KR101835371B1 - Cosmetic Textile for High Durable Health Care Containing Natural Extract - Google Patents
Cosmetic Textile for High Durable Health Care Containing Natural Extract Download PDFInfo
- Publication number
- KR101835371B1 KR101835371B1 KR1020170121563A KR20170121563A KR101835371B1 KR 101835371 B1 KR101835371 B1 KR 101835371B1 KR 1020170121563 A KR1020170121563 A KR 1020170121563A KR 20170121563 A KR20170121563 A KR 20170121563A KR 101835371 B1 KR101835371 B1 KR 101835371B1
- Authority
- KR
- South Korea
- Prior art keywords
- extract
- weight
- fiber
- cosmetic
- solution
- Prior art date
Abstract
Description
본 발명은 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유 에 관한 것으로, 내부에 천연추출물과 한방원료가 로딩되는 인캡슐레이션 기술을 적용한 웨어러블 코스메틱 섬유로 여러 번 세탁 후에도 그 성능이 유지되며, 코스메틱 기능성을 지속적으로 발현할 수 있도록 설계된 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유에 관한 것이다.The present invention relates to a high-durability healthcare cosmetic fiber containing a natural extract, which is a wearable cosmetic fiber applied with an encapsulation technology in which a natural extract and a herbal ingredient are loaded, and its performance is maintained even after washing several times. To a durable healthcare cosmetic fiber containing a natural extract which is designed to continuously express the hair.
최근 경제와 문화 수준의 향상으로 환경과 건강에 대한 관심이 증대되면서 삶의 질을 중요시하는 웰빙/로하스(Well-being, LOHAS)를 추구하는 방향으로 생활 패턴이 변화함에 따라 인체에 무해하면서, 환경 친화적이고 위생적인 천연소재 또는 천연 추출물에 대한 다양한 욕구가 점점 증가하고 있는 추세로서 이러한 관심은 친환경 먹거리나 친환경 화장품뿐만 아니라 점점 친환경 의류로 확대되고 있다.Recently, due to the increase of interest in environment and health due to the improvement of economy and culture level, life style has been changed in the direction of pursuing Well-being (LOHAS), which emphasizes quality of life, The growing interest in friendly and hygienic natural materials or natural extracts is increasingly being driven not only by eco-friendly foods and eco-friendly cosmetics but also by increasingly environmentally friendly clothing.
또한, 다양한 스포츠 활동을 통해 여가를 즐기는 여성들이 증가하고 있으며, 이러한 여성들은 다이어트와 건강관리에 관심이 많으며, 이에 입기만 해도 미용효과를 획득할 수 있는 코스메틱, 안티에이징 관련 섬유제품에 대한 관심도 증가하고 있으며, 한방 코스메틱 섬유 및 고탄력 TPU소재를 활용한 피부노화방지와 근효율 증가 기능의 여성용 고성능 한방소재 웨어 개발을 통한 한방의류 및 애슬레저 웨어 시장의 블루오션 창출이 가능하다.In addition, there are increasing numbers of women who enjoy leisure activities through various sports activities. These women are interested in diet and health care, and they are increasingly interested in cosmetics and anti-aging related textile products It is possible to create a blue ocean of oriental clothing and athletic wear market through the development of high performance herbal material wear for women with skin anti-aging and muscular efficiency enhancement utilizing herbal cosmetic fibers and high-elasticity TPU materials.
위와 같이 옷의 기능이 섬유기술 발전 속도에 맞춰 점점 확대됨으로서 단순히 입기 위한 것이 아니라 몸을 보호하고 가꾸는 미용의 기능으로까지 자리를 넓혀감에 따라 현대 섬유제품에는 환경문제 해결과 자연 회귀, 건강한 삶, 쾌적함의 추구 등의 경향이 반영되고 피부를 숨쉬게 한다는 기본 개념에 입각해 화장품의 주요 성분들이 직물에 도입되고 있다.As the function of clothes is gradually expanded in accordance with the speed of textile technology development, it is not only for wearing but also expanding to the function of beauty to protect and care for the body. Therefore, modern textile products include environment problem solving, natural return, The main ingredients of cosmetics are being introduced into fabrics based on the basic concept of reflecting the tendency of pursuit of comfort and breathing the skin.
입는 화장품으로 알려진 코스메틱 섬유는 섬유에 화장품 기능을 융·복합화한 섬유 소재로서 인체에 직/간접적으로 건강(혈행개선, 통증완화 등)과 뷰티(슬리밍, 보습/퍼밍 등)의 효과를 부여하는 섬유상의 소재를 말한다.Cosmetic fibers, known as wearing cosmetics, are fiber materials that combine and combine the functions of cosmetics with fibers. They are fiber materials that directly or indirectly impart to the body the effects of health (blood circulation improvement, pain relief) and beauty (slimming, moisturizing / Is the material of.
화장품(Cosmetic)과 섬유(Textile)를 결합한 '코스메토텍스타일(Cosmeto textile)로도 불리우며 유럽표준화위원회(European Committee for Standardization)는 미용 기능 유효성분을 피부로 지속적으로 방출하는 섬유 제품을 화장품 기능 섬유(Cosmetic Textile)로 정의하고 있다.It is also called 'Cosmeto textile' which combines cosmetics and textiles. The European Committee for Standardization is a cosmetics functional fiber that continuously releases the active ingredients of cosmetics to the skin. Textile).
아침과 저녁에 한 번씩 바르는 것에 그치기 때문에 뷰티와 케어에서 한계가 있는 화장품에 비하여 섬유에 화장품이 결합된 코스메틱 섬유를 입게 되면 착용하는 동안에 계속해서 화장품의 기능의 뷰티와 의복 기능의 웨어러블 기능이 유기적으로 결합된 웨어러블 스킨케어(wearable skincare)효과로 신체에 작용하여 건강과 뷰티 및 외부로부터 신체를 보호하고, 신체를 장식하는 의복의 복합 상승효과를 구현하게 되는 것으로서 이제 섬유는 단순한 기능에서 화장품을 포함하는 영역으로 확대되고 있으며, 항균, 방취, 치유(힐링, healing) 효과를 가지면서 기능성이 보강된 감성섬유로서 요구가 날로 증가하고 있는 코스메틱 섬유는 그 예로서 고유의 향미성, 항곰팡이성, 항미생물 특성, 살균성, 살충성, 항바이러스성, 항암 특성 등이 우수한 식물성 천연 추출물 또는 식물 정유(oil), 향료 등을 직물에 직접 도포하거나 마이크로 캡슐(micro capsule)화 하여 섬유 표면에 부착시켜 사용시 마찰에 의해 캡슐이 터지면서 사람의 피부에 점진적으로 화장품의 활성성분을 방출하는 것으로 시간이 지나면 수분 등 기타 원인에 의해 탈락 및 변형이 되므로 효능이 쉽게 감소되고, 땀 냄새와 향료 냄새가 혼합하여 더 심한 악취의 원인이 되어 오히려 역효과를 나타낼 수 있으며 세척 후에 효과가 감소함으로써 천연추출물이나 정유 등 본래의 기능을 쉽게 상실하게 되는 문제점이 있었다.As it is applied only once in the morning and evening, when cosmetic fibers combined with cosmetics combined with fiber are put on compared to cosmetics with limit in beauty and care, wearability function of cosmetics function and cosmetics function continue to be organically Combined wearable skincare effects that work on the body to protect the body from health, beauty and outside, and to realize a composite synergy of garments that decorate the body. As a result, cosmetic fibers having increased antibacterial, deodorant, healing and functional properties and enhanced functionality have been increasingly demanded. Examples of such cosmetic fibers include unique flavor, antifungal, antimicrobial, Natural vegetable extracts with excellent characteristics, bactericidal, insecticidal, antiviral and anticancer properties Water or plant oil or fragrance is applied directly to the fabric or attached to the surface of the fiber in the form of micro capsules and the capsules burst due to friction when used to gradually release the active ingredient of the cosmetic to the human skin After a long time, it is eliminated and deformed by other causes such as moisture, so that the efficacy is easily reduced. It is mixed with sweat odor and fragrance odor, which causes more bad odor and may show adverse effect. And the essential functions such as refining oil are easily lost.
또한 상기와 같은 종래의 코스메틱 섬유는 여러 기술적 한계로 다양한 기능을 내포하고 있지 못하고 흡한 속건성, 항균 방취, 보온, 축열이나 발열 및 원적외선 또는 음이온 방사 기능중 어느 한가지만의 특정 기능만을 가지고 있어 여러 가지의 기능을 포함하지 못하므로 단순 기능이 아닌 다기능을 포함한 효능효과를 추구하며 기능성 원단을 이용한 것 이상의 새로운 다기능성 섬유 제품을 요구하는 현대의 소비자에게 있어서 부족한 기능성을 커버하기 위해서는 요구되는 기능별 섬유를 각각 구비하여야 하므로 번거럽고 경제적이지 못한 문제점이 있다.In addition, the conventional cosmetic fiber does not have various functions due to various technical limitations and has only specific functions such as quick-drying, antibacterial deodorization, thermal insulation, heat storage, heat generation and far infrared ray or negative ion radiation function, In order to cover the functionality that is lacking for modern consumers who demand a new multifunctional fiber product that uses functional fabric rather than functional fabric, It is troublesome and uneconomical.
기존의 한방천연물질(감초, 상황버섯, 율피, 지유 등)과 새로운 천연 한방 기능원료 선정 및 추출을 통해 복합기능을 개발하여 피트니스 활동을 즐기는 여성을 대상에게 적합한 한방 코스메틱 기능구현의 서방형 중공 캡슐 제조 및 가공조건을 확립 및 개발이 필요하게 되었다.It is a new type of hollow capsule that can be applied to a woman who enjoys fitness activities by developing complex functions through the selection and extraction of natural herbal ingredients (licorice, mushroom, ufpy, and jiu) It has become necessary to establish and develop manufacturing and processing conditions.
상기와 같은 문제점을 해결하기 위한 본 발명은 내부는 한방원료, 향원료 또는 화장품원료가 로딩되고 외부는 쉘로 캡슐화된 마이크로캡슐이 포함된 중합액을, 피트니스와 에슬레져 및 아웃웨어에 사용되는 내구성 섬유에 침지공정, 패딩공정을 포함하는 공정으로 결합시켜 제조하는 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유를 제공함에 있다.In order to solve the above-mentioned problems, the present invention provides a method for manufacturing a dental implant, which comprises a polymerized liquid containing microcapsules in which an oriental raw material, an fragrance raw material or a cosmetic raw material is loaded and an external shell is encapsulated, To a process comprising an immersion process and a padding process. The present invention also provides a high-durability health care cosmetic fiber containing a natural extract.
본 발명의 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유는 내부는 한방원료, 향원료 또는 화장품원료가 로딩되고 외부는 쉘로 캡슐화된 마이크로캡슐(Microcapsule)이 포함된 중합액을, 피트니스(Fitness)와 에슬레져(Athleisure) 및 아웃웨어(Outer Wear)에 사용되는 내구성 섬유에 침지공정, 패딩공정을 포함하는 공정으로 결합시켜 제조한다.The highly durable healthcare cosmetic fiber containing the natural extract of the present invention can be prepared by mixing a polymeric solution containing microcapsules in which a raw material, an aromatic or cosmetic raw material is loaded and an outer shell is encapsulated, It is manufactured by combining the durable fiber used in Athleisure and Outer Wear by a process including an immersion process and a padding process.
상기 내구성 섬유는 면(Cotton), 폴리에스터(Polyester), 나이론(Nylon), 서쿨러 니트(Circular Knit) 또는 트리코(Tricot) 소재로 제조된 것이다.The durable fiber is made of Cotton, Polyester, Nylon, Circular Knit or Tricot material.
상기 마이크로캡슐은 상기 한방원료, 향원료 또는 화장품원료가 천천히 방출되는 서방형 타입이다.The microcapsule is a sustained-release type in which the oriental raw material, fragrant raw material or cosmetic raw material is slowly released.
상기 중합액은 상기 한방원료, 향원료 또는 화장품원료로 제조되는 원액 및 추출물이 1~10중량%가 함유된 추출물 솔루션을 물 100 중량부에 대하여 계면활성제 1~30중량부와, 개시제 0.2~0.5 중량부와, 모노머 2~5 중량부와, 분산제 0.2~0.5 중량부가 함유된 중합탱크에 넣은 후 교반하여 유화중합(Emulsion Polymerization) 또는 현탁중합(Suspension Polymerization)시켜 상기 마이크로캡슐이 생성되게 제조되며, 상기 마이크로캡슐의 입자 크기는 40~200 nm 이다.The polymer solution is prepared by mixing 1 to 30 parts by weight of a surfactant, 0.2 to 0.5 parts by weight of an initiator with respect to 100 parts by weight of an extract solution containing 1 to 10% by weight of a raw solution and an extract made of the herbal raw materials, And 2 to 5 parts by weight of a monomer and 0.2 to 0.5 parts by weight of a dispersant are added to a polymerization tank containing the above components and then stirred and emulsion polymerized or suspended polymerized to produce the microcapsules. The particle size of the microcapsules is 40 to 200 nm.
상기 코스메틱 섬유는 내구성 섬유 100중량부에 대하여 상기 마이크로캡슐 1~20 중량부와, 바인더 1~20 중량부를 포함한다.The cosmetic fiber comprises 1 to 20 parts by weight of the microcapsule and 1 to 20 parts by weight of a binder based on 100 parts by weight of the durable fiber.
상기 코스메틱 섬유는 한방원료, 향원료 또는 화장품원료의 추출물 솔루션을 제조하는 추출물 솔루션 제조공정과; 상기 추출물 솔루션을 중합액이 제조된 중합탱크에 넣고 교반하여 중합하여 상기 중합액을 제조하는 중합 및 중합액 제조공정과; 일정 폭의 상기 내구성 섬유를 권취롤러에 권취하여 내구성 섬유를 준비하는 내구성 섬유 준비공정과; 침지용액을 제조하는 침지용액 제조공정과; 상기 침지용액에 내구성 섬유를 침지하는 침지공정과; 침지공정을 거친 상기 중합액이 코팅된 내구성 섬유를 오토 맹글 머신 투입하고, 균입하게 압입하며, 중간 건조 후 폭을 당겨 소정의 폭으로 조정하며 최종 건조하여 코스메틱 섬유를 제조하는 패딩공정과; 완전히 건조되어 코스메틱 섬유를 권취하는 완제품 권취공정을 포함하여 제조된다. Wherein the cosmetic fiber comprises: an extract solution manufacturing process for preparing an extract solution of a herbal raw material, a fragrance raw material or a cosmetic raw material; A polymerization and a polymerization solution production step in which the above extract solution is put into a polymerization tank in which a polymerization solution is prepared and stirred to polymerize the solution to prepare the polymerization solution; A durable fiber preparation step of winding the durable fiber of a predetermined width on a take-up roller to prepare a durable fiber; An immersion solution manufacturing process for producing an immersion solution; An immersion step of immersing the durable fiber in the immersion solution; A padding step of putting the durable fiber coated with the polymerization liquid through the immersion step into an automender machine, pressurizing the dummy fiber intimately, pulling the width after the intermediate drying, adjusting the fiber width to a predetermined width, and finally drying to prepare a cosmetic fiber; And a finished product winding process in which the cosmetic fibers are completely dried and wound.
상기 한방원료는 원료를 일정 크기로 잘라 준비하는 원료준비단계와; 준비된 원료를 세척한 후 물기를 제거하는 세척단계와; 수분이 제거된 상기 원료를 일정 압력의 증기압을 갖는 증기로 일정 시간 동안 살균하는 살균단계와; 살균된 상기 원료를 추출기에 넣고 정제수 또는 에탄올을 가하여 추출하여 중간추출물을 얻는 중간추출단계와; 상기 중간추출물에서 상청액(Supernatant)추출물을 분리하는 상청액분리단계와; 상청액추출물에서 불순물을 제거하는 필터링단계와; 여과된 상청액추출물을 증발건조시켜 증발건조추출물을 제조하는 증발건조단계와; 상기 증발건조추출물을 일정 온도와 일정 진공도에서 일정 시간 동안 농축 동결건조하는 동결건조단계와; 동결건조된 추출물을 분쇄기에 넣고 일정 입도 분포로 분쇄하여 분말 추출물을 만드는 분쇄단계와; 일정량의 분말 추출물을 일정량의 정제수에 넣고 교반하여 일정 함량의 추출물 솔루션으로 만드는 추출물 솔루션 제조단계로 제조된다.Wherein the one-shot raw material comprises a raw material preparation step of preparing a raw material by cutting to a predetermined size; A washing step of washing the prepared raw material and then removing water; A sterilizing step of sterilizing the raw material from which moisture has been removed by steam having a vapor pressure of a predetermined pressure for a predetermined time; An intermediate extraction step of adding the sterilized raw material to an extractor and extracting it with purified water or ethanol to obtain an intermediate extract; A supernatant separation step of separating the supernatant extract from the intermediate extract; A filtering step of removing impurities from the supernatant extract; An evaporation drying step of evaporating and drying the filtered supernatant extract to produce an evaporated dry extract; A freeze-drying step of concentrating and freeze-drying the evaporated and dried extract at a constant temperature and a constant degree of vacuum for a predetermined time; Pulverizing the lyophilized extract into a powder and pulverizing the powder into a predetermined particle size distribution; A certain amount of powdered extract is mixed with a certain amount of purified water and stirred to produce a certain amount of extract solution.
상기 패딩공정은 오토 맹글 머신(Auto Mangle Machine)에서 진행되며, 상기 침지공정을 거친 상기 침지용액이 코팅된 내구성 섬유가 투입되는 투입단계와, 상기 중합액을 상기 내구성 섬유에 균입하게 압입 하는 압착단계와, 중간 건조단계와, 폭을 당겨 소정의 폭으로 조정하며 최종 건조하는 스텐터 단계를 포함한다.The padding process is carried out in an Auto Mangle Machine. The padding process includes a charging step in which the durable fiber coated with the immersion solution after the immersion process is charged, and a pressing step in which the polymer solution is press- And an intermediate drying step and a stenter step of adjusting the width to a predetermined width by pulling the width and finally drying.
상기 마이크로캡슐의 쉘은 이중층 구조를 가지게 상기 유화중합 또는 현탁중합 후 염기성 분위기 하에서 가수분해하여 내부에 무기층이 형성되고, 외부에 고분자층의 형성될 수도 있다.The shell of the microcapsule may be hydrolyzed in a basic atmosphere after emulsion polymerization or suspension polymerization so as to have a bilayer structure to form an inorganic layer inside and a polymer layer outside.
상기 중합탱크에는 상기 마이크로캡슐의 쉘이 이중층 구조를 가지게 하기 위하여 물 100 중량부에 대하여 무기물 전구체 1.5~5.5 중량부가 추가로 함유된다.The polymerization tank further contains 1.5 to 5.5 parts by weight of an inorganic precursor based on 100 parts by weight of water to make the shell of the microcapsule have a double layer structure.
상기 한방원료는 항산화 항염증 작용과 항알러지 작용 및 자외선을 차단하는 감초추출물, 항산화 작용 및 자외선을 차단하는 상황버섯추출물, 항산화과 항염증 작용 및 자외선을 차단하는 밤껍질인 율피추출물, 오이풀의 뿌리와 뿌리 줄기를 말린 지유(地楡)추출물, 비타민C를 다량 함유하고 항산화 및 향균성 작용을 하는 감귤추출물, 피부진정효과 및 피부영양을 공급하는 알로에추출물, 세포재생효과와 상처치유효과 및 염증완화효과가 있는 병풀추출물 중 하나 또는 둘 이상을 혼합하여 사용한다.The herbal ingredients include antioxidant anti-inflammatory action, antiallergic action, licorice extract to block ultraviolet light, antioxidant activity, mushroom extract to block ultraviolet light, antioxidant anti-inflammatory action, ultraviolet ray-shielding chestnut bark extract, Rootstock with dried extracts of ground oil, citrus extract containing antioxidant and antibacterial activity, vitamin C and aloe extract to supply skin soothing effect and skin nutrition, cell regeneration effect, wound healing effect and inflammation relieving effect And a mixture of two or more of them.
상기 한방원료는 항산화 항염증 작용과 항알러지 작용 및 자외선을 차단하는 감초추출물 5~30 중량%와; 항산화 작용 및 자외선을 차단하는 상황버섯추출물 5~30 중량%와; 항산화과 항염증 작용 및 자외선을 차단하는 밤껍질인 율피추출물 5~30 중량%와; 오이풀의 뿌리와 뿌리 줄기를 말린 지유(地楡)추출물 5~30 중량%와; 비타민C를 다량 함유하고 항산화 및 향균성 작용을 하는 감귤추출물 5~30 중량%와; 피부진정효과 및 피부영양을 공급하는 알로에추출물 5~30 중량%와; 세포재생효과와 상처치유효과 및 염증완화효과가 있는 병풀추출물 3~20 중량%와; 변비에 효과가 있고 식이성섬유, 칼슘 철분이 함유된 백련초추출물 3~20중량로 조성될 수도 있다.The herbal ingredients include 5 to 30% by weight of an extract of licorice root which blocks antioxidative anti-inflammatory action, antiallergic action and ultraviolet rays; 5 to 30% by weight of mushroom extract to block antioxidative action and ultraviolet rays; 5 to 30% by weight of an antioxidant anti-inflammatory action and a chestnut shell which blocks ultraviolet rays; 5 to 30% by weight of a ground oil extract of dried root and rootstock of Oleaceae; 5 to 30% by weight of a citrus extract containing a large amount of vitamin C and antioxidant and antibacterial activity; 5 to 30% by weight of an aloe extract to provide skin soothing and skin nutrition; 3 to 20% by weight of Centella asiatica extract having cell regeneration effect, wound healing effect and inflammation relieving effect; It is effective in constipation and may be composed of 3 to 20 weight of Paeoniae herb extract containing dietary fiber and calcium iron.
상기 패딩공정의 압착단계는 롤러 압을 3.5~4.5kgf/cm2, 롤러 스피드를 10~20m/min 압착하고, 상기 중간 건조단계는 110~130℃에서 1.5~3분간 건조하며, 상기 스텐터 단계는 160~180℃ 에서 1.5~3분간 실시한다.The pressing step of the padding step presses the roller pressure at 3.5 to 4.5 kgf / cm 2 and the roller speed at 10 to 20 m / min, and the intermediate drying step is performed at 110 to 130 ° C for 1.5 to 3 minutes, It is carried out at 160 to 180 ° C for 1.5 to 3 minutes.
상기 개시제는 Potassium persulfate, Ammonium persulfate, BPO(Benzoyl Peroxide), Rongalite C 중 어느 하나를 사용하며, 상기 모노머는 PMMA(Poly Methyl Methacrylate)), PVA(Polyvinyl Alcohol), 폴리우레아(Polyurea), 멜라민(Melamine), 아크릴산(Acrylic Acid), 방향족산(Aromatic Acid) 중 어느 하나를 사용하며, 상기 분산제는 CTAB(Cetyl trimethylammonium bromide), Polyethylene glycol ether, Polyoxyethylene sorbitan mono-oleate, SDS(Sodium dodecylsulfate)로 이루어진 군에서 선택되는 1종 또는 2종 이상이다.The initiator may be selected from the group consisting of Potassium persulfate, Ammonium persulfate, Benzoyl peroxide (BPO), and Rongalite C. The monomer may be selected from the group consisting of PMMA (Poly Methyl Methacrylate), PVA (Polyvinyl Alcohol), Polyurea, Melamine ), Acrylic acid, and aromatic acid. The dispersant is selected from the group consisting of CTAB (Cetyl trimethylammonium bromide), Polyethylene glycol ether, Polyoxyethylene sorbitan mono-oleate, and SDS (sodium dodecylsulfate) And one or more selected from the group.
상기 침지공정은 침지용액에 상기 내구성 섬유를 침지하여 시행하며, 상기 침지용액은 상기 중합액 1000 중량부에 대하여 바인더 10~200중량부와, 발수제 70~90 중량부와, 가교제 5.5~7.5 중량부와, 촉매 1.5~3.5 중량부와, UV 차단제 15~30 중량부와, 대전방지제 5~15 중량부와, 방오제 5~15 중량부와, 가공제 20~40 중량부로 조성되는 것을 특징으로 하는 천연추출물을 함유한다.The immersion solution is prepared by immersing the durable fiber in an immersion solution, wherein the immersion solution comprises 10 to 200 parts by weight of a binder, 70 to 90 parts by weight of a water repellent, 5.5 to 7.5 parts by weight of a cross- 1.5 to 3.5 parts by weight of a catalyst, 15 to 30 parts by weight of a UV blocking agent, 5 to 15 parts by weight of an antistatic agent, 5 to 15 parts by weight of an antifouling agent and 20 to 40 parts by weight of a working agent. Contains natural extracts.
상술한 코스메틱 섬유로 본 발명의 해결하고자 하는 과제를 해결할 수 있다.The problems to be solved by the present invention can be solved with the cosmetic fibers described above.
본 발명의 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유에 따르면 입을 수 있는 섬유 형태로 제조가 가능하여 웨어러블 코스메틱 섬유이며, 한방원료, 향원료 또는 화장품원료를 캡슐에 로딩하여 여러 번 세탁 후에도 그 성능을 유지하며, 기능성을 지속적으로 발현할 수 있는 장점이 있다.According to the highly durable healthcare cosmetic fiber containing the natural extract of the present invention, the wearable cosmetic fiber can be manufactured in the form of a wearable fiber, and it is possible to load the herbal raw material, the fragrance raw material or the cosmetic raw material into the capsule, , And has the advantage of continuously exhibiting the functionality.
도 1은 본 발명의 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유의 단면도 및 전자현미경 촬영사진
도 2는 본 발명의 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유의 피부 침투 설명도
도 3은 본 발명의 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유의 제조공정 순서도
도 4는 본 발명의 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유의 제조공정 중 한방원료 추출물 솔루션 제조공정 순서도
도 5는 본 발명의 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유의 제조공정 숭 침지공정과 패팅공정 설명도1 is a cross-sectional view and an electron microscope photograph of a highly durable healthcare cosmetic fiber containing the natural extract of the present invention
FIG. 2 is a graph showing penetration of the skin of the highly durable healthcare cosmetic fiber containing the natural extract of the present invention
Figure 3 is a flow chart of the manufacturing process of a highly durable healthcare cosmetic fiber containing the natural extract of the present invention
FIG. 4 is a flow chart of a process for manufacturing a herbal raw material extract solution in a process for producing a highly durable healthcare cosmetic fiber containing the natural extract of the present invention
FIG. 5 is an explanatory diagram of a dipping process and a padding process of a durable dental health care cosmetic fiber containing the natural extract of the present invention
먼저, 본 발명의 구체적인 설명에 들어가기에 앞서, 본 발명에 관련된 공지 기술 또는 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명은 생략한다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS First, a detailed description of known functions and configurations incorporated herein will be omitted when it may make the subject matter of the present invention rather unclear.
또한, 후술 되는 용어들은 본 발명에서의 기능을 고려하여 정의된 용어들로서 이는 사용자, 운용자의 의도 또는 관례 등에 따라 달라질 수 있으므로, 그 정의는 본 발명에 따른 "천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유"를 설명하는 본 명세서 전반에 걸친 내용을 토대로 내려져야 할 것이다.It is to be understood that the following terms are defined in consideration of the functions of the present invention and may vary depending on the intention or custom of the user, the operator, and the like. Therefore, the definition is "high durability health care cosmetic Quot; fibers "in the specification and claims.
이하, 본 발명에 따른 "천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유"에 관한 바람직한 실시 예를 상세하게 설명한다. Hereinafter, a preferred embodiment of the "highly durable healthcare cosmetic fiber containing a natural extract" according to the present invention will be described in detail.
다음의 실시 예는 단지 본 발명을 설명하기 위하여 예시된 것에 불과하고, 본 발명의 범위를 제한하기 위한 것은 아니다.The following examples are merely illustrative of the present invention and are not intended to limit the scope of the present invention.
도 1은 본 발명의 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유의 단면도 및 전자현미경 촬영사진이며, 도 2는 본 발명의 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유의 피부 침투 설명도이고, 도 3은 본 발명의 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유의 제조공정 순서도이며, 도 4는 본 발명의 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유의 제조공정 중 한방원료 추출물 솔루션 제조공정 순서도이고, 도 5는 본 발명의 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유의 제조공정 숭 침지공정과 패팅공정 설명도이다. FIG. 1 is a cross-sectional view and an electron microscope photograph of a high-durability healthcare cosmetic fiber containing the natural extract of the present invention, FIG. 2 is an explanatory diagram of skin penetration of a highly durable healthcare cosmetic fiber containing the natural extract of the present invention, FIG. 3 is a flow chart showing a manufacturing process of a highly durable health care cosmetic fiber containing the natural extract of the present invention, and FIG. 4 is a view showing a process of manufacturing a high- And FIG. 5 is an explanatory diagram of a soaking process and a patting process of a high-durability healthcare cosmetic fiber containing the natural extract of the present invention.
도 1에 도시되어 있는 것 같이 본 발명의 코스메틱 섬유는 코어라 불리우는 내부는 한방원료, 향원료 또는 화장품원료가 로딩(Loading)되고 외부는 쉘(Shell)로 캡슐화된 마이크로캡슐(Microcapsule)이 포함된 중합액을, 피트니스(Fitness)와 에슬레져(Athleisure)에 사용되는 내구성 섬유에 침지공정, 패딩공정을 포함하는 공정으로 결합시켜 제조한다.As shown in FIG. 1, the cosmetic fiber of the present invention includes a microcapsule in which a core, called a core, is filled with a herbal raw material, a fragrance raw material or a cosmetic raw material and the outside is encapsulated with a shell, The polymerized liquid is prepared by combining the durable fiber used in Fitness and Athleisure with a process including an immersion process and a padding process.
상기 내구성 섬유는 면(Cotton), 폴리에스터(Polyester), 나이론(Nylon), 서큘러 니트(Circular Knit) 또는 트리코트(Tricot)를 포함한 내구성 소재로 제조된다.The durable fiber is made of a durable material including Cotton, Polyester, Nylon, Circular Knit or Tricot.
상기 에슬레져는 애슬레틱(운동경기)과 레저(여가)를 합친 스포츠웨어 업계의 용어. “가벼운 스포츠” 등으로 번역되는데, 스포츠의 흥미로부터 일반인들도 스포츠를 일상적으로 받아들여 손쉽게 레저와 같은 즐거움을 맛보자는 경향을 가리킨다. 1980년대의 건강 스포츠가 붐이 일어났을때 생긴 말. 시대에 따라 즐기는 스포츠의 유행은 조금씩 달라지는데 배드민턴, 테니스, 조깅, 에어로빅, 볼링 등 그 종류가 다양하다.The above-mentioned eraser is a term of sportswear industry that combines Athletic (leisure sport) and leisure (leisure). "Light Sports", etc., and the tendency of ordinary people to enjoy sports such as leisure easily by taking sports daily is interesting from the interest of sports. A word that came up when the health sports of the 1980s boomed. The trends of sports enjoyed by the times are slightly different, but there are various kinds of badminton, tennis, jogging, aerobics and bowling.
상기 마이크로캡슐은 상기 한방원료, 향원료 또는 화장품원료가 천천히 방출되는 서방형 타입이다.The microcapsule is a sustained-release type in which the oriental raw material, fragrant raw material or cosmetic raw material is slowly released.
상기 마이크로캡슐의 입자 크기는 200~4,000 nm 인 것이 바람직하다.The particle size of the microcapsule is preferably 200 to 4,000 nm.
상기 중합액은 상기 한방원료, 향원료 또는 화장품원료로 제조되는 원액 및 추출물(혹은 원액 또는 추출물)이 1~10중량%가 함유된 추출물 솔루션을 물 100 중량부에 대하여 계면활성제 1~30중량부와, 개시제 0.2~0.5 중량부와, 모노머 2~5 중량부와, 분산제 0.2~0.5 중량부가 함유된 중합탱크에 넣은 후 교반하여 유화중합(Emulsion Polymerization) 또는 현탁중합(Suspension Polymerization)시켜 상기 마이크로캡슐이 생성되게 제조된다.The polymer solution is prepared by mixing 1 to 10% by weight of an extract solution containing the raw material and the extract (or raw extract or extract) prepared from the herbal raw materials, fragrance raw materials or cosmetic raw materials with 1 to 30 parts by weight of a surfactant , 0.2 to 0.5 part by weight of an initiator, 2 to 5 parts by weight of a monomer, and 0.2 to 0.5 part by weight of a dispersant, followed by stirring and emulsion polymerization or suspension polymerization, Is produced.
상기 향원료의 경우 Oil로 구성되어 계면활성제로 분산을 시켜야 한다.In case of the fragrance raw material, it should be dispersed with surfactant composed of oil.
상기 중합탱크에는 물 100 중량부에 대하여 상기 마이크로캡슐의 쉘이 이중층 구조를 가지게 하기 위하여 무기물 전구체 1.5~5.5 중량부가 추가로 함유될 수도 있다.The polymerization tank may further contain 1.5 to 5.5 parts by weight of an inorganic precursor to make the shell of the microcapsule have a double layer structure with respect to 100 parts by weight of water.
상기 마이크로캡슐의 쉘은 이중층 구조를 가지게 상기 유화중합 또는 현탁중합 후 염기성 분위기 하에서 가수분해하여 내부에 무기층이 형성되고, 외부에 고분자층의 형성할 수도 있다.The shell of the microcapsule may be hydrolyzed in a basic atmosphere after emulsion polymerization or suspension polymerization to have a bilayer structure, and an inorganic layer may be formed inside and a polymer layer may be formed on the outside.
상기 코스메틱 섬유는 내구성 섬유 100중량부에 대하여 상기 마이크로캡슐 1~20 중량부와, 바인더 1~20 중량부를 포함한다.The cosmetic fiber comprises 1 to 20 parts by weight of the microcapsule and 1 to 20 parts by weight of a binder based on 100 parts by weight of the durable fiber.
상기 한방원료는 항산화 항염증 작용과 항알러지 작용 및 자외선을 차단하는 감초추출물, 항산화 작용 및 자외선을 차단하는 상황버섯추출물, 항산화과 항염증 작용 및 자외선을 차단하는 밤껍질인 율피추출물, 오이풀의 뿌리와 뿌리 줄기를 말린 지유(地楡)추출물, 비타민C를 다량 함유하고 항산화 및 향균성 작용을 하는 감귤추출물, 피부진정효과 및 피부영양을 공급하는 알로에추출물, 세포재생효과와 상처치유효과 및 염증완화효과가 있는 병풀추출물 중 하나 또는 둘 이상을 혼합하여 사용한다.The herbal ingredients include antioxidant anti-inflammatory action, antiallergic action, licorice extract to block ultraviolet light, antioxidant activity, mushroom extract to block ultraviolet light, antioxidant anti-inflammatory action, ultraviolet ray-shielding chestnut bark extract, Rootstock with dried extracts of ground oil, citrus extract containing antioxidant and antibacterial activity, vitamin C and aloe extract to supply skin soothing effect and skin nutrition, cell regeneration effect, wound healing effect and inflammation relieving effect And a mixture of two or more of them.
상기 한방원료는 항산화 항염증 작용과 항알러지 작용 및 자외선을 차단하는 감초추출물 5~30 중량%와; 항산화 작용 및 자외선을 차단하는 상황버섯추출물 5~30 중량%와; 항산화과 항염증 작용 및 자외선을 차단하는 밤껍질인 율피추출물 5~30 중량%와; 오이풀의 뿌리와 뿌리 줄기를 말린 지유(地楡)추출물 5~30 중량%와; 비타민C를 다량 함유하고 항산화 및 향균성 작용을 하는 감귤추출물 5~30 중량%와; 피부진정효과 및 피부영양을 공급하는 알로에추출물 5~30 중량%와; 세포재생효과와 상처치유효과 및 염증완화효과가 있는 병풀추출물 3~20 중량%와; 변비에 효과가 있고 식이성섬유, 칼슘 철분이 함유된 백련초추출물 3~20중량로 조성될 수도 있다.The herbal ingredients include 5 to 30% by weight of an extract of licorice root which blocks antioxidative anti-inflammatory action, antiallergic action and ultraviolet rays; 5 to 30% by weight of mushroom extract to block antioxidative action and ultraviolet rays; 5 to 30% by weight of an antioxidant anti-inflammatory action and a chestnut shell which blocks ultraviolet rays; 5 to 30% by weight of a ground oil extract of dried root and rootstock of Oleaceae; 5 to 30% by weight of a citrus extract containing a large amount of vitamin C and antioxidant and antibacterial activity; 5 to 30% by weight of an aloe extract to provide skin soothing and skin nutrition; 3 to 20% by weight of Centella asiatica extract having cell regeneration effect, wound healing effect and inflammation relieving effect; It is effective in constipation and may be composed of 3 to 20 weight of Paeoniae herb extract containing dietary fiber and calcium iron.
본 발명의 코스메틱 섬유는 입을 수 있는 섬유 형태로 제조가 가능하여 웨어러블 코스메틱 섬유이며, 한방원료, 향원료 또는 화장품원료를 캡슐에 로딩하여 여러 번 세탁 후에도 그 성능을 유지하며, 기능성을 지속적으로 발현할 수 있으며, 상기 한방원료, 향원료 또는 화장품원료로 만든 추출물이 피부로 자연스럽게 전달된다.The cosmetic fiber of the present invention can be manufactured in the form of a wearable fiber and is a wearable cosmetic fiber. The cosmetic fiber of the present invention can be obtained by loading the herbal raw material, the fragrance raw material or the cosmetic raw material into the capsule, maintaining its performance even after washing several times, And the herbal raw materials, the fragrance raw materials or the extracts made from the cosmetic raw materials are naturally delivered to the skin.
도 2에 도시되어 있는 것 같이 본 발명의 코스메틱 섬유는 상기 마이크로캡슐에서 상기 한방원료, 향원료 또는 화장품원료의 추출물이 천천히 방출되며, 상기 쉘의 기공(Pore)을 통하여 방출되며, 도시된 아래 그림은 상기 한방원료, 향원료 또는 화장품원료의 추출물이 천천히 방출되고, 상기 쉘의 한 분자 안에 물을 싫어하는 성질인 소수성(hydrophobic)을 띠는 부분과 물을 좋아하는 성질인 친수성(hydrophilic)을 보이는 부분을 동시에 가지고 있는 리포좀(Liposome)과 피부의리포좀이 만나 결합하여 상기 한방원료, 향원료 또는 화장품원료의 추출물이 피부를 통과하여 흡수되는 것을 보여준다.As shown in FIG. 2, the cosmetic fiber of the present invention slowly releases the herbal raw material, the fragrance raw material or the cosmetic raw material extract from the microcapsule and is discharged through the pores of the shell, The extract of the herbal raw material, the fragrance raw material or the cosmetic raw material is slowly released, and a part of the shell having a hydrophilic part which dislikes water and a part which shows hydrophilic property which is a favorable property of water And liposome of the skin are combined with each other to show that the herbal raw material, the fragrance raw material or the extract of the cosmetic raw material is absorbed through the skin.
도 3에 도시되어 있는 것 같이 상기 코스메틱 섬유는 상기 한방원료, 향원료 또는 화장품원료의 추출물 솔루션을 제조하는 추출물 솔루션 제조공정과; 상기 추출물 솔루션을 중합액이 제조된 중합탱크에 넣고 교반하여 중합하여 상기 중합액을 제조하는 중합 및 중합액 제조공정과; 일정 폭의 상기 내구성 섬유를 권취롤러에 권취하여 내구성 섬유를 준비하는 내구성 섬유 준비공정과; 침지용액을 제조하는 침지용액 제조공정과; 상기 침지용액에 내구성 섬유를 침지하는 침지공정과; 상기 침지공정을 거친 상기 중합액이 코팅된 내구성 섬유를 오토 맹글 머신 투입하고, 균입하게 압입하며, 중간 건조 후 폭을 당겨 소정의 폭으로 조정하며 최종 건조하여 코스메틱 섬유를 제조하는 패딩공정과; 완전히 건조되어 코스메틱 섬유를 권취하는 완제품 권취공정을 포함하여 제조된다. As shown in FIG. 3, the cosmetic fiber comprises an extract solution manufacturing process for producing an extract solution of the oriental raw material, fragrant raw material or cosmetic raw material; A polymerization and a polymerization solution production step in which the above extract solution is put into a polymerization tank in which a polymerization solution is prepared and stirred to polymerize the solution to prepare the polymerization solution; A durable fiber preparation step of winding the durable fiber of a predetermined width on a take-up roller to prepare a durable fiber; An immersion solution manufacturing process for producing an immersion solution; An immersion step of immersing the durable fiber in the immersion solution; A padding step of pouring the durable fiber coated with the polymerization solution through the immersion step into an automender machine, pressurizing the padded fiber by wetting, pulling the padding after the intermediate drying, adjusting the padding to a predetermined width, and finally drying to prepare a cosmetic fiber; And a finished product winding process in which the cosmetic fibers are completely dried and wound.
도 4에 도시되어 있는 것 같이 상기 추출물 솔루션 제조공정은 상기 한방원료, 향원료 또는 화장품원료의 추출물 솔루션을 제조하는 공정으로, 원료를 일정 크기로 잘라 준비하는 원료준비단계와; 준비된 원료를 세척한 후 물기를 제거하는 세척단계와; 수분이 제거된 상기 원료를 일정 압력의 증기압을 갖는 증기로 일정 시간 동안 살균하는 살균단계와; 살균된 상기 원료를 추출기에 넣고 정제수 또는 에탄올을 가하여 추출하여 중간추출물을 얻는 중간추출단계와; 상기 중간추출물에서 상청액(Supernatant)추출물을 분리하는 상청액분리단계와; 상청액추출물에서 불순물을 제거하는 필터링단계와; 여과된 상청액추출물을 증발건조시켜 증발건조추출물을 제조하는 증발건조단계와; 상기 증발건조추출물을 일정 온도와 일정 진공도에서 일정 시간 동안 농축 동결건조하는 동결건조단계와; 동결건조된 추출물을 분쇄기에 넣고 일정 입도 분포로 분쇄하여 분말 추출물을 만드는 분쇄단계와; 일정량의 분말 추출물을 일정량의 정제수에 넣고 교반하여 일정 함량의 추출물 솔루션으로 만드는 추출물 솔루션 제조단계로 구성된다.As shown in FIG. 4, the extract solution manufacturing process is a process for preparing an extract solution of the herbal raw material, the fragrant raw material or the cosmetic raw material, comprising: a raw material preparing step of preparing a raw material by cutting to a predetermined size; A washing step of washing the prepared raw material and then removing water; A sterilizing step of sterilizing the raw material from which moisture has been removed by steam having a vapor pressure of a predetermined pressure for a predetermined time; An intermediate extraction step of adding the sterilized raw material to an extractor and extracting it with purified water or ethanol to obtain an intermediate extract; A supernatant separation step of separating the supernatant extract from the intermediate extract; A filtering step of removing impurities from the supernatant extract; An evaporation drying step of evaporating and drying the filtered supernatant extract to produce an evaporated dry extract; A freeze-drying step of concentrating and freeze-drying the evaporated and dried extract at a constant temperature and a constant degree of vacuum for a predetermined time; Pulverizing the lyophilized extract into a powder and pulverizing the powder into a predetermined particle size distribution; And a step of preparing an extract solution by adding a certain amount of the powdery extract into a certain amount of purified water and stirring to obtain a certain amount of the extract solution.
상기 중간추출단계는 원료 중량 대비 1~10배의 정제수 또는 에타놀을 부과하여 1 내지 2기압, 80∼120℃하에 1∼12시간 열수 추출한다.In the intermediate extraction step, 1 to 10 times of purified water or ethanol is added to the raw material weight, and the mixture is subjected to hot water extraction under 1 to 2 atm and 80 to 120 ° C for 1 to 12 hours.
상기 살균단계는 1.0kg/cm2G 이상의 증기압을 갖는 증기로 5~10분 동안 살균한다.The sterilization step is sterilized with steam having a vapor pressure of 1.0 kg / cm < 2 > G or more for 5 to 10 minutes.
상기 동결건조단계는 -20 ~ -55℃, 진공도 0.01~1torr에서 20~100시간 동안 농축 동결건조시킨다.The lyophilization step is performed by lyophilizing at -20 to -55 ° C and a degree of vacuum of 0.01 to 1 torr for 20 to 100 hours.
상기 분쇄단계에서 분말 추출물은 정제수에 잘 녹을 수 있도록 200Mesh(74μm) 이하의 사이즈가 95% 이상 되게 분쇄하여야 한다.In the pulverization step, the powder extract should be pulverized to have a size of 200 Mesh (74 μm) or less of 95% or more so as to be well dissolved in purified water.
상기 추출물 솔루션에서 추출물의 함량은 1~10중량% 인 것이 바람직하다.The content of the extract in the extract solution is preferably 1 to 10% by weight.
상기 중합 및 중합액 제조공정은 상기 추출물 솔루션을 중합액이 제조된 중합탱크에 넣고 교반하여 중합하여 상기 중합액을 제조하는 공정이다.The above-mentioned polymerization and polymerization liquid manufacturing process is a step of putting the above-mentioned extract solution into a polymerization tank in which a polymerization liquid is prepared, stirring and polymerization to prepare the polymerization liquid.
상기 중합액은 상기 한방원료, 향원료 또는 화장품원료로 제조되는 원액 및 추출물(원액 또는 추출물)이 1~10중량%가 함유된 추출물 솔루션을 물 100 중량부에 대하여 계면활성제 1~30중량부와, 개시제 0.2~0.5 중량부와, 모노머 2~5 중량부와, 분산제 0.2~0.5 중량부가 함유된 중합탱크에 넣은 후 교반하여 유화중합(Emulsion Polymerization) 또는 현탁중합(Suspension Polymerization)시켜 상기 마이크로캡슐이 생성되게 제조된다.The polymer solution is prepared by mixing 1 to 30 parts by weight of a surfactant with 100 parts by weight of an extract solution containing 1 to 10% by weight of a raw solution and an extract (raw solution or extract) prepared from the herbal raw materials, fragrance raw materials or cosmetic raw materials, , 0.2 to 0.5 part by weight of an initiator, 2 to 5 parts by weight of a monomer and 0.2 to 0.5 part by weight of a dispersing agent, stirring the mixture, and performing emulsion polymerization or suspension polymerization, .
상기 마이크로캡슐의 쉘이 이중층 구조를 가질 때의 상기 중합액은 상기 한방원료, 향원료 또는 화장품원료로 제조되는 추출물이 1~10중량%가 함유된 추출물 솔루션을 물 100 중량부에 대하여 계면활성제 1~30중량부와, 개시제 0.2~0.5 중량부와, 모노머 2~5 중량부와, 무기물 전구체 1.5~5.5 중량부와 분산제 0.2~0.5 중량부가 함유된 중합탱크에 넣은 후 교반하여 유화중합(Emulsion Polymerization) 또는 현탁중합(Suspension Polymerization) 후 염기성 분위기 하에서 가수분해하여 내부에 무기층이 형성되고, 외부에 고분자층이 형성되는 이중층 구조의 상기 마이크로캡슐이 생성되게 제조된다.When the microcapsule shell has a bilayer structure, the above-mentioned polymerization solution is prepared by adding an extract solution containing 1 to 10% by weight of the extract prepared from the herbal raw material, the fragrance raw material or the cosmetic raw material to the surfactant 1 30 parts by weight of an initiator, 0.2 to 0.5 parts by weight of an initiator, 2 to 5 parts by weight of a monomer, 1.5 to 5.5 parts by weight of an inorganic precursor and 0.2 to 0.5 parts by weight of a dispersing agent, followed by emulsion polymerization ) Or suspension polymerization, and hydrolyzing the polymer in a basic atmosphere to form an inorganic layer on the inside and a polymer layer on the outside of the microcapsule.
상기 무기물의 전구체는 알칼리금속, 알칼리토금속, 보론(B), 알루미늄(Al), 갈륨(Ga), 인듐(In), 티타늄(Ti), 실리콘(Si), 게르마늄(Ge), 주석(Sn), 납(Pb), 인(P), 비소(As), 안티모니(Sb) 및 비스무스(Bi) 중에서 선택된 1종의 단일원소 또는 2종 이상의 혼합물의 카르복실산염 및 알콕사이드 화합물 중에서 선택된 것이다.The precursor of the inorganic material may be an alkali metal, an alkaline earth metal, boron (B), aluminum (Al), gallium (Ga), indium (In), titanium (Ti), silicon (Si), germanium (Ge) , A single element selected from lead (Pb), phosphorus (P), arsenic (As), antimony (Sb) and bismuth (Bi) or a mixture of two or more thereof.
상기 무기층은 무기금속의 옥사이드, 설파이드, 셀레나이드. 나이트라이드 및 포스파이드 중에서 선택된 산화물층이다.The inorganic layer is an inorganic metal oxide, a sulfide, or a selenide. Oxide, nitride, and phosphide.
상기 개시제는 반응을 시작할 수 있게 하는 물질로, Potassium persulfate, Ammonium persulfate, BPO(Benzoyl Peroxide), Rongalite C 중 어느 하나를 사용한다.The initiator is a substance capable of initiating the reaction, and one of Potassium persulfate, Ammonium persulfate, BPO (Benzoyl Peroxide) and Rongalite C is used.
상기 Potassium persulfate는 무색 또는 백색의 결정으로 물에 가용되며 저장중 서서히 분해되면서 산성염을 생성하며, 반응 온도는 약 75～85℃정도이다.Potassium persulfate is colorless or white crystals, soluble in water, and gradually decomposes during storage to form acid salts, with a reaction temperature of about 75 to 85 ° C.
상기 Ammonium persulfate는 백색 분말이며 물에 녹기 쉬우며 그 수용액은 약산성이며, 쉽게 라디칼을 생성하며 강력한 산화작용을 하고, 습기에 의해서도 산소를 발생하면서 서서히 분해되며, 습도의 상승에 따라서 분해가 촉진되고 120℃에서는 급속히 촉진된다.Ammonium persulfate is a white powder and is easy to dissolve in water. Its aqueous solution is weakly acidic, easily generates radicals, has strong oxidizing action, decomposes gradually while generating oxygen by moisture, accelerates decomposition with increasing humidity ℃.
상기 BPO(Benzoyl Peroxide)는 백색의 분말결정이며 무미, 무취의 분말이며, 폭발성을 가지고 있으며 융점은 103～105℃이다.The above-mentioned BPO (Benzoyl Peroxide) is a white powder crystal, tasteless, odorless powder, explosive and has a melting point of 103 to 105 ° C.
상기 Rongalite C는 백색 분말, 무취, 약 60℃에서 융해, 80℃ 이상에서 분해를 시작하며, 약간의 흡습성, 온액에서 분해, 고온에서 분해되어 환원효과를 나타내고, 산에서는 분해하나 pH 3이상에서는 비교적 안정하다.Rongalite C is a white powder, odorless, melts at about 60 ° C, starts to decompose at 80 ° C or higher, decomposes at a low temperature, decomposes at a high temperature and exhibits a reducing effect. It is stable.
상기 모노머는 PMMA(Poly Methyl Methacrylate)), PVA(Polyvinyl Alcohol), 폴리우레아(Polyurea), 멜라민(Melamine), 아크릴산(Acrylic Acid), 방향족산(Aromatic Acid) 중 어느 하나를 사용한다.The monomer may be selected from the group consisting of PMMA (Poly Methyl Methacrylate), PVA (Polyvinyl Alcohol), Polyurea, Melamine, Acrylic Acid, and Aromatic Acid.
상기 분산제는 일반적으로 분산작용이 요구되는 용도에 사용되며, 고체/액체의 성질에 현저한 변화를 주어 분산효과를 나타내는 물질로, CTAB(Cetyl trimethylammonium bromide), Polyethylene glycol ether, Polyoxyethylene sorbitan mono-oleate, SDS(Sodium dodecylsulfate)로 이루어진 군에서 선택되는 1종 또는 2종 이상이다.The dispersant is generally used in applications requiring a dispersing action, and exhibits a dispersing effect by significantly changing the properties of a solid / liquid. CTAB (Cetyl trimethylammonium bromide), Polyethylene glycol ether, Polyoxyethylene sorbitan mono-oleate, SDS (Sodium dodecylsulfate), and the like.
분산제의 역할은 분산매(Dispersion Medium)내에 고체 입자들을 젖게 하고 분쇄를 도우며 입자들의 재응집을 방지하는 것이다.The role of the dispersant is to wet the solid particles within the Dispersion Medium, assist in milling and prevent re-agglomeration of the particles.
상기 내구성 섬유 준비공정은 일정 폭의 상기 내구성 섬유를 권취롤러에 권취하여 내구성 섬유를 준비하는 공정이다.The durable fiber preparing step is a step of preparing the durable fiber by winding the durable fiber having a predetermined width on the take-up roller.
상기 침지용액 제조공정은 침지용액을 제조하는 공정이다.The immersion solution production process is a process for producing an immersion solution.
상기 침지용액은 상기 중합액 1000 중량부에 대하여 바인더 10~200중량부와, 발수제 70~90 중량부와, 가교제 5.5~7.5 중량부와, 촉매 1.5~3.5 중량부와, UV 차단제 15~30 중량부와, 대전방지제 5~15 중량부와, 방오제 5~15 중량부와, 가공제 20~40 중량부를 포함하여 조성된다.The immersion solution is prepared by mixing 10 to 200 parts by weight of a binder, 70 to 90 parts by weight of a water repellent, 5.5 to 7.5 parts by weight of a crosslinking agent, 1.5 to 3.5 parts by weight of a catalyst, 15 to 30 parts by weight of a UV blocker 5 to 15 parts by weight of an antistatic agent, 5 to 15 parts by weight of an antifouling agent and 20 to 40 parts by weight of a processing agent.
상기 바인더는 아크릴계 또는 폴리우레탄을 사용한다.The binder is acrylic or polyurethane.
상기 코스메틱 섬유에 있어서, 상기 바인더의 종류와 상기 마이크로캡슐의 재질은 코어의 내부의 한방원료, 향원료 또는 화장품원료가 방출되는 속도와 상기 마이크로캡슐의 장기성능과 지속성에 영향을 미치므로 서서히 방출되고, 장기간 성능이 지속될 수 있도록 해야 한다.In the cosmetic fiber, the type of the binder and the material of the microcapsules are gradually released because they affect the speed at which the one-sided raw material, the fragrance raw material or the cosmetic raw material in the core is released and the long-term performance and the persistence of the microcapsule , So that long-term performance can be sustained.
도 5이 도시되어 있는 것 같이 상기 침지공정은 상기 침지용액이 담기 침지탱크에 에 내구성 섬유를 침지하는 공정이다.As shown in FIG. 5, the immersion process is a process of immersing the durable fiber in the immersion tank containing the immersion solution.
도 5에 도시되어 있는 것 같이 상기 패딩공정은 침지공정을 거친 상기 중합액이 코팅된 내구성 섬유를 오토 맹글 머신 투입하고, 균입하게 압입하며, 중간 건조 후 폭을 당겨 소정의 폭으로 조정하며 최종 건조하여 코스메틱 섬유를 제조하는 공정이다.As shown in FIG. 5, the padding process is a process in which the durable fiber coated with the polymerization liquid, which has undergone the immersion process, is charged into an automechanical machine, Thereby producing a cosmetic fiber.
상기 패딩공정은 오토 맹글 머신(Auto Mangle Machine)에서 진행되며, 상기 침지공정을 거친 상기 침지용액이 코팅된 내구성 섬유가 투입되는 투입단계와, 상기 중합액을 상기 내구성 섬유에 균입하게 압입 하는 압착단계와, 중간 건조단계와, 폭을 당겨 소정의 폭으로 조정하며 최종 건조하는 스텐터(Stenter) 단계를 포함한다.The padding process is carried out in an Auto Mangle Machine. The padding process includes a charging step in which the durable fiber coated with the immersion solution after the immersion process is charged, and a pressing step in which the polymer solution is press- An intermediate drying step, and a stenter step of adjusting the width to a predetermined width by pulling the width and finally drying.
상기 패딩공정의 압착단계는 롤러 압을 3.5~4.5kgf/cm2, 롤러 스피드를 10~20m/min 압착하고, 상기 중간 건조단계는 110~130℃에서 1.5~3분간 건조하며, 상기 스텐터 단계는 160~180℃ 에서 1.5~3분간 실시한다.The pressing step of the padding step presses the roller pressure at 3.5 to 4.5 kgf / cm 2 and the roller speed at 10 to 20 m / min, and the intermediate drying step is performed at 110 to 130 ° C for 1.5 to 3 minutes, It is carried out at 160 to 180 ° C for 1.5 to 3 minutes.
상기 오토 맹글 머신(Auto Mangle Machine)은 상기 침지공정을 거친 상기 중합액이 코팅된 내구성 섬유가 투입되며, 상기 중합액을 상기 내구성 섬유에 균입하게 압입하는 압착부와; 110~130℃에서 1.5~3분간 건조하는 중간건조부와; 폭을 당겨 소정의 폭으로 조정하며 160~180℃ 에서 1.5~3분간 최종 건조하는 스텐트부로 구성된다.The Auto Mangle Machine includes a compression bonding portion into which the durable fiber coated with the polymerization solution having undergone the immersion process is introduced and press-fitting the polymer solution into the durable fiber so as to be intruded into the durable fiber; An intermediate drying part for drying at 110 to 130 DEG C for 1.5 to 3 minutes; And a stent part which is adjusted to a predetermined width by pulling its width and finally dried at 160 to 180 ° C for 1.5 to 3 minutes.
상기 중간건조부와 스텐트부는 단열구조로 되어 있고, 내부에 컨베이어가 설치되어 상기 중합액이 코팅된 내구성 섬유가 진행된다.The intermediate drying part and the stent part have a heat insulating structure, and a conveyor is installed inside the durable fiber coated with the polymerization liquid.
상기 중간건조부는 송풍기와 히팅코일을 가지는 중간히팅코일부가 형성되어 열을 방출한다.In the intermediate drying unit, an intermediate heating coil unit having a blower and a heating coil is formed to emit heat.
상기 스텐트부는 송풍기와 히팅코일을 가지는 스텐트히팅코일부가 형성되어 열을 방출한다.The stent part is formed with a blower and a stent heating coil part having a heating coil to emit heat.
본 발명의 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유에 따르면 입을 수 있는 섬유 형태로 제조가 가능하여 웨어러블 코스메틱 섬유이며, 한방원료, 향원료 또는 화장품원료를 캡슐에 로딩하여 여러 번 세탁 후에도 그 성능을 유지하며, 기능성을 지속적으로 발현할 수 있는 장점이 있다.According to the highly durable healthcare cosmetic fiber containing the natural extract of the present invention, the wearable cosmetic fiber can be manufactured in the form of a wearable fiber, and it is possible to load the herbal raw material, the fragrance raw material or the cosmetic raw material into the capsule, , And has the advantage of continuously exhibiting the functionality.
Claims (9)
상기 내구성 섬유는 면(Cotton), 폴리에스터(Polyester), 나이론(Nylon), 서큘러 니트(Circular Knit) 또는 트리코트(Tricot)를 포함한 내구성 소재로 제조되고,
상기 마이크로캡슐은 상기 한방원료, 향원료 또는 화장품원료가 천천히 방출되는 서방형 타입이며,
상기 중합액은 상기 한방원료, 향원료 또는 화장품원료로 제조되는 원액 및 추출물이 1~10중량%가 함유된 추출물 솔루션을 물 100 중량부에 대하여 계면활성제 1~30중량부와, 개시제 0.2~0.5 중량부와, 모노머 2~5 중량부와, 분산제 0.2~0.5 중량부가 함유된 중합탱크에 넣은 후 교반하여 유화중합(Emulsion Polymerization) 또는 현탁중합(Suspension Polymerization)시켜 상기 마이크로캡슐이 생성되게 제조되고,
상기 코스메틱 섬유는 내구성 섬유 100중량부에 대하여 상기 마이크로캡슐 1~20 중량부와, 바인더 1~20 중량부를 포함하며,
상기 패딩공정은 오토 맹글 머신(Auto Mangle Machine)에서 진행되며, 상기 침지공정을 거친 침지용액이 코팅된 내구성 섬유가 투입되는 투입단계와, 상기 중합액을 상기 내구성 섬유에 균입하게 압입 하는 압착단계와, 중간 건조단계와, 폭을 당겨 소정의 폭으로 조정하며 최종 건조하는 스텐터 단계를 포함하고,
상기 중합탱크에는 물 100 중량부에 대하여 상기 마이크로캡슐의 쉘이 이중층 구조를 가지게 하기 위하여 무기물 전구체 1.5~5.5 중량부가 추가로 함유되며,
상기 마이크로캡슐의 쉘은 이중층 구조를 가지게 상기 유화중합 또는 현탁중합 후 염기성 분위기 하에서 가수분해하여 내부에 무기층이 형성되고, 외부에 고분자층이 형성되는 것을 특징으로 하는 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유
The inside is made by combining a polymerization liquid containing microcapsules, which is loaded with oriental raw materials, fragrance raw materials or cosmetic raw materials, and the outside is encapsulated with shells, into a durable fiber used in fitness and eraser by a process including an immersion process and a padding process In cosmetic fibers,
The durable fiber is made of a durable material including Cotton, Polyester, Nylon, Circular Knit or Tricot,
The microcapsule is a sustained-release type in which the oriental raw material, fragrant raw material or cosmetic raw material is slowly released,
The polymer solution is prepared by mixing 1 to 30 parts by weight of a surfactant, 0.2 to 0.5 parts by weight of an initiator with respect to 100 parts by weight of an extract solution containing 1 to 10% by weight of a raw solution and an extract made of the herbal raw materials, And 2 to 5 parts by weight of a monomer and 0.2 to 0.5 part by weight of a dispersant are added to a polymerization tank and stirred to prepare a microcapsule by emulsion polymerization or suspension polymerization,
Wherein the cosmetic fiber comprises 1 to 20 parts by weight of the microcapsule and 1 to 20 parts by weight of a binder based on 100 parts by weight of the durable fiber,
The padding process is carried out in an Auto Mangle Machine. The padding process includes a charging step in which the durable fiber coated with the immersion solution through the immersion process is charged, a compression step in which the polymerization liquid is press-fit into the durable fiber, , An intermediate drying step, and a stenter step of adjusting the width to a predetermined width by pulling the width,
The polymerization tank further contains 1.5 to 5.5 parts by weight of an inorganic precursor in order to make the shell of the microcapsule have a double layer structure with respect to 100 parts by weight of water,
Wherein the microcapsule shell is hydrolyzed in a basic atmosphere after the emulsion polymerization or suspension polymerization to have a bilayer structure to form an inorganic layer inside and a polymer layer on the outside, Care cosmetic fiber
상기 한방원료는 항산화 항염증 작용과 항알러지 작용 및 자외선을 차단하는 감초추출물, 항산화 작용 및 자외선을 차단하는 상황버섯추출물, 항산화과 항염증 작용 및 자외선을 차단하는 밤껍질인 율피추출물, 오이풀의 뿌리와 뿌리 줄기를 말린 지유(地楡)추출물, 비타민C를 다량 함유하고 항산화 및 향균성 작용을 하는 감귤추출물, 피부진정효과 및 피부영양을 공급하는 알로에추출물, 세포재생효과와 상처치유효과 및 염증완화효과가 있는 병풀추출물 중 하나 또는 둘 이상을 혼합하여 사용하는 것을 특징으로 하는 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유
The method according to claim 1,
The herbal ingredients include antioxidant anti-inflammatory action, antiallergic action, licorice extract to block ultraviolet rays, antioxidant activity, mushroom extract to block ultraviolet rays, antioxidant anti-inflammatory action, ultraviolet ray-shielding chestnut bark extract, Rootstock with dried extracts of ground oil, citrus extract containing antioxidant and antibacterial activity, vitamin C and aloe extract to supply skin soothing effect and skin nutrition, cell regeneration effect, wound healing effect and inflammation relieving effect Which is characterized in that one or two or more of the centromeric extracts are used in combination with a natural dermatological extract
상기 한방원료는 항산화 항염증 작용과 항알러지 작용 및 자외선을 차단하는 감초추출물 5~30 중량%와;
항산화 작용 및 자외선을 차단하는 상황버섯추출물 5~30 중량%와;
항산화과 항염증 작용 및 자외선을 차단하는 밤껍질인 율피추출물 5~30 중량%와;
오이풀의 뿌리와 뿌리 줄기를 말린 지유(地楡)추출물 5~30 중량%와;
비타민C를 다량 함유하고 항산화 및 향균성 작용을 하는 감귤추출물 5~30 중량%와;
피부진정효과 및 피부영양을 공급하는 알로에추출물 5~30 중량%와;
세포재생효과와 상처치유효과 및 염증완화효과가 있는 병풀추출물 3~20 중량%와;
변비에 효과가 있고 식이성섬유, 칼슘 철분이 함유된 백련초추출물 3~20중량%로 조성되는 것을 특징으로 하는 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유
The method according to claim 1,
The herbal ingredients include 5 to 30% by weight of an extract of licorice root which blocks antioxidative anti-inflammatory action, antiallergic action and ultraviolet rays;
5 to 30% by weight of mushroom extract to block antioxidative action and ultraviolet rays;
5 to 30% by weight of an antioxidant anti-inflammatory action and a chestnut shell which blocks ultraviolet rays;
5 to 30% by weight of a ground oil extract of dried root and rootstock of Oleaceae;
5 to 30% by weight of a citrus extract containing a large amount of vitamin C and antioxidant and antibacterial activity;
5 to 30% by weight of an aloe extract to provide skin soothing and skin nutrition;
3 to 20% by weight of Centella asiatica extract having cell regeneration effect, wound healing effect and inflammation relieving effect;
Which is effective for constipation and is composed of 3 to 20% by weight of Rhus verniciflua extract containing dietary fiber and calcium iron, and a durable healthcare cosmetic fiber containing natural extract
상기 패딩공정의 압착단계는 롤러 압을 3.5~4.5kgf/cm2, 롤러 스피드를 10~20m/min 압착하고, 상기 중간 건조단계는 110~130℃에서 1.5~3분간 건조하며, 상기 스텐터 단계는 160~180℃ 에서 1.5~3분간 실시하는 것을 특징으로 하는 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유
The method according to claim 1,
The pressing step of the padding step presses the roller pressure at 3.5 to 4.5 kgf / cm 2 and the roller speed at 10 to 20 m / min, and the intermediate drying step is performed at 110 to 130 ° C for 1.5 to 3 minutes, Characterized in that it is carried out at 160 to 180 DEG C for 1.5 to 3 minutes, characterized in that a high-durable healthcare cosmetic fiber
상기 개시제는 Potassium persulfate, Ammonium persulfate, BPO(Benzoyl Peroxide), Rongalite C 중 어느 하나를 사용하며,
상기 모노머는 PMMA(Poly Methyl Methacrylate)), PVA(Polyvinyl Alcohol), 폴리우레아(Polyurea), 멜라민(Melamine), 아크릴산(Acrylic Acid), 방향족산(Aromatic Acid) 중 어느 하나를 사용하며,
상기 분산제는 CTAB(Cetyl trimethylammonium bromide), Polyethylene glycol ether, Polyoxyethylene sorbitan mono-oleate, SDS(Sodium dodecylsulfate)로 이루어진 군에서 선택되는 1종 또는 2종 이상인 것을 특징으로 하는 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유
The method according to claim 1,
The initiator may be any one of Potassium persulfate, Ammonium persulfate, BPO (Benzoyl Peroxide) and Rongalite C,
The monomer may be selected from the group consisting of PMMA (Poly Methyl Methacrylate), PVA (Polyvinyl Alcohol), Polyurea, Melamine, Acrylic Acid and Aromatic Acid.
Wherein the dispersant is at least one selected from the group consisting of CTAB (Cetyl trimethylammonium bromide), Polyethylene glycol ether, Polyoxyethylene sorbitan mono-oleate and SDS (sodium dodecylsulfate). Cosmetic fiber
상기 침지공정은 상기 침지용액에 상기 내구성 섬유를 침지하여 시행하며,
상기 침지용액은 상기 중합액 1000 중량부에 대하여 바인더 10~200중량부와, 발수제 70~90 중량부와, 가교제 5.5~7.5 중량부와, 촉매 1.5~3.5 중량부와, UV 차단제 15~30 중량부와, 대전방지제 5~15 중량부와, 방오제 5~15 중량부와, 가공제 20~40 중량부를 포함하여 조성되는 것을 특징으로 하는 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유
The method according to claim 1,
The dipping step is carried out by immersing the durable fiber in the immersion solution,
The immersion solution is prepared by mixing 10 to 200 parts by weight of a binder, 70 to 90 parts by weight of a water repellent, 5.5 to 7.5 parts by weight of a crosslinking agent, 1.5 to 3.5 parts by weight of a catalyst, 15 to 30 parts by weight of a UV blocker , 5 to 15 parts by weight of an antistatic agent, 5 to 15 parts by weight of an antifouling agent, and 20 to 40 parts by weight of a processing agent, wherein the antioxidant is a durable healthcare cosmetic fiber containing a natural extract
상기 코스메틱 섬유는 한방원료, 향원료 또는 화장품원료의 추출물 솔루션을 제조하는 추출물 솔루션 제조공정과;
상기 추출물 솔루션을 중합액이 제조된 중합탱크에 넣고 교반하여 중합하여 상기 중합액을 제조하는 중합 및 중합액 제조공정과;
일정 폭의 상기 내구성 섬유를 권취롤러에 권취하여 내구성 섬유를 준비하는 내구성 섬유 준비공정과;
침지용액을 제조하는 침지용액 제조공정과;
상기 침지용액에 내구성 섬유를 침지하는 침지공정과;
침지공정을 거친 상기 중합액이 코팅된 내구성 섬유를 오토 맹글 머신 투입하고, 균입하게 압입하며, 중간 건조 후 폭을 당겨 소정의 폭으로 조정하며 최종 건조하여 코스메틱 섬유를 제조하는 패딩공정과;
완전히 건조되어 코스메틱 섬유를 권취하는 완제품 권취공정을 포함하여 제조되며,
상기 마이크로캡슐의 입자 크기는 200~4000 nm 인 것을 특징으로 하는 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유
The method according to claim 1,
Wherein the cosmetic fiber comprises: an extract solution manufacturing process for preparing an extract solution of a herbal raw material, a fragrance raw material or a cosmetic raw material;
A polymerization and a polymerization solution production step in which the above extract solution is put into a polymerization tank in which a polymerization solution is prepared and stirred to polymerize the solution to prepare the polymerization solution;
A durable fiber preparation step of winding the durable fiber of a predetermined width on a take-up roller to prepare a durable fiber;
An immersion solution manufacturing process for producing an immersion solution;
An immersion step of immersing the durable fiber in the immersion solution;
A padding step of putting the durable fiber coated with the polymerization liquid through the immersion step into an automender machine, pressurizing the dummy fiber intimately, pulling the width after the intermediate drying, adjusting the fiber width to a predetermined width, and finally drying to prepare a cosmetic fiber;
And a finished product winding process in which the cosmetic fiber is completely dried and wound,
Characterized in that the particle size of said microcapsules is from 200 to 4000 nm. ≪ RTI ID = 0.0 > 8. < / RTI >
상기 한방원료는 원료를 일정 크기로 잘라 준비하는 원료준비단계와;
준비된 원료를 세척한 후 물기를 제거하는 세척단계와;
수분이 제거된 상기 원료를 일정 압력의 증기압을 갖는 증기로 일정 시간 동안 살균하는 살균단계와;
살균된 상기 원료를 추출기에 넣고 정제수 또는 에탄올을 가하여 추출하여 중간추출물을 얻는 중간추출단계와;
상기 중간추출물에서 상청액(Supernatant)추출물을 분리하는 상청액분리단계와;
상청액추출물에서 불순물을 제거하는 필터링단계와;
여과된 상청액추출물을 증발건조시켜 증발건조추출물을 제조하는 증발건조단계와;
상기 증발건조추출물을 일정 온도와 일정 진공도에서 일정 시간 동안 농축 동결건조하는 동결건조단계와;
동결건조된 추출물을 분쇄기에 넣고 일정 입도 분포로 분쇄하여 분말 추출물을 만드는 분쇄단계와;
일정량의 분말 추출물을 일정량의 정제수에 넣고 교반하여 일정 함량의 추출물 솔루션으로 만드는 추출물 솔루션 제조단계로 제조되는 것을 특징으로 하는 천연추출물을 함유하는 고내구성 헬스케어 코스메틱 섬유 9. The method according to any one of claims 1 to 8,
Wherein the one-shot raw material comprises a raw material preparation step of preparing a raw material by cutting to a predetermined size;
A washing step of washing the prepared raw material and then removing water;
A sterilizing step of sterilizing the raw material from which moisture has been removed by steam having a vapor pressure of a predetermined pressure for a predetermined time;
An intermediate extraction step of adding the sterilized raw material to an extractor and extracting it with purified water or ethanol to obtain an intermediate extract;
A supernatant separation step of separating the supernatant extract from the intermediate extract;
A filtering step of removing impurities from the supernatant extract;
An evaporation drying step of evaporating and drying the filtered supernatant extract to produce an evaporated dry extract;
A freeze-drying step of concentrating and freeze-drying the evaporated and dried extract at a constant temperature and a constant degree of vacuum for a predetermined time;
Pulverizing the lyophilized extract into a powder and pulverizing the powder into a predetermined particle size distribution;
Characterized in that a predetermined amount of the powdery extract is put into a certain amount of purified water and stirred to prepare an extract solution solution having a certain amount of the extract solution solution. The durable healthcare cosmetic fiber