KR100215359B1 - Tile, method and device for manufacturing the tile - Google Patents

Tile, method and device for manufacturing the tile Download PDF

Info

Publication number
KR100215359B1
KR100215359B1 KR1019970014471A KR19970014471A KR100215359B1 KR 100215359 B1 KR100215359 B1 KR 100215359B1 KR 1019970014471 A KR1019970014471 A KR 1019970014471A KR 19970014471 A KR19970014471 A KR 19970014471A KR 100215359 B1 KR100215359 B1 KR 100215359B1
Authority
KR
South Korea
Prior art keywords
tile
strap
nozzle
extruded
mixing
Prior art date
Application number
KR1019970014471A
Other languages
Korean (ko)
Other versions
KR19980077368A (en
Inventor
심재경
Original Assignee
심재경
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 심재경 filed Critical 심재경
Priority to KR1019970014471A priority Critical patent/KR100215359B1/en
Publication of KR19980077368A publication Critical patent/KR19980077368A/en
Application granted granted Critical
Publication of KR100215359B1 publication Critical patent/KR100215359B1/en

Abstract

본 발명은 예컨대 바닥재나 외장재로 사용되는 타일을 제조하기 위한 방법과, 상기 제조방법을 수행하기 위한 장치와, 그리고 상기 방법 및 장치에 의하여 제조되는 타일에 관한 것으로서, 타일의 생산성도 높일 수 있는 타일제조방법 및 장치와, 타일의 상면에 다양한 음각 무늬가 형성됨과 아울러 타일의 상면이 다단 구조가 될 수 있도록 하는 것을 목적으로 한다.The present invention relates to a method for manufacturing a tile used as a flooring or an exterior material, to an apparatus for performing the manufacturing method, and to a tile manufactured by the method and the device, wherein the tile can increase the productivity of the tile. An object of the present invention is to provide a manufacturing method and apparatus and various intaglio patterns on the upper surface of the tile, and to enable the upper surface of the tile to have a multi-stage structure.
본 발명에 따른 타일은, 점토 및 고령토를 주원료로 하여 이루어지는 것으로서, 상·하면에 차례로 소정의 음각무늬(511) 및 다수의 그루브(521)가 형성되고, 또한 상면이 다단 구조로 형성된다. 타일(51)의 음각무늬(511)와 다수의 그루브(521)는 진공토련성형기(1)에 의하여 연속압출성형되는 타일 스트랩(5)의 상·하면을 노즐(13)의 출구단에 인접하여 설치되고 각각의 외주면에 양각무늬(211)와 리브(221)가 차례로 형성된 상·하부 압연롤러(21)(22)에 의하여 가압되어 형성된다. 2줄의 타일 스트랩(5)(5)이 상하로 겹쳐진 상태로 압출성형하기 위하여, 상·하면에 다수의 리브(141)(142)가 각각 형성된 압출다이(14)가 노즐(13) 내부 중앙에 설치되고, 노즐(13) 출구단에 인접하여 양각무늬(211)가 각각 형성된 상·하부 압연롤러(26)(27)가 설치된다. 따라서, 상하의 타일 스트랩(5)(5)의 양면에는 각각 음각무늬(511) 및 다수의 그루브(521)가 형성된다.The tile according to the present invention is composed of clay and kaolin as main raw materials. A predetermined intaglio pattern 511 and a plurality of grooves 521 are sequentially formed on the upper and lower surfaces, and the upper surface is formed in a multistage structure. The intaglio pattern 511 and the plurality of grooves 521 of the tile 51 have upper and lower surfaces of the tile strap 5 continuously extruded by the vacuum drill machine 1 adjacent to the outlet end of the nozzle 13. It is provided by pressing the upper and lower rolling rollers (21, 22) formed on each of the outer circumferential surface of the embossed pattern 211 and the rib 221 in turn. In order to extrude two rows of tile straps 5 and 5, the extrusion die 14 having a plurality of ribs 141 and 142 formed on the upper and lower surfaces, respectively, has a center inside the nozzle 13. The upper and lower rolling rollers 26 and 27 which are provided in the upper and lower sides of the nozzle 13 are provided with embossed patterns 211, respectively. Accordingly, the intaglio pattern 511 and the plurality of grooves 521 are formed on both surfaces of the upper and lower tile straps 5 and 5, respectively.

Description

타일제조방법 및 장치와, 상기 방법 및 장치에 의하여 제조되는 타일Tile manufacturing method and apparatus, and tiles manufactured by the method and apparatus
본 발명은 예컨대 바닥재나 외장재로 사용되는 타일을 제조하기 위한 방법과, 상기 제조방법을 수행하기 위한 장치와, 그리고 상기 방법 및 장치에 의하여 제조되는 타일에 관한 것으로서, 타일의 생산성도 높일 수 있는 타일 제조방법 및 장치와, 타일의 상면에 다양한 음각 무늬가 형성됨과 아울러 타일의 상면이 다단 구조로 형성된 타일에 관한 것이다.The present invention relates to a method for manufacturing a tile used as a flooring or an exterior material, to an apparatus for performing the manufacturing method, and to a tile manufactured by the method and the device, wherein the tile can increase the productivity of the tile. The present invention relates to a manufacturing method and apparatus, and a tile in which various intaglio patterns are formed on the upper surface of the tile, and the upper surface of the tile is formed in a multi-stage structure.
건축공사나 인테리어 공사시에는 벽면을 마감처리하거나 바닥면을 마감처리하기 위하여 다양한 종류의 타일이 사용된다. 이러한 다양한 종류의 타일 중에는 고령토 및 점토를 주원료로 하여 제조된 타일도 포함된다.In construction or interior construction, various types of tiles are used to finish walls or floors. Among these various types of tiles include tiles manufactured using kaolin and clay as main raw materials.
고령토 및 점토를 주원료로 한 종래의 타일을 제조하는 방법은 통상적으로 다음과 같은 공정을 포함하여 이루어진다.The conventional method for producing a tile based on kaolin and clay usually comprises the following steps.
① 원료혼합공정① Raw material mixing process
수분이 대략 20% 함유된 점토 분말 및 고령토 분말을 혼합기에 의하여 혼합한다.Clay powder and kaolin powder containing approximately 20% of moisture are mixed by a mixer.
② 원료공급공정② Raw Material Supply Process
점토 분말 및 고령토 분말의 혼합물을 컨베이어 벨트에 의하여 롤러 크러셔에 공급한다.The mixture of clay powder and kaolin powder is fed to a roller crusher by a conveyor belt.
③ 분쇄공정③ grinding process
컨베이어 벨트에 의하여 이송된 점토 분말 및 고령토 분말의 혼합물을 미세하게 분쇄한다.The mixture of clay powder and kaolin powder transferred by the conveyor belt is finely ground.
④ 혼수·혼련공정④ Coma and Kneading Process
점토 분말 및 고령토 분말의 혼합 분쇄물이 혼수·혼련기에 이송되면 혼합 분쇄물에 22% 정도의 수분을 공급하면서 혼수·혼련기의 한 쌍의 스크류우에 의하여 혼합 분쇄물을 혼합, 분쇄하여 이송한다.When the mixed pulverized powder of clay powder and kaolin powder is transferred to the coma and kneader, the mixed pulverized powder is mixed, pulverized and conveyed by a pair of screws of the coma and kneader while supplying about 22% of the water to the mixed pulverized powder.
⑤ 진공토련성형⑤ Vacuum drill molding
혼수·혼련공정을 거친 혼합물이 진공토련성형기 내에 공급되면 혼합물에 포함된 공기를 진공압에 의하여 제거하면서 혼합물을 타일 스트랩 형태로 노즐을 통하여 연속 압출하고, 진공토련성형기의 노즐의 출구 선단에 인접하여 상하로 설치된 한 쌍의 압연롤러에 의하여 압출되는 타일 스트랩의 상하면을 가압한다.When the mixture that has undergone the coma-kneading process is supplied into the vacuum drilling machine, the air contained in the mixture is removed by vacuum pressure, and the mixture is continuously extruded through the nozzle in the form of a tile strap, and adjacent to the outlet end of the nozzle of the vacuum drilling machine. Pressing the upper and lower surfaces of the tile strap extruded by a pair of rolling rollers installed up and down.
⑥ 절단공정⑥ Cutting process
압연롤러로부터 컨베이어 벨트에 의하여 이송되는 진공토련성형된 타일 스트랩을 절단기에 의하여 소정의 크기로 연속 절단하여 타일을 만든다.The vacuum-molded tile straps, which are carried by the conveyor belt from the rolling rollers, are continuously cut to a predetermined size by a cutter to make tiles.
⑦ 건조공정⑦ Drying process
절단기에 의하여 절단된 타일에는 아직 소정의 수분이 함유되어 있기 때문에 이 수분을 건조하기 위하여 타일을 건조대차에 적재하여 건조실에 투입한 후 100℃ ∼ 120℃ 범위의 온도하에서 약 2일간 건조한다.Since the tile cut by the cutter still contains a predetermined amount of moisture, the tile is placed in a drying cart and dried in a drying chamber for drying the moisture, and then dried at a temperature ranging from 100 ° C to 120 ° C for about 2 days.
⑧ 소성공정⑧ Firing process
건조된 타일을 소성대차에 적재하여 건조실로부터 소성로에 투입하고, 강도를 높이기 위하여 건조된 타일을 1,250℃∼1,300℃ 범위의 온도하에서 20시간 내지 22시간 동안 환원소성시킨 후 출하한다.The dried tiles are loaded into a baking trolley and put in a firing furnace from a drying chamber, and the dried tiles are reduced-baked for 20 to 22 hours at a temperature in the range of 1,250 ° C to 1,300 ° C in order to increase the strength.
상기한 바와 같은 종래의 타일 제조방법 및 장치에 있어서는, 진공토련성형기의 상하의 압연롤러가 통상적인 원통 형태로 되어 있기 때문에 진공토련성형공정을 거쳐 형성되는 타일 스트랩의 상하면이 거의 평면 형태로 이루어진다. 이 때문에 완성된 타일은 벽면이나 바닥면에 부착시공할 때 타일과 모르타르 등의 습식소재와의 부착력이 약하여 벽면에 대한 부착력이 약하다. 또한, 타일의 외관이 통상적인 직육면체 구조로만 되어 있어서 미려하지 못하기 때문에 타일 시공시 벽면이나 바닥면을 아름답게 마감처리하기에는 한계가 있다. 따라서, 벽면이나 바닥면을 아름답게 마감처리하기 위해서는 타일들의 배열방법을 지그재그 형태로 배열하는 방법이 주로 채용되었다. 또한, 상기 타일제조방법의 공정들 중 타일 스트랩을 압출성형하기 위하여 사용되는 진공토련성형기는 1줄의 타일 스트랩만을 압출성형할 수 있도록 구성되어 있기 때문에 타일의 생산성이 높지 못한 문제점도 있었다.In the conventional tile manufacturing method and apparatus as described above, the upper and lower rolling rollers of the vacuum drilling machine have a general cylindrical shape, so that the upper and lower surfaces of the tile straps formed through the vacuum drilling process are almost planar. For this reason, when the finished tile is attached to the wall or floor surface, the adhesive strength between the tile and the wet material such as mortar is weak, and thus the adhesion to the wall is weak. In addition, since the exterior of the tile is only a regular rectangular parallelepiped structure, it is not beautiful, and thus there is a limit to beautifully finish the wall or the bottom surface when the tile is constructed. Therefore, in order to finish the wall or floor beautifully, a method of arranging tiles in a zigzag form is mainly adopted. In addition, the vacuum drill machine used to extrude the tile straps during the tile manufacturing process has a problem in that the productivity of the tiles is not high because it is configured to extrude only one row of the tile straps.
본 발명은 상기한 종래의 문제점을 해결하기 위하여 안출된 것으로서, 타일의 생산성을 높일 수 있음과 아울러 타일의 상면에 다양한 음각 무늬가 형성되도록 함과 아울러 음각무늬가 형성된 타일의 상면이 다단 구조로 이루어질 수 있도록 하는 것을 목적으로 한다.The present invention has been made in order to solve the above-mentioned problems, it is possible to increase the productivity of the tile, and to form a variety of intaglio pattern on the top surface of the tile and the top surface of the intaglio pattern is formed of a multi-stage structure The purpose is to make it possible.
도 1은 본 발명에 따른 타일제조방법을 나타내는 블록도이다.1 is a block diagram showing a tile manufacturing method according to the present invention.
도 2는 본 발명에 따른 타일제조장치의 주요부인 진공토련성형기의 예를 나타내는 측면도이다.2 is a side view showing an example of a vacuum drill molding machine which is a main part of a tile manufacturing apparatus according to the present invention.
도 3은 도 2의 정면도이다.3 is a front view of FIG. 2.
도 4는 도 2의 진공토련성형기에 의하여 타일 스트랩이 압출성형되는 상태를 요부 단면도이다.4 is a cross-sectional view of a main part of a state in which the tile strap is extruded by the vacuum drill machine of FIG. 2.
도 5는 도 4의 Ⅴ - Ⅴ선 단면도이다.5 is a cross-sectional view taken along the line VV of FIG. 4.
도 6은 다른 예의 압연롤러에 의하여 타일 스트랩이 가압되는 상태를 나타내는 정면도이다.6 is a front view showing a state in which the tile strap is pressed by the rolling roller of another example.
도 7은 또 다른 예의 압연롤러에 의하여 타일 스트랩이 가압되는 상태를 나타내는 정면도이다.7 is a front view showing a state in which the tile strap is pressed by a rolling roller of another example.
도 8은 진공토련성형기의 다른 예를 나타내는 부분 확대 정면도이다.8 is a partially enlarged front view showing another example of the vacuum drill machine.
도 9는 도 8의 진공토련성형기에 의하여 타일 스트랩이 압출성형되는 상태를 나타내는 요부 정면도이다.FIG. 9 is a front view illustrating main parts of the tile strap extruded by the vacuum drill machine of FIG. 8.
도 10은 타일의 예를 나타내는 사시도이다.10 is a perspective view illustrating an example of a tile.
도 11은 타일의 다른 예를 나타내는 사시도이다.11 is a perspective view showing another example of a tile.
도 12는 타일의 또 다른 예를 나타내는 사시도이다.12 is a perspective view showing another example of a tile.
도면의 주요 부분에 대한 부호의 설명Explanation of symbols for the main parts of the drawings
1 : 진공토련성형기5 : 타일 스트랩1: vacuum drill molding machine 5: tile strap
11 : 호퍼12 : 컨테이너11: hopper 12: container
13 : 노즐14 : 압출다이13 nozzle 14 extrusion die
21, 22, 26, 27 : 압연롤러51 : 타일21, 22, 26, 27: rolling roller 51: tile
141. 142. 221 : 리브211 : 양각무늬141.142.221: Rib 211: Embossed pattern
511 : 음각무늬521 : 그루브511: engraving pattern 521: groove
상기 목적을 달성하기 위하여, 본 발명은, 점토 및 고령토를 주원료로 하여 이루어지는 타일로서, 상면에는 소정의 음각무늬가 형성되고, 하면에는 길이방향으로 다수의 그루브가 형성되며, 또한 음각무늬가 형성된 타일의 상면이 다단 구조로 이루어지는 것을 특징으로 한다.In order to achieve the above object, the present invention is a tile consisting of clay and kaolin as a main raw material, a predetermined intaglio pattern is formed on the upper surface, a plurality of grooves are formed in the longitudinal direction on the lower surface, and the tile is formed in the intaglio pattern The upper surface of is characterized by consisting of a multi-stage structure.
또한, 본 발명은, 상기 타일을 제조하기 위한 방법으로서, 원료혼합공정, 원료공급공정, 분쇄공정 및 혼수·혼련공정을 차례로 거친 점토 및 고령토 혼합물을 진공토련성형기에 의하여 연속압출성형하여 타일 스트랩으로 형성함과 아울러 압출되어 나오는 타일 스트랩의 상·하면을 진공토련성형기의 노즐의 출구단에 인접하여 설치되는 상·하부 압연롤러에 의하여 가압하는 진공토련성형공정과, 상기 진공토련성형공정을 거쳐 이송되는 타일 스트랩을 소정의 길이로 연속 절단하여 타일을 만드는 절단공정과, 상기 절단된 타일을 건조 및 환원소성하는 공정을 포함하는 타일 제조공정에 있어서, 상기 진공토련성형공정 중 압출되어 나오는 타일 스트랩의 상면은 다단 구조로 형성되고, 다단 구조로 형성된 타일 스트랩의 상면은 외주면에 소정의 양각무늬가 형성됨과 아울러 외주면이 다단으로 형성된 상부 압연롤러의 가압에 의하여 상기 양각무늬에 대응하는 음각무늬가 연속적으로 형성되고, 타일 스트랩의 하면에는 외주면에 다수의 리브가 형성된 하부 압연롤러의 가압에 의하여 상기 리브에 대응하는 다수의 그루브가 압출방향으로 연속적으로 형성됨을 특징으로 한다.In addition, the present invention, as a method for producing the tile, the clay and kaolin mixture which is subjected to the raw material mixing step, the raw material supply step, the grinding step and the mixing and kneading step in order by continuous extrusion molding with a vacuum molder to form a tile strap Forming and conveying the upper and lower surfaces of the extruded tile strap by the upper and lower rolling rollers, which are installed adjacent to the outlet end of the nozzle of the vacuum drilling machine, through the vacuum drilling molding process and the vacuum drilling molding process. In the tile manufacturing process comprising the step of continuously cutting the tile strap to a predetermined length to make a tile, and the step of drying and reducing the calcining the cut tile, of the tile strap extruded during the vacuum drill molding process The upper surface is formed of a multi-stage structure, the upper surface of the tile strap formed of a multi-stage structure is a predetermined embossed on the outer peripheral surface A groove is formed and an intaglio pattern corresponding to the embossed pattern is continuously formed by the pressing of the upper rolling roller having the outer circumferential surface formed in multiple stages, and the pressing of the lower rolling roller having a plurality of ribs formed on the outer circumferential surface of the tile strap A plurality of grooves corresponding to the ribs are formed continuously in the extrusion direction.
또한, 본 발명에 따른 타일제조방법에 있어서는, 2줄의 타일 스트랩이 상하로 겹쳐진 상태로 압출성형되어 나오도록 진공토련성형공정이 이루어질 수 있고, 이 때에는 상부 타일 스트랩의 하면과 하부 타일 스트랩의 상면에 다수의 그루브가 길이방향으로 형성되도록 함과 아울러 상부 타일 스트랩의 상면과 하부 타일 스트랩의 하면은 다단 구조로 형성되도록 상하의 타일 스트랩이 압출성형되고, 또한 노즐을 통하여 압출되어 나오는 상하의 타일 스트랩의 각각의 다단 구조로 형성된 면은 각 외주면에 소정의 양각무늬가 형성됨과 아울러 외주면이 상기 타일 스트랩의 다단 구조와 대응되는 다단 구조로 형성된 상·하부 압연롤러의 가압에 의하여 상기 양각무늬에 대응하는 연속 음각무늬를 각각 가진다.In addition, in the tile manufacturing method according to the present invention, a vacuum drill molding process may be performed so that two rows of tile straps are extruded in a state of overlapping up and down, and at this time, the lower surface of the upper tile strap and the upper surface of the lower tile strap. The upper and lower tile straps are extruded to form a plurality of grooves in the lengthwise direction, and the upper and lower tile straps are formed in a multi-stage structure. The surface formed by the multi-stage structure of a predetermined embossed pattern is formed on each outer circumferential surface and the continuous intaglio corresponding to the embossed pattern by the pressing of the upper and lower rolling rollers formed of the multi-stage structure corresponding to the multi-stage structure of the tile strap. Each has a pattern.
또한, 본 발명은, 상기 타일을 제조하기 위한 장치로서, 원료혼합공정, 원료공급공정, 분쇄공정 및 혼수·혼련공정을 차례로 거친 점토 및 고령토 혼합물을 호퍼를 통하여 컨테이너 내부에 투입하여 공기를 제거한 후 노즐을 통하여 연속압출성형함으로써 타일 스트랩으로 형성함과 아울러 노즐을 통하여 압출되는 타일 스트랩의 상·하면을 노즐의 출구단에 인접하여 설치된 한 쌍의 압연롤러에 의하여 가압하도록 이루어진 진공토련성형기를 포함하는 타일제조장치에 있어서, 상기 상부 압연롤러의 외주면에는 압출되어 나오는 타일 스트랩의 상면에 상부 압연롤러의 가압에 의하여 소정의 음각무늬가 형성되도록 소정의 양각무늬가 형성되고, 상기 하부 압연롤러의 외주면에는 압출되어 나오는 타일 스트랩의 하면에 하부 압연롤러의 가압에 의하여 길이방향을 따라 다수의 그루브가 형성되도록 다수의 리브가 형성되어 있는 것을 특징으로 한다.In addition, the present invention, as a device for producing the tile, the clay and kaolin mixture through the raw material mixing step, the raw material supply step, the crushing step and the mixing and kneading step in order through the hopper to remove the air after removing the air It comprises a vacuum drill molding machine formed by continuously extruding through the nozzle to form a tile strap and pressurizes the upper and lower surfaces of the tile strap extruded through the nozzle by a pair of rolling rollers installed adjacent to the outlet end of the nozzle. In the tile manufacturing apparatus, a predetermined embossed pattern is formed on the outer circumferential surface of the upper rolling roller so that a predetermined intaglio pattern is formed on the upper surface of the extruded tile strap by pressing the upper rolling roller, and on the outer circumferential surface of the lower rolling roller. By pressing the lower rolling roller on the lower surface of the extruded tile strap A plurality of ribs are formed so that a plurality of grooves are formed along the longitudinal direction.
또한, 본 발명의 타일제조장치에 있어서는, 2줄의 타일 스트랩이 상하로 겹쳐진 상태로 진공토련성형기에 의하여 압출성형되도록 하기 위하여, 상하의 타일 스트랩의 서로 접촉하는 면에 다수의 그루브가 길이방향으로 형성되도록 상하면에 다수의 리브가 각각 형성된 압출다이가 노즐 내부에 설치되고, 또한 2줄의 타일 스트랩의 다른 면에 소정의 음각무늬가 각각 형성되도록 상기 상·하부 압연롤러의 외주면에는 상기 음각무늬와 대응하는 양각무늬가 각각 형성될 수 있다.In addition, in the tile manufacturing apparatus of the present invention, a plurality of grooves are formed in the longitudinal direction on the surfaces in contact with each other of the upper and lower tile straps in order to be extruded by a vacuum drill machine in a state in which two rows of the tile straps are stacked up and down. Extrusion dies each having a plurality of ribs formed on the upper and lower surfaces thereof are installed inside the nozzle, and the outer peripheral surfaces of the upper and lower rolling rollers correspond to the intaglio patterns so that predetermined intaglio patterns are formed on the other side of the two rows of tile straps, respectively. Embossed patterns may be formed respectively.
상기한 구성에 의하면, 다단 구조로 형성된 압연롤러의 외주면에 형성된 소정의 양각무늬 형태에 따라 다양한 음각무늬를 가진 타일 스트랩이 압출성형될 수 있기 때문에 타일 스트랩이 절단공정을 거쳐 건조 및 환원소성되면 다양한 음각무늬를 가진 타일의 제조될 수 있다. 그리고, 2줄의 타일 스트랩이 압출되어 나오도록 이루어진 타일제조방법 및 타일제조장치에 따르면, 진공토련성형시간의 단축을 물론 그 이후의 타일제조공정도 이에 따라 단축되므로 타일의 생산성이 현저하게 향상된다.According to the above configuration, since the tile straps having various intaglio patterns can be extruded according to a predetermined relief pattern formed on the outer circumferential surface of the rolling roller formed in a multi-stage structure, the tile straps are dried and reduced-fired through a cutting process. Tiles with intaglio can be made. In addition, according to the tile manufacturing method and the tile manufacturing apparatus, in which two rows of tile straps are extruded, the productivity of the tile is markedly improved since not only the shortening time of vacuum molding time but also the subsequent tile manufacturing process are shortened accordingly. .
본 발명의 다른 특징 및 이점들은 첨부도면에 의거한 다음의 설명으로 더욱 명백해질 것이다.Other features and advantages of the present invention will become more apparent from the following description based on the accompanying drawings.
도 1은 본 발명에 따른 타일제조방법을 나타내는 블록도로서, 본 발명에 따른 타일제조방법은 다음과 같은 공정을 차례로 거쳐 이루어진다.1 is a block diagram showing a tile manufacturing method according to the present invention, the tile manufacturing method according to the present invention is made through the following steps in sequence.
① 원료혼합공정① Raw material mixing process
이 공정에 있어서는, 수분이 대략 20% 함유된 점토 분말 및 고령토 분말을 통상의 혼합기에 투입하여 혼합한다.In this step, clay powder and kaolin powder containing approximately 20% of water are added to a conventional mixer and mixed.
② 원료공급공정② Raw Material Supply Process
원료혼합공정을 거친 점토 분말 및 고령토 분말의 혼합물을 컨베이어 벨트에 의하여 롤러 크러셔에 공급한다.A mixture of clay powder and kaolin powder, which has been subjected to a raw material mixing process, is fed to a roller crusher by a conveyor belt.
③ 분쇄공정③ grinding process
컨베이어 벨트에 의하여 이송되는 혼합물을 호퍼를 통하여 롤러 크러셔 내부에 투입하면서 롤러에 의하여 미세하게 분쇄한다.The mixture conveyed by the conveyor belt is finely pulverized by the roller while being introduced into the roller crusher through the hopper.
④ 혼수·혼련공정④ Coma and Kneading Process
분쇄공정을 거쳐 컨베이어 벨트에 혼합 분쇄불이 혼수·혼련기의 베이스에 이송되면, 수분이 22% 정도가 되도록 물공급호스를 통하여 혼합 분쇄물에 수분을 공급하면서 혼수·혼련기의 베이스상에 나란하게 설치된 한 쌍의 스크류우에 의하여 혼합 분쇄물을 분쇄 및 혼합하면서 압송한다.When the mixed grinding fire is conveyed to the base of the coma and kneader through the grinding process, the water is mixed with the base of the coma and kneader while supplying water to the mixed grind through the water supply hose so that the moisture is about 22%. The mixed pulverized product is conveyed while being pulverized and mixed by a pair of screw threads.
⑤ 진공토련성형공정⑤ Vacuum drill molding process
혼수·혼련공정을 거친 혼합물이 컨베이어에 의하여 도 2 및 도 3에 도시된 바와 같이, 진공토련성형기(1)의 호퍼(11)를 통하여 진공토련성형기(1)의 컨테이너(12) 내부에 공급되면 타일(51)(도 10 내지 도 12 참조)이 균일한 물성을 가지도록 하기 위하여 진공압에 의하여 혼합물에 포함된 공기를 제거한다. 공기가 제거된 점토 및 고령토 혼합물 빌렛을 압출스크류우 램에 의하여 노즐(13) 쪽으로 밀어냄으로써 노즐(13)의 출구를 통하여 도 4 내지 도 7에 도시된 바와 같이, 타일 스트랩(5)을 연속 압출한다.When the mixture after the mixing / kneading process is supplied to the inside of the container 12 of the vacuum drill machine 1 through the hopper 11 of the vacuum drill machine 1 as shown in FIGS. 2 and 3 by a conveyor. In order for the tile 51 (see FIGS. 10 to 12) to have uniform physical properties, air contained in the mixture is removed by vacuum pressure. Continuously extruding the tile strap 5 through the outlet of the nozzle 13 by pushing the air-depleted clay and kaolin mixture billet towards the nozzle 13 by means of an extrusion screw ram. do.
이 압출되는 타일 스트랩(5)의 단면은 노즐(13)의 압출부의 단면과 동일한 형상을 하게 된다. 이 타일 스트랩(5)은 압출되면서 노즐(13)의 출구단에 인접하여 설치된 상·하부 압연롤러(21)(22) 사이를 통과하면서 상·하면이 가압된다. 이 가압에 의하여, 상부 압연롤러(21)의 외주면에 형성된 소정의 양각무늬(211)에 의하여 타일 스트랩(5)의 상면에는 상부 압연롤러(21)의 양각무늬(211)와 대응하는 음각무늬(511)가 형성되고, 하부 압연롤러(22)의 외주면에 형성된 다수의 리브(221)에 의하여 타일 스트랩(5)의 하면에는 하부 압연롤러(22)의 리브(221)와 대응하는 그루브(521)가 다수개 길이방향으로 형성된다.The cross section of the extruded tile strap 5 has the same shape as the cross section of the extruded portion of the nozzle 13. The upper and lower surfaces of the tile strap 5 are pressed while passing between the upper and lower rolling rollers 21 and 22 provided adjacent to the outlet end of the nozzle 13 while being extruded. By this pressing, the upper surface of the tile strap 5 by the predetermined relief pattern 211 formed on the outer circumferential surface of the upper rolling roller 21 on the upper surface of the tile roll 5, the intaglio pattern corresponding to the embossed pattern 211 of the upper rolling roller 21 ( 511 is formed, and the groove 521 corresponding to the rib 221 of the lower rolling roller 22 is formed on the lower surface of the tile strap 5 by a plurality of ribs 221 formed on the outer circumferential surface of the lower rolling roller 22. A plurality of are formed in the longitudinal direction.
상기 상부 압연롤러(21)의 양각무늬(211)는 예컨대, 도 5에 도시된 바와 같은 조약돌 형태나 도 6에 도시된 바와 같은 나이테 형태 등 다양한 형태로 이루어질 수 있고, 이에 따라 타일 스트랩(5)이 상하의 압연롤러(21)(22) 사이를 통과하면, 상기한 바와 같은 상부 압연롤러(21)의 양각무늬(211)에 대응하여, 타일 스트랩(5)의 상면에는 도 10에 도시된 바와 같은 조약돌 형태나 도 11에 도시된 바와 같은 나이테 형태의 음각무늬(511)가 형성될 수 있다.The embossed pattern 211 of the upper rolling roller 21 may be formed in various forms such as, for example, a pebble shape as shown in FIG. 5 or a ring type as shown in FIG. 6, and thus the tile strap 5. When passing between the upper and lower rolling rollers 21 and 22, the upper surface of the tile strap 5 corresponds to the embossed pattern 211 of the upper rolling roller 21 as shown in FIG. 10. A cobblestone pattern or a ring-shaped intaglio pattern 511 as illustrated in FIG. 11 may be formed.
또한, 본 발명에 있어서는, 특히 상부 압연롤러(21)는 도 7에 도시된 바와 같이 외주면이 다단 구조로 이루어짐과 아울러 각 단의 외주면에는 다양한 양각무늬(211)가 복합적으로 형성되어 이루어짐으로써, 타일 스트랩(5)이 상하의 압연롤러(21)(22) 사이를 통과하면 타일 스트랩(5)의 상면이 도 12에 도시된 바와 같은 다단 구조로 형성됨과 아울러 각 단에는 다양한 형태의 음각무늬(511)가 복합적으로 형성될 수 있게 된다.In addition, in the present invention, in particular, the upper rolling roller 21, as shown in Figure 7, the outer peripheral surface is made of a multi-stage structure, and various embossed patterns 211 are formed on the outer peripheral surface of each stage, the tile, When the strap 5 passes between the upper and lower rolling rollers 21 and 22, the upper surface of the tile strap 5 is formed in a multi-stage structure as shown in FIG. 12, and various intaglio patterns 511 are formed at each end. Can be formed complex.
그리고, 하부 압연롤러(22)의 리브(221)는 그 끝부분의 폭이 바닥면의 폭보다 크도록 이루어짐으로써 타일 스트랩(5)의 그루브(521)는 예각홈 형태로 이루어지는 것이 바람직하다. 즉, 그루브(521)가 예각홈 형태로 이루어짐으로써 채널형 홈 형태로 되어 있을 때보다 타일 시공시 모르타르와 같은 습식소재를 파지하는 힘이 더 크게 작용함으로써 벽면이나 바닥면에 타일이 견고하게 부착될 수 있다.And, the rib 221 of the lower rolling roller 22 is made so that the width of the end portion is larger than the width of the bottom surface groove 521 of the tile strap 5 is preferably made of an acute groove shape. That is, since the groove 521 is formed in the shape of an acute groove, the force of gripping a wet material such as mortar acts more when the tile is applied than when the groove is in the form of a channel groove so that the tile is firmly attached to the wall or the floor. Can be.
한편, 도면에는 도시되지 않았지만, 이 압출되는 타일 스트랩(5)의 단면은 노즐(13)의 압출부의 단면과 동일한 형상을 하게 되는 점을 감안하여 상하의 압연롤러(21)(22)를 거치기 전에 압출되는 타일 스트랩(5)의 상면이 다단 구조로 형성되도록 함과 아울러 타일 스트랩(5)의 하면에는 다수의 그루브(521)가 미리 형성될 수 있도록 노즐(13)이 구성될 수 있다. 즉, 노즐 내주면의 상부에 다단 구조로 된 면이 설치되고, 노즐 내주면의 하부에는 다수의 리브가 형성된 면이 설치되면 된다.On the other hand, although not shown in the drawing, the cross section of the extruded tile strap 5 has the same shape as the cross section of the extruded portion of the nozzle 13, so that it is extruded before passing through the upper and lower rolling rollers 21 and 22. The nozzle 13 may be configured such that the upper surface of the tile strap 5 is formed in a multi-stage structure, and the plurality of grooves 521 may be previously formed on the lower surface of the tile strap 5. That is, a surface having a multi-stage structure may be provided above the nozzle inner circumferential surface, and a surface having a plurality of ribs formed below the nozzle inner circumferential surface.
위에서는 1줄의 타일 스트랩(5)을 압출성형하는 진공토련성형공정이 상세히 설명되어 있지만, 본 발명에 따르면, 타일의 생산성 향상을 위하여 2줄의 타일 스트랩(5)(5)을 동시에 압출성형할 수 있도록 진공토련성형공정이 이루어질 수 있다. 즉, 이 경우에는, 도 8에 도시된 바와 같이, 진공토련성형기(1)의 노즐(13) 내부 중앙에 수평으로, 상하면에 다수의 리브(141)(142)가 길이방향으로 형성된 압출다이(14)가 설치됨으로써 노즐(13)의 내부를 상하로 구획되도록 한다. 따라서, 압출스크류우 램에 의하여 컨테이너(12) 내의 점토 및 고령토 혼합 빌렛이 압력을 받아 노즐(13)쪽으로 밀려 도 9에 도시된 바와 같이, 타일 스트립(5)(5)으로 압출성형될 때 빌렛이 압출다이(14)의 상하면을 통과하여 압출됨으로써 상하의 타일 스트랩(5)(5)의 접촉면, 즉 상부 타일 스트랩(5)의 하면과 하부 타일 스트랩(5)의 상면에는 압출다이(14)의 상하면에 각각 형성된 다수의 리브(141)(142)에 의하여 다수의 그루브(521)가 길이방향으로 각각 형성된다. 상기한 바와 같이, 상하의 타일 스트랩(5)(5)이 노즐(13)을 통하여 압출되면, 상하의 타일 스트랩(5)(5)은 노즐(13)의 출구단에 인접한 상하의 압연롤러(26)(27) 사이를 통과하면서 상하의 압연롤러(26)(27)에 의하여 가압을 받게 된다. 이 경우에는 상하의 압연롤러(26)(27) 공히 외주면에 소정의 양각무늬(211)가 각각 형성된다. 즉, 상하의 압연롤러(26)(27)에 동일한 양각무늬(211)가 각각 형성될 수 있고, 도 8 및 도 9에 도시된 바와 같이, 서로 다른 양각무늬(211)(211)(도면에서는 상부 압연롤러(26)에는 조약돌 형태의 양각무늬(211)가 형성되어 있고, 하부 압연롤러(27)에는 나이테 형태의 양각무늬(211)가 형성된 것이 도시됨)가 형성될 수 있다. 따라서, 이 상하의 압연롤러(26)(27)의 가압에 의하여 상부 타일 스트랩(5)의 상면에는 상부 압연롤러(26)의 양각무늬(211)와 대응하는 음각무늬(511)가 형성되고, 하부 타일 스트랩(5)의 하면에는 하부 압연롤러(27)의 양각무늬(211)와 대응하는 음각무늬(511)가 동시에 형성된다.In the above, the vacuum drill molding process for extruding a single row of tile straps 5 is described in detail, but according to the present invention, two rows of tile straps 5 and 5 are simultaneously extruded to improve the productivity of the tile. Vacuum drill molding process can be made to do so. That is, in this case, as shown in Fig. 8, the extrusion die (10) in which the plurality of ribs 141, 142 are formed horizontally in the center of the nozzle 13 of the vacuum drill machine 1 and in the longitudinal direction. The 14 is installed to partition the inside of the nozzle 13 up and down. Thus, the clay and kaolin mixing billets in the container 12 are pushed toward the nozzles 13 under pressure by means of an extrusion screw ram and extruded into the tile strips 5 and 5, as shown in FIG. 9. By extruding through the upper and lower surfaces of the extrusion die 14, the contact surface of the upper and lower tile straps 5 and 5, that is, the lower surface of the upper tile strap 5 and the upper surface of the lower tile strap 5, A plurality of grooves 521 are formed in the longitudinal direction by the plurality of ribs 141 and 142 formed on the upper and lower surfaces, respectively. As described above, when the upper and lower tile straps 5 and 5 are extruded through the nozzle 13, the upper and lower tile straps 5 and 5 are upper and lower rolling rollers 26 adjacent to the outlet end of the nozzle 13 ( It is pressurized by the upper and lower rolling rollers 26 and 27 while passing between them. In this case, predetermined embossed patterns 211 are formed on the outer circumferential surface of the upper and lower rolling rollers 26 and 27, respectively. That is, the same embossed pattern 211 may be formed on the upper and lower rolling rollers 26 and 27, respectively, and as shown in FIGS. 8 and 9, different embossed patterns 211 and 211 (the upper part in the drawing). The rolled roller 26 has a pebble embossed pattern 211 is formed, the lower rolling roller 27 is shown that the ring-shaped embossed pattern 211 is formed). Accordingly, by pressing the upper and lower rolling rollers 26 and 27, the upper surface of the upper tile strap 5 is formed with an intaglio pattern 511 corresponding to the embossed pattern 211 of the upper rolling roller 26, The lower surface of the tile strap 5 is formed with the embossed pattern 211 and the corresponding intaglio pattern 511 of the lower rolling roller 27 at the same time.
또한, 상하의 압연롤러(26)(27)의 각각의 외주면이 도 7에 도시된 바와 같은 상부 압연롤러와 같은 다단 구조의 외주면 형태로 이루어질 수 있다. 이 경우에는 노즐(13) 내주면의 상부 및 하부에 각각 다단 구조의 면이 설치됨으로써 상하의 압연롤러(21)(22)를 거치기 전에 압출되는 상부 타일스트랩(5)의 상면 및 하부 타일 스트랩(5)의 하면이 미리 다단 구조로 형성될 수 있도록 하는 것이 바람직하다. 또한, 이와는 달리, 압출다이(14)의 형태를 날일(日)자 형태로 형성하여 중앙부의 상·하면에는 리브(141)(142)를 형성하고, 상·하부는 각각 다단 구조로 형성하면, 위와 동일한 다단 구조의 타일 스트랩(5)이 2줄 얻어질 수 있다.In addition, the outer circumferential surface of each of the upper and lower rolling rollers 26 and 27 may be formed in the form of an outer circumferential surface of a multi-stage structure such as an upper rolling roller as shown in FIG. 7. In this case, the upper and lower tile straps 5 of the upper tile strap 5 which are extruded before passing through the upper and lower rolling rollers 21 and 22 are installed by respectively providing the upper and lower surfaces of the inner circumferential surface of the nozzle 13. It is desirable to allow the bottom surface of the to be formed in a multi-stage structure in advance. Alternatively, if the extrusion die 14 is formed in the shape of a blade, ribs 141 and 142 are formed on the upper and lower surfaces of the central portion, and the upper and lower portions are formed in a multistage structure, respectively. Two rows of tile straps 5 of the same multistage structure can be obtained.
상기한 바와 같이 상하의 타일 스트랩(5)(5)이 상하의 압연롤러(26)(27) 사이를 통과하면 컨베이어(3)(도 4 참조)를 따라 절단기쪽으로 이송된다.As described above, when the upper and lower tile straps 5 and 5 pass between the upper and lower rolling rollers 26 and 27, they are conveyed toward the cutter along the conveyor 3 (see FIG. 4).
⑥ 절단공정⑥ Cutting process
진공토련성형공정을 거친 타일 스트랩(5)은 이송 켄베이어(3) 도중에 설치된 절단기에 의하여 소정의 크기로 연속 절단되어 타일(51)(도 10 내지 도 12 참조)로 형성된다. 상하의 타일 스트랩(5)(5)이 상하로 겹쳐진 채 동시에 이송되어 올 경우에는 상하의 타일 스트랩(5)(5)이 동시에 연속적으로 절단되며, 따라서 1줄만의 타일 스트랩(5)을 절단할 때보다 절단작업시간이 훨씬 줄어든다. 그리고, 절단시에는 후술하는 건조 및 소성공정 중에 타일(51)이 수축되는 량을 고려하여 길이방향의 수축량을 더한 길이로 절단하는 것이 바람직하다. 이 절단공정에서 절단길이가 맞지 않는 등 잘못 절단된 타일(51)은 재생을 위하여 진공토련성형기(1)의 호퍼(11)를 통하여 컨테이너(12) 내부에 투입되어 다시 타일 스트랩(5)을 압출하는데 사용된다.The tile strap 5 which has undergone the vacuum drill molding process is continuously cut into a predetermined size by a cutter provided in the middle of the conveying kenvey 3 and is formed into a tile 51 (see FIGS. 10 to 12). When the upper and lower tile straps 5 and 5 are conveyed at the same time while being piled up and down, the upper and lower tile straps 5 and 5 are cut continuously at the same time, and thus, than when cutting only one row of the tile straps 5. Cutting time is much shorter. In addition, at the time of cutting | disconnection, it is preferable to cut | disconnect to the length which added the shrinkage amount of the longitudinal direction in consideration of the quantity which the tile 51 shrinks during the drying and baking process mentioned later. In this cutting process, the tiles 51 that are incorrectly cut, such as the cutting lengths do not fit, are introduced into the container 12 through the hopper 11 of the vacuum drill machine 1 for regeneration, and the tile strap 5 is extruded again. It is used to
⑦ 건조공정⑦ Drying process
절단기에 의하여 절단된 타일(51)에는 아직 소정의 수분이 함유되어 있기 때문에 절단기에 의하여 절단된 타일(51)을 건조대차에 적재하여 건조실에 투입하고 100℃ ∼ 120℃ 범위의 온도하에서 약 2일간 건조함으로써 상기 수분을 제조한다.Since the tile 51 cut by the cutter still contains a predetermined amount of water, the tile 51 cut by the cutter is loaded into a drying truck, placed in a drying chamber, and then put into the drying chamber for about 2 days at a temperature ranging from 100 ° C to 120 ° C. The moisture is prepared by drying.
⑧ 소성공정⑧ Firing process
건조공정을 거쳐 수분이 제거된 건조 타일(51)을 경화시키기 위하여 소성대차에 적재하여 건조실로부터 소성로에 투입하여 1,250℃∼1300℃ 범위의 온도하에서 20시간 내지 22시간 동안 환원소성시켜 최종적으로 타일(51)을 완성한 후 출하한다.In order to cure the drying tile 51 from which moisture is removed through the drying process, the drying tile 51 is loaded into a baking trolley and put into a baking furnace from a drying chamber, and reduced baking is carried out for 20 to 22 hours at a temperature ranging from 1,250 ° C to 1300 ° C. Complete 51) and ship.
상기한 바와 같은 제조공정을 거쳐 획득되는 타일(51)은 하면에는 길이방향을 따라 다수의 그루브(521)가 형성됨으로써 시공시 모르타르와 같은 습식소재가 상기 그루브(521)에 삽입되어 파지됨으로써 타일(51)과, 벽면 또는 바닥면과의 부착력이 현저하게 향상된다. 특히, 그루브(521)가 예각홈 형태로 형성될 경우에는 타일(51)과, 벽면 또는 바닥면과의 부착력은 더욱 커진다. 또한, 타일(51)의 상면에는 압연롤러(21)(26)(27)의 외주면에 형성되는 양각무늬(211)의 형태에 따라 다양한 형태의 음각무늬(511)가 형성될 수 있을 뿐만 아니라 타일(51)의 상면이 다단 구조로 형성됨으로써, 상기한 바와 같이 제조되는 타일(51)들을 사용하여 벽면이나 바닥면을 마감처리할 때에는 일반적인 타일 배열방법으로 타일을 배열하더라도 타일(51)의 다양한 음각무늬(511)에 의하여 다양한 장식이 가능할 뿐만 아니라 일반적인 배열방법과는 다른 배열방법이 채용될 경우에는 더욱 다양한 장식효과를 얻을 수 있다.The tile 51 obtained through the manufacturing process as described above is formed with a plurality of grooves 521 formed in a lower surface thereof in the lower surface thereof so that a wet material such as mortar is inserted into the grooves 521 and gripped during construction. 51) and the adhesion between the wall surface or the bottom surface is remarkably improved. In particular, when the groove 521 is formed in the shape of an acute groove, the adhesion force between the tile 51 and the wall surface or the bottom surface is further increased. In addition, according to the shape of the embossed pattern 211 formed on the outer circumferential surface of the rolling rollers (21), (26), (27) on the upper surface of the tile 51, various types of intaglio patterns (511) may be formed. Since the upper surface of the 51 is formed in a multi-stage structure, when finishing the wall surface or the bottom surface using the tiles 51 manufactured as described above, various intaglio of the tile 51 even if the tiles are arranged in a general tile arrangement method. By the pattern 511, not only various decorations are possible, but also when a different arrangement method is adopted than a general arrangement method, more various decoration effects can be obtained.
상기한 바와 같이 구성된 본 발명에 의하면, 타일(51)이 그루브(521)에 의하여 벽면이나 바닥면에 견고하게 부착될 수 있으므로 타일 시공품질을 향상시킬 수 있다. 또한, 타일(51)이 다양한 음각무늬(511) 뿐만 아니라 다단 구조의 상면을 가짐으로써 다양한 장식효과를 거둘 수 있게 되므로, 타일 시공범위가 확대됨과 아울러 장식성이 우수하여 건축물의 품질 향상을 도모할 수 있다. 더욱이, 타일 스트랩(5)을 동시에 2줄을 압출성형할 수 있는 타일제조방법 및 장치가 채용되면, 타일의 생산성이 향상되고, 이에 따라 타일제조원가의 절감된다.According to the present invention configured as described above, the tile 51 can be firmly attached to the wall or the bottom surface by the groove 521 can improve the tile construction quality. In addition, since the tile 51 has various decorative effects as well as various intaglio patterns 511, it is possible to achieve a variety of decorative effects, thereby expanding the scope of tile construction and excellent decorative properties to improve the quality of the building. have. Moreover, when the tile manufacturing method and apparatus capable of extruding two rows of tile straps 5 at the same time are adopted, the productivity of the tiles is improved, thereby reducing the tile manufacturing cost.

Claims (7)

  1. 원료혼합공정, 원료공급공정, 분쇄공정 및 혼수·혼련공정을 차례로 거친 점토 및 고령토 혼합물을 진공토련성형기에 의하여 연속압출성형하여 타일 스트랩으로 형성함과 아울러 압출되어 나오는 타일 스트랩의 상·하면을 진공토련성형기의 노즐의 출구단에 인접하여 설치되는 상·하부 압연롤러에 의하여 가압하는 진공토련성형공정과, 상기 진공토련성형공정을 거쳐 이송되는 타일 스트랩을 소정의 길이로 연속 절단하여 타일을 만드는 절단공정과, 상기 절단된 타일을 건조 및 환원소성하는 공정을 포함하는 타일 제조공정에 있어서,The clay and kaolin mixtures, which have undergone the raw material mixing process, the raw material feeding process, the crushing process, and the mixing / mixing process, are continuously extruded by a vacuum drill machine to form a tile strap, and the upper and lower surfaces of the extruded tile strap are vacuumed. Vacuum forming process for pressurizing by the upper and lower rolling rollers installed adjacent to the outlet end of the nozzle of the pottery molding machine, and cutting to make tiles by continuously cutting the tile straps transferred through the vacuum drilling process to a predetermined length. In the tile manufacturing process comprising the step of drying and reducing the calcining the cut tile,
    상기 진공토련성형공정 중 압출되어 나오는 타일 스트랩의 상면은 다단 구조로 형성되고,The upper surface of the tile strap extruded during the vacuum drilling process is formed in a multi-stage structure,
    다단 구조로 형성된 타일 스트랩의 상면은 외주면에 소정의 양각무늬가 형성됨과 아울러 외주면이 다단으로 형성된 상부 압연롤러의 가압에 의하여 상기 양각무늬에 대응하는 음각무늬가 연속적으로 형성되며,The upper surface of the tile strap formed of a multi-stage structure has a predetermined embossed pattern is formed on the outer circumferential surface and the negative pattern corresponding to the embossed pattern is continuously formed by pressing the upper rolling roller formed of the multi-stage outer circumferential surface,
    타일 스트랩의 하면에는 외주면에 다수의 리브가 형성된 하부 압연롤러의 가압에 의하여 상기 리브에 대응하는 다수의 그루브가 압출방향으로 연속적으로 형성됨을 특징으로 하는 타일제조방법.And a plurality of grooves corresponding to the ribs are continuously formed in the extrusion direction by pressing the lower rolling roller having a plurality of ribs formed on the outer circumferential surface of the tile strap.
  2. 원료혼합공정, 원료공급공정, 분쇄공정 및 혼수·혼련공정을 차례로 거친 점토분말과 고령토 분말과의 혼합물을 진공토련성형기에 의하여 노즐을 통하여 연속압출성형하여 타일 스트랩으로 형성함과 아울러 압출되어 나오는 타일 스트랩의 상·하면을 노즐의 출구단에 인접하여 설치되는 상·하부 압연롤러에 의하여 가압하는 진공토련성형공정과, 상기 진공토련성형공정을 거쳐 이송되는 타일 스트랩을 소정의 길이로 연속 절단하여 타일을 만드는 절단공정과, 상기 절단된 타일을 건조 및 환원소성하는 공정을 포함하는 타일 제조공정에 있어서,The clay powder and kaolin powder mixture, which have undergone the raw material mixing process, the raw material supply process, the crushing process, and the mixing and mixing process, are continuously extruded through a nozzle using a vacuum drill machine to form a tile strap and extruded tiles. A vacuum drill molding process for pressurizing the upper and lower surfaces of the strap by means of upper and lower rolling rollers provided adjacent to the outlet end of the nozzle, and the tile straps conveyed through the vacuum drilling process are continuously cut to a predetermined length. In the tile manufacturing process comprising a cutting step of forming a step, and the step of drying and reducing the calcining the cut tile,
    상기 진공토련성형공정 중 상·하면에 다수의 리브를 가져 진공토련성형기의 노즐 내부에 설치되는 압출다이에 의하여 2줄의 타일 스트랩이 겹쳐진 상태로 압출성형되어 나옴으로써 상부 타일 스트랩의 하면과 하부 타일 스트랩의 상면에 상기 리브와 대응하는 다수의 그루브가 형성되고,The lower and lower tiles of the upper tile strap are extruded in a state where two rows of tile straps are overlapped by an extrusion die installed in the nozzle of the vacuum drill machine having a plurality of ribs on the upper and lower surfaces of the vacuum drill molding process. On the upper surface of the strap is formed a plurality of grooves corresponding to the ribs,
    상기 다수의 그루브가 형성되어 나오는 상하의 타일 스트랩은 노즐의 출구단에 인접하여 설치됨과 아울러 외주면에 각각 소정의 양각무늬가 형성된 상·하부 압연롤러의 사이를 통과하여 가압됨으로써 상부 타일 스트랩의 상면과 하부 타일 스트랩의 하면에는 상기 상하의 압연롤러의 양각무늬에 대응하는 음각무늬가 연속적으로 각각 형성됨을 특징으로 하는 타일제조방법.The upper and lower tile straps, in which the plurality of grooves are formed, are installed adjacent to the outlet end of the nozzle and pressed through the upper and lower rolling rollers each having a predetermined embossed pattern on the outer circumferential surface thereof so that the upper and lower surfaces of the upper tile straps are pressed. A tile manufacturing method, characterized in that the intaglio pattern corresponding to the embossed pattern of the upper and lower rolling rollers are formed successively on the lower surface of the tile strap.
  3. 원료혼합공정, 원료공급공정, 분쇄공정 및 혼수·혼련공정을 차례로 거친 점토 분말과 고령토 분말과의 혼합물을 호퍼를 통하여 컨테이너 내부에 투입한 후 공기를 제거하여 노즐을 통하여 연속압출성형함으로써 타일 스트랩으로 형성함과 아울러 노즐을 통하여 압출되는 타일 스트랩의 상·하면을 노즐의 출구단에 인접하여 상하로 설치된 한 쌍의 압연롤러에 의하여 가압하도록 이루어진 진공토련성형기를 포함하는 타일제조장치에 있어서,The mixture of clay powder and kaolin powder, which have undergone the raw material mixing process, the raw material feeding process, the crushing process, and the mixing and mixing process, is introduced into the container through a hopper, and the air is removed to continuously extrude through a nozzle to form a tile strap. In the tile manufacturing apparatus comprising a vacuum drill machine for forming and pressing the upper and lower surfaces of the tile strap is extruded through the nozzle by a pair of rolling rollers installed up and down adjacent to the outlet end of the nozzle,
    상기 상부 압연롤러는 외주면이 다단 구조로 되어 있음과 아울러 그 외주면에는 압출되어 나오는 타일 스트랩의 상면에 상부 압연롤러의 가압에 의하여 소정의 음각무늬가 형성되도록 소정의 양각무늬가 형성되고,The upper rolling roller has a multi-stage structure of the outer circumferential surface, and a predetermined embossed pattern is formed on the outer circumferential surface of the upper rolling roller to form a predetermined intaglio pattern by pressing the upper rolling roller.
    상기 하부 압연롤러의 외주면에는 압출되어 나오는 타일 스트랩의 하면에 하부 압연롤러의 가압에 의하여 길이방향을 따라 다수의 그루브가 형성되도록 다수의 리브가 형성되어 있는 것을 특징으로 하는 타일제조장치.The outer peripheral surface of the lower rolling roller tile manufacturing apparatus, characterized in that a plurality of ribs are formed on the lower surface of the extruded tile strap to form a plurality of grooves in the longitudinal direction by the pressure of the lower rolling roller.
  4. 제 3 항에 있어서, 상기 진공토련성형기의 노즐은 내주면 상부에 설치되는 다단 구조의 면과 내주면 하부에 설치되는 다수의 리브를 포함하여 이루어지는 것을 특징으로 하는 타일제조장치.4. The tile manufacturing apparatus according to claim 3, wherein the nozzle of the vacuum drill machine comprises a surface of a multi-stage structure installed on an inner circumferential surface and a plurality of ribs provided on a lower portion of the inner circumferential surface.
  5. 원료혼합공정, 원료공급공정, 분쇄공정 및 혼수·혼련공정을 차례로 거친 점토 분말과 고령토 분말과의 혼합물을 호퍼를 통하여 컨테이너 내부에 투입한 후 공기를 제거하여 노즐을 통하여 연속압출성형함으로써 타일 스트랩으로 형성함과 아울러 노즐을 통하여 압출되는 타일 스트랩의 상·하면을 노즐의 출구단에 인접하여 상하로 설치된 한 쌍의 압연롤러에 의하여 가압하도록 이루어진 진공토련성형기를 포함하는 타일제조장치에 있어서,The mixture of clay powder and kaolin powder, which have undergone the raw material mixing process, the raw material feeding process, the crushing process, and the mixing and mixing process, is introduced into the container through a hopper, and the air is removed to continuously extrude through a nozzle to form a tile strap. In the tile manufacturing apparatus comprising a vacuum drill machine for forming and pressing the upper and lower surfaces of the tile strap is extruded through the nozzle by a pair of rolling rollers installed up and down adjacent to the outlet end of the nozzle,
    2줄의 타일 스트랩이 동시에 겹쳐진 상태로 압출성형되도록 함과 아울러 겹쳐져 서로 접촉하는 면에 다수의 그루브가 길이방향으로 형성되도록 상하면에 다수의 리브가 각각 형성된 압출다이가 노즐 내부에 수평으로 설치되고,Extrusion dies having a plurality of ribs formed on the upper and lower surfaces are horizontally installed inside the nozzle so that two rows of tile straps can be extruded at the same time, and a plurality of grooves are formed in the longitudinal direction on the overlapping and contacting surfaces.
    상하의 타일 스트랩의 다른 면에 소정의 음각무늬가 각각 형성되도록 상기 상·하부 압연롤러의 외주면에는 상기 음각무늬와 대응하는 양각무늬가 각각 형성되어 있는 것을 특징으로 하는 타일제조장치.And an embossed pattern corresponding to the intaglio pattern on the outer circumferential surface of the upper and lower rolling rollers, respectively, so that a predetermined intaglio pattern is formed on the other side of the upper and lower tile straps, respectively.
  6. 제 5 항에 있어서, 상기 상·하부 압연롤러 중 어느 한 압연롤러는 외주면이 다단으로 형성되어 있는 것을 특징으로 하는 타일제조장치.The tile manufacturing apparatus according to claim 5, wherein one of the upper and lower rolling rollers has an outer circumferential surface formed in multiple stages.
  7. 점토 및 고령토를 주원료로 하여 이루어지는 타일로서,As a tile composed mainly of clay and kaolin,
    상면이 다단 구조로 형성됨과 아울러 다단 구조의 표면에는 소정의 음각무늬가 단일 또는 복합적으로 형성되고,In addition to the upper surface is formed in a multi-stage structure, a predetermined intaglio pattern is formed on the surface of the multi-stage structure, single or multiple,
    하면에는 길이방향으로 다수의 그루브가 형성되어 이루어지는 것을 특징으로 하는 타일.The lower surface of the tile is characterized in that a plurality of grooves are formed in the longitudinal direction.
KR1019970014471A 1997-04-18 1997-04-18 Tile, method and device for manufacturing the tile KR100215359B1 (en)