JPH11335616A - Non-baked color pencil lead - Google Patents

Non-baked color pencil lead

Info

Publication number
JPH11335616A
JPH11335616A JP16424898A JP16424898A JPH11335616A JP H11335616 A JPH11335616 A JP H11335616A JP 16424898 A JP16424898 A JP 16424898A JP 16424898 A JP16424898 A JP 16424898A JP H11335616 A JPH11335616 A JP H11335616A
Authority
JP
Japan
Prior art keywords
synthetic mica
non
raw material
wt
lubricant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP16424898A
Other languages
Japanese (ja)
Other versions
JP3928904B2 (en
Inventor
Yuka Tsuemura
由佳 杖村
Original Assignee
Sakura Color Prod Corp
株式会社サクラクレパス
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sakura Color Prod Corp, 株式会社サクラクレパス filed Critical Sakura Color Prod Corp
Priority to JP16424898A priority Critical patent/JP3928904B2/en
Priority claimed from EP19990921271 external-priority patent/EP1000987B1/en
Publication of JPH11335616A publication Critical patent/JPH11335616A/en
Application granted granted Critical
Publication of JP3928904B2 publication Critical patent/JP3928904B2/en
Anticipated expiration legal-status Critical
Application status is Expired - Fee Related legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To obtain a non-baked color pencil lead having excellent mechanical strengths and exhibiting good writing feeling and coloring power by including a binder, a colorant, an extender and a lubricant comprising a synthetic mica.
SOLUTION: This color pencil lead contains (A) a binder, (B) a coloring material, (C) an extender material and (D) a lubricant containing a synthetic mica as raw material composition and optionally oil, and fat and/or a wax. The synthetic mica of the component D is preferably a swelling mica free from swelling property with oil and fat and/or wax. The compounding amount of the synthetic mica is preferably 1-15 wt.% based on the total raw material composition (solid basis). The amounts of the components A, B and C are preferably 3-15 wt.%, 5-25 wt.% and 60-80 wt.% based on the total raw material composition (solid basis), respectively. The codor pencil lead produced by this process has excellent mechanical, strengths and is resistant to the breakage of lead compared with a lead produced by using baron nitride as the lubricant.
COPYRIGHT: (C)1999,JPO

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は非焼成色鉛筆芯において、特にその機械的強度を改善して芯折れを防止すると共に、コストパフォーマンスを改善した非焼成色鉛筆芯に関するものである。 The present invention relates in a non-baked color pencil lead, particularly as to prevent breakage core to improve its mechanical strength, it relates to non-baked color pencil lead having improved cost performance.

【0002】 [0002]

【従来の技術】従来の非焼成色鉛筆芯は、結合材、着色材、体質材、滑材及び溶剤などの原料組成物を配合し混練したものを押出成形し、必要に応じて乾燥などを施して製造されている。 Conventional non-baked color pencil lead, the binder, colorant, extender material, extruding a material obtained by kneading blended raw material composition, such as lubricant and solvent, dried and subjected if necessary It is manufactured Te.

【0003】ここで、滑材としては、一般に各種の材料が用いられているが、中でも窒化硼素は、その結晶構造が黒鉛と類似して潤滑性に優れており、また白色であることから色鉛筆芯の色調を損なわないという利点があるため広く使用されている。 [0003] As the lubricant, generally in a variety of materials are used, color pencil since inter alia boron nitride are excellent in lubricating properties similar crystal structure graphite, also a white widely used because of the advantage of not impairing the color tone of the core.

【0004】 [0004]

【発明が解決しようとする課題】しかし、かかる窒化硼素を含有した非焼成色鉛筆芯は、機械的強度の点で必ずしも充分でなく、筆記時に芯折れしたり、落下した衝撃によって芯の途中で芯折れする場合がある。 [SUMMARY OF THE INVENTION However, non-calcined color pencil leads containing such boron nitride is not necessarily sufficient in terms of mechanical strength, or broken core during writing, the core in the middle of the core by falling impact there is a case to be broken. また、窒化硼素は原料コストが高く、元来比較的廉価に提供する必要性の高い色鉛筆芯においてそのコストパフォーマンスが未だ充分でないという欠点がある。 Further, boron nitride has a high raw material cost, there is a disadvantage that its cost at high pencil leads of the need to provide inherently relatively low cost is not yet sufficient. 従って、当業者間にあっては、窒化硼素の代替材料としての開発が広くが求められている。 Therefore, in those skilled in time, widely developed as an alternative material for the boron nitride is required.

【0005】本発明の課題は、窒化硼素と比較して、機械的強度に優れ、芯折れを起こし難く、しかも書き味及び着色性も良好であり、更にコストパフォーマンスに優れた非焼成色鉛筆芯を提供する点にある。 An object of the present invention, compared to boron nitride, excellent in mechanical strength, hardly cause core broken, yet a better taste and coloring properties write, non-baked color pencil leads further excellent cost performance some in that it provides.

【0006】 [0006]

【課題を解決するための手段】本発明者は上記課題を達成するため鋭意検討した結果、結合材、着色材、体質材及び滑材を原料組成物として含み、必要に応じて油脂及び/又はワックス類を含み、上記滑材として合成雲母を含有してなる非焼成色鉛筆芯を開発した。 The present inventors SUMMARY OF THE INVENTION As a result of intensive investigations to achieve the above object, binder, colorant comprises an extender material and lubricant as a feed composition, fat and / or optionally include waxes, developed a non-calcined pencil leads comprising a synthetic mica as the lubricant.

【0007】本発明の非焼成色鉛筆芯は、滑材として合成雲母を含有しているため、窒化硼素と比較して、優れた機械的強度を非焼成色鉛筆芯に与えることができ、芯折れを起こし難い。 [0007] Non-baked color pencil leads of the present invention, which contains the synthetic mica as a lubricant, as compared to boron nitride, excellent mechanical strength can be given to the non-baked color pencil lead, lead bending the hardly cause. また合成雲母は窒化硼素と比較して原料コストが廉価であるため、コストパフォーマンスに優れている。 The synthetic mica because raw material cost is inexpensive compared to boron nitride, is excellent in cost performance. また、書き味や着色性も良好であり、窒化硼素の場合と比較して同等のレベルの書き味や着色性を保有することができる。 Also, a better writing feeling and coloring property, it is possible to hold the writing feeling and coloring properties comparable level compared to that of boron nitride.

【0008】本発明に使用する合成雲母は、劈開性に優れており、これを非焼成色鉛筆芯の滑材として使用した場合、芯に適度な硬さを与えながら、筆記時においては芯の先端部が筆記面との摩擦により劈開し、書き味を向上させることができる。 [0008] synthetic mica used in the present invention is excellent in cleavage, using this as a lubricating material of a non-baked color pencil lead, while giving moderate hardness to the core, the core at the time of writing tip parts are cleaved by friction with the writing surface, thereby improving the writing performance.

【0009】上記合成雲母としては、いわゆる天然雲母に対して人工的に生成されたフッ素雲母系鉱物を意味し、その構造はたとえば天然雲母の結晶中の結晶水をフッ素で置き換えたものとしてとらえられる層状化合物であり、その層間で剥離しやすい劈開性を有する。 [0009] As the synthetic mica is viewed as means fluorine-based mineral that is artificially generated, the structure is replaced by fluorine water of crystallization, for example of natural mica crystal to a so-called natural mica a layered compound, having easy cleavage peeling between the layers. 具体的には、フッ素金雲母、カリ四ケイ素雲母等の非膨潤性雲母や、Naテトラシリシックマイカ、Na又はLiデニオライト、Na又はLiヘクトライト等の膨潤性雲母を例示することができる。 Specifically, there can be mentioned fluorine phlogopite, and swellable mica such as potassium tetrasilic mica, Na tetrasilicic mica, Na or Li Denioraito, swelling mica such as Na or Li hectorite.

【0010】ここで、上記膨潤性雲母とは、水と共存すると層間域に水分子を取り込んで膨潤していくものをいい、これに対して非膨潤性雲母とは、水によって膨潤しない合成雲母をいう。 [0010] Here, the above-mentioned swellable mica, when coexisting with water referred to herein is gradually swollen captures water molecules in the interlayer region, whereas the non-swellable mica, synthetic mica that does not swell with water the say.

【0011】 [0011]

【発明の実施の形態】本発明は、結合材、着色材、体質材及び滑材を原料組成物として含み、必要に応じて油脂及び/又はワックス類を含み、上記滑材として合成雲母を含有してなる非焼成色鉛筆芯である。 DETAILED DESCRIPTION OF THE INVENTION The present invention is, binder, colorant comprises an extender material and lubricant as a raw material composition comprises a fat and / or wax optionally containing synthetic mica as the lubricant is a non-calcined pencil leads obtained by.

【0012】本発明で用いる合成雲母は、既述の通り、 [0012] The synthetic mica used in the present invention, as described above,
膨潤性雲母及び非膨潤性雲母のいずれも可能である。 It can be either of the swellable mica and non-swellable mica. しかし、膨潤性雲母の方が、書き味の向上、及び着色性の向上に優れているため本発明の滑材としては適している。 However, towards the swellable mica, it is suitable as a lubricating material for writing feeling improved, and the present invention because it is excellent in improvement of coloring property.

【0013】但し、膨潤性合成雲母であっても、ワックス類又は油脂で膨潤する性質のものは、芯自体に含まれるワックスや油脂により膨潤し、芯の強度が得られにくくなることから本発明の色鉛筆芯には適さない。 [0013] However, even in the swelling synthetic mica, those of property of swelling with waxes or fats, swollen with wax or fat contained in the core itself, the present invention since the strength of the core is difficult to obtain not suitable for the color pencil leads.

【0014】合成雲母の具体例としては、例えば、トビー工業社製の商品名「DMA−350」等がある。 [0014] Examples of synthetic mica, for example, there is a Toby Industry Co., Ltd. under the trade name "DMA-350", and the like. この合成雲母は、人工的に製造することができるため、原料コストに優れており、また性状や品質等が安定している点で好ましい。 The synthetic mica, it is possible to artificially manufactured, has excellent raw material costs, also properties and quality, etc. are preferable in that stable.

【0015】本発明の滑材には、上記合成雲母のうち任意のものを単独で、又はその他滑材として使用できるもの、たとえばフッ化黒鉛、窒化硼素と混合して用いることもできる。 [0015] skids of the present invention are those which can be used alone, or any other lubricating material to any of the above synthetic mica, for example fluorinated graphite, may be mixed with boron nitride. 合成雲母を従来の窒化硼素に替えて又は窒化硼素と共に滑材として配合した場合、窒化硼素単独で配合した場合と比較して、非焼成色鉛筆芯の機械的強度が向上し、芯折れを防止することができる。 When the synthetic mica is blended as a lubricant or as with boron nitride instead of the conventional boron nitride, as compared to when blended with boron nitride alone, it improves the mechanical strength of the non-baked color pencil lead is prevented from core breakage be able to.

【0016】この合成雲母の配合量は特に限定されない。 [0016] The amount of the synthetic mica is not particularly limited. しかし合成雲母を原料組成物(固形分)全量に対して1〜15重量%を配合することが好ましい。 However the synthetic mica raw material composition (solid content) preferably be blended 1-15 wt% of the total amount. 合成雲母の配合量が原料組成物(固形分)全量に対して1重量% Amount of synthetic mica raw material composition (solid content) 1% by weight relative to the total amount
未満の場合は、実用上支障はないものの着色性及び書き味は共にやや低下する。 When it is less than, practical problem is not although coloring and writing performance are both slightly decreased. 一方、合成雲母の配合量を原料組成物(固形分)全量に対して15重量%を越えて配合した場合も、実用上支障はないものの着色性及び書き味は共にやや低下する。 On the other hand, even if the amount of the synthetic mica was blended more than 15 wt% relative to the raw material composition (solid content) based on the total amount of practical problem of the coloring property and writing performance but not both slightly decreased.

【0017】なお、窒化硼素と混合して使用した場合は、窒化硼素の使用量が低減できる点で、非焼成色鉛筆芯の機械的強度やコストパフォーマンスを改善することができる。 [0017] Note that when used in admixture with boron nitride, in that it can reduce the use amount of boron nitride, it is possible to improve the mechanical strength and cost performance of the non-baked color pencil lead.

【0018】合成雲母に混合する窒化硼素としては、昭和電工社製の商品名「UHP−S1」等を例示することができるが、必ずしもこれに限定されない。 Examples of the boron nitride to be mixed with the synthetic mica, can be exemplified by Showa Denko Co., Ltd. under the trade name "UHP-S1" or the like may not be limited thereto.

【0019】また、本発明で使用される結合材としては、従来使用されているものの中から適宜選択して使用することができる。 [0019] As the binder used in the present invention can be appropriately selected and used from among those conventionally used. 例えば、カルボキシメチルセルロースナトリウム(CMCナトリウム)、カルボキシメチルセルロースアンモニウム(CMCアンモウニウム)、カルボキシメチルセルロース酸(CMC酸)、メチルセルロース、ニトロセルロース、硫酸セルロース、アセチルセルロース、フェノール樹脂、ポリビニルアルコール、 For example, sodium carboxymethylcellulose (CMC sodium), carboxymethylcellulose ammonium (CMC Anmouniumu), carboxymethylcellulose acid (CMC acid), methylcellulose, nitrocellulose, cellulose sulfate, cellulose acetate, phenol resin, polyvinyl alcohol,
アラビアガム等が挙げられる。 Gum arabic, and the like. これらは単独または組み合わせて使用することができる。 These may be used alone or in combination. その配合量は、原料組成物(固形分)全量に対して3〜15重量%、好ましくは5〜10重量%である。 The amount thereof, the raw material composition (solid content) of 3 to 15% by weight based on the total amount, preferably from 5 to 10 wt%. 結合材が原料組成物(固形分)全量の15重量%より過剰である場合には書き味が低下し、また原料組成物(固形分)全量の3重量%より過小に配合された場合には機械的強度が低下すると共に芯状への成型性が低下する。 If binder material composition reduces the writing feeling when in excess than 15% by weight of the (solid) the total amount, and the raw material composition (solid content) was under-formulated than 3 wt% of the total volume moldability to wick decreases the mechanical strength is lowered.

【0020】着色材は、通常使用されている無機顔料、 [0020] The colorant, inorganic pigments which are usually used,
有機顔料のいずれも単独で又は組み合わせて使用することができる。 Any of organic pigments, alone or in combination may be used. また、パール顔料、蛍光顔料、金属粉等も使用できる。 Further, pearl pigments, fluorescent pigments, also metal powders and the like can be used. その配合量は、原料組成物(固形分)全量に対して5〜25重量%、好ましくは15〜20重量% The amount thereof, the raw material composition (solids) 5-25% by weight based on the total amount, preferably 15 to 20 wt%
である。 It is. 上記配合量が原料組成物(固形分)全量の25 25 The above amount is the raw material composition (solid content) of the total amount
重量%より過剰であると書き味が低下し、5重量%より過小であると発色性が必ずしも十分でない。 It reduces the writing feeling as the excess over wt%, is not necessarily sufficient coloring property to be too small than 5 wt%.

【0021】体質材としては、タルク、炭酸マグネシウム、炭酸カルシウム、シリカ、アルミナシリケート、カオリン、ベントナイト等を例示することができる。 [0021] Examples of the extender material can be exemplified talc, magnesium carbonate, calcium carbonate, silica, alumina silicate, kaolin, bentonite and the like. そしてこれらの中から適宜選択して単独で又は組み合わせて使用できる。 And it can be used alone or in combination with appropriately selected from these. その配合量は、原料組成物(固形分)全量の60〜80重量%、好ましくは65〜75重量%である。 The amount thereof, the raw material composition (solid content) of 60 to 80 wt% of the total amount, preferably from 65 to 75 wt%. 体質材の配合量が原料組成物(固形分)全量の80 80 the amount of extender material is a raw material composition (solid content) of the total amount
重量%より過剰であると芯状への成型性が低下し、60 It reduces the moldability of the wick to be in excess of the weight percent, 60
重量%より過小であると書き味が低下する。 Writing feel is reduced to be too small than the weight%.

【0022】また、本発明の非焼成色鉛筆芯には、必要に応じて成形後、油脂、ワックス類を含浸させることができる。 Further, the non-calcined pencil leads of the present invention may be impregnated after molding as needed, fats, waxes. また、この油脂、ワックス類は、成形後に含浸させるのではなく、原料組成物としてあらかじめ練り込むこともできる。 Further, the fats, waxes, rather than impregnated after molding, it is also a way to push previously kneading a raw material composition. この油脂、ワックス類は、非焼成色鉛筆芯の着色性を向上させることができる。 The fats, waxes, it is possible to improve the coloring properties of the non-baked color pencil lead.

【0023】油脂、ワックス類としては、具体的には、 [0023] fats and oils, as waxes, specifically,
流動パラフィン、シリコーンオイル、α−オレフィンオリゴマー、パラフィンワックス、マイクロクリスタリンワックス、ケトンワックス、ワセリン、蜜ロウ、牛脂硬化油、木ロウ、カルナウバワックス、ステアリン酸等を例示することができる。 Liquid paraffin, silicone oil, alpha-olefin oligomer, paraffin wax, microcrystalline wax, ketone wax, vaseline, beeswax, beef tallow hardened oil, Japan wax, carnauba wax, may be exemplified stearic acid. 油脂、ワックス類は合成、天然を問わずこれらを単独で又は組み合わせて使用することができる。 Fats, waxes can be used synthetic, natural and whether not these alone or in combination.

【0024】本発明の非焼成色鉛筆芯は、たとえば次の製造方法により得ることができる。 The non-calcined pencil leads of the present invention can be for example obtained by the following manufacturing method. まず、滑材として合成雲母を含む上記原料組成物に、この原料組成物と約同量の溶剤(水、有機溶剤等からなる)を添加して混練する。 First, the raw material composition containing a synthetic mica as a lubricant, are kneaded with the addition of a solvent of the starting composition and about the same amount (water, consisting of an organic solvent, etc.). ここで溶剤は上記原料組成物の混練と成形を容易にするために加えられる。 Here the solvent is added to facilitate the molding and kneading of the raw material composition. 次に、上記混練された原料組成物をプランジャー型又はスクリュー型押出成形機によって直径約3mmの色鉛筆芯に成形する。 Next, molded into color pencil leads having a diameter of about 3mm said kneaded raw material composition by a plunger or screw-type extruder. 次に、この成型物を乾燥してこの成型物から溶剤を除去した後、更にこの成型物に油脂、ワックス類を含浸させることによって非焼成色鉛筆芯を得る。 Next, this molded product was dried after removal of the solvent from the molded product to obtain the non-calcined pencil leads by further impregnating oils and waxes in this molding material.

【0025】このようにして製造された色鉛筆芯は、合成雲母が滑材として配合されているため、窒化硼素の場合と比較して、機械的強度に優れ、芯折れを起こし難い。 The pencil leads produced in this way, since the synthetic mica is blended as a lubricant, as compared with the case of boron nitride, excellent in mechanical strength, hardly cause core breakage. また滑材として安価な原料であり、コストパフォーマンスに優れている。 In addition is a low-cost raw materials as a lubricant, is excellent in cost performance. また、潤滑性も高く、その劈開性によって筆記時に色鉛筆芯がなめらかに摩耗し良好な書き味を得ることができる。 Also, lubricity is high, pencil leads during writing by the cleavage is smoothly worn it is possible to obtain an excellent writing feeling. また合成雲母は白色であるため、色鉛筆芯の色に影響を与えることなく着色性も良好である。 The synthetic mica for a white coloration resistance are excellent without affecting the color of the color pencil leads.

【0026】従って、従来の窒化硼素を滑材として使用していた場合と同等以上の品質を確保することができ、 [0026] Accordingly, it is possible to ensure the same or higher quality as we have used the conventional boron nitride as a lubricant,
しかも材料コストの低減を図ることができる。 Moreover it is possible to reduce the material cost.

【0027】 [0027]

【実施例】以下、本発明のさらに具体的な実施例について説明する。 BRIEF DESCRIPTION For a more specific example of the present invention. 但し、本発明はこの実施例に限定されるものではない。 However, the present invention is not limited to this embodiment.

【0028】表1に示す配合により実施例及び比較例の非焼成色鉛筆芯を製造した。 [0028] was prepared non-baked color pencil leads of Examples and Comparative Examples by the formulation shown in Table 1. すなわち、表1に示す配合原料を水と有機溶剤とともに混練し、その後、プランジャー型押し出し成形機で3mmφの芯に成形した後、溶剤を乾燥、除去し、70℃で12時間加熱後、流動パラフィンを含浸させて製造した。 That is, the compounding ingredients shown in Table 1 were kneaded together with water and an organic solvent, then, after forming the core of 3mmφ in plunger-type extruder, the solvent is dried, removed, after heating at 70 ° C. 12 h, flow It was prepared impregnated with paraffin.

【0029】表1中、実施例1〜5及び比較例5及び比較例6は合成雲母を滑材として使用した場合、比較例1 [0029] In Table 1, when Examples 1 to 5 and Comparative Examples 5 and 6 using synthetic mica as a lubricant, Comparative Example 1
〜3は窒化硼素を滑材として使用した場合、比較例4は滑材として合成雲母及び窒化硼素をいずれも配合しない場合である。 To 3 when using boron nitride as a lubricant, Comparative Example 4 is a case where not added any synthetic mica and boron nitride as lubricant.

【0030】 [0030]

【表1】 [Table 1]

【0031】表1中、CMCナトリウムはダイセル化学工業社製、商品名「CMC1130」、タルクは日本タルク社製、商品名「MICROACE P−4」、窒化硼素は昭和電工社製、商品名「UHP−S1」、合成雲母はトピー工業社製、商品名「DMA−350」を使用し、着色材としては、赤色の着色材はウオッチングレッドSr(C.I.PR 48:3)、青色の着色材はフタロシアニンブルー(C.I.PB 15)、黄色の着色材はハンザエロー10G(C.I.PY 3)を使用した。 [0031] In Table 1, CMC sodium is manufactured by Daicel Chemical Industries, Ltd., trade name "CMC1130", talc Nippon Talc Co., Ltd., trade name "MICROACE P-4", boron nitride is manufactured by Showa Denko KK, trade name "UHP -S1 ", synthetic mica Topy Industries, Ltd., using the trade name" DMA-350 ", as the coloring material, red colorant watching red Sr (C.I.PR 48: 3), blue colorants phthalocyanine blue (C.I.PB 15), the yellow colorant was used Hansa 10G (C.I.PY 3).

【0032】(機械的強度試験)次に、上記の製造によって得られた実施例及び比較例の各非焼成色鉛筆芯について、芯折れを評価するため曲げ強度を測定した。 [0032] (Mechanical Strength Test) Next, for each non-calcined pencil leads of Examples and Comparative Examples obtained by the above production was measured flexural strength to evaluate the core breakage. 曲げ強度は JIS S 6005に準拠して測定した。 Flexural strength was measured according to JIS S 6005. すなわち、 That is,
両支点間に支持した色鉛筆芯の中央部に荷重を加えて、 Applying a load to the central portion of the color pencil leads which is supported between both supports,
芯が折損したときの荷重を測定し、JIS 試験法に定められた計算式に代入して行った。 The load when the core is broken and measurements were performed by substituting the formula defined in JIS test method. 評価は算出された曲げ強さの値(MPa)で行った。 Evaluation was performed at the calculated flexural strength values ​​(MPa). 数値が大きい程曲げ強度が大きく芯折れし難いことを示している。 Figures higher bending strength indicates that hardly break large core large.

【0033】(書き味評価)上記各実施例及び比較例の非焼成色鉛筆芯について書き味の評価の試験を行った。 [0033] (writing feeling Evaluation) were tested for evaluation of writing feeling for the non-calcined pencil leads of Examples and Comparative Examples.
評価方法は、各実施例及び比較例の非焼成色鉛筆芯を用いた色鉛筆を製造し、10名のモニターを用いて、各実施例、比較例の番号を隠した色鉛筆を使って画用紙に筆記し、その書き味のフィーリングを評価した。 Evaluation method, to produce a colored pencil using a non-calcined pencil leads of Examples and Comparative Examples, by using a monitor of ten, each example, handwritten drawing paper with colored pencils hid number of comparative examples , to evaluate its writing feeling of feeling. 結果は1 Results 1
0名中8名以上が書き味がよいと判断したものを○、7 What 0 people 8 or more people in the writing feeling was determined that good ○, 7
名から5名の者が書き味がよいと判断したものが△、4 What a person of five has determined that good writing feeling from the name is △, 4
名以下のものを×として前記表1に示した。 Shown in Table 1 what name below as ×.

【0034】(着色性評価)上記各実施例及び比較例の非焼結色鉛筆芯について着色性の評価を行った。 [0034] were evaluated coloring for (coloring Evaluation) The non-sintered color pencil leads of Examples and Comparative Examples. 評価方法は、各実施例及び比較例の非焼成色鉛筆芯を用いた色鉛筆を製造し、10名のモニターを用いて、各実施例、 Evaluation method, to produce a colored pencil using a non-calcined pencil leads of Examples and Comparative Examples, by using a monitor of ten, each example,
比較例の番号を隠した色鉛筆を使って画用紙に筆記し、 Was written on construction paper using colored pencils to hide the number of the comparative example,
その着色性の良さを評価した。 To evaluate its coloring of the good. その結果、10名中8名以上が着色がよいと判断したものを○、7名から5名の者が書き味がよいと判断したものが△、よいと判断したものが4名以下のものを×とし、前記表1に示した。 As a result, those ten 8 or more people in determines that good coloring ○, those 7 persons 5 persons from persons is determined that good writing feeling is △, those ones of the following four it is determined that good It was a ×, shown in table 1.

【0035】上記各試験結果により、合成雲母を使用した実施例1乃至5及び比較例5及び比較例6の各非焼成色鉛筆芯は、いずれも窒化硼素を使用した色鉛筆芯と比較して曲げ強度が向上し、芯折れを起こし難くいことが判明した。 [0035] The above test results, the non-calcined pencil leads of Examples 1 to 5 and Comparative Examples 5 and 6 using synthetic mica are all bent in comparison with pencil leads using boron nitride strength but improved, it has been found that have hardly caused a core break.

【0036】また、合成雲母を使用した実施例1〜5の各非焼成色鉛筆芯は、いずれも窒化硼素を使用した比較例1〜3の各非焼成色鉛筆芯と同等の良好な書き味及び着色性が認められた。 Further, the non-calcined pencil leads of Examples 1 to 5 using synthetic mica are both equivalent good writing performance and the non-baked color pencil lead of Comparative Examples 1 to 3 using boron nitride and coloring gender was observed.

【0037】また、合成雲母の配合量が表1に示す原料組成物(固形分)全量に対して1重量%より過小である比較例5の場合、及び同原料組成物(固形分)全量に対して15%を越える比較例6の場合には、いずれも、合成雲母を含有しない比較例4のものと比較すれば書き味及び着色性がともに良好であったが、窒化硼素含有の比較例1〜3の各非焼成色鉛筆芯と比較すれば、実用上は使用可能であるが、書き味及び着色性の低下がみられた。 Further, if the amount of the synthetic mica of Comparative Example 5 is too small than 1% by weight with respect to the raw material composition (solid content) the total amount shown in Table 1, and the raw material composition (solid content) in the total amount in Comparative example 6 exceeding 15% for the both, the writing feeling when compared and coloring property as that of Comparative example 4 containing no synthetic mica were good, comparative examples containing boron nitride in comparison with the non-baked color pencil lead of 1-3, but practically usable, decrease in taste and coloring write it was observed.

【0038】従って、機械的強度の向上と共に、従来の窒化硼素含有の非焼成色鉛筆芯と同等の書き味及び着色性を備えた非焼成色鉛筆芯を得るには、合成雲母の配合量は原料組成物(固形分)全量に対して1〜15重量% [0038] Therefore, the improvement of the mechanical strength, in order to obtain the non-calcined pencil leads having non-baked color pencil leads equivalent writing feel and coloring of the conventional boron nitride content, the amount of synthetic mica raw material composition objects (solids) 1-15 wt% of the total amount
配合することが好適であることを見いだした。 Blending was found to be suitable.

【0039】なお、合成雲母及び窒化硼素のいずれも使用しなかった比較例4の非焼成色鉛筆は、書き味及び着色性ともに実用上満足できるものではなかった。 [0039] The non-baked color pencil in Comparative Example 4 in which none of the synthetic mica and boron nitride was not used, was not practically satisfactory in both flavor and coloring write.

【0040】 [0040]

【発明の効果】本発明は、結合材、着色材、体質材及び滑材を原料組成物として含み、必要に応じて油脂及び/ The present invention exhibits, binder, colorant comprises an extender material and lubricant as a raw material composition, optionally fat and /
又はワックス類を含み、上記滑材として合成雲母を含有してなる非焼成色鉛筆芯であるので、窒化硼素を滑材として使用した従来の非焼成色鉛筆芯と比較して、機械的強度が改善され、芯折れを起こし難く、また窒化硼素と同等の良好な書き味と着色性をもつ非焼結色鉛筆芯とすることができる。 Or comprises a wax, since it is non-baked color pencil lead comprising a synthetic mica as the lubricant, as compared with conventional non-baked color pencil lead using boron nitride as a lubricant, the mechanical strength is improved hardly cause core breakage, and may be a non-sintered color pencil leads having coloring properties and the writing feeling good comparable to boron nitride. しかも、合成雲母は窒化硼素と比較して原料コストが安価であることから、比較的廉価に提供する必要性の高い非焼成色鉛筆芯においてそのコストパフォーマンスは良好である。 Moreover, synthetic mica from that raw material costs as compared to boron nitride is inexpensive, the cost performance is good at relatively low cost highly necessary to provide a non-baked color pencil leads.

Claims (2)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 結合材、着色材、体質材及び滑材を原料組成物として含み、必要に応じて油脂及び/又はワックス類を含み、上記滑材として合成雲母を含有してなる非焼成色鉛筆芯。 1. A binder comprising a colorant, an extender material and lubricant as a raw material composition, optionally comprises a fat and / or wax, non-baked color pencil comprising a synthetic mica as the lubricant core.
  2. 【請求項2】 合成雲母が、原料組成物(固形分)全量に対して1〜15重量%配合されている請求項1記載の非焼成色鉛筆芯。 2. A synthetic mica is, the raw material composition (solids) Non-baked color pencil lead according to claim 1, wherein is 1-15 wt% blend of the total amount.
JP16424898A 1998-05-27 1998-05-27 Non-firing colored pencil lead Expired - Fee Related JP3928904B2 (en)