KR100860270B1 - Manufacturing method of artificial carving work using cement - Google Patents

Manufacturing method of artificial carving work using cement Download PDF

Info

Publication number
KR100860270B1
KR100860270B1 KR1020080024767A KR20080024767A KR100860270B1 KR 100860270 B1 KR100860270 B1 KR 100860270B1 KR 1020080024767 A KR1020080024767 A KR 1020080024767A KR 20080024767 A KR20080024767 A KR 20080024767A KR 100860270 B1 KR100860270 B1 KR 100860270B1
Authority
KR
South Korea
Prior art keywords
cement
plastering
artificial
layer
sculpture
Prior art date
Application number
KR1020080024767A
Other languages
Korean (ko)
Inventor
이여백
Original Assignee
(주) 아트파밀리아
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주) 아트파밀리아 filed Critical (주) 아트파밀리아
Priority to KR1020080024767A priority Critical patent/KR100860270B1/en
Application granted granted Critical
Publication of KR100860270B1 publication Critical patent/KR100860270B1/en

Abstract

An artificial sculpture manufacturing method using cement is provided to minimize cracks and peel-off generated on the artificial sculpture after a long time by plastering the sculpture with the first and second cement mixtures at least two times. An artificial sculpture manufacturing method using cement comprises the steps of: making the structure by metal frames(10); installing a metal net(20) on the metal framed structure; forming a first plastered layer(22) by firstly plastering the metal net with kneaded materials, wherein the kneaded material is produced by mixing very-early-strength cement, Portland cement, waterproof liquid, a cement thickening agent, reinforced resin fiber, and color pigments and then kneading the mixture with the water; scratching the surface of the first plastered layer and applying resin bond; forming a second plastered layer(24) by secondly plastering the scratched surface of the first plastered layer with the kneaded material; and carving and painting the surface of the second plastered layer.

Description

시멘트를 이용한 인공 조각품의 제작방법{Manufacturing method of artificial carving work using cement}Manufacturing method of artificial carving work using cement

본 발명은 시멘트를 이용한 인공 조각품 제작방법에 관한 것으로, 구체적으로는 공원, 테마파크, 및 박물관 등에 사용되는 인공 조형물을 자연스러운 이미지로 연출할 수 있는 시멘트 조각품 제작방법에 관한 것이다.The present invention relates to a method of manufacturing artificial sculpture using cement, and more particularly, to a method of manufacturing a cement sculpture that can produce artificial sculptures used in parks, theme parks, museums, etc. in a natural image.

인공 조각품이라 함은, 사람이 인공적으로 폭포의 표면이나 인공암 등을 통해 현대인의 시각 만족을 꾀하고 있는 것으로서, 이러한 인공 조형물은 근래에 들어와서 각종 놀이동산이나 테마파크, 전시회 및 박물관 등에 널리 조성되고 있다.Artificial sculptures are artificially designed to satisfy the visual needs of modern people through the surface of waterfalls and artificial rocks. These artificial sculptures have recently been widely established in various amusement parks, theme parks, exhibitions and museums. have.

이와같은 인공 조각품중 특히 인공암은 천연바위와 동일할 정도의 질감이 표현되고 색상, 체적, 강도 면에서도 일반인이 구별하기가 어려울 정도로 천연바위와 유사하다.Of these artificial sculptures, in particular, the artificial rock is similar to natural rock, so that the texture is expressed to the same as the natural rock, and color, volume, and strength are difficult for the general public to distinguish.

따라서, 이러한 인공 조각품은, 최근 취미생활로 각광을 받고 있는 인공암벽 등반 또는 도로의 환경 개선을 위한 인공폭포 등의 암벽에 흔히 사용되고, 최근에 들어와서는 건축의 외장재로서도 많이 이용되고 있다. 이러한 인공 조각품은 콘크리트 문명의 도시화된 사회에서 자연을 접하기 어려운 도시인의 휴식공간을 연출하는데 매우 효과적이고, 자연을 연출하고자 하는 동물원, 분수, 수영장, 연못 등에 빠르게 보급되어 그 사용범위가 넓어지고 있는 실정이다.Therefore, such artificial sculptures are commonly used in artificial rock climbing, which has been spotlighted as a hobby in recent years, or artificial waterfalls for improving the environment of roads, and have recently been used as exterior materials for architecture. These artificial sculptures are very effective in creating a resting place for urban people who are difficult to encounter nature in the urbanized society of concrete civilization, and are rapidly spreading to the zoos, fountains, swimming pools, and ponds that want to produce nature. It is true.

이러한 인공 조각품은 주로 유리섬유 강화 시멘트(Glassfiber Reinforced Cement : 이하 'GRC'라 함)로 다수의 패널을 제작한 뒤, 상기 패널에 설치된 철심 등과 같은 연결부재로 용접과 같은 방법으로 상기 패널들이 연결되거나, 연결부위에 모르타르나 GRC를 주입하여 상기 패널들을 연결하고 있다.These artificial sculptures are mainly made of glass fiber reinforced cement (Glassfiber Reinforced Cement) (hereinafter referred to as 'GRC') to make a number of panels, and then the panels are connected by welding or the like by a connecting member such as an iron core installed on the panel or The panels are connected by injecting mortar or GRC into the connection part.

그러나 상기 패널들이 상호 일체로 제작된 것이 아니기 때문에 장시간이 지나면 연결부위에 크랙(crack)이 발생하게 되는 문제가 있다. 따라서, 인공 조각품에 크랙이 발생하면, 빗물이 유입되어 인공 조각품의 내부에 설치된 철골구조물이 부식되는 문제가 발생한다. 또한, 인공 조각품을 지지하는 철골구조물이 부식되면, 지지하는 힘이 약해지므로 인공 조형물의 형태가 변형되는 문제가 발생된다.However, since the panels are not manufactured integrally with each other, there is a problem that a crack occurs in the connection part after a long time. Therefore, when a crack occurs in the artificial sculpture, rainwater flows into the steel structure installed inside the artificial sculpture to cause a problem. In addition, when the steel structure supporting the artificial sculpture is corroded, the supporting force is weakened, so that the shape of the artificial sculpture is deformed.

그러나, GRC는 시멘트 성분이 40~60%를 차지하고 있으므로, 오랜 시간이 경과하면 백화현상 일어나는 문제점이 있으며, 풍화작용이나 빗물에 의해 인공 조성물의 표면이 얼룩지거나 부식되는 문제점이 있다.However, since the GRC occupies 40-60% of cement, there is a problem that whitening occurs after a long time, and the surface of the artificial composition is stained or corroded by weathering or rainwater.

그리고, GRC 패널의 크기를 크게 제작하는 것에 한계가 있어, 크기가 작은 다수의 GRC 패널들에 의해 조립된 인공 조형품은 천연적 자연미를 가지지 못하는 문제점이 있다.In addition, there is a limit to making the size of the GRC panel large, and the artificial sculpture assembled by the plurality of small GRC panels has a problem of not having natural natural beauty.

본 발명은 상기 문제를 해결하기 위해 발명된 것으로, 제 1 혼합 시멘트와 제 2 혼합 시멘트로 인공 조각품에 미장작업을 함으로써, 인공 조각품에 발생되는 크랙과 인공 조각품 내부에 설치된 금속구조물의 부식방지를 최소화하여 인공 조각품의 변형을 방지 할 수 있는 시멘트를 이용한 인공 조각품의 제작방법을 제공하는데 있다.The present invention has been invented to solve the above problems, by performing the plastering work on the artificial sculpture with the first mixed cement and the second mixed cement, minimizing corrosion prevention of cracks generated in the artificial sculpture and metal structures installed inside the artificial sculpture. By providing a method of manufacturing artificial sculpture using cement that can prevent the deformation of the artificial sculpture.

또한, 인공 조각품에 발생하는 백화현상이나, 인위적 충돌에 의한 파손으로 발생하는 파손을 최소화하여 자연적 이미지를 그대로 간직할 수 있는 시멘트를 이용한 인공 조각품의 제작방법을 제공하는데 있다.In addition, the present invention provides a method of manufacturing artificial sculpture using cement that can retain the natural image by minimizing the damage caused by the whitening phenomenon or the damage caused by artificial collision.

상기 목적을 달성하기 위해 본 발명은, 인공 조각품 제작방법에 있어서, 금속프레임으로 골격을 제작하는 단계와, 상기 단계에 의해 제작된 금속프레임 골격에 금속망을 설치하는 단계와, 상기 단계에 의해 설치된 금속망에 1차 미장작업을 하여 제 1 미장층을 형성하는 단계와, 상기 단계에 의해 형성된 제 1 미장층의 표면에 스크래치 작업과, 수지성 본드를 도포하는 단계와, 상기 단계에 의해 스크래치 작업을 마친 제 1 미장층의 표면에 2차 미장작업을 하여 제 2 미장층을 형성하는 단계 및 상기 단계에 의해 형성된 제 2 미장층의 표면에 조각 및 페인팅하는 단계를 포함하여 이루어진 것을 특징으로 한다.In order to achieve the above object, the present invention, in the artificial sculpture manufacturing method, the step of manufacturing a skeleton with a metal frame, the step of installing a metal net on the metal frame skeleton produced by the step, and installed by the step Forming a first plastering layer by primary plastering on the metal mesh; scratching the surface of the first plastering layer formed by the step; applying a resin bond; and scratching by the step A second plastering process is performed on the surface of the first plastering layer after completing the step of forming a second plastering layer and the engraving and painting on the surface of the second plastering layer formed by the above steps.

또한, 상기 1차 미장단계에서는 초속경 시멘트와, 포틀랜트 시멘트, 방수액, 시맨트 증점제, 강화수지섬유 및 색상안료를 혼합한 뒤 물과 반죽하여 금속망에 도포하며, 2차 미장단계에서는 초속경 시멘트와, 포틀랜트 시멘트, 모르타르, 방수액, 시맨트 증점제, 강화수지섬유 및 색상안료를 혼합한 뒤 물과 반죽하여 제 1 미장층의 표면에 도포하는 것을 특징으로 한다.In the first plastering step, cemented carbide, portland cement, waterproofing solution, cement thickener, reinforced resin fiber, and color pigments are mixed and kneaded with water and applied to the metal net. It is characterized in that the cement is mixed with water, portland cement, mortar, waterproofing solution, semantic thickener, reinforcing resin fiber and color pigment, and then kneaded with water and applied to the surface of the first plastering layer.

본 발명에 따른 시멘트를 이용한 인공 조각품의 제작방법에 따른면, 제 1, 2 시멘트 혼합물을 사용하여 적어도 2번 이상의 미장작업을 함으로써, 장시간 경과 후에 인공 조각품에 발생되는 균열이나 벗겨짐 현상을 최소화하여 인공 조각품의 형태를 그대로 유지시킬 수 있을 뿐만 아니라 자연적 이미지를 그대로 유지시킬 수 있는 효과가 있다.According to the manufacturing method of the artificial sculpture using the cement according to the present invention, by performing at least two or more plastering operations using the first and second cement mixture, by minimizing the crack or peeling phenomenon generated in the artificial sculpture after a long time In addition to maintaining the shape of the sculpture as well as the effect that can maintain the natural image.

또한, 인공 조각품의 내부에 설치되는 지지재의 부식을 최소화하여, 구조적으로 안정적인 인공 조각품을 제공함으로써 사후관리가 편한 효과가 있다.In addition, by minimizing the corrosion of the support material installed inside the artificial sculpture, by providing a structurally stable artificial sculpture has a post-management effect is easy.

이하에서는, 본 발명의 따른 시멘트를 이용한 인공 조각품 제작방법의 바람직한 실시예가 상세하게 설명될 것이다. 실시예를 설명됨에 있어, 관련된 공지기능 혹은 구성에 대한 구체적인 설명은 발명의 요지를 모호하지 않게 하기 위하여 생략된다.Hereinafter, a preferred embodiment of the artificial sculpture manufacturing method using the cement according to the present invention will be described in detail. In describing the embodiments, detailed descriptions of related well-known functions or configurations are omitted in order not to obscure the subject matter of the invention.

이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시 예를 상세히 설명한 다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 1은 본 발명에 따른 시멘트를 이용한 인공 조각품의 제작방법을 도시한 공정도이고, 도 2는 도 1의 과정을 통해 인공 바위를 제작하는 방법을 도시한 단면도이며, 도 3은 도 2의 과정을 거쳐 완성된 인공 바위의 사시도이다.1 is a process chart showing a method of manufacturing an artificial sculpture using cement according to the present invention, Figure 2 is a cross-sectional view showing a method of manufacturing an artificial rock through the process of Figure 1, Figure 3 is a process of FIG. It is a perspective view of an artificial rock completed through.

도 1 및 도 2에 도시된 바와 같이, 시멘트를 이용한 인공 조각품의 제작방법은, 금속프레임(10)으로 골격을 형성하는 단계(S10)와, 상기 단계(S10)에 의해 형성된 골격에 금속망(20)을 설치하는 단계(S20)와, 상기 단계(S20)에 의해 형성된 금속망(20)에 1차 미장을 하여 제 1 미장층(22)을 형성하는 단계(S30)와, 상기 단계(S30)에 의해 형성된 제 1 미장층(22)의 표면에 스크래치 작업 및 수지성 본드를 도포하는 단계와(S40), 상기 단계(S40)에 의해 스크래치 작업을 마친 제 1 미장층(22)의 표면에 2차 미장을 하여 제 2 미장층(24)을 형성하는 단계(S50)와, 상기 제 2 미장층(24)의 표면에 조각 및 페이팅 작업을 하는 단계(S60)로 이루어진다.As shown in Figure 1 and 2, the manufacturing method of artificial sculpture using cement, the step of forming a skeleton with a metal frame (10) (S10), and the metal mesh (S) in the skeleton formed by the step (S10) 20 to install (S20), and the first plastering to form a first plastering layer 22 to the metal mesh 20 formed by the step (S20) (S30), and the step (S30) And applying a scratch operation and a resinous bond to the surface of the first plastering layer 22 formed by (S40) and the surface of the first plastering layer 22 which has been scratched by the step (S40). The second plastering step is performed to form a second plastering layer 24 (S50), and the step of performing the engraving and painting work on the surface of the second plastering layer (24).

상기 골격형성단계(S10)는 금속프레임(10)으로 제작하려는 인공 조각품의 기초가 되는 골격을 형성하는 단계이다.The skeleton forming step (S10) is a step of forming a skeleton that is the basis of the artificial sculpture to be produced by the metal frame (10).

상기 금속망을 설치하는 단계(S20)는 상기 골격형성단계(S10)에 의해 제작된 금속프레임(10)에 금속망(20)을 설치하여, 제작하고자 하는 인공 조각품의 외형을 형성하고 후술할 미장작업을 용이토록 해주는 준비단계이다.The step of installing the metal net (S20) is to install the metal net 20 in the metal frame 10 produced by the skeleton forming step (S10), to form the appearance of the artificial sculpture to be produced and the plasterer to be described later This is a preparatory step to make the work easier.

상기 금속망(10)은 일반적으로 우리가 미장작업을 할 때 사용하는 메탈라스(metal lath)나 와이어 메쉬(wire mesh)로서, 미장작업을 할 때 밑바탕이 되는 금속으로 된 망이다.The metal mesh 10 is generally a metal lath or a wire mesh that we use when performing plastering, and is a metal mesh that is used as a foundation for plastering.

또한, 인공 조각품의 두께를 두껍게 할 경우에는 상기 금속망(20)을 2겹으로 설치하는 것이 바람직하다.In addition, in the case of increasing the thickness of the artificial sculpture, it is preferable to install the metal mesh 20 in two layers.

상기 1차 미장단계(S30)는 상기 금속망(20)에 의해 형성된 미장면(21)에, 제 1 혼합 시멘트에 물을 혼합하여 1~2㎝의 두께로 제 1 미장층(22)을 형성시키는 단계이다.In the first plastering step (S30), the first plastering layer 22 is formed to a thickness of 1 to 2 cm by mixing water in the first mixed cement on the plastering surface 21 formed by the metal mesh 20. This is the step.

상기 제 1 혼합 시멘트는, 초속경 시멘트 40kg 1포대를 기준으로 하여, 포틀랜드 시멘트 15~22kg과, 방수액 0.3~0.5ℓ, 시멘트 증점제 0.2~0.3ℓ, 강화수지섬유 300~500g 및 색상안료를 혼합하여 이루어진 것이다.The first mixed cement, based on one bag of super fast cement 40kg, 15-22kg Portland cement, 0.3-0.5L waterproofing liquid, 0.2-0.3L cement thickener, 300-500g reinforced resin fiber and color pigments It is done.

상기 1차 미장단계(S30)는, 분무장치를 이용하여 금속망(20)에 고르게 도포하는 방법이 사용될 수도 있다. 즉, 분무 작업을 하면 보다 세밀하고 균일하게 제 1 혼합 시멘트를 금속망(20)에 도포할 수 있다.In the first plastering step (S30), a method of evenly applying to the metal mesh 20 using a spray device may be used. That is, by spraying, the first mixed cement can be applied to the metal mesh 20 more precisely and uniformly.

또한, 상기 제 1 혼합 시멘트는 방수 및 부식방지 수지가 첨가되기 때문에 상기 금속프레임(10)과 금속망(20)에 물이 스며들지 않아 부식을 방지하는 효과를 가진다. 또한, 제 1 미장층(22)의 균열을 최소화하기 위해 강화수지섬유가 첨가되어 강도가 증대되는 장점이 있다.In addition, the first mixed cement has an effect of preventing corrosion due to water does not penetrate the metal frame 10 and the metal mesh 20 because the waterproof and anti-corrosion resin is added. In addition, reinforcing resin fibers are added to minimize cracking of the first plastering layer 22, which has the advantage of increasing strength.

상기 스크래치 단계(S40)는 상기 1차 미장단계(S30)에 의해 형성된 제 1 미장층(22)의 표면에 얇게 홈(23)을 파내는 단계이다. 이는 2차 미장단계(S50)를 위한 준비단계이다.The scratch step (S40) is a step of digging a thin groove 23 on the surface of the first plastering layer 22 formed by the first plastering step (S30). This is a preparation step for the second plastering step (S50).

상기 제 1 미장층(22)에 홈(23)을 파는 이유는, 2차 미장작업시에 사용되는 제 2 혼합 시멘트가 제 1 미장층(22)에 형성된 홈(23)에 스며들어 굳어짐으로써, 제 1 미장층(22)과 견고히 점착되도록 하기 위해서이다. 그리고, 2차 미장작업시에 사용되는 제 2 혼합 시멘트가 견고히 점착될 수 있도록 상기 홈(23)을 파낸 후에 수지성 본드를 제 1 미장층(22)의 표면에 도포하는 것이 바람직하다.The reason for digging the grooves 23 into the first plastering layer 22 is that the second mixed cement used in the second plastering operation penetrates and hardens into the grooves 23 formed in the first plastering layer 22, This is to adhere firmly to the first plastering layer 22. Then, it is preferable to apply the resinous bond to the surface of the first plastering layer 22 after digging the groove 23 so that the second mixed cement used in the second plastering operation can be firmly adhered.

상기 스크래치 단계(S40)는 상기 제 1차 미장단계(S30)가 완료된 후, 온도 15도를 기준으로 약 4시간 후에 실시하는 것이 바람직하다.The scratch step (S40) is preferably carried out after about 4 hours on the basis of the temperature 15 degrees after the first plastering step (S30) is completed.

상기 2차 미장단계(S50)는 상기 1차 미장단계(S30)에 의해 형성된 제 1 미장층(22)의 표면에 제 2 혼합 시멘트를 미장작업하여 제 2 미장층(24)을 형성시키는 단계이다.The second plastering step (S50) is a step of forming a second plastering layer 24 by plastering the second mixed cement on the surface of the first plastering layer 22 formed by the first plastering step (S30). .

상기 제 2 혼합 시멘트는, 초속경 시멘트 40kg 1포대를 기준으로 하여, 포틀랜드 시멘트 25~30kg, 모르타르 15~20kg, 방수액 0.5~1ℓ, 시멘트 증점제 0.3~0.5ℓ, 강화수지섬유 100~200g 및 색상안료를 혼합하여 이루어진 것이다.The second mixed cement is based on one bag of super fast cement 40kg, Portland cement 25-30kg, mortar 15-20kg, waterproofing 0.5-1l, cement thickener 0.3-0.5l, reinforced resin fiber 100-200g and color pigment It is made by mixing.

상기 색상안료는 제 2 미장층(24)의 표면이 색상을 띄도록 하기 위해 첨가되는 것이며, 제작하려는 인공 조각품의 베이스 색상에 맞추어 사용하면 된다.The color pigment is added to make the surface of the second plastering layer 24 to have a color, and may be used according to the base color of the artificial sculpture to be manufactured.

또한, 상기 제 2 혼합 시멘트는 색상안료를 혼합하였기 때문에 제 2 미장층(24)의 표면이 풍화작용이나 외부의 충격에 의해 벗겨지더라도, 상기 1차 미장단계(S30)에 사용되어진 제 1 혼합 시멘트에도 색상안료가 첨가되었기 때문에 오히려 자연스럽게 인공 조각품의 베이스 색상이 그대로 표현된다.In addition, since the second mixed cement is a color pigment mixed, even if the surface of the second plastering layer 24 is peeled off due to weathering or external impact, the first mixing used in the first plastering step (S30). Since color pigments are added to cement, the base color of artificial sculpture is naturally expressed.

2차 미장단계(S50)에 의한 미장 작업은, 상기 제 1 미장층(22)이 굳어지는 시점에 실시되는 것이 바람직하다. 제 1 미장층(22)이 충분히 굳어지지 않은 채로 미장작업을 실시하면 상기 제 1 미장층(22)에 잘 달라붙지 않을뿐더러 강도도 약해진다.Plastering work by the second plastering step (S50) is preferably carried out when the first plastering layer 22 is solidified. Plastering work without sufficiently hardening the first plastering layer 22 does not easily adhere to the first plastering layer 22, and the strength is also weakened.

참고로, 도 4에서는 상기 1,2 미장단계(S30, S50)에 의해 형성된 미장층(22, 24)이 조각 및 미장을 위해 양생되는 시간이 그래프로 도시되어 있다.For reference, in FIG. 4, the time when the plastering layers 22 and 24 formed by the first and second plastering steps S30 and S50 are cured for engraving and plastering is shown in a graph.

도 4에 그래프로 도시된 바와 같이, 상기 미장층(22, 24)이 양생되는 시간은 환경적 요소에 의해 편차가 생기는 것을 알 수 있으며, 미장되는 두께에 따라 양생되는 시간이 편차가 나는 것을 알 수 있다.As shown in the graph in FIG. 4, it can be seen that the time for curing the plastering layers 22 and 24 varies due to environmental factors, and that the curing time varies depending on the thickness of the plastering. Can be.

상기 조각 및 페인팅 단계(S60)는 상기 2차 미장단계(S50)에 의해 형성된 제 2 미장층(24)이 완전히 굳어진 후, 상기 제 2 미장층(24)의 표면에 여러 가지 조각 기법을 이용하여 인공 조각품의 이미지를 구현하고, 도료나 염료를 통한 페인팅 작업을 하면 인공 조각품이 완성이 된다.In the engraving and painting step S60, after the second plastering layer 24 formed by the second plastering step S50 is completely hardened, various engraving techniques are used on the surface of the second plastering layer 24. If you create an image of an artificial sculpture and paint with paint or dye, the artificial sculpture is completed.

이하, 본 발명에 따른 시멘트를 이용한 인공 바위의 제작방법을 상세히 설명한다.Hereinafter, a method of manufacturing artificial rock using cement according to the present invention will be described in detail.

먼저, 인공 바위를 지탱할 수 있도록 금속프레임(10)으로 기본 골격을 형성한다. 상기 금속프레임(10)은 제작하려는 인공 바위의 기본 뼈대가 되는 부분으로서 인공 바위의 하중을 지탱하는 역할을 한다.First, to form a basic skeleton with a metal frame 10 to support the artificial rock. The metal frame 10 serves as a basic skeleton of the artificial rock to be manufactured to support the load of the artificial rock.

그리고 나서 금속망(20)을 상기 금속프레임에 설치한다. 상기 금속망(20)은 흔히 우리가 건축공사에서 미장작업시에 바르는 모르타르가 떨어지지 않도록 하기 위해 밑바탕에 설치되는 금속제 망이다.Then, the metal mesh 20 is installed in the metal frame. The metal mesh 20 is often a metal mesh installed in the base to prevent the mortar that we apply during the plastering work in the building construction to fall.

상기 금속망(20)은 미장작업 후에 인장력을 보완해주기 때문에 균열이 발생 되지 않도록 해주며, 미장을 두껍게 할 시에는 2겹으로 설치하는 것이 바람직하다.The metal mesh 20 prevents cracking because it supplements the tensile force after the plastering operation, and when thickening the plastering, it is preferable to install two layers.

상기 금속망(20) 설치 후에는 1차 미장작업을 실시한다.After the metal mesh 20 is installed, the first plastering operation is performed.

1차 미장작업은 초속경 시멘트 40kg 1포를 기준으로 포틀랜드 시멘트 20kg과, 방수액 0.5ℓ, 시멘트 증점제 0.3ℓ, 강화수지섬유 400g 및 색상안료를 함께 혼합한, 제 1 혼합 시멘트를 물 4ℓ와 함께 반죽하는 것이 바람직하며, 제 1 혼합 시멘트를 상기 금속망(20)에 도포하여 제 1 미장층(22)을 형성시키며, 두께는 1~2㎝로 형성시키는 것이 바람직하다.The first plastering work is to knead the first mixed cement with 4 liters of water, 20 kg of Portland cement, 0.5 liters of cement, 0.3 liters of cement thickener, 400 grams of reinforced resin fiber, and color pigments, based on 40 kg of superhard cement. Preferably, the first mixed cement is applied to the metal mesh 20 to form the first plastering layer 22, and the thickness is preferably 1 to 2 cm.

또한, 상기 미장작업은, 분무장치를 이용한 분무 작업으로 제 1 혼합 시멘트를 금속망(20)에 도포할 수도 있다.In addition, in the above-mentioned plastering operation, the first mixed cement may be applied to the metal mesh 20 by a spraying operation using a spraying apparatus.

상기 1차 미장작업이 완료되면 평균온도 15도를 기준으로 4시간 후에 스크래치작업을 실시한다. 상기 스크래치 작업은 제 1 미장층(22)의 표면에 홈(23)을 내는 작업이다.When the first plastering operation is completed, the scratch operation is performed after 4 hours on the basis of the average temperature of 15 degrees. The scratching operation is to cut out the grooves 23 on the surface of the first plastering layer 22.

상기 제 1 미장층(22)의 표면에 홈(23)을 가공하여 2차 미장작업을 실시하였을 때, 상기 홈에 제 2 혼합 시멘트가 스며들어 제 1 미장층(22)과 결속을 견고히 하기 위함이다. 또한, 제 2 혼합 시멘트와의 점착능력을 증가시키기 위해, 상기 홈(23)을 가공한 뒤 수지성 본드를 제 1 미장층(22)의 표면에 도포하는 것이 바람직하다.When the second plastering process is performed by processing the grooves 23 on the surface of the first plastering layer 22, the second mixed cement penetrates the grooves so as to firmly bond with the first plastering layer 22. to be. In addition, in order to increase adhesion with the second mixed cement, it is preferable to apply the resinous bond to the surface of the first plastering layer 22 after the groove 23 is processed.

2차 미장작업은 제 1 미장층(22)이 충분히 양생되는 시점에서 실시하는 것이 바람직하다.The secondary plastering work is preferably performed at the time when the first plastering layer 22 is sufficiently cured.

상기 1차 미장층(22)이 충분히 양생되지 않은 시점에서 2차 미장작업을 실시 하면 1차 미장층(22)의 점착능력과 강도가 떨어지는 문제가 발생 될 수 있기 때문이다.This is because when the second plastering operation is performed at a time when the primary plastering layer 22 is not sufficiently cured, a problem of deterioration of adhesive strength and strength of the primary plastering layer 22 may occur.

양생시간은 미장층의 두께와 주위 온도에 따라 차이가 있으며, 참고로 도 4에 최적양생시간이 그래프로 도시되어 있다.Curing time is different depending on the thickness of the plaster layer and the ambient temperature, the optimum curing time is shown in Figure 4 as a reference.

상기 2차 미장작업은 초속경 시멘트 40kg 1포대를 기준으로 모르타르 15kg과, 포틀랜드 시멘트 25kg, 방수액 0.5ℓ, 시멘트 증점제 0.3ℓ, 강화수지섬유 150g 및 색상염료를 함께 혼합한 제 2 혼합 시멘트를, 물 4ℓ와 함께 반죽하는 것이 바람직하며, 상기 제 1 미장층(22)의 표면에 도포되어 제 2 미장층(24)을 형성시킨다.The second plastering work is based on a bag of cement 40kg cement 15kg mortar 15kg, Portland cement 25kg, waterproofing 0.5l, cement thickener 0.3l, reinforced resin fiber 150g and the color mixture of the second mixed cement, water It is preferable to knead together with 4 L, and is applied to the surface of the first plastering layer 22 to form a second plastering layer 24.

참고로 제 1, 2 혼합 시멘트에 첨가되는 색상안료는, 인공 조각물이 연출하고자 하는 대상물에 따라 색상과 용량을 달리하여 제 1, 2 혼합 시멘트에 첨가되는 것이 바람직하다.For reference, the color pigment added to the first and second mixed cement is preferably added to the first and second mixed cement by varying the color and capacity according to the object to be produced by the artificial sculpture.

또한, 상기 2차 미장작업은 1차 미장작업과 마찬가지로 분무 장치를 이용한 뿜칠 작업으로 제 2 혼합 시멘트를 제 1 미장층(22)에 도포하여 제 2 미장층(24)을 형성시킬 수 있다.In addition, in the second plastering operation, as in the first plastering operation, the second mixing cement may be applied to the first plastering layer 22 by the spraying operation using the spraying device to form the second plastering layer 24.

상기 제 1 혼합 시멘트와 제 2 혼합 시멘트에는 인공 바위의 베이스 색상이 되는 색상안료가 혼합되었기 때문에, 상기 제 2 미장층(24)의 표면이 벗겨지거나 백화현상이 일어나도 오히려 자연스러운 분위기를 연출한다.Since the color pigment which is the base color of the artificial rock is mixed with the first mixed cement and the second mixed cement, even if the surface of the second plastering layer 24 is peeled off or whitening occurs, a natural atmosphere is produced.

또한, 상기 제 1, 2 혼합 시멘트에는 금속프레임(10)과 금속망(20)에 발생하는 부식을 방지하기 위해 방수액이 첨가되며, 제 1, 2 미장층(22, 24)의 강도를 강 화하기 위해 유리섬유가 첨가된다. 따라서, 제, 1, 2 미장층(22, 24)에 균열이 발생하는 것을 막아준다.In addition, a waterproofing liquid is added to the first and second mixed cements in order to prevent corrosion occurring in the metal frame 10 and the metal mesh 20, and the strength of the first and second plastering layers 22 and 24 is enhanced. Fiberglass is added to this. Therefore, cracks are prevented from occurring in the first and second plastering layers 22 and 24.

마지막으로 2차 미장작업에 의해 형성된 제 2 미장층(24)이 충분히 양생되면, 그 표면에 다양한 기법으로 조각을 하고 도료나 염료를 통한 페인팅 작업을 함으로써 인공 바위의 제작이 완료된다.Finally, when the second plastering layer 24 formed by the second plastering process is sufficiently cured, the artificial rock is completed by carving the surface by various techniques and painting with paint or dye.

본 발명의 실시예 에서는, 인공 바위를 제작하는 것을 예시하여 설명하였지만 이에 한정되지 않고, 인공폭포나 인공나무 등 다양한 인공 조각품에 적용가능함은 물론이다. 또한, 본 발명에서는 인공 조각품을 다수의 패널로 제작하여 연결하지 않고, 적어도 2번 이상의 미장작업을 실시하므로 미장층에 발생되는 균열을 최소화하는 장점이 있다. In the embodiment of the present invention, the manufacturing of the artificial rock has been described by way of example, but is not limited thereto. Of course, it is applicable to various artificial sculptures such as artificial waterfalls and artificial trees. In addition, the present invention has the advantage of minimizing the cracks generated in the plastering layer because at least two or more plastering operations are performed without connecting the artificial sculpture made of a plurality of panels.

이상에서 설명한 본 발명은 진술한 실시예 및 첨부된 도면에 의해 한정되는 것이 아니고, 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 여러 가지 치환, 변형 및 변경이 가능함은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에게 있어서 명백할 것이다.The present invention described above is not limited to the stated embodiments and the accompanying drawings, and various substitutions, modifications, and changes can be made without departing from the technical spirit of the present invention. It will be evident to those who have knowledge of.

도 1은 시멘트를 이용한 인공 조각품 제작하는 공정을 나타낸 공정도.1 is a process chart showing a process of manufacturing artificial sculpture using cement.

도 2는 도 1의 과정을 통해 인공 바위를 제작하는 모습을 보인 단면도.2 is a cross-sectional view showing a state of manufacturing artificial rock through the process of FIG.

도 3은 도 2의 과정을 통해 제작된 인공 바위의 정면도.3 is a front view of the artificial rock produced through the process of FIG.

도 4는 미장층의 최적 양생시간을 그래프로 도시한 참고도.Figure 4 is a reference diagram graphically showing the optimal curing time of the plaster layer.

Claims (5)

인공 조각품 제작방법에 있어서,In the artificial sculpture production method, 금속프레임(10)으로 골격을 제작하는 단계(S10);Manufacturing a skeleton with a metal frame 10 (S10); 상기 단계(S10)에 의해 제작된 금속프레임(10) 골격에 금속망(20)을 설치하는 단계(S20);Installing a metal mesh 20 in the skeleton of the metal frame 10 produced by the step S10 (S20); 상기 단계(S20)에 의해 설치된 금속망(20)에 초속경 시멘트와, 포틀랜트 시멘트, 방수액, 시멘트 증점제, 강화수지섬유 및 색상안료를 혼합한 뒤 물로 반죽한 반죽물을 1차 미장작업을 하여 제 1 미장층(22)을 형성하는 단계(S30);After mixing the cemented carbide cement, Portland cement, waterproofing liquid, cement thickener, reinforced resin fiber and color pigments in the metal mesh 20 installed by the step (S20), the dough kneaded with water is firstly plastered. Forming a first plastering layer 22 (S30); 상기 단계(S30)에 의해 형성된 제 1 미장층(22)의 표면에 스크래치 작업과, 수지성 본드를 도포하는 단계(S40);Scratching the surface of the first plastering layer (22) formed by the step (S30) and applying a resinous bond (S40); 상기 단계(S40)에 의해 스크래치 작업을 마친 제 1 미장층(22)의 표면에 초속경 시멘트와, 포틀랜트 시멘트, 모르타르, 방수액, 시멘트 증점제, 강화수지섬유 및 색상안료를 혼합한 뒤 물과 반죽한 반죽물을 2차 미장작업을 하여 제 2 미장층(24)을 형성하는 단계(S50); 및After mixing the superhard cement, portland cement, mortar, waterproofing liquid, cement thickener, reinforcing resin fiber and color pigment on the surface of the first plastering layer 22 after the scratching step (S40), water and dough Forming a second plastering layer 24 by performing secondary plastering on one dough (S50); And 상기 단계(S50)에 의해 형성된 제 2 미장층(24)의 표면에 조각 및 페인팅하는 단계(S60)를 포함하여 이루어진 것을 특징으로 하는 시멘트를 이용한 인공 조각품의 제작방법.Method of producing an artificial sculpture using cement, comprising the step (S60) of carving and painting on the surface of the second plastering layer (24) formed by the step (S50). 삭제delete 제1항에 있어서,The method of claim 1, 상기 1차 미장단계(S30)에서는 초속경 시멘트 40kg 1포대를 기준으로, 포틀랜드 시멘트15~22kg과, 방수액 0.3~0.5ℓ, 시멘트 증점제 0.2~0.3ℓ, 강화수지섬유 300~500g 및 색상안료를 혼합한 뒤 물 3~4ℓ와 반죽하여 금속망(20)에 도포하고, 상기 2 차 미장단계(S40)에서는 초속경 시멘트 40kg 1포대를 기준으로, 포틀랜드 시멘트 25~30kg과, 모르타르 15~20kg, 방수액 0.5~1ℓ, 시멘트 증점제 0.3~0.5ℓ, 강화수지섬유 100~200g 및 색상안료를 혼합한 뒤 물 3~4ℓ와 반죽하여 제 1 미장층(22)의 표면에 도포하는 것을 특징으로 하는 시멘트를 이용한 인공 조각품의 제작방법.In the first plastering step (S30), based on one bag of cement fast cement 40kg, 15 ~ 22kg of Portland cement, 0.3 ~ 0.5ℓ of waterproofing solution, 0.2 ~ 0.3ℓ of cement thickener, 300 ~ 500g of reinforced resin fiber and color pigments And then kneaded with 3 ~ 4ℓ of water and applied to the metal net 20, in the second plastering step (S40), based on 1 kg of cement fast cement 40kg, Portland cement 25 ~ 30kg, mortar 15 ~ 20kg, waterproofing solution 0.5 ~ 1ℓ, cement thickener 0.3 ~ 0.5ℓ, reinforcing resin fiber 100 ~ 200g and color pigment, mix with 3 ~ 4L of water and apply to surface of first plastering layer 22 How to make an artificial sculpture. 삭제delete 삭제delete
KR1020080024767A 2008-03-18 2008-03-18 Manufacturing method of artificial carving work using cement KR100860270B1 (en)