KR102365825B1 - A method for manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides and a bracelet connector manufactured by the same - Google Patents

A method for manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides and a bracelet connector manufactured by the same Download PDF

Info

Publication number
KR102365825B1
KR102365825B1 KR1020210133160A KR20210133160A KR102365825B1 KR 102365825 B1 KR102365825 B1 KR 102365825B1 KR 1020210133160 A KR1020210133160 A KR 1020210133160A KR 20210133160 A KR20210133160 A KR 20210133160A KR 102365825 B1 KR102365825 B1 KR 102365825B1
Authority
KR
South Korea
Prior art keywords
bracelet
connector
bracelet connector
manufacturing
tensile reinforcement
Prior art date
Application number
KR1020210133160A
Other languages
Korean (ko)
Inventor
안은경
Original Assignee
안은경
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 안은경 filed Critical 안은경
Priority to KR1020210133160A priority Critical patent/KR102365825B1/en
Application granted granted Critical
Publication of KR102365825B1 publication Critical patent/KR102365825B1/en

Abstract

The present invention relates to a method for manufacturing a bracelet connector and a bracelet connector manufactured thereby and, more specifically, to a method for manufacturing a bracelet connector, which has an overall ㄷ shape and has tensile reinforcement parts formed on both sides thereof to reinforce the strength against tensile force during polishing and having an increased thickness with a reduced thickness of a portion thereof connected to a bracelet chain, thereby minimizing a difference in weight from the conventional bracelet connector and forming a pattern on or adding decorations to an area of the part having the increased thickness, and a bracelet connector manufactured thereby. To this end, according to one embodiment of the present invention, a method for manufacturing a bracelet connector having tensile reinforcement parts formed on both sides thereof comprises: a 3D printing step of forming a bracelet connector-shaped molded article by using a 3D printer; a gypsum mold manufacturing step of fixing the molded article through the 3D printing step and manufacturing a gypsum mold by injecting and curing gypsum; a material melting and injecting step of melting and removing the molded article in the gypsum mold through heating, melting a raw material to be manufactured into a bracelet connector, and injecting the same into the gypsum mold; a curing step of curing the raw material injected into the gypsum mold; a gypsum mold removal step of melting and removing the gypsum mold when the curing is completed; a grinding step of removing the gypsum mold and grinding the cured bracelet connector by using a file; and a polishing step of polishing the grinded bracelet connector.

Description

양측에 인장 보강부가 형성되는 팔찌 연결구 제조 방법 및 이에 의해 제조된 팔찌 연결구{A method for manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides and a bracelet connector manufactured by the same}A method for manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides, and a bracelet connector manufactured thereby

본 발명은 팔찌 연결구 제조방법 및 이에 의해 제조된 팔찌 연결구에 관한 것으로, 보다 상세하게는 전체적으로 'ㄷ'자 형태를 이루는 팔찌 연결구에서 팔찌 체인과 연결되는 부위의 두께를 감소하면서 그 양측에는 연마 작업 시 인장력에 대한 강도를 보강하기 위해 두께를 보강한 인장 보강부가 형성되어 기존 중량과 편차를 최소화 하고, 보강된 두께 부분의 면적에는 무늬를 형성하거나 장식을 부가할 수 있는 팔찌 연결구 제조 방법 및 이에 의해 제조된 팔찌 연결구에 관한 것이다. The present invention relates to a method of manufacturing a bracelet connector and a bracelet connector manufactured thereby, and more particularly, while reducing the thickness of the portion connected to the bracelet chain in the bracelet connector forming a 'C' shape as a whole, both sides are polished during the polishing operation In order to reinforce the strength against tensile force, a tensile reinforcing part with reinforced thickness is formed to minimize deviation from the existing weight, and a method for manufacturing a bracelet connector that can form a pattern or add decorations to the area of the reinforced thickness, and manufactured by the same It is about a bracelet connector that has been used.

일반적으로 팔찌를 제조함에 있어서 체인 형태의 팔찌와 그 양쪽에 연결되는 연결구를 결합하여 탈착 가능하도록 제조한다. In general, in manufacturing a bracelet, a chain-shaped bracelet and a connector connected to both sides are combined to be detachable.

이러한 팔찌는 원료를 용융하여 석고틀을 이용해 성형한 후 석고틀을 제거하여 제조하게 되는데 이때, 성형 과정에서 모서리 부분에 날카로운 부분이나 돌출되는 부분을 연마에 의해 제거한다.These bracelets are manufactured by melting raw materials and molding them using a plaster mold, and then removing the plaster mold. In this case, sharp parts or protruding parts on the corners are removed by grinding during the molding process.

이때, 팔찌를 별도의 고정대에 고정한 후 당겨주면서 줄을 이용해 연마 작업을 수행하는데 팔지 연결구의 양측 부분이 인장력이 가해지면 변형되거나 과도한 힘이 작용하면 끊어지는 문제가 발생하게 된다. At this time, the bracelet is fixed to a separate holder and polished using a file while pulling it, but when tensile force is applied to both sides of the bracelet connector, it is deformed or breaks when excessive force is applied.

관련하여 선행문헌 1(등록특허 10-0802100 체인형 장신구의 잠금장치)에서는 장신구 잠금장치에 있어서 'ㄷ'자 형태를 이루는 연결구의 두께가 일정한 두께로 이루어진 구성이 개시되어 있습니다. In relation to this, Prior Document 1 (Registration Patent No. 10-0802100 Locking Device for Chain-Type Accessories) discloses a configuration in which the thickness of the connector forming the 'C' shape in the accessory locking device has a constant thickness.

이러한 선행문헌 1은 연마 작업 시 인장력이 작용되면 과도한 힘에 의해 변형되거나 파손되는 문제가 발생하게 된다. In this prior document 1, when a tensile force is applied during a polishing operation, a problem occurs in that it is deformed or damaged by an excessive force.

선행문헌 1(등록특허 10-0802100 체인형 장신구의 잠금장치)Prior Document 1 (Registration Patent 10-0802100 Locking device for chain-type ornaments)

본 발명은 상기한 문제점을 해결하기 위해 안출된 것으로서, 팔찌 연결구에서 팔찌 체인과 연결되는 부분의 두께를 줄이면서 길이방향으로 연장되는 양측의 두께를 보강하여 인장 보강부를 형성함에 따라 인장 강도를 보강하여 기존 중량과 편차를 최소화하면서 연마 작업 시 인장력에 의해 팔찌 연결구가 변형되거나 손상되는 것을 방지할 수 있는 양측에 인장 보강부가 형성되는 팔찌 연결구 제조 방법 및 이에 의해 제조된 팔찌 연결구를 제공하는 것을 목적으로 한다. The present invention has been devised to solve the above problems, and by reinforcing the thickness of both sides extending in the longitudinal direction while reducing the thickness of the part connected to the bracelet chain in the bracelet connector, the tensile strength is reinforced by forming the tensile reinforcement part. An object of the present invention is to provide a method for manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides that can prevent the bracelet connector from being deformed or damaged by tensile force during grinding while minimizing deviation from the existing weight, and a bracelet connector manufactured thereby. .

상기한 문제점을 해결하기 위한 본 발명의 일실시예에 따른 양측에 인장 보강부가 형성되는 팔찌 연결구 제조 방법 및 이에 의해 제조된 팔찌 연결구는, 인장 보강부(120)를 포함하는 팔찌 연결구 형상의 성형물을 3D 프린터를 이용하여 성형하는 3D 프린팅 단계(S10), 3D 프린팅 단계(S10)를 통해 성형된 성형물을 고정하고, 석고를 주입하여 경화시킴에 따라 석고틀을 제조하는 석고틀 제조 단계(S20), 석고틀에서 가열을 통해 성형물을 용융하여 제거하고, 팔찌 연결구로 제조할 원료를 용융하여 석고틀로 주입시키는 소재 용융 및 주입 단계(S30), 석고틀로 주입된 원료를 경화시키는 경화 단계(S40), 경화가 완료되면 석고틀을 녹여서 제거하는 석고틀 제거 단계(S50), 석고틀을 제거하고 경화된 팔찌 연결구를 줄을 이용하여 연마하는 연마 단계(S60), 및 연마된 팔찌 연결구에 광택을 부여하는 광택 단계(S70)를 포함하는 것을 특징으로 한다.A method for manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides according to an embodiment of the present invention for solving the above problems, and a bracelet connector manufactured thereby, include a bracelet connector-shaped molding including a tensile reinforcement part 120 . 3D printing step (S10) of molding using a 3D printer, fixing the molded product through the 3D printing step (S10), and injecting and curing gypsum to produce a plaster mold manufacturing step (S20), Melting and removing the molding through heating in the gypsum mold, melting and injecting the raw material to be manufactured by the bracelet connector into the gypsum mold and melting (S30), and curing the raw material injected into the gypsum mold (S40) , when curing is completed, the plaster mold removal step (S50) of melting and removing the plaster mold, a polishing step (S60) of removing the plaster mold and polishing the hardened bracelet connector using a file (S60), and varnishing the polished bracelet connector It is characterized in that it comprises a polishing step (S70).

상기한 방법에 의해 제조되는 것으로, 팔찌의 길이방향 양측에는 두께를 보강하여 인장 강도를 보강하는 인장 보강부(120)가 형성되고, 팔찌 체인과 완결되는 끝부분은 인장 보강부(120)에 비해 얇은 두께로 이루어지는 경량 연결부(130)가 형성되는 것을 특징으로 한다. Manufactured by the above method, tensile reinforcement parts 120 for reinforcing tensile strength by reinforcing thickness are formed on both sides of the bracelet in the longitudinal direction, and the end of the bracelet chain and complete is formed on both sides of the bracelet compared to the tension reinforcement part 120 . It is characterized in that the lightweight connection part 130 made of a thin thickness is formed.

여기서, 상기 인장 보강부(120)에는 무늬나 장식을 선택적으로 적용할 수 있는 장식부(140)가 더 구비된 것을 특징으로 한다. Here, it is characterized in that the tensile reinforcement part 120 is further provided with a decoration part 140 to which a pattern or decoration can be selectively applied.

이때, 상기 장식부(140)는 외측으로 볼록한 타원형이나 외측 양측이 상하 경사진 형상으로 적용되어 장식부(140)의 형상에 따라 선택적으로 무늬나 장식을 적용할 수 있는 것을 특징으로 한다. At this time, the decorative part 140 is characterized in that it is applied in an outwardly convex oval or both sides of the outer side inclined up and down, so that a pattern or decoration can be selectively applied according to the shape of the decorative part 140 .

상기 경량 연결부(130)가 구비되는 위치에 길이방향에서 한쪽 방향으로 볼록하게 곡면을 이루는 곡면형 보강 연결부(150)가 적용되는 것을 특징으로 한다.It is characterized in that the curved reinforcing connection part 150 is applied to the position where the lightweight connection part 130 is provided, which forms a convexly curved surface in one direction in the longitudinal direction.

본 발명의 일실시예에 따른 양측에 인장 보강부가 형성되는 팔찌 연결구 제조 방법 및 이에 의해 제조된 팔찌 연결구는 팔찌를 제조함에 있어서 기존 팔찌 연결구와 중량 편차를 최소화하면서 인장 보강부를 형성하여 연마를 통한 마감 작업 시 인장력에 의해 팔찌 연결구가 변형되거나 손상 및 파손되는 것을 방지할 수 있는 효과가 있다. The method for manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides according to an embodiment of the present invention and the bracelet connector manufactured thereby minimizes the weight deviation from the existing bracelet connector in manufacturing the bracelet, and forms a tensile reinforcement part to finish it through polishing It has the effect of preventing the bracelet connector from being deformed, damaged or broken by tensile force during operation.

도 1은 본 발명의 일실시예에 따른 양측에 인장 보강부가 형성되는 팔찌 연결구 제조 방법의 전체 공정도
도 2는 본 발명의 일실시예에 따른 양측에 인장 보강부가 형성되는 팔찌 연결구 제조 방법에서 연마 단계를 상세히 나타낸 공정도
도 3은 본 발명의 일실시예에 따른 양측에 인장 보강부가 형성되는 팔찌 연결구 제조 방법에서 연마 단계를 나타낸 사시도
도 4는 본 발명의 일실시예에 따른 양측에 인장 보강부가 형성되는 팔찌 연결구 제조 방법에 의해 제조된 팔찌 연결구의 사시도
도 5는 본 발명의 일실시예에 따른 양측에 인장 보강부가 형성되는 팔찌 연결구 제조 방법에 의해 제조된 팔찌 연결구에 장식부가 형성된 상태를 나타낸 사용상태도
도 6은 본 발명의 일실시예에 따른 양측에 인장 보강부가 형성되는 팔찌 연결구 제조 방법에 의해 제조된 팔찌 연결구에 곡면형 보강 연결부가 더 구비된 상태를 나타낸 실시예도1 is an overall process diagram of a method for manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides according to an embodiment of the present invention;
Figure 2 is a process diagram showing in detail the polishing step in the method of manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides according to an embodiment of the present invention;
3 is a perspective view showing a polishing step in a method for manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides according to an embodiment of the present invention;
4 is a perspective view of a bracelet connector manufactured by a method for manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides according to an embodiment of the present invention;
5 is a state diagram showing a state in which decorative parts are formed on a bracelet connector manufactured by a method for manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides according to an embodiment of the present invention;
6 is an embodiment view showing a state in which a curved reinforcing connector is further provided in a bracelet connector manufactured by a method for manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides according to an embodiment of the present invention;

본 발명은 팔찌 연결구 제조 방법 및 이에 의해 제조된 팔찌에 관한 것으로, 특히 팔찌 체인과 연결되는 부분의 두께는 얇게하고 길이방향 양측에는 인장 강도를 높일 수 있는 인장 보강부를 보다 두껍게 형성하여 연마 작업 시 팔찌 연결구 부분이 변형되거나 손상, 파손되는 것을 방지할 수 있는 것을 특징으로 한다.The present invention relates to a method for manufacturing a bracelet connector and a bracelet manufactured thereby. In particular, the thickness of the portion connected to the bracelet chain is thin and the tensile reinforcement parts that can increase the tensile strength are formed thicker on both sides in the longitudinal direction to increase the tensile strength of the bracelet during polishing. It is characterized in that the connector part can be prevented from being deformed, damaged or broken.

이하, 본 발명의 일실시예에 따른 양측에 인장 보강부가 형성되는 팔찌 연결구 제조 방법 및 이에 의해 제조된 팔찌 연결구를 첨부된 도면을 참조하여 상세히 설명한다. Hereinafter, a method for manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides according to an embodiment of the present invention and a bracelet connector manufactured thereby will be described in detail with reference to the accompanying drawings.

도 1은 본 발명의 일실시예에 따른 양측에 인장 보강부가 형성되는 팔찌 연결구 제조 방법의 전체 공정도이다.1 is an overall process diagram of a method for manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides according to an embodiment of the present invention.

도 1을 참조하면, 인장 보강부(120)를 포함하는 팔찌 연결구 형상의 성형물을 3D 프린터를 이용하여 파라핀 필라멘트로 성형하는 3D 프린팅 단계(S10), 3D 프린팅 단계(S10)를 통해 성형된 성형물을 별도의 틀에 고정하고, 석고를 주입하여 경화시킴에 따라 석고틀을 제조하는 석고틀 제조 단계(S20), 석고틀에서 가열을 통해 성형물을 용융하여 제거하고, 팔찌 연결구로 제조할 원료를 용융하여 석고틀로 주입시키는 소재 용융 및 주입 단계(S30), 석고틀로 주입된 원료를 경화시키는 경화 단계(S40), 경화가 완료되면 석고틀을 녹여서 제거하는 석고틀 제거 단계(S50), 석고틀을 제거하고 경화된 팔찌 연결구를 줄을 이용하여 연마하는 연마 단계(S60) 및 연마된 팔찌 연결구에 광택을 부여하는 광택 단계(S70)를 포함하여 이루어진다. Referring to FIG. 1 , a 3D printing step (S10) of forming a bracelet connector-shaped molding including a tensile reinforcement part 120 into a paraffin filament using a 3D printer (S10), a 3D printing step (S10) A plaster mold manufacturing step (S20) of manufacturing a plaster mold by fixing it in a separate mold, injecting and curing the plaster, and melting and removing the molding through heating in the plaster mold, and melting the raw material to be manufactured with a bracelet connector. Melting and injecting the material injected into the gypsum mold (S30), curing the raw material injected into the gypsum mold (S40), removing the gypsum mold by melting and removing the gypsum mold when curing is complete (S50), removing the gypsum mold It is made including a polishing step (S60) of removing and polishing the hardened bracelet connector using a file and a polishing step (S70) of giving a gloss to the polished bracelet connector.

도 2는 본 발명의 일실시예에 따른 양측에 인장 보강부가 형성되는 팔찌 연결구 제조 방법에서 연마 단계를 상세히 나타낸 공정도이다.Figure 2 is a process diagram showing in detail the polishing step in the method for manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides according to an embodiment of the present invention.

도 2를 참조하면, 연마 단계(S60)는 팔찌를 고정대(300)에 고정시키는 고정대 고정 단계(S61)와, 줄(200)에 비산 방지액을 고르게 분사하는 비산 방지액 분무 단계(S62) 및 줄(200)에 비산 방지액이 도포된 상태에서 팔찌의 모서리와 성형 과정에서 발생된 버(burr) 등을 제거하여 마감하는 마감 가공 단계(S63)를 포함하여 이루어진다.Referring to Figure 2, the polishing step (S60) is a fixing step (S61) for fixing the bracelet to the fixing table (300), and an anti-scattering liquid spraying step (S62) and In a state in which the anti-scattering liquid is applied to the file 200, a finishing processing step (S63) of removing and finishing the edges of the bracelet and burrs generated during the molding process is included.

이로 인해 착용 시 이질감이 들거나 날카로운 부분에 의해 피부에 상처가 발생하는 것을 방지하고 착용감을 좋게 할 수 있게 된다. Due to this, it is possible to prevent a feeling of foreignness or damage to the skin due to a sharp part during wearing, and to improve the wearing comfort.

도 3은 본 발명의 일실시예에 따른 양측에 인장 보강부가 형성되는 팔찌 연결구 제조 방법에서 연마 단계를 나타낸 사시도이다.3 is a perspective view illustrating a polishing step in a method for manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides according to an embodiment of the present invention.

도 3을 참조하면, 고정대(300)에 팔찌의 한쪽 끝부분에 구비된 팔찌 연결구(100)를 고정하고, 손으로 당겨준 상태에서 줄(200)을 이용해 연마작업을 한다.Referring to FIG. 3 , the bracelet connector 100 provided at one end of the bracelet is fixed to the holder 300 , and a polishing operation is performed using the file 200 in a state where it is pulled by hand.

여기서 상기 고정대(300)는 팔찌를 올려서 연마할 때 팔찌를 지지하는 고정판(310) 및 상기 고정판(310)에 설치되어 팔찌의 한쪽 끝부분에 연결된 팔찌 연결구(100)를 고정하는 고정 후크(320)를 포함하여 구성된다. Here, the holder 300 is a fixing plate 310 that supports the bracelet when the bracelet is raised and polished, and a fixing hook 320 that is installed on the fixing plate 310 and fixes the bracelet connector 100 connected to one end of the bracelet. is comprised of

도 4는 본 발명의 일실시예에 따른 양측에 인장 보강부가 형성되는 팔찌 연결구 제조 방법에 의해 제조된 팔찌 연결구의 사시도이다.4 is a perspective view of a bracelet connector manufactured by a method for manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides according to an embodiment of the present invention.

도 4를 참조하면, 팔찌 연결구(100)는 전체적으로 'ㄷ'자 형태로 이루어지고 개방된 부분에는 다른 연결구외 체결되는 연결핀(110)이 구비되고, 그 양측으로 인장력에 대한 강도를 보강할 수 있도록 다른 부위에 비해 보다 두껍게 인장 보강부(120)가 구비된다.Referring to FIG. 4 , the bracelet connector 100 is formed in a 'C' shape as a whole, and a connecting pin 110 that is fastened to other connectors is provided in the open portion, and the strength against the tensile force can be reinforced on both sides thereof. The tensile reinforcing part 120 is provided to be thicker than other parts so that it is possible.

그리고 상기 연결핀(110)이 구비된 타측에는 상기 인장 보강부(120)의 보강에 따른 중량 증가로 전체적은 중량을 줄이기 위해 인장 보강부(120)에 비해 얇은 두께의 경량 연결부(130)가 구비된다.And on the other side where the connecting pin 110 is provided, a lightweight connecting portion 130 having a thinner thickness than the tensile reinforcing portion 120 is provided in order to reduce the overall weight due to an increase in weight according to the reinforcement of the tensile reinforcing portion 120 . do.

이때 인장 보강부(120)는 전체적으로 삼각형을 이루거나 타원형 등 3D 프린터에 의해 다양한 형태로 제조 가능하여 다양한 디자인으로 제조할 수 있게 된다.At this time, the tensile reinforcement unit 120 can be manufactured in various designs by a 3D printer such as a triangular shape or an oval as a whole.

이로 인해 기존의 팔찌 연결구(100) 대비 전체적인 중량에 있어서 기본 중량과 편차를 최소화 하면서 인장력이 가해지는 부분을 보강하여 연마 과정에서 팔찌 연결구(100)가 손상되거나 파손되는 것을 방지할 수 있게 된다. Due to this, it is possible to prevent the bracelet connector 100 from being damaged or broken during the polishing process by reinforcing the portion to which the tensile force is applied while minimizing the deviation from the basic weight in the overall weight compared to the existing bracelet connector 100 .

도 5는 본 발명의 일실시예에 따른 양측에 인장 보강부가 형성되는 팔찌 연결구 제조 방법에 의해 제조된 팔찌 연결구에 장식부가 형성된 상태를 나타낸 사용상태도이다.5 is a state diagram showing a state in which decorative parts are formed in a bracelet connector manufactured by a method for manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides according to an embodiment of the present invention.

도 5를 참조하면, 본원 발명의 팔찌 연결구(100)에는 장식부(140)가 형성될 수 있다.Referring to Figure 5, the bracelet connector 100 of the present invention may be formed with a decorative portion (140).

상기 장식부(140)는 인장 보강부의 형태에 따라 반원 형상으로 형성될 수 있고, 상하가 경사진 형상으로 형성될 수도 있다. The decorative part 140 may be formed in a semicircular shape depending on the shape of the tensile reinforcement part, or may be formed in an inclined shape.

이러한 장식부(140)는 인장 보강부(120)의 보강되는 면적에 따라 형성되어 무늬를 각인하거나 장식을 설치할 수도 있고, 사용자가 선택적으로 이니셜이나 문구 등을 각인하여 착용할 수 있다.The decoration unit 140 is formed according to the area to be reinforced by the tensile reinforcement unit 120 , so that a pattern may be engraved or a decoration may be installed.

이로 인해 팔찌 연결구(100)의 인장 강도를 보강하여 후작업을 용이하게 하면서 강도 보강에 따라 장식부(140)를 형성하여 개성있는 디자인으로 제작할 수도 있게 된다. As a result, the tensile strength of the bracelet connector 100 is reinforced to facilitate post-work, and the decorative part 140 is formed according to the strength reinforcement, thereby making it possible to produce a unique design.

도 6은 본 발명의 일실시예에 따른 양측에 인장 보강부가 형성되는 팔찌 연결구 제조 방법에 의해 제조된 팔찌 연결구에 곡면형 보강 연결부가 더 구비된 상태를 나타낸 실시예도이다.6 is an embodiment view showing a state in which a curved reinforcing connector is further provided in a bracelet connector manufactured by a method for manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides according to an embodiment of the present invention.

도 6을 참조하면, 팔찌 연결구(100)에서 팔찌 체인과 이어지는 연결부위에 곡면형 보강 연결부(150)가 구비될 수 있다.Referring to FIG. 6 , a curved reinforcing connection part 150 may be provided at a connection portion connected to the bracelet chain in the bracelet connector 100 .

상기 곡면형 보강 연결부(150)는 볼록한 부분이 고정 후크(320)에 걸리는 방향으로 위치되어 연마 작업 시 고정 후크(320)에 고정한 상태에서 당겨지는 힘에 의해 휨 응력이 발생하더라도 곡면 형상에 의해 휘어지지 않도록 지지되어 제품의 변형이나 손상을 방지할 수 있게 된다. The curved reinforcing connection part 150 is positioned in the direction in which the convex part is caught by the fixing hook 320, so even if bending stress occurs due to the pulling force while being fixed to the fixing hook 320 during polishing, it is bent by the curved shape It is supported so that it does not fall, and it is possible to prevent deformation or damage to the product.

이로 인해 제품의 중량을 증가시키지 않으면서 휨 응력을 높여주고, 디자인적으로도 보다 미려한 디자인으로 제조할 수 있게 된다.Due to this, it is possible to increase the bending stress without increasing the weight of the product, and to manufacture it in a more beautiful design.

상기와 같이 이루어진 본 발명은 팔찌를 제조함에 있어서, 팔찌 연결구에서 팔찌의 길이방향 양측에 인장 보강부를 형성하여 후작업인 연마 공정에서 팔찌 연결구를 고정대에 고정하여 딩기면서 연마함에 따른 인장으로 인한 손상이나 파손을 방지할 수 있고, 인장 보강부의 크기에 따라 반원형이나 상하 경사면 형태로 형성된 부위에 무늬를 각인하거나 장식을 설치하여 보다 개성있고 미려하게 착용할 수 있게 된다. In the present invention made as described above, in manufacturing the bracelet, tensile reinforcement parts are formed on both sides of the bracelet in the longitudinal direction in the bracelet connector to fix the bracelet connector to the fixture in the polishing process, which is a post-work, and damage due to tension caused by grinding. It is possible to prevent damage, and depending on the size of the tensile reinforcement, engraving patterns or installing decorations on the parts formed in the shape of a semi-circle or an upper and lower slope makes it possible to wear them more individually and beautifully.

100 : 팔찌 연결구 110 : 연결핀
120 : 인장 보강부 130 : 경량 연결부
140 : 장식부 150 : 곡면형 보강 연결부
200 : 줄 300 : 고정대
310 : 고정판 320 : 고정 후크100: bracelet connector 110: connecting pin
120: tensile reinforcement 130: lightweight connection
140: decorative part 150: curved reinforcement connection part
200: line 300: fixture
310: fixing plate 320: fixing hook

Claims (5)

인장 보강부(120)를 포함하는 팔찌 연결구 형상의 성형물을 3D 프린터를 이용하여 성형하는 3D 프린팅 단계(S10);
3D 프린팅 단계(S10)를 통해 성형된 성형물을 고정하고, 석고를 주입하여 경화시킴에 따라 석고틀을 제조하는 석고틀 제조 단계(S20);
석고틀에서 가열을 통해 성형물을 용융하여 제거하고, 팔찌 연결구로 제조할 원료를 용융하여 석고틀로 주입시키는 소재 용융 및 주입 단계(S30);
석고틀로 주입된 원료를 경화시키는 경화 단계(S40);
경화가 완료되면 석고틀을 녹여서 제거하는 석고틀 제거 단계(S50);
석고틀을 제거하고 경화된 팔찌 연결구를 줄(200)을 이용하여 연마하는 연마 단계(S60); 및
연마된 팔찌 연결구에 광택을 부여하는 광택 단계(S70)를 포함함에 있어서,
상기 연마 단계(S60)는 팔찌를 고정대(300)에 고정시키는 고정대 고정 단계(S61)와, 줄(200)에 비산 방지액을 고르게 분사하는 비산 방지액 분무 단계(S62) 및 줄(200)에 비산 방지액이 도포된 상태에서 팔찌의 모서리와 성형 과정에서 발생된 버(burr) 등을 제거하여 마감하는 마감 가공 단계(S63)를 포함하되,
상기 고정대 고정 단계(S61)는 팔찌 연결구(100)와 팔찌 체인이 연결된 상태에서 이를 올려 고정하는 고정판(310)과 상기 고정판(310)의 상부에 구비되어 팔찌 연결구(100)를 고정하는 고정 후크(320)를 포함하는 고정대(300)에 팔찌 연결구(100)와 팔찌 체인을 고정한 상태로 줄(200)을 이용해 연마하는 것을 특징으로 하는 양측에 인장 보강부가 형성되는 팔찌 연결구 제조 방법.
3D printing step (S10) of molding a bracelet connector-shaped molding including a tensile reinforcement part 120 using a 3D printer;
A gypsum mold manufacturing step (S20) of fixing the molded product through the 3D printing step (S10) and preparing a gypsum mold by injecting and curing the gypsum;
A material melting and injection step (S30) of melting and removing the molding through heating in the plaster mold, melting the raw material to be manufactured as a bracelet connector, and injecting it into the plaster mold;
A curing step of hardening the raw material injected into the plaster mold (S40);
When curing is completed, the plaster mold removal step (S50) of melting and removing the plaster mold;
A polishing step (S60) of removing the plaster mold and polishing the hardened bracelet connector using a file (200); and
In including a polishing step (S70) of giving a gloss to the polished bracelet connector,
The polishing step (S60) includes the fixing step (S61) of fixing the bracelet to the fixing table (300), and the spraying step of the anti-scattering solution (S62) of evenly spraying the anti-scattering solution on the line (200) and the line (200). A finishing processing step (S63) of removing and finishing the edges of the bracelet and burrs generated during the molding process in a state in which the anti-scattering liquid is applied,
In the fixing step (S61), the bracelet connector 100 and the bracelet chain are connected to the fixing plate 310 for lifting and fixing it, and a fixing hook provided on the fixing plate 310 to fix the bracelet connector 100 ( A method of manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides, characterized in that the bracelet connector 100 and the bracelet chain are fixed to the fixture 300 including 320 and polished using a file 200.
 청구항 1에 의해 제조되는 것으로,
팔찌의 길이방향 양측에는 두께를 보강하여 인장 강도를 보강하는 인장 보강부(120)가 형성되고, 팔찌 체인과 연결되는 끝부분은 인장 보강부(120)에 비해 얇은 두께로 이루어지고 길이방향에서 한쪽 방향으로 볼록하게 곡면을 이루는 곡면형 보강 연결부(150)가 구비되고,
상기 인장 보강부(120)에는 양측이 상하 경사진 형상으로 적용되어 경사면에 무늬를 적용할 수 있는 장식부(140)가 더 구비되는 것을 특징으로 하는 팔찌 연결구.
As manufactured according to claim 1,
Tensile reinforcement part 120 for reinforcing tensile strength by reinforcing the thickness is formed on both sides of the bracelet in the longitudinal direction, and the end connected to the bracelet chain is made thinner than the tensile reinforcement part 120 and is formed on one side in the longitudinal direction. A curved reinforcing connection part 150 forming a convexly curved surface in the direction is provided,
Bracelet connector, characterized in that the tensile reinforcement part 120 is further provided with a decorative part 140 that can apply a pattern to the inclined surface by applying both sides of the upper and lower inclined shape.
 삭제delete 삭제delete 삭제delete
KR1020210133160A 2021-10-07 2021-10-07 A method for manufacturing a bracelet connector in which tensile reinforcement parts are formed on both sides and a bracelet connector manufactured by the same KR102365825B1 (en)