KR101133360B1 - Low Volatile Organic Compounds Decoration Sheet Manufacturing Method and Decoration Sheet thereof - Google Patents
Low Volatile Organic Compounds Decoration Sheet Manufacturing Method and Decoration Sheet thereof Download PDFInfo
- Publication number
- KR101133360B1 KR101133360B1 KR1020040098652A KR20040098652A KR101133360B1 KR 101133360 B1 KR101133360 B1 KR 101133360B1 KR 1020040098652 A KR1020040098652 A KR 1020040098652A KR 20040098652 A KR20040098652 A KR 20040098652A KR 101133360 B1 KR101133360 B1 KR 101133360B1
- Authority
- KR
- South Korea
- Prior art keywords
- decorative sheet
- layer
- weight
- parts
- porous filler
- Prior art date
Abstract
본 발명은 다층구조의 장식시트에 있어서, 휘발성 유기화합물의 방출이 적고 기재의 휘발성 유기화합물 방출을 억제하는 다공성 무기 필러가 함유된 장식시트 제조방법을 개시한다.The present invention discloses a method for manufacturing a decorative sheet containing a porous inorganic filler in the decorative sheet having a multi-layered structure, which emits less volatile organic compounds and suppresses release of volatile organic compounds on the substrate.
본 발명의 목적은 종래의 PVC 장식시트 제조기술 및 시공기술을 그대로 이용하여 제조와 시공이 가능하고, 각층의 반제품 배합에 휘발성 유기화합물을 포집할 수 있는 다공성 무기 필러를 사용하여 제품에 잔류하는 유기화합물의 휘발을 억제하고 장식기재 및 시공 시 사용된 접착제 유기화합물이 실내건축 공간으로 휘발되는 것을 억제하기 위한 것이다. 이를 위하여 본 발명은 제품의 치수안정 및 시공성 등을 고려하여 부가된 발포 또는 비발포층 구조로 된 이지층 위에 원하는 무늬를 공지의 인쇄방식에 의해 작업하여서 된 인쇄필름 및 투명층 등 표면처리층을 합지하여 다층구조의 시트를 제조하되, 전사 인쇄필름의 반제품 배합에 유기화합물을 흡착할 수 있는 다공성 필러를 투입하되, 다공성 필러를 제품 배합에 투입하기 전에 비점 섭씨 150℃ 미만의 다가 알코올과 하이드로 카본류 용제에 미리 침적, 코팅하여 배합가공중의 가소제와 고비점 용제의 흡착을 방지하고 완제품 엠보공정중 고온가공을 통해 무기필러에 침적, 코팅된 물질을 휘발, 제거하여 다시 본래의 흡착성능을 발휘하도록 하여서 된 것이다.An object of the present invention is to manufacture and construct using conventional PVC decorative sheet manufacturing technology and construction technology as it is, the organic residue remaining in the product using a porous inorganic filler that can collect volatile organic compounds in the semi-finished product of each layer It is to suppress the volatilization of the compound and to suppress the volatilization of the adhesive organic compound used in the decoration materials and construction to the interior construction space. To this end, the present invention laminates a surface treatment layer such as a print film and a transparent layer, which is made by a known printing method on a desired layer having a foamed or non-foamed layer structure added in consideration of product dimensional stability and workability. In order to prepare a multi-layered sheet, a porous filler capable of adsorbing an organic compound is added to the semi-finished product formulation of the transfer printing film, but the polyhydric alcohol and hydrocarbons having a boiling point of less than 150 ° C. before the porous filler is added to the product formulation. To prevent adsorption of plasticizer and high boiling point solvent during compounding process by pre-deposition and coating in solvent, volatilize and remove material deposited and coated on inorganic filler through high temperature processing during finished product embossing process to show original adsorption performance. It was done.
이에 따라, 본 발명은 다공성 필러의 흡착성능에 의하여 제품에 잔류하는 유기화합물의 휘발과, 시공시 사용된 접착제 유기화합물이 실내로 휘발됨을 억제하여 실내 거주자를 유해 물질로부터 보호할 수 있게 되는 친환경적인 장식시트를 제공할 수 있게 되는 효과가 있다.Accordingly, the present invention is environmentally friendly to protect the indoor residents from harmful substances by suppressing the volatilization of the organic compound remaining in the product and the volatilization of the adhesive organic compound used in the construction by the adsorption performance of the porous filler to the room There is an effect that can provide a decorative sheet.
장식시트, 유기화합물, PVC Decorative sheet, organic compound, PVC
Description
도 1,2,3은 본 발명을 적용하기 위한 다층 구조 장식시트를 보인 단면도.1,2,3 is a cross-sectional view showing a multi-layer decorative sheet for applying the present invention.
***도면의 주요 부분에 대한 부호의 설명****** Description of the symbols for the main parts of the drawings ***
1 : 투명층 1-1 : 표면처리층1: transparent layer 1-1: surface treatment layer
2 : 인쇄층 3 : 인쇄필름 2: printed layer 3: printed film
4 : 이지층 4: easy layer
본 발명은 저휘발성 장식시트 및 그 제조방법에 관한 것으로, 휘발성 유기화합물의 발생이 적고 또한 건축자재와 접착제에서 발생하는 휘발성 유기화합물의 발생을 최소화한 저휘발성 장식시트 및 그 제조 방법에 관한 것이다. The present invention relates to a low-volatile decorative sheet and a method for manufacturing the same, and to a low-volatile decorative sheet and a method of manufacturing the same, which is less volatile organic compound generation and minimizes the generation of volatile organic compounds generated in building materials and adhesives.
주지하는 바와 같이 장식시트란 재료를 보호하거나 외관을 다양한 색상과 질감으로 표현하기 위한 마감재를 일컫는 것으로, 특히 실내 인테리어용품 건자재나 가구 책상 등의 표면을 장식하는 표면마감재와 글라스화이버로 치수안정성을 강화하여 가정용 또는 상업용의 바닥재에 많이 사용된다. As is well known, the decorative sheet is a finishing material for protecting the material or expressing the exterior in various colors and textures. In particular, the dimensional stability is enhanced by the surface finishing material and glass fiber that decorate the surface of interior materials such as interior materials and furniture desks. It is widely used in flooring for home or commercial use.
표면마감재는 도장과 라미네이팅(Laminating) 방법으로 제조되며, 라미네이팅 필름(Laminating Film)은 접착형과 점착형이 있다.The surface finish material is manufactured by painting and laminating methods, and the laminating film has an adhesive type and an adhesive type.
이러한 장식시트 원료로는 작업성과 가격적인 장점으로 PVC 소재가 많이 사용되고 있으나 PVC 시트는 유기 가소제와 인쇄 잉크에 포함된 휘발성 유기화합물이 완제품에 잔류하여 사용 시 제품표면을 통해 휘발하는 단점이 있다.PVC materials are widely used as raw materials for the decorative sheet because of their workability and cost. However, the PVC sheet has a disadvantage that volatile organic compounds contained in organic plasticizers and printing inks remain in the finished product and volatilize through the product surface when used.
이러한 단점을 극복하기 위해 폴리우레탄계나 폴리프로필렌계 등 친환경 소재 장식시트가 개발되어 일부 사용되고 있으나 가격이 고가 이면서 PVC 보다 작업성이 떨어지는 단점으로 널리 사용되지 못하는 문제점이 있다. In order to overcome these drawbacks, eco-friendly decorative sheets, such as polyurethane or polypropylene, have been developed and used in part. However, there is a problem in that they are not widely used due to the disadvantages of low price and high workability.
또한, 일례로 대한민국 특허 공개 공보(공개번호 1999-0056878; 발명의 명칭:탈취효과를 갖는 황토가 첨가된 비닐 바닥재 및 그 제조방법)등에 의하여 알려진 바와 같이, 다공성 필러를 함유한 시트나 장식시트는 다공성 필러를 파우더 상태 그대로 투입하는 것이어서, 가공중에 첨가된 휘발성 가소제나 기타 첨가제에 의해 다공성 필러가 가공도중 고비점의 기체를 흡유 또는 흡착하게 되어 완제품 상에서 흡착성능을 발휘하지 못하는 문제점이 있어서, 다공성 필러의 기능이 상실되어 이를 함유한 시트나 장식시트는 그 별다른 유해물질의 흡착등 원하는 친환경적 기능을 얻지 못하게 되는 문제점이 있다.Further, an example in Republic of Korea Patent Laid-Open;: a, as by a known (publication number 1999-0056878 invention Name of the method that the loess has a deodorizing added vinyl flooring and its production) or the like, containing a porous filler sheet or decorative sheet Since the porous filler is injected into the powder state, the porous filler may not absorb or adsorb high boiling gas during processing due to the volatile plasticizer or other additives added during processing. The function of the filler is lost and the sheet or decorative sheet containing the same does not have the desired environmentally friendly functions such as adsorption of the other harmful substances.
또한, 이러한 다공성 필러를 함유한 시트나 장식시트는 가공 공정중에 다공성 필러에 포함된 기포로 인하여 제품 가공불량이 발생하는 문제점이 있어서, 생산성이 저조한 문제점이 있는 것이다.In addition, the sheet or decorative sheet containing such a porous filler has a problem that a product processing defect occurs due to bubbles contained in the porous filler during the processing process, there is a problem of poor productivity.
본 발명은 상기한 바와 같은 종래 PVC 장식시트의 문제점을 해결하기 위하여 안출된 것으로서, 본 발명의 목적은 종래의 PVC 장식시트 제조기술 및 시공기술을 그대로 이용하여 제조와 시공이 가능하고, 각층의 반제품 배합에 휘발성 유기화합물을 포집할 수 있는 다공성 필러를 사용하여 제품에 잔류하는 유기화합물의 휘발을 억제하고 장식기재 및 시공 시 사용된 접착제 유기화합물이 실내건축 공간으로 휘발되는 것을 억제하는 친환경적인 저 휘발성 장식시트 및 그 제조 방법를 제공함에 있다. The present invention has been made to solve the problems of the conventional PVC decorative sheet as described above, the object of the present invention can be manufactured and constructed using the conventional PVC decorative sheet manufacturing technology and construction technology, semi-finished products of each layer Eco-friendly low volatility that suppresses volatilization of organic compounds remaining in products by using porous fillers that can collect volatile organic compounds in the formulation and volatilization of adhesive organic compounds used in decorative materials and construction It is to provide a decorative sheet and a method of manufacturing the same.
상기 목적을 달성하기 위하여 본 발명은 제품의 치수안정 및 시공성등을 고려하여 부가된 발포 또는 비발포층 구조로 된 이지층위에 원하는 무늬를 공지의 인쇄방식에 의해 작업하여서 된 인쇄필름 및 투명필름 등 표면 처리층을 합지하여 다층구조의 시트를 제조하되, 이지층, 인쇄필름, 투명필름, 등의 구성층 중 어느 한층 이상의 반제품 배합에 유기화합물을 흡착할 수 있는 다공성 필러를 투입하고, 상기 다공성 필러를 제품 배합에 투입하기 전에 비점 섭씨 150℃ 미만의 다가 알코올과 하이드로 카본류 용제에 미리 침적, 코팅하여 배합가공중의 가소제와 고비점 용제의 흡착을 방지하고 완제품 엠보공정중 고온가공을 통해 무기필러에 침적, 코팅된 물질을 휘발, 제거하여 다시 본래의 흡착성능을 발휘하도록 하여서 된 저휘발성 장식시트 및 그 제조 방법을 제안한다.In order to achieve the above object, the present invention is a printing film and a transparent film made by working a desired pattern on the easy layer having a foamed or non-foamed layer structure added in consideration of the dimensional stability and workability of the product by a known printing method. The surface treatment layer is laminated to produce a sheet having a multi-layer structure, a porous filler capable of adsorbing an organic compound is added to a semi-finished product mixture of at least one layer of a component layer such as an easy layer, a printing film, a transparent film, and the like, and the porous filler In order to prevent the adsorption of plasticizers and high-boiling solvents during compounding process and high temperature processing during finished product embossing process, inorganic fillers are deposited and coated in polyhydric alcohols and hydrocarbon solvents with boiling point below 150 ° C before adding them to product formulation. Low volatility decorative sheet which volatilizes and removes material deposited on it and removes it to show its original adsorption performance It suggests a crude way.
이에 따라, 본 발명은 다공성 필러의 흡착성능에 의하여 제품에 잔류하는 유기화합물의 휘발과, 시공 시 사용된 접착제 유기화합물이 실내로 휘발됨을 억제하 여 실내 거주자를 유해 물질로부터 보호할 수 있게 되는 친환경적인 장식시트를 제공할 수 있게 되는 효과가 있다.Accordingly, the present invention is environmentally friendly to protect the indoor residents from harmful substances by suppressing the volatilization of the organic compound remaining in the product and the adhesive organic compound used in the construction by the adsorption performance of the porous filler to the interior volatilization There is an effect that can provide a decorative sheet.
이러한 본 발명을 더욱 상세히 설명하면 다음과 같다.When explaining the present invention in more detail as follows.
본 발명의 다공성 필러가 함유된 제품의 첨부 도면을 참조하여 상세하게 설명하면 다음과 같다.When described in detail with reference to the accompanying drawings of the product containing the porous filler of the present invention.
본 발명에 따른 예로서, 도 1에 도시된 PVC 장식시트는 이지층(4)위에 그라비아 인쇄를 통해 다양한 인쇄층(2)이 형성된 인쇄필름(3)과 투명필름(1)을 합지하여 구성된다.As an example according to the present invention, the PVC decorative sheet shown in FIG. 1 is formed by laminating a
이와 같이, 원하는 무늬가 인쇄된 인쇄필름(3)과 그의 상부에 투명 필름(1)을 합지하는 방법은 열합지 방식을 이용한다. 합지하려는 필름을 140~170℃의 히팅드럼이나 오븐을 이용하여 충분히 가열한 다음 압력을 주면 열가소성 PVC 수지의 특성상 합지가 가능하다. 이때 각각의 인쇄필름(3), 투명필름(1)은 카렌다를 이용한 압연가공이나 티다이를 이용한 압출가공으로 시트를 제작한 후 열합지 한다.As such, the method of laminating the
상기 이지층(4)은, 예로서 중합도 800~1000의 PVC 스트레이트 수지 100중량부, 가소제 10~30중량부, 안정제 2~4중량부, 충진제 1~20중량부, 선택적으로 다공성 필러 0.5~50중량부를 카렌다에서 압연 가공하거나 혹은 티다이에서 압출 가공하여 시트를 얻을 수 있다. 상기 가소제는 디옥틸프탈레이트(DOP)나 에폭시계 가소제를 단독 또는 혼용하여 사용하며, 안정제는 카드뮴-바륨-아연계 또는 바륨-아연계의 복합안정제를 사용하고, 충진제는 탄산칼슘이나 실리카를 입자크기 0.1~1㎛으로 한 코팅 타입의 필러 형태로 사용한다. 특히 다공성 필러는 미리 비점 150℃ 미만 의 다가 알코올과 하이드로 카본류 용제에 침적시킨 다공성 필러를 사용한다. 사용되는 다가 알코올로는 노말부틸알콜, 이소프로필 알코올 등이 있으며, 하이드로 카본류 용제로는 탄소수가 10개 이하인 데칸(Decane)이나 카본 백등유 등이 있다. The
상기 인쇄필름(3)은, 예로서 중합도 800~1000의 PVC 스트레이트 수지 100중량부, 가소제 5~30 중량부, 안정제 1~3중량부, 충진제 2~20중량부, 다공성 필러 0.5~50중량부를 카렌다에서 압연 가공하거나 혹은 티다이에서 압출 가공하여 시트를 얻을 수 있다. 상기 가소제, 안정제, 충진제는 상기 이지층(4)에서 제시된 것과 동일한 종류의 것을 사용하며, 다공성 필러 역시 상기 이지층(4)에서 사용한 것과 동일한 종류의 물질을 동일한 방법으로 미리 다가 알코올과 하이드로 카본류 용제에 침적시킨 것을 사용한다. 이의 상부에 그라비아 인쇄방식을 이용하여 장식효과를 부여한 인쇄층(2)을 형성하여 얻을 수 있다.The
인쇄층(2) 형성시 이용되는 잉크는 예로서 중합도 600~700의 PVC계 공중합체 10~40중량부, 메틸에틸케톤 30~70중량부, 일반적인 공지의 안료 1~20중량부를 투입하여 고속믹서로 혼합하여 적용할 수 있다.The ink used to form the
상기 투명필름(1)은, 예로서 중합도 600~1500의 PVC 스트레이트 수지 100중량부, 가소제 5~30 중량부, 안정제 1~3중량부, 다공성필러 0.5~ 50 중량부를 정량투입하여 카렌다에서 압연 가공하거나 혹은 티다이에서 압출 가공하여 시트를 얻을 수 있다. 상기 가소제, 안정제는 상기 이지층(4) 및 인쇄필름(3)에서 제시된 것과 동일한 종류의 것을 사용하며, 다공성 필러 역시 상기 이지층(4)에서 사용한 것과 동일한 종류의 물질을 동일한 방법으로 미리 다가 알코올과 하이드로 카본류 용제 에 침적시킨 것을 사용한다. 단, 투명필름(1)에 사용하는 다공성 필러는 입도가 크면 투명성이 떨어지는 단점이 있으므로 1.0㎛ 이하의 미립 다공성 필러를 사용하는 것이 바람직하다.The
이러한, 본 발명에서 사용되는 다공성 필러는 무기입자로 입도는 0.05㎛~50㎛인 것이 바람직하다. 각각의 입도가 0.05㎛ 미만이면 비표면적이 증가하여 유기화합물의 흡착성능은 좋으나 PVC 와 혼련이 어렵고 가공시간이 오래 소요되는 단점이 있으며, 입도가 50㎛를 초과하면 투입량 대비 표면적이 적어 투입량 대비 휘발성 유기화합물의 흡착성능이 떨어지며 필름의 인장강도, 인열강도, 신율 등 기계적인 물성이 떨어지는 단점이 있다. 다공성 필러로는 제올라이트, 실리카, 유리, 세라믹, 활성탄 등의 무기계 원료 중 어느 하나로 하거나 복합시켜 사용할 수 있다. 본 발명의 실시예에서는 다공성 필러로 비표면적이 30-50 ㎡/g 인 제올라이트를 사용하였으며 유기화합물의 흡착뿐만 아니라 중금속 흡착에도 뛰어난 성능을 발휘한다. The porous filler used in the present invention is an inorganic particle, the particle size is preferably 0.05㎛ ~ 50㎛. If the particle size is less than 0.05㎛, the specific surface area increases, so that the adsorption performance of organic compounds is good, but it is difficult to knead with PVC and takes long processing time.If the particle size exceeds 50㎛, the surface area compared to the input volume is less volatile compared to the input volume. Adsorption performance of organic compounds is poor, and mechanical properties such as tensile strength, tear strength, and elongation of the film are inferior. As the porous filler, any one of inorganic materials such as zeolite, silica, glass, ceramic, activated carbon, or the like can be used or combined. In the embodiment of the present invention, a zeolite having a specific surface area of 30-50
본 발명에서의 다공성 필러는 입자,괴 등의 고체속에 크기가 다양한 기공을 갖는 것이며, 특히, 본 발명에서는 다공성 필러를 비점 섭씨 150℃ 미만의 다가 알코올, 하이드로 카본 용제에 분산제로 미리 침적을 시켜 표면을 코팅 후 배합에 투입하여 가공 중에는 가소제의 흡유나 기타 유기화합물의 흡착을 방지할 수 있게 된다. In the present invention, the porous filler has pores of various sizes in solids such as particles and ingots. Particularly, in the present invention, the porous filler is pre-deposited with a dispersant in a polyhydric alcohol and a hydrocarbon solvent having a boiling point of less than 150 ° C. After coating, it is added to the compounding to prevent oil absorption of plasticizers and adsorption of other organic compounds during processing.
상기와 같이 얻어지는 각 반제품을 열합지기를 통하여 합지하고, 완제품 엠보공정 중에서 섭씨 150℃ 이상의 고열로 가열하여 주면 다공성 필러를 감싸고 있 던 코팅제가 증발하면서 파괴되어 다공성 필러가 다시 특유의 흡착기능을 발휘, 휘발성 유기화합물을 효과적으로 흡착할 수 있게 되는 기능을 갖게 되는 것이다. When each semi-finished product obtained as described above is laminated through a thermocoupler and heated to a high temperature of 150 ° C. or higher during the finished product embossing process, the coating agent surrounding the porous filler is destroyed while evaporating and the porous filler again exhibits its unique adsorption function. It will have the function to effectively adsorb volatile organic compounds.
이와 같은 다공성 필러를 본 발명의 장식시트의 각 구성층 반제품 배합에 포함시킴에 있어서, 투명필름(1), 인쇄필름(3), 이지층(4) 등의 구성층 중 어느 한층 이상에 포함시켜 유기화합물의 흡착성능을 발휘하게 한다. In incorporating such a porous filler into each component layer semifinished product of the decorative sheet of the present invention, it is included in any one or more of the component layers such as the
한편, 본 발명에서 투명필름(1),인쇄필름(3)은 가장 가공성이 우수한 폴리염화 비닐수지 또는 폴리 에틸렌 테레프탈레이트(PET) 또는 아크릴필름 또는 폴리 프로필렌(PP)를 사용할 수 있다.Meanwhile, in the present invention, the
아울러, 본 발명은 도2로 보인 바와 같이 투명필름(1)을 적용하지 않고, 공지의 단색 인쇄필름(3)을 이지층(4)에 합지하여 사용할 수도 있으며, 도3으로 보인 바와 같이 이지층(4)위에 인쇄층(2)이 구비된 인쇄필름(3)을 합지한 다음 그 위를 공지의 표면처리층(1-1)으로 합지하여 다양한 질감을 창출할 수도 있다.In addition, the present invention may use a known
이하, 실시예를 통하여 본 발명을 상세하게 설명하며, 본 발명의 내용은 이하 실시예에 한정되는 것은 아니다.Hereinafter, the present invention will be described in detail through examples, and the content of the present invention is not limited to the following examples.
<실시예><Examples>
A 시편제조A Specimen Manufacturing
중합도 1000의 PVC 스트레이트 수지 100중량부, 디옥틸프탈레이트(DOP) 15중량부, 에폭시계 가소제(Epoxidized Soybean Oil) 5중량부, 카드뮴-바륨-아연계 안정제 2중량부, 미리 비점 150℃ 미만의 이소프로필 알코올과 백등유에 침적시킨 평균입경 0.5㎛ 다공성 제올라이트 10중량부를 고속 임펠러가 있는 믹서기에서 20분 간 믹싱하고 반바리 믹서(BANBURY MIXER)나 압출기에서 혼련한 후 카렌다에서 압연 가공한 0.10mm 투명필름과, 100 parts by weight of a PVC straight resin having a degree of polymerization of 1000, 15 parts by weight of dioctylphthalate (DOP), 5 parts by weight of an epoxy plasticizer (Epoxidized Soybean Oil), 2 parts by weight of a cadmium-barium-zinc-based stabilizer, and an isotropy of less than 150 ° C in advance. 10 parts by weight of a 0.5 μm porous zeolite with an average particle diameter of 0.5 μm deposited on propyl alcohol and white kerosene were mixed in a mixer with a high speed impeller for 20 minutes, kneaded in a BANBURY MIXER or an extruder, and rolled in a calender and 0.10 mm transparent film. ,
중합도 1000의 PVC 스트레이트 수지 100중량부, 디옥틸프탈레이트(DOP) 10 중량부, 에폭시계 가소제(Epoxidized Soybean Oil) 5중량부, 카드뮴-바륨-아연계 안정제 2중량부, 탄산칼슘 5중량부, 등과 미리 비점 150℃ 미만의 이소프로필 알코올과 백등유에 침적시킨 평균입경 0.5㎛ 다공성 제올라이트 20중량부를 고속 임펠러가 있는 믹서기에서 20분간 믹싱하고 반바리 믹서(BANBURY MIXER)나 압출기에서 혼련한 후 카렌다에서 압연 가공하고, 이의 상부에 그라비아 인쇄공법을 이용하여 장식효과를 부여한 0.10mm 인쇄필름과,100 parts by weight of a PVC straight resin having a degree of polymerization of 1000, 10 parts by weight of dioctylphthalate (DOP), 5 parts by weight of epoxy-based plasticizer (Epoxidized Soybean Oil), 2 parts by weight of cadmium-barium-zinc-based stabilizer, 5 parts by weight of calcium carbonate, etc. 20 parts by weight of an average particle diameter of 0.5 μm porous zeolite deposited in isopropyl alcohol below 150 ° C and white kerosene were mixed in a mixer with a high speed impeller for 20 minutes, kneaded in a BANBURY MIXER or an extruder, and then rolled in a calendar. And 0.10mm printing film to give a decorative effect on the upper part using a gravure printing method,
중합도 1000의 PVC 스트레이트 수지 100중량부, 디옥틸프탈레이트(DOP) 15중량부, 에폭시계 가소제(Epoxidized Soybean Oil) 5중량부, 카드뮴-바륨-아연계 안정제 2중량부, 탄산칼슘 10중량부, 등을 반바리 믹서(BANBURY MIXER)나 압출기에서 혼련한 후 카렌다에서 압연 가공한 0.10mm 이지층을, 100 parts by weight of a PVC straight resin having a degree of polymerization of 1000, 15 parts by weight of dioctylphthalate (DOP), 5 parts by weight of epoxy-based plasticizer (Epoxidized Soybean Oil), 2 parts by weight of cadmium-barium-zinc-based stabilizer, 10 parts by weight of calcium carbonate, etc. Was kneaded in a BANBURY MIXER or an extruder, and then rolled in a calendar,
각각 열 합지기를 통해 150℃의 열조건에서 합지하고 다시 표면에 180℃ 이상의 열을 가하여 제올라이트에 침적된 코팅제를 휘발시키면서 엠보작업을 완료한 후 장식시트를 완성하였다. Each of them was laminated under thermal conditions of 150 ° C., and then heated to 180 ° C. or higher on the surface to volatilize the coating deposited on the zeolite while completing the embossing, and then finished the decorative sheet.
B 시편제조B Specimen Manufacturing
중합도 1000의 PVC 스트레이트 수지 100중량부, 디옥틸프탈레이트(DOP) 15중량부, 에폭시계 가소제(Epoxidized Soybean Oil) 5중량부, 카드뮴-바륨-아연계 안정제 2중량부, 미리 침적시키지 않은 평균입경 0.5㎛ 다공성 제올라이트 20중량부 를 고속 임펠러가 있는 믹서기에서 20분간 믹싱하고 반바리 믹서(BANBURY MIXER)나 압출기에서 혼련한 후 카렌다에서 압연 가공한 0.10mm 투명필름과, 100 parts by weight of a PVC straight resin having a degree of polymerization of 1000, 15 parts by weight of dioctylphthalate (DOP), 5 parts by weight of an epoxy plasticizer (Epoxidized Soybean Oil), 2 parts by weight of a cadmium-barium-zinc-based stabilizer, an average particle diameter not previously deposited 0.5 0.10 mm transparent film, 20 parts by weight of the porosity zeolite was mixed in a mixer with a high speed impeller for 20 minutes, kneaded in a BANBURY MIXER or an extruder, and rolled in a calender.
중합도 1000의 PVC 스트레이트 수지 100중량부, 디옥틸프탈레이트(DOP) 10 중량부, 에폭시계 가소제(Epoxidized Soybean Oil) 5중량부, 카드뮴-바륨-아연계 안정제 2중량부, 탄산칼슘 5중량부, 등과 미리 침적시키지 않은 평균입경 0.5㎛ 다공성 제올라이트 20중량부를 고속 임펠러가 있는 믹서기에서 20분간 믹싱하고 반바리 믹서(BANBURY MIXER)나 압출기에서 혼련한 후 카렌다에서 압연 가공하여 이의 상부에 그라비아 인쇄공법을 이용하여 장식효과를 부여한 0.10mm 인쇄필름과,100 parts by weight of a PVC straight resin having a degree of polymerization of 1000, 10 parts by weight of dioctylphthalate (DOP), 5 parts by weight of epoxy-based plasticizer (Epoxidized Soybean Oil), 2 parts by weight of cadmium-barium-zinc-based stabilizer, 5 parts by weight of calcium carbonate, etc. 20 parts by weight of 0.5 μm porous zeolite, which is not pre-deposited, was mixed in a mixer with a high speed impeller for 20 minutes, kneaded in a BANBURY MIXER or an extruder, and then rolled in a calender, and then gravure printing was applied on the top thereof. 0.10mm printing film with decorative effect,
중합도 1000의 PVC 스트레이트 수지 100중량부, 디옥틸프탈레이트(DOP) 15중량부, 에폭시계 가소제(Epoxidized Soybean Oil) 5중량부, 카드뮴-바륨-아연계 안정제 2중량부, 탄산칼슘 10중량부, 등을 반바리 믹서(BANBURY MIXER)나 압출기에서 혼련한 후 카렌다에서 압연 가공한 0.10mm 이지층을, 100 parts by weight of a PVC straight resin having a degree of polymerization of 1000, 15 parts by weight of dioctylphthalate (DOP), 5 parts by weight of epoxy-based plasticizer (Epoxidized Soybean Oil), 2 parts by weight of cadmium-barium-zinc-based stabilizer, 10 parts by weight of calcium carbonate, etc. Was kneaded in a BANBURY MIXER or an extruder, and then rolled in a calendar,
각각 열 합지기를 통해 150℃의 열조건에서 합지하여 장식시트를 완성하였다.Each was laminated under a thermal condition of 150 ℃ through a thermal combiner to complete a decorative sheet.
C 시편제조C Specimen Manufacturing
중합도 1000의 PVC 스트레이트 수지 100중량부, 디옥틸프탈레이트(DOP) 15중량부, 에폭시계 가소제(Epoxidized Soybean Oil) 5중량부, 카드뮴-바륨-아연계 안정제 2중량부를 정량투입하여 고속 임펠러가 있는 믹서기에서 20분간 믹싱하며 반바리 믹서(BANBURY MIXER)나 압출기에서 혼련한 후 카렌다에서 압연 가공한 0.10mm 투명필름과, 100 parts by weight of a PVC straight resin with a degree of polymerization of 1000, 15 parts by weight of dioctylphthalate (DOP), 5 parts by weight of an epoxy plasticizer (Epoxidized Soybean Oil), and 2 parts by weight of a cadmium-barium-zinc-based stabilizer. 0.10mm transparent film which was kneaded in BANBURY MIXER or extruder for 20 minutes in
중합도 1000의 PVC 스트레이트 수지 100중량부, 디옥틸프탈레이트(DOP) 10 중량부, 에폭시계 가소제(Epoxidized Soybean Oil) 5중량부, 카드뮴-바륨-아연계 안정제 2중량부, 평균입경 0.5㎛ 탄산칼슘 20중량부, 등을 정량투입하여 고속 임펠러가 있는 믹서기에서 20분간 믹싱하며 반바리 믹서(BANBURY MIXER)나 압출기에서 혼련한 후 카렌다에서 압연 가공하여 이의 상부에 그라비아 인쇄공법을 이용하여 장식효과를 부여한 0.10mm 인쇄필름과,100 parts by weight of a PVC straight resin having a degree of polymerization of 1000, 10 parts by weight of dioctylphthalate (DOP), 5 parts by weight of an epoxy plasticizer (Epoxidized Soybean Oil), 2 parts by weight of a cadmium-barium-zinc-based stabilizer, an average particle diameter of 0.5 μm calcium carbonate 20 0.10 weight part, etc. is mixed and mixed in a mixer with a high speed impeller for 20 minutes, kneaded in a BANBURY MIXER or an extruder, and rolled in a calender to give a decorative effect to the upper part by using a gravure printing method. mm printing film,
중합도 1000의 PVC 스트레이트 수지 100중량부, 디옥틸프탈레이트(DOP) 15중량부, 에폭시계 가소제(Epoxidized Soybean Oil) 5중량부, 카드뮴-바륨-아연계 안정제 2중량부, 평균입경 0.5㎛ 탄산칼슘 20중량부, 등을 반바리 믹서(BANBURY MIXER)나 압출기에서 혼련한 후 카렌다에서 압연 가공한 0.10mm 이지층을, 100 parts by weight of a PVC straight resin having a degree of polymerization of 1000, 15 parts by weight of dioctylphthalate (DOP), 5 parts by weight of an epoxy plasticizer (Epoxidized Soybean Oil), 2 parts by weight of a cadmium-barium-zinc-based stabilizer, an average particle diameter of 0.5 μm calcium carbonate 20 The 0.10 mm easy layer rolled by calender after kneading parts by weight in a BANBURY MIXER or an extruder,
각각 열 합지기를 통해 180℃의 열조건에서 합지하여 입체 장식시트를 완성하였다.Each of them was laminated under thermal conditions of 180 ° C. to form a three-dimensional decorative sheet.
이러한 본 발명은 하기의 분석표에서 확인되는 바와 같이 본 발명에 의한 A,B시편은 TVOCs와 포름알데히드의 방출량이 무기 필러를 전혀 사용하지 않은 종래의 C시편에 비하여 약 25% 내지 75% 정도 현저히 낮으며, As can be seen from the analysis table below, the A and B specimens according to the present invention have a significantly lower emission rate of about 25% to 75% of TVOCs and formaldehyde than conventional C specimens without using any inorganic filler. And
휘발성 유기화합물 발생에 있어서도 절반이하로 현저히 감소하여 친 환경적인 기능을 발휘된다. 따라서, 이를 이용하여 건축 자재등으로 활용하게 되면, 종래의 유해 화학 물질 방출로 인하여 야기되었던 두통, 천식, 피로, 피부염 등 소위 새집 증후군의 예방에 기여할 수 있게 되는 것이다. In the generation of volatile organic compounds, it is significantly reduced to less than half, thereby exhibiting environmentally friendly functions. Therefore, by using it as a building material, it is possible to contribute to the prevention of the so-called sick house syndrome, such as headache, asthma, fatigue, dermatitis caused by the conventional release of harmful chemicals.
<표1> 휘발성 유기화합물 분석표 단위 (㎎/㎡h)
Table 1 Analysis Table of Volatile Organic Compounds (mg / ㎡h)
(C시편대비)Reduction rate
(Compared to C specimen)
1) 소형 챔버법 1주일 후 측정1) 1 week after small chamber method
2) 방출시험챔버내의 온도 및 상대습도(25℃, 50%)를 유지 2) Maintain temperature and relative humidity (25 ℃, 50%) in emission test chamber
온도 : 25±0℃ 상대습도 : 50±5%
Temperature: 25 ± 0 ℃ Relative Humidity: 50 ± 5%
<표 2> 휘발감량 분석표<Table 2> Volatility Loss Analysis Table
(C시편대비)Reduction rate
(Compared to C specimen)
휘발감량 측정Stored in an oven for 8 hours and cooled at room temperature for 1 hour
Volatility Loss Measurement
분석표단위 (%)Analytical Table Unit (%)
이와 같이 본 발명은 휘발성 유기화합물 발생을 최소화하여 친환경장식시트를 제조할 수 있다.
As such, the present invention can manufacture an eco-friendly decorative sheet by minimizing the generation of volatile organic compounds.
Claims (7)