KR100400700B1 - Method for making high glossy metallic glaze and use thereof - Google Patents

Method for making high glossy metallic glaze and use thereof Download PDF

Info

Publication number
KR100400700B1
KR100400700B1 KR1020020041499A KR20020041499A KR100400700B1 KR 100400700 B1 KR100400700 B1 KR 100400700B1 KR 1020020041499 A KR1020020041499 A KR 1020020041499A KR 20020041499 A KR20020041499 A KR 20020041499A KR 100400700 B1 KR100400700 B1 KR 100400700B1
Authority
KR
South Korea
Prior art keywords
glaze
materials
melting
introducing
hours
Prior art date
Application number
KR1020020041499A
Other languages
Korean (ko)
Inventor
In Ho Jeon
Original Assignee
Korea Technology Ceramic Co Lt
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Korea Technology Ceramic Co Lt filed Critical Korea Technology Ceramic Co Lt
Priority to KR1020020041499A priority Critical patent/KR100400700B1/en
Application granted granted Critical
Publication of KR100400700B1 publication Critical patent/KR100400700B1/en

Abstract

PURPOSE: A method for making a high glossy metallic glaze is provided to obtain a glaze, which is capable of forming a smooth surface and protecting the attack by an external liquid or gas, and has excellent chemical stability, various colors, cleaning acceptability and wearing resistance. CONSTITUTION: The method comprises the steps of: introducing a mixture containing 57-70 wt% of SiO2, 6-12 wt% of Al2O3, 10-13 wt% of CaO, 1-3 wt% of MgO, 1-4 wt% of K2O, 2-8 wt% of Na2O, 5-7 wt% of B2O3 and 5-15 wt% of PbO into a refractory melting pot; mounting the refractory pot to a melting furnace; covering the lid of the furnace and gradually heating at 1200-1350 deg.C for about 3-4 hours; maintaining the peak temperature for about 1-2 hours to help the complete melting of the materials; quenching the completely molten materials with cold water; drying the quenched glassy powder to form frit; introducing 35-55 wt% of the frit, 40-60 wt% of Pb3O4, 15 wt% of silica and 3-10 wt% of ZnO into a ball mill; adding water thereto; milling the materials to a retention ratio with a standard sieve of 325 mesh of about 1% or less to form a glaze; and mixing 100 wt% of the glaze with 1-15 wt% of a pigment.
KR1020020041499A 2002-07-16 2002-07-16 Method for making high glossy metallic glaze and use thereof KR100400700B1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
KR1020020041499A KR100400700B1 (en) 2002-07-16 2002-07-16 Method for making high glossy metallic glaze and use thereof

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
KR1020020041499A KR100400700B1 (en) 2002-07-16 2002-07-16 Method for making high glossy metallic glaze and use thereof

Publications (1)

Publication Number Publication Date
KR100400700B1 true KR100400700B1 (en) 2003-10-08

Family

ID=37422367

Family Applications (1)

Application Number Title Priority Date Filing Date
KR1020020041499A KR100400700B1 (en) 2002-07-16 2002-07-16 Method for making high glossy metallic glaze and use thereof

Country Status (1)

Country Link
KR (1) KR100400700B1 (en)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101053089B1 (en) 2011-05-16 2011-08-01 주식회사 신성씨앤씨 Glaze for providing high glossy water color and a method for preparing tile having water color using the same
KR20210042698A (en) 2019-10-10 2021-04-20 강혜숙 Glaze composition for high firing capable of long-term storage and manufaturing method thereof

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS63123837A (en) * 1986-11-13 1988-05-27 Ngk Insulators Ltd Enamel for enameled aluminum ware
JPH0297437A (en) * 1988-05-26 1990-04-10 Ikebukuro Horo Kogyo Kk Frit composition for enamel for direct enameling
KR970015528A (en) * 1995-09-26 1997-04-28 오재명 Pottery manufacturing method
US5710081A (en) * 1996-02-15 1998-01-20 Cerdec Aktiengesellschaft Keramische Farben Black glass frit, process for the production thereof and use thereof
KR19990010432A (en) * 1997-07-16 1999-02-18 최무식 Porcelain Glaze Composition with Far-Infrared Wavelength Effect at Room Temperature
KR20010092981A (en) * 2000-03-28 2001-10-27 김형순 tile glaze and its manufacturing method
KR20020008892A (en) * 2000-07-20 2002-02-01 백우현 Loese tile and it's manufacturing method
KR20020050077A (en) * 2001-08-02 2002-06-26 김민호 Method for preparing article coated with gold

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS63123837A (en) * 1986-11-13 1988-05-27 Ngk Insulators Ltd Enamel for enameled aluminum ware
JPH0297437A (en) * 1988-05-26 1990-04-10 Ikebukuro Horo Kogyo Kk Frit composition for enamel for direct enameling
KR970015528A (en) * 1995-09-26 1997-04-28 오재명 Pottery manufacturing method
US5710081A (en) * 1996-02-15 1998-01-20 Cerdec Aktiengesellschaft Keramische Farben Black glass frit, process for the production thereof and use thereof
KR19990010432A (en) * 1997-07-16 1999-02-18 최무식 Porcelain Glaze Composition with Far-Infrared Wavelength Effect at Room Temperature
KR20010092981A (en) * 2000-03-28 2001-10-27 김형순 tile glaze and its manufacturing method
KR20020008892A (en) * 2000-07-20 2002-02-01 백우현 Loese tile and it's manufacturing method
KR20020050077A (en) * 2001-08-02 2002-06-26 김민호 Method for preparing article coated with gold

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101053089B1 (en) 2011-05-16 2011-08-01 주식회사 신성씨앤씨 Glaze for providing high glossy water color and a method for preparing tile having water color using the same
KR20210042698A (en) 2019-10-10 2021-04-20 강혜숙 Glaze composition for high firing capable of long-term storage and manufaturing method thereof

Similar Documents

Publication Publication Date Title
CA1333622C (en) Lead-free glass frit compositions
JP4251582B2 (en) Lead-free and cadmium-free glass composition for glass or glass-ceramic polishing, enamelling and decoration
EP1294651B1 (en) Enamel composition
CA1274857A (en) Lead-free glass frit compositions
US5605869A (en) Glass compositions
CA2279785A1 (en) Lead-and cadmium-free glass composition for glazing, enamelling and decorating glasses or glass-ceramics, and process for the production of a glass-ceramic coated therewith
WO2009058746A1 (en) Tile glaze
ES2357521T3 (en) FRITAS MANUFACTURING PROCEDURE FOR ANCIENT TILES.
KR970061802A (en) Black glass frit, preparation method thereof and use thereof
FR2796063B1 (en) NOVEL BLACK RECYCLABLE ENAMEL COMPOSITION COMPRISING ZINC, MANUFACTURING METHOD AND ENAMELLED PRODUCTS OBTAINED
US7037868B2 (en) Transparent tile glaze
CN102408197A (en) Self-cleaning enamel glaze powder
KR100400700B1 (en) Method for making high glossy metallic glaze and use thereof
JPH04325440A (en) Nontoxic glass frit and method of glazing and decorating product comprising glass, glass ceramic or ceramic
US20040018932A1 (en) Composition for producing a porcelain enamel having a metallic appearance
JPH06191874A (en) Rose-pink borosilicate glass, production thereof and article produced from said glass
CA2141378C (en) Fluorine-containing lead- and cadmium-free glazes
SU1715729A1 (en) Frit for enamel coating with brown color
RU2263638C1 (en) Enamel for silicate articles
SU1779672A1 (en) Opacified glass
SU1723074A1 (en) Glaze
SU1763397A1 (en) Nonground-coat colored enamel for steel
MXPA02003747A (en) Water resistant porcelain enamel coatings and method of manufacturing same.
SU863524A1 (en) Frit for colour enamel coating
SU1787964A1 (en) Frit for enamel coating for steel

Legal Events

Date Code Title Description
A201 Request for examination
A302 Request for accelerated examination
E902 Notification of reason for refusal
E701 Decision to grant or registration of patent right
GRNT Written decision to grant
FPAY Annual fee payment

Payment date: 20120910

Year of fee payment: 10

FPAY Annual fee payment

Payment date: 20130911

Year of fee payment: 11

LAPS Lapse due to unpaid annual fee