KR102620230B1 - 복합시트를 이용한 콘크리트 구조물의 균열보수보강공법 - Google Patents
복합시트를 이용한 콘크리트 구조물의 균열보수보강공법 Download PDFInfo
- Publication number
- KR102620230B1 KR102620230B1 KR1020230015765A KR20230015765A KR102620230B1 KR 102620230 B1 KR102620230 B1 KR 102620230B1 KR 1020230015765 A KR1020230015765 A KR 1020230015765A KR 20230015765 A KR20230015765 A KR 20230015765A KR 102620230 B1 KR102620230 B1 KR 102620230B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- crack repair
- sheet
- crack
- Prior art date
Abstract
본 발명은 복합시트를 이용한 콘크리트 구조물의 균열보수공법에 관한 것으로, 보다 상세하게는 콘크리트 구조물의 벽면 누수균열이나 3mm이상의 대균열에 복합시트를 이용하여 부착시공함으로써 균열보수보강이 가능하고 시공 편의성이 향상되며, 균열보수보강성이 향상되도록 개선된 복합시트를 이용한 콘크리트 구조물의 균열보수보강공법에 관한 것이다.
Description
본 발명은 복합시트를 이용한 콘크리트 구조물의 균열보수보강공법에 관한 것으로, 보다 상세하게는 콘크리트 구조물의 벽면 누수균열이나 3mm이상의 대균열에 복합시트를 이용하여 부착시공함으로써 균열보수보강이 가능하고 시공 편의성이 향상되며, 균열보수보강성이 향상되도록 개선된 복합시트를 이용한 콘크리트 구조물의 균열보수보강공법에 관한 것이다.
콘크리트 구조물은 현대 사회에 가장 많이 사용되고 있는 구조물 형태의 하나이다.
이러한 콘크리트는 구조물은 내구성능이 우수하며, 가격적인 면에서도 저렴한 장점을 가지고 있다.
그렇지만 콘크리트의 재료 고유의 특성상 외부의 충격에 의한 균열이 발생하고, 이를 통하여 외부 빗물 등이 침투함에 따라 콘크리트 구조물의 내구성이 약화되고 노후화를 촉진시키게 된다.
이와 같이 균열은 그 균열이 발생한 위치와 균열의 폭 및 깊이에 따라 콘크리트구조물의 구조적인 안전성에 영향을 미치기도 하고 철근 부식 등을 통한 열화의 원인이 되거나 내구성을 저하시키는 요인이 되기도 한다.
이에, 균열 보수제를 주입시공하여 보수하고 있으나, 종래 주입 보수방식은 보수액이 흘러나오는 것을 방지하기 위해 실링제를 도포하는 작업과, 또한 보수 후에도 설치된 주입핀등을 제거하고, 주입홀을 메꾸는 작업을 실시해야하는 번거로운 문제점이 있다.
또한, 일반적인 에폭시 균열 보수재를 이용하는 경우에는 균열 깊숙한 곳까지 충전되지 않고 습윤 표면에서 부착강도, 인장강도 등이 불량한 한계점도 있다.
본 발명은 상술한 바와 같은 종래 기술상의 제반 문제점들을 감안하여 이를 해결하고자 창출된 것으로, 본 발명의 목적은 콘크리트 구조물의 벽면 누수균열이나 3mm이상의 대균열에 복합시트를 이용하여 부착시공함으로써 균열보수보강이 가능하고 시공 편의성이 향상되며, 균열보수보강성이 향상되도록 개선된 복합시트를 이용한 콘크리트 구조물의 균열보수보강공법을 제공하는 것이다.
본 발명은 상기한 목적을 달성하기 위한 수단으로, 균열부위를 정리한 후 퍼티로 메우는 바탕정리 단계, 정리된 바탕에 프라이머를 도포하는 제1도포단계, 프라이머가 도포된 도포면에 복합시트를 부착하는 시트부착단계, 복합시트가 부착된 상태에서 방수재를 도포하는 제2도포단계, 제2도포단계 후 도장하여 마감하는 도장단계를 포함하는 것을 특징으로 하는 복합시트를 이용한 콘크리트 구조물의 균열보수보강공법을 제공한다.
본 발명에 따르면, 콘크리트 구조물의 벽면 누수균열이나 3mm이상의 대균열에 복합시트를 이용하여 부착시공함으로써 균열보수보강이 가능하고 시공 편의성이 향상되며, 균열보수보강성이 향상되도록 개선된 효과를 얻을 수 있다.
도 1은 본 발명에 따른 균열보수보강공법을 설명하는 플로우챠트이다.
이하에서는, 첨부도면을 참고하여 본 발명에 따른 바람직한 실시예를 보다 상세하게 설명하기로 한다.
본 발명 설명에 앞서, 이하의 특정한 구조 내지 기능적 설명들은 단지 본 발명의 개념에 따른 실시예를 설명하기 위한 목적으로 예시된 것으로, 본 발명의 개념에 따른 실시예들은 다양한 형태로 실시될 수 있으며, 본 명세서에 설명된 실시예들에 한정되는 것으로 해석되어서는 아니된다.
본 발명에 따른 복합시트를 이용한 콘크리트 구조물의 균열보수보강공법은 균열부위를 정리한 후 퍼티로 메우는 바탕정리 단계, 정리된 바탕에 프라이머를 도포하는 제1도포단계, 프라이머가 도포된 도포면에 복합시트를 부착하는 시트부착단계, 복합시트가 부착된 상태에서 방수재를 도포하는 제2도포단계, 제2도포단계 후 도장하여 마감하는 도장단계를 포함한다.
이때, 바탕정리 단계는 시공부위 주변을 청소용 도구나 공구를 이용하여 청소함과 함께 균열부위를 퍼티로 메우는 단계이다.
이 경우, 상기 퍼티는 아크릴퍼티가 바람직하고, 상기 아크릴퍼티 100중량부에 대해, 붕규산유리 5중량부, 디메틸아크릴아마이드 8.5중량부, 카프릭산 5중량부, 10㎛ 입도의 산화세륨 분말 5중량부를 혼합하여 사용할 수 있다.
이 경우, 붕규산유리는 내열충격성이 뛰어나고 화학적내구성이 우수하며 점도를 낮춰 흐름성을 향상시키므로 미세크랙 침투력을 높이기 위해 첨가된다.
그리고, 디메틸아크릴아마이드는 유동성과 흐름성을 증대시키면서 수축방지를 통해 균열을 억제하기 위해 첨가된다.
뿐만 아니라, 카프릭산(Capric Acid)은 기포발생을 억제하면서 흐름성을 증대시켜 균열 보수성을 강화시킨다.
아울러, 10㎛ 입도의 산화세륨 분말은 금속산화물로서 마찰저항을 높여 계면간 층분리 억제력을 증진시킨다.
한편, 상기 제1도포단계는 프라이머를 도포하여 방수성을 강화시키는 단계로서, 상기 프라이머는 DMF(N,N-dimethylformamide) 100중량부에 대해, 하이드로콜로이드 15중량부, 옥틸아크릴아미드 6.5중량부, 4-디아조디페닐아민 바이황산염 6.5중량부, P-페닐아조아닐린 5.5중량부, 에틸렌 비스 스테아마이드 4.5중량부가 혼합되어 형성된다.
이때, DMF는 유기용매로서 높은 용해도, 유전율, 자연적 비양자성, 낮은 휘발성 및 고정안정성을 갖는 특징이 있다.
그리고, 하이드로콜로이드(Hydrocolloid)는 점착성을 높이고, 유연할 뿐만 아니라 고착력, 피막형성력이 강해 유분의 용출을 차단하고, 부착력을 증대시키는 특성이 있다.
뿐만 아니라, 옥틸아크릴아미드(Octylacrylamide)는 탄산칼슘 생성을 억제하여 콘크리트의 중성화를 막고, 수밀화를 높이기 위해 첨가된다.
또한, 4-디아조디페닐아민 바이황산염(4-Diazodiphenylamine sulfate)은 CAS 넘버 4477-28-5에 해당하는 물질로서, 변색을 방지하면서 내화학성과 내약품성을 강화시킨다.
아울러, P-페닐아조아닐린은 소수화에 따른 발수특성은 물론 방수, 방습 특성을 강화시킨다.
나아가, 에틸렌 비스 스테아마이드(Ethylene Bis Stearamide)는 황변을 억제하면서 표면 평활도를 증대시키고, 유분 및 수분, 산소의 용출을 차단하고 크랙을 방지하는 특성이 있다.
다른 한편, 상기 시트부착 단계에서 사용되는 복합시트는 테프론계 부직포 시트이다.
부직포 시트는 부직포 형태로서 나일론이나 폴리에스터와 같은 다공성 고분자의성분의 얇은 막을 화학적으로 결합한 소재이며 평방 센티미터당(㎠) 약 14억개 정도의 홀이 있어 통기성을 유지하면서 수증기 이상의 물은 통과하지 못하도록 차단하는 방수 기능이 뛰어난 시트이다.
특히, 압축성을 부여하여 인장강도와 신도가 향상되므로 부착후 보수 부분을 안정적으로 고정할 수 있다.
이때, 상기 부직포 시트의 표면에는 1-하이드록시-3-메틸벤젠과 메타-크레졸을 1:1의 중량비로 혼합한 혼합물이 스프레이되어 표면 거칠기를 증대시킴으로써 후속하여 도포되는 방수재의 부착력과, 도장의 고정력을 증대시키도록 구성됨이 더욱 바람직하다.
또다른 한편, 상기 제2도포단계는 아크릴계 방수재를 도포하여 방수처리하는 단계이다.
상기 방수재는 복합시트들 사이, 복합시트와 보수면 사이의 틈새를 메워 최종 방수되게 처리하는 도포액이다.
이러한 방수재는 아크릴수지 100중량부에 대해, 무수말레인산 6.5중량부, 소듐파이로설파이트(Sodium Pyrosulfite, NaS2O5)를 8.5중량부, 오르토인산수소나트륨 5.5중량부, 사이클로메티콘 3.5중량부, 나트륨-시트레이트(Na-citrate)와 황산제1철(FeSO4.7H2O)이 2:1의 중량비로 혼합된 혼합물 15중량부를 혼합하여 조성된다.
이때, 무수말레인산(Maleic anhydride)은 수축변형성을 억제하고, 소듐파이로설파이트는 산화를 억제하여 크랙발생과 계면탈락 및 계면 분리를 억제한다.
또한, 오르토인산수소나트륨은 방수면의 내크랙성, 내침식성, 내부식성을 강화시킨다.
그리고, 사이클로메티콘은 자외선에 대한 차단특성을 더욱 더 강화시킨다.
아울러, 나트륨-시트레이트(Na-citrate:Na3C6H5O7)는 방수 착체 형성을 위해 첨가되고, 황산제1철(FeSO4.7H2O)은 용해시 pH가 질산염이나 염산염에 비하여 높기 때문에 pH를 약염기 영역(7~9)으로 조절하여 별도로 pH 조절제(Na2CO3, K2HPO4, KH2PO4 등)을 첨가하지 않고도 콘크리트의 중성화을 막을 수 있다. 즉, 철-시트레이트 킬레이트 화합물을 생성하여 치밀한 조직을 갖는 균일한 방수구조를 갖는다.
이렇게 조성된 방수재를 사용하게 되면, 복합시트의 특성을 100%로 보강 보충할 수 있게 된다.
마지막으로, 도장단계는 바탕면을 도색하는 것으로, 마감재이다.
이와 같이, 본 발명은 콘크리트 구조물의 벽면 누수균열이나 3mm이상의 대균열에 대해 복합시트를 이용하여 부착시공함으로써 균열 보수가 가능하고 시공 편의성이 향상되며, 균열 보수보강성이 향상되게 된다.
Claims (4)
- 균열부위를 정리한 후 퍼티로 메우는 바탕정리 단계, 정리된 바탕에 프라이머를 도포하는 제1도포단계, 프라이머가 도포된 도포면에 복합시트를 부착하는 시트부착단계, 복합시트가 부착된 상태에서 방수재를 도포하는 제2도포단계, 제2도포단계 후 도장하여 마감하는 도장단계를 포함하되,
상기 시트부착단계에서 사용되는 복합시트는 부직포 시트이며, 상기 부직포 시트 표면에는 1-하이드록시-3-메틸벤젠과 메타-크레졸을 1:1의 중량비로 혼합한 혼합물이 스프레이 된 것을 특징으로 하는 복합시트를 이용한 콘크리트 구조물의 균열보수보강공법. - 제1항에 있어서,
상기 바탕정리 단계에서 사용되는 퍼티는, 아크릴퍼티 100중량부에 대해, 붕규산유리 5중량부, 디메틸아크릴아마이드 8.5중량부, 카프릭산 5중량부, 10㎛ 입도의 산화세륨 분말 5중량부를 혼합 조성한 것을 특징으로 하는 복합시트를 이용한 콘크리트 구조물의 균열보수보강공법. - 삭제
- 제1항에 있어서,
상기 제2도포단계에서 도포되는 방수재는 아크릴수지 100중량부에 대해, 무수말레인산 6.5중량부, 소듐파이로설파이트(Sodium Pyrosulfite, NaS2O5)를 8.5중량부, 오르토인산수소나트륨 5.5중량부, 사이클로메티콘 3.5중량부, 나트륨-시트레이트(Na-citrate)와 황산제1철(FeSO4.7H2O)이 2:1의 중량비로 혼합된 혼합물 15중량부를 혼합조성한 것을 특징으로 하는 복합시트를 이용한 콘크리트 구조물의 균열보수보강공법.