JPH11262626A - Deodorant and deodorization sheet - Google Patents

Deodorant and deodorization sheet

Info

Publication number
JPH11262626A
JPH11262626A JP6890598A JP6890598A JPH11262626A JP H11262626 A JPH11262626 A JP H11262626A JP 6890598 A JP6890598 A JP 6890598A JP 6890598 A JP6890598 A JP 6890598A JP H11262626 A JPH11262626 A JP H11262626A
Authority
JP
Grant status
Application
Patent type
Prior art keywords
semiconductor
sheet
materials
photoreactive
deodorant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP6890598A
Other languages
Japanese (ja)
Inventor
Yoichiro Azuma
Junji Harada
Katsumitsu Suzaki
純二 原田
洋一郎 東
活光 須崎
Original Assignee
Mitsubishi Paper Mills Ltd
三菱製紙株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

PROBLEM TO BE SOLVED: To decompose and remove harmful materials such as malodorous materials and bacteria, to neutralize and remove various aldehydes and acids formed by the decomposition of the harmful materials and to prevent the deactivation of an adsorbent by the acids by preparing a deodorant from at least a photoreactive semiconductor and an amine-contg. sheet phosphate.
SOLUTION: The deodorant that can adsorb and remove aldehydes, etc., formed by the decomposition of harmful materials by the photocatalytic action of a photoreactive semiconductor is prepd. from the photoreactive semiconductor and an amine-contg. sheet phosphate. The deodorant is incorporated into a substrate such as a nonwoven fabric or applied to a substrate to form the objective deodorization sheet. The photoreactive semiconductor is preferably a semiconductor having 1-3 eV forbidden band width and causing a photocatalytic reaction and particles of the semiconductor having 10-500 m2/g specific surface area are appropriately used. The amine in the amine-contg. sheet phosphate is, e.g. vinylbenzyldimethylamine as a compd. having a tert. amino group.
COPYRIGHT: (C)1999,JPO

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、脱臭剤およびそれを用いた脱臭シートに関し、さらに詳しくは、光反応性半導体の光触媒作用により、効率よく各種のアルデヒドをアミン含有層状リン酸塩で吸着することによって分解除去することを特徴とする脱臭剤およびそれを用いた脱臭シートに関する。 BACKGROUND OF THE INVENTION The present invention relates to deodorants and deodorizing sheet using the same, more particularly, by the photocatalytic action of the photoreactive semiconductor, efficiently adsorb various aldehyde with an amine-containing layered phosphate about deodorizing sheet using the same deodorants and characterized by decomposing removed by.

【0002】 [0002]

【従来の技術】従来、工場などにおける工業的に発生する悪臭や、多量の廃棄物を排出する飲食店やホテルなどのサービス産業における廃棄物に起因した悪臭が問題となっていたが、最近では、自動車内や一般室内などの日常生活空間における悪臭もクローズアップされてきている。 Conventionally, stench and the industrial development in the factories, but bad odor caused has been a problem in waste in the service industries such as restaurants and hotels to discharge a large amount of waste, recently , also stink in the day-to-day living space, such as an automobile in and general room have been closed up. 従って、これら悪臭などの有害物質の除去に対するニーズが高まっており、悪臭除去装置や悪臭除去フィルターなどを組み込んだ空気清浄機の開発が盛んに行なわれている。 Therefore, there is an increasing need for removal of harmful substances such as these malodor development of the air cleaner is actively incorporating such malodor removing device and odors removal filter.

【0003】一般の空気清浄機には、活性炭を含有するフィルターが使用されており、活性炭に悪臭などの有害物質を吸着させる方法がとられている。 [0003] In general the air cleaner has been used a filter containing activated carbon, a method of adsorbing harmful substances such as malodor to the activated carbon is employed. しかしながら、 However,
活性炭は大部分の有害物質に対して吸着作用しか示さず、一定量の有害物質を吸着するとフィルターを交換せねばならない、あるいは、周囲の温度上昇や有害物質の濃度上昇などにより、一度吸着した有害物質が離脱し易いという問題点があった。 Activated carbon exhibit only adsorption for most hazardous substances and adsorbs a certain amount of hazardous substances must be exchanged filter, or the like increase in the concentration of the surrounding temperature rises and toxic substances, once adverse adsorbed substance there has been a problem that is easy to withdrawal.

【0004】近年、このような問題を解決するために、 [0004] In recent years, in order to solve such a problem,
有害物質を分解し得る触媒を用いた材料、あるいは該触媒と活性炭のような吸着剤とを組み合わせた材料が開発されてきている。 Material with a catalyst capable of decomposing harmful substances material or a combination of an adsorbent such as the catalyst and activated carbon, have been developed. 例えば、特開平1−234729号公報では、ハニカム状活性炭表面に光触媒能を有する二酸化チタンの層を形成してなる脱臭剤を組み込んだ空気調和機が開示されている。 For example, Japanese Laid-1-234729, JP-air conditioner is disclosed incorporating a deodorant in a honeycomb activated carbon surface by forming a layer of titanium dioxide having a photocatalytic activity. 該空気調和機には紫外線ランプが装着されており、該脱臭剤に紫外線を照射することによって、二酸化チタンの光触媒作用で活性炭に吸着した有害物質を分解除去する。 The air conditioner is an ultraviolet lamp is mounted, by irradiating ultraviolet rays to the deodorizing agent, decomposing and removing harmful substances adsorbed on activated carbon by photocatalytic action of titanium dioxide.

【0005】その他にも、特開平2−253848号公報では、無機質繊維状担体にアナターゼ型酸化チタン、 [0005] Besides, in JP-A 2-253848 and JP-anatase type titanium oxide inorganic fibrous carrier,
活性炭、並びにマンガン、鉄、銅、コバルト、ニッケルなどのオゾン分解能を有する成分を担持したオゾン分解触媒、特開平3−233100号公報では、二酸化チタン、活性炭、鉄系金属化合物の混合物と、これに300 Activated carbon, and manganese, iron, copper, cobalt, ozonolysis catalyst carrying component having ozone resolution such as nickel, in JP-A 3-233100 and JP-titanium dioxide, activated carbon, and a mixture of iron-based metal compound, in which 300
nm以上の波長の光を照射する光源とからなる自動車道トンネル用換気設備、特開平4−256755号公報では、二酸化チタンなどの光反応性半導体を担持させた粒状パルプからなる光反応性有害物質除去材といった具合に実に様々な有害物質を分解除去可能な材料が開示されている。 Motorway tunnel ventilation equipment consisting of a light source for irradiating light of nm or more wavelengths, in JP-A 4-256755 and JP-photoreactive noxious substance composed of granular pulp was supported photoreactive semiconductors such as titanium dioxide wide variety of toxic substances capable decomposed and removed material and so have been disclosed, such as removing material.

【0006】このように有害物質を分解し得る触媒を用いた材料や、該触媒と活性炭のような吸着剤とを複合化した材料を用いることによって、吸着剤を単独で使用した場合に比べて、より効果的な脱臭が可能となる。 [0006] Materials and using a catalyst capable of decomposing this way the harmful substances, an adsorbent such as the catalyst and the activated carbon by the use of composite materials, as compared to when used alone adsorbent , thereby enabling more effective deodorization. しかしながら、これらの従来技術においては、有害物質の分解によって生ずる各種のアルデヒドに対する考慮は何らなされていない。 However, in these prior art, consideration for various aldehyde produced by the decomposition of harmful substances has not been made at all. 例えば、アルコール類の触媒による分解作用により、代表悪臭物質の一つであるアルデヒド類が生成するが、一般にアルデヒド類はアルコール類よりはより健康に好ましくないことが知られている。 For example, the decomposition by the catalyst of the alcohol, typical malodor is one aldehyde materials are produced, but generally aldehydes are known to be undesirable to healthier than alcohols.

【0007】さらに一般住宅環境において特に新建材を用いた場合に接着在中に含まれるホルムアルデヒド成分が室内に放出され呼吸疾患や皮膚疾患を引き起こすなどの、いわゆるシックビル症候群が社会的な問題になったり、タバコの主成分として含まれるアセトアルデヒドにより健康を害するなどの問題が指摘されているが、通常の活性炭ではアルデヒド類が効率よく除去できないうえ、たとえアルデヒド吸着能に優れた吸着剤を使用しても飽和してしまえばそれ以上のアルデヒド除去効果が望めないばかりか、周囲のアルデヒド濃度が低い場合には逆に吸着したアルデヒドを放出するという基本的な問題があった。 [0007] such further formaldehyde component in particular contained in the adhesive Enclosed in the case of using the new building materials in residential environment is released into the room cause respiratory diseases and skin diseases, or so-called sick building syndrome becomes social problems Although problems such as a health hazard by acetaldehyde contained as the main component of tobacco has been pointed out, after the aldehyde in normal activated carbon can not be efficiently removed, even with superior adsorbent if aldehydes adsorbability not only can not be expected saturated with Shimae if more aldehyde removal effect, there was a fundamental problem that if the aldehyde concentration of the surrounding low releasing adsorbed aldehydes reversed. これらのアルデヒドは活性炭に吸着されにくく、有効に光分解されれば最終的に水と二酸化炭素に分解され得る可能性もあるが、活性炭が吸着飽和した場合や、吸着飽和に達していなくても周辺温度が上昇した場合には外部に放散され、異臭の発生や周辺材料の汚染の原因となる恐れがある。 These aldehydes hardly adsorbed to the activated carbon, if effectively photolyzed finally there is a possibility that may be decomposed into water and carbon dioxide, but or if charcoal is adsorbed saturated, even not reached the adsorption saturation it is dissipated to the outside when the ambient temperature rises, which may cause the contamination of odor generation and peripheral materials.

【0008】 [0008]

【発明が解決しようとする課題】本発明は、上記の問題点を解決するものであり、光反応性半導体の光触媒作用による有害物質の分解で発生するアルデヒドや、新建材など住環境に放出されるアルデヒド類などを吸着除去することにより、吸着剤の失活や、アルデヒドの放散による異臭の発生や健康阻害、周辺材料の腐食のない脱臭剤およびそれを用いた脱臭シートを提供することを目的とする。 The present invention is to challenge it to solve] is to solve the above problems, an aldehyde or generated by decomposition of harmful substances by the photocatalytic action of the photoreactive semiconductor, is released into the living environment, such as new construction materials by adsorbing and removing such aldehydes that aims to provide and deactivation of the adsorbent, development and health inhibition of odor due to dissipation of aldehydes, corrosion-free deodorant near material and deodorizing sheet using the same to.

【0009】 [0009]

【課題を解決するための手段】本発明者は、上記の課題を解決するために鋭意検討した結果、脱臭剤およびそれを用いた脱臭シートを発明するに至った。 The present inventors SUMMARY OF THE INVENTION As a result of intensive studies for solving the above problems has led to the invention of deodorants and deodorizing sheet using the same.

【0010】すなわち本発明の脱臭剤は、少なくとも光反応性半導体とアミン含有層状リン酸塩よりなることを特徴とする脱臭剤である。 [0010] That deodorizing agent of the present invention is a deodorant, characterized in that comprises at least photoreactive semiconductor with an amine-containing layered phosphate.

【0011】少なくとも光反応性半導体とアミン含有層状リン酸塩からなる脱臭剤を基材に内添してなることを特徴とする均一系脱臭シート。 [0011] At least homogeneous deodorizing sheet photoreactive semiconductor and amine-containing deodorant comprising a layered phosphate, characterized by comprising internally added to the base material.

【0012】少なくとも光反応性半導体とアミン含有層状リン酸塩からなる脱臭剤を基材に塗工してなることを特徴とする塗工系脱臭シート。 [0012] Coating systems deodorizing sheet characterized by being obtained by coating at least a photoreactive semiconductor and amine-containing deodorant comprising a layered phosphate to the substrate.

【0013】少なくとも光反応性半導体とアミン含有層状リン酸塩からなる脱臭剤を2枚以上の基材間に封入してなることを特徴とする封入脱臭シート。 [0013] encapsulated deodorant sheet characterized by formed by sealing at least a photoreactive semiconductor and amine-containing layered phosphate consists deodorizer between two or more substrates.

【0014】基材が不織布であることを特徴とする均一系脱臭シート、あるいは塗工系脱臭シート、あるいは封入脱臭シート。 [0014] Homogeneous deodorizing sheet base material characterized in that it is a non-woven fabric or applied based deodorizing sheet, or encapsulated deodorant sheet.

【0015】 [0015]

【発明の実施の形態】以下、本発明の脱臭剤およびそれを用いた脱臭シートについて、詳細に説明する。 BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, deodorants and deodorizing sheet using the same of the present invention will be described in detail.

【0016】まず、脱臭剤の構成成分である光反応性半導体とアミン含有層状リン酸塩について、以下に具体的に説明する。 [0016] First, the photoreactive semiconductor and the amine-containing layered phosphate is a component of the deodorizing agent will be specifically described below.

【0017】本発明で用いられる光反応性半導体とは、 [0017] The photoreactive semiconductor used in the present invention,
0.5〜5eV、好ましくは1〜3eVの禁止帯幅を有する光触媒反応を生ずる半導体であって、光反応性半導体で生成したOHラジカルにより有害物質が分解される。 0.5~5EV, preferably a semiconductor causing a photocatalytic reaction having a band gap of 1~3EV, harmful substances are decomposed by OH radicals generated by the photoreactive semiconductor. 光反応性半導体の形状としては、粒子状のものが好ましく、比表面積が10〜500m 2 /gの粒子を適宜選択して用いる。 The shape of the photoreactive semiconductor, preferably those of the particulate, the specific surface area is suitably selected and used particles of 10 to 500 m 2 / g.

【0018】このような光反応性半導体としては、特開平2−273514号公報に開示されているものを挙げることが可能であり、酸化亜鉛、三酸化タングステン、 [0018] As the photoreactive semiconductor, it is possible to include those disclosed in JP-A-2-273514, zinc oxide, tungsten trioxide,
酸化チタン、酸化セリウムなどの金属酸化物が好ましく、これらの中でも、酸化チタンは、構造安定性、光反応性半導体としての能力、取扱い上の安全性などを考慮した場合、特に好ましい材料である。 Titanium oxide, preferably a metal oxide such as cerium oxide, among these, titanium oxide, structural stability, ability as photoreactive semiconductor, when considering the handling safety, it is particularly preferred material. 酸化チタンとしては、二酸化チタンのほか、含水酸化チタン、水和酸化チタン、メタチタン酸、オルトチタン酸、水酸化チタンなどを使用することが可能であり、その結晶型については特に制限はない。 Titanium oxide, in addition to titanium dioxide, it is possible to use hydrous titanium oxide, hydrated titanium oxide, metatitanic acid, orthotitanic acid, etc. titanium hydroxide, no particular limitation is imposed on the crystalline form. 酸化チタンを用いる場合には、その比表面積は50〜400m 2 /gのものが好ましい。 When using a titanium oxide, a specific surface area of preferably from 50 to 400 m 2 / g. さらに、酸化チタンの表面に白金、金、銀、パラジウム、ロジウム、ルテニウムなどの金属、酸化ルテニウム、酸化ニッケルなどの金属酸化物を被覆したものであっても何ら構わない。 Furthermore, platinum on the surface of the titanium oxide, gold, silver, palladium, rhodium, a metal such as ruthenium, ruthenium oxide, may no be those coated with a metal oxide such as nickel oxide.

【0019】次に、アミン含有層状リン酸塩について、 [0019] Next, the amine-containing layered phosphate,
以下に説明する。 It will be described below. 本発明の脱臭剤およびそれを用いた脱臭シートは、光反応性半導体の光触媒能により、有害物質を分解除去するものであるが、光触媒による分解作用により、アルコール類などからは分解中間生成物としてアルデヒド類が発生する場合がある。 Deodorants and deodorizing sheet using the same of the present invention, by the photocatalytic ability of the photoreactive semiconductor, but is intended to decompose and remove hazardous substances, the decomposition action of the photocatalyst, as a decomposition intermediate products from such alcohols there is a case in which aldehydes are generated.

【0020】これらのアルデヒドは代表的な悪臭物質であったり、健康を損ねる化合物であったりするため効果的に住環境より除去できることが好ましいが、効果的に吸着できる吸着剤がなかったり、吸着が飽和すると吸着分を放出するなどの問題があった。 [0020] or a These aldehydes representative malodorous substance, it is desirable to be able to remove more effectively living environment for or a compound impairs the health, or no adsorbent capable of effectively adsorbing, adsorption there is a problem, such as releasing the adsorbed fraction with saturated.

【0021】しかしながら、アミン含有層状リン酸塩を含有してなる本発明の脱臭剤およびそれを用いた脱臭シートでは、例えば各種アルデヒドとアミン含有層状リン酸塩との間で化学吸着反応が起こり、雰囲気中のアルデヒドや光反応性半導体反応により生成したアルデヒドおよび酸成分を除去することができる。 [0021] However, the deodorants and deodorizing sheet using the same of the present invention which comprises an amine-containing layered phosphates, e.g. chemisorption reactions between the various aldehyde and an amine-containing layered phosphate occurs, it can be removed resulting aldehyde and acid components by aldehyde and photoreactive semiconductor reaction in the atmosphere. また、アミン含有層状リン酸塩は上記の担体と同様の作用、すなわち光反応性半導体を担持し、樹脂系バインダーや基材などとの接触部分を減少させることによって脱臭シートの劣化や変色を抑制する作用も併せ持っている。 Further, amine-containing layered phosphate same action as the above carrier, i.e. photoreactive semiconductor carries, suppress deterioration or discoloration of the deodorizing sheet by reducing the contact portion between a resin binder and substrate It has also combines action to.

【0022】アミン含有層状リン酸塩に用いられるアミンとしては、例えば第3級アミノ基を有する化合物としてビニルベンジルジメチルアミン、ビニルベンジルジエチルアミン、スチレンアクリル酸ジエチルアミン、スチレンメタクリル酸ジエチルアミン、スチレンアクリル酸ジメチルアミン、スチレンメタクリル酸ジメチルアミン、スチレンメタクリル酸エチルジメチルアミン、スチレンアクリル酸エチルジメチルアミン、スチレンメタクリル酸エチルジエチルアミン、スチレンアクリル酸エチルジエチルアミン、トリエチルアミン等の化合物、モノマー、オリゴマー、ポリマーあるいはこれらの化合物から誘導される第3級アミノ基を含有する誘導体などを用いることができる。 The amine as the containing layered phosphate amine used in, for example, vinylbenzyl dimethyl amine as a compound having a tertiary amino group, vinyl benzyl diethylamine, styrene-acrylic acid diethylamine, styrene methacrylic acid diethylamine, styrene-acrylic acid dimethylamine , styrene methacrylic acid dimethylamine, styrene ethyl methacrylate dimethylamine, styrene-acrylic acid ethyl dimethylamine, styrene ethyl methacrylate diethylamine, ethyl styrene acrylate diethylamine, compounds such as triethylamine, derived monomers, oligomers, a polymer or these compounds like it can be used derivatives containing tertiary amino groups that.

【0023】第2級アミノ基を有する化合物としてはエチルアニリン、ジエチルアミン、メチルビニルアミン、 The ethyl aniline as a compound having a secondary amino group, diethyl amine, methyl vinyl amine,
スチレンアクリル酸メチルメチルアミン、ビニルベンジルメチルアミン、スチレンメタクリル酸エチルメチルアミン等の化合物、モノマー、オリゴマー、ポリマーあるいはこれらの化合物から誘導される第2級アミノ基を含有する誘導体などを用いることができる。 Styrene-acrylic acid methyl methylamine, vinylbenzyl methyl amine, compounds such as styrene ethyl methacrylate methyl amine, can be used a monomer, oligomer, and derivatives containing secondary amino group derived from a polymer or these compounds .

【0024】第1級アミノ基を有する化合物としてはアニリン、ベンジルアミン、ナフチルアミン、シクロヘキシルアミン、スチレンメタクリル酸エチルアミン、スチレンアクリル酸アミン等の化合物、モノマー、オリゴマー、ポリマーあるいはこれらの化合物から誘導される第1級アミノ基を含有する誘導体などを用いることができる。 The aniline compound having a primary amino group, benzylamine, naphthylamine, the induced cyclohexylamine, styrene methacrylic acid ethylamine, compound, styrene-acrylic acid amines, monomers, oligomers, a polymer or these compounds such derivatives containing a primary amino group can be used.

【0025】これらのアミン化合物は層状リン酸と部分的に中和しながらインターカレーションを行うことによりアミン含有層状リン酸塩とすることができる。 [0025] These amine compounds may be an amine-containing layered phosphate by performing intercalation with neutralized partially layered phosphate. 効率的にインターカレートできるアミン化合物と層状リン酸の組み合わせは限定されるが、アミン化合物が挿入されることにより層間距離が拡げられることにより、アルデヒドを層状リン酸塩の層間に取り込むことが可能になる。 The combination of efficient amine compound which can intercalate and layered phosphate is limited, by the interlayer distance is expanded by the amine compound is inserted, it can be incorporated aldehyde between layers of the layered phosphate become.

【0026】ここで重要なことは、アミン含有層状リン酸塩がアルデヒドを吸着する能力に優れるだけでなく、 [0026] What is important here is that, not only excellent in ability of the amine containing layered phosphate adsorbs aldehydes,
アミン化合物単独、あるいは層状リン酸化合物単独で光反応性半導体と混合した場合に比べて経時的なアルデヒド処理能力に特に優れることにある。 Amine compound alone, or in that particularly excellent in temporal aldehyde capacity a layered phosphate compound alone compared to when mixed with photoreactive semiconductor. すなわち、ある種のアミン化合物および層状リン酸塩はアルデヒド吸着能力があるが物理吸着タイプ、中和タイプに限らず、飽和量以上の吸着、中和をすることはあり得ない。 In other words, certain amine compounds and layered phosphate is aldehyde adsorption capacity but physical adsorption type, not limited to the neutralization type, saturation amount or more of adsorption, there can be no possible to neutralization. 光反応性半導体は有効な紫外線存在下でアルデヒドなどを酸化分解することができるが、この酸化反応は無差別に起こるため有機系の吸着剤などが併存する場合はそれすらも分解してしまう。 Although photoreactive semiconductor can be oxidatively decomposed and aldehyde valid ultraviolet presence, if such adsorbent organic for this oxidation reaction occurs indiscriminately coexist it even be will decompose. このため、アミン化合物をアルデヒド吸着剤に使用しても光反応性半導体が存在する場合、アルデヒドとともにアミン化合物も分解されるため一定時間が経過するとアルデヒドの処理ができない状態になる。 Therefore, if also there is photoreactive semiconductor using an amine compound to the aldehyde adsorbent, a state can not be processed aldehyde after a certain period of time for the amine compound is also degraded with aldehydes.
光反応性半導体が存在する場合のアミン化合物のアルデヒド処理量は、光反応性半導体が存在しない場合に比べて高々数10%から数倍の増加でしかない。 Aldehyde treating amount of the amine compound in the case where the photoreactive semiconductor is present, only at most an increase of several fold from several tens percent as compared with the case where the photoreactive semiconductor is not present. しかしながらアミン含有層状リン酸塩として光反応性半導体と併存した場合には驚くべきことに相当するアミン化合物単独の場合に比べて数10倍以上のアルデヒド処理が可能であることが明らかになった。 However, it is possible to aldehyde treating several 10 times or more than that of the amine compound alone corresponding Surprisingly when coexisting photoreactive semiconductor as the amine-containing layered phosphate revealed.

【0027】さらに、開発当初には期待しなかったことであるが、アミン化合物、または光反応性半導体とアミン化合物の併存した系には特有な臭気があるが、アミン含有層状リン酸塩および光反応性半導体と併存した系とした場合にはその臭気が極めて少なくなることが判明した。 Furthermore, although developed initially is that did not expect, amine compound, or the coexistence with the system of the photoreactive semiconductor and the amine compound has peculiar odor, amine-containing layered phosphates and light when a comorbid the system with reactive semiconductor has been found that the odor is very little. これはアミン化合物が有する飽和蒸気圧に相当する蒸発化合物あるいはアミン化合物に含まれる微量の不純物、光反応性半導体によるアミン化合物の分解物が層状リン酸に吸着され、さらに時間と共に光反応性半導体で分解される結果と考えられる。 This trace impurities contained in the vaporized compound or an amine compound corresponding to the saturated vapor pressure of the amine compound has, degradation of an amine compound according to the photoreactive semiconductor is adsorbed to the layered phosphate, further photoreactive semiconductor with time considered the results to be degraded. これらの相乗効果により、アミン含有層状リン酸塩と光反応性半導体を併存した系では非常に効率的にアルデヒド臭の脱臭、アミン臭の脱臭を行うことができることが判明した。 These synergistic effects, very efficiently deodorizing aldehydes odor in a system coexist amine-containing layered phosphate and photoreactive semiconductor, it can perform deodorization of amine odor was found.

【0028】層状リン酸中に含まれるアミンの含有量は特に制限はないがアルデヒドの吸着量は主にアミンの量によって決まるため多いほど好ましい。 The content of the amine contained in the layered phosphate is preferably as particularly adsorption limit although not aldehydes often because mainly determined by the amount of amine. アミン含有層状リン酸塩の配合量は、アミンの含有量によるが光反応性半導体100重量部に対して、10〜500重量部が好ましい。 The amount of the amine-containing layered phosphate is by the content of amine relative to the photoreactive semiconductor 100 parts by weight, preferably 10 to 500 parts by weight. ここで、10重量部未満では、アルデヒドの吸着能力に不足するので好ましくない。 Undesirable where it is less than 10 parts by weight, since the insufficient adsorption capacity of aldehyde. 一方、500重量部を超えて多いと、吸着能力は大きいが、光反応性半導体表面のアミン含有層状リン酸塩被覆部分が増大し、光反応性半導体能が低下するので好ましくない。 On the other hand, when it is more beyond 500 parts by weight, although the adsorption capacity is large, an amine-containing layered phosphate coating portion of the photoreactive semiconductor surface is increased, since the photoreactive semiconductor ability is undesirably reduced.

【0029】本発明の脱臭剤、脱臭シートは、光反応性半導体とアミン含有層状リン酸塩の他に担体を含有させて脱臭剤構造を作成してもよい。 The deodorant of the present invention, the deodorizing sheet may create a deodorant structure in addition to contain a carrier of the photoreactive semiconductor and the amine-containing layered phosphate. この担体について、以下に説明する。 This carrier will be described below. 本発明に用いられる担体とは、光反応性半導体を担持させるためのものである。 The carrier used in the present invention is intended for supporting the photoreactive semiconductor. 光反応性半導体は、光触媒作用により悪臭などの有害物質を分解除去することができる反面、該光反応性半導体と接触する樹脂系バインダーなどの有機成分を劣化、変色させるという短所も併せ持っている。 Photoreactive semiconductors, although capable of decomposing and removing hazardous substances such as malodorous photocatalytically, degrade the organic component such as a resin binder in contact with the photoreactive semiconductor, but also combines disadvantage discolor. しかしながら、担体に光反応性半導体を担持させることによって、樹脂系バインダーや基材などとの接触部分を減少させることが可能であり、脱臭シートの劣化や変色を抑制することができる。 However, by supporting the photoreactive semiconductor on a support, it is possible to reduce the contact portion between a resin binder and the base material, it is possible to suppress the deterioration or discoloration of the deodorizing sheet.

【0030】さらには、悪臭物質に対して吸着能を有する担体を使用することも可能であり、この場合、担体で吸着した悪臭物質を光反応性半導体で分解除去することができるため、極めて高い脱臭性能を得ることができる。 Furthermore, it is also possible to use a carrier having a suction capacity for malodorous substances, in this case, it is possible to decompose and remove the malodorous substances adsorbed by the carrier in the photoreactive semiconductor, very high deodorizing performance can be obtained. 他に、触媒作用を有する担体も好ましい材料の一つである。 Otherwise, one of the carrier is also preferably a material having a catalytic action.

【0031】具体的な担体の例としては、活性炭、ゼオライト、酸化鉄などの鉄系化合物、酸化亜鉛、酸化マグネシウム、酸化アルミニウム、シリカ、シリカ−酸化亜鉛複合物、シリカ−アルミナ−酸化亜鉛複合物、複合フィロケイ酸塩、あるいはこれらの混合物などが挙げられる。 [0031] Examples of specific carriers, activated carbon, zeolite, iron compounds such as iron oxide, zinc oxide, magnesium oxide, aluminum oxide, silica, silica - zinc oxide composite, silica - alumina - zinc oxide composite , like composite phyllosilicate or mixtures thereof. これらの担体の形状は特に限定されるものではないが、光反応性半導体の担持能力を考慮した場合、粒子状のものが好ましく、比表面積が50〜2000 m 2 /g The shape of these carriers is not particularly limited, but if considering the carrying capacity of the photoreactive semiconductor, preferably those of the particulate, a specific surface area of 50 to 2000 m 2 / g
のものを適宜選択して用いることが可能であり、例えば活性炭の場合には、500〜1500m 2 /gのものが好ましい。 It is possible to use a suitably selected and those, for example, in the case of activated carbon, preferably from 500 to 1500 2 / g.

【0032】次に、脱臭剤の作製方法について、以下に具体的に説明する。 [0032] Next, a method for manufacturing deodorants, specifically described below. 本発明の脱臭剤は光反応性半導体、 Deodorant of the present invention is a photoreactive semiconductor,
アミン含有層状リン酸塩の混合体、凝集複合体、あるいは該凝集複合体中に担体や微細繊維を含有してなる凝集複合体である。 Mixture of amine-containing layered phosphate, aggregate complexes, or in agglomerated complex is aggregated complexes comprising the carrier and fine fibers. 凝集複合体の形成方法としては、例えば次の方法が挙げられる。 As a method of forming the aggregate complexes include, for example, the following method.

【0033】まず、光反応性半導体、アミン含有層状リン酸塩、必要ならば担体を水中に添加混合する。 Firstly, photoreactive semiconductor, amine-containing layered phosphate, admixed if necessary carrier in water. 微細繊維を用いる場合には、同じくこの段階で水中に添加する。 In the case of using the fine fibers, like added at this stage in water. 次いで、適当な凝集剤を用いて光反応性半導体、アミン含有層状リン酸塩、(担体、並びに微細繊維)の凝集複合体を形成するか、あるいは粒状に乾燥させるか、 Then, the photoreactive semiconductor with a suitable aggregating agent, an amine-containing layered phosphate, or dried or formed (carrier and fine fibers) aggregation complex of, or granulated,
適当なバインダーを混合して塗工/乾燥時の接着強度を持たせるように調整する。 By mixing an appropriate binder is adjusted so as to have a bond strength of at coating / drying.

【0034】凝集剤としては、カチオン性高分子凝集剤、例えばカチオン性ポリアクリルアマイド、ポリ塩化アルミニウムなどを使用することができる。 Examples of the aggregating agent may be used cationic polymer flocculant, such as cationic polyacrylamide, poly aluminum chloride and the like. 凝集剤の添加量は、使用する光反応性半導体、担体、アミン含有層状リン酸塩、微細繊維の種類や配合量によって異なるが、光反応性半導体、担体、アミン含有層状リン酸塩、 The addition amount of the aggregating agent, photoreactive semiconductor used, the carrier, an amine-containing layered phosphate varies depending on the kind and amount of the fine fibers, the photoreactive semiconductor, a carrier, an amine-containing layered phosphate,
微細繊維の総量100重量部に対して0.01〜10重量部添加するのが適当である。 It is appropriate to add 0.01 to 10 parts by weight per 100 parts by weight of the fine fibers.

【0035】さらに、これらのカチオン性高分子凝集剤と複合体を形成し、凝集を強化するようなアニオン性高分子凝集剤、例えばアニオン性ポリアクリルアマイドなど、あるいはアニオン性無機微粒子、例えばコロイダルシリカやベントナイト水分散物などを併用することもできる。 Furthermore, it forms a complex with the cationic polymer flocculating agent, an anionic polymer flocculant so as to enhance the aggregation, such as anionic, such as polyacrylamide, and anionic inorganic particles, e.g. colloidal silica etc. and bentonite aqueous dispersion can be used in combination.

【0036】使用目的に応じて、上記の凝集複合体水分散物のまま脱臭剤として使用しても構わないし、あるいは濾過や遠心脱水などの方法で該水分散物から凝集複合体を分離、次いで乾燥した後、必要に応じて粉砕して使用しても構わない。 [0036] Depending on the intended use, it does not may be used as a leave deodorant of the aggregated composite aqueous dispersion, or filtered and separated aggregate complex from the aqueous dispersion by a method such as centrifugal dehydration and then after drying, it may be used by optionally milled.

【0037】次に、上記の脱臭剤を用いた脱臭シートについて、以下に具体的に説明する。 Next, the deodorization sheet using the above deodorizer, specifically described below.

【0038】本発明の脱臭シートは、該脱臭剤を基材に内添(均一系脱臭シート)または塗工(塗工系脱臭シート)、あるいは少なくとも2枚以上の基材間に該脱臭剤を封入(封入脱臭シート)してなるものである。 The deodorizing sheet of the present invention, internally added deodorizing agent to a substrate (homogeneous deodorizing sheet) or coating (coating type deodorizing sheet), or the deodorizing agent between at least two or more substrates one in which you made in sealed (sealed deodorizing sheet).

【0039】本発明の均一系、塗工系の脱臭シートの基材としては、脱臭剤を保持し得るものであれば使用できる。 The homogeneous system of the present invention, as the base material of the deodorizing sheet coating system may be used as long as it can retain the deodorant. できれば光触媒反応により分解しない基材であることが好ましが、脱臭シートとした後の加工性も加味して選択する必要があり、不織布が好ましい基材のひとつとして挙げられる。 Shi preferred that a base material which is not decomposed by the photocatalytic reaction, if possible, but should be selected in consideration workability after deodorization sheet, cited as one of the nonwoven fabric is preferred substrate. 本発明において、封入系基材の特性としては、有害物質を通過させるための通気性、光反応性半導体を活性化させるための光透過性を有することである。 In the present invention, the characteristics of the encapsulating base material is that it has hazardous material permeable for the passage of the light transmissive for activating the photoreactive semiconductor. このような基材の形態としては、不織布あるいは多孔質フィルム状のものなどが挙げられるが、坪量、通気性を制御し易く、加工性にも優れている点から不織布が特に好ましい基材である。 The form of such substrates include, but like those of a nonwoven fabric or a porous film-like, the basis weight, easy to control breathability, with particularly preferred substrate nonwovens are terms that are excellent in workability is there.

【0040】不織布は、ポリアミド系繊維、ポリエステル系繊維、ポリアルキレンパラオキシベンゾエート系繊維、ポリウレタン系繊維、ポリビニルアルコール系繊維、ポリ塩化ビニリデン系繊維、ポリ塩化ビニル系繊維、ポリアクリロニトリル系繊維、ポリオレフィン系繊維、フェノール系繊維などの合成繊維、ガラス繊維、金属繊維、アルミナ繊維、活性炭素繊維などの無機繊維、 The nonwoven fabric, polyamide fibers, polyester fibers, polyalkylene para oxybenzoate fibers, polyurethane fibers, polyvinyl alcohol fibers, polyvinylidene chloride fibers, polyvinyl chloride fibers, polyacrylonitrile fibers, polyolefin fibers , synthetic fibers such as phenolic fibers, glass fibers, metal fibers, alumina fibers, inorganic fibers such as activated carbon fibers,
木材パルプ、麻パルプ、コットンリンターパルプなどの天然繊維、再生繊維、あるいはこれらの繊維に親水性や難燃性などの機能を付与した繊維などを使用し、各種方法によって製造したものである。 Natural fibers such as wood pulp, hemp pulp, cotton linter pulp, using such fibers imparted with functions such as recycled fibers or hydrophilic and flame retardancy of these fibers, is that produced by various methods.

【0041】不織布の製造方法については特に制限はなく、目的・用途に応じて、乾式法、湿式抄造法、メルトブローン法、スパンボンド法などで得られたウェブをウォータージェット法、ニードルパンチ法、ステッチボンド法などの物理的方法、サーマルボンド法などの熱による接着方法、レジンボンドなどの接着剤による方法で強度を発現させる方法を適宜組み合わせて製造することができる。 [0041] No particular limitation is imposed on the method of manufacturing a non-woven fabric, depending on the purpose and application, a dry method, a wet paper-making method, melt-blown method, spun bond method water jet method and the resulting web or the like, and needle punching, stitch physical methods such as bonding method, bonding method by heat, such as thermal bonding method, can be produced by combining the method of expressing the strength in the method according to the adhesive, such as resin-bonded appropriately.

【0042】上述の基材に、本発明の脱臭剤を内添して均一系脱臭シートを製造する場合は、例えば基材の製造時に基材の素材と共に該脱臭剤を添加して製造することで本発明の脱臭シートを製造することができる。 [0042] the above-described substrate, it the case of producing a homogeneous deodorizing sheet deodorizing agent internally added in the present invention, for example be prepared by adding a deodorizing agent with the substrate material during the production of the base material in it is possible to produce the deodorization sheet of the present invention.

【0043】塗工系脱臭シートの製造方法としては、本発明の脱臭剤単独、あるいは該脱臭剤とバインダーとして熱可塑性樹脂の水性エマルジョンなどを混合して塗工、熱溶融させた熱可塑性樹脂中に該脱臭剤を添加して練り込み、基材に熱融着させて塗工するなど基材に応じて種々変えることができる。 [0043] As a method for producing a coating system deodorizing sheet, deodorant alone or deodorizing agent and a binder as the thermoplastic resin such as aqueous emulsion by mixing the coating of the present invention, a thermoplastic resin obtained by heat-melting it can be variously changed depending on the substrate, such as kneading by adding a deodorizing agent, heat sealed to the substrate to coating to.

【0044】封入脱臭シートの製造方法としては、少なくとも2枚以上の基材を用いて、一方の基材に本発明の脱臭剤を介在させた後、加熱ロールを用いて全面接着する方法、エンボスロールを用いて部分的に接着させる方法、高温の大気中で処理する方法、超音波溶融、レーザー溶融、高周波溶融などにより接着する方法などがあり、これらを単独、あるいは組み合わせて本発明の脱臭シートを製造することができる。 [0044] As a method for producing encapsulated deodorizing sheet using at least two or more substrates, after interposing a deodorizing agent of the present invention on one substrate, a method of entirely bonded by using a heating roll, embossing method for partially bonding using a roll, a method of processing at high temperature in air, ultrasonic melting, laser melting, there is a method of bonding by high-frequency melting, deodorizing sheets singly, or in combination present invention it can be produced.

【0045】さらに、基材上に本発明の脱臭剤を積載し、上記の方法で基材に接着させて該脱臭剤を固定化した脱臭シートとした後、該脱臭シート同士、あるいは該脱臭シートと基材を少なくとも1層以上積層するか、いずれかの方法によって積層した後、熱圧着により一体化する方法が挙げられる。 [0045] Further, after the stacked deodorant of the present invention on a substrate, and a deodorizing sheet obtained by immobilizing the deodorizing agent is adhered to the substrate in the manner described above, the deodorizing sheet or between the deodorizing sheet, whether laminated substrate at least one layer, after laminating by any method, and a method of integrated by thermocompression bonding. また、積層したものを、ニードルパンチ、ウォータージェット、ステッチボンド、レジンボンド法などで一体化することも好ましい方法である。 Moreover, those stacked, needle punched, it is also preferable to integrate water jet, stitch bonding, resin bonding method or the like.

【0046】本発明に用いる熱可塑性樹脂としては、具体的には、エチレン酢酸ビニル共重合樹脂またはこの変性ポリマー、エチレンアクリレート共重合樹脂、アイオノマー樹脂、ポリアミド、ナイロン樹脂、ポリエステル、ポリプロピレン、酢酸ビニル共重合体系、セルロース誘導体系、ポリメチルメタクリレート系、ポリビニルエーテル系、ポリウレタン系、ポリカーボネイト系の樹脂などが挙げられる。 [0046] As the thermoplastic resin used in the present invention, specifically, ethylene-vinyl acetate copolymer resin or a modified polymer, an ethylene acrylate copolymer resin, ionomer resin, polyamide, nylon resin, polyester, polypropylene, vinyl acetate copolymer polymer system, a cellulose derivative-based, polymethyl methacrylate-based, polyvinyl ether, polyurethane, or resin polycarbonate systems.

【0047】熱可塑性樹脂の使用量は、脱臭剤の総重量100重量部に対して1〜100重量部が好ましく、さらに好ましくは2〜80重量部である。 The amount of the thermoplastic resin is preferably 1 to 100 parts by weight based on the total weight 100 parts by weight of the deodorant, more preferably from 2 to 80 parts by weight. 1重量部未満では、脱臭剤を基材に十分に固定することができず、基材からの脱落を招くので好ましくない。 In less than 1 part by weight, it is impossible to sufficiently secure the deodorizing agent to the base material, so leading to falling off from the substrate is not preferable. 一方、100重量部を超えて多いと、基材への固定能は大きいが、熱可塑性樹脂による脱臭剤被覆部分が増大し、脱臭剤の機能が損なわれるので好ましくない。 On the other hand, when it is more than 100 parts by weight, although greater fixing ability to a substrate, deodorants covering part according to the thermoplastic resin is increased, since the function of the deodorant is impaired undesirably.

【0048】 [0048]

【作用】本発明の脱臭剤およびそれを用いた脱臭シートは、光反応性半導体の光反応性半導体作用により悪臭物質、細菌などの有害物質を分解除去するものである。 Deodorant sheet deodorants and using the same DETAILED DESCRIPTION OF THE INVENTION The present invention, malodorous substances by the photoreactive semiconductor action of the photoreactive semiconductor, is to decompose and remove harmful substances such as bacteria. また、アミン含有層状リン酸塩を含有させることにより、 Further, by containing the amine-containing layered phosphate,
光反応性半導体作用による有害物質の分解で生じた各種のアルデヒドや酸を中和除去することが可能であり、酸に起因した異臭発生や周辺機器の腐食を防ぐことができるばかりでなく、効果的な脱臭を図るべく担体に吸着剤を使用した場合には、酸による吸着剤の失活をも防ぐことが可能である。 Various aldehydes and acid generated in the decomposition of harmful substances by photoreactive semiconductor action able to neutralize removed, not only can inhibit the corrosion of odor generation and peripherals due to acid, effect specific when used carrier adsorbent to achieve deodorization, it is possible to prevent also the deactivation of the sorbent by acid. さらに、アミン含有層状リン酸塩と光反応性半導体を一体化凝集させたような系においては、 Further, in a system such as it is integrated aggregate amine-containing layered phosphate and photoreactive semiconductor,
光反応性半導体が基材に直接接触する面積が激減し、かつバインダーを分解する危険性も減少するため非常に耐光性の高い脱臭シートを構成することが可能になる。 Depleted area photoreactive semiconductor is in direct contact with the substrate, and also the risk of decomposition of the binder it is possible to configure very high deodorizing sheet light resistance to decrease.

【0049】 [0049]

【実施例】以下に実施例を挙げて本発明を具体的に説明するが、本発明は本実施例に限定されるものではない。 EXAMPLES The following examples illustrate the present invention in detail, but the present invention is not limited to this embodiment.

【0050】実施例1 <脱臭剤1の作製>光反応性半導体として二酸化チタン粉末(日本アエロジル社製、P25S6)100重量部、アミン含有層状リン酸塩としてアニリン含有層状リン酸100重量部を水中に添加混合した後、凝集剤としてポリ塩化アルミニウム(水澤化学工業社製、PAC) [0050] Example 1 <Preparation of deodorant 1> titanium dioxide powder as photoreactive semiconductor (Nippon Aerosil Co., P25S6) 100 parts by weight, water 100 parts by weight of aniline containing layered phosphate as an amine-containing layered phosphate after mixing added to the polyaluminum chloride as a coagulant (Mizusawa chemical Industries, Ltd., PAC)
を3重量部添加し、光反応性半導体とアミン含有層状リン酸塩の凝集複合体を形成した。 3 parts by weight was added to form a photoreactive semiconductor and aggregation complex of an amine-containing layered phosphate. 該凝集複合体を濾別、 Filtering off the aggregated complex,
乾燥した後、粉砕して実施例1の脱臭剤1を作製した。 After drying, to prepare a deodorizing agent 1 in Example 1 was pulverized.

【0051】実施例2 <脱臭剤2の作製>光反応性半導体として二酸化チタン粉末(日本アエロジル社製、P25S6)100重量部、アミン含有層状リン酸塩としてトリエチルアミン含有層状リン酸100重量部、活性炭粉末(クラレケミカル社製、クラレコール)50重量部を水中に添加混合した後、凝集剤としてポリ塩化アルミニウム(水澤化学工業社製、PAC)を5重量部添加し、光反応性半導体、 [0051] Example 2 <deodorant Preparation of 2> titanium dioxide powder as photoreactive semiconductor (Nippon Aerosil Co., P25S6) 100 parts by weight of triethylamine containing 100 parts by weight of the layered phosphate as an amine-containing layered phosphate, activated carbon powder was added and mixed (Kuraray chemical Co., KURARAY COAL) 50 parts by weight in water, polyaluminum chloride (Mizusawa chemical Industries, Ltd., PAC) was added 5 parts by weight as an aggregating agent, photoreactive semiconductor,
アミン含有層状リン酸塩、活性炭の凝集複合体を形成した。 Amine-containing layered phosphate, to form aggregated composite of activated carbon. 該凝集複合体を濾別、乾燥した後、粉砕して実施例2の脱臭剤2を作製した。 Filtered aggregated complex was dried to prepare a deodorant 2 of Example 2 was ground.

【0052】実施例3 <脱臭剤3の作製>光反応性半導体として二酸化チタン粉末(日本アエロジル社製、P25S6)100重量部、アミン含有層状リン酸塩としてトリエチルアミン含有層状リン酸100重量部、複合フェロケイ酸塩粉末(水澤化学工業社製、ミズカナイトAP)を水中に添加混合した後、凝集剤としてポリ塩化アルミニウム(水澤化学工業社製、PAC)を5重量部添加し、光反応性半導体、アミン含有層状リン酸塩、活性炭の凝集複合体を形成した。 [0052] Example 3 <deodorant Preparation of 3> titanium dioxide powder as photoreactive semiconductor (Nippon Aerosil Co., P25S6) 100 parts by weight of triethylamine containing 100 parts by weight of the layered phosphate as an amine-containing layered phosphate, the composite Ferokei salt powder (Mizusawa chemical industry Co., Mizukanaito AP) was added and mixed in water, polyaluminum chloride (Mizusawa chemical Industries, Ltd., PAC) was added 5 parts by weight as an aggregating agent, photoreactive semiconductor, amine containing layered phosphate, to form aggregated composite of activated carbon. 該凝集複合体を濾別、乾燥した後、粉砕して実施例3の脱臭剤3を作製した。 Filtered aggregated complex, dried to prepare a deodorant 3 of Example 3 was ground.

【0053】実施例4 <脱臭シート用基材水分散物の調製>芯鞘型熱融着性ポリエステル繊維(ユニチカ社製、#4080、繊度2デニール、繊維長5mm)55重量%、ポリエステル繊維(帝人社製、テピルス、繊度0.5デニール、繊維長5 [0053] Example 4 <deodorizing preparation of the sheet base material for aqueous dispersion> core-sheath heat-fusible polyester fibers (manufactured by Unitika Ltd., # 4080, fineness 2 deniers, fiber length 5 mm) 55 wt%, polyester fibers ( Teijin Ltd., Tepirusu, fineness 0.5 deniers, fiber length 5
mm)40重量%、針葉樹晒クラフトパルプ(カナダ標準濾水度480mL)5重量%を水中に添加混合し、脱臭シート用基材水分散物を調製した。 mm) 40 wt%, softwood bleached kraft pulp (Canadian Standard Freeness 480 mL) 5 wt% were added and mixed in water to prepare a deodorizing sheet base material for aqueous dispersion.

【0054】<均一系脱臭シートの作製>上記の脱臭シート用水分散物に、実施例1記載の脱臭剤1(濾別前の水分散物)を該繊維配合分に対して50重量%に相当する量を添加混合し、水性スラリーを調製した。 [0054] in <homogeneous deodorizing Preparation of Sheet> The deodorizing sheet water dispersion, equivalent Example 1 according deodorant 1 (water dispersion prior to filtration) in 50% by weight relative to the fiber blending component the amount to be added and mixed to prepare an aqueous slurry. 該水性スラリーから円網抄紙機を用いて坪量100g/m 2の実施例5の均一系脱臭シートを作製した。 To prepare a homogeneous deodorizing sheet of Example 5 having a basis weight of 100 g / m 2 by using a cylinder paper machine from the aqueous slurry.

【0055】実施例5 <塗工系脱臭シート用基材1の作製>実施例4記載の脱臭シート用基材水分散物から円網抄紙機を用いて坪量1 [0055] Example 5 <Coating system deodorizing Preparation of sheet substrate 1> Example 4 a basis weight using a cylinder paper machine from the deodorizing sheet base aqueous dispersion according to 1,
00g/m 2の塗工系脱臭シート用基材1を作製した。 The coating system deodorizing sheet substrate 1 of 200 g / m 2 was produced.

【0056】<塗工系脱臭シート1の作製>上記の塗工系脱臭シート用基材1上に、実施例1記載の脱臭剤1 [0056] in <Coating system deodorizing Preparation of Sheet 1> The above coating system deodorizing sheet substrate 1, described in Example 1 deodorizer 1
(濾別前の水分散物)にバインダーとして塩化ビニリデン系ラテックスを脱臭剤1に対して15%重量部混合し、これを30g/m 2となるように塗工し、実施例5の塗工系脱臭シート1を作製した。 Vinylidene chloride latex as a binder were mixed 15% parts by weight based on the deodorant 1 (aqueous dispersion of pre-filtered), was applied to thereto in a 30 g / m 2, coating of Example 5 to produce a system deodorizing sheet 1.

【0057】実施例6 <塗工系脱臭シート2の作製>厚さ20μmのポリエステルフィルム上に、実施例1記載の脱臭剤と塩化ビニリデン系ラテックスを脱臭剤1に対して10%重量部混合しの混合物を30g/m 2となるように塗工し、実施例6 [0057] on a polyester film of Example 6 <Preparation of a coating system deodorizing sheet 2> thickness 20 [mu] m, Example 1 deodorant vinylidene chloride latex 10% parts by weight with respect deodorant 1 according was applied a mixture of a such that 30 g / m 2, example 6
の塗工系脱臭シート2を作製した。 The coating system deodorizing sheet 2 was prepared.

【0058】実施例7 <封入脱臭シート用基材1の作製>ポリエステル繊維(旭化成工業社製、ビサイロン、繊度0.15デニール、繊維長7.5mm)70重量%、ポリエステル繊維(帝人社製、テトロン、繊度1.5デニール、繊維長2 [0058] Example 7 <encapsulated deodorant Preparation of sheet substrate 1> polyester fiber (Asahi Kasei Kogyo, Bisairon, fineness 0.15 deniers, fiber length 7.5 mm) 70 wt%, polyester fibers (manufactured by Teijin Ltd., Tetron, fineness 1.5 denier, fiber length 2
0mm)30重量%を水中に添加混合して水性スラリーを調製し、該水性スラリーより円網抄紙機を用いて坪量60g/m 2のウェブを抄造した。 0 mm) 30 wt% were added and mixed into water and the aqueous slurry was prepared, and papermaking to a basis weight of 60 g / m 2 web using a cylinder paper machine from the aqueous slurry. 次いで、該ウェブを1 Next, 1 the web
00メッシュのステンレスワイヤーからなる多孔質支持体に積載し、100kg/cm 2の高圧柱状水流を噴射して繊維を交絡し、エアドライヤーで乾燥して封入脱臭シート用基材1を作製した。 00 loaded on a porous support made of stainless wire mesh, by injecting high-pressure columnar water flow 100 kg / cm 2 to entangle the fibers, to prepare a sealed deodorizing sheet base material 1 and dried in air dryer.

【0059】<封入脱臭シートの作製>実施例1記載の脱臭剤1にバインダーとして酢酸ビニル系樹脂の顆粒体を脱臭剤1に対して5%重量部を混合したものを上記の脱臭シート用基材上に30g/m 2となるように積載し、 [0059] <inclusion deodorizing sheet produced> Example 1 above deodorizing sheet based on what granules of vinyl acetate resin were mixed with 5% weight parts per deodorant 1 to deodorants 1 as a binder according stacked so that 30 g / m 2 on wood,
次いで、該脱臭剤積載基材上にさらに1枚上記の脱臭シート用基材を積層した後、160℃に加熱したエンボスロールで加圧し、実施例7の封入脱臭シートを作製した。 Then, after further laminated one above deodorizing sheet substrate on deodorizing agent loading substrates, pressed with an embossing roll heated to 160 ° C., to produce a sealed deodorizing sheet of Example 7.

【0060】比較例1 アミン含有層状リン酸塩を使用しなかった点を除いて、 [0060] except that was not used in Comparative Example 1 an amine-containing layered phosphate,
実施例1と同様の方法で比較例1の脱臭剤を作製した。 To prepare a deodorizing agent Comparative Example 1 in the same manner as in Example 1.

【0061】比較例2 アミン含有層状リン酸塩の代わりに活性炭粉末(クラレケミカル社製、クラレコール)を使用した点を除いて、 [0061] Comparative Example 2 Amine-containing layered activated carbon powder instead of phosphate (Kuraray Chemical Co., KURARAY COAL) except using,
実施例1と同様の方法で比較例2の脱臭剤を作製した。 To prepare a deodorizing agent Comparative Example 2 in the same manner as in Example 1.

【0062】比較例3 実施例1の脱臭剤1の代わりに比較例1の脱臭剤を使用した点を除いて、実施例4と同様の方法で比較例3の均一系脱臭シートを作製した。 [0062] except using a deodorant Comparative Example 1 in place of deodorant 1 Comparative Example 3 Example 1 was prepared homogeneous deodorizing sheet of Comparative Example 3 in the same manner as in Example 4.

【0063】比較例4 実施例1の脱臭剤1の代わりに比較例2の脱臭剤を使用した点を除いて、実施例4と同様の方法で比較例4の均一系脱臭シートを作製した。 [0063] except using the deodorant of Comparative Example 2 in place of deodorant 1 Comparative Example 4 Example 1 was prepared homogeneous deodorizing sheet of Comparative Example 4 in the same manner as in Example 4.

【0064】比較例5 実施例1の脱臭剤1の代わりに比較例2の脱臭剤を使用した点を除いて、実施例5と同様の方法で比較例5の塗工系脱臭シートを作製した。 [0064] except using the deodorant of Comparative Example 2 in place of deodorant 1 Comparative Example 5 Example 1 was prepared coating system deodorizing sheet of Comparative Example 5 in the same manner as in Example 5 .

【0065】比較例6 実施例1の脱臭剤1の代わりに比較例2の脱臭剤を使用した点を除いて、実施例7と同様の方法で比較例6の封入脱臭シートを作製した。 [0065] except using the deodorant of Comparative Example 2 in place of deodorant 1 Comparative Example 6 Example 1 was prepared encapsulated deodorant sheet of Comparative Example 6 in the same manner as in Example 7.

【0066】<脱臭剤および脱臭シートの性能評価>上記実施例1〜7、比較例1〜4で作製した脱臭剤および脱臭シートについて、下記性能試験に従って評価し、その結果をまとめて下記表1に示した。 [0066] <deodorants and performance evaluation of the deodorizing sheet> The above Examples 1 to 7, for deodorants and deodorizing sheet prepared in Comparative Examples 1-4 were evaluated according to the following performance tests, the following Table 1 are summarized the results It was shown to.

【0067】<脱臭能>実施例1〜3および比較例1、 [0067] <deodorizing ability> Examples 1-3 and Comparative Example 1,
2の脱臭剤については0.3gの脱臭剤を、実施例4〜 The deodorant 0.3g for 2 deodorant, Example 4
7および比較例3〜6の脱臭シートについては10cm 7 and 10cm for deodorizing sheet of Comparative Example 3-6
×10cmの大きさに裁断したシートを、6Wのブラックランプを備えた5.6Lの密閉容器の底部に静置した。 The sheet was cut to a size of × 10 cm, it was placed in the bottom of the sealed container of 5.6L equipped with black lamp 6W. この容器中にアセトアルデヒドおよび酢酸を濃度1 Concentration 1 acetaldehyde and acetic acid in the vessel
00ppmになるように注入し、脱臭剤あるいは脱臭シートの上方約2cmからブラックランプで紫外線を照射し、アセトアルデヒドおよび酢酸が光分解するのに十分な時間である60分後の容器内のアセトアルデヒドおよび酢酸の濃度を検知管で測定した。 Implanted so as to 00Ppm, deodorant or an ultraviolet black lamps from above about 2cm of the deodorizing sheet is irradiated, acetaldehyde and acetic acid in the vessel after 60 minutes is sufficient time to acetaldehyde and acetic acid are photodegradation the concentration was measured with a detector tube. なお、検知管にはガステック社製のものを使用し、アセトアルデヒドには9 Note that the detector tube using those made of Gastec Corporation, the acetaldehyde 9
2L(測定範囲1〜20ppm)、酢酸には81L(測定範囲0.125〜25ppm)の検知管を使用した。 2L (measuring range 1 to 20 ppm), the acetic acid was used detector tube 81L (measuring range 0.125~25ppm).
また、60分後の容器内の臭気について、官能試験を実施した。 Further, the odor in the container after 60 minutes was a sensory test.

【0068】<耐光性>実施例4、比較例3の均一系脱臭シートにウェザーメーターで強力な紫外線を1ヶ月照射した所、実施例4の均一系脱臭シートは形状と性能に格段の変化はなかったが、比較例3の脱臭シートは基材繊維の劣化が起き、シートとしての形状を保持できなくなっていた。 [0068] <Light Resistance> Example 4, strong ultraviolet month irradiated place in weatherometer in homogeneous deodorizing sheet of Comparative Example 3, homogeneous deodorizing sheet of Example 4 is much variation in shape and performance There was no deodorizing sheet of Comparative example 3 deterioration of the base material fibers occurred was no longer able to maintain the shape as a sheet. 実施例4の脱臭シートがアミン含有層状リン酸塩の作用で高い耐光性を有することが明かとなった。 Deodorizing sheet of Example 4 is revealed to have high light resistance by the action of an amine-containing layered phosphate.

【0069】 [0069]

【表1】 [Table 1]

【0070】実施例1〜7のいずれの脱臭剤、脱臭シートについても、アセトアルデヒド除去性能は良好で、光照射30分後のアセトアルデヒド濃度は検出限界以下となっている。 [0070] Any of the deodorant of Examples 1 to 7, for deodorizing sheet also, the acetaldehyde removal performance is good, concentration of acetaldehyde light irradiation 30 minutes after is equal to or less than the detection limit. しかしながら、実施例の脱臭剤および脱臭シートでは、アセトアルデヒドの分解中間生成物である酢酸発生量も検出限界以下であるのに対して、比較例の脱臭剤および脱臭シートでは、低濃度ではあるもののアセトアルデヒド及び酢酸が検出され、且つ酸臭と感じられる異臭も感じられた。 However, the deodorants and deodorizing sheet of Example, acetic generation amount is an exploded intermediate product acetaldehyde whereas is below the detection limit, the deodorants and deodorizing sheet of the comparative example, of some at low concentrations of acetaldehyde and acetic acid were detected, also felt and odor perceived to Sanshu. 人間の嗅覚は酸臭に敏感で、p The human sense of smell is sensitive to acid odor, p
pbオ−ダーの酸臭をも感ずると言われており、実施例と比較例との間には十分な有意差がある。 pb o - is said to feel even an acid smell of loaders, there is enough significant difference between the example and the comparative example.

【0071】 [0071]

【発明の効果】本発明の脱臭剤およびそれを用いた脱臭シートは、光反応性半導体作用により悪臭物質や細菌などの有害物質を分解除去可能であり、有害物質の分解によって生ずる各種のアルデヒド、酸をアミン含有層状リン酸塩で中和除去することにより、酸に起因した異臭発生や周辺機器の腐食を防ぐことができるばかりでなく、 Deodorants and deodorizing sheet using the same of the present invention according to the present invention is the toxic substances such as malodorous substances and bacteria can decomposed and removed by the photoreactive semiconductor action, various aldehydes produced by the decomposition of harmful substances, by neutralizing and removing the acids with an amine containing layered phosphate, not only can inhibit the corrosion of odor generation and peripherals due to acid,
効果的な脱臭を図るべく担体に活性炭などの吸着剤を使用した場合には、酸による吸着剤の失活を防ぐことも可能である。 When using an adsorbent, such as a carrier activated carbon to achieve effective deodorization, it is also possible to prevent the deactivation of the sorbent by acid. 従って、本発明の脱臭剤およびそれを用いた脱臭シートは、様々な使用環境の下で有害物質の除去剤として活用することができ、空気清浄機、空調設備、一般室内、自動車内などの脱臭フィルター、病院のベッドなどの仕切り用カーテンやシーツ、喫煙室の仕切り用カーテンなどとして有効に作用する。 Accordingly, deodorants and deodorizing sheet using the same of the present invention can be used as removers of hazardous substances under various use environments, air cleaner, air conditioning, general indoor, deodorization, such a motor vehicle filter, partitioning curtains and sheets, such as hospital beds, effectively acting as such as partitioning curtain of the smoking room.

フロントページの続き (51)Int.Cl. 6識別記号 FI B01J 20/22 B01J 20/28 Z 20/28 21/06 M // B01D 53/86 35/02 J ZAB B01D 53/34 116J B01J 21/06 53/36 H 35/02 ZABJ Front page continued (51) Int.Cl. 6 identifications FI B01J 20/22 B01J 20/28 Z 20/28 21/06 M // B01D 53/86 35/02 J ZAB B01D 53/34 116J B01J 21 / 06 53/36 H 35/02 ZABJ

Claims (5)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 少なくとも光反応性半導体とアミン含有層状リン酸塩からなることを特徴とする脱臭剤。 1. A deodorizing agent characterized in that it consists of at least photoreactive semiconductor and amine-containing layered phosphate.
  2. 【請求項2】 少なくとも光反応性半導体とアミン含有層状リン酸塩からなる脱臭剤を基材に内添してなることを特徴とする均一系脱臭シート。 Wherein at least homogeneous deodorizing sheet photoreactive semiconductor and amine-containing deodorant comprising a layered phosphate, characterized by comprising internally added to the base material.
  3. 【請求項3】 少なくとも光反応性半導体とアミン含有層状リン酸塩からなる脱臭剤を基材に塗工してなることを特徴とする塗工系脱臭シート。 3. A coating system deodorizing sheet characterized by being obtained by coating at least a photoreactive semiconductor and amine-containing deodorant comprising a layered phosphate to the substrate.
  4. 【請求項4】 少なくとも光反応性半導体とアミン含有層状リン酸塩からなる脱臭剤を2枚以上の基材間に封入してなることを特徴とする封入脱臭シート。 4. The encapsulated deodorant sheet characterized by formed by sealing at least a photoreactive semiconductor and amine-containing layered phosphate consists deodorizer between two or more substrates.
  5. 【請求項5】 基材が不織布であることを特徴とする請求項2、3または4記載の脱臭シート。 5. A deodorizing sheet according to claim 2, 3 or 4, wherein the substrate is characterized in that it is a non-woven fabric.
JP6890598A 1998-03-18 1998-03-18 Deodorant and deodorization sheet Pending JPH11262626A (en)