JPH11181261A - Biodegradable resin molded product - Google Patents

Biodegradable resin molded product

Info

Publication number
JPH11181261A
JPH11181261A JP36617597A JP36617597A JPH11181261A JP H11181261 A JPH11181261 A JP H11181261A JP 36617597 A JP36617597 A JP 36617597A JP 36617597 A JP36617597 A JP 36617597A JP H11181261 A JPH11181261 A JP H11181261A
Authority
JP
Grant status
Application
Patent type
Prior art keywords
product
molded
resin
biodegradable
starch
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP36617597A
Other languages
Japanese (ja)
Inventor
Mutsuo Hirota
Akira Ishibashi
Makoto Sakai
Mamoru Tanaka
睦夫 広田
守 田中
石橋  亮
誠 酒井
Original Assignee
Ykk Corp
ワイケイケイ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

PROBLEM TO BE SOLVED: To obtain a molded product comprising a biodegradable resin degradable by actions of microorganisms existing in the natural world even by disposal and capable of retaining a practically sufficient strength without causing the disruption of natural environments or waste pollution. SOLUTION: This molded product comprises a biodegradable resin consisting essentially of a polybutylene succinate-based and/or a polyethylene adipate-based aliphatic polyester and starch and has a structure in which particles of the starch part are dispersed in the aliphatic polyester. The content of the starch based on the total weight of the resin material is preferably 10-60 wt.%. The molded product can be used as a product in various fields by molding thereof into a desired shape. Since a sufficiently high strength is retained, the molded product can advantageously be applied to especially a slide fastener or a Hook- and-Loop fastener.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、生分解機能を有するポリブチレンサクシネート系及び/又はポリエチレンアジペート系脂肪族ポリエステルと澱粉からなる生分解性樹脂成形品に関するものである。 The present invention relates to relates to a biodegradable resin molded article comprising the polybutylene succinate-based and / or polyethylene adipate aliphatic polyester and the starch having the biodegradability function. 特に、射出成形、押出成形により加工されるファスナー成形品に関するものである。 In particular, it relates to fastener molded article to be processed injection molded, by extrusion.

【0002】 [0002]

【従来の技術】生分解性樹脂であるポリブチレンサクシネートとポリエチレンアジペートは、主としてグリコールと脂肪族ジカルボン酸とから化学的に合成される脂肪族ポリエステルの一種である。 Polybutylene succinate and polyethylene adipate is ## ART biodegradable resin is a kind of aliphatic polyester are chemically synthesized from a predominantly glycol and an aliphatic dicarboxylic acid. その主たる化学構造式は下記一般式(1)及び(2)で表わされる。 Its principal chemical structural formula represented by the following general formula (1) and (2).

【化1】 [Formula 1] このうち、ポリブチレンサクシネートについては、これを主成分とする生分解性樹脂「ビオノーレ」が既に上市されており、製造元である昭和高分子(株)の発行する「TECHNICAL DATA SHEET、ビオノーレ・生分解性プラスチック(1996)」にその概要、性状及び構造などが示されている。 Of these, there are polybutylene succinate, which are biodegradable resins "Bionolle" mainly been marketed a, issues of a manufacturer Showa Kobunshi Co. "TECHNICAL DATA SHEET Copyright, Bionolle & raw As outlined in degradable plastic (1996) ", etc. properties and structure are shown. この脂肪族ポリエステルは、木や紙のように空気中では安定であるが、堆肥中、湿った土中、活性汚泥中、淡水中及び海水中で生分解し、最終的には水と二酸化炭素に分解される。 The aliphatic polyesters are stable in air like wood and paper, compost, moist soil, in the activated sludge, and biodegradable in freshwater and seawater, eventually water and carbon dioxide It is decomposed into.

【0003】従来より使用されている合成樹脂製品は、 [0003] The synthetic resin products that are conventionally used,
軽量かつ安価で加工が容易であるという優れた特性によって、我々の日常生活のあるゆる領域に浸透し、現代の経済社会に必要不可欠な素材となっている。 By excellent properties that are lightweight and inexpensive process is easy, we penetrate into a loose areas of everyday life, it has become an indispensable material in modern economic society. ファスナーにおいてもその例外ではなく、合成樹脂を利用した樹脂ファスナーは、その特徴を活かして様々な製品に利用されている。 Not even an exception in fastener, plastic fasteners utilizing a synthetic resin is used in various products utilizing its features. しかしながら、それらの合成樹脂製品は、使用後に廃棄されると、そのままの形で分解することなく自然環境中に蓄積されるため、自然環境の破壊や汚染といった公害問題を引き起こしつつある。 However, those plastic products is when discarded after use, because they are accumulated in the natural environment without decomposing intact, while causing the pollution problems of destruction and pollution of the natural environment. これに対して、 On the contrary,
実用化例はまだ少ないものの、既存の合成樹脂に代わるものとして、自然環境に与える負荷の小さい生分解性樹脂を使用した製品が登場している。 Although practical example is still small, as an alternative to existing synthetic resins, products using low biodegradable resins load on the natural environment have appeared.

【0004】 [0004]

【発明が解決しようとする課題】しかしながら、前記したような生分解性樹脂をファスナー等の実際の製品として使用するにあたっては、その強度、成形性など解決しなければならない問題が数多くある。 [0007] However, in using a biodegradable resin as mentioned above as an actual product of the fastener, etc., the strength, there are many problems to be solved, such as moldability. ところが、現時点では、これら全ての要件を満足する生分解性樹脂は上市されていない。 However, at this time, the biodegradable resin satisfying all of these requirements have not been marketed. 従って、本発明の目的は、生分解性樹脂にファスナー等としての使用に充分耐えうる強度を付与できる処理法を開発し、もって使用後に廃棄されても自然環境の破壊や汚染といった公害問題を引き起こすことがなく、実用的に充分な機械的性質を保持する生分解性樹脂からなる成形品を提供することにある。 Accordingly, an object of the present invention is to develop a treatment method which can provide sufficient endure strength for use as a biodegradable resin to fasteners like, be disposed of after use with cause pollution problems, such as destruction or pollution of the natural environment it not, is to provide a practically sufficient mechanical properties molded article comprising a biodegradable resin to retain.

【0005】 [0005]

【課題を解決するための手段】前記目的を達成するために、本発明によれば、ポリブチレンサクシネート系及び/又はポリエチレンアジペート系脂肪族ポリエステルを主成分とする生分解性樹脂に澱粉を添加した樹脂材料から作製されてなることを特徴とする生分解性樹脂成形品が提供される。 Means for Solving the Problems] To achieve the above object, added according to the present invention, the polybutylene succinate-based and / or polyethylene adipate aliphatic polyester starch biodegradable resin as a main component biodegradable resin molded article is provided which is characterized in that it consists of a resin material is produced that. 好適には、樹脂材料全重量に対する澱粉の割合は10〜60重量%である。 Preferably, the proportion of starch to resin material the total weight is 10 to 60 wt%. このような生分解性樹脂成形品は、所望の形状に成形することにより各種分野の製品として用いることができるが、充分高い強度を保持するため、特にスライドファスナーや面ファスナーに有利に適用できる。 Such biodegradable resin molded article, can be used as a product of various fields by molding into a desired shape, for retaining a sufficiently high strength it can be particularly advantageously applied to a slide fastener or surface fastener.

【0006】 [0006]

【発明の実施の形態】本発明は、生分解性樹脂であるポリブチレンサクシネート系及び/又はポリエチレンアジペート系脂肪族ポリエステルに、コーンスターチ、片栗粉等の澱粉を添加することにより、ファスナー等としての使用に充分耐えうるように強度を向上させ、より良好な性能を引き出そうとするものである。 DETAILED DESCRIPTION OF THE INVENTION The present invention relates to polybutylene succinate-based and / or polyethylene adipate aliphatic polyester is a biodegradable resin, cornstarch, by adding a starch such as potato starch, for use as fasteners or the like improves strength so that it can sufficiently withstand, it is an attempt to get better performance. なお、従来の合成樹脂の範疇において、この手法はポリマーに充填剤を添加するという技術であり、その技術内容については、 Incidentally, in the category of conventional synthetic resins, this technique is a technique of adding a filler to the polymer, its technical content can
例えば古谷正之「プラスチック材料講座18 塩化ビニル樹脂」日刊工業新聞社発行(1972)に詳しい。 For example Masayuki Furuya "Plastic Material Lecture 18 vinyl chloride resin" familiar with Nikkan Kogyo issued (1972). 本発明者らは、生分解性樹脂をファスナー等へ利用するにあたっての問題点である生分解性樹脂の強度について鋭意研究を進めた結果、生分解性樹脂材料であるポリブチレンサクシネート系及び/又はポリエチレンアジペート系脂肪族ポリエステルに澱粉を添加することにより、生分解性樹脂材料の曲げ強さや曲げ弾性率等が高くなること、また、その強度は澱粉の添加量に依存性のあることを見出した。 The present inventors have made extensive studying the intensity of the biodegradable resin is a problem when using a biodegradable resin to fasteners such as polybutylene succinate-based and biodegradable resin material / or by the addition of polyethylene adipate aliphatic polyester to starch, flexural strength and flexural modulus, etc. of the biodegradable resin is increased, also the intensity found that a dependency on the added amount of starch It was. さらに、前記課題を解決するための処理法・解決法を実験によって確認し、実製品へ適宜応用することで、実際の射出成形ファスナーの強度の強化を果たし、本発明を完成するに至った。 Moreover, the problem was confirmed by experiments treatment-solutions for solving, by applying appropriate to a real product, it plays an enhancement of strength of the actual injection molding fastener, thereby completing the present invention.

【0007】一般に高分子材料においては、微粒度充填剤の添加により引張り強さ、硬さ、曲げ剛性、引裂抵抗が変化する。 [0007] In the general polymeric materials, the tensile strength of the addition of the fineness fillers, stiffness, bending stiffness, tear resistance changes. 例えば、塩化ビニル樹脂への炭酸カルシウムの添加においてこのような現象が見られる(前掲刊行物にも述べられている)。 For example, (also described supra publication) This phenomenon is seen in the addition of calcium carbonate to vinyl chloride resin. ポリブチレンサクシネート系及び/又はポリエチレンアジペート系脂肪族ポリエステルに澱粉を添加した場合、引張り強さがかなり減少し、 If the addition of polybutylene succinate-based and / or polyethylene adipate aliphatic polyester to starch, tensile strength is significantly reduced,
澱粉添加量が全体量の20重量%を超えてからは漸減するが、曲げ強さ及び曲げ弾性率は後述する図16及び図17に示すように増大する。 Starch amount is gradually reduced from more than 20% by weight of the total amount, but flexural strength and flexural modulus increases as shown in FIGS. 16 and 17 described below. その結果、上記生分解性樹脂材料からファスナー製品を成形した場合、或る範囲までは、澱粉の添加量を増加するにつれて、ファスナーの強度も増大することが確認された。 As a result, when molding the fastener product from the biodegradable resin material, to a certain range, with increasing the amount of starch, it was confirmed that the strength of the fastener also increased.

【0008】ファスナーの横引き試験の際に、ファスナーに掛かる力は引張りと圧縮の両方向の力であるが、ファスナーの横引き強度に対しては圧縮強度が支配的である。 [0008] When the lateral pulling test of the fastener, the force applied to the fastener is a bidirectional force tension and compression, for lateral pulling strength of the fastener is a compression strength is dominant. 圧縮強度が低い樹脂を用いたファスナーでは、横引き試験の結果、務歯の噛み合い部分が外れる。 The fastener with compressive strength less resin, the result of the crosscut test, deviates meshing portions of the engaging elements. このような現象をチェーン割れと呼んでいる。 Such a phenomenon is referred to as a chain breaking. 一方、圧縮強度の高い樹脂を用いたファスナーでは、横引き試験の結果、 On the other hand, in the fastener with high compressive strength resins, of crosscut test results,
ファスナーの務歯がテープから外れる。 The engaging element of the fastener is removed from the tape. このような現象を務歯取れという。 Such a phenomenon tooth take that. このことは、曲げ強さを測定することにより、ファスナーの横引き強度と破断状態を評価できることを示している。 This is by measuring the flexural strength, indicating that can evaluate the fracture state lateral pulling strength of the fastener. 実際、後述する図18に示すように、ファスナーの横引き強度は、前記脂肪族ポリエステル単独の場合に比べて澱粉を添加した樹脂材料において高くなっており、特に樹脂材料全重量に対して10〜 In fact, as shown in FIG. 18 to be described later, lateral pulling strength of the fastener, it said has become high in a resin material obtained by adding a starch in comparison with the case of the aliphatic polyester alone, especially 10 to the resin material to the total weight
60重量%の澱粉添加量において高い横引き強度が得られる。 High lateral pulling strength in the starch amount of 60% by weight.

【0009】本発明に用いる生分解性樹脂、ポリブチレンサクシネート系及び/又はポリエチレンアジペート系脂肪族ポリエステルは、公知の方法により製造されたものを特に制限無く使用できる。 [0009] The present invention for use biodegradable resins, polybutylene succinate-based and / or polyethylene adipate-based aliphatic polyesters are those prepared by known methods without particular use restrictions. また、本発明の成形品の製造方法は特定の方法に限定されるものではない。 A method of manufacturing a molded article of the present invention is not intended to be limited to the specific methods. 最も代表的な製造方法を例示すれば、まず、上記脂肪族ポリエステルと澱粉を、脂肪族ポリエステルの多い重量成分比にて、混練装置を用いて約190℃で混練を行う。 To exemplify the most representative production method, first, the aliphatic polyesters and starch, in many cases the weight ratio of components of aliphatic polyesters, perform kneading at about 190 ° C. using a kneading device. 次いで、混練された樹脂を射出成形機によって成形を行うことにより、澱粉部分の粒子が脂肪族ポリエステル媒体中に分散した二相構造からなることを特徴とする、より高強度の生分解性樹脂製射出成形品が容易にかつ再現性良く得られる。 Then, by performing the shaping by the kneaded resin injection molding machine, the particles of the starch portion is characterized by comprising a dispersed two-phase structure in the aliphatic polyester medium, higher strength of the biodegradable resin injection molded article can be obtained easily and reproducibly. 混練温度は上記温度に限られるものではなく、当該樹脂の溶融する温度以上であればその温度で混練すればよい。 The kneading temperature is not limited to the above temperature, it may be kneaded at the temperature as long as temperature or higher to melt of the resin. また両成分の混練方法について、混練装置を用いない、すなわち、両成分をペレット及び粉末の状態にて成形前に混合する方法も採用することができる。 As for the kneading method of the two components, without using a kneading apparatus, i.e., a method of mixing prior to molding both components in pellet and powder form may also be employed.

【0010】本発明の生分解性樹脂成形品は、各種分野に適用可能であるが、充分に高い強度を有するため、スライドファスナーや面ファスナーなどにも有利に用いることができる。 [0010] The biodegradable resin molded article of the present invention is applicable to various fields, because they have a sufficiently high strength, can be advantageously used also like a slide fastener or surface fastener. 以下、添付図面を参照しながら各種ファスナーへの本発明の適用態様を具体的に説明する。 Will be specifically described below apply aspects of the present invention to various fastener with reference to the accompanying drawings. 図1 Figure 1
は、例えば衣服やバッグ等の開口部の開閉に用いられるスライドファスナー1を示しており、左右一対のファスナーストリンガー2の上下端部が切断された製品形態を有する。 It has, for example, illustrates a slide fastener 1 which is used to open and close the opening, such as clothing and bags, with the product form upper and lower ends of the pair of right and left fastener stringers 2 is disconnected. ファスナーストリンガー2は、生分解性樹脂製ファスナーテープ3とそれらの対向する縁部にそれぞれ止着された一列の生分解性樹脂製エレメント(コイル状エレメント)4とから構成されている。 Fastener stringer 2 is composed of a biodegradable resin fastener tape 3 with a row biodegradable resin elements that are fastened respectively to the edges thereof to the opposite (coiled element) 4. ファスナーテープ3は生分解性樹脂繊維を織成及び/又は編成して構成されたもの、もしくは不織布から作製されたもの、あるいは生分解性樹脂製シートからなる。 The fastener tape 3 which the biodegradable resin fibers are constituted by woven and / or knitted, or those made from non-woven fabric, or made of a biodegradable resin sheet. エレメント4としては、個々のエレメントを射出成形すると同時にファスナーテープの縁部に止着する射出タイプや、生分解性樹脂製モノフィラメントをコイル状に巻回してなるコイル状エレメントや平面内に横方向のU字形に屈曲した部分を長手方向に沿って上下交互に連続してジグザグ状に形成したいわゆるジグザグ状エレメントなどの連続状エレメント、押出成形によって長手方向に平行に離隔した2 The element 4, the injection type and the fastening of the individual elements in the edge portion of the same time the fastener tape when injection molding, the lateral coiled element and the plane of the biodegradable resin monofilament formed by winding into a coil continuous-like elements, such as a so-called zigzag elements formed in a zigzag shape successively a portion bent in a U-shape vertically alternately along the longitudinal direction, 2 spaced parallel to the longitudinal direction by extrusion
本の連結紐(芯紐)に個々のエレメントの両端部が連結されてはしご状に成形されたものを長手方向中心線を中心にU字状に折曲した押出成形エレメントなど、種々のタイプのものがある。 Book tether to (the core thread), such as extrusion molding element what both end portions are formed are connected in a ladder shape by bending about the longitudinal center line in a U-shaped individual elements, the various types of there are things. また、例えばコイル状エレメントの場合、さらに芯紐や縫糸が構成部品として加わる。 Further, in the case of coiled element, the further core thread or sewing thread applied as components. 符号5は、対向するエレメント上を摺動して噛合・開離するためのスライダーである。 Reference numeral 5 is a slider for meshing-separable slide on elements opposed.

【0011】図2に示すスライドファスナー1aは、各ファスナーストリンガー2の上端部が切断された形態を有するが、噛み合わされたエレメント4の列の下部所定位置が溶着されて下止部6が形成されている点で図1に示すスライドファスナーとは異なる。 [0011] The slide fastener 1a illustrated in FIG. 2, has a form in which the upper end portion of each fastener stringer 2 is cut, the lower stopper portion 6 under predetermined position of interdigitated rows of elements 4 are welded are formed and in that it is different from the slide fastener illustrated in FIG. 一方、図3に示すスライドファスナー1bは、各ファスナーストリンガー2bのファスナーテープ3bに止着されたエレメント4 On the other hand, the slide fastener 1b is the element 4 which is secured to the fastener tapes 3b of each fastener stringer 2b shown in FIG. 3
bの列の上端部に上止具7が、また下端部に下止具8が止着されている点で図1に示すスライドファスナーと異なる。 Top end stop 7 on the upper end of the column of b is also bottom end stop 8 at the lower end portion is different from the slide fastener illustrated in FIG. 1 in that it is secured.

【0012】図4は開放式のスライドファスナー1cを示している。 [0012] FIG. 4 shows a slide fastener 1c of the open-ended. 各ファスナーストリンガー2cのファスナーテープ3cの下端部にはそれぞれ接着層(図示せず) Each adhesive layer to the lower end portion of the fastener tape 3c of each fastener stringer 2c (not shown)
を介して補強用シート状部材(タフタ)9が溶着されている。 Reinforcing sheet-like members (taffeta) 9 are welded through. これらの対向する補強用シート状部材9の一方の内側縁部には開離嵌挿具10を構成する箱体11が取り付けられ、他方の補強用シート状部材9の内側縁部には蝶棒17が取り付けられている。 One of the box body 11 of the separable bottom end stop 10 on the inner edge of the reinforcing sheet member 9 to these opposing is attached to the inner edge of the other reinforcing sheet-like member 9 the insert pin 17 is attached. 箱体11はその側部のガイド突部13及び箱棒12と一体成形されており、箱棒12とガイド突部13の間にはスライダー5の下端部が滑り込めるように凹溝14が形成されている。 Box body 11 is integrally molded with the guide projection 13 and the box pin 12 in its sides, grooves 14 so Suberikomeru the lower end portion of the slider 5 between the box pin 12 and the guide projection 13 is formed It is. 同様に、一体成形された蝶棒17とその側部のガイド突条1 Similarly, the insert pin 17 which is integrally molded the side guide protrusions 1
8との間にもガイド溝19が形成されている。 Guide groove 19 is also formed between the 8. 箱体11 The box 11
の左側部分には上下方向に貫通された蝶棒挿入孔15が形成されており、この蝶棒挿入孔15の外壁には側溝1 The left portion of which is separable pin insertion hole 15 passing through in the vertical direction is formed, groove 1 in the outer wall of the butterfly rod inserting hole 15
6が形成されている。 6 is formed. 従って、蝶棒17を箱体11の蝶棒挿入孔15に挿入する際、ガイド突条18の下端部内側が箱体11の側溝16の縁部を滑動し、蝶棒17の挿入をガイドするため、円滑に挿入操作を行うことができる。 Therefore, when inserting the insert pin 17 into the insert pin insertion hole 15 of the box body 11, the lower end portion inside the guide protrusion 18 slides the edge of the side groove 16 of the box 11, to guide the insertion of the separable pin 17 Therefore, it is possible to smoothly insert operation. 図4において、符号20はコイル状エレメント4c 4, reference numeral 20 denotes coiled element 4c
の螺旋内空間に長手方向に挿通された芯紐であり、符号21はこれら芯紐20とコイル状エレメント4cをファスナーテープ3cの長手方向縁部に縫着した縫糸である。 Of a core thread inserted through the longitudinal direction in the spiral space, reference numeral 21 is a sewing thread which is sewn to the longitudinal edge of these core thread 20 and the coil-shaped element 4c fastener tape 3c.

【0013】なお、開離嵌挿具としてはスライダー5の構造と同様なものを箱体にし、スライドファスナーの下端より解離したり閉鎖したり出来る、いわゆる逆開放タイプのものが知られており、図4に示すものに限られない。 [0013] As the separable bottom end stop to one similar to the structure of the slider 5 in the box, can or closed or dissociation from the lower end of the slide fastener are known so-called reverse open type, not limited to those shown in FIG. さらにまた、図示の例では開離嵌挿具と別個の補強用シート状部材をファスナーテープの下端部に溶着したものとして説明したが、生分解性樹脂材料からシート状部分を箱体や蝶棒と一体射出成形し、ファスナーテープの幅全体に取り付けたもの、あるいはシート状部分に任意の模様のスリット等を形成して柔軟性を付与したものなど、補強片と開離嵌挿具を一体成形したものがあり、 Furthermore, although in the illustrated example has been described as having been welded to the separable bottom end stop and a separate reinforcing sheet-like members to the lower end portion of the fastener tape, the box and the sheet-like portion from the biodegradable resin separable pin When integrally injection molded, those attached to the entire width of the fastener tape, or sheet-like portion, such as those imparting flexibility to form a slit or the like of any pattern, integrally molded reinforcements and the separable bottom end stop There is a thing that was,
特定のものに限られない。 Not limited to a specific one.

【0014】本発明によれば、前記したファスナーテープ、エレメント、スライダー、上下止具、縫糸、芯紐、 According to the present invention, the above-described fastener tape, the element, the slider, the upper and lower stop members, sewing thread, the core thread,
開離嵌挿具及び補強用シート状部材の全てを前述した本発明の生分解性樹脂から作製することもできるし、あるいは、一部の部材を他の生分解性樹脂や合成樹脂から作製することもできる。 It all separable bottom end stop and reinforcing sheet-like members can also be made from a biodegradable resin of the present invention described above, or to produce a part of the member from the other biodegradable resin or a synthetic resin it is also possible. 樹脂製スライドファスナーを作製する場合、どのような樹脂材料が適するかはスライドファスナーの製品形態や個々の構成部品の構造にも依存する。 Case of preparing a resin slide fastener, what resin material is suitable also depends on the product form and structure of the individual components of the slide fastener. 要求される機能や構造によっては、例えばスライダー自体は他の樹脂や金属から作製することが必要な場合もあり、そのような場合には要求される材料で作製できる。 Depending on the required functions and structures, for example, the slider itself may need to be made from other resin or metal, it can be made of material that is required in such cases. また、前記したようなタイプのスライドファスナーだけでなく、例えばレール状ファスナーなど、他のタイプにも適用できる。 Further, not only the type of slide fastener as described above, for example, rail-like fastener, can also be applied to other types.

【0015】生分解性樹脂製の面ファスナーにおいては、その機能の点からある程度の繰り返し使用によっても充分な係合力を有する耐久性が要求されることになる。 [0015] In the biodegradable resin surface fastener would durability with sufficient engaging force by some repeated use in terms of its function is required. 面ファスナーの係合要素は小さく、あるいは細いものであるため微生物による生分解が比較的に円滑に進行するが、基部はある程度の厚みがあるため生分解が進行し難い。 Engagement element is small surface fastener itself or biodegradation by microorganisms because it is thin object proceeds relatively smoothly, the base biodegradable hardly proceeds because of the certain thickness. 基部を薄くすれば、微生物による生分解は進行し易くなるが、反面、耐久性や強度が低下してしまう。 Thinner base, biodegradation by microorganisms is likely to proceed, the other hand, the durability and strength is lowered.
そこで、好適な態様においては、面ファスナーの少なくとも基部を、その比表面積が大きくなるような断面形状とし、例えば少なくとも基部に溝部及び/又は孔部を形成したり、あるいは基部裏面から係合要素内部にかけて延在する孔部を形成する。 Accordingly, in a preferred embodiment, at least the base portion of the surface fastener, the cross-sectional shape, such as a specific surface area is increased, for example, the internal engagement element at least the base or to form a groove and / or holes in, or from the base back surface subjected to a hole portion extending. なお、ここでいう孔部とは、 Note that the hole here,
貫通孔及び非貫通孔(もしくは凹部)の両態様を含む概念と理解されるべきである。 It should be understood that the concept including both embodiments of the through-holes and blind holes (or recesses). 平板状の基部においては、 In flat base,
その表面を粗面とすることも一つの有効な手段である。 It is also one of effective means for the surface a rough surface.
このように、面ファスナーの基部の比表面積を大きくすることにより、充分な耐久性、強度を確保しつつ、微生物の作用による基部の分解も速やかに進行するようになる。 Thus, by increasing the specific surface area of ​​the base portion of the surface fastener, sufficient durability, while ensuring the strength, degradation of the base by the action of microorganisms so rapidly proceeds. また、基部に溝部及び/又は孔部を形成することにより、基部に柔軟性を与えることができ、従って、基部変形により係合要素間の係合が速やかに行え、係合力の向上も期待できる。 Further, by forming a groove and / or holes in the base, it is possible to give flexibility to the base, therefore, engagement quickly performed between the engaging elements by the base deformation can be expected improvement of the engaging force .

【0016】本発明の面ファスナーの製造は、使用する材料が生分解性樹脂である点を除けば従来公知の種々の方法で行うことができ、またその形態も特定のものに限定されるものではない。 [0016] Production of surface fastener of the present invention are those materials to be used, except a biodegradable resin can be carried out in various known ways and that modes are also limited to a certain type is not. 例えば、雄部材としては、フック状の係合要素、半円球状の頭部を有する係合要素、円錐状の頭部を有する係合要素など種々の形状の係合要素が基部から突設するように生分解性樹脂から一体成形された面ファスナーや、生分解性樹脂繊維の織物又は編物からなる基布に突設したループを切断してフック状にした面ファスナーなど、種々の構造のものが使用でき、また雌部材としても、生分解性樹脂繊維からループを形成するようにパイル状に織編成した物、織物や編物を起毛して表面に多数のループを形成したもの、あるいは不織布など、雄部材の係合要素が係合できるものであれば全て使用可能である。 For example, as the male member, the engaging elements of the hook-shaped engaging element having a head semispherical engaging elements of various shapes such as engagement element having a conical head portion is protruded from the base portion as or surface fastener are integrally molded from the biodegradable resin, and cutting the loops projecting from the base fabric made of woven or knitted fabric of the biodegradable resin fibers such as a surface fastener which is a hook-shaped, those of various structures There can be used, also as a female member, those that weave the pile knitting to form a loop from the biodegradable resin fiber, those that have been formed a number of loops on the surface and brushed fabrics and knitted, or nonwoven fabric, etc. , engaging elements of the male member can be used all as long as it can engage. さらに、係合要素の頭部を両側又は多数方向にフック部が突出した形状とすることによって、これらのフック部が相互に係合することにより、同時に雄部材としても、また雌部材としても機能するように構成した面ファスナーとすることもできる。 Furthermore, by the hook portion of the head of the engaging element on both sides or multiple direction and shape projected by these hook portions are engaged with each other, even as the male member at the same time, also as a female member functions It can be configured with a surface fastener to.

【0017】以下、本発明の生分解性樹脂製面ファスナーの各種態様について図面を参照しながら具体的に説明する。 [0017] will be specifically described with reference to the drawings various aspects of the biodegradable resin surface fastener of the present invention. 図5及び図6は本発明の生分解性樹脂製面ファスナーの第一実施態様を示しており、図5は雄面ファスナー30の斜視図、図6は雄面ファスナー30と雌面ファスナー40の係合状態を示している。 5 and 6 show a first embodiment of the biodegradable resin surface fastener of the present invention, FIG 5 is a perspective view of Yumen fastener 30, FIG. 6 is a Yumen fastener 30 and Mesmin fastener 40 It shows an engagement state. 雄面ファスナー3 Yumen fastener 3
0は、基部31と該基部から突設された多数のフック状の係合要素32とが前記したような生分解性樹脂から一体成形されたものであり、各係合要素32は、基部の長手方向に所定の間隔で列設された補強用のリブ33に跨るように形成されている。 0 is for a base 31 and a number of hook-shaped engaging elements 32 projecting from the base portion is integrally molded from a biodegradable resin such as mentioned above, each engagement element 32, the base of the longitudinally it is formed so as to straddle the rib 33 for reinforcement that is column set at predetermined intervals. また、基部31の裏面には、 Further, on the rear surface of the base 31,
微生物の作用による分解が速やかに進行するように、また適度の柔軟性と強度を保持するように、長手方向に延在する溝部(縦溝)34が形成されており、それによって各溝部34の間に縦リブ35が形成されている。 To proceed decomposition rapidly by the action of microorganisms, and as to hold the appropriate flexibility and strength, the groove portion (longitudinal grooves) 34 extending in the longitudinal direction is formed, whereby the respective groove portions 34 vertical ribs 35 are formed between. この雄面ファスナー30は、生分解性樹脂の繊維から織成又は編成された基部41の表面に多数のループ状の係合要素42が突設された雌面ファスナー40と、図6に示すようにフック状の係合要素32がループ状の係合要素4 The Yumen fastener 30 includes a female surface fastener 40 which many loop-shaped engaging elements 42 on the surface of the base 41 from the fiber of the biodegradable resin is woven or knitted is projected, as shown in FIG. 6 engagement element hook-shaped engaging elements 32 is looped 4
2に引っ掛かることによって係合する。 Engagement by being caught in 2.

【0018】図7及び図8は本発明の生分解性樹脂製面ファスナーの第二実施態様を示し、図7は雄面ファスナー30aの斜視図、図8は雄面ファスナー30aと雌面ファスナー40の係合状態を示している。 [0018] Figures 7 and 8 show a second embodiment of the biodegradable resin surface fastener of the present invention, FIG. 7 is a perspective view of Yumen fasteners 30a, Figure 8 is Yumen fastener 30a and Mesmin fastener 40 It shows the engagement state. 本実施態様の雄面ファスナー30aは、係合要素としてフック状先端が逆向きの一対の隣接するフック片36,37からなる係合要素32aが基部31a上に突設されている点、補強リブ33aが各係合要素32aの基端部のみに断続的に形成されている点、及び横方向への曲げを確保するために基部31aの裏面に横方向の溝部(横溝)34aが形成されている点において、前記第一実施態様とは異なる。 Yumen fastener 30a of this embodiment are that engagement element 32a consisting of hooks 36 and 37 hook-shaped tip is a pair of adjacent opposite as an engaging element is projected on the base 31a, the reinforcing ribs point 33a is intermittently formed only on the base end portion of the engagement elements 32a, and lateral grooves on the rear surface of the base portion 31a in order to ensure the bending in the lateral direction (lateral groove) 34a is formed in that there, different from the first embodiment. なお、雌面ファスナー40の構成は前記第一実施態様の場合と同じである。 The configuration of the Mesmin fasteners 40 are the same as in the first embodiment. 前記のような生分解性樹脂製雄面ファスナーは、例えば米国特許第3312583号明細書、特開平6−38811号に記載の成形装置に適当な設計変更(例えば、ダイへの溝成形用突部の付加、溝成形用ロールの追加等)を加えることにより製造することができる。 Biodegradable resin Yumen fastener as described above, for example U.S. Pat. No. 3312583, appropriate design change in the molding apparatus described in JP-A-6-38811 (e.g., groove forming projections to the die additions, can be prepared by adding an additional, etc.) of the roll groove molding.

【0019】図9及び図10は、本発明の生分解性樹脂製面ファスナーの第三実施態様を示しており、雌雄同一タイプの片状の面ファスナー30bを示している。 [0019] FIGS. 9 and 10 show a third embodiment of the biodegradable resin surface fastener of the present invention shows a strip-shaped surface fastener 30b of the male and female same type. この面ファスナー30bは、基部31bと多数の係合要素3 The surface fastener 30b includes a base 31b and a number of engaging elements 3
2bが生分解性樹脂から一体成形されている点は前記実施態様と同様であるが、係合要素32bが両側に弧状に突出された一対のフック片36b,37bからなる頭部を有し、また、該係合要素32bの接合箇所において基部31b上面に長手方向の溝部34bが多数形成されていると共に、該溝部34bの係合要素32b両側部に孔部38bが形成されている点において異なる。 2b is but the point which is integrally molded from the biodegradable resin is similar to the previous embodiment, a pair of hooks 36b for engaging element 32b is protruded in an arc on either side, it has a head portion consisting of 37b, also, different base 31b upper surface in the joint of the engaging element 32b with the longitudinal direction of the groove portion 34b are formed a large number, in that the hole portion 38b in the engaging element 32b both sides of the groove portion 34b is formed . このような溝部34b及び孔部38bを面ファスナー30bの基部31bに形成することによって、微生物による分解作用を早めることができると共に、面ファスナーに適度の柔軟性と強度を付与することができる。 By forming such a groove portion 34b and the hole 38b in the base 31b of the surface fastener 30b, it is possible to hasten the decomposition by microorganisms, it is possible to impart appropriate flexibility and strength to the surface fastener. この面ファスナー30bは、両側に突出する一対のフック片36b,3 The surface fastener 30b has a pair of hooks 36b that protrude on both sides, 3
7bとからなる多数の係合要素32bを有するので、双方の係合要素が向き合うように重ね合わせることにより、一方の面ファスナーのフック片が他方の面ファスナーのフック片に係合できる。 Since having a number of engaging elements 32b consisting of 7b, by superimposing so that both of the engaging elements facing, hooks on one surface fastener can engage the hook pieces of the other surface fastener. なお、本実施態様の面ファスナー30bの場合、所定形状のキャビティ面を有する上型と下型のキャビティ内に生分解樹脂を射出することにより成形できる。 In the case of the surface fastener 30b of this embodiment can be molded by injecting the biodegradable resin into the upper mold and the lower mold cavity having a cavity surface of a predetermined shape. また、前記した実施態様と異なり、 Further, unlike the above-described embodiment,
所定面積の片状(ワンピース物)に成形されるので、広い面積に用いる場合には多数の面ファスナー30bを相隣接するように配列して用いる。 Because it is formed into a predetermined area of ​​the flake (One Piece thereof) when used in large area used by arranging such that adjacent to each of the plurality of surface fastener 30b.

【0020】図11及び図12は本発明の生分解性樹脂製雄面ファスナーの第四実施態様を示しており、生分解性樹脂でモノフィラメント又はマルチフィラメントを作製し、これを織成して作製した面ファスナーを示している。 [0020] FIGS. 11 and 12 shows a fourth embodiment of the biodegradable resin Yumen fastener of the present invention to prepare monofilament or multifilament with a biodegradable resin, the surface was produced by weaving this It shows the fastener. 図11に示す雌面ファスナー40aにおいては、生分解性樹脂フィラメントからなるパイル糸が同様に生分解性樹脂フィラメントから平織りされた基部(基布)4 In the female surface fastener 40a shown in FIG. 11, the base of the pile yarn made of biodegradable resin filaments are plain weave of biodegradable resin filaments as well (base fabric) 4
1aにパイル状に織り込まれてループ状の雌係合要素4 Female engaging element loop woven into pile-like to 1a 4
2aが基部表面から突出するように形成されている。 2a is formed so as to protrude from the base surface. 一方、図12に示す雄面ファスナー30cは、ループの一部を切断してフック状係合要素32cが形成されていること以外は上記雌面ファスナーと同様な構造を有する。 On the other hand, Yumen fastener 30c shown in FIG. 12, except that by cutting a part of the loop is formed with hook-like engaging element 32c has the same structure as the female surface fastener.
なお、図12に示す面ファスナーは雌雄同一タイプの面ファスナーとして用いることもできる。 The surface fastener shown in FIG. 12 can also be used as male and female same type of surface fastener. また、雌面ファスナー40a及び雄面ファスナー30cの裏面には、ほつれ防止のために水溶性樹脂又は生分解性樹脂のバックコート45が施されている。 Further, on the back surface of the Mesmin fasteners 40a and Yumen fastener 30c, the back coat 45 of the water-soluble resin or biodegradable resin is applied to the fraying prevention. なお、このバックコート4 It should be noted that the back coat 4
5に水溶性樹脂を用いることにより、このバックコート45は水で湿らせることによって接着層として機能する。 By using a water-soluble resin 5, the back coat 45 functions as an adhesive layer by moistening with water. また、このような面ファスナー30c,40aが廃棄されても、生分解性樹脂から作製されている部分(3 Moreover, such a surface fastener 30c, even 40a is discarded, the portion being made of a biodegradable resin (3
1c,32c,41a,42a)は微生物の作用によって分解されるし、また水溶性樹脂から作製されているバックコート45の部分は雨水等によって溶解して消失してしまうので、廃棄物公害の問題を生ずることはない。 1c, 32c, 41a, 42a) is to be decomposed by the action of microorganisms, also the portion of the back coat 45 is manufactured from a water-soluble resin disappears by dissolving by rainwater, waste pollution It does not produce.
しかも水溶性樹脂のバックコート45が溶解して消失することにより、基部(基布)31c,41aは多数の空隙を有する生分解性樹脂フィラメントの織物生地となるので、微生物による分解作用も速やかに進行する。 Moreover by backcoat 45 of the water-soluble resin is lost by dissolving the base (base fabric) 31c, so 41a becomes woven fabric biodegradable resin filaments having numerous voids, decomposition by microorganisms promptly proceed.

【0021】図13及び図14は本発明の生分解性樹脂製面ファスナーの第五実施態様を示し、水溶性樹脂の溶媒中への溶出によって面ファスナーの基部に孔部及び溝部を形成する方法の一例を示している。 [0021] FIGS. 13 and 14 show a fifth embodiment of the biodegradable resin surface fastener of the present invention, a method of forming a hole and the groove at the base of the surface fastener by elution of the water-soluble resin in a solvent It shows an example of. なお、雄面ファスナー30dの係合要素32dの形状は図7に示す実施態様と同様である。 The shape of the engagement elements 32d of Yumen fastener 30d is similar to the embodiment shown in FIG. この場合、雄面ファスナー30dの係合要素32d及び基部31dの一部を生分解性樹脂により、基部の孔部及び溝部となる部分を水溶性樹脂46 In this case, by partially biodegradable resin engaging elements 32d and the base 31d of Yumen fastener 30d, partially water-soluble resin as a hole portion and the groove portion of the base portion 46
により成形した後、これを水、アルコール水溶液等の溶媒中に浸漬して水溶性樹脂46を溶出させることにより、図14に示すような基部31dに孔部38d及び溝部34dが形成された雄面ファスナー30dが得られる。 Yumen after molding, this water, by eluting the water-soluble resin 46 is immersed in a solvent such as an alcohol aqueous solution, the holes 38d and the groove 34d is formed in the base 31d, as shown in FIG. 14 by fastener 30d can be obtained. なお、図13に示すように基部31d裏面に水溶性樹脂46が積層された状態の雄面ファスナー30dをそのまま使用することもできる。 It is also possible to keep the Yumen fastener 30d in a state where the water-soluble resin 46 is laminated to the base 31d back surface as shown in FIG. 13. この場合、水溶性樹脂4 In this case, the water-soluble resin 4
6を水で湿らせることによって接着層として機能する。 6 functions as a bonding layer by moistening with water.
また、このような雄面ファスナー30dが廃棄されても、雨水等によって水溶性樹脂46は溶解、消失し、それによって生分解性樹脂からなる雄面ファスナー30d Further, Yumen fastener 30d be discarded such Yumen fastener 30d is, the water-soluble resin 46 is dissolved, disappeared by rainwater, consisting whereby biodegradable resin
には孔部38d及び溝部34dが形成されるので、微生物による分解作用も速やかに進行する。 Since the hole portion 38d and the groove 34d is formed in, also it proceeds rapidly decomposing action of microorganisms. 上記図13に示すような雄面ファスナー30dの成形は、予め孔部及び溝部に対応する凸部が形成された水溶性樹脂フィルムを、生分解性樹脂から成形された半溶融状態の雄面ファスナーの裏面に圧着することにより形成することもできる。 The molding of Yumen fastener 30d, as shown in Figure 13, pre-hole and a water-soluble resin film protrusion which is formed corresponding to the groove, Yumen fastener semi-molten state that is molded from a biodegradable resin It can also be formed by crimping the rear surface.

【0022】図15は、本発明の生分解性樹脂製雄面ファスナーの第六実施態様を示している。 FIG. 15 shows a sixth embodiment of the biodegradable resin Yumen fastener of the present invention. この実施態様の雄面ファスナー30eは、基部31eから係合要素32 Yumen fastener 30e of this embodiment, the engagement from the base 31e elements 32
eにかけて延在する孔部38eを有しており、さらに高い柔軟性を有し、また微生物による分解速度も高くなる。 Has a hole 38e extending toward e, further comprising a flexible, also increases the decomposition rate by microorganisms. このような孔部38eの形成は、例えば、成形された直後の半溶融状態又は軟化状態にある雄面ファスナー30eに、上記孔部38eの形状に対応する鋭角な突部を予め形成した水溶性樹脂フィルムを上記突部が埋入されるように圧着してラミネートし、その後、雄面ファスナーが冷却、固化された後、水溶性樹脂フィルムを適当な溶媒中に溶出させることによって行うことができる。 The formation of such holes 38e, for example, the Yumen fastener 30e in the semi-molten state or softened state immediately after being molded, preformed water soluble sharp projections corresponding to the shape of the hole portion 38e the resin film was laminated and pressed so that the protrusion is embedded, then, after the Yumen fasteners cooled and solidified, it can be carried out by eluting the water-soluble resin film in a suitable solvent .
また、前記したような孔部及び/又は溝部の形成方法の別の例として、予め孔部及び/又は溝部に対応する突部及び/又は突条が形成された水溶性樹脂フィルムを下型のキャビティ内に配置し、この水溶性樹脂フィルムを下型のキャビティ面として利用して生分解性樹脂から面ファスナーを成形する方法も採用することができる。 Another example of the hole portion and / or the groove forming method as described above, the pre-holes and / or projections corresponding to the grooves and / or ridges are formed water-soluble resin film lower die was placed in the cavity, a method for molding the surface fastener of a biodegradable resin by utilizing the water-soluble resin film as a lower die cavity surface can be adopted.

【0023】前記溝部及び/又は孔部の形成に、又は接着層として用いられる水溶性樹脂としては、水酸基、カルボキシル基、スルホン基等の親水性基を有する水溶性であって、成形性を有するものであれば使用可能であり、例えばポリビニルアルコール、変性ポリビニルアルコール、ポリアクリル酸、ポリエチレンオキサイド、C [0023] formation of the grooves and / or holes, or as a water-soluble resin used as the adhesive layer, a hydroxyl group, a carboxyl group, a water-soluble having a hydrophilic group such as a sulfonic group, having formability may be used as long as, for example, polyvinyl alcohol, modified polyvinyl alcohol, polyacrylic acid, polyethylene oxide, C
MC、ガム等が挙げられるが、これらの中でも変性ポリビニルアルコール(例えば日本合成化学工業(株)製エコマティAX(ビニルアルコール−アリルアルコール共重合物へのポリオキシアルキレンのグラフト物)を好適に用いることができる。 MC, although gums and the like, even modified polyvinyl alcohol (e.g., Nippon Synthetic Chemical Industry Co., Ltd. Ekomati AX (vinyl alcohol among these - graft of a polyoxyalkylene to allyl alcohol copolymer) preferably used to can.

【0024】また、必要に応じて本発明に係る生分解性樹脂と組み合わせて用いることができる他の生分解性樹脂としては、成形性と適度の柔軟性及び硬度を有し、微生物の作用により崩壊し得る樹脂であれば使用可能であり、例えばゼネカ(株)製バイオポール(ヒドロキシ酪酸とヒドロキシ吉草酸の共重合体)等の微生物発酵生産型樹脂、日本合成化学工業(株)製マタービー、アメリカ、ワーナー・ランバード社製ノボン等の天然高分子(澱粉)系樹脂、ダイセル化学工業(株)製プラクセル(ポリカプロラクトン)等の化学合成型樹脂、(株)島津製作所製ラクティ等のポリ乳酸などが挙げられる。 [0024] As another biodegradable resin which can be used in combination with a biodegradable resin according to the present invention optionally has a proper flexibility and hardness and moldability, by the action of microorganisms disintegration may be used as long as you can resins, for example, Zeneca Co. Biopol (a copolymer of hydroxybutyric acid and hydroxyvaleric acid) microbial fermentation production type resins such as Nippon Synthetic Chemical Industry Co. Matabi, USA, natural polymer (starch) systems such as Warner-Lambert Co. Nobon resin, manufactured by Daicel chemical Industries, Ltd. Placcel (polycaprolactone) chemical synthesis type resin such as, manufactured by Shimadzu Corporation Lacty etc. polylactic acid and the like.

【0025】 [0025]

【実施例】以下に本発明の効果について具体的に確認した実施例を示すが、本発明が下記実施例に限定されるものでないことはもとよりである。 EXAMPLES show embodiments specifically confirmed the effect of the present invention below, that the invention is not limited to the following Examples are well.

【0026】実施例1 原料としては市販の生分解性樹脂と澱粉を用いた。 [0026] As Example 1 starting material used was a commercially available biodegradable resin and starch. 本実施例においては、ポリブチレンサクシネートとして昭和高分子(株)製の脂肪族ポリエステル系生分解性樹脂である「ビオノーレ」#S1005を、また、澱粉として日本食品工業(株)製のコーンスターチである「COR In this embodiment, a Showa Kobunshi Co., Ltd. aliphatic polyester type biodegradable resin as polybutylene succinate the "Bionolle" # S1005, also in Japan Food Industry Co., Ltd. of cornstarch as a starch a "COR
N BOY」をそれぞれ使用した。 N BOY "was used, respectively. まず、これらの材料を減圧下80℃にて24時間乾燥した。 First, and dried 24 hours these materials under reduced pressure at 80 ° C.. 両材料を重量比でビオノーレ/コーンスターチ=90/10、70/3 Bionolle / cornstarch both materials in a weight ratio = 90/10, 70/3
0、50/50、40/60となるように計量し、混練装置へ投入した。 Were weighed so as to 0,50 / 50, 40/60, it was charged to the kneading apparatus. 混練温度190℃、ミキサー回転数6 Kneading temperature 190 ° C., the mixer rotation speed 6
0r/min及び混練時間12分にて混練後、表1に示す樹脂a(90/10)、b(70/30)、c(50 After kneaded 0r / min and kneading time 12 minutes, the resin a (90/10) shown in Table 1, b (70/30), c (50
/50)、d(40/60)を得た。 / 50) to obtain d (40/60). なお、樹脂eはビオノーレ#S1005単体である。 The resin e is BIONOLLE # S1005 alone. 上記の方法で調製した各樹脂a、b、c、d及びeを、厚さ3mmの板にプレス成形し、それぞれ曲げ強さ及び曲げ弾性率を測定した。 Each resin a was prepared by the method described above, b, c, d and e, then press-molded into a plate having a thickness of 3 mm, were respectively measured flexural strength and flexural modulus. その結果を下記表1並びに図16及び図17に示す。 The results are shown in Table 1 and Figures 16 and 17. これらの結果から、澱粉の添加量が増すにつれて曲げ強さ及び曲げ弾性率が増大することが分かる。 From these results, it is seen that flexural strength and flexural modulus as the added amount of starch is increased to increase.

【0027】さらに各樹脂a、b、c、d及びeについて、射出成形機にて5VS規格の射出ファスナーを成形し、各ファスナー成形品A、B、C、D及びEを得た。 Furthermore the resins a, b, c, the d and e, by molding the injection fastener 5VS standards by injection molding machine to obtain each fastener molded article A, B, C, D and E.
成形品A、B、C、D及びEのそれぞれについて横引き強度の測定を行った。 Molded article A, went B, C, the measurement of the lateral pulling strength for each of the D and E. その結果を下記表1及び図18に示す。 The results are shown in Table 1 and Figure 18. なお、横引き強度は図19に示すように測定した。 Incidentally, lateral pulling strength was measured as shown in Figure 19. すなわち、務歯4dを噛み合わせたファスナーチェーン2dの状態で、チェーン噛み合い方向に対して図1 That is, FIG. 1 in the state of the fastener chain 2d which engage the coupling element 4d, relative to the chain meshing direction
9のように一定速度(300mm/分)で、引張試験機を利用してファスナーテープ3dを引張り抵抗を測定する。 At a constant rate (300 mm / min) as 9, by using a tensile tester for measuring the tensile resistance fastener tape 3d. なお、クランプ50の幅は25mmである。 The width of the clamp 50 is 25 mm. 表1及び図18に示す結果から、澱粉の添加によりファスナーの横引き強度が大きくなることが分かる。 From the results shown in Table 1 and FIG. 18, lateral pulling strength of the fastener it is can be seen that significantly by the addition of starch. また、樹脂材料全重量に対するコーンスターチの量が10〜50重量%において、5VSのJIS規格に定める25kgf/ Further, in the 10 to 50% by weight the amount of the corn starch to the resin material to the total weight, defined in 5VS JIS standard 25 kgf /
25mmの横引き強度を上回る値を示し、特にコーンスターチの量が30重量%付近において強度は最も大きくなることが確認された。 Shows a value greater than the lateral pulling strength of 25 mm, in particular quantities strength in the vicinity of 30% by weight of corn starch was confirmed that the largest.

【表1】 [Table 1]

【0028】 [0028]

【発明の効果】以上のように、本発明によれば、澱粉部分の粒子がポリブチレンサクシネート系及び/又はポリエチレンアジペート系脂肪族ポリエステル中に分散した二相構造を有し、実用的に充分に高い強度を有する生分解性樹脂成形品が提供され、スライドファスナー、面ファスナーなど、各種分野の製品として利用可能である。 As is evident from the foregoing description, according to the present invention has a dispersed two phase structure particles polybutylene succinate-based partial starch and / or polyethylene adipate-based aliphatic polyesters, practically sufficient biodegradable resin molded article having a high strength is provided in the slide fastener, such as a surface fastener, is available as a product of various fields.
しかも、このような生分解性樹脂成形品を成形性良く製造できる。 Moreover, such a biodegradable resin molded article molded with good can be produced. また、本発明の生分解性樹脂成形品は、生分解性樹脂であるポリブチレンサクシネート系及び/又はポリエチレンアジペート系脂肪族ポリエステルと、生分解される天然高分子化合物である澱粉とからなるため、 Also, the biodegradable resin molded article of the present invention, a polybutylene succinate-based and / or polyethylene adipate aliphatic polyester is a biodegradable resin, to become the starch is a natural polymer compound biodegraded ,
廃棄されても土中や水中の微生物により分解されるため、地球環境の破壊や廃棄物公害を引き起こすことはない。 Because be discarded is decomposed by microorganisms in soil or water, it does not cause destruction and waste pollution of the global environment. しかも、生分解性樹脂製の製品は、コンポスト(堆肥)にして大地に還元されるので、通常のプラスチック製品のような散乱ゴミになって野生動物への危害となる恐れもなく、また、分解して嵩が減少するので埋立地の延命化や安定化にも役立つ。 Moreover, biodegradable plastic products, since it is reduced to the ground in the compost (compost), there is no fear that the harm to wild animals become scattering garbage, such as a conventional plastic products, also, decomposition also help in extended life and stabilization of the landfill because the bulk is reduced to. さらに、これらの製品が焼却処分されても、生分解性樹脂は焼却時の発熱量が少ないため、焼却炉を損傷する危険性も減少する。 Moreover, these products be incinerated, the biodegradable resin because small amount of heat generated during incineration, also reduces the risk of damaging the incinerator. さらに、 further,
本発明を適用した生分解性面ファスナーは、例えば生分解性樹脂や水溶性樹脂から作製された結束バンドや苗木カバー、エノキ茸育苗カバー、おむつなど各種使い捨て製品の連結具として好適に用いることができる。 Biodegradable surface fastener according to the present invention, for example, biodegradable resin and a binding band and seedlings cover made from a water-soluble resin, enoki mushroom nursery cover, be suitably used as a connector for various disposable products such as diapers it can.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】生分解性樹脂製スライドファスナーの一態様を示す平面図である。 1 is a plan view illustrating one embodiment of a biodegradable resin slide fastener.

【図2】生分解性樹脂製スライドファスナーの他の態様を示す平面図である。 2 is a plan view showing another embodiment of the biodegradable resin slide fastener.

【図3】生分解性樹脂製スライドファスナーのさらに他の態様を示す平面図である。 3 is a plan view showing still another embodiment of the biodegradable resin slide fastener.

【図4】生分解性樹脂製スライドファスナーの別の態様を示す部分破断平面図である。 4 is a partially cutaway plan view showing another embodiment of the biodegradable resin slide fastener.

【図5】生分解性樹脂製雄面ファスナーの第一実施態様の部分斜視図である。 5 is a partial perspective view of a first embodiment of the biodegradable resin Yumen fasteners.

【図6】図5に示す生分解性樹脂製雄面ファスナーと生分解性樹脂製雌面ファスナーの係合状態を示す部分断面図であり、雄面ファスナーは図5のA−A線矢視方向の断面を示す。 Figure 6 is a partial sectional view showing an engagement state of the biodegradable resin Yumen fastener biodegradable resin female surface fastener shown in FIG. 5, A-A taken along the line of Yumen fastener 5 It indicates the direction of the cross section.

【図7】生分解性樹脂製雄面ファスナーの第二実施態様の部分斜視図である。 7 is a partial perspective view of a second embodiment of the biodegradable resin Yumen fasteners.

【図8】図7に示す生分解性樹脂製雄面ファスナーと生分解性樹脂製雌面ファスナーの係合状態を示す部分断面図であり、雄面ファスナーは図7のB−B線矢視方向の断面を示す。 Figure 8 is a partial sectional view showing an engagement state of the biodegradable resin Yumen fastener biodegradable resin female surface fastener shown in FIG. 7, Yumen fastener view taken along line B-B in FIG. 7 It indicates the direction of the cross section.

【図9】生分解性樹脂製面ファスナーの第三実施態様の斜視図である。 9 is a perspective view of a third embodiment of the biodegradable resin surface fastener.

【図10】図9に示す生分解性樹脂製面ファスナーの係合方法を示す部分破断側面図である。 10 is a partial cutaway side view showing the engagement process of the biodegradable resin surface fastener shown in FIG.

【図11】第四実施態様の生分解性樹脂製雌面ファスナーの部分断面図である。 11 is a partial cross-sectional view of the biodegradable resin female surface fastener of the fourth embodiment.

【図12】第四実施態様の生分解性樹脂製雄面ファスナーの部分断面図である。 12 is a partial cross-sectional view of the biodegradable resin Yumen fastener fourth embodiment.

【図13】生分解性樹脂製雄面ファスナーの第五実施態様の基部裏面に水溶性樹脂をラミネートした状態を示す部分断面図である。 13 is a partial cross-sectional view showing a state in which by laminating a water-soluble resin on the base back surface of the fifth embodiment of the biodegradable resin Yumen fasteners.

【図14】生分解性樹脂製雄面ファスナーの第五実施態様を示す部分断面図である。 14 is a partial cross-sectional view showing a fifth embodiment of the biodegradable resin Yumen fasteners.

【図15】生分解性樹脂製雄面ファスナーの第六実施態様の部分断面図である。 15 is a partial cross-sectional view of a sixth embodiment of the biodegradable resin Yumen fasteners.

【図16】ポリブチレンサクシネート(ビオノーレ#S [16] Polybutylene succinate (Bionolle #S
1005)/澱粉の各種混合比の樹脂の曲げ強さを示すグラフである。 1005) is a graph showing the bending strength of the resin of various mixing ratios / starch.

【図17】ポリブチレンサクシネート(ビオノーレ#S [17] Polybutylene succinate (Bionolle #S
1005)/澱粉の各種混合比の樹脂の曲げ弾性率を示すグラフである。 1005) is a graph showing the flexural modulus of the resin of various mixing ratios / starch.

【図18】ポリブチレンサクシネート(ビオノーレ#S [18] Polybutylene succinate (Bionolle #S
1005)/澱粉の各種混合比の樹脂から成形したスライドファスナーの横引き強度を示すグラフである。 1005) is a graph showing the lateral pulling strength of the molded slide fastener of a resin / starch various mixing ratios.

【図19】実施例1における横引き強度の測定方法を示す概略図である。 19 is a schematic diagram showing a method of measuring the lateral pulling strength in the first embodiment.

【符号の説明】 DESCRIPTION OF SYMBOLS

1,1a,1b,1c スライドファスナー 2,2b,2c,2d ファスナーチェーン 3,3b,3c,3d ファスナーテープ 4,4b,4c,4d エレメント 5 スライダー 6 下止部 7 上止具 8 下止具 9 補強用シート状部材 10 開離嵌挿具 30,30a,30b,30c,30d,30e 雄面ファスナー 31,31a,31b,31c,31d,31e,4 1, 1a, 1b, 1c slide fastener 2 and 2b, 2c, 2d fastener chain 3, 3b, 3c, 3d fastener tape 4, 4b, 4c, 4d element 5 slider 6 bottom end portion 7 top end stop 8 bottom end stop 9 reinforcing sheet-like members 10 separable bottom end stop 30,30a, 30b, 30c, 30d, 30e Yumen fastener 31,31a, 31b, 31c, 31d, 31e, 4
1,41a 基部 34,34a,34b,34d 溝部 38b,38d,38e 孔部 40,40a 雌面ファスナー 6 下止部 7 上止具 8 下止具 9 補強用シート状部材 10 開離嵌挿具 30,30a,30b,30c,30d,30e 雄面ファスナー 31,31a,31b,31c,31d,31e,4 1,41a base 34, 34a, 34b, 34d grooves 38b, 38d, 38e holes 40,40a Mesmin fastener 6 bottom end portion 7 top end stop 8 bottom end stop 9 reinforcing sheet-like members 10 separable bottom end stop 30 , 30a, 30b, 30c, 30d, 30e Yumen fastener 31,31a, 31b, 31c, 31d, 31e, 4
1,41a 基部 32,32a,32b,32c,32d,32e フック状係合要素 34,34a,34b,34d 溝部 38b,38d,38e 孔部 40,40a 雌面ファスナー 1,41a base 32,32a, 32b, 32c, 32d, 32e hook-shaped engaging elements 34, 34a, 34b, 34d grooves 38b, 38d, 38e holes 40,40a Mesmin fastener

Claims (4)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 ポリブチレンサクシネート系及び/又はポリエチレンアジペート系脂肪族ポリエステルを主成分とする生分解性樹脂に澱粉を添加した樹脂材料から作製されてなることを特徴とする生分解性樹脂成形品。 [Claim 1], characterized by comprising made from polybutylene succinate-based and / or polyethylene adipate-based resin material obtained by adding starch to the biodegradable resin as a main component an aliphatic polyester biodegradable resin molded goods.
  2. 【請求項2】 樹脂材料全重量に対する澱粉の割合が1 Ratio of 2. A resin material starch to the total weight 1
    0〜60重量%であることを特徴とする請求項1に記載の成形品。 The molded article according to claim 1, characterized in that 0 to 60% by weight.
  3. 【請求項3】 成形品がスライドファスナーである請求項1又は2に記載の成形品。 3. A molded article according to claim 1 or 2 molded article is a slide fastener.
  4. 【請求項4】 成形品が面ファスナーである請求項1又は2に記載の成形品。 4. A molded article according to claim 1 or 2 molded article is a surface fastener.
JP36617597A 1997-12-25 1997-12-25 Biodegradable resin molded product Pending JPH11181261A (en)