JPH11129426A - Decorative sheet - Google Patents

Decorative sheet

Info

Publication number
JPH11129426A
JPH11129426A JP30009697A JP30009697A JPH11129426A JP H11129426 A JPH11129426 A JP H11129426A JP 30009697 A JP30009697 A JP 30009697A JP 30009697 A JP30009697 A JP 30009697A JP H11129426 A JPH11129426 A JP H11129426A
Authority
JP
Japan
Prior art keywords
sheet
decorative sheet
decorative
layer
surface
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP30009697A
Other languages
Japanese (ja)
Inventor
Keishi Hanamoto
Kahori Miyashita
香保里 宮下
恵嗣 花本
Original Assignee
Dainippon Printing Co Ltd
大日本印刷株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dainippon Printing Co Ltd, 大日本印刷株式会社 filed Critical Dainippon Printing Co Ltd
Priority to JP30009697A priority Critical patent/JPH11129426A/en
Publication of JPH11129426A publication Critical patent/JPH11129426A/en
Application status is Pending legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide a new decorative sheet which shows proper weatherability and molding/working properties required for the decorative sheet and is naturally perishable when it is discarded as a waste and left alone.
SOLUTION: The decorative sheet S is a decoratively treated base material sheet 1 made up of a polylactic acid resin sheet composed mainly of poly-L- lactic acid, or the decoratively treated base sheet 1 on which a surface protecting layer 7 is laminated. The base material sheet 1 is degraded completely into water and carbonic acid gas by the activity of bacteria in the soil, so that the sheet 1 is friendly to global environments.
COPYRIGHT: (C)1999,JPO

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、内装材を始めとして各種の装飾に使用される化粧シートに関するものである。 BACKGROUND OF THE INVENTION The present invention relates to a decorative sheet that is used in a variety of decorations including the interior material.

【0002】 [0002]

【従来の技術】従来、この種の化粧シートとしては、ポリ塩化ビニル系樹脂からなるシートを利用したものが主に用いられてきた。 Conventionally, as this type of decorative sheet, which utilizes a sheet made of polyvinyl chloride resin it has been mainly used. このポリ塩化ビニル系のシートは印刷適正、エンボス加工適正に優れ、化粧シートに加工しやすいだけでなく、Vカット、ラッピング等の後加工性にも優れており、さらに安価であるという利点がある。 The poly vinyl sheets chloride printability, embossed properly superior not only easily processed into decorative sheet, V-cut, is excellent in workability after lapping or the like, the advantage of being less expensive .
しかしながら、このタイプの化粧シートは、耐熱性が不足するとか、可塑剤のブリードにより表面の耐汚染性が悪いと言う欠点がある。 However, this type of decorative sheet has a drawback referred Toka insufficient heat resistance and poor stain resistance of the surface by bleeding of the plasticizer. そこで、最近では、ポリ塩化ビニル系樹脂に代わる素材としてスチレン系、オレフィン系、ウレタン系、ポリアミド系、エステル系等の熱可塑性エラストマーやEVA(エチレンビニルアルコール共重合体)、PET(ポリエチレンテレフタレート)、アクリル樹脂を用いた化粧シートが各種提案されている。 Therefore, recently, poly styrene as a material in place of the vinyl chloride resin, olefin-based, urethane-based, polyamide-based, thermoplastic ester, such as elastomers and EVA (ethylene-vinyl alcohol copolymer), PET (polyethylene terephthalate), decorative sheet using an acrylic resin have been proposed.

【0003】 [0003]

【発明が解決しようとする課題】ところで、上記したいずれの素材を使用した化粧シートも、廃棄処分した際に樹脂がそのままゴミとして永久に残ってしまい、自然環境保護の観点から好ましくないという問題点がある。 The object of the invention is to be Solved by the way, also a decorative sheet using any of the materials described above, will remain forever as it is as a waste resin is when you waste disposal, a problem that is not preferable from the point of view of the natural environment protection point there is.

【0004】本発明は、上記のような問題点に鑑みてなされたものであり、その目的とするところは、化粧シートに必要な耐候性、成形加工適正があり、しかも廃棄処分して放置しても自然に消滅してしまう新規な化粧シートを提供することにある。 [0004] The present invention has been made in view of the above problems, and an object, the weather resistance required for the decorative sheet has the proper molding, yet was left discarded even if is to provide a novel decorative sheet disappear naturally.

【0005】 [0005]

【課題を解決するための手段】上記の目的を達成するため、本発明の化粧シートは、ポリ−L−乳酸を主成分とするポリ乳酸系樹脂シートからなる基材シートに装飾処理を施したことを特徴とする。 Means for Solving the Problems] To achieve the above object, the decorative sheet of the present invention, decorated processing the base material sheet comprising a polylactic acid-based resin sheet mainly composed of polylactic -L- acid it is characterized in.

【0006】また、本発明の化粧シートは、ポリ−L− [0006] In addition, the decorative sheet of the present invention include poly -L-
乳酸を主成分とするポリ乳酸系樹脂シートからなる基材シートに装飾処理を施し、該基材シートに表面保護層を積層したことを特徴とする。 Lactic decorated processing the base material sheet comprising a polylactic acid-based resin sheet mainly composed of, it is characterized in that by laminating a surface protective layer to the substrate sheet.

【0007】 [0007]

【発明の実施の形態】基材シートを構成するポリ乳酸系樹脂はデンプンから製造されるもので、本発明で使用するポリ乳酸系樹脂はポリ−L−乳酸を主成分とする。 Polylactic acid resin constituting the DETAILED DESCRIPTION OF THE INVENTION The substrate sheet are those prepared from starch, polylactic acid resin used in the present invention is composed mainly of polylactic -L- acid. このポリ−L−乳酸としては、重量平均分子量が10万以上、好ましくは20万以上のものを使用する。 As the polylactic -L- acid, weight average molecular weight of 100,000 or more, preferably to use a 200,000 or more. そして必要に応じ、このポリ乳酸系樹脂に紫外線吸収剤、光安定剤、防黴剤、難燃剤等の各種の添加剤を加える。 And if necessary, an ultraviolet absorber in the polylactic acid-based resin, a light stabilizer, an antifungal, adding various additives such as flame retardants.

【0008】紫外線吸収剤と光安定剤はともに基材シート(化粧シート)に耐候(光)性を付与するために添加するものであり、いずれかの単独使用でもよいが、通常は両者を混合して使用する。 [0008] UV absorbers and light stabilizers are those both added to the base sheet (decorative sheet) for imparting weathering (light) resistance, but may be either used alone, usually mixed together to to use. 紫外線吸収剤としては、ベンゾトリアゾール系、ベンゾフェノン系、サリシレート系等の有機系のもの、或いは微粒子の二酸化チタン、酸化セリウム等の無機系のものが用いられる。 As the ultraviolet absorber, benzotriazole-based, benzophenone-based, those of organic type salicylate, etc., or titanium dioxide particles, those inorganic such as cerium oxide used. また、光安定剤としては、ヒンダードアミン系ラジカル捕捉剤等が用いられる。 As the light stabilizer, hindered amine radical scavenger or the like is used. 紫外線吸収剤、光安定剤とも0.1〜1重量%程度の添加量である。 Ultraviolet absorber, both light stabilizer is added the amount of about 0.1 to 1 wt%.

【0009】基材シートは延伸でも無延伸でもよい。 [0009] The base sheet may be either non-stretched at a stretch. 延伸する場合は1軸延伸でも2軸延伸でも構わないが、通常は2軸延伸とする。 Although the case of stretching may be either biaxially oriented in uniaxial stretching, usually a biaxially stretched. また、延伸倍率は2〜4倍程度が好ましい。 The stretching ratio is about 2 to 4 times is preferable. 無延伸の基材シートは塑性変形しやすく成形性が良好であるが、延伸した基材シートは透明度が高く、また弾性が強まり、引張強度や伸度に優れている。 Substrate sheet unstretched although moldability tends to plastic deformation is good, stretched base sheet has high transparency, also intensified elastic, is excellent in tensile strength and elongation.
さらに、80〜120℃程度で加熱処理(アニーリング)して耐熱性、耐熱収縮性を付与するのが望ましい。 Further, heat resistance and heat treatment (annealing) at about 80 to 120 ° C., it is desirable to impart heat shrinkability.
また、本発明で使用する基材シートの厚さは25〜20 The thickness of the substrate sheet used in the present invention is from 25 to 20
0μm程度である。 It is about 0μm.

【0010】基材シートには所望の装飾処理を施す。 [0010] The base sheet subjected to a desired decorative treatment. この装飾処理としては、顔料又は染料の練込みによる着色、インキ絵柄層や金属層の模様からなる装飾層形成、 As the design process, colored by kneading the pigment or dye, a decorative layer formed consisting of a pattern of the ink pattern layer and a metal layer,
凹凸模様形成等がある。 There is an uneven pattern formation and the like. 装飾層或いは凹凸模様は、基材シートが透明な場合は基材シートの表面、裏面或いは表裏両面に形成してもよいが、基材シートが不透明な場合は表面側に形成する必要がある。 Decorative layer or uneven pattern, when the substrate sheet is transparent surface of the substrate sheet, may be formed on the back surface or both surfaces, when the substrate sheet is opaque, it is necessary to form on the surface side. なお、裏打ちシートのように基材シートのままで被着体の裏面に貼り合わせる化粧シートとして使用する場合には装飾処理の必要はない。 It is not necessary decoration processing when used as a decorative sheet bonded to the back surface of the adherend while the substrate sheet as the backing sheet.

【0011】顔料或いは染料の練込みにより着色する場合、用途に応じて透明着色又は不透明(隠蔽性)着色とする。 [0011] When colored by kneading a pigment or dye, a colored transparent or opaque (concealing property) colored depending on the application. 顔料としては、チタン白、亜鉛華、群青、コバルトブルー、弁柄、朱、黄鉛、チタン黄、カーボンブラック等の無機顔料、キナクリドン、パーマネントレッド4 As the pigment, titanium white, zinc white, ultramarine blue, cobalt blue, red iron, Zhu, chrome yellow, titanium yellow, inorganic pigments such as carbon black, quinacridone, Permanent Red 4
R、イソインドリノン、ハンザイエローA、フタロシアニンブルー、インダスレンブルーRS、アニリンブラック等の有機顔料乃至は染料、アルミニウム、真鍮等の箔粉からなる金属顔料、二酸化チタン被覆雲母、塩基性炭酸鉛の箔粉等からなる真珠光沢(パール)顔料等が用いられる。 R, isoindolinone, Hansa yellow A, phthalocyanine blue, indanthrene blue RS, organic pigments or dyes such as aniline black, aluminum, metal pigments consisting of foil powder such as brass, titanium dioxide-coated mica, basic lead carbonate nacreous (pearl) pigment consisting of a foil powder or the like is used. この他、必要に応じて炭酸カルシウム、シリカ(二酸化硅素)、アルミナ(酸化アルミニウム)、硫酸バリウムのような体質顔料(充填剤)を添加する。 In addition, calcium carbonate optionally silica (silicon dioxide), alumina (aluminum oxide), addition of extender pigments (fillers) such as barium sulfate.

【0012】インキ絵柄層により模様を形成するには、 [0012] In order to form a pattern by the ink pattern layer,
グラビア印刷、オフセット印刷、凸版印刷、シルクスクリーン印刷等のような通常の印刷方式を用いることができるが、描画でも差し支えない。 Gravure printing, offset printing, letterpress printing, can be used ordinary printing method such as silk screen printing or the like, no problem in drawing. 絵柄層は樹脂バインダーと顔料又は染料からなるインキを任意の模様状に形成してなる。 Pattern layer is formed by forming an ink comprising a resin binder and a pigment or dye to any pattern. また、剥離性の支持体シート上にインキ層、 Further, the ink layer on the release of the support sheet,
さらに必要に応じて接着剤層が形成された転写シートを予め準備しておき、転写シートに形成されたインキ層を加圧、又は加圧と加熱により模様層(インキ絵柄層)を形成する面に転写させる、いわゆる転写印刷法によることもできる。 Leave prepare a transfer sheet on which the adhesive layer has been formed, if necessary in advance to form a pattern layer (ink design layer) by heating the ink layer formed on the transfer sheet pressure, or a pressure surface is transferred to, it is also possible according to the so-called transfer printing method. 模様の例としては、木目、石目、布目、皮紋、文字、図形、全面ベタ等がある。 As an example of the pattern, wood, stone eyes, a weft, Kawamon, characters, figures, and the entire surface of a solid or the like. インキの樹脂バインダーとしては、2液硬化型ウレタン樹脂、アクリル樹脂、セルロース系樹脂、塩化ビニル酢酸ビニル共重合体等が用いられる。 The ink resin binder, two-component curable urethane resin, acrylic resin, cellulose resin, etc. vinyl chloride-vinyl acetate copolymer. 顔料又は染料としては前記と同様のものが用いられる。 The pigment or dye the same examples as described above.

【0013】金属層による模様は、アルミニウム、クロム、金、銀、銅等の金属を真空蒸着するなどして形成する。 [0013] pattern by the metal layer, aluminum, chromium, gold, silver, a metal such as copper is formed by, for example, vacuum deposition. 斯かる金属層は全面に形成してもよく、或いは模様状(パターン状)に形成してもよいが、模様状に形成するには金属層不要部分に水溶性インキにより除去層を所望の模様で設けた上から全面に金属を蒸着させ、しかる後に水洗して上記除去層と共にその直上の金属層を除去する等の公知の手法による。 Such metal layer may be formed on the entire surface, or pattern shape may be formed in a (pattern), but the desired pattern of the removal layer by water-soluble ink in the metal layer unnecessary portion to form the pattern shape in by depositing metal on the entire surface over which it is provided, by a known method such as washing with water thereafter to remove the metal layer directly thereon with the removal layer. また、予め転写シートに形成しておいた金属層を模様層(金属層)を形成する面に転写させる、いわゆる転写印刷法によることもできる。 Further, to transfer the metal layer that has been formed in advance transfer sheet on the surface to form a pattern layer (metal layer) may be so-called transfer printing method.

【0014】凹凸模様を形成する手法としては、ヘアライン加工、サンドブラスト加工、エンボス加工等があり、これらの方法により基材シートに凹凸形状からなる凹凸模様を形成する。 [0014] As a method for forming the uneven pattern is hair line process, sandblasting, have embossing or the like to form an uneven pattern composed of concave-convex shape on the substrate sheet by these methods.

【0015】エンボス加工は、熱プレス方式の枚葉又は輪転式エンボス機を使用して、加熱し軟化させた基材シートの表面にエンボス版を押圧し、該エンボス版表面の凹凸形状を賦形することにより凹凸模様を形成する方法である。 [0015] Embossing can use the sheet or a rotary embossing machine hot press method, an embossing plate was pressed against the heated and softened is allowed substrate surface of the sheet, shape the irregular shape of the embossing surface it is a method of forming a rugged pattern by. このエンボス加工により形成する凹凸模様としては、木目導管溝、木目木肌、石材表面凹凸、布帛の表面テクスチュア、梨地、砂目、ヘアライン等を表現したもの、又はそれらを組み合わせたものが挙げられる。 The uneven pattern formed by the embossing, wood vessel grooves, wood bark, stone surface irregularities, fabric surface texture, satin, grain, a representation of a hairline like, or the like a combination thereof. また、該凹凸模様の凹部には必要に応じて公知のワイピング法により着色インキが充填される。 Further, the coloring ink is filled by a known wiping method if necessary in the recess of the uneven pattern. 該着色インキとしてはウレタン樹脂、アクリル樹脂、ポリエステル樹脂、 Urethane The colored ink resins, acrylic resins, polyester resins,
その他の常用のビヒクルに顔料又は染料を加えたものを選択使用するが、2液硬化型の密着性、耐溶剤性の良好なものが好ましい。 Other for selection using the plus pigment or dye vehicles conventional, but adhesion two-part curable, having good solvent resistance are preferable. また、ワイピングは、ドクターブレード法、ロールコート法等の従来から使用されているワイピング法のいずれによってもよい。 Also, wiping a doctor blade method, or by any of the wiping techniques which are conventionally used, such as roll coating. これらの方法により、凹凸模様全面に着色インキを塗工し、しかる後に凸部のインキを掻き取って凹部に着色インキを残留せしめる。 These methods, coating a coloring ink on uneven pattern over the entire surface, allowed to remain a coloring ink in the recess scrapes the ink protrusions thereafter.

【0016】化粧シートの形態としては、図1に示すような基材シートのみからなる単層のもの、図2に示すような基材シートと表面保護層からなる2層のもの、さらには3層以上積層したもの(図示略)がある。 [0016] The form of the decorative sheet, a single layer composed of only the substrate sheet, as shown in FIG. 1, a two-layer consisting of the base sheet and the surface protective layer as shown in FIG. 2, further 3 a laminate of more layers there are (not shown).

【0017】図1(a)に示す化粧シートSは基材シート1に顔料等の着色剤2を添加して着色したものであり、図1(b)の化粧シートSは基材シート1に易接着層3を設け、その上から印刷で絵柄層4(全面ベタ又は部分的模様)を形成したものである。 The decorative sheet S shown in FIG. 1 (a) is obtained by colored by adding a coloring agent 2 such as a pigment in the substrate sheet 1, the decorative sheet S in FIG. 1 (b) to the substrate sheet 1 the provided adhesive layer 3, is obtained by forming a pattern layer 4 (entirely solid or partially pattern) in the printing thereon. また、図1(c) Further, FIG. 1 (c)
の化粧シートSは基材シート1の表面に凹部5からなる凹凸模様を形成したものであり、図1(d)の化粧シートSは表面の凹部に着色剤6をワイピングで充填したものである。 Is obtained by forming an uneven pattern composed of concave portions 5 on the surface of the substrate sheet 1, the decorative sheet S is obtained by filling a colorant 6 in wiping into the recess of the surface shown in FIG. 1 (d) of the decorative sheet S .

【0018】図2(a)に示す化粧シートSは、基材シート1に印刷で絵柄層4を形成し、その上に表面保護層7を積層したものである。 The decorative sheet S shown in FIG. 2 (a), the pattern layer 4 was formed by printing on the base sheet 1 is formed by laminating a surface protective layer 7 thereon. また図2(b)に示す化粧シートは、顔料等の着色剤2を添加して着色した基材シート1の表面に印刷で絵柄層4を形成し、その上に表面保護層7を積層したものである。 The decorative sheet shown in FIG. 2 (b), the pattern layer 4 was formed by a printing colorant 2 was added to colored substrate sheet 1 on the surface of the pigment, it was laminated surface protective layer 7 thereon it is intended. 表面保護層7としてポリ乳酸系樹脂を使用するのが生分解性の点では好ましい。 As a surface protective layer 7 in terms of the biodegradable using the polylactic acid-based resin.
ただし、所望の表面物性を出すため、その他の樹脂を使用してもよい。 However, to issue the desired surface properties may be used other resins. 例えば、ポリ弗化ビニリデン等の弗素樹脂、ポリメチルメタクリレート等のアクリル樹脂、ポリプロピレン等のオレフィン樹脂、電子線又は紫外線硬化型のアクリレート系、エポキシ系等の樹脂が挙げられる。 For example, fluorine resins such as polyvinylidene fluoride, acrylic resins such as polymethyl methacrylate, polypropylene, etc. olefin resin, an electron beam or ultraviolet curable acrylate based, include resins such as epoxy based. この表面保護層7は予め製膜したシートを貼り合わせるか、或いは樹脂を塗工することで形成する。 Or the surface protective layer 7 is bonded to advance film sheets, or formed by coating the resin.

【0019】図2(c)に示す化粧シートSは、顔料等の着色剤2を添加して着色した基材シート1の表面に印刷で絵柄層4を形成し、その上に表面保護層7を積層した後、エンボス加工により凹部5からなる凹凸模様を化粧シートしたものである。 The decorative sheet S shown in FIG. 2 (c), by adding a coloring agent 2 such as a pigment the pattern layer 4 was formed by printing on the colored substrate sheet 1 of the surface, the surface protective layer 7 thereon after stacking the one in which an uneven pattern composed of a concave portion 5 by embossing the decorative sheet. また図2(d)に示す化粧シートSは、図2(c)の化粧シートに対してさらに表面の凹部に着色剤6をワイピングで充填したものである。 The decorative sheet S shown in FIG. 2 (d) are those filled with colorant 6 in wiping into the recess of the further surface against the decorative sheet of FIG. 2 (c).
これら図2(a)〜(d)で示すような2層積層構成の化粧シートの場合、裏面側の基材シート1には前記の如き条件で延伸したものを用い、表面保護層7にはポリ乳酸系樹脂からなる無延伸のものを用いることが好ましい。 For decorative sheet of Figure 2 (a) ~ (d) 2-layer laminated structure as shown in, the base sheet 1 on the back side with those drawn in such conditions above, the surface protective layer 7 it is preferable to use a unstretched consisting polylactic acid resin.

【0020】図2(c)に示す如き化粧シートSの好ましい製造方法は次のようである。 A preferred method for producing such decorative sheet S shown in FIG. 2 (c) are as follows. まず、ポリ乳酸系樹脂を延伸シート化して基材シート1を製造し、この基材シート1に必要に応じて印刷やプライマー塗工を行っておく。 First, the polylactic acid-based resin is stretched sheeting to produce a substrate sheet 1, previously subjected to printing or primer coating as needed to the substrate sheet 1. そして、図3に示すように、圧力ロール(圧胴)1 Then, as shown in FIG. 3, the pressure roll (pressure drum) 1
1と冷却ロール(エンボス版胴)12の間に基材シート1を通しながら、表面保護層7としてポリ乳酸系樹脂をTダイ13から熔融状態で押し出すことにより、基材シート1に表面保護層7を積層すると同時にエンボス版を兼用した冷却ロール12の作用により表面保護層7に凹凸模様を賦形する。 While passing the base sheet 1 during a cooling roll (embossing cylinder) 12, by extruding the polylactic acid resin as a surface protective layer 7 from a T-die 13 in a molten state, a surface protective layer on the substrate sheet 1 When the 7 stacked to shape the uneven pattern in the surface protective layer 7 by the action of the cooling roll 12 which also serves as an embossing plate at the same time. このようにして製造された化粧シートは、表面保護層7が未延伸であるので塑性変形によりエンボスが入りやすく、しかも基材シート1が延伸して引張強度や伸度に優れているので、Vカット加工、ラッピング加工等の加工適正が良好である。 Such decorative sheet thus manufactured, since the surface protective layer 7 is in unstretched easily enter embossed by plastic deformation, and since the substrate sheet 1 is excellent in tensile strength and elongation by stretching, V cutting, processing proper is good, such as lapping. すなわち、この種のポリ乳酸系樹脂の化粧シートでは元来両立し難かったエンボス加工適正(良好な凹凸の賦形)とVカット加工等の曲げ加工が可能なだけの引張強度及び伸度を両立させることができる。 That is, both tensile strength and elongation of only capable bending V-cut processing, etc. and embossing proper which has been difficult to achieve both originally in the decorative sheet of this type of polylactic acid resin (shaping good uneven) it can be.

【0021】本発明の化粧シートは他の被着体(裏打材)に積層することができる。 The decorative sheet of the present invention can be laminated to another adherend (backing). 被着体が最終製品であり、その表面化粧のために化粧シートを積層する場合もあれば、必要に応じ化粧シートの力学的強度の補強、或いは隠蔽性の付与のため化粧シート裏面に被着体を積層する場合もある。 Adherend is a final product, applied Some case of laminating a decorative sheet, reinforcing the mechanical strength of the decorative sheet as required, or the decorative sheet back surface for concealment of imparting to the surface decorative there is also a case of stacking the body. 被着体への積層に際し、被着体に化粧シート自体が(熱融点等で)接着可能な場合は接着剤層を省いてもよい。 Upon lamination to an adherend, the decorative sheet itself to an adherend (a thermal melting point, etc.) if possible adhesive may be omitted an adhesive layer. また、化粧シート自体では被着体と接着しない場合は適当な接着剤を使用する。 Further, if the decorative sheet itself does not adhere to the adherend using a suitable adhesive.

【0022】図4及び図5は被着体に積層した化粧シートをその被着体とともに示す断面図で、図4に示すものは図2(c)に示した化粧シートSを被着体8である平板に接着剤層9を介して積層したものであり、図5に示すものは基材シート1に印刷で絵柄層4を施してなる化粧シートSを被着体10である凹凸立体物の表面に成形同時ラミネート法(後述)で積層したものである。 FIG. 4 and FIG. 5 is a sectional view showing a decorative sheet laminated to an adherend with its adherend, the adherend 8 decorative sheet S shown in FIG. 2 is that shown in FIG. 4 (c) in which is obtained by laminating through the flat plate the adhesive layer 9, uneven three-dimensional object as shown in FIG. 5 is a adherend 10 the decorative sheet S comprising subjecting the pattern layer 4 in the printing on the substrate sheet 1 molding simultaneous lamination method on the surface of those obtained by laminating at (described later).

【0023】被着体としては、各種素材の平板(図4)、曲面板等の板材、立体形状物品(図5)、シート(或いはフィルム)等の各種形状の物品が対象となる。 [0023] As an adherend, various materials of the plate (FIG. 4), the plate material of the curved plate or the like, three-dimensional shaped article (5), articles of various shapes such as a sheet (or film) is of interest.
板材、立体形状物品、シート(フィルム)のいずれにも用いられる素材としては、木材単板、木材合板、パーティクルボード、中密度繊維板(MDF)等の木材板、木質繊維板等の木質板、鉄、アルミニウム等の金属、アクリル樹脂、ポリカーボネート樹脂、エチレン・酢酸ビニル共重合体、エチレンビニルアセテート、ポリエステル樹脂、ポリスチレン、ポリオレフィン樹脂、ABS、フェノール樹脂、ポリ塩化ビニル、セルロース系樹脂、ゴム等の樹脂がある。 Plate, as the one in use also materials of the three-dimensional shaped article, a sheet (film), wood veneer, wood plywood, particle board, medium density fiberboard (MDF) or the like timber board, wood fiber board, etc. wood board of, iron, metal such as aluminum, an acrylic resin, a polycarbonate resin, an ethylene-vinyl acetate copolymer, ethylene vinyl acetate, polyester resin, polystyrene, polyolefin resin, ABS, phenolic resins, polyvinyl chloride, cellulose resins, resins such as rubber there is. 専ら板材、或いは立体形状物品として用いられる素材としては、硝子、陶磁器、等のセラミックス、ALC(発泡軽量コンクリート)等のセメント、珪酸カルシウム、石膏等の非セメント窯業系材料がある。 The material used exclusively plate, or as a three-dimensional shaped article, glass, porcelain, ceramics etc., ALC (foamed lightweight concrete) cement such as calcium silicate, there is a non-cementitious ceramic materials such as gypsum. 専らシート(或いはフィルム)として用いられる素材としては、上質紙、和紙等の紙、炭素、石綿、チタン酸カリウム、硝子、合成樹脂等の繊維からなる不織布又は織布等がある。 The material used exclusively as a sheet (or film), there is a high-quality paper, paper Japanese paper or the like, carbon, asbestos, potassium titanate, glass, consisting of fibers such as synthetic resin nonwoven fabric or woven fabric.

【0024】これら各種被着体への化粧シートの積層方法としては、例えば、接着剤層を間に介して板状基材に加圧ローラーで加圧して積層する方法、特公昭50 [0024] As the method of laminating the decorative sheet to these various adherends, for example, a method of pressurizing laminate with a pressure roller to the plate-shaped substrate via between the adhesive layer, JP-B-50
−19132号公報、特公昭43−27488号公報等に記載されるように、化粧シートを射出成形の雌雄両金型間に挿入して両金型を閉じ、雄型のゲートから熔融樹脂を射出充填した後、冷却して樹脂成形品の成形と同時にその表面に化粧シートを接着積層する、所謂射出成形同時ラミネート法、特公昭56−45768号公報、 -19132 discloses, as described in JP-B 43-27488 Patent Publication, by inserting the decorative sheet between the male and female molds of injection molding to close both molds, injecting the molten resin from the male mold gate after filling, the decorative sheet is adhesively laminated on the surface simultaneously with the molding of the resin molded article is cooled, so-called simultaneous injection molding lamination method, JP-B 56-45768, JP-
特公昭60−58014号公報等に記載されるように、 As described in JP-B 60-58014 Patent Publication,
接着剤層を間に介して成形品の表面に化粧シートを対向乃至は載置し、成形品側からの真空吸引による圧力差により化粧シートを成形品表面に積層する、所謂真空プレス積層法、特公昭61−5895号公報、特公平3− The decorative sheet to the surface of the molded article through between the adhesive layer facing to the placing, laminating the decorative sheet to the molded article surface by the pressure difference caused by the vacuum suction from the molded product side, so-called vacuum press lamination method, JP-B-61-5895, JP-fair 3-
2666号公報等に記載されるように、円柱、多角柱等の柱状基材の長軸方向に、接着剤層を間に介して化粧シートを供給しつつ、複数の向きの異なるローラーにより、柱状体を構成する複数の側面に順次化粧シートを加圧接着して積層していく、所謂ラッピング加工法、実公大15−31122号公報、特開昭48−47972 As described in 2666 JP like, cylindrical, in the axial direction of the columnar base material such as a polygonal column, while supplying decorative sheet through between the adhesive layer, a plurality of orientations of different rollers, columnar will laminated sequentially decorative sheet into a plurality of sides that constitute the body by vulcanization press, so-called lapping method, Jitsuoyakedai 15-31122, JP-Sho 48-47972
号公報等に記載されるように、先ず化粧シートを板状基材に接着剤層を介して積層し、次いで板状基材の化粧シートとは反対側の面に、化粧シートと板状基材との界面に到達する、断面がV字状又はU字状溝を切削し、次いで該溝内に接着剤を塗布した上で、該溝を折り曲げて箱体又は柱状体を成形する、所謂Vカット又はUカット加工方法等がある。 No. As described in Japanese or the like, first, a decorative sheet laminated through an adhesive layer to a plate-shaped substrate, then the surface opposite to the decorative sheet of plate-shaped substrates, the decorative sheet and the plate-shaped base reaches the interface between the wood cross-section cutting the V-shaped or U-shaped grooves, and then in terms of an adhesive is applied into the groove, forming a box body or columnar body by bending the groove, so-called there are V-cut or U-cutting method or the like.

【0025】特に、本発明の化粧シートを凹凸立体物に貼り合わせる方法としては、前記方法のうち、射出成形同時ラミネート法、真空プレス積層法、ラッピング加工法、Vカット加工法等が好ましい。 [0025] Particularly, as a method for bonding the decorative sheet of the present invention to uneven three-dimensional object, of the method, injection-molding simultaneous lamination method, a vacuum press lamination method, lapping method, V-cutting method or the like are preferable.

【0026】本発明の化粧シートは、各種被着体に積層し、所定の成形加工等を施して、各種用途に用いられる。 The decorative sheet of the present invention, laminated to various adherends is subjected to a predetermined molding, and is used in various applications. 例えば、壁、天井、床等建築物の内装、扉、窓枠、 For example, the wall, the ceiling, the floor and the like building interior, doors, window frames,
扉枠、手摺等の建具の表面化粧、箪笥等の家具、弱電・ Door frame, fittings of surface decorative such as handrails, furniture, such as a chest of drawers, weak electric,
OA機器のキャビネット等の表面化粧、自動車、電車等の車両内装、航空機や船舶の内装、窓硝子の化粧などである。 Surface makeup of the cabinet such as OA equipment, is automobile, vehicle interior, such as a train, the interior of the aircraft and a ship, the window glass cosmetic, such as.

【0027】 [0027]

【実施例】 【Example】

(実施例1)基材シートを次のようにして作製した。 It was prepared (Example 1) a substrate sheet in the following manner. すなわち、100重量部のポリ−L−乳酸系樹脂(重量平均分子量20万)に、着色顔料であるチタン白を10重量部、ベンゾトリアゾール系紫外線吸収剤を0.5重量部添加し、この組成物を伸倍率3倍で2軸延伸し、10 That is, 100 parts by weight of poly -L- acid-based resin (weight average molecular weight 200,000), 10 parts by weight of titanium white colored pigments, the benzotriazole-based ultraviolet absorber was added 0.5 part by weight, the composition things biaxially stretched in extension ratio of 3, 10
0℃で熱処理して厚さ80μmに製膜した。 Was heat-treated at 0 ℃ was formed to a thickness of 80μm.

【0028】次に上記の基材シートに絵柄を印刷した。 [0028] was then printed a pattern on the substrate sheet.
具体的には、ヘキサメチレンジイソシアネートとアクリルポリオールからなる2液硬化型ポリウレタン樹脂をバインダーとし、顔料として弁柄、カーボンブラック、二酸化チタン、ベンジジンイエローを混合してなるインキを用い、グラビア印刷により楢板目の木目絵柄を印刷して絵柄層を形成した。 Specifically, the two-component curable polyurethane resin consisting of hexamethylene diisocyanate and acrylic polyol as a binder, red iron as a pigment, carbon black, titanium dioxide, an ink obtained by mixing benzidine yellow used, oak plate by a gravure printing to form a pattern layer by printing eye woodgrain pattern.

【0029】そして、100重量部のポリ−L−乳酸系樹脂(重量平均分子量20万)にベンゾトリアゾール系紫外線吸収剤を0.5重量部、及びヒンダードアミン系ラジカル捕捉剤を0.5重量部添加した組成物を使用し、図3に示す如くこの組成物をTダイから熔融状態で押し出して、基材シートの印刷面に厚さ60μmに積層すると同時にエンボス版を兼用した冷却ロールにより楢材表面の導管溝凹凸をエンボスした。 [0029] Then, 0.5 part by weight of benzotriazole ultraviolet absorbers 100 parts by weight of poly -L- acid-based resin (weight average molecular weight of 200,000), and added 0.5 part by weight of hindered amine radical scavenger and using compositions, the composition as shown in FIG. 3 are extruded at a molten state from a T-die, oak material surface by a cooling roll which also serves as a embossing and simultaneously laminated to a thickness of 60μm to the printing surface of the base sheet the conduit groove irregularities were embossed. 次いで、導管溝内にセピア色の着色インキ(バインダーはアクリル樹脂、 Then, sepia colored ink in the conduit groove (binder acrylic resins,
顔料は弁柄)をワイピング法で充填した。 Pigment was filled with red iron oxide) in the wiping method. そして最後に上塗り層を3μmの厚さで塗装して化粧シートを製造した。 And to produce a decorative sheet was coated with a thickness of 3μm and finally overcoating layer. この上塗り層は、ヘキサメチレンジイソシアネートとアクリルポリオールからなる2液硬化型ウレタン樹脂をバインダーとし、これの100重量部に対し艶消剤としてシリカ顔料を3重量部添加した組成物を使用して形成した。 The overcoat layer is a two-component curable urethane resin consisting of hexamethylene diisocyanate and acrylic polyol as a binder, were formed using a composition prepared by adding 3 parts by weight of silica pigment as matting agent per 100 parts by weight of this .

【0030】(実施例2)実施例1で製造した化粧シートを厚さ2.5mmのラワン合板に接着剤で貼り合わせて化粧板とした。 [0030] and (Example 2) by bonding with an adhesive lauan plywood of thickness 2.5mm the decorative sheet prepared in Example 1 veneer. 使用した接着剤は、酢酸ビニル系の2 Adhesive used was 2 vinyl acetate
液硬化型のエマルジョン(イソシアネートを硬化剤とする)である。 A liquid curable emulsion (a and hardener isocyanate).

【0031】(評価) 耐候性 カーボンアーク燈型サンシャインウェザオメータにて1 [0031] (Evaluation) 1 at the weather-resistant carbon arc 燈型 sunshine weather-o meter
000時間照射する曝露試験を行った。 The exposure test to be irradiated 000 hours was performed. 条件はブラックパネル温度63℃、降雨サイクル18分/120分とした。 Conditions black panel temperature 63 ° C., and the rain cycle 18 min / 120 min. そして、曝露後における引張強度の保持率を測定し、また目視にて変褪色を観察したところ、実施例1の化粧シートは引張強度の保持率が70%であり、外観に目立った変化は見られなかった。 Then, by measuring the retention of tensile strength after exposure, and observation of the discoloration was visually a 70% retention of the decorative sheet tensile strength of Example 1, changes seen noticeable appearance It is did not.

【0032】分解性 実施例1の化粧シートを埼玉県入間郡三芳町の土壌中に埋設し、4月〜9月の6箇月間放置してから発掘した。 [0032] The decorative sheet of degradable Example 1 was buried in the soil in Saitama Prefecture Iruma-gun, Miyoshi-cho, was excavated from the left between 6 months of April to September.
そして、目視にて外観を観察したところ、分解が進行しており、原形を保持しておらずシートが断片状になっていた。 Then, observation of the appearance was visually degradation has progressed, the sheet does not hold the original shape had become fragmented form. また、回収した化粧シートの断片について参考までに分子量保持率を測定したところ40%であった。 Also, it was 40% when measured molecular weight retention rate for reference for fragment recovered decorative sheet.

【0033】 [0033]

【発明の効果】以上説明したように、本発明の化粧シートは、化粧シートに必要な耐候性、成形加工適正を備えており、建築物の内装材等に用いられている間は空気中の水分や細菌で生分解変質せず、しかも一旦廃棄処分して土壌に接して或いは土壌中に放置した際にその基材シートが土中の微生物の働きにより水と炭酸ガスに完全に分解して消滅するので、地球環境にとって好ましいものである。 As described above, according to the present invention, the decorative sheet of the present invention, weather resistance required for the decorative sheet has a proper molding, while used in interior materials of buildings in the air not biodegradable deterioration in moisture and bacteria, yet once the base sheet be disposed of when allowed to stand or in the soil in contact with the soil is completely decomposed into water and carbon dioxide by the action of soil microorganisms since the disappearance, it is preferred for the global environment.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】本発明に係る化粧シートの例を示す断面図である。 It is a cross-sectional view showing an example of a decorative sheet according to the present invention; FIG.

【図2】本発明に係る化粧シート他の例を示す断面図である。 2 is a sectional view showing a decorative sheet another example according to the present invention.

【図3】表面保護層に凹凸模様を施した化粧シートの製造方法の説明図である。 3 is an explanatory view of a method of manufacturing the decorative sheet subjected to uneven pattern in the surface protective layer.

【図4】被着体に積層した化粧シートをその被着体とともに示す断面図である。 4 is a sectional view showing a decorative sheet laminated to an adherend with its adherend.

【図5】被着体に積層した化粧シートをその被着体とともに示す断面図である。 5 is a cross-sectional view showing a decorative sheet laminated to an adherend with its adherend.

【符号の説明】 DESCRIPTION OF SYMBOLS

S 化粧シート 1 基材シート 2 着色剤 3 易接着層 4 絵柄層 5 凹部 6 着色剤 7 表面保護層 8 被着体 9 接着剤 10 被着体 11 圧力ロール 12 冷却ロール 13 Tダイ S decorative sheet 1 base sheet 2 colorant 3 adhesive layer 4 adherend 11 pressure pattern layer 5 recess 6 colorant 7 surface protective layer 8 adherend 9 adhesive 10 rolls 12 cooling roll 13 T-die

Claims (4)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 ポリ−L−乳酸を主成分とするポリ乳酸系樹脂シートからなる基材シートに装飾処理を施したことを特徴とする化粧シート。 1. A decorative sheet, characterized in that decorated processing the base material sheet comprising a polylactic acid-based resin sheet mainly composed of polylactic -L- acid.
  2. 【請求項2】 延伸したポリ乳酸系樹脂シートを基材シートに用いた請求項1に記載の化粧シート。 2. A decorative sheet according to claim 1 using a stretched polylactic acid-based resin sheet to the base sheet.
  3. 【請求項3】 ポリ−L−乳酸を主成分とするポリ乳酸系樹脂シートからなる基材シートに装飾処理を施し、該基材シートに表面保護層を積層したことを特徴とする化粧シート。 3. A decorative sheet polylactic -L- acid decorated processing the base material sheet comprising a polylactic acid-based resin sheet mainly composed of, is characterized in that by laminating a surface protective layer to the substrate sheet.
  4. 【請求項4】 延伸したポリ乳酸系樹脂シートを基材シートに用い、未延伸のポリ乳酸系樹脂を表面保護層に用いた請求項3に記載の化粧シート。 4. Using the stretched polylactic acid-based resin sheet to the base sheet, the decorative sheet according to claim 3 using an undrawn polylactic acid-based resin in the surface protective layer.
JP30009697A 1997-10-31 1997-10-31 Decorative sheet Pending JPH11129426A (en)