방출이 일어나지 않을 수도 있는 것이 또한 큰 특징이다. In the case of contact with the gums also large stimulation using the whitening agent of the trace is not a concern, if desired at the time of touching only the tooth attachment patch gum is also a great characteristic that the release of the whitening agent may not occur. 따라서 본 발명의 첫번 째 특징은 dry type 패취의 접착 층(Adhesive)에 친수성 글라스 폴리머를 사용하는 것이다. Thus, first aspect of the present invention is to use a hydrophilic glass polymer in the adhesive layer (Adhesive) of the dry type patch.

이러한 목적으로 Matrix Type 패취의 Adhesive 층에 주로 사용된 글라스 폴리머는 폴리 알킬 비닐 에테르-말레인산 공중합체(PVM/MA copolymer, Gantrez AN 119, AN 139, S-97), 폴리 비닐 알코올, 폴리 아크릴 산, Poloxamer 407(Pluronic), 폴리 비닐 피롤리돈-비닐 아세테이트 공중합체(PVP/VA copolymer; Luviskol VA, Plasdone S PVP/VA), 폴리 비닐 피롤리돈(PVP, K-15 ~ K-120), Polyquaterium-11(Gafquat 755N), Polyquaterium-39(Merquat plus 3330), Carbomer (Carbopol), 하이드록시 프로필 메틸 셀룰로오즈, 하이드록시 에틸 셀룰로오즈, 하이드록시 프로필 셀룰로오즈, 젤라틴 (Gelatin), 알긴 산(Sodium Alginate) 단독 또는 이들의 혼합물을 사용될 수 있다. The glass polymer primarily used in Adhesive layer of Matrix Type patch for this purpose are poly alkyl vinyl ether-maleic acid copolymer (PVM / MA copolymer, Gantrez AN 119, AN 139, S-97), polyvinyl alcohol, polyacrylic acid, Poloxamer 407 (Pluronic), polyvinyl pyrrolidone-vinyl acetate copolymer (PVP / VA copolymer; Luviskol VA, Plasdone S PVP / VA), polyvinyl pyrrolidone (PVP, K-15 ~ K-120), Polyquaterium -11 (Gafquat 755N), Polyquaterium-39 (Merquat plus 3330), Carbomer (Carbopol), hydroxypropyl methyl cellulose, hydroxyethyl cellulose, hydroxypropyl cellulose, gelatin (gelatin), algin acid (Sodium alginate) alone or It may be a mixture thereof. 이 들의 용매로는 주로 물, 에탄올 그리고 이들의 혼합비를 조절하여 사용할 수도 있다. The solvent of these may be used in mainly control the water, ethanol and their mixture ratio.

치아 에나멜 패취는 치아에 직접 부착하여 치아의 굴곡에 따라 쉽게 모양이 만들어져야 하기 때문에 충분히 유연해야 한다. Patch enamel is directly attached to the tooth must be sufficiently flexible because it can easily be made in accordance with the shape of the tooth bending. 폴리머에 따라서는 이러한 유연성이 떨어지는 것도 있기 때문에 적당한 가소제를 첨가하기도 하였다. Therefore, the polymer was also adding an appropriate plasticizer because it falls This flexibility. 적당한 가소제는 폴리머의 종류와 그 처방에 따라 차이가 있지만 일반적으로 사용되는 polypropylene glycol, glycerin, polyethylene glycol이며 모두 사용 가능하다. Suitable plasticizers vary depending on the type of polymer and its formulation, but is typically polypropylene glycol, glycerin, polyethylene glycol is used as it is can be used.

상기 치아 에나멜 부착 층에 함유된 치아 미백제는 과산화 수소(hydrogen peroxide), 과산화 요소(carbamide peroxide), 과산화 칼슘(calcium peroxide), 과탄산 나트륨(sodium percarbonate), 과붕산 나트륨(sodium perborate), 과산화피로인산나트륨(tetrasodium pyrophosphate peroxidate) 및 이들의 혼합물로 구성되는 군으로부터 선택하여 사용하였다. The tooth of the tooth whitening agent contained in the enamel adhesion layer is hydrogen peroxide (hydrogen peroxide), hydrogen peroxide urea (carbamide peroxide), calcium peroxide (calcium peroxide), and sodium carbonate (sodium percarbonate), sodium perborate (sodium perborate), peroxide fatigue selected from sodium phosphate (tetrasodium pyrophosphate peroxidate) and the group consisting of and mixtures thereof were used. 피로 인산 나트륨과 과산화 수소의 부가 화합물인 과산화 피로 인산 나트륨(TSPP-H 2 O 2 )은 수용액이나 결정 상태에서 과산화 수소의 성질을 나타내면서 동시에 피로 인산 나트륨 그 자체의 특성을 발휘해 주는 특성이 있다. Sodium phosphate (TSPP-H 2 O 2) Fatigue of peroxide addition compound of sodium with hydrogen peroxide has a fatigue characteristic that exercised at the same time indicating the characteristics of sodium pyrophosphate to the nature of the hydrogen peroxide in aqueous solution or crystalline state itself. 보통의 경우도 피로 인산 나트륨은 과산화 수소가 원래 지니고 있는 성질을 변화 시키지 않으면서 안정화 시킨다. Normally FIG sodium pyrophosphate is stabilized without changing the properties in the hydrogen peroxide originally has. 또한 과산화 수소를 단독으로 사용할 때 나타나는 결점을 방지해 준다. Also it makes it prevent the defects that appear when using hydrogen peroxide alone. 즉 과산화 수소는 금속 촉매(catalase), 자외선, 산화제(oxidase), 가열 처리 등에 의해 분해가 촉진되지만 과산화 피로 인산 나트륨은 이런 모든 것들에 대하여 안정하며 과산화 수소의 원래의 성질과 특성을 발휘해 준다. I.e., hydrogen peroxide gives exercised metal catalyst (catalase), ultraviolet radiation, oxidizing agent (oxidase), heat treatment such as peroxide sodium pyrophosphate is stable for all of these things, and the original characteristics and properties of the hydrogen peroxide, but the decomposition is promoted by. 실제로 액상이나 겔(Gel), 페이스트 상에서 과산화물만 사용했을 때보다 과산화 피로 인산 나트륨은 40℃에서의 과산화물의 경시 안정성이 우수하였다. In fact than when using peroxide only on the liquid phase or the gel (Gel), silver paste sodium fatigue peroxide was excellent in stability with time of peroxide in 40 ℃. 그러나 패취 내에서의 과산화물 안정성은 미백제로 과산화 피로 인산 나트륨을 사용해도 쉽게 얻을 수 없었다. However, the peroxide stability in the patch could not be easily obtained using a sodium peroxide as a whitening agent fatigue.

일반적으로 과산화물은 반응성이 우수하여 제품 내 안정화 시키는 데 어려움이 있지만 특히 폴리머들과는 상용성이 좋지 않은 것으로 알려져 있다. In general, the peroxide is a difficulty in that the stabilized product is excellent in reactivity, but is known to have particularly good from those compatible with the polymer. 이러한 과산화물의 제품 내 안정화는 제품의 형태나 처방과도 관련이 많으며 일반적인 겔(Gel)이나 paste, 용액 상에 대해서는 비교적 과산화물 안정화 관련 특허도 많고, 부분적으로 고온에서 어느 정도의 안정성은 확보할 수 있는 것으로 알려져 있지만 얇게 도포된 겔이나 패취 내에서의 과산화물 안정화는 알려진 기술이 아니며, 본 발명자들의 연구 결과에 의하면 일반적으로 알려진 과산화물 안정화제로는 쉽게 해결될 수 있는 문제가 아니었다. Products within the stabilization of such peroxide are often associated also with the shape and formulation of the product lots of common gel (Gel) or a paste, solution to about a relatively peroxide stabilization patent phase, to some extent the stability of the part at high temperature can be ensured as known, peroxide stability in the patch, a gel or a thin coating is not a known technique, according to the findings of the present inventors peroxide stabilizers generally known was not a problem which can easily be solved.

본 발명자는 패취 내 과산화물의 안정화제를 screening 하던 중 패취의 기본 물성이나 본 발명의 이용 범위에 사용할 수 있는 안정화제를 찾게 되어 본 발명에서의 패취 내 과산화물의 고온에서의 경시 안정성을 상당히 향상시킬 수 있게 되었다. The present inventor to significantly improve the time stability in the patch in the peroxide in this is to find a stabilizer that can be used for basic physical properties and use of the scope of the present invention the patch while trying screening a stabilizer in peroxide patches invention high temperature so it was. 따라서 본 발명의 두 번째 특징은 치아 미백제인 과산화물을 과산화물 안정화제와 함께 사용하는 것이다. Therefore, the second feature of the present invention for use with the tooth whitening agent is a peroxide, a peroxide stabilizer.

과산화물과 상용성이 좋은 안정화제는 알킬 아릴 설포네이트, 알킬 설포네이트 염, 알킬 카르복실레이트 염, 알킬 디페닐 옥사이드 디설포네이트, 스판(Span 60; Sorbitan Stearate, Span 80; Sorbitan Oleate , Span 85; Sorbitan Trioleate) 및 이들의 혼합물로 구성되는 군으로부터 선택되는 것을 사용하였다. Peroxide compatible with a good stabilizing agent is an alkyl aryl sulfonate, alkyl sulfonate salts, alkyl carboxylate salts, alkyl diphenyl oxide di-sulfonate, Span (Span 60; Sorbitan Stearate, Span 80; Sorbitan Oleate, Span 85; It was used which is selected from the group consisting of Sorbitan Trioleate), and mixtures thereof. 더 자세히 설명하면 아래와 같다. In more detail as follows.

본 발명에서는 패취 내 주요 치아 미백제로서 과산화물을 사용하였다. In the present invention, use of peroxide as a whitening agent in the patch main teeth. 그러나 상기 미백제 만으로 패취를 만들었을 때 40℃에서 보관했을 때도 패취 내 과산화물 함량이 시간이 지남에 따라 감소하여 in vitro 미백 효과도 처음보다 많이 떨어지는 것을 확인할 수 있었다. However, even when stored at 40 ℃ when a patch made of only the whitening agent in the patch within the peroxide content decreases over time, it was confirmed that a lot less than the first in vitro whitening effect. 겔(Gel) 형태일 때는 Adhesive와 동일한 과산화물을 함유한 처방의 경우 필름 형성제로 폴리머를 과량 사용한 경우도 별도의 안정화제 없이 과산화물의 손실이 매우 작았고, 다소 과산화물 안정성이 부족한 처방도 일반적인 과산화물 안정화제로 알려진 킬레이팅제 예를 들면 EDTA나 시트르산 나트륨을 소량 첨가함에 의해 원하는 수준의 처방을 얻을 수 있었다. Gel (Gel) form it indicates also the case of using an excess in the case of formulation containing the same peroxide and Adhesive film forming agent polymer was small so the loss of the peroxide without stabilizers, some peroxide stability is prescribed also common peroxide agent known stabilization lacking chelating, for example, the prescription for the desired levels could be obtained by as small amount of EDTA or sodium citrate. 그러나 본 발명에서와 같이 겔(Gel)의 용매를 증발시켜 얻은 시트(sheet) 형태의 패취의 경우 동일한 처방을 사용했더라도 안정화제를 첨가하지 않은 경우에 용액 상태보다도 과산화물의 경시 안정성이 떨어졌을 뿐만 아니라, 용액에서와 같이 킬레이팅제를 첨가해 주었을 때 오히려 첨가하기 전보다도 패취 내 과산화물의 안정성이 떨어진 것을 확인할 수 있었다. However, not only it drops the time stability of the case of sheet (sheet) form of a patch obtained by evaporating the solvent of the gel (Gel) than the solution in the case, even if using the same recipe without the addition of stabilizers peroxide as in the present invention , when given away by adding a chelating agent as in the solution rather than the addition also it was confirmed to inferior in stability of the peroxide in the patch. 또한 과산화물 안정화 효과가 뛰어난 것으로 알려진 Dequest 포스포네이트 류를 패취에 첨가했을 때도 과산화물 안정화 효과는 얻을 수 없었다. In addition, when the peroxide stabilizing effect when added to the Dequest phosphonates acids are known to have excellent stabilizing effect on the peroxide patch has not been obtained.

이와 같이 동일한 조성이 겔(Gel) 또는 액상이냐 시트 상이냐에 따라 처방 내 과산화물 경시 안정성이 다른 이유는 여러 가지로 생각할 수 있지만, 미국 특허 제 4,320,102호에 의하면 과산화물의 경우 금속에 의한 촉매 반응으로 극소량의 금속만 처방에 있어도 굉장히 민감하게 분해되는 특성이 있다고 한다. Thus, the same composition of the gel (Gel) or why liquid yinya sheet yinya to the formula in peroxide stability over time is different in accordance with, but can be considered in many ways, U.S. Patent Nos. According to the 4,320,102 call for peroxide a very small amount by the catalytic reaction by the metal of the metal only and that the characteristics may be degraded very sensitive to the formulation. 즉 1ℓ당 0.1㎎의 철, 0.2㎎의 구리, 0.1㎎의 마그네슘, 0.02㎎의 크롬만 있어도 과산화 수소는 분해된다고 한다. I.e. of 1ℓ per 0.1㎎ iron, 0.2㎎ of copper, magnesium 0.1㎎, even if only the chromium 0.02㎎ hydrogen peroxide is said to be decomposed. 이러한 자료를 근거로 보면 용액 상태나 겔(Gel) 상태에서 용매가 증발되면서 만들어진 시트 형태의 패취의 경우 얇은 두께 안에 높은 함량의 금속들을 함유하게 되고, 표면적이 넓어져서 반응성이 높아 지기 때문에 상대적으로 더욱 과산화물의 경시 안정성이 부족하게 되는 것으로 생각된다. In the basis of this data, if in solution, or gel (Gel) a sheet form of a patch made as solvent evaporates from the state and the contained metal of a high content in the thin-walled, relatively more because so the surface area is expanded it becomes reactive high it is believed that the lack of stability with time of peroxide. 본 발명에서 패취 내 과산화물 안정화제로 사용된 물질들은 주로 계면활성제나 유화제로 이들이 시트 상에서 micelle을 형성하여 과산화물 안정화에 긍정적인 영향을 미친 것으로 생각된다. The material used in the peroxide stabilizer patch in the present invention are thought to be primarily a surfactant or emulsifier in which they form a micelle on a sheet mad a positive effect on the peroxide stabilization. 실제로 용기에 든 겔은 비교적 고온에서의 과산화물 경시 안정성이 우수한 반면 같은 겔 처방이라도 strip에 얇게 도포 시켜서 표면적을 넓게 해 준 후에 경시 안정성을 평가했을 때는 경시 기간에 따라 잔존 과산화물비가 많이 줄어든 것을 확인할 수 있었다. Gel actually somehow the vessel was confirmed when we assess the stability over time after a relatively high even Peroxide storage stability of gel formulation as excellent, whereas in by a thin coating on the strip gave it a wider surface area decreased much residual peroxides ratio depending on the passage of time periods . 그러나 본 발명자는 친수성 글라스 폴리머(glass polymer) 중에서 일부는 과산화물과 상용성이 우수하여 과산화물 안정화제를 첨가하지 않고도 용매의 비율을 적절히 조절함으로써 충분히 안정 할 수 있음을 발견하였다. However, the present inventors have found that a part can be sufficiently stabilized by appropriately adjusting the ratio of the solvent without the addition of the peroxide stabilizer is excellent in compatibility with a peroxide and a hydrophilic glass polymer in (glass polymer). 따라서 본 발명은 과산화물과 과산화물 안정화제를 반드시 같이 사용하는 것에 제한되지는 않는다. Therefore, the present invention is not limited to be used as a peroxide and a peroxide stabilizer. 좀 더 자세히 설명하면 아래와 같다. In more detail as follows.

친수성 글라스 폴리머(glass polymer) 중 폴리 비닐 피롤리돈(PVP, K-15,~ K-120), Polyquaternium-11, Polyquaternium-39, 폴리 비닐 피롤리돈-비닐 아세테이트 공중합체(PVP/VA copolymer)는 물과 에탄올에 모두 잘 녹을 뿐 아니라 과산화물과 상용성이 우수하여 과산화물 안정화제를 첨가하지 않아도 물과 에탄올 비를 9:1 ~ 0:10 으로 조절해 주었을 때 패취 내 과산화물 경시 안정성이 우수함을 보였다. Hydrophilic glass polymers of polyvinylpyrrolidone (PVP, K-15, ~ K-120), Polyquaternium-11, Polyquaternium-39, polyvinyl pyrrolidone of the (glass polymer) - vinyl acetate copolymer (PVP / VA copolymer) is the ratio of water and ethanol do not need the addition of a peroxide stabilizer, as well as all well soluble in the peroxide and excellent compatibility in water and ethanol 9: it shows the patch is excellent in stability with time when peroxide gave adjust 1 to 0:10 . 이러한 과산화물과 폴리 비닐 피롤리돈의 좋은 상용성은 폴리 비닐 피롤리돈과 과산화물의 수소 결함에 의해 complex를 형성함에 의해 안정화됨에 의한 것으로 생각된다. Good compatibility of these peroxide and polyvinylpyrrolidone castle is thought to be due As stabilized by forming a complex with hydrogen defects polyvinylpyrrolidone and peroxide. 또한 Polyquaternium과 같이 quaternary ammonium 구조를 가진 폴리머와 과산화물이 상용성이 좋은 것을 확인할 수 있었다. In addition, a polymer, a peroxide having a quaternary ammonium structure, such as Polyquaternium it was confirmed that good compatibility. 용매를 물과 에탄올의 혼합 용매를 사용한 것은 이들 과산화물과 상용성이 좋은 글라스 폴리머들이 친수성이 매우 커서 release liner나 다른 sheet에 균일하게 도포 되지 않는 데, 용매로 물과 에탄올의 혼합 용매를 사용 시 이러한 문제가 해결되어 균일한 sheet 상을 얻을 수 있기 때문이다. The solvent used for the mixed solvent of water and ethanol, these peroxide compatible with a good glass polymer are hydrophilic so large release liner or to non-uniformly applied to the other sheet, when a solvent is a mixed solvent of water and ethanol such the problem is solved because you can get on a uniform sheet. 따라서, 본 발명의 세 번째 특징은 과산화물과 상용성이 좋은 글라스 폴리머를 사용했을 때 치아 미백제로 과산화물을 사용하고 별도의 과산화물 안정화제 첨가 없이, 제조 시 접착 층 조성에 물과 에탄올 용매 비를 조절하는 것에 의해 고온에서의 과산화물 안정성이 우수한 패취를 만들 수 있다는 것이다. Thus, using a peroxide in the third version of the invention is a tooth whitening agent, when used a peroxide compatible with a good glass polymer and separate the peroxide stability without the agent added, to adjust the water and ethanol solvent ratio in the adhesive layer composition in the manufacture the peroxide stability at a high temperature by being able to make a good patch. 또한 앞에서 과산화물 안정화제를 넣은 패취에서와 같이 패취에 충분한 유연성을 주기위하여 폴리머에 따라서는 적당한 가소제를 첨가 할 수 있다. In addition, according to the earlier polymer to give sufficient flexibility to the patch, such as patch placed in a peroxide stabilizer may be added a suitable plasticizer. 적당한 가소제는 폴리머의 종류와 그 처방에 따라 차이가 있지만 일반적으로 사용되는 polypropylene glycol, glycerin, polyethylene glycol이며 모두 사용 가능하다. Suitable plasticizers vary depending on the type of polymer and its formulation, but is typically polypropylene glycol, glycerin, polyethylene glycol is used as it is can be used.

또한, 본 발명에서는 주요 미백제로 과산화물을 사용하지만 미백 효과의 향상을 위해 미백제로 축합 인산염을 과산화물과 함께 사용하였다. Further, in the present invention using a peroxide as the main whitening agent but it used a condensed phosphate as a whitening agent for improving the bleaching effect with peroxide.

사용된 축합 인산염은 예를 들면 피로 인산 나트륨(tetrasodium pyrophosphate, TSPP), 산성 피로 인산 나트륨(sodium acid pyrophosphate, SAPP), 메타 인산 나트륨(sodium hexametaphosphate, SHMP), 폴리 인산 나트륨(sodium tripolyphosphate, STP), 피로 인산 나트륨칼륨(sodium potassium tripolyphosphate, SKTP), 피로 인산 칼륨(tetrapotassium pyrophosphate, TKPP), 울트라 메타 인산염인 스포릭스(acidic sodium meta-polyphosphate, Sporix), 멀티포스(acidic sodium polyphosphate, Multiphos) 중에서 1종 또는 그 이상을 과산화물과 같이 사용하였다. Condensed phosphates, for example sodium pyrophosphate used (tetrasodium pyrophosphate, TSPP), acidic sodium pyrophosphate (sodium acid pyrophosphate, SAPP), sodium metaphosphate (sodium hexametaphosphate, SHMP), sodium polyphosphate (sodium tripolyphosphate, STP), fatigue 1 kinds from among sodium phosphate, potassium (sodium potassium tripolyphosphate, SKTP), potassium pyrophosphate (tetrapotassium pyrophosphate, TKPP), ultra metaphosphate the spokes Riggs (acidic sodium meta-polyphosphate, Sporix), multi-phosphine (acidic sodium polyphosphate, Multiphos) or more was used as the peroxide. 일반적으로 축합 인산염은 치약에 tartar control 제로 치석 생성 억제나 치석 제거에 효과적인 것으로 알려져 있다. In general, the condensed phosphate is known to be effective in removing tartar control agent or inhibition of plaque generation in plaque toothpaste. 또한, 이들은 금속의 좋은 킬레이팅제로 치아의 stain 중에서 음식물이나 작업 환경 속의 철, 칼슘, 마그네슘 등의 금속에 의해 생성된 치아 stain을 효과적으로 제거할 수 있어서 미백 효과의 향상에 다소 기여할 수 있는 것으로 알려져 있다. In addition, it is known to be able to be able to remove the tooth stain generated by a metal such as in a good chelating agent stain the teeth of the metal food or working conditions in the iron, calcium, and magnesium efficiently rather contribute to the improvement of the bleaching effect . 따라서 본 발명에서 이들 폴리 인산염을 과산화물과 함께 사용했을 때 미백 효과 향상 뿐 아니라 치아와 폴리 인산염의 접촉 시간을 연장해 주어서 치석 형성 억제나 치석 제거에도 효과가 있을 것이 기대된다. Therefore, it is expected that, when used in the present invention these polyphosphates with the peroxide, as well as improved whitening effect be effective in giving extended calculus formation inhibition or plaque removal the contact time between teeth and polyphosphates. 실제로 이들을 함유한 패취 부착 시 치아 표면이나 치아 사이사이가 깨끗해지는 것을 볼 수 있었다. In fact, when a patch attached containing them could be seen between the tooth surface and become the teeth clean.

본 발명에서 메트릭스 형 패취의 Backing 층에 사용 가능한 폴리머는 폴리 비닐 아세테이트, 에틸 셀룰로오즈, 폴리 메틸 메타 크릴레이트, 메타크릴산 공중합체 예를 들면 메타크릴로일 에틸 베타인/메타크릴레이트 공중합체(Yukaformer: 제조 회사 Mitsubishi, Metacryloyl Ethyl Betain/Metacylate Copolymer), 메타 아크릴 공중합체(methacrylic acid copolymers; Eudragit L 100, Eudragit L 12,5, Eudragit L 100-55, Eudragit L 30D-55), 아미노 알킬 메타 아크릴레이트 공중합체(aminoalkyl methacrylate copolymers; Eudragit E 100, Eudragit E 12,5, Eudragit RL 100, Eudragit RL 30D), 셀룰로오즈 아세테이트 프탈레이트 단독 또는 이들의 혼합물이다. Polymers available for Backing layer of a matrix-type patch in the present invention include polyvinyl acetate, ethyl cellulose, polymethyl methacrylate, methacrylic acid copolymer, for example a methacryloyl ethyl betaine / methacrylate copolymer (Yukaformer : manufacturer Mitsubishi, Metacryloyl Ethyl Betain / Metacylate copolymer), methacrylate copolymer (methacrylic acid copolymers; Eudragit L 100, Eudragit L 12,5, Eudragit L 100-55, Eudragit L 30D-55), aminoalkyl methacrylate copolymers (aminoalkyl methacrylate copolymers; Eudragit E 100, Eudragit E 12,5, Eudragit RL 100, Eudragit RL 30D), cellulose acetate phthalate is the sole, or a mixture thereof. 그 외에도 enteric coating 물질로 pH 6 내지 8 사이의 구강 조건 내에서는 녹지 않는 폴리머라면 사용 가능하다. In addition, in the oral cavity conditions between pH 6 to 8 with enteric coating material, if insoluble polymer may be used.

Backing 층도 Adhesive 층과 같은 이유로 여러 가소제를 첨가하여 사용하는 것이 가능하다. Backing layer also is possible to use by the addition of various plasticizers for the following reasons Adhesive layer. 위에서 언급된 가소제(plasticizer)인 propylene glycol, glycerin, polyethylene glycol 외에 사용한 용매에 따라 더 많은 종류의 가소제를 사용하는 것이 가능하며, caster oil, hydrogenated caster oil도 사용할 수 있다. It is possible to use a wider range of plasticizer in accordance with the plasticizer (plasticizer) of propylene glycol, the solvents used in addition to glycerin, polyethylene glycol and the above mentioned, caster oil, hydrogenated caster oil may be used.

또한 본 발명의 패취를 치아에 붙었을 때 화학적, 물리적 작용에 의한 미백 뿐 아니라 눈으로 보기에(visually) 하얗게 보일 수 있도록 Backing 층에 하얀 색 안료인 이산화 티탄(titanium dioxide), 활제(talc), 수산화 인회석(hydroxyapatite), 산화 아연 등을 혼용하여 사용할 수 있으며, 이러한 안료들이 Adhesive 층의 미백제와 상용성이 좋지 않을 때에는 표면 처리된 이산화 티탄을 사용할 수도 있다. In addition, chemical, whitening, as well as in the eye (visually) of titanium dioxide (titanium dioxide) White Pigment to Backing layer to appear white, a lubricant by a physical action (talc) when stuck to the patch of the present invention to a tooth, HA (hydroxyapatite), can be used by mixing the zinc oxide, these pigments may be used are titanium dioxide surface-treated when it is a whitening agent and the compatibility of the Adhesive layer good. 하얀 색 안료 외에 개성에 따라 pearl제나 다양한 색상의 안료를 적용할 수도 있다. In addition to the white color pigment according to the personality may apply pearl pigments Jenna various colors.

본 발명에서 사용된 제형으로는 치약에 적용 시 경시 안정성 문제로 적용하기 힘들었던 효소, 특히 덱스트라나제, 글루코오즈 옥시 다아제 등을 단독 또는 혼합 하여 사용할 수도 있고, 치아 미백에 효과가 있다는 papain도 첨가할 수 있다. In the formulation used in the present invention can be used alone or in combination difficult to apply as storage stability problems when applied to toothpaste enzyme, and in particular index trad xylanase, glucose oxidase kinase, adding even papain that is effective in whitening teeth can do. 구강 질환 치료성 약용으로는 트리클로산(triclosan), 클로로헥시딘 (chlorohexidin), 비타민 E 또는 이의 유도체 그 중에서도 비타민 E 아세테이트, 또는 구취 제거에 효과적인 산화제나 엽록소(chlorophyll) 또는 그의 유도체, 향신료 등이 적용 가능하다. By oral disease therapeutic medicine is subject to the triclosan (triclosan), chloro-hexyl when Dean (chlorohexidin), vitamin E or derivatives thereof In particular, vitamin E acetate, or effective oxidizing agents or chlorophyll to remove bad breath (chlorophyll) or a derivative thereof, spices, etc. It is possible.

이하 본 발명의 바람직한 실시 예를 제시한다. It presents a less preferred embodiment of the present invention. 다만 하기 실시 예들은 본 발명의 이해를 돕기 위한 것 일 뿐 본 발명이 하기 실시 예에 한정되는 것은 아니다. However, the examples are not limited to the embodiment to which the present one only to aid the understanding of the present invention.

실시 예 1 내지 10, 비교 예 1 내지 4 Examples 1 to 10 and Comparative Examples 1 to 4

하기에 기재된 바와 같은 조성으로 실시 예 1 내지 10 및 비교 예 1 내지 4의 치아 미백 용 패취를 제조하였다. To the composition was prepared in the Examples 1 to 10 and Comparative Examples 1 to 4 of the patch for whitening teeth as described.

[실시 예 1] Example 1

제조 후 두께: 윗부분 50㎛, 가운데 부분 115㎛, 아래 부분 50㎛ After manufacturing Thickness: top 50㎛, the middle part 115㎛, under section 50㎛

Adhesive 제조 용액 Adhesive solution prepared

하이드록시 프로필 셀룰로오즈 12%, 에탄올 to 100 Hydroxypropyl cellulose 12% ethanol to 100

약물 층 제조 용액 The drug layer solution is prepared

폴리알킬 비닐 에테르 - 말레인산 공중합체(Gantrez S 97) 12%, 과산화 수소 3%,에탄올 to 100 Poly alkyl vinyl ether-maleic acid copolymer (Gantrez S 97) 12%, 3% hydrogen peroxide, ethanol to 100

Backing 제조 용액 Backing prepared solution

에틸 셀룰로오즈 10%, caster oil 6%, 에탄올 to 100 Ethyl cellulose 10%, caster oil 6%, ethanol to 100

[실시 예 2] Example 2

제조 후 두께: 윗부분 35㎛, 나머지 부분 130㎛ After production thickness: 35㎛ upper, rest 130㎛

Adhesive 제조 용액 Adhesive solution prepared

부착 점착제 층(Contact Adhesive, 1 st layer) 제조 용액 Attaching the pressure-sensitive adhesive layer (Contact Adhesive, 1 st layer) prepared solution

폴리알킬 비닐 에테르 - 말레인산 공중합체(Gantrez S 97) 12%, 글리세린 3%, TKPP 2%, sodium bicarbonate 5%, 물 to 100 Poly alkyl vinyl ether-maleic acid copolymer (Gantrez S 97) 12%, glycerol 3%, TKPP 2%, sodium bicarbonate 5%, water to 100

보호 층(Barrier, 2 nd layer) 제조 용액 The protective layer (Barrier, 2 nd layer) prepared solution

폴리 비닐 알코올 10%, 물 to 100 10% polyvinyl alcohol and water to 100

약물 저장 층(Drug Reservoir, 3 rd layer) 제조 용액폴리 비닐 피롤리돈 15%, 과산화 수소 1.5%, 글리세린 3%, span 80 2%, 물 to 100 Drug storage layer (Drug Reservoir, 3 rd layer) prepared solution of 15% polyvinylpyrrolidone, 1.5% hydrogen peroxide, glycerol 3%, 2% span 80, water to 100

Backing 제조 용액 Backing prepared solution

에틸 셀룰로오즈 8% , Eudragit 5%, caster oil 4%, 에탄올 to 100 Ethyl cellulose 8%, Eudragit 5%, caster oil 4%, of ethanol to 100

[실시 예 3] Example 3

제조 후 두께: 윗부분 80㎛, 가운데 부분 215㎛, 아래 부분 115㎛ After manufacturing Thickness: top 80㎛, the middle part 215㎛, under section 115㎛

Adhesive 제조 용액 Adhesive solution prepared

Polyquaternium-39 10%, 과산화 요소 10%, 프로필렌 글라이콜 50% 물 to 100 Polyquaternium-39 10%, peroxide urea 10%, Propylene glycol 50% Water to 100

Backing 제조 용액 Backing prepared solution

셀룰로오즈 아세테아트 프탈레이트 30%, caster oil 4%, 아세톤 : 에탄올 = 4 : 1 혼합 용액 to 100 Cellulose acetate phthalate Theater 30%, caster oil 4%, acetone: ethanol = 4: 1 mixed solution to 100

[실시 예 4] Example 4

제조 후 두께: 윗부분 15㎛, 가운데 부분 160㎛, 아래 부분 15㎛ After manufacturing Thickness: top 15㎛, the middle part 160㎛, 15㎛ bottom

Adhesive 제조 용액 Adhesive solution prepared

폴리알킬 비닐 에테르 - 말레인산 공중합체(Gantrez S 97) 12%, 과산화 피로 인산 나트륨 6%, Span 85 2%, 물 to 100 Poly alkyl vinyl ether-maleic acid copolymer (Gantrez S 97) 12%, 6% sodium peroxide fatigue, Span 85 2%, water to 100

Backing 제조 용액 Backing prepared solution

에틸 셀룰로오즈 10%, caster oil 6%, 에탄올 to 100 Ethyl cellulose 10%, caster oil 6%, ethanol to 100

[실시 예 5] Example 5

제조 후 두께: 윗부분 60㎛, 가운데 부분 120㎛, 아래 부분 60㎛ After manufacturing Thickness: top 60㎛, the middle part 120㎛, under section 60㎛

Adhesive 제조 용액 Adhesive solution prepared

폴리알킬 비닐 에테르 - 말레인산 공중합체(Gantrez S 97) 12%, 과산화 피로 인산 나트륨 6%, 알킬 아릴 설포네이트(SLS) 10%, NaOH 적당량(pH up to 7), 글리세린 60%, 물 to 100 Poly alkyl vinyl ether-maleic acid copolymer (Gantrez S 97) 12%, 6% sodium peroxide fatigue, alkyl aryl sulfonate (SLS) 10% NaOH appropriate amount (pH up to 7), 60% glycerol, water to 100

Backing 제조 용액 Backing prepared solution

에틸 셀룰로오즈 10%, caster oil 6%, 에탄올 to 100 Ethyl cellulose 10%, caster oil 6%, ethanol to 100

[실시 예 6] Example 6

제조 후 두께: 윗부분 100㎛, 가운데 부분 300㎛, 아래 부분 100㎛ After manufacturing Thickness: top 100㎛, the middle part 300㎛, under section 100㎛

Adhesive 제조 용액 Adhesive solution prepared

폴리알킬 비닐 에테르 - 말레인산 공중합체(Gantrez S 97) 11%, 폴리 비닐 피롤리돈 3%, 과산화 수소 3%, SAPP 4%, 알킬 설포네이트 염 2%, NaOH 적당량(pH up to 7) 물 to 100 Poly alkyl vinyl ether-maleic acid copolymer (Gantrez S 97) 11% polyvinylpyrrolidone 3%, hydrogen peroxide 3% SAPP 4%, 2% alkyl sulfonate salt, NaOH appropriate amount (pH up to 7) Water to 100

Backing 제조 용액 Backing prepared solution

폴리 메틸 메타 아크릴레이트 8%, 아세톤 to 100 Polymethyl methacrylate 8% Acetone to 100

[실시 예 7] Example 7

제조 후 두께: 윗부분 10㎛, 가운데 부분 50㎛, 아래 부분 10㎛ After manufacturing Thickness: top 10㎛, the middle part 50㎛, under section 10㎛

Adhesive 제조 용액 Adhesive solution prepared

Polyquaternium-11 20%, PC 4%, TKPP 4%, 알킬 디페닐 옥사이드 디설포네이트 2%, 물 to 100 Polyquaternium-11 20%, PC 4%, TKPP 4%, alkyl diphenyl oxide di-sulfonate 2%, water to 100

Backing 제조 용액 Backing prepared solution

Eudragit 15%, 프로필렌 글라이콜 5%, 에탄올 to 100 Eudragit 15% Propylene glycol 5% Ethanol to 100

[실시 예 8] Example 8

제조 후 두께: 윗부분 50㎛, 가운데 부분 150㎛, 아래 부분 50㎛ After manufacturing Thickness: top 50㎛, the middle part 150㎛, under section 50㎛

Adhesive 제조 용액 Adhesive solution prepared

폴리 비닐 피롤리돈 10%, 과산화 수소 1.5%, SAPP 2%, 알킬 디페닐 옥사이드 디설포네이트 1%, 글리세린 5%, 물 to 100 Polyvinylpyrrolidone 10%, 1.5% hydrogen peroxide, SAPP 2%, 1% di-alkyl diphenyl oxide sulfonates, glycerol 5% water to 100

Backing 제조 용액 Backing prepared solution

에틸 셀룰로오즈 12%, caster oil 6%, 에탄올 to 100 Ethyl cellulose 12%, caster oil 6%, ethanol to 100

[실시 예 9] Example 9

제조 후 두께: 윗부분 20㎛, 가운데 부분 64㎛, 아래 부분 40㎛ After manufacturing Thickness: top 20㎛, the middle part 64㎛, under section 40㎛

Adhesive 제조 용액 Adhesive solution prepared

폴리 비닐 알코올 12%, 과산화 수소 1.5%, TSPP 3.4%, Span 60 5%, 프로필렌 글리콜 3%, 물 to 100 12% polyvinyl alcohol, 1.5% hydrogen peroxide, 3.4% TSPP, Span 60 5% Propylene glycol 3% Water to 100

Backing 제조 용액 Backing prepared solution

에틸 셀룰로오즈 8%, 셀룰로오즈 아세테이트 프탈레이트 2% 에탄올: 아세톤 = 1 : 4 혼합 용매 to 100 Ethyl cellulose 8%, cellulose acetate phthalate 2% ethanol: acetone = 1: 4 mixed solvent to 100

[실시 예 10] Example 10

제조 후 두께: 윗부분 10㎛, 가운데 부분 50㎛, 아래 부분 10㎛ After manufacturing Thickness: top 10㎛, the middle part 50㎛, under section 10㎛

Adhesive 제조 용액 Adhesive solution prepared

폴리 비닐 피롤리돈 18%, 과산화 수소 1.5%, 에탄올 to 100 Polyvinylpyrrolidone 18%, 1.5% hydrogen peroxide, ethanol to 100

Backing 제조 용액 Backing prepared solution

에틸 셀룰로오즈 10%, Eudragit 2%, caster oil 7%, 에탄올 to 100 Ethyl cellulose 10%, Eudragit 2%, caster oil 7%, of ethanol to 100

[비교 예 1] Comparative Example 1

제조 후 두께: 전체 50㎛ After manufacturing Thickness: Full 50㎛

Adhesive 제조 용액 Adhesive solution prepared

폴리 비닐 피롤리돈 10%, 과산화 수소 1.5%, SAPP 2%, 알킬 디페닐 옥사이드 디설포네이트 1%, 글리세린 5%, 물 to 100 Polyvinylpyrrolidone 10%, 1.5% hydrogen peroxide, SAPP 2%, 1% di-alkyl diphenyl oxide sulfonates, glycerol 5% water to 100

Backing 제조 용액 Backing prepared solution

에틸 셀룰로오즈 10%, caster oil 6%, 에탄올 to 100 Ethyl cellulose 10%, caster oil 6%, ethanol to 100

[비교 예 2] Comparative Example 2

제조 후 두께: 전체 150㎛ After manufacturing Thickness: Full 150㎛

Adhesive 제조 용액 Adhesive solution prepared

폴리 비닐 피롤리돈 10%, 과산화 수소 1.5%, SAPP 2%, 알킬 디페닐 옥사이드 디설포네이트 1%, 글리세린 5%, 물 to 100 Polyvinylpyrrolidone 10%, 1.5% hydrogen peroxide, SAPP 2%, 1% di-alkyl diphenyl oxide sulfonates, glycerol 5% water to 100

Backing 제조 용액 Backing prepared solution

에틸 셀룰로오즈 10%, caster oil 6%, 에탄올 to 100 Ethyl cellulose 10%, caster oil 6%, ethanol to 100

[비교 예 3] [Comparative Example 3]

제조 후 두께: 전체 300㎛ After manufacturing Thickness: Full 300㎛

Adhesive 제조 용액 Adhesive solution prepared

폴리알킬 비닐 에테르 - 말레인산 공중합체(Gantrez S 97) 11%, 폴리 비닐 피롤리돈 3%, 과산화 수소 3%, SAPP 4%, 알킬 설포네이트 염 2%, NaOH 적당량(pH up to 7) 물 to 100 Poly alkyl vinyl ether-maleic acid copolymer (Gantrez S 97) 11% polyvinylpyrrolidone 3%, hydrogen peroxide 3% SAPP 4%, 2% alkyl sulfonate salt, NaOH appropriate amount (pH up to 7) Water to 100

Backing 제조 용액 Backing prepared solution

폴리 메틸 메타 아크릴레이트 8%, 아세톤 to 100 Polymethyl methacrylate 8% Acetone to 100

[비교 예 4] Comparative Example 4

전체 두께: 240㎛ Total thickness: 240㎛

Adhesive 제조 용액 Adhesive solution prepared

Carbopol 12%, 과산화 수소 4.5%, SAPP 0.48%, 글리세린 80%, 물 to 100 Carbopol 12% hydrogen peroxide 4.5% SAPP 0.48%, glycerol 80% and water to 100

Backing 층 Backing layer

폴리에틸렌 strip Polyethylene strip

TKPP; TKPP; tetrapotassium pyrophosphate, SAPP; tetrapotassium pyrophosphate, SAPP; sodium acid pyrophosphate, TSPP; sodium acid pyrophosphate, TSPP; tetrasodium pyrophosphate tetrasodium pyrophosphate

[실험 예 1] Experimental Example 1

패취를 직접 치아에 붙인 후 유연한 정도에 따라 5점 척도로 가장 우수할 때가 5로 가장 나쁠 때는 0으로, 잇몸에 닿을 때 자극을 5점 척도로, 자극이 심하면 5점, 전혀 없으면 0점, 뒤에 접어 넣을 때 이물감을 5점 척도로 이물감이 심하면 5점, 없으면 0으로 평가하여 정리한 것이 표 1이다 0 when then attached a patch directly on the teeth, depending on flexible enough time to best a 5-point scale, worst of 5, irritating it touches the gums with a 5-point scale, severe irritation 5 points, if no 0 points, behind when loading is folded to a Table 1 If the two extreme cases, foreign body sensation, foreign body sensation to the 5-point scale of 5, the evaluation are summarized in 0

유연성 flexibility 잇몸 자극 Gum irritation 뒤에 접어 넣을 때 이물감 When you fold the back discomfort
실시 예 1 Example 1 5 5 0 0 2 2
실시 예 2 Example 2 5 5 2 2 3 3
실시 예 3 Example 3 5 5 3 3 3 3
실시 예 4 Example 4 5 5 1 One 1 One
실시 예 5 Example 5 5 5 2 2 2 2
실시 예 7 Example 7 5 5 0 0 0 0
실시 예 8 Example 8 5 5 0 0 2 2
실시 예 9 Example 9 5 5 1 One 1 One
실시 예 10 Example 10 5 5 0 0 0 0
비교 예 1 Comparative Example 1 4 4 0 0 1 One
비교 예 2 Comparative Example 2 3 3 2 2 3 3
비교 예 3 Comparative Example 3 3 3 3 3 5 5
비교 예 4 Comparative Example 4 4 4 3 3 5 5

표 1에서 볼 수 있듯이 패취의 두께를 부위별로 다르게 한 실시 예의 경우가 전체 두께가 동일한 비교 예의 경우보다 유연성에서 특히 우수하며, 패취의 윗부분이 얇을수록 잇몸에 자극이 적고, 아래 부분이 얇을수록 뒤에 접어 넣을 때 이물감이 적었다. As can be seen in Table 1 and, if carried out by a different thickness of the patches by site example is particularly excellent in flexibility than the total thickness manners same comparison, the more the top of the patch is thin less irritation to the gums, the bottom of the thinner after when you fold the less discomfort. 특히 wet type 이라도 두께에 차이가 있는 실시 예 3과 5가 동일한 두께를 가진 wet type의 비교 예 4보다 접어 넣을 때 이물감이 적었다. In particular, the less foreign body sensation when you fold than Comparative Example 4 of the wet type is wet type, even in Example 3 and 5 there is a difference in thickness having the same thickness.

[실험 예 2] [Example 2]

상기 치아 미백용 패취에 의한 미백 효과는 다음 방법으로 측정하였다. Whitening effect by the above-mentioned tooth whitening patch was measured in the following way.

(1) 오염시킨 하이드록시 아파타이트(HAP) 태블릿 시편 제조 (1) in which a hydroxyapatite (HAP) tablet specimen contamination produced

하이드록시 아파타이트 분말을 IR 프레스로 태블릿을 만든 후 1000℃에서 소결한 후 에폭시 수지로 몰딩하여 수지를 만든 후, 강산으로 표면을 에칭 시킨 후 차, 커피, 철, 뮤신을 녹인 TSB(trypticase soybroth) 용액에 시편을 담갔다가 건조 시키는 과정을 반복하였고, 이 조작을 1주일 계속하여 오염시켰다. Hydroxyapatite after the powder made of the tablet to the IR press after creating the resin molded with an epoxy resin and then sintered at 1000 ℃, then etching the surface with a strong acid difference, TSB (trypticase soybroth) dissolved coffee, iron and mucin solution was immersed in a process of drying the sample repeatedly, the operation was continued for one week by pollution. 오염 시킨 후 시편을 흐르는 물에 칫솔로 가볍게 씻어 주어 물에 의해 녹거나 쉽게 제거되는 오염을 제거해 준 후 실온에서 건조 시켜 주었다. Given lightly washed with a toothbrush under running the sample was contaminated water gave after removing the contaminated melt, which was easily removed by water and dried at room temperature.

(2) 미백 효과 평가 법 (2) Whitening effect Evaluation method

오염시킨 HAP 태블릿 시편의 초기 L값(L은 명도를 나타내며 100 일 때는 white, 0 일 때는 black)을 색차계로 측정하고, 상기 실시 예 및 비교 예에서 제조한 치아 미백 용 패취를 물에 적신 시편에 붙이고, 실제 구강 조건과 비슷하게 해주기 위해 온도를 37℃, 습도를 95%로 세팅 시킨 항온 항습기에 방치한 다음, 일정 시간 후에 패취를 떼어 낸 후 흐르는 물에 가볍게 칫솔로 문질러 준 후 실온에서 건조 시킨 후에 L값을 측정하였다. The initial L value was contaminated HAP tablet specimen (L is black when it indicates 100 days white, 0 represents the brightness) measurement of the color difference to step, and soaked in a tooth whitening patches prepared in Examples and Comparative Examples in water specimen attached, the actual mouth condition and 37 ℃ temperature for now Similarly, humidity was allowed to stand in that thermo-hygrostat set at 95% and then, after after removing the patch gently with running water and dried after gave rubbed with a toothbrush room temperature after a period of time the L value was measured. 패취 붙이기 전후의 L값의 차이인 △L을 계산하였다. Patch, paste were calculating a difference △ L of L values ​​before and after. 그 결과는 아래의 표 2와 같다. The results are shown in Table 2 below.

△L (1 시간) △ L (1 hour) △L (3 시간) △ L (3 hours)
실시 예 6 Example 6 42.00±1.03 42.00 ± 1.03 48.85±2.37 48.85 ± 2.37
실시 예 8 Example 8 32.38±3.44 32.38 ± 3.44 40.00±3.88 40.00 ± 3.88
비교 예 1 Comparative Example 1 19.55±1.71 19.55 ± 1.71 36.00±2.55 36.00 ± 2.55
비교 예 2 Comparative Example 2 31.99±2.87 31.99 ± 2.87 41.08±2.99 41.08 ± 2.99
비교 예 3 Comparative Example 3 42.00±1.03 42.00 ± 1.03 48.85±2.37 48.85 ± 2.37
비교 예 4 Comparative Example 4 14.55±2.41 14.55 ± 2.41 30.35±3.24 30.35 ± 3.24

표 2의 결과에서 볼 수 있는 것은 동일한 미백제를 동일한 중량 비로 함유한 처방의 경우 실제 치아의 stain과 접하는 부분의 두께에 따라서 미백 효과의 차이가 많음을 보인다. It can be seen from the results in Table 2 show that the differences thus plenty whitening effect on the thickness of the portion in contact with the stain of the actual teeth for a prescribed whitening agent containing the same ratio of the same weight. 표 1의 결과와 같이 생각해 보면 패취의 가운데 부분 즉 실제 치아의 stain과 접하는 부분의 두께가 미백 효과와는 관계가 있으며, 어느 정도 두께가 두꺼워야 단시간에 미백 효과를 볼 수 있기 때문에 사용감을 위해서는 윗부분이나 아래 부분은 상대적으로 얇게 하고 가운데 부분만 두껍게 하는 것이 가장 바람직한 것으로 보인다. Consider, as the results in Table 1 In the middle part of the patch, i.e. the thickness of the portion in contact with the stain of the actual teeth and a relationship with the whitening effect, the upper part to the feeling because you can see the whitening effect in a short time be thick to some extent thick and the lower part is relatively thin and it seems to be the most preferred thickened central portion only.

이상에서 살펴 본 바와 같이, 본 발명은 치아 미백 효과가 우수함과 동시에 패취의 두께를 위 부분과 나머지 부분 또는 위, 가운데, 아래 부분으로 나누고 두께를 상대적으로 조절하여 보다 유연하며, 잇몸에 닿게 될 때 과산화물 함량이 낮아 보다 안전하고, 치아 뒤 부분에 접어 넣을 때 편하고 이물감이 적어 사용감이 우수하며 고온에서 패취 내 과산화물 안정성이 우수한 치아 미백 용 패취를 제공하는 데 효과가 있다. As present at from above, the present invention provides a tooth whitening effect is excellent and at the same time above the thickness of the patch portion and the remaining portion or upper, center, and more flexibility to share relatively adjusting the thickness of the bottom, when touching the gums secure than the peroxide content decreases, and comfortable when put on the folded back portion of the tooth discomfort feeling is excellent and there is less effect to provide a patch for the peroxide within the tooth whitening patch stability is excellent at high temperatures.

Claims (15)

  1. 치아에 부착하는 치아 미백 용 패취에 있어서, 미백제로 과산화물과 과산화물 안정화제를 함유하고, 패취의 두께가 윗부분이 상대적으로 얇고, 가운데와 아랫 부분이 상대적으로 두꺼운 것이 특징인 치아 미백용 패취 In the teeth whitening patch for adhering to tooth whitening agent into the peroxide and the peroxide-containing stabilizer, and the thickness of the patch, the upper part is relatively thin, the center and bottom of the patch for a relatively thick characterized by the tooth whitening
  2. 제 1항에 있어서, 과산화물은 과산화 수소(hydrogen peroxide), 과산화 요소(carbamide peroxide), 과산화 칼슘(calcium peroxide), 과탄산 나트륨(sodium percarbonate), 과붕산 나트륨(sodium perborate), 과산화피로인산나트륨 (tetrasodium pyrophosphate peroxidate) 중에서 선택되는 1종 이상임을 특징으로 하는 치아 미백용 패취 The method of claim 1 wherein the peroxide is hydrogen peroxide (hydrogen peroxide), hydrogen peroxide urea (carbamide peroxide), calcium peroxide (calcium peroxide), and sodium carbonate (sodium percarbonate), sodium perborate (sodium perborate), peroxide, sodium pyrophosphate ( tetrasodium pyrophosphate peroxidate) patch for tooth whitening, characterized in that at least one member selected from
  3. 제 1항에 있어서, 과산화물 안정화제는 알킬 아릴 설포네이트, 알킬 설포네이트 염, 알킬 카르복실레이트 염, 알킬 디페닐 옥사이드 디설포네이트, 스판(Span 60; Sorbitan Stearate, Span 80; Sorbitan Oleate , Span 85; Sorbitan Trioleate) 중에서 선택되는 1종 이상임을 특징으로 하는 치아 미백 용 패취 The method of claim 1, wherein the peroxide stabilizer is an alkyl aryl sulfonate, alkyl sulfonate salts, alkyl carboxylate salts, alkyl diphenyl oxide di-sulfonate, Span (Span 60; Sorbitan Stearate, Span 80; Sorbitan Oleate, Span 85 ; Sorbitan Trioleate) patch for tooth whitening, characterized in that at least one member selected from
  4. 제 1항에 있어서, 미백 효과의 증진을 위해 축합 인산염을 추가로 함유하는 것을 특징으로 하는 치아 미백용 패취 The method of claim 1, wherein the patch for tooth whitening, characterized in that it contains in addition a condensed phosphate to promote the whitening effect
  5. 제 4항에 있어서, 축합 인산염은 tetrasodium pyrophosphate(TSPP), sodium acid pyrophosphate(SAPP), sodium hexametaphosphate(SHMP), sodium tripolyphosphate(STP), sodium potassium tripolyphosphate(SKTP), tetrapotassium pyrophosphate(TKPP), acidic sodium metapolyphosphate(Sporix) 중에서 선택되는 1종 이상임을 특징으로 하는 치아 미백용 패취 The method of claim 4 wherein the condensed phosphate is tetrasodium pyrophosphate (TSPP), sodium acid pyrophosphate (SAPP), sodium hexametaphosphate (SHMP), sodium tripolyphosphate (STP), sodium potassium tripolyphosphate (SKTP), tetrapotassium pyrophosphate (TKPP), acidic sodium metapolyphosphate (Sporix) patch for tooth whitening, characterized in that one or more species selected from
  6. 제 1항에 있어서, 패취가 dry type 일 경우, 과산화물이 함유된 adhesive와 backing으로 된 double layer 구조 또는 과산화물이 함유되지 않은 adhesive 층, 과산화물이 함유된 약물 층, backing 층의 triple layer 구조 또는 과산화물 활성화제가 든 adhesive 층, 보호 층, 과산화물이 든 약물 저장 층, 지지체의 multiple layer 구조 중 하나인 것을 특징으로 하는 치아 미백용 패취 The method of claim 1, wherein when the patch is dry type one, a peroxide containing an adhesive and a by backing double layer structure or the adhesive layer peroxide is not contained, the peroxide-containing drug layer, active triple layer structure or a peroxide of the backing layer any adhesive agent layer, a protective layer, the peroxide is any drug storage layer, the patch for tooth whitening, characterized in that one of the multiple layer structure of the support,
  7. 제 1항 내지 제 6항 중 어느 한 항에 있어서, 패취의 윗부분의 두께가 1~300㎛ 이고 패취의 가운데와 아랫부분의 두께가 30~500㎛ 인 것을 특징으로 하는 치아 미백 용 패취 Any one of claims 1 to 6 according to any one of items, and the thickness of the upper part of the patch 1 ~ 300㎛ a patch for tooth whitening, characterized in that the thickness of the middle and bottom of the patch is 30 ~ 500㎛
  8. 제 7항에 있어서, 패취의 윗부분의 두께가 5~100㎛ 이고 패취의 가운데와 아랫 부분의 두께가 50~200㎛ 인 것을 특징으로 하는 치아 미백 용 패취 The method of claim 7, wherein the thickness of the upper portion of patch 5 ~ 100㎛ a patch for tooth whitening, characterized in that the thickness of the middle and bottom of the patch is 50 ~ 200㎛
  9. 치아에 부착하는 치아 미백 용 패취에 있어서, 미백제로 과산화물을 함유하고, 약물 저장 층에 주요기제로 사용하는 폴리머로는 과산화물과 상용성이 좋은 폴리 비닐 피롤리돈-비닐 아세테이트 공중합체(PVP/VA copolymer; Luviskol VA, Plasdone S PVP/VA), 폴리 비닐 피롤리돈(PVP, K-30 ~ K-120), Polyquaterium-11(Gafquat 755N), Polyquaterium-39(Merquat plus 3330)에서 선택되는 1종 이상의 친수성의 글라스 폴리머(glass polymer)를 사용하고, 약물 층 조성에 물과 에탄올 비를 9:1 내지 0:10 으로 조절함으로써 별도의 과산화물 안정화제 첨가 없이 과산화물의 안정성이 확보되며, 패취의 두께가 윗부분이 상대적으로 얇고, 가운데는 두껍고, 아랫 부분이 얇은 것이 특징인 치아 미백용 패취 In the patch for whitening teeth adhering to the teeth, it contains a peroxide as a whitening agent and a polymer used as the main base in the drug storage layer is poly good peroxide compatible with vinyl pyrrolidone-vinyl acetate copolymer (PVP / VA one member selected from Luviskol VA, Plasdone S PVP / VA), polyvinyl pyrrolidone (PVP, K-30 ~ K-120), Polyquaterium-11 (Gafquat 755N), Polyquaterium-39 (Merquat plus 3330); copolymer using more than the glass polymer (glass polymer) of the hydrophilic and the water and ethanol in the drug layer composition ratio 9: 1 to 0:10, and by controlling the stability of the peroxide obtained without additional peroxide stabilizer is added, the thickness of the patch the upper part is relatively thin, the center is thicker, patch for tooth whitening is characterized by a thin bottom portion
  10. 제 9항에 있어서, 과산화물은 과산화 수소(hydrogen peroxide), 과산화 요소(carbamide peroxide), 과산화 칼슘(calcium peroxide), 과탄산 나트륨(sodium percarbonate), 과붕산 나트륨(sodium perborate), 과산화피로인산나트륨 (tetrasodium pyrophosphate peroxidate) 중에서 선택되는 1종 이상임을 특징으로 하는 치아 미백용 패취 The method of claim 9, wherein the peroxide is hydrogen peroxide (hydrogen peroxide), hydrogen peroxide urea (carbamide peroxide), calcium peroxide (calcium peroxide), and sodium carbonate (sodium percarbonate), sodium perborate (sodium perborate), peroxide, sodium pyrophosphate ( tetrasodium pyrophosphate peroxidate) patch for tooth whitening, characterized in that at least one member selected from
  11. 제 9항에 있어서, 미백 효과의 증진을 위해 축합 인산염을 추가로 함유하는 것을 특징으로 하는 치아 미백용 패취 The method of claim 9, wherein the patch for tooth whitening, characterized in that it contains in addition a condensed phosphate to promote the whitening effect
  12. 제 11항에 있어서, 축합 인산염은 tetrasodium pyrophosphate(TSPP), sodium acid pyrophosphate(SAPP), sodium hexametaphosphate(SHMP), sodiumtripolyphosphate(STP), sodium potassium tripolyphosphate(SKTP), tetrapotassium pyrophosphate(TKPP), acidic sodium metapolyphosphate(Sporix) 중에서 선택되는 1종 이상임을 특징으로 하는 치아 미백용 패취 The method of claim 11 wherein the condensed phosphate is tetrasodium pyrophosphate (TSPP), sodium acid pyrophosphate (SAPP), sodium hexametaphosphate (SHMP), sodiumtripolyphosphate (STP), sodium potassium tripolyphosphate (SKTP), tetrapotassium pyrophosphate (TKPP), acidic sodium metapolyphosphate ( patch for tooth whitening, characterized in that one or more species selected from Sporix)
  13. 제 9항에 있어서, 패취가 dry type일 경우 과산화물이 함유된 adhesive와 backing으로 된 double layer 구조 또는 과산화물이 함유되지 않은 adhesive 층, 과산화물이 함유된 약물 층, backing 층의 triple layer 구조 또는 과산화물 활성화제가 든 adhesive 층, 보호 층, 과산화물이 든 약물 저장 층, 지지체의 multiple layer 구조 중 하나인 것을 특징으로 하는 치아 미백용 패취 The method of claim 9, wherein the patch is dry type one, if the peroxide is a cost to the adhesive and the backing-containing double layer structure or the adhesive layer peroxide is not contained, the peroxide is contained the drug layer, triple layer structure or a peroxide active of the backing layer I any adhesive layer, a protective layer, the peroxide is any drug storage layer, the patch for tooth whitening, characterized in that one of the multiple layer structure of the support,
  14. 제 9항 내지 제 13항 중 어느 한 항에 있어서, 패취의 윗부분과 아래 부분의 두께가 1~200㎛ 이고 패취의 가운데 부분의 두께가 30~400㎛ 인 것을 특징으로 하는 치아 미백용 패취 Of claim 9 to claim 13 according to any one of claims, wherein the thickness of the top and bottom of the patch 1 ~ 200㎛ a patch for tooth whitening, characterized in that a 30 ~ 400㎛ thickness of the center of the patch
  15. 제 14항에 있어서, 패취의 윗부분과 아래 부분의 두께가 5~100㎛ 이고 패취의 가운데 부분의 두께가 50~200㎛ 인 것을 특징으로 하는 치아 미백 용 패취 The method of claim 14 wherein the thickness of the top and bottom of the patch 5 ~ 100㎛ a patch for tooth whitening, characterized in that the thickness of the center of the patch of 50 ~ 200㎛
KR20010039851A 2001-07-04 2001-07-04 Flexible patches for teeth whitening KR100471919B1 (en)