KR101456546B1 - Compound for prepating carbon fiber reinforced plastic core using overhead eletric cable - Google Patents

Compound for prepating carbon fiber reinforced plastic core using overhead eletric cable Download PDF

Info

Publication number
KR101456546B1
KR101456546B1 KR1020080086720A KR20080086720A KR101456546B1 KR 101456546 B1 KR101456546 B1 KR 101456546B1 KR 1020080086720 A KR1020080086720 A KR 1020080086720A KR 20080086720 A KR20080086720 A KR 20080086720A KR 101456546 B1 KR101456546 B1 KR 101456546B1
Authority
KR
South Korea
Prior art keywords
carbon fiber
composition
reinforced plastic
epoxy resin
core material
Prior art date
Application number
KR1020080086720A
Other languages
Korean (ko)
Other versions
KR20100027706A (en
Inventor
배만억
방윤혁
이영상
Original Assignee
주식회사 효성
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 효성 filed Critical 주식회사 효성
Priority to KR1020080086720A priority Critical patent/KR101456546B1/en
Publication of KR20100027706A publication Critical patent/KR20100027706A/en
Application granted granted Critical
Publication of KR101456546B1 publication Critical patent/KR101456546B1/en

Abstract

본 발명은 가공송전선의 탄소섬유 강화 플라스틱 심재를 제조하기 위하여 모재인 탄소섬유의 표면에 코팅되는 조성물에 관한 것으로, 보다 상세하게는 디글리시딜 에테르 비스페놀A형 에폭시수지 및 우레탄 변성 에폭시수지가 일정한 함량으로 혼합되어 구성되며, 탄소섬유의 외경에 용이하게 코팅 성형되고, 상기 성형된 코팅층에서 기포가 발생하지 않으며, 심재의 단면이 정확한 원 형태로 성형되면서 상기 심재에서의 수지 함량이 항상 일정한 범위가 되도록 가공할 수 있는 가공송전선의 탄소섬유 강화 플라스틱 심재 제조용 조성물을 제공한다.The present invention relates to a composition coated on the surface of a carbon fiber, which is a base material, for producing a carbon fiber-reinforced plastic core material of a processed transmission line. More specifically, the present invention relates to a composition wherein diglycidyl ether bisphenol A type epoxy resin and urethane- The carbon fiber is easily coated on the outer diameter of the carbon fiber, the bubble is not generated in the formed coating layer, and the cross-section of the core is molded into an accurate circle, so that the resin content in the core is always constant And which is capable of being processed as required.

가공송전선, 탄소섬유 강화 플라스틱 심재, 에폭시수지, 경화제, CFRP Transmission line, Carbon fiber reinforced plastic core, Epoxy resin, Curing agent, CFRP

Description

가공송전선의 탄소섬유 강화 플라스틱 심재 제조용 조성물{Compound for prepating carbon fiber reinforced plastic core using overhead eletric cable}TECHNICAL FIELD [0001] The present invention relates to a composition for preparing a carbon fiber-reinforced plastic core material for a transmission line,

본 발명은 가공송전선의 탄소섬유 강화 플라스틱 심재를 제조하기 위하여 모재인 탄소섬유의 표면에 코팅되는 조성물에 관한 것으로, 상세하게는 탄소섬유의 외경에 용이하게 코팅 성형되고, 상기 성형된 코팅층에서 기포가 발생하지 않으며, 심재의 단면이 정확한 원 형태로 성형되면서 상기 심재에서의 수지 함량이 항상 일정한 범위가 되도록 가공할 수 있는 가공송전선의 탄소섬유 강화 플라스틱 심재 제조용 조성물에 관한 것이다.The present invention relates to a composition coated on the surface of a carbon fiber, which is a base material, for producing a carbon fiber-reinforced plastic core material of a transmission line. More particularly, And can be processed so that the resin content in the core material is always in a constant range while the cross section of the core material is molded into an accurate circular shape.

송전철탑에 설치되어 외부환경에 노출된 상태로 전류를 송전하는 일반적인 가공송전선은 도 1, 도 2를 참조하면, 가공송전선을 지지하고 강도를 유지하도록 중심에 형성되고 단면이 원 형태를 이루는 심재(11), 상기 단면이 원 형태인 심재(11)를 둘러싸는 형태로 형성되는 전도성 재료인 알루미늄 재질의 도체부(12)로 구성된다. 1 and 2, a conventional working transmission line installed in a power transmission tower and transmitting electric current in a state exposed to an external environment includes a core member formed in the center and having a circular shape in section to support the working transmission line and maintain the strength 11, and a conductive portion 12 made of aluminum, which is a conductive material formed in such a manner as to surround the core member 11 having a circular cross section.

종래의 가공송전선에 포함되는 심재는 탄소강 등의 강재를 소재로 사용하여 구성되는데, 송전시 가공송전선의 자체온도가 90 ℃ 이상으로 상승하여 가공송전선 을 지지하는 심재를 팽창시키고, 이에 따라 결국 가공송전선의 처짐 현상을 유발하게 된다는 문제점이 있으며, 이러한 문제점은 최근 송전량의 증가 추세에 따라 더욱 심화되고 있다. 이러한 가공송전선의 처짐 현상의 문제점을 해결하기 위해서는 더 높은 송전철탑을 설치하거나, 또는 송전철탑 사이의 간격을 단축시켜야 하며, 이는 결국 송전시설의 설치 및 유지비용의 증가로 연결된다.The core material contained in the conventional transmission power transmission line is made of a steel material such as carbon steel. During the transmission, the temperature of the transmission power transmission line rises to 90 DEG C or higher, thereby expanding the core material supporting the transmission power transmission line, And this problem is further exacerbated by an increase in the amount of the recent transmission. In order to solve the problem of the deflection phenomenon of the machined transmission line, it is necessary to install a higher transmission tower or shorten the interval between the transmission towers, which leads to an increase in the installation and maintenance cost of the transmission facility.

따라서, 탄소섬유를 모재로 사용하고, 상기 모재인 탄소섬유의 외경을 포용하는 수지조성물로 구성되는 탄소섬유 강화 플라스틱 심재가 개발되었다. 이러한 탄소섬유 강화 플라스틱 심재를 구성하기 위해서는, 모재인 탄소섬유의 외경을 수지조성물로 코팅해야 하는 것이 필수적이다. 그러나, 수지조성물을 탄소섬유의 외경에 코팅 성형하는 것 자체가 기술적으로 곤란하고, 수지조성물을 탄소섬유의 외경에 코팅 성형시킨다고 하더라도 성형된 코팅층에서 기포가 발생하게 될 뿐만 아니라 심재의 단면이 정확한 원 형태로 성형하는 것도 극히 곤란하다. 게다가, 가공송전선의 탄소섬유 강화 플라스틱 심재의 특성을 유지하기 위해서는 상기 심재에서의 수지 함량이 35∼50 중량%의 범위로 구성되는 것이 바람직한데, 종래의 수지조성물로서는 심재에서의 수지 함량이 상기 범위가 되도록 조절하는 것이 매우 곤란하다는 문제점도 있다.Therefore, a carbon fiber-reinforced plastic core material composed of a resin composition using carbon fiber as a base material and embracing the outer diameter of the carbon fiber as the base material has been developed. In order to form such a carbon fiber-reinforced plastic core material, it is essential that the outer diameter of the carbon fiber, which is the base material, be coated with the resin composition. However, it is technically difficult to coat the resin composition to the outer diameter of the carbon fiber. Even if the resin composition is coated on the outer diameter of the carbon fiber, bubbles are generated in the formed coating layer, It is extremely difficult to form it into a shape. In addition, in order to maintain the characteristics of the carbon fiber-reinforced plastic core material of the processed transmission line, it is preferable that the resin content in the core material is in the range of 35 to 50 wt%. In the conventional resin composition, It is very difficult to adjust the temperature to be low.

따라서, 본 발명의 목적은 에폭시수지계 조성물로 이루어져서 탄소섬유의 외경에 용이하게 코팅 성형되고, 상기 성형된 코팅층에서 기포가 발생하지 않으며, 심재의 단면이 정확한 원 형태로 성형되면서 상기 심재에서의 수지 함량이 항상 일정한 범위가 되도록 코팅할 수 있는 가공송전선의 탄소섬유 강화 플라스틱 심재 제조용 조성물을 제공하는데 있다.Accordingly, it is an object of the present invention to provide a resin composition which is made of an epoxy resin composition and which is easily coated on the outer diameter of the carbon fiber, bubbles are not generated in the molded coating layer, Which can always be coated in a predetermined range. The present invention also provides a composition for manufacturing a carbon fiber-reinforced plastic core material.

상기와 같은 과제를 달성하기 위하여, 본 발명에서는 디글리시딜 에테르 비스페놀A형 에폭시수지 50∼200 중량부; 및 우레탄 변성 에폭시수지 10∼50 중량부를 포함하는 가공송전선의 탄소섬유 강화 플라스틱 심재 제조용 조성물이 제공된다.In order to achieve the above object, the present invention provides a resin composition comprising 50 to 200 parts by weight of a diglycidyl ether bisphenol A type epoxy resin; And 10 to 50 parts by weight of a urethane-modified epoxy resin are provided.

본 발명에 의한 가공송전선의 탄소섬유 강화 플라스틱 심재 제조용 조성물은 모재인 탄소섬유의 외경에 쉽게 코팅 성형되므로 탄소섬유 강화 플라스틱 심재의 제조가 용이하게 할 수 있다.The carbon fiber-reinforced plastic core material composition of the transmission line according to the present invention is easily coated on the outer diameter of the carbon fiber, which is the base material, so that the carbon fiber-reinforced plastic core material can be easily manufactured.

또한, 본 발명의 가공송전선의 탄소섬유 강화 플라스틱 심재 제조용 조성물은 탄소섬유의 외경에 형성된 코팅층에서 기포가 발생하지 않으며, 심재의 단면이 정확한 원 형태로 성형되면서 상기 심재에서의 수지 함량이 항상 일정한 범위가 되도록 가공할 수 있으므로, 탄소섬유 강화 플라스틱 심재의 품질을 크게 향상시키는 효과를 지니고 있다.Further, the composition for producing a carbon fiber-reinforced plastic core material of the working power transmission line of the present invention is characterized in that no bubbles are generated in the coating layer formed on the outer diameter of the carbon fiber and the resin content in the core material is always in a constant range So that the quality of the carbon fiber-reinforced plastic core material is greatly improved.

본 발명에 의한 가공송전선의 탄소섬유 강화 플라스틱 심재 제조용 조성물에 대하여 실시예를 참조하여 상세하게 설명한다.A composition for manufacturing a carbon fiber-reinforced plastic core material of a transmission line according to the present invention will be described in detail with reference to examples.

가공송전선의 탄소섬유 강화 플라스틱 심재를 제조하기 위해서는 모재인 탄소섬유의 외경을 수지조성물로 코팅해야 하는 것이 필수적이지만, 수지조성물을 탄소섬유의 외경에 코팅 성형하는 것 자체가 기술적으로 곤란하고, 수지조성물을 탄소섬유의 외경에 코팅 성형시킨다고 하더라도 성형된 코팅층에서 기포가 발생하게 되고, 심재의 단면이 정확한 원 형태로 성형하는 것도 극히 곤란할 뿐만 아니라, 상기 심재에서의 수지 함량이 35∼50 중량%의 범위가 되도록 조절하는 것도 매우 곤란하다는 문제점이 있다.In order to produce the carbon fiber-reinforced plastic core material of the processed transmission line, it is essential that the outer diameter of the carbon fiber as the base material is coated with the resin composition. However, it is technically difficult to coat the resin composition with the outer diameter of the carbon fiber itself, Bubbles are generated in the molded coating layer and it is extremely difficult to form the core in a precise circular shape even when the outer diameter of the carbon fiber is coated with the resin. The resin content in the core material is in the range of 35 to 50 wt% It is also very difficult to adjust it so that it is in the range

상기와 같은 문제점을 해결하기 위하여, 본 발명자들이 다수의 실험을 반복 실시한 결과, 열경화성 에폭시 수지가 가공송전선의 탄소섬유 강화 플라스틱 심재 제조용 조성물에 요구되는 각종 물성 조건을 충족할 수 있으며, 이러한 열경화성 에폭시 수지 중에서도 인장력이 탁월하고 가공성이 우수한 열경화성 에폭시 수지인 디글리시딜 에테르 비스페놀A형 에폭시수지를 주성분으로 하고, 기계적 물성이 양호하고 점성이 높은 우레탄 변성 에폭시수지를 첨가하여 이루어지는 에폭시수지계 조성물을 구성하는 것이 바람직하다는 결론을 내렸다.In order to solve the above problems, the present inventors have repeatedly conducted a number of experiments. As a result, it has been found that a thermosetting epoxy resin can satisfy various physical properties required for a composition for manufacturing a carbon fiber-reinforced plastic core material of a transmission line, An epoxy resin composition comprising a diglycidyl ether bisphenol A type epoxy resin as a main component, which is a thermosetting epoxy resin excellent in tensile strength and excellent in workability, and a urethane-modified epoxy resin having a high mechanical property and a high viscosity, It is desirable.

따라서, 본 발명에서는 하기 화학식 1의 디글리시딜 에테르 비스페놀A형 에폭시수지 50∼200 중량부를 주성분으로 하고, 상기 디글리시딜 에테르 비스페놀A형 에폭시수지에 점성을 제공하기 위한 우레탄 변성 에폭시수지 10∼50 중량부가 혼합되어 가공송전선의 탄소섬유 강화 플라스틱 심재 제조용 조성물이 구성된다.Therefore, in the present invention, a urethane-modified epoxy resin 10 for providing viscosity to the diglycidyl ether bisphenol A type epoxy resin as a main component and 50 to 200 parts by weight of a diglycidyl ether bisphenol A type epoxy resin represented by the following formula To 50 parts by weight are mixed to constitute a composition for manufacturing carbon fiber-reinforced plastic core material of a working transmission line.

< 화학식 1 >&Lt; Formula 1 >

Figure 112008062696663-pat00001
Figure 112008062696663-pat00001

탄소섬유 강화 플라스틱 심재 제조용 조성물을 구성하기 위하여 디글리시딜 에테르 비스페놀A형 에폭시수지 50∼200 중량부에 혼합되는 우레탄 변성 에폭시수지의 함량이 10 중량부 미만이면 상기 디글리시딜 에테르 비스페놀A형 에폭시수지로부터 구성되는 조성물의 점성 부족으로 인하여 탄소섬유의 외경에 제대로 코팅 성형되지 않으며, 디글리시딜 에테르 비스페놀A형 에폭시수지 50∼200 중량부에 혼합되는 우레탄 변성 에폭시수지의 함량이 50 중량부를 초과하면 상기 디글리시딜 에테르 비스페놀A형 에폭시수지로부터 구성되는 조성물을 탄소섬유의 외경에 코팅 성형할 때 코팅층에서 기포가 발생하게 될 뿐만 아니라, 코팅 성형되어 이루어지는 심재의 단면이 정확한 원 형태로 성형되지 않게 된다.When the content of urethane-modified epoxy resin mixed in 50 to 200 parts by weight of diglycidyl ether bisphenol A type epoxy resin is less than 10 parts by weight for constituting the composition for producing carbon fiber-reinforced plastic core material, diglycidyl ether bisphenol A type The content of the urethane-modified epoxy resin to be mixed with 50 to 200 parts by weight of the diglycidyl ether bisphenol A type epoxy resin is 50 parts by weight because the viscosity of the composition composed of the epoxy resin is insufficient, The bubbles are generated in the coating layer when the composition composed of the diglycidyl ether bisphenol A type epoxy resin is coated on the outer diameter of the carbon fiber and the cross section of the coated core material is formed into an accurate circular shape .

상기와 같은 성분과 조성으로 이루어지는 에폭시수지계 조성물을 경화시키는 경화제가 혼합되는 것이 바람직하다.It is preferable that a curing agent for curing the epoxy resin-based composition having the above-described components and composition is mixed.

이에 따라, 본 발명의 가공송전선의 탄소섬유 강화 플라스틱 심재 제조용 조성물은 상기 디글리시딜 에테르 비스페놀A형 에폭시수지 50∼200 중량부, 우레탄 변성 에폭시수지 10∼50 중량부가 혼합된 에폭시계 수지조성물에 경화제 60∼140 중량부가 첨가되어 이루어지며, 상기 경화제는 경화제 중에서도 에폭시계 수지를 경화시키는 기능이 탁월한 메틸 하이드로프탈릭 무수물, 메틸 테트라하이드로프탈릭 무수물로 이루어지는 군으로부터 단독으로 선택하거나 또는 혼합되어 이루어지는 혼합물이 사용되어 탄소섬유 강화 플라스틱 심재 제조용 조성물이 구성되는 것이다.Accordingly, the composition for producing a carbon fiber-reinforced plastic core material of the working transmission line of the present invention comprises an epoxy resin composition comprising 50 to 200 parts by weight of diglycidyl ether bisphenol A type epoxy resin and 10 to 50 parts by weight of a urethane- Wherein the curing agent is selected from the group consisting of methylhydrophthalic anhydride and methyltetrahydrophthalic anhydride which are excellent in the function of curing the epoxy resin among the curing agents, Is used to constitute a composition for manufacturing a carbon fiber-reinforced plastic core material.

탄소섬유 강화 플라스틱 심재 제조용 조성물을 구성하기 위하여 에폭시계 수지조성물에 혼합되는 경화제의 함량이 60 중량부 미만이면 상기 경화제의 함량 부족으로 인하여 에폭시계 수지조성물로부터 구성되는 조성물을 탄소섬유의 외경에 코팅 성형할 때 상기 조성물이 충분한 강도로 경화되지 않으며, 에폭시계 수지조성물에 혼합되는 경화제의 함량이 140 중량부를 초과하면 상기 경화제의 함량 과다로 인하여 에폭시계 수지조성물로부터 구성되는 조성물을 탄소섬유의 외경에 코팅 성형할 때 상기 조성물이 과다하게 경화되어 심재의 유연성이 저하되고 취급이 곤란하게 된다.If the content of the curing agent to be mixed in the epoxy resin composition is less than 60 parts by weight for constituting the composition for producing the carbon fiber-reinforced plastic core material, the composition composed of the epoxy resin composition is coated on the outer diameter of the carbon fiber due to insufficient content of the curing agent The composition does not harden to a sufficient strength. If the content of the curing agent mixed in the epoxy resin composition exceeds 140 parts by weight, the composition composed of the epoxy resin composition may be coated on the outer diameter of the carbon fiber The composition is excessively cured at the time of molding, so that the flexibility of the core material is lowered and handling becomes difficult.

상기와 같이 에폭시계 수지조성물에 포함되는 경화제는 탄소섬유의 외경에 코팅 처리되는 조성물에 기계적 물성을 제공하는 동시에, 심재의 단면이 정확한 원 형태로 성형되면서 상기 심재에서의 수지 함량이 35∼45 중량%가 되게 가공할 수 있도록 지원하는 역할을 수행한다.As described above, the curing agent contained in the epoxy resin composition provides mechanical properties to the composition coated on the outer diameter of the carbon fiber, and when the cross-section of the core material is molded into an accurate circular shape, the resin content in the core material is 35 to 45 weight % Of the total processing time.

상기와 같이 경화제가 포함된 조성물의 경화를 촉진하는 경화 촉진제가 혼합되는 것이 바람직하다.It is preferable that the curing accelerator for accelerating the curing of the composition containing the curing agent as described above is mixed.

이에 따라, 본 발명의 가공송전선의 탄소섬유 강화 플라스틱 심재 제조용 조 성물은 상기 디글리시딜 에테르 비스페놀A형 에폭시수지 50∼200 중량부, 우레탄 변성 에폭시수지 10∼50 중량부 및 경화제 60∼140 중량부로 이루어지는 수지조성물에 벤질 디메틸 아민계 경화 촉진제 1∼5 중량부가 첨가되어 구성된다.Accordingly, the composition for manufacturing a carbon fiber-reinforced plastic core material of the transmission line of the present invention comprises 50 to 200 parts by weight of diglycidyl ether bisphenol A type epoxy resin, 10 to 50 parts by weight of a urethane-modified epoxy resin and 60 to 140 parts by weight of a curing agent And 1 to 5 parts by weight of a benzyldimethylamine-based curing accelerator is added to the resin composition.

탄소섬유 강화 플라스틱 심재 제조용 조성물을 제조하도록 에폭시계 수지조성물에 혼합되는 경화 촉진제는, 경화 촉진제 중에서도 메틸 하이드로프탈릭 무수물 또는 메틸 테트라하이드로프탈릭 무수물의 경화를 촉진시키는 기능이 탁월한 벤질 디메틸 아민계 경화 촉진제를 사용하는 것이 바람직하다.The curing accelerator to be mixed into the epoxy resin composition for producing the composition for producing carbon fiber-reinforced plastic core material is preferably a benzyldimethylamine curing accelerator having an excellent function of accelerating curing of methylhydropthalic anhydride or methyltetrahydrophthalic anhydride among curing accelerators Is preferably used.

탄소섬유 강화 플라스틱 심재 제조용 조성물을 구성하기 위하여 에폭시계 수지조성물에 혼합되는 경화 촉진제의 함량이 1 중량부 미만이면 상기 경화 촉진제의 함량 부족으로 인하여 에폭시계 수지조성물로부터 구성되는 조성물을 탄소섬유의 외경에 코팅 성형할 때 상기 조성물이 신속하게 경화되지 않으며, 에폭시계 수지조성물에 혼합되는 경화 촉진제의 함량이 5 중량부를 초과하면 에폭시계 수지조성물로부터 구성되는 조성물을 탄소섬유의 외경에 코팅 성형할 때 상기 조성물이 더 이상 신속하게 경화되지 않는다.If the content of the curing accelerator mixed in the epoxy resin composition is less than 1 part by weight for constituting the composition for producing the carbon fiber reinforced plastic core material, the composition composed of the epoxy resin composition may be added to the outer diameter of the carbon fiber When the content of the curing accelerator mixed in the epoxy resin composition is more than 5 parts by weight, when the composition composed of the epoxy resin composition is coated on the outer diameter of the carbon fiber, the composition Is no longer cured quickly.

상기와 같이 에폭시계 수지조성물에 포함되는 경화 촉진제는 탄소섬유의 외경에 코팅 처리되는 조성물을 신속하게 경화시키므로써, 가공송전선의 탄소섬유 강화 플라스틱 심재의 제조에 소요되는 시간을 단축하여 생산효율을 향상시키는 동시에, 상기 탄소섬유의 외경에 코팅 성형되는 코팅층에서 기포가 발생하는 것을 방지하는 역할을 수행한다.As described above, the curing accelerator included in the epoxy resin composition rapidly cures the composition to be coated on the outer diameter of the carbon fiber, thereby shortening the time required for manufacturing the carbon fiber-reinforced plastic core material of the transmission line and improving the production efficiency And also prevents bubbles from being generated in the coating layer coated on the outer diameter of the carbon fiber.

상기에서 기술된 디글리시딜 에테르 비스페놀A형 에폭시수지, 우레탄 변성 에폭시수지, 경화제 및 경화 촉진제가 혼합되어 이루어지는 가공송전선의 탄소섬유 강화 플라스틱 심재 제조용 조성물은 모재인 탄소섬유의 외경에 용이하게 코팅 성형되고, 상기 성형된 코팅층에서 기포가 발생하지 않으며, 심재의 단면이 정확한 원 형태로 성형되면서 상기 심재에서의 수지 함량이 항상 일정한 범위가 되도록 가공할 수 있게 한다.The composition for producing a carbon fiber-reinforced plastic core material of a working power transmission line comprising the above-described diglycidyl ether bisphenol A type epoxy resin, a urethane-modified epoxy resin, a curing agent and a curing accelerator is mixed with the carbon fiber- So that bubbles are not generated in the molded coating layer, and the cross-section of the core material is molded into an accurate circular shape, so that the resin content in the core material can be processed to be always in a constant range.

본 발명의 조성물이 코팅되어 구성되는 탄소섬유 강화 플라스틱 심재의 제조공정에 대하여 도면과 실시에를 참조하여 상세하게 설명한다.A manufacturing process of a carbon fiber-reinforced plastic core material constituted by coating the composition of the present invention will be described in detail with reference to the drawings and embodiments.

도 3은 본 발명의 조성물에 의하여 구성되는 탄소섬유 강화 플라스틱 심재의 제조공정을 도시한 것이다.Fig. 3 shows a process for producing a carbon fiber-reinforced plastic core material composed of the composition of the present invention.

도 3을 참조하면, 디글리시딜 에테르 비스페놀A형 에폭시수지 50∼200 중량부, 우레탄 변성 에폭시수지 10∼50 중량부, 경화제 60∼140 중량부 및 경화 촉진제 1∼5 중량부를 혼합하여 혼합물을 형성한다. 수지 코팅조(21)에 상기 혼합물을 투입하고 용융하여 용융 조성물을 형성한다. 3, 50 to 200 parts by weight of a diglycidyl ether bisphenol A type epoxy resin, 10 to 50 parts by weight of a urethane-modified epoxy resin, 60 to 140 parts by weight of a curing agent, and 1 to 5 parts by weight of a curing accelerator, . The mixture is introduced into the resin coating tank 21 and melted to form a molten composition.

다수의 탄소섬유 보빈(22)에 감겨진 탄소섬유(13)를 집속하고, 일정한 장력으로 이송하여 상기 수지 코팅조(21)의 용융 조성물을 통과시켜서 상기 탄소섬유의 외경에 용융 조성물을 코팅한다. The carbon fibers 13 wound on the plurality of carbon fiber bobbins 22 are focused and transported with a constant tension to pass the molten composition of the resin coating tank 21 to coat the outer diameter of the carbon fiber with the molten composition.

상기 조성물이 코팅된 탄소섬유를 일정한 직경의 세라믹 홀(23)에 통과시켜서. 심재에서의 수지 함량이 35∼50 중량%의 범위가 되도록 상기 탄소섬유의 외경에 코팅된 조성물의 양을 조절한다. 즉, 세라믹 홀(23)의 직경 사이즈에 의거하여 탄소섬유의 외경에 코팅된 조성물의 양을 조절하므로써, 심재에서의 수지 함량이 35∼50 중량%의 범위가 되도록 구성할 수 있다.The carbon fiber coated with the composition is passed through ceramic holes 23 of a certain diameter. The amount of the composition coated on the outer diameter of the carbon fiber is adjusted so that the resin content in the core material is in the range of 35 to 50 wt%. That is, by controlling the amount of the composition coated on the outer diameter of the carbon fibers based on the diameter size of the ceramic hole 23, the resin content in the core material can be configured to be in the range of 35 to 50 wt%.

일정한 직경의 세라믹 홀(23)을 통과한 조성물 코팅 탄소섬유를 경화용 오븐(24)을 통과시키면서 일정한 온도로 열처리하여 상기 조성물을 경화시키므로써 본 발명의 탄소섬유 강화 플라스틱 심재 제조용 조성물을 구성한다. The composition-coated carbon fibers having passed through the ceramic holes 23 having a predetermined diameter are heat-treated at a constant temperature while passing through a curing oven 24 to cure the composition, thereby constituting the carbon fiber-reinforced plastic core material composition of the present invention.

상기 구성된 탄소섬유 강화 플라스틱 심재 제조용 조성물을 심재용 보빈(25)에 감아서 제조 완료한다.The composition for manufacturing the carbon fiber-reinforced plastic core material is wound around the core bobbin 25 to complete the manufacturing.

본 발명의 가공송전선의 탄소섬유 강화 플라스틱 심재 제조용 조성물의 구성 및 상기 조성물로 구성되는 가공송전선의 탄소섬유 강화 플라스틱 심재의 제조에 대하여 구체적인 실시예를 참조하여 상세하게 설명한다. 단, 다음에 기술되는 실시예들은 본 발명을 구체적으로 예시하기 위한 것일 뿐이며, 본 발명을 제한하는 것은 아니다.The constitution of the composition for producing carbon fiber-reinforced plastic core material of the working transmission line of the present invention and the production of the carbon fiber-reinforced plastic core material of the working transmission line composed of the composition will be described in detail with reference to specific examples. It is to be understood, however, that the following examples are illustrative only and do not limit the present invention.

< 실시예 1 >&Lt; Example 1 >

1. 디글리시딜 에테르 비스페놀A형 에폭시수지 100 중량부, 우레탄 변성 에폭시수지 20 중량부, 메틸 테트라하이드로프탈릭 무수물인 경화제 100 중량부 및 벤질 디메틸 아민계 경화 촉진제 2 중량부를 혼합하여 혼합물을 형성하였다.1. 100 parts by weight of diglycidyl ether bisphenol A type epoxy resin, 20 parts by weight of a urethane-modified epoxy resin, 100 parts by weight of a curing agent as methyltetrahydrophthalic anhydride and 2 parts by weight of a benzyldimethylamine curing accelerator were mixed to form a mixture Respectively.

2, 수지 코팅조에 상기 혼합물을 투입하고 용융하여 용융 조성물을 형성하였다.2, the mixture was introduced into a resin coating tank and melted to form a molten composition.

3. 탄소섬유 보빈에 감겨진 탄소섬유를 집속하고, 일정한 장력으로 이송하여 상기 수지 코팅조의 용융 조성물을 통과시켜서 상기 탄소섬유의 외경에 용융 조성물을 코팅하였다.3. The carbon fibers wound on the carbon fiber bobbins were focused and transferred with a constant tension to pass the molten composition of the resin coating tank to coat the outer diameter of the carbon fiber with the molten composition.

4. 상기 조성물이 코팅된 탄소섬유를 세라믹 홀에 통과시켜서. 심재에서의 수지 함량이 50 중량%의 범위가 되도록 상기 탄소섬유의 외경에 코팅된 조성물의 양을 조절하였다.4. Passing the carbon fiber coated with the composition through a ceramic hole. The amount of the composition coated on the outer diameter of the carbon fiber was adjusted so that the resin content in the core material was in the range of 50 wt%.

5. 상기 세라믹 홀을 통과한 조성물 코팅 탄소섬유를 제 1 오븐에서 170 ℃로 1차 경화 처리하고, 제 2 오븐에서 200 ℃로 2차 경화 처리하여 탄소섬유 강화 플라스틱 심재 제조용 조성물을 구성하였다.5. The composition-coated carbon fibers passed through the ceramic holes were first cured at 170 ° C in a first oven and then cured at 200 ° C in a second oven to form a carbon fiber-reinforced plastic core material composition.

6. 상기 탄소섬유 강화 플라스틱 심재 제조용 조성물을 냉각하고 심재용 보빈에 감아서 제조 완료하였다.6. The composition for manufacturing a carbon fiber-reinforced plastic core material was cooled and wound on a bobbin for core material to complete the manufacture.

< 실시예 2 >&Lt; Example 2 >

디글리시딜 에테르 비스페놀A형 에폭시수지 100 중량부, 우레탄 변성 에폭시수지 10 중량부, 메틸 테트라하이드로프탈릭 무수물인 경화제 80 중량부 및 벤질 디메틸 아민계 경화 촉진제 1 중량부를 혼합하여 혼합물을 형성하는 것과, 조성물이 코팅된 탄소섬유를 세라믹 홀에 통과시켜서. 심재에서의 수지 함량이 35 중량%의 범위가 되도록 상기 탄소섬유의 외경에 코팅된 조성물의 양을 조절하는 것 이외에는 상기 실시예 1과 동일하다.A mixture of 100 parts by weight of diglycidyl ether bisphenol A type epoxy resin, 10 parts by weight of a urethane-modified epoxy resin, 80 parts by weight of a curing agent as methyltetrahydrophthalic anhydride, and 1 part by weight of a benzyldimethylamine curing accelerator , Passing the composition-coated carbon fiber through a ceramic hole. Except that the amount of the composition coated on the outer diameter of the carbon fiber is controlled such that the resin content in the core material is in the range of 35 wt%.

< 비교예 1 >&Lt; Comparative Example 1 &

디글리시딜 에테르 비스페놀A형 에폭시수지 100 중량부, 메틸 테트라하이드로프탈릭 무수물인 경화제 100 중량부 및 벤질 디메틸 아민계 경화 촉진제 2 중량부를 혼합하여 혼합물을 형성하는 것 이외에는 상기 실시예 1과 동일하다.Except that 100 parts by weight of diglycidyl ether bisphenol A type epoxy resin, 100 parts by weight of a curing agent as methyltetrahydrophthalic anhydride, and 2 parts by weight of a benzyldimethylamine curing accelerator were mixed to form a mixture .

< 비교예 2 >&Lt; Comparative Example 2 &

조성물이 코팅된 탄소섬유를 세라믹 홀에 통과시키지 않는다는 것 이외에는 상기 실시예 1과 동일하다.Except that the carbon fiber coated with the composition was not passed through the ceramic hole.

< 비교예 3 >&Lt; Comparative Example 3 &

디글리시딜 에테르 비스페놀A형 에폭시수지 100 중량부, 메틸 테트라하이드로프탈릭 무수물인 경화제 80 중량부 및 벤질 디메틸 아민계 경화 촉진제 1 중량부를 혼합하여 혼합물을 형성하는 것 외에는 상기 실시예 2와 동일하다.Except that 100 parts by weight of diglycidyl ether bisphenol A type epoxy resin, 80 parts by weight of a curing agent as methyltetrahydrophthalic anhydride, and 1 part by weight of a benzyldimethylamine curing accelerator were mixed to form a mixture .

< 비교예 4 >&Lt; Comparative Example 4 &

조성물이 코팅된 탄소섬유를 세라믹 홀에 통과시키지 않는다는 것 이외에는 상기 실시예 2와 동일하다.The second embodiment is the same as the second embodiment except that the composition does not allow the coated carbon fibers to pass through the ceramic holes.

상기 실시예 1, 2 및 비교예 1 내지 4에 의거하여 제조된 탄소섬유 강화 플라스틱 심재 제조용 조성물의 공정 조건 및 물성을 다음의 표 1에 나타낸다.Table 1 below shows the processing conditions and physical properties of the compositions for preparing carbon fiber-reinforced plastic core materials prepared in Examples 1 and 2 and Comparative Examples 1 to 4.

< 표 1 > <Table 1>

구 분division 실시예1Example 1 실시예2Example 2 비교예1Comparative Example 1 비교예2Comparative Example 2 비교예3Comparative Example 3 비교예4Comparative Example 4 조성비
(중량부)
Composition ratio
(Parts by weight)
비스페놀A 에폭시Bisphenol A epoxy 100100 100100 100100 100100 100100 100100
우레탄변성 에폭시Urethane-modified epoxy 2020 2020 -- 2020 2020 -- 경화제Hardener 100100 8080 100100 100100 8080 8080 경화 촉진제Hardening accelerator 22 1One 22 22 1One 1One 세라믹 홀Ceramic Hole 사용use 사용use 사용use 미사용unused 사용use 미사용unused 물 성Properties 단면 원형도Section circularity 1.021.02 1.051.05 1.121.12 1.821.82 1.081.08 1.951.95 수지 함량(중량%)Resin content (% by weight) 4040 3737 2828 5252 3232 4949

상기 표 1에서 본 발명의 실시예에 의한 탄소섬유 강화 플라스틱 심재 제조용 조성물이, 비교예에 의한 탄소섬유 강화 플라스틱 심재 제조용 조성물 보다 물성이 탁월하여, 가공송전선의 탄소섬유 강화 플라스틱 심재의 제조에 적당한 것으로 나타났다.In Table 1, the composition for preparing a carbon fiber-reinforced plastic core material according to an embodiment of the present invention is superior to the composition for preparing a carbon fiber-reinforced plastic core material according to the comparative example and is suitable for manufacturing a carbon fiber- appear.

본 발명은 상술한 특정의 바람직한 실시예에 한정되지 아니하며, 특허청구범 위에서 청구하는 본 발명의 요지를 벗어남이 없이 당해 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 누구든지 다양한 변형 실시가 가능한 것은 물론이고, 그와 같은 변경은 청구범위 기재의 범위 내에 있게 된다.The present invention is not limited to the above-described specific preferred embodiments, and various modifications may be made to those skilled in the art without departing from the spirit and scope of the present invention as claimed above. Of course, such modifications are within the scope of the claims.

도 1은 가공송전선의 구조도Fig. 1 is a schematic view of a working transmission line

도 2는 가공송전선의 평면도2 is a plan view of the machining power transmission line

도 3은 본 발명의 조성물로 구성되는 탄소섬유 강화 플라스틱 심재의 제조공정도Fig. 3 is a view showing a manufacturing process of a carbon fiber-reinforced plastic core material composed of the composition of the present invention

* 도면의 주요 부분에 대한 부호의 설명DESCRIPTION OF THE REFERENCE NUMERALS

11 : 심재 12 : 도체부11: core member 12: conductor member

13 : 탄소섬유 21 : 수지 코팅조13: carbon fiber 21: resin coating tank

22 : 탄소섬유 보빈 23 : 세라믹 홀22: Carbon fiber bobbin 23: Ceramic hole

24 : 오븐 25 : 심재용 보빈24: oven 25: bobbin for core material

Claims (2)

디글리시딜 에테르 비스페놀A형 에폭시수지 50∼200 중량부, 우레탄 변성 에폭시수지 10∼50 중량부, 메틸 하이드로프탈릭 무수물, 메틸 테트라하이드로프탈릭 무수물로 이루어지는 군으로부터 단독으로 선택하거나 또는 혼합되어 이루어지는 혼합물인 경화제 60∼140 중량부 및 벤질 디메틸 아민계 경화 촉진제 1∼5 중량부가 혼합되어 구성되는 것을 특징으로 하는 탄소섬유 강화 플라스틱 심재 제조용 조성물.50 to 200 parts by weight of a diglycidyl ether bisphenol A type epoxy resin, 10 to 50 parts by weight of a urethane-modified epoxy resin, methylhydrophthalic anhydride and methyltetrahydrophthalic anhydride, 60 to 140 parts by weight of a curing agent as a mixture and 1 to 5 parts by weight of a benzyldimethylamine-based curing accelerator. 삭제delete
KR1020080086720A 2008-09-03 2008-09-03 Compound for prepating carbon fiber reinforced plastic core using overhead eletric cable KR101456546B1 (en)