KR100516276B1 - Method for producing artificial leather with 3-dimension pattern - Google Patents

Method for producing artificial leather with 3-dimension pattern Download PDF

Info

Publication number
KR100516276B1
KR100516276B1 KR10-2002-0082262A KR20020082262A KR100516276B1 KR 100516276 B1 KR100516276 B1 KR 100516276B1 KR 20020082262 A KR20020082262 A KR 20020082262A KR 100516276 B1 KR100516276 B1 KR 100516276B1
Authority
KR
South Korea
Prior art keywords
pattern
leather
weight
parts
embossing
Prior art date
Application number
KR10-2002-0082262A
Other languages
Korean (ko)
Other versions
KR20040055846A (en
Inventor
류재승
배인기
김장태
노민섭
Original Assignee
(주)대우인터내셔널
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)대우인터내셔널 filed Critical (주)대우인터내셔널
Priority to KR10-2002-0082262A priority Critical patent/KR100516276B1/en
Publication of KR20040055846A publication Critical patent/KR20040055846A/en
Application granted granted Critical
Publication of KR100516276B1 publication Critical patent/KR100516276B1/en

Abstract

본 발명은 3차원 입체무늬를 가지는 인공피혁을 제조하는 방법에 관한 것으로, 본 발명은 베이스 피혁 표면에 그라비아인쇄 또는 전사인쇄를 하여 무늬인쇄층을 형성시키는 무늬인쇄공정, 상기 무늬인쇄된 베이스 피혁에 투명 또는 반투명 열가소성 시트를 합포하는 합포공정, 상기 합포된 베이스 피혁을 엠보싱하여 열가소성 시트에 미세한 엠보스를 형성시키는 엠보싱공정을 포함하거나, 베이스 피혁 표면에 그라비아인쇄 또는 전사인쇄를 하여 무늬인쇄층을 형성시키는 무늬인쇄공정, 이형지에 투명 또는 반투명한 피막용 합성수지 배합액을 1차로 도포한 후 가온 건조하여 경화시킨 다음, 상기 1차 경화된 이형지에 접착용 합성수지 배합액을 2차로 도포하는 합성수지 도포공정, 상기 접착용 합성수지 배합액이 도포된 이형지와 상기 무늬가 인쇄된 베이스 피혁을 서로 합포시킨 다음, 가온 건조하여 경화시키는 숙성공정, 상기 숙성된 베이스 피혁으로부터 이형지를 박리시키는 이형공정, 상기 이형지가 박리된 베이스 피혁을 엠보싱하여 미세한 엠보스를 형성시키는 엠보싱공정을 포함하여, 종래 인공피혁에서 낼 수 없었던 3차원적인 입체무늬를 가지는 인공피혁을 제공한다.The present invention relates to a method of manufacturing an artificial leather having a three-dimensional solid pattern, the present invention is a pattern printing process for forming a pattern printing layer by gravure printing or transfer printing on the surface of the base leather, the pattern printed base leather A step of encapsulating the transparent or translucent thermoplastic sheet, and an embossing step of embossing the combined base leather to form a fine emboss on the thermoplastic sheet, or forming a pattern printing layer by gravure printing or transfer printing on the surface of the base leather. A synthetic resin coating process of applying a transparent or semi-transparent film-forming synthetic resin composition to a release paper first, followed by heating and curing, followed by second application of the adhesive synthetic resin compound to the first cured release paper. Release paper coated with the adhesive synthetic resin compound and the pattern is printed A maturing process of combining the base leathers with each other, followed by heating and drying to cure, a release process of peeling off the release paper from the aged base leather, and an embossing process of embossing the base leather from which the release paper is peeled off to form fine embossing. It provides an artificial leather having a three-dimensional three-dimensional pattern that could not be produced in the conventional artificial leather.

Description

3차원 입체무늬를 가지는 인공피혁의 제조 방법{ METHOD FOR PRODUCING ARTIFICIAL LEATHER WITH 3-DIMENSION PATTERN}Manufacturing method of artificial leather having three-dimensional solid pattern {METHOD FOR PRODUCING ARTIFICIAL LEATHER WITH 3-DIMENSION PATTERN}
본 발명은 신발, 가방, 핸드백, 잡화, 가구 등에 사용되는 인공피혁 제조 방법에 관한 것으로, 특히 3차원 입체무늬를 가지는 인공피혁을 제조하는 방법에 관한 것이다.The present invention relates to a method of manufacturing artificial leather used in shoes, bags, handbags, sundries, furniture, and the like, and more particularly, to a method of manufacturing artificial leather having a three-dimensional solid pattern.
일반적으로 인공피혁은 부직포 등과 같은 원단에 합성수지를 코팅하여 제조하는 데, 코팅방법에는 습식법, 습건식법 등이 있다.In general, artificial leather is manufactured by coating a synthetic resin on a fabric such as a non-woven fabric, such as a wet method, a wet dry method.
먼저 습식법은 합성수지 함침액에 원단을 함침시켜 합성수지를 원단 내부에 침투시킨 다음 응고조에서 상기 합성수지를 응고시키고, 상기 응고된 함침포 위에 습식 은면코팅용 합성수지를 적당량 도포한 후 이를 다시 응고조에서 응고시키고, 상기 원단에 남아있는 잔여 용제를 수세한 후, 건조한 다음, 필요한 무늬를 인쇄하거나 음각과 양각으로 무늬가 새겨진 열이 있는 롤(roll)을 이용하여 압착시켜 필요한 색상과 무늬를 가진 인공피혁 표면에 형성시키게 된다.First, the wet method impregnates the synthetic resin impregnation with the fabric to infiltrate the synthetic resin inside the fabric, and then solidifies the synthetic resin in the coagulation bath, and after applying the appropriate amount of wet silver coating synthetic resin on the solidified impregnation cloth, it is solidified again in the coagulation bath The surface of the artificial leather having the required color and pattern is washed with water, and the remaining solvent remaining on the fabric is washed with water, dried, and then printed by printing the required pattern or by using a roll with a heat inscribed in an intaglio and an embossed pattern. To form.
그리고, 건식법은 이형지(Release Paper) 위에 건식 피막용 합성수지를 도포한 후 적정온도에서 가온 건조하여 경화시키고, 상기 경화된 이형지에 접착용 합성수지를 도포하고 습식법에 의해 제조되는 합성피혁 원단과 합포한 다음 가온 건조하여 이형지에 경화된 합성수지 피막과 원단을 접착시키고 나서 이형지(Release Paper)를 박리시켜 이형지(Release Paper)의 무늬를 인공피혁 표면으로 전이시켜 필요한 무늬를 형성시키게 된다.In the dry method, the synthetic resin for dry coating is applied on a release paper, and then dried by curing at an appropriate temperature. Then, the synthetic release resin is coated on the cured release paper, and then combined with a synthetic leather fabric prepared by a wet method. It is heated and dried to bond the cured synthetic resin film to the release paper, and then release the release paper (Release Paper) to transfer the pattern of the release paper (Release Paper) to the artificial leather surface to form the required pattern.
이러한 종래 인공피혁 제품은 인공피혁 표면에 롤러(roller)에 의해 엠보싱에 의한 무늬 내기 및 그라비아(gravure) 롤(roll)에 의한 무늬 내기 또는 이형지(release paper)에 의한 무늬 내기로 단순한 평면적인 무늬 또는 약간의 굴곡이 있는 정도의 무늬를 형성하게 된다.Such conventional artificial leather products have a simple flat pattern by patterning by embossing and patterning by gravure roll or patterning by release paper on the surface of artificial leather. There is a slight curvature pattern.
따라서 종래 방법으로는 인공피혁의 표면에 3차원(dimension)적인 입체 무늬를 형성시키지 못하는 문제점이 있다.Therefore, the conventional method has a problem that can not form a three-dimensional (three-dimensional) pattern on the surface of artificial leather.
이에 본 발명은 상술한 바와 같이 단순한 평면적인 무늬 또는 약간의 굴곡을 지닌 무늬만을 제공하는 종래 인공피혁의 문제점을 해결하여 3차원 입체무늬를 가지는 인공피혁을 제조하는 방법을 제공함에 그 목적이 있다.Accordingly, an object of the present invention is to provide a method of manufacturing an artificial leather having a three-dimensional three-dimensional pattern by solving the problems of the conventional artificial leather, which provides only a simple flat pattern or a pattern having a slight curvature as described above.
상기 목적을 달성하기 위한 본 발명의 3차원 입체무늬를 가지는 인공피혁 제조 방법은, 베이스 피혁 표면에 그라비아인쇄 또는 전사인쇄를 하여 무늬를 형성시키는 무늬인쇄공정, 상기 무늬인쇄된 베이스 피혁에 투명 또는 반투명 열가소성 시트를 합포하는 합포공정, 상기 합포된 베이스 피혁을 엠보싱하여 열가소성 시트에 미세한 엠보스를 형성시키는 엠보싱공정을 포함한다. Artificial leather manufacturing method having a three-dimensional solid pattern of the present invention for achieving the above object is a pattern printing process for forming a pattern by gravure printing or transfer printing on the surface of the base leather, transparent or translucent to the patterned base leather An encapsulation step of encapsulating the thermoplastic sheet, and an embossing step of embossing the encapsulated base leather to form fine embossment on the thermoplastic sheet.
상기 목적을 달성하기 위한 본 발명의 또 다른 3차원 입체무늬를 가지는 인공피혁 제조 방법은, 베이스 피혁 표면에 그라비아인쇄 또는 전사인쇄를 하여 무늬를 형성시키는 무늬인쇄공정, 이형지에 투명 또는 반투명한 피막용 합성수지 배합액을 1차로 도포한 후 가온 건조하여 경화시킨 다음, 상기 1차 경화된 이형지에 접착용 합성수지 배합액을 2차로 도포하는 합성수지 도포공정, 상기 접착용 합성수지 배합액이 도포된 이형지와 상기 무늬가 인쇄된 베이스 피혁을 서로 합포시킨 다음, 가온 건조하여 경화시키는 숙성공정, 상기 숙성된 베이스 피혁으로부터 이형지를 박리시키는 이형공정, 상기 이형지가 박리된 베이스 피혁을 엠보싱하여 미세한 엠보스를 형성시키는 엠보싱공정을 포함한다.Artificial leather manufacturing method having another three-dimensional three-dimensional pattern of the present invention for achieving the above object is a pattern printing process for forming a pattern by gravure printing or transfer printing on the surface of the base leather, for transparent or translucent coating on the release paper After applying the synthetic resin mixture first and then heating and curing, the synthetic resin coating step of applying the adhesive synthetic resin composition to the secondary cured release paper secondly, the release paper and the pattern coated with the adhesive synthetic resin mixture The embossed process of combining the printed base leathers with each other, followed by a maturing process of heating and drying to cure, a release process of peeling release paper from the aged base leather, and embossing the base leather from which the release paper was peeled off to form a fine embossing process. It includes.
이하 본 발명의 3차원 입체무늬를 가지는 인공피혁 제조 방법을 상세히 설명한다.Hereinafter will be described in detail the artificial leather manufacturing method having a three-dimensional solid pattern of the present invention.
도 1은 본 발명의 투명 또는 반투명 합성수지 시트를 이용한 3차원 입체무늬를 가지는 인공피혁 제조 공정도이다.1 is a manufacturing process of artificial leather having a three-dimensional solid pattern using a transparent or translucent synthetic resin sheet of the present invention.
도 2는 본 발명의 투명 또는 반투명 합성수지 시트를 이용한 인공피혁의 단면도이다.2 is a cross-sectional view of artificial leather using a transparent or translucent synthetic resin sheet of the present invention.
본 발명의 3차원 입체무늬를 가지는 인공피혁 제조 방법은, 베이스 피혁(1) 표면에 그라비아인쇄 또는 전사인쇄를 하여 무늬인쇄층(2)을 형성시키는 무늬인쇄공정, 상기 무늬인쇄된 베이스 피혁에 투명 또는 반투명 열가소성 시트(3)를 합포하는 합포공정, 상기 합포된 베이스 피혁을 엠보싱하여 열가소성 시트에 미세한 엠보스를 형성시키는 엠보싱공정을 포함한다.Artificial leather manufacturing method having a three-dimensional three-dimensional pattern of the present invention is a pattern printing step of forming a pattern printing layer (2) by gravure printing or transfer printing on the surface of the base leather (1), transparent to the pattern printed base leather Or an encapsulation step of encapsulating the translucent thermoplastic sheet 3, and an embossing step of embossing the encapsulated base leather to form fine embossment on the thermoplastic sheet.
상기 무늬인쇄공정에서 사용되는 베이스 피혁(1)은 종래 습식법 또는 습건식법 인공피혁 제조 방법에 의해 제조될 수 있다.The base leather 1 used in the pattern printing process may be manufactured by a conventional wet method or a wet-dry artificial leather manufacturing method.
습식법에 의한 베이스 피혁은 일반적으로 원단을 합성수지, 디메틸 포름 아미드 용제, 계면활성제 및 안료가 적정비로 이루어진 함침용 합성수지 배합액에 충분히 함침시킨 다음, 물이 담긴 응고조에 넣어 1차로 응고시키고, 인공피혁의 피막을 형성하기 위하여 상기 1차 응고된 원단에 과량의 합성수지, 소량의 디메틸 포름 아미드 용제, 계면활성제, 및 안료로 이루어진 습식 은면코팅용 폴리우레탄 배합액을 도포한 다음, 이를 다시 응고조에 넣어 2차로 응고시키고, 상기 2차 응고된 원단을 수세조에서 충분히 수세한 다음, 건조시켜 제조된다. 이러한 베이스 피혁은 필요한 용도에 따라 후처리되어 완제품이 된다.In general, the base leather by the wet method is sufficiently impregnated with a synthetic resin, a dimethyl formamide solvent, a surfactant and a pigment in an impregnated synthetic resin mixture consisting of a suitable ratio, and then solidified first in a coagulation bath containing water, In order to form a film, the wet solidified polyurethane coating solution comprising an excess of synthetic resin, a small amount of dimethyl formamide solvent, a surfactant, and a pigment was applied to the first solidified fabric, and then it was put into a coagulation bath again. It is prepared by coagulation, washing the secondary solidified fabric sufficiently in a washing tank, and then drying. These base leathers are post-treated according to the required use to become finished products.
습건식법에 의한 베이스 피혁은 이형지(release paper)에 건식 피막용 합성수지 배합액을 도포한 후 이를 건조시키고, 상기 건조된 이형지의 피막용 합성수지에 다른 종류의 접착용 합성수지 배합액을 도포한 다음 습식법에 의하여 제조된 베이스 피혁을 합포시킨 후 고온(약 70 내지 80℃)에서 숙성시킨 다음 이형지를 박리시켜 제조된다.The base leather by the wet-drying method is applied to the release paper (release paper) after coating the synthetic resin compound for dry film and dried it, and then coated with the synthetic resin compound for coating of the dried release paper different types of adhesive synthetic resin compound solution in the wet method After the base leather was prepared by aging and aged at a high temperature (about 70 to 80 ℃), it is prepared by peeling the release paper.
상기 무늬인쇄공정은 상기 습식 또는 습건식법에 의하여 제조된 베이스 피혁(1) 표면에 인쇄하고자 하는 무늬를 그라비아 인쇄 또는 전사 인쇄 방법으로 인쇄하여 인쇄층(2)을 형성시킨다. 상기 인쇄공정에 의하여 베이스 피혁 표면에는 미세한 도트(dot)형태의 무수히 많은 화소가 그려지게 된다.The pattern printing process forms a print layer 2 by printing a pattern to be printed on the surface of the base leather 1 manufactured by the wet or wet-dry method by a gravure printing or a transfer printing method. By the printing process, a myriad of pixels in the form of fine dots are drawn on the surface of the base leather.
또 상기 무늬인쇄공정은 베이스 피혁 표면에 엠보싱을 하여 양각과 음각의 굴곡을 형성시킨 후, 양각 부분에 그라비아인쇄 또는 전사인쇄를 하여 무늬를 형성시키는 것도 가능하다.In addition, the pattern printing process may be embossed on the surface of the base leather to form the embossed and intaglio bent, and then the gravure printing or the transfer printing may be formed on the embossed portion to form the pattern.
상기 합포공정에서 열가소성 시트(3)는 후술하는 엠보싱 공정에 의하여 만들어지는 엠보싱에 의하여 베이스 피혁에 인쇄된 무늬가 시트 표면에 투사되어 입체적으로 보이도록 하기 위하여 두께가 0.3mm 이상인 투명 또는 반투명한 합성수지 시트를 사용하는 것이 바람직하다. 상기 열가소성 시트(3)는 폴리 우레탄, 실리콘수지, 폴리 에틸렌 등 각종 열가소성 수지로 이루어지는 것이 가능하다.In the lamination process, the thermoplastic sheet 3 is a transparent or translucent synthetic resin sheet having a thickness of 0.3 mm or more so that the pattern printed on the base leather is projected on the surface of the sheet by embossing made by an embossing process to be described later. Preference is given to using. The thermoplastic sheet 3 may be made of various thermoplastic resins such as polyurethane, silicone resin, and polyethylene.
상기 엠보싱공정은 상기 열가소성 시트가 합포된 베이스 피혁을 100 내지 130℃온도에서 엠보싱 롤러를 이용하여 엠보싱하게 되면 열가소성 시트는 고온에 의하여 엠보싱 롤러의 모양대로 성형된다. 3차원적 입체무늬를 형성하기 위하여 엠보싱은 도 2에서 보이는 바와 같이 반구(hemisphere)형태로 성형되는 것이 바람직하고, 상기 무늬인쇄공정에서 인쇄된 미세한 도트(dot) 상층부에 반구(hemisphere)모양이 생기도록 열가소성 시트를 엠보싱하는 것이 바람직하다.In the embossing process, when the base leather in which the thermoplastic sheet is incorporated is embossed using an embossing roller at a temperature of 100 to 130 ° C., the thermoplastic sheet is molded in the shape of the embossing roller by a high temperature. In order to form a three-dimensional solid pattern, the embossing is preferably formed in a hemisphere shape as shown in FIG. 2, and a hemisphere shape is formed in the upper part of the fine dots printed in the pattern printing process. It is preferable to emboss the thermoplastic sheet so that it is.
상기 엠보싱공정에 의하여 형성된 엠보싱에 의하여 베이스 피혁의 인쇄무늬가 투명 열가소성 시트의 표면위로 확대되어 떠 있는 듯한 느낌의 3차원적 입체무늬를 가지게 된다.By the embossing formed by the embossing process, the printed pattern of the base leather is expanded on the surface of the transparent thermoplastic sheet to have a three-dimensional three-dimensional pattern with a feeling of floating.
도 3은 본 발명의 투명 또는 반투명한 피막용 합성수지 배합액을 이용한 3차원 입체무늬를 가지는 인공피혁 제조 공정도이다.Figure 3 is a manufacturing process of artificial leather having a three-dimensional solid pattern using a transparent or translucent film synthetic resin formulation of the present invention.
도 4는 본 발명의 투명 또는 반투명한 피막용 합성수지 배합액을 이용한 인공피혁의 단면도이다.Figure 4 is a cross-sectional view of artificial leather using a transparent or translucent coating synthetic resin formulation of the present invention.
본 발명의 또 다른 3차원 입체무늬를 가지는 인공피혁 제조 방법은, 베이스 피혁(1) 표면에 그라비아인쇄 또는 전사인쇄를 하여 무늬인쇄층(2)을 형성시키는 무늬인쇄공정, 이형지에 투명 또는 반투명한 피막용 합성수지 배합액을 1차로 도포한 후 가온 건조하여 경화시킨 다음, 상기 1차 경화된 이형지에 접착용 합성수지 배합액을 2차로 도포하는 합성수지 도포공정, 상기 접착용 합성수지 배합액이 도포된 이형지와 상기 무늬가 인쇄된 베이스 피혁을 서로 합포시킨 다음, 가온 건조하여 경화시키는 숙성공정, 상기 숙성된 베이스 피혁으로부터 이형지를 박리시키는 이형공정, 상기 이형지가 박리된 베이스 피혁을 엠보싱하여 미세한 엠보스를 형성시키는 엠보싱공정을 포함한다.Another method for manufacturing artificial leather having a three-dimensional three-dimensional pattern of the present invention is a pattern printing step of forming a pattern printing layer (2) by gravure printing or transfer printing on the surface of the base leather (1), transparent or translucent on the release paper After coating the synthetic resin compound for coating first and warming and curing, the synthetic resin coating step of applying the adhesive synthetic resin compound secondary to the first cured release paper, and the release paper coated with the adhesive synthetic resin compound After mating the pattern-printed base leather with each other, and then drying and curing by heating and drying, a release process for peeling release paper from the aged base leather, embossing the base leather peeled off the release paper to form a fine embossed Embossing process is included.
상기 피막용 합성수지 배합액의 성분비는 바람직하게는 아래와 같다.Preferably the component ratio of the synthetic resin compound for coating is as follows.
합성수지 100 중량부 100 parts by weight of synthetic resin
소수성 계면활성제 0 내지 10 중량부 0 to 10 parts by weight of hydrophobic surfactant
친수성 계면활성제 0 내지 10 중량부 0 to 10 parts by weight of hydrophilic surfactant
메틸 에틸 케톤 10 내지 60 중량부 10 to 60 parts by weight of methyl ethyl ketone
디메틸 포름 아미드 0 내지 50 중량부0-50 parts by weight of dimethyl formamide
상기 접착용 합성수지 배합액의 바람직한 성분비는 아래와 같다.The preferable component ratio of the said adhesive synthetic resin compound is as follows.
합성수지 100 중량부 100 parts by weight of synthetic resin
경화제 5 내지 20 중량부 5 to 20 parts by weight of curing agent
촉진제 0 내지 10 중량부 0 to 10 parts by weight of accelerator
메틸 에틸 케톤 0 내지 60 중량부 Methyl ethyl ketone 0 to 60 parts by weight
디메틸 포름 아미드 0 내지 80 중량부Dimethyl formamide 0 to 80 parts by weight
이하 실시예를 통하여 본 발명의 3차원 입체무늬를 가지는 인공피혁 제조 방법을 상세히 설명한다.Hereinafter will be described in detail the artificial leather manufacturing method having a three-dimensional solid pattern of the present invention.
그러나 이들 실시예는 본 발명의 예시일 뿐, 본 발명이 이에 한정되는 것은 아니다.However, these examples are merely illustrative of the present invention, the present invention is not limited thereto.
[실시예 1]Example 1
1) 원단을 폴리우레탄 수지 100 중량부에 대하여 친수성 계면활성제 2 중량부, 소수성 계면활성제 2 중량부, 디메틸 포름 아미드 270 중량부, 안료 10 중량부가 혼합된 함침용 폴리우레탄 배합액에 함침시킨 후, 응고조로 이동시켜 4분 가량 1차로 응고시킨 다음, 상기 1차 응고된 원단에 폴리우레탄 수지 100 중량부에 대하여 친수성 계면활성제 2 중량부, 소수성 계면활성제 1 중량부, 디메틸 포름 아미드 40 중량부, 안료 10 중량부가 혼합된 습식 은면코팅용 폴리우레탄 배합액을 도포한 후, 이를 다시 응고조에서 2차로 응고시켰다. 상기 2차 응고된 원단을 수세조에서 세정하여 원단에 잔류하는 디메틸 포름 아미드를 제거한 다음, 약 130 내지 140℃의 건조기 내에서 건조시켜 습식 베이스 피혁을 제조하였다.1) The fabric was impregnated into the impregnated polyurethane compound mixture containing 2 parts by weight of hydrophilic surfactant, 2 parts by weight of hydrophobic surfactant, 270 parts by weight of dimethyl formamide, and 10 parts by weight of pigment based on 100 parts by weight of polyurethane resin. After moving to a coagulation bath for 4 minutes to solidify first, the first solidified fabric, 2 parts by weight of hydrophilic surfactant, 1 part by weight of hydrophobic surfactant, 40 parts by weight of dimethyl formamide, pigment, based on 100 parts by weight of polyurethane resin After applying 10 parts by weight of a mixed wet polyurethane coating solution, it was solidified again in a coagulation bath in the second. The secondary solidified fabric was washed in a water bath to remove dimethyl formamide remaining in the fabric, and then dried in a dryer at about 130 to 140 ° C. to produce a wet base leather.
2) 상기 습식 베이스 피혁 표면에 안료 100중량부, 처리제 30중량부, 수지 10중량부의 배합액을 그라비아 롤을 이용하여 미세한 도트(dot)들을 인쇄하고 건조시켰다.2) 100 parts by weight of the pigment, 30 parts by weight of the treatment agent and 10 parts by weight of the resin were printed on the surface of the wet base leather using a gravure roll, and fine dots were printed and dried.
3) 투명 열가소성 폴리우레탄(thermoplastic polyurethane)을 압출기를 이용하여 0.35mm 두께의 폴리우레탄 시트로 압출시킴과 동시에 상기 폴리우레탄 시트를 상기 인쇄된 베이스 피혁과 합포한 다음, 100 내지 130℃온도에서 엠보싱 롤을 이용하여 상기 미세한 도트 상층부에 미세한 반구(hemisphere)모양이 생기도록 폴리우레탄 시트 표면을 엠보싱하여 3차원적인 입체 무늬가 있는 폴리 우레탄 인공 피혁을 제조하였다.3) Extrude the thermoplastic thermoplastic polyurethane into a 0.35mm thick polyurethane sheet using an extruder and at the same time combine the polyurethane sheet with the printed base leather, and then embossing roll at a temperature of 100 to 130 ℃ By using the embossed surface of the polyurethane sheet to produce a fine hemisphere (hemisphere) in the upper part of the fine dot to produce a three-dimensional three-dimensional polyurethane artificial leather.
도 5는 본 발명의 실시예 1에 의해 3차원적인 입체무늬를 가지는 폴리우레탄 인공피혁의 단면 현미경 사진이고, 도 6은 평면 현미경 사진이다.Figure 5 is a cross-sectional micrograph of a polyurethane artificial leather having a three-dimensional solid pattern in accordance with Example 1 of the present invention, Figure 6 is a planar micrograph.
[실시예 2]Example 2
1) 실시예 1에서 제조된 습식 베이스 피혁을 130 내지 180℃ 에서 엠보싱 롤로 1차 무늬 내기를 한 후 베이스 피혁 표면의 양각 부분에 안료 100중량부, 처리제 30중량부, 수지 10중량부의 배합액을 그라비아 롤을 이용하여 미세한 도트(dot)들을 인쇄하고 건조시켰다.1) After the wet base leather prepared in Example 1 was subjected to primary patterning with an embossing roll at 130 to 180 ° C., 100 parts by weight of the pigment, 30 parts by weight of the treatment agent, and 10 parts by weight of the resin were added to the embossed portion of the surface of the base leather. Fine dots were printed and dried using a gravure roll.
2) 투명 열가소성 폴리우레탄(thermoplastic polyurethane)을 압출기를 이용하여 0.35mm 두께의 폴리우레탄 시트로 압출시킴과 동시에 상기 폴리우레탄 시트를 상기 인쇄된 베이스 피혁과 합포한 다음, 100 내지 130℃온도에서 엠보싱 롤을 이용하여 상기 미세한 도트 상층부에 미세한 반구(hemisphere)모양이 생기도록 폴리우레탄 시트 표면을 엠보싱하여 3차원적인 입체 무늬가 있는 폴리 우레탄 인공 피혁을 제조하였다.2) extruding the transparent thermoplastic polyurethane into a 0.35 mm thick polyurethane sheet using an extruder and simultaneously encapsulating the polyurethane sheet with the printed base leather and then embossing roll at a temperature of 100 to 130 ° C. By using the embossed surface of the polyurethane sheet to produce a fine hemisphere (hemisphere) in the upper part of the fine dot to produce a three-dimensional three-dimensional polyurethane artificial leather.
도 7은 본 발명의 실시예 2에 의해 제조된 인공피혁 사진이다.7 is an artificial leather photograph produced by Example 2 of the present invention.
도 8, 도 9는 본 인공피혁의 표면 현미경 사진으로, 도7은 인쇄층과 폴리우레탄 시트 표면의 엠보싱 무늬와 일치하는 현미경 사진이며, 도8은 인쇄층과 폴리우레탄 시트 표면의 엠보싱 무늬가 엇갈리는 현미경 사진이다.8 and 9 are surface micrographs of the present artificial leather, and FIG. 7 is a micrograph that matches the embossed pattern of the printed layer and the surface of the polyurethane sheet, and FIG. 8 shows the embossed patterns of the printed layer and the surface of the polyurethane sheet interlaced. Photomicrograph.
이처럼 인쇄층과 엠보싱 무늬가 일치하는 부분은 인쇄층의 미세한 도트(dot)층을 반구(hemisphere)모양의 엠보싱층에 의해 확대되어 표면에 떠있는 듯한 느낌을 주고 인쇄층과 엠보싱 무늬가 엇갈리는 부분은 미세한 도트(dot)가 엠보싱 무늬와 일치하지 않아 도트(dot)가 확대되지 않는다. 이러한 부분이 반복적으로 형성됨에 따라 3차원적인 입체무늬가 형성된다.As such, the part where the printed layer and the embossed pattern coincide is enlarged by the hemissphere-shaped embossed layer to give a feeling of floating on the surface, and the part where the printed layer and the embossed pattern are crossed The fine dots do not match the embossed pattern so that the dots do not enlarge. As these portions are repeatedly formed, three-dimensional solid patterns are formed.
[실시예 3]Example 3
1) 이형지에 폴리우레탄 수지 100 중량부에 대하여 메틸 에틸 케톤 40 중량부, 디메틸 포름 아미드 30 중량부 및 안료 10 중량부가 혼합된 건식 피막용 폴리우레탄 배합액을 1차로 도포한 다음 약 90 내지 100℃의 건조기에서 가온 건조하여 경화시킨 후, 상기와 동일 방법으로 2차 도포후 가온 건조하여 경화 시킨후 상기 1차 경화된 이형지를 폴리우레탄 수지 100중량부에 대하여 경화제 10 중량부, 촉진제 3 중량부, 메틸 에틸 케톤 20 중량부, 디메틸 포름 아미드 10 중량부가 혼합된 접착용 폴리우레탄 배합액으로 도포하여 3차로 도포한 후, 실시예 1에 의하여 생산된 습식 베이스 피혁과 서로 합포시키고, 상기 합포된 원단을 숙성실에서 약 24시간 숙성시킨 다음, 상기 원단으로부터 이형지를 박리시켜 습건식 베이스 피혁을 제조하였다.1) A dry coating polyurethane compounding solution containing 40 parts by weight of methyl ethyl ketone, 30 parts by weight of dimethyl formamide and 10 parts by weight of pigment is first applied to a release paper and then about 90 to 100 ° C. After curing by heating and drying in a dryer of 2, the second coating in the same manner as described above, after curing by heating and drying, the primary cured release paper 10 parts by weight of the curing agent, 3 parts by weight of accelerator, 20 parts by weight of methyl ethyl ketone and 10 parts by weight of dimethyl formamide were applied with a mixed adhesive polyurethane blend, and then applied in the third step, and then combined with the wet base leather produced according to Example 1, and the fabric was fabricated. After aging in the aging room for about 24 hours, release paper was peeled from the fabric to prepare a wet-based base leather.
2) 상기 습건식 베이스 피혁 표면에 안료 100중량부, 처리제 30중량부, 수지 10중량부의 배합액을 그라비아 롤을 이용하여 인쇄하고 건조시켰다.2) 100 parts by weight of the pigment, 30 parts by weight of the treatment agent and 10 parts by weight of the resin were printed and dried on the surface of the wet-based base leather using a gravure roll.
3) 투명 열가소성 폴리우레탄(thermoplastic polyurethane)을 압출기를 이용하여 0.35mm 두께의 폴리우레탄 시트로 압출시킴과 동시에 상기 폴리우레탄 시트를 상기 인쇄된 베이스 피혁과 합포한 다음, 폴리우레탄 시트 표면에 100 내지 130℃온도에서 엠보싱 롤을 이용하여 미세한 반구(hemisphere)모양으로 엠보싱하여 3차원적인 입체 무늬가 있는 폴리 우레탄 인공 피혁을 제조하였다.3) extruding the transparent thermoplastic polyurethane into a 0.35 mm thick polyurethane sheet using an extruder and simultaneously laminating the polyurethane sheet with the printed base leather and then 100 to 130 on the surface of the polyurethane sheet. Embossing was carried out in the shape of fine hemispheres using an embossing roll at a temperature of 3 ° C. to prepare a polyurethane artificial leather having a three-dimensional three-dimensional pattern.
[실시예 4]Example 4
1) 실시예 1에서 제조된 습식 베이스 피혁 표면에 130 내지 180℃ 엠보싱 롤로 1차 무늬 내기를 한후 제품 표면의 양각 부분에 안료 100중량부, 처리제 30중량부, 수지 10중량부의 배합액을 그라비아 롤을 이용하여 인쇄하고 건조하였다.1) After the primary pattern was placed on the surface of the wet base leather prepared in Example 1 with an embossing roll of 130 to 180 ° C., 100 parts by weight of the pigment, 30 parts by weight of the treatment agent, and 10 parts by weight of the resin were added to the embossed roll on the surface of the product. Was printed and dried.
2) 투명성이 높은 에나멜 이형지에 폴리우레탄 수지 100 중량부에 대하여 메틸 에틸 케톤 40 중량부, 디메틸 포름 아미드 10 중량부가 혼합된 건식 피막용 폴리우레탄 배합액을 1차로 도포한 다음 약 90 내지 100℃의 건조기에서 가온 건조하여 경화시킨 후, 상기와 동일 방법으로 2차 도포후 가온 건조하여 경화 시켰다.2) After applying a dry coating polyurethane blend containing 40 parts by weight of methyl ethyl ketone and 10 parts by weight of dimethyl formamide to the highly transparent enamel release paper first, and then about 90 to 100 ° C. After drying by drying in a dryer and curing, it was cured by heating and drying after the second coating in the same manner as above.
3) 상기 2차 경화된 이형지를 폴리우레탄 수지 100중량부에 대하여 경화제 10중량부, 촉진제 3중량부, 메틸 에틸 케톤 13중량부, 디메틸 포름 아미드 10중량부가 혼합된 접착용 폴리우레탄 배합액으로 도포하여 3차로 도포한 다음, 상기 인쇄된 습식 베이스 피혁과 서로 합포시키고, 상기 합포된 베이스 피혁을 숙성실에서 약 24시간 숙성시킨 다음, 상기 베이스 피혁으로부터 이형지를 박리시켜 투명층이 있는 폴리우레탄 인공피혁을 제조하였다.3) The secondary cured release paper is coated with a polyurethane adhesive for adhesion, in which 10 parts by weight of a curing agent, 3 parts by weight of accelerator, 13 parts by weight of methyl ethyl ketone, and 10 parts by weight of dimethyl formamide are mixed with respect to 100 parts by weight of polyurethane resin. After the third coating, and then combined with the printed wet base leather, the combined base leather is aged in a aging room for about 24 hours, then release the release paper from the base leather to produce a polyurethane artificial leather with a transparent layer It was.
4) 상기 투명층이 있는 폴리우레탄 인공피혁 표면에 100 내지 130℃온도에서 엠보싱 롤을 이용하여 미세한 반구(hemisphere)모양으로 엠보싱하여 3차원적인 입체 무늬가 있는 폴리 우레탄 인공 피혁을 제조하였다.4) The polyurethane artificial leather having a three-dimensional solid pattern was manufactured by embossing a fine hemisphere shape using an embossing roll at a temperature of 100 to 130 ° C. on the surface of the polyurethane artificial leather having a transparent layer.
도 5, 도 6, 도 7에서 보이는 바와 같이 실시예 1, 2에 의해서 제조된 인공피혁은 종래 생산되는 인공피혁과는 달리 입체무늬가 뚜렸이 나타남을 알 수 있다.As shown in FIGS. 5, 6, and 7, the artificial leathers manufactured according to Examples 1 and 2 may be seen to have three-dimensional patterns, unlike artificial leathers produced in the prior art.
본 발명에 의해 제조된 인공피혁은 종래 인공피혁에서 낼 수 없었던 3차원적인 입체무늬를 부여함으로써, 종래 엠보싱 롤러에 의한 단순 평면 무늬 및 이형지에 의한 단순 평면 무늬의 한계를 극복하여 보다 다양한 이중의 입체 무늬를 가진 인공피혁을 제공하는 효과가 있다.The artificial leather manufactured by the present invention provides a three-dimensional three-dimensional pattern that cannot be produced by the conventional artificial leather, thereby overcoming the limitations of the simple flat pattern by the conventional embossing roller and the simple flat pattern by the release paper, and thus, the more various double solids. It is effective to provide patterned artificial leather.
도 1은 본 발명의 투명 또는 반투명 합성수지 시트를 이용한 인공피혁 제조 공정도,1 is a process for manufacturing artificial leather using a transparent or translucent synthetic resin sheet of the present invention,
도 2는 본 발명의 투명 또는 반투명 합성수지 시트를 이용한 인공피혁의 단면도,2 is a cross-sectional view of artificial leather using a transparent or translucent synthetic resin sheet of the present invention,
도 3은 본 발명의 투명 또는 반투명한 피막용 합성수지 배합액을 이용한 인공피혁 제조 공정도,Figure 3 is an artificial leather manufacturing process using the transparent or translucent film synthetic resin formulation of the present invention,
도 4는 본 발명의 투명 또는 반투명한 피막용 합성수지 배합액을 이용한 인공피혁의 단면도,Figure 4 is a cross-sectional view of artificial leather using a transparent or translucent film synthetic resin formulation of the present invention,
도 5는 실시예 1에 의해 제조된 폴리우레탄 인공피혁의 단면 현미경 사진,5 is a cross-sectional photomicrograph of the polyurethane artificial leather prepared in Example 1,
도 6은 실시예 1에 의해 제조된 폴리우레탄 인공피혁의 평면 현미경 사진,6 is a planar photomicrograph of the polyurethane artificial leather prepared in Example 1,
도 7은 실시예 2에 의해 제조된 폴리우레탄 인공피혁의 평면 사진,7 is a plan view of the polyurethane artificial leather prepared by Example 2,
도 8은 실시예 2에 의해 제조된 폴리우레탄 인공피혁 인쇄층의 도트와 상부층의 미세한 반구가 일치하는 부분의 표면 현미경 사진,8 is a surface photomicrograph of a portion where the dots of the polyurethane artificial leather printing layer prepared in Example 2 coincide with the fine hemispheres of the upper layer,
도 9은 실시예 2에 의해 제조된 폴리우레탄 인공피혁 인쇄층의 도트와 상부층의 미세한 반구가 엇갈리는 부분의 표면 현미경 사진이다.FIG. 9 is a surface micrograph of a portion in which dots of the polyurethane artificial leather printed layer prepared in Example 2 and the fine hemispheres of the upper layer are staggered.
* 도면의 주요부에 대한 설명* Description of the main parts of the drawings
1. 베이스 피혁 2. 무늬인쇄층1. Base leather 2. Pattern printing layer
3. 투명 또는 반투명 합성수지 시트3. Transparent or translucent synthetic resin sheet
4. 투명 또는 반투명 합성수지 코팅층4. Transparent or translucent synthetic resin coating layer
5. 접착용 합성수지 코팅층5. Adhesive synthetic resin coating layer

Claims (5)

  1. 베이스 피혁(1) 표면에 그라비아인쇄 또는 전사인쇄를 하여 무늬인쇄층(2)을 형성시키는 무늬인쇄공정; 상기 무늬인쇄된 베이스 피혁에 접착용 폴리우레탄 배합액을 도포한 다음 폴리우레탄 수지로 이루어진 투명 또는 반투명 열가소성 시트(3)를 접착시키는 합포공정; 상기 합포된 베이스 피혁을 100 내지 130℃에서 롤러로 가압하여 열가소성 시트에 미세한 엠보스를 형성시키는 엠보싱공정; 을 포함하는 것을 특징으로 하는 3차원 입체무늬를 가지는 인공피혁 제조 방법.A pattern printing step of forming a pattern printing layer 2 by performing gravure printing or transfer printing on the surface of the base leather 1; A bonding step of applying a polyurethane compound for adhesion to the patterned base leather and then adhering a transparent or translucent thermoplastic sheet 3 made of a polyurethane resin; An embossing process of pressing the combined base leather with a roller at 100 to 130 ° C. to form fine embossing on the thermoplastic sheet; Artificial leather manufacturing method having a three-dimensional solid pattern comprising a.
  2. 제1항에 있어서, 무늬인쇄공정은 베이스 피혁(1) 표면에 엠보싱을 한 후, 그라비아인쇄 또는 전사인쇄를 하여 무늬인쇄층(2)을 형성시키는 것을 특징으로 하는 3차원 입체무늬를 가지는 인공피혁 제조 방법.The artificial leather having a three-dimensional solid pattern according to claim 1, wherein the pattern printing process forms the pattern printing layer 2 by embossing the surface of the base leather 1 and then performing gravure printing or transfer printing. Manufacturing method.
  3. 제1항 또는 제2항에 있어서, 상기 무늬인쇄공정에서 무늬인쇄층은 상기 베이스 피혁에 미세한 도트(dot)들로 인쇄되고, 상기 엠보싱공정에서 미세한 엠보스는 반구(hemisphere)모양으로 상기 미세한 도트(dot) 상층부에 형성되도록 엠보싱하는 것을 특징으로 하는 3차원 입체무늬를 가지는 인공피혁 제조 방법.The pattern printing layer of claim 1 or 2, wherein the pattern printing layer is printed on the base leather as fine dots, and the fine embossing in the embossing process is performed in the form of hemispheres. dot) Artificial leather manufacturing method having a three-dimensional solid pattern characterized in that the embossed to be formed on the upper layer.
  4. 베이스 피혁(1) 표면에 그라비아인쇄 또는 전사인쇄를 하여 무늬인쇄층(2)을 형성시키는 무늬인쇄공정; 이형지에 투명 또는 반투명한 피막용 폴리우레탄 배합액(4)을 1차로 도포한 후 가온 건조하여 경화시킨 다음, 상기 1차 경화된 이형지에 접착용 폴리우레탄 배합액(5)을 2차로 도포하는 폴리우레탄 도포공정; 상기 접착용 폴리우레탄 배합액이 도포된 이형지와 상기 무늬가 인쇄된 베이스 피혁을 서로 합포시킨 다음, 가온 건조하여 경화시키는 숙성공정; 상기 숙성된 베이스 피혁으로부터 이형지를 박리시키는 이형공정; 상기 이형지가 박리된 베이스 피혁을 100 내지 130℃에서 롤러로 압력을 가압하여 열가소성 시트에 미세한 엠보스를 형성시키는 엠보싱공정; 을 포함하는 것을 특징으로 하는 3차원 입체무늬를 가지는 인공피혁 제조 방법.A pattern printing step of forming a pattern printing layer 2 by performing gravure printing or transfer printing on the surface of the base leather 1; Polyurethane coating the polyurethane composition liquid (4) transparent or semi-transparent to the release paper first, followed by heating and drying to cure, and then applying the adhesive polyurethane mixture liquid (5) to the primary cured release paper secondly. Urethane coating process; A maturation step of laminating the release paper coated with the adhesive polyurethane compounding solution and the base-printed base leather to each other, followed by heating and drying to cure; A release process of peeling release paper from the aged base leather; An embossing step of forming a fine embossing on the thermoplastic sheet by pressurizing a pressure with a roller at 100 to 130 ° C. in which the release paper is peeled off; Artificial leather manufacturing method having a three-dimensional solid pattern comprising a.
  5. 제4항에 있어서, 상기 피막용 폴리우레탄 배합액(4)은 폴리 우레탄 100 중량부에 대하여 소수성 계면활성제 0 내지 10 중량부, 친수성 계면활성제 0 내지 10 중량부, 메틸 에틸 케톤 10 내지 60 중량부 및 디메틸 포름 아미드 0 내지 50 중량부의 배합액이고, 상기 접착용 폴리 우레탄 배합액(5)은 폴리 우레탄 수지 100 중량부에 대하여 경화제 5 내지 20 중량부, 촉진제 0 내지 10 중량부, 메틸 에틸 케톤 0 내지 60 중량부, 디메틸 포름 아미드 0 내지 80 중량부의 배합액인 것을 특징으로 하는 3차원 입체무늬를 가지는 인공피혁 제조 방법.The polyurethane coating liquid (4) according to claim 4, wherein the polyurethane compound for coating (4) comprises 0 to 10 parts by weight of hydrophobic surfactant, 0 to 10 parts by weight of hydrophilic surfactant, and 10 to 60 parts by weight of methyl ethyl ketone, based on 100 parts by weight of polyurethane. And 0 to 50 parts by weight of dimethyl formamide, wherein the adhesive polyurethane compounding solution (5) is 5 to 20 parts by weight of a curing agent, 0 to 10 parts by weight of accelerator, and methyl ethyl ketone 0 to 100 parts by weight of polyurethane resin. To 60 parts by weight, dimethyl formamide 0 to 80 parts by weight of the compound, characterized in that the three-dimensional solid pattern artificial leather manufacturing method.
KR10-2002-0082262A 2002-12-23 2002-12-23 Method for producing artificial leather with 3-dimension pattern KR100516276B1 (en)