KR100541420B1 - a fiber inorganic heat-resistant composition and method of treating heat-resistant of the using - Google Patents

a fiber inorganic heat-resistant composition and method of treating heat-resistant of the using Download PDF

Info

Publication number
KR100541420B1
KR100541420B1 KR1020030041093A KR20030041093A KR100541420B1 KR 100541420 B1 KR100541420 B1 KR 100541420B1 KR 1020030041093 A KR1020030041093 A KR 1020030041093A KR 20030041093 A KR20030041093 A KR 20030041093A KR 100541420 B1 KR100541420 B1 KR 100541420B1
Authority
KR
South Korea
Prior art keywords
weight
flame retardant
fibers
composition
retardant composition
Prior art date
Application number
KR1020030041093A
Other languages
Korean (ko)
Other versions
KR20050000629A (en
Inventor
전인기
김종국
이승철
이익수
Original Assignee
주식회사 디피아이
엔브이에이치코리아(주)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 디피아이, 엔브이에이치코리아(주) filed Critical 주식회사 디피아이
Priority to KR1020030041093A priority Critical patent/KR100541420B1/en
Publication of KR20050000629A publication Critical patent/KR20050000629A/en
Application granted granted Critical
Publication of KR100541420B1 publication Critical patent/KR100541420B1/en

Abstract

섬유용 무기질 난연 처리제 조성물 및 이를 이용한 섬유의 난연 처리방법이 개시되어 있다. 상기 조성물은 알칼리 실리케이트 화합물 60 내지 85중량%, 에멀젼 평균입자경이 50 내지 250 nm 범위인 아크릴/스티렌 공중합체 보조수지 0.01 내지 10중량%, 표면장력 조정제 0.01 내지 3.0중량%, 기타 첨가제 0.05 내지 10중량% 및 물(H2O) 5 내지 40중량%을 포함하고 있다. 이러한 구성요소를 갖는 섬유용 난연 처리제 조성물은 외관상태, 저장안정성, 함침작업성 및 건조성이 양호할 뿐만 아니라, 각종 섬유 펠트의 난연 처리제로 사용될 수 있으며, 상기 조성물에 의해 난연 처리된 섬유 펠트는 우수한 난연성, 단열성, 흡음성 및 압축강도 등을 가지고 있다.An inorganic flame retardant composition for fibers and a flame retardant treatment method of fibers using the same are disclosed. The composition is 60 to 85% by weight of the alkali silicate compound, 0.01 to 10% by weight of the acrylic / styrene copolymer auxiliary resin in the emulsion average particle size range of 50 to 250 nm, 0.01 to 3.0% by weight surface tension modifier, 0.05 to 10% by weight of other additives % And 5 to 40% by weight of water (H 2 O). The flame retardant composition for fibers having such a component is not only good in appearance, storage stability, impregnation and dryness, but also can be used as a flame retardant for various fiber felts. It has excellent flame retardancy, heat insulation, sound absorption and compressive strength.

Description

섬유용 무기질 난연 처리제 조성물 및 이를 이용한 난연 처리방법{a fiber inorganic heat-resistant composition and method of treating heat-resistant of the using }Fiber inorganic heat-resistant composition and method of treating heat-resistant of the using}
본 발명은 섬유용 무기질 난연 처리제 조성물 및 이를 이용한 난연 처리방법에 관한 것으로서, 상세하게는 실리케이트 수지를 주성분으로 함유하며, 외관상태, 저장안정성, 함침작업성, 건조성이 양호하고 함침 처리된 섬유 펠트의 난연성, 단열성, 흡음성 및 압축강도를 증가시키는 섬유용 무기질 난연 처리제 조성물 및 이를 이용한 섬유의 난연 처리방법에 관한 것이다.The present invention relates to an inorganic flame retardant composition for textiles and a flame retardant treatment method using the same, and in particular, silicate resin as a main component, appearance condition, storage stability, impregnation workability, good dryness and impregnated fiber felt The present invention relates to an inorganic flame retardant composition for fibers that increases the flame retardancy, heat insulation, sound absorption and compressive strength of the fiber, and to a flame retardant treatment method of fibers using the same.
종래에 있어서 패널형태의 건축용 자재나 산업용 자재의 내장재 또는 충진재로는 스티로폼, 유리섬유, 암면 등이 주로 사용되고 있으나, 스티로폼의 경우에는 가연성 재료이기 때문에 화재 위험으로부터 매우 취약하다는 단점을 갖고 있다. 또한 이런 물질들은 제조단계에서 환경 공해를 심하게 유발할 뿐만 아니라 폐기하려고 하는 경우에도 자연 부식이 곤란하기 때문에 폐기 비용이 많이 소요되는 문제점이 있으므로 그 사용이 사회적으로 규제되고 있는 추세이다.Conventionally, styrofoam, glass fiber, rock wool, etc. are mainly used as interior materials or filling materials for panel-type building materials or industrial materials. However, styrofoam is a flammable material, which is very vulnerable to fire hazard. In addition, these materials are not only causing serious environmental pollution at the manufacturing stage, but also natural waste is difficult even when trying to dispose, which is a problem that takes a lot of disposal costs, so the use is socially regulated.
이런 내장재 또는 충진재를 대체하기 위한 대안으로, 각종 섬유를 적층하여 만든 섬유 펠트는 단열효과와 흡음 효과를 갖고 있기 때문에 유용한 소재가 될 수 있다. 현재는 섬유 펠트를 그대로 사용하거나 또는 후 가공하여 산업용 단열재나 흡음재로 사용하고 있는데 이러한 섬유 펠트를 만들기 위한 섬유소재로는 열가소성 수지가 사용되고 있다. 여기서 상기 열가소성 수지 섬유로는 폴리에스터수지, 폴리프로필렌수지, 폴리에틸렌수지, 복합 폴리프로필렌수지 및 복합 폴리에틸렌수지, 나일론, 아크릴, 비닐론 등으로 이루어진 군으로부터 선택된 합성수지를 한 종류이상 포함하고 있다. 또한, 섬유직물의 가공 공정에서 발생하는 산업폐기물인 단섬유의 경화체 혼합물이나 폐섬유의 경화체 혼합물을 포함할 수 있으며, 각종 섬유직물의 산업 폐기물인 면섬유, 천연섬유, 합성섬유의 가공공정에서 발생되는 산업폐기물을 포함할 수 있다. As an alternative to replacing such interior materials or fillers, fiber felt made by laminating various fibers may be a useful material because it has insulation and sound absorption effects. Currently, the fiber felt is used as it is or is processed after use as an industrial insulation or sound absorbing material. As a fiber material for making such a fiber felt, a thermoplastic resin is used. Here, the thermoplastic resin fibers include at least one synthetic resin selected from the group consisting of polyester resins, polypropylene resins, polyethylene resins, composite polypropylene resins and composite polyethylene resins, nylon, acrylic, vinylon, and the like. In addition, it may include a hardened body mixture of short fibers, which is an industrial waste generated in the processing of textile fabrics, or a hardened body mixture of waste fibers, and may be produced in the processing of cotton fibers, natural fibers, and synthetic fibers, which are industrial wastes of various textile fabrics. May contain industrial waste.
그러나, 상술한 물질로 형성된 섬유 펠트는 쉽게 인화 및 연소되는 고유 특성을 갖고 있기 때문에 상기 섬유 펠트는 천장용 보드나 벽용 보드와 같은 패널형태의 건축자재의 내장재용 또는 난연성을 요구하는 산업 자재용으로 응용할 수 없었다. 또한 건축자재로서의 압축강도도 부족하기 때문에 기존의 섬유 펠트를 그대로 응용할 수 없는 문제점을 가지고 있다.However, since the fiber felt formed from the above-mentioned materials has inherent properties of being easily ignited and burned, the fiber felt is used for interior materials of panel-type building materials such as ceiling boards and wall boards or for industrial materials requiring flame retardancy. Could not apply. In addition, the lack of compressive strength as a building material has a problem that can not be applied to the existing fiber felt as it is.
상술한 문제점을 해결하기 위한 본 발명의 제1목적은 섬유 펠트의 난연 처리 및 압축 강도를 보강시킬 수 있는 섬유용 무기질 난연 처리제 조성물을 제공하는 데 있다.A first object of the present invention for solving the above problems is to provide an inorganic flame retardant composition for fibers that can reinforce the flame retardant treatment and compressive strength of the fiber felt.
또한, 본 발명의 제2목적은 상기 난연 처리제 조성물을 적용하여 각종 섬유 소재로 형성된 섬유 펠트의 장점은 그대로 유지하면서 난연성과 압축 강도 보강효과를 부여시키기 위한 섬유 펠트의 난연 처리 방법을 제공하는데 있다.In addition, a second object of the present invention is to provide a flame retardant treatment method for imparting flame retardancy and compressive strength reinforcement effect while maintaining the advantages of the fiber felt formed of various fiber materials by applying the flame retardant treatment composition.
상술한 본 발명의 제1목적을 달성하기 위한 섬유용 무기질 난연 처리제 조성물은,The inorganic flame retardant composition for fibers to achieve the first object of the present invention described above,
알칼리 실리케이트 화합물 60 내지 85중량%, 에멀젼 평균입자경이 50 내지 250nm 범위인 아크릴/스티렌 공중합체 보조수지 0.01 내지 10중량%, 표면장력 조정제 0.01 내지 3.0중량%, 기타 첨가제 0.05 내지 10중량% 및 물(H2O) 5 내지 40중량%를 포함하고 있다. 60 to 85% by weight of the alkali silicate compound, 0.01 to 10% by weight of the acrylic / styrene copolymer auxiliary resin having an average particle diameter in the range of 50 to 250 nm, 0.01 to 3.0% by weight of the surface tension modifier, 0.05 to 10% by weight of other additives and water ( H 2 O) 5 to 40% by weight.
또한, 본 발명의 제2목적을 달성하기 위한 섬유의 난연 처리방법은,In addition, the flame retardant treatment method of the fiber for achieving the second object of the present invention,
알칼리 실리케이트 화합물 60 내지 85중량%, 에멀젼 평균입자경이 50 내지 250nm 범위인 아크릴/스티렌 공중합체 보조수지 0.01 내지 10중량%, 표면장력 조정제 0.01 내지 3.0중량%, 기타 첨가제 0.05 내지 10중량% 및 물(H2O) 5 내지 40중량%를 포함하는 섬유용 무기질 난연 처리제 조성물 형성한다.60 to 85% by weight of the alkali silicate compound, 0.01 to 10% by weight of the acrylic / styrene copolymer auxiliary resin having an average particle diameter in the range of 50 to 250 nm, 0.01 to 3.0% by weight of the surface tension modifier, 0.05 to 10% by weight of other additives and water ( H 2 O) to form an inorganic flame retardant composition for fibers comprising 5 to 40% by weight.
이어서, 상기 섬유용 무기질 난연 처리제 조성물을 섬유 펠트 소지에 섬유 펠트대 조성물 고형분의 중량비율이 1:0.1 내지 1:0.5 가 되도록 함침시킨 이후에 상기 조성물에 함침된 섬유 펠트를 건조하는 단계를 포함하고 있다.Subsequently, after impregnating the inorganic fiber-based flame retardant composition for the fiber felt so that the weight ratio of the fiber felt to the composition solids is 1: 0.1 to 1: 0.5, and drying the fiber felt impregnated in the composition; have.
따라서, 본 발명의 섬유용 난연 처리제 조성물은 섬유 펠트에 적용시 난연 처리제의 외관상태, 저장안정성, 함침작업성 및 건조성 등이 양호할 뿐만 아니라 섬유 펠트의 난연성, 단열성, 흡음성 및 압축강도 등을 향상시키는 효과를 가지고 있다. Therefore, the flame retardant composition for the fiber of the present invention is not only good in appearance, storage stability, impregnation workability and dryness of the flame retardant when applied to the fiber felt, but also improves the flame retardancy, heat insulation, sound absorption and compressive strength of the fiber felt. It has the effect of improving.
이하, 본 발명을 더욱 상세히 설명하기로 한다.Hereinafter, the present invention will be described in more detail.
섬유용 무기질 난연 처리제 조성물Inorganic flame retardant composition for textiles
본 발명의 섬유용 무기질 난연 처리제 조성물은 각종 섬유재질로 형성된 섬유 펠트의 난연성, 단열성, 흡음성 및 압축강도 등을 향상시키기 위한 조성물로서, 알칼리 실리케이트 화합물 60 내지 85중량%, 에멀젼 평균입자경이 50 내지 250 nm 범위인 아크릴/스티렌 공중합체 보조수지 0.01 내지 10중량%, 표면장력 조정제 0.01 내지 3.0중량%, 기타 첨가제 0.05 내지 10중량% 및 물(H2O) 5 내지 40중량%를 포함하고 있다.The inorganic flame retardant composition for fibers of the present invention is a composition for improving the flame retardancy, heat insulation, sound absorption, compressive strength, etc. of fiber felt formed of various fiber materials, alkali silicate compound 60 to 85% by weight, emulsion average particle size of 50 to 250 0.01 to 10% by weight of acrylic / styrene copolymer auxiliary resin in the nm range, 0.01 to 3.0% by weight surface tension modifier, 0.05 to 10% by weight of other additives and 5 to 40% by weight of water (H 2 O).
본 발명의 난연 처리제 조성물에 포함되는 제1성분으로서는 알칼리 실리케이트 수지를 들 수 있는데, 상기 알칼리 실리케이트 화합물은 변성소디움 실리케이트 수지, 포타시움 실리케이트 수지 또는 변성소디움 실리케이트 수지와 포타시움 실리케이트 수지 혼합물(혼합비율 변성소디움실리케이트 수지: 포타시움실리케이트=100:0 ~ 0:100) 중에서 선택된 하나가 사용된다.Examples of the first component included in the flame retardant treatment composition of the present invention include alkali silicate resins, and the alkali silicate compound may be a modified sodium silicate resin, a potassium silicate resin, or a modified sodium silicate resin and a potassium silicate resin mixture (mixed ratio modified sodium silicate). Resin: potassium silicate = 100: 0 to 0: 100).
상기 알칼리 실리케이트 화합물인 변성소디움 실리케이트 수지는 금속성분으로 변성되어 있으며, SiO2와 K2O의 몰비(Molecular Ratio)가 3.2 내지 4.5 범위이고, 고형분 함량이 30 내지 40중량%의 범위를 갖는 것이 사용된다. 바람직하게는 SiO2와 K2O의 몰비가 3.3 내지 4.2 범위이고, SiO2의 함량이 22 내지 28중량%의 범위 를 갖는 변성소디움 실리케이트 수지가 사용된다. The modified silicate silicate resin, which is the alkali silicate compound, is modified with a metal component, and has a molar ratio of SiO 2 to K 2 O in a range of 3.2 to 4.5 and a solid content of 30 to 40% by weight. do. Preferably, a modified sodium silicate resin having a molar ratio of SiO 2 to K 2 O in the range of 3.3 to 4.2 and a content of SiO 2 in the range of 22 to 28% by weight is used.
또한, 상기 포타시움실리케이트 수지는 SiO₂와 K2O의 몰비(Molecular Ratio)가 2.6 내지 4.0 범위를 갖고, 고형분 함량이 26 내지 34중량%인 것이 사용된다. 바람직하게는 SiO₂와 K2O의 몰비가 3.0 내지 3.2 이고, 고형분 함량이 28 내지 32중량%의 범위를 갖는 포타시움실리케이트 수지가 사용된다.In addition, the potassium silicate resin has a molar ratio of SiO 2 to K 2 O (Molecular Ratio) of 2.6 to 4.0, a solid content of 26 to 34% by weight is used. Preferably, a potassium silicate resin having a molar ratio of SiO 2 to K 2 O of 3.0 to 3.2 and a solid content of 28 to 32% by weight is used.
여기서, 상기 섬유용 난연 처리제 조성물을 형성하기 위해 사용되는 원료들 중 상술한 알칼리 실리케이트 화합물(Alkali Silicate Compound)의 사용량이 60중량% 미만이면, 난연성과 단열성 등이 현저히 저하되는 등 난연 처리제로서의 효과가 미흡하기 때문에 바람직하지 않고, 85%중량을 초과하여 사용하면, 섬유펠트를 함침시키는 작업성이 떨어지기 때문에 바람직하지 않다.Here, when the amount of the above-mentioned alkali silicate compound (Alkali Silicate Compound) of the raw materials used to form the flame retardant treatment agent composition for the fiber is less than 60% by weight, the effect as a flame retardant such as significantly reduced flame retardancy, heat insulation, etc. It is not preferable because it is insufficient, and if it is used in excess of 85% by weight, the workability of impregnating fiber felt is inferior.
따라서, 상기 섬유용 난연 처리제 조성물을 형성하기 위해 사용되는 상기 알칼리 실리케이트 화합물은 60 내지 85중량% 범위 내에서 사용해야 하며, 바람직하게는 70 내지 85중량% 범위 내에서 사용해야 한다.Therefore, the alkali silicate compound used to form the flame retardant composition for fibers should be used in the range of 60 to 85% by weight, preferably in the range of 70 to 85% by weight.
본 발명의 난연 처리제 조성물에 포함되는 제2성분으로서는 보조수지가 있다. 상기 보조수지로 사용되는 수성 에멀젼 수지는 실리케이트수지에 사용 가능하도록 고안된 부틸아크릴/스티렌 공중합체로서, 고형분 함량이 48 내지 52중량%, 에멀젼 평균입자크기가 50 내지 250nm범위를 갖고, 최저도막형성온도(MFFT, Minimum Film Forming Temperature)가 -5내지 10℃인 부틸아크릴/스티렌 공중합체가 사용된다.As the second component contained in the flame retardant composition of the present invention, there is an auxiliary resin. The aqueous emulsion resin used as the auxiliary resin is a butylacryl / styrene copolymer designed to be used in the silicate resin, having a solid content of 48 to 52% by weight, an emulsion average particle size of 50 to 250 nm, and a minimum film forming temperature. A butylacryl / styrene copolymer having a minimum film forming temperature (MFFT) of -5 to 10 ° C is used.
일반적인 아크릴 공중합체는 포타시움 실리케이트 또는 변성소디움 실리케이트와 서로 상용성이 부족하여 쉽게 섞이지 않는 반면에 이렇게 제조된 공중합체는 포타시움 실리케이트 및 변성소디움 실리케이트와 상용성이 매우 양호하기 때문에 이와 용이하게 혼합될 수 있다. 이 경우, 후술하는 기타 첨가제를 적용하면 알칼리 실리케이트 화합물의 상용성이 더욱 우수해지는 효과를 얻을 수 있다.Typical acrylic copolymers are not easily mixed with potassium silicate or modified sodium silicate, and thus are not easily mixed with each other, whereas copolymers prepared in this way can be easily mixed with potassium silicate and modified sodium silicate because they are very compatible. . In this case, the application of the other additives described later can obtain the effect of further improving the compatibility of the alkali silicate compound.
여기서, 상기 섬유용 난연 처리제 조성물을 형성하기 위해 사용되는 보조 수지의 사용량이 0.01중량% 미만이면, 에멀젼의 효과가 미미하게 나타나기 때문에 바람직하지 않고, 10중량%을 초과하여 사용하면, 난연성, 단열성 등의 성능이 현저히 저하되기 때문에 바람직하지 않다.Here, if the amount of the auxiliary resin used to form the flame retardant composition for the fiber is less than 0.01% by weight, the effect of the emulsion is shown to be insignificant, and when used in excess of 10% by weight, flame retardancy, heat insulation, etc. It is not preferable because its performance is significantly lowered.
따라서, 상기 섬유용 난연 처리제 조성물을 형성하기 위해 사용되는 보조수지 0.01 내지 10중량% 범위 내에서 사용해야 하며, 바람직하게는 0.5 내지 5중량% 범위 내에서 사용해야 한다.Therefore, the auxiliary resin used to form the flame retardant treatment composition for fibers should be used in the range of 0.01 to 10% by weight, preferably in the range of 0.5 to 5% by weight.
본 발명의 난연 처리제 조성물에 포함되는 제3성분으로서는 표면장력 조정제를 들 수 있다. 상기 표면장력 조정제는 폴리에테르변성실록산공중합체, 비이온유기계면활성제, 폴리카르보닉산염용액, 불소변성폴리아크릴레이트, 소디움폴리아크릴레이트등이 적용된다.As a 3rd component contained in the flame-retardant composition of this invention, a surface tension regulator is mentioned. The surface tension modifiers include polyether modified siloxane copolymers, nonionic organic surfactants, polycarbonate salt solutions, fluorine modified polyacrylates, sodium polyacrylates, and the like.
여기서, 상기 섬유용 난연 처리제 조성물을 형성하기 위해 사용되는 표면장력 조정제가 0.01중량% 미만이면, 표면장력을 떨어뜨리는 효과가 미흡하기 때문에 바람직하지 않고, 3중량%을 초과하여 사용하면, 표면장력을 떨어뜨리는 효과는 증가하지 않고 비용만 상승하기 때문에 바람직하지 않다.Here, when the surface tension modifier used to form the flame retardant treatment agent composition for fibers is less than 0.01% by weight, the effect of lowering the surface tension is insufficient, and when used in excess of 3% by weight, the surface tension is increased. The dropping effect is not preferable because only the cost rises without increasing.
따라서, 상기 섬유용 난연 처리제 조성물을 형성하기 위해 사용되는 표면장력 조정제는 0.01 내지 3중량% 범위 내에서 사용해야 하며, 바람직하게는 0.1 내지 2중량% 범위 내에서 사용해야 한다.Therefore, the surface tension modifier used to form the flame retardant treatment composition for fibers should be used in the range of 0.01 to 3% by weight, preferably in the range of 0.1 to 2% by weight.
본 발명의 난연 처리제 조성물을 형성하기 위해 포함되는 제4성분으로서는 기타 첨가제를 들 수 있다As the fourth component included to form the flame retardant composition of the present invention, other additives may be mentioned.
상기 기타 첨가제로는 안정제, 발수제 ,살균제, 소포제, 동결방지제 등이 사용되며, 바람직하게는 상기 그룹 중에서 선택된 적어도 2개의 물질이 적용된다.As the other additives, stabilizers, water repellents, disinfectants, antifoams, cryoprotectants, and the like are used, and preferably at least two substances selected from the group are applied.
상기 기타 첨가제 중에서 안정제로서는 조성물 100중량%를 기준으로 0.01 내지 3.0중량%의 범위를 갖는 쿼터너리암모니움 용액을 사용하고, 바람직하게는 0.05 내지 2중량%의 범위를 갖는 안정제를 사용한다.Among the other additives, as a stabilizer, a quaternary ammonium solution having a range of 0.01 to 3.0% by weight based on 100% by weight of the composition is used, and a stabilizer having a range of 0.05 to 2% by weight is preferably used.
상기 발수제로는 조성물 100중량%를 기준으로 0.01 내지 3.0중량%의 범위를 갖는 폴리실록산에멀젼을 사용하고, 바람직하게는 0.05 내지 2중량%의 범위를 갖는 발수제를 사용한다. The water repellent is a polysiloxane emulsion having a range of 0.01 to 3.0% by weight based on 100% by weight of the composition, preferably a water repellent having a range of 0.05 to 2% by weight.
상기 살균제로는 조성물 100중량%를 기준으로 0.01 내지 2.0중량%의 범위를 갖는 티아졸계 화합물을 사용하고, 바람직하게는 0.02 내지 1중량%의 범위를 갖는 살균제가 사용된다. As the fungicide, a thiazole compound having a range of 0.01 to 2.0% by weight based on 100% by weight of the composition is used, and a fungicide having a range of 0.02 to 1% by weight is preferably used.
상기 동결방지제로는 조성물 100중량%를 기준으로 0.01 내지 3.0중량%의 범위를 갖는 글리콜을 사용하고, 바람직하게는 0.02 내지 2중량%의 범위를 갖는 동결방지제를 사용한다.The cryoprotectant is a glycol having a range of 0.01 to 3.0% by weight based on 100% by weight of the composition, preferably a cryoprotectant having a range of 0.02 to 2% by weight.
상기 소포제로는 조성물의 중량%를 기준으로 0.01 내지 2중량%의 범위를 폴 리에테르 변성실록산 공중합체를 사용하고, 바람직하게는 0.02 내지 1.5중량%의 범위를 갖는 소포제를 사용한다.The antifoaming agent is a polyether-modified siloxane copolymer in the range of 0.01 to 2% by weight based on the weight% of the composition, preferably an antifoaming agent having a range of 0.02 to 1.5% by weight.
또한, 본 발명의 난연 처리제 조성물을 형성하기 위해 포함되는 제5성분으로서는 물(H2O)을 들 수 있다Further, as a fifth component included in order to form the flame retardation processing agent composition of the present invention may include water (H 2 O)
여기서, 상기 섬유용 난연 처리제 조성물을 형성하기 위해 사용되는 물의 사용량이 5중량% 미만이면, 난연 처리제의 점도가 너무 높아서 함침작업하기에 적당하지 못하기 때문에 바람직하지 않고, 40중량%를 초과하여 사용하면, 함침작업에 따른 함침효율이 적당하지 못하기 때문에 바람직하지 않다.Here, if the amount of water used to form the flame retardant composition for the fiber is less than 5% by weight, the viscosity of the flame retardant is too high, which is not suitable for impregnation work, and is used in excess of 40% by weight. This is not preferable because the impregnation efficiency due to the impregnation operation is not suitable.
따라서, 상기 섬유용 난연 처리제 조성물을 형성하기 위해 사용되는 물은 5 내지 40중량% 범위 내에서 사용해야 하며, 바람직하게는 10 내지 30중량% 범위 내에서 사용해야 한다.Therefore, the water used to form the flame retardant composition for the fiber should be used in the range of 5 to 40% by weight, preferably in the range of 10 to 30% by weight.
섬유 펠트의 난연 처리방법Flame retardant treatment method of fiber felt
섬유용 무기질 난연 처리제 조성물에 의해 난연 처리된 섬유 펠트 제조방법은 먼저, 알칼리 실리케이트 화합물(변성소디움실리케이트 수지 또는 포타시움실리케이트 수지 또는 변성소디움실리케이트 수지와 포타시움실리케이트 수지 혼합물) 60중량% 내지 85중량%, 에멀젼 평균입자경이 50 내지 250nm 범위를 갖는 아크릴/스티렌 공중합체 보조수지 0.01중량% 내지 10중량%, 표면장력 조정제 0.01중량% 내지 5.0중량% 기타 첨가제 0.05 내지 10중량% 및 물 5중량% 내지 40중량%를 포함하는 섬유용 무기질 난연 처리제 조성물을 형성한다. The method for producing a fiber felt flame-retarded by the inorganic flame retardant composition for fibers, firstly, an alkali silicate compound (modified sodium silicate resin or potassium silicate resin or modified sodium silicate resin and potassium silicate resin mixture), 60% by weight to 85% by weight, emulsion 0.01 wt% to 10 wt% of acrylic / styrene copolymer auxiliary resin having an average particle size in the range of 50 to 250 nm, 0.01 wt% to 5.0 wt% of surface tension modifier 0.05 wt% to 10 wt% of other additives, and 5 wt% to 40 wt% of water To form an inorganic flame retardant composition for fibers comprising a.
이어서, 상기 조성물을 각종 섬유소재로 만든 섬유 펠트 소지에 섬유 펠트에대한 조성물 고형분의 중량비율이 1:0.1 내지 1:0.5 가 되도록 함침시키는 단계 및 함침된 섬유 펠트를 건조하는 단계를 수행함으로서 난연 처리된 섬유 펠트를 제조할 수 있다.Subsequently, impregnating the composition into a fiber felt substrate made of various fiber materials such that the weight ratio of the composition solids to the fiber felt is 1: 0.1 to 1: 0.5, and drying the impregnated fiber felt. Fiber felt can be prepared.
여기서, 섬유용 무기질 난연 처리제 조성물을 형성하기 위해 적용되는 물질에 대해서는 위에서 상세히 설명하였기 때문에 생략하기로 한다.Here, since the material applied to form the inorganic flame retardant composition for fibers has been described in detail above, it will be omitted.
상기 섬유 펠트에 대한 조성물 고형분의 중량비율이 1:0.1 미만일 경우, 난연 처리제의 처리효과가 미흡하기 때문에 바람직하지 않고, 1:0.5를 초과하면, 난연성 ,단열성 등의 성능이 필요이상으로 증가하면서 밀도가 급격히 증가하여 취급하는데 적당하지 않기 때문에 바람직하지 않다. If the weight ratio of the composition solid content to the fiber felt is less than 1: 0.1, the treatment effect of the flame retardant treatment agent is insufficient, and if it exceeds 1: 0.5, the density of flame retardancy, insulation, etc. increases more than necessary, and the density is more than necessary. Is not preferable because is rapidly increased and is not suitable for handling.
따라서, 상기 섬유용 난연 처리제 조성물을 이용한 섬유의 난연 처리 방법은 섬유 펠트에 대한 조성물의 고형분 중량비율이 1:0.1 내지 1:0.5가 되도록 함침시켜야 하며, 바람직하게는 1:0.1 내지 1:0.45의 범위 내에서 사용해야 한다.Therefore, the flame retardant treatment method of the fiber using the flame retardant treatment composition for fibers should be impregnated so that the solid content weight ratio of the composition to the fiber felt is 1: 0.1 to 1: 0.5, preferably 1: 0.1 to 1: 0.45 Must be used within range
여기서, 본 발명의 발명 기술로 제조되는 섬유용 무기질 난연 처리제의 외관, 저장안정성, 함침 작업성 및 건조성과 함침처리된 섬유 펠트의 난연성, 단열성, 흡음성 및 압축강도 등을 이하의 실시예로서 더욱 상세히 설명하는바, 본 발명의 범위가 이들 실시예에 국한되는 것이 아니다. Here, the appearance, storage stability, impregnation workability and dryness of the inorganic inorganic flame retardant for textiles produced by the inventive technique of the present invention, flame retardancy, heat insulation, sound absorption and compressive strength of the impregnated fiber felt are described in more detail below. As will be described, the scope of the present invention is not limited to these examples.
실시예 1Example 1
변성소디움 실리케이트 수지 70.5중량%에 아크릴/스티렌 공중합체 보조수지(Acronal S-559, 바스프) 0.8중량%, 표면장력 조정제(Tego Wet KL-245, 티고) 1.0중량%, 안정제(Betolinquart -25, 웰너시리카트) 0.1중량%, 발수제(Tego Phobe 1400, 티고) 0.4중량%, 물 27.0중량%를 투입하여 균일한 용액상태를 갖는가를 확인한 다음 살균제(Sky-Bio B-95, SK케미칼) 0.1중량%, 소포제(Tego Foamex 810, 티고) 0.1중량%를 투입하여 균일한 상태가 될 때까지 혼합한 다음에 여과 포장함으로써 초기점도가 11초(Fordcup #4), 고형분 함량이 26 중량%인 섬유용 무기질 난연 처리제 조성물을 제조하였다.70.5 wt% of modified sodium silicate resin, 0.8 wt% of acrylic / styrene copolymer auxiliary resin (Acronal S-559, BASF), 1.0 wt% of surface tension modifier (Tego Wet KL-245, Tigo), stabilizer (Betolinquart -25, welder Sirikat) 0.1% by weight, water repellent (Tego Phobe 1400, Tigo), 0.4% by weight, water 27.0% by weight to check whether a uniform solution state and then disinfectant (Sky-Bio B-95, SK chemical) 0.1% by weight , 0.1% by weight of antifoaming agent (Tego Foamex 810, Tigo), mixed until uniform, and then filtered and packaged.Inorganic fiber for fiber with an initial viscosity of 11 seconds (Fordcup # 4) and a solid content of 26% by weight A flame retardant treatment composition was prepared.
실시예 2Example 2
포타시움실리케이트 수지 84.5중량%에 아크릴/스티렌 공중합체 보조수지(Acronal S-559, 바스프) 0.8중량%, 표면장력조정제(Tego Wet KL-245, 티고) 1.0중량%, 안정제(Betolinquart-25, 웰너시리카트) 0.1중량%, 발수제(Tego Phobe 1400, 티고) 0.4중량%, 물 13.0중량%를 투입하여 균일한 용액상태를 갖는가를 확인한 다음 살균제(Sky-Bio B-95, SK케미칼) 0.1중량%, 소포제(Tego Foamex 810, 티고) 0.1중량%를 투입하여 균일한 상태가 될 때까지 혼합한 다음에 여과 포장함으로써 초기점도가 13초(Fordcup #4), 고형분 함량이 32중량%인 섬유용 무기질 난연 처리제 조성물을 제조하였다.84.5% by weight of potassium silicate resin, 0.8% by weight of acrylic / styrene copolymer auxiliary resin (Acronal S-559, BASF), 1.0% by weight of surface tension modifier (Tego Wet KL-245, Tigo), stabilizer (Betolinquart-25, Wenner Siri) Cart) 0.1% by weight, water repellent (Tego Phobe 1400, Tigo) 0.4% by weight, 13.0% by weight of water to check whether a uniform solution state and then 0.1% by weight of disinfectant (Sky-Bio B-95, SK Chemical), 0.1 wt% of antifoaming agent (Tego Foamex 810, Tigo) was added and mixed until uniform, and then filtered and packaged.Inorganic flame retardant for fiber having an initial viscosity of 13 seconds (Fordcup # 4) and a solid content of 32 wt% Treating agent compositions were prepared.
실시예 3Example 3
변성소디움 실리케이트 수지 62.4중량%와 포타시움실리케이트 수지 11.1중량% 수지 혼합물에 아크릴/스티렌 공중합체 보조수지(Acronal S-559, 바스프) 0.8중량%, 표면장력조정제(Tego Wet KL-245, 티고) 1.0중량%, 안정제(Betolinquart -25, 웰너시리카트) 0.1중량%, 발수제(Tego Phobe 1400, 티고) 0.4중량%, 물 24.0중량%를 투입하여 균일한 용액상태를 갖는가를 확인한 다음 살균제(Sky-Bio B-95, SK케미칼) 0.1중량%, 소포제(Tego Foamex 810, 티고) 0.1중량%를 투입하여 균일한 상태가 될 때까지 혼합한 다음에 여과 포장함으로써 초기점도가 11초(Fordcup #4), 고형분 함량이 26중량%인 섬유용 무기질 난연 처리제 조성물을 제조하였다.62.4% by weight of modified sodium silicate resin and 11.1% by weight of potassium silicate resin, 0.8% by weight of acrylic / styrene copolymer auxiliary resin (Acronal S-559, BASF), 1.0 weight of surface tension modifier (Tego Wet KL-245, Tigo) %, Stabilizer (Betolinquart -25, Welner silicate) 0.1% by weight, water repellent (Tego Phobe 1400, Tigo) by adding 0.4% by weight, water 24.0% by weight to check whether a uniform solution state and then disinfectant (Sky-Bio B -95, SK Chemicals) 0.1% by weight, 0.1% by weight of antifoaming agent (Tego Foamex 810, Tigo) was added and mixed until uniform, followed by filtration and packaging for an initial viscosity of 11 seconds (Fordcup # 4), solid content An inorganic flame retardant composition for fibers having a content of 26 wt% was prepared.
비교예 1Comparative Example 1
실시예 1과 동일한 방법으로 수행하되, 변성소디움실리케이트 수지 70.5중량%에 아크릴/스티렌 공중합체 보조수지(Acronal S-559, 바스프) 0.8중량%, 표면장력조정제(Tego Wet KL-245, 티고) 1.0중량%, 안정제(Betolinquart-25, 웰너시리카트) 0.1중량%, 발수제(Tego Phobe 1400, 티고) 0.4중량%, 물 27.0중량%를 사용하는 대신에 소디움실리케이트 수지 52.5중량%에 아크릴/스티렌 공중합체 보조수지(Acronal S-559, 바스프) 18.0중량%, 표면장력 조정제(Tego Wet KL-245, 티고) 1.0중량%, 안정제(Betolinquart-25, 웰너시리카트) 0.1중량%, 발수제(Tego Phobe 1400, 티고) 0.4중량%, 물 27.8중량%를 사용하여 초기점도가 13초(Fordcup #4), 고형분 함량이 31중량%인 섬유용 무기질 난연 처리제 조성물을 제조하였다.Performed in the same manner as in Example 1, 0.8% by weight of acrylic / styrene copolymer auxiliary resin (Acronal S-559, BASF) in modified sodium silicate resin 70.5% by weight, surface tension modifier (Tego Wet KL-245, Tigo) 1.0 Weight%, Stabilizer (Betolinquart-25, Welner silicate) 0.1% by weight, Water repellent (Tego Phobe 1400, Tigo), instead of using 0.4% by weight of water, 27.0% by weight of sodium silicate resin 52.5% by weight of acrylic / styrene copolymer Auxiliary resin (Acronal S-559, BASF) 18.0% by weight, surface tension modifier (Tego Wet KL-245, Tigo) 1.0% by weight, stabilizer (Betolinquart-25, Welner silicate) 0.1% by weight, water repellent (Tego Phobe 1400, Tigo) The inorganic flame retardant composition for fibers having an initial viscosity of 13 seconds (Fordcup # 4) and a solid content of 31% by weight was prepared using 0.4% by weight and 27.8% by weight of water.
비교예 2Comparative Example 2
실시예 1과 동일한 방법으로 수행하되, 변성소디움실리케이트 수지 70.5중량%에 아크릴/스티렌 공중합체 보조수지(Acronal S-559, 바스프) 0.8중량%, 표면장력조정제(Tego Wet KL-245, 티고) 1.0중량%, 안정제(Betolinquart-25, 웰너시리카트) 0.1중량%, 발수제(Tego Phobe 1400, 티고) 0.4중량%, 물 27.0중량%를 사용하는 대신에 포타시움실리케이트 수지 58.5중량%에 아크릴/스티렌 공중합체 보조수지(Acronal S-559, 바스프) 18중량%, 표면장력 조정제(Tego Wet KL-245, 티고) 1.0중량%, 안정제(Betolinquart-25, 웰너시리카트) 0.1중량%, 발수제(Tego Phobe 1400, 티고) 0.4중량%, 물 21.8중량%를 사용하여 초기점도가 13초(Fordcup #4), 고형분 함량이 31중량%인 섬유용 무기질 난연 처리제 조성물을 제조하였다.Performed in the same manner as in Example 1, 0.8% by weight of acrylic / styrene copolymer auxiliary resin (Acronal S-559, BASF) in modified sodium silicate resin 70.5% by weight, surface tension modifier (Tego Wet KL-245, Tigo) 1.0 Wt%, Stabilizer (Betolinquart-25, Welner silicate), 0.1% by weight, Water repellent (Tego Phobe 1400, Tigo), instead of using 0.4% by weight of water and 27.0% by weight instead of 57.0% by weight of the potassium silicate acrylic / styrene copolymer Auxiliary resin (Acronal S-559, BASF) 18% by weight, surface tension modifier (Tego Wet KL-245, Tigo) 1.0% by weight, stabilizer (Betolinquart-25, Welner silicate) 0.1% by weight, water repellent (Tego Phobe 1400, Tigo) The inorganic flame retardant composition for fibers having an initial viscosity of 13 seconds (Fordcup # 4) and a solid content of 31% by weight was prepared using 0.4% by weight and 21.8% by weight of water.
실험예 1Experimental Example 1
섬유 펠트에 본 발명의 실시예 1-3 및 비교예 1-2에서 제조한 조성물을 충분히 함침시키되, 섬유 펠트에 대한 조성물 고형분의 중량비율이 1:0.5 내지 1:0.1이 되도록 함침정도를 조정한 다음에 170℃ 건조기에서 20분 동안 건조시켜 난연 처리된 섬유 펠트를 제조하였다. 이렇게 제조된 것을 시험방법의 시편으로 사용하였다. The fiber felt was sufficiently impregnated with the compositions prepared in Examples 1-3 and Comparative Examples 1-2, but the degree of impregnation was adjusted so that the weight ratio of the composition solids to the fiber felt was 1: 0.5 to 1: 0.1. It was then dried in a 170 ℃ dryer for 20 minutes to prepare a flame retardant fiber felt. This prepared was used as a test specimen.
상기 실시예 및 비교예의 섬유용 무기질 난연 처리제 조성물에 대해서는 외관, 저장안정성, 함침 작업성 및 건조성 등을 평가하고, 상기 난연 처리제 조성물에 함침처리된 섬유 펠트에 대해서는 난연성, 단열성, 흡음성 및 압축강도 등을 시험 평가하였는데 각각의 시험방법을 하기 표 1에 개시하였다. The inorganic flame retardant composition for fibers of Examples and Comparative Examples was evaluated for appearance, storage stability, impregnation workability and dryness, and for the fiber felt impregnated with the flame retardant composition, flame retardancy, heat insulation, sound absorption and compressive strength were evaluated. The test was evaluated and each test method is shown in Table 1 below.
그리고, 상기 시험방법으로 나타나는 시험결과가 양호한 경우, 시험결과가 양호하지는 못하지만 사용 가능한 수준을 보통의 경우, 사용할 수 없는 수준을 불량의 경우로 구분하여 하기 표 2에 나타내었다. In addition, when the test result represented by the test method is good, the test result is not good, but the usable level is shown in Table 2 by dividing the unusable level into a normal case.
섬유용 무기질 난연 처리제 및 함침처리된 섬유 펠트의 시험방법Test method for inorganic flame retardant for fiber and impregnated fiber felt
구분division 시험방법Test Methods 양호한 경우If good
외관Exterior 난연처리제의 상태를 육안으로 확인 평가한다.Visually evaluate and evaluate the condition of the flame retardant. 이물질이 없고 균일한 상태인 경우When there is no foreign matter and it is uniform
저장안정성Storage stability 난연처리제를 40℃에서 7일간 보관한 후 점도와 초기점도와 초기점도를 비교하여 점도상승률로 평가한다.After the flame retardant was stored at 40 ° C. for 7 days, the viscosity and initial viscosity were compared and the initial viscosity was evaluated. 20% 미만인 경우Less than 20%
함침작업성Impregnation Workability 난연처리제로 섬유펠트로 함침처리한 다음에 그 상태를 전자현미경(800배)으로 관찰 평가한다.After impregnating with a fiber felt with a flame retardant, the state was observed and evaluated by an electron microscope (800 times). 난연처리제가 섬유사에 맺힘이 없이 균일하게 코팅되어 있는 경우When the flame retardant is uniformly coated without forming fibers
냄새smell 난연처리제를 함침작업하는 동안 냄새를 후각으로 평가한다.Odor is assessed by smell during flame impregnation. 눈과 코를 자극하는 심한 악취가 없는 경우No severe odor that irritates eyes and nose
건조성Dryness 함침하여 밀도를 조정한 섬유펠트를 170℃ 열풍순환식 oven을 이용하여 20분 건조시킨 후 외관을 평가한다.Impregnated fiber felt by impregnation was dried for 20 minutes using a 170 ℃ hot air circulation oven and the appearance was evaluated. 외관상태가 끈적거림이 없이 충분히 건조되어 있는 경우If the appearance is dry enough without stickiness
내곰팡이성Mildew Resistance KSM-5000(3431)-1990[도료의 내곰팡이성 시험방법]에 따라 곰팡이의 생성에 대한 저항성을 평가한다Evaluate the resistance to mold formation according to KSM-5000 (3431) -1990 [Testing method for mold resistance of paint] 피막의변색이나 변형이 거의 없는 경우(10등급)Almost no discoloration or deformation of the film (grade 10)
난연성Flame retardant KSF 2271-1998[건축물의 재장재료 및 구조의 난연성 시험방법]에 따라 시험 평가한다.The test shall be assessed in accordance with KSF 2271-1998 [Testing methods for flame retardancy of building materials and structures of buildings]. 난연 3급이상인 경우If flame retardant level 3 or higher
단열성Heat insulation KSF 2277-1985[주택용 단열재의 단열 성능시험방법]에 따라 열관류률(W/m2ㆍK)을 측정하여 평가한다.The thermal permeability (W / m 2 ㆍ K) is measured and evaluated according to KSF 2277-1985 [Insulation Performance Test Method of Insulation Material for Housing]. 1 이하인 경우1 or less
흡음성Sound absorption KSF 2805-1972[잔향실법의 흡음률의 측정방법]에 따라 흡음률을 측정하여 평가한다.The sound absorption rate is measured and evaluated according to KSF 2805-1972 [Method of measuring the sound absorption rate of the reverberation chamber method]. 2kHz에서 0.7이상인 경우 (시편 두께 40mm이상)0.7 or more at 2 kHz (40 mm or more of specimen thickness)
압축강도Compressive strength KSM 3831-1997[경질발포 플라스틱의 압축시험방법]에 따라 압축강도(kgf)를 측정한다.The compressive strength (kgf) is measured according to KSM 3831-1997 [Compression Test Method for Rigid Foam Plastics]. 1 이상인 경우1 or more
투습성Breathable KSF 2607-1996[건축재료의 투습성 측정방법]에 따라 투습계수(컵법,g/m2ㆍhㆍmmHg)를 측정하여 평가한다.The moisture permeability coefficient (Cup method, g / m 2 · h · mmHg) is measured and evaluated according to KSF 2607-1996 [Method of measuring moisture permeability of building materials]. 1 이하인 경우1 or less
섬유용 무기질 난연 처리제 및 함침처리된 섬유펠트의 시험평가 결과Test Evaluation Results of Inorganic Flame Retardant for Textiles and Fiber Felt Impregnated
구분division 실시예 1Example 1 실시예 2Example 2 실시예 3Example 3 비교예 1Comparative Example 1 비교예 2Comparative Example 2
외관Exterior 양호Good 양호Good 양호Good 양호Good 양호Good
저장안정성Storage stability 양호Good 양호Good 양호Good 불량Bad 불량Bad
함침작업성Impregnation Workability 양호Good 양호Good 양호Good 보통usually 보통usually
냄새smell 양호Good 양호Good 양호Good 보통usually 보통usually
건조성Dryness 양호Good 보통usually 양호Good 보통usually 보통usually
내곰팡이성Mildew Resistance 양호Good 양호Good 양호Good 보통usually 보통usually
난연성Flame retardant 양호Good 양호Good 양호Good 불량Bad 불량Bad
단열성Heat insulation 양호Good 양호Good 양호Good 불량Bad 불량Bad
흡음성Sound absorption 양호Good 양호Good 양호Good 보통usually 보통usually
압축강도Compressive strength 양호Good 양호Good 양호Good 불량Bad 불량Bad
투습성Breathable 양호Good 양호Good 양호Good 보통usually 보통usually
따라서, 이와 같은 본 발명의 섬유용 무기질 난연처리제 조성물은 알칼리 실리케이트 화합물에 적정량의 보조수지, 표면장력 조정제, 기타 첨가제 및 물을 혼합하여 제조됨으로서 외관상태, 저장안정성, 함침작업성 및 건조성 등이 양호한 특성을 가지고 있다.Therefore, the inorganic flame retardant composition for fibers of the present invention is prepared by mixing an appropriate amount of auxiliary resin, surface tension modifier, other additives and water in an alkali silicate compound, thereby improving appearance, storage stability, impregnation workability and dryness. It has good characteristics.
또한, 이러한 본 발명의 섬유용 무기질 난연 처리제 조성물에 함침처리된 각종 섬유 펠트는 우수한 난연성, 단열성, 흡음성 및 압축강도 등이 향상되는 효과를 얻을 수 있다. In addition, the various fiber felts impregnated in the inorganic flame retardant composition for fibers of the present invention can obtain the effect of improving the excellent flame retardancy, heat insulation, sound absorption and compressive strength.
상기에서는 본 발명의 바람직한 실시예를 참조하여 설명하였지만, 해당 기술 분야의 숙련된 당업자는 하기의 특허 청구의 범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다.Although described above with reference to a preferred embodiment of the present invention, those skilled in the art will be variously modified and changed within the scope of the invention without departing from the spirit and scope of the invention described in the claims below I can understand that you can.

Claims (9)

  1. 알칼리 실리케이트 화합물 60 내지 85중량%, 에멀젼 평균입자경이 50nm~250 nm 범위인 아크릴/스티렌 공중합체 보조수지 0.01 내지 10중량%, 표면장력 조정제 0.01 내지 3.0중량%, 기타 첨가제 0.05 내지 10중량% 및 물(H2O) 5 내지 40중량%를 포함하는 섬유용 무기질 난연 처리제 조성물.60 to 85% by weight of alkali silicate compound, 0.01 to 10% by weight of acrylic / styrene copolymer auxiliary resin with emulsion average particle size in the range of 50 nm to 250 nm, 0.01 to 3.0% by weight surface tension modifier, 0.05 to 10% by weight of other additives and water (H 2 O) Inorganic flame retardant composition for fibers comprising 5 to 40% by weight.
  2. 제1항에 있어서, 상기 알칼리 실리케이트 화합물은 변성소디움 실리케이트 수지, 포타시움 실리케이트 수지 또는 이들의 혼합물 중에서 선택된 하나인 것을 특징으로 하는 섬유용 무기질 난연 처리제 조성물. The inorganic flame retardant composition for fibers according to claim 1, wherein the alkali silicate compound is one selected from a modified sodium silicate resin, a potassium silicate resin, or a mixture thereof.
  3. 제2항에 있어서, 상기 변성소디움 실리케이트 수지는 금속성분으로 변성되어 있으며, SiO2와 K2O의 몰비(Molecular Ratio)가 3.2 내지 4.5 범위이고, 고형분 함량이 30중량 내지 40중량%인 것을 특징으로 하는 섬유용 무기질 난연 처리제 조성물.The method of claim 2, wherein the modified sodium silicate resin is modified with a metal component, the mole ratio of SiO 2 and K 2 O (Molecular Ratio) is in the range of 3.2 to 4.5, the solid content is 30 to 40% by weight An inorganic flame retardant composition for fibers.
  4. 제2항에 있어서, 상기 포타시움 실리케이트 수지는 SiO2와 K2O의 몰비(Molecular Ratio)가 2.6 내지 4.0 범위이고, 고형분 함량이 26 내지 34중량%인 것을 특징으로 하는 섬유용 무기질 난연 처리제 조성물.The inorganic flame retardant composition for fibers of claim 2, wherein the potassium silicate resin has a molar ratio of SiO 2 to K 2 O in the range of 2.6 to 4.0, and a solid content of 26 to 34% by weight.
  5. 제1항에 있어서, 상기 아크릴/스티렌 공중합체 보조 수지는 고형분 함량이 48 내지 52중량% 범위이고, 최저도막형성온도(MFFT, Minimum Film Forming Temperature)가 -5 내지 10℃ 범위인 것을 특징으로 하는 섬유용 무기질 난연 처리제 조성물.The method of claim 1, wherein the acrylic / styrene copolymer auxiliary resin has a solid content of 48 to 52% by weight, the minimum film forming temperature (MFFT, characterized in that the range of -5 to 10 ℃) Inorganic flame retardant composition for fibers.
  6. 제1항에 있어서, 상기 표면장력 조정제는 폴리에테르 변성실록산공중합체, 비이온유기계면활성제, 폴리카르보닉산염용액, 불소변성폴리아크릴레이트 및 소디움폴리아크릴레이트로 이루어진 그룹 중에서 선택된 하나인 것을 특징으로 하는 섬유용 무기질 난연 처리제 조성물.The method of claim 1, wherein the surface tension modifier is selected from the group consisting of polyether modified siloxane copolymer, nonionic organic surfactant, polycarbonate salt solution, fluorine modified polyacrylate and sodium polyacrylate. An inorganic flame retardant composition for fibers.
  7. 제1항에 있어서, 상기 기타 첨가제는 안정제, 발수제, 살균제, 소포제 및 동결방지제로 이루어진 그룹 중에서 선택된 적어도 2개의 물질을 포함하고 있는 것을 특징으로 하는 섬유용 무기질 난연 처리제 조성물 The inorganic flame retardant composition for textiles according to claim 1, wherein the other additives comprise at least two substances selected from the group consisting of stabilizers, water repellents, bactericides, antifoaming agents and antifreeze agents.
  8. 제7항에 있어서, 상기 안정제는 쿼터너리암모니움 용액이고, 상기 발수제는 폴리실록산에멀젼이고, 상기 살균제는 티아졸계 화합물이고, 상기 소포제는 폴리에테르변성실록산 공중합체이고, 상기 동결방지제는 글리콜인 것을 특징으로 하는 섬유용 무기질 난연 처리제 조성물.The method of claim 7, wherein the stabilizer is a quaternary ammonium solution, the water repellent is a polysiloxane emulsion, the fungicide is a thiazole-based compound, the antifoaming agent is a polyether-modified siloxane copolymer, the cryoprotectant is glycol An inorganic flame retardant composition for fibers.
  9. 알칼리 실리케이트 화합물 60 내지 85중량%, 에멀젼 평균입자경이 50 내지 250nm 범위인 아크릴/스티렌 공중합체 보조수지 0.01 내지 10중량%, 표면장력 조정제 0.01 내지 3.0중량%, 기타 첨가제 0.05 내지 10중량% 및 물(H2O) 5 내지 40중량% 균일하게 혼합하여 섬유용 무기질 난연 처리제 조성물 형성하는 단계;60 to 85% by weight of the alkali silicate compound, 0.01 to 10% by weight of the acrylic / styrene copolymer auxiliary resin having an average particle diameter in the range of 50 to 250 nm, 0.01 to 3.0% by weight of the surface tension modifier, 0.05 to 10% by weight of other additives and water ( H 2 O) uniformly mixing 5 to 40% by weight to form an inorganic flame retardant composition for fibers;
    상기 섬유용 무기질 난연 처리제 조성물을 섬유 소지에 섬유 소지에 대한 조성물 고형분의 중량비율이 1:0.1 내지 1:0.5 가 되도록 함침하는 단계: 및Impregnating the inorganic flame retardant composition for fibers to a fiber base such that the weight ratio of composition solids to fiber base is 1: 0.1 to 1: 0.5: and
    상기 조성물에 함침된 섬유 소지를 건조하는 단계를 포함하는 섬유의 난연 처리방법.Flame retardant treatment method of the fiber comprising the step of drying the fiber base impregnated in the composition.
KR1020030041093A 2003-06-24 2003-06-24 a fiber inorganic heat-resistant composition and method of treating heat-resistant of the using KR100541420B1 (en)