JPH119126A - Animal vessel - Google Patents

Animal vessel

Info

Publication number
JPH119126A
JPH119126A JP18735597A JP18735597A JPH119126A JP H119126 A JPH119126 A JP H119126A JP 18735597 A JP18735597 A JP 18735597A JP 18735597 A JP18735597 A JP 18735597A JP H119126 A JPH119126 A JP H119126A
Authority
JP
Japan
Prior art keywords
animal
container
norbornene
ring
preferably
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP18735597A
Other languages
Japanese (ja)
Other versions
JP3807461B2 (en
Inventor
Kazuyuki Kobuchi
Koji Minami
幸治 南
和之 小渕
Original Assignee
Nippon Zeon Co Ltd
日本ゼオン株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Zeon Co Ltd, 日本ゼオン株式会社 filed Critical Nippon Zeon Co Ltd
Priority to JP18735597A priority Critical patent/JP3807461B2/en
Publication of JPH119126A publication Critical patent/JPH119126A/en
Application granted granted Critical
Publication of JP3807461B2 publication Critical patent/JP3807461B2/en
Anticipated expiration legal-status Critical
Application status is Expired - Fee Related legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide an animal vessel that is transparent and excellent in resistance to chemicals and shock, moreover can be readily washed off the excretions of animals. SOLUTION: A molding material comprising the polymer prepared by the ring-opening polymerization of norbornene monomers containing more than 50 wt.% of dicyclic or tricyclic norbornenes or their hydrogenated product is used to form the objective animal vessel. This vessel is transparent, excellent in the resistance to chemicals, particularly microbicidal agents, and to shock, further this vessel repels animal excretions and is readily washable. Mammalian animals as rats, mice, small-sized rabbits, reptiles and amphibia as snake, frog, turtle or lizard may be bred as a pet and mice, rats and guinea pigs also can be bred as an experimental small animal. Therefore this animal vessel is very useful for development of drugs and the medical industry.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は動物飼育用容器に関し、さらに詳しくは、透明性が高く内容物視認性に優れており、動物の排泄物の洗浄が容易であり、各種殺菌剤等に対する耐薬品性、耐熱性、耐衝撃性が優れた、動物容器に関する。 The present invention relates to relates to a container for animal breeding, more particularly, it is excellent in high content visibility transparency, easy cleaning of animal waste, resistance against various fungicides such as chemical resistance, heat resistance, impact resistance and excellent, on animal container.

【0002】 [0002]

【従来の技術】従来、ネズミや小型うさぎ等の哺乳類、 Conventionally, mammals such as rats and small rabbits,
ヘビ、蛙、亀、トカゲ等の両生類などをペット用あるいはマウス、ラット及びモルモットなどの哺乳類を実験用として飼育するための動物容器としては、金属製の網、 Snake, frog, turtle, amphibians etc. pet or mouse lizards, etc., as an animal container for rearing as experimental mammals such as rats and guinea pigs, metal net,
金属製のかご、金属板、ガラス、透明または不透明の熱可塑性樹脂が素材として使用されている。 Metal basket, metal plates, glass, transparent or opaque thermoplastic resin is used as a material. これらの素材の中でも、容器の移送に関して重量が軽い事や、透明で容器内部が確認できる事、量産が可能である事、落下等乱暴な取り扱いをしても、変形したり破損しにくい事などから、透明な熱可塑性樹脂が好ましく用いられてきている。 Among these materials, that the weight is light with respect to the transfer of the container and, it can be confirmed transparent container inside, that mass production is possible, even if the fall, such as rough handling, deformed or damaged difficult thing such as from transparent thermoplastic resin has been used preferably.

【0003】特に、実験用小動物用の飼育容器の場合は、水等で洗浄し、動物の病原菌感染防止のための滅菌を行った上で繰返し使用される。 In particular, in the case of breeding containers for small laboratory animals, and washed with water or the like, are repeatedly used after performing sterilization for preventing animal pathogens infection. 洗浄では、汚れを効果的に落すために、必要により洗剤や、作業者が火傷しない程度の温度の温水洗浄をすることもあるが、洗浄の際の取扱いや、動物を飼育して実験時に取扱いの際に破損しない機械強度が動物容器には要求される。 The cleaning, handling in order to remove dirt effectively, and detergents necessary, but sometimes the temperature of the hot water washing to the extent that the operator does not burn, handling and during cleaning, during experiments with animal husbandry mechanical strength which is not damaged when the can is required for the animal container. また、動物容器のような容積の大きい物の殺菌では、各種殺菌剤等の水溶液に1晩浸漬したり、アルコール殺菌などの方法がとられるため、動物容器はアルコールや各種薬剤に対する耐薬品性を有していることが好ましい。 Further, in the sterilization of large ones volume such as an animal container, or immersed overnight in an aqueous solution of various fungicides, because a method such as an alcohol sterilization is taken, the chemical resistance animal container for alcohol and various drugs it is preferable to have.

【0004】従来、動物飼育用容器を成形するための熱可塑性樹脂材料としては、透明で、あることから、ポリエチレン樹脂、ポリプロピレン樹脂、ポリスチレン樹脂やポリカーボネート樹脂などが用いられてきた。 Conventionally, as the thermoplastic resin material for molding an animal rearing container, transparent, since there, polyethylene resins, polypropylene resins, polystyrene resins, polycarbonate resins have been used. ところが、ポリエチレン樹脂は機械強度、耐薬品性は優れるが、透明性が低く、動物容器にした場合に内容物を外から確認するのが困難であるという問題点があった。 However, the polyethylene resin has mechanical strength, chemical resistance is superior, low transparency, there is a problem that it is difficult to confirm the contents from the outside when the animal container. ポリプロピレン樹脂は機械強度、耐薬品性は優れるが、透明性が十分で無い等の問題点があった。 Polypropylene resin mechanical strength, but is superior chemical resistance, there are problems such as transparency is not sufficient. ポリスチレン樹脂は、透明であるいう点で優れているが、耐衝撃性をはじめとする機械強度が低く、成形時に割れやすいため動物容器のような大きな成形品を成形しにくく、できた動物容器も落したり、ぶつけたりのちょっとした衝撃で破損するという問題点があった。 Polystyrene resin is excellent in that it is transparent, mechanical strength is low, including impact resistance, large hard to the molded article by molding, such as fragile for animal container during molding, even animals vessel was It dropped or, there is a problem that damaged a little shock or hit. ポリカーボネート樹脂は透明性や耐衝撃性には優れるものの、耐薬品性が劣り、例えば動物飼育実験で慣用されるエチルアルコールなどの薬品に動物容器が接触した時にクラックと呼ばれる割れが発生し強度が低下するなどの不都合がある。 Although polycarbonate resin is excellent in transparency and impact resistance, poor chemical resistance, for example, cracking occurs strength called crack decreases when the animal container in contact with chemicals such as ethyl alcohol customary in animal breeding experiments there are inconveniences such as. 以上のように、従来から用いられている熱可塑性樹脂材料には、 As described above, the thermoplastic resin material that has been conventionally used,
透明で、耐衝撃性などの機械強度を有し、耐薬品性を備えた動物容器に適した材料は知られていなかった。 Transparent, has a mechanical strength such as impact resistance, materials suitable for animals vessel equipped with a chemical resistance has not been known.

【0005】また、動物容器には、飼育する動物の排泄物である糞や尿が付着し、洗浄しにく、汚れが堆積しやすいという問題がある。 Moreover, the animal container adhered bred to feces and urine is animal waste, washed difficulty, there is a problem that dirt is easily deposited. 特に実験小動物用の容器の場合は、その痕跡に雑菌が発生した場合、当初の目的である動物実験に支障をきたすなどの問題があった。 In particular, in the case of a container for a small laboratory animal, if the bacteria occurs in the trace, there has been a problem, such as an obstacle to animal experiments is the original purpose.

【0006】一方、透明性と耐熱性に優れ、成形収縮も小さい樹脂として、ノルボルネン類の開環重合体等が提案されており、該樹脂からなる成形材料で成形してなる成形品は、透明で、耐薬品性が良く、各種溶剤又は酸若しくはアルカリ等の各種薬品に対して侵されない、溶出物が少ないなどの特徴が知られており、主に使い捨てまたは短期の使用に適した医療用途への使用が知られていた。 On the other hand, excellent in transparency and heat resistance, as mold shrinkage is also small resin, ring-opening polymer and the like of norbornene have been proposed molded articles obtained by molding a molding material made of the resin, transparent in, good chemical resistance, not attacked against various chemicals, such as various solvents or acid or alkali, are known features such as a small eluate, the main disposable or short medical applications suitable for use in the use of it has been known. しかし、排泄物の付着やそれによる変性が少ないかどうか、動物飼育容器等の動物容器として長期間使用した時に成形品が変質するかどうかは知られておらず、また、従来の知見を元に予見することも不可能であった。 However, if adhesion and if it by degeneration less waste, molded articles is not known whether altered when used for a long period of time as an animal containers such as animal breeding container, also based on the conventional wisdom was impossible also be foreseen.

【0007】 [0007]

【発明が解決しようとする課題】本発明が解決しようとする課題は、透明で、耐薬品性、耐衝撃性に優れ、しかも動物の排泄物の易洗浄性に優れた動物容器を提供することにある。 An object of the present invention [0005] to solve is a transparent, chemical resistance, high impact resistance, yet providing an excellent animal containers easy cleaning of the animal waste It is in.

【0008】 [0008]

【課題を解決するための手段】本発明者らは、上記従来技術の問題点を解決すべく鋭意研究の結果、特定の単量体組成から開環重合される樹脂からなる成形材料で成形された動物容器が、透明で、殺菌剤等に対する耐薬品性、耐衝撃性に優れていること、動物の排泄物が付着しにくく易洗浄性にも優れたものであることを見いだした。 Means for Solving the Problems The present inventors have found that the results of the prior art problems of extensive to solve studies, is molded of molding material comprising a resin which is ring-opening polymerization from a specific monomer composition animal container is transparent, chemically resistant against disinfectants, etc., that are excellent in impact resistance, was found to be those which animal waste is also excellent in hardly easy cleanability deposition. 本発明はこれらの知見に基づいて完成するに至ったものである。 The present invention has been completed based on these findings.

【0009】かくして本発明によれば、2環体若しくは3環体のノルボルネン類を50重量%以上含むノルボルネン系単量体の開環重合体またはその水素添加物からなる成形材料を成形してなる動物容器が提供される。 [0009] Thus, according to the present invention, formed by molding a molding material comprising norbornene two annulus or tricyclic body from ring-opening polymer or a hydrogenated product of norbornene monomer containing 50 wt% or more the animal container is provided.

【0010】 [0010]

【発明の実施の形態】 DETAILED DESCRIPTION OF THE INVENTION

(ノルボルネン系開環重合体またはその水素添加物)本発明においては、2環体若しくは3環体のノルボルネン類を50重量%以上含むノルボルネン系単量体の開環重合体またはその水素添加物が用いられる。 In (ring-opened norbornene polymer or a hydrogenated product thereof) present invention, ring-opening polymer or a hydrogenated product of norbornene monomers containing a norbornene two annulus or tricyclic body 50 wt% or more used. 具体的には、 In particular,
特開昭63−264646号公報、特開昭64−170 JP-A-63-264646, JP-Sho 64-170
5号公報、特開平1−168724号公報、特開平1− 5, JP-A No. 1-168724, JP-A No. 1-
168725号公報などに開示されるノルボルネン系単量体の開環重合体およびその水素添加物などのうち、原料となるノルボルネン系単量体が2環体若しくは3環体のノルボルネン類を50重量%以上含むものである。 Norbornene is disclosed in, 168725 JP monomer ring-opening polymers and of such a hydrogenated product thereof, a norbornene-based monomer as a raw material is 2 annulus or tricyclic body norbornene of 50% by weight it is intended to include more.

【0011】一般に開環重合は、ノルボルネン系単量体(分子内にノルボルネン環構造を有する単量体を主成分とする単量体をいう)を、メタセシス開環重合触媒系の存在下に反応させる。 [0011] Generally the ring-opening polymerization, norbornene monomer (referred to the monomer as a main component a monomer having a norbornene ring structure in a molecule), the reaction in the presence of a metathesis ring-opening polymerization catalyst system make. 本発明においてはノルボルネン類(ノルボルネン環を有する単量体をいう)であって2環体若しくは3環体であるものを50重量%以上含むノルボルネン系単量体を用いる(ここで分子中に炭化水素環をn個有する単量体をn環体の単量体というものとする)。 In the present invention use a norbornene-based monomer including those which are norbornenes (refers to a monomer having a norbornene ring) is a by 2 ring members or tricyclic 50 wt% or more (carbonized here in the molecule monomers having n number of hydrogen rings will be referred to as monomer n annulus). ノルボルネン類は2環体以上の多環体が多数知られているが、本発明では2環体若しくは3環体のノルボルネン類を50重量%以上含むノルボルネン系単量体を用いる。 Norbornenes 2 annulus or more polycyclic body are known a large number, but in the present invention using a norbornene-based monomer comprising a norbornene two annulus or tricyclic 50 wt% or more. 動物容器は例えば内容積が5リットル程度以上と比較的大型で重く、洗浄や乾燥時には乱雑に扱われたり、空の動物容器は重ねて保管されるため、動物容器には乱雑な取扱いや積重ね保管に耐え得る耐衝撃性が特に必要であり、2環体若しくは3環体のノルボルネン類を50重量%以上含むノルボルネン系単量体を用いることにより初めてそのような高度な耐衝撃性が達成される。 Animals containers are heavy in relatively large, for example, internal volume about 5 l or more, or messy treated during washing and drying, since the empty animal containers are stored on top, the animal container messy handling and stacking storage is particularly necessary impact resistance to withstand the first time such a high degree of impact resistance can be achieved by using a norbornene-based monomer include norbornene two annulus or tricyclic body 50 wt% or more .

【0012】更に、本発明者らは、鋭意研究の結果、上記のノルボルネン類組成からなるノルボルネン系単量体から開環重合される重合体またはその水素添加物からなる成形材料を成形してなる動物容器が、動物の排泄物が付着しにくく易洗浄性にも優れたものであることを見いだした。 Furthermore, the present invention intensively studied, by molding the molding material made of polymer is ring-opening polymerization of a norbornene-based monomer consisting of aforementioned norbornenes composition or a hydrogenated product thereof animals containers were found to be those which animal waste is also excellent in hardly easy cleanability deposition. これは、該成形材料を使用した場合、動物容器の表面が滑らかで微少な凹凸が無いものとしやすいこと、動物の排泄物の成分が染込みにくいことや侵されにくいことに由来していると考えられる。 This, when using molding material, the surface of the animal container easily that there is no smooth and finely uneven, the component of animal waste are derived from it difficult that Ya the affected hard to penetration Conceivable.

【0013】2環体のノルボルネン類は、置換若しくは非置換の非環状オレフィン類若しくは非環状ジエン類とシクペンタジエンの付加物であり、具体的には、ビシクロ[2.2.1]ヘプタ−2−エン(慣用名ノルボルネン)、5−メチル−ビシクロ[2.2.1]ヘプタ−2 [0013] norbornenes two ring bodies is an addition product of a substituted or unsubstituted non-cyclic olefins or acyclic dienes and consequent pentadiene, specifically, bicyclo [2.2.1] hept -2 - ene (common name norbornene), 5-methyl - bicyclo [2.2.1] hept -2
−エン、5,5−ジメチル−ビシクロ[2.2.1]ヘプタ−2−エン、5−エチル−ビシクロ[2.2.1] - ene, 5,5-dimethyl - bicyclo [2.2.1] hept-2-ene, 5-ethyl - bicyclo [2.2.1]
ヘプタ−2−エン、5−ブチル−ビシクロ[2.2. Hept-2-ene, 5-butyl - bicyclo [2.2.
1]ヘプタ−2−エン、5−エチリデン−ビシクロ[2.2.1]−ヘプタ2−エン、5−ヘキシル−ビシクロ[2.2.1]ヘプタ−2−エン、5−オクチル− 1] hept-2-ene, 5-ethylidene - bicyclo [2.2.1] - hept 2-ene, 5-hexyl - bicyclo [2.2.1] hept-2-ene, 5- octyl -
ビシクロ[2.2.1]ヘプタ−2−エン、5−オクタデシル−ビシクロ[2.2.1]ヘプタ−2−エン、5 Bicyclo [2.2.1] hept-2-ene, 5-octadecyl - bicyclo [2.2.1] hept-2-ene, 5
−エチリデン−ビシクロ[2.2.1]ヘプタ−2−エン、5−メチリデン−ビシクロ[2.2.1]ヘプタ− - ethylidene - bicyclo [2.2.1] hept-2-ene, 5-methylidene - bicyclo [2.2.1] hept -
2−エン、5−ビニル−ビシクロ[2.2.1]ヘプタ−2−エン、5−プロペニル−ビシクロ[2.2.1] 2-ene, 5-vinyl - bicyclo [2.2.1] hept-2-ene, 5-propenyl - bicyclo [2.2.1]
ヘプタ−2−エンなどのノルボルネン誘導体、およびこれらのノルボルネン誘導体のハロゲン、水酸基、エステル基、アルコキシ基、シアノ基、アミド基、イミド基、 Norbornene derivatives such as hept-2-ene, and halogen of these norbornene derivatives, hydroxyl group, ester group, alkoxy group, cyano group, amido group, imido group,
シリル基などの極性基により置換された置換体(例えば、5−メトキシ−カルボニル−ビシクロ[2.2. Substituents substituted with polar groups, such as silyl groups (e.g., 5-methoxy - carbonyl - bicyclo [2.2.
1]ヘプタ−2−エン、5−シアノ−ビシクロ[2. 1] hept-2-ene, 5-cyano - bicyclo [2.
2.1]ヘプタ−2−エン、5−メチル−5−メトキシカルボニル−ビシクロ[2.2.1]ヘプタ−2−エンなど)を挙げることができる。 2.1] hept-2-ene, 5-methyl-5-methoxycarbonyl - bicyclo [2.2.1] hept-2-ene, etc.) can be mentioned. これらの中でも、動物容器の耐薬品性および排泄物の易洗浄性の点から極性基を有さないノルボルネン誘導体が好ましい。 Among these, norbornene derivatives having no polar group in view of easy cleaning of the chemical and animal waste container is preferred.

【0014】3環体のノルボルネン類は、置換若しくは非置換の環状オレフィン類若しくは環状ジエン類とシクペンタジエンの付加物であり、シクロペンタジエンの2 [0014] 3 norbornenes annulus is an addition product of a substituted or unsubstituted cyclic olefins or cyclic dienes and consequent pentadiene, 2 cyclopentadiene
量体であるトリシクロ[4.3.1 2,5 It is a dimer tricyclo [4.3.1 2,5. 1,6 ]デカ− 0 1,6] deca -
3,7−ジエン(慣用名ジシクロペンタジエン)、その部分水素添加物(またはシクロペンタジエンとシクロペンテンの付加物)であるトリシクロ[4.3.1 2,5 3,7-diene (common name dicyclopentadiene) is its partially hydrogenated product (or an adduct of cyclopentadiene and cyclopentene) tricyclo [4.3.1 2,5.
1,6 ]デカ−3−エン;シクロペンタジエンとシクロヘキサジエンの付加物であるトリシクロ[4.4.1 0 1,6] dec-3-ene; adducts of cyclopentadiene and cyclohexadiene tricyclo [4.4.1
2,5 2,5. 1,6 ]ウンデカ−3,7−ジエン若しくはトリシクロ[4.4.1 2, 0 1,6] undec-3,7-diene or tricyclo [4.4.1 2, 5 5. 1,6 ]ウンデカ−3,8−ジエンまたはこれらの部分水素添加物(またはシクロペンタジエンとシクロヘキセンの付加物)であるトリシクロ[4.4.1 2, 0 1,6] undec-3,8-diene or tricyclo is these partially hydrogenated product (or an adduct of cyclopentadiene and cyclohexene) [4.4.1 2, 5 5. 1,6 ]ウンデカ−3−エン;シクロペンタジエンと脂環基若しくは芳香環基を有するビニル化合物との付加物である5−シクロペンチル−ビシクロ[2.2.1]ヘプト−2−エン、5−シクロヘキシル−ビシクロ[2.2.1]ヘプト−2−エン、5−シクロヘキセニルビシクロ[2.2.1]ヘプト−2−エン、5−フェニル−ビシクロ[2.2.1]ヘプト−2 0 1,6] undec-3-ene; adducts of vinyl compounds having a cyclopentadiene and alicyclic group or aromatic ring group of 5-cyclopentyl - bicyclo [2.2.1] hept-2-ene, 5 - cyclohexyl - bicyclo [2.2.1] hept-2-ene, 5-cyclohexenyl bicyclo [2.2.1] hept-2-ene, 5-phenyl - bicyclo [2.2.1] hept -2
−エンなどの3環体のノルボルネン類;などを挙げることができる。 - norbornenes tricyclic body such as ene; and the like. さらに、これらのノルボルネン類のハロゲン、水酸基、エステル基、アルコキシ基、シアノ基、アミド基、イミド基、シリル基などの極性基により置換された置換体(例えば、5−メトキシカルボニルビシクロ[2.2.1]ヘプト−2−エン、5−エトキシカルボニルビシクロ[2.2.1]ヘプト−2−エン、5−メチル−5−メトキシカルボニルビシクロ[2.2.1] Further, the halogen of these norbornenes, hydroxyl, ester group, alkoxy group, cyano group, amido group, imido group, substituents substituted by a polar group such as a silyl group (e.g., 5-methoxycarbonyl bicyclo [2.2 .1] hept-2-ene, 5-ethoxycarbonyl-bicyclo [2.2.1] hept-2-ene, 5-methyl-5-methoxycarbonyl-bicyclo [2.2.1]
ヘプト−2−エン、5−メチル−5−エトキシカルボニルビシクロ[2.2.1]ヘプト−2−エン、ビシクロ[2.2.1]ヘプト−5−エニル−2−メチルプロピオネイト、ビシクロ[2.2.1]ヘプト−5−エニル−2−メチルオクタネイト、ビシクロ[2.2.1]ヘプト−2−エン−5,6−ジカルボン酸無水物、5−ヒドロキシメチルビシクロ[2.2.1]ヘプト−2−エン、5,6−ジ(ヒドロキシメチル)ビシクロ[2. Hept-2-ene, 5-methyl-5-ethoxycarbonyl-bicyclo [2.2.1] hept-2-ene, bicyclo [2.2.1] hept-5-enyl-2-methyl-propionitrile Nate, bicyclo [2.2.1] hept-5-enyl-2-methyl-oct Nate, bicyclo [2.2.1] hept-2-ene-5,6-dicarboxylic anhydride, 5-hydroxymethyl-bicyclo [2. 2.1] hept-2-ene, 5,6-di (hydroxymethyl) bicyclo [2.
2.1]ヘプト−2−エン、5−ヒドロキシ−i−プロピルビシクロ[2.2.1]ヘプト−2−エン、5,6 2.1] hept-2-ene, 5-hydroxy -i- propyl bicyclo [2.2.1] hept-2-ene, 5,6
−ジカルボキシビシクロ[2.2.1]ヘプト−2−エンなどの酸素原子を含む置換基を有するノルボルネン誘導体;5−シアノビシクロ[2.2.1]ヘプト−2− - dicarboxylate Sibi [2.2.1] norbornene derivative having a substituent containing an oxygen atom, such as hept-2-ene; 5- Shianobishikuro [2.2.1] hept-2
エン、ビシクロ[2.2.1]ヘプト−2−エン−5, Ene, bicyclo [2.2.1] hept-2-ene -5,
6−ジカルボン酸イミドなどの窒素原子を含む置換基を有するノルボルネン誘導体など)であっても良い。 It may be a norbornene derivative, etc.) having a substituent containing a nitrogen atom, such as 6-dicarboxylic acid imide. これらの中でも、動物容器の耐薬品性および排泄物の易洗浄性の点から極性基を有さないものが好ましく、更に耐衝撃性と耐熱性のバランスが優れる点でトリシクロ[4. Among these, preferably those having no polar group in view of easy cleaning of the chemical and animal waste container, tricyclo in that it further excellent balance of impact resistance and heat resistance [4.
3.1 2,5 3.1 2,5. 1,6 ]デカ−3,7−ジエンが特に好ましい。 0 1,6] deca-3,7-diene is especially preferred.

【0015】これらの2環体のノルボルネン類と3環体のノルボルネン類は、それぞれ単独であるいは2種以上を組み合わせて用いる。 [0015] norbornenes of norbornenes and 3 rings of these two annulus, used alone or in combination of two or more. 2環体若しくは3環体のノルボルネン類の合計量のうち3環体のノルボルネン類の量は、好ましくは50重量%以上、好ましくは60重量% The amount of norbornene of 3 annulus of the total amount of norbornene in 2 annulus or tricyclic body is preferably 50 wt% or more, preferably 60 wt%
以上、特に好ましくは70重量%以上であり、100重量%以下である。 Or more, particularly preferably 70 wt% or more and 100 wt% or less. このような範囲にある時に成形される動物容器の耐衝撃性と耐熱性などの特性が高度にバランスして良好である。 Properties such as impact resistance and heat resistance of the animal container to be formed when in this range is good and highly balanced.

【0016】ノルボルネン系単量体中の、これらの2環体若しくは3環体のノルボルネン類以外の成分は共重合可能な単量体成分であれば特に限定されないが、通常は、4環体以上のノルボルネン類を用いることができる。 The norbornene monomers in components other than norbornenes these two annulus or tricyclic body is not particularly limited as long as the copolymerizable monomer component, typically 4 annulus or it is possible to use of norbornenes.

【0017】4環体以上のノルボルネン類としては、テトラシクロ[4.4.1 2,5 [0017] As 4 annulus or more norbornenes is tetracyclo [4.4.1 2,5. 7,1 1 7,1 0 0]−ドデカ−3 0 0] - dodeca -3
−エン(単にテトラシクロドデセンともいう)、8−メチルテトラシクロ[4.4.1 2,5 - ene (also simply referred to as tetracyclododecene), 8-methyl tetracyclo [4.4.1 2,5. 7,10 0]−ドデカ−3−エン、8−エチルテトラシクロ[4.4.1 1 7,10 0] - dodeca-3-ene, 8-ethyl-tetracyclo [4.4.1
2,5 2,5. 7,10 1 7,10. 0]−ドデカ−3−エン、8−メチリデンテトラシクロ[4.4.1 2,5 0] - dodeca-3-ene, 8-methylidene-tetracyclo [4.4.1 2,5. 7,10 0]−ドデカ−3−エン、8−エチリデンテトラシクロ[4.4.1 1 7,10 0] - dodeca-3-ene, 8-ethylidene tetracyclo [4.4.1
2,5 2,5. 7,10 0]−ドデカ−3−エン、8−ビニルテトラシクロ[4.4.0.1 2,5 1 7,10 0] - dodeca-3-ene, 8-vinyl-tetracyclo [4.4.0.1 2, 5. 7,10 1 7,10. ]−ドデカ− ] - dodeca -
3−エン、8−プロペニル−テトラシクロ[4.4. 3-ene, 8-propenyl - tetracyclo [4.4.
0.1 2,5 0.1 2,5. 7,10 1 7,10. ]−ドデカ−3−エンなどのテトラシクロドデセン(4環体)構造を有する4環体のノルボルネン類;8−シクロペンチル−テトラシクロ[4. ] - dodeca-3-norbornene of 4 rings having a tetracyclododecene (4 annulus) structure, such as ene; 8-cyclopentyl-- tetracyclo [4.
4.1 2,5 4.1 2,5. 7,10 1 7,10. 0]−ドデカ−3−エン、8−シクロヘキシル−テトラシクロ[4.4.1 2,5 0] - dodeca-3-ene, 8-cyclohexyl - tetracyclo [4.4.1 2,5.
7,10 1 7,10. 0]−ドデカ−3−エン、8−シクロヘキセニル−テトラシクロ[4.4.1 2,5 0] - dodeca-3-ene, 8-cyclohexenyl - tetracyclo [4.4.1 2,5. 7,10 1 7,10. 0]−ドデカ−3−エン、8−フェニル−シクロペンチル−テトラシクロ[4.4.1 2,5 0] - dodeca-3-ene, 8-phenyl - cyclopentyl - tetracyclo [4.4.1 2,5. 7,10 1 7,10. 0]−ドデカ−3 0] - dodeca -3
−エンなどのテトラシクロドデセン環構造と脂環若しくは芳香環をもつ5環体のノルボルネン類;テトラシクロ[7.4.1 10,13 - norbornene tetracyclododecene ring and alicyclic or 5 ring member having an aromatic ring such as ene; tetracyclo [7.4.1 10,13. 1,9 0 1,9. 2,7 ]トリデカ−2, 0 2,7] trideca -2,
4,6,11−テトラエン(1,4−メタノ−1,4, 4,6,11- tetraene (1,4-methano-1,4,
4a,9a−テトラヒドロフルオレンともいう)、テトラシクロ[8.4.1 11,14 4a, also referred 9a- tetrahydrofluorene), tetracyclo [8.4.1 11,14. 1,10 0 1,10. 3,8 ]テトラデカ−3,5,7,12−テトラエン(1,4−メタノ− 0 3,8] tetradec -3,5,7,12- tetraene (1,4-methano -
1,4,4a,5,10,10a−ヘキサヒドロアントラセンともいう)などのテトラシクロドデセン環以外のノルボルネン環構造と芳香環を有する5環体のノルボルネン類;シクロペンタジエンの3量体で5環体の単量体であるペンタシクロ[6.5.1 1,8 : Synthesis of 1,4,4, 5,10,10a also called hexa hydro anthracene) tetracyclododecene norbornenes five ring having a norbornene ring structure and an aromatic ring other than Sen ring such as; in trimer cyclopentadiene 5 pentacyclo monomeric annulus [6.5.1 1,8. 3,6 1 3,6. 2,7 0 2,7.
9,13 ]ペンタデカ−3,10−ジエンおよびペンタシクロ[7.4.1 3,6 0 9,13] pentadeca-3,10-diene and pentacyclo [7.4.1 3,6. 10,13 1 10, 13 . 1,9 0 1,9. 2,7 ]ペンタデカ−4,11−ジエン;シクロペンタジエンの4量体以上の付加物;などが挙げられる。 0 2,7] pentadeca-4,11-diene; tetramer or more adducts of cyclopentadiene; and the like.

【0018】4環体以上のノルボルネン類は、上記の4 [0018] 4 ring body more norbornenes is, 4 above
環体以上のノルボルネン類の極性基を有する誘導体(例えば8−メトキシカルボニルテトラシクロ[4.4.1 Derivative having a polar group annulus or more norbornenes (such as 8-methoxycarbonyl tetracyclo [4.4.1
2,5 2,5. 7,10 1 7,10. 0]−ドデカ−3−エン、8−メチル− 0] - dodeca-3-ene, 8-methyl -
8−メトキシカルボニルテトラシクロ[4.4. 8 methoxycarbonyltetracyclo [4.4.
2,5 1 2,5. 7,10 1 7,10. 0]−ドデカ−3−エン、8−ヒドロキシメチルテトラシクロ[4.4.1 2,5 0] - dodeca-3-ene, 8-hydroxymethyl-tetracyclo [4.4.1 2,5. 7,10 1 7,10.
0]−ドデカ−3−エン、8−カルボキシテトラシクロ[4.4.1 2,5 0] - dodeca-3-ene, 8-carboxy-tetracyclo [4.4.1 2,5. 7,10 1 7,10. 0]−ドデカ−3−エン、 0] - dodeca-3-ene,
などの酸素原子を含む置換基を有するテトラシクロドデセン誘導体など)であっても良い。 It may be a tetra-like cyclododecene derivative) having a substituent containing an oxygen atom, such as. これらの4環体以上のノルボルネン類の中でも、動物容器の耐薬品性および排泄物の易洗浄性の点から極性基を有さないものが好ましい。 Among these 4 annulus above norbornenes, those preferably has no polar group in view of easy cleaning of the chemical and animal waste container.

【0019】ノルボルネン類(2環体若しくは3環体のノルボルネン類と4環体以上のノルボルネン類の合計) [0019] norbornenes (sum of 2 annulus or 3 norbornenes annulus and 4 annulus or more norbornenes)
のうち、2環体若しくは3環体のノルボルネン類は50 Of, norbornenes two annulus or 3 annulus 50
重量%以上、好ましくは60重量%以上、特に好ましくは70重量%以上であり、100重量%以下である。 Wt% or more, preferably 60 wt% or more, and particularly preferably 70 wt% or more and 100 wt% or less. このような範囲にある時に成形される動物容器の耐衝撃性と耐熱性などの特性が高度にバランスして良好である。 Properties such as impact resistance and heat resistance of the animal container to be formed when in this range is good and highly balanced.

【0020】ノルボルネン系単量体(単量体の合計)のうちノルボルネン類(2環体若しくは3環体と4環体以上を合わせた量)は、70重量%以上、好ましくは80 The norbornene monomer (total monomer) norbornenes of (2 annulus or 3 annulus and 4 combined amount of more than annulus) is 70 wt% or more, preferably 80
重量%以上、特に好ましくは90重量%以上であり、1 Wt% or more, particularly preferably 90 wt% or more, 1
00重量%以下である。 00% by weight or less. このような範囲にあるときに開環重合反応の活性が高く好適である。 A high preferred activity of ring-opening polymerization reaction when in this range.

【0021】ノルボルネン系単量体(単量体の合計量) [0021] The norbornene-based monomer (the total amount of the monomer)
のうちノルボルネン類(2環体若しくは3環体と4環体以上を合わせた量)は、70重量%以上、好ましくは8 Norbornenes of (2 annulus or 3 annulus and 4 combined amount of more than annulus) is 70 wt% or more, preferably 8
0重量%以上、特に好ましくは90重量%以上であり、 0 wt% or more, particularly preferably 90 wt% or more,
100重量%以下である。 It is 100% by weight or less. このような範囲にあるときに開環重合反応の活性が高く好適である。 A high preferred activity of ring-opening polymerization reaction when in this range.

【0022】共重合可能な他の単量体としては、エチレン、プロピレン、1−ブテン、4−メチル−1−ペンテンなどの炭素数2〜12からなるα−オレフィン類;スチレン、α−メチルスチレン、p−メチルスチレン、p Examples of the other copolymerizable monomer, ethylene, propylene, 1-butene, 4-methyl-1-pentene consisting 2-12 carbon atoms such as alpha-olefins; styrene, alpha-methyl styrene , p- methyl styrene, p
−クロロスチレンなどのスチレン類;1,3−ブタジエン、1,4−ブタジエン、イソプレンなどの直鎖または分岐のジエン類;エチルビニルエーテル、イソブチルビニルエーテルなどのビニルエーテル類;シクロブテン、 - styrenes such as chlorostyrene; 1,3-butadiene, 1,4-butadiene, straight chain or branched dienes such as isoprene; ethyl vinyl ether and isobutyl vinyl; cyclobutene,
シクロペンテン、シクロヘキセン、シクロヘプテン、シクロオクテン単環の環状オレフィン系単量体:1、3− Cyclopentene, cyclohexene, cycloheptene, cyclooctene monocyclic cycloolefin monomer: 1,3
シクロペンタジエン、1、3−シクロヘキサジエン、 Cyclopentadiene, 1,3-cyclohexadiene,
1、3−シクロヘプタジエン、1、3−シクロオクタジエンなどの共役若しくは非共役の環状ジエン系単量体が挙げられる。 1,3-cycloheptadiene, conjugated or non-conjugated cyclic diene monomers such as 1,3-cyclooctadiene and the like.

【0023】上記のノルボルネン系単量体はメタセシス開環重合触媒系を用いて公知の方法により開環重合される。 The norbornene monomer described above is the ring-opening polymerization by a known method using a metathesis ring-opening polymerization catalyst system. メタセシス開環重合触媒系は、主触媒と活性化剤からなり、必要に応じて反応調整剤を組合わせて使用する。 Metathesis ring-opening polymerization catalyst system consists of a main catalyst and activator are used in combination the reaction adjusting agent, if necessary.

【0024】開環重合の結果得られるノルボルネン系開環重合体は分子中に不飽和結合が残留するため、その不飽和結合により、ノルボルネン系開環重合体の耐候安定性や熱安定性が低下することがある。 [0024] Since resulting norbornene ring-opening polymer of a ring-opening polymerization of the unsaturated bond in the molecule remaining, by its unsaturated bonds, reduced weathering stability and thermal stability of the norbornene-based ring-opening polymer sometimes. これを改良することを目的として、水素添加することにより不飽和結合の80%以上、好ましくは90%以上を飽和化させて用いることが好ましい。 The purpose of improving this, more than 80% of the unsaturated bonds by hydrogenation, preferably be used to saturate the more than 90%. このような水素添加率とすることにより、動物容器を長時間使用した時の耐候変色が少なく、一層動物の排泄物が付着しにくく易洗浄性にも優れたものとなり好ましい。 With such a hydrogenation rate, less weathering discoloration when using animal container long, preferably becomes excellent in more excretions hardly easy cleanability adhesion of animals. 水素添加方法、水素添加触媒については公知の方法により行うことができる。 Hydrogenation process can be carried out by methods known for the hydrogenation catalyst.

【0025】ノルボルネン系開環重合体およびその水素添加物(以下ノルボルネン類系開環重合体等という)の分子量は、適宜選択されるが、シクロヘキサン溶液(ノルボルネン系開環重合体等が溶解しない場合はトルエン溶液)のゲル・パーミエーション・クロマトグラフ法で測定した数平均分子量(ポリイソプレン換算)で通常3,000〜200,000、好ましくは5,000〜 The molecular weight of the norbornene ring-opening polymer and its hydrogenated product (hereinafter referred to as norbornene-based ring-opening polymer and the like) is appropriately selected, cyclohexane solution (if ring-opened norbornene polymer and the like is not dissolved Usually the number-average molecular weight measured by gel permeation chromatography of toluene solution) (in terms of polyisoprene) 3,000 to 200,000, preferably 5,000 to
100、000、特に好ましくは10、000〜80、 100,000, particularly preferably 10,000~80,
000の範囲である。 It is in the range of 000. ノルボルネン系開環重合体等の数平均分子量がこの範囲にある時に耐衝撃性などの機械的強度や成形加工性に優れるので好適である。 The number average molecular weight of such a norbornene-based ring-opening polymer is preferred because of excellent mechanical strength and moldability such as impact resistance when in this range.

【0026】ノルボルネン系開環重合体等のガラス転移温度(Tg)は、適宜選択されればよいが、動物容器の環境温度で変形せず、温水洗浄でも変形しないことが必要であることから、高い方が好ましく、また適正な範囲を越えて高すぎると、樹脂が硬質なものとなり耐衝撃性などの機械強度が低下することから、適切な温度範囲にあることが好ましい。 The glass transition temperature of such ring-opened norbornene polymer (Tg) of, since it may be employed to appropriately selected, not deformed at ambient temperature of an animal vessel, it is necessary not to deform even with warm water washing, When higher is preferred, and too high beyond the appropriate range, since the mechanical strength such as impact resistance becomes as resin is hard is reduced, preferably in a suitable temperature range. Tgは、通常30〜140℃、好ましくは50〜120℃、より好ましくは60〜110 Tg is usually 30 to 140 ° C., preferably 50 to 120 ° C., more preferably 60-110
℃、最も好ましくは70〜100℃の範囲である。 ° C., and most preferably in the range of 70 to 100 ° C.. この範囲にTgがある場合に、動物容器が変形や破損をせず長期間の使用に耐えることができ好適である。 If this range is Tg, are preferred can be an animal vessel withstand use for a long time without deformation or breakage.

【0027】ノルボルネン系開環重合体等は、単独で、 [0027] The norbornene-based ring-opening polymer or the like, alone,
あるいは2種以上を組み合わせて用いることができる。 Or it may be used in combination of two or more.

【0028】(その他のポリマー成分)本発明に使用される成形材料には、ノルボルネン系開環重合体等以外にその他のポリマー成分を必要に応じて配合できる。 [0028] The molding material used in the (other polymer component) the present invention can be formulated as needed other polymer components in addition to the norbornene ring-opening polymer or the like. その他のポリマー成分としては、ゴム質重合体や、ノルボルネン系開環重合体等以外の熱可塑性樹脂などが挙げられる。 Other polymer components, the rubbery polymer and, norbornene ring-opening polymer thermoplastic resin other than the like.

【0029】ゴム質重合体はガラス転移温度が常温付近以下具体的には40℃以下のゴム質重合体が好ましい。 The rubber polymer is the glass transition temperature is less specifically around room temperature preferably 40 ° C. or less of the rubber polymer.
なお、ブロック共重合したゴム質重合体などでガラス転移温度が2点以上ある場合があるが、その場合は、最も低いガラス転移温度が40℃以下であれば本発明のガラス転移温度が40℃以下のゴム質重合体として用いることができる。 Although there may be a glass transition temperature of more than 2 points on such as a block copolymer rubber polymer, in which case, if the lowest glass transition temperature of 40 ° C. below the glass transition temperature of the present invention is 40 ° C. it can be used as the rubbery polymer of the following. 好ましいゴム質重合体の例としては、天然ゴム、ポリブタジエンゴム、ポリイソプレンゴム、その水素添加物;クロロプレンゴム、その水素添加物;エチレン・プロピレン共重合体などのエチレン・α−オレフィン共重合体、プロピレン・その他のα−オレフィンの共重合体などの飽和ポリオレフィンゴム;エチレン・プロピレン・ジエン共重合体、α−オレフィン・ジエン共重合体、イソブチレン・イソプレン共重合体、イソブチレン・ジエン共重合体などのα−オレフィン・ジエン系重合体、これらハロゲン化物;アクリロニトリル・ブタジエン共重合体、その水素添加物;フッ化ビニリデン・ Examples of preferred rubbery polymer is natural rubber, polybutadiene rubber, polyisoprene rubber, hydrogenated products thereof; chloroprene rubber, a hydrogenated product thereof, ethylene-alpha-olefin copolymers such as ethylene-propylene copolymer, saturated polyolefin rubbers such as copolymers of propylene and other alpha-olefins, ethylene-propylene-diene copolymer, alpha-olefin-diene copolymer, isobutylene-isoprene copolymers, such as isobutylene-diene copolymer α- olefin diene polymer, these halides; acrylonitrile-butadiene copolymer, hydrogenated products thereof; vinylidene fluoride-
三フッ化エチレン共重合体、フッ化ビニリデン・六フッ化プロピレン共重合体、フッ化ビニリデン・六フッ化プロピレン・四フッ化エチレン共重合体、プロピレン・四フッ化エチレン共重合体などのフッ素ゴム;ウレタンゴム、シリコーンゴム、ポリエーテル系ゴム、アクリルゴム、クロルスルホン化ポリエチレンゴム、エピクロルヒドリンゴム、プロピレンオキサイドゴム、エチレンアクリルゴムなどの特殊ゴム;ノルボルネン類とエチレンまたはα−オレフィンの共重合体、ノルボルネン類とエチレンとα−オレフィンの三元共重合体などのノルボルネン系ゴム質重合体;スチレン・ブタジエン共重合体ゴム、スチレン・イソプレン共重合体ゴム、スチレン・ブタジエン・イソプレン三元共重合体ゴムなどの芳香族ビニル系モノマー・共役 Ethylene trifluoride copolymer, vinylidene fluoride-hexafluoropropylene copolymer, vinylidene fluoride-hexafluoropropylene-tetrafluoroethylene copolymer, fluorinated rubber and propylene-tetrafluoroethylene copolymer ; urethane rubber, silicone rubber, polyether rubber, acrylic rubber, chlorosulfonated polyethylene rubber, epichlorohydrin rubber, propylene oxide rubber, special rubber such as ethylene-acrylic rubber; norbornenes and ethylene or α- olefin copolymer, norbornene norbornene-based rubbery polymer, such as a terpolymer of s ethylene and α- olefin; styrene-butadiene copolymer rubber, styrene-isoprene copolymer rubber, styrene-butadiene-isoprene terpolymer rubber such as aromatic vinyl monomers, conjugated ジエンのランダム共重合体、及びこれらの水素添加物、スチレン・ブタジエン・スチレンブロック共重合体ゴム、スチレン・イソプレン・スチレンブロック共重合体ゴムなどの芳香族ビニル系モノマー・共役ジエンの直鎖状または放射状ブロック共重合体、 Random copolymers of a diene, and hydrogenated products thereof, styrene-butadiene-styrene block copolymer rubber, an aromatic vinyl monomer-conjugated diene such as styrene-isoprene-styrene block copolymer rubber linear or radial block copolymer,
及びそれらの水素添加物などのスチレン系熱可塑性エラストマー;ウレタン系熱可塑性エラストマー;ポリアミド系熱可塑性エラストマー;1,2−ポリブタジエン系熱可塑性エラストマー、塩化ビニル系熱可塑性エラストマー;フッ素系熱可塑性エラストマーなどの熱可塑性エラストマーが挙げられる。 And styrenic thermoplastic elastomers such as hydrogenated product thereof; urethane-based thermoplastic elastomers; polyamide thermoplastic elastomers; 1,2-polybutadiene-based thermoplastic elastomer, vinyl chloride thermoplastic elastomer, such as a fluorine-based thermoplastic elastomer thermoplastic elastomers.

【0030】ゴム質重合体は、ノルボルネン系開環重合体等との屈折率差が小さいもの、ノルボルネン系開環重合体等と混合した時にミクロドメインをとって微分散しやすいものが好ましいが、これらの選択は、使用しようとするノルボルネン系開環重合体等との組み合わせでなされる。 The rubber polymer, a refractive index difference between the norbornene-based ring-opening polymer or the like is small, but is preferably one easily finely dispersed taking microdomains when mixed with norbornene ring-opening polymer or the like, these selections are made in combination with a norbornene-based ring-opening polymer or the like to be used. ゴム質重合体の添加量が多い場合でも高い透明性を維持するためには、ゴム質重合体とノルボルネン系開環重合体等の屈折率の差は小さいほど、透明性に優れ好ましい。 To maintain the amount is often even higher transparency of rubber polymer, as the difference between the rubbery polymer and a norbornene-based ring-opening polymer such as the refractive index of the small, preferably excellent in transparency. 特に配合量が多い場合は屈折率差が小さい配合剤を用いることが好ましく、その場合の屈折率差は通常0.2以下、好ましくは0.1以下、より好ましくは0.05以下に、最も好ましくは0.02以下である。 Especially often amount is preferable to use a refractive index difference is small formulations, the refractive index difference in this case is usually 0.2 or less, preferably 0.1 or less, more preferably 0.05 or less, most preferably 0.02 or less.
ノルボルネン系開環重合体等の種類が異なれば屈折率も異なるが、例えば、ゴム質重合体はモノマーの比率を変化させたり、主鎖の不飽和結合の数を水素添加などにより変化させることにより、連続的に屈折率を変えることが可能である。 Refractive index Different types of such ring-opened norbornene polymer also differ, for example, rubber polymer or by changing the ratio of monomers, by changing due hydrogenation the number of unsaturated bonds in the main chain , it is possible to vary continuously the refractive index. 用いるノルボルネン系開環重合体等の屈折率に応じて、適当な屈折率を有するゴム質重合体を選択することが好ましい。 Depending on the refractive index, such as ring-opened norbornene polymer used, it is preferable to select a rubbery polymer having a suitable refractive index.

【0031】上記のゴム質重合体の中でも、芳香族ビニル系モノマーと共役ジエン系モノマーの共重合体、その水素添加物、及びノルボルネン系ゴム質重合体が、ノルボルネン系開環重合体等との分散性が良く、ノルボルネン系開環重合体等との屈折率が近いものを選択できるので好ましい。 [0031] Among the rubber polymer described above, a copolymer of an aromatic vinyl monomer and a conjugated diene monomer, hydrogenated products thereof, and norbornene-based rubber-like polymer, the norbornene ring-opening polymer or the like good dispersibility, since the refractive index of the norbornene-based ring-opening polymer or the like to select a close preferable. ここで、芳香族ビニル系モノマーと共役ジエン系モノマーの共重合体はブロック共重合体でもランダム共重合体でも良い。 Here, a copolymer of an aromatic vinyl monomer and a conjugated diene monomer may be a random copolymer in the block copolymer. 好ましい具体的な例としては、 Preferred specific examples,
スチレン・ブタジエンブロック共重合体、スチレン・ブタジエン・スチレン・ブロック共重合体、スチレン・イソプレン・ブロック共重合体、スチレン・イソプレン・ Styrene-butadiene block copolymer, styrene-butadiene-styrene block copolymer, styrene-isoprene block copolymer, styrene-isoprene-
スチレン・ブロック共重合体、スチレン・ブタジエン・ Styrene block copolymer, styrene-butadiene-
ランダム共重合体およびこれらの水素添加物などが挙げられる。 Random copolymers and the like hydrogenated products thereof. これらの中でも、動物容器を長期間使用した時の、排泄物からの汚染や耐候劣化による透明性の低下が少ないことなどの点から芳香環以外の炭素−炭素不飽和結合の一部または全部を水素添加しているものがより好ましく、スチレン・ブタジエンブロック共重合体の水素添加物、スチレン・ブタジエン・スチレン・ブロック共重合体の水素添加物、スチレン・イソプレン・ブロック共重合体の水素添加物、スチレン・イソプレン・スチレン・ブロック共重合体の水素添加物、スチレン・ブタジエン・ランダム共重合体の水素添加物などが特に好ましい。 Some or all of the carbon unsaturated bond - Among these, when using an animal container long time, carbon points from other than an aromatic ring, such that reduction in transparency due to contamination or weathered from excrement is small more preferably those hydrogenated, hydrogenated product of styrene-butadiene block copolymer, hydrogenated product of styrene-butadiene-styrene block copolymer, hydrogenated product of a styrene-isoprene block copolymer, hydrogenated product of a styrene-isoprene-styrene block copolymer, and hydrogenated products of styrene-butadiene random copolymer is particularly preferred.

【0032】これらのゴム質重合体は、それぞれ単独で、あるいは組み合わせて用いることができる。 [0032] These rubber polymers may be used alone or in combination. ゴム質重合体の配合量は、ノルボルネン系開環重合体等100 The amount of rubber polymer, norbornene ring-opening polymer or the like 100
重量部に対してゴム質重合体が通常0.01〜30重量部、好ましくは0.05〜20重量部、より好ましくは0.10〜10重量部である。 Usually 0.01-30 parts by weight rubber polymer with respect to parts by weight, preferably 0.05 to 20 parts by weight, more preferably 0.10 to 10 parts by weight.

【0033】ノルボルネン系開環重合体等以外の熱可塑性樹脂を組み合わせて使用することもできる。 [0033] a combination of thermoplastic resin other than the norbornene ring-opening polymer or the like may be used. このような熱可塑性樹脂としては、例えば、低密度ポリエチレン、高密度ポリエチレン、直鎖状低密度ポリエチレン、 Examples of the thermoplastic resin, for example, low density polyethylene, high density polyethylene, linear low density polyethylene,
超低密度ポリエチレン、ポリプロピレン、シンジオタクチックポリプロピレン、ポリブテン、ポリペンテンなどのポリオレフィン;ポリエチレンテレフタレート、ポリブチレンテレフタレートなどのポリエステル;ナイロン6、ナイロン66などのポリアミド;エチレン−エチルアクリレート共重合体、エチレン−酢酸ビニル共重合体、ポリスチレン、シンジオタクチックポリスチレン、 Ultra low density polyethylene, polypropylene, syndiotactic polypropylene, polybutene, polyolefins such as polypentene, polyethylene terephthalate, polyesters such as polybutylene terephthalate; nylon 6, polyamide such as nylon 66, ethylene - ethyl acrylate copolymer, ethylene - vinyl acetate copolymer, polystyrene, syndiotactic polystyrene,
ポリフェニレンスルフィド、ポリフェニレンエーテル、 Polyphenylene sulfide, polyphenylene ether,
ポリアミド、ポリエステル、ポリカーボネートなどが挙げられる。 Polyamides, polyesters, and polycarbonate. これらのその他の熱可塑性樹脂は、それぞれ単独で、あるいは2種以上を組み合わせて用いることができ、その配合量は、本発明の目的を損なわない範囲で適宜選択される。 These other thermoplastic resins, singly or may be used in combination of two or more, the amount is appropriately selected in a range that does not impair the object of the present invention.

【0034】(配合剤)本発明に使用される成形材料には、本発明の目的を阻害しない範囲で、合成樹脂用に一般的に用いられる配合剤を配合しても良い。 [0034] The molding material used in the (formulation) present invention, in a range that does not impair the object of the present invention, generally formulations used may be added to the synthetic resin.

【0035】成形時の成形性を改良すること等を目的として、ノルボルネン系開環重合体等に多価アルコールのエーテル化物または多価アルコールのエステル化物を添加してもよい。 The purpose of such to improve the moldability during molding, may be added to the ring-opened norbornene ethers of polyhydric alcohol polymer and the like or polyhydric alcohol ester. 具体的には、例えば特開昭63−275 More specifically, for example, JP-A-63-275
654号で公知のグリセリンモノステアレート、グリセリンモノラウレート、グリセリンモノベヘネート、ジグリセリンモノステアレート、グリセリンジステアレート、グリセリンジラウレート、ペンタエリスリトールモノステアレート、ペンタエリスリトールモノラウレート、ペンタエリスリトールモノベヘレート、ペンタエリスリトールジステアレート、ペンタエリスリトールジラウレート、ペンタエリスリトールトリステアレート、ジペンタエリスリトールジステアレートなどの多価アルコールのエーテル化物;3−(オクチルオキシ)−1,2 Known glycerol monostearate at No. 654, glycerin monolaurate, glycerin monobehenate, diglycerin monostearate, glycerin distearate, glycerin dilaurate, pentaerythritol monostearate, pentaerythritol monolaurate, pentaerythritol monobehenate rate, pentaerythritol distearate, pentaerythritol dilaurate, pentaerythritol tristearate, ethers of polyhydric alcohols such as dipentaerythritol distearate; 3- (octyloxy) -1,2
−プロパンジオール、3−(デシルオキシ)−1,2− - propanediol, 3- (decyloxy) -1,2
プロパンジオール、3−(ラウリルオキシ)−1,2− Propanediol, 3- (lauryloxy) -1,2
プロパンジオール、3−(4−ノニイルフェニルオキシ)−1,2−プロパンジオール、1,6−ジヒドロキシ−2,2−ジ(ヒドロキシメチル)−7−(4−ノニルフェニルオキシ)−4−オキソヘプタン、p−ノニルフェノールとホルムアルデヒドの縮合体とグリシドールの反応により得られるエーテル化合物、p−オクチルフェノールとホルムアルデヒドの縮合体とグリシドールの反応により得られるエーテル化合物、p−オクチルフェノールとジシクロペンタジエンの縮合体とグリシドールの反応により得られるエーテル化合物などの多価アルコールのエステル化物が挙げられる。 Propanediol, 3- (4-nonyl-yl-phenyl) -1,2-propanediol, 1,6-dihydroxy-2,2-di (hydroxymethyl) -7- (4-nonylphenyloxy) -4-oxo heptane, p- nonylphenol with condensate and ether compound obtained by reaction of glycidol formaldehyde, p- octylphenol and ether compound obtained by reaction of a condensate and glycidol formaldehyde, p- octylphenol and condensate and glycidol dicyclopentadiene polyhydric alcohol ester of such ether compounds obtained by the reaction.

【0036】これらの多価アルコールのエーテル化物またはエステル化物の分子量は特に限定しないが、通常5 The molecular weight of these polyhydric alcohol ether compound or ester compound is not particularly limited, usually 5
00〜2000、好ましくは800〜1500のものが、溶出しにくく、かつ透明性の低下も少なく好ましい。 00-2000, preferably of 800 to 1500 are eluted difficult, and even less preferred reduction in transparency. これらの多価アルコールのエーテル化物またはエステル化物は単独でまたは2種以上を組み合わせて使用され、その配合量は、ノルボルネン系開環重合体等100 Etherified products or esters of these polyhydric alcohols are used individually or in combination of two or more kinds, the amount thereof, norbornene ring-opening polymer or the like 100
重量部に対して、通常0.01〜5重量部、好ましくは0.05〜2重量部、特に好ましく0.1〜1.0重量部である。 Relative parts by weight, usually 0.01 to 5 parts by weight, preferably 0.05 to 2 parts by weight, particularly preferably 0.1 to 1.0 parts by weight. 添加量がこの範囲にある時に、成形性の改良と溶出を少なくすることの効果を高度にバランスすることができる。 When the addition amount is in this range, it is possible to highly balanced the effect of reducing the dissolution and moldability improvement.

【0037】ゴム質重合体と、多価アルコールのエーテル化物またはエステル化物を併用して用いることも好ましい。 [0037] and the rubber polymer, it is also preferably used in combination with an ether compound or ester of a polyhydric alcohol.

【0038】離型性などの成形性を改良することを目的として滑剤を用いることもできる。 [0038] Lubricants can also be used for the purpose of improving the moldability of such releasability. 滑剤としては、例えば無機微粒子を用いることができる。 As the lubricant, it can be used, for example inorganic fine particles. ここで、無機微粒子とは、長周期律表の1族、2族、4族、6族、7族、 Here, the inorganic fine particles, Group 1 of the long periodic table, Group 2, Group 4, Group 6, Group 7,
8〜10族、11族、12族、13族、14族元素の酸化物、水酸化物、硫化物、窒素化物、ハロゲン化物、炭酸塩、硫酸塩、酢酸塩、燐酸塩、亜燐酸塩、有機カルボン酸塩、珪酸塩、チタン酸塩、硼酸塩などの粒子状のもの、これらの化合物や塩の含水化合物の粒子状のもの、 Group 8-10, Group 11, Group 12, Group 13, oxides of Group 14 elements, hydroxides, sulfides, nitrides, halides, carbonates, sulfates, acetates, phosphates, phosphites, organic carboxylates, silicates, titanates, those particulate, such as borate, those particulate of these compounds or hydrate of a salt,
これらの塩中心とする複合化合物の粒子状のもの、またはこれらの塩を主成分とする天然鉱物の粒子などを示す。 Those particulate composite compounds to these salts center, or indicating, for example, particles of natural mineral mainly composed of these salts. 滑剤の添加量は、使用目的に応じて適宜選択されるが、ノルボルネン系開環重合体等100重量部に対して、通常0.001〜5重量部、好ましくは0.005 The addition amount of the lubricant is suitably selected depending on the intended use, with respect to 100 parts by weight of such a norbornene-based ring-opening polymer is usually 0.001 to 5 parts by weight, preferably from 0.005
〜3重量部の範囲であであり、添加量がこの範囲にあるときに、動物容器の透明性とその成形時の成形加工性が高度にバランスされる。 To 3 and the Ah in the range of parts by weight, the amount is in when it is in this range, moldability transparency and its time of molding the animal container is highly balanced.

【0039】成形時の酸化や保存、長期使用している間の酸化劣化、老化劣化を防ぐことを目的として酸化防止剤を用いることが好ましい。 The oxidation and storage at the time of molding, oxidative degradation of while long-term use, it is preferable to use an antioxidant for the purpose of preventing aging degradation. 酸化防止剤としては、例えば、フェノール系酸化防止剤、リン系酸化防止剤、イオウ系酸化防止剤などが挙げられ、これらの中でも、フェノール系酸化防止剤が好ましく、アルキル置換フェノール系酸化防止剤が特に好ましい。 Examples of the antioxidant include phenol antioxidants, phosphorus antioxidants, include such sulfur-based antioxidant, among these, phenolic antioxidants are preferred, and alkyl-substituted phenolic antioxidants particularly preferred.

【0040】フェノール系酸化防止剤としては、従来公知のものが使用でき、例えば2,6−ジ−t−ブチル− [0040] As the phenolic antioxidant, a conventionally known ones can be used, for example, 2,6-di -t- butyl -
4−メチルフェノール、2,6−ジ−t−ブチル−4− 4-methylphenol, 2,6-di -t- butyl-4
エチルフェノール、オクタデシル−3−(3,5−ジ− Ethylphenol, octadecyl-3- (3,5-di -
t−ブチル−4−ヒドロキシフェニル)プロピオネート、2,2′−メチレン−ビス(4−メチル−6−t− t-butyl-4-hydroxyphenyl) propionate, 2,2'-methylene - bis (4-methyl -6-t-
ブチルフェノール)、4,4′−ブチリデン−ビス(6 Butylphenol), 4,4'-butylidene - bis (6
−t−ブチル−m−クレゾール)、4,4′−チオビス(3−メチル−6−t−ブチルフェノール)、ビス(3 -t- butyl -m- cresol), 4,4'-thiobis (3-methyl -6-t-butylphenol), bis (3
−シクロヘキシル−2−ヒドロキシ−5−メチルフェニル)メタンなどが挙げられる。 - cyclohexyl-2-hydroxy-5-methylphenyl) methane, and the like.

【0041】リン系酸化防止剤としては、一般の樹脂工業で通常使用されているものであれば格別な制限はなく、例えば、トリフェニルホスファイト、ジフェニルイソデシルホスファイト、フェニルジイソデシルホスファイト、トリス(ノニルフェニル)ホスファイトなどを挙げることができる。 [0041] As the phosphorus-based antioxidant, a general resin industry not particularly limitation as long as it is usually used, for example, triphenyl phosphite, diphenyl isodecyl phosphite, phenyl diisodecyl phosphite, tris etc. (nonylphenyl) phosphite and the like. イオウ系酸化防止剤としては、例えば、ジラウリル 3,3′−チオジプロピオネート、ジミリスチル 3,3′−チオジプロピオネート、ジステアリル 3,3′−チオジプロピオネート、ラウリルステアリル 3,3′−チオジプロピオネート、ペンタエリスリトール−テトラキス−(β−ラウリル−チオ−プロピオネート)、3,9−ビス(2−ドデシルチオエチル)−2,4,8,10−テトラオキサスピロ[5, Examples of the sulfur antioxidant include dilauryl 3,3'-thiodipropionate, dimyristyl 3,3'-thiodipropionate, distearyl 3,3'-thiodipropionate, lauryl stearyl 3,3 ' - thiodipropionate, pentaerythritol - tetrakis - (beta-lauryl - thio - propionate), 3,9-bis (2-dodecyl-thioethyl) -2,4,8,10-spiro [5,
5]ウンデカンなどが挙げられる。 5] undecane.

【0042】これらの酸化防止剤は、それぞれ単独で、 [0042] These antioxidants, each alone,
あるいは2種以上を組み合わせて用いることができる。 Or it may be used in combination of two or more.
酸化防止剤の配合量は、ノルボルネン系開環重合体等1 The amount of the antioxidant, norbornene ring-opening polymer or the like 1
00重量部に対して、通常0.001〜5重量部、好ましくは0.01〜1重量部の範囲である。 Against 00 parts by weight, usually 0.001 to 5 parts by weight, preferably 0.01 to 1 parts by weight.

【0043】耐候性などを改良することを目的として紫外線防止剤を添加することもできる。 [0043] It is also possible to add an ultraviolet inhibitor for the purpose of improving the weather resistance. 埃の付着、静電気の防止を目的として、帯電防止剤を使用することもできる。 Dust attachment, in order to prevent static electricity, it is also possible to use an antistatic agent. その他にも、例えば、着色するための顔料や染料; Besides, for example, pigments and dyes for coloring;
ブロッキング防止剤;天然油、合成油、ワックスなどの滑剤;難燃剤などを配合しても良い。 Antiblocking agents; natural oils, synthetic oils, lubricants such as wax; and flame retardants may be incorporated. これらのその配合剤は、それぞれ単独であるいは2種以上を組み合わせて用いることができ、その配合量は、本発明の目的を損ねない範囲で適宜選択される。 These its formulations can be used each alone or in combination of two or more thereof, the amount is appropriately selected in a range not impairing the object of the present invention.

【0044】(成形材料)本発明に使用される成形材料は、ノルボルネン系開環重合体等に上記成分を混合したものが用いられる。 The molding material used in (molding material) A, a mixture of the components in the norbornene-based ring-opening polymer or the like is used. 混合する方法は、ノルボルネン系開環重合体等とその他のポリマー成分や配合剤が十分に分散する方法であれば、特に限定されない。 Mixing method of, if the method of ring-opened norbornene polymer and the like and other polymer components or formulation is thoroughly dispersed is not particularly limited. 例えば、ミキサー、二軸混練機などで樹脂を溶融状態で混練する方法、適当な溶剤に溶解して分散させて凝固法、キャスト法、または直接乾燥法により溶剤を除去する方法などがある。 For example, a mixer, a method of kneading a resin in a molten state in such twin-screw kneader, coagulation is dispersed and dissolved in an appropriate solvent, and a method of removing the solvent by casting or direct drying method.

【0045】混練する場合には、樹脂温度がその樹脂のガラス転移温度+50℃〜ガラス転移温度+150℃の温度とすることが適当であり、十分にシェアをかけることにより好ましい均一な混合状態とすることができる。 [0045] When the kneading is appropriate that the resin temperature is a glass transition temperature of + 50 ° C. ~ glass transition temperature + 150 ℃ the temperature of the resin, and preferably uniformly mixed state by applying a sufficiently share be able to.
樹脂温度が低すぎると粘度が高くなり混練が困難であり、高すぎると樹脂やゴム質重合体が劣化し、粘度や融点の差により両者がうまく混練できない。 The viscosity when the resin temperature is too low, it is difficult to high becomes kneading, too high a resin or rubber polymer is deteriorated, is not well kneaded both by the difference in viscosity and melting point. スクリュー形状等、混練の条件は混練機の種類、形状等によりそれぞれ適切な条件とすべきである。 Screw shape, condition of kneading should be respectively appropriate conditions kinds of kneaders, the shape or the like. 用いる樹脂、ゴム質重合体、混練に用いる装置の組み合せによって、予備的に混練して、その組み合せにあった回転数、滞留時間等を決めることが好ましい。 Resins, rubbery polymer used, a combination of an apparatus used for kneading, and preliminarily kneaded, the rotational speed was in the combination, it is preferable to determine the residence time and the like. 混練後は、通常は、溶融状態で棒状に押し出し、ストランドカッターで適当な長さに切り、ペレットとして用いられることが多い。 After the kneading, usually, extruded into a rod in a molten state, cut to length by a strand cutter, is often used as pellets.

【0046】(成形方法)本発明の動物容器は上記の成形材料を成形して得られるものである。 [0046] Animals container (molding method) The present invention is obtained by molding the molding material described above. 成形方法は、従来公知の成形方法に従えば良く、射出成形、押出ブロー成形、射出ブロー成形、多層ブロー成形、コネクションブロー成形、二重壁ブロー成形、延伸ブロー成形、真空成形、回転成形などが挙げられる。 Molding method may according to the conventionally known molding method, injection molding, extrusion blow molding, injection blow molding, multilayer blow molding, connection blow molding, double wall blow molding, stretch blow molding, vacuum molding, rotational molding and the like and the like. 成形時の樹脂の溶融温度はノルボルネン系開環重合体等の種類によっても異なるが通常150〜350℃が好適である。 Melting temperature of the resin during molding is preferred different but usually 150 to 350 ° C. depending on the kind of such a norbornene-based ring-opening polymer. また、特開平4―276253号公報に知られるように他の樹脂との多層成形や、二重壁成形で、さらなるガスバリア性や、耐候、耐光性などを高めることは、目的に応じて、 Moreover, and multilayer molded with other resins as known in Japanese Patent Laid-Open No. 4-276253, a double wall forming, to enhance further gas barrier properties and, weatherability, and light resistance, depending on the purpose,
内容物の視認性に影響がない程度で可能である。 Effect on the visibility of the contents is possible to the extent that there is no. また、 Also,
動物容器の内容物の視認性を高め、動物の排泄物を容易に洗い流すことができることから、金型表面仕上げ特に容器内容面に対応する金型部分の表面仕上げは、シボリ加工などが無い通常のエメリークロス研磨仕上げ、鏡面加工仕上げで、動物容器表面に目に見える大きな凸凹の無いことが好ましい。 Enhance the visibility of the contents of the animal container, the animal waste because it can be easily washed away, the surface finish of the mold portion corresponding to the mold surface finish especially container contents plane, drawing such normal no emery cloth finish polishing, a mirror finishing is preferably no greater irregularities visible to the animal container surface. 但し、装飾や内容物の識別等の目的で主に外側表面の一部に凹凸が設けられていても差し支えない。 However, no problem even if the main irregularities are provided on a part of the outer surface for identification purposes such as decoration and contents.

【0047】動物容器の底面や側面を含む主要部分は一体となって成形されることがこのましいが、生産性、強度の点で困難はあるものの、板状の成形物など部分品を別々に成形しておいて、これらを接着、溶着、凹凸を組み合わせて固定する、またはこれらの方法の組み合わせによる方法で所望の形状の容器としても良い。 [0047] Although the main portion including a bottom surface and side surfaces of the animal container preferable to be molded together, productivity, although difficulties in terms of intensity is, separate plate-shaped molded product such as parts keep in molded, these adhesion, welding, securing a combination of irregularities, or may be a container of a desired shape by way of a combination of these methods.

【0048】また、落下衝撃等に対する機械強度を改良するために、成形時の金型中に金網などの補強材を予めセットしておき、インサート成形したり、成形後または成形中に他の補強材を動物容器の表面に積層させて用いても良い。 [0048] In order to improve the mechanical strength against drop impact or the like, in advance set the reinforcing material, such as wire mesh into a mold during molding, insert molding or other reinforcing or during molding after the molding Material may be used by laminating on the surface of the animal container.

【0049】また、ゴム質重合体を配合した成形材料を使用する場合には、動物容器は、ゴム質重合体等の配合剤を添加することにより、一般に透明性は低下することが多いが、樹脂、配合剤、配合割合によって透明性の低下の度合は異なり、動物容器の面の一部を切り出して測定した時の、波長領域450〜700nmの範囲での光線透過率の最小値が通常20%以上、好ましくは30% [0049] In the case of using a molding material obtained by blending a rubber polymer, animal container, by adding the compounding agents rubbery polymer such as, but is generally in transparency often lowered, resins, compounding agents, unlike the degree of lowering of transparency by blending ratio, when measured by cutting out a portion of the surface of the animal container, usually the minimum value of light transmittance in the wavelength range of 450 to 700 nm 20 % or more, preferably 30%
以上、より好ましくは40%以上であることが好ましい。 Or higher, and more preferably 40% or more. 同一の配合剤、配合剤量の場合でも、配合剤がミクロドメンを形成して分散している場合は、0.3μm以下、特に0.2μm以下のミクロドメインを形成していれば、可視光の波長よりも配合剤の直径が小さく、光が散乱しにくいため、透明性に優れ好ましい。 Same formulation, even if the formulation amount, if the formulation is dispersed to form a Mikurodomen is, 0.3 [mu] m or less, if the particular form the following microdomains 0.2 [mu] m, visible light smaller diameter of formulation than the wavelength, light is hardly scattered, preferably excellent in transparency. また、ゴム質重合体と、多価アルコールのエーテル化物またはエステル化物を併用して用いる場合には、形成されるミクロドメインの直径を0.15μm以下、好ましくは0.1 Further, the rubbery polymer, when used in combination with polyhydric alcohol ether compound or ester is the diameter of the microdomains formed 0.15μm or less, preferably 0.1
μm以下までも分散させることが容易になるため好ましい。 μm preferable because it becomes easy to disperse to below.

【0050】(容器)本発明の動物容器は、動物を扱う各種容器に用いることができ、例えば動物用実験容器や特に長期間使用する動物飼育容器として有用である。 [0050] (container) Animal container of the present invention can be used for various containers to handle animals are useful as animal breeding container used for example animal laboratory vessel and especially long term. 本発明の動物容器はネズミや小型うさぎ等の哺乳類、ヘビ、蛙、亀、トカゲ等の両生類などをペット用として飼育したり、マウス、ラットやモルモットなどの実験用小動物を医薬品の開発、安全性試験を行なうために飼育するのに適している。 Mammalian animal container rats and small rabbits or the like of the present invention, snake, frog, turtle, or breeding, such as amphibians, lizards, etc. as for pets, developed a mouse, a small laboratory animals such as rats and guinea pigs of pharmaceuticals, safety suitable for breeding in order to perform the test. 特に種々の動物実験に用いる薬品からの汚染に対する耐性があり、排泄物の易洗浄性に優れることから実験用動物飼育容器として好適である。 In particular is resistant to contamination from chemicals used in the various animal experiments, it is suitable as a laboratory animal breeding containers because of excellent easy cleaning of excrement.

【0051】動物容器の形状はこれらの目的にかなうものであれば特に限定しない。 [0051] The shape of the animal container is not particularly limited as long as it meets these objectives. しかし、中で動物を飼育することから、平らな底面を有することがこのましい。 However, since the animal husbandry in, preferable to have a flat bottom surface. 特に実験動物飼育用容器の場合は、成形加工性を良くし、 Especially in the case of laboratory animal breeding containers, to improve the moldability,
排泄物の易洗浄性を良くし、空の動物容器をコンパクトに収容できる点から、底面、側面および上面がほぼ長方形である直方体形状で、かつ上面または側面の一面が開放された形状であることが好ましい。 To improve the easy cleanability of excrement from the viewpoint that can accommodate compactly empty animal container bottom, a rectangular parallelepiped shape sides and the top are substantially rectangular, and that one side of the upper surface or side is in an open shape It is preferred. この開放面には通常はフタが取り付けられる。 This open surface usually lid is attached. このような底面を含む部分を以下本体と呼ぶ。 A portion including such bottom hereinafter referred to as the body.

【0052】動物容器の本体の大きさは、動物の種類または飼育する数によって適宜選択されれば良い。 [0052] The size of the body of the animal container may be selected appropriately depending on the number of the type of animal or breeding. 好適には、1匹以上好ましくは例えば4匹またはそれ以上の複数の小動物がその中で飼育され、飼育される動物が精神的なストレスの無い状態で飼育されることが好ましく、 Preferably, more than one animal preferably housed therein, for example, four mice or more of the plurality of small animals, it is preferred to be kept in a state animals kept is no mental stress,
外から中の状態を観察でき、また容器の収納場所からの出し入れの際に取り扱い易い大きさであることがこのましい。 Can observe the state in the outside, also preferred to be easy to handle size at the time of removing them from storage locations of the container. 好ましい大きさは内容積1〜100リットル、さらに好ましくは10〜60リットルである。 The preferred size is the internal volume from 1 to 100 liters, more preferably 10 to 60 liters. 小さければ中で小動物が飼育しにくい、または飼育できる動物数が少なく、動物実験の目的である複数の検体に対して同一条件で飼育比較するという目的に適わなくなることがある。 Small animal is hard reared in smaller or fewer number of animals that can be bred, and may not compete on the object of rearing compared under the same conditions for a plurality of analytes is an object of the animal experiments. また、大き過ぎれば取り扱いしにくい、収納場所に困るなどの難点がある。 In addition, there are drawbacks, such as difficult to handle if too large, troubled in the storage location. ここで内容積とは、容器の動物取り出し口などの大きな穴があいていればこれを塞いだ時の容器の内部、即ち主に凹面と平面によって形成される面によって水などの液体を貯えたと想定したばあいに貯えられる液体の最大容積として定義される。 Here the internal volume and the interior of the container when closes this if big hole, such as animal outlet of the container, i.e. mainly has stored a liquid such as water by the plane formed by the concave and plane It is defined as the maximum volume of liquid to be stored in case of assuming. また、底面および側面の各辺の長さは、高さは通常50〜800 The length of each side of the bottom and side surfaces, the height usually 50 to 800
mm、好ましくは80〜600mmであり、底面の1辺は80〜1000mm、好ましくは100〜800m mm, preferably 80~600mm, 1 side of the bottom 80~1000Mm, preferably 100~800m
m、底面の長手方向の長さと、それに垂直な方向の長さの比(短い方向の長さ/長手方向の長さ)は通常0.4 m, longitudinal length and, perpendicular thereto direction length ratio of the bottom surface (short direction length / longitudinal length) is usually 0.4
〜1、好ましくは0.5〜である。 To 1, preferably 0.5. これらの条件を満たす時に、動物が快適に過ごすことができる空間を確保することができ、動物容器の収納にも効率がよく好ましい。 Upon satisfying these conditions, the animals can be secured a space can spend comfortably even efficient preferred storage of animal container.

【0053】動物容器の厚みは、全体に渡って0.5〜 [0053] Animal container of thickness, 0.5 over the whole
30.0mm、好ましくは0.7〜25mm、より好ましくは1.0〜22mmの範囲である。 30.0 mm, preferably 0.7~25Mm, more preferably from 1.0~22Mm. 薄過ぎれば機械強度が低下し破損しやすくなり、厚いと重くて取り扱い難いなどの不都合がある。 If Sugire thin becomes mechanical strength is easily broken lowered, there is a disadvantage such as hard thick and heavy handling. 但し、通気や動物の出し入れのための穴については容器全体の強度を損ねず、飼育容器に使用する目的を損ねない範囲においていくつあっても不都合は無い。 However, without impairing the strength of the entire container for hole for out of aeration and animals, inconvenience any number of times within a range not impairing the purpose of using the rearing container no. また、一方向に開いた部分を除いて、 In addition, with the exception of the open portion in one direction,
容器の側面や底面などの全ての面の面積の総和に対して、好ましくは20%以下の面積であれば上記の厚みの好ましい範囲を外れて厚いまたは薄い部分があっても差し支えないし、一方向に開いた穴以外のこれに比べて小さな穴が開いていても差し支えない。 With respect to the total sum of the areas of all the terms of the side surface or the bottom surface of the container, preferably to no problem even if the thick or thin portions out of the preferable range of the thickness if the area of ​​20% or less, one-way no problem be open a small hole in comparison to the other hole open to the. 例えば、容器の上面または側面に餌箱や水のみ用器具をとりつけることがあり、このような部分に必要な穴あっても差し支えない。 For example, it may attach the feeders and water alone instrument the top or side of the container, no problem even holes required for such parts. また、通気性を良くすることを目的として、このましくは上面または側面に、中に飼育する動物が逃避できない程度の大きさの1個または複数の通気孔を設けても良い。 Further, for the purpose of improving the breathability, preferably the upper surface or side, animal breeding may be provided one or more ventilation holes of a size that can not escape into.

【0054】底面、辺の部分それぞれの厚みは、0.5 [0054] bottom, sides of portions each thickness, 0.5
〜40mm、好ましくは0.7〜30mm、より好ましくは1.0〜25mmである。 ~40Mm, preferably 0.7~30Mm, more preferably 1.0~25Mm. 底部の厚みt1は、側面の厚みt2に比べてほぼ等しいか、もしくは、より厚いことが好ましい。 The thickness t1 of the bottom, approximately equal than the thickness of the side surface t2, or is preferably thicker. しかし、厚みの差が大きくなるほど、 However, as the difference in thickness is large,
落下時の応力集中が大きくなるので、好ましくは0.7 Since the stress concentration is increased at the time of fall, preferably 0.7
≦t1/t2≦3、より好ましくは0.8≦t1/t2 ≦ t1 / t2 ≦ 3, more preferably 0.8 ≦ t1 / t2
≦2.5、より好ましくは0.9≦t1/t2≦2の範囲が好ましい。 ≦ 2.5, more preferably in the range of 0.9 ≦ t1 / t2 ≦ 2. この場合の底部の厚みとは、底部で最も薄い部分の厚みを示す。 The thickness of the bottom of the case, showing the thickness of the thinnest portion at the bottom. 厚みは厚くすることで、容器に使用する樹脂の量が多くなり、容器コストが高くなったり、重くなったりする。 By thickness thicker, the number the amount of resin used in the container, the container cost or higher, or heavier. 薄すぎると、落下強度が低下するなどの不具合が生ずる。 If too thin, defects may occur, such as drop strength decreases. 厚みは、容器動物容器容器側面とでは均一であることが、衝撃強度の面では好ましいが、特に限定しない。 Thickness, it is uniform in the container animal container vessel sides is preferred in terms of impact strength is not particularly limited.

【0055】動物容器の局部的な形状の特徴に関して、 [0055] With respect to the characterization of the local shape of the animal container,
構成する各面は平面または穏やかな曲面であり、面と面の境界は穏やかな局面を形成していることが好ましいことが本願の研究の過程で見いだされた。 Surfaces constituting is flat or gently curved, it is preferable boundary surface and the surface is forming a gentle aspects were found in the course of the present study.

【0056】例えば容器底面と容器側面とが連続した外側表面を形成している場合、両面の交わる部分すなわち辺は曲率半径(以降この曲率半径をROと表す)で好ましくは2.0mm以上、さらに好ましくは3.0mm以上の大きさの曲率半径を有している曲面から形成されることにより、動物容器を長期間使用していく場合の耐排泄物汚染性が良好であることが本発明者らによって新しく見いだされた。 [0056] For example, when the container bottom and the container side form a continuous outer surface, both surfaces of intersecting portion or edges (representing the radius of curvature after the RO) radius of curvature preferably 2.0mm or more, more preferably by being formed from a curved surface having a radius of curvature than the size 3.0 mm, it is the present inventors is excellent withstand excrement contamination resistance when going to use the animal container long term It was found newly by et al. 各辺における曲率半径が2.0mm未満である場合、この部分に動物容器を成形した時の応力が残留し(以下動物容器または成形品の残留応力という)、その残留応力が大きい部分に、温水洗浄や乾燥などを繰返すうちにクラック(微小な割れ、外観上白っぽく見える)が発生し、ここに排泄物が染み込み、洗浄が困難になり、十分洗浄できなかった部分にさらに排泄物が固着しやすくなるという悪循環により、長期間使用するうちにどんどん汚染が進むという問題が発生しやすくなり好ましくない。 If the radius of curvature at each side is less than 2.0 mm, and the residual stress at the time of molding the animal container in this part (hereinafter referred to as animal containers or moldings residual stress), the portion thereof residual stress is large, hot water cracks while repeating such as cleaning and drying (micro cracks, appearance whitish) is generated, wherein the excrement permeates, cleaning becomes difficult and easier to excrement is fixed to part could not wash the vicious cycle of becoming, a long period of time more and more pollution is is likely to occur a problem that the advance is not preferable to one that you want to use. また、曲率半径が小さい場合、落下等に対する強度が低下し好ましくない。 Further, when the curvature radius is small, undesirable strength against dropping or the like is reduced. ROの上限は特に無いが、必要以上に大きな値であれば、動物容器のなかで局面部が大きく、底面の平らな部分が相対的に小さくなり、飼育する動物の居住空間が狭くなり好ましくないことこら、ROは通常300mm以下、好ましくは2 The upper limit of the RO is not particularly, if unnecessarily large value, a large phase portion among the animals vessel, becomes flat portion of the bottom surface is relatively small, the living space of the breeding animal is narrowed undesirable it Hey, RO is typically 300mm or less, preferably 2
00mm以下である。 00mm is less than or equal to.

【0057】また、本発明の動物容器は上記の容器外側の面の各辺(凸面)の曲率半径RO以外に、容器内側の面の各辺(凹面)に対してもなだらかな曲面となっていることが好ましく(以降内面の辺の曲率半径をRIと表す)、耐衝撃強度が良好なこと、動物の排泄物を洗浄しやすい形状となる。 [0057] In addition to the radius of curvature RO of the animal container of the present invention each side of the container outer surface (convex surface), also a gentle curved surfaces with respect to each side of the container inner surface (concave surface) it is preferred to have (hereinafter represents the radius of curvature of the inner surface side and RI), it impact strength is good, the washed animal excrement tends shape. RIは通常0.1〜300mm、好ましくは0.5〜200mmであり、小さい場合は、その辺に付着した排泄物が洗浄しにくく、また、残留応力を持ちやすい構造であることから、長期間の耐排泄物汚染性が低下する。 RI typically 0.1~300Mm, preferably 0.5~200Mm, if small, difficult to wash excrement adhering to the sides, also because it is easy to have the residual stress structure, long term anti excrement contamination deteriorates the. 大き過ぎれば、ROが大きい場合と同様に底面の平らな部分が相対的に小さくなり、飼育する動物の居住空間が狭くなり好ましくない。 If too large, RO flat portion of the bottom surface as if large becomes relatively small, the living space of the breeding animal is narrowed undesirable.

【0058】以上のROとRIの値は、辺の曲面の断面形状が円弧であるとして、曲面のなだらかさの指標として用いた値であるが、局面の断面形状は特に円弧とは限らなく、放物線、正弦曲線などに近い、曲率半径が一定でない形状もありうる。 [0058] or more values ​​of RO and RI are as cross-sectional shape of the sides of the curved surface is an arc, but is a value used as an index of smoothness of the curved surface, aspects of the cross-sectional shape is not particularly limited to a circular arc, parabola, close to such sinusoidal, there may be shaped curvature radius is not constant. この場合、局面中の連続的に変化する曲率半径の最小値が上記で議論した値となっていれば良い。 In this case, the minimum value of the radius of curvature continuously changes in aspect has only to a value discussed above.

【0059】容器の厚みが露出した部分、すなわち前記開放面や穴の縁は面取りして丸くする(以降曲率半径r [0059] portion thickness of the container is exposed, i.e. the edge of the open surface and hole are round chamfered (hereinafter the radius of curvature r
と表す)ことが好ましい。 Represent) is preferred. 縁取りの曲率半径rの大きさは、使用目的に応じて適宜選択されるが、通常0.01 The size of the radius of curvature r of the border is appropriately selected depending on the intended use, typically 0.01
〜50mm、好ましくは0.1〜20mmの範囲のものが、残留応力を充分に小さくでき、長期間にわたっての薬液との接触によるクラックの発生や外部衝撃に対する割れ等を低減できるので好適である。 ~50Mm, preferably in the range of 0.1~20mm is, the residual stress can sufficiently small, it is preferable because it reduces the cracks for cracks or external shock caused by contact with chemical liquid for a long period of time. 更に端面をゆるやかに折り返して(この部分の凸面側の曲率半径をREと表す)、2重構造の縁取りとすることも、全体の機械強度の向上、耐溶剤・耐薬品性が良好となる点、取り扱い時に指をかけて出し入れ、持ち運びができる点で好ましい。 Further gently folded end face (representing the radius of curvature of the convex side of this part and RE), also be a border of double structure, improvement in overall mechanical strength, that solvent and chemical resistance will be good , and out over the finger at the time of handling, preferable in that it is portable. また一方向に開いた穴の周りに、動物容器の衝撃強度等を向上させる目的で、リブと呼ばれる構造を設けることもできる。 Also around the hole opened in one direction, for the purpose of improving the impact strength of the animal container or the like, it may also be provided a structure called a rib. リブは側面に対して垂直またはこれに近い突起で、大きさは、縦方向(動物容器の高さ方向)は動物容器の高さの通常1/20〜19/20、横方向(動物容器の側面に垂直な方向)は通常5〜150m Rib in projection near vertical or hand side, the size, the vertical direction (the animal container height direction) is usually 1 / 20-19 / 20 of the height of the animal container, lateral (animal container perpendicular to the lateral direction) is usually 5~150m
m、厚みは動物容器の側面の厚みの通常1/2〜10倍である。 m, the thickness is usually 1 / 2-10 times the thickness of the side surface of the animal container.

【0060】動物容器の本体に上記の一方向に開いた穴をがある場合、なんらかのフタが必要となる。 [0060] If there is a hole opened to the one-way to the body of the animal container, some cover is required. 可能であればこの穴を塞ぐフタを本発明の動物容器の一部として本体との一体成形をしても良いし、本体とフタに別々に成形しても良い。 If possible may be integrally molded with the body as part of the animal container of the present invention a lid for closing the hole, it may be formed separately on the body and lid. 本発明の容器の一部としてノルボルネン系開環重合体等からなる成形材料で成形したものが好ましく用いることができるが、本体に比べて排泄物などの汚染が少ないことからノルボルネン系開環重合体等以外の透明熱可塑性樹脂からなる成形材料を成形したもの、金網や金属板などの金属製のものであっても差し支えない。 May be used is preferably one molded by the molding material as part of the container of the present invention made of a norbornene-based ring-opening polymer or the like, a ring-opened norbornene polymer since there is less contamination of the excrement than the body those molding a molding material comprising a non-transparent thermoplastic resin etc., no problem be of metal, such as wire mesh or metal plate. 容器がフタと本体に別れている場合において、 When the container is divided into lid and body,
フタをノルボルネン系開環重合体等で成形する場合には、フタは必ずしも強度を要求されないので、フタの辺において上記のROやRIの好ましい範囲を満たす必要は無いが、満たしていても良い。 When molding the cover in ring-opened norbornene polymer and the like, since the lid is not necessarily required strength, it is not necessary to satisfy the preferable range of the above RO and RI at the sides of the lid, may be satisfied. 通常、フタには通気孔を設け、かつ水や餌箱が取り付けられるようになっている。 Usually, the cover is adapted to the vent hole is provided, and water or feeders are attached. この場合は、本体の側面等に水や餌用の穴を設ける必要は無い。 In this case, it is not necessary to provide a hole for water or food on the side surface or the like of the body.

【0061】また、糞や尿などの排泄物や餌の残骸が動物の体に付着してそこに雑菌がついて、動物が予定しない病気にかかるのを防ぐ目的で、本体内側の底面には、 [0061] In addition, the debris of excrement and food, such as feces and urine is attached to the body of the animal with a bacteria in there, in order to prevent the applied to the sick animals is not scheduled, on the bottom surface of the inner body,
底面に平行に近い配置でスノコ状に穴のあいた板や金網を設けても良い。 It may be provided a plate or wire mesh with a hole in the grating-like parallel close arrangement on the bottom. スノコ状に穴のあいた板は可能であれば本発明の動物容器の本体の一部としてノルボルネン系開環重合体等からなる成形材料を用いて本体との一体成形をする、またはノルボルネン系開環重合体等からなる成形材料を用いて別々に成形したものも好ましいが、分離可能である場合には、必ずしも透明性を必要としないことから、他の材料で成形したものであっても差し支えない。 The integrally molded with the body by using a molding material composed of a ring-opened norbornene polymer and the like as part of the body of the animal container of the present invention as long grating-like hole in the perforated plate is possible in, or a ring-opened norbornene is also preferable that molded separately using a molding material comprising a polymer or the like, no problem if it is separable from necessarily requiring no transparency, even if the molded with other materials .

【0062】また、動物容器表面は硬く、すべりやすいため、飼育される動物にとって必ずしも居心地が良くないため、麦わらや各種繊維からなるマットなどを敷いてその上で動物を飼育する様にして用いることも差し支えない。 [0062] In addition, the animal container surface hard, because the slippery, because not always cozy for breeding animal being, be used in the manner to breed the animal on the monitor on a mat made of straw and various fiber no problem also.

【0063】成形された動物容器は、一定期間の間、そのなかで動物を飼育したあと、内部の排泄物などの汚れを洗浄し、必要に応じて消毒され、さらにすすぎ洗い、 [0063] molded animals vessel during a certain period, after reared animals among them, washing the dirt, such as the interior of the waste, disinfected optionally further rinsing,
乾燥などの工程を経て繰返し使用される。 It is used repeatedly through steps such as drying. 洗浄の際には、消毒剤または洗浄剤が組み合わせて又は単独で使用されることが好ましい。 During washing it is preferably used in combination disinfectants or cleaning agents or alone. 消毒剤(洗浄剤)としては、アルコール系消毒剤、ヨード系消毒剤、逆性石鹸系消毒剤、グルコン酸クロルヘキシジン系消毒剤、塩素系消毒剤、酸系消毒剤、アルカリ系消毒剤などが挙げられる。 The disinfectant (cleaner), alcoholic disinfectants, iodine-based disinfectants, invert soap disinfectant chlorhexidine gluconate based disinfectants, chlorine disinfectants, acid disinfectants, and alkaline disinfectants mentioned It is.
アルコール系消毒剤としては、メタノール、エタノール、イソプロピルアルコール等の70%溶液製剤、ヨード系消毒剤としては、「ポピドンヨード」(明治製菓)、「ポピヨドン」(ヨシダ製薬)、「マイクロクリーン」(東洋理工(株))、逆性石鹸系消毒剤としては、「オスバン液」(日本製薬)、「マイクロカット」 The alcohol-based disinfectants, methanol, ethanol, as a 70% solution formulations, iodine disinfectants such as isopropyl alcohol, "povidone" (Meiji Seika), "Popiyodon" (Yoshida Pharmaceutical), "Micro clean" (Toyoriko Co., Ltd.), as the reverse of soap-based disinfectant, "Osban solution" (Nihon pharmaceutical), "micro-cut"
(東洋理工(株))などの塩化ベンザルコニウム製剤、 (Toyoriko Co., Ltd.) benzalkonium chloride preparations such as,
グルコン酸クロルヘキシジン系消毒剤としては、「ヒビテン」などのグルコネート製剤、塩素系消毒剤としては、次亜塩素酸塩製剤、酸系消毒剤としては、塩酸、硝酸、硫酸、りん酸などの溶液製剤、アルカリ系消毒剤としては、水酸化ナトリウム、水酸化カリウムなどの溶液製剤などが挙げられる。 The chlorhexidine gluconate based disinfectants, gluconate formulations such as "Hibitane", as the chlorine-based disinfectant, hypochlorite formulations, the acid-based disinfectant, the solution formulations such as hydrochloric, nitric, sulfuric, phosphoric acid as the alkali-based disinfectant, sodium hydroxide and the solution formulations such as potassium hydroxide.

【0064】これらの洗浄剤または消毒剤の使用方法としては、上記の消毒剤を常温の水または温水(40℃から90℃)で希釈し、常温の水の場合は、数時間から1 [0064] As methods of using these cleaners or disinfectants diluted the disinfectant at room temperature water or hot water (90 ° C. from 40 ° C.), in the case of room temperature water, from a few hours 1
0日間、温水の場合は、2時間から一昼夜浸けおきした後、水で消毒剤を洗い流し、水滴を乾燥することが一般的である。 0 days, in the case of hot water, after soaking overnight from 2 hours, water rinse disinfectant, it is common to dry the water droplets.

【0065】 [0065]

【実施例】以下、本発明について、実施例及び比較例を挙げてより具体的に説明するが、本発明は、これらの実施例のみに限定されるものではない。 EXAMPLES Hereinafter, the present invention will be described more specifically with Examples and Comparative Examples, the present invention is not limited only to these examples. 特に動物容器の形状については、実施例においては簡単な構造を有するものを試験的に作成し試験するが、この形状に限定されるものではない。 In particular the shape of the animal container, but to create and those having a simple structure experimentally tested in examples, but is not limited to this shape.

【0066】(参考例1)窒素雰囲気下、トリシクロ[4.3.1 2,5 [0066] (Reference Example 1) under a nitrogen atmosphere, tricyclo [4.3.1 2,5. 1,6 ]デカ−3,7−ジエン(3環体ノルボルネン類、慣用名ジシクロペンタジエン、日本ゼオン製、純度95重量%以上、以下DCPと略す)1 0 1,6] deca-3,7-diene (3 annulus norbornenes, common name dicyclopentadiene, Nippon Zeon, purity 95 wt% or more, hereinafter abbreviated as DCP) 1
00重量部を公知のメタセシス開環重合触媒系で重合し、次いで公知の方法で水素添加しDCP開環重合体水素添加物を得た。 00 parts by weight polymerized in known metathesis ring-opening polymerization catalyst system, and then to obtain a hydrogenated DCP ring-opening polymer hydrogenation product in a known manner. このDCP開環重合体水素添加物は、 The DCP ring-opening polymer hydrogenation product is
シクロエキサンを溶媒としたGPC(ゲル・パーミエーション・クロマトグラフ)でポリイソプレン換算で測定される数平均分子量Mnは、13,000であった。 The number average molecular weight Mn measured by the terms of polyisoprene by GPC the cycloexane as solvent (gel permeation chromatography) was 13,000. このDCP開環重合体水素添加物を公知の方法で乾燥した。 The DCP ring-opening polymer hydrogenation product was dried in a known manner. プロトンNMR法により水素添加反応の前後で比較して水素添加率が99.8%以上、DSCにより測定したTgは97℃、25℃における屈折率1.5230 Hydrogenation rate compared before and after the hydrogenation reaction is 99.8% or more by proton NMR method, Tg is 97 ° C. as measured by DSC, refractive index at 25 ° C. 1.5230
(ASTM D542準拠)であった。 It was (ASTM D542 compliant). このペレット1 The pellets 1
00重量部に対して0.2重量部のフェノール系老化防止剤ペンタエリスリチル−テトラキス(3−(3,5− 00 weight phenolic antioxidant 0.2 parts by weight per part pentaerythrityl - tetrakis (3- (3,5
ジ−ターシャリーブチル−4−ヒドロキシフェニル)プロピオネート)と0.4重量部の水添スチレン・ブタジエン・スチレン・ブロック共重合体(旭化成工業株式会社製タフテックH1051、クラム状、30℃における屈折率1.5173)を混合し、二軸混練機で混練し、 Di - tert-butyl-4-hydroxyphenyl) propionate) and hydrogenated styrene-butadiene-styrene block copolymer 0.4 parts by weight (Asahi Chemical Industry Co., Ltd. Tuftec H1051, crumb, refractive index at 30 ° C. 1 .5173) were mixed and kneaded by a twin-screw kneader,
ストランド(棒状の溶融樹脂)をストランドカッターを通してペレット(粒状)状の成形材料を得た。 The strand (rod-shaped molten resin) to obtain pellets (granular) form of the molding material through a strand cutter. このペレットを、熱プレス(樹脂温度160℃、300kgf/ The pellet, heat press (resin temperature 160 ° C., 300 kgf /
cm 2 、3分)で20mm×15mm、厚さ3.0mm cm 2, 3 minutes) in a 20mm × 15mm, thickness 3.0mm
の板を成形した。 The plate was molded. この板は透明で、400〜700nm This plate is transparent, 400~700nm
での光線透過率は最小で90.0%であった。 Light transmittance at was 90.0% at the minimum. この板を約0.05μmの厚さにスライスし、四酸化ルテニウムでポリスチレン部分を染色し、透過型電子顕微鏡により観察したところ、ゴム質重合体は樹脂のマトリックス中で直径約0.04μmのほぼ球状のミクロドメイン構造をとっていた。 Slicing the plate to a thickness of about 0.05 .mu.m, four ruthenium oxide stained polystyrene part was observed by a transmission electron microscope, the rubber polymer is generally a diameter of about 0.04μm in the resin matrix I was taking a micro-domain structure of spherical. このペレットのガラス転移温度は96℃ The glass transition temperature of the pellets 96 ° C.
であった。 Met.

【0067】(参考例2)DCPの代わりに、8−メチル−テトラシクロ[4.4.1 2,5 [0067] (Reference Example 2) instead of DCP, 8- methyl - tetracyclo [4.4.1 2,5. 7,10 1 7,10. 0]ドデカ−3−エン(4環体ノルボルネン類、以下MTCDと略す)5重量部、ジシクロ[2.2.1]−ヘプト−2 0] dodeca-3-ene (4 annulus norbornenes, abbreviated as MTCD below) 5 parts by weight, dicyclo [2.2.1] - hept -2
−エン(2環体ノルボルネン類、以下NBと略す)15 - ene (2 annulus norbornenes, hereinafter referred to as NB) 15
重量部とDCP80重量部に代え(計100重量部)、 Instead of the weight portion and DCP80 parts by weight (100 parts by weight in total),
水添スチレン・ブタジエン・スチレン・ブロック共重合体を用いなかった以外は、参考例1と同様にしてMTC Except for using no hydrogenated styrene-butadiene-styrene block copolymer, in the same manner as in Reference Example 1 MTC
D/NB/DCP開環共重合体水素添加物を得た。 To obtain a D / NB / DCP ring-opening copolymer hydrogenated product. 重合体中の各ノルボルネン類の共重合比率を、重合後の溶液中の残留ノルボルネン類組成(ガスクロマトグラフィー法による)から計算したところ、MTCD/NB/TC When the copolymerization ratio of each norbornenes in the polymer was calculated from the residual norbornenes composition in solution after polymerization (by gas chromatography), MTCD / NB / TC
D=5/15/80でほぼ仕込組成に等しかった。 It equaled approximately feed composition with D = 5/15/80. このMTCD/NB/DCP開環重合体水素添加物は、Mn The MTCD / NB / DCP ring-opening polymer hydrogenation product is, Mn
は、14,000であり、水素添加率が99.8%以上、Tgは、81℃であった。 Is 14,000, hydrogenation rate of 99.8% or more, Tg was 81 ° C..

【0068】まず、本実験で行った物性試験について説明する。 [0068] First, a description will be given of the physical properties tests performed in this experiment.

【0069】(試験法1:透明性)成形後の未使用の動物容器にBALB−c雄性マウス(5週齢、日本クレア社)を5匹入れ、目視でどの程度まで動物が見えるか観察し、1m離れたところからマウスの動きまわる状態が観察でき、かつ、容器の一部分を切り出して分光光度計により測定した波長450〜700nmでの光線透過率の最小値が20%以上であるものを良好と判断した。 [0069] (Test Method 1: Transparency) unused animal container BALB-c male mice (5 weeks old, Nippon Clea) after molding were placed five, to what extent was observed whether the animal is visible with the naked eye can be observed a state in which around mouse movements from a distance 1 m, and better ones minimum value of light transmittance at wavelengths 450~700nm measured spectrophotometrically by cutting a portion of the container is 20% or more It was determined that.

【0070】(試験法2:耐衝撃試験)動物容器に鉄製の釘を錘として500g入れ、容器を垂直方向から45 [0070]: put 500g of iron nails (Test Method 2 impact resistance test) Animal vessel as a weight, 45 containers from the vertical direction
°傾けて、120cm高さから、コンクリート床面に落下させる試験を5回繰返した。 ° inclined from 120cm height was repeated 5 times a test of dropping a concrete floor. 10個の動物容器について同様に試験して、割れや亀裂の入るものがあるかどうかを観察し、10個とも割れや亀裂の無いものを良好と判断した。 10 for animals vessel was similarly tested, and observe whether there is to enter the crack or cracks was judged as good ones without cracks or cracks with ten.

【0071】(試験法3:残留応力と耐溶剤性の試験) [0071] (Test Method 3: Test of residual stress and solvent resistance)
成形時の応力が残りやすいと思われるR部に各種の溶剤を湿らせた布を当てて、60分間保持した後に発生するソルベントクラックを目視で観察し、動物容器中の残留応力と耐溶剤性を試験した。 Against stress during molding dampened various solvents in the R portion seems likely to rest cloth, solvent crack that occurs after holding for 60 minutes was visually observed, the residual stress in the animal container and solvent resistance It was tested. 溶剤としてはエチルアルコール、メチルメタクリレートとジメチルエーテルの3種類とし、各々の溶剤に対して試験を行い、全ての溶剤に対して、目視による白い傷、変色が無いものを良好とした。 The solvent and three ethyl alcohol, methyl methacrylate and dimethyl ether, were tested for each of the solvent, with respect to all solvents, white flaws visually, was considered good as discoloration no.

【0072】(試験法4:排泄物の易洗浄性試験)成形した動物容器にBALB−c雄性マウス(5週齢、日本クレア社)を5匹、14日間飼育したあと、容器に水道水をほぼ満杯に満たし、10分経過後、中の水を捨て、 [0072]: molded animal container in BALB-c male mice (5 weeks old, CLEA Japan, Inc.) (Test Method 4 easy-to-clean test of excrement) 5 mice, and after that were kept for 14 days, the tap water in a container meet almost full, after the lapse of 10 minutes, discard the water in,
さらに多量の水道水の流水で約2分洗い流したあと、スポンジで各面を2回ずつこすり洗いすることにより物理的に排泄物を除去させた。 Furthermore, after washing away about 2 minutes in the running water of a large amount of tap water, it was physically the waste is removed by scrubbing twice each surface with a sponge. 乾燥後の特に底面を詳細に目視観察し、シミや排泄物の残りがないかどうか確認し、 Was visually observed, especially the bottom surface detail after drying, to see if there are any remaining stains and excrement,
シミ、痕跡のないものを良好と判断した。 Stains, was judged to be good things without trace.

【0073】(試験法5:耐薬品性及び長期の排泄物耐性試験)成形した動物容器にBALB−c雄性マウス(5週齢、日本クレア社)を5匹、7日間飼育したあと、容器からマウスと餌を取り出し、中に水道水をほぼ満杯に満たし、10分経過後、中の水を捨て、さらに多量の水道水の流水で約2分洗い流した。 [0073] (Test Method 5: chemical resistance and long-term waste tolerance test) BALB-c male mice in molded animal container (5-week-old, CLEA Japan, Inc.) Five, after bred for 7 days, from the container removed mice and food, almost full fill the tap water in, after 10 minutes, discard the water in, was flushed for about another 2 minutes in running water of a large amount of tap water. スポンジで各面を10回ずつこすり洗いをした。 Each face with a sponge was scrubbed 10 times. 洗浄した後の動物容器を (1)酸系消毒剤の日本クレア(株)社製「ライム・ア・ウェイ」(PH1.6−2.0)を10倍に希釈し、 The animal container after cleaning the (1) of the acid-based disinfectant CLEA Japan Co., Ltd. "Lime-A-Way" (PH1.6-2.0) was diluted 10-fold,
12時間浸漬した。 It was immersed for 12 hours. (2)アルカリ系消毒剤アイセイ(株)社製「ネオバスキーL」(PH11.3)10倍に希釈し、12時間浸漬した。 (2) alkaline disinfectant son-in-law K.K. diluted "neovastat ski L" (pH 11.3) 10 times, and soaked for 12 hours. (3)アルコール系消毒剤のエタノールの70%水溶液製剤に12時間浸漬した。 (3) was immersed for 12 hours in a 70% aqueous solution formulation of ethanol alcohol disinfectant. (4)ヨード系消毒剤の日本クレア(株)社製「マイクロクリーン」を600倍に希釈し、12時間浸漬した。 (4) of iodine-based disinfectant CLEA Japan Co., Ltd. to "micro-clean" was diluted to 600 times, it was immersed for 12 hours. (5)塩素系消毒剤の日本クレア(株)社製「フジラックス」を500倍に希釈し、12時間浸漬した。 (5) Japan Clare of chlorine-based disinfectant Co., Ltd. to "Fuji Lux" was diluted to 500 times, was immersed for 12 hours. 以上のように洗浄、消毒した後、全体を水洗しながらブラシでこすり、その後3回水洗した。 After washing, disinfection as described above, rubbing with a brush while rinsing the whole was washed with water then three times. この一連の7日間のマウスの飼育と流水洗浄と滅菌処理を1サイクルとした。 The breeding and water cleaning and sterilization of mice in this series of seven days was one cycle. これを10サイクル行った後の動物容器を目視で、 Visually animals vessel after which 10 cycles,
シミや排泄物の付き方を観察し、汚れの無いものを良好とした。 To observe the way marked with spots and excrement, was a good thing no dirt.

【0074】(実施例1)参考例1のペレットを用いて、型締め圧350トン射出成形機にて、成形時の樹脂温度260℃、金型温度60℃の条件で射出成形し、以下の形状の容器を作成した。 [0074] The pellets of Example 1 Reference Example 1, at a mold clamping pressure 350 t injection molding machine, at the time of molding resin temperature 260 ° C., and injection molded under the conditions of a mold temperature of 60 ° C., the following you create a container of shape.

【0075】・形状:図1に示す長方形の底面と、それに接する台形状の4つの側面をもち、直方体に近い形の容積を有し、上面が無く(開放)、底面よりも開方面の方がやや広い面積を有するパッド状の形状。 [0075] Shape: the bottom surface of the rectangle shown in Figure 1, has four side surfaces of the contact therewith trapezoidal, has the form of a volume close to a rectangular parallelepiped, the top surface without (open) towards the opening direction than the bottom surface pad shape but having a slightly larger area. ・底面の厚みt1=3.0mm、側面の厚みt2=3. - the bottom surface of the thickness t1 = 3.0 mm, the thickness of the side t2 = 3.
0mm。 0mm. ・底面と側面の成す辺の容器外側の曲率半径RO=10 - bottom and curvature of the container outer sides formed by the side surface radius RO = 10
mm、同容器内側の曲率半径RI=7.0mm、開放部の辺(上辺)が曲率半径RE=10mmで容器外側に緩やかなカーブを描いて下向きに15mm折り返され、端面が下向きとなっている縁取りのある形状で、端面のエッジ部の面取りがされており、その曲率半径r=0.2 mm, the container inner radius of curvature RI = 7.0 mm, the opening portion of the side (upper side) is folded 15mm downward drawing a gentle curve to the container outer radius of curvature RE = 10 mm, the end face is in the downward shape with a border, are chamfered edge portion of the end surface, the radius of curvature r = 0.2
mm ・底面部の面積(容器外側)180×230mm ・上面(開口部)の面積188×238mm ・高さ150mm ・容積5.5リットル Area of ​​mm · bottom portion (container outside) 180 × 230 mm · top area 188 × 238 mm · Height 150 mm · volume 5.5 l of (opening)

【0076】試験法1から5までの各試験結果はいずれも良好であった。 [0076] Each test results from Test Method 1 to 5 were good.

【0077】(実施例2)参考例2のペレットを用いた以外は実施例1と同様にして動物容器を得た。 [0077] (Example 2) except for using Reference Example 2 Pellets were obtained Animals container in the same manner as in Example 1. 試験法1 Test Method 1
から5までの各試験結果はいずれも良好であった。 Each test result to 5 were good.

【0078】(比較例1)成形材料として、ポリカーボネート樹脂(帝人化成株式会社製、商標名パンライトL [0078] (Comparative Example 1) molding material, polycarbonate resin (Teijin Chemicals Ltd., trade name Panlite L
−1225)を用いた他以外は実施例1と同様にして動物容器を得た。 Other non with -1225) got animal container in the same manner as in Example 1.

【0079】試験法1と2の試験結果は良好であったが、試験法3,4と5の試験結果は良好でなかった。 [0079] Test Results Test Method 1 and 2 was good, but the test results of Test Method 3, 4 and 5 were not good. 動物容器は、排泄物易洗浄性試験の結果、微かに跡が残り、良好でなく、耐薬品性及び長期の排泄物耐性試験後の結果は、サイクルを重ねるにしたがって、シミや着色、が顕著となり、7サイクル目で中のマウスの活動状況が分かりにくくなってきたので、耐薬品性及び長期の排泄物耐性試験の結果は劣るものであった。 Animals container, excrement easily washed test results, slight remaining traces, not good, results after excrement resistance test of chemical resistance and long-term, in accordance with overlapping cycles, stains and coloring is remarkably next, the activities of mouse middle in the seventh cycle has become obscure, the result of excrement resistance testing of chemical resistance and long term was inferior. 残留応力と耐溶剤性試験では、用いた3種の溶剤のいずれでもソルベントクラックが発生し、耐薬品性は劣るものであった。 The residual stress and solvent resistance test, either solvent cracking of the three solvents used occurred were those chemical resistance inferior.

【0080】(実施例3)t1=t2=3.0mm、R [0080] (Example 3) t1 = t2 = 3.0mm, R
0=5.0mm、RI=2.0mmとした以外は実施例1と同様にして、動物容器を得た。 0 = 5.0 mm, except that the RI = 2.0 mm in the same manner as in Example 1 to obtain an animal container. 試験法1から5までの各試験結果はいずれも良好であった。 Each test results from Test Method 1 to 5 were good.

【0081】 [0081]

【発明の効果】本発明により、ノルボルネン系開環重合体等からなる成形材料を成形してなる動物容器が供給される。 According to the present invention, the animal container obtained by molding the molding material made of a norbornene-based ring-opening polymer or the like is supplied. 該動物容器は従来の動物容器に比べて、透明で、 Animal container compared to conventional animal containers, transparent,
耐熱性、耐薬品性等に優れ、更に動物の排泄物が容易に洗浄できるという特徴を持つ。 Excellent heat resistance and chemical resistance, etc., further has a feature that animal waste can be easily cleaned. 本発明により供給される動物容器により、ネズミや小型うさぎ等の哺乳類、ヘビ、蛙、亀、トカゲ等の両生類などをペット用として飼育したり、マウスやラット、モルモットなどの実験用小動物を医薬品の開発、安全性試験を行なうために飼育することが可能であり、該容器はペット用として一般に使用できるほか、医薬等の開発のための実験ひいては産業の発達に極めて有用である。 Animal container supplied by the present invention, such as rats and small rabbits mammals, snakes, frogs, turtles, or breeding, such as amphibians, lizards or the like as a pet, mice and rats, the experimental small animals such as guinea pigs of pharmaceuticals development, it is possible to breed in order to perform the safety test, the container well, which can be used commonly as a pet, is very useful for experiments thus the development of industry for the development of pharmaceutical and the like.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】実施例1で作成した動物容器の斜視図 1 is a perspective view of an animal vessel prepared in Example 1

【図2】実施例1で作成した動物容器の長手方向の断面図 Longitudinal cross-sectional view of the animal container created in Figure 2 EXAMPLE 1

【符号の説明】 DESCRIPTION OF SYMBOLS

1:底面 2:側面 3:辺のうち曲率半径ROを有する部分 4:辺のうち曲率半径RIを有する部分 5:端面 6:二重構造の縁取り部分 7:リブ 1: a bottom 2: Side 3: portion having a radius of curvature RO of the sides 4: portion having a radius of curvature RI of the sides 5: end face 6: double-structured border portions 7: ribs

Claims (3)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 2環体若しくは3環体のノルボルネン類を50重量%以上含むノルボルネン系単量体の開環重合体またはその水素添加物からなる成形材料を成形してなる動物容器。 1. A 2 annulus or 3 rings of norbornenes animals container obtained by molding the molding material made of a ring-opening polymer or a hydrogenated product of norbornene monomer containing 50 wt% or more.
  2. 【請求項2】 容器底面の外側表面と容器側面の外側表面との交わる部分が2.0mm以上の曲率半径を有する曲面から形成されている請求項1記載の動物容器。 Wherein the outer surface and the vessel side animals container according to claim 1, wherein are formed from a curved surface which intersects the portion of the outer surface having the above curvature radius 2.0mm of the container bottom.
  3. 【請求項3】 動物飼育容器である請求項1または2のいずれかに記載の動物容器。 3. Animals container according to claim 1 or 2 which is an animal rearing container.
JP18735597A 1997-06-27 1997-06-27 Animal container Expired - Fee Related JP3807461B2 (en)