KR100756016B1 - An inflatable fabrics - Google Patents

An inflatable fabrics Download PDF

Info

Publication number
KR100756016B1
KR100756016B1 KR20060027870A KR20060027870A KR100756016B1 KR 100756016 B1 KR100756016 B1 KR 100756016B1 KR 20060027870 A KR20060027870 A KR 20060027870A KR 20060027870 A KR20060027870 A KR 20060027870A KR 100756016 B1 KR100756016 B1 KR 100756016B1
Authority
KR
Grant status
Grant
Patent type
Prior art keywords
fabric
air
tissue
part
air permeability
Prior art date
Application number
KR20060027870A
Other languages
Korean (ko)
Inventor
곽동진
윤정훈
이상목
정재홍
Original Assignee
주식회사 코오롱
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Grant date

Abstract

A double fabric is provided to suppress the generation of creases, by swelling air remaining between two fabric layers through heat in a high-temperature hardening process, after coating a rear surface of the double fabric so as to swell the double fabric. A fabric comprises an expansion portion(10) including two fabric layers separated from each other and simultaneously woven by using a weaving machine, and a connection portion(30) for partially connecting two fabric layers to seal and define the expansion portion. The fabric further comprises a normal structure and an abnormal structure. The normal structure is different from the abnormal structure in a difference of air permeability, wherein the difference of air permeability is equal to or more than 1 ft^3/min.

Description

기체에 의해 부품성을 갖는 이중직물{AN INFLATABLE FABRICS} Dual having sex parts by gas Fabrics {AN INFLATABLE FABRICS}

도 1은 본 발명의 공기투과도 차이를 보이는 부분을 포함하는 공기부품성 직물의 제직 구조도로서, 비정상 조직이 형성된 일면을 나타낸 평면도. 1 is a structural view of an air weaving parts St. fabric including a portion showing the difference in air permeability of the present invention, the plan view of the one side is an abnormal tissue formed.

도 2는 발명의 공기투과도 차이를 보이는 부분을 포함하는 공기부품성 직물의 제직 구조도로서 조직이 형성된 다른 일면의 평면도. Figure 2 is a plan view of another embodiment the tissue formed as a woven structure diagram of an air part St. fabric including a portion showing the air permeability difference invention.

도 3은 본 발명의 공기투과도 차이를 보이는 조직 또는 비정상 조직이 삽입된 부품성을 가지는 직물의 횡단면도. Figure 3 is a cross-sectional view of a fabric having a property component tissue or abnormal tissue showing the difference in air permeability of the present invention is inserted.

<도면의 주요부분에 대한 부호의 설명> <Description of the Related Art>

10 : 부품성이 있는 이중직물 10: Double fabric parts castle

20 : 공기투과도 차이를 보이는 조직 또는 비정상 조직 20: The organization looks for air permeability differences or abnormal tissue

30 : 부분적인 접결부 30: partial contact associated

32 : 부분적인 접결부의 횡단면 32: cross section of a partial contact with bound

12 : 부품성이 있는 이중직물의 횡단면 12: Cross section of double fabric parts castle

22 : 공기투과도 차이를 보이는 조직 또는 비정상 조직 22: The organization looks for air permeability differences or abnormal tissue

40 : 공기투과도가 높은 층의 횡단면 40: Cross section of the high air permeability layer

50 : 공기투과도가 낮은 층의 횡단면 50: Cross section of the low air permeability layer

[기술분야] [Technology]

본 발명은 기체에 의한 부품성을 갖는 직물에 관한 것으로, 보다 상세하게는 차량용 에어백 또는 구명조끼 등에 활용성이 우수한 공기 부품성을 갖는 직물에 관한 것이다. The present invention relates to a fabric having a property component of the gas, more particularly to a fabric having excellent air utilization part sex like airbag or a life jacket.

[종래기술] [Prior art]

부품성이 있는 직물은 차량용 에어백, 구명용 조끼 등의 용도로 사용 할 수 있다. Fabrics with a part sex can be used in applications such as automotive air bags, jackets for nine people. 특히, 자동차가 전복하여 구를 경우 운전자나 승객의 머리 부분이 자동차의 유리창이나 측면 구조물에 의하여 다치는 것을 방지할 목적으로 사고시 자동차의 측면 유리창 부위에서 커튼형의 에어백이 펼쳐지게 되는 사이드커튼 형태의 에어백에 부품성 직물을 사용하고 있다. In particular, the vehicle is in the overturned obtain when the driver or passenger of the head car of the window or in the air bag of the side curtain type that this air bag curtain unfold from the side window areas of the accident car for the purpose of preventing, by the side structures injured by and use the components castle fabrics. 상기 사이드커튼 형태의 에어백은 사고시 안전하게 승객을 보호하기 위해서 차가 구르는 동안 해당 에어백이 적어도 5초 이상은 부풀려 진 상태로 있어야 하며 이 경우 부품성이 있는 직물이 유용하다. The side curtain type of airbag safety accident over the air bag for the car to roll at least 5 seconds to protect the passenger is useful in this case, with a component property, and have a binary inflated condition the fabric.

차량용 에어백 등과 같이 공기 부품성을 갖는 제품을 제조하는 방법은 크게 두 개의 직물을 봉제, 융착 또는 접착하여 사용하는 방법과, 두 개층의 직물이 접결점에 의해 부분적으로 접결되어 있는 직물을 사용하는 방법으로 구분된다. Process for preparing a product having an air component Castle, such as vehicle airbags method for increasing use of two textile garment, the method for use by fusing or bonding and a fabric that has a two-layer fabric is partially stitched by the stitching defect It is divided into.

그러나, 첫 번째 방법과 같이 두개의 직물을 봉제하거나, 열 또는 초음파 처리로 융합하거나, 또는 접착제로 접착하여 공기 부품성 제품을 제조하는 방법은 두 개의 층을 구성하는 원단을 제조한 후 별도 봉제공정, 융착공정 또는 접착공정이 필요하여 공정이 복잡해지고 제조원가도 상승하게 되는 문제가 발생하였다. However, after manufacturing the two fabrics sewn to the fabric, or fusion with heat or ultrasonic treatment, or how to bond an adhesive agent for producing the air part sex product consists of two layers as shown in the first method, a separate sewing processes , to require a fusion process or a bonding process is a complicated process was a problem that increases go manufacturer.

이러한 문제점을 해결하기 위해, 최근에는 두 번째의 방법을 이용한 공기 부품성을 갖는 직물을 사용하여 에어백 등과 같은 공기 부품성 제품을 제조하는 방법이 시도되고 있다. To solve this problem, in recent years there has been attempted a method of manufacturing an air bag component products, such as sex, use a fabric having an air castle parts using the second method.

공기와 같은 기체에 의한 부품성이 있는 직물은 분리된 이중 직물과 이 이중 직물간의 접결부를 가지고 있다. Fabrics with a part sex by gas such as air, has an associated contact between the separated double fabric and the double fabric. 접결부에 의해 폐쇄된 계를 가지는 직물은 각 단일층이 공기 등에 급격히 팽창할 때 두 개의 층을 견고하게 결속시키는 역할을 하므로, 두 개의 층이 이어지는 부분의 기체의 유출현상이 없어야 한다. Fabric having a system closed by the associated contact when the respective single layer can rapidly swell in air, so serve to firmly bond the two layers, should be free from leakage of the developing section of the two layers are leading gas.

상기 공기 부품성을 갖는 직물의 제조방법으로서, 미국특허 제 6,701,971호, 미국특허 제 6,698,458호, 및 한국특허공개 제 2005-0095382호의 경우 두 개층의 직물이 접결점에 의해 부분적으로 접결되어 있는 이중직물을 제직하여 양면 코팅을 하는 방법을 사용하고 있다. A method for producing a fabric having the said air part Castle, U.S. Patent No. 6,701,971, U.S. Patent No. 6,698,458, and South Korea double fabric, which is partially stitched by the defect when the Patent Publication 2005-0095382 favor of the two-layer fabric in contact and the weaving method of using a double-sided coating. 그러나, 상기 방법들은 두 개의 층이 이어지는 부분의 기체의 유출현상을 막기 위하여 고중량으로 코팅하고 있어 코팅시 내부공기 팽창에 의해 부품성이 있는 직물부의 팽창으로 직물의 표면에 주름이 발생하는 문제점이 있다. However, these methods, there is a problem that a part sex is inflated fabric portion that by it, and coated with a heavy coating upon the internal air expanded wrinkles generated on the surface of the fabric to prevent leakage phenomenon of a portion of the two layers, leading gas . 즉 일반적으로, 양면코팅은 직물의 한면을 코팅한 후 뒷면을 코팅하게 되는데, 뒷면 코팅에 의해 부분 접결부에 공기가 몰리는 현상이 발생되어 그 부분은 직물이 팽창되어 주름이 발생된다. That is generally, there is two-sided coating is to coat the back side was coated to one surface of the fabric, a phenomenon in part by the back of the associated contact coating driven air is generated that part of wrinkles are caused by tissue expansion.

또한, 한국특허공개 제 2003-0050135호에서는 원단의 일면 또는 양면에 접착용 필름을 라이네이팅 한 후 원단을 봉제하여 공기 부품성을 갖는 이중직물의 제작하는 방법에 대해 개시하였고, 한국특허공개 제 2002-0059911호는 두 장의 원단을 봉제한 후 일면 또는 양면을 코팅하는 방법이 개시되어 있고, 한국특허공개 제 2002-0043729호는 원단의 일면 또는 양면에 코팅한 후 접착제를 사용하여 두 원단을 접착하는 방법에 대해 개시하고 있다. Also, Korea Patent Publication No. 2003-0050135 call in after rayineyiting the adhesive film on one side or both sides of the fabric by sewing the fabrics were described for the method for manufacturing the double fabric having an air component Province, Korea Patent Publication No. 2002- No. 0,059,911 is disclosed a method for coating one or both sides and then sewing the two pieces of fabric, Korea Patent Publication No. 2002-0043729 discloses a method for bonding the two fabrics and was coated on one side or both sides of the fabric using an adhesive in discloses. 그러나, 이러한 방법들은 두 개의 층을 구성하는 원단을 제조한 후 별도의 봉제공정, 융착공정 또는 접착공정이 필요하여 공정이 복잡해지고 제조원가도 상승하게 되는 문제가 발생한다. However, these methods are process is complicated by the need for a separate sewing process, fusion process or a bonding process after producing the fabric that make up the two layers there is a problem that increases go manufacturer. 또한, 제직시 부분적으로 접결되는 이중직물을 제직한 후 양면 코팅하여 제조하는 방법에 비해 두 개의 층이 이어지는 부분의 기체 유출현상이 크다는 단점이 있다. In addition, there is a disadvantage that the gas outlet of the developing part the two layers compared to a subsequent method for manufacturing the double-sided coating after weaving the duplex fabric which is stitched in part during weaving greater.

상기 종래 기술의 문제점을 해결하기 위하여, 본 발명의 목적은 부분적으로 접결되어 있는 직물부를 제직한 후 양면코팅작업에 의해 공기에 의해 부품성이 있는 직물을 제작할 때, 뒷면 코팅시 발생하는 공기부품성이 있는 이중직물의 팽창에 의한 이중직물의 표면 주름 발생을 해결할 수 있는 기체에 의해 부품성을 갖는 직물을 제공하기 위한 것이다. In order to solve the problems of the prior art, an object of the present invention after the woven fabric is partially stitched by parts when producing a fabric of the component property by air by a double-sided coating operation, the air that occurs during the back coating components Castle due to the expansion of the double fabric to provide a fabric having sex parts by gas which can solve the wrinkling of the surface of the double fabric.

상기 목적을 달성하기 위하여, 본 발명은 직기를 이용하여 동시에 직조되는 서로 분리된 2개의 직물층을 포함하는 팽창부, 및 상기 팽창부를 이루기 위해 밀폐되도록 상기 서로 분리된 2개의 직물의 주위를 단일직으로 부분적으로 접결한 접결부를 포함하는 공기부품성 직물로서, 상기 공기부품성 직물의 적어도 하나는 공기투과도 차이를 갖는 정상조직 및 비정상 조직을 포함하여 직조된 것인 기체에 의해 부품성을 갖는 직물에 관한 것이다. In order to achieve the above object, the present invention is expanded portion comprising two layers of fabric which are separated from each other is by using a weaving machine weaving at the same time, and the vertical one the periphery of the two fabrics with the separated so that the sealing in order to achieve part the expansion in part as a folded integral air components St. fabric, comprising a contact coupled, at least one of the air components St. fabric is the fabric having a component property by using in the woven to a gas comprising a normal tissue and abnormal tissue has an air permeability difference relate to.

이하에서 본 발명을 상세하게 설명한다. The present invention will be described in detail below.

본 발명은 직기를 이용하여 동시에 직조되는 서로 분리된 두 개의 직물층의 제직시 이중직물의 일부를 상층과 하층의 조직구조를 상이하게 함으로써, 두 층의 공기투과도의 차이가 발생하도록 하는 직물을 제작하는 특징이 있다. The invention produce a fabric using a loom to by a part of the weaving during the double fabric of the two fabric layers which are separated from each other are woven differently the organizational structure of the upper layer and the lower layer, the difference in air permeability of the two layers occurs at the same time It is characterized in that.

본 발명은 상기 두 층의 공기투과도 차이에 의해, 양면코팅 중 두 개의 직물층을 포함하는 직물부의 뒷면 코팅시, 부품성이 있는 직물을 부분접결 하는 부분에 팽창된 공기가 모이지 않고 두 층 중 공기투과도가 높은 층을 통해 팽창된 공기가 유출되게 함으로써, 코팅 작업시 발생되었던 직물의 표면 주름 문제를 해결할 수 있다. The invention air of the two layers without the expansion in part by an air transmission rate difference between the two layers, the portion stitched to that when the back of the coated fabric portion comprising two fabric layers of the double-sided coating, parts St. fabric air gather , it can solve the problem of the fabric surface wrinkles that were generated during the coating operation by causing the permeability of the air flows out through the high expansion layer.

이때, 공기투과도 차이를 발생시키는 부분은 부품성이 있는 직물의 내부에 포함시켜 직조할 경우 공기 부품성 직물의 성능에 영향을 미치게 되므로, 이러한 부분은 항상 공기 부품성 직물의 외부(또는 외각부)에 삽입하여 직조하는 것이 바람직하다. At this time, part of the so affect the performance of the air part St. fabric if the weave to include the interior of the fabric in the parts Castle, outside (or outer portions) of these portions is always air components St. fabric for generating an air permeability difference inserted into it is preferred to weaving. 즉, 공기부품성 직물의 최종 양면 코팅 후 부분적으로 접결되어 있는 부분의 외곽은 재단에 의해 제품의 형상을 만들어 내기 때문에, 상기 공기투과도 차이를 보이는 부분은 제품 형상 재단시 재단되어 버려져 최종 제품에는 포함되지 않으므로, 공기투과도 차이를 발생시키는 부분은 외각부에 포함시켜 제직하여야 한다. That is, the air component castle outside of the portion that is partially stitched after the final coating on both sides of the fabric, because to create the shape of the product to cut, the visible portion of the air permeability difference is cut when the product shape is cut discarded included in the end product not part for generating an air permeability differences are to be woven to include the outer shell portion.

이하, 첨부된 도면을 참조하여 본 발명의 기체에 의해 부품성을 갖는 직물에 대하여 보다 상세히 설명한다. Will be described in detail with respect to the fabric having a part by a gas property the following, the present invention will be described with reference to the accompanying drawings. 도 1은 본 발명의 일실시예에 따른 공기투과도 차이를 보이는 부분을 포함하는 공기부품성 직물의 제직 구조도로서, 비정상 조직이 형성된 일면을 나타낸 평면도이다. 1 is a structural view of an air weaving parts St. fabric including a portion showing the difference in air permeability in accordance with one embodiment of the present invention, a plan view of the one side is an abnormal tissue formed. 도 2는 본 발명의 공기투과도 차이를 보이는 부분을 포함하는 공기부품성 직물의 제직 구조도로서, 조직이 형성된 다른 일면의 평면도이다. 2 is a plan view of the other side as the weaving structure diagram of an air part St. fabric, having a tissue including a portion showing a difference between air permeability of this invention. 도 3은 본 발명의 공기투과도 차이를 보이는 부분을 포함하는 부품성을 갖는 직물의 직물의 횡단면도를 나타낸 것이다. Figure 3 illustrates a cross-sectional view of a fabric having a property component comprising part showing the difference between air permeability of this invention.

도 1 및 2에서, 도면 부호 10은 서로 분리된 2개의 직물층을 포함하여 직조되어 팽창부를 이루기 위한 공기부품성을 가지는 직물 부분이다. In Figures 1 and 2, reference numeral 10 is a weave including two fabric layers which are separated from each other is a tissue section having an air component property to achieve the expansion portion. 도면 부호 20은 공기투과도 차이를 보이는 정상조직 및 비정상조직을 포함하여 직조되어 코팅시 공기를 배출시키는 공기 배출(vent) 부분이다. Reference numeral 20 is an air vent (vent) portion which is woven, including normal tissue and abnormal tissue showing the air permeability difference between the discharge air during coating. 도면 부호 30은 공기부품성 이중직물 내의 공기 유출을 막아주는 상기 서로 분리된 2개의 직물층이 부분적으로 접결되어 직조된 접결부분이다. Reference numeral 30 is a woven stitched part where the two fabric layers which are separated from each other for preventing the air in the air outlet part sex double fabric are partially stitched by. 이때, 본 발명에서 '팽창부'라 함은 이중직 사이로 공기가 들어가 부풀어지는 부분을 말한다. At this time, as the 'expansion part "in the present invention means the part that contains the air bulging between yijungjik. 또한, '접결부'는 상기 팽창부를 이루기 위하여 밀폐되도록 이중직(서로 분리된 2개의 직물층을 포함하는 팽창부) 주위를 단일직으로 결합한 부분을 말한다. In addition, the "contact associated" refers to a part that combines the periphery (expansion portion comprising two layers of fabric which are separated from each other) so that yijungjik closed to effect the inflatable portion of a single tissue. 또한, 본 발명에서 '정상 조직'이라 함은 경사 및 위사가 서로 교차하여 조직을 형성하는 것을 말하며, '비정상 조직'이라 함은 경사 및 위사가 서로 교차 없이 직조되어 이들이 서로 얽히지 않아 전혀 조직을 이루지 않는 것을 말한다. Further, the term "normal tissue" in the present invention, warps and wefts are means to form the tissue to cross each other, the term "abnormal tissue" is a tissue at all the warps and wefts do not seaweed they are entangled with each other are woven without crossing each other It means unbalanced. 또한, 본 발명에서 비정상 조직이란 경사 및 위사를 이용하여 직조되어 엉성한 조직으로 이루어진 것을 의미한다. Further, the weaving using warps and wefts is the abnormal tissue in the present invention means consisting of a loose tissue. 상기 비정상 조직의 일실시예를 들면 경사 및 위사를 이용하여 서로 교차되지 않도록 직조되어 엉성한 형태를 가지는 것을 포함한다. Is woven so that, for one embodiment of the abnormal tissue is not cross each other by using the warp and weft involves having a loose form.

이때, 최종 제품 제조시는 공기부품성 직물에서 접결된 외곽 부분을 따라 재 단하여 상기 공기투과도 차이를 보이는 부분을 제외하고 최종 제품을 제작하지만, 부품성이 있는 직물을 제직할 때는 부품성을 주기 위하여 기체를 삽입하는 삽입구 부분이 존재하여야 한다. In this case, the manufacture end products give Part castle when the end member along the outer portions stitched in the air part St. fabric except for a portion shown the air permeability difference and making a final product, but the woven fabric with a part castle In order to be present in the insertion hole portion for inserting the gas. 따라서, 공기 부품성 직물 부분의 일부를 재단하여 최종 제품의 단계에서 재단된 일부 부분이 기체 삽입을 위하여 열려 있도록 제작하여야 한다. Therefore, some parts cut by cutting some parts of the air St. fabric portion at the stage of final product should be designed to open to a gas insert.

상세히 설명하면, 도 1에서 보이는 것처럼, 20 부분은 재단시 최종 제품과는 상관없이 재단되어 버려져 최종 제품에 포함되지 않는 부분이므로, 공기투과도 차이를 발생시키는 조직은 20부분에 삽입하여 코팅시 팽창된 공기가 이 조직을 통하여 유출되도록 한 후 재단 시 20 부분을 재단하여 분리함으로써, 최종 제품에는 이 공기투과도 차이가 발생하는 조직이 삽입되어 있지 않도록 한다. More specifically, as also shown in Figure 1, 20 portion is inserted into the tissue is 20 parts to generate a foundation upon because the final product and is cut regardless discarded portion not contained in the final product, an air permeability difference between the expansion during coating by the air is separated by cutting the part 20 during cutting so that after the outflow through the tissue, the end product is to ensure that the tissue is inserted by the air permeability differences.

본 발명의 공기부품성 직물에서 공기투과도 차이를 발생시키는 부분은 두개의 직물층 중 한면은 정상조직으로 이루어지고, 나머지 한면은 비정상 조직으로 이루어지도록 제직한다. Part for generating a difference in air permeability in the air part sex fabrics of the present invention on one side of the two fabric layers is made of a normal tissue, and the remaining one side is woven to occur by the abnormal tissue. 즉, 상기 공기투과도 차이를 갖는 정상조직 및 비정상 조직은 상기 서로 분리된 2개의 직물충의 상층 및 하층 또는 하층 및 상층에 각각 위치하여 직조되고, 공기부품성 직물의 외곽부에 직조된다. That is, normal tissue and abnormal tissue has a difference between the air permeability is woven to each of two locations on upper and lower layer fabrics caterpillars or the lower layer and the upper layer of the separated from each other, are woven on the outside portion of the air part St. fabric. 바람직하게, 상기 공기투과도 차이를 보이는 정상조직 및 비정상 조직은 직물 제직시 두층 중 상층은 경사 및 위사를 서로 교차하면서 직조하여 정상적인 직물의 형태로 직조하고, 하층은 경사 및 위사를 서로 교차시키지 않아 조직이 이루어지지 않게 직조하여 형성한다. Preferably, the upper layer of the normal tissue and abnormal tissue showing the air permeability difference is when the fabric weaving two layers is the weave in the form of a normal fabric by weaving with each other crossing the warp and weft, the lower layer is not not cross each other the warps and wefts tissue formed by weaving does not take place.

도 3에서 보면, 도면 부호 32는 두 개의 직물층을 부분적으로 접결하며, 부품성이 있는 직물의 공기의 유출을 막아주는 부분의 횡단면도이며, 도면부호 12는 두개의 직물층을 포함하는 부품성이 있는 직물의 횡단면도 부분이며, 도면부호 22는 공기투과도 차이를 발생시키는 조직의 횡단면도이다. In Figure 3, the reference numeral 32, and partly stitched to the two fabric layers, a transverse sectional view of the part which parts St. prevent the leakage of air in the fabric, the reference numeral 12 is a component property comprising two fabric layers a transverse sectional view in part of the fabric, the reference numeral 22 is a cross-sectional view of the tissue to generate a difference in air permeability.

도면부호 22 부분의 공기투과도 차이를 보이는 조직 중 도면부호 50 부분은 부품성이 있는 직물의 한 층과 동일한 조직으로 구성된 정상조직이며, 도면부호 40부분은 경사 및 위사가 서로 얽히지 않아 전혀 조직을 이루지 않아 40부분의 조직을 통하여 팽창된 공기가 유출되는 효과를 보이는 비정상 조직이다. Drawing the reference numeral 50 portion of the tissue showing the air permeability difference between the code 22 portion is part St. normal tissue composed of a layer with the same tissue of the fabric, the reference numeral 40 portion of the tissue at all the warps and wefts do not seaweed tangle each other do not fulfill the abnormal tissue showing the effect of the expanded air flows out through the tissue of the part 40.

이때, 코팅 후 정상조직 및 비정상조직의 두 층의 공기투과도 차이는 코팅량에 따라서 달라질 수 있으며, 바람직하게는 ASTM D 737의 방법으로 공기투과도 테스트를 진행하였을 때, 공기투과도 차이는 최소 1 cfm(ft 3 /min) 이상의 차이를 보여야만 공기가 잘 빠질 수 있다. In this case, two layer air permeability difference between normal tissue and abnormal tissue and then the coating will vary depending on the coating amount, preferably when proceeding the air permeability test method of ASTM D 737, an air permeability difference is minimum 1 cfm ( only show the difference ft more than 3 / min) is that air can well fall. 보다 바람직한 일예를 들면, 상기 공기투과도 차이는 1 내지 50 cfm(ft 3 /min)일 수 있다. G. A more preferred embodiment, the air permeability differences can be 1 to 50 cfm (ft 3 / min) .

만약 코팅 후 두 층의 공기투과도 차이가 1 cfm(ft 3 /min) 이하의 경우는 그 차이가 미비하여 코팅 시 팽창된 공기의 유출의 효과를 만족하지 못한다. If after the coating is less than or equal to the air permeability difference between the two layers 1 cfm (ft 3 / min) by the difference is insufficient does not meet the effect of the outflow of expanded air during coating. 또한, 위 아래 두 층 모두 공기투과도를 높이기 위하여, 조직을 구성하지 않을 경우 코팅시 코팅 약제가 비정상 조직 위에 도포되지 않고 반대쪽으로 흘러 내리기 때문에 정상적인 코팅이 이루어지지 않는다. In addition, not be achieved because of the normal coating to increase the air permeability both layers above and below, if not configuring the tissue down to the other end of the flow does not coat the medicament is applied onto the abnormal tissue during coating.

이하 본 발명의 실시예를 기재한다. It is described below an embodiment of the present invention. 단, 하기 실시예는 본 발명을 예시하기 위한 것일 뿐 본 발명이 하기 실시예에 한정되는 것은 아니다. The following Examples are not limited to the examples provided below are intended only to illustrate the present invention the present invention.

실시예 1 Example 1

315 데니어의 폴리아미드 멀티필라멘트를 경사 및 위사로 사용하여 제직시 부분적으로 접결되는 접결부를 포함하는 부품성이 있는 직물을 직조하였다. When weaving by using 315-denier polyamide multifilament as warp and weft were woven fabric with a part comprising a contact last name associated with and partially stitched. 이 중 재단시 분리되어 버려지는 직물의 외곽 부분에 공기투과도의 차이를 보일 수 있도록, 두층중 위층은 정상적인 직물 형태로 직조하고, 아래층은 경사 및 위삭 서로 얽히지 않게 직조하여 비정상 조직을 형성시켜 공기투과도 차이를 보이는 조직을 삽입하였다. This allows one can show differences in air permeability in the outer portions of the fabric be discarded separately when cutting, upper level of the two layers is to weave a normal tissue types, underlayer by weaving warps and Wei Shuo no seaweed tangle with each other to form an abnormal tissue air was inserted into a tissue permeability looks different. 이후, 상기 공기부품성 직물에 양면 코팅을 실시하였다. Then, a double-sided coating in the air part St. fabric was carried out. 이때, 코팅 후 ASTM D 737의 방법으로 두 층의 공기투과도를 측정한 결과 그 차이가 2.3cfm 이었다. In this case, after coating a result of measuring the air permeability of the two layers by the method of ASTM D 737 it was the difference is 2.3cfm. 본 실시예의 경우 양면 코팅시 경사 및 위사의 얽힘이 없이 조직이 구성되지 않는 비정상 조직 부분으로 팽창된 공기가 유출되어 부품성이 있는 직물 부분이 팽창하지 않아 공기부품성 직물의 주름이 발생하지 않았다. In the case of the present embodiment it has not the double-side coating when the folds of the gradient and is no entanglement of the weft tissue is the expanded air to the abnormal tissue area outlet that are not components St. fabric portion is not expanded with air components St. fabric occurs.

비교예 1 Comparative Example 1

315 데니어의 폴리아미드 멀티필라멘트를 경사 및 위사로 사용하여 제직시 부분적으로 접결되는 접결부를 포함하는 부품성이 있는 직물을 직조하였다. When weaving by using 315-denier polyamide multifilament as warp and weft were woven fabric with a part comprising a contact last name associated with and partially stitched. 이후, 공기투과도 차이를 유발하는 조직을 삽입하지 않고 양면 코팅을 실시하였다. Then, without inserting the tissue to cause a difference in air permeability it was conducted for two-sided coating. 이때 부품성이 있는 직물의 부분에 내부 공기가 팽창하여 일부 이중직물의 부분에서 주름이 생기는 문제점이 발생하였다. The problems are wrinkles on the part of some dual fabric was caused by parts castle air inside expands the portion of the fabric.

비교예 2 Comparative Example 2

상기 비교예 1과 동일한 방법으로 직물을 직조하되, 직물의 위 층과 아래 층의 제직밀도를 상이하게 제작한 후 양면 코팅을 실시하였다. But the woven fabric in the same manner as in Comparative Example 1, a two-sided coating was performed after the differently manufactured weaving density of the upper layer and lower layer of the fabric. 이때 코팅 후 ASTM D 737의 방법으로 이중직물의 위 층과 아래 층의 공기투과도를 측정한 결과 그 차이 는 0.6cfm 이었다. At this time, after the coating results of the measurement of the air permeability of the top layer and the bottom layer of the double fabric by the method of ASTM D 737, the difference was 0.6cfm. 양면 코팅을 실시한 결과 그 공기투과도의 차이가 미비하여 부품성이 있는 직물의 부분에 공기가 팽창하여 일부 직물의 부분에서 주름이 생기는 문제점이 발생하였다. The problem with a result of the two-sided coating is insufficient difference in air permeability to air is expanded to the portion of the fabric in the parts St. generated wrinkles in the portion of the part of the fabric has occurred.

비교예 3 Comparative Example 3

상기 비교예 1과 동일한 방법으로 이중직물을 직조하되, 직물의 위 층과 아래 층을 모두 조직을 구성하지 않는 비정상 조직으로 제작한 후 양면 코팅을 실시하였다. But the double weave fabric in the same manner as in Comparative Example 1, the coating on both sides were then produced does not constitute a tissue layer both above and below the layers of fabric abnormal tissue. 그러나, 위, 아래 층 모두 비정상 조직으로 제직되어 코팅 약제가 비정상 조직 위에 정상적으로 도포되지 않고 반대면으로 흘러내려 코팅이 정상적으로 이루어지지 않았다. However, the woven in abnormal tissue both upper and lower layer coating agent is not built is made to flow to the reverse side coating it is not applied properly on the abnormal tissue as normal.

본 발명의 기체에 의해 부품성을 갖는 직물은 제직단계에서 봉제공정을 생략할 수 있어 제조단가를 획기적으로 낮출 수 있으며, 특히 직물층이 모두 평직이기 때문에 자카드를 이용한 다양한 형태의 공기 주머니의 제작이 가능할 뿐 아니라, 제직성과 평활성이 우수하여 자동차 측면의 커튼형 에어백과 같은 충격 완충형 제품 등에 유용하게 사용될 수 있다. Fabric having a component property by gas of the present invention it is possible to omit the sewing process in a weaving step, and to lower the manufacturing cost significantly, especially in the production of various types of air bag using a Jacquard since the fabric layer are both plain weave as well as possible, and excellent officers and smoothness it can be useful, such as shock absorbing type products, such as curtain airbag of the vehicle side.

Claims (5)

  1. 직기를 이용하여 동시에 직조되는 서로 분리된 2개의 직물층을 포함하는 팽창부, 및 상기 팽창부를 이루기 위해 밀폐되도록 상기 서로 분리된 2개의 직물의 주위를 단일직으로 부분적으로 접결한 접결부를 포함하는 공기부품성 직물로서, Using a weaving machine expansion portion comprising two layers of fabric which are separated from each other are woven at the same time, and including a contact integral contact associated the periphery of the two fabrics with the separated so that the sealing in order to achieve part said expanded by a single straight part, an air component castle fabric,
    상기 공기부품성 직물의 적어도 하나는 공기투과도 차이를 갖는 정상조직 및 비정상 조직을 포함하여 직조된 것이며, At least one part of the air will St. fabric woven to a normal tissue and abnormal tissue has a difference in air permeability,
    공기투과도 차이를 갖는 정상조직 및 비정상 조직에서 공기투과도 차이는 적어도 1 cfm (ft 3 /min) 이상인 기체에 의해 부품성을 갖는 직물. Air permeability difference from normal tissue and abnormal tissue has an air permeability difference fabric having a component property by the gas is at least 1 cfm (ft 3 / min) .
  2. 제 1항에 있어서, 상기 공기투과도 차이를 갖는 정상조직 및 비정상 조직은 상기 서로 분리된 2개의 직물충의 상층 및 하층, 또는 하층 및 상층에 각각 위치하여 직조되고, 공기부품성 직물의 외곽부에 직조되는 것인 기체에 의해 부품성을 갖는 직물. The method of claim 1, wherein the normal tissue and abnormal tissue having the air permeability differences are woven to each position in the two fabric caterpillars upper layer and lower layer, or the lower layer and the upper layer of the separated from one another, weave to the outer frame unit of the air part St. fabric fabric having a component property by that the gas.
  3. 제 1항에 있어서, 상기 비정상 조직은 경사 및 위사가 서로 교차 없이 직조되어 이들이 서로 얽히지 않는 형태인, 기체에 의해 부품성을 갖는 직물. The method of claim 1, wherein the abnormal tissue is a fabric having a property component by the form the warps and wefts are woven without crossing each other they do seaweed tangle with each other, gas.
  4. 삭제 delete
  5. 제 1항에 있어서, 상기 공기투과도 차이를 보이는 정상조직 및 비정상 조직은 직물 제직시 두층 중 상층은 경사 및 위사를 서로 교차하면서 직조하여 정상적인 직물의 형태로 직조하고, 하층은 경사 및 위사를 서로 교차시키지 않아 조직이 이루어지지 않게 직조하여 형성되는 것인 기체에 의해 부품성을 갖는 직물. The method of claim 1, wherein the normal tissue and abnormal tissue showing the air permeability difference and woven in the form of a normal fabric by weaving the upper layer of the city fabric weaving two layers, while another crossing the warp and weft, the lower layer to each other crossing the warp and weft fabric having a part by sex because of not being formed by weaving not supporting tissue is made gas.
KR20060027870A 2006-03-28 2006-03-28 An inflatable fabrics KR100756016B1 (en)