KR101587044B1 - Ping-pong table upper surface with increasing ping-pong ball rotation and method for manufacturing of the same - Google Patents

Ping-pong table upper surface with increasing ping-pong ball rotation and method for manufacturing of the same Download PDF

Info

Publication number
KR101587044B1
KR101587044B1 KR1020150097078A KR20150097078A KR101587044B1 KR 101587044 B1 KR101587044 B1 KR 101587044B1 KR 1020150097078 A KR1020150097078 A KR 1020150097078A KR 20150097078 A KR20150097078 A KR 20150097078A KR 101587044 B1 KR101587044 B1 KR 101587044B1
Authority
KR
South Korea
Prior art keywords
weight
parts
melamine resin
table tennis
top plate
Prior art date
Application number
KR1020150097078A
Other languages
Korean (ko)
Inventor
안현호
Original Assignee
주식회사 티마운트
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 티마운트 filed Critical 주식회사 티마운트
Priority to KR1020150097078A priority Critical patent/KR101587044B1/en
Application granted granted Critical
Publication of KR101587044B1 publication Critical patent/KR101587044B1/en

Abstract

탁구대 상판 표면의 마찰력을 증가시킬 수 있는 탁구대 상판 및 그 제조 방법에 대하여 개시한다. Capable of increasing the friction table tennis top surface is disclosed with respect to the table tennis top plate and a method of manufacturing the same.
본 발명에 따른 탁구대 상판은 나무 재질의 상판; Table tennis top plate according to the invention the top plate of the wood material; 및 상기 상판 표면에 형성되며, 모양지 및 상기 모양지에 함침되는 멜라민 수지 조성물로 형성되는 시트;를 포함하고, 상기 멜라민 수지 조성물은 멜라민 수지 100 중량부;에 대하여, 천연 규사분말(natural silica flour) 10~20 중량부; And is formed on the top surface, shaped paper and the sheet is formed of a melamine resin composition is impregnated on whether the shape;, natural silica powder (natural silica flour) with respect to; said melamine resin composition, comprising a 100 parts by weight of melamine resin 10 to 20 parts by weight; 및 상기 멜라민 수지의 안정성을 증가시키는 분산제 15~30 중량부;를 포함하고, 상기 천연 규사분말은 탁구대 상판의 마찰력을 증가시키는 것을 특징으로 한다. And dispersing 15-30 parts by weight of increasing the stability of the melamine resin; it characterized in that the inclusion of, and the natural silica powder to increase the frictional force of the table tennis top plate.

Description

탁구공 회전량을 증가시킬 수 있는 탁구대 상판 및 그 제조 방법{PING-PONG TABLE UPPER SURFACE WITH INCREASING PING-PONG BALL ROTATION AND METHOD FOR MANUFACTURING OF THE SAME} Table tennis table tennis balls once the top plate capable of increasing the amount and a production method {PING-PONG TABLE UPPER SURFACE WITH INCREASING PING-PONG BALL ROTATION AND METHOD FOR MANUFACTURING OF THE SAME}

본 발명은 탁구공의 회전량을 증가시킬 수 있는 탁구대 상판 및 그 제조 방법에 관한 것으로, 보다 상세하게는 멜라민 수지 및 천연 규사분말을 혼합하여 마찰력을 증가시킬 수 있는 탁구대 상판에 관한 것이다. The present invention relates to a table tennis top plate which relates to a table tennis table top board and a manufacturing method thereof which can increase the amount of rotation of the table tennis balls, and more particularly to a mixture of a melamine resin and a natural silica powder to increase the frictional force.

또한, 본 발명은 현행 탁구공의 회전량을 증가시키기 위한 탁구대 상판의 제조 방법에 관한 것이다. The invention also relates to a process for preparing a table tennis top plate for increasing the amount of rotation of the current ping-pong ball.

일반적으로 탁구대란, 테이블의 중앙에 설치된 네트를 사이에 두고 1개의 탁구공을 서로 건내며, 탁구 경기를 하기 위해 사용되는 것이다. In general, tennis is, across the network is installed in the middle of the table naemyeo each case one tennis ball, it is being used for a tennis match. 이러한 탁구대는 사각형의 판 형상을 이루는 테이블을 지면과 일정거리를 유지하기 위해 상기 테이블의 하단으로 다수개의 고정다리가 결합되고, 상기 테이블 판 형상에는 테이블의 중앙을 가르도록 네트가 설치되어 구성되며, 테이블의 상부면에는 코팅층을 형성한다. The table tennis is a plurality of fixing legs coupled to the bottom of the table, the table plate shape is consists of the net is provided so as to instruct the center of the table to the table forming the plate-like rectangular holding the ground a certain distance, the upper surface of the table to form a coating layer. 상기 코팅층은 주로 아크릴 수지 및 표면 강화제(액상하드너)를 사용하여 테이블의 강도를 증대시키고 또한 테이블의 상부면을 매끄럽게 한다. The coating layer is mainly to use an acrylic resin and a surface reinforcing agent (Liquid Hardener) to increase the strength of the table and also to smooth the top surface of the table. 위와 같은 작업을 통해 형성된 탁구대 테이블의 상부면에서는, 탁구공이 회전할 경우, 공의 표면 돌기와 이음새로 인해, 원활한 탄성력을 갖고, 사용자가 원하는 방향을 향하여 유동되며 최대 9000rpm로 회전하였다. In the above, the upper surface of the table tennis table, is formed through the same operation, if a ping-pong ball is rotated, because of the surface projection and the joint ball, having a smooth elastic force, the user is flowing towards the desired orientation were rotated at up to 9000rpm.

하지만, 최근에 사용되는 탁구공은 PVC(Polyvinyl chloride) 및 충격강도가 우수한 ABS의 재질로, 탁구공의 표면에 미세한 돌기가 없고, 이음매(seam)가 없는 형태로 제조된다. However, recent ping-pong ball is used in the PVC (Polyvinyl chloride), and a material of an excellent impact strength ABS, there is no minute projections on the surface of a table tennis ball, it is made of a shape without a seam (seam). 따라서, 현행의 탁구공은 유리판처럼 매끈하기 때문에 공과 라켓, 탁구대 표면의 마찰력을 감소시켜 탁구공의 회전량이 최대 6900rpm로 감소되는 것으로 알려져 있다. Thus, the current ping-pong ball is because as smooth as a glass plate to reduce the friction of the ball racket, table tennis surface rotation amount of the table tennis ball is known to be reduced by up to 6900rpm.

공의 스핀과 가장 밀접한 관계가 있는 부분인 탁구대 표면은, 탁구공의 스핀과 속도 변화를 고려하여, 마찰력 증가에 따라 탁구공의 회전량을 증가시키고, 광택이 없는 코팅층으로 형성할 필요가 있다. The portion that is most closely related to the spin of the ball table tennis surfaces it is necessary to consider the spin and speed change of the table tennis ball, in accordance with the friction force increases and to increase the rotation amount of the table tennis ball, luster formed in a free coating layer.

본 발명에 관련된 배경기술로는 대한민국 공개특허공보 제 10-1993-0023047호(1993.12.18. 공개)가 있으며, 상기 문헌에는 탁구대 천판의 제조방법이 개시되어 있다. As background art to the present invention is a (public. 18.12.1993), Republic of Korea Laid-Open Patent Publication No. 10-1993-0023047 Ho, supra, discloses a method of making a table tennis top plate.

본 발명의 목적은 탁구공 회전량을 증가시키기 위해, 마찰력을 증가시킬 수 있는 탁구대 상판 및 그 제조 방법을 제공하는 것이다. An object of the present invention is to provide a table tennis top plate and a manufacturing method which, to increase the friction in order to increase the amount of rotation table tennis balls.

상기 하나의 목적을 달성하기 위한 본 발명의 실시예에 따른 탁구대 상판은, 나무 재질의 상판; Table tennis top plate according to an embodiment of the present invention for achieving the above object is one, the top plate of the wood material; 및 상기 상판 표면에 형성되며, 모양지 및 상기 모양지에 함침되는 멜라민 수지 조성물로 형성되는 시트;를 포함하고, 상기 멜라민 수지 조성물은 멜라민 수지 100 중량부;에 대하여, 천연 규사분말(natural silica flour) 10~20 중량부; And is formed on the top surface, shaped paper and the sheet is formed of a melamine resin composition is impregnated on whether the shape;, natural silica powder (natural silica flour) with respect to; said melamine resin composition, comprising a 100 parts by weight of melamine resin 10 to 20 parts by weight; 및 상기 멜라민 수지의 안정성을 증가시키는 분산제 15~30 중량부;를 포함하고, 상기 천연 규사분말은 탁구대 상판 표면의 마찰력을 증가시키는 것을 특징으로 한다. And dispersing 15-30 parts by weight of increasing the stability of the melamine resin; the natural silica powder, comprising the is characterized in that to increase the friction force of the table tennis top surface.

이때, 상기 멜라민 수지는 멜라민 100중량부 및 상기 멜라민 100 중량부에 대해, 포르말린 30~40 중량부를 포함하는 것이 바람직하다. In this case, the melamine resin is preferred to include for 100 parts by weight of melamine and 100 parts by weight of the melamine, formalin and 30 to 40 parts by weight.

상기 천연 규사분말은 40~50㎛ 입자의 크기를 갖는 것이 바람직하다. The natural silica powder preferably has a particle size of 40 ~ 50㎛.

상기 분산제는 소듐 폴리아크릴레이트를 포함한다. And the dispersing agent comprises sodium polyacrylate.

상기 멜라민 수지 조성물은 멜라민 수지 100 중량부에 대하여, 테트라부틸포스포늄 테트라플루오로보레이트를 10 중량부 이하로 더 포함할 수 있다. The melamine resin composition may further include a borate, tetrabutylphosphonium tetrafluoroborate, based on 100 parts by weight of melamine resin to less than 10 parts by weight.

상기 멜라민 수지 조성물은 멜라민 수지 100 중량부에 대하여, 클로로설폰화 폴리에틸렌고무(CSM)를 10 중량부 이하로 더 포함할 수 있다. The melamine resin composition may further include, chlorosulfonated polyethylene rubber (CSM), relative to 100 parts by weight of melamine resin to less than 10 parts by weight.

상기 멜라민 수지 조성물은, 상기 멜라민 수지 100 중량부에 대하여, 수산화 칼슘 10중량% 수용액을 5 중량부 이하로 더 포함할 수 있다. The melamine resin composition is, with respect to the 100 parts by weight of a melamine resin, may further contain 10% by weight of calcium hydroxide aqueous solution to less than 5 parts by weight.

상기 다른 목적을 달성하기 위한 본 발명의 실시예에 따른 탁구대 상판의 제조 방법은, (a) 멜라민 수지 100 중량부에, 천연 규사분말 10~20 중량부 및 분산제 15~30 중량부를 첨가하여 교반한 후 코팅제를 형성하는 단계; Production method of the table tennis top plate according to an embodiment of the present invention for achieving the above further object is, (a) a melamine resin, 100 parts by weight of natural silica powder of 10 to 20 parts by weight of a dispersing agent, stirring was added 15 to 30 parts by weight after forming a coating agent; 및 (b) 상기 액상의 코팅제를 모양지에 함침하여 고화시킨 후, 시트(sheet)를 형성하는 단계; And (b) forming, the sheet (sheet) and then solidified to form a coating on whether the impregnation of the liquid; 및 (c) 나무재질의 상판 표면에 상기 시트를 접착시켜 프레스(press)하는 단계;를 특징으로 한다. And (c) by adhering the sheet on the top surface of the wood material comprising: a press (press); characterized by a.

이때, 상기 (c) 단계의 프레스는 1분~2분 동안, 180~190℃에서 프레스 기계로 10~20kgf/cm 2 의 압력을 가하여 수행된다. At this time, the press of the (c) step is carried out by adding 1-2 minutes, 10 to a pressure of 20kgf / cm 2 with a press machine at 180 ~ 190 ℃.

본 발명에 따르면, 멜라민 수지 및 천연 규사분말이 함침된 시트를 나무 재질의 상판 표면에 접착시킴으로써, 기존 물성은 그대로 유지하고, 탁구대 상판 표면의 마찰력을 증가시킬 수 있는 효과가 있다. By, according to the present invention, the melamine resin adhesive and the impregnated sheet of natural silica powder to the top surface of the wood material, it is that the existing physical properties are maintained, and may increase the friction force of the table tennis top surface effect.

또한, 클로로설폰화 폴리에틸렌고무(CSM)를 첨가하여 탄성을 갖는 탁구대 표면을 제조함으로써, 탁구공과의 마찰에서 충격을 흡수하고, 탁구공의 회전량을 증가시킬 수 있다. Further, by preparing a tennis surface having a chlorosulfonated polyethylene rubber elasticity by the addition of (CSM), it is possible to absorb the impact of the tennis ball on the friction and increase the amount of rotation of the table tennis balls.

도 1은 본 발명의 실시예에 따른 탁구대 상판을 제조하는 단계를 나타낸 순서도이다. 1 is a flow chart illustrating the steps for producing a table tennis top plate in the embodiment;

본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 첨부되는 도면과 함께 상세하게 후술되어 있는 실시예들을 참조하면 명확해질 것이다. Methods of accomplishing the advantages and features of the present invention and reference to the embodiments that are described later in detail in conjunction with the accompanying drawings will be apparent. 그러나 본 발명은 이하에서 개시되는 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 본 실시예들은 본 발명의 개시가 완전하도록 하며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 발명은 청구항의 범주에 의해 정의될 뿐이다. However, the invention is not limited to the embodiments set forth herein be embodied in many different forms, only, and the present embodiments are to complete the disclosure of the present invention, ordinary skill in the art will to those provided to indicate that the full scope of the invention, the present invention will only be defined by the appended claims.

명세서 전체에 걸쳐 동일 참조 부호는 동일 구성요소를 지칭한다. Like reference numerals throughout the specification refer to like elements.

이하 첨부된 도면을 참조하여 본 발명의 바람직한 실시예에 따른, 탁구대 상판 및 그 제조 방법에 관하여 상세히 설명하면 다음과 같다. If described in detail, table tennis top plate and a manufacturing method according to a preferred embodiment of the present invention with reference to the accompanying drawings as follows.

본 발명에 따른 탁구대 상판은 나무 재질의 상판 및 시트를 포함한다. Table tennis top plate according to the present invention includes a top plate and a sheet of wood material. 상기 시트는 상기 상판 표면에 형성되며, 모양지 및 상기 모양지에 함침되는 멜라민 수지 조성물로 형성된다. The sheet is formed on the top surface shape and the support is formed from a melamine resin composition is impregnated on whether the shape.

멜라민 수지 조성물은, 멜라민 수지 100 중량부에 대해, 천연 규사분말(natural silica flour) 10~20 중량부 및 분산제 15~30 중량부를 포함한다. Melamine resin composition comprises about 100 parts by weight of a melamine resin, a natural silica powder (natural silica flour) 10 ~ 20 parts by weight of a dispersing agent of 15 to 30 parts by weight.

상기 멜라민 수지는 양호한 내수성, 내열성 및 높은 표면경도를 가지며, 나무 재질의 상판에 코팅되는 경우, 상기 표면에서 마찰력을 증가시킬 수 있다. Wherein the melamine resin has a good water resistance, heat resistance and high surface hardness, and, to increase the frictional force at the surface when coated on the top board of wood material.

본 발명에 사용되는 멜라민 수지는 멜라민과 포르말린을 혼합하여 가열하고, 메티놀 멜라민을 형성한 후, 탈수축합 과정을 통해 얻게 되는 열경화성 수지로 액상이다. Melamine resin used in the present invention is a liquid thermosetting resin that is obtained through After heating a mixture of melamine and formaldehyde to form a methicillin play melamine, dehydration condensation process. 이때, 멜라민과 포르말린을 혼합하는 경우, 멜라민은 100 중량부를 사용하고, 포르말린은 상기 멜라민 100중량부에 대해, 30~40중량부를 사용하는 것이 바람직하다. In this case, if the mixture of melamine and formalin, melamine is used on 100 parts by weight, and the formaldehyde is preferably used based on 100 parts by weight of the melamine, 30 to 40 parts by weight. 상기 포르말린이 상기 사용 범위를 초과할 경우, 제조되는 멜라민 수지의 물성이 저하될 수 있다. When the formaldehyde used exceed the range, the physical properties of the melamine resin to be produced may be degraded.

천연 규사분말(natural silica flour)은 규석을 파쇄한 미분으로, 천연 실리카 플로워라고도 불리우며, 보통 99.5중량%의 실리카를 함유한다. Natural silica powder (natural silica flour) is the differential one shred silica, natural silica, also known as bulriwoomyeo floor, it contains a usual silica 99.5% by weight.

상기 천연 규사분말은 탁구대 상판의 강도와 내구성을 높이고, 마찰력을 증가시킨다. The natural silica powder to increase the strength and durability of the table tennis top plate, thereby increasing the frictional force. 상기 천연 규사분말은 40~50㎛ 크기의 입자를 갖는 것이 바람직하다. The natural silica powder preferably has a particle size of 40 ~ 50㎛. 상기 제시된 크기를 벗어나는 경우, 마찰력이 감소되거나 탁구대 미관을 해칠 우려가 있다. If the size falls outside the above set out, there is a possibility that the frictional force is reduced or impair the aesthetics table tennis.

상기 천연 규사분말은, 멜라민 수지 100 중량부에 대해, 10~20 중량부를 포함하는 것이 바람직하다. The natural silica powder is preferably contained based on 100 parts by weight of melamine resin, 10 to 20 parts by weight. 10 중량부 미만일 경우, 내구성이 저하되며, 20 중량부를 초과할 경우, 광택 방지기능 및 마찰력이 저하될 수 있다. If less than 10 parts by weight, the durability is lowered, it can be a glossy and anti-friction force exceeds 20 parts by weight decreases.

분산제는 상기 멜라민 수지의 안정성을 증가시키고, 혼합물의 충분한 분산작용을 일으킨다. Dispersants increases the stability of the melamine resin and, cause a sufficient dispersion effect of the mixture. 상기 분산제는 수지-친화성기로, 상기 수지에 대해 높은 친화도를 갖는 화학기를 갖는다. The dispersant resin by affinity group, and has chemical groups with a high affinity for the resin. 상기 분산제는 폴리에스터, 아크릴레이트 및 우레탄 사슬이 사용될 수 있으나, 보다 구체적으로는 소듐 폴리아크릴레이트(sodium polyacrylate)를 사용하는 것이 바람직하다. The dispersing agents include, but are polyester, acrylate, and urethane chains may be used, and more specifically is preferably used as a sodium polyacrylate (sodium polyacrylate).

상기 분산제는 멜라민 수지 100 중량부에 대해, 15 ~ 30 중량부를 포함하는 것이 바람직하다. The dispersant is preferably contained with respect to 100 parts by weight of melamine resin, 15 to 30 parts by weight. 상기 분산제가 15 중량부 미만일 경우, 혼합물을 분산시키는 기능이 저하될 수 있으며, 30 중량부를 초과하는 경우, 상기 멜라민 수지의 안정성을 감소시켜, 혼합물 속에서는 첨가된 성분끼리 응집되는 현상이 발생할 수 있다. If the dispersant is 15 parts by weight of less, and a function of dispersing the mixture may be reduced, if it exceeds 30 parts by weight, to reduce the stability of the melamine resin, the mixture may cause a phenomenon of agglomeration among the additive components sokeseoneun. 상기 분산제는 실온에서 고체 또는 액체일 수 있다. The dispersant may be either solid or liquid at room temperature.

상기 멜라민 수지 조성물은 테트라부틸포스포늄 테트라플루오로보레이트(tetrbuthylphosphonium tetrafluoroborate)를 더 포함할 수 있다. The melamine resin composition may further comprise a borate (tetrbuthylphosphonium tetrafluoroborate) as tetrabutylphosphonium tetrafluoroborate. 상기 테트라부틸포스포늄 테트라플루오로보레이트를 사용할 경우, 정전기 방지 효과뿐만 아니라, 광택을 감소시키고, 눈부심을 방지할 수 있는 효과가 있다. When using a borate as the tetrabutylphosphonium tetrafluoroborate, there is an effect that it is possible, as well as anti-static effect, and reduce gloss, anti-glare. 또한, 고온에서 열분해를 일으키지 않기 때문에, 작업성을 향상시킬 수 있다. In addition, because the cause decomposition at high temperatures, it is possible to improve the workability. 상기 테트라부틸포스포늄 테트라플루오로보레이트는 멜라민 수지 100 중량부에 대해, 10 중량부 이하로 더 포함될 수 있다. With the tetrabutylphosphonium tetrafluoroborate may be further included to more than 10 parts by weight based on 100 parts by weight of melamine resin. 10 중량부를 초과할 경우, 정전기 및 눈부심 방지 효과가 저하될 수 있다. If more than 10 parts by weight, the antistatic and antiglare effect can be reduced.

상기 멜라민 수지 조성물은 멜라민 수지 100 중량부에 대하여, 클로로설폰화 폴리에틸렌(chlorosulphonated polyethylene, CSM) 고무를 10 중량부 이하로 더 포함할 수 있다. The melamine resin composition may further include, chlorosulfonated polyethylene (chlorosulphonated polyethylene, CSM) rubber based on 100 parts by weight of melamine resin to less than 10 parts by weight.

상기 고무는 탄성 및 내마모성이 우수하기 때문에, 탁구대 표면에서 탁구공과의 마찰에서 충격을 흡수하고 탁구공의 회전량을 증가시킬 수 있는 효과가 있다. Because the rubber is excellent in elasticity and abrasion resistance, to absorb the shock from the table tennis table tennis balls and the friction in the surface and there is an effect that it is possible to increase the amount of rotation of the table tennis balls.

클로로설폰화폴리에틸렌이 10 중량부를 초과하는 경우, 과도한 함량으로 인해 탄성이 저하될 수 있으며, 탁구공과의 마찰에서 충격 흡수가 어려울 수 있다. When chlorosulfonated polyethylene is more than 10 parts by weight, and because of the excessive amount to be elastic is lowered, it can be difficult shock absorption in the ping-pong ball and friction.

상기 탁구대 상판의 멜라민 수지 조성물은, 상기 멜라민 수지 100 중량부에 대하여, 수산화 칼슘 10% 수용액을 5 중량부 이하로 더 포함할 수 있다. Melamine resin composition of the table tennis top plate, with respect to the 100 parts by weight of a melamine resin, may further include a calcium hydroxide aqueous solution of 10% to less than 5 parts by weight.

수산화 칼슘 10% 수용액은 pH를 조절하기 위해 사용된다. Calcium hydroxide 10% aqueous solution is used to adjust the pH.

수산화 칼슘 10% 수용액이 5 중량부 이하로 첨가되는 경우, pH가 7.0 ~7.7로 유지될 수 있으며, 반대로, 첨가량이 5 중량부를 초과하는 경우, 후술할 액상 코팅제를 형성하는 과정에서 급속한 고형화가 발생할 수 있다. When the calcium hydroxide 10% aqueous solution is added to less than 5 parts by weight, result in the pH can be maintained at 7.0 ~ 7.7, on the contrary, if the addition amount exceeds 5 parts by weight, the rapid solidification in the process of forming a liquid coating agent to be described later can.

따라서, 상기 탁구대 상판은 기존의 탁구대와 같이, 물성은 그대로 유지하고 탁구대 상판 표면의 마찰력을 증가시킴으로써, 탁구공의 회전량을 증가시킬 수 있으며, 기존의 탁구공이 갖는 회전량과 유사한 회전량을 가질 수 있다. Thus, the table tennis top plate, such as traditional table tennis, physical properties by maintaining and increasing the friction force of the table tennis top surface as it is, can increase the amount of rotation of the table tennis balls, having a rotation amount similar to the amount of rotation with the ball traditional table tennis can.

탁구대 상판을 제조하는 방법에 관하여 상세히 설명하면 다음과 같다. More specifically with respect to a method for producing a table tennis top plate as follows.

도 1은 본 발명의 실시예에 따른 탁구대 상판의 제조 방법를 나타낸 순서도이다. 1 is a flow chart showing manufacturing bangbeopreul the table tennis top plate in the embodiment;

탁구대 상판의 제조 방법은 코팅제 형성 단계(S100), 시트 형성 단계(S110), 시트를 접착하여 프레스(press)하는 단계(S120)를 포함한다. Table tennis and manufacturing method of the top plate includes the step (S120) that the coating-forming step (S100), the sheet-forming step (S110), by adhering a sheet press (press).

코팅제 형성 단계(S100)는 멜라민 수지 100 중량부가 수용된 용기에 천연 규사분말 10 ~ 20 중량부 및 분산제 15 ~ 30 중량부를 첨가하여 교반한 후 액상의 코팅제를 형성하는 단계이다. Coating formation step (S100) is a step in which after stirring was added to the vessel melamine resin 100 parts by weight of natural silica powder accommodated portions 10 to 20 parts by weight of a dispersing agent of 15 to 30 parts by weight to form a liquid coating.

교반은 대략 30~120분 동안 수행될 수 있으나, 이에 제한되는 것은 아니다. Agitation, but it can be carried out for about 30-120 minutes, without being limited thereto.

이때, pH조절을 위해 상기 멜라민 수지 100 중량부에 대하여, 수산화 칼슘 10% 수용액을 5 중량부 이하로 더 첨가할 수 있다. At this time, with respect to the 100 parts by weight of a melamine resin for the pH adjustment, it can be further added to the calcium hydroxide aqueous solution of 10% to less than 5 parts by weight. 또한, 멜라민 수지 100 중량부에 대하여, 테트라부틸포스포늄 테트라플루오로보레이트 및 클로로설폰화 폴리에틸렌고무(CSM)를 10 중량부 이하로 각각 더 첨가할 수 있다. In addition, the, tetrabutylphosphonium tetrafluoroborate, and chlorosulfonated polyethylene rubber (CSM) with respect to 100 parts by weight of melamine resin can be further added to each of 10 parts by weight or less.

(S110) 단계는 상기 코팅제를 모양지에 함침하여 고화시킨 후, 시트(sheet)를 형성하는 단계이다. (S110) step is then solidified by impregnating the coating whether shape, forming a sheet (sheet).

상기 함침은 가스 상태나 액체로 된 물질을 물체 안에 침투시켜, 그 물체의 특성을 사용 목적에 따라 개선할 수 있다. The impregnation is impregnated with a substance in a gaseous state or a liquid in the object it can be improved according to the characteristics of the object with the intended use. 상기 액상 코팅제를 모양지에 함침한 후에 대략 90~110℃의 온도에서 건조한 뒤, 고화시키면 마찰력이 증가된 시트를 형성할 수 있다. It has been dried at a temperature of approximately 90 ~ 110 ℃ After impregnation the liquid coating on whether shape, when solidified may form a friction increasing sheet. 상기 건조는 코팅제 형성 단계에서 사용된 수용액을 건조시키기 위한 것으로 10~30분 정도 수행될 수 있다. The drying may be carried out about 10-30 minutes for drying to the aqueous solution used in the coating formation step.

(S120) 단계는 나무 재질의 상판 표면에 상기 시트를 접착시켜 프레스(press)하는 단계이다. (S120) is a step to adhere the sheet to the top surface of the wood material comprising: a press (press).

상기 접착 단계는, 상기 상판 표면에 상기 시트가 접착된 상태에서, 1분~2분 동안, 180~190℃에서 프레스 기계로 10~20kgf/cm 2 의 압력을 가하여 수행될 수 있다. The bonding step, in the state in the upper surface of the sheet are bonded together, it can be carried out by adding 1-2 minutes, 10 to a pressure of 20kgf / cm 2 with a press machine at 180 ~ 190 ℃. 상기 온도 및 압력에서 프레스 기계로 열압 접착을 할 경우, 내열성 및 내마모성 등의 표면 물성이 우수한 효과가 있다. When the hot-press bonding by the press machine at the temperature and pressure, it is excellent in surface physical properties such as heat resistance and wear resistance effect.

따라서, 전술한 제조 방법에 따른 상기 탁구대 상판은 증가된 마찰력으로 인해, 탁구공과의 마찰에서 마찰 충격을 흡수할 수 있으며, 이로 인해 탁구공의 회전량의 증가시킴으로써, 기존의 탁구공의 회전량만큼 현행 탁구공의 회전량을 유지시킬 수 있다. Thus, due to the increased frictional force the table tennis top plate according to the method described above produced, can absorb the friction shock in the ping-pong ball and friction, and which thereby causes an increase in the amount of rotation of the table tennis ball, as the amount of rotation of the conventional table tennis balls it is possible to maintain the current amount of rotation of a ping pong ball.

이와 같이 탁구공 회전량을 증가시킬 수 있는 탁구대 상판 및 그 제조 방법에 대하여 그 구체적인 실시예를 살펴보면 다음과 같다. As described above with respect to the table tennis top plate and a method of manufacturing the same which can increase the amount of rotation table tennis ball Referring to the specific examples as follows.

1. 탁구대 상판의 제조 1. Preparation of a ping-pong table tops

실시예 1 Example 1

멜라민 수지 100 중량부에 40 ㎛ 크기의 천연 규사분말(제조원: HOKKO) 10 중량부를 첨가한 후, 소듐 폴리아크릴레이트인 분산제(ADMATECH) 20 중량부를 첨가하여 교반한 후 액상의 코팅제를 형성하였다. Melamine resin 100 parts by weight of natural silica powder 40 ㎛ size of the (manufactured by: HOKKO) 10 weight parts was added, and then stirred by adding sodium polyacrylate dispersing agent of (ADMATECH) 20 parts by weight, to form a liquid coating. 그 다음, 상기 코팅제를 모양지에 함침하여 고화시킨 후, 시트를 형성하고, 나무 재질의 상판 표면에 상기 시트를 접착한 후, 180℃에서 10kgf/cm 2 의 압력을 1분 동안 가하였다. Then, after the solidified was impregnated with the varnish on whether shape after forming a sheet, and bonding the sheet on a top surface of a wooden material, a pressure of 10kgf / cm 2 at 180 ℃ was added over one minute. 결과, 나무 재질의 상판 및 상기 상판 표면에 접착된 시트를 포함하는 탁구대 상판을 제조하였다. Results prepare a table tennis top plate comprising a sheet adhered to the top plate and the upper surface of the wood material.

실시예 2 Example 2

50㎛ 크기의 천연 규사분말을 사용하고, 코팅제에 멜라민 수지 100 중량부에 대하여, 수산화 칼슘10% 수용액을 3 중량부로 더 첨가한 것, 20kgf/cm 2 의 압력을 가하여 접착한 것을 제외하고는 실시예 1과 동일한 조건으로 하였다. 50㎛ size, using natural silica powder with respect to 100 parts by weight of melamine resin in the coating agent, and is carried out, except that it was further added calcium hydroxide 10% aqueous solution of 3 parts by weight, the bonding by applying pressure of 20kgf / cm 2 example 1 and was in the same condition.

실시예 3 Example 3

코팅제에 멜라민 수지 100 중량부에 대하여, 테트라부틸포스포늄 테트라플루오로보레이트(SHINETSU)를 10 중량부 더 첨가한 것을 제외하고는 실시예 1과 동일한 조건으로 하였다. Relative to 100 parts by weight of melamine resin in the coating, was the same condition as in Example 1 except as tetrabutylphosphonium tetrafluoroborate that a borate (SHINETSU) 10 parts by weight is further added.

실시예 4 Example 4

코팅제에 멜라민 수지 100 중량부에 대하여, 클로로설폰화 폴리에틸렌고무(CSM, 제조원: Nippon Kayaku)를 10 중량부로 더 첨가한 것을 제외하고는 실시예 1과 동일한 조건으로 하였다. Relative to 100 parts by weight of melamine resin in the coating, chlorosulfonated polyethylene rubber: was made in the same manner as in Example 1 except that the addition of more (CSM, manufactured by Nippon Kayaku) 10 parts by weight.

실시예 5 Example 5

코팅제에 멜라민 수지 100 중량부에 대하여, 수산화 칼슘10% 수용액 3 중량부, 테트라부틸포스포늄 테트라플루오로보레이트(SHINETSU) 10 중량부 및 클로로설폰화 폴리에틸렌고무(CSM, 제조원: Nippon Kayaku)를 10 중량부를 더 첨가한 것을 제외하고는 실시예 1과 동일한 조건으로 하였다. With respect to the melamine resin 100 parts by weight of the coating agent, 3 parts by weight of calcium hydroxide 10% aqueous solution, tetrabutylphosphonium tetrafluoroborate (SHINETSU) 10 parts by weight of chlorosulfonated polyethylene rubber (CSM, manufacturer: Nippon Kayaku) to 10 parts by weight was in the same condition as in example 1 except that the addition of further parts.

비교예 1 Comparative Example 1

사용된 수지는 멜라민 수지가 아닌 메탈 아크릴수지(Nagase Chemtex)인 것을 제외하고는 실시예 1과 동일한 조건으로 하였다. The resin was used under the same conditions as in Example 1 except that the metal is an acrylic resin (Nagase Chemtex) other than melamine resins.

비교예 2 Comparative Example 2

40 ㎛ 크기의 천연 규사분말 40 중량부를 사용한 것을 제외하고는 실시예 1과 동일한 조건으로 하였다. Size of 40 ㎛, except that natural silica powder 40 parts by weight, was in the same condition as in Example 1.

2. 물성 평가 방법 및 그 결과 2. The property evaluation method and results

상기의 실시예와 비교예는, 나무 재질의 상판 표면에 동일한 두께의 시트를 접착시킨 후, 탁구대 상판을 제조하였다. The above embodiments and comparative examples, after the bonding of the same thickness on the top surface of the wood material sheets to prepare a table tennis top plate. 상기 탁구대 상판 표면에서 아래 항목에 대한 평가를 하였으며, 그 측정 결과(마찰계수)를 다음 [표 1]에 나타내었다. The table tennis was evaluated for the following items in the top surface, the measurement results (friction coefficient) are shown in [Table 1].

(1) 마찰계수 (1) Friction coefficient

Pin on Disk 마찰 마모 시험기(㈜ KNR SYSTEMS사)를 통해 탁구대 상판 표면의 마찰계수를 측정하였다. The friction coefficient of the table tennis top surface was measured via a Pin on Disk Wear and Friction Tester (㈜ KNR SYSTEMS Inc.). 시험조건은 하중 50N, 100N, 거리 2/3㎞, 반경 6㎜, 선속도 100㎜/s, 오일GF4에서 평가하였다. The test conditions were evaluated at a load 50N, 100N, distance 2 / 3㎞, 6㎜ radius, the linear velocity 100㎜ / s, five days GF4.

(2) 표면광택 (2) The surface gloss

디지털 광택제 UGV-4D를 사용하여 입사각 60°에서의 반사광을 측정하였다. The light reflected by the incidence angle 60 ° was measured using a digital polish UGV-4D.

[표1] TABLE 1

Figure 112015066108416-pat00001

실시예 1, 2에 따라 형성된 시트는 멜라민 수지, 천연 규사분말, 분산제 및수산화 칼슘 10% 수용액의 중량부 비율이 제시된 조건의 범위와 일치하였고, 그 결과 탁구대 상판 표면에서의 마찰력이 비교예 1, 2보다 높은 것을 확인할 수 있다. Example 1, was sheet formed in accordance with the second matches the range of the condition parts by weight ratio of the melamine resin, a natural silica powder, a dispersing agent and calcium hydroxide 10% aqueous solution presented, comparing the friction in the result table tennis top surface Example 1, it can be seen that higher than two. 테트라부틸포스포늄 테트라플루오로보레이트가 더 첨가된 실시예 3의 경우, 표면광택의 수치가 실시예1, 2, 4 및 비교예1, 2보다 낮은 것으로 보아, 상기 테트라부틸포스포늄 테트라플루오로보레이트가 멜라민 수지 100중량부에 대해, 대략 10 중량부로 첨가되어야, 눈부심 및 광택 방지 효과가 큰 것을 확인할 수 있다. Tetrabutylphosphonium For the embodiment of tetrafluoroborate is further added to Example 3, as viewed by the surface gloss levels are lower than in Example 1, 2 and 4 and Comparative Examples 1 and 2, the baud rate to the tetrabutylphosphonium tetrafluoroborate is based on 100 parts by weight of a melamine resin, to be added in an amount of about 10 parts by weight, it can be confirmed that the anti-glare and shine effect large.

실시예 4에서는 클로로설폰화 폴리에틸렌고무(CSM)를 10 중량부를 더 첨가하였으며, 탄성력으로 인해 마찰계수가 실시예 1보다 상대적으로 높았다. In Example 4, it was further added to chlorosulfonic polyethylene rubber (CSM) 10 parts by weight, due to the relatively high elasticity coefficient of friction than the first embodiment. 이는 탁구공과의 마찰에서 충격을 흡수하고, 탁구공의 회전량을 증가시키는 것을 예상할 수 있다. This may be expected to absorb the impact of the tennis ball on the friction and increase the amount of rotation of the table tennis balls.

특히, 실시예 5에서와 같이, 수산화 칼슘 10% 수용액, 테트라부틸포스포늄 테트라플루오로보레이트 및 클로로설폰화 폴리에틸렌고무를 코팅제 더 첨가한 경우, 실시예1~4 보다 마찰계수가 월등히 높고, 표면 광택 수치가 현저하게 낮은 것을 확인할 수 있다. In particular, the embodiment as shown in Figure 5, when the coating agent is further added a borate and chlorosulfonated polyethylene rubber as calcium hydroxide 10% aqueous solution, tetrabutylphosphonium tetrafluoroborate, Example coefficient of friction than 1-4 is significantly high, and surface gloss it can be seen that figure is significantly lower.

멜라민 수지 대신 메탈 아크릴 수지를 사용한 비교예 1의 탁구대 상판은, 멜라민 수지를 주 성분으로 한 실시예 1, 2에 비해 마찰계수 값이 낮았다. Table tennis top plate of Comparative Example 1 with a melamine resin instead of metal is an acrylic resin, one embodiment of a melamine resin as a main component in Example 1, the friction coefficient value lower than 2. 천연 규사분말의 함유량이 40 중량부인 비교예 2는, 마찰계수 값이 실시예 1,2 보다 낮았다. Deny the content of 40 parts by weight of natural silica powder in Comparative Example 2, a friction coefficient value lower than that of Examples 1 and 2.

따라서, 상기 제시된 함유량의 멜라민 수지, 마이크로 입자의 천연 규사분말, 분산제 뿐만 아니라, 테트라부틸포스포늄 테트라플루오로보레이트, 클로로설폰화 폴리에틸렌고무(CSM)을 더 첨가하여 탁구대 상판을 제조함으로써, 마찰력을 높이고, 광택을 최소화할 수 있는 효과가 있다. Thus, by the proposed amount of melamine resin, the micro-particles of natural silica powder, a dispersing agent, as well as to a tetrabutylphosphonium tetrafluoroborate, further added the chlorosulfonated polyethylene rubber (CSM) producing a table tennis top plate, increasing the frictional force there is an effect that minimizes gloss.

이상 첨부된 도면을 참조하여 본 발명의 실시예들을 설명하였으나, 본 발명은 상기 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 제조될 수 있으며, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. Been described the above embodiments of the invention with reference to the accompanying drawings, the present invention is not limited to the above embodiments may be made in many different forms, one of ordinary skill in the art it will appreciate that without changing the technical spirit or essential features of the present invention may be embodied in other specific forms. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다. Thus the embodiments described above are only to be understood as illustrative and non-restrictive in every respect.

S100 : 코팅제 형성 단계 S100: coating formation step
S110 : 시트(sheet) 형성 단계 S110: the sheet (sheet) formation step
S120 : 상판 표면에 시트를 접착하는 단계 S120: step of bonding the sheet to the top surface

Claims (9)

  1. 나무 재질의 상판; The top of the wooden material; And
    상기 상판 표면에 형성되며, 모양지 및 상기 모양지에 함침되는 멜라민 수지 조성물로부터 형성되는 시트;를 포함하고, Is formed on the top surface, and a sheet-shaped support is formed from a melamine resin composition is impregnated on whether the shape; includes,
    상기 멜라민 수지 조성물은 멜라민 수지 100 중량부;에 대하여, 천연 규사분말(natural silica flour) 10~20 중량부; The melamine resin composition comprises 100 parts by weight of a melamine resin; with respect to a natural silica powder (natural silica flour) 10 ~ 20 parts by weight; 및 상기 멜라민 수지의 안정성을 증가시키는 분산제 15~30 중량부;를 포함하고, And dispersing 15-30 parts by weight of increasing the stability of the melamine resin; includes,
    상기 천연 규사분말은 마찰력을 증가시키고, The natural silica powder to increase the frictional force,
    상기 멜라민 수지 조성물은 멜라민 수지 100 중량부에 대하여, 테트라부틸포스포늄 테트라플루오로보레이트(tetrabuthylphosphonium tetrafluoroborate)를 10 중량부 이하로 더 포함하는 것을 특징으로 하는 탁구대 상판. The melamine resin composition table tennis top plate further comprises a borate (tetrabuthylphosphonium tetrafluoroborate) with respect to 100 parts by weight of melamine resin, tetrabutylphosphonium tetrafluoroborate in 10 parts by weight or less.
  2. 제1항에 있어서, According to claim 1,
    상기 멜라민 수지는 멜라민 100중량부 및 상기 멜라민 100 중량부에 대해 포르말린 30~40 중량부를 포함하는 것을 특징으로 하는 탁구대 상판. The melamine resins table tennis top plate characterized in that it comprises 30 to 40 parts by weight of formaldehyde for 100 parts by weight of melamine and 100 parts by weight of the melamine.
  3. 제1항에 있어서, According to claim 1,
    상기 천연 규사분말은 40~50㎛ 입자의 크기를 갖는 것을 특징으로 하는 탁구대 상판. The natural silica powder is table tennis top plate, characterized in that having a size of 40 ~ 50㎛ particles.
  4. 제1항에 있어서, According to claim 1,
    상기 분산제는 소듐 폴리아크릴레이트(sodium polyacrylate)를 포함하는 것을 특징으로 하는 탁구대 상판. The dispersant table tennis top plate comprises a sodium polyacrylate (sodium polyacrylate).
  5. 삭제 delete
  6. 제1항에 있어서, According to claim 1,
    상기 멜라민 수지 조성물은 멜라민 수지 100 중량부에 대하여, 클로로설폰화 폴리에틸렌고무(chlorosulphonated polyethylene, CSM)를 10 중량부 이하로 더 포함하는 것을 특징으로 하는 탁구대 상판. The melamine resin composition table tennis top plate according to claim 1, further including, chlorosulfonated polyethylene rubber (chlorosulphonated polyethylene, CSM), relative to 100 parts by weight of melamine resin to less than 10 parts by weight.
  7. 제1항에 있어서, According to claim 1,
    상기 멜라민 수지 조성물은 상기 멜라민 수지 100 중량부에 대하여, 수산화 칼슘 10% 수용액을 5 중량부 이하로 더 포함하는 것을 특징으로 하는 탁구대 상판. The melamine resin composition per 100 parts by weight of the melamine resin, a table tennis top plate further comprises a calcium hydroxide aqueous solution of 10% to less than 5 parts by weight.
  8. (a) 멜라민 수지 100 중량부에, 천연 규사분말 10~20 중량부 및 분산제 15~30중량부를 첨가하여 교반한 후 코팅제를 형성하는 단계; (A) a melamine resin of 100 parts by weight, to form a natural silica powder of 10 to 20 parts by weight of a dispersing agent and then stirred by adding 15 to 30 parts by weight of a coating agent;
    (b) 상기 코팅제를 모양지에 함침하여 고화시킨 후, 시트(sheet)를 형성하는단계; (B) forming, the sheet (sheet) and then solidified was impregnated with the varnish on whether shape; And
    (c) 나무재질의 상판 표면에 상기 시트를 접착시켜 프레스(press)하는 단계;를 포함하고, (C) by adhering the sheet on the top surface of the wood material comprising: a press (press); and include,
    상기 (c) 단계의 프레스는 1분~2분 동안, 180~190℃에서 프레스 기계로 10~20kgf/cm 2 의 압력을 가하여 수행되는 것을 특징으로 하는 탁구대 상판 제조 방법. (C) the press-in step is 1-2 minutes, table tennis top board manufacturing method characterized by being performed by applying a pressure of 10 to 20kgf / cm 2 with a press machine at 180 ~ 190 ℃.
  9. 삭제 delete
KR1020150097078A 2015-07-08 2015-07-08 Ping-pong table upper surface with increasing ping-pong ball rotation and method for manufacturing of the same KR101587044B1 (en)