KR101783084B1 - Polypropylene composition having low density and low linear thermal expansion, and molded product - Google Patents

Polypropylene composition having low density and low linear thermal expansion, and molded product Download PDF

Info

Publication number
KR101783084B1
KR101783084B1 KR1020140172178A KR20140172178A KR101783084B1 KR 101783084 B1 KR101783084 B1 KR 101783084B1 KR 1020140172178 A KR1020140172178 A KR 1020140172178A KR 20140172178 A KR20140172178 A KR 20140172178A KR 101783084 B1 KR101783084 B1 KR 101783084B1
Authority
KR
South Korea
Prior art keywords
polypropylene resin
resin composition
ethylene
crystallinity
weight
Prior art date
Application number
KR1020140172178A
Other languages
Korean (ko)
Other versions
KR20160066859A (en
Inventor
김윤영
유재정
이수민
김응수
김홍진
임성남
Original Assignee
주식회사 엘지화학
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 엘지화학 filed Critical 주식회사 엘지화학
Priority to KR1020140172178A priority Critical patent/KR101783084B1/en
Publication of KR20160066859A publication Critical patent/KR20160066859A/en
Application granted granted Critical
Publication of KR101783084B1 publication Critical patent/KR101783084B1/en

Abstract

본 발명은 저 비중, 저 선팽창 폴리프로필렌 수지 조성물, 및 성형품에 관한 것으로, 본 발명에 따르면, 열변화에 따른 선팽창 계수가 낮아 주변 환경 온도변화에 민감하지 않고 부품의 치수를 유지하면서도 제품의 중량을 결정짓는 비중이 낮아 부품의 경량화가 가능한 폴리프로필렌 수지 조성물, 및 성형품을 제공하는 효과가 있다.The present invention relates to a low specific gravity, low linear expansion polypropylene resin composition, and a molded article. According to the present invention, since the coefficient of linear expansion due to thermal change is low, It is possible to provide a polypropylene resin composition and a molded article which are low in specific gravity and can be lighter in weight.

Description

저 비중, 저 선팽창 폴리프로필렌 수지 조성물, 및 성형품{Polypropylene composition having low density and low linear thermal expansion, and molded product}TECHNICAL FIELD [0001] The present invention relates to a low specific gravity, low linear expansion polypropylene resin composition,

본 발명은 저 비중, 저 선팽창 폴리프로필렌 수지 조성물, 및 성형품에 관한 것으로, 보다 상세하게는 열변화에 따른 선팽창 계수가 낮아 주변 환경 온도변화에 민감하지 않고 부품의 치수를 유지하면서도 제품의 중량을 결정짓는 비중이 낮아 부품의 경량화가 가능한 폴리프로필렌 수지 조성물, 및 성형품에 관한 것이다. More particularly, the present invention relates to a low specific gravity, low linear expansion polypropylene resin composition, and a molded product. More particularly, the present invention relates to a low specific gravity, low linear expansion polypropylene resin composition, To a polypropylene resin composition which can reduce the weight of parts, and a molded article.

자동차용 부품이 점진적으로 얇아짐에 따라 소재의 기계적 특성은 더욱 우수해져야 하는 상황에서 부품의 치수를 결정짓는 중요한 특성의 하나인 열변화에 따른 선팽창계수와 제품의 중량을 결정짓는 비중이 낮은 폴리프로필렌 수지 조성물이 중요시되고 있다. As automotive parts become progressively thinner, the mechanical properties of the material must be improved. In this situation, one of the important characteristics that determines the dimensions of the parts is the coefficient of linear expansion due to the heat change and the low specific gravity of the polypropylene The resin composition is important.

즉, 차량의 무게를 줄여 연비 향상 등을 실현하려는 목적으로 성형 부품의 특성 중 무기물 함량이 저감되고도 열적 특성이 우수하고, 사출성형이 용이하며, 주변온도 변화에 따른 치수 안정성이 탁월한 자동차 내외장 부품용 폴리프로필렌 수지 조성물 개발이 절실하다. In other words, for the purpose of realizing fuel efficiency improvement by reducing the weight of the vehicle, it is possible to reduce the inorganic content of the molded parts and to improve the thermal characteristics, injection molding is easy, There is an urgent need to develop a polypropylene resin composition for parts.

종래 탈크 등의 무기 충진재를 20% 이상 사용하고 고무 등의 충격보강제로 강성과 충격 밸런스를 갖춘 폴리프로필렌 복합 수지는 비중이 1.2 이상이었으며, 이를 비중 감소화 및 저 수축 특성을 구현하고자 글라스 버블(glass bubble) 등의 저비중 고강성 무기필러을 도입하는 예가 한국공개특허 제2011-0062430호 등에 개시되었고, 혹은 침상형의 울라스토나이트(wollastonite) 등의 도입에 대한 연구가 제시되었다. Conventional polypropylene composite resins, which use 20% or more of inorganic fillers such as talc and have stiffness and impact balance as impact modifiers such as rubber, have a specific gravity of 1.2 or more. In order to achieve the specific gravity reduction and low shrinkage properties, a glass bubble bubble and the like have been disclosed in Korean Patent Laid-Open Publication No. 2011-0062430, or a study on the introduction of a needle-shaped wollastonite has been proposed.

그러나, 무기 충진재의 분산성 및 원가 상승, 그리고 침상형의 울라스토나이트의 경우 이방 수축율 차이가 커 사출후의 휨 변형 등의 문제가 있으며 충격강도에 취약한 한계가 있다.
However, the dispersibility and cost increase of inorganic fillers and the acicular type of wollastonite have different anisotropic shrinkage ratios, resulting in problems such as warpage after injection and there is a limit to the impact strength.

특히 계절변화에 따른 칫수 안정성이 중요한 외장부품 중 사이드실 몰딩(sidesill molding)과 같은 부품이 길고 두께가 얇은 경우에도 적용할 수 있도록, 낮은 함량의 무기 충진재를 사용하면서도 강성, 충격강도, 저 수축성과 치수 안정성을 모두 확보하는 소재의 개발이 필요하게 되었다. Especially, it is possible to use rigid, impact strength, low shrinkage and low shrinkage while using a low content of inorganic filler to be applied even when the parts such as sidesill molding are long and thin in thickness, It has become necessary to develop a material having both dimensional stability.

상기와 같은 종래기술의 문제점을 해결하고자, 본 발명은 자동차 내외장재 용도에 사용하는 폴리프로필렌 수지 조성물 관련하여, 특정 등급의 폴리프로필렌을 포함하는 폴리프로필렌 수지와 특정 성분의 무기 충진재를 포함하는 폴리프로필렌 수지 조성물, 및 이를 포함하는 압출 조성물을 제공함으로써 자동차 내외장재 부품, 특히 부품이 길고 두께가 얇은 부품에까지 계절변화에 따른 칫수 안정성을 확보하면서, 강성, 충격강도, 저 수축성을 제공할 수 있는 폴리프로필렌 수지 조성물, 및 성형품을 제공하는 것을 목적으로 한다. In order to solve the problems of the prior art as described above, the present invention relates to a polypropylene resin composition for use in automobile interior and exterior materials, which comprises a polypropylene resin containing a specific grade of polypropylene and a polypropylene resin A polypropylene resin composition capable of providing rigidity, impact strength, and low shrinkage while securing dimensional stability to automobile interior and exterior parts, particularly long and thin parts, by providing a composition and an extrusion composition containing the same , And a molded article.

상기의 목적을 달성하기 위하여, 본 발명은 In order to achieve the above object,

폴리프로필렌 수지 60 내지 70 중량%, 폴리올레핀계 탄성체 20 내지 35 중량%, 무기충진재 1 내지 12 중량%를 포함하되, 60 to 70% by weight of a polypropylene resin, 20 to 35% by weight of a polyolefin elastomer, and 1 to 12% by weight of an inorganic filler,

상기 폴리프로필렌 수지는 결정화도가 70% 이상인(또는 isotacticity가 95% 이상인) 폴리프로필렌 수지와, 결정화도가 50 내지 70%인 폴리프로필렌 수지를 97:3 내지 60:40의 중량비로 포함하고, The polypropylene resin contains a polypropylene resin having a crystallinity of 70% or more (or an isotacticity of 95% or more) and a polypropylene resin having a crystallinity of 50 to 70% in a weight ratio of 97: 3 to 60:40,

상기 무기충진재는 판상형 필러와 침상형 필러를 10:90 내지 90:10의 중량비로 포함하는 것을 특징으로 하는 폴리프로필렌 수지 조성물을 제공한다.
Wherein the inorganic filler comprises a platy filler and an acicular filler in a weight ratio of 10:90 to 90:10.

또한, 본 발명은 상술한 폴리프로필렌 수지 조성물을 성형시켜 수득되고, 선팽창 계수 변화(△(TD-MD), 여기서 TD는 흐름방향 반대 방향을, MD는 흐름방향을 칭함)가 7.0 이하인 것을 특징으로 하는 성형품을 제공한다. Further, the present invention is characterized in that the polypropylene resin composition is obtained by molding the polypropylene resin composition and has a coefficient of linear expansion (DELTA (TD-MD), where TD is the direction opposite to the flow direction and MD is the direction of flow) To provide a molded article.

본 발명에 따르면, 열변화에 따른 선팽창 계수가 낮아 주변 환경 온도변화에 민감하지 않고 부품의 치수를 유지하면서도 제품의 중량을 결정짓는 비중이 낮아 부품의 경량화가 가능한 폴리프로필렌 수지 조성물, 및 성형품을 제공하는 효과가 있다.According to the present invention, there is provided a polypropylene resin composition which is low in coefficient of linear expansion due to thermal change and insensitive to changes in ambient temperature, can reduce the weight of the product while maintaining the dimensions of the component while reducing the weight of the product, and a molded article .

이하 본 발명을 상세하게 설명한다.
Hereinafter, the present invention will be described in detail.

본 발명의 폴리프로필렌 수지 조성물은 폴리프로필렌 수지 60 내지 70 중량%, 폴리올레핀계 탄성체 20 내지 35 중량%, 무기충진재 1 내지 12 중량%를 포함하되,The polypropylene resin composition of the present invention comprises 60 to 70% by weight of a polypropylene resin , 20 to 35% by weight of a polyolefin elastomer , and 1 to 12% by weight of an inorganic filler,

상기 폴리프로필렌 수지는 결정화도가 70% 이상인 폴리프로필렌 수지와, 결정화도가 50 내지 65%인 폴리프로필렌 수지를 97:3 내지 60:40의 중량비로 포함하고, 상기 무기충진재는 판상형 필러와 침상형 필러를 10:90 내지 90:10의 중량비로 포함하는 것을 특징으로 한다.
Wherein the polypropylene resin comprises a polypropylene resin having a crystallinity of 70% or more and a polypropylene resin having a crystallinity of 50 to 65% in a weight ratio of 97: 3 to 60:40, the inorganic filler comprising a plate- In a weight ratio of 10:90 to 90:10.

상기 결정화도가 70% 이상(또는 isotacticity가 95% 이상)인 폴리프로필렌 수지는 일례로, ASTM D1238에 따라 측정된 용융지수(230 ℃, 2.16 kg 하중)가 10 내지 60 g/10분, 혹은 15 내지 45 g/10분인 것을 사용할 수 있고, 이 범위 내에서 소재의 유동성을 향상시켜 대형부품의 사출 가공성을 확보하는 효과를 제공할 수 있다. The polypropylene resin having a crystallinity of 70% or more (or isotacticity of 95% or more) has a melt index (230 DEG C, 2.16 kg load) measured according to ASTM D1238 of 10 to 60 g / 10 min, 45 g / 10 minutes can be used, and the fluidity of the material can be improved within this range, and the effect of ensuring the injection processability of a large-sized component can be provided.

상기 용어 "결정화도"는 달리 특정하지 않는 한, XRD 분석에 의한 값을 지칭하는 것으로, 그 결정화도가 약 70% 정도이거나, 통상적으로 NMR 분석에 의한 입체규칙도가 95% 이상, 또는 용매추출법인 Xylene Soluble 의 함량이 1.0% 미만인 경우를 고결정성 폴리프로필렌이라 정의한다.
The term "crystallinity" refers to a value obtained by XRD analysis, unless otherwise specified. The term " crystallinity " refers to a value obtained by XRD analysis. The degree of crystallinity is about 70%, or the stereoregularity by NMR analysis is usually 95% A case where the content of solubles is less than 1.0% is defined as high-crystallinity polypropylene.

상기 결정화도가 70% 이상인 폴리프로필렌 수지는 다른 예로, 결정화 온도(Tc) 120 내지 140℃, 및 용융온도(Tm) 160 내지 170℃인 에틸렌-프로필렌 블록 공중합체, 또는 그 혼합물일 수 있다.Polypropylene resin having a crystallinity of 70% For another example, the crystallization temperature (Tc) 120 to 140 ℃, and melting temperature (Tm) 160 to 170 ℃ of ethylene may be a propylene block copolymer, or a mixture thereof.

상기 용어 "결정화 온도(Tc)" 및 "용융 온도(Tm)"은 달리 특정하지 않는 한, 고분자 물질의 열분석 장비인 시차주사열량계 (Differential ScanningUnless otherwise specified, the terms "crystallization temperature (Tc)" and "melting temperature (Tm)" refer to a differential scanning calorimeter

Calorimeter, DSC)를 이용하여 측정한 값을 지칭한다.
Calorimeter, DSC).

상기 결정화도가 50 내지 70%인 폴리프로필렌 수지는 일례로, ASTM D1238에 따라 측정된 용융지수(230 ℃, 2.16 kg 하중)가 5 내지 30 g/10분, 혹은 15 내지 20 g/10분인 것을 사용할 수 있다.
The polypropylene resin having a crystallinity of 50 to 70% is, for example, one having a melt index (230 DEG C, 2.16 kg load) measured according to ASTM D1238 of 5 to 30 g / 10 min, or 15 to 20 g / 10 min .

상기 결정화도가 50 내지 70%인 폴리프로필렌 수지는 구체적인 예로, 에틸렌-프로필렌 코폴리머, 에틸렌-1-부텐 코폴리머, 에틸렌-1-헥산 코폴리머, 에틸렌-4-메틸펜텐 코폴리머 중 1종 이상 선택된 C2계 이종 블록 공중합체 폴리머, 및 프로필렌과의 코폴리머, 랜덤 공중합체 혹은 이들의 혼합물을 사용할 수 있다.
The polypropylene resin having a crystallinity of 50 to 70% is, for example, at least one selected from among ethylene-propylene copolymer, ethylene-1-butene copolymer, ethylene-1-hexene copolymer and ethylene- C2-based heteroblock copolymer polymer, and a copolymer with propylene, a random copolymer, or a mixture thereof.

상기 결정화도가 50 내지 70%인 폴리프로필렌 수지는 다른 예로, 상기 결정화 온도(Tc) 110 내지 130℃, 및 용융온도(Tm) 160 내지 165℃인 에틸렌-프로필렌 및 에틸렌-부텐 공중합체, 및 프로필렌과의 블록 또는 랜덤 공중합체, 또는 그들의 혼합물일 수 있다.
Another example of the polypropylene resin having a crystallinity of 50 to 70% is an ethylene-propylene and ethylene-butene copolymer having a crystallization temperature (Tc) of 110 to 130 ° C and a melting temperature (Tm) of 160 to 165 ° C, Or random copolymers, or mixtures thereof.

상기 C2계 이종 블록 공중합체는 일례로, 상기 소재 조성 중 전체 폴리프로필렌 수지 100 중량% 중 20중량% 이하 범위 내로 포함되고, 이 범위 내에서 범용 폴리프로필렌 대비 우수한 저수축 특성을 나타내며 고 충격강도 특성으로 필러 보강 폴리프로필렌의 약점을 보완할 수 있다.
The C2-based heteroblock copolymer is contained, for example, in the range of 20% by weight or less of 100% by weight of the total polypropylene resin in the material composition, exhibits excellent low shrinkage characteristics in comparison with the general polypropylene within this range, Can compensate for the weak points of the filler-reinforced polypropylene.

상기 폴리올레핀계 탄성체는 일례로, 무정형 에틸렌-알파 올레핀 공중합체일 수 있다. The polyolefin-based elastomer may be, for example, an amorphous ethylene-alpha olefin copolymer.

상기 무정형 에틸렌-알파 올레핀 공중합체는 일례로, 알파 올레핀으로서 옥텐을 포함하되, 상기 알파 올레핀은 무정형 에틸렌-알파 올레핀 공중합체 총 100 중량% 중 30 중량% 이하를 충격강보 보강제 역할로 포함할 수 있다. The amorphous ethylene-alpha olefin copolymer may include octene as the alpha olefin, and the alpha olefin may include not more than 30 wt% of the total 100 wt% of the amorphous ethylene-alpha olefin copolymer as an impact reinforcing agent .

상기 무정형 에틸렌-알파 올레핀 공중합체는 구체적인 예로, 용융지수(190 ℃, 2.16kg)이 1-10g/10분, 혹은 1-7g/10분이고, 밀도가 0.850 내지 0.890 g/cm3, 혹은 0.860 내지 0.880 g/cm3인 것을 사용할 수 있다.
Specific examples of the amorphous ethylene-alpha olefin copolymer include a melt index (190 占 폚, 2.16 kg) of 1-10 g / 10 min or 1-7 g / 10 min, a density of 0.850-0.890 g / cm3 , or 0.860-0.880 g / cm < 3 > can be used.

상기 판상형 필러는 일례로, 비중이 2.5 내지 3.0이고, 직경이 1 내지 15 ㎛인 것을 사용할 수 있다. As the plate-like filler, for example, one having a specific gravity of 2.5 to 3.0 and a diameter of 1 to 15 탆 can be used.

상기 판상형 필러는 구체적인 예로, 탈크(hydrous magnesium silicate)을 사용할 수 있다.
The plate-like filler may be, for example, hydrous magnesium silicate.

상기 침상형 필러는 비중이 1.5 내지 2.5이고, 직경이 0.5 내지 1.0 ㎛이고, 길이가 10 내지 20 ㎛인 것을 사용할 수 있다. The needle-shaped filler may have a specific gravity of 1.5 to 2.5, a diameter of 0.5 to 1.0 mu m, and a length of 10 to 20 mu m.

상기 침상형 필러는 마그네슘계 휘스커(magnesium hydroxide sulfate trihydrate)를 사용할 수 있다.
The needle-shaped filler may be magnesium hydroxide sulfate trihydrate.

상기 수지 조성물은 상기 침상형 필러의 분산제를 더 포함할 수 있다. The resin composition may further comprise a dispersant of the needle-shaped filler.

상기 침상형 필러의 분산제는 일례로, 수지 조성물 총 100 중량% 중 0.1 내지 5 중량%, 혹은 0.5 내지 2 중량% 범위 내로 포함할 수 있고, 이 범위 내에서 침상형 필러의 분산 효과를 극대화할 수 있다. As the dispersing agent for the acicular filler, for example, 0.1 to 5% by weight, or 0.5 to 2% by weight, of 100% And the dispersion effect of the needle-shaped filler can be maximized within this range.

상기 침상형 필러의 분산제는 구체적인 예로, 마그네슘이 10 내지 90중량% 범위로 포함된 스테아레이트계 화합물을 사용할 수 있다.
As the dispersant of the needle-like filler, a stearate compound containing magnesium in an amount of 10 to 90% by weight may be used.

본 발명의 폴리프로필렌 수지 조성물은 구체적인 예로 폴리프로필렌 수지 60 내지 75 중량%, 폴리올레핀계 탄성체 15 내지 30 중량%, 무기충진재 1 내지 10 중량%를 포함하되, The polypropylene resin composition of the present invention includes, for example, 60 to 75% by weight of a polypropylene resin , 15 to 30% by weight of a polyolefin elastomer , and 1 to 10% by weight of an inorganic filler,

상기 폴리프로필렌 수지는 결정화도가 70% 이상인 폴리프로필렌 수지와, 결정화도가 50 내지 70%인 폴리프로필렌 수지를 92:8 내지 70:30의 중량비로 포함하고, 상기 무기충진재는 판상형 필러와 침상형 필러를 20:80 내지 80:20의 중량비로 포함하는 것일 수 있다.
Wherein the polypropylene resin contains a polypropylene resin having a crystallinity of 70% or more and a polypropylene resin having a crystallinity of 50 to 70% in a weight ratio of 92: 8 to 70:30, and the inorganic filler comprises a plate- In a weight ratio of 20:80 to 80:20.

상기 수지 조성물은 필요에 따라 산화방지제, 활제, 광안정제, 사슬연장제, 촉매, 이형제, 안료, 염료, 대전방지제, 항균제, 가공조제, 금속불활성화제, 발연억제제, 무기 충진제, 유리섬유, 내마찰제, 내마모제 및 커플링제 중에서 선택된 1종 이상의 첨가제를 더 포함할 수 있다. 상기 첨가제는 일례로 본 발명의 수지 조성물의 물성에 악영향을 미치지 않는 범위 내에서 사용할 수 있다.
The resin composition may further contain additives such as antioxidants, lubricants, light stabilizers, chain extenders, catalysts, mold release agents, pigments, dyes, antistatic agents, antibacterial agents, processing aids, metal deactivators, And may further include at least one additive selected from the group consisting of an antistatic agent, a wear-inhibiting agent, and a coupling agent. The additive can be used, for example, within a range not adversely affecting the physical properties of the resin composition of the present invention.

본 발명의 폴리프로필렌 수지 조성물은 사출성형 금형에 적용되는 것을 특징으로 한다.
The polypropylene resin composition of the present invention is characterized by being applied to an injection molding die.

본 발명에 따른 성형품은 상술한 폴리프로필렌 수지 조성물을 성형시켜 수득되고, 선팽창 계수 변화(△(TD-MD), 여기서 TD는 흐름방향 반대 방향을, MD는 흐름방향을 칭함)가 7.0 이하인, 혹은 4.2 내지 7.0 범위 내일 수 있다. The molded article according to the present invention is obtained by molding the above-mentioned polypropylene resin composition and has a linear expansion coefficient change (DELTA (TD-MD), where TD is the direction opposite to the flow direction and MD is the flow direction) May range from 4.2 to 7.0.

상기 성형품은 일례로, 자동차용 인스트루먼트 패널, 도어 트림, 콘솔 바디, 필러, 범퍼 등의 내장 부품, 사이드 몰딩, 사이드실 몰딩 등의 외장 부품일 수 있다.
The molded article may be an external component such as an automobile instrument panel, a door trim, a console body, a built-in part such as a pillar or a bumper, a side molding, or a side seal molding.

상기 압출 조성물은 일례로, 에틸렌계 충격보강제를 압출 조성물을 구성하는 펠릿 및 화합물 총 100 중량부 기준, 5 내지 35 중량부, 혹은 20 내지 30 중량부 범위 내로 포함할 수 있고, 이 범위 내에서 어떠한? 효과를 제공할 수 있다.
The extrusion composition may include, for example, an ethylenic impact modifier within the range of 5 to 35 parts by weight, or 20 to 30 parts by weight, based on 100 parts by weight of the total of the pellets and the compounds constituting the extrusion composition, ? Effect can be provided.

이하, 본 발명의 이해를 돕기 위하여 바람직한 실시예를 제시하나, 하기 실시예는 본 발명을 예시하는 것일 뿐 본 발명을 이에 한정하려는 것은 아니다. Hereinafter, preferred embodiments of the present invention will be described in order to facilitate understanding of the present invention, but the present invention is not limited thereto.

[실시예][Example]

실시예 1 내지 4, 비교예 1 내지 4Examples 1 to 4, Comparative Examples 1 to 4

하기 표 1에 나타낸 성분 및 함량을 니더(kneader)에 투입하고 혼련한 다음 이축 압출기를 통해 압출하고 펠릿타이저로부터 펠릿을 수득하였다.
The components and contents shown in Table 1 below were fed into a kneader, kneaded, extruded through a twin screw extruder, and pellets were obtained from the pelletizer.

이하 실시예 및 비교예에서 재료들은 다음과 같다:The materials in the following Examples and Comparative Examples are as follows:

* 폴리프로필렌 수지1(PP-1): 결정화도 70%이상, 결정화온도(Tc) 120℃ 이상 및 용융온도 (Tm) 162℃이며 ASTM D1238에 따라, 230℃의 온도에서 2.16kg 하중 하에서 10분간 측정되는 무게(g)가 30g/10분인 에틸렌 프로필렌 폴리머와 프로필렌의 공중합체(대한유화사, 제품명 Moplen CB5230). Polypropylene resin 1 (PP-1): Measured at a temperature of 230 占 폚 under a load of 2.16 kg for 10 minutes in accordance with ASTM D1238 at a crystallization degree of 70% or more, a crystallization temperature (Tc) of 120 占 폚 or more and a melting temperature (Tm) By weight (g) of 30 g / 10 min. (Copolymer of Ethylene Propylene Polymer and Propylene, product name Moplen CB5230).

*폴리프로필렌 수지2(PP-2): 결정화도 50~70%, 결정화온도(Tc) 110-130℃ 및 용융온도(Tm) 160℃이며, ASTM D1238에 따라, 230℃의 온도에서 2.16kg 하중 하에서 10분간 측정되는 무게(g)가 20g/10분인 에틸렌 프로필렌 및 에틸렌 부텐 폴리머와 프로필렌의 공중합체(폴리미래사, 제품명 Clyrell EC5082). Polypropylene resin 2 (PP-2): having a crystallization degree of 50 to 70%, a crystallization temperature (Tc) of 110-130 占 폚 and a melting temperature (Tm) of 160 占 폚, a temperature of 230 占 폚 and a load of 2.16 kg according to ASTM D1238 A copolymer of ethylene propylene and ethylene butene polymer and propylene having a weight (g) measured for 10 minutes of 20 g / 10 min (Plymouth, product name Clyrell EC5082).

*폴리올레핀계 탄성체(EOR-1): 옥텐 함량이 30중량% 이하인 에틸렌-옥텐계 공중합체로서 용융지수(190℃, 2.16 kg 하중)가 1.1 6/10분이고, 밀도가 0.870g/cm3임(LG화학사 제조 제품명 LUCENE LC170). (EOR-1): an ethylene-octene copolymer having an octene content of 30% by weight or less and having a melt index (at 190 占 폚 under a load of 2.16 kg) of 1.1 6/10 minutes and a density of 0.870 g / Product name: LUCENE LC170).

*판상형 필러(MF-1): 비중 2.7, 직경 1-15㎛인 탈크(hydrous magnesium silicate). * Plate-like filler (MF-1): hydrous magnesium silicate having a specific gravity of 2.7 and a diameter of 1-15 μm.

*침상형 필러(MF-2): 비중 2.3, 직경 0.5-1.0㎛, 길이 10-20㎛인 마그네슘계 휘스커(magnesium hydroxide sulfate trihydrate). * Needle-shaped filler (MF-2): Magnesium hydroxide sulfate trihydrate having a specific gravity of 2.3, a diameter of 0.5-1.0 mu m and a length of 10-20 mu m.

*침상형 필러의 분산제(A-2): 마그네슘-스테아레이트계 화합물. * Dispersant of acicular filler (A-2): Magnesium-stearate compound.

구분
(wt%)
division
(wt%)
실시예Example 비교예Comparative Example
1One 22 33 44 1One 22 33 44 PP-1PP-1 5959 5959 5454 5151 6464 4040 5656 5656 PP-2PP-2 55 55 1010 1515 -- 2525 55 55 EOR-1EOR-1 2626 2626 2626 2424 2626 2525 2828 2828 MF-1MF-1 22 55 55 77 77 55 -- 1010 MF-2MF-2 77 44 44 22 22 44 -- 1010 A-1A-1 1One 1One 1One 1One 1One 1One 1One 1One 총합total 100100 100100 100100 100100 100100 100100 100100 100100 PP-1:PP-2
(중량비)
PP-1: PP-2
(Weight ratio)
92:892: 8 92:892: 8 84:1684:16 77:2377:23 100:0100: 0 62:3862:38 84:1684:16 84:1684:16
MF-1:MF-2
(중량비)
MF-1: MF-2
(Weight ratio)
22:7822:78 56:4456:44 56:4456:44 78:2278:22 78:2278:22 56:4456:44 0:1000: 100 100:0100: 0

<사출 성형품><Injection molded article>

상기 펠릿을 사출기(ENGEL 80Ton)에서 바렐 온도 230 ℃ 조건하 사출하여 충격강도 측정용(6.4mm thick) 시편 및 인장시험용(수축율 측정용) 3.2mm thick Bar 형태의 시편을 준비하여 물성 테스트에 사용하였다. The pellets were injected under the condition of a barrel temperature of 230 ° C in an injection machine (ENGEL 80Ton) to prepare a 3.2 mm thick bar specimen for measuring the impact strength (6.4 mm thick) and a tensile test (for measuring the shrinkage) .

물성 테스트 방식은 다음과 같으며, 결과를 하기 표 2에 정리하였다.The physical properties test method is as follows, and the results are summarized in Table 2 below.

<시험 방식><Test method>

*비중(g/cm3): ASTM D792에 의거하여 측정하였다. Specific gravity (g / cm 3): Measured according to ASTM D792.

*굴곡 탄성률(10mm/min, kgf/cm2): ASTM D270에 의거하여 속도 10mm/min 조건하에 시험하였다. * Flexural modulus (10 mm / min, kgf / cm2): Under the condition of a speed of 10 mm / min in accordance with ASTM D270.

*충격 강도(kgf.cm/cm, 23℃, -30℃): ASTM D256에 의거하여 시편을 Notch내어 시험하였다. * Impact strength (kgf.cm/cm, 23 ° C, -30 ° C): Specimens were tested in Notch according to ASTM D256.

*수축율(3T 인장시편, 1/1000 단위: 인장시편 양끝단에 표시된(금형상 150mm 간격) 두 선의 길이를 2일간 시편 Aging 뒤에 측정하여 수축율을 계산하였다. * Shrinkage (3T tensile specimen, 1/1000 Unit: The shrinkage was calculated by measuring the length of two lines (gold-shaped 150 mm intervals) on both ends of the tensile specimen after 2 days of aging.

* 산팽창 계수( CLTE , the Coefficient of Linear Thermal Expansion , 10(㎛/m℃): 3mm 두께 x 1cm2 면적 시편을 TMA 기기를 사용하여 -40 내지 80℃ 온도 변화에 따른 -30 내지 30℃ 구간 길이 변화를 확인하였다. MD는 시편에서 흐름 방향을 그리고 TD는 시편에서 흐름 반대방향을 칭한다. * Acid expansion coefficient ( CLTE , the Coefficient of Linear Thermal Expansion , 10 (占 퐉 / m 占 폚): 3 mm thickness x 1 cm2 area The specimen was examined for the change in the length of -30 to 30 占 폚 according to the temperature change of -40 to 80 占 폚 using a TMA instrument. MD is the direction of flow in the specimen and TD is the direction of flow in the specimen.

물성Properties 단위unit 실시예Example 비교예Comparative Example 1One 22 33 44 1One 22 33 44 비중importance g/cm3g / cm3 0.950.95 0.950.95 0.950.95 0.950.95 0.940.94 0.950.95 0.980.98 0.970.97 굴곡탄성율
(10mm/min)
Flexural modulus
(10 mm / min)
Kgf/cm2Kgf / cm2 16001600 17201720 16501650 18801880 18201820 14501450 1900019000 2100021000
충격강도(23℃)Impact strength (23 ℃) kgf.cm/cmkgf.cm/cm 5050 4545 4848 4040 3535 5353 3636 3232 충격강도(-30℃)Impact strength (-30 ℃) kgf.cm/cmkgf.cm/cm 55 4.54.5 55 44 2.52.5 5.55.5 3.73.7 2.22.2 수축율(3T 인장시편)Shrinkage (3T tensile specimen) 1/10001/1000 7.87.8 7.37.3 77 7.57.5 7.77.7 6.56.5 88 66 CLTE(MD)CLTE (MD) 10(㎛/m℃)10 (占 퐉 / m 占 폚) 7.87.8 66 5.55.5 6.76.7 77 5.55.5 77 5.85.8 CLTE(TD)CLTE (TD) 1212 11.711.7 1111 1313 13.513.5 10.610.6 1212 13.613.6 △(TD-MD)DELTA (TD-MD) 4.24.2 5.75.7 5.55.5 6.36.3 6.56.5 5.15.1 55 7.57.5

상기 표 2에서 보듯이, 본 발명에 따라 폴리프로필렌 수지, 폴리올레핀계 탄성체, 무기충진재를 포함하되, 상기 폴리프로필렌 수지는 고결정 등급의 폴리프로필렌 수지와 특정 범용 폴리프로필렌 수지를 적정 중량비로 포함하고, 상기 무기충진재는 판상형 필러와 침상형 필러를 적정 중량비로 포함하는 실시예 1 내지 4의 압출 성형품에서는 비중, 굴곡 탄성율, 충격강도(상온, 저온) 및 수축율, 선팽창 계수가 모두 개선된 것을 확인할 수 있었다.
As shown in Table 2, the polypropylene resin according to the present invention comprises a polypropylene resin, a polyolefin elastomer, and an inorganic filler, wherein the polypropylene resin contains a high-crystalline polypropylene resin and a specific general-purpose polypropylene resin in an appropriate weight ratio, It was confirmed that the extrusion molded articles of Examples 1 to 4 containing the tabular filler and the needle-shaped filler in an appropriate weight ratio were improved in specific gravity, flexural modulus, impact strength (room temperature and low temperature), shrinkage ratio and coefficient of linear expansion .

반면, 폴리프로필렌 수지, 폴리올레핀계 탄성체, 무기충진재를 포함하되, 상기 폴리프로필렌 수지는 특정 C2계 이종 공중합 폴리프로필렌 수지를 미포함한 비교예 1의 사출 성형품은 실시예 1 내지 4 대비 충격강도(상온, 저온)가 현저하게 저감되고, 선팽창계수 편차가 다소 불량한 것을 확인할 수 있었다.
On the other hand, the injection-molded product of Comparative Example 1, which contains a polypropylene resin, a polyolefin elastomer, and an inorganic filler, and the polypropylene resin does not contain a specific C2-based heteropolymerized polypropylene resin, Low temperature) was remarkably reduced, and it was confirmed that the linear expansion coefficient deviation was somewhat poor.

또한, 폴리프로필렌 수지, 폴리올레핀계 탄성체, 무기충진재를 포함하되, 상기 폴리프로필렌 수지로서 고결정 등급의 폴리프로필렌 수지를 적정량 미달 함량으로 사용하고, C2계 이종 공중합 폴리프로필렌 수지를 적정량보다 과량 포함한 비교예 2의 사출 성형품은 실시예 1 내지 4 대비 굴곡탄성율이 확연히 저감되는 것을 확인할 수 있었다.
The polypropylene resin composition according to the present invention is a polypropylene resin composition comprising a polypropylene resin, a polyolefin elastomer, and an inorganic filler, wherein a polypropylene resin having a high crystalline grade is used in an amount less than the proper amount and a C2 type heteropolymerized polypropylene resin is over- It was confirmed that the bending modulus of elasticity of the injection-molded article of Examples 1 to 4 was significantly lower than that of Examples 1 to 4.

또한, 폴리프로필렌 수지, 폴리올레핀계 탄성체, 무기충진재를 포함하되, 상기 무기충진재는 침상형 필러를 미포함하는 비교예 3의 사출 성형품은 실시예 1 내지 4 대비 비중이 현저하게 증가하고, 충격강도가 상대적으로 저감된 것을 확인할 수 있었다.
Also, the injection molded article of Comparative Example 3, which contains a polypropylene resin, a polyolefin elastomer, and an inorganic filler, wherein the inorganic filler does not include an acicular filler, exhibits a significant increase in specific gravity compared to Examples 1 to 4, , Respectively.

또한, 폴리프로필렌 수지, 폴리올레핀계 탄성체, 무기충진재를 포함하되, 상기 무기충진재는 판상형 필러를 미포함하는 비교예 4의 사출 성형품은 실시예 1 내지 4 대비 비중이 다소 증가되고, 충격강도(상온, 저온), 감소하며, 선팽창 계수(MD)값은 낮아지지만 MD/TD 차이가 커진 것을 확인할 수 있었다.Further, the injection molded article of Comparative Example 4, which contains a polypropylene resin, a polyolefin elastomer, and an inorganic filler, in which the inorganic filler does not include a plate-like filler, has slightly increased specific gravity compared with Examples 1 to 4, ), And the linear expansion coefficient (MD) value was lower, but the MD / TD difference was larger.

Claims (16)

폴리프로필렌 수지 60 내지 70 중량%, 폴리올레핀계 탄성체 20 내지 35 중량%, 무기충진재 1 내지 12 중량% 및 침상형 필러의 분산제 0.1 내지 5 중량%를 포함하되,
상기 폴리프로필렌 수지는 결정화도가 70% 이상인 폴리프로필렌 수지와, 결정화도가 50 내지 70%인 폴리프로필렌 수지를 97:3 내지 60:40의 중량비로 포함하고,
상기 결정화도가 50 내지 70%인 폴리프로필렌 수지는 폴리프로필렌 수지의 총 100 중량% 중 20 중량% 이하인 C2계 이종 공중합 폴리프로필렌 수지를 포함하고,
상기 무기충진재는 판상형 필러와 침상형 필러를 10:90 내지 90:10의 중량비로 포함하고,
상기 침상형 필러의 분산제는 마그네슘이 10 내지 90 중량% 포함된 스테아레이트계 화합물인 것을 특징으로 하는
폴리프로필렌 수지 조성물.
Wherein the polyolefin elastomer comprises 60 to 70% by weight of a polypropylene resin , 20 to 35% by weight of a polyolefin elastomer , 1 to 12% by weight of an inorganic filler , and 0.1 to 5%
The polypropylene resin contains a polypropylene resin having a crystallinity of 70% or more and a polypropylene resin having a crystallinity of 50 to 70% in a weight ratio of 97: 3 to 60:40,
Wherein the polypropylene resin having a crystallinity of 50 to 70% contains 20% by weight or less of a C2-based heteropolymerized polypropylene resin in a total of 100% by weight of the polypropylene resin,
Wherein the inorganic filler comprises a plate-like filler and an acicular filler in a weight ratio of 10:90 to 90:10,
Wherein the dispersing agent of the needle-shaped filler is a stearate-based compound containing 10 to 90% by weight of magnesium
Polypropylene resin composition.
제1항에 있어서,
상기 결정화도가 70% 이상인 폴리프로필렌 수지는 용융지수가 10 내지 60 g/10분인 것을 특징으로 하는
폴리프로필렌 수지 조성물.
The method according to claim 1,
And the polypropylene resin having a crystallinity of 70% or more has a melt index of 10 to 60 g / 10 min
Polypropylene resin composition.
제1항에 있어서,
상기 결정화도가 70% 이상인 폴리프로필렌 수지는 결정화 온도(Tc) 120 내지 140℃, 및 용융온도(Tm) 160 내지 170℃인 에틸렌-프로필렌 블록 공중합체, 또는 그 혼합물인 것을 특징으로 하는
폴리프로필렌 수지 조성물.
The method according to claim 1,
The crystallinity of the polypropylene resin is 70% or more in crystallization temperature (Tc) 120 to 140 ℃, and melting temperature (Tm) of 160 to 170 ethylene ℃ -, characterized in that the propylene block copolymer, or a mixture of
Polypropylene resin composition.
제1항에 있어서,
상기 결정화도가 50% 내지 70%인 폴리프로필렌 수지는 용융지수가 5 내지 30 g/10분인 것을 특징으로 하는
폴리프로필렌 수지 조성물.
The method according to claim 1,
The polypropylene resin having a crystallinity of 50% to 70% has a melt index of 5 to 30 g / 10 min
Polypropylene resin composition.
제1항에 있어서,
상기 결정화도가 50% 내지 70%인 폴리프로필렌 수지는 에틸렌-프로필렌 코폴리머, 에틸렌-1-부텐 코폴리머, 에틸렌-1-헥산 코폴리머, 에틸렌-4-메틸펜텐 코폴리머 중 1종 이상 선택된 C2계 이종 블록 공중합체 폴리머, 와 프로필렌과의 코폴리머, 랜덤 공중합체 혹은 이들의 혼합물인 것을 특징으로 하는
폴리프로필렌 수지 조성물.
The method according to claim 1,
The polypropylene resin having a degree of crystallinity of 50% to 70% may be a C2-type resin selected from at least one type of ethylene-propylene copolymer, ethylene-1-butene copolymer, ethylene-1-hexene copolymer and ethylene- A random copolymer, a mixture thereof, a copolymer of propylene with a homopolymer,
Polypropylene resin composition.
제1항에 있어서,
상기 결정화도가 50 내지 70%인 폴리프로필렌 수지는 상기 결정화 온도(Tc) 110 내지 130℃, 및 용융온도(Tm) 160 내지 165℃인 에틸렌-프로필렌 및 에틸렌-부텐 공중합체, 와 프로필렌과의 블록 또는 랜덤 공중합체, 또는 그들의 혼합물인 것을 특징으로 하는
폴리프로필렌 수지 조성물.
The method according to claim 1,
The polypropylene resin having a crystallinity of 50 to 70% is a block of ethylene-propylene and ethylene-butene copolymers and propylene having the above crystallization temperature (Tc) of 110 to 130 캜 and a melting temperature (Tm) of 160 to 165 캜 Random copolymers, or mixtures thereof.
Polypropylene resin composition.
삭제delete 제1항에 있어서,
상기 폴리올레핀계 탄성체는 무정형 에틸렌-알파 올레핀 공중합체인 것을 특징으로 하는
폴리프로필렌 수지 조성물.
The method according to claim 1,
Wherein the polyolefin-based elastomer is an amorphous ethylene-alpha olefin copolymer
Polypropylene resin composition.
제8항에 있어서,
상기 무정형 에틸렌-알파 올레핀 공중합체는 알파 올레핀으로서 옥텐을 포함하되, 상기 알파 올레핀은 무정형 에틸렌-알파 올레핀 공중합체 총 100 중량% 중 30 중량% 이하인 것을 특징으로 하는
폴리프로필렌 수지 조성물.
9. The method of claim 8,
Wherein the amorphous ethylene-alpha olefin copolymer comprises octene as the alpha olefin, wherein the alpha olefin is 30 wt% or less in the total 100 wt% of the amorphous ethylene-alpha olefin copolymer
Polypropylene resin composition.
제1항에 있어서,
상기 판상형 필러는 비중이 2.5 내지 3.0이고, 직경이 1 내지 15 ㎛인 것을 특징으로 하는
폴리프로필렌 수지 조성물.
The method according to claim 1,
Wherein the plate-like filler has a specific gravity of 2.5 to 3.0 and a diameter of 1 to 15 mu m
Polypropylene resin composition.
제1항에 있어서,
상기 침상형 필러는 비중이 1.5 내지 2.5이고, 직경이 0.5 내지 1.0 ㎛이고, 길이가 10 내지 20 ㎛인 것을 특징으로 하는
폴리프로필렌 수지 조성물.
The method according to claim 1,
Characterized in that the acicular filler has a specific gravity of 1.5 to 2.5, a diameter of 0.5 to 1.0 mu m, and a length of 10 to 20 mu m
Polypropylene resin composition.
삭제delete 삭제delete 제1항에 있어서,
상기 수지 조성물은 사출성형 금형에 적용되는 것을 특징으로 하는
폴리프로필렌 수지 조성물.
The method according to claim 1,
Characterized in that the resin composition is applied to an injection molding die
Polypropylene resin composition.
제1항의 폴리프로필렌 수지 조성물을 성형시켜 수득되고, 선팽창 계수 변화(△(TD-MD), 여기서 TD는 흐름방향 반대 방향을, MD는 흐름방향을 칭함)가 7 이하인 것을 특징으로 하는
성형품.
(TD (MD), where TD is the direction opposite to the flow direction, and MD is the direction of flow) obtained by molding the polypropylene resin composition of claim 1,
Shaped article.
제15항에 있어서,
상기 성형품은 자동차용 인스트루먼트 패널, 도어 트림, 콘솔 바디, 필러, 범퍼, 사이드 몰딩, 또는 사이드실 몰딩인 것을 특징으로 하는
성형품.
16. The method of claim 15,
Wherein the molded article is an automotive instrument panel, a door trim, a console body, a filler, a bumper, a side molding, or a side seal molding
Shaped article.
KR1020140172178A 2014-12-03 2014-12-03 Polypropylene composition having low density and low linear thermal expansion, and molded product KR101783084B1 (en)