KR101634911B1 - Method of manufacturing a micro-sized needle - Google Patents

Method of manufacturing a micro-sized needle Download PDF

Info

Publication number
KR101634911B1
KR101634911B1 KR20150166974A KR20150166974A KR101634911B1 KR 101634911 B1 KR101634911 B1 KR 101634911B1 KR 20150166974 A KR20150166974 A KR 20150166974A KR 20150166974 A KR20150166974 A KR 20150166974A KR 101634911 B1 KR101634911 B1 KR 101634911B1
Authority
KR
Grant status
Grant
Patent type
Prior art keywords
pattern
needle
method
concave
mold
Prior art date
Application number
KR20150166974A
Other languages
Korean (ko)
Inventor
강문식
Original Assignee
주식회사 이너센서
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Grant date

Abstract

마이크로 니들의 제조 방법에 있어서, 하부로 갈수록 작아지는 수평 면적을 갖는 제1 오목 패턴이 형성된 제1 몰드를 준비한 후, 상기 제1 오목 패턴 내에 제1 니들 패턴을 형성한다. A method of manufacturing a microneedle, and then preparing the first mold of claim 1 having a concave pattern having a horizontal area that is gradually reduced downward, a first needle and a pattern in the first concave pattern. 한편, 상기 제1 오목 패턴에 대응되며, 하부로 갈수록 작아지는 수평 면적을 갖는 제2 오목 패턴이 형성된 제2 몰드를 준비한 후, 상기 제2 오목 패턴 내에 제2 니들 패턴을 형성한다. On the other hand, it corresponds to the first concave patterns, After preparing the second mold the second concave pattern formed with a horizontal area becomes smaller toward the bottom, a second needle pattern in the second concave pattern. 이어서, 상기 제1 오목 패턴으로부터 상기 제1 니들 패턴을 이형시켜, 상기 이형된 제1 니들 패턴을 상기 제2 니들 패턴에 결합시킨다. Then, by releasing the first needle pattern from the first recess pattern, thereby combining the first needle and the release pattern to the second pattern needle.

Description

마이크로 니들의 제조 방법{Method of manufacturing a micro-sized needle} Method of manufacturing a microneedle {Method of manufacturing a micro-sized needle}

본 발명은 마이크로 니들의 제조 방법에 관한 것으로, 보다 상세하게는 3차원 구조를 갖는 마이크로 니들의 제조 방법에 관한 것이다. The present invention relates to a method of manufacturing a microneedle, a method of manufacturing a micro-needle having a more particularly to a three-dimensional structure.

인체의 손상을 봉합하기 위하여, 봉합용 니들을 이용하거나 유기 접착제를 이용해 밀봉하는 형식의 밀봉패치를 개발하여 사용하고 있다. In order to seal the body of the damage, using the needle or suture and used to develop a sealing patch for the seal type that use of an organic adhesive.

유기 접착제를 이용하는 경우 그 접착력은 우수하나 화학적 안정성에 대한 논의가 지속되고 있는 상황이다. When using an organic adhesive that the adhesive force is a situation where the continued discussion of the superior one chemical stability. 따라서, 유기 접착제를 대체하기 위하여, 봉합용 니들에 대한 연구가 진행중에 있다. Therefore, to replace the organic adhesive, in the research is in progress for the suture needle.

특히, 인체의 손상을 안정적으로 봉합하기 위하여 3차원 형상, 예를 들면 뿔 형상을 갖는 니들이 요구되고 있다. In particular, the needle having a three-dimensional shape, for example, pyramid shape is required in order to reliably seal the damage to the human body.

상기 봉합용 니들이3차원 형상을 가짐에 따라 그 제작 공정이 복잡하다. Needle for said seaming is complex is that the manufacturing process in accordance with having a three-dimensional shape. 예를 들면, 상기 봉합용 니들의 제작 공정에 있어서 종례의 기술은 CNC 또는 반도체 MEMS 공정기술이 이용되고 있다. For example, in the manufacturing steps of the suture needle of jongrye technology it has been used a CNC or a semiconductor MEMS process technology. 하지만, 상기 종래의 기술의 경우 공정 시간이 상대적으로 길거나 또는 복잡한 세부 공정이 요구된다. However, in the case of the conventional technique the process time is relatively long or complex or detailed process is required.

본 발명은 3차원 구조를 갖는 마이크로 니들을 단순화된 공정을 통하여 용이하게 제조할 수 있는 마이크로 니들의 제조 방법을 제공한다. The present invention provides a method of micro-needle that can be easily manufactured through a simplified process, a microneedle having a three-dimensional structure.

본 발명의 일 실시예에 따른 마이크로 니들의 제조 방법에 있어서, 하부로 갈수록 작아지는 수평 면적을 갖는 제1 오목 패턴이 형성된 제1 몰드를 준비한 후, 상기 제1 오목 패턴 내에 제1 니들 패턴을 형성한다. A method of manufacturing a micro-needle according to an embodiment of the present invention, after preparing the first mold the first concave pattern having a horizontal area becomes smaller toward the bottom is formed, forming a first needle pattern in the first concave pattern do. 한편, 상기 제1 오목 패턴에 대응되며, 하부로 갈수록 작아지는 수평 면적을 갖는 제2 오목 패턴이 형성된 제2 몰드를 준비한 후, 상기 제2 오목 패턴 내에 제2 니들 패턴을 형성한다. On the other hand, it corresponds to the first concave patterns, After preparing the second mold the second concave pattern formed with a horizontal area becomes smaller toward the bottom, a second needle pattern in the second concave pattern. 이어서, 상기 제1 오목 패턴으로부터 상기 제1 니들 패턴을 이형시켜, 상기 이형된 제1 니들 패턴을 상기 제2 니들 패턴에 결합시킨다. Then, by releasing the first needle pattern from the first recess pattern, thereby combining the first needle and the release pattern to the second pattern needle.

본 발명의 일 실시예에 있어서, 상기 제1 오목 패턴 내에 제1 니들 패턴을 형성하기 위하여, 상기 제1 몰드 상에 제1 약액을 도포한 후, 상기 제1 몰드로부터 상기 제1 약액을 스퀴징하여 상기 제1 오목 패턴 내에 선택적으로 제1 약액 패턴을 형성하다. In one embodiment of the present invention, the first recess to form a first needle pattern in the pattern, after applying the first chemical liquid onto the first mold, the switch of the first liquid medicament from the first mold squeezing it is to selectively form a first pattern in the chemical liquid of the first concave pattern. 이후, 상기 제1 약액 패턴을 경화시킬 수 있다. Then, it is possible to cure the first liquid medicament-pattern.

여기서, 상기 제1 약액은 poly(glycerol sebacate acrylate) 또는 PEG-(NH2)6)와 같은 생체 친화성 흡수성 고분자 물질을 포함할 수 있다. Here, the first chemical solution may include a bio-compatible water-absorbent polymer materials, such as (glycerol sebacate acrylate) or poly PEG- (NH2) 6).

또한, 상기 제1 약액을 경화시키기 위하여, 열경화 공정 또는 자외선 경화 공정이 수행될 수 있다. Further, a thermosetting process or a UV curing process can be carried out, in order to cure the first liquid medicament.

본 발명의 일 실시예에 있어서, 상기 제1 니들 패턴을 이형시키기 위하여, 상기 제1 니들 패턴을 향하여 템플릿으로 가압하여, 상기 제1 몰들로부터 상기 템플릿 상에 제1 니들 패턴을 이형킬 수 있다. In one embodiment of the present invention, the first in order to release the needle pattern, said first and towards the needle pattern pressed in the template, and a first needle pattern on the template from the first malls can Kiel release.

본 발명의 일 실시예에 있어서, 상기 제1 및 제2 니들 패턴들 각각은 뿔 형상을 가짐에 따라 복층의 등대 형상으로 마이크로 니들이 제조될 수 있다. In one embodiment of the present invention, the each of the first and second needle pattern is micro-needles may be manufactured in the shape of a beacon in accordance with the multi-layer has a horn shape.

본 발명에 따른 마이크로 니들의 제조 방법에 따르면, 복수의 몰드들을 이용하는 몰딩 공정 및 전사 공정을 통하여 복층의 뿔 형상과 같은 3차원 구조를 갖는 마이크로 니들을 용이하게 제조할 수 있다. According to the production method of microneedle of the present invention, a microneedle having a three-dimensional structure such as a double layer pyramid shaped through a molding process and a transfer process using a plurality of molds can be easily produced.

도 1은 본 발명의 일 실시예에 따른 마이크로 니들의 제조 방법을 설명하기 위한 공정 단면도들이다. Figure 1 are sectional views for explaining a method of manufacturing a micro-needle according to an embodiment of the present invention.
도 2는 도1의 제조 방법에 따라 제조되 마이크로 니들을 설명하기 위한 단면도이다. Figure 2 is a sectional view illustrating a micro-needle being produced according to the production method of FIG.

이하, 첨부한 도면을 참조하여 본 발명의 실시예에 따른 마이크로 니들의 방법에 대해 상세히 설명한다. Will be described in detail the method of the micro-needle according to the following embodiments, the present invention will be described with reference to the accompanying drawings. 본 발명은 다양한 변경을 가할 수 있고 여러 가지 형태를 가질 수 있는 바, 특정 실시 예들을 도면에 예시하고 본문에 상세하게 설명하고자 한다. The invention will be described in an example in bars, reference to specific embodiments which may have a variety of forms can be applied to various changes and detailed in the text. 그러나, 이는 본 발명을 특정한 개시 형태에 대해 한정하려는 것이 아니며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변경, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다. This, however, is by no means to restrict the invention to the particular form disclosed, it is to be understood as embracing all included in the spirit and scope of the present invention changes, equivalents and substitutes. 각 도면을 설명하면서 유사한 참조부호를 유사한 구성요소에 대해 사용하였다. In describing the drawings was used for a similar reference numerals to like elements. 첨부된 도면에 있어서, 구조물들의 치수는 본 발명의 명확성을 기하기 위하여 실제보다 확대하여 도시한 것이다. In the accompanying drawings, the dimensions of the structure shows an enlarged scale than actual for clarity of the invention.

제1, 제2 등의 용어는 다양한 구성요소들을 설명하는데 사용될 수 있지만, 상기 구성요소들은 상기 용어들에 의해 한정되어서는 안 된다. First, the term of the second, etc., can be used in describing various elements, but the above elements shall not be restricted to the above terms. 상기 용어들은 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다. These terms are only used to distinguish one element from the other. 예를 들어, 본 발명의 권리 범위를 벗어나지 않으면서 제1 구성요소는 제2 구성요소로 명명될 수 있고, 유사하게 제2 구성요소도 제1 구성요소로 명명될 수 있다. For example, without departing from the scope of the present invention, the first component may be referred to as a second configuration can be named as an element, similar to the first component is also a second component.

본 출원에서 사용한 용어는 단지 특정한 실시 예를 설명하기 위해 사용된 것으로, 본 발명을 한정하려는 의도가 아니다. The terms used in the present specification are merely used to describe particular embodiments, and are not intended to limit the present invention. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. Expression in the singular number include a plural forms unless the context clearly indicates otherwise. 본 출원에서, "포함하다" 또는 "가지다" 등의 용어는 명세서 상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다. In this application, the terms "inclusive" or "gajida" terms, such as is that which you want to specify that the features, numbers, steps, operations, elements, parts or to present combinations thereof described in the specification, the one or more other features , numbers, steps, actions, components, parts, or the presence or possibility of combinations thereof and are not intended to preclude.

다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가지고 있다. Unless otherwise defined, including technical and scientific terms, all terms used herein have the same meaning as commonly understood by one of ordinary skill in the art. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥 상 가지는 의미와 일치하는 의미를 가지는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다. Any term that is defined in a general dictionary used shall be construed to have the same meaning in the context of the relevant art, unless expressly defined in this application, it not is interpreted to have an idealistic or excessively formalistic meaning no.

도 1은 본 발명의 일 실시예에 따른 마이크로 니들의 제조 방법을 설명하기 위한 공정 단면도들이다. Figure 1 are sectional views for explaining a method of manufacturing a micro-needle according to an embodiment of the present invention. 도 2는 도1의 제조 방법에 따라 제조되 마이크로 니들을 설명하기 위한 단면도이다. Figure 2 is a sectional view illustrating a micro-needle being produced according to the production method of FIG.

도 1 및 도 2를 참조하면, 본 발명의 일 실시예에 따른 마이크로 니들의 제조 방법에 있어서, 하부로 갈수록 작아지는 수평 면적을 갖는 제1 오목 패턴(115)이 형성된 제1 몰드(110)를 준비한다. 1 and 2, the first concave pattern the first mold 110, 115 is formed with a horizontal area which is a method of manufacturing a micro-needle, gradually decreases downward in accordance with one embodiment of the present invention prepare.

상기 제1 몰드(110)는 실리콘 엘라스토머 계열의 연질의 고분자 물질을 부분적으로 이용함으로써, 후속하여 상기 제1 오목 패턴(115) 내에 형성된 제1 나노 패턴을 상기 제1 몰드(110)로부터 용이하게 이형시킬 수 있다. The first mold 110 easily release from by the soft part, used as a polymer material, and subsequently the first recessed pattern claim wherein the first nano-pattern first mold 110 is formed in the portion 115 of the silicone elastomer-based can.

상기 제1 오목 패턴(115)은 포토 리소그래피 공정 또는 나노 임프링팅 공정 등을 통하여 상기 제1 몰드(110)의 상부 표면에 형성될 수 있다. The first concave pattern 115 may be formed on the upper surface of the first mold 110, such as through a photolithographic process or a nano being spring boot process.

상기 포토 리소그래피 공정에 따르면, 식각 마스크로 상기 제1 몰드(110) 상에 형성하고, 상기 식각 마스크를 이용하여 식각 공정을 통하여 상기 제1 오목 패턴(115)을 형성한다. According to the photolithography process, an etching mask formed on the first mold 110, and using the etching mask to form the first concave patterns 115 through the etching process. 나아가, 상기 식각 마스크를 형성하기 전, 제1 몰드(110) 상에 하드 마스크막(미도시)을 추가적으로 형성할 수도 있다. Further, prior to forming said etching mask, the hard mask layer may be a further (not shown) formed on the first mold (110).

상기 나노 임프린팅 공정에 따르면, 고분자 수지와 같은 유연 물질로 이루어진 유연 베이스를 향하여 스탬프를 가압함으로써, 상기 유연 베이스 상에 오목 패턴이 형성된다. According to the nano-imprinting process, by pressing the stamp against the flexible base made of a flexible material such as polymer resin, the concave pattern on the flexible base is formed. 이후, 상기 유연 베이스를 경화시켜 제1 오목 패턴(115)이 형성된 제1 몰드(110)를 형성할 수 있다. Subsequently, curing the flexible base can be formed in the first concave pattern the first mold 110, 115 is formed.

상기 제1 오목 패턴(115)은 상부에서 하부로 갈수록 좁아지는 수평 단면적을 갖는 오목부에 대응된다. The first concave pattern 115 corresponds to the recessed portion having a horizontal sectional area gradually narrowing from top to bottom. 이로써, 상기 제1 오목 패턴(110)을 매립할 경우, 하부로 갈수록 작은 수평 단면적을 갖는 패턴이 형성될 수 있다. Thus, if the embedding of the first concave pattern 110, toward the lower portion may be formed with a pattern having a horizontal cross-sectional area. 즉, 역전된 뿔 형상을 갖는 패턴이 형성될 수 있다. That is, a pattern having an inverted pyramid shape can be formed.

이후, 상기 제1 오목 패턴(115) 내에 제1 니들 패턴(130)을 형성한다. Then, to form a first needle pattern 130 in the first concave pattern 115. 이로써 역전된 뿔 형상을 갖는 제1 니들 패(130)턴이 형성될 수 있다. Whereby the first needle L 130 turns can be formed with an inverted pyramid shape.

본 발명의 일 실시예에 있어서, 상기 제1 몰드(110) 상에 제1 약액(10)을 도포한다. In one embodiment of the present invention is applied to the first liquid medicament (10) on said first mold (110).

여기서, 상기 제1 약액(10)은 생체 적합성 물질로 이루어진다. Here, the first liquid medicament (10) is made of a biocompatible material. 예를 들면, 상기 제1 약액(10)은 poly(glycerol sebacate acrylate) 또는 PEG-(NH2)6)와 같은 생체 친화성 흡수성 고분자 물질을을 포함할 수 있다. For example, the first liquid medicament 10 may comprise a bio-compatible water-absorbent polymer material such as poly (glycerol sebacate acrylate) or PEG- (NH2) 6). 이와 다르게, 상기 제1 약액(10)은 글루코오스, 락토오스, 프럭토오스, 갈락토오스, 만노오스, 말투로오스, 락투로오스, 말토오스, 수크로오스, 트레할로스, 라피노스, 멜지토오스, 멜리비오스, 자일로비오스, 셀로비오스, 스타키오스(stachyose), 소르비톨, 만니톨, 에리쓰리톨(erythritol), 자이리톨, 라시톨 (lacitol), 말리톨(maltitol); Alternatively, the first liquid medicament (10) is glucose, lactose, fructose, galactose, mannose, speech to trehalose, galacturonic as agarose, maltose, sucrose, trehalose, raffinose, Mel Zito trehalose, melibiose, xylene agarobiose, cellobiose, stachyose (stachyose), sorbitol, mannitol, erythritol (erythritol), jayiritol, Lashio Tall (lacitol), dry tall (maltitol); 글루콘산 및 글루콘산 γ-락톤과 같은 알돈산(aldonic acid) 및 그의 락톤 유도체, 리바라산(ribaraic acid), 아라비나르산(arabinaric acid) 및 갈락타르(galactaric acid)과 같은 알다르산(aldaric acid) 및 그의 락톤 유도체; Gluconic acid and gluconic acid, such as aldonic acid γ- lactone (aldonic acid) and its lactone derivative, Li barasan (ribaraic acid), Arabian carry acid (arabinaric acid) and galactose tar (galactaric acid) as seen differently acid (aldaric acid, such as ) and their lactone derivatives; 글루쿠론산(glucuronic acid), 갈락쿠론산(galaccuronic acid) 및 만뉴론산(mannuronic acid)과 같은 유론산(uronic acid); Glucuronic acid (glucuronic acid), organic acid, such as going rakku acid (galaccuronic acid) and mannyu acid (mannuronic acid) (uronic acid); 전분, 식물성 검(vegetable gums), 치환 셀룰로오스(예컨대, 카복시메틸셀룰로오스, 하이드록시에틸셀룰로오스 및 알킬셀룰로오스), 결정셀룰로오스, 헤파린, 히아루론산, 키토산, 덱스트란, 알지네이트, 트라가칸타, 아가 및 카라기난을 포함한다. Starches, vegetable gums (vegetable gums), a substituted cellulose (e.g., carboxymethyl cellulose, hydroxyethyl cellulose, and alkyl cellulose), the crystalline cellulose, heparin, hyaluronic acid, chitosan, dextran, alginate, Tra including decanter, agar and carrageenan do.

이후, 상기 제1 몰드(110)로부터 상기 제1 약액(10)을 스퀴징하여 상기 제1 오목 패턴(115) 내에 선택적으로 제1 약액 패턴을 형성하다. Then, optionally, it is formed in a first pattern in the chemical liquid from the said first mold (110) squeezing the switch of the first liquid medicament 10, the first concave pattern 115. 이때, 상기 제1 오목 패턴(115)을 제외한 나머지 제1 몰드(110)의 상면에 잔류하는 제1 약액(10)은 제거될 수 있다. In this case, the first liquid medicament 10 remaining on the upper surface of the first rest of the first mold (110) other than the concave pattern 115 may be removed.

이후, 상기 제1 약액 패턴을 경화시킬 수 있다. Then, it is possible to cure the first liquid medicament-pattern. 상기 제1 약액 패턴은 열경화 공정 또는 자외선 경화 공정을 통하여 경화될 수 있다. The first chemical solution pattern may be cured by the heat curing process or a UV curing process.

나아가, 상기 제1 약액 패턴을 경화시키기 위하여, 자연 경화, 건조 경화 또는 송풍 경화 방식이 수행될 수 있다. Further, in order to cure the first liquid medicament-pattern, a natural hardening, drying and curing or hardening the ventilation system it can be performed.

한편, 상기 제1 오목 패턴(115)에 대응되며, 하부로 갈수록 작아지는 수평 면적을 갖는 제2 오목 패턴(125)이 형성된 제2 몰드(120)를 준비한다. On the other hand, the first concave pattern 115 corresponds to and, preparing a second concave pattern the second mold 120, 125 is formed with a horizontal area which is gradually reduced to the lower.

상기 제2 몰드(120)는 제1 몰드(110)와 실질적으로 유사한 공정을 통하여 준비될 수 있다. The second mold 120 can be prepared through a similar process to substantially the first mold (110). 다만, 제2 오목 패턴(125)은 제1 몰드(110)에 형성된 상기 제1 오목 패턴(115)에 대응되는 위치에 형성된다. However, the second concave pattern 125 is formed at a position corresponding to the first concave pattern 115 formed in the first mold (110).

또한 상기 제2 오목 패턴(125)은 상기 제1 오목 패(125)턴보다 실질적으로 작은 수평 단면적으로 가질 수 있다. Further, the second concave pattern 125 may have a first recess panel 125, the horizontal cross-sectional area substantially less than the turn. 이로써 상기 제2 오목 패턴(125) 내에 형성되는 제2 니들 패턴(140)이 상기 제1 니들 패턴(130) 상에 결합되어 마이크로 니들을 제조할 때, 상기 마이크로 니들이 전체적으로 안정적인 구조를 가질 수 있다. This may have a second concave pattern 125, the second needle pattern 140 the first time to produce a micro-needle is coupled to the needle pattern 130, the micro-needle as a whole a stable structure is formed in the.

이어서, 상기 제2 오목 패턴(125) 내에 제2 니들 패턴(140)을 형성한다. Then, the formation of the second concave pattern second needle pattern 140 in 125. The 이때, 상기 제2 니들 패턴(140)은 상기 제1 니들 패턴(130)과 실질적으로 동일한 공정을 통하여 형성될 수 있다. At this time, the second needle pattern 140 may be formed through substantially the same process as with the first needle pattern 130.

이어서, 상기 제1 오목 패턴(115)으로부터 상기 제1 니들 패턴(130)을 이형시켜, 상기 이형된 제1 니들 패턴(130)을 상기 제2 니들 패턴(140)에 결합시킨다. Then, by releasing the first needle pattern 130 from the first concave pattern 115, it is coupled to the release of the first needle and pattern 130 on the second needle pattern 140.

본 발명의 일 실시예에 있어서, 상기 제1 니들 패턴(130)을 이형시키기 위하여, 상기 제1 니들 패턴(130)을 향하여 템플릿(30)으로 가압하여, 상기 제1 몰드(110)로부터 상기 템플릿(30) 상에 제1 니들 패턴(130)을 이형시킬 수 있다. In one embodiment of the present invention, in order to release the first needle pattern 130, and towards the first needle pattern 130 is urged in the template 30, the template from the first mold (110) 30 is a possible variant of the first needle pattern 130 a.

상기 템플릿(30)은 플레이트 형상을 가질 수 있다. The template 30 may have a plate shape. 또한 상기 템플릿(30)의 표면은 접착제로 코팅될 수 있다. In addition, the surface of the template 30 may be coated with adhesive. 이로써, 상기 템플릿(30)에 상기 제1 니들 패턴(130)을 견고하게 부착시킬 수 있다. In this way, the first needle pattern 130 on the template (30) can be securely attached.

나아가, 상기 제1 니들 패턴(130)이 경화되기 전, 상기 템플릿(30)은 상기 제1 몰드(110)를 향하여 가압함으로써, 상기 제1 니들 패턴(130)이 상기 제1 몰드(110)로부터 용이하게 이형되어 상기 템플릿(30)에 용이하게 부착될 수 있다. From In addition, the first by pressing the needle pattern 130 before the curing, the template (30) toward the first mold 110, the first needle pattern 130, the first mold 110 is easily release it can easily be attached to the template (30).

상기 이형된 제1 니들 패턴(130)을 상기 제2 니들 패턴(140)에 결합시키기 위하여, 상기 제1 니들 패턴(130)을 상기 제2 니들 패턴(140)에 마주보도록 정렬시킨다. In order to couple the variant of the first needle and pattern 130 on the second needle pattern 140, the alignment so as to face the first needle pattern 130 on the second needle pattern 140. 이후, 상기 제1 및 제2 니들 패턴들(130, 140)은 상호 열압착 공정을 통하여 결합할 수 있다. Thereafter, the first and second needle patterns 130 and 140 may be coupled through a mutual heat-pressing process. 이 경우, 상기 열압착 공정에 있어서, 상기 제1 및 제2 니들 패턴들(130, 140)에 대한 가열 및 가압을 통하여 상기 제1 및 제2 니들 패턴들(130, 140)이 상호 결합될 수 있다. In this case, in the thermocompression bonding process, the first and second of the first and second needle patterns 130 and 140 through the heating and pressure for the needle pattern (130, 140) can be mutually coupled have.

이와 다르게 상기 제1 및 제2 니들 패턴들(130, 140)은 이들의 접촉 부위에 레이저를 인가하는 레이저 본딩 공정을 통하여 상호 결합될 수 있다. Alternatively the first and second needle patterns 130 and 140 may be coupled together via a laser bonding process of applying a laser to these contacts.

본 발명의 일 실시예에 있어서, 상기 제1 및 제2 니들 패턴들(130, 140) 각각은 뿔 형상을 가짐에 따라 복층의 등대 형상으로 마이크로 니들이 제조될 수 있다. In one embodiment of the present invention, the first and the second needle each of the patterns 130 and 140 are micro-needles may be manufactured in the shape of a beacon in accordance with the multi-layer has a horn shape. 이로써 마이크로 니들을 이용하여 인체의 손상 부위가 용이하게 봉합될 수 있다. Thus there is a damaged area of ​​a human body can be easily sealed by using the micro-needle. 또한 마이크로 니들(100)은 생체 접합용 물질로 이루어진 제1 및 제2 니들 패턴들(130, 140)로 이루어짐에 따라 인체의 해가 발생하는 것이 억제될 수 있다. In addition, micro-needle 100 can be suppressed to a solution of the human body caused by the living body made of an adhesive material the first and second needle patterns 130 and 140 made of for.

상술한 바와 같이, 본 발명에 따른 마이크로 니들의 제조 방법에 따르면, 복수의 몰드들을 이용하는 몰딩 공정 및 전사 공정을 통하여 복층의 뿔 형상과 같은 3차원 구조를 갖는 마이크로 니들을 용이하게 제조할 수 있다. As described above, according to the production method of microneedle of the present invention, it is possible to easily manufacture the microneedle having a three-dimensional structure such as a double layer pyramid shaped through a molding process and a transfer process using a plurality of molds. 상기 3차원 구조를 갖는 마이크로 니들의 형상 및 크기를 조절함으로써, 여러 용도로 응용될 수 있다. By adjusting the shape and size of the micro-needle having the three-dimensional structure, it may be applied for various purposes.

상기에서는 본 발명의 바람직한 실시예를 참조하여 설명하였지만, 해당 기술 분야의 숙련된 당업자는 하기의 특허 청구 범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다. The In has been described with reference to a preferred embodiment of the invention, to vary the invention within the scope not departing from the spirit and scope of the invention defined in the claims of the skilled in the art is to in the art modify and alter that will be able to understand.

Claims (7)

  1. 하부로 갈수록 작아지는 수평 면적을 갖는 제1 오목 패턴이 형성된 제1 몰드를 준비하는 단계; Comprising: a first concave pattern having a horizontal area which is gradually reduced to the lower portion preparing a first mold is formed;
    상기 제1 오목 패턴 내에 제1 니들 패턴을 형성하는 단계; Forming a first pattern in the needle of the first concave pattern;
    상기 제1 오목 패턴에 대응되며, 하부로 갈수록 작아지는 수평 면적을 갖는 제2 오목 패턴이 형성된 제2 몰드를 준비하는 단계; Further comprising: the first corresponds to a concave pattern, preparing a second mold the second concave pattern having a horizontal area becomes smaller toward the lower part is formed;
    상기 제2 오목 패턴 내에 제2 니들 패턴을 형성하는 단계; Forming a second needle pattern in the second concave pattern; And
    상기 제1 오목 패턴으로부터 상기 제1 니들 패턴을 이형시켜, 상기 이형된 제1 니들 패턴을 상기 제2 니들 패턴에 경화된 상태에서 결합시키는 단계를 포함하고, To release the needle and the first pattern from the first concave patterns, and comprising the step of combining the first needle and the release pattern in the cured state to the second needle pattern,
    상기 제1 오목 패턴 내에 제1 니들 패턴을 형성하는 단계는, Forming a first pattern in the needle of the first concave patterns,
    상기 제1 몰드 상에 제1 약액을 도포하는 단계; Applying a first chemical liquid onto the first mold;
    상기 제1 몰드로부터 상기 제1 약액을 스퀴징하여 상기 제1 오목 패턴 내에 선택적으로 제1 약액 패턴을 형성하는 단계: 및 To the switch from the first mold squeezing the first chemical step of selectively forming a first pattern in the chemical liquid of the first concave pattern: and
    상기 제1 약액 패턴을 경화시키는 단계를 포함하고, And curing the first liquid medicament-pattern,
    상기 제1 및 제2 니들 패턴들은 레이저 본딩 공정을 통하여 결합되는 것을 특징으로 하는 마이크로 니들의 제조 방법. The first and second needle patterns method of producing a microneedle, characterized in that coupled through the laser bonding process.
  2. 삭제 delete
  3. 제1항에 있어서, 상기 제1 약액은 poly(glycerol sebacate acrylate) 또는 PEG-(NH2)6)을 포함하는 것을 특징으로 하는 마이크로 니들의 제조 방법. The method of claim 1, wherein the first chemical-liquid method of manufacturing a microneedle, comprising a step of including a poly (glycerol sebacate acrylate) or PEG- (NH2) 6).
  4. 제1항에 있어서, 상기 제1 약액을 경화시키는 단계는 열경화 공정 또는 자외선 경화 공정을 수행하는 것을 특징으로 하는 마이크로 니들의 제조 방법. The method of claim 1 wherein the step of curing the first liquid medicament is method of producing a microneedle, characterized in that to perform a heat curing process or a UV curing process.
  5. 제1항에 있어서, 상기 제1 니들 패턴을 이형시키는 단계는, 상기 제1 니들 패턴을 향하여 템플릿으로 가압하여, 상기 제1 몰들로부터 상기 템플릿 상에 제1 니들 패턴을 이형시키는 단계를 포함하는 것을 특징으로 하는 마이크로 니들의 제조 방법. The method of claim 1 wherein the step of releasing the first needle pattern, comprising the steps of: by pressing the template towards the first needle pattern, the release of the first needle pattern on the template from the first malls method for manufacturing a micro-needle according to claim.
  6. 제1항에 있어서, 상기 제1 및 제2 니들 패턴들 각각은 뿔 형상을 가짐에 따라 복층의 등대 형상으로 제조된 것을 특징으로 하는 마이크로 니들의 제조 방법. The method of claim 1, wherein the first and second needle pattern to each of the method for manufacturing a micro-needle according to claim prepared by lighthouse shape of the multi-layer according to the having a horn shape.
  7. 삭제 delete
KR20150166974A 2015-11-27 2015-11-27 Method of manufacturing a micro-sized needle KR101634911B1 (en)