KR102510720B1 - Retainer ring used in chemical mechanical polishing apparatus - Google Patents
Retainer ring used in chemical mechanical polishing apparatus Download PDFInfo
- Publication number
- KR102510720B1 KR102510720B1 KR1020210057567A KR20210057567A KR102510720B1 KR 102510720 B1 KR102510720 B1 KR 102510720B1 KR 1020210057567 A KR1020210057567 A KR 1020210057567A KR 20210057567 A KR20210057567 A KR 20210057567A KR 102510720 B1 KR102510720 B1 KR 102510720B1
- Authority
- KR
- South Korea
- Prior art keywords
- retainer ring
- sheet
- polyimide sheet
- polyimide
- glass fiber
- Prior art date
Abstract
CMP(Chemical Mechanical Polishing: 화학적 기계적 연마) 장치에 이용되는 리테이너 링(retainer ring)이 개시된다. 본 발명의 일 실시 예에 따른 CMP 장치에 이용되는 리테이너 링은 상기 CMP 장치의 웨이퍼 캐리어의 하부에 결합되는 프레임 유닛, 상기 프레임 유닛의 하부에 결합되는 제1 폴리이미드 시트(PI sheet), 상기 제1 폴리이미드 시트의 하부에 배치되는 적어도 하나의 유리섬유 시트, 상기 적어도 하나의 유리섬유 시트의 하부에 배치되는 제2 폴리이미드 시트, 상기 제1 폴리이미드 시트의 하면 및 상기 유리섬유 시트의 상면을 접착하기 위한 제1 접착 레이어 및 상기 유리섬유 시트의 하면 및 상기 제2 폴리이미드 시트의 상면을 접착하기 위한 제2 접착 레이어를 포함할 수 있다.A retainer ring used in a chemical mechanical polishing (CMP) device is disclosed. A retainer ring used in a CMP apparatus according to an embodiment of the present invention includes a frame unit coupled to a lower portion of a wafer carrier of the CMP apparatus, a first polyimide sheet coupled to the lower portion of the frame unit, and the first polyimide sheet. At least one glass fiber sheet disposed under a polyimide sheet, a second polyimide sheet disposed under the at least one glass fiber sheet, a lower surface of the first polyimide sheet, and an upper surface of the glass fiber sheet It may include a first adhesive layer for bonding and a second adhesive layer for bonding the lower surface of the glass fiber sheet and the upper surface of the second polyimide sheet.
Description
본 발명은 화학적 기계적 연마 장치에 이용되는 리테이너 링에 대한 것으로, 보다 상세하게는 쿠션력 및 복원력이 향상된 화학적 기계적 연마 장치에 이용되는 리테이너 링에 대한 것이다.The present invention relates to a retainer ring used in a chemical mechanical polishing device, and more particularly, to a retainer ring used in a chemical mechanical polishing device having improved cushioning force and restoring force.
반도체 제조 공정 중 화학적 기계적 연마(Chemical Mechanical Polishing, CMP) 공정은 화학액인 슬러리와 연마 패드를 이용하여 웨이퍼와 화학적 반응을 일으킴과 동시에 기계적인 힘을 웨이퍼에 전달함으로써 웨이퍼를 평탄화하는 공정이다.Among semiconductor manufacturing processes, a chemical mechanical polishing (CMP) process is a process of flattening a wafer by using a chemical slurry and a polishing pad to generate a chemical reaction with a wafer and simultaneously transmit mechanical force to the wafer.
웨이퍼의 연마 과정에서, 웨이퍼 캐리어의 하단에 배치된 리테이너 링은, 웨이퍼 연마 도중 웨이퍼 캐리어로부터 웨이퍼가 이탈되는 것을 방지하는 역할을 한다. 리테이너 링은 일반적으로 웨이퍼 캐리어의 최하단에 위치하는 것으로, 웨이퍼의 측면을 둘러싸는 링 형태이다. 일반적으로 리테이너 링은 사출 및 인서트 사출(insert injection molding) 방식으로 제작되고 있다.During wafer polishing, the retainer ring disposed at the lower end of the wafer carrier serves to prevent the wafer from being separated from the wafer carrier during wafer polishing. The retainer ring is generally located at the bottom of the wafer carrier and has a ring shape surrounding the side of the wafer. In general, retainer rings are manufactured by injection and insert injection molding methods.
본 발명의 배경이 되는 기술의 일 예로, 대한민국 등록특허공보 제10-1304353호(2013.09.11.)는 드레인 홀이 형성된 화학 기계적 연마 장치용 리테이너 링을 개시하고 있다.As an example of the background technology of the present invention, Korean Patent Registration No. 10-1304353 (2013.09.11.) discloses a retainer ring for a chemical mechanical polishing device having a drain hole formed thereon.
기존의 리테이너 링은 웨이퍼의 연마 과정에서 두께가 감소하고 쿠션력이 저하됨으로써 사용횟수가 감소되고 비용이 발생하였다.In the conventional retainer ring, the thickness decreases and the cushioning force decreases during the wafer polishing process, resulting in a decrease in the number of uses and cost.
본 발명은 상술한 문제점을 해결하기 위해 안출된 것으로, 본 발명은 쿠션력, 복원력 및 내열성이 크게 향상되고, 웨이퍼의 연마 시에 발생하는 이물질을 크게 저감할 수 있는 리테이너 링을 제공하는 것을 목적으로 한다.The present invention has been made to solve the above problems, and the present invention is to provide a retainer ring that greatly improves cushioning force, restoring force and heat resistance, and can greatly reduce foreign substances generated during wafer polishing. do.
본 발명의 다양한 실시 예에 따른 CMP(Chemical Mechanical Polishing: 화학적 기계적 연마) 장치에 이용되는 리테이너 링(retainer ring)은, 상기 CMP 장치의 웨이퍼 캐리어의 하부에 결합되는 프레임 유닛, 상기 프레임 유닛의 하부에 결합되는 제1 폴리이미드 시트(PI sheet), 상기 제1 폴리이미드 시트의 하부에 배치되는 적어도 하나의 유리섬유 시트, 상기 적어도 하나의 유리섬유 시트의 하부에 배치되는 제2 폴리이미드 시트, 상기 제1 폴리이미드 시트의 하면 및 상기 유리섬유 시트의 상면을 접착하기 위한 제1 접착 레이어 및 상기 유리섬유 시트의 하면 및 상기 제2 폴리이미드 시트의 상면을 접착하기 위한 제2 접착 레이어를 포함할 수 있다.A retainer ring used in a chemical mechanical polishing (CMP) apparatus according to various embodiments of the present invention includes a frame unit coupled to a lower portion of a wafer carrier of the CMP apparatus and a lower portion of the frame unit. A first polyimide sheet (PI sheet) to be bonded, at least one glass fiber sheet disposed below the first polyimide sheet, a second polyimide sheet disposed below the at least one glass fiber sheet, the first 1 may include a first adhesive layer for bonding the lower surface of the polyimide sheet and the upper surface of the glass fiber sheet, and a second adhesive layer for bonding the lower surface of the glass fiber sheet and the upper surface of the second polyimide sheet. .
본 발명의 다양한 실시 예에 따르면, 리테이너 링의 쿠션력, 복원력 및 내열성이 크게 향상되고, 웨이퍼의 연마 시에 리테이너 링으로부터 발생하는 이물질을 크게 저감할 수 있다.According to various embodiments of the present invention, cushioning force, restoring force, and heat resistance of the retainer ring can be greatly improved, and foreign matter generated from the retainer ring during wafer polishing can be greatly reduced.
도 1은 본 발명의 일 실시 예에 따른 CMP 장치를 도시한다.
도 2는 본 발명의 일 실시 예에 따른 리테이너 링을 도시한다.
도 3은 본 발명의 일 실시 예에 따른 합성수지 층의 사시도이다.
도 4는 본 발명의 일 실시 예에 따른 합성수지 층의 단면도이다.
도 5는 본 발명의 일 실시 예에 따른 합성수지 층에 대한 성능실험 결과이다.
도 6은 본 발명의 다른 실시 예에 따른 합성수지 층의 단면도이다.
도 7은 본 발명의 일 실시 예에 따른 폴리이미드 시트의 단면도이다.
도 8은 본 발명의 다른 실시 예에 따른 폴리이미드 시트의 단면도이다.
도 9는 본 발명의 다른 실시 예에 따른 합성수지 층의 사시도이다.1 shows a CMP apparatus according to an embodiment of the present invention.
2 shows a retainer ring according to one embodiment of the present invention.
3 is a perspective view of a synthetic resin layer according to an embodiment of the present invention.
4 is a cross-sectional view of a synthetic resin layer according to an embodiment of the present invention.
5 is a performance test result for a synthetic resin layer according to an embodiment of the present invention.
6 is a cross-sectional view of a synthetic resin layer according to another embodiment of the present invention.
7 is a cross-sectional view of a polyimide sheet according to an embodiment of the present invention.
8 is a cross-sectional view of a polyimide sheet according to another embodiment of the present invention.
9 is a perspective view of a synthetic resin layer according to another embodiment of the present invention.
이하 첨부된 도면을 참조하여 본 발명의 바람직한 실시 예에 대한 동작원리를 상세히 설명한다. 또한, 발명에 대한 실시 예를 설명함에 있어 관련된 공지 기능 또는 구성에 대한 구체적인 설명이 본 개시의 요지를 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략할 것이다. 그리고 하기에서 사용되는 용어들은 본 발명에서의 기능을 고려하여 정의된 용어들로써, 이는 사용자, 운용자의 의도 또는 관례 등에 따라 달라질 수 있다. 그러므로 사용된 용어들의 정의는 본 명세서 전반에 걸친 내용 및 이에 상응한 기능을 토대로 해석되어야 할 것이다.Hereinafter, the operating principle of a preferred embodiment of the present invention will be described in detail with reference to the accompanying drawings. In addition, when it is determined that a detailed description of a related known function or configuration may obscure the gist of the present disclosure in describing an embodiment of the present invention, the detailed description will be omitted. In addition, the terms used in the following are terms defined in consideration of functions in the present invention, which may vary according to the intention or custom of a user or operator. Therefore, the definitions of the terms used should be interpreted based on the content throughout this specification and the corresponding function.
도 1은 본 발명의 일 실시 예에 따른 CMP 장치를 도시한다.1 shows a CMP apparatus according to an embodiment of the present invention.
도 1을 참조하면, CMP 장치(1)는 기판 캐리어(11), 리테이너 링(12), 턴테이블(13), 연마 패드(또는 CMP 패드)(14) 및 노즐(15)을 포함할 수 있다.Referring to FIG. 1 , a CMP apparatus 1 may include a
기판 캐리어(11)는 후술할 연마 패드(14)의 상면에 기판(예를 들면, 웨이퍼, PCB)을 압착시켜 연마를 수행할 수 있다. The
기판 캐리어(11)는 몸체부(111) 및 구동축(112)을 포함할 수 있다.The
몸체부(111)는 후술할 리테이너 링(12)이 결합될 수 있다. 몸체부(111)는 구동축(112)으로부터의 동력에 의해 회전 및 이동 가능하다.A
리테이너 링(12)은 프레임 유닛(121) 및 합성수지 층(122)을 포함할 수 있다. 또는, 리테이너 링(12)은 합성수지 층(122)만을 가리키는 것으로 정의할 수도 있을 것이다.The
프레임 유닛(121)은 합성수지층(122)이 결합되는 프레임이며, 금속 재질일 수 있다. 프레임 유닛(121)은 상측이 기판 캐리어(11)의 몸체부(111)의 하부에 결합될 수 있다. 이를 위해, 프레임 유닛(121)은 볼트가 체결될 수 있는 관통공 또는 체결부가 형성될 수 있다.The
프레임 유닛(121)은 일체형의 원형 고리 형태일 수 있으나, 실시 예에 따라서는 분할형의 원형 고리 형태일 수도 있다.The
합성수지층(122)은 일 예로, 적어도 하나의 폴리이미드 시트 및 적어도 하나의 유리섬유 시트가 적층될 수 있다. 합성수지층(122)은 일 예로, 프레임 유닛(121)의 하단에 배치되어 하부가 후술할 연마 패드(14)에 접촉될 수 있다. 이 경우, 합성수지층(122)은 웨이퍼를 리테이닝(retaining)할 수 있다.For the
합성수지층(122)의 구성에 대하여는 도 2를 참조하여 상세히 후술한다.The configuration of the
턴테이블(13)은 연마 패드(14)를 소정의 속도로 회전시켜 기판(예를 들어 웨이퍼, PCB)을 연마시킬 수 있다. The
턴테이블(13)은 디스크 형상일 수 있다. 일 예로, 구동축(131)에 의해 구동 모터에 의해 전달되는 동력을 전달받아 회전될 수 있다.The
노즐(15)은 슬러리 공급장치로부터 공급되는 슬러리 용액을 공급한다. 슬러리 용액은 웨이퍼를 화학적으로 평탄화시킬 수 있다.The nozzle 15 supplies a slurry solution supplied from a slurry supply device. The slurry solution can chemically planarize the wafer.
추가적으로, CMP 장치(1)는 패드 컨디셔너를 더 포함할 수 있다. 패드 컨디셔너는 연마 패드(14)가 마모된 경우 연마 패드(14)의 표면을 연삭하여 표면 거칠기(surface roughness)를 일정 수준으로 재생시킬 수 있다. Additionally, the CMP device 1 may further include a pad conditioner. When the
연마 패드(14)는 일정 시간 사용하면 기판과의 마찰에 의해 구비된 돌기 등이 손상될 수 있다. 이 때, 연마 패드(30)는 패드 컨디셔너를 통해서 재생 가능하여 교체되지 않고도 장 기간 사용 가능하다.If the
상술한 CMP 장치(1)는 일반적으로 사용되는 CMP 장치와 실질적으로 동일하거나 유사한 구성요소를 더 포함할 수도 있을 것이다.The above-described CMP device 1 may further include components substantially the same as or similar to those of commonly used CMP devices.
도 2는 본 발명의 일 실시 예에 따른 리테이너 링을 도시한다.2 shows a retainer ring according to one embodiment of the present invention.
도 2를 참조하면, 리테이너 링(12')은 상술한 바와 같이 프레임 유닛(121') 및 합성수지층(122')이 결합된 구성일 수 있다.Referring to FIG. 2 , the retainer ring 12' may have a structure in which the frame unit 121' and the synthetic resin layer 122' are combined as described above.
리테이너 링(12')은 일반적으로 기판 캐리어(11)의 최하단에 위치하며, 기판의 측면을 둘러싸는 링 형태이다. 일 예로, 리테이너 링(12')에는 기판 캐리어(11)의 하단과 볼트 결합을 위한 적어도 하나 이상의 홀이 형성될 수 있다.The retainer ring 12' is generally located at the lowermost end of the
리테이너 링(12')은 기판 캐리어(11)와 함께 이동할 수 있다. 리테이너 링(12')은 기판 캐리어(11)의 중심 축을 기준으로 회전 이동(X 방향) 및 좌우 이동(Y 방향)이 가능하다. 또한, 리테이너 링(12')은 기판에 압력을 가하는 과정에서 상하 이동(Z축)도 가능하다. The retainer ring 12' is movable with the
이하에서, 도 3 내지 도 5를 참조하여 리테이너 링(12')에 포함된 합성수지 층의 구성에 대한 다양한 실시 예에 대해 상세히 설명한다.Hereinafter, various embodiments of the configuration of the synthetic resin layer included in the retainer ring 12' will be described in detail with reference to FIGS. 3 to 5 .
도 3은 본 발명의 일 실시 예에 따른 합성수지 층의 사시도이다.3 is a perspective view of a synthetic resin layer according to an embodiment of the present invention.
도 3을 참조하면, 본 발명의 일 실시 예에 따른 합성수지 층(300)은 복수의 폴리이미드 시트(PI sheet)(301) 및 적어도 하나의 접착 레이어(302)를 포함할 수 있다.Referring to FIG. 3 , a
복수의 폴리이미드 시트(301)는 접착 레이어(302)를 사이에 두어 서로 접착될 수 있다. 복수의 폴리이미드 시트(301)가 3매 이상인 경우에도 복수의 폴리이미드 시트(301) 각각의 사이에는 적어도 둘 이상의 접착 레이어(302)가 배치될 수 있을 것이다.The plurality of
폴리이미드는 300 이상의 고내열성을 가지며 내마모성이 매우 우수하다. 이러한 폴리이미드가 합성수지 층(300)에 사용됨에 따라 연마 과정에서 리테이너 링(122')의 표면 및 모서리 부분의 파단으로 인한 이물 발생이 크게 저감될 수 있다.Polyimide is 300 It has high heat resistance and excellent wear resistance. As such polyimide is used in the
일 예로, 폴리이미드 시트(301)에 포함된 폴리이미드 시트 각각은 5um 내지 250um 두께로 형성될 수 있다.For example, each polyimide sheet included in the
또한, 일 예로, 복수의 폴리이미드 시트(301) 중 최외곽에 배치되는 폴리이미드 시트의 외측 면에는 정전기 발생을 억제하기 위한 대전처리 또는 불소코팅 마감될 수 있다. 여기서, 복수의 폴리이미드 시트(301)의 전면에 대전처리 또는 불소코팅 마감될 수 있음은 물론이다.In addition, as an example, an outer surface of the outermost polyimide sheet among the plurality of
또한, 일 예로, 적어도 하나의 접착 레이어(302)은 상기 리테이너 링의 쿠션 및 복원력을 위해 에폭시, 열가소성 폴리이미드 및 에폭시 고무를 포함할 수 있다.Also, for example, at least one
도 4는 본 발명의 일 실시 예에 따른 합성수지 층의 단면도이다.4 is a cross-sectional view of a synthetic resin layer according to an embodiment of the present invention.
도 4를 참조하면, 본 발명의 일 실시 예에 따른 합성수지 층(400)은 복수의 폴리이미드 시트(401, 402), 적어도 하나의 유리섬유 시트(403) 및 복수의 접착 레이어를 포함할 수 있다. 여기서, 복수의 접착 레이어는 설명의 편의상 도시하지 않았으나, 상술한 접착 레이어(302)와 동일한 내용으로 설명될 수 있을 것이다.Referring to FIG. 4 , a
복수의 폴리이미드 시트(401, 402)는 합성수지층(400)의 외곽에 배치될 수 있다. 일 예로, 제1 폴리이미드 시트(401)는 프레임 유닛의 하부에 결합될 수 있다.The plurality of
적어도 하나의 유리섬유 시트(403)는 제1 폴리이미드 시트(401)의 하부에 배치될 수 있다. 여기서, 적어도 하나의 유리섬유 시트(403)는 복수의 유리섬유 시트가 적층되고, 리테이너 링의 쿠션 및 복원력을 위해 다수의 조밀한 공극이 형성될 수 있다.At least one
또한, 제2 폴리이미드 시트(402)는 적어도 하나의 유리섬유 시트(403)의 하부에 배치될 수 있다.In addition, the
또한, 제1 접착 레이어는 제1 폴리이미드 시트(401) 및 유리섬유 시트(403)의 사이에 배치되어, 제1 폴리이미드 시트(401)의 하면 및 유리섬유 시트(403)의 상면을 접착할 수 있다. 또한, 제2 접착 레이어는 유리섬유 시트(403) 및 제2 폴리이미드 시트(402)의 사이에 배치되어, 유리섬유 시트(403)의 하면 및 제2 폴리이미드 시트(402)의 상면을 접착할 수 있다.In addition, the first adhesive layer is disposed between the
상술한 적어도 하나의 유리섬유 시트(403)는 적어도 하나의 유리섬유 시트가 적층된 형태일 수 있다.The at least one
도 5는 본 발명의 일 실시 예에 따른 합성수지 층에 대한 성능실험 결과이다.5 is a performance test result for a synthetic resin layer according to an embodiment of the present invention.
도 5는 상술한 도 4의 합성수지 층(400)이 포함된 리테이너 링에 대한 성능실험을 수행한 결과를 도시한다.FIG. 5 shows the result of a performance test on the retainer ring including the
여기서, H1은 합성수지 층의 두께, H2는 합성수지 층의 압축시 두께, H3은 합성수지 층에 대한 압축 해제 후의 두께이다. 기존 리테이너 링은 고무 및 섬유 재질의 합성수지 층으로 구성되었으며, 기존 리테이너 링 및 본 발명의 일 실시 예에 따른 리테이너 링의 두께는 동일하도록 설정하였다. 또한, 동일한 조건에서 기존 리테이너 링 및 본 발명의 일 실시 예에 따른 리테이너 링으로 50회의 핫프레스 압축 과정을 수행하였다.Here, H1 is the thickness of the synthetic resin layer, H2 is the thickness of the synthetic resin layer upon compression, and H3 is the thickness of the synthetic resin layer after compression is released. The existing retainer ring is composed of a synthetic resin layer made of rubber and fiber, and the existing retainer ring and the retainer ring according to an embodiment of the present invention have the same thickness. In addition, 50 hot press compression processes were performed with the existing retainer ring and the retainer ring according to an embodiment of the present invention under the same conditions.
도 5를 참조하면, 기존 리테이너 링의 경우 핫프레스 압축 실험 후 두께가 20% 감소하였고 탄력이 떨어졌다. 또한, 기존 리테이너 링의 경우 리테이너 링 상의 위치에 따라 두께 편차가 10% 내지 20% 발생하였다. 즉 제품의 평탄도가 불균일하였다.Referring to FIG. 5 , in the case of the existing retainer ring, the thickness decreased by 20% and the elasticity decreased after the hot press compression test. In addition, in the case of the existing retainer ring, a thickness deviation of 10% to 20% occurred depending on the position on the retainer ring. That is, the flatness of the product was non-uniform.
이에 반해, 본 발명의 일 실시 에에 따른 리테이너 링의 경우 핫프레스 압축 실험 후에도 두께 감소율이 1% 내지 5% 내외로 크게 개선되었다. 또한, 본 발명의 일 실시 예에 따른 리테이너 링의 위치별 두께 편차는 5% 내지 10%로 기존 리테이너 링의 두께 편차보다 크게 개선됨을 확인할 수 있었다.In contrast, in the case of the retainer ring according to one embodiment of the present invention, the thickness reduction rate was greatly improved to about 1% to 5% even after the hot press compression test. In addition, it was confirmed that the thickness deviation of each position of the retainer ring according to the embodiment of the present invention is 5% to 10%, which is greatly improved compared to the thickness deviation of the existing retainer ring.
이에 따라, 본 발명의 일 실시 에에 따른 리테이너 링은 새 제품의 성능을 획기적으로 연장할 수 있으므로, 연마 과정에서의 사용 횟수를 크게 증가시켜 비용 절감을 당성할 수 있다.Accordingly, since the retainer ring according to one embodiment of the present invention can dramatically extend the performance of a new product, cost reduction can be achieved by greatly increasing the number of uses in the polishing process.
도 6은 본 발명의 다른 실시 예에 따른 합성수지 층의 단면도이다.6 is a cross-sectional view of a synthetic resin layer according to another embodiment of the present invention.
도 6을 참조하면, 본 발명의 일 실시 예에 따른 합성수지 층(600)은 복수의 폴리이미드 시트(601, 602, 604, 605), 적어도 하나의 유리섬유 시트(603) 및 복수의 접착 레이어를 포함할 수 있다. Referring to FIG. 6 , a
복수의 폴리이미드 시트(601, 602, 604, 605)는 적어도 하나의 유리섬유 시트(603)을 중심으로 적층될 수 있다.The plurality of
복수의 폴리이미드 시트(601, 602, 604, 605) 각각의 두께는 일반적으로 5um 내지 250um 두께로 생산될 수 있는데, 더 두꺼운 시트가 필요한 경우 상술한 접착제를 이용하여 적층하여 사용할 수 있다.Each of the plurality of
상술한 복수의 폴리이미드 시트(601, 602, 604, 605) 각각 및 적어도 하나의 유리섬유 시트(603) 각각은 서로 접착제(또는 접착 레이어)로 접착될 수 있다. 여기서, 복수의 접착 레이어는 설명의 편의상 도시하지 않았으나, 상술한 접착 레이어(302)와 동일하게 설명될 수 있을 것이다.Each of the plurality of
일 예로, 제1 폴리이미드 시트(602)의 상면에는 적어도 하나의 제3 폴리이미드 시트(601)가 접착제로 접착되고, 제2 폴리이미드 시트(604)의 하면에는 적어도 하나의 제4 폴리이미드 시트(605)가 접착제로 접착될 수 있다.For example, at least one
도 7은 본 발명의 일 실시 예에 따른 폴리이미드 시트의 단면도이다. 도 8은 본 발명의 다른 실시 예에 따른 폴리이미드 시트의 단면도이다.7 is a cross-sectional view of a polyimide sheet according to an embodiment of the present invention. 8 is a cross-sectional view of a polyimide sheet according to another embodiment of the present invention.
도 7을 참조하면, 폴리이미드 시트(700)의 일 면에는 복수의 막대형 돌기(702)가 배치될 수 있다. Referring to FIG. 7 , a plurality of rod-shaped
구체적으로, 폴리이미드 시트(700)는 폴리이미드 레이어(701)에 복수의 막대형 돌기(702)가 배치될 수 있다. 여기서, 막대형 돌기(802)는 폴리이미드로 형성되거나, 레진이 사출되어 형성될 수 있다.Specifically, in the
도 7의 폴리이미드 시트(700)를 참조하면, 복수의 막대형 돌기(702)가 간격 없이 서로 접하도록 형성되었다. Referring to the
도 8을 참조하면, 폴리이미드 시트(800)는 폴리이미드 레이어(801)에 복수의 막대형 돌기(802)가 배치될 수 있다. 이 경우, 복수의 막대형 돌기(802)는 기정의된 간격으로 배치되어, 복수의 막대형 돌기(802)에는 평탄한 면이 형성될 수 있다.Referring to FIG. 8 , a plurality of rod-shaped
이하, 도 9를 참조하여 복수의 막대형 돌기가 배치된 폴리이미드 시트를 포함하는 합성수지 층의 일 예를 상세히 설명한다.Hereinafter, an example of a synthetic resin layer including a polyimide sheet on which a plurality of rod-shaped protrusions are disposed will be described in detail with reference to FIG. 9 .
도 9는 본 발명의 다른 실시 예에 따른 합성수지 층의 사시도이다.9 is a perspective view of a synthetic resin layer according to another embodiment of the present invention.
도 9를 참조하면, 합성수지 층(900)은 복수의 폴리이미드 시트(901, 902), 적어도 하나의 유리섬유 시트(903) 및 복수의 접착 레이어(904, 905)를 포함할 수 있다. 여기서, 도 9는 고리형의 합성수지 층(900)의 적층 구조를 설명하기 위해 합성수지 층(900)의 일부를 도시한 것일 수 있다.Referring to FIG. 9 , a
일 예로, 제1 폴리이미드 시트(901) 및 제2 폴리이미드 시트(902) 중 적어도 하나는 복수의 막대형 돌기가 배치될 수 있다.For example, at least one of the
예를 들면, 제1 폴리이미드 시트(901)의 하면은 제1 방향으로 정렬된 복수의 제1 막대형 돌기가 배치될 수 있다.For example, a plurality of first rod-shaped protrusions aligned in a first direction may be disposed on the lower surface of the
또는, 제2 폴리이미드 시트(902)의 상면은 제2 방향으로 정렬된 복수의 제2 막대형 돌기가 배치될 수 있다. Alternatively, a plurality of second bar-shaped protrusions aligned in a second direction may be disposed on the upper surface of the
또는, 제1 폴리이미드 시트(901)의 하면은 제1 방향으로 정렬된 복수의 제1 막대형 돌기가 배치되고, 제2 폴리이미드 시트(902)의 상면은 제2 방향으로 정렬된 복수의 제2 막대형 돌기가 배치될 수 있다. Alternatively, the lower surface of the
상술한 본 발명의 일 실시 예에서, 도 7과 같이, 복수의 제1 막대형 돌기는 기정의된 제1 간격으로 서로 평행하게 배치되고, 복수의 제2 막대형 돌기는 기정의된 제2 간격으로 서로 평행하게 배치될 수 있다.In one embodiment of the present invention described above, as shown in FIG. 7 , a plurality of first rod-shaped protrusions are disposed parallel to each other at a first predefined interval, and a plurality of second rod-shaped protrusions are arranged at a predefined second interval. can be placed parallel to each other.
제1 막대형 돌기 및 제2 막대형 돌기는 복수의 접착 레이어(904, 905) 내로 침투하여 경화되고, 제1 폴리이미드 시트(901)의 하면에 배치된 복수의 제1 막대형 돌기의 배치 방향 및 제2 폴리이미드 시트(902)의 하면에 배치된 복수의 제2 막대형 돌기의 배치 방향이 서로 직교하도록 형성됨에 따라, 연마 작업 시 리테이너 링이 가혹하게 압착되고 평면의 여러 방향으로 뒤틀림 힘이 발생하더라도 강건하게 형태를 유지할 수 있다.The first bar-like protrusions and the second bar-like protrusions are hardened by penetrating into the plurality of
일 예로, 적어도 하나의 유리섬유 시트(903)의 표면에도 복수의 막대형 돌기 예를 들면, 프리즘 형태의 복수의 막대형 돌기가 배치될 수 있다. 이 경우, 적어도 하나의 유리섬유 시트(903)의 상면에 배치된 복수의 막대형 돌기의 배치 방향과 적어도 하나의 유리섬유 시트(903)의 하면에 배치된 복수의 막대형 돌기의 배치 방향은 서로 직교할 수 있다.For example, a plurality of rod-shaped protrusions, for example, a plurality of prism-shaped rod-shaped protrusions may be disposed on the surface of at least one
상술한 본 발명의 다양한 실시 예에 따르면, 리테이너 링의 쿠션력, 복원력 및 내열성이 크게 향상되고, 웨이퍼의 연마 시에 리테이너 링으로부터 발생하는 이물질을 크게 저감할 수 있다.According to various embodiments of the present invention described above, the cushioning force, restoring force, and heat resistance of the retainer ring can be greatly improved, and foreign substances generated from the retainer ring during wafer polishing can be greatly reduced.
이상으로, 본 발명의 실시 예들이 도시되고 설명되었지만, 당업자는 첨부된 청구항들 및 그에 동등한 것들에 의해 정의되는 바와 같은 본 실시 예의 사상 및 범위를 벗어나지 않고 형태 및 세부 사항들에 있어 다양한 변경이 이루어질 수 있음을 이해할 것이다.While embodiments of the present invention have been shown and described above, those skilled in the art may make various changes in form and detail without departing from the spirit and scope of the present embodiments as defined by the appended claims and equivalents thereto. you will understand that you can
CMP 장치: 1
기판 캐리어: 11
리테이너 링: 12, 12'
턴테이블: 13
연마 패드(또는 CMP 패드): 14
노즐: 15
합성수지 층: 300, 400, 600, 900CMP unit: 1
Substrate carriers: 11
Retainer ring: 12, 12'
Turntables: 13
Abrasive Pads (or CMP Pads): 14
Nozzles: 15
Synthetic Resin Layer: 300, 400, 600, 900
Claims (10)
상기 CMP 장치의 웨이퍼 캐리어의 하부에 결합되는 프레임 유닛;
상기 프레임 유닛의 하부에 결합되는 제1 폴리이미드 시트(PI sheet);
상기 제1 폴리이미드 시트의 하부에 배치되는 적어도 하나의 유리섬유 시트;
상기 적어도 하나의 유리섬유 시트의 하부에 배치되는 제2 폴리이미드 시트;
상기 제1 폴리이미드 시트의 하면 및 상기 유리섬유 시트의 상면을 접착하기 위한 제1 접착 레이어; 및
상기 유리섬유 시트의 하면 및 상기 제2 폴리이미드 시트의 상면을 접착하기 위한 제2 접착 레이어;를 포함하고,
상기 유리섬유 시트는,
복수의 유리섬유 시트가 적층되고,
상기 리테이너 링의 쿠션 및 복원력을 위해 다수의 조밀한 공극이 형성된, 리테이너 링.
In a retainer ring used in a CMP (Chemical Mechanical Polishing) device,
a frame unit coupled to a lower portion of the wafer carrier of the CMP apparatus;
A first polyimide sheet (PI sheet) coupled to the lower portion of the frame unit;
at least one glass fiber sheet disposed under the first polyimide sheet;
a second polyimide sheet disposed under the at least one glass fiber sheet;
a first adhesive layer for bonding the lower surface of the first polyimide sheet and the upper surface of the glass fiber sheet; and
A second adhesive layer for bonding the lower surface of the glass fiber sheet and the upper surface of the second polyimide sheet,
The glass fiber sheet,
A plurality of glass fiber sheets are laminated,
A retainer ring in which a plurality of dense air gaps are formed for cushioning and restoring force of the retainer ring.
상기 제1 접착 레이어 및 상기 제2 접착 레이어는,
상기 리테이너 링의 쿠션 및 복원력을 위해 에폭시, 열가소성 폴리이미드 및 에폭시 고무를 포함하는, 리테이너 링.
According to claim 1,
The first adhesive layer and the second adhesive layer,
A retainer ring comprising epoxy, thermoplastic polyimide and epoxy rubber for cushioning and restoring force of the retainer ring.
상기 제1 폴리이미드 시트의 상면에는 적어도 하나의 제3 폴리이미드 시트가 접착제로 접착되고,
상기 제2 폴리이미드 시트의 하면에는 적어도 하나의 제4 폴리이미드 시트가 접착제로 접착되는, 리테이너 링.
According to claim 1,
At least one third polyimide sheet is bonded to the upper surface of the first polyimide sheet with an adhesive,
At least one fourth polyimide sheet is bonded to the lower surface of the second polyimide sheet with an adhesive.
상기 제1 폴리이미드 시트 내지 상기 제4 폴리이미드 시트는 5um 내지 250um 두께인, 리테이너 링.
According to claim 4,
Wherein the first polyimide sheet to the fourth polyimide sheet have a thickness of 5 um to 250 um, the retainer ring.
상기 제1 폴리이미드 시트의 상면 및 상기 제2 폴리이미드 시트의 하면에는 정전기 발생을 억제하기 위한 대전처리 또는 불소코팅 마감된, 리테이너 링.
According to claim 1,
An upper surface of the first polyimide sheet and a lower surface of the second polyimide sheet are treated with an electrical charge or fluorine coating to suppress generation of static electricity, the retainer ring.
상기 제1 폴리이미드 시트의 하면은 제1 방향으로 정렬된 복수의 제1 막대형 돌기가 배치되고,
상기 제2 폴리이미드 시트의 상면은 제2 방향으로 정렬된 복수의 제2 막대형 돌기가 배치되는, 리테이너 링.
According to claim 1,
On the lower surface of the first polyimide sheet, a plurality of first bar-shaped protrusions aligned in a first direction are disposed,
A retainer ring, wherein a plurality of second rod-shaped protrusions aligned in a second direction are disposed on an upper surface of the second polyimide sheet.
상기 복수의 제1 막대형 돌기는 제1 간격으로 서로 평행하게 배치되고,
상기 복수의 제2 막대형 돌기는 제2 간격으로 서로 평행하게 배치된, 리테이너 링.
According to claim 7,
The plurality of first rod-shaped protrusions are disposed parallel to each other at a first interval,
The retainer ring of claim 1 , wherein the plurality of second bar-like protrusions are disposed parallel to each other at a second interval.
상기 복수의 제1 막대형 돌기 및 상기 복수의 제2 막대형 돌기는 프리즘형인, 리테이너 링.
According to claim 7,
The retainer ring of claim 1 , wherein the plurality of first bar-like projections and the plurality of second bar-like projections are prismatic.
상기 제1 폴리이미드 시트의 하면에 배치된 상기 복수의 제1 막대형 돌기의 배치 방향 및 상기 제2 폴리이미드 시트의 하면에 배치된상기 복수의 제2 막대형 돌기의 배치 방향은 서로 직교하는, 리테이너 링.
According to claim 7,
The arrangement direction of the plurality of first bar-shaped projections disposed on the lower surface of the first polyimide sheet and the arrangement direction of the plurality of second bar-shaped projections disposed on the lower surface of the second polyimide sheet are orthogonal to each other, retainer ring.