KR101244059B1 - Fiber Reinforced Woven Material And Reinforcing Component Having Excellent Physical Property - Google Patents

Fiber Reinforced Woven Material And Reinforcing Component Having Excellent Physical Property Download PDF

Info

Publication number
KR101244059B1
KR101244059B1 KR20090099511A KR20090099511A KR101244059B1 KR 101244059 B1 KR101244059 B1 KR 101244059B1 KR 20090099511 A KR20090099511 A KR 20090099511A KR 20090099511 A KR20090099511 A KR 20090099511A KR 101244059 B1 KR101244059 B1 KR 101244059B1
Authority
KR
Grant status
Grant
Patent type
Prior art keywords
continuous fiber
thickness
reinforcing
weft
thermoplastics
Prior art date
Application number
KR20090099511A
Other languages
Korean (ko)
Other versions
KR20110042714A (en )
Inventor
윤용훈
정기훈
김희준
Original Assignee
(주)엘지하우시스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Grant date

Abstract

본 발명은 기계적 물성이 뛰어난 보강직물 및 보강재에 관한 것으로, 보다 상세하게는 연속섬유 함유량이 같은 2 군의 열가소성 플라스틱-연속섬유 혼성 복합체 스트랜드가 각각 경사 및 위사로 서로 교차하도록 엮이어 형성되되, 상기 열가소성 플라스틱-연속섬유 혼성 복합체 스트랜드는 소정 폭으로 균일하게 펼쳐진 연속섬유 다발과 이와 동일한 폭의 테이프 형상의 열가소성 플라스틱을 접합한 다음, 반 또는 지그재그 형태로 접고, 이를 열 압착시켜 제조된 것이고, 상기 경사는 두께가 상기 위사 두께의 n 배(n은 1 이상의 정수이다)이고, 폭은 상기 위사 두께의 1/n 배인 것을 특징으로 하는 보강직물에 관한 것이다. The present invention, more particularly to thermoplastics in the group 2, such as a continuous fiber content of the excellent mechanical properties reinforcing fabric and reinforcing material - being followed laced the continuous fiber hybrid composite strands to intersect each other at each warp and weft yarn formed, the thermoplastics-continuous fiber hybrid composite strands will cost uniformly spread continuous fiber bundle, and this bonding thermoplastics of the tape shape of the same width as the predetermined width to fold to the next, half or a zigzag form, by heat-pressing them prepared, the inclined is n times (n is an integer of 1 or more) of the thickness of the weft thickness, the width is related to a reinforcing fabric as 1 / n times said thickness of the weft.
본 발명에 따르면, 특정 방향으로 기계적 물성이 최적화되고, 함침 후 경사와 위사의 교차점에서 보이드가 적고, 보강된 섬유가 크게 휘지 않아 기계적 물성이 뛰어난 보강직물 및 보강재를 제공하는 효과가 있다. According to the invention, this has the effect of and optimize the mechanical properties in a particular direction, small voids at the intersection of the warp and weft and then impregnated, provides a not significantly bending the reinforcing fiber with excellent mechanical properties, the reinforcing fabric and reinforcing material.
기계적 물성, 보강직물, 보강재, 플라스틱-연속섬유 혼성 복합체, 유리섬유, 보이드, 보강직물, 보강재 Mechanical properties, the reinforcing fabric, a reinforcing material, plastic-continuous fiber hybrid composite, glass fibers, voids, the reinforcing fabric, reinforcing material

Description

기계적 물성이 뛰어난 보강직물 및 보강재{Fiber Reinforced Woven Material And Reinforcing Component Having Excellent Physical Property} Excellent mechanical properties, reinforcing fabric and reinforcements {Fiber Reinforced Woven Material And Reinforcing Component Having Excellent Physical Property}

본 발명은 기계적 물성이 뛰어난 보강직물 및 보강재에 관한 것으로, 보다 상세하게는 특정 방향으로 기계적 물성이 최적화되고, 함침후 경사와 위사의 교차점에서 보이드가 적고, 보강된 섬유가 크게 휘지 않아 기계적 물성이 뛰어난 보강직물 및 보강재에 관한 것이다. The present invention relates to reinforcing fabric and reinforcing material with excellent mechanical properties, more specifically, less a void at the intersection of and mechanical properties optimized in a particular direction, then impregnated warp and weft, the reinforcing fiber does not bend greatly Mechanical Properties It relates to outstanding reinforcing fabric and reinforcements.

높은 기계적 물성이 요구되는 플라스틱 구조물에는 통상 보강재가 사용되는데, 상기 보강재로 연속섬유강화 플라스틱이 많이 이용된다. Plastic structures that require high mechanical properties are used there is normally a reinforcing material, a continuous fiber-reinforced plastic in the reinforcing material is often used.

상기 연속섬유강화 플라스틱은 섬유 다발 또는 직물 형태로 제조되어 사용되는데, 이중 직물 형태가 더 다루기 쉽고, 구조변경에 따라 성능 최적화가 가능하며, 물성의 예측이 용이하여 더욱 많이 이용된다. The continuous fiber-reinforced plastics are used are made of a fiber bundle or fabric form, and easily form a double fabric is more manageable, the performance optimization from, depending on the structure changes, the prediction of physical properties is easy to use more and more.

상기 직물 형태는 보강된 연속섬유가 곧게 펴져야 우수한 기계적 물성을 발휘할 수 있는데, 위사와 경사의 교차점에서 보강된 연속섬유가 크게 구부러져 물성이 저하되는 문제가 있다. The fabric forms may exhibit excellent mechanical properties should straighten the reinforcing continuous fibers, there is a problem that the continuous fiber reinforcement at the intersection of the weft and inclined greatly bent is reduced physical properties.

또한, 상기 직물 형태의 연속섬유강화 플라스틱(보강직물)은 열간압착 과정을 거쳐 열가소성 플라스틱이 연속섬유에 용융 함침되는데, 이 경우 위사와 경사의 교차점에서 연속섬유의 휘어진 각도가 크면 보이드가 발생할 확률이 높아지고, 이는 물성 저하를 초래한다. In addition, the fabric forms a continuous fiber-reinforced plastic (reinforced fabric) of the there is a thermoplastics melt impregnated into the continuous fibers through a hot-pressing process, is in this case the bent angle of the continuous fibers at the intersections of weft and diagonal probability of large voids increases, which results in decreased physical properties.

상기와 같은 종래기술의 문제점을 해결하고자, 본 발명은 특정 방향으로 기계적 물성이 최적화되고, 함침 후 경사와 위사의 교차점에서 보이드가 적고, 보강된 섬유가 크게 휘지 않아 기계적 물성이 뛰어난 보강직물 및 보강재를 제공하는 것을 목적으로 한다. In order to solve the problems of the prior art, the present invention is the mechanical properties optimized in a particular direction, small voids at the intersection of the post-impregnated warp and weft, the reinforcing fiber does not bend significantly superior mechanical property reinforcing fabric and reinforcing material to provide an object.

상기의 목적을 달성하기 위하여, 본 발명은 연속섬유 함유량이 같은 2 군의 열가소성 플라스틱-연속섬유 혼성 복합체 스트랜드가 각각 경사 및 위사로 서로 교차하도록 엮이어 형성되되, 상기 열가소성 플라스틱-연속섬유 혼성 복합체 스트랜드는 소정 폭으로 균일하게 펼쳐진 연속섬유 다발과 이와 동일한 폭의 테이프 형상의 열가소성 플라스틱을 접합한 다음, 반 또는 지그재그 형태로 접고, 이를 열 압착시켜 제조된 것이고, 상기 경사는 두께가 상기 위사 두께의 n 배(n은 1 이상의 정수이다)이고, 폭은 상기 위사 두께의 1/n 배인 것을 특징으로 하는 보강직물 및 보강재를 제공한다. In order to achieve the above object, the invention of the second group, such as a continuous fiber content of thermoplastics-continuous fiber hybrid composite strands are being formed after laced to cross each other in each of warp and weft, the thermoplastics-continuous fiber hybrid composite strand a is uniformly spread continuous fiber bundle, and this bonding thermoplastics of the tape shape of the same width, then half or folded in a zigzag form, would prepared by heat-pressing them, the slope is that the weft thickness of thickness at a predetermined width n times (n is an integer of 1 or more), and the width of the fabric provides reinforcement and a stiffener for a 1 / n times said thickness of the weft.

이하 본 발명을 상세하게 설명한다. It will be described in detail below the present invention.

본 발명의 보강직물은 연속섬유 함유량이 같은 2 군의 열가소성 플라스틱-연속섬유 혼성 복합체 스트랜드가 각각 경사 및 위사로 서로 교차하도록 엮이어 형성되되, 상기 열가소성 플라스틱-연속섬유 혼성 복합체 스트랜드는 소정 폭으로 균일하게 펼쳐진 연속섬유 다발과 이와 동일한 폭의 테이프 형상의 열가소성 플라스틱을 접합한 다음, 반 또는 지그재그 형태로 접고, 이를 열 압착시켜 제조된 것이고, 상기 경사는 두께가 상기 위사 두께의 n 배(n은 1 이상의 정수이다)이고, 폭은 상기 위사 두께의 1/n 배인 것을 특징으로 한다. Reinforcing fabric is of group 2, such as a continuous fiber content of the thermoplastic plastic of the present invention-continuous fiber hybrid composite strands are being formed after laced to cross each other in each of warp and weft, the thermoplastics-continuous fiber hybrid composite strands are uniform in a predetermined range the one after the first continuous fiber bundle, and this bonding thermoplastics of the tape shape of the same width to fold to the next, half or zigzag form, would prepared by heat-pressing them, the slope is n times that of the weft thickness of the thickness (n is 1 is an integer equal to or greater than a), the width shall be 1 / n times said thickness of the weft.

상기 연속섬유는 유리섬유일 수 있고, 열가소성 플라스틱-연속섬유 혼성복합체 스트랜드에 대하여 40 내지 80 중량%로 포함되는 것이 바람직하다. Is preferably included in 40 to 80% by weight with respect to the continuous fiber hybrid composite strand, wherein the continuous fibers are glass fibers can be a thermoplastic plastic.

상기 유리섬유는 상기 열가소성 플라스틱과의 화학적 결합력을 높이기 위해 사이징 처리될 수 있다. The glass fiber may be treated sizing to increase the chemical bonding strength between the thermoplastic plastic. 상기 유리섬유의 직경은 15 내지 20 ㎛인 것이 사용될 수 있는데, 작을수록 좋다. The diameter of the glass fibers may be used is from 15 to 20 ㎛, it may be smaller.

상기 유리섬유 다발은 그 크기에 있어 특별히 제한되지 않으나, 적은 값의 TEX는 광폭화 측면에서 유리하고, 큰 값의 TEX는 경제적 측면(생산성)에서 유리하다. The glass fiber bundle is not particularly limited in its size, a small value TEX is advantageous in terms of gwangpokhwa, TEX a large value is advantageous in economic terms (productivity).

상기 테이프 형상의 열가소성 플라스틱은 접힘이 용이하도록 복수 개의 일정 폭의 플라스틱 테이프가 펼져진 상태에서, 나란히 동일 평면에 간극 없이 배열된 것일 수 있는데, 혼합방사 공정을 포함하는 종래기술과는 달리 특별한 일롱게이션(Elongation) 특성이 요구되지 않으므로, 필름 또는 테이프 형태로 가공될 수 있는 대부분의 상업화된 열가소성 플라스틱이 적용될 수 있다. Thermoplastics in the tape shape is different from the prior art, including in jyeojin a plastic tape is pliers of the plurality of predetermined width, there may be side by side are arranged without a gap in the same plane, a mixed spinning process to facilitate the folding special ilrong ligated (Elongation) property is not required, the most commercialized thermoplastics that can be processed into a film or tape form may be used.

상기 테이프 형상의 열가소성 플라스틱은, 구체적인 일례로 복수의 폴리프로필렌 테이프로 이루어진 것일 수 있고, 이 경우 커플링제를 포함할 수 있으며, 그 두께는 30 내지 200 ㎛인 것이 바람직하다. Thermoplastics in the tape shape, and may be formed of a plurality of polypropylene tape in a specific example, may include a coupling agent in this case, its thickness is preferably from 30 to 200 ㎛. 또한, 그 개수는 이에 한정하는 것은 아니나 2 내지 8개인 것이 상용화 측면을 감안할 때 바람직하다. Also, the number thereof, but are not limited to when it is preferred that two to eight, given the commercially available side.

상기 유리섬유 다발과 테이프 형상의 열가소성 플라스틱의 접합은 펼쳐진 유리섬유 다발을 120 내지 280 ℃의 온도로 가열한 다음, 이를 테이프 형상의 열가소성 플라스틱에 고정시키는 것으로, 상기 온도 범위에서 접합하는 경우 제조되는 열가소성 플라스틱-연속섬유 혼성 복합체의 유연성이 뛰어나 직조가 용이해진다. The glass fiber bundles and a thermoplastic bonding of the tape-shaped is heated to a temperature of 120 to 280 ℃ the bundle of the glass fibers after the first, and then, by securing them to the thermoplastic plastic of the tape-like, thermoplastic is made if the bond at that temperature range Plastics - the weaving is easy and excellent flexibility of the continuous fiber hybrid composite.

상기 온도는 사용되는 테이프 형상의 열가소성 플라스틱의 종류에 따라 용융온도를 참고로 하여 적절히 선택되며, 혼성복합체가 유연성을 유지할 수 있는 가급적 높은 온도로 최적화하는 것이 바람직하다. The temperature, depending on the type of thermoplastic in the tape shape to be used is properly selected by a melting temperature as a reference, it is desirable to optimize the hybrid composite to a temperature as much as possible to maintain the flexibility.

상기 펼쳐진 유리섬유 다발이 접합된 테이프 형상의 열가소성 플라스틱은, 반 또는 지그재그 형태로 접히게 되는데, 접히는 횟수에 따라 두께와 폭이 다른 열가소성 플라스틱-유리섬유 혼성복합체 스트랜드가 만들어진다. Wherein after the first bundle of the glass fibers is a thermoplastic plastic of the bonded tape shape, there is folded in half or zigzag form, depending on the number of different folding the thickness and width of the thermoplastic plastic-made of a glass fiber hybrid composite strands. 이때 접히는 횟수는 이에 한정하는 것은 아니나, 예를 들면, 위사의 경우 요구되는 혼성복합체의 물성에 따라 처음 폭의 1~1/4로 접고, 경사의 경우도 마찬가지로 필요에 따라 1~1/4 폭을 가지는 스트랜드로 각각 제작하는 것이 바람직하다. At this time, folding number of times, but are not limited to, for example, in the case of a weft according to the physical properties of the hybrid composite is required to fold to 1 to 1/4 of the first width, 1 to 1/4 width as needed as well, if the slope having a preferably each made from strands.

상기 접히는 횟수에 대하여 상기 두께는 비례하고, 폭은 반비례하는데, 일례로 두 께가 두껍고 폭이 좁은 플라스틱-유리섬유 혼성복합체 스트랜드는 직조시 동일 면적을 채우기 위해 더 많은 양이 필요하고, 이 스트랜드의 길이방향을 따라 더 큰 저항력을 가질 수 있게 된다. Wherein with respect to the folding number proportional is the thickness, and the width is inversely proportional to, the narrow plastic Thickness is thick and wide as an example - glass fiber hybrid composite strands have a greater amount to fill the weave during the same area, and the strand along the longitudinal direction, it is possible to have a greater resistance.

따라서, 상기 플라스틱-유리섬유 혼성복합체 스트랜드를 위사로 사용하는 경우와 경사로 사용하는 경우를 나누어 그 두께와 폭을 조절하여 보강직물로 직조하는 경우, 특정방향으로 최적화된 물성을 가지는 보강직물을 제조할 수 있고, 또한 섬유 교차점에서 발생하는 섬유의 휘어지는 각도를 작게 할 수 있어 보이드의 발생 확률을 낮추고, 기계적 물성을 향상시킬 수 있다. Thus, the plastic-divided into a case of using the case of using the glass fiber hybrid composite strand as a weft and a ramp by adjusting the thickness and width if the woven reinforcing fabric, to produce a reinforcing fabric having optimized physical properties in a particular direction number, and it may also be possible to reduce the bending angle of the fibers occurring in the fiber crossing it lowers the probability of occurrence of voids, improving the mechanical properties.

상기 열 압착은 120 내지 280 ℃의 조건 하에서 실시될 수 있는데, 온도가 너무 낮을 경우 상기 열가소성 플라스틱-연속섬유 혼성복합체 스트랜드의 접힌 상태가 풀어지는 문제가 있고, 온도가 너무 높을 경우에는 열가소성 플라스틱이 연속섬유에 과도하게 함침되어 유연성을 상실하는 문제가 있다. The thermocompression bonding was 120 there to be carried out under conditions of 280 ℃, if the temperature is too low, the thermoplastics-is a problem in that the folded state of the continuous fiber hybrid composite strands to be released and, in the thermoplastic continuous if too high temperature excessively impregnated into the fiber, there is a problem that loss of flexibility.

상기 보강직물은 여러 종류의 섬유를 사용하지 않고 열가소성 플라스틱과 연속섬유의 함유량은 같으나 두께와 폭이 다른 열가소성 플라스틱-연속섬유 혼성 복합체 스트랜드를 각각 경사 및 위사로 사용함으로써 더 큰 저항력이 요구되는 일방향(또는 특정방향)으로 최적화된 물성을 가질 수 있다. The reinforcing fabric is various types of content of the thermoplastic resin and continuous fiber without the fiber is gateuna a thickness and a width different thermoplastics-one way that this greater resistance requires the use of continuous fiber hybrid composite strands in each warp and weft ( or you can have the optimized properties in a particular direction).

상기 보강직물은 유연성이 커 다양한 구조에 적용이 가능하고 작업이 용이하다. The reinforcing fabric is applicable to various structures is increased flexibility and easy to work. 상기 경사는 두께가 상기 위사 두께의 n 배(n은 1 이상의 정수이다)이고, 폭은 상기 위사 두께의 1/n 배일 수 있는데, 이 경우 보강효율 및 경제성 등이 우수하다. The slope there is a thickness of the n-times of the weft thickness (n is an integer of 1 or more), the width is 1 / n times the thickness of the weft, this case is superior to enhance the efficiency and economy and the like.

본 발명의 보강재는 상기 보강직물을 열간 압착하여 열가소성 플라스틱이 연속섬유 내로 열용융 함침되는 것을 특징으로 한다. A reinforcing material of the present invention the reinforcement fabric characterized in that the hot rolled pressing is a thermoplastic hot-melt impregnated into the continuous fibers.

상기 보강직물을 열간 압착할 때, 열가소성 플라스틱이 연속섬유 내부로 용융함침되는데, 본 발명은 연속섬유와 열가소성 플라스틱이 교대로 적층된 다층구조를 가짐으로써, 고점도 수지와 같이 유동 거리가 100 ㎛ 이하로 제한되는 경우에도 매우 우수한 함침성을 발휘할 수 있다. When hot-pressing the reinforcing fabric, there is a thermoplastic plastic melt impregnated into the continuous fibers, the invention is by having a multi-layer structure laminated with a continuous fiber and the thermoplastics in turn, to the moving distance less than 100 ㎛ as a high-viscosity resin even if the limit can exhibit excellent impregnation.

상기에서 살펴본 바와 같이, 본 발명에 따르면 특정 방향으로 기계적 물성이 최적화되고, 경사와 위사의 교차점에서 보이드가 적고 보강되는 섬유가 크게 휘지 않아 기계적 물성이 뛰어난 보강직물 및 보강재를 제공하는 효과가 있다. As described above, according to the present invention and the mechanical properties optimized in a particular direction, it is effective to provide a slope and the fiber is less void reinforcement at the junction of the weft does not bend significantly superior mechanical property reinforcing fabric and reinforcing material.

이하, 본 발명의 보강직물 및 보강재의 제조방법을 구체적인 실시예로써 첨부된 도면을 참조하여 설명한다. Hereinafter, a method of manufacturing the reinforcing fabric and reinforcing material of the present invention will be described with reference to the accompanying drawings by specific examples.

상기 유리섬유 다발을 광폭으로 균일하게 펼치는 단계를 하기 도 1에 구체적으로 나타내었다. To uniformly spreading step the glass fiber bundles in the wide was specifically shown in Figure 1. 본 발명에 사용된 유리섬유 다발은 17 ㎛ 직경의 유리섬유 4000 가닥으로 구성된 2400 TEX를 사용하였으며, 폴리프로필렌 수지에 적합하도록 사이징 처리된 것을 사용하였다. The glass fiber bundle used in the present invention was done using 2400 TEX consisting of glass fiber strands of the 4000 17 ㎛ diameter, it was used as a sizing treatment to be suitable for the polypropylene resin. 초기 유리섬유 다발은 약 5 mm 폭을 가지고 있기 때문에, 제1 안내 바(1)의 중앙부는 5 mm의 평평한 부분을 가지고, 그 양단부 대비 들어간 형태를 취한다. Since the initial glass fiber bundles it has a width of about 5 mm, the center portion of the first guide bar (1) has a flat portion of 5 mm, it takes the form preparation into the both end portions.

이어 제1 볼록 바(2)는 상기 수학식 1의 조건을 만족하도록 설계된 것으로 유리섬유 다발을 12 mm의 폭으로 1차 광폭화 시켰다. Following the first convex bar (2) is a glass fiber bundle to be designed to satisfy the condition of Equation 1 was gwangpokhwa 1 to 12 mm-width difference. 이어 제2 안내 바(3)의 중앙부는 10 mm의 평탄한 부분을 가지며, 이는 12 mm의 폭으로 1차 광폭화시킨 유리섬유 다발을 10 mm의 폭으로 정렬하는 역할을 수행한다. After the center portion of the second guide bar 3 has a flat portion of 10 mm, which plays a role of aligning the bundle of the glass fibers in which the primary gwangpokhwa a width of 12 mm to 10 mm in width.

제2 볼록 바(4)는 상기 수학식 1의 조건을 만족하도록 설계된 것으로 제2 안내 바(3)로부터 나온 10 mm 폭의 유리섬유 다발을 24 mm의 폭으로 2차 광폭화시켰다. The second convex bar 4 has a 10 mm width of the glass fiber bundle from that from the second guide bar (3) is designed to satisfy the condition of Equation (1) was secondary to gwangpokhwa of 24 mm width. 이어 제3 안내 바(5)의 중앙부는 20 mm의 평탄한 부분을 가지며, 이는 24 mm의 폭으로 2차 광폭화시킨 유리섬유 다발을 20 mm의 폭으로 정렬하는 역할을 한다. After the center portion of the third guide bar 5 has a flat portion of 20 mm, which plays a role of aligning the bundle of the glass fibers in which secondary gwangpokhwa a width of 24 mm to 20 mm in width. 결과적으로 초기 5 mm 폭의 유리섬유 다발은 20 mm 광폭으로 균일하게 펼쳐지게 된다. As a result, the glass fiber bundle in the initial 5 mm width is unfold uniformly 20 mm wide. 상기 광폭으로 펼쳐진 유리섬유 다발은 2~3개의 유리섬유로 이루어진 두께를 형성하였다. Glass fiber bundle spread by the large-width was formed in a thickness made up of two or three glass fiber.

상기 열가소성 플라스틱-연속섬유 혼성복합체 스트랜드를 제조하는 방법을 하기 도 2에 개략적으로 나타내었다. The thermoplastics-was schematically shown in Figure 2, to a method for producing a continuous fiber hybrid composite strands.

상기 도 1에서 광폭으로 펼쳐진 유리섬유 다발을 가열한 다음, 이를 커플링제가 처방된 폴리프로필렌 테이프로 이루어진 테이프 형상의 열가소성 플라스틱에 접합시켰다. Above also heating the glass fiber bundle after the first one from the wide, then it was bonded to the coupling agent a thermoplastic plastic of the tape-like made of a prescribed polypropylene tape. 상기 유리섬유 다발이 접합된 열가소성 플라스틱을 가로 방향 혹은 세로 방향으로 지그재그 형태로 접은 다음(위사의 경우 요구되는 혼성복합체의 물성에 따라 처음 폭의 1/4로 접고, 경사는 1/2 폭으로 접는다), 200 ~ 300℃ 조건으로 열 압착하여 열가소성 플라스틱-연속섬유 혼성복합체 스트랜드를 제조한다. For this the glass fiber bundle bonded thermoplastics in the horizontal direction or the vertical direction, and then folded in a zigzag form (the weft according to the physical properties of the hybrid composite is required to fold in the first quarter of the width, the slope is folded in half width ), by heat-pressing under the conditions 200 ~ 300 ℃ thermoplastics-continuous fiber hybrid composite to produce a strand. 제조된 열가소성 플라스틱-연속섬유 혼성복합체 스트랜드는 유리섬유를 50 중량%로 포함한다. The prepared thermoplastics-continuous fiber hybrid composite strand comprises a glass fiber to 50% by weight.

하기 도 3은 상기 위사와 경사로 각각 제조된 열가소성 플라스틱-연속섬유 혼성복합체 스트랜드를 사용하여 직조된 보강직물을 개략적으로 나타낸 도면이다. To 3 is the weft and ramps each prepared thermoplastics-a schematic view of a woven reinforcing fabric using continuous fiber hybrid composite strands. 상기 보강직물을 250 ~ 350℃ 조건에서 열간 압착하여 보강직물의 열가소성 플라스틱을 연속섬유에 열용융 함침시킴으로써 최종적으로 본 발명의 보강재를 제조하였다. The reinforcing fabric was prepared in a final reinforcement of the present invention by hot-pressing and hot-melt impregnation of thermoplastics of the reinforcing fabric in the continuous fiber in conditions 250 ~ 350 ℃.

하기 도 4는 종래기술의 보강직물과 본 발명의 보강직물의 단면을 개략적으로 나타내는데, <종래기술의 예>의 보강직물(10)은 경사(12)의 휨이 매우 큼을 알 수 있으나, <본 발명의 실시예>의 보강직물(10)은 경사(12)의 휨이 상대적으로 작음을 확인할 수 있었다. To 4 represent the prior art of the reinforcing fabric and the cross-section of the reinforcement fabric of the present invention schematically, <Example of Conventional Techniques> reinforcement fabric 10 of the can, but shows the bending of the warp 12 so is great, <present examples> reinforcement fabric 10 of the invention was confirmed that the deflection of the warp 12 is relatively small.

이상의 본 발명의 보강직물 및 보강재는 본 발명을 예시하는 것일 뿐 본 발명의 범주 및 기술사상 범위 내에서 다양한 변경 및 수정 가능함은 당업자에게 있어서 명백한 것이며, 이러한 변형 및 수정이 첨부된 특허청구범위에 속하는 것도 당연한 것이다. Or more reinforcing fabric and reinforcing material of the invention is obvious according to intended as possible various changes and modifications within the scope and spirit the scope of the present invention, those skilled in the art to illustrate the present invention, such changes and modifications that the patent belonging to the scope of the appended claims it is taken for granted.

도 1은 본 발명에 따른 볼록 바(convex bar) 및 안내 바(guide bar)로 유리섬유 다발을 광폭으로 균일하게 펼치는 과정을 개략적으로 도시한 것이다. Figure 1 schematically illustrates a convex bar (convex bar) and a process widely and uniformly stretching the bundle of the glass fibers as a wide guide bars (guide bar) in accordance with the present invention.

도 2는 본 발명의 열가소성 플라스틱-연속섬유 혼성 복합체의 제조방법을 개략적으로 도시한 것이다. Figure 2 is a thermoplastic resin of the present invention schematically showing a method of manufacturing a continuous fiber hybrid composite.

도 3은 본 발명의 보강직물을 개략적으로 도시한 평면도이다. Figure 3 is a schematic plan view of the reinforcement fabric of the present invention.

도 4는 종래의 보강직물과 본 발명의 보강직물을 개략적으로 도시한 단면도이다. Figure 4 is a schematic cross-sectional view showing a conventional reinforcing fabric of the reinforcement fabric of the present invention.

*도면의 주요 부호에 대한 설명* * Description of the Related sign of the drawings *

1: 제1 안내 바 2: 제1 볼록 바 1: a first guide bar 2: the first convex bar

3: 제2 안내 바 4: 제2 볼록 바 3: the second guide bar 4: The second convex bar

5: 제3 안내 바 10: 보강직물 5: the third guide bar 10: Reinforcement Fabrics

11: 위사 12: 경사 11: 12 Filling: Slope

Claims (6)

  1. 연속섬유 함유량이 같은 2 군의 열가소성 플라스틱-연속섬유 혼성 복합체 스트랜드가 각각 경사 및 위사로 서로 교차하도록 엮이어 형성되되, Continuous fiber content of the thermoplastic plastic of the second group, such as-continuous fiber hybrid composite strands are being formed so as to cross each other in each lead laced warps and wefts,
    상기 열가소성 플라스틱-연속섬유 혼성 복합체 스트랜드는 소정 폭으로 균일하게 펼쳐진 유리섬유 다발과 이와 동일한 폭의 테이프 형상의 열가소성 플라스틱을 접합하되, 이 플라스틱은 두께가 30 내지 200 ㎛이고, 커플링제를 포함하는 폴리프로필렌으로 구성된 것으로, The thermoplastics-continuous fiber hybrid composite strand, but uniformly stretching the bundle of the glass fibers and this bonding thermoplastics of the tape shape of the same width as the predetermined width, the plastic had a thickness of 30 to 200 ㎛, polyester containing a coupling agent to consist of polypropylene,
    접합 후 가로 혹은 세로 방향으로 지그재그 형태로 겹쳐지게 접은 다음 이를 열 압착시켜 제조한 것이고, After joining overlap in a zigzag form in the transverse or longitudinal direction it will then folded prepared by heat-pressing them,
    상기 경사는 두께가 상기 위사 두께의 n 배(n은 1 이상의 정수이다)이고, 폭은 상기 위사 두께의 1/n 배인 것을 특징으로 하는 보강직물. The slope reinforcing fabric, characterized in that a thickness of an n-times (n is an integer of 1 or more) of the weft thickness, the width times the 1 / n of the weft thickness.
  2. 삭제 delete
  3. 삭제 delete
  4. 제 1항에 있어서, According to claim 1,
    상기 연속섬유는, 유리섬유인 것을 특징으로 하는 보강직물. The continuous fibers are the reinforcing fabric, characterized in that the glass fiber.
  5. 제 4항에 있어서, 5. The method of claim 4,
    상기 유리섬유는, 열가소성 플라스틱-연속섬유 혼성 복합체에 대하여 40 내지 80 중량%로 포함되는 것을 특징으로 하는 보강직물. The glass fibers, thermoplastic-reinforced fabric, characterized in that contained in 40 to 80% by weight with respect to the continuous fiber hybrid composite.
  6. 삭제 delete
KR20090099511A 2009-10-20 2009-10-20 Fiber Reinforced Woven Material And Reinforcing Component Having Excellent Physical Property KR101244059B1 (en)