KR100254172B1 - Candle light personal ornaments making method - Google Patents

Abstract

PURPOSE: A method for manufacturing a metal accessory by using luminous material is provided to serve a delicately patterned accessory durable on the outside shock and changes of temperature and humidity. CONSTITUTION: The method includes the following steps of: (i) forming insertion grooves as desired pattern shapes on the surface of diverse shapes of metal body; (ii) getting a luminous filling material by mixing a transparent resin such as epoxy with luminous phosphorus powder; (iii) filling the resulting luminous material in the patterned insertion grooves; (iv) hardening filled the luminous material to be united with the metal body at 60-80deg.C; and then (v) polishing the surface of the metal body.

Description

Candles jewelry and manufacturing method

The present invention forms a variety of insertion grooves on the surface of the usual jewelry used to beautify the body, such as necklaces, rings, earrings, buttons, tie pins, handbags, eyeglass frames and the like; And a method of manufacturing the same, which is completed by filling the photosensitive filler prepared by mixing a transparent resin such as epoxy and an epoxy, and curing the surface integrally.

Generally, various shapes of ornaments such as necklaces, rings, earrings, buttons, tie pins, handbags and eyeglass frames are used to decorate the body beautifully. These traditional ornaments are mainly made by the sun or the light of the sun. Could boast.

Therefore, in order to make the light effect show out even in the dark night, the tactile material (glow material) is molded into various shapes and the whole is made of tactile jewelry made of the tactile material (luminous material), or part or all of the surface of the jewelry. The trinkets with the tactile paint applied by applying the tactile paint were conceived.The trinkets are small, fine, and sophisticated, and the beauty and beauty must be embodied. In the former case, the entire body is made of tactile material (luminous material). It was difficult to make small, fine, and precise, and it was very difficult and inconvenient to handle during molding and storage and carrying after manufacturing, such as having a problem of being easily damaged by a small impact due to weak external shock.

Also, in the latter case, it was difficult to express a fine and precisely in a desired pattern by applying a luminous paint made of a tactile material (luminous material) to a part or all of the surface of the jewelry as well, which was applied to the surface during the use of the jewelry. The luminous paint, which is a tactile material (luminous material), was easily worn or peeled off, and thus had a problem of greatly reducing its effect as an accessory.

On the other hand, in addition to the above-mentioned ornaments, a luminous paint, which is a tactile material, is applied to the surface in a desired pattern shape, and an adhesive sheet coated with an adhesive is formed on the back surface, and the adhesive sheet is cut off and attached to the surface of the ornaments. Since the adhesive sheet attached to the surface of the protrudes more than the surface of the jewelry, the surface is easily worn out due to external impact, temperature, or humidity, or the adhesive part of the adhesive sheet is displaced, or the adhesive sheet itself is detached from the jewelry surface. As a whole, ornaments manufactured using luminous paint, which is a conventional tactile material, have been greatly deteriorated in effectiveness and have many problems in use.

The present invention relates to an ornament using a tactile material (luminous material) and a method for manufacturing the same, forming a variety of insertion grooves on the surface of the decorative body made of metal and to the photosensitive grooves (P) and epoxy Filling the tactile fillers made of a tactile material (glow material) by mixing the transparent resin of, or by adding a color pigment when mixing the transparent resin such as the pulverulent powder (phosphorus (P) and epoxy) to the color added tactile material ( After filling the photosensitive filler with a variety of methods and curing it, the surface is polished, or the colored filler obtained by adding a color pigment to a transparent resin such as epoxy in the groove of the decorative body is first filled and cured. Dig into pieces by embossing or engraving in the desired shape, and filling the curing material therein to harden them, thereby resisting external shocks, changes in temperature, humidity, etc. It has a long service life, easy to store and carry, and is very easy to handle.The fine and detailed patterns make the exterior look beautiful even during the day, and it is especially fine at night. The purpose is to make the beautiful and beautiful pattern of light shine brightly so that they can play the role of jewelry at night.

1 is a process diagram according to an embodiment of the present invention.

2 is a process diagram showing another embodiment of the present invention.

3 is an illustration of ornaments in accordance with an embodiment of the present invention.

Figure 4 is a cross-sectional view of the ornament according to an embodiment of the present invention.

5 is a cross-sectional view of the ornament according to another embodiment of the present invention.

♣ Explanation of symbols for the main parts of the drawing ♣

100: decorative body 100a: insertion groove

200: Filler 200a: Fragment groove

300: transparent epoxy

The present invention for achieving the above object is to make a decorative body made of metal and to form a variety of insertion grooves on the surface of the decorative body to manufacture ornaments made by filling the tactile material (glow material) in detail according to the embodiment The explanation is as follows.

Example 1

First step: decorative body forming process

In molding various types of decorative bodies made of metal, insertion grooves are formed in a predetermined pattern shape to be integrally represented on the surface of the decorative body by a method such as during molding or post-processing of the decorative body.

Second Process: Manufacturing Process of Candle Filler

By mixing the dough (phosphorus; P) with a transparent resin such as epoxy to obtain a tactile filler made of a tactile material (luminous material).

Here, when mixing the dough powder (phosphorus; P) to the resin, such as transparent epoxy, by adding a color pigment can be obtained a tactile filler material (phosphorus; P) having a variety of colors.

Third Process: Filling Process of Candle Filler

In the second step, the filling material made of the tactile material obtained by mixing and mixing the dough powder (phosphorus (P)) in the transparent epoxy in the first step is filled with the inside of the insertion groove formed integrally in various patterns on the surface of the decorative body in the first step. Fill.

Fourth Step: Curing Process of Candle Filler

In the third step, in the state of filling the tactile fillers made of tactile materials into the insert grooves formed in the shape of various patterns on the surface of the decorative body, they are heated to a temperature of about 60 to 70 ° C. to harden the fillers. Harden.

Fifth Step: Polishing Process

In the fourth step, the decorative body filled with the tactile filler made of the tactile material is placed in a furnace and heated to cure the tactile filler, and then the surface of the cured tactile filler is smoothed using a known polishing machine such as photo medicine. Polish it.

Example 2

First step; Decorative body molding process

In molding various types of decorative bodies made of metal, insertion grooves are formed in a predetermined pattern shape to be integrally represented on the surface of the decorative body by a method such as during molding or post-processing of the decorative body.

Second Process: Manufacturing Process of Colored and Candle Filler

Color pigments are mixed with transparent resins such as epoxy to obtain colored fillers of various colors, and photosensitive fillers (phosphorus (P)) are mixed with transparent resins such as epoxy to obtain a tactile filler made of a tactile material.

Third process: filling process for colored filler

In the second step, the colored filler obtained by blending a color pigment with a transparent resin such as epoxy is filled in the insertion recess formed in various patterns on the surface of the decorative body in the first step.

4th step: curing of color filler

Filling the insertion groove of the decorative body by heating it to a temperature of about 60 ~ 70 ℃ in a state in which the colored filler is filled in the insertion groove formed in the surface of the decorative body in various patterns in the third step in the third step Harden the colored filler.

5th Process: Pattern Sculpture Process

In the fourth step, the colored filler, which is filled in the recesses of the decorative body and cured, is carved and engraved in a negative or embossed shape into a desired shape using a laser or the like.

6th Step: Filling Process of Candle Filler

In the fifth step, the colored filler filled in the grooves of the decorative body was engraved in an intaglio or embossed using a laser or the like to fill the photosensitive filler obtained by mixing the photosensitive powder (phosphorus (P)) with a transparent resin such as epoxy. do.

7th Step: Curing Process of Candle Filler

In the sixth step, the colored filler is sculpted and filled into the tactile filler filled in the furnace, and heated to a temperature of about 60 to 70 ℃ to cure.

8th Step: Polishing Process

In the seventh step, the decorative body filled with the tactile filler made of the tactile material is placed in a furnace and heated to cure the tactile filler, and then the surface of the cured tactile filler is smoothed using a known polishing machine such as photo medicine. Polish it.

In the ornaments of the present invention obtained by the method according to the above embodiments 1 and 2, as shown in FIG.

Molding various types of decorative body 100 made of metal, integrally forming the insertion groove (100a) of various shapes on the surface of the decorative body 100,

The filling groove (200) after filling the tactile filler (200) made of a tactile material (glow material) obtained by mixing the dough (phosphorus (P)) with a transparent resin such as epoxy in the insertion groove (100a) (not shown) ) To harden by heating to a temperature of about 60 ~ 70 ℃, the surface of the cured tactile filler 200 is smoothly polished by filling the grooves on the surface of the decorative body integrally filled with the tactile trinkets Configured.

The ornaments of the present invention, as shown in Figure 2 attached to the insertion groove (100a) formed on the surface of the decorative body 100 made of metal, by mixing a color pigment of various colors in a transparent resin such as epoxy Fill the colored filler 210, fill it into a furnace, heat it to a temperature of about 60 ~ 70 ℃, and cure, then carved into an embossed or intaglio into a desired shape, and filled with the photosensitive filler 200 therein to cure it When the surface is polished smoothly, colored fillers and candle fillers of various colors form a tactile ornament that displays beautiful patterns.

Therefore, when the ornament of the present invention is used to decorate a part of the body, the ornaments look more beautiful by the shape of the tactile filler 200 made of the tactile material even during the day, and in particular, the tactile filler made of the tactile material (200) The various patterns of the) shine brightly, and the trinkets perform well even at night without lights.

Here, if various colors are added to the tactile filler 200 made of the tactile material, the user may freely select a favorite color.

Then, as shown in Figure 2, the color filling the colored filler 210 inside the insertion groove (100a) integrally formed in the metal body 100, carved into various patterns and dug out, the filling material in the excavated space If you fill the (200) and harden integrally, the color of these harmonizes with the harmonious harmony of the day, as well as at night and more beautiful and vivid pattern to give out the role of the ornament is maximized.

The present invention is not limited to necklaces, but can be applied to all kinds of ornaments for decorating interior and exterior as well as all kinds of ornaments of various shapes such as earrings, buttons, tie pins, handbags, eyeglass frames, and the like.

As described above, the present invention forms a variety of insertion grooves on the surface of the tall body made of metal, and the colored grooves and the filling material prepared by mixing transparent resin and color pigments such as tactile powder (phosphorus) and epoxy in the insertion grooves. Is filled in a variety of ways and then hardened by heating to manufacture the jewelry using a tactile material, even if the jewelry is large, as well as small, only the insertion groove can be formed on the surface of the metal jewelry Small and fine parts can be precisely processed to maximize the characteristics of the jewelry, as well as the filling material made of the tactile material is formed in the insertion recess formed integrally with the surface of the metal decorative body. Strong strength to withstand changes in the back, so there is no risk of being easily damaged by smooth impact Decorative or not at all fear of spoiling that I am away at the body surface extended service life, of course, will have to handle the storage and convenient mobile, etc. very easily.

In addition, when the insertion grooves are formed on the surface of the decorative body, only fine processing to the desired pattern shape can obtain a fine and precise pattern shape according to the desired pattern even if the filler is made of a tactile material in the insertion grooves. Not only very beautiful, but especially at night, when the ornaments of the present invention are seen, the fine and elaborate pattern of the filling material made of the candle material is clearly revealed, and the decorative effect is doubled.

On the other hand, colored fillers and candle fillers with different colors inside the grooves formed on the decorative body are carved into various patterns, so that you can feel the harmony of the beautiful colors even during the day, as well as fluorescent fillers at night. The distinction of color is felt more vividly, and it harmonizes with the darkness around it, and it shows the maximum effect as ornaments to the degree of ecstasy.

As described above, the jewelry produced according to the present invention completely escapes the concept of the existing jewelry that emits light only in the daytime or where there is a light, thereby challenging the new concept to show its beauty even more at night. It is a very innovative and useful invention that can improve the qualitative quality of the jewelry by making the expression of the jewelry of the new concept more completely different.

Claims (4)

A first step of forming a decorative body for forming an insertion recess in a pattern shape to be expressed on various types of decorative bodies made of metal; A second step of manufacturing a tactile filler material in which a pulverizing tactile powder (phosphorus (P)) is mixed with transparent resin such as epoxy to obtain a tactile filler made of a tactile material; A third step of filling the inside of the recessed groove formed with various pattern shapes formed on the surface of the decorative body in the first step by using the photosensitive material obtained in the second step; In the third step, in the state of filling the tactile filler material made of the tactile material in the insertion groove formed in the shape of various patterns on the surface of the decorative body in the furnace (kiln) to heat about 60 ~ 70 ℃ to cure the tactile fillers The fourth process, which is the curing process of the candle filler, The polishing tack process of curing the tactile filler made of the tactile material by integrally with the decorative body by heating in the fourth process, and then polishing the surface of the filler smoothly using a well-known polishing machine after applying the photo medicine to the surface of the tactile filler. The method of manufacturing a candle ornaments, characterized in that consisting of a fifth step. The first step of forming a decorative body made of metal, which is a decorative body molding step of forming an insertion recess in a predetermined pattern shape to be integrally represented on the surface of the decorative body by molding or post-processing the decorative body. , It is a manufacturing process for manufacturing colored and tactile fillers by mixing color pigments into transparent resins such as epoxy to obtain colored fillers of various colors, and by mixing tactile powder (phosphorus (P)) to transparent resins such as epoxy to obtain tactile fillers made of tactile materials. 2 process, A third color filling material filling step of filling a colored filler obtained by blending a color pigment with a transparent resin such as epoxy in the second step, into an insertion recess formed in various pattern shapes on the surface of the decorative body in the first step; Fair, Filling the insertion groove of the decorative body by heating it to a temperature of about 60 ~ 70 ℃ in a state in which the colored filler is filled in the insertion groove formed in the surface of the decorative body in various patterns in the third step in the third step A fourth process, which is a process of hardening the colored filler, wherein the colored filler is cured; The fifth step, which is a sculpting process of engraving and digging the colored filler filled in the recesses of the decorative body in the fourth step into an intaglio or embossed shape using a laser or the like; In the fifth step, the colored filler filled in the grooves of the decorative body was engraved in an intaglio or embossed using a laser or the like to fill the photosensitive filler obtained by mixing the photosensitive powder (phosphorus (P)) with a transparent resin such as epoxy. The sixth process, which is the filling process In the sixth step, the seventh step, which is a step of curing the tactile filler material to squeeze the colored filler material filled in the excavated portion in the furnace (heat) to heat to a temperature of about 60 ~ 70 ℃, and In the seventh step, the decorative body filled with the tactile filler made of the tactile material is placed in a furnace and heated to cure the tactile filler, and then the surface of the cured tactile filler is smoothed using a known polishing machine such as photo medicine. Candles ornaments and manufacturing method characterized by comprising the eighth step of the polishing step to be polished. In constructing ornaments that embellish the body, Form insertion grooves of various shapes on the surface of the decorative body of various shapes made of metal, and after filling the catalyst filling material of the tactile material obtained by mixing the tactile powder with a transparent resin such as epoxy into the insertion groove, put it in the kiln about 60 ~ After curing by heating to a temperature of 70 ℃, by smoothly polishing the surface of the tactile filler material, the tactile material is configured to be filled in the grooves on the surface of the decorative body integrally molded to be displayed at night. In constructing ornaments that embellish the body, Forming grooves of various shapes on the surface of the decorative body made of metal, and filling the colored filler obtained by adding a color pigment to a transparent resin such as epoxy to the groove of the decorative body first, and then hardened to a desired shape Dig into pieces by embossing or engraving, and filling and curing the tactile filler therein to smoothly polish the surface of the tactile filler so that the colored filler and the tactile filler are integrally filled and molded in the grooves on the surface of the decorative body to be displayed at night. Candles ornaments characterized in that.