KR100741447B1

KR100741447B1 - Molding goods manufacturing method and using paper mulberry fiber

Info

Publication number: KR100741447B1
Application number: KR1020070034683A
Authority: KR
Inventors: 박동운
Original assignee: 박동운
Priority date: 2007-04-09
Filing date: 2007-04-09
Publication date: 2007-07-20

Abstract

A manufacturing method of Korean paper by using a mulberry fiber molding formation method is provided to protect the human beings from the influence of the environmental hormone discharged from various plastic products. The skin of a mulberry tree is peeled and the peeled skin is inserted into a cauldron and boiled. Thereafter, the skin of the mulberry tree is washed and the general mulberry tree working such as a tapping process of the mulberry tree is performed(S1). The paste made of a mulberry tree is injected into the skin of the mulberry tree in order to have viscosity so that the skin is processed to the fiber(10) of the mulberry tree containing moisture(S2). Thereafter, the fiber of the mulberry tree is injected into a mold(200) of upper and lower molds(210,220). Thereafter, the molding by the heat compression is performed so that the Korean paper formation(20) with a three-dimensional shape is manufactured(S3). At the third process, an oil treatment is performed.

Description

Molded goods manufacturing method and using paper mulberry fiber}

도 1은 본 발명의 일 실시예에 의한 한지성형물의 제조 공정도.1 is a manufacturing process diagram of a Hanji molded article according to an embodiment of the present invention.

도 2는 본 발명에 의한 도 1의 제조공정에 의해 제조되는 한지성형물의 일 예를 보인 사진.Figure 2 is a photograph showing an example of a Hanji molded article produced by the manufacturing process of Figure 1 according to the present invention.

도 3은 본 발명에 의한 도 1의 제조공정에 사용되는 몰딩금형을 나타낸 사진.Figure 3 is a photograph showing the molding mold used in the manufacturing process of Figure 1 according to the present invention.

도 4는 본 발명의 다른 실시예에 의한 한지성형물의 제조 공정도.Figure 4 is a manufacturing process diagram of the hanji molding according to another embodiment of the present invention.

*** 도면의 주요부분에 대한 부호의 설명 ****** Explanation of symbols for main parts of drawing ***

10,110: 닥섬유재 20,140: 한지성형물10,110: Doc fiber 20,140: Hanji molding

120: 한지성형틀 130: 사출물120: cold mold 130: injection molding

200: 몰딩금형 300: 사출금형200: molding mold 300: injection mold

본 발명은 닥섬유 몰딩 성형공법을 이용한 한지성형물의 제조방법에 관한 것으로서, 더욱 상세하게는 닥나무를 이용한 한지 뜨기 이전상태의 닥풀이 입혀진 닥나무(이하 "닥섬유"라 한다.)를 사용하여 한지효능을 발휘하는 성형물을 제작함으로써 친환경적인 제품을 만들 수 있도록 하며 각종 플라스틱제품에서 배출되는 환경호르몬의 영향력으로부터 인체를 보호할 수 있도록 하는 닥섬유 몰딩 성형공법을 이용한 한지성형물의 제조방법에 관한 것이다.The present invention relates to a method for manufacturing a Hanji molding using a mulberry fiber molding molding method, and more particularly, using the mulberry coated paper mulberry (hereinafter referred to as "dough fiber") using the mulberry to demonstrate the Hanji efficacy The present invention relates to a method for manufacturing Hanji moldings using the Doc-fiber molding molding method to make an environment-friendly product by making a molding to protect the human body from the influence of environmental hormones emitted from various plastic products.

일반적으로 합성수지는 800 ~ 1000℃의 고온에서 가열하여 가공하는 유리 또는 도자기 등에 비해 상대적으로 200 ~ 300℃의 저온에서 가열 성형됨으로 인해 기본적으로 환경호르몬을 배출하게 되며, 인체에 유입되었을 경우 사람의 호르몬 계통에 혼란을 가져와 알레르기, 암, 아토피 등 여러 질병을 유발시킬 수 있으며, 유전에도 영향을 미쳐 다음 세대에 태어날 아기에게도 선천성 질병을 유발 시킬 수 있는 문제점을 가지고 있다.In general, synthetic resins are produced by heating at a low temperature of 200 ~ 300 ℃ relatively compared to glass or ceramics processed by heating at a high temperature of 800 ~ 1000 ℃ basically discharge environmental hormones, when human hormone enters the human body It can cause confusion in the system and cause various diseases such as allergies, cancer, and atopy, and it also affects heredity and can cause congenital diseases in babies born in the next generation.

한편, 상기 합성수지재의 경우에는 차가운 느낌이 들어 특히 정서가 메마르고, 환경호르몬을 유발시킬 뿐만 아니라, 폐기시에도 지구환경을 장기간 오염시키는 문제점을 안고 있는 실정이다.On the other hand, in the case of the synthetic resin material has a cold feeling, especially the emotion is dry, not only causes environmental hormones, but also has a problem of contaminating the global environment for a long time when disposed.

물론 이와 같은 오염의 문제점을 해결하고자 최근에는 원목으로 건축물의 내외장재 및 각종 용품들을 제조하고는 있으나, 원목 자체를 제단해서 이용하므로 짧게는 1년생부터 수십 수백년 된 고목(古木)까지 사용하므로 벌목으로 인한 산림의 훼손이 심각한 지경에 이르고 있으며, 그 원자재가격이 고가(高價)이고 무거운 문제점을 가지고 있다.Of course, in order to solve the problem of pollution, recently, the interior and exterior materials and various items of the building are manufactured from solid wood, but since the wood itself is used as an altar, it can be used from a year old to hundreds of years old wood (old wood). The deterioration of forests has reached a serious level, and the raw material prices are high and have heavy problems.

특히 원목을 이용한 대부분의 물품은 다양한 색상을 나타내도록 하기 위해 페인트 등의 색소를 칠한 것을 사용하는데 이는 상당량의 중금속이 함유되어 있고, 초기 사용시에는 악취가 많이 발생되어 이 역시 인체에 치명적인 문제점을 여전히 가지고 있다.In particular, most items using solid wood use pigments such as paints in order to display various colors, which contain a considerable amount of heavy metals, and odors are generated during the initial use, which is still fatal to humans. have.

그리고, 현재와 미래에 살고 또는 살아가게 되는 영아에서부터 노인에 이르는 사람들은 상술한 환경호르몬의 영향력에 노출된 채로 무방비하게 삶을 영위해가고 있는데, 특히 영아나 유아는 초기 접하게 되는 완구나 놀이블록에서부터 환경호르몬의 영향을 받고 있다.In addition, people ranging from infants and seniors who live or live now and in the future are living unprotected lives exposed to the effects of environmental hormones described above. It is affected by environmental hormones.

따라서, 이러한 문제점들을 해결하기 위하여 안출된 것으로서, 그 목적으로 하는 바는 닥나무를 이용한 한지 뜨기 이전의 닥섬유상태의 것을 사용하되 닥과 닥풀의 배합비율을 개선하여 한지성형물품의 제작을 가능하게 함으로써 한지효능을 발휘하는 성형물품을 제작할 수 있도록 하고 친환경성을 갖도록 하며 각종 플라스틱제품에서 배출되는 환경호르몬의 영향력으로부터 인체를 보호할 수 있도록 하는 닥섬유 몰딩 성형공법을 이용한 한지성형물의 제조방법을 제공하는데 있다. Therefore, it was devised to solve these problems, and its purpose is to use the mulberry fiber state before the floating of Hanji using the mulberry wood, but to improve the mixing ratio of the mulberry and mulberry by making the hanji molded articles possible The present invention provides a method for manufacturing a Hanji molded article using a Doc-fiber molding molding process that enables the manufacture of molded articles exhibiting efficacy, to have environmental friendliness, and to protect the human body from the influence of environmental hormones emitted from various plastic products.

본 발명의 다른 목적은 한지와 같은 효능 및 느낌의 발휘로 제조된 물품에 한지특유의 부드러움 및 포근함과 정서적인 안정의 유익함을 하는 제공할 수 있도록 하는 닥섬유 몰딩 성형공법 이용한 한지성형물의 제조방법을 제공하는데 있다.Another object of the present invention is to provide a method for producing Hanji moldings using Doc fiber molding molding method to provide the benefits of the softness and warmth and emotional stability unique to Korean paper to manufactured articles exhibiting the same efficacy and feeling as Hanji To provide.

이와 같은 목적을 달성하기 위한 본 발명은, 닥나무를 채취하여 껍질을 벗긴 후, 그 벗긴 껍질을 가마솥에 넣고 삶은 후 씻고 삶은 닥나무 껍질을 두드리는 공지의 닥나무 가공을 행하는 제1단계와; 상기 제1단계의 닥나무 껍질에 닥풀을 풀어 점성을 갖도록 하고 습기를 머금은 상태의 닥섬유재로 가공하는 제2단계와; 상기 제2단계의 닥섬유재를 일정형상을 갖는 상부금형과 하부금형의 몰딩금형에 투입한 후, 열압착에 의한 몰딩을 행하여 입체적 형상을 갖는 한지성형물로 성형하는 제3단계로 이루어지는 것을 기술적 특징으로 한다.The present invention for achieving the above object, the first step of performing a known mulberry processing to take off the bark, peeled, put the peeled bark in the cauldron, washed, and then tapping the boiled mulberry bark; A second step of dissolving the mulberry on the bark of the first step to make it viscous and processing it into a mulberry fiber material containing moisture; The third step of molding the medicinal fiber of the second step into the molding mold of the upper mold and the lower mold having a predetermined shape, and then molding by a cold pressing molding having a three-dimensional shape by molding by thermocompression. do.

또한, 본 발명은 닥나무를 채취하여 껍질을 벗긴 후, 그 벗긴 껍질을 가마솥에 넣고 삶은 후 씻고 삶은 닥나무 껍질을 두드리는 공지의 닥나무 가공을 행하는 제1단계와; 상기 제1단계의 닥나무 껍질에 닥풀을 풀어 점성을 갖도록 하고 습기를 머금은 상태의 닥섬유재로 가공하는 제2단계와; 상기 제2단계의 닥섬유재를 일정형상을 갖는 상부금형과 하부금형의 몰딩금형에 투입한 후, 열압착에 의한 몰딩으로 입체적 형상을 갖는 한지성형틀을 성형하는 제3단계와; 상기 한지성형틀을 합성수지를 사출성형하기 위한 사출금형에 삽입한 후 사출금형의 주입홀을 통해 용융된 상태의 합성수지를 주입하는 제4단계와; 상기 주입된 합성수지를 성형하여 한지성 형틀의 내면에 사출물이 일체로 결합된 한지성형물품을 완성하는 제5단계를 포함하여 이루어지는 것을 다른 기술적 특징으로 한다.In addition, the present invention is the first step of performing a known mulberry processing to remove the bark and peel off, put the peeled bark in the cauldron and boiled, then washed and tapping the boiled mulberry bark; A second step of dissolving the mulberry on the bark of the first step to make it viscous and processing it into a mulberry fiber material containing moisture; A third step of inserting the Doc-fiber material of the second step into a molding mold of an upper mold and a lower mold having a predetermined shape, and then forming a three-dimensional Hanji molding die by molding by thermocompression molding; Inserting the hanji mold into an injection mold for injection molding, and then injecting the synthetic resin in a molten state through an injection hole of the injection mold; It is another technical feature that comprises the fifth step of molding the injected synthetic resin to complete the Hanji molded article in which the injection molding is integrally coupled to the inner surface of the hanji mold.

삭제delete

이하, 본 발명에 의한 바람직한 실시예를 첨부한 도면을 참조하여 상세히 설명하기로 하며, 기술되는 실시예에 의하여 그 특징들을 이해할 수 있을 것이다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings, and the characteristics will be understood by the embodiments described.

도 1은 본 발명의 일 실시예에 의한 한지성형물의 제조 공정도이고, 도 2는 본 발명에 의한 도 1의 제조공정에 의해 제조되는 한지성형물의 일 예를 보인 도면이고, 도 3은 본 발명에 의한 도 1의 제조공정에 사용되는 몰딩금형을 나타낸 도면이고, 도 4는 본 발명의 다른 실시예에 의한 한지성형물의 제조 공정도이다.1 is a manufacturing process diagram of a Hanji molded article according to an embodiment of the present invention, Figure 2 is a view showing an example of a Hanji molded article produced by the manufacturing process of Figure 1 according to the present invention, Figure 3 is a present invention Figure 1 is a view showing a molding mold used in the manufacturing process of Figure 1, Figure 4 is a manufacturing process diagram of a paper-forming molding according to another embodiment of the present invention.

도 1에 나타낸 바와 같이, 본 발명의 일 실시예에 의한 닥섬유 몰딩 성형공법을 이용한 한지성형물의 제조방법은 닥나무를 채취하여 껍질을 벗긴 후, 그 벗긴 껍질을 가마솥에 넣고 삶은 후 씻고 삶은 닥나무 껍질을 두드리는 공지의 닥나무 가공을 행하는 제1단계(S1)와; 상기 제1단계(S1)의 닥나무 껍질에 닥풀을 풀어 점성을 갖도록 하고 습기를 머금은 상태의 닥섬유재(10)로 가공하는 제2단계(S2)와; 상기 제2단계(S2)의 닥섬유재(10)를 일정형상을 갖는 상부금형(210)과 하부금형(220)의 몰딩금형(200)에 투입한 후, 열압착에 의한 몰딩(molding)을 행하여 입체적 형상을 갖는 한지성형물(20)을 만들어내는 제3단계(S3)로 이루어진다.As shown in Figure 1, the manufacturing method of the Hanji molding using the Doc fiber molding molding method according to an embodiment of the present invention, after removing the bark and peeled, put the peeled bark in the cauldron and boiled and washed boiled mulberry bark A first step (S1) of performing a well-known mulberry processing; A second step (S2) of dissolving the mulberry on the bark of the first step (S1) to have a viscosity and processing it with the mulberry fiber material 10 having moisture; The Doc fiber material 10 of the second step (S2) is put into the molding mold 200 of the upper mold 210 and the lower mold 220 having a predetermined shape, and then molded by thermocompression molding. It consists of a third step (S3) for producing a Hanji molding 20 having a three-dimensional shape.

또한, 상기 제3단계(S3)에서 제조되어 완성되는 한지성형물(20)의 표면에는 한지섬유의 일어남을 방지하기 위하여 오일 처리를 행함이 바람직하며, 이때, 사용되는 오일은 인체에 무해한 것이 좋으며, 아마기름, 호두기름, 동백기름 중에서 선택된 어느 하나 또는 선택 조합으로 구성될 수 있다.In addition, it is preferable to perform oil treatment on the surface of the Hanji molding 20 manufactured and completed in the third step (S3) to prevent the occurrence of Hanji fibers, wherein the oil used is preferably harmless to the human body, and probably It may be composed of any one selected from oil, walnut oil, camellia oil, or a combination thereof.

상기 제2단계(S2)에서의 닥섬유재(10)는 2ℓ의 물에 닥풀 35㎖를 넣어 혼합하는 제1과정과, 3ℓ의 물에 닥나무 껍질 120g을 혼합하는 제2과정과, 상기 제2과정의 닥나무 껍질이 담긴 물에 상기 제1과정의 닥풀이 풀린 물 120㎖~180㎖를 넣고 혼합하여 닥섬유를 만드는 제3과정과, 상기 제3과정의 닥섬유를 1~2mm 크기의 물빠짐홀을 갖는 뜰채에서 닥섬유 틀뜨기를 행하여 점착성을 갖고 습기를 머금은 닥섬유재(10)로 만드는 제4과정으로 이루어진다.The mulberry fiber material 10 in the second step (S2) is a first process of mixing 35 ml of mulberry in 2 liters of water, a second process of mixing 120 g of mulberry bark in 3 liters of water, and the second process The third step of making the mulberry fibers by mixing 120ml ~ 180ml of the loose water of the first step into the water containing the bark of the mulberry bark, the mulberry fibers of the third process having a water drain hole of 1 ~ 2mm size It consists of a 4th process which makes a docile fiber twisting in a garden fiber and makes it into the tack fiber material 10 which has adhesiveness and contains moisture.

여기서, 상기한 닥나무 껍질과 닥풀의 배합비는 상기 닥섬유재(10)를 200mm(가로) × 200mm(세로) × 1mm(높이)로 5~6장을 뜨기할 수 있는 분량을 기술한 것이다.Here, the mixing ratio of the bark and the mulberry described the amount that can float 5 to 6 sheets of the mulberry fiber material 10 in 200mm (width) × 200mm (length) × 1mm (height).

이때, 상기 제3과정에서 닥풀이 풀린 물, 즉 닥풀 액체량을 120㎖ 미만으로 할 경우 점성이 약해 제3단계(S3)의 열압착에 의한 성형시 한지성형물(20)이 찢어지게 되고 닥풀 액체량을 180㎖ 초과할 경우 점성이 너무 강해 흩어짐에 의해 한지성형물(20)의 형상화를 위한 성형작업이 어렵게 된다.At this time, when the amount of water loosened in the third process, that is, the amount of the liquid of the mulberry is less than 120ml, the viscosity is weak, and the cold-fat molded product 20 is torn during molding by thermocompression of the third step (S3). If the amount exceeds 180ml, the viscosity is so strong that it is difficult to mold the shaping for forming the cold-jiji molding 20.

상기 제4과정에서 사용되는 뜰채는 닥섬유의 물빠짐 흐름을 원활하게 하면서 닥풀을 통한 닥섬유간의 균일한 결합성(한 부분으로 닥섬유가 뭉치는 것을 방지)을 유지할 수 있도록 하기 위한 것이다.The garden grass used in the fourth process is to maintain a uniform bond between the mulberry fibers through the mulberry (prevents the bunching of the mulberry fibers in one portion) while smoothing the water flow of the mulberry fibers.

또한, 습기를 머금은 상태의 닥섬유재(10)를 이용하는 것은 몰딩금형(200)을 통하여 한지성형물(20)로 성형할시 신축기능을 발휘할 수 있고 쉽게 찢겨짐을 방지하므로 성형의 용이성을 제공할 수가 있다.In addition, using the doc fiber material 10 in a wet state can exert an elastic function when forming the cold-foamed product 20 through the molding mold 200 and can easily provide tearing since it can easily be torn. .

상기 제3단계(S3)에서 닥섬유재(10)를 몰딩금형(200)에 투입하여 열압착에 의한 몰딩을 행함으로써 획득한 한지성형물(20)은 일정한 두께 및 강도를 가지고 형상 또한 입체감을 가지므로 이러한 제조공정을 통해서 닥섬유재(10)에 의한 완구나 놀이블록 또는 장난감 등의 한지성형물을 제작할 수 있게 되는 것이다.In the third step S3, the cold-finished product 20 obtained by inserting the doc fiber material 10 into the molding mold 200 and performing molding by thermocompression has a certain thickness and strength and also has a three-dimensional shape. Through such a manufacturing process it is possible to manufacture a paper, such as toys, play blocks or toys made of doc fiber material (10).

부연하여, 상기 제3단계(S3)에서는 몰딩금형(200)의 하부금형(220) 상에 닥섬유재(10)를 2층 이상으로 적층하여 투입하게 되고, 양측부가 하부금형(220)의 상면에 안착되고 습기를 머금은 축축함에 의해 중심부가 하부금형(220)의 성형홈(222)측으로 쳐짐이 형성된 상태에서 상부금형(210)과 하부금형(220)을 매칭 결합하여 몰딩 성형을 행하게 되며, 닥섬유재(110)의 양측부가 점성에 의한 닥섬유간의 밀착성으로 금형의 내측으로 밀려들어가면서 몰딩 성형되어 한지성형물(20)이 되는 것이다.In other words, in the third step (S3), the Doc fiber material 10 is laminated in two or more layers on the lower mold 220 of the molding mold 200, and both sides are disposed on the upper surface of the lower mold 220. The upper mold 210 and the lower mold 220 are matched with each other in a state in which the center portion is slumped to the forming groove 222 side of the lower mold 220 by the damp and moistened with moisture, and molding is performed. Both sides of the 110 are molded by being pushed into the mold due to viscous adhesion between the Doc fibers to form the Hanji molding 20.

한편, 상기한 제조공정에 의해 성형되는 한지성형물의 이해를 돕기 위하여 도 2에 도 1의 제조공정으로 제조된 한지성형물(20)의 실제 성형물을 나타내었으며, 도 3에 도 1의 제조공정에 사용되는 몰딩금형(200)의 목업 성형기를 나타내었다.On the other hand, in order to help the understanding of the Hanji molding molded by the above-described manufacturing process, Figure 2 shows the actual molding of the Hanji molding 20 manufactured by the manufacturing process of Figure 1, Figure 3 used in the manufacturing process of Figure 1 Shown is a mock-up molding machine of the molding mold 200.

한편, 도 4에 나타낸 바와 같이, 본 발명의 다른 실시예에 의한 닥섬유 몰딩 성형공법을 이용한 한지성형물의 제조방법은 닥나무를 채취하여 껍질을 벗긴 후, 그 벗긴 껍질을 가마솥에 넣고 삶은 후 씻고 삶은 닥나무 껍질을 두드리는 공지의 닥나무 가공을 행하는 제1단계(S11)와; 상기 제1단계(S11)의 닥나무 껍질에 닥풀을 풀어 점성을 갖도록 하고 습기를 머금은 상태의 닥섬유재(110)로 가공하는 제2단계(S12)와; 상기 제2단계(S12)의 닥섬유재(110)를 일정형상을 갖는 상부금형(210)과 하부금형(220)의 몰딩금형(200)에 투입한 후, 열압착에 의한 몰딩으로 입체적 형상을 갖는 한지성형틀(120)을 만들어내는 제3단계(S13)와; 상기 한지성형틀(120)을 합성수지를 사출성형하기 위한 사출금형(300)에 삽입한 후 사출금형(300)의 주입홀(312)을 통해 용융된 상태의 합성수지를 주입하는 제4단계(S14)와; 상기 주입된 합성수지를 성형하여 한지성형틀(120)의 내면에 사출물(130)이 일체로 결합된 한지성형물품(140)을 완성하는 제5단계(S15)와, 상기 사출금형(300)을 냉각시킨 후 한지성형물품(140)을 탈형하는 제6단계(S16)를 포함하여 이루어진다.On the other hand, as shown in Figure 4, according to another embodiment of the present invention, the manufacturing method of the Korean paper molding using the mulberry fiber molding molding method, after taking off the bark and peeled, put the peeled bark in the cauldron, washed and boiled A first step (S11) of performing a known mulberry processing to tap the bark; A second step (S12) of dissolving the mulberry on the bark of the first step (S11) to have viscous, and processing into a mulberry fiber material 110 in a state containing moisture; After inserting the doc fiber material 110 of the second step (S12) into the molding mold 200 of the upper mold 210 and the lower mold 220 having a predetermined shape, and has a three-dimensional shape by molding by thermal compression A third step (S13) of making the Hanji molding frame 120; Inserting the Hanji molding mold 120 into the injection mold 300 for injection molding the synthetic resin and then injecting the synthetic resin in the molten state through the injection hole 312 of the injection mold 300 (S14) Wow; The fifth step (S15) and the injection mold 300 to cool the injection mold 300 by completing the injection molded product 140 is integrally coupled to the inner surface of the mold forming mold 120 by molding the injected synthetic resin After the sixth step (S16) is made to demold the Hanji molded article 140.

또한, 상기 제6단계(S16)를 거친 한지성형물품(140)의 표면에 한지성형틀(120)측의 한지섬유가 일어남을 방지하기 위하여 오일처리를 행하는 제7단계(S17)를 포함하여 이루어지게 함이 바람직하며, 이때에도, 사용되는 오일은 인체에 무해한 것이 좋으며, 아마기름, 호두기름, 동백기름 중에서 선택된 어느 하나 또는 선택 조합으로 구성될 수 있다.In addition, the seventh step (S17) to perform the oil treatment to prevent the occurrence of the Hanji fiber on the side of the Hanji molding die 120 on the surface of the Hanji molding article 140 through the sixth step (S16). Preferably, the oil used is harmless to the human body, and may be composed of any one selected from flax oil, walnut oil, and camellia oil.

이때, 상기 제2단계(S12)에서의 닥섬유재(110) 가공공정은 도 1을 참조하여 설명한 닥섬유재(10)의 제조과정과 동일하게 이루어지므로 이를 준용하고 참조하기로 하며, 닥풀 액체량의 범주를 정한 이유와 닥나무 껍질이나 닥풀을 물에 혼합하는 이유 또한 도 1의 실시예를 통해 설명한 바와 동일하다.At this time, the process of processing the doc fiber material 110 in the second step (S12) is made the same as the manufacturing process of the doc fiber material 10 described with reference to FIG. The reason for setting the category and the reason for mixing the bark or the paper mulberry in water is also the same as described through the embodiment of FIG.

상기 제3단계(S13)에 사용되는 몰딩금형(200)과 상기 제4단계(S14)에 사용되는 사출금형(300)은 성형을 위한 내부 구성이 동일하게 형성되는 것이다.The molding mold 200 used in the third step S13 and the injection mold 300 used in the fourth step S14 have the same internal configuration for molding.

나아가, 상기 제3단계(S13)에서는 몰딩금형(200)의 하부금형(220) 상에 닥섬유재(110)를 투입하게 되는데, 한지성형틀(120)의 일정 두께를 형성하기 위해 닥섬유재(110)를 2층 이상으로 적층하여 투입하게 되며, 도시된 바와 같이, 양측부가 하부금형(220)의 상면에 안착되고 습기를 머금은 축축함에 의해 중심부가 하부금형(220)의 성형홈(222)측으로 쳐짐이 형성된다. 이러한 상태에서 상부금형(210)과 하부금형(220)을 매칭 결합하여 몰딩 성형을 행하면 닥섬유재(110)의 양측부가 점성에 의한 닥섬유간의 밀착성으로 금형의 내측으로 밀려들어가면서 몰딩 성형되어 일정 두께를 갖는 한지성형틀(120)이 완료되는 것이다.Further, in the third step (S13) is to put the doc fiber material 110 on the lower mold 220 of the molding mold 200, Doc fiber material 110 to form a predetermined thickness of the Hanji molding frame 120 ) Is laminated in two or more layers, and as shown in the drawing, both sides are seated on the upper surface of the lower mold 220 and moist with moisture, so that the center portion is struck by the forming groove 222 side of the lower mold 220. Is formed. In this state, when the molding is performed by matching the upper mold 210 and the lower mold 220, both sides of the doc fiber material 110 are molded into the mold while being pushed into the mold due to the adhesion between the duct fibers due to the viscosity, and having a predetermined thickness. Hanji molding frame 120 is completed.

이때, 몰딩 성형에 의해 얻어진 한지성형틀(120)은 0.2mm~5mm의 두께로 형성함이 바람직하며, 여기서 한지성형틀(120)의 두께를 0.2mm 미만으로 할 경우에는 성형금형(200)에서 직각 이하의 각을 형성시키기 어렵게 되고, 5mm를 초과할 경우에는 몰딩을 위한 성형 사이클이 길어지고 비용소모가 많아지는 단점을 갖게 된다.At this time, the cold forming mold 120 obtained by molding molding is preferably formed to a thickness of 0.2mm ~ 5mm, where the thickness of the cold forming mold 120 is less than 0.2mm in the molding mold 200 It becomes difficult to form an angle below the right angle, and when it exceeds 5 mm, a molding cycle for molding is long and a disadvantage is that it becomes expensive.

바람직하기로는 한지성형틀(120)의 두께를 0.8mm~3mm로 형성함이 효율적이라 할 수 있다.Preferably it can be said that forming the thickness of the cold forming mold 120 to 0.8mm ~ 3mm.

상기 제4단계(S14)에 사용되는 합성수지는 폴리프로필렌(PP), 폴리카보네이트(PC), 폴리에틸렌(PE) 등과 같은 다양한 재질이 사용될 수 있으며, 일정 두께를 갖는 한지성형틀(120)의 내측면으로 합성수지가 주입된다.Synthetic resin used in the fourth step (S14) may be used a variety of materials, such as polypropylene (PP), polycarbonate (PC), polyethylene (PE), etc., the inner surface of the Hanji molding die 120 having a certain thickness Synthetic resin is injected into

상기 제5단계(S15)에서의 성형에 의해 이루어지는 한지성형물품(140)은 닥섬 유재로 구성되어 닥풀에 의한 점착성을 갖는 한지성형틀(120)과 합성수지의 구성인 사출물(130)이 내외측에 위치하여 일체 결합되는 것으로, 한지성형틀(120)이 표피재가 되고 사출물(130)이 내부구성물이 되는 것이며, 사출금형에 의한 사출 성형시 한지성형틀(120)의 점착성에 의해 사출물(130)과 더욱 견고한 결합력을 갖게 된다.The Hanji molded article 140 formed by the molding in the fifth step (S15) is composed of a dakseom material and the injection molding 130, which is a composition of the Hanji molding frame 120 and the synthetic resin having adhesiveness by the buckwheat on the inside and outside Positioned and integrally coupled, the Hanji molding die 120 is a skin material and the injection molding 130 is an internal constituent, and the injection molding 130 and the injection molding 130 by the adhesiveness of the Hanji molding die 120 during the injection molding by the injection mold It will have a stronger bond.

그리고, 완성된 한지성형물품(140)의 표면에 인체에 무해한 오일을 발라줌으로써 한지섬유가 일어남을 방지하여 매끈한 표면처리가 이루어질 수 있게 하면 된다.Then, by applying oil harmless to the human body on the surface of the finished Hanji molded article 140, it is possible to prevent the Hanji fiber to occur to enable a smooth surface treatment.

한편, 본 발명의 실시예에 의한 기술적 사상 및 기술은 유아나 아동용 완구, 놀이블록 또는 장난감 등의 제작에 적용될 수 있을 뿐만 아니라 합성수지재로 만들어지는 제품의 표면을 감싸는 표피재로서 적용하여 한지효능을 발휘되게 할 수 있고, 자동차의 내장재나 가정용 인테리어제품 등 다양한 분야에 폭넓게 적용할 수 있으며, 특히 합성수지에서 배출되는 환경호르몬의 나쁜 영향력을 최소화하거나 제거할 수 있어 인체와의 직접적인 접촉을 차단하고 인체를 보호하는데 아주 유용하게 적용될 수 있는 것이다.On the other hand, the technical idea and technology according to the embodiment of the present invention can be applied not only to the production of toys, play blocks or toys for infants and children, but also applied as a skin material covering the surface of the product made of synthetic resin material to apply the effect of Hanji It can be applied to a wide range of fields such as automobile interiors and home interior products.In particular, it can minimize or eliminate the adverse effects of environmental hormones emitted from synthetic resins, blocking direct contact with the human body and It can be very useful to protect.

이러한 본 발명에 의한 제조방법 및 이에 의해 제조되는 한지성형물과 한지성형물품은 닥나무를 사용하므로 자연친화적이면서 친환경성을 갖는다 할 것이며, 일정 강도 및 견고함을 유지하게 되며, 한지특유의 질감이 부여되므로 부드럽고 포근한 느낌과 정서적인 안정감을 제공할 수 있다.The manufacturing method according to the present invention and the Hanji molded article and the Hanji molded article produced by it will have a nature-friendly and eco-friendly because of the use of the mulberry, it will maintain a certain strength and robustness, so that the unique texture of Hanji It can provide a soft, cozy feeling and emotional stability.

이상에서 설명한 것은 본 발명을 실시하기 위한 하나의 실시 예에 불과한 것 으로서, 본 발명은 상기한 실시 예에 한정되지 않고, 이하 특허청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 누구든지 다양한 변경 실시가 가능한 범위까지 본 발명의 기술적 사상이 미친다고 할 것이다.What has been described above is only one embodiment for carrying out the present invention, and the present invention is not limited to the above-described embodiment, and the present invention belongs without departing from the gist of the present invention as claimed in the following claims. Anyone with ordinary knowledge in the field will have the technical idea of the present invention to the extent that various modifications can be made.

상술한 바와 같이 본 발명에 의한 제조방법에 의하면, 한지의 느낌 및 효능을 발휘하는 성형물품을 제작할 수 있고 닥나무를 이용하므로 자연친화적이면서 친환경적인 제품을 만들 수 있으며, 각종 플라스틱제품에서 배출되는 환경호르몬의 영향력으로부터 인체를 보호할 수 있을 뿐만 아니라 각종 플라스틱제품을 대체할 수 있는 기술로서 한지와 같은 효능 및 느낌의 발휘는 물론 본 발명에 의해 제조되는 물품으로는 한지특유의 부드러움 및 포근함과 정서적인 안정의 유익함을 제공할 수 있다.As described above, according to the manufacturing method according to the present invention, it is possible to manufacture molded articles exhibiting the feeling and efficacy of Hanji, and by using the mulberry wood to create a nature-friendly and environmentally friendly products, environmental hormones emitted from various plastic products As a technology that can protect the human body from the influence of the human body as well as replace various plastic products, it exhibits the same efficacy and feel as the Korean paper, as well as the softness, warmth and emotional stability peculiar to the Korean paper. Can provide benefits.

또한, 본 발명은 인체에 무해한 다양한 색상의 표출이 가능하고 다양한 분야 및 제조물품에 폭넓게 적용하거나 응용하여 사용할 수 있는 범용성을 갖는 것이다.In addition, the present invention is capable of expressing a variety of colors harmless to the human body and has a versatility that can be widely applied or applied to various fields and manufactured articles.

Claims

Taking the peeled bark and removing the bark, putting the peeled bark into a cauldron, boiling, washing and tapping the boiled mulberry bark, the first step of performing known mulberry processing;

A second step of dissolving the mulberry on the bark of the first step to make it viscous and processing it into a mulberry fiber material containing moisture;

The third step of the step of inserting the doc fiber material of the second step into the molding mold of the upper mold and the lower mold having a predetermined shape, and then molding by a cold pressing molding having a three-dimensional shape by molding by thermocompression molding. Korean paper molding method using Doc fiber molding molding method.

A third step of inserting the Doc-fiber material of the second step into a molding mold of an upper mold and a lower mold having a predetermined shape, and then forming a three-dimensional Hanji molding die by molding by thermocompression molding;

Inserting the hanji mold into an injection mold for injection molding, and then injecting the synthetic resin in a molten state through an injection hole of the injection mold;

The method of manufacturing a Hanji molded article using the Doc-fiber molding molding method comprising the fifth step of molding the injected synthetic resin to complete the Hanji molded article in which the injection molding is integrally coupled to the inner surface of the Hanji molding die.

The method according to claim 1 or 2,

Hanji molded article manufacturing method using a Doc-fiber molding molding method characterized in that the surface of the Hanji molded article or Hanji molded article is configured to prevent the occurrence of Hanji fibers by applying oil.

The method of claim 3, wherein

The oil is a method for producing cold-water molded article using a doc fiber molding molding method characterized in that it is composed of any one selected from flax oil, walnut oil, camellia oil.

The method according to claim 1 or 2,

The mulberry fiber material is a standard that can float 5 ~ 6 sheets of mulberry fiber material of 200mm × 200mm × 1mm standard, the first process of mixing 35ml of mulberry in 2L of water, and mixing 120g of mulberry bark in 3L of water. The second step, the third step of making the mulberry fibers by mixing 120ml ~ 180ml of the water of the mulberry extract of the first step in the water containing the bark of the second step and the mulberry fiber of the third step 1 Korean paper molding method using a mulberry fiber molding molding method characterized in that it comprises a fourth step of making a mulberry fiber material by moistening the mulberry fiber in the garden with a water drain hole of ~ ~ 2mm size.

The method of claim 2,

The hanji molding die is a 0.2mm ~ 5mm thick paper manufacturing method using a doc fiber molding molding method, characterized in that formed.

delete