JPH1095090A - Laminating method, laminating device, manufacture of fluorescent pattern, fluorescent pattern, and back-face plate for plasma display panel - Google Patents

Laminating method, laminating device, manufacture of fluorescent pattern, fluorescent pattern, and back-face plate for plasma display panel

Info

Publication number
JPH1095090A
JPH1095090A JP9139455A JP13945597A JPH1095090A JP H1095090 A JPH1095090 A JP H1095090A JP 9139455 A JP9139455 A JP 9139455A JP 13945597 A JP13945597 A JP 13945597A JP H1095090 A JPH1095090 A JP H1095090A
Authority
JP
Japan
Prior art keywords
film
thermoplastic resin
resin layer
substrate
laminating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP9139455A
Other languages
Japanese (ja)
Other versions
JP3925749B2 (en
Inventor
Hajime Kakumaru
Naoki Kimura
Takeshi Nojiri
Kazuya Sato
Hideyasu Tachiki
Seiji Tai
Hiroyuki Tanaka
Seikichi Tanno
Yumiko Wada
清吉 丹野
和也 佐藤
有美子 和田
直紀 木村
誠司 田井
裕之 田仲
秀康 立木
肇 角丸
剛 野尻
Original Assignee
Hitachi Chem Co Ltd
日立化成工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to JP8-136036 priority Critical
Priority to JP13603696 priority
Application filed by Hitachi Chem Co Ltd, 日立化成工業株式会社 filed Critical Hitachi Chem Co Ltd
Priority to JP13945597A priority patent/JP3925749B2/en
Publication of JPH1095090A publication Critical patent/JPH1095090A/en
Application granted granted Critical
Publication of JP3925749B2 publication Critical patent/JP3925749B2/en
Anticipated expiration legal-status Critical
Application status is Expired - Fee Related legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To use two kinds or more of films and laminate respective films on a base with good workability by feeding a film A from a first feed source, also feeding a film B from a second source and laminate the film A on the base, on which the film B is laminated. SOLUTION: A substrate film 5A is transferred to a first feed roll 1 for feeding a film A and a film with a thermoplastic resin layer A3 is transferred to a laminating roll 10 by a transfer roll 12, and a thermoplastic resin layer A3 having the substrate film 5a is laminated on a base 7. On the other hand, a substrate film 5B is transferred to a second feed roll 2 for feeding a film B, and a film with a thermoplastic resin layer B4 is transferred to the laminating roll 10 by the transfer roll 12, and the thermoplastic resin layer B with the substrate film 5B is laminated on the thermoplastic resin layer A3 laminated on the base 7. Respective films, therefore, can be laminated on the base with good workability by using two kinds or more of films.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、積層方法、積層装置、蛍光体パターンの製造法、蛍光体パターン及びプラズマディスプレイパネル用背面板に関する。 The present invention relates to a laminated method, lamination apparatus, method for producing the phosphor pattern relates phosphor pattern and the back panel for a plasma display panel.

【0002】 [0002]

【従来の技術】熱可塑性樹脂層を有するフィルムを基板上に積層する方法としては、常圧積層法、減圧下で積層を行う真空積層法等が知られている(特開昭57−19 BACKGROUND ART A film having a thermoplastic resin layer as a method for laminating on the substrate, normal lamination method, a vacuum lamination method or the like for stacking under reduced pressure are known (JP 57-19
7891号公報、特開昭57−34947号公報等)。 7891 JP, Sho 57-34947 Patent Publication).
上記方法は、いずれも、一種類のフィルムを積層する場合に限られており、二種類以上のフィルムを積層する場合においては、二工程以上を必要とし、作業性が悪い等の問題がある。 The method, both are limited in the case of laminating one kind of film, in the case of laminating two or more films may require two or more steps, there is a workability poor such problems.

【0003】近年、平板ディスプレイの1つとして、プラズマ放電により発光する蛍光体を設けることによって多色表示を可能にしたプラズマディスプレイパネル(以下PDPと記す)の検討が盛んに行われている。 Recently, as one of flat panel display, consider a plasma display panel that enables multicolor display (hereinafter referred to as PDP) has been actively by providing a phosphor which emits light by plasma discharge. PDP PDP
は、ガラスからなる平板状の前面板と背面板とが互いに平行にかつ対向して配設され、両者はその間に設けられたバリアリブにより一定の間隔に保持されており、前面板、背面板及びバリアリブに囲まれた空間で放電する構造になっている。 Is disposed in a flat plate-like back plate and are parallel to and face the front plate made of glass, they are held at predetermined intervals by a barrier rib disposed therebetween, the front plate, back plate and It has a structure to discharge in the space surrounded by the barrier ribs. このような空間には、表示のための蛍光体が塗布され、放電によって封入ガスから発生する紫外線によって蛍光体が発光させられ、この光を観察者が視認できるようになっている。 Such space, the phosphor for the display is applied, the phosphor is caused to emit light by ultraviolet rays generated from the charged gas by a discharge, the light observer is adapted to be visually recognized.

【0004】従来、この蛍光体を設ける方法としては、 Conventionally, as a method of providing the phosphor,
各色蛍光体を分散させたスラリー液もしくはペーストをスクリーン印刷等の印刷方法によって塗布する方法が提案されており、特開平1−115027号公報、特開平1−124929号公報、特開平1−124930号公報、特開平2−155142号公報等に開示されている。 Each color phosphor slurry or paste dispersed has been proposed a method of coating by printing methods such as screen printing, JP-1-115027, JP-A No. 1-124929, JP-A No. 1-124930 publications, disclosed in JP-a 2-155142 Patent Publication. しかし、上記の蛍光体分散スラリー液は液状であるため、蛍光体の沈澱等による分散不良が生じやすく、またスラリー液に液状の感光性レジストを用いた場合には、暗反応の促進等により保存安定性が乏しくなる等の欠点を有する。 However saving, since the phosphor-dispersed slurry solution described above is a liquid, it tends to occur poor dispersion due to precipitation or the like of the phosphor, also in the case of using a photosensitive resist liquid in the slurry liquid, the promotion of dark reaction It has drawbacks such as stability becomes poor. さらにスクリーン印刷等の印刷方法は印刷精度に劣るため、将来的なPDPの大画面化への対応は困難である等の問題がある。 Furthermore a printing method such as screen printing may have poor printing precision, corresponding some problems like is difficult to screen size of future PDP.

【0005】これらの問題点の解決には、蛍光体を含有させた感光性エレメント(感光性フィルムともいう)を用いる方法が提案されている(特開平6−267421 [0005] To solve these problems, (JP-A method has been proposed to use a photosensitive element which contains a phosphor (also referred to as a photosensitive film) 6-267421
及び6−273925号公報)。 And 6-273925 JP). 感光性エレメントを用いる方法とは、蛍光体を含有する感光性樹脂層と支持体フィルムよりなる感光性エレメントの蛍光体を含有する感光性樹脂層を、加熱圧着(ラミネート)により前記P The method of using a photosensitive element, wherein P a photosensitive resin layer by thermocompression bonding (laminate) containing the phosphor of the photosensitive element and a photosensitive resin layer containing a phosphor composed of a support film
DP用基板の空間に埋め込み、次に、ネガフィルムを用いて、写真法により紫外線等の活性光で像的に露光し、 Embedded in the space DP substrate, then, by using a negative film, the image to be exposed with actinic light such as ultraviolet rays by a photographic method,
その後、アルカリ水溶液等の現像液で、未露光部分を除去し、さらに、焼成により不必要な有機成分を取り除いて、必要な部分のみに蛍光体パターンを形成するものである。 Thereafter, a developing solution such as an alkaline aqueous solution, the unexposed portion is removed, further, by removing the unnecessary organic components by firing, thereby forming a phosphor pattern only at necessary portions. このような感光性エレメントを使用する方法は、 Methods of using such photosensitive element,
写真法を用いるため、精度良く蛍光体パターンを形成することができる。 For using a photographic method, it is possible to form accurately phosphor pattern.

【0006】しかし、従来の方法により感光性エレメントを使用して蛍光体を含有する感光性樹脂層を、ラミネートにより前記PDP用基板の空間(セル内)に埋め込むと、バリアリブ壁面及び空間底面上に蛍光体パターンを均一な層厚、形状で形成することが困難であった。 However, the conventional photosensitive resin layer containing a phosphor by using the photosensitive element by the method, when embedded in the space of the substrate for the PDP by laminating (a cell), the barrier rib wall and space the bottom surface it has been difficult to form a phosphor pattern uniform layer thickness, shape. そこで、蛍光体パターンを均一な層厚、形状で形成するための種々の方法が検討されている。 Therefore, various methods for forming a phosphor pattern uniform layer thickness, shape has been studied.

【0007】 [0007]

【発明が解決しようとする課題】請求項1記載の発明は、二種類以上のフィルムを用いて、それぞれのフィルムを作業性よく基板上に積層することができる積層方法を提供するものである。 [SUMMARY OF THE INVENTION] The invention of claim 1 wherein, there is provided a lamination method that may be stacked, to each of the film with good workability on a substrate using two or more kinds of films. 請求項2記載の発明は、請求項1記載の発明の効果に加え、さらにPDP用基板等の凹凸を有する基板上に、作業性よく積層することができる積層方法を提供するものである。 According to a second aspect of the invention is to provide a lamination method that may be the effect of the invention according to claim 1, further over a substrate having an unevenness of a substrate such as a PDP, laminated good workability. 請求項3記載の発明は、請求項1又は2記載の発明の効果に加え、より作業性よく積層することができる積層方法を提供するものである。 According to a third aspect, the effect of the invention according to claim 1 or 2, is to provide a laminate method can be more workability laminate.

【0008】請求項4記載の発明は、請求項1、2又は3記載の発明の効果に加え、さらにプリント配線板用基板、カラーフィルタ等の製造に好適な積層方法を提供するものである。 [0008] The invention of claim 4, wherein, in addition to the effect of the invention of claim 1, 2 or 3, further printed circuit board substrate, and provides a suitable lamination method for the manufacture of such a color filter. 請求項5記載の発明は、請求項4記載の発明の効果に加え、さらにプラズマディスプレイパネル、EL基板等の製造に好適な積層方法を提供するものである。 According to a fifth aspect, the effect of the invention according to claim 4, further plasma display panel, and provides a suitable lamination method for the production of such EL substrate. 請求項6記載の発明は、請求項1、2、3、4 According to a sixth aspect of the invention, claim 1, 2, 3, 4
又は5記載の発明の効果に加え、よりプラズマディスプレイパネル等の製造に好適な積層方法を提供するものである。 Or in addition to the effects of the 5 invention described is to provide a suitable lamination method for the production of more such as a plasma display panel. 請求項7記載の発明は、請求項1、2、3、4、 According the invention in claim 7, wherein the claim 1, 2, 3, 4,
5又は6記載の発明の効果に加え、より作業性に優れる積層方法を提供するものである。 In addition to the 5 or 6 Effect of the invention described is to provide a lamination method with more excellent workability.

【0009】請求項8及び9記載の発明は、熱可塑性樹脂層を有する、二種類以上のフィルムを用いて、それぞれの熱可塑性樹脂層を作業性よく基板上に積層することができる積層装置を提供するものである。 [0009] The invention of claim 8 and 9 wherein has a thermoplastic resin layer, by using two or more kinds of films, a laminated device of each of the thermoplastic resin layer may be laminated to the workability substrate it is intended to provide. 請求項10記載の発明は、熱可塑性樹脂層を有する、二種類以上のフィルムを用いて、それぞれの熱可塑性樹脂層を作業性よく基板上に積層することができ、スペースをとらない積層装置を提供するものである。 Invention according to claim 10, having a thermoplastic resin layer, by using two or more kinds of films, each of the thermoplastic resin layer can be laminated to the good workability substrate, a laminating apparatus which does not take the space it is intended to provide. 請求項11記載の発明は、請求項8、9又は10記載の発明の効果に加え、さらに作業開始準備が容易であり、メンテナンス性に優れる積層装置を提供するものである。 The invention of claim 11, wherein, in addition to the effect of the invention of claim 8, 9 or 10, wherein it is easy to further work start preparation, is to provide a laminate device having excellent maintainability. 請求項12記載の発明は、請求項8、9又は10記載の発明の効果に加え、 The invention of claim 12, wherein, in addition to the effect of the invention of claim 8, 9 or 10, wherein,
さらに積層時の欠陥を抑制できる積層装置を提供するものである。 Further there is provided a laminating apparatus capable of suppressing defects during lamination.

【0010】請求項13記載の発明は、高精度な蛍光体パターンの製造法を提供するものである。 [0010] The invention of claim 13 wherein, there is provided a method for producing high-precision phosphor pattern. 請求項14記載の発明は、高精度に形成された蛍光体パターンを提供するものである。 The invention of claim 14 wherein is to provide a phosphor pattern formed with high precision. 請求項15記載の発明は、高精度に形成された蛍光体パターンを備えたプラズマディスプレイパネル用背面板を提供するものである。 According the invention in claim 15 wherein, there is provided a plasma display panel back plate having a phosphor pattern formed with high precision.

【0011】 [0011]

【課題を解決するための手段】本発明は、フィルムAを第1の供給部から供給し、フィルムBを第2の供給部から供給して、基板上にフィルムAを、その上にフィルムBを積層することを特徴とする積層方法に関する。 The present invention SUMMARY OF] is the film A is supplied from the first supply unit, the film B is supplied from the second supply unit, the film A on the substrate, the film B thereon a laminated method characterized by laminating. また、本発明は、基板が、凹凸を有する基板である前記積層方法に関する。 Further, the present invention, the substrate, to the lamination method is a substrate having an uneven. また、本発明は、フィルムAが、熱可塑性樹脂層Aを有するフィルムであり、フィルムBが、 Further, the present invention is a film A is a film having a thermoplastic resin layer A, the film B,
熱可塑性樹脂層Bを有するフィルムである前記積層方法に関する。 The related lamination method is a film having a thermoplastic resin layer B.

【0012】また、本発明は、熱可塑性樹脂層Aが、 Further, the present invention is the thermoplastic resin layer A,
(a)フィルム性付与ポリマ、(b)末端にエチレン性不飽和基を有する光重合性不飽和化合物及び(c)活性光の照射により遊離ラジカルを生成する光開始剤を含む感光性樹脂組成物層である前記積層方法に関する。 (A) a film-imparting polymer, (b) a photopolymerizable unsaturated compound having an ethylenically unsaturated group at the terminal and (c) active light sensitive resin composition comprising a photoinitiator which generates free radicals by irradiation of about the lamination method is a layer. また、本発明は、熱可塑性樹脂層Aが、さらに、(d)蛍光体を含む感光性樹脂組成物層である前記積層方法に関する。 Further, the present invention is the thermoplastic resin layer A further relates to the lamination method is a photosensitive resin composition layer comprising (d) is a phosphor. また、本発明は、熱可塑性樹脂層Bが、(e)熱可塑性樹脂、を含む前記積層方法に関する。 Further, the present invention is a thermoplastic resin layer B is relates to the lamination method comprising, (e) a thermoplastic resin.

【0013】また、本発明は、熱可塑性樹脂層Aを有するフィルムが、支持体フィルム、熱可塑性樹脂層A及びカバーフィルムを有するものであり、熱可塑性樹脂層B Further, the present invention provides a film having a thermoplastic resin layer A, the support film are those having a thermoplastic resin layer A and the cover film, the thermoplastic resin layer B
を有するフィルムが、支持体フィルム、熱可塑性樹脂層B及びカバーフィルムを有するものである前記積層方法に関する。 Film having found support film, to the lamination method is one having a thermoplastic resin layer B and the cover film.

【0014】また、本発明は、フィルムAを供給する第1の供給手段、フィルムBを供給する第2の供給手段及び基板上にフィルムAを、その上にフィルムBを積層する積層手段を備えてなる積層装置に関する。 Further, the present invention includes a first supply means for supplying a film A, the film A in the second supply means and the substrate for supplying the film B, provided with a laminating means for laminating the film B thereon on becomes Te laminating device. また、本発明は、支持体フィルム(5A)、熱可塑性樹脂層A Further, the present invention is a support film (5A), the thermoplastic resin layer A
(3)及びカバーフィルム(6A)を有するフィルムA (3) and the film A having a cover film (6A)
並びに支持体フィルム(5B)、熱可塑性樹脂層B And the support film (5B), the thermoplastic resin layer B
(4)及びカバーフィルム(6B)を有するフィルムB (4) and the film B having a cover film (6B)
を用いて、基板(7)上に熱可塑性樹脂層A(3)、その上に熱可塑性樹脂層B(4)を積層する装置であって、フィルムAを供給する第1の供給手段、フィルムB With the substrate (7) the thermoplastic resin layer A (3) on a device for laminating a thermoplastic resin layer B (4) thereon, the first supply means for supplying a film A, film B
を供給する第2の供給手段、カバーフィルム((6A)及び(6B))を取るため手段、支持体フィルム(5A)を取るための手段及び熱可塑性樹脂層A(3)と熱可塑性樹脂層B(4)を積層するための積層手段を備えた積層装置に関する。 Second supply means for supplying the cover film ((6A) and (6B)) means for taking the means and the thermoplastic resin layer A (3) for taking the support film (5A) and the thermoplastic resin layer It relates to a laminated device having a lamination means for laminating B (4).

【0015】また、本発明は、支持体フィルム(5 Further, the present invention, the support film (5
A)、熱可塑性樹脂層A(3)及びカバーフィルム(6 A), the thermoplastic resin layer A (3) and the cover film (6
A)を有するフィルムA並びに支持体フィルム(5 Film A and the support film having A) (5
B)、熱可塑性樹脂層B(4)及びカバーフィルム(6 B), the thermoplastic resin layer B (4) and the cover film (6
B)を有するフィルムBを用いて、基板(7)上に熱可塑性樹脂層A(3)、その上に熱可塑性樹脂層B(4) B) using a film B having a heat on the substrate (7) the thermoplastic resin layer A (3), the thermoplastic resin layer B thereon (4)
を積層する装置であって、基板(7)を送る搬送手段、 An apparatus for stacking, conveying means for feeding the substrate (7),
フィルムAを供給する第1の供給手段、フィルムBを供給する第2の供給手段、カバーフィルム((6A)及び First supply means for supplying a film A, the second supply means for supplying a film B, the cover film ((6A) and
(6B))を取るための手段、熱可塑性樹脂層A(3)又は熱可塑性樹脂層B(4)を有するフィルムを送るための手段、支持体フィルム(5A)を送るための手段、支持体フィルム(5A)を取るための手段、熱可塑性樹脂層A(3)又は熱可塑性樹脂層B(4)を有するフィルムを基板(7)に積層する積層手段を設けた積層装置に関する。 Means for removing (6B)), means for sending a film having a thermoplastic resin layer A (3) or the thermoplastic resin layer B (4), the support film (5A) means for sending, support means for taking the film (5A), a laminated device having a laminating means for laminating the substrate (7) a film having a thermoplastic resin layer a (3) or the thermoplastic resin layer B (4).

【0016】また、本発明は、基板(7)を送る搬送ロール(11)、フィルムAを供給する第1の供給ロール(1)、カバーフィルム(6A)を巻取るカバーフィルム巻取ロール(8)、支持体フィルム(5A)及び熱可塑性樹脂層A(3)を有するフィルムを送る送りロール(12)、支持体フィルム(5A)及び熱可塑性樹脂層A(3)を有するフィルムを基板(7)上に積層する積層ロール(10)、支持体フィルム(5A)を送る送りロール(12)、支持体フィルム(5A)を巻取る支持体フィルム巻取ロール(9)、フィルムBを供給する第2の供給ロール(2)、カバーフィルム(6B)を巻取るカバーフィルム巻取ロール(8)、支持体フィルム(5B)及び熱可塑性樹脂層B(4)を有するフィルムを送る送りロール( Further, the present invention provides conveying rolls Send substrate (7) (11), a first supply roll for supplying a film A (1), cover film take-up roll (8 winding the cover film (6A) ), the support film (5A) and the thermoplastic resin layer a (feed roll Send film having 3) (12), the support film (5A) and the thermoplastic resin layer a (substrate a film having a 3) (7 ) laminating roll to be stacked (10), feed rolls sending support film (5A) (12), the support film (5A) of the winding takes support film winding roll (9), the supply of the film B 2 of the supply roll (2), the cover film take-up roll (8) for winding the cover film (6B), the support film (5B) and feed roll to send a film having a thermoplastic resin layer B (4) ( 2)、基板(7)上に積層された熱可塑性樹脂層A(3)の上に、支持体フィルム(5 2) on a substrate (7) the thermoplastic resin layer A (3 laminated on), the support film (5
B)及び熱可塑性樹脂層B(4)を有するフィルムを積層する積層ロール(10)を設けた前記積層装置に関する。 B) and to said stacking device having a laminating roll for laminating (10) a film having a thermoplastic resin layer B (4).

【0017】また、本発明は、基板(7)を送る搬送ロール(11)、フィルムAを供給する第1の供給ロール(1)、フィルムAを送る送りロール(12)、カバーフィルム(6A)を巻取るカバーフィルム巻取ロール(8)、支持体フィルム(5A)及び熱可塑性樹脂層A Further, the present invention provides conveying rolls Send substrate (7) (11), a first supply roll for supplying a film A (1), feed rolls for sending a film A (12), cover film (6A) take a winding cover film take-up roll (8), the support film (5A) and the thermoplastic resin layer a
(3)を有するフィルムを送る送りロール(12)、フィルムBを供給する第2の供給ロール(2)、フィルムBを送る送りロール(12)、カバーフィルム(6B) Feed roll to send a film having a (3) (12), a second supply roll for supplying a film B (2), feed roll Send film B (12), cover film (6B)
を巻取るカバーフィルム巻取ロール(8)、支持体フィルム(5B)及び熱可塑性樹脂層B(4)を有するフィルムを送る送りロール(12)、支持体フィルム(5 Take a winding cover film take-up roll (8), the support film (5B) and feed roll (12) for sending a film having a thermoplastic resin layer B (4), the support film (5
A)及び熱可塑性樹脂層A(3)を有するフィルムと支持体フィルム(5B)及び熱可塑性樹脂層B(4)を有するフィルムを貼り合わせる合わせロール(13)、支持体フィルム(5A)を送る送りロール(12)、支持体フィルム(5A)を巻取る支持体フィルム巻取ロール(9)、熱可塑性樹脂層A(3)、熱可塑性樹脂層B A) and the thermoplastic resin layer A (3) a film having a support film (5B) and the thermoplastic resin layer B (combined roll (13 bonding a film having a 4)), and sends the support film (5A) feed roll (12), the support film takeup roll for taking up the support film (5A) (9), the thermoplastic resin layer a (3), the thermoplastic resin layer B
(4)及び支持体フィルム(5B)を有するフィルムを送る送りロール(12)、熱可塑性樹脂層A(3)、熱可塑性樹脂層B(4)及び支持体フィルム(5B)を有するフィルムを基板(7)上に積層する積層ロール(1 (4) and the feed roll to send a film having a support film (5B) (12), the thermoplastic resin layer A (3), a substrate film having the thermoplastic resin layer B (4) and the support film (5B) (7) laminating roll to be stacked (1
0)を設けた前記積層装置に関する。 0) relating to the stack apparatus provided with.

【0018】また、本発明は、(I)凹凸を有する基板の凹凸表面上に、前記の積層方法により蛍光体を含有する感光性樹脂組成物層である熱可塑性樹脂層Aを有するフィルムA及び熱可塑性樹脂層Bを有するフィルムBを積層して熱可塑性樹脂層A及び熱可塑性樹脂層Bを形成する工程、(II)活性光線を像的に照射する工程、(II Further, the present invention is, on the uneven surface of the substrate having the (I) uneven, the film A and a thermoplastic resin layer A is a photosensitive resin composition layer containing a phosphor by lamination methods forming a thermoplastic resin layer a and the thermoplastic resin layer B are laminated film B having a thermoplastic resin layer B, the step of irradiating (II) active light rays imagewise, (II
I)現像により不要部を除去する工程及び(IV)焼成により不要分を除去する工程を含む蛍光体パターンの製造法に関する。 I) a process for producing a phosphor pattern comprising the step of removing the unnecessary components by the process and (IV) calcining to remove unnecessary portion by development. また、本発明は前記の蛍光体パターンの製造法により製造された蛍光体パターンに関する。 The present invention relates to a phosphor pattern produced by the production method of the phosphor pattern. また、 Also,
本発明はプラズマディスプレイパネル用基板上に前記の蛍光体パターンを備えてなるプラズマディスプレイパネル用背面板に関する。 The present invention relates to a plasma display panel back plate made provided with the phosphor pattern on the plasma display panel substrate.

【0019】 [0019]

【発明の実施の形態】本発明の積層方法は、フィルムA Lamination method of the embodiment of the present invention, the film A
を第1の供給部から供給し、フィルムBを第2の供給部から供給して、基板上にフィルムAを、その上にフィルムBを積層することを特徴とする。 Was supplied from the first supply unit, the film B is supplied from the second supply unit, the film A on the substrate, characterized by laminating a film B thereon. 本発明における基板としては、特に制限はなく、例えば、プリント配線板製造用基板(銅張積層板、ガラスエポキシ基板、紙フェノール基板等)、カラーフィルタ製造用基板(透明ガラス基板、プラスチック基板、金属基板(アルミニウム、 The substrate in the present invention is not particularly limited, for example, printed wiring board fabrication substrate (copper clad laminate, a glass epoxy substrate, paper phenol substrate), a color filter formation substrate (transparent glass substrate, a plastic substrate, a metal board (aluminum,
銅、ニッケル、ステンレス等)、セラミック基板等)、 Copper, nickel, stainless steel, etc.), ceramic substrate, or the like),
プラズマディスプレイパネル製造用基板(PDP用基板)(透明な接着のための表面処理を施していてもよい、ガラス板、セラミック基板、絶縁処理された金属基板、合成樹脂板等の基板に、電極及びバリアリブが形成された基板等)、有機EL製造用基板(透明ガラス基板、プラスチック基板、金属基板(アルミニウム、銅、 Manufacturing a PDP substrate (substrate for PDP) (it may be subjected to a surface treatment for a transparent adhesive, a glass plate, a ceramic substrate, insulated metal substrates, the substrate of a synthetic resin plate or the like, electrodes and like substrate which barrier ribs are formed), an organic EL manufacturing substrate (transparent glass substrate, a plastic substrate, a metal substrate (aluminum, copper,
ニッケル、ステンレス等)、セラミック基板、電極が形成された基板等)、フィールドエミッションディスプレイの蛍光体層形成用基板(透明ガラス基板、プラスチック基板、金属基板(アルミニウム、銅、ニッケル、ステンレス等)、セラミック基板等)などが挙げられる。 Nickel, stainless steel, etc.), a ceramic substrate, the substrate electrodes are formed and the like), a phosphor layer-forming substrate (transparent glass substrate of a field emission display, a plastic substrate, a metal substrate (aluminum, copper, nickel, stainless steel, etc.), ceramic substrate, or the like) and the like.

【0020】本発明における凹凸を有する基板としては、例えば、バリアリブが形成されたプラズマディスプレイパネル用基板(PDP用基板)等が挙げられる。 [0020] As a substrate having unevenness in the present invention include, for example, such as barrier ribs is formed a plasma display panel substrate (a substrate for PDP) and the like. P
DP用基板としては、例えば、透明な接着のための表面処理を施していてもよい、ガラス板、セラミック基板、 As the substrate for DP, for example, it may be subjected to a surface treatment for a transparent adhesive, a glass plate, a ceramic substrate,
絶縁処理された金属基板、合成樹脂板等の基板に、電極及びバリアリブが形成されたものなどが挙げられる。 Insulated metal substrate, the substrate of a synthetic resin plate or the like, and the like which electrodes and barrier ribs are formed. バリアリブの形成には、特に制限なく、公知の材料を使用できるが、例えば、シリカ、熱硬化性樹脂、低融点ガラス(酸化鉛等)、溶剤などを含むリブ材を用いることができる。 The formation of the barrier ribs is not particularly limited, and a known material can be used, for example, silica, thermosetting resin, low melting point glass (lead oxide), can be used rib material including solvent. また、PDP用基板には、電極及びバリアリブの他に、必要に応じて、誘電膜、絶縁膜、補助電極、抵抗体等が形成されていてもよい。 Further, the substrate for PDP, in addition to the electrodes and barrier ribs, as necessary, a dielectric film, insulating film, the auxiliary electrode, resistor or the like may be formed. これらのものを、基板へ形成する方法としては、特に制限はなく、例えば、基板に、蒸着、スパッタリング、メッキ、塗布、印刷等の方法で電極を形成することができ、印刷法、サンドブラスト法、埋め込み法等の方法でバリアリブを形成することができる。 These things, as a method of forming the substrate is not particularly limited, for example, the substrate, deposition, sputtering, plating, coating, it is possible to form an electrode by a method such as printing, a printing method, sand blasting method, it is possible to form the barrier ribs by the method of embedding method.

【0021】図1及び図2にバリアリブが形成されたP The barrier ribs in Figures 1 and 2 are formed P
DP用基板の一例の模式図を示した。 It shows a schematic view of an example of a DP substrate. バリアリブは、通常、高さが20〜500μm、幅が20〜200μmとされる。 Barrier ribs are typically height 20 to 500 [mu] m, the width is set to 20 to 200 [mu] m. バリアリブで囲まれた放電空間の形状には、特に制限はなく、格子状、ストライプ状、ハニカム状、3 The shape of the discharge space surrounded by the barrier ribs is not particularly limited, grid-like, stripe-shaped, honeycomb-shaped, 3
角形状、楕円形状等が可能であるが、通常、図1及び図2等に示すような、格子状又はストライプ状の放電空間が形成される。 Square shape, although it is possible elliptical shape, usually, as shown in FIGS. 1 and 2, etc., lattice-shaped or stripe-shaped discharge space is formed. 図1及び図2において、透明基板14上にはバリアリブ15が形成されており、図1では格子状放電空間16が、図2ではストライプ状放電空間17が形成されている。 1 and 2, on the transparent substrate 14 is formed with a barrier rib 15, the lattice-shaped discharge space 16 in FIG. 1, a stripe-shaped discharge space 17 in FIG. 2 is formed. 放電空間の大きさは、PDPの大きさと解像度によって決められ、通常、図1のような格子状放電空間であれば、縦及び横の長さは、50μm〜1mm The size of the discharge space, is determined by the PDP size and resolution, usually, if the lattice-shaped discharge space as shown in FIG. 1, the vertical and horizontal lengths are 50Myuemu~1mm
となり、図2のようなストライプ状放電空間であれば、 Next, if the striped discharge space as shown in FIG. 2,
間隔は、30μm〜1mmとなる。 Interval is a 30μm~1mm.

【0022】本発明におけるフィルムA及びフィルムB Film A and Film B in [0022] the present invention
としては、特に制限はないが、作業性等の点から、フィルムAが、熱可塑性樹脂層Aを有するフィルムであることが好ましく、フィルムBが、熱可塑性樹脂層Bを有するフィルムであることが好ましい。 As is not particularly limited, from the viewpoint of workability and the like, the film A is preferably a film having a thermoplastic resin layer A, that the film B is a film having a thermoplastic resin layer B preferable.

【0023】本発明における熱可塑性樹脂層Aとしては、熱可塑性を有する樹脂であれば特に制限はなく、例えば、(a)フィルム性付与ポリマ、(b)末端にエチレン性不飽和基を有する光重合性不飽和化合物及び(c)活性光の照射により遊離ラジカルを生成する光開始剤を含む感光性樹脂組成物層等が好ましいものとして挙げられる。 [0023] As the thermoplastic resin layer A in the present invention is particularly limited as long as it is a resin having thermoplasticity is not, for example, light having a (a) a film-imparting polymer, ethylenically unsaturated group (b) end polymerizable unsaturated compound and (c) the photosensitive resin composition layer or the like comprising a photoinitiator which generates free radicals by irradiation of active light may be mentioned as preferred.

【0024】本発明における(a)フィルム性付与ポリマとしては、ビニル共重合体が好ましく、ビニル共重合体に用いられるビニル単量体としては、例えば、アクリル酸、メタクリル酸、マレイン酸、フマル酸、イタコン酸、アクリル酸メチル、メタクリル酸メチル、アクリル酸エチル、メタクリル酸エチル、アクリル酸n−プロピル、メタクリル酸n−プロピル、アクリル酸iso−プロピル、メタクリル酸iso−プロピル、アクリル酸n−ブチル、メタクリル酸n−ブチル、アクリル酸iso−ブチル、メタクリル酸iso−ブチル、アクリル酸sec−ブチル、メタクリル酸sec−ブチル、アクリル酸tert−ブチル、メタクリル酸tert−ブチル、アクリル酸ペンチル、 [0024] (a) as a film-imparting polymer in the present invention, the vinyl copolymer is preferable. Examples of the vinyl monomer used in the vinyl copolymer include acrylic acid, methacrylic acid, maleic acid, fumaric acid , itaconic acid, methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, acrylic acid n- propyl, methacrylic acid n- propyl, acrylate iso- propyl methacrylate iso- propyl, n- butyl acrylate, methacrylate n- butyl, butyl iso- acrylate, butyl iso- methacrylate, butyl sec- acrylate, butyl sec- methacrylate, butyl tert- acrylate, tert- butyl methacrylate, pentyl acrylate,
メタクリル酸ペンチル、アクリル酸ヘキシル、メタクリル酸ヘキシル、アクリル酸ヘプチル、メタクリル酸ヘプチル、アクリル酸2−エチルヘキシル、メタクリル酸2 Pentyl methacrylate, hexyl acrylate, hexyl methacrylate, heptyl acrylate, heptyl methacrylate, 2-ethylhexyl acrylate, methacrylic acid 2
−エチルヘキシル、アクリル酸オクチル、メタクリル酸オクチル、アクリル酸ノニル、メタクリル酸ノニル、アクリル酸デシル、メタクリル酸デシル、アクリル酸ドデシル、メタクリル酸ドデシル、アクリル酸テトラデシル、メタクリル酸テトラデシル、アクリル酸ヘキサデシル、メタクリル酸ヘキサデシル、アクリル酸オクタデシル、メタクリル酸オクタデシル、アクリル酸エイコシル、メタクリル酸エイコシル、アクリル酸ドコシル、メタクリル酸ドコシル、アクリル酸シクロペンチル、メタクリル酸シクロペンチル、アクリル酸シクロヘキシル、 - ethylhexyl, octyl acrylate, octyl methacrylate, nonyl acrylate, nonyl methacrylate, decyl acrylate, decyl methacrylate, dodecyl acrylate, dodecyl methacrylate, tetradecyl acrylate, tetradecyl methacrylate, hexadecyl acrylate, hexadecyl methacrylate , octadecyl acrylate, octadecyl methacrylate, eicosyl acrylate, eicosyl methacrylate, docosyl acrylate, docosyl methacrylate, cyclopentyl acrylate, cyclopentyl methacrylate, cyclohexyl acrylate,
メタクリル酸シクロヘキシル、アクリル酸シクロヘプチル、メタクリル酸シクロヘプチル、アクリル酸ベンジル、メタクリル酸ベンジル、アクリル酸フェニル、メタクリル酸フェニル、アクリル酸メトキシエチル、メタクリル酸メトキシエチル、アクリル酸メトキシジエチレングリコール、メタクリル酸メトキシジエチレングリコール、アクリル酸メトキシジプロピレングリコール、メタクリル酸メトキシジプロピレングリコール、アクリル酸メトキシトリエチレングリコール、メタクリル酸メトキシトリエチレングリコール、アクリル酸2−ヒドロキシエチル、メタクリル酸2−ヒドロキシエチル、アクリル酸2−ヒドロキシプロピル、メタクリル酸2−ヒドロキシプロピル、アクリル酸ジメチルアミノエチル、メタクリル酸ジメチルアミ Cyclohexyl methacrylate, acrylic acid cycloheptyl, methacrylic acid cycloheptyl, benzyl acrylate, benzyl methacrylate, phenyl acrylate, phenyl methacrylate, methoxyethyl acrylate, methacrylic acid methoxy ethyl, methoxy acrylic acid diethylene glycol methacrylate methoxy diethylene glycol, methoxy dipropylene glycol acrylate, methacrylic acid methoxy dipropylene glycol, methoxy triethylene glycol acrylate, methacrylic acid methoxy triethylene glycol, 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl acrylate, methacrylic 2-hydroxypropyl methacrylate, dimethylaminoethyl acrylate, dimethylaminopyridine methacrylate エチル、アクリル酸ジエチルアミノエチル、メタクリル酸ジエチルアミノエチル、アクリル酸ジメチルアミノプロピル、メタクリル酸ジメチルアミノプロピル、アクリル酸2−クロロエチル、メタクリル酸2−クロロエチル、アクリル酸2−フルオロエチル、メタクリル酸2−フルオロエチル、アクリル酸2− Ethyl, diethylaminoethyl acrylate, diethylaminoethyl methacrylate, acrylic acid dimethylaminopropyl, dimethylaminopropyl methacrylate, 2-chloroethyl acrylate, 2-chloroethyl methacrylate, 2-fluoroethyl acrylate, 2-fluoroethyl methacrylate, acrylic acid 2-
シアノエチル、メタクリル酸2−シアノエチル、スチレン、α−メチルスチレン、ビニルトルエン、塩化ビニル、酢酸ビニル、N−ビニルピロリドン、ブタジエン、 Cyanoethyl methacrylate, 2-cyanoethyl, styrene, alpha-methyl styrene, vinyl toluene, vinyl chloride, vinyl acetate, N- vinyl pyrrolidone, butadiene,
イソプレン、クロロプレン、アクリルアミド、メタクリルアミド、アクリロニトリル、メタクリロニトリル等が挙げられる。 Isoprene, chloroprene, acrylamide, methacrylamide, acrylonitrile, methacrylonitrile, and the like. これらは単独で又は2種類以上を組み合わせて使用される。 These may be used alone or in combination of two or more.

【0025】本発明における(a)フィルム性付与ポリマの重量平均分子量は、5,000〜300,000とすることが好ましく、20,000〜150,000とすることがより好ましい。 The weight average molecular weight of (a) a film-imparting polymer in the present invention is preferably in the 5,000 to 300,000, and more preferably in the 20,000 to 150,000. この重量平均分子量が、5, The weight average molecular weight, 5,
000未満では、感光性エレメントとした場合にフィルム形成性及び可とう性が低下する傾向があり、300, If it is less than 000, there is a tendency that film-forming property and flexibility is lowered when a photosensitive element, 300,
000を超えると、現像性(不要部が現像により、容易に除去できる性質)が低下する傾向がある。 Exceeds 000, developability (the unnecessary portion developing nature easily removable) tends to decrease. なお、重量平均分子量は、ゲルパーミエーションクロマトグラフィー法により測定し、標準ポリスチレン検量線を用いて換算した値である。 The weight average molecular weight, measured by gel permeation chromatography, is a value obtained by converting using a standard polystyrene calibration curve.

【0026】また、熱可塑性樹脂Aが、公知の各種現像液により現像可能となるように、 (a)フィルム性付与ポリマのカルボキシル基含有率(酸価(mgKOH/g)で規定できる)を適宜調整することができる。 Further, the thermoplastic resin A, so as to enable development by various known developing solution, the (a) film-imparting carboxyl group content of the polymer (can be defined by the acid value (mg KOH / g)) as appropriate it can be adjusted. 例えば、炭酸ナトリウム又は炭酸カリウム等のアルカリ水溶液を用いて現像する場合には、酸価を、 For example, in the case of developing using an alkaline aqueous solution such as sodium carbonate or potassium carbonate, the acid value,
90〜260とすることが好ましい。 It is preferable that the 90-260. この酸価が、90 The acid value, 90
未満では、現像が困難となる傾向があり、260を超えると、耐現像液性(現像により除去されずに残りパターンとなる部分が、現像液によって侵されない性質)が低下する傾向がある。 By weight, there is a tendency that development becomes difficult, and when it is more than 260, developing solution resistance (the remaining pattern portion without being removed by development is not affected by the developer properties) tends to be lowered. また、水又はアルカリ水溶液と一種以上の有機溶剤とからなる水系現像液を用いて現像する場合には、酸価を、16〜260とすることが好ましい。 Further, in the case of developing using an aqueous developer consisting of water or an alkaline aqueous solution and one or more organic solvents, the acid value is preferably set to 16 to 260. この酸価が、16未満では、現像が困難となる傾向があり、260を超えると、耐現像液性が低下する傾向がある。 The acid value is less than 16, there is a tendency that development becomes difficult, and when it is more than 260, developing solution resistance tends to decrease. さらに、1,1,1−トリクロロエタン等の有機溶剤現像液又はエマルジョン現像液を用いる場合には、カルボキシル基を含有しなくても良い。 Furthermore, in the case of using an organic solvent developer or emulsion developer 1,1,1-trichloroethane, etc., may not contain a carboxyl group.

【0027】本発明における(b)末端にエチレン性不飽和基を有する光重合性不飽和化合物としては、従来、 Examples of the photopolymerizable unsaturated compound in (b) terminal of the present invention having an ethylenically unsaturated group, conventionally,
光重合性多官能モノマとして知られているものを全て用いることができる。 It can be used all those known as the photopolymerizable polyfunctional monomer.

【0028】例えば、下記一般式(I) [0028] For example, the following general formula (I)

【化1】 [Formula 1] (式中、Rは水素原子又はメチル基を示し、kは1〜1 (Wherein, R represents a hydrogen atom or a methyl group, k is 1 to 1
0の整数であり、Yは置換基を有していてもよい飽和又は不飽和の炭化水素基又は複素環残基若しくはポリアルキレングリコール残基、 0 is an integer, Y is a hydrocarbon group or a heterocyclic residue or a polyalkylene glycol residue may be saturated or unsaturated optionally having a substituent,

【化2】 ## STR2 ## (式中、R 1及びR 2は各々独立には水素原子、メチル基、エチル基、プロピル基又はトリフルオロメチル基を示し、R 3及びR 4は各々独立に炭素数1〜6のアルキル基を示し、m及びnは各々独立に1〜20の整数を示す)を示す)で表される化合物等が挙げられる。 (Wherein, R 1 and R 2 are each independently hydrogen atom, a methyl group, an ethyl group, a propyl group, or a trifluoromethyl group, R 3 and R 4 are each independently an alkyl group having 1 to 6 carbon atoms are shown, m and n are each independently indicate shown) an integer of 1 to 20) a compound represented by the like.

【0029】一般式(I)中、Yで示される置換基を有していてもよい飽和又は不飽和の炭化水素残基又は複素環残基としては、例えば、ハロゲン原子、ヒドロキシル基、アミノ基、カルボキシル基等の置換基を有していてもよい炭素数1〜22の直鎖、分岐若しくは脂環状のアルカン残基(メタン残基、エタン残基、プロパン残基、 Examples of the hydrocarbon residue or heterocyclic residue of the general formula (I) in saturated may have a substituent group represented by Y or unsaturated, for example, a halogen atom, a hydroxyl group, an amino group , straight-chain having 1 to 22 carbon atoms which may have a substituent such as a carboxyl group, branched or alicyclic alkanes residue (methane residue, ethane residue, propane residue,
シクロプロパン残基、ブタン残基、イソブタン残基、シクロブタン残基、ペンタン残基、イソペンタン残基、ネオペンタン残基、シクロペンタン残基、ヘキサン残基、 Cyclopropane residue, butane residue, isobutane residue, cyclobutane residue, pentane residue, isopentane residue, neopentane residue, cyclopentane residue, hexane residue,
シクロヘキサン残基、ヘプタン残基、シクロヘプタン残基、オクタン残基、ノナン残基、デカン残基等)、芳香族環残基(ベンゼン残基、ナフタレン残基、アントラセン残基、ビフェニル残基、ターフェニル残基等)、複素環残基(フラン残基、チオフェン残基、ピロール残基、 Cyclohexane residue, heptane residue, cycloheptane residue, octane residue, nonane residue, decane residues, etc.), aromatic ring residue (benzene residue, naphthalene residue, an anthracene residue, biphenyl residue, ter phenyl residues, etc.), a heterocyclic residue (furan residue, a thiophene residue, a pyrrole residue,
オキサゾール残基、チアゾール残基、イミダゾール残基、ピリジン残基、ピリミジン残基、ピラジン残基、トリアジン残基、キノリン残基、キノキサリン残基等)などが挙げられる。 Oxazole residue, a thiazole residue, imidazole residue, pyridine residue, pyrimidine residue, pyrazine residue, triazine residue, quinoline residue, quinoxaline residues, etc.) and the like.

【0030】具体的には、一個の不飽和結合を有する単量体としては、例えば、アクリル酸又はメタクリル酸のエステル系モノマ(アクリル酸メチル、メタクリル酸メチル、アクリル酸エチル、メタクリル酸エチル、アクリル酸n−プロピル、メタクリル酸n−プロピル、アクリル酸iso−プロピル、メタクリル酸iso−プロピル、アクリル酸n−ブチル、メタクリル酸n−ブチル、アクリル酸iso−ブチル、メタクリル酸iso−ブチル、アクリル酸 [0030] Specifically, the monomer having an unsaturated bond, for example, ester-based monomer (methyl acrylate acrylic acid or methacrylic acid, methyl methacrylate, ethyl acrylate, ethyl methacrylate, acrylic acid n- propyl, methacrylic acid n- propyl, acrylate iso- propyl methacrylate iso- propyl, n- butyl acrylate, n- butyl methacrylate, butyl iso- acrylate, butyl iso- methacrylic acid, acrylic acid
sec−ブチル、メタクリル酸sec−ブチル、アクリル酸te sec- butyl, sec- butyl methacrylate, acrylic acid te
rt−ブチル、メタクリル酸tert−ブチル、アクリル酸ペンチル、メタクリル酸ペンチル、アクリル酸ヘキシル、 rt- butyl, butyl tert- methacrylate, pentyl acrylate, pentyl methacrylate, hexyl acrylate,
メタクリル酸ヘキシル、アクリル酸ヘプチル、メタクリル酸ヘプチル、アクリル酸2−エチルヘキシル、メタクリル酸2−エチルヘキシル、アクリル酸オクチル、メタクリル酸オクチル、アクリル酸ノニル、メタクリル酸ノニル、アクリル酸デシル、メタクリル酸デシル、アクリル酸ドデシル、メタクリル酸ドデシル、アクリル酸テトラデシル、メタクリル酸テトラデシル、アクリル酸ヘキサデシル、メタクリル酸ヘキサデシル、アクリル酸オクタデシル、メタクリル酸オクタデシル、アクリル酸エイコシル、メタクリル酸エイコシル、アクリル酸ドコシル、メタクリル酸ドコシル、アクリル酸シクロペンチル、メタクリル酸シクロペンチル、アクリル酸シクロヘキシル、メタクリル酸シクロヘキシル、アクリル酸シクロヘプチル、メタクリ Hexyl methacrylate, heptyl acrylate, heptyl methacrylate, 2-ethylhexyl acrylate, 2-ethylhexyl methacrylate, octyl acrylate, octyl methacrylate, nonyl acrylate, nonyl methacrylate, decyl acrylate, decyl methacrylate, acrylic acid dodecyl methacrylate, dodecyl methacrylate, tetradecyl acrylate, tetradecyl methacrylate, hexadecyl acrylate, hexadecyl methacrylate, octadecyl acrylate, octadecyl methacrylate, eicosyl acrylate, eicosyl methacrylate, docosyl acrylate, docosyl methacrylate, cyclopentyl acrylate, cyclopentyl methacrylate, cyclohexyl acrylate, cyclohexyl methacrylate, acrylic acid cycloheptyl, methacryl 酸シクロヘプチル、アクリル酸ベンジル、メタクリル酸ベンジル、アクリル酸フェニル、メタクリル酸フェニル、アクリル酸メトキシエチル、メタクリル酸メトキシエチル、アクリル酸ジメチルアミノエチル、メタクリル酸ジメチルアミノエチル、アクリル酸ジメチルアミノプロピル、メタクリル酸ジメチルアミノプロピル、アクリル酸2−クロロエチル、メタクリル酸2−クロロエチル、アクリル酸2−フルオロエチル、メタクリル酸2−フルオロエチル、アクリル酸2 Acid cycloheptyl, benzyl acrylate, benzyl methacrylate, phenyl acrylate, phenyl methacrylate, methoxyethyl acrylate, methacrylic acid methoxyethyl, dimethylaminoethyl acrylate, dimethylaminoethyl methacrylate, acrylate dimethylaminopropyl methacrylate dimethylaminopropyl, 2-chloroethyl acrylate, 2-chloroethyl methacrylate, 2-fluoroethyl acrylate, 2-fluoroethyl methacrylate, acrylic acid 2
−シアノエチル、メタクリル酸2−シアノエチル、アクリル酸メトキシジエチレングリコール、メタクリル酸メトキシジエチレングリコール、アクリル酸メトキシジプロピレングリコール、メタクリル酸メトキシジプロピレングリコール、アクリル酸メトキシトリエチレングリコール、メタクリル酸メトキシトリエチレングリコール等)、スチレン系モノマ(スチレン、α−メチルスチレン、p−t−ブチルスチレン等)、ポリオレフィン系モノマ(ブタジエン、イソプレン、クロロプレン等)、ビニル系モノマ(塩化ビニル、酢酸ビニル等)、ニトリル系モノマ(アクリロニトリル、メタクリロニトリル等)、1−(メタクリロイロキシエトキシカルボニル) - cyanoethyl methacrylate, 2-cyanoethyl, methoxy acrylic acid diethylene glycol methacrylate methoxy diethylene glycol, methoxy dipropylene glycol acrylate, methacrylic acid methoxy dipropylene glycol, methoxy triethylene glycol acrylate, methoxy methacrylate triethylene glycol), styrene system monomer (styrene, alpha-methyl styrene, p-t-butylstyrene, etc.), polyolefin-based monomer (butadiene, isoprene, chloroprene, etc.), vinyl monomers (vinyl chloride, vinyl acetate, etc.), nitrile-based monomers (acrylonitrile, methacryl Ronitoriru etc.), 1- (methacryloyloxy ethoxycarbonyl)
−2−(3′−クロロ−2′−ヒドロキシプロポキシカルボニル)ベンゼンなどが挙げられる。 Such as 2- (3'-chloro-2'-hydroxypropoxy carbonyl) benzene.

【0031】二個の不飽和結合を有する単量体としては、例えば、エチレングリコールジアクリレート、エチレングリコールジメタクリレート、ジエチレングリコールジアクリレート、ジエチレングリコールジメタクリレート、トリエチレングリコールジアクリレート、トリエチレングリコールジメタクリレート、テトラエチレングリコールジアクリレート、テトラエチレングリコールジメタクリレート、ポリエチレングリコールジアクリレート、ポリエチレングリコールジメタクリレート、ヘキサプロピレングリコールジアクリレート、ヘキサプロピレングリコールジメタクリレート、ポリプロピレングリコールジアクリレート、ポリプロピレングリコールジメタクリレート、ブチレングリコールジアクリレート、ブチレングリコールジメ [0031] monomer having two unsaturated bonds, such as ethylene glycol diacrylate, ethylene glycol dimethacrylate, diethylene glycol diacrylate, diethylene glycol dimethacrylate, triethylene glycol diacrylate, triethylene glycol dimethacrylate, tetra ethylene glycol diacrylate, tetraethylene glycol dimethacrylate, polyethylene glycol diacrylate, polyethylene glycol dimethacrylate, hexamethylene glycol diacrylate, hexamethylene glycol dimethacrylate, polypropylene glycol diacrylate, polypropylene glycol dimethacrylate, butylene glycol diacrylate, butylene glycol dimethyl クリレート、ネオペンチルグリコールジアクリレート、ネオペンチルグリコールジメタクリレート、1,3−ブタンジオールジアクリレート、 Acrylate, neopentyl glycol diacrylate, neopentyl glycol dimethacrylate, 1,3-butanediol diacrylate,
1,3−ブタンジオールジメタクリレート、1,4−ブタンジオールジアクリレート、1,4−ブタンジオールジメタクリレート、1,5−ペンタンジオールジアクリレート、1,5−ペンタンジオールジメタクリレート、 1,3-butanediol dimethacrylate, 1,4-butanediol diacrylate, 1,4-butanediol dimethacrylate, 1,5-pentanediol diacrylate, 1,5-pentanediol dimethacrylate,
1,6−ヘキサンジオールジアクリレート、1,6−ヘキサンジオールジメタクリレート、ペンタエリスリトールジアクリレート、ペンタエリスリトールジメタクリレート、トリメチロールプロパンジアクリレート、トリメチロールプロパンジメタクリレート、ビスフェノールA 1,6-hexanediol diacrylate, 1,6-hexanediol dimethacrylate, pentaerythritol diacrylate, pentaerythritol dimethacrylate, trimethylolpropane diacrylate, trimethylolpropane dimethacrylate, bisphenol A
ジアクリレート、ビスフェノールAジメタクリレート、 Diacrylate, bisphenol A dimethacrylate,
2,2−ビス(4−アクリロキシエトキシフェニル)プロパン、2,2−ビス(4−メタクリロキシエトキシフェニル)プロパン、2,2−ビス(4−アクリロキシジエトキシフェニル)プロパン、2,2−ビス(4−メタクリロキシジエトキシフェニル)プロパン、2,2−ビス(4−アクリロキシポリエトキシフェニル)プロパン、2,2−ビス(4−メタクリロキシポリエトキシフェニル)プロパン、ビスフェノールAジグリシジルエーテルジアクリレート、ビスフェノールAジグリシジルエーテルジメタクリレート、ウレタンジアクリレート化合物等が挙げられる。 2,2-bis (4-acryloxy ethoxyphenyl) propane, 2,2-bis (4-methacryloxy-ethoxyphenyl) propane, 2,2-bis (4-acryloxydiethoxyphenyl) propane, 2,2 bis (4-methacryloxydiethoxyphenyl Siji ethoxyphenyl) propane, 2,2-bis (4-acryloxy polyethoxy phenyl) propane, 2,2-bis (4-methacryloxy polyethoxy phenyl) propane, bisphenol A diglycidyl ether di acrylate, bisphenol A diglycidyl ether dimethacrylate, urethane diacrylate compounds.

【0032】三個の不飽和結合を有する単量体としては、例えば、トリメチロールプロパントリアクリレート、トリメチロールプロパントリメタクリレート、ペンタエリスリトールトリアクリレート、ペンタエリスリトールトリメタクリレート、エチレンオキシド変性トリメチロールプロパントリアクリレート、エチレンオキシド変性トリメチロールプロパントリメタクリレート、トリメチロールプロパントリグリシジルエーテルトリアクリレート、トリメチロールプロパントリグリシジルエーテルトリメタクリレート等が挙げられる。 Examples of the monomer having three unsaturated bonds, for example, trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, pentaerythritol triacrylate, pentaerythritol trimethacrylate, ethylene oxide-modified trimethylolpropane triacrylate, ethylene oxide modified trimethylolpropane trimethacrylate, trimethylolpropane triglycidyl ether triacrylate, trimethylolpropane triglycidyl ether trimethacrylate, and the like. 四個の不飽和結合を有する単量体としては、例えば、テトラメチロールプロパンテトラアクリレート、テトラメチロールプロパンテトラメタクリレート、ペンタエリスリトールテトラアクリレート、ペンタエリスリトールテトラメタクリレート等が挙げられる。 The monomer having four unsaturated bonds, for example, tetra trimethylol propane tetraacrylate, tetra trimethylol propane tetramethacrylate, pentaerythritol tetraacrylate, pentaerythritol tetramethacrylate, and the like.

【0033】五個の不飽和結合を有する単量体としては、例えば、ジペンタエリスリトールペンタアクリレート、ジペンタエリスリトールペンタメタクリレート等が挙げられる。 [0033] As a monomer having five unsaturated bonds, for example, dipentaerythritol pentaacrylate, dipentaerythritol penta methacrylate. 六個の不飽和結合を有する単量体としては、例えば、ジペンタエリスリトールヘキサアクリレート、ジペンタエリスリトールヘキサメタクリレート等が挙げられる。 The monomer having a six unsaturated bonds, e.g., dipentaerythritol hexaacrylate, dipentaerythritol hexa methacrylate. これらの不飽和結合を有する単量体は、いずれにしても、光照射によりラジカル重合するものであればよく、また、これらの不飽和結合を有する単量体は、単独で又は2種類以上を組み合わせて使用される。 These monomers having unsaturated bonds, in any event, as long as the radical polymerization by light irradiation, and monomers having these unsaturated bonds alone, or two or more kinds It is used in combination.

【0034】また、本発明における熱可塑性樹脂層A Further, the thermoplastic resin layer A in the present invention
を、蛍光体パターンの製造に使用する場合には、作製時に、焼成により不要分を除去する必要があるため、前記した(b)末端にエチレン性不飽和基を有する光重合性不飽和化合物の中から、熱分解性が良好な、ポリエチレングリコールジアクリレート、ポリエチレングリコールジメタクリレート、ポリプロピレングリコールジアクリレート、ポリプロピレングリコールジメタクリレート、 And when used in the preparation of the phosphor pattern, at the time of manufacturing, it is necessary to remove unnecessary components by calcination, the photopolymerizable unsaturated compound having an ethylenically unsaturated group in the above-mentioned (b) end from within, pyrolytic is good, polyethylene glycol diacrylate, polyethylene glycol dimethacrylate, polypropylene glycol diacrylate, polypropylene glycol dimethacrylate,
ポリ(エチレン・プロピレン)アクリレート複合体、 Poly (ethylene-propylene) acrylate complex,
(エチレン・プロピレン)グリコールジメタアクリレート等を使用することがより好ましい。 It is more preferable to use (ethylene-propylene) glycol dimethacrylate and the like.

【0035】また、(a)フィルム性付与ポリマと(b)末端にエチレン性不飽和基を有する光重合性不飽和化合物の両方の機能を有する化合物として、側鎖にエチレン性不飽和基を有する光重合性高分子結合剤を(a)フィルム性付与ポリマの代わりに用いることができる。 Further, as a compound having both functions of the photopolymerizable unsaturated compound having (a) a film-imparting polymer and (b) terminal ethylenically unsaturated groups, having an ethylenically unsaturated group in the side chain can be used photopolymerizable polymer binder instead of (a) a film-imparting polymer. 具体的には、カルボキシル基、水酸基、アミノ基、イソシアネート基、オキシラン環、酸無水物等の官能基を有するビニル共重合体に、少なくとも1個のエチレン性不飽和基と、オキシラン環、イソシアネート基、 Specifically, a carboxyl group, a hydroxyl group, an amino group, an isocyanate group, oxirane ring, a vinyl copolymer having a functional group such as acid anhydride, and at least one ethylenically unsaturated group, oxirane ring, isocyanate group ,
水酸基、カルボキシル基等の1個の官能基を有する化合物を付加反応させて得られる光重合性ビニル共重合体等が挙げられる。 Hydroxyl, one compound addition reacted photopolymerizable vinyl copolymer obtained by having a functional group such as a carboxyl group.

【0036】カルボキシル基、水酸基、アミノ基、オキシラン環、酸無水物等の官能基を有するビニル共重合体の合成に用いられるビニル単量体としては、例えば、アクリル酸、メタクリル酸、マレイン酸、フマル酸、イタコン酸、ケイ皮酸、アクリル酸2−ヒドロキシエチル、 [0036] carboxyl group, hydroxyl group and the amino group, oxirane ring, a vinyl monomer used in the synthesis of the vinyl copolymer having a functional group such as acid anhydrides, such as acrylic acid, methacrylic acid, maleic acid, fumaric acid, itaconic acid, cinnamic acid, 2-hydroxyethyl acrylate,
メタクリル酸2−ヒドロキシエチル、アクリル酸2−ヒドロキシプロピル、メタクリル酸2−ヒドロキシプロピル、アクリルアミド、メタクリルアミド、イソシアン酸エチルメタクリレート、グリシジルアクリレート、グリシジルメタクリレート、無水マレイン酸等のカルボキシル基、水酸基、アミノ基、オキシラン環、酸無水物等の官能基を有するビニル単量体が挙げられ、またその他のビニル単量体としては、例えば、アクリル酸メチル、メタクリル酸メチル、アクリル酸エチル、メタクリル酸エチル、アクリル酸n−プロピル、メタクリル酸n−プロピル、アクリル酸iso−プロピル、メタクリル酸iso−プロピル、アクリル酸n−ブチル、メタクリル酸n−ブチル、アクリル酸iso−ブチル、メタクリル酸iso−ブチル、アクリル酸sec−ブチ 2-hydroxyethyl methacrylate, 2-hydroxypropyl acrylate, 2-hydroxypropyl methacrylate, acrylamide, methacrylamide, ethyl isocyanate methacrylate, glycidyl acrylate, glycidyl methacrylate, carboxyl group such as maleic anhydride, hydroxyl group, an amino group, oxirane ring, a vinyl monomer can be mentioned having a functional group such as acid anhydride, and as the other vinyl monomer, for example, methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, acrylic acid n- propyl, methacrylic acid n- propyl, acrylate iso- propyl methacrylate iso- propyl, n- butyl acrylate, n- butyl methacrylate, butyl iso- acrylate, iso- butyl methacrylate, acrylic acid sec- butyrate 、メタクリル酸sec−ブチル、アクリル酸tert−ブチル、メタクリル酸tert−ブチル、アクリル酸ペンチル、メタクリル酸ペンチル、アクリル酸ヘキシル、メタクリル酸ヘキシル、アクリル酸ヘプチル、メタクリル酸ヘプチル、アクリル酸2−エチルヘキシル、メタクリル酸2−エチルヘキシル、アクリル酸オクチル、メタクリル酸オクチル、アクリル酸ノニル、メタクリル酸ノニル、アクリル酸デシル、メタクリル酸デシル、アクリル酸ドデシル、メタクリル酸ドデシル、アクリル酸テトラデシル、メタクリル酸テトラデシル、アクリル酸ヘキサデシル、メタクリル酸ヘキサデシル、アクリル酸オクタデシル、メタクリル酸オクタデシル、アクリル酸エイコシル、メタクリル酸エイコシル、 , Butyl sec- methacrylate, butyl tert- acrylate, butyl tert- methacrylate, pentyl acrylate, pentyl methacrylate, hexyl acrylate, hexyl methacrylate, heptyl acrylate, heptyl methacrylate, 2-ethylhexyl acrylate, methacrylic 2-ethylhexyl acrylate, octyl acrylate, octyl methacrylate, nonyl acrylate, nonyl methacrylate, decyl acrylate, decyl methacrylate, dodecyl acrylate, dodecyl methacrylate, tetradecyl acrylate, tetradecyl methacrylate, hexadecyl acrylate, methacrylic acid hexadecyl, octadecyl acrylate, octadecyl methacrylate, eicosyl acrylate, eicosyl methacrylate,
アクリル酸ドコシル、メタクリル酸ドコシル、アクリル酸シクロペンチル、メタクリル酸シクロペンチル、アクリル酸シクロヘキシル、メタクリル酸シクロヘキシル、 Docosyl acrylate, docosyl methacrylate, cyclopentyl acrylate, cyclopentyl methacrylate, cyclohexyl acrylate, cyclohexyl methacrylate,
アクリル酸シクロヘプチル、メタクリル酸シクロヘプチル、アクリル酸ベンジル、メタクリル酸ベンジル、アクリル酸フェニル、メタクリル酸フェニル、アクリル酸メトキシエチル、メタクリル酸メトキシエチル、アクリル酸メトキシジエチレングリコール、メタクリル酸メトキシジエチレングリコール、アクリル酸メトキシジプロピレングリコール、メタクリル酸メトキシジプロピレングリコール、アクリル酸メトキシトリエチレングリコール、メタクリル酸メトキシトリエチレングリコール、アクリル酸ジメチルアミノエチル、メタクリル酸ジメチルアミノエチル、アクリル酸ジエチルアミノエチル、メタクリル酸ジエチルアミノエチル、アクリル酸ジメチルアミノプロピル、メタクリル酸ジメチルアミノプロピル、 Acrylic acid cycloheptyl, methacrylic acid cycloheptyl, benzyl acrylate, benzyl methacrylate, phenyl acrylate, phenyl methacrylate, methoxyethyl acrylate, methacrylic acid methoxy ethyl, methoxy acrylic acid diethylene glycol methacrylate methoxy diethylene glycol, Metokishiji acrylate propylene glycol, methoxy dipropylene glycol methacrylate, methoxy triethylene glycol acrylate, methacrylic acid methoxy triethylene glycol, dimethylaminoethyl acrylate, dimethylaminoethyl methacrylate, diethylaminoethyl acrylate, diethylaminoethyl methacrylate, acrylic acid dimethylamino propyl, dimethylaminopropyl methacrylate,
アクリル酸2−クロロエチル、メタクリル酸2−クロロエチル、アクリル酸2−フルオロエチル、メタクリル酸2−フルオロエチル、アクリル酸2−シアノエチル、メタクリル酸2−シアノエチル、スチレン、α−メチルスチレン、ビニルトルエン、塩化ビニル、酢酸ビニル、N Acrylate, 2-chloroethyl methacrylate, 2-chloroethyl, 2-fluoroethyl acrylate, 2-fluoroethyl methacrylate, acrylic acid 2-cyanoethyl methacrylate, 2-cyanoethyl, styrene, alpha-methyl styrene, vinyl toluene, vinyl chloride , vinyl acid, N
−ビニルピロリドン、ブタジエン、イソプレン、クロロプレン、アクリロニトリル、メタクリロニトリル等が挙げられる。 - vinylpyrrolidone, butadiene, isoprene, chloroprene, acrylonitrile, methacrylonitrile, and the like. これらは、カルボキシル基、水酸基、アミノ基、オキシラン環、酸無水物等の官能基を有するビニル単量体を必須成分として、単独で又は2種類以上を組み合わせて使用される。 These carboxyl group, a hydroxyl group, an amino group, an oxirane ring, as an essential component a vinyl monomer having a functional group such as an acid anhydride may be used alone or in combination of two or more.

【0037】少なくとも1個のエチレン性不飽和基と、 [0037] and at least one ethylenically unsaturated group,
オキシラン環、イソシアネート基、水酸基、カルボキシル基、アミノ基、酸無水物等の1個の官能基を有する化合物としては、例えば、グリシジルアクリレート、グリシジルメタクリレート、イソシアン酸エチルメタクリレート、アクリル酸2−ヒドロキシエチル、メタクリル酸2−ヒドロキシエチル、アクリル酸2−ヒドロキシプロピル、メタクリル酸2−ヒドロキシプロピル、アクリル酸、メタクリル酸、マレイン酸、フマル酸、イタコン酸、ケイ皮酸、アクリルアミド、メタクリルアミド、無水マレイン酸等が挙げられる。 The compound having an oxirane ring, an isocyanate group, a hydroxyl group, a carboxyl group, an amino group, one functional group such as acid anhydride, for example, glycidyl acrylate, glycidyl methacrylate, ethyl isocyanate methacrylate, 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl acrylate, 2-hydroxypropyl methacrylate, acrylic acid, methacrylic acid, maleic acid, fumaric acid, itaconic acid, cinnamic acid, acrylamide, methacrylamide, maleic acid anhydride and the like. これらは単独で又は2種類以上を組み合わせて使用される。 These may be used alone or in combination of two or more.

【0038】本発明における側鎖にエチレン性不飽和基を有する光重合性高分子結合剤の重量平均分子量は、 The weight average molecular weight of the photopolymerizable polymer binder having an ethylenically unsaturated group in the side chain in the present invention,
5,000〜300,000とすることが好ましく、2 It is preferable that the 5,000 to 300,000, 2
0,000〜150,000とすることがより好ましい。 It is more preferable that the 0,000~150,000. この重量平均分子量が、5,000未満では、感光性エレメントとした場合にフィルム形成性及び可とう性が低下する傾向があり、300,000を超えると、現像性(不要部が現像により、容易に除去できる性質)が低下する傾向がある。 The weight average molecular weight is less than 5,000, there is a tendency that film-forming property and flexibility is lowered when a photosensitive element, exceeds 300,000, developability (unnecessary portion by development, easily It tends to decrease properties) that can be removed.

【0039】また、蛍光体を含有する熱可塑性樹脂層A Further, the thermoplastic resin layer A containing a phosphor
が、公知の各種現像液により現像可能となるように、側鎖にエチレン性不飽和基を有する光重合性高分子結合剤のカルボキシル基含有率(酸価(mgKOH/g)で規定できる)を適宜調整することができる。 But so as to be developed by various known developing solution, a carboxyl group content of the photopolymerizable polymer binder having an ethylenically unsaturated group in its side chain (it can be defined by the acid value (mg KOH / g)) it can be appropriately adjusted. 例えば、炭酸ナトリウム又は炭酸カリウム等のアルカリ水溶液を用いて現像する場合には、酸価を、90〜260とすることが好ましい。 For example, in the case of developing using an alkaline aqueous solution such as sodium carbonate or potassium carbonate, the acid value is preferably set to 90 to 260. この酸価が、90未満では、現像が困難となる傾向があり、260を超えると、耐現像液性(現像により除去されずに残りパターンとなる部分が、現像液によって侵されない性質)が低下する傾向がある。 The acid value is less than 90, there is a tendency that development becomes difficult, and when it is more than 260, developing solution resistance (the remaining pattern portion without being removed by development is not affected by the developer properties) decrease there is a tendency to. また、水又はアルカリ水溶液と一種以上の有機溶剤とからなる水系現像液を用いて現像する場合には、酸価を、16〜26 Further, in the case of developing using an aqueous developer consisting of water or an alkaline aqueous solution and one or more organic solvents, an acid value, 16-26
0とすることが好ましい。 0 it is preferable that the. この酸価が、16未満では、 The acid value is less than 16,
現像が困難となる傾向があり、260を超えると、耐現像液性が低下する傾向がある。 Tend to development becomes difficult, and when it exceeds 260, developing solution resistance tends to decrease. さらに、1,1,1−トリクロロエタン等の有機溶剤現像液又はエマルション現像液を用いる場合には、カルボキシル基を含有しなくてもよい。 Furthermore, in the case of using an organic solvent developer or an emulsion developer 1,1,1-trichloroethane and the like, it may contain no carboxyl group.

【0040】本発明における(c)活性光の照射により遊離ラジカルを生成する光開始剤としては、例えば、芳香族ケトン(ベンゾフェノン、N,N′−テトラメチル−4,4′−ジアミノベンゾフェノン(ミヒラーケトン)、N,N′−テトラエチル−4,4′−ジアミノベンゾフェノン、4−メトキシ−4′−ジメチルアミノベンゾフェノン、1−ヒドロキシ−シクロヘキシル−フェニル−ケトン、2,4−ジエチルチオキサントン、2− [0040] As the photoinitiator generating free radicals by irradiation of (c) activating light in the present invention, for example, aromatic ketones (benzophenone, N, N'-tetramethyl-4,4'-diamino benzophenone (Michler's ketone ), N, N'-tetraethyl-4,4'-diamino benzophenone, 4-methoxy-4'-dimethylamino benzophenone, 1-hydroxy - cyclohexyl - phenyl - ketone, 2,4-diethyl thioxanthone, 2-
エチルアントラキノン、フェナントレンキノン等)、ベンゾインエーテル(ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインフェニルエーテル等)、ベンゾイン(メチルベンゾイン、エチルベンゾイン等)、ベンジル誘導体(2−ベンジル−2−ジメチルアミノ−1−(4−モルホリノフェニル)−ブタノン− Ethylanthraquinone, phenanthrenequinone, etc.), benzoin ethers (benzoin methyl ether, benzoin ethyl ether, benzoin phenyl ether, etc.), benzoin (methyl benzoin, ethyl benzoin, etc.), benzyl derivatives (2-benzyl-2-dimethylamino-1- ( 4-morpholinophenyl) - butanone -
1、2−メチル−1−(4−(メチルチオ)フェニル) Methyl 1,2-1- (4- (methylthio) phenyl)
−2−モルホリノプロパノン−1、2,2−ジメトキシ−1,2−ジフェニルエタン−1−オン、ベンジルジメチルケタール等)、2,4,5−トリアリールイミダゾール二量体(2−(o−クロロフェニル)−4,5−ジフェニルイミダゾール二量体、2−(o−クロロフェニル)−4,5−ジ(m−メトキシフェニル)イミダゾール二量体、2−(o−フルオロフェニル)−4,5−フェニルイミダゾール二量体、2−(o−メトキシフェニル)−4,5−ジフェニルイミダゾール二量体、2− 2-morpholinopropanone-1,2,2-dimethoxy-1,2-benzyl dimethyl ketal), 2,4,5-triaryl imidazole dimer (2-(o- chlorophenyl) -4,5-diphenyl imidazole dimer, 2-(o-chlorophenyl) -4,5-di (m-methoxyphenyl) imidazole dimer, 2-(o-fluorophenyl) -4,5 phenylimidazole dimer, 2- (o-methoxyphenyl) -4,5-diphenyl imidazole dimer, 2-
(p−メトキシフェニル)−4,5−ジフェニルイミダゾール二量体、2,4−ジ(p−メトキシフェニル)− (P- methoxyphenyl) -4,5-diphenyl imidazole dimer, 2,4-di (p- methoxyphenyl) -
5−フェニルイミダゾール二量体、2−(2,4−ジメトキシフェニル)−4,5−ジフェニルイミダゾール二量体等)、アクリジン誘導体(9−フェニルアクリジン、1,7−ビス(9,9′−アクリジニル)ヘプタン等)などが挙げられる。 5-phenylimidazole dimer, 2- (2,4-dimethoxyphenyl) -4,5-diphenyl imidazole dimer, etc.), acridine derivatives (9-phenyl acridine, 1,7-bis (9,9'- acridinyl) heptane and the like), and the like. これらは単独で又は2種類以上を組み合わせて使用される。 These may be used alone or in combination of two or more.

【0041】本発明における(a)成分の配合量は、 The amount of component (a) in the present invention,
(a)成分及び(b)成分の総量が100重量部として、10〜90重量部とすることが好ましく、20〜8 As the total amount of components (a) and component (b) is 100 parts by weight, preferably 10 to 90 parts by weight, 20-8
0重量部とすることがより好ましい。 More preferably 0 parts by weight. この配合量が、1 The amount is, 1
0重量部未満では、感光性エレメントとしてロール状で供給した場合、感光性樹脂組成物がロール端部からしみ出す(以下エッジフュージョンと記す)ことにより、感光性エレメントのラミネート時にロールからの繰り出しが困難となり、また、しみ出した部分が、PDP用基板等を使用した場合には、PDP用基板の空間に部分的に過剰に埋め込まれ、製造歩留りが著しく低下する等の問題が生じたり、フィルム形成性が低下する傾向があり、 Is less than 0 parts by weight, when supplied in roll form as a photosensitive element, by which the photosensitive resin composition is exuded from the roll end (hereinafter referred to as edge fusion), the feeding of the roll when laminating the photosensitive element It becomes difficult, and when the exuded portion, was used for PDP substrates, etc., partially embedded in excess into the space PDP substrate, or cause problems such as production yield is remarkably lowered, the film There is a tendency for formation of drops,
90重量部を超えると、感度が不充分となる傾向がある。 When more than 90 parts by weight, there is a tendency that the sensitivity becomes insufficient.

【0042】本発明における(b)成分の配合量は、 The amount of component (b) in the present invention,
(a)成分及び(b)成分の総量が100重量部として、10〜90重量部とすることが好ましく、20〜8 As the total amount of components (a) and component (b) is 100 parts by weight, preferably 10 to 90 parts by weight, 20-8
0重量部とすることがより好ましい。 More preferably 0 parts by weight. この配合量が、1 The amount is, 1
0重量部未満では、感光性樹脂組成物の感度が不充分となる傾向があり、90重量部を超えると、光硬化物が脆くなる傾向があり、また、感光性エレメントとした場合に、感光性樹脂組成物が流動によって端部からしみ出したり、フィルム形成性が低下する傾向がある。 Is less than 0 part by weight, there is a tendency that the sensitivity of the photosensitive resin composition becomes insufficient, and when it exceeds 90 parts by weight, there is a tendency that the photocured product becomes brittle and, when the photosensitive element, the photosensitive or exuded from the edge portion sexual resin composition by the flow, the film-forming property tends to be lowered.

【0043】本発明における(c)成分の配合量は、 [0043] The amount of component (c) in the present invention,
(a)成分及び(b)成分の総量100重量部に対して、0.01〜30重量部とすることが好ましく、0. Based on 100 parts by weight of component (a) and component (b), preferably to 0.01 to 30 parts by weight, 0.
1〜20重量部とすることがより好ましい。 And more preferably 1 to 20 parts by weight. この配合量が、0.01重量部未満では、感光性樹脂組成物の感度が不充分となる傾向があり、30重量部を超えると、感光性樹脂組成物の露光表面での活性光の吸収が増大して、内部の光硬化が不充分となる傾向がある。 If the amount is less than 0.01 part by weight, there is a tendency that the sensitivity of the photosensitive resin composition becomes insufficient, and when it exceeds 30 parts by weight, the absorption of the active light at the exposure surface of the photosensitive resin composition there was increased, there is a tendency that the interior of the light curing becomes insufficient.

【0044】本発明における熱可塑性樹脂層Aを構成する感光性樹脂組成物には、公知の染料、顔料、発色剤、 [0044] The photosensitive resin composition constituting the thermoplastic resin layer A in the present invention, known dyes, pigments, coloring agents,
可塑剤、重合禁止剤、表面改質剤、安定剤、密着性付与剤、熱硬化剤等を必要に応じて添加することができる。 Plasticizers, polymerization inhibitors, surface modifiers, stabilizers, adhesion imparting agent, a heat curing agent, etc. may be added as necessary.
このような熱可塑性樹脂層Aを構成する感光性樹脂組成物は、プリント配線板製造用樹脂、カラーフィルタ製造用樹脂等として、好適に使用することができる。 Such a photosensitive resin composition that constitutes the thermoplastic resin layer A printed wiring board for producing a resin, as a color filter for producing resins can be suitably used.

【0045】また、本発明における熱可塑性樹脂層Aを構成する感光性樹脂組成物は、これに(d)蛍光体を含ませることにより、PDP用基板製造用樹脂、EL基板製造用樹脂、フィールドエミッションディスプレイ用蛍光体層形成樹脂等として使用することができる。 Further, the photosensitive resin composition constituting the thermoplastic resin layer A in the present invention, which in (d) of by including the phosphor, PDP substrate for producing a resin, EL substrates for producing resins, field it can be used as the phosphor layer forming resin for emission displays.

【0046】本発明における(d)蛍光体としては、特に限定はなく、通常の金属酸化物を主体とするものが使用できる。 [0046] As (d) the phosphor in the present invention is not particularly limited, those mainly comprising normal metal oxides can be used. 赤色発色の蛍光体としては、例えば、Y 22 The phosphor of the red color, for example, Y 2 O 2
S:Eu、Zn 3 (PO 4 ) 2 :Mn、Y 23 :Eu、YV S: Eu, Zn 3 (PO 4) 2: Mn, Y 2 O 3: Eu, YV
4 :Eu、(Y,Gd)BO 3 :Eu、γ−Zn 3 (PO 4 ) O 4: Eu, (Y, Gd) BO 3: Eu, γ-Zn 3 (PO 4)
2:Mn、(ZnCd)S:Ag+In 2 O等が挙げられる。 2: Mn, (ZnCd) S : Ag + In 2 O , and the like. 緑色発色の蛍光体としては、例えば、ZnS:C The phosphor of the green color, for example, ZnS: C
u、Zn 2 SiO 4 :Mn、ZnS:Cu+Zn 2 Si u, Zn 2 SiO 4: Mn , ZnS: Cu + Zn 2 Si
4 :Mn、Gd 22 S:Tb、Y 3 Al 512 :Ce、 O 4: Mn, Gd 2 O 2 S: Tb, Y 3 Al 5 O 12: Ce,
ZnS:Cu,Al、Y 22 S:Tb、ZnO:Zn、 ZnS: Cu, Al, Y 2 O 2 S: Tb, ZnO: Zn,
ZnS:Cu,Al+In 23 、LaPO 4 :Ce,T ZnS: Cu, Al + In 2 O 3, LaPO 4: Ce, T
b、BaO・6Al 23 :Mn等が挙げられる。 b, BaO · 6Al 2 O 3 : Mn , and the like. 青色発色の蛍光体としては、例えば、ZnS:Ag、ZnS: The phosphor of blue color, for example, ZnS: Ag, ZnS:
Ag,Al、ZnS:Ag,Ga,Al、ZnS:A Ag, Al, ZnS: Ag, Ga, Al, ZnS: A
g,Cu,Ga,Cl、ZnS:Ag+In 23 、Ca g, Cu, Ga, Cl, ZnS: Ag + In 2 O 3, Ca
259 Cl:Eu 2+ 、(Sr,Ca,Ba,Mg) 10 (P 2 B 5 O 9 Cl: Eu 2+, (Sr, Ca, Ba, Mg) 10 (P
4 ) 6 Cl 2 :Eu 2+ 、Sr 10 (PO 4 ) 6 Cl 12 :Eu 2+ O 4) 6 Cl 2: Eu 2+, Sr 10 (PO 4) 6 Cl 12: Eu 2+,
BaMgAl 1017 :Eu 2+ 、BaMgAl 1423 :E BaMgAl 10 O 17: Eu 2+, BaMgAl 14 O 23: E
2+ 、BaMgAl 1626 :Eu 2+等が挙げられる。 u 2+, BaMgAl 16 O 26: Eu 2+ and the like.

【0047】本発明における(d)蛍光体の粒径は、 [0047] The particle size of the (d) phosphor of the present invention,
0.1〜20μmであることが好ましく、1〜15μm It is preferably a 0.1~20μm, 1~15μm
であることがより好ましく、2〜8μmであることが特に好ましい。 More preferably, particularly preferably 2 to 8 m. この粒径が0.1μm未満では、発光効率が低下する傾向があり、また、20μmを超えると、分散性が低下する傾向がある。 This particle size is less than 0.1 [mu] m, there is a tendency that emission efficiency is lowered, and if more than 20 [mu] m, there is a tendency that dispersibility decreases. また、本発明における(d)蛍光体の形状としては、球形であることが好ましく、その表面積はより小さい方が好ましい。 The shape of (d) the phosphor in the present invention is preferably a spherical shape, its surface area is preferably smaller.

【0048】本発明における(d)成分の配合量は、 The amount of component (d) in the present invention,
(a)成分、(b)成分及び(c)成分の総量100重量部に対して、10〜400重量部とすることが好ましく、50〜350重量部とすることがより好ましく、7 Component (a), based on 100 parts by weight of component (b) and component (c), preferably to 10 to 400 parts by weight, more preferably to 50 to 350 parts by weight, 7
0〜300重量部とすることが特に好ましい。 It is particularly preferred to 0-300 parts by weight. この配合量が、10重量部未満では、PDPとして発光させた場合に発光効率が低下する傾向があり、400重量部を超えると、感光性エレメントとした場合に、フィルム形成性が低下したり、可とう性が低下する傾向がある。 If the amount is less than 10 parts by weight, there is a tendency that emission efficiency is lowered when the light is emitted as a PDP, if it exceeds 400 parts by weight, when the photosensitive element, a film forming property is lowered, flexibility tends to decrease.

【0049】本発明における熱可塑性樹脂層Aを構成する感光性樹脂組成物には、フィルム性を良好なものとするために可塑剤を添加することができる。 [0049] The photosensitive resin composition constituting the thermoplastic resin layer A in the present invention may be added a plasticizer to the film properties good. 可塑剤としては、一般式(II) As the plasticizer, the general formula (II)

【化3】 [Formula 3] (式中、R 5は水素原子、メチル基を示し、Y 1は水素原子、置換基を有していてもよい飽和の炭化水素基若しくはポリアルキレングリコール残基を示し、Y 2は、水酸基、置換基を有していてもよい飽和の炭化水素基若しくはポリアルキレングリコール残基を示し、aは1〜10 (Wherein, R 5 represents a hydrogen atom, a methyl group, Y 1 represents a hydrocarbon group or a polyalkylene glycol residue hydrogen atom, a saturated which may have a substituent group, Y 2 is a hydroxyl group, it may have a substituent represents a hydrocarbon group or a polyalkylene glycol residue saturation, a is 1 to 10
0の整数を示す)で表されるポリプロピレングリコール及びその誘導体、ポリエチレングリコール及びその誘導体などのポリアルキレングリコール誘導体並びにジオクチルフタレート、ジヘプチルフタレート、ジブチルフタレート、トリクレジルフォスフェート、クレジルジフェニルフォスフェート、ビフェニルジフェニルフォスフェート等が挙げられる。 Polypropylene glycol and derivatives thereof represented by 0 an integer of), polyethylene glycol and polyalkylene glycol derivatives and dioctyl phthalate, such as derivatives thereof, di-heptyl phthalate, dibutyl phthalate, tricresyl phosphate, cresyl diphenyl phosphate, biphenyl diphenyl phosphate, and the like.

【0050】可塑剤の配合量は、(a)及び(b)成分の総量が100重量部として、0〜90重量部とすることが好ましく、0〜80重量部とすることがより好ましく、0〜70重量部とすることが特に好ましい。 The amount of the plasticizer, the total amount 100 parts by weight of components (a) and (b), preferably to 0 to 90 parts by weight, more preferably to 0 to 80 parts by weight, 0 it is particularly preferable to 70 parts by weight. この配合量が、90重量部を超えると、熱可塑性樹脂層Aを構成する感光性樹脂組成物の感度が不充分となる傾向がある。 This amount tends to exceeds 90 parts by weight, the sensitivity of the photosensitive resin composition constituting the thermoplastic resin layer A is insufficient.

【0051】本発明における熱可塑性樹脂層Aを構成する感光性樹脂組成物には、長期間増粘を起こさず、貯蔵安定性を良好にするために、カルボキシル基を有する化合物を含有させることができる。 [0051] The photosensitive resin composition constituting the thermoplastic resin layer A in the present invention, without causing thickening long time, in order to improve the storage stability, also contain a compound having a carboxyl group it can. カルボキシル基を有する化合物としては、例えば、飽和脂肪酸、不飽和脂肪酸、脂肪族二塩基酸、芳香族二塩基酸、脂肪族三塩基酸、芳香族三塩基酸等が挙げられる。 The compound having a carboxyl group, for example, saturated fatty acids, unsaturated fatty acids, aliphatic dibasic acid, an aromatic dibasic acids, aliphatic tribasic acid, aromatic tribasic acid and the like.

【0052】具体的には、例えば、ぎ酸、酢酸、クロロ酢酸、ジクロロ酢酸、トリクロロ酢酸、プロピオン酸、 [0052] Specifically, for example, formic acid, acetic acid, chloroacetic acid, dichloroacetic acid, trichloroacetic acid, propionic acid,
カプリン酸、ウンデカン酸、ラウリン酸、トリデカン酸、ミリスチン酸、ペンタデカン酸、パルミチン酸、ヘプタデカン酸、ステアリン酸、ノナデカン酸、アラキジン酸、パルミトオレイン酸、オレイン酸、エライジン酸、リノレン酸、リノール酸、しゅう酸、マロン酸、メチルマロン酸、エチルマロン酸、マロン酸モノメチル、 Capric acid, undecanoic acid, lauric acid, tridecanoic acid, myristic acid, pentadecanoic acid, palmitic acid, heptadecanoic acid, stearic acid, nonadecanoic acid, arachidic acid, palmitoleic acid, oleic acid, elaidic acid, linolenic acid, linoleic acid, oxalic acid, malonic acid, methylmalonic acid, ethyl malonate, monomethyl malonate,
マロン酸モノエチル、こはく酸、メチルこはく酸、アジピン酸、メチルアジピン酸、ピメリン酸、スベリン酸、 Malonic acid monoethyl succinic acid, methyl succinic acid, adipic acid, methyl adipic acid, pimelic acid, suberic acid,
アゼライン酸、セバシン酸、マレイン酸、イタコン酸、 Azelaic acid, sebacic acid, maleic acid, itaconic acid,
フタル酸、イソフタル酸、テレフタル酸、トリメリト酸、クエン酸、サリチル酸、ピルビン酸、リンゴ酸等が挙げられる。 Phthalic acid, isophthalic acid, terephthalic acid, trimellitic acid, citric acid, salicylic acid, pyruvic acid, and malic acid. 中でも、増粘を抑制する効果が高い点から、しゅう酸、マロン酸、メチルマロン酸、エチルマロン酸、クエン酸等が好ましく、しゅう酸、マロン酸、クエン酸等がより好ましい。 Among these, from the viewpoint of high effect of suppressing the thickening, oxalic acid, malonic acid, methylmalonic acid, ethyl malonic acid, and citric acid are preferred, oxalic acid, malonic acid, and citric acid are more preferable. これらは単独で又は2種類以上組み合わせて使用される。 These may be used alone or in combination of two or more.

【0053】カルボキシル基を有する化合物の配合量は、(a)成分100重量部に対して、0〜30重量部とすることが好ましく、0.01〜30重量部とすることがより好ましい。 [0053] The amount of a compound having a carboxyl group, to the component (a) 100 parts by weight, preferably to 0 to 30 parts by weight, and more preferably in a 0.01 to 30 parts by weight. この配合量が、30重量部を超えると感度が不充分となる傾向がある。 This amount tends to be insufficient sensitivity exceeds 30 parts by weight.

【0054】本発明における熱可塑性樹脂層Aを構成する感光性樹脂組成物には、蛍光体の分散を良好とするために、分散剤を添加することが好ましい。 [0054] The photosensitive resin composition constituting the thermoplastic resin layer A in the present invention, in order to obtain a good dispersion of the phosphor, it is preferable to add a dispersing agent. 分散剤としては、無機分散剤(シリカゲル系、ベントナイト系、カオリナイト系、タルク系、ヘクトライト系、モンモリロナイト系、サポナイト系、バイデライト系等)、有機分散剤(脂肪族アマイド系、脂肪族エステル系、酸化ポリエチレン系、硫酸エステル系アニオン活性剤、ポリカルボン酸アミン塩系、ポリカルボン酸系、ポリアマイド系、 As the dispersant, inorganic dispersant (silica gel-based, bentonite, kaolinite type, talc-based, hectorite type, montmorillonite, saponite type, beidellite system, etc.), organic dispersant (aliphatic amide, aliphatic ester , polyethylene oxide-based, sulfate ester-based anionic surfactants, polycarboxylic acid amine salt-based, polycarboxylic acid, polyamide-based,
高分子ポリエーテル系、アクリル共重合物系、特殊シリコン系等)等が挙げられる。 Polymeric polyether, acrylic copolymer-based, and special silicon-based) or the like. これらは単独で又は2種類以上を組み合わせて使用することができる。 These may be used alone or in combination of two or more.

【0055】分散剤の使用量としては、特に制限はなく、(a)成分100重量部に対して、0〜100重量部とすることが好ましく0.01〜100重量部とすることがより好ましい。 [0055] The use amount of the dispersant is not particularly limited, (a) with respect to 100 parts by weight of component, and more preferably it is a preferably 0.01 to 100 parts by weight of 0 to 100 parts by weight . この使用量が、100重量部を超えると、パターン形成精度(蛍光体を含有する感光性樹脂組成物からなるパターンを、現像後、寸法的に正確に、所望の形状で得られる性質)が低下する傾向がある。 This amount is more than 100 parts by weight, reduced patterning accuracy (a pattern composed of the photosensitive resin composition containing a phosphor, after development, in dimensionally accurate, properties obtained with the desired shape) there is a tendency to.

【0056】本発明における熱可塑性樹脂層Aを構成する感光性樹脂組成物には、焼成後、PDP用基板から蛍光体が剥離しないようにするために、結着剤を使用することができる。 [0056] The photosensitive resin composition constituting the thermoplastic resin layer A in the present invention, after calcination, to the phosphor from the substrate for PDP is prevented from peeling, it can be used a binder. 結着剤としては、例えば、低融点ガラス、金属アルコキシド、シランカップリング剤等が挙げられる。 As the binder, for example, low-melting glass, metal alkoxide, silane coupling agent, and the like. これらは単独で又は2種類以上を組み合わせて使用される。 These may be used alone or in combination of two or more. 結着剤の使用量としては、特に制限はなく、(d)成分100重量部に対して、0〜100重量部とすることが好ましく、0〜50重量部とすることがより好ましく、0〜30重量部とすることが特に好ましい。 The amount of the binder is not particularly limited, with respect to 100 parts by weight of component (d), preferably to 0 to 100 parts by weight, more preferably to 0 to 50 parts by weight, 0 particularly preferably 30 parts by weight. この使用量が、100重量部を超えると、発光効率が低下する傾向がある。 This amount is more than 100 parts by weight, the emission efficiency tends to decrease.

【0057】本発明における熱可塑性樹脂層Aを有するフィルムは、前記熱可塑性樹脂層Aを構成する各成分を、溶解又は分散可能な溶剤に、溶解又は混合させることにより、均一に溶解又は分散した溶液とし、支持体フィルム上に、塗布、乾燥することにより、感光性エレメントとして得ることができる。 Film having a thermoplastic resin layer A in [0057] the present invention, the respective components constituting the thermoplastic resin layer A, the soluble or dispersible solvents, by dissolving or mixing and uniformly dissolving or dispersing a solution, on a support film, coating, followed by drying, can be obtained as a photosensitive element. 前記各成分を、溶解又は分散可能な溶剤としては、例えば、トルエン、アセトン、メチルエチルケトン、メチルイソブチルケトン、メチルセロソルブ、エチルセロソルブ、γ−ブチロラクトン、N−メチルピロリドン、ジメチルホルムアミド、テトラメチルスルホン、ジエチレングリコールジメチルエーテル、ジエチレングリコールモノブチルエーテル、クロロホルム、塩化メチレン、メチルアルコール、エチルアルコール等があげられる。 Wherein each component as a dissolution or dispersible solvents are, for example, toluene, acetone, methyl ethyl ketone, methyl isobutyl ketone, methyl cellosolve, ethyl cellosolve, .gamma.-butyrolactone, N- methylpyrrolidone, dimethylformamide, tetramethyl sulfone, diethylene glycol dimethyl ether , diethylene glycol monobutyl ether, chloroform, methylene chloride, methyl alcohol, ethyl alcohol and the like. これらは単独で又は2種類以上を組み合わせて使用される。 These may be used alone or in combination of two or more.

【0058】支持体フィルムとしては、化学的及び熱的に安定であり、また、可とう性の物質で構成された、例えば、ポリエチレンテレフタレート、ポリカーボネート、ポリエチレン、ポリプロピレン等が挙げられ、その中でも、ポリエチレンテレフタレート、ポリエチレンが好ましく、ポリエチレンテレフタレートがより好ましい。 [0058] As the support film is chemically and thermally stable, also composed of a flexible material, such as polyethylene terephthalate, polycarbonate, polyethylene, polypropylene and the like, and among them, polyethylene terephthalate, polyethylene is preferable, and polyethylene terephthalate is more preferable. 支持体フィルムは、後に熱可塑性樹脂層Aから除去可能でなくてはならないため、除去が不可能となるような表面処理が施されたものであったり、材質であったりしてはならない。 Support film, because must be removed from the thermoplastic resin layer A after, or even those that removal surface treatment such that not has been subjected, must not or a material. 支持体フィルムの厚さは、5〜100 The thickness of the support film, 5 to 100
μmとすることが好ましく、10〜80μmとすることががより好ましく、10〜70μmとすることが特に好ましい。 It is preferable that the [mu] m, is more preferably to 10 to 80 [mu] m, and particularly preferably to 10 to 70 [mu] m.

【0059】塗布方法としては、公知の方法を用いることができ、例えば、ナイフコート法、ロールコート法、 [0059] As the coating method may be a known method, for example, knife coating, roll coating,
スプレーコート法、グラビアコート法、バーコート法、 Spray coating method, gravure coating method, bar coating method,
カーテンコート法等が挙げられる。 A curtain coating method, and the like. 乾燥温度は、60〜 The drying temperature is 60
130℃とすることが好ましく、乾燥時間は、3分〜1 Preferably to 130 ° C., the drying time is 3 minutes to one
時間とすることが好ましい。 It is preferable that the time.

【0060】感光性エレメントの熱可塑性樹脂層Aの厚さは、特に制限はないが、プリント配線板用基板の製造に使用する場合や、カラーフィルタの画素として使用する場合は、その膜厚は、1〜10μmとすることが好ましく、1〜5μmとすることがより好ましい。 [0060] The thickness of the thermoplastic resin layer A of the photosensitive element is not particularly limited, and when used in the manufacture of a substrate for a printed wiring board, when used as a pixel of a color filter, the thickness , preferably to 1 to 10 [mu] m, and more preferably to 1 to 5 [mu] m. また、P In addition, P
DP用基板の製造に使用する場合は、その膜厚は、10 When used in the production of DP substrate, the film thickness is 10
〜200μmとすることが好ましく、20〜120μm It is preferable that the ~200μm, 20~120μm
とすることがより好ましく、20〜80μmとすることが特に好ましく、30〜80μmとすることが最も好ましい。 More preferably to, particularly preferably to 20 to 80 [mu] m, and most preferably to 30 to 80 [mu] m. この膜厚が、10μm未満では、後述する焼成後の蛍光体パターンが薄くなり、発光効率が低下する傾向があり、200μmを超えると、焼成後の蛍光体パターンが厚くなり、放電空間が少なくなる傾向がある。 The film thickness is less than 10 [mu] m, thinner phosphor pattern after calcination to be described later, there is a tendency that emission efficiency is reduced, if it exceeds 200 [mu] m, phosphor pattern after calcination becomes thick, the discharge space is reduced Tend.

【0061】感光性エレメントの熱可塑性樹脂層Aは、 [0061] The thermoplastic resin layer A of the photosensitive element,
100℃での粘度が1〜1×10 9 Pa・secであることが好ましく、2〜1×10 8 Pa・secであることがより好ましく、5〜1×10 7 Pa・secであることが特に好ましく、10〜1×10 6 Pa・secであることが極めて好ましい。 Preferably the viscosity at 100 ° C. is 1~1 × 10 9 Pa · sec, more preferably 2~1 × 10 8 Pa · sec, it is 5~1 × 10 7 Pa · sec particularly preferred, extremely preferably 10~1 × 10 6 Pa · sec. この100℃での粘度が、1Pa・sec未満では、室温での粘度が低くなりすぎて感光性エレメントとした場合に、熱可塑性樹脂層Aが流動により端部から滲み出す傾向があり、フィルム形成性が低下する傾向がある。 The viscosity at this 100 ° C. is less than 1 Pa · sec, when the viscosity is too low the photosensitive element at room temperature, the thermoplastic resin layer A tends to bleed from the edge by the flow, the film-forming gender tends to decrease. また、1×10 9 Pa・secを超えると、PDP用基板の製造等に使用する場合に、凹凸を有する基板の凹部内面への熱可塑性樹脂層Aの形成性が低下する傾向がある。 Further, 1 the × exceeds 10 9 Pa · sec, when used in the manufacture or the like of the substrate for PDP, formation of the thermoplastic resin layer A to the recess inner surface of a substrate having an uneven tends to decrease.

【0062】感光性エレメントの熱可塑性樹脂層Aの上には、さらに剥離可能なカバーフィルムを積層することができる。 [0062] On the thermoplastic resin layer A of the photosensitive element, it can be further laminated peelable cover film. カバーフィルムとしては、ポリエチレン、ポリプロピレン、ポリエチレンテレフタレート、ポリカーボネート等が挙げられ、支持体フィルムと熱可塑性樹脂層Aとの接着力よりも、カバーフィルムと熱可塑性樹脂層Aとの接着力の方が小さいものであることが好ましい。 The cover film of polyethylene, polypropylene, polyethylene terephthalate, polycarbonate and the like, than the adhesion between the support film and the thermoplastic resin layer A, the smaller the adhesive force between the cover film and the thermoplastic resin layer A it is preferable that. このようにして得られる感光性エレメントは、ロール状に巻いて保管可能とすることができる。 Such photosensitive element obtained in this may be a storable wound into a roll.

【0063】本発明における熱可塑性樹脂層Bを構成する(e)熱可塑性樹脂としては、熱可塑性を有する樹脂であれば特に制限はないが、例えば、ポリエチレン、ポリプロピレン、ポリ塩化ビニル、ポリ酢酸ビニル、ポリ塩化ビニリデン、ポリスチレン、ポリビニルトルエン、 [0063] As the thermoplastic resin layer constituting the B (e) a thermoplastic resin in the present invention is not particularly limited as long as it is a resin having thermoplasticity, such as polyethylene, polypropylene, polyvinyl chloride, polyvinyl acetate , polyvinylidene chloride, polystyrene, polyvinyl toluene,
ポリアクリル酸エステル、ポリメタクリル酸エステル、 Polyacrylic acid ester, polymethacrylic acid ester,
エチレンと酢酸ビニルの共重合体、エチレンとアクリル酸エステルの共重合体、塩化ビニルと酢酸ビニルの共重合体、スチレンとアクリル酸エステル又はメタクリル酸エステルとの共重合体、ビニルトルエンとアクリル酸エステル又はメタクリル酸エステルとの共重合体、ポリビニルアルコール系樹脂(ポリアクリル酸エステル又はポリメタクリル酸エステルの加水分解物、ポリ酢酸ビニルの加水分解物、エチレンと酢酸ビニルとの共重合体の加水分解物、エチレンとアクリル酸エステルとの共重合体の加水分解物、塩化ビニルと酢酸ビニルとの共重合体の加水分解物、スチレンとアクリル酸エステル又はメタクリル酸エステルとの共重合体の加水分解物、ビニルトルエンとアクリル酸エステル又はメタクリル酸エステルとの共重合体の加水 Copolymers of ethylene and vinyl acetate, copolymers of ethylene and acrylic acid ester, copolymers of vinyl chloride and vinyl acetate, a copolymer of styrene and acrylic acid esters or methacrylic acid esters, vinyl toluene and acrylic acid ester or a copolymer of methacrylic acid esters, polyvinyl alcohol resins (polyacrylic acid ester or a hydrolyzate of polymethacrylic acid ester, a hydrolyzate of polyvinyl acetate, a hydrolyzate of a copolymer of ethylene and vinyl acetate , hydrolyzate of a copolymer of ethylene and acrylic acid ester, a hydrolyzate of a copolymer of vinyl chloride and vinyl acetate, a hydrolyzate of a copolymer of styrene and acrylic acid ester or methacrylic acid ester, hydrolysis of a copolymer of vinyl toluene and acrylic acid ester or methacrylic acid ester 解物等)、カルボキシアルキルセルロースの水溶性塩、水溶性セルロースエーテル類、カルボキシアルキルでん粉の水溶性塩、ポリビニルピロリドン、不飽和カルボン酸とこれらと共重合可能な不飽和単量体を共重合することにより得られるカルボキシル基を有する樹脂などが挙げられる。 Solutions, etc.), water-soluble salts of carboxyalkyl cellulose, water-soluble cellulose ethers, water-soluble salts of carboxyalkyl starch, polyvinyl pyrrolidone, co-polymerizing an unsaturated carboxylic acid and copolymerizable with these unsaturated monomers a resin having a carboxyl group obtained by the like.

【0064】また、熱可塑性樹脂層Bは、PDP用基板の製造等に使用する場合において、混色防止、作業性、 [0064] Further, the thermoplastic resin layer B, when used for the manufacture or the like of the substrate for PDP, preventing color mixture, workability,
フィルム性の向上等の点から、可塑剤を含有させることもできる。 From the viewpoint of improvement of the film properties, it may contain a plasticizer. 使用する可塑剤としては、(b)末端にエチレン性不飽和基を有する光重合性不飽和化合物、前記一般式(II)で表されるポリプロピレングリコール及びその誘導体、ポリエチレングリコール及びその誘導体などのポリアルキレングリコール誘導体、ジオクチルフタレート、ジヘプチルフタレート、ジブチルフタレート、 The plasticizer to be used, (b) a photopolymerizable unsaturated compound having an ethylenically unsaturated group at the terminal, polypropylene glycol and derivatives thereof represented by the general formula (II), such as poly polyethylene glycol and derivatives thereof alkylene glycol derivatives, dioctyl phthalate, di-heptyl phthalate, dibutyl phthalate,
トリクレジルフォスフェート、クレジルジフェニルフォスフェート、ビフェニルジフェニルフォスフェート等が挙げられる。 Tricresyl phosphate, cresyl diphenyl phosphate, biphenyl diphenyl phosphate, and the like. また、熱可塑性樹脂層Bには、(c)活性光の照射により遊離ラジカルを生成する光開始剤を含有してもよい。 Further, the thermoplastic resin layer B, may contain a photoinitiator that generates free radicals by irradiation of (c) active light.

【0065】熱可塑性樹脂層Bに含有される(e)熱可塑性樹脂成分の配合量は、樹脂成分及び可塑剤成分の総量が100重量部として、10〜100重量部とすることが好ましく、20〜100重量部とすることがより好ましい。 [0065] The amount of the thermoplastic resin layer (e) a thermoplastic resin component contained in B are, as the total amount of 100 parts by weight of the resin component and the plasticizer component preferably has 10 to 100 parts by weight, 20 and more preferably to 100 parts by weight. この配合量が、10重量部未満では、エレメントとした場合に、樹脂組成物が流動によって端部からしみ出したり、フィルム形成性が低下する等の傾向がある。 If the amount is less than 10 parts by weight, when an element, or exuded from the end resin composition by the flow, the film-forming property tends such to decrease.

【0066】また、熱可塑性樹脂層Bに含有される可塑剤成分の配合量は、樹脂成分及び可塑剤成分の総量が1 [0066] The amount of plasticizer component contained in the thermoplastic resin layer B, the total amount of the resin component and the plasticizer component 1
00重量部として、0〜90重量部とすることが好ましく、0〜80重量部とすることがより好ましい。 As 00 parts by weight, preferably to 0-90 parts by weight, and more preferably to 0 to 80 parts by weight. この配合量が、90重量部を超えると、エレメントとした場合に、流動によって端部からしみ出したり、フィルム形成性が低下する等の傾向がある。 This amount is more than 90 parts by weight, when an element, or exuded from the end by the flow, there is a tendency such that the film forming property is lowered.

【0067】さらに、熱可塑性樹脂層Bに含有される(c)活性光の照射により遊離ラジカルを生成する光開始剤成分の配合量は、樹脂成分及び可塑剤成分の総量が100重量部として、0〜30重量部とすることが好ましく、0〜20重量部とすることがより好ましい。 [0067] Further, the amount of the photoinitiator component to generate free radicals by irradiation of contained in the thermoplastic resin layer B (c) activating light is, the total amount of the resin component and the plasticizer component is 100 parts by weight, preferably to 0 to 30 parts by weight, and more preferably 0 to 20 parts by weight. この配合量が、30重量部を超えると、露光表面での活性光の吸収が増大して、内部の光硬化が不充分となる傾向がある。 This amount is more than 30 parts by weight, and the absorption of the active light in the exposure surface is increased, there is a tendency that the interior of the light-curing may be insufficient.

【0068】また、本発明における熱可塑性樹脂層B [0068] Further, the thermoplastic resin layer B in the present invention
は、後述する現像工程において、熱可塑性樹脂層A及び熱可塑性樹脂層Bが、同一の現像液を使用して現像できるものであることが、工程を少なくできる点から好ましい。 , In the development process to be described later, the thermoplastic resin layer A and the thermoplastic resin layer B is, it is intended that can be developed using the same developer, from the viewpoint of possible to reduce the process. 同一の現像液で現像できるものとしては、水又はアルカリ水溶液に可溶なものが挙げられる。 As it can be developed with the same developer, those soluble and the like in water or an aqueous alkaline solution.

【0069】水又はアルカリ水溶液に可溶な熱可塑性樹脂層Bを構成する樹脂としては、例えば、ポリビニルアルコール系樹脂(ポリアクリル酸エステル又はポリメタクリル酸エステルの加水分解物、ポリ酢酸ビニルの加水分解物、エチレンと酢酸ビニルとの共重合体の加水分解物、エチレンとアクリル酸エステルとの共重合体の加水分解物、塩化ビニルと酢酸ビニルとの共重合体の加水分解物、スチレンとアクリル酸エステル又はメタクリル酸エステルとの共重合体の加水分解物、ビニルトルエンとアクリル酸エステル又はメタクリル酸エステルとの共重合体の加水分解物等)、カルボキシアルキルセルロースの水溶性塩、水溶性セルロースエーテル類、カルボキシアルキルでん粉の水溶性塩、ポリビニルピロリドン、不飽和カルボン酸と [0069] As the water or the resin constituting the soluble thermoplastic resin layer B in an aqueous alkali solution, for example, polyvinyl alcohol resins (polyacrylic acid ester or a hydrolyzate of polymethacrylic acid esters, polyvinyl acetate hydrolyzed things, a hydrolyzate of a copolymer of ethylene and vinyl acetate, copolymers of hydrolyzate of ethylene and acrylic acid ester, a hydrolyzate of a copolymer of vinyl chloride and vinyl acetate, styrene and acrylic acid hydrolyzate of a copolymer of an ester or methacrylic acid ester, a hydrolyzate of a copolymer of vinyl toluene and acrylic acid ester or methacrylic acid ester, etc.), water-soluble salts of carboxyalkyl cellulose, water-soluble cellulose ethers , water-soluble salts of carboxyalkyl starch, polyvinyl pyrrolidone, unsaturated carboxylic acids れらと共重合可能な不飽和単量体を共重合することにより得られるカルボキシル基を有する樹脂などが挙げられる。 A resin having a carboxyl group obtained by copolymerizing these copolymerizable unsaturated monomers.

【0070】不飽和カルボン酸とこれらと共重合可能な不飽和単量体を共重合することにより得られるカルボキシル基を有する樹脂としては、例えば、不飽和カルボン酸(アクリル酸、メタクリル酸、マレイン酸、フマル酸、イタコン酸等)と、前記熱可塑性樹脂層Aを構成する(a)フィルム性付与ポリマに使用可能なビニル単量体とを共重合して得られるビニル共重合体などを使用することが好ましい。 [0070] As the resin having a carboxyl group obtained by copolymerizing an unsaturated carboxylic acid and copolymerizable with these unsaturated monomers, for example, unsaturated carboxylic acids (acrylic acid, methacrylic acid, maleic acid , using fumaric acid, and itaconic acid, etc.), etc. the thermoplastic resin layer constituting the a (a) film-imparting polymer available vinyl monomer and copolymerizing obtained vinyl copolymer it is preferable. 不飽和カルボン酸とこれらと共重合可能な不飽和単量体を共重合することにより得られるカルボキシル基を有する樹脂は、重量平均分子量が、5, Resin having a carboxyl group obtained by copolymerizing an unsaturated carboxylic acid and these copolymerizable unsaturated monomers, the weight-average molecular weight, 5,
000〜300,000とすることが好ましく、20, It is preferable that the 000~300,000, 20,
000〜150,000とすることがより好ましい。 It is more preferable that the 000~150,000. この重量平均分子量が、5,000未満では、感光性エレメントとした場合にフィルム形成性及び可とう性が低下する傾向があり、300,000を超えると、現像性が低下する傾向がある。 The weight average molecular weight is less than 5,000, there is a tendency that film-forming property and flexibility is lowered when a photosensitive element, exceeds 300,000, there is a tendency that developing property lowers.

【0071】また、アルカリ水溶液に可溶な熱可塑性樹脂層Bとして、公知の各種現像液により現像可能となるように、不飽和カルボン酸とこれらと共重合可能な不飽和単量体を共重合することにより得られるカルボキシル基を有する樹脂のカルボキシル基含有率(酸価(mgKOH/ [0071] Further, as soluble thermoplastic resin layer B in an aqueous alkaline solution, so as to be developed by various known developer, copolymerizing these copolymerizable unsaturated monomer and an unsaturated carboxylic acid carboxyl group content of the resin having a carboxyl group obtained by (acid value (mg KOH /
g)で規定できる)を適宜調整することができる。 Can be defined by g)) can be appropriately adjusted. 例えば、炭酸ナトリウム、炭酸カリウム等のアルカリ水溶液を用いて現像する場合には、酸価が、90〜260とすることが好ましい。 For example, sodium carbonate, when developed with an alkaline aqueous solution such as potassium carbonate, acid value, it is preferable to 90-260. この酸価が、90未満では、現像が困難となる傾向があり、260を超えると、耐現像液性が低下する傾向がある。 The acid value is less than 90, there is a tendency that development becomes difficult, and when it is more than 260, developing solution resistance tends to decrease. また、水又はアルカリ水溶液と一種以上の有機溶剤とからなる水系現像液を用いて現像する場合には、酸価が、16〜260とすることが好ましい。 Further, in the case of developing using an aqueous developer consisting of water or an alkaline aqueous solution and one or more organic solvents, acid value, it is preferable to 16-260. この酸価が、16未満では、現像が困難となる傾向があり、260を超えると、耐現像液性が低下する傾向がある。 The acid value is less than 16, there is a tendency that development becomes difficult, and when it is more than 260, developing solution resistance tends to decrease.

【0072】本発明における熱可塑性樹脂層Bを有するフィルムは、前記熱可塑性樹脂層Bを構成する各成分を溶解する溶剤に、溶解又は混合させることにより、均一な溶液とし、前記した支持体フィルム上に、ナイフコート法、ロールコート法、スプレーコート法、グラビアコート法、バーコート法、カーテンコート法等の公知の塗布方法を用いて、塗布、乾燥することによりフィルム状に形成することができる。 Film having a thermoplastic resin layer B in [0072] the present invention, the solvent which dissolves the respective components constituting the thermoplastic resin layer B, by dissolving or mixing, a homogeneous solution, the support film having the above, knife coating, roll coating, spray coating, gravure coating, bar coating method, a known coating or curtain coating method or the like, coating can be formed into a film by drying . 熱可塑性樹脂層Bを構成する樹脂を溶解する溶剤としては、例えば、水、トルエン、 The solvent for dissolving the resin constituting the thermoplastic resin layer B, for example, water, toluene,
アセトン、メチルエチルケトン、メチルイソブチルケトン、メチルセロソルブ、エチルセロソルブ、γ−ブチルラクトン、N−メチルピロリドン、ジメチルホルムアミド、テトラメチルスルホン、ジエチレングリコールジメチルエーテル、ジエチレングリコールモノブチルエーテル、クロロホルム、塩化メチレン、メチルアルコール、 Acetone, methyl ethyl ketone, methyl isobutyl ketone, methyl cellosolve, ethyl cellosolve, .gamma.-butyrolactone, N- methylpyrrolidone, dimethylformamide, tetramethyl sulfone, diethylene glycol dimethyl ether, diethylene glycol monobutyl ether, chloroform, methylene chloride, methyl alcohol,
エチルアルコール等が挙げられる。 Ethyl alcohol and the like. これらは単独で又は2種類以上を組み合わせて使用される。 These may be used alone or in combination of two or more.

【0073】本発明における熱可塑性樹脂層Bの厚さは、特に制限はないが、PDP用基板の製造に使用する場合において、凹凸を有する基板の凹部内面への埋め込み性等の点から、10〜200μmとすることが好ましく、20〜100μmとすることがより好ましい。 [0073] The thickness of the thermoplastic resin layer B in the present invention is not particularly limited, when used for the manufacture of a substrate for PDP, from the viewpoint of embeddability like into the recess inner surface of the substrate having unevenness, 10 it is preferably in the ~200Myuemu, and more preferably to 20 to 100 [mu] m. また、本発明における熱可塑性樹脂層Bは、100℃での粘度が1〜1×10 9 Pa・secであることが好ましく、2 The thermoplastic resin layer B in the present invention preferably has viscosity at 100 ° C. is 1~1 × 10 9 Pa · sec, 2
〜1×10 8 Pa・secであることがより好ましく、5〜1 More preferably ~1 × 10 8 Pa · sec, 5~1
×10 7 Pa・secであることが特に好ましく、10〜1× Particularly preferably a × 10 7 Pa · sec, 10~1 ×
10 6 Pa・secであることが極めて好ましい。 It is highly preferred is 10 6 Pa · sec. この100 This 100
℃での粘度が、1Pa・sec未満では、室温での粘度が低くなりすぎてフィルムとした場合に、熱可塑性樹脂層Bが流動により端部から滲み出す傾向があり、フィルム形成性が低下する傾向がある。 Viscosity at ℃ is less than 1 Pa · sec, when the film becomes too low viscosity at room temperature, the thermoplastic resin layer B tends to bleed from the edge by the flow, film forming property is lowered Tend. また、1×10 9 Pa・secを超えると、PDP用基板の製造に使用する場合において、 If it exceeds 1 × 10 9 Pa · sec, when used for the manufacture of a substrate for PDP,
凹凸を有する基板の凹部内面への熱可塑性樹脂層Aの形成性が低下する傾向がある。 Forming thermoplastic resin layer A to the recess inner surface of a substrate having an uneven tends to decrease.

【0074】また、本発明における熱可塑性樹脂層Bの上には、さらに剥離可能なカバーフィルムを積層することができる。 [0074] Further, on the thermoplastic resin layer B in the present invention can be further laminated peelable cover film. カバーフィルムとしては、ポリエチレン、 The cover film, polyethylene,
ポリプロピレン、ポリエチレンテレフタレート、ポリカーボネート等が挙げられ、支持体フィルムと熱可塑性樹脂層Bとの接着力よりも、カバーフィルムと熱可塑性樹脂層Bとの接着力の方が小さいものが好ましい。 Polypropylene, polyethylene terephthalate, polycarbonate and the like, than the adhesion between the support film and the thermoplastic resin layer B, those who adhesion between the cover film and the thermoplastic resin layer B is preferably small. このようにしてフィルム状に形成された熱可塑性樹脂層Bは、 The thermoplastic resin layer formed into a film shape B is
ロール状に巻いて保管可能とすることができる。 It can be can be stored wound into a roll.

【0075】本発明における熱可塑性樹脂層Aを有するフィルム及び熱可塑性樹脂層Bを有するフィルムは、作業性等の点から、熱可塑性樹脂層Aを有するフィルムが、支持体フィルム、熱可塑性樹脂層A及びカバーフィルムを有するものであることが好ましく、熱可塑性樹脂層Bを有するフィルムが、支持体フィルム、熱可塑性樹脂層B及びカバーフィルムを有するものであることが好ましい。 [0075] film having the film of the present invention and a thermoplastic resin layer having a thermoplastic resin layer A in B, from the viewpoint of workability, a film having a thermoplastic resin layer A, the support film, a thermoplastic resin layer is preferably those having an a and a cover film, a film having a thermoplastic resin layer B is, the support film is preferably one having a thermoplastic resin layer B and the cover film. また、本発明における熱可塑性樹脂層Aを有するフィルム及び熱可塑性樹脂層Bを有するフィルムは、 Further, a film having a film and the thermoplastic resin layer B having a thermoplastic resin layer A in the present invention,
それぞれの熱可塑性樹脂層は、必ずしも一層である必要はなく、二層以上であってもよい。 Each of the thermoplastic resin layer is not necessarily more, it may be two or more layers.

【0076】本発明における積層方法は、フィルムAを第1の供給部から供給し、フィルムBを第2の供給部から供給して、基板上にフィルムAを、その上にフィルムBを積層する必要があり、その方法としては、以下に示す本発明の積層装置を使用する方法等が挙げられる。 [0076] laminating method in the present invention, the film A is supplied from the first supply unit, the film B is supplied from the second supply unit, the film A on the substrate, laminating the film B thereon must, as the method, the method and the like to use a laminated device of the present invention described below.

【0077】本発明の積層装置は、フィルムAを供給する第1の供給手段、フィルムBを供給する第2の供給手段及び基板上にフィルムAを、その上にフィルムBを積層する積層手段を備えたものである。 [0077] stacking apparatus of the present invention, the first supply means for supplying a film A, the film A in the second supply means and the substrate for supplying the film B, the lamination means for laminating the film B thereon It includes those were. また、本発明の積層装置は、支持体フィルム(5A)、熱可塑性樹脂層A The layered device of the present invention, the support film (5A), the thermoplastic resin layer A
(3)及びカバーフィルム(6A)を有するフィルムA (3) and the film A having a cover film (6A)
並びに支持体フィルム(5B)、熱可塑性樹脂層B And the support film (5B), the thermoplastic resin layer B
(4)及びカバーフィルム(6B)を有するフィルムB (4) and the film B having a cover film (6B)
を用いて、基板(7)上に熱可塑性樹脂層A(3)、その上に熱可塑性樹脂層B(4)を積層する装置であって、フィルムAを供給する第1の供給手段、フィルムB With the substrate (7) the thermoplastic resin layer A (3) on a device for laminating a thermoplastic resin layer B (4) thereon, the first supply means for supplying a film A, film B
を供給する第2の供給手段、カバーフィルム((6A)及び(6B))を取るため手段、支持体フィルム(5A)を取るための手段及び熱可塑性樹脂層A(3)と熱可塑性樹脂層B(4)を積層するための積層手段を備えたものである。 Second supply means for supplying the cover film ((6A) and (6B)) means for taking the means and the thermoplastic resin layer A (3) for taking the support film (5A) and the thermoplastic resin layer B (4) are those having a laminating means for laminating.

【0078】また、本発明の積層装置は、基板(7)を送る搬送手段、フィルムAを供給する第1の供給手段、 [0078] The layered device of the present invention, conveying means for feeding the substrate (7), the first supply means for supplying a film A,
フィルムBを供給する第2の供給手段、カバーフィルム((6A)及び(6B))を取るための手段、熱可塑性樹脂層A(3)又は熱可塑性樹脂層B(4)を有するフィルムを送るための手段、支持体フィルム(5A)を送るための手段、支持体フィルム(5A)を取るための手段、 Send second supply means for supplying a film B, means for taking a cover film ((6A) and (6B)), the thermoplastic resin layer A (3) or the thermoplastic resin layer B of the film having the (4) means for means for sending a support film (5A), means for taking the support film (5A),
熱可塑性樹脂層A(3)又は熱可塑性樹脂層B(4)を有するフィルムを基板(7)に積層する積層手段を設けたものである。 Is provided with a laminating means for laminating a film having a thermoplastic resin layer A (3) or the thermoplastic resin layer B (4) to the substrate (7). 前記した本発明の積層装置としては、具体的には、図3及び図4に示す積層装置等が挙げられる。 The laminating apparatus of the present invention described above, and specific examples thereof include lamination apparatus or the like shown in FIGS.

【0079】以下、図3及び図4を用いて、本発明の積層装置を説明する。 [0079] Hereinafter, with reference to FIGS. 3 and 4, illustrating a stacking device of the present invention. 図3及び図4は、本発明の積層装置の一例を示した模式図である。 3 and 4 are schematic views showing an example of a lamination apparatus of the present invention. 図3の積層装置は、基板(7)を送る搬送ロール(11)、フィルムAを供給する第1の供給ロール(1)、カバーフィルム(6A)を巻取るカバーフィルム巻取ロール(8)、支持体フィルム(5A)及び熱可塑性樹脂層A(3)を有するフィルムを送る送りロール(12)、支持体フィルム(5A) Laminating apparatus of Figure 3, the transport roll to send the substrate (7) (11), a first supply roll for supplying a film A (1), cover film take-up roll for taking up the cover film (6A) (8), feed roll to send a film having a support film (5A) and the thermoplastic resin layer a (3) (12), the support film (5A)
及び熱可塑性樹脂層A(3)を有するフィルムを基板(7)上に積層する積層ロール(10)、支持体フィルム(5A)を送る送りロール(12)、支持体フィルム(5A)を巻取る支持体フィルム巻取ロール(9)、フィルムBを供給する第2の供給ロール(2)、カバーフィルム(6B)を巻取るカバーフィルム巻取ロール(8)、支持体フィルム(5B)及び熱可塑性樹脂層B And laminating roll for laminating a film having a thermoplastic resin layer A (3) on the substrate (7) (10), the feed rolls and sends a support film (5A) (12), winding the support film (5A) support film winding roll (9), a second supply roll for supplying a film B (2), the cover film take-up roll (8) for winding the cover film (6B), the support film (5B) and thermoplastic resin layer B
(4)を有するフィルムを送る送りロール(12)、基板(7)上に積層された熱可塑性樹脂層A(3)の上に、支持体フィルム(5B)及び熱可塑性樹脂層B Feed roll to send a film having a (4) (12), on a substrate (7) the thermoplastic resin layer A (3) laminated on the support film (5B) and the thermoplastic resin layer B
(4)を有するフィルムを積層する積層ロール(10) (4) laminating roll for laminating a film having a (10)
を設けたものである。 In which the provided.

【0080】フィルムAを供給する第1の供給ロール(1)に、支持体フィルム(5A)、熱可塑性樹脂層A [0080] the first supply roll supplying a film A (1), the support film (5A), the thermoplastic resin layer A
(3)及びカバーフィルム(6A)を有するロール状のフィルムAを設置し、カバーフィルム巻取ロール(8) (3) and set up a roll of film A having a cover film (6A), a cover film take-up roll (8)
で、カバーフィルム(6A)を巻取りながら、支持体フィルム(5A)及び熱可塑性樹脂層A(3)を有するフィルムを、送りロール(12)で、積層ロール(10) In, while maintaining the cover film (6A) winding, a film having a support film (5A) and the thermoplastic resin layer A (3), with feed roll (12), laminating roll (10)
に送り、基板(7)の上に支持体フィルム(5A)を有する熱可塑性樹脂層A(3)が積層される。 Feeding the thermoplastic resin layer A having a support film on a substrate (7) (5A) (3) are stacked. 熱可塑性樹脂層A(3)が積層された基板(7)は、搬送ロール(11)で送られ、熱可塑性樹脂層A(3)上の支持体フィルム(5A)は、送りロール(12)で、支持体フィルム巻取ロール(9)へ送られ、支持体フィルム巻取ロール(9)で巻取られ、基板(7)上には、熱可塑性樹脂層A(3)のみが積層された状態となる。 Substrate thermoplastic resin layer A (3) are laminated (7) is sent by the transport roll (11), the thermoplastic resin layer A (3) supports on the film (5A) is feed roll (12) in, is sent to the support film winding roll (9), is wound with the support film winding roll (9), on a substrate (7), only the thermoplastic resin layer a (3) are laminated the state.

【0081】一方、フィルムBを供給する第2の供給ロール(2)に、支持体フィルム(5B)、熱可塑性樹脂層B(4)及びカバーフィルム(6B)を有するロール状のフィルムBを設置し、カバーフィルム巻取ロール(8)で、カバーフィルム(6B)を巻取りながら、支持体フィルム(5B)及び熱可塑性樹脂層B(4)を有するフィルムを、送りロール(12)で、積層ロール(10)に送り、基板(7)の上に積層された熱可塑性樹脂層A(3)の上に、支持体フィルム(5B)を有する熱可塑性樹脂層B(4)が積層される。 [0081] On the other hand, the second supply roll for supplying a film B (2), the support film (5B), placed a roll of film B with the thermoplastic resin layer B (4) and the cover film (6B) and, a cover film take-up roll (8), while taking up the cover film (6B), a film having a support film (5B) and the thermoplastic resin layer B (4), at a feed roll (12), stacked feed to the roll (10), on a substrate (7) the thermoplastic resin layer a (3) laminated on the thermoplastic resin layer B having a support film (5B) (4) is laminated. なお、積層過程の部分的拡大図も図3に併せて示した。 Incidentally, partial enlarged view of a laminated process is also shown together in FIG.

【0082】支持体フィルム(5A)を有する熱可塑性樹脂層A(3)を積層する積層ロール(10)の圧着圧力は、ゲージ圧(常圧1atmが0である)で、1×10 2 [0082] In support film bonding pressure laminating roll for laminating a thermoplastic resin layer A (3) having (5A) (10) is a gauge pressure (atmospheric pressure 1atm is 0), 1 × 10 2
〜1×10 7 Paとすることが好ましく、5×10 2 〜5× Preferably to ~1 × 10 7 Pa, 5 × 10 2 ~5 ×
10 6 Paとすることがより好ましく、1×10 4 〜1×1 More preferably to 10 6 Pa, 1 × 10 4 ~1 × 1
6 Paとすることが特に好ましい。 It is particularly preferred to 0 6 Pa. この圧着圧力は、ラミネーターのシリンダー圧力であり、線圧に換算でき、 The crimping pressure is the cylinder pressure of the laminator can be converted to a line pressure,
線圧で、50〜1×10 5 N/mとすることが好ましく、 A linear pressure, preferably to 50~1 × 10 5 N / m,
2.5×10 2 〜5×10 4 N/mとすることがより好ましく、5×10 2 〜4×10 4 N/mとすることが特に好ましい。 More preferably to 2.5 × 10 2 ~5 × 10 4 N / m, and particularly preferably to 5 × 10 2 ~4 × 10 4 N / m. この圧着圧力が、50N/m未満では、熱可塑性樹脂層A(3)が、基板(7)上に充分に密着できない傾向があり、1×10 5 N/mを超えると、基板(7)が破壊される傾向がある。 The crimping pressure is less than 50 N / m, the thermoplastic resin layer A (3) is a substrate (7) tend not to be sufficiently close contact on, exceeds 1 × 10 5 N / m, the substrate (7) there tends to be destroyed. ここで、線圧を5×10 3 N/mとする方法としては、例えば、シリンダ径が40mmφのラミネータを用い、厚さが3mm、縦10cm×横10cm(正方形) As a method for the 5 × 10 3 N / m linear pressure, for example, using a laminator cylinder diameter 40 mm diameter, thickness of 3 mm, lengthwise 10 cm × horizontal 10 cm (square)
の基板を用いて、ラミネータのシリンダ圧力(常圧1at With the substrate, the cylinder pressure laminator (normal pressure 1at
mが0である)を、2kgf/cm 2とすることにより、線圧を5×10 3 N/mとする方法、シリンダ径が40mmφのラミネータを用い、厚さが3mm、縦20cm×横20cm(正方形)の基板を用いて、ラミネータのシリンダ圧力(常圧1atmが0である)を、4kgf/cm 2とすることにより、線圧を5×10 3 N/mとする方法等が挙げられる。 The m is 0), by a 2 kgf / cm 2, a method for the 5 × 10 3 N / m linear pressure, using a laminator cylinder diameter 40 mm diameter, thickness of 3 mm, vertical 20cm × horizontal 20cm using a substrate of (square), the cylinder pressure laminator (normal pressure 1atm is 0), by a 4 kgf / cm 2, and a method of a 5 × 10 3 N / m linear pressure .

【0083】また、支持体フィルム(5A)を有する熱可塑性樹脂層A(3)を積層する積層ロール(10) [0083] Furthermore, laminating roll for laminating a support film the thermoplastic resin layer A (3) having (5A) (10)
は、熱可塑性樹脂層A(3)の基板(7)への密着性を向上させる点から、加熱圧着ロールとし、加熱を伴うこともできる。 From the viewpoint of improving the adhesion to the substrate (7) of the thermoplastic resin layer A (3), the heating press roll may be accompanied by heating. 加熱を伴う場合の加熱温度は、10〜14 The heating temperature in the case with the heating, 10 to 14
0℃とすることが好ましく、10〜130℃とすることがより好ましく、20〜130℃とすることが更に好ましく、30〜130℃とすることが特に好ましく、30 Preferably to 0 ° C., more preferably to 10 to 130 ° C., more preferably be 20 to 130 ° C., particularly preferably to 30 to 130 ° C., 30
〜110℃とすることが最も好ましい。 And most preferably to to 110 ° C.. この加熱温度が、10℃未満では、熱可塑性樹脂層A(3)が、基板(7)上に充分に密着できない傾向があり、140℃を超えると、熱可塑性樹脂層A(3)が熱硬化する傾向がある。 The heating temperature is less than 10 ° C., the thermoplastic resin layer A (3) is a substrate (7) tend not to be sufficiently close contact on, exceeds 140 ° C., the thermoplastic resin layer A (3) heat there is a tendency to cure. 熱可塑性樹脂層A(3)前記のように加熱すれば、基板(7)を予熱処理することは必要ではないが、 If heated as the thermoplastic resin layer A (3) above, it is not necessary to preheat processing a substrate (7),
熱可塑性樹脂層A(3)の基板(7)への密着性をさらに向上させる点から、前記基板(7)の予熱処理を行うことが好ましい。 From the viewpoint of adhering property further improvement to the substrate (7) of the thermoplastic resin layer A (3), it is preferable to perform preheating process of the substrate (7).

【0084】支持体フィルム(5A)を有する熱可塑性樹脂層A(3)を積層する積層ロール(10)の材質としては、特に制限はないが、熱可塑性樹脂層A(3)の基板(7)への密着性をさらに向上させる点から、ロールの表面が、ゴム、プラスチック等の柔軟性に富んだ材質のものを使用することが好ましい。 [0084] The support as the material of the film laminating roll for laminating a thermoplastic resin layer A (3) having (5A) (10), is not particularly limited, the substrate of the thermoplastic resin layer A (3) (7 further from the viewpoint of improving the adhesion to) the surface of the roll, a rubber, it is preferable to use those rich material flexible such as plastic. なお、柔軟性に富んだ材質の層の厚さは、200〜400μmとすることが好ましい。 The thickness of the layer of material rich in flexibility, it is preferable to 200 to 400.

【0085】支持体フィルム(5B)を有する熱可塑性樹脂層B(4)を積層する積層ロール(10)の圧着圧力は、ゲージ圧(常圧1atmが0である)で、1×10 4 [0085] In support film bonding pressure laminating roll for laminating a thermoplastic resin layer B (4) having a (5B) (10) is a gauge pressure (atmospheric pressure 1atm is 0), 1 × 10 4
〜1×10 7 Paとすることが好ましく、2×10 4 〜5× Preferably to ~1 × 10 7 Pa, 2 × 10 4 ~5 ×
10 6 Paとすることがより好ましく、4×10 4 〜1×1 More preferably to 10 6 Pa, 4 × 10 4 ~1 × 1
6 Paとすることが特に好ましい。 It is particularly preferred to 0 6 Pa. この圧着圧力は、ラミネーターのシリンダー圧力であり、線圧に換算でき、 The crimping pressure is the cylinder pressure of the laminator can be converted to a line pressure,
線圧で、5〜1×10 5 N/mとすることが好ましく、2. A linear pressure, preferably to 5~1 × 10 5 N / m, 2.
5×10 2 〜5×10 4 N/mとすることがより好ましく、 More preferably to 5 × 10 2 ~5 × 10 4 N / m,
1×10 2 〜4×10 4 N/mとすることが特に好ましい。 It is particularly preferred to 1 × 10 2 ~4 × 10 4 N / m.
この圧着圧力が、50N/m未満では、熱可塑性樹脂層B The crimping pressure is less than 50 N / m, the thermoplastic resin layer B
(4)が、熱可塑性樹脂層A(3)上に充分に密着できない傾向があり、1×10 5 N/mを超えると、基板(7) (4), tend not to be sufficiently close contact on the thermoplastic resin layer A (3), exceeds 1 × 10 5 N / m, the substrate (7)
が破壊される傾向がある。 There tends to be destroyed.

【0086】また、支持体フィルム(5B)を有する熱可塑性樹脂層B(4)を積層する積層ロール(10) [0086] Furthermore, laminating roll for laminating a thermoplastic resin layer B having a support film (5B) (4) (10)
は、熱可塑性樹脂層B(4)の熱可塑性樹脂層A(3) The thermoplastic resin layer A of the thermoplastic resin layer B (4) (3)
への密着性を向上させる点から、加熱圧着ロールとし、 From the viewpoint of improving adhesion to, and heat pressing roll,
加熱を伴うこともできる。 It can also be accompanied by heating. 加熱を伴う場合の加熱温度は、10〜140℃とすることが好ましく、10〜13 The heating temperature in the case with the heating is preferably set to 10 to 140 ° C., 10 to 13
℃とすることがより好ましく、20〜130℃とすることが更に好ましく、30〜130℃とすることが特に好ましく、30〜110℃が最も好ましい。 ° C., more preferably to, more preferably be 20 to 130 ° C., particularly preferably to 30 to 130 ° C., most preferably 30 to 110 ° C.. この加熱温度が、10℃未満では、熱可塑性樹脂層B(4)が、熱可塑性樹脂層A(3)上に充分に密着できない傾向があり、140℃を超えると、熱可塑性樹脂層A(3)及び熱可塑性樹脂層B(4)が熱硬化する傾向がある。 The heating temperature is less than 10 ° C., the thermoplastic resin layer B (4) is a thermoplastic resin layer A (3) tend not to be sufficiently close contact on, exceeds 140 ° C., the thermoplastic resin layer A ( 3) and the thermoplastic resin layer B (4) tends to be thermally cured.

【0087】なお、基板(7)が凹凸を有するPDP用基板等である場合には、凹凸を有する基板の凹凸表面上に熱可塑性樹脂層A(3)を密着させる必要があり、その場合、熱可塑性樹脂層B(4)は埋め込み層の役割を果たすため、上記した熱可塑性樹脂層B(4)を積層する積層ロール(10)の加熱は、必須条件となる。 [0087] Incidentally, when the substrate (7) is a substrate for PDP or the like having an uneven, it is necessary to contact the thermoplastic resin layer A (3) on the uneven surface of the substrate having unevenness, in which case, to serve the thermoplastic resin layer B (4) is embedded layer, heating the laminate rolls (10) for laminating the thermoplastic resin layer B (4) is a prerequisite. 図5 Figure 5
は、凹凸を有する基板の凹凸表面上を示した模式図であり、図5において、凹凸表面上(18)は斜線部にして示した。 Is a schematic view showing the upper irregular surface of the substrate having unevenness, in FIG. 5, on the uneven surface (18) is shown in the shaded area.

【0088】支持体フィルム(5B)を有する熱可塑性樹脂層B(4)を積層する積層ロール(10)の材質としては、特に制限はないが、熱可塑性樹脂層B(4)の熱可塑性樹脂層A(3)への密着性を向上させる点から、ロールの表面が、ゴム、プラスチック等の柔軟性に富んだ材質のものを使用することが好ましい。 [0088] As the material of the laminating roll (10) of laminating a support film the thermoplastic resin layer B having (5B) (4), is not particularly limited, the thermoplastic resin of the thermoplastic resin layer B (4) from the viewpoint of improving the adhesion to the layer a (3), the surface of the roll, a rubber, it is preferable to use those rich material flexible such as plastic. なお、柔軟性に富んだ材質の層の厚さは、200〜400μmとすることが好ましい。 The thickness of the layer of material rich in flexibility, it is preferable to 200 to 400. 基板(7)の搬送速度は、0.0 Conveying speed of the substrate (7), 0.0
1〜10m/分とすることが好ましく、0.02〜5m It is preferable that the 1~10m / min, 0.02~5m
/分とすることがより好ましく、0.1〜2m/分とすることが特に好ましい。 More preferably to / min, and particularly preferably 0.1~2M / min.

【0089】図4の積層装置は、基板(7)を送る搬送ロール(11)、フィルムAを供給する第1の供給ロール(1)、フィルムAを送る送りロール(12)、カバーフィルム(6A)を巻取るカバーフィルム巻取ロール(8)、支持体フィルム(5A)及び熱可塑性樹脂層A [0089] stacking apparatus of FIG. 4, the transport roll (11) for sending the substrate (7), a first supply roll for supplying a film A (1), feed rolls (12) to send the film A, the cover film (6A ) winding take the cover film take-up roll (8), the support film (5A) and the thermoplastic resin layer a
(3)を有するフィルムを送る送りロール(12)、フィルムBを供給する第2の供給ロール(2)、フィルムBを送る送りロール(12)、カバーフィルム(6B) Feed roll to send a film having a (3) (12), a second supply roll for supplying a film B (2), feed roll Send film B (12), cover film (6B)
を巻取るカバーフィルム巻取ロール(8)、支持体フィルム(5B)及び熱可塑性樹脂層B(4)を有するフィルムを送る送りロール(12)、支持体フィルム(5 Take a winding cover film take-up roll (8), the support film (5B) and feed roll (12) for sending a film having a thermoplastic resin layer B (4), the support film (5
A)及び熱可塑性樹脂層A(3)を有するフィルムと支持体フィルム(5B)及び熱可塑性樹脂層B(4)を有するフィルムを貼り合わせる合わせロール(13)、支持体フィルム(5A)を送る送りロール(12)、支持体フィルム(5A)を巻取る支持体フィルム巻取ロール(9)、熱可塑性樹脂層A(3)、熱可塑性樹脂層B A) and the thermoplastic resin layer A (3) a film having a support film (5B) and the thermoplastic resin layer B (combined roll (13 bonding a film having a 4)), and sends the support film (5A) feed roll (12), the support film takeup roll for taking up the support film (5A) (9), the thermoplastic resin layer a (3), the thermoplastic resin layer B
(4)及び支持体フィルム(5B)を有するフィルムを送る送りロール(12)、熱可塑性樹脂層A(3)、熱可塑性樹脂層B(4)及び支持体フィルム(5B)を有するフィルムを基板(7)上に積層する積層ロール(1 (4) and the feed roll to send a film having a support film (5B) (12), the thermoplastic resin layer A (3), a substrate film having the thermoplastic resin layer B (4) and the support film (5B) (7) laminating roll to be stacked (1
0)を設けたものである。 0) in which the provided.

【0090】フィルムAを供給する第1の供給ロール(1)に、支持体フィルム(5A)、熱可塑性樹脂層A [0090] the first supply roll supplying a film A (1), the support film (5A), the thermoplastic resin layer A
(3)及びカバーフィルム(6A)を有するロール状のフィルムAを設置し、送りロール(12)で、カバーフィルム(6A)をカバーフィルム巻取ロール(8)に送り、カバーフィルム巻取ロール(8)で、カバーフィルム(6A)を巻取りながら、支持体フィルム(5A)及び熱可塑性樹脂層A(3)を有するフィルムを、送りロール(12)で、合わせロール(13)に送る。 (3) and set up a roll of film A having a cover film (6A), with the feed roll (12), feeding the cover film (6A) to the cover film take-up roll (8), the cover film take-up roll ( 8), while taking up the cover film (6A), a film having a support film (5A) and the thermoplastic resin layer a (3), with feed roll (12), combined and sends to the roll (13). 一方、 on the other hand,
フィルムBを供給する第2の供給ロール(2)に、支持体フィルム(5B)、熱可塑性樹脂層B(4)及びカバーフィルム(6B)を有するロール状のフィルムBを設置し、送りロール(12)で、カバーフィルム(6B) A second supply roll for supplying a film B (2), the support film (5B), was placed a roll of film B with the thermoplastic resin layer B (4) and the cover film (6B), feed rolls ( 12), the cover film (6B)
をカバーフィルム巻取ロール(8)に送り、カバーフィルム巻取ロール(8)で、カバーフィルム(6B)を巻取りながら、支持体フィルム(5B)及び熱可塑性樹脂層B(4)を有するフィルムを、送りロール(12)で合わせロール(13)に送る。 Feeding the cover film take-up roll (8) has a cover film take-up roll (8), while taking the cover film (6B) winding, the support film (5B) and the thermoplastic resin layer B (4) Film and it sends to the roll (13) combined with feed roll (12).

【0091】支持体フィルム(5A)及び熱可塑性樹脂層A(3)を有するフィルムと支持体フィルム(5B) [0091] support film (5A) and the film and the support film having a thermoplastic resin layer A (3) (5B)
及び熱可塑性樹脂層B(4)を有するフィルムを、合わせロール(13)で張りあわせ、送りロール(12) And a film having a thermoplastic resin layer B (4), combined together tension roll (13), feed rolls (12)
で、支持体フィルム(5A)を支持体フィルム巻取ロール(9)に送り、支持体フィルム巻取ロール(9)で、 In the support film (5A) support film feeding to the winding roll (9), the support film winding roll (9),
支持体フィルム(5A)を巻取りながら、送りロール(12)で、熱可塑性樹脂層A(3)、熱可塑性樹脂層B(4)及び支持体フィルム(5B)を有するフィルムを、積層ロール(10)に送る。 While taking up the support film (5A), at a feed roll (12), the thermoplastic resin layer A (3), the thermoplastic resin layer B (4) and the support film a film having a (5B), laminating roll ( send to 10). 基板(7)は、搬送ロール(11)で送られながら、積層ロール(10)により、基板(7)上に、熱可塑性樹脂層A(3)、熱可塑性樹脂層B(4)及び支持体フィルム(5B)を有するフィルムが積層される。 Substrate (7), while being fed by the transport roll (11), the lamination roll (10), on a substrate (7), the thermoplastic resin layer A (3), the thermoplastic resin layer B (4) and the support film having a film (5B) are laminated. なお、積層過程の部分的拡大図も図4に併せて示した。 Incidentally, partial enlarged view of a laminated process is also shown together in Figure 4.

【0092】熱可塑性樹脂層A(3)、熱可塑性樹脂層B(4)及び支持体フィルム(5B)を有するフィルムを積層する積層ロール(10)の圧着圧力は、ゲージ圧(常圧1atmが0である)で、1×10 4 〜1×10 7 Pa [0092] The thermoplastic resin layer A (3), the crimping pressure of the lamination roll (10) for laminating a film having a thermoplastic resin layer B (4) and the support film (5B) is, gauge pressure (atmospheric pressure 1atm is 0 is a), 1 × 10 4 ~1 × 10 7 Pa
とすることが好ましく、2×10 4 〜5×10 6 Paとすることがより好ましく、4×10 4 〜1×10 6 Paとすることが特に好ましい。 It is preferable that a, more preferably, to 2 × 10 4 ~5 × 10 6 Pa, and particularly preferably to 4 × 10 4 ~1 × 10 6 Pa. この圧着圧力は、ラミネーターのシリンダー圧力であり、線圧に換算でき、線圧で、5〜1 The crimping pressure is the cylinder pressure of the laminator can be converted to a line pressure, a line pressure, 5-1
×10 5 N/mとすることが好ましく、2.5×10 2 〜5 × preferably to 10 5 N / m, 2.5 × 10 2 ~5
×10 4 N/mとすることがより好ましく、1×10 2 〜4 × more preferably to 10 4 N / m, 1 × 10 2 ~4
×10 4 N/mとすることが特に好ましい。 × It is especially preferred to 10 4 N / m. この圧着圧力が、50N/m未満では、熱可塑性樹脂層A(3)及び熱可塑性樹脂層B(4)が、基板(7)上に充分に密着できない傾向があり、1×10 5 N/mを超えると、基板(7)が破壊される傾向がある。 The crimping pressure is less than 50 N / m, the thermoplastic resin layer A (3) and the thermoplastic resin layer B (4) is a substrate (7) tend not to be sufficiently close contact on, 1 × 10 5 N / exceeds m, they tend to substrate (7) is destroyed.

【0093】また、熱可塑性樹脂層A(3)、熱可塑性樹脂層B(4)及び支持体フィルム(5B)を有するフィルムを積層する積層ロール(10)は、熱可塑性樹脂層A(3)及び熱可塑性樹脂層B(4)の、基板(7) [0093] Further, the thermoplastic resin layer A (3), the thermoplastic resin layer B (4) and the laminating roll for laminating a film having a support film (5B) (10), the thermoplastic resin layer A (3) and the thermoplastic resin layer B (4), the substrate (7)
への密着性を向上させる点から、加熱圧着ロールとし、 From the viewpoint of improving adhesion to, and heat pressing roll,
加熱を伴うこともできる。 It can also be accompanied by heating. 加熱を伴う場合の加熱温度は、0〜130℃とすることが好ましく、10〜130 The heating temperature in the case with the heating is preferably set to 0 to 130 ° C., 10 to 130
℃とすることがより好ましく、10〜120℃とすることが更に好ましく、20〜120℃とすることが更に好ましく、20〜110℃とすることが特に好ましく、3 ° C., more preferably to, more preferably be 10 to 120 ° C., more preferably to 20 to 120 ° C., particularly preferably to 20 to 110 ° C., 3
0〜110℃とすることが最も好ましい。 And most preferably to 0 to 110 ° C.. この加熱温度が、0℃未満では、熱可塑性樹脂層A(3)及び熱可塑性樹脂層B(4)が、基板(7)上に充分に密着できない傾向があり、130℃を超えると、熱可塑性樹脂層A The heating temperature is less than 0 ° C., the thermoplastic resin layer A (3) and the thermoplastic resin layer B (4) is a substrate (7) tend not to be sufficiently close contact on, exceeds 130 ° C., thermal thermoplastic resin layer A
(3)及び熱可塑性樹脂層B(4)が熱硬化する傾向がある。 (3) and the thermoplastic resin layer B (4) tends to be thermally cured.

【0094】なお、基板(7)が凹凸を有するPDP用基板等である場合には、凹凸を有する基板の凹凸表面上に熱可塑性樹脂層A(3)を密着させる必要があり、その場合、熱可塑性樹脂層B(4)は埋め込み層の役割を果たすため、上記した積層ロール(10)の加熱は、必須条件となる。 [0094] Incidentally, when the substrate (7) is a substrate for PDP or the like having an uneven, it is necessary to contact the thermoplastic resin layer A (3) on the uneven surface of the substrate having unevenness, in which case, to serve the thermoplastic resin layer B (4) is embedded layer, heating the laminate rolls (10) is a prerequisite. また、熱可塑性樹脂層A(3)及び熱可塑性樹脂層B(4)を前記のように加熱すれば、基板(7)を予熱処理することは必要ではないが、熱可塑性樹脂層A(3)及び熱可塑性樹脂層B(4)の基板(7)への密着性をさらに向上させる点から、前記基板(7)の予熱処理を行うことが好ましい。 The thermoplastic resin layer A (3) and by heating the thermoplastic resin layer B (4) as described above, is not necessary to preheat processing a substrate (7), the thermoplastic resin layer A (3 ) and the adhesion from the viewpoint of further improving to the substrate (7) of the thermoplastic resin layer B (4), it is preferable to perform the preheating process of the substrate (7).

【0095】熱可塑性樹脂層A(3)、熱可塑性樹脂層B(4)及び支持体フィルム(5B)を有するフィルムを積層する積層ロール(10)の材質としては、特に制限はないが、熱可塑性樹脂層A(3)及び熱可塑性樹脂層B(4)の基板(7)への密着性を向上させる点から、ロールの表面が、ゴム、プラスチック等の柔軟性に富んだ材質のものを使用することが好ましい。 [0095] The thermoplastic resin layer A (3), as the material of the laminating roll (10) for laminating a film having a thermoplastic resin layer B (4) and the support film (5B), is not particularly limited, heat from the viewpoint of improving the adhesion to the substrate (7) of the thermoplastic resin layer a (3) and the thermoplastic resin layer B (4), the surface of the roll, rubber, those materials rich in flexibility, such as plastic it is preferable to use. なお、柔軟性に富んだ材質の層の厚さは、200〜400μmとすることが好ましい。 The thickness of the layer of material rich in flexibility, it is preferable to 200 to 400. また、基板(7)の搬送速度は、 The transport speed of the substrate (7),
0.01〜10m/分とすることが好ましく、0.02 It is preferable that the 0.01~10M / min, 0.02
〜5m/分とすることがより好ましく、0.1〜2m/ It is more preferable to the ~5m / min, 0.1~2m /
分とすることが特に好ましい。 It is particularly preferable that the minute.

【0096】また、本発明の積層方法は、5×10 4 Pa [0096] Moreover, lamination method of the present invention, 5 × 10 4 Pa
以下の減圧下で行ってもよく、本発明の積層装置を減圧可能なものとし、5×10 4 Pa以下の減圧下で、本発明の積層装置を使用することもできる。 May be carried out under a reduced pressure of not more than, the laminating apparatus of the present invention and capable vacuum, under a vacuum of 5 × 10 4 Pa or less, it is also possible to use a laminated device of the present invention.

【0097】 [0097]

【作用】本発明の積層装置は、熱可塑性樹脂層を有する二種類以上のフィルムを、一台の装置のみで積層できるものであり、作業性が良好である。 [Action] stacking apparatus of the present invention, two or more types of film having a thermoplastic resin layer, which can be stacked in only single apparatus, workability is excellent. 本発明の積層装置における積層ロール(10)の圧着圧力、加熱温度等を調整することにより、熱可塑性樹脂層の基板(7)への密着性が良好に積層でき、作業性も良好である。 Crimping pressure laminating roll (10) in the laminating apparatus of the present invention, by adjusting the heating temperature and the like, adhesion to the substrate (7) of the thermoplastic resin layer can be satisfactorily laminated, a good workability. また、P In addition, P
DP用基板等の凹凸を有する基板においても、熱可塑性樹脂層を凹部内面へ、埋め込み性良く積層できる。 Even in a substrate having irregularities such as a substrate for DP, the thermoplastic resin layer into the recess inner surface, can be laminated embedding good. 本発明の積層装置を使用することにより、一台の装置のみで積層できるため、装置の省スペース化が得られる。 By using the laminated device of the present invention, it is possible to stack only single apparatus, space saving of the apparatus is obtained. また、本発明における図3の積層装置は、構造がシンプルであり、作業開始準備が容易であり、メンテナンス性にも優れる。 The layered device of FIG. 3 in the present invention, the structure is simple, easy to work start preparation, excellent in maintainability. また、本発明における図4の積層装置は、二種類以上の熱可塑性樹脂層を、一回の積層で基板上に形成できるため、積層時の欠陥を抑制できるものである。 The layered device of FIG. 4 in the present invention, two or more kinds of thermoplastic resin layer, it is possible to form on a substrate in a single stack, in which can suppress defects during lamination.

【0098】本発明の積層方法及び積層装置は、二種類以上のフィルムを作業性良く積層するために好適であり、多層ラミネートを必要とする、カラーフィルタの製造、プラズマディスプレイパネルの製造、EL基板、フィールドエミッションディスプレイ蛍光体層形成用基板の製造等に有効に使用でき、比較的凹凸の差が大きい基板を使用するプラズマディスプレイパネルの製造等には、より好適である。 [0098] laminating method and laminating apparatus of the present invention is suitable for laminating workability of two or more films, require multilayer laminate, the production of color filters, the production of plasma display panels, EL substrates , a field emission display phosphor layer forming substrate effectively be used in the manufacture or the like, the relatively difference of unevenness using the substrate is greater manufacturing a PDP or the like, is more preferable.

【0099】以下、本発明の積層方法及び本発明の積層装置を用いた一例として、プラズマディスプレイパネルの製造における蛍光体パターンの製造法を説明する。 [0099] As an example using the laminated device of lamination method and the present invention of the present invention, explaining a manufacturing method of the phosphor pattern in manufacturing plasma display panels. 本発明の蛍光体パターンの製造法は、(I)凹凸を有する基板の凹凸表面上に、蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A)及び熱可塑性樹脂層Bを形成する工程、(II)活性光線を像的に照射する工程、(II Preparation of the phosphor pattern of the present invention, form (I) irregularities on the irregular surface of a substrate having a photosensitive resin composition layer containing a phosphor (thermoplastic resin layer A) and the thermoplastic resin layer B to process step of irradiating (II) active light rays imagewise, (II
I)現像により不要部を除去する工程及び(IV)焼成により不要分を除去する工程の各工程を有する。 A step and (IV) each step of the process of removing unnecessary components by calcination to remove unnecessary portions by I) development.

【0100】以下、図6を用いて、蛍光体パターンの製造法の各工程を説明する。 [0100] Hereinafter, with reference to FIG. 6, illustrating each step of the process of the phosphor pattern. なお、図6は、蛍光体パターンの製造法の各工程を示した模式図である。 Incidentally, FIG. 6 is a schematic diagram showing the steps of the method for producing the phosphor pattern. 〔(I)凹凸を有する基板の凹凸表面上に、蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A)及び熱可塑性樹脂層Bを形成する工程〕バリアリブ(15)が形成されたPDP用透明基板(14)(凹凸を有する基板)の凹凸表面上に、本発明の積層方法及び積層装置を用いて、蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A)(3)及び熱可塑性樹脂層B(4)を形成させた状態を図6(I)に示した。 [On the uneven surface of the substrate having the (I) irregularity, the photosensitive resin composition layer containing a phosphor step of forming a (thermoplastic resin layer A) and the thermoplastic resin layer B] barrier ribs (15) are formed PDP transparent substrate (14) on the uneven surface of the (a substrate having an uneven), using a laminating method and laminating apparatus of the present invention, the photosensitive resin composition layer containing a phosphor (thermoplastic resin layer a) (3) the state and to form a thermoplastic resin layer B (4) shown in FIG. 6 (I).

【0101】〔(II)活性光線を像的に照射する工程〕 [0102] [(II) irradiating active light to imagewise]
活性光線(20)を像的に照射する状態を図6(II)に示した。 The state of the image irradiated with active light (20) shown in FIG. 6 (II). 図6(II)の工程において、活性光線(20) In the step of FIG. 6 (II), active light (20)
を像的に照射する方法としては、図6(I)の状態の熱可塑性樹脂層B(4)の上に、ネガフィルム、ネガガラス、ポジフィルム、ポジガラス等のフォトマスク(1 As a method of image to irradiation with, on the thermoplastic resin layer B in the state FIG. 6 (I) (4), negative film, Negagarasu, positive film, a photomask such Pojigarasu (1
9)を介して、活性光線(20)を像的に照射することができる。 9) through, it can be irradiated with active light rays (20) in imagewise. この時、熱可塑性樹脂層B(4)の上に支持体フィルム(5B)が存在する場合は、その支持体フィルム(5B)を積層したまま活性光線(20)を像的に照射してもよく、また、支持体フィルム(5B)を除去した後に活性光線(20)を像的に照射してもよい。 At this time, if the support film on the thermoplastic resin layer B (4) (5B) is present, it is irradiated with the support film (5B) while laminating the active rays (20) in imagewise well, also, the active light (20) may be imagewise irradiated after removal of the support film (5B). なお、この時、熱可塑性樹脂層B(4)が、感光性を有するものである場合は、熱可塑性樹脂層B(4)は、蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A) At this time, the thermoplastic resin layer B (4) is, if those having a photosensitive property, thermoplastic resin layer B (4), the photosensitive resin composition layer containing a phosphor (thermoplastic resin layer A)
(3)と同時に光硬化することとなる。 (3) at the same time so that the photocuring.

【0102】活性光線(20)としては、公知の活性光源が使用でき、例えば、カーボンアーク、水銀蒸気アーク、キセノンアーク、その他から発生する光等が挙げられる。 [0102] As actinic rays (20), known active light source can be used, for example, carbon arc, mercury vapor arc, xenon arc, light or the like generated from the others. 光開始剤の感受性は、通常、紫外線領域において最大であるので、その場合の活性光源は、紫外線を有効に放射するものにすべきである。 Sensitivity of the photoinitiator is usually because the maximum in the ultraviolet region, its activity light source case, should be one that effectively emits ultraviolet rays. また、光開始剤が可視光線に感受するもの、例えば、9、10−フェナンスレンキノン等である場合には、活性光線(20)としては、可視光が用いられ、その光源としては、前記のもの以外に写真用フラッド電球、太陽ランプ等も使用することができる。 Moreover, those photoinitiators are sensitive to visible light, for example, in the case of 9,10-phenanthrenequinone and the like, as the active light (20), visible light is used as the light source, the photographic flood light bulb in addition to the well of the, it is possible to use the sun lamp or the like. また、活性光線(20)としては、平行光線、散乱光線等が挙げられ、平行光線及び散乱光線のどちらを使用してもよく、また、両方を一工程において使用してもよく、両方を二段階で別々に使用してもよい。 As the active light (20), parallel light, scattered light and the like, may be used either parallel rays and scattered rays, also both may be used in one step, and both two it may be used separately in stages.
なお、両方を二段階で別々に使用する場合には、どちらを先に行ってもよい。 In the case of both used separately in two stages are both may be performed first.

【0103】〔(III)現像により不要部を除去する工程〕現像により不要部を除去した状態を図6(III)に示した。 [0103] The state of removing the unnecessary portion by development [(III) Step of removing the unnecessary portion by development] shown in FIG. 6 (III). なお、図6(III)において、3′は光硬化後の蛍光体を含有する感光性樹脂組成物層である。 Incidentally, in FIG. 6 (III), 3 'is a photosensitive resin composition layer containing a phosphor after photocuring. 図6 Figure 6
(III)において、現像方法としては、例えば、図6(I (III), the developing method, for example, FIG. 6 (I
I)の状態の後、熱可塑性樹脂層B(4)の上に支持体フィルム(5B)が存在する場合には、これを除去した後、アルカリ水溶液、水系現像液、有機溶剤等の公知の現像液を用いて、スプレー、揺動浸漬、ブラッシング、 After the state of I), when the support film on the thermoplastic resin layer B (4) (5B) is present, after removing this alkaline aqueous solution, aqueous developing solution, known as organic solvent using a developer, spraying, reciprocal dipping, brushing,
スクラッピング等の公知方法により現像を行い、不要部を除去する方法などが挙げられる。 And developed by known methods scrapping etc., and a method of removing an unnecessary portion.

【0104】不要部を除去する場合には、まず、蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A) [0104] In the case of removing an unnecessary portion, first, the photosensitive resin composition layer containing a phosphor (thermoplastic resin layer A)
(3)を溶解しない水、アルカリ水溶液、半溶剤水溶液、半溶剤アルカリ水溶液、有機溶剤等を用いて、熱可塑性樹脂層B(4)の不要部を溶解により除去した後に、現像液を用いて、蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A)(3)の不要部を除去してもよく、また、蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A)(3)及び熱可塑性樹脂層B(4) (3) does not dissolve the water, alkali aqueous solution, semi-solvent solution, semi-solvent aqueous alkaline solution, an organic solvent or the like, after removing by dissolving the unnecessary portion of the thermoplastic resin layer B (4), with a developer It may be removed unnecessary portions of the photosensitive resin composition layer containing a phosphor (thermoplastic resin layer a) (3), the photosensitive resin composition layer containing a phosphor (thermoplastic resin layer A) (3) and the thermoplastic resin layer B (4)
が、同一の現像液を使用して現像できるものである場合には、その現像液を用いて、蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A)(3)の不要部及び熱可塑性樹脂層B(4)の不要部を一工程で除去することもできる。 But when those can be developed using the same developer, the developer used, unnecessary portions of the photosensitive resin composition layer containing a phosphor (thermoplastic resin layer A) (3) and an unnecessary portion of the thermoplastic resin layer B (4) may be removed in one step. また、蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A)(3)の不要部及び熱可塑性樹脂層B(4)の不要部を除去する方法として、ドライ現像にて、それぞれ単独に又は一工程で行うこともできる。 Further, as a method for removing the unnecessary portion of the photosensitive resin composition layer containing a phosphor (thermoplastic resin layer A) (3) of the unnecessary portion and the thermoplastic resin layer B (4), in dry development, respectively It can be performed individually or in one step.

【0105】なお、(III)の工程においては、前記(I [0105] In the step of (III), the (I
I)の工程により、形成された凹部内面以外の、蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A) Through the steps I), other than the location recess inner surface, the photosensitive resin composition layer containing a phosphor (thermoplastic resin layer A)
(3)及び熱可塑性樹脂層B(4)(熱可塑性樹脂層B (3) and the thermoplastic resin layer B (4) (the thermoplastic resin layer B
(4)が感光性を有するものである場合は、凹部内面以外熱可塑性樹脂層B(4))は、不要部であり、これを現像により除去する必要がある。 If (4) are those having photosensitivity, except the recess inner surface thermoplastic resin layer B (4)) is not necessary portion, it is necessary to remove this by development. なお、図7は、凹部内面を示した模式図であり、図7において、凹部内面(2 Note that FIG. 7 is a schematic view showing a concave inner surface, in FIG. 7, the recess inner surface (2
2)は斜線部にして示した。 2) showed in the shaded area.

【0106】また、前記(III)工程の現像時間及び現像温度は、不要部を除去できるように適宜調節することができる。 [0106] The (III) development time and development temperature steps can be adjusted to allow removal of the unnecessary portion as appropriate. 現像時間は、蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A)(3)の最小現像時間(蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A)(3)をPDP用基板の凹部内面に埋め込んだ後、 Development time, the minimum developing time (the photosensitive resin composition layer containing a phosphor (thermoplastic resin layer A) (3 of the photosensitive resin composition layer containing a phosphor (thermoplastic resin layer A) (3) ) the after embedding the recess inner surface of the PDP substrate,
蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A)(3)が現像によって除去される最短の時間)の1 Phosphor photosensitive resin composition containing layer of the shortest time to (thermoplastic resin layer A) (3) is removed by development) 1
〜10倍の時間とすることが好ましく、現像温度は、1 Preferably to 10 times as long, the developing temperature, 1
0〜60℃とすることが好ましい。 It is preferable that the 0~60 ℃. 現像時間が、最小現像時間未満では、現像残りが発生する傾向があり、最小現像時間の10倍の時間を超えると、蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A)(3)の必要部まで除去される傾向がある。 Developing time is less than the minimum developing time, tend to developing residue is generated, if it exceeds 10 times the minimum developing time, the photosensitive resin composition layer containing a phosphor (thermoplastic resin layer A) ( until required portion of 3) tends to be removed. また、現像温度が、10 In addition, the developing temperature, 10
℃未満では、現像性が低下する傾向があり、60℃を超えると、耐現像液性が低下する傾向がある。 Is less than ° C., there is a tendency that developing property lowers, and when it exceeds 60 ° C., developing solution resistance tends to be lowered.

【0107】アルカリ水溶液の塩基としては、水酸化アルカリ(リチウム、ナトリウム又はカリウムの水酸化物等)、炭酸アルカリ(リチウム、ナトリウム又はカリウムの炭酸塩若しくは重炭酸塩等)、アルカリ金属リン酸塩(リン酸カリウム、リン酸ナトリウム等)、アルカリ金属ピロリン酸塩(ピロリン酸ナトリウム、ピロリン酸カリウム等)、水酸化テトラメチルアンモニウム、トリエタノールアミンなどが挙げられ、中でも、炭酸ナトリウム、水酸化テトラメチルアンモニウム等が好ましいものとして挙げられる。 [0107] As the base of the alkaline aqueous solution, an alkali hydroxide (lithium, sodium or potassium hydroxide, etc.), alkali carbonates (lithium, carbonate or bicarbonate of sodium or potassium), alkali metal phosphate ( potassium phosphate, sodium phosphate, etc.), alkali metal pyrophosphates (sodium pyrophosphate, potassium pyrophosphate, etc.), tetramethyl ammonium hydroxide, triethanolamine, and among them, sodium carbonate, tetramethylammonium hydroxide and the like as preferred. 現像に用いるアルカリ水溶液のpH The pH of the alkaline aqueous solution used for development
は、9〜11とすることが好ましく、また、その温度は、蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A)(3)及び熱可塑性樹脂層B(4)の現像性に合わせて調整することができる。 Is preferably in the 9-11, also, the temperature, the developability of the photosensitive resin composition layer containing a phosphor (thermoplastic resin layer A) (3) and the thermoplastic resin layer B (4) it can be adjusted to suit the. また、アルカリ水溶液中には、表面活性剤、消泡剤、現像を促進させるための少量の有機溶剤等を混入させることができる。 Further, in the alkaline aqueous solution, a surface active agent, can be mixed antifoam, a small amount of organic solvent to accelerate development.

【0108】水系現像液としては、水又はアルカリ水溶液と一種以上の有機溶剤とからなるものが挙げられる。 [0108] As the aqueous developer, include those composed of water or an aqueous alkali solution and one or more organic solvents.
ここで、アルカリ水溶液の塩基としては、前記物質以外に、例えば、ホウ砂、メタケイ酸ナトリウム、エタノールアミン、エチレンジアミン、ジエチレントリアミン、 Here, as the base an alkali aqueous solution, in addition to the material, for example, borax, sodium metasilicate, ethanolamine, ethylenediamine, diethylenetriamine,
2−アミノ−2−ヒドロキシメチル−1、3−プロパンジオール、1,3−ジアミノプロパノール−2−モルホリン、水酸化テトラメチルアンモニウム等が挙げられる。 2-amino-2-hydroxymethyl-1,3-propanediol, 1,3-diamino-propanol-2-morpholine, tetramethyl ammonium and the like hydroxide. 水系現像液のpHは、8〜12とすることが好ましく、9〜10とすることがより好ましい。 The pH of the aqueous developer is preferably in a 8-12, more preferably to 9-10.

【0109】有機溶剤としては、例えば、三アセトンアルコール、アセトン、酢酸エチル、炭素数1〜4のアルコキシ基をもつアルコキシエタノール、エチルアルコール、イソプロピルアルコール、ブチルアルコール、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノブチルエーテル等が挙げられる。 [0109] As the organic solvent, for example, a three-acetone alcohol, acetone, ethyl acetate, alkoxyethanol having an alkoxy group having 1 to 4 carbon atoms, ethyl alcohol, isopropyl alcohol, butyl alcohol, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol mono-butyl ether, and the like. これらは単独で又は2 These can be used alone or in combination with 2
種類以上を組み合わせて使用される。 It is used in combination or more. 有機溶剤の濃度は、通常、2〜90重量%の範囲とされ、また、その温度は、現像性にあわせて調整することができる。 The concentration of the organic solvent is usually in the range of 2 to 90 wt%, and its temperature can be adjusted to suit the developability. また、 Also,
水系現像液中には、界面活性剤、消泡剤等を少量混入することができる。 The aqueous developing solution, a surfactant may be incorporated a small amount of antifoaming agent. 単独で用いる有機溶剤現像液としては、例えば、1,1,1−トリクロロエタン、N−メチルピロリドン、N、N−ジメチルホルムアミド、シクロヘキサノン、メチルイソブチルケトン、γ−ブチロラクトン等が挙げられる。 As the organic solvent developer used alone, for example, 1,1,1-trichloroethane, N- methylpyrrolidone, N, N- dimethylformamide, cyclohexanone, methyl isobutyl ketone, .gamma.-butyrolactone. これらの有機溶剤は、引火防止のため、1〜20重量%の範囲で水を添加してもよい。 These organic solvents, for ignition prevention, water may be added in a range of 1 to 20 wt%.

【0110】このようにして、凹部内面以外に形成された蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A)(3)(不要部)(熱可塑性樹脂層B(4)が感光性を有するものである場合は、凹部内面以外の熱可塑性樹脂層B(4))が、現像により除去され、凹部内面には、光硬化後の蛍光体を含有する感光性樹脂組成物層3′(熱可塑性樹脂層B(4)が感光性を有する場合は、光硬化後の熱可塑性樹脂層Bも含む)が形成される。 [0110] In this way, the photosensitive resin composition layer containing a phosphor formed in addition to the recess inner surface (the thermoplastic resin layer A) (3) (unnecessary portion) (thermoplastic resin layer B (4) is If those having a photosensitive property, thermoplastic resin layer B other than the recess inner surface (4)) is removed by development, in the recess inner surface, the photosensitive resin composition layer containing a phosphor after photocuring 3 '(thermoplastic resin layer B (4) may have photosensitivity also includes thermoplastic resin layer B after photocuring) is formed.

【0111】また、現像後、PDP用基板の凹部内面の表面における蛍光体含有フォトレジストの密着性及び耐薬品性等を向上させる目的で、高圧水銀ランプ等による紫外線照射や加熱を行うこともできる。 [0111] Also, after the development, for the purpose of improving the adhesion and chemical resistance of the phosphor-containing photoresist on the surface of the recess inner surface of the substrate for PDP, it is possible to perform ultraviolet irradiation or heating by a high-pressure mercury lamp, etc. . この時の、紫外線の照射量は、通常、5〜10000mJ/cm 2とすることが好ましく、7〜5000mJ/cm 2とすることがより好ましく、10〜3000mJ/cm 2とすることが特に好ましい。 At this time, the irradiation amount of ultraviolet rays is generally preferably be 5~10000mJ / cm 2, more preferably to 7~5000mJ / cm 2, and particularly preferably to 10~3000mJ / cm 2. また、加熱時の温度は、60〜180℃とすることが好ましく、100〜180℃とすることがより好ましい。 The temperature at the time of heating is preferably set to 60 to 180 ° C., and more preferably set to 100 to 180 ° C.. また、加熱時間は、15〜90分間とすることが好ましい。 The heating time is preferably set to between 15 to 90 minutes. これらの紫外線の照射と加熱は、照射と加熱を別々に行ってもよく、どちらを先に行ってもよい。 Irradiation and heating of these ultraviolet may be subjected to heat and irradiation separately, either may be performed first.

【0112】〔(IV)焼成により不要分を除去する工程〕焼成により不要分を除去した後の蛍光体パターンを形成した状態を図6(IV)に示した。 [0112] shown in FIG. 6 the state of forming a phosphor pattern after removing the unnecessary components by calcination [(IV) step to remove unnecessary components by calcination] (IV). なお、図6(IV) Incidentally, FIG. 6 (IV)
において、21は蛍光体パターンである。 In, 21 is a phosphor pattern. 図6(IV)において、焼成方法としては、特に制限はなく、公知の焼成方法を使用し、蛍光体及び結着剤以外の不要分を除去し、蛍光体パターンを形成することができる。 In FIG. 6 (IV), as sintering method is not particularly limited, using known sintering methods, to remove unnecessary components other than the phosphor and the binder, it is possible to form a phosphor pattern. この時の、最高焼成温度は、350〜800℃とすることが好ましく、400〜600℃とすることがより好ましい。 At this time, the maximum firing temperature is preferably set to 350 to 800 ° C., and more preferably set to 400 to 600 ° C..
また、最高焼成温度での焼成時間は、3〜120分間とすることが好ましく、5〜90分間とすることがより好ましい。 Further, the firing time at the maximum firing temperature, preferably to between 3 to 120 minutes, and more preferably to between 5 to 90 minutes. この時の、昇温速度は、0.5〜50℃/分とすることが好ましく、1〜45℃/分とすることがより好ましい。 At this time, heating rate is preferably set to 0.5 to 50 ° C. / min, and more preferably set to 1 to 45 ° C. / min. また、最高焼成温度に到達する前の350〜 Also, before reaching the maximum firing temperature 350
450℃の間に、その温度を保持するステップを設けることができ、その保持時間は5〜100分間とすることが好ましい。 Between 450 ° C., can be provided with a step of holding the temperature, the retention time is preferably between 5 to 100 minutes.

【0113】本発明の蛍光体パターンの製造法は、工程数を低減できる等の点から、前記(I)〜 (III)の各工程を1色毎に繰り返して、赤色、緑色及び青色に発色する蛍光体を含有する感光性樹脂組成物層からなる多色パターンを形成した後、(IV)の工程を行ない多色の蛍光体パターンを形成することが好ましい。 [0113] phosphor pattern producing method of the present invention, from the viewpoint of capable of reducing the number of steps, wherein (I) ~ Repeat steps for each color (III), color red, green and blue after forming the multi-color pattern composed of the photosensitive resin composition layer containing a phosphor, it is preferable to form a multi-colored phosphor pattern performs steps (IV). 本発明の蛍光体パターンの製造法において、赤色、青色及び緑色に発色するそれぞれの蛍光体を単独で含む蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A)(3)は、 In the phosphor pattern producing method of the present invention, a red photosensitive resin composition layer containing a phosphor comprising alone each phosphor coloring in blue and green (thermoplastic resin layer A) (3) it is,
赤色、青色及び緑色の各色について、どの様な順番でも行うことができる。 Red, for blue and green colors, can be performed in any kind of order.

【0114】本発明の蛍光体パターンの製造法における(I)〜(III)の各工程を1色毎に繰り返して、赤色、緑色及び青色に発色する蛍光体を含有する感光性樹脂組成物層を含む多色パターンを形成した状態を図8に示した。 [0114] Repeat the process for producing the phosphor pattern of the present invention the steps of (I) ~ (III) in each color, red, green, and photosensitive resin composition layer containing a phosphor which developed a blue color the state of forming a multicolor pattern comprising shown in FIG. 図8において、3′aは1色目のパターン、 In FIG. 8, 3'a the first color pattern,
3′bは2色目のパターン及び3′cは3色目のパターンである。 3'b the second color pattern and 3'c is a pattern of third color. また、本発明の蛍光体パターンの製造法における(IV)の工程を行ない多色の蛍光体パターンを形成した状態を図9に示した。 Also showed a phosphor pattern state of forming a multicolor phosphor pattern performs steps in the production method (IV) of the present invention in FIG. 図9において、21aは1色目の蛍光体パターン、21bは2色目の蛍光体パターン及び21cは3色目の蛍光体パターンである。 In Figure 9, 21a is a first color phosphor pattern, 21b is a phosphor pattern and 21c of the second color is a phosphor pattern of third color.

【0115】また、本発明の蛍光体パターンの製造法は、凹部内面に形成された蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A)(3)の膜べりの抑制等の点から、前記蛍光体パターンの製造法における(I) [0115] The manufacturing method of the phosphor pattern of the present invention, the photosensitive resin composition layer containing a phosphor formed on the recess inner surface film loss of suppression, etc. (thermoplastic resin layer A) (3) from the point, in the production method of the phosphor pattern (I)
〜(IV)の各工程を1色毎に繰り返して、赤色、緑色及び青色に発色する多色の蛍光体パターンを形成することが好ましい。 ~ Each step is repeated for each color (IV), red, it is preferable to form a multi-colored phosphor pattern for green color, and blue.

【0116】本発明のプラズマディスプレイパネル用背面板は、上述のようにして得られた蛍光パターンを、プラズマディスプレイパネル用基板上に備えてなるものである。 [0116] A PDP back plate of the present invention, the fluorescence pattern obtained as described above, is made comprising a plasma display panel substrate. 以下に、プラズマディスプレイパネル用背面板について、図10を用いて説明する。 Hereinafter, the back plate for a plasma display panel will be described with reference to FIG. なお、図10は、プラズマディスプレイパネル(PDP)の一例を示した模式図であり、図10において14は透明基板、15はバリアリブ、17はストライプ状放電空間、21は蛍光体パターン、23はアドレス用電極、24は保護膜、25 Incidentally, FIG. 10 is a schematic diagram showing an example of a plasma display panel (PDP), 14 is a transparent substrate 10, 15 is barrier ribs, a stripe-shaped discharge space 17, the phosphor pattern 21, the address 23 use the electrode, 24 is a protective film, 25
は誘電体層、26は表示用電極及び27は前面板用基板である。 The dielectric layer 26 is the display electrode and 27 is a substrate for the front plate. 図10において、透明基板14、バリアリブ1 10, the transparent substrate 14, barrier ribs 1
5、蛍光体パターン21及びアドレス用電極23を含む下部がPDP用背面板であり、保護膜24、誘電体層2 5, the lower containing a phosphor pattern 21 and the address electrode 23 is a back plate for PDP, the protective layer 24, the dielectric layer 2
5、表示用電極26及び前面板用基板27を含む上部がPDP用前面板である。 5, the upper including a display electrode 26 and the front panel for the substrate 27 is a front panel for PDP. PDPは、電圧の印加方式から、AC(交流)型PDP、DC(直流)型PDP等に分類でき、一例として示した図10の模式図は、AC型PDPである。 PDP from application method of voltage, AC (alternating current) type PDP, it can be classified into DC (direct current) type PDP or the like, the schematic diagram of FIG. 10 shows as an example, an AC type PDP.

【0117】 [0117]

【実施例】以下、実施例により本発明を説明する。 EXAMPLES The following examples illustrate the invention. 製造例1 〔フィルム性付与ポリマ(a)溶液の作製〕撹拌機、還流冷却機、不活性ガス導入口及び温度計を備えたフラスコに、表1に示すを仕込み、窒素ガス雰囲気下で80 Production Example 1 [Film-imparting polymer (a) Preparation of Solution] stirrer, reflux condenser, a flask equipped with an inert gas inlet and a thermometer, was charged shown in Table 1, under a nitrogen gas atmosphere 80
℃に昇温し、反応温度を80℃±2℃に保ちながら、表1に示すを4時間かけて均一に滴下した。 ° C. the temperature was raised to, while maintaining the reaction temperature at 80 ° C. ± 2 ° C., it was uniformly added dropwise over 4 hours are shown in Table 1. の滴下後、80℃±2℃で6時間撹拌を続け、重量平均分子量が80,000、酸価が130mgKOH/gのフィルム性付与ポリマ(a)の溶液(固形分45.5重量%)を得た。 After the addition, continued 6 hours at 80 ° C. ± 2 ° C., a weight average molecular weight of 80,000, a solution of the acid value is 130 mgKOH / g film-imparting polymer (a) (solid content 45.5 wt%) Obtained.

【0118】 [0118]

【表1】 [Table 1]

【0119】製造例2 〔熱可塑性樹脂層A用溶液(Aー1)の作製〕表2に示す材料を、ライカイ機を用いて15分間混合し、熱可塑性樹脂層A用溶液(Aー1)を調製した。 [0119] The materials shown in Table 2 [Preparation of thermoplastic resin layer A solution (A-1)] Preparation Example 2, and mixed for 15 minutes using a chaser mill, a thermoplastic resin layer A solution (A-1 ) was prepared.

【0120】 [0120]

【表2】 [Table 2]

【0121】製造例3 〔熱可塑性樹脂層A用溶液(Aー2)の作製〕表3に示す材料を、ライカイ機を用いて15分間混合し、熱可塑性樹脂層A用溶液(Aー2)を調製した。 [0121] The materials shown in Table 3 Preparation of thermoplastic resin layer A solution (A-2)] Preparation Example 3, was mixed for 15 minutes using a chaser mill, a thermoplastic resin layer A solution (A-2 ) was prepared.

【0122】 [0122]

【表3】 [Table 3]

【0123】製造例4 〔感光性エレメント(i)の作製〕製造例2で得られた、熱可塑性樹脂層A用溶液(A−1)を、50μmの厚さのポリエチレンテレフタレートフィルム上に均一に塗布し、110℃の熱風対流式乾燥機で10分間乾燥して溶剤を除去し、熱可塑性樹脂層Aを形成した。 [0123] Production Example 4 was obtained in Production Example 2 [Preparation of photosensitive element (i)], the thermoplastic resin layer A solution (A-1), uniformly on a polyethylene terephthalate film having a thickness of 50μm coating, and dried at 110 ° C. hot air convection dryer for 10 minutes to remove the solvent, to form a thermoplastic resin layer a. 得られた熱可塑性樹脂層Aの厚さは60μmであった。 The thickness of the obtained thermoplastic resin layer A was 60 [mu] m. 次いで、熱可塑性樹脂層Aの上に、さらに、25μmの厚さのポリエチレンフィルムを、カバーフィルムとして張り合わせて、感光性エレメント(i)を作製した。 Then, on the thermoplastic resin layer A, further, the polyethylene film with a thickness of 25 [mu] m, by laminating a cover film to prepare a photosensitive element (i).

【0124】得られた感光性エレメント(i)のエッジフュージョン性を下記の方法で評価し、結果を表6に示した。 [0124] The edge fusion property of the resulting photosensitive element (i) and evaluated by the following methods. The results are shown in Table 6. 〔エッジフュージョン性〕ロール状に巻き取られた長さ90mの感光性エレメント(i)を、温度が23℃、湿度が60%Rhで保管し、ロール側面から感光層のしみ出しの様子を、6カ月間にわたって目視で評価した。 The photosensitive element of length 90m wound up in [Edge fusion property] rolled (i), the temperature is 23 ° C., humidity and stored at 60% Rh, the manner from the roll side surface of the exudation of the light-sensitive layer, It was visually evaluated over a period of six months. 評価基準は次の通りである。 The evaluation criteria are as follows. ○:エッジフュージョン性が良好なもの(6カ月間でも感光層のしみ出しがないもの) ×:エッジフュージョン性が不良なもの(6カ月間で感光層のしみ出しが発生したもの) ○: Edge fusion property is favorable (six that there is no exudation of the photosensitive layer at month) ×: those edge fusion resistance failure (at 6 months that exudation of the photosensitive layer occurs)

【0125】製造例5 〔感光性エレメント(ii)の作製〕製造例4において、 [0125] Preparation of photosensitive element (ii)] Production Example 5 Production Example 4,
製造例2で得られた熱可塑性樹脂層A用溶液(A−1) The thermoplastic resin layer A solution obtained in Production Example 2 (A-1)
を、製造例3で得られた熱可塑性樹脂層A用溶液(A− The thermoplastic resin layer A solution obtained in Production Example 3 (A-
2)に代えた以外は、製造例4と同様にして、感光性エレメント(ii)を作製した。 Except that instead of 2), in the same manner as in Production Example 4 was prepared a photosensitive element (ii). なお、感光性エレメント(ii)の熱可塑性樹脂層Aの厚さは、40μmであった。 The thickness of the thermoplastic resin layer A of the photosensitive element (ii) was 40 [mu] m. 得られた感光性エレメント(ii)のエッジフュージョン性を、製造例4と同様にして評価し、結果を表6に示した。 Edge fusion property of the resulting photosensitive element (ii), and evaluated in the same manner as in Example 4. The results are shown in Table 6.

【0126】製造例6 〔感光性エレメント(iii)の作製〕表4に示す材料を、ライカイ機を用いて15分間混合し、熱可塑性樹脂層A用溶液(A−3)を調製した。 [0126] The materials shown in Table 4 Preparation of photosensitive element (iii)] Production Example 6, and mixed for 15 minutes using a chaser mill, a thermoplastic resin layer A solution of (A-3) was prepared.

【0127】 [0127]

【表4】 [Table 4]

【0128】次いで、製造例4において、熱可塑性樹脂層A用溶液(A−1)を熱可塑性樹脂層A用溶液(A− [0128] Then, in Production Example 4, the thermoplastic resin layer A solution (A-1) a thermoplastic resin layer A solution (A-
3)に代えた以外は、製造例4と同様にして、感光性エレメント(iii)を作製した。 Was replaced 3), in the same manner as in Production Example 4 was prepared a photosensitive element (iii). なお、感光性エレメント(iii)の熱可塑性樹脂層Aの厚さは、40μmであった。 The thickness of the thermoplastic resin layer A of the photosensitive element (iii) was 40 [mu] m. 得られた感光性エレメント(iii)のエッジフュージョン性を、製造例4と同様にして評価し、結果を表6 Edge fusion property of the resulting photosensitive element (iii), and evaluated in the same manner as in Preparation Example 4, Table 6 Results
に示した。 It was shown to.

【0129】製造例7 〔感光性エレメント(iv)の作製〕表5に示す材料を、 [0129] The materials shown in Table 5 Preparation of photosensitive element (iv)] Preparation Example 7,
ライカイ機を用いて15分間混合し、熱可塑性樹脂層A And mixed for 15 minutes using a chaser mill, a thermoplastic resin layer A
用溶液(A−4)を調製した。 Use solution (A-4) was prepared.

【0130】 [0130]

【表5】 [Table 5]

【0131】次いで、製造例4において、熱可塑性樹脂層A用溶液(A−1)を熱可塑性樹脂層A用溶液(A− [0131] Then, in Production Example 4, the thermoplastic resin layer A solution (A-1) a thermoplastic resin layer A solution (A-
4)に代えた以外は、製造例4と同様にして、感光性エレメント(iv)を作製した。 Was replaced 4), in the same manner as in Production Example 4 was prepared a photosensitive element (iv). なお、感光性エレメント(iv)の熱可塑性樹脂層Aの厚さは、40μmであった。 The thickness of the thermoplastic resin layer A of the photosensitive element (iv) was 40 [mu] m. 得られた感光性エレメント(iv)のエッジフュージョン性を、製造例4と同様にして評価し、結果を表6に示した。 Edge fusion property of the resulting photosensitive element (iv), and evaluated in the same manner as in Example 4. The results are shown in Table 6.

【0132】 [0132]

【表6】 [Table 6]

【0133】表6の結果から、製造例4〜7で作製した、感光性エレメントのエッジフュージョン性は良好であった。 [0133] From the results in Table 6 were prepared in Production Example 4-7, was good edge fusion properties of the photosensitive element.

【0134】製造例8 〔熱可塑性樹脂層Bを有するフィルム(B−1)の作製〕表7に示す材料からなる樹脂溶液を、20μmの厚さのポリエチレンテレフタレートフィルム上に均一に塗布し、80〜110℃の熱風対流式乾燥機で10分間乾燥して蒸留水を除去し、熱可塑性樹脂層Bを形成した。 [0134] The resin solution consisting shown in Table 7 material Production Example 8 [Preparation of a film having a thermoplastic resin layer B (B-1)] was uniformly coated on a polyethylene terephthalate film thickness of 20 [mu] m, 80 dried for 10 minutes with distilled water to remove at to 110 ° C. hot air convection dryer to form a thermoplastic resin layer B.
得られた熱可塑性樹脂層Bの乾燥後の厚さは、70μm The dry thickness after the obtained thermoplastic resin layer B, 70 [mu] m
であった。 Met.

【0135】 [0135]

【表7】 [Table 7]

【0136】次いで、熱可塑性樹脂層Bの上に、厚さが25μmのポリエチレンフィルムをカバーフィルムとして張り合わせて、支持体フィルム、熱可塑性樹脂層B及びカバーフィルムからなる、熱可塑性樹脂層Bを有するフィルム(B−1)を作製した。 [0136] Then, on the thermoplastic resin layer B, by laminating a cover film is a polyethylene film 25μm thick, the support film, a thermoplastic resin layer B and the cover film has a thermoplastic resin layer B film (B-1) was prepared.

【0137】製造例9 〔熱可塑性樹脂層Bを有するフィルム(B−2)の作製〕表7に示す材料からなる樹脂溶液を、20μmの厚さのポリエチレンテレフタレートフィルム上に均一に塗布し、80〜110℃の熱風対流式乾燥機で10分間乾燥して溶剤を除去し、熱可塑性樹脂層Bを形成した。 [0137] The resin solution consisting shown in Table 7 material Preparation Example 9 Preparation of a film having a thermoplastic resin layer B (B-2)] was uniformly coated on a polyethylene terephthalate film thickness of 20 [mu] m, 80 dried for 10 minutes to remove the solvent at to 110 ° C. hot air convection dryer to form a thermoplastic resin layer B. 得られた熱可塑性樹脂層Bの乾燥後の厚さは、45μmであった。 Dry thickness after the obtained thermoplastic resin layer B was 45 [mu] m.

【0138】 [0138]

【表8】 [Table 8]

【0139】次いで、熱可塑性樹脂層Bの上に、厚さが25μmのポリエチレンフィルムをカバーフィルムとして張り合わせて、支持体フィルム、熱可塑性樹脂層B及びカバーフィルムからなる、熱可塑性樹脂層Bを有するフィルム(B−2)を作製した。 [0139] Then, on the thermoplastic resin layer B, by laminating a cover film is a polyethylene film 25μm thick, the support film, a thermoplastic resin layer B and the cover film has a thermoplastic resin layer B film (B-2) was prepared.

【0140】〔熱可塑性樹脂層Aを有する感光性エレメント及び熱可塑性樹脂層Bを有するフィルムの積層〕 実施例1 凹凸を有するPDP用基板(ストライプ状のバリアリブ、バリアリブ間の開口幅150μm、バリアリブの幅70μm、バリアリブの高さ150μm)のバリアリブが形成された側に、図3に示す本発明の積層装置を用いて、製造例4で得られた熱可塑性樹脂層Aを有する感光性エレメント(i)のポリエチレンフィルムを剥がしながら、ラミネート温度が60℃、ラミネート速度が0. [0140] PDP substrate having a [photosensitive element and the laminated film having a thermoplastic resin layer B having a thermoplastic resin layer A] Example 1 uneven (striped barrier ribs, the opening width 150μm between the barrier ribs, the barrier ribs width 70 [mu] m, the side barrier ribs are formed in the height 150 [mu] m) of the barrier rib, a stacked device of the present invention shown in FIG. 3, a photosensitive element having a thermoplastic resin layer a obtained in production example 4 (i while peeling off the polyethylene film), laminating temperature is 60 ° C., laminating speed is zero.
5m/分、圧着圧力(シリンダ圧力)が5×10 4 Pa 5 m / min, crimped pressure (cylinder pressure) is 5 × 10 4 Pa
(幅10cmの基板を用いたため、このときの線圧は1. (For using a substrate of width 10 cm, the linear pressure at this time is 1.
2×10 3 N/m)で積層し、感光性エレメント(i)のバリアリブと接していない面のポリエチレンテレフタレートフィルムを剥離、熱可塑性樹脂層A上に熱可塑性樹脂層Bを有するフィルム(B−1)のポリエチレンフィルムを剥がしながら、ラミネート温度が120℃、ラミネート速度が0.5m/分、圧着圧力(シリンダ圧力)が4×10 5 Pa(幅10cmの基板を用いたため、このときの線圧は9.8×10 3 N/m)で積層し、凹部内面に熱可塑性樹脂層A及び熱可塑性樹脂層Bを埋め込んだ。 2 × laminated in 10 3 N / m), peeling the polyethylene terephthalate film surface not in contact with the barrier rib of the photosensitive element (i), a film having a thermoplastic resin layer B on the thermoplastic resin layer A (B- while peeling off the polyethylene film of 1), laminating temperature is 120 ° C., laminating speed is 0.5 m / min, since the crimping pressure (cylinder pressure) using a substrate of 4 × 10 5 Pa (width 10 cm, the linear pressure at this time is laminated with 9.8 × 10 3 N / m) , embedded thermoplastic resin layer a and the thermoplastic resin layer B in the recess inner surface.

【0141】熱可塑性樹脂層A及び熱可塑性樹脂層Bが積層された基板を、ストライプ方向に対して直角の方向に切断し、その切断面を電子顕微鏡にて観察し、蛍光体層形成性を確認した結果、均一で良好な蛍光体層が形成されていることが分かった。 [0141] The substrate thermoplastic resin layer A and the thermoplastic resin layer B is laminated, and cut into a direction perpendicular to the stripe direction, and observe the cut surface with an electron microscope, the phosphor layer-forming results of verification, it was found that uniform and excellent phosphor layer is formed.

【0142】実施例2 図4に示す本発明の積層装置を用いて、製造例5で得られた熱可塑性樹脂層Aを有する感光性エレメント(ii) [0142] Example 2 using the laminated device of the present invention shown in FIG. 4, a photosensitive element having a thermoplastic resin layer A obtained in Production Example 5 (ii)
及び熱可塑性樹脂層Bを有するフィルム(B−2)それぞれのポリエチレンフィルムを剥がしながら、ラミネート温度が20℃、ラミネート速度が0.5m/分、圧着圧力(シリンダ圧力)が5×10 4 Pa(幅10cmのフィルムを用いたため、このときの線圧は1.2×10 3 N/ And while peeling off the film (B-2) of each polyethylene film having a thermoplastic resin layer B, laminating temperature is 20 ° C., laminating speed is 0.5 m / min, crimped pressure (cylinder pressure) is 5 × 10 4 Pa ( for using the film of width 10 cm, the linear pressure at this time is 1.2 × 10 3 N /
m)で積層し、感光性エレメント(ii)の熱可塑性樹脂層Bと接していない面のポリエチレンテレフタレートフィルムを剥離しながら、凹凸を有するPDP用基板(ストライプ状のバリアリブ、バリアリブ間の開口幅150 Layered in m), while peeling the polyethylene terephthalate film surface not in contact with the thermoplastic resin layer B of the photosensitive element (ii), PDP substrate (striped barrier ribs, the opening width between the barrier ribs 150 having an irregular
μm、バリアリブの幅70μm、バリアリブの高さ15 μm, width 70μm of the barrier ribs, the barrier rib height 15
0μm)のバリアリブが形成された側に、ラミネート温度が120℃、ラミネート速度が0.5m/分、圧着圧力(シリンダ圧力)が4×10 5 Pa(幅10cmの基板を用いたため、このときの線圧は9.8×10 3 N/m)で積層し、凹部内面に熱可塑性樹脂層A及び熱可塑性樹脂層Bを埋め込んだ。 The side barrier rib is formed of 0 .mu.m), laminating temperature is 120 ° C., laminating speed is 0.5 m / min, since the crimping pressure (cylinder pressure) using a substrate of 4 × 10 5 Pa (width 10 cm, in this case line pressure laminated in 9.8 × 10 3 N / m) , embedded thermoplastic resin layer a and the thermoplastic resin layer B in the recess inner surface.

【0143】熱可塑性樹脂層A及び熱可塑性樹脂層Bが積層された基板を、ストライプ方向に対して直角の方向に切断し、その切断面を電子顕微鏡にて観察し、蛍光体層形成性を確認した結果、均一で良好な蛍光体層が形成されていることが分かった。 [0143] The substrate thermoplastic resin layer A and the thermoplastic resin layer B is laminated, and cut into a direction perpendicular to the stripe direction, and observe the cut surface with an electron microscope, the phosphor layer-forming results of verification, it was found that uniform and excellent phosphor layer is formed.

【0144】実施例3 図4に示す本発明の積層装置を用いて、製造例6で得られた熱可塑性樹脂層Aを有する感光性エレメント(ii [0144] Using a lamination apparatus of the present invention shown in Example 3 Fig. 4, a photosensitive element having a thermoplastic resin layer A obtained in Production Example 6 (ii
i)及び熱可塑性樹脂層Bを有するフィルム(B−2) i) and a film having a thermoplastic resin layer B (B-2)
それぞれのポリエチレンフィルムを剥がしながら、ラミネート温度が20℃、ラミネート速度が0.5m/分、 While peeling off the respective polyethylene film, laminating temperature is 20 ° C., laminating speed is 0.5 m / min,
圧着圧力(シリンダ圧力)が5×10 Pa(幅10c Crimping pressure (cylinder pressure) is 5 × 10 4 Pa (width 10c
mのフィルムを用いたため、このときの線圧は1.2× Since using m of the film, the linear pressure at this time is 1.2 ×
10 3 N/m)で積層し、感光性エレメント(iii)の熱可塑性樹脂層Bと接していない面のポリエチレンテレフタレートフィルムを剥離しながら、凹凸を有するPDP用基板(ストライプ状のバリアリブ、バリアリブ間の開口幅150μm、バリアリブの幅70μm、バリアリブの高さ150μm)のバリアリブが形成された側に、ラミネート温度が120℃、ラミネート速度が0.5m/ 10 3 laminated in N / m), while peeling the polyethylene terephthalate film of the thermoplastic resin layer B and not in contact with the surface of the photosensitive element (iii), PDP substrate having an uneven (striped barrier ribs, between the barrier ribs opening width 150 [mu] m, the width 70μm of the barrier ribs, the side barrier ribs are formed in the height 150 [mu] m) of the barrier rib, laminating temperature is 120 ° C., laminating speed is 0.5 m /
分、圧着圧力(シリンダ圧力)が4×10 5 Pa(幅10c Min, crimping pressure (cylinder pressure) is 4 × 10 5 Pa (width 10c
mの基板を用いたため、このときの線圧は9.8×10 3 Since using the substrate of m, the linear pressure at this time is 9.8 × 10 3
N/m)で積層し、凹部内面に熱可塑性樹脂層A及び熱可塑性樹脂層Bを埋め込んだ。 Laminated in N / m), embedded thermoplastic resin layer A and the thermoplastic resin layer B in the recess inner surface.

【0145】熱可塑性樹脂層A及び熱可塑性樹脂層Bが積層された基板を、ストライプ方向に対して直角の方向に切断し、その切断面を電子顕微鏡にて観察し、蛍光体層形成性を確認した結果、均一で良好な蛍光体層が形成されていることが分かった。 [0145] The substrate thermoplastic resin layer A and the thermoplastic resin layer B is laminated, and cut into a direction perpendicular to the stripe direction, and observe the cut surface with an electron microscope, the phosphor layer-forming results of verification, it was found that uniform and excellent phosphor layer is formed.

【0146】実施例4 図4に示す本発明の積層装置を用いて、製造例7で得られた熱可塑性樹脂層Aを有する感光性エレメント(iv) [0146] Example 4 using the laminated device of the present invention shown in FIG. 4, a photosensitive element having a thermoplastic resin layer A obtained in Production Example 7 (iv)
及び熱可塑性樹脂層Bを有するフィルム(B−2)それぞれのポリエチレンフィルムを剥がしながら、ラミネート温度が20℃、ラミネート速度が0.5m/分、圧着圧力(シリンダ圧力)が5×10 4 Pa(幅10cmのフィルムを用いたため、このときの線圧は1.2×10 3 N/ And while peeling off the film (B-2) of each polyethylene film having a thermoplastic resin layer B, laminating temperature is 20 ° C., laminating speed is 0.5 m / min, crimped pressure (cylinder pressure) is 5 × 10 4 Pa ( for using the film of width 10 cm, the linear pressure at this time is 1.2 × 10 3 N /
m)で積層し、感光性エレメント(iv)の熱可塑性樹脂層Bと接していない面のポリエチレンテレフタレートフィルムを剥離しながら、凹凸を有するPDP用基板(ストライプ状のバリアリブ、バリアリブ間の開口幅150 Layered in m), while peeling the polyethylene terephthalate film surface not in contact with the thermoplastic resin layer B of the photosensitive element (iv), PDP substrate (striped barrier ribs, the opening width between the barrier ribs 150 having an irregular
μm、バリアリブの幅70μm、バリアリブの高さ15 μm, width 70μm of the barrier ribs, the barrier rib height 15
0μm)のバリアリブが形成された側に、ラミネート温度が120℃、ラミネート速度が0.5m/分、圧着圧力(シリンダ圧力)が4×10 5 Pa(幅10cmの基板を用いたため、このときの線圧は9.8×10 3 N/m)で積層し、凹部内面に熱可塑性樹脂層A及び熱可塑性樹脂層Bを埋め込んだ。 The side barrier rib is formed of 0 .mu.m), laminating temperature is 120 ° C., laminating speed is 0.5 m / min, since the crimping pressure (cylinder pressure) using a substrate of 4 × 10 5 Pa (width 10 cm, in this case line pressure laminated in 9.8 × 10 3 N / m) , embedded thermoplastic resin layer a and the thermoplastic resin layer B in the recess inner surface.

【0147】熱可塑性樹脂層A及び熱可塑性樹脂層Bが積層された基板を、ストライプ方向に対して直角の方向に切断し、その切断面を電子顕微鏡にて観察し、蛍光体層形成性を確認した結果、均一で良好な蛍光体層が形成されていることが分かった。 [0147] The substrate thermoplastic resin layer A and the thermoplastic resin layer B is laminated, and cut into a direction perpendicular to the stripe direction, and observe the cut surface with an electron microscope, the phosphor layer-forming results of verification, it was found that uniform and excellent phosphor layer is formed.

【0148】実施例5 〔赤蛍光体パターンの作製〕 〔(I)凹凸を有する基板の凹凸表面上に、赤蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A)及び熱可塑性樹脂層Bを形成する工程〕実施例2と同様にして、感光性エレメント(ii)及びフィルム(B−2)を用いて基板に熱可塑性樹脂層A及び熱可塑性樹脂層Bを積層した。 [0148] on the uneven surface of the substrate having the Preparation of the red phosphor pattern] [(I) uneven Example 5, the photosensitive resin composition layer containing a red phosphor (thermoplastic resin layer A) and a thermoplastic in a similar manner to step] example 2 to form a resin layer B, was laminated thermoplastic resin layer a and the thermoplastic resin layer B to a substrate using a photosensitive element (ii) and film (B-2). 〔(II)活性光線を像的に照射する工程〕次に、ポリエチレンテレフタレートフィルムごと熱可塑性樹脂層Bを剥離して除き、熱可塑性樹脂層A上に試験用フォトマスクを密着させて、(株)オーク製作所製HMW−590型露光機を使用し、500mJ/cm 2で活性光線を像的に照射した。 [(II) Step of irradiating active light rays imagewise Next, removed by peeling off the polyethylene terephthalate film by the thermoplastic resin layer B, and is adhered a photomask for test on the thermoplastic resin layer A, (strain ) using oak Seisakusho HMW-590 type exposure machine, the active light was imagewise irradiated with 500 mJ / cm 2.

【0149】〔(III)現像により不要部を除去する工程〕次いで、活性光線の照射後、常温で1時間放置した後、1重量%炭酸ナトリウム水溶液を用いて、30℃で120秒間スプレー現像した。 [0149] Then [(III) Step of removing the unnecessary portion by development], after the irradiation with actinic rays, after standing for 1 hour at room temperature, using a 1 wt% aqueous solution of sodium carbonate and 120 seconds spray development at 30 ° C. . 現像後、80℃で10分間乾燥し、東芝電材(株)製東芝紫外線照射装置を使用して、3J/cm 2の紫外線照射を行い、さらに、150℃で1時間、乾燥器中で加熱した。 After the development, and dried at 80 ° C. 10 minutes, using a Toshiba UV irradiation apparatus by Toshiba material Co., irradiated with ultraviolet rays of 3J / cm 2, further 1 hour at 0.99 ° C., it was heated in a dryer . 〔(IV)焼成により不要分を除去する工程〕次いで、5 [(IV) step to remove unnecessary components by calcination] Then, 5
00℃で30分間加熱処理(焼成)を行い、不必要な樹脂成分を除去し、PDP用基板の凹部内面に赤蛍光体パターンを形成させた。 00 performed ℃ for 30 minutes heat treatment (baking) to remove unnecessary resin component to form a red phosphor pattern in the recess inner surface of the substrate for PDP.

【0150】得られた赤蛍光体パターンの断面を、実体顕微鏡及びSEMにより目視にて観察し、青蛍光体パターンの形成状況を評価した結果、赤蛍光体層がPDP用基板の凹部内面(バリアリブ壁面及び基板面)上に均一に形成されていた。 [0150] The cross section of the red phosphor pattern, were visually observed by a stereoscopic microscope and SEM, blue phosphor pattern result of evaluating the formation conditions of the recess inner surface (barrier ribs of the substrate for the red phosphor layer PDP It was uniformly formed on the wall surface and the substrate surface).

【0151】実施例6 〔青蛍光体パターンの作製〕 〔(I)凹凸を有する基板の凹凸表面上に、青蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A)及び熱可塑性樹脂層Bを形成する工程〕実施例2と同様にして、感光性エレメント(iii)及びフィルム(B−2) [0151] Preparation of blue phosphor pattern] Example 6 [on the uneven surface of the substrate having the (I) uneven, blue phosphor photosensitive resin composition layer containing a (thermoplastic resin layer A) and a thermoplastic step of forming a resin layer B in the same manner as in example 2, the photosensitive element (iii) and the film (B-2)
を用いて基板に熱可塑性樹脂層A及び熱可塑性樹脂層B The thermoplastic resin layer A and the thermoplastic resin layer B to a substrate using a
を積層した。 It was laminated. 〔(II)活性光線を像的に照射する工程〕次に、ポリエチレンテレフタレートフィルムごと熱可塑性樹脂層Bを剥離して除き、熱可塑性樹脂層A上に試験用フォトマスクを密着させて、(株)オーク製作所製HMW−590型露光機を使用し、500mJ/cm 2で活性光線を像的に照射した。 [(II) Step of irradiating active light rays imagewise Next, removed by peeling off the polyethylene terephthalate film by the thermoplastic resin layer B, and is adhered a photomask for test on the thermoplastic resin layer A, (strain ) using oak Seisakusho HMW-590 type exposure machine, the active light was imagewise irradiated with 500 mJ / cm 2.

【0152】〔(III)現像により不要部を除去する工程〕次いで、活性光線の照射後、常温で1時間放置した後、1重量%炭酸ナトリウム水溶液を用いて、30℃で120秒間スプレー現像した。 [0152] Then [(III) Step of removing the unnecessary portion by development], after the irradiation with actinic rays, after standing for 1 hour at room temperature, using a 1 wt% aqueous solution of sodium carbonate and 120 seconds spray development at 30 ° C. . 現像後、80℃で10分間乾燥し、東芝電材(株)製東芝紫外線照射装置を使用して、3J/cm 2の紫外線照射を行い、さらに、150℃で1時間、乾燥器中で加熱した。 After the development, and dried at 80 ° C. 10 minutes, using a Toshiba UV irradiation apparatus by Toshiba material Co., irradiated with ultraviolet rays of 3J / cm 2, further 1 hour at 0.99 ° C., it was heated in a dryer . 〔(IV)焼成により不要分を除去する工程〕次いで、5 [(IV) step to remove unnecessary components by calcination] Then, 5
00℃で30分間加熱処理(焼成)を行い、不必要な樹脂成分を除去し、PDP用基板の凹部内面に青蛍光体パターンを形成させた。 00 performed ℃ for 30 minutes heat treatment (baking) to remove unnecessary resin component to form a blue phosphor pattern in the recess inner surface of the substrate for PDP.

【0153】得られた青蛍光体パターンの断面を、実体顕微鏡及びSEMにより目視にて観察し、青蛍光体パターンの形成状況を評価した結果、青蛍光体層がPDP用基板の凹部内面(バリアリブ壁面及び基板面)上に均一に形成されていた。 [0153] The cross section of the blue phosphor pattern, were visually observed by a stereoscopic microscope and SEM, blue phosphor pattern result of evaluating the formation conditions of the blue phosphor layer concave inner surface of the substrate for PDP (barrier rib It was uniformly formed on the wall surface and the substrate surface).

【0154】実施例7 〔緑蛍光体パターンの作製〕 〔(I)凹凸を有する基板の凹凸表面上に、緑蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A)及び熱可塑性樹脂層Bを形成する工程〕実施例2と同様にして、感光性エレメント(iv)及びフィルム(B−2)を用いて基板に熱可塑性樹脂層A及び熱可塑性樹脂層Bを積層した。 [0154] on the uneven surface of the substrate having the Preparation of green phosphor pattern] [(I) irregularities Example 7, the photosensitive resin composition layer containing a green phosphor (the thermoplastic resin layer A) and a thermoplastic in a similar manner to step] example 2 to form a resin layer B, was laminated thermoplastic resin layer a and the thermoplastic resin layer B to a substrate using a photosensitive element (iv) and film (B-2). 〔(II)活性光線を像的に照射する工程〕次に、ポリエチレンテレフタレートフィルムごと熱可塑性樹脂層Bを剥離して除き、熱可塑性樹脂層A上に試験用フォトマスクを密着させて、(株)オーク製作所製HMW−590型露光機を使用し、500mJ/cm 2で活性光線を像的に照射した。 [(II) Step of irradiating active light rays imagewise Next, removed by peeling off the polyethylene terephthalate film by the thermoplastic resin layer B, and is adhered a photomask for test on the thermoplastic resin layer A, (strain ) using oak Seisakusho HMW-590 type exposure machine, the active light was imagewise irradiated with 500 mJ / cm 2.

【0155】〔(III)現像により不要部を除去する工程〕次いで、活性光線の照射後、常温で1時間放置した後、1重量%炭酸ナトリウム水溶液を用いて、30℃で120秒間スプレー現像した。 [0155] Then [(III) Step of removing the unnecessary portion by development], after the irradiation with actinic rays, after standing for 1 hour at room temperature, using a 1 wt% aqueous solution of sodium carbonate and 120 seconds spray development at 30 ° C. . 現像後、80℃で10分間乾燥し、東芝電材(株)製東芝紫外線照射装置を使用して、3J/cm 2の紫外線照射を行い、さらに、150℃で1時間、乾燥器中で加熱した。 After the development, and dried at 80 ° C. 10 minutes, using a Toshiba UV irradiation apparatus by Toshiba material Co., irradiated with ultraviolet rays of 3J / cm 2, further 1 hour at 0.99 ° C., it was heated in a dryer . 〔(IV)焼成により不要分を除去する工程〕次いで、5 [(IV) step to remove unnecessary components by calcination] Then, 5
00℃で30分間加熱処理(焼成)を行い、不必要な樹脂成分を除去し、PDP用基板の凹部内面に緑蛍光体パターンを形成させた。 00 performed ℃ for 30 minutes heat treatment (baking) to remove unnecessary resin component and the recess inner surface of the substrate for PDP to form a green phosphor pattern.

【0156】得られた緑蛍光体パターンの断面を、実体顕微鏡及びSEMにより目視にて観察し、緑蛍光体パターンの形成状況を評価した結果、緑蛍光体層がPDP用基板の凹部内面(バリアリブ壁面及び基板面)上に均一に形成されていた。 [0156] The cross section of the green phosphor pattern was observed visually by a stereoscopic microscope and SEM, green phosphors result of evaluating the formation conditions of the pattern, concave inner surface (barrier rib green phosphor layer substrate for PDP It was uniformly formed on the wall surface and the substrate surface).

【0157】以上の結果から、本発明の積層方法及び積層装置を用いて蛍光体パターンを製造することにより、 [0157] From the above results, by preparing a phosphor pattern using the lamination method and laminating apparatus of the present invention,
良好な蛍光体パターンを製造することができる。 It is possible to produce a good phosphor pattern.

【0158】実施例8 〔3色パターンの形成〕実施例5における(I)〜(II [0158] in Example 8 Formation of 3-color pattern] Example 5 (I) ~ (II
I)の工程を行って得られた、1色目の赤色に発色する蛍光体を含有する感光性樹脂組成物層が形成された基板を用いて、試験例2の(I)〜(III)と同様の工程を行って、2色目の青色に発色する蛍光体を含有する感光性樹脂組成物層を形成し、次いで、試験例3の(I)〜 Obtained by performing the steps of I), using a substrate with a photosensitive resin composition layer formed thereon containing a phosphor coloring in red first color, Test Example 2 and (I) ~ (III) by performing the same process, the second color to form a photosensitive resin composition layer containing a phosphor which developed a blue color, then the test example 3 (I) ~
(III)と同様の工程を行って、3色目の緑色に発色する蛍光体を含有する感光性樹脂組成物層を形成して多色のパターンを作製した。 By performing the same processes as (III), to produce a multi-colored pattern to form a photosensitive resin composition layer containing a phosphor coloring in green third color. 次に、得られた多色のパターンを用いて、実施例5における(IV)の工程を行い、多色の蛍光体パターンが形成されたPDP用背面板を作製した。 Then, using the pattern of the resulting multicolor, a step of (IV) in Example 5, to prepare a back plate for PDP of multicolor phosphor pattern is formed.

【0159】得られた多色の蛍光体パターンの断面を、 [0159] The cross-section of the resulting multicolor phosphor pattern,
実体顕微鏡及びSEMにより目視にて観察し、多色の蛍光体パターンの形成状況を評価した結果、赤、青及び緑に発色する多色の蛍光体パターンがPDP用背面板の空間(バリアリブ壁面及びセル底面上)に均一に形成されていることを確認した。 Was visually observed by a stereoscopic microscope and SEM, the results of evaluating the formation conditions of the multi-colored phosphor pattern, red, space (barrier rib wall multicolor phosphor pattern Backplate PDP coloring in blue and green, and it was confirmed that are uniformly formed in the cell on the bottom).

【0160】 [0160]

【発明の効果】請求項1記載の積層方法は、二種類以上のフィルムを用いて、それぞれのフィルムを作業性よく基板上に積層することができる。 The method of laminating according to claim 1, wherein, according to the present invention, using two or more kinds of films, each film can be laminated with good workability on a substrate. 請求項2記載の積層方法は、請求項1記載の発明の効果を奏し、さらにPDP The method of laminating the second aspect, to provide an advantage of the invention described in claim 1, further PDP
用基板等の凹凸を有する基板上に、作業性よく積層することができる。 On a substrate having an unevenness of use substrate, it can be laminated good workability. 請求項3記載の積層方法は、請求項1又は2記載の発明の効果を奏し、より作業性に優れる。 The method of laminating the third aspect, to provide an advantage of the invention of claim 1 or 2, more excellent workability. 請求項4記載の積層方法は、請求項1、2又は3記載の発明の効果を奏し、さらにプリント配線板用基板、カラーフィルタ等の製造に好適である。 The method of laminating a fourth aspect, to provide an advantage of the invention of claim 1, 2 or 3, further printed circuit board substrate, is suitable for the production of such a color filter. 請求項5記載の積層方法は、請求項4記載の発明の効果を奏し、さらにプラズマディスプレイパネル、EL基板等の製造に好適である。 The method of laminating according to claim 5, wherein the to provide an advantage of the invention of claim 4, further plasma display panel is suitable for the production of such EL substrate. 請求項6記載の積層方法は、請求項1、2、3、4 The method of laminating according to claim 6, wherein the claim 1, 2, 3, 4
又は5記載の発明の効果を奏し、よりプラズマディスプレイパネル等の製造に好適である。 Or 5 to provide an advantage of the invention described is suitable for more production of such a plasma display panel. 請求項7記載の積層方法は、請求項1、2、3、4、5又は6記載の発明の効果を奏し、より作業性に優れる。 The method of laminating according to claim 7, wherein the to provide an advantage of the invention of claim 2, 3, 4, 5 or 6, more excellent workability.

【0161】請求項8及び9記載の積層装置は、熱可塑性樹脂層を有する、二種類以上のフィルムを用いて、それぞれの熱可塑性樹脂層を作業性よく基板上に積層することができる。 [0161] laminating apparatus according to claim 8 and 9 wherein has a thermoplastic resin layer, by using two or more kinds of films, each of the thermoplastic resin layer may be laminated to the workability substrate. 請求項10記載の積層装置は、熱可塑性樹脂層を有する、二種類以上のフィルムを用いて、それぞれの熱可塑性樹脂層を作業性よく基板上に積層することができ、スペースをとらない積層装置である。 Stacking device according to claim 10 includes a thermoplastic resin layer, by using two or more kinds of films, each of the thermoplastic resin layer can be laminated to the good workability substrate lamination apparatus which does not take the space it is. 請求項11記載の積層装置は、請求項8、9又は10記載の発明の効果を奏し、さらに作業開始準備が容易であり、メンテナンス性に優れる。 Stacking device according to claim 11 is to provide an advantage of the invention of claim 8, 9 or 10, wherein it is easy to further work start preparation, excellent maintainability. 請求項12記載の積層装置は、 Stacking apparatus of claim 12, wherein the
請求項8、9又は10記載の発明の効果を奏し、さらに積層時の欠陥を抑制できる。 Provide an advantage of the invention of claim 8, 9 or 10, wherein it further suppress defects during lamination.

【0162】請求項13記載の蛍光体パターンの製造法は、高精度な蛍光体パターンを製造できるものである。 [0162] preparation of a phosphor pattern according to claim 13 are those capable of producing high-precision phosphor pattern.
請求項14記載の蛍光体パターンは、高精度に形成されたもので、均一性に優れたものである。 Phosphor pattern according to claim 14 has been formed with high accuracy, is excellent in uniformity. 請求項15記載のプラズマディスプレイパネル用背面板は、高精度に形成された蛍光体パターンを備えたものである。 A PDP back plate according to claim 15, wherein is one having a phosphor pattern formed with high precision.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】バリアリブが形成されたPDP用基板の一例を示した模式図である。 1 is a schematic diagram showing an example of a substrate for the PDP barrier ribs are formed.

【図2】バリアリブが形成されたPDP用基板の一例を示した模式図である。 [Figure 2] barrier rib is a schematic view showing an example of a PDP substrate formed it is.

【図3】本発明の積層装置の一例を示した模式図である。 3 is a schematic diagram showing an example of a lamination apparatus of the present invention.

【図4】本発明の積層装置の一例を示した模式図である。 4 is a schematic diagram showing an example of a lamination apparatus of the present invention.

【図5】凹凸を有する基板の凹凸表面上を示した模式図である。 5 is a schematic view showing the upper irregular surface of the substrate having unevenness.

【図6】蛍光体パターンの製造法の各工程の一例を示した模式図である。 6 is a schematic diagram showing an example of each step of the process of the phosphor pattern.

【図7】凹部内面を示した模式図である。 7 is a schematic view showing a concave inner surface.

【図8】蛍光体を含有する感光性樹脂組成物層からなる多色パターンを形成した状態を示した模式図である。 8 is a schematic view showing a state of forming a multi-color pattern composed of the photosensitive resin composition layer containing a phosphor.

【図9】多色の蛍光体パターンを形成した状態を示した模式図である。 9 is a schematic view showing a state of forming a multicolor phosphor pattern.

【図10】プラズマディスプレイパネル用背面板の一例を示した模式図である。 10 is a schematic view showing an example of a plasma display panel back plate.

【符号の説明】 DESCRIPTION OF SYMBOLS

1 …第1の供給ロール 2 …第2の供給ロール 3 …熱可塑性樹脂層A 3 …蛍光体を含有する感光性樹脂組成物層(熱可塑性樹脂層A) 3′…光硬化後の蛍光体を含有する感光性樹脂組成物層 3′a…1色目のパターン 3′b…2色目のパターン 3′c…3色目のパターン 4 …熱可塑性樹脂層B 5A …支持体フィルム 5B …支持体フィルム 6A …カバーフィルム 6B …カバーフィルム 7 …基板 8 …カバーフィルム巻取ロール 9 …支持体フィルム巻取ロール 10 …積層ロール 11 …搬送ロール 12 …送りロール 13 …合わせロール 14 …透明基板 15 …バリアリブ 16 …格子状放電空間 17 …ストライプ状放電空間 18 …凹凸表面上 19 …フォトマスク 20 …活性光線 21 …蛍光体パターン 21a…1色目の蛍 1 ... first supply roll 2 ... photosensitive resin composition layer containing a second supply roll 3 ... thermoplastic resin layer A 3 ... phosphor (thermoplastic resin layer A) 3 '... phosphor after photocuring the photosensitive resin composition layer 3'a ... 1-color pattern 3'b ... 2-color pattern 3'c ... 3-color pattern 4 ... thermoplastic resin layer B 5A containing ... support film 5B ... support film 6A ... cover film 6B ... cover film 7 ... substrate 8 ... cover film take-up roll 9 ... support film takeup roll 10 ... laminating roll 11 ... conveying rolls 12 ... feed rolls 13 ... mating roll 14 ... transparent substrate 15 ... barrier ribs 16 firefly ... lattice-shaped discharge space 17 ... striped discharge space 18 ... irregular surface on 19 ... photomask 20 ... active light 21 ... phosphor pattern 21a ... 1 color 光体パターン 21b…2色目の蛍光体パターン 21c…3色目の蛍光体パターン 22 …凹部内面 23 …アドレス用電極 24 …保護膜 25 …誘電体層 26 …表示用電極 27 …前面板用基板 Light body pattern 21b ... 2-color phosphor pattern 21c ... 3-color phosphor pattern 22 ... concave inner surface 23 ... address electrodes 24 ... substrate protective layer 25 ... dielectric layer 26 ... display electrodes 27 ... front plate

───────────────────────────────────────────────────── フロントページの続き (72)発明者 田仲 裕之 茨城県日立市東町四丁目13番1号 日立化 成工業株式会社茨城研究所内 (72)発明者 和田 有美子 茨城県日立市東町四丁目13番1号 日立化 成工業株式会社茨城研究所内 (72)発明者 佐藤 和也 茨城県日立市東町四丁目13番1号 日立化 成工業株式会社茨城研究所内 (72)発明者 木村 直紀 茨城県日立市東町四丁目13番1号 日立化 成工業株式会社茨城研究所内 (72)発明者 丹野 清吉 茨城県日立市東町四丁目13番1号 日立化 成工業株式会社半導体・液晶材料事業部開 発センタ内 (72)発明者 角丸 肇 茨城県日立市東町四丁目13番1号 日立化 成工業株式会社山崎工場内 ────────────────────────────────────────────────── ─── of the front page continued (72) inventor Hiroyuki Tanaka Hitachi City, Ibaraki Prefecture Higashi chome 13th No. 1 Hitachi Chemical industry Co., Ltd. Ibaraki the laboratory (72) inventor Yumiko Wada Hitachi City, Ibaraki Prefecture Higashi chome No. 13 No. 1 Hitachi Chemical industry Co., Ltd. Ibaraki the laboratory (72) inventor Kazuya Sato Hitachi City, Ibaraki Prefecture Higashi chome 13th No. 1 Hitachi Chemical industry Co., Ltd. Ibaraki the laboratory (72) inventor Naoki Kimura Hitachi City, Ibaraki Prefecture Higashimachi chome 13th No. 1 Hitachi Chemical industry Co., Ltd. Ibaraki the laboratory (72) inventor Seikichi Tanno Hitachi City, Ibaraki Prefecture Higashi chome 13th No. 1 Hitachi Chemical industry Co., Ltd. semiconductor and liquid crystal materials business BuHiraki onset within the center (72) inventor rounded Hajime Hitachi City, Ibaraki Prefecture Higashi chome 13th No. 1 Hitachi Chemical industry Co., Ltd. Yamazaki in the factory

Claims (15)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 フィルムAを第1の供給部から供給し、 The method according to claim 1 Film A was supplied from the first supply unit,
    フィルムBを第2の供給部から供給して、基板上にフィルムAを、その上にフィルムBを積層することを特徴とする積層方法。 The film B is supplied from the second supply unit, the film A on the substrate, lamination method comprising laminating a film B thereon.
  2. 【請求項2】 基板が、凹凸を有する基板である請求項1記載の積層方法。 2. A substrate The method of laminating according to claim 1, wherein the substrate having unevenness.
  3. 【請求項3】 フィルムAが、熱可塑性樹脂層Aを有するフィルムであり、フィルムBが、熱可塑性樹脂層Bを有するフィルムである請求項1又は2記載の積層方法。 Wherein film A is a film having a thermoplastic resin layer A, film B The method of laminating according to claim 1 or 2, wherein a film having a thermoplastic resin layer B.
  4. 【請求項4】 熱可塑性樹脂層Aが、(a)フィルム性付与ポリマ、(b)末端にエチレン性不飽和基を有する光重合性不飽和化合物及び(c)活性光の照射により遊離ラジカルを生成する光開始剤を含む感光性樹脂組成物層である請求項3記載の積層方法。 Wherein the thermoplastic resin layer A, (a) a film-imparting polymer, a free radical by irradiation of the photopolymerizable unsaturated compound and (c) active light having an ethylenically unsaturated group (b) end the method of laminating according to claim 3, wherein the photosensitive resin composition layer containing the product photoinitiators.
  5. 【請求項5】 熱可塑性樹脂層Aが、(a)成分、 5. The thermoplastic resin layer A, (a) component,
    (b)成分及び(c)成分を含みさらに、(d)蛍光体を含む感光性樹脂組成物層である請求項4記載の積層方法。 Component (b) and (c) further comprise components, (d) a method of laminating according to claim 4, wherein the photosensitive resin composition layer containing a phosphor.
  6. 【請求項6】 熱可塑性樹脂層Bが、(e)熱可塑性樹脂を含む請求項3、4又は5記載の積層方法。 6. The thermoplastic resin layer B is, (e) The method of laminating according to claim 3, 4 or 5, further comprising a thermoplastic resin.
  7. 【請求項7】 熱可塑性樹脂層Aを有するフィルムが、 7. A film having a thermoplastic resin layer A,
    支持体フィルム、熱可塑性樹脂層A及びカバーフィルムを有するものであり、熱可塑性樹脂層Bを有するフィルムが、支持体フィルム、熱可塑性樹脂層B及びカバーフィルムを有するものである請求項3、4、5又は6記載の積層方法。 Support film, those having a thermoplastic resin layer A and the cover film, a film having a thermoplastic resin layer B is, the support film, according to claim one having a thermoplastic resin layer B and the cover film 3,4 , 5 or 6 method of a multilayer according.
  8. 【請求項8】 フィルムAを供給する第1の供給手段、 8. A first supply means for supplying a film A,
    フィルムBを供給する第2の供給手段及び基板上にフィルムAを、その上にフィルムBを積層する積層手段を備えてなる積層装置。 The film A to the second supply means and the substrate for supplying the film B, the laminated device including a laminating means for laminating the film B thereon.
  9. 【請求項9】 支持体フィルム(5A)、熱可塑性樹脂層A(3)及びカバーフィルム(6A)を有するフィルムA並びに支持体フィルム(5B)、熱可塑性樹脂層B 9. A support film (5A), the film A and the support film having the thermoplastic resin layer A (3) and a cover film (6A) (5B), the thermoplastic resin layer B
    (4)及びカバーフィルム(6B)を有するフィルムB (4) and the film B having a cover film (6B)
    を用いて、基板(7)上に熱可塑性樹脂層A(3)、その上に熱可塑性樹脂層B(4)を積層する装置であって、フィルムAを供給する第1の供給手段、フィルムB With the substrate (7) the thermoplastic resin layer A (3) on a device for laminating a thermoplastic resin layer B (4) thereon, the first supply means for supplying a film A, film B
    を供給する第2の供給手段、カバーフィルム((6A)及び(6B))を取るため手段、支持体フィルム(5A)を取るための手段及び熱可塑性樹脂層A(3)と熱可塑性樹脂層B(4)を積層するための積層手段を備えた積層装置。 Second supply means for supplying the cover film ((6A) and (6B)) means for taking the means and the thermoplastic resin layer A (3) for taking the support film (5A) and the thermoplastic resin layer stacking apparatus having a laminating means for laminating the B (4).
  10. 【請求項10】 支持体フィルム(5A)、熱可塑性樹脂層A(3)及びカバーフィルム(6A)を有するフィルムA並びに支持体フィルム(5B)、熱可塑性樹脂層B(4)及びカバーフィルム(6B)を有するフィルムBを用いて、基板(7)上に熱可塑性樹脂層A(3)、 10. A support film (5A), the thermoplastic resin layer A (3) and the film A as well as the support film having a cover film (6A) (5B), the thermoplastic resin layer B (4) and the cover film ( 6B) using a film B having a substrate (7) the thermoplastic resin layer a (3 on),
    その上に熱可塑性樹脂層B(4)を積層する装置であって、基板(7)を送る搬送手段、フィルムAを供給する第1の供給手段、フィルムBを供給する第2の供給手段、カバーフィルム((6A)及び(6B))を取るための手段、熱可塑性樹脂層A(3)又は熱可塑性樹脂層B(4)を有するフィルムを送るための手段、支持体フィルム(5A)を送るための手段、支持体フィルム(5 An apparatus for laminating a thermoplastic resin layer B (4) thereon, transport means for feeding a substrate (7), the first supply means for supplying a film A, the second supply means for supplying a film B, It means for taking a cover film ((6A) and (6B)), means for sending a film having a thermoplastic resin layer a (3) or the thermoplastic resin layer B (4), the support film (5A) means for sending, the support film (5
    A)を取るための手段、熱可塑性樹脂層A(3)又は熱可塑性樹脂層B(4)を有するフィルムを基板(7)に積層する積層手段を設けた積層装置。 Means for taking the A), the thermoplastic resin layer A (3) or stacking apparatus the film was provided with a laminating means for laminating the substrate (7) having a thermoplastic resin layer B (4).
  11. 【請求項11】 基板(7)を送る搬送ロール(1 11. A transport roll Send substrate (7) (1
    1)、フィルムAを供給する第1の供給ロール(1)、 1), the first supply roll supplying a film A (1),
    カバーフィルム(6A)を巻取るカバーフィルム巻取ロール(8)、支持体フィルム(5A)及び熱可塑性樹脂層A(3)を有するフィルムを送る送りロール(1 The cover film take-up roll for taking up the cover film (6A) (8), the support film (5A) and feed roll to send a film having a thermoplastic resin layer A (3) (1
    2)、支持体フィルム(5A)及び熱可塑性樹脂層A 2), the support film (5A) and the thermoplastic resin layer A
    (3)を有するフィルムを基板(7)上に積層する積層ロール(10)、支持体フィルム(5A)を送る送りロール(12)、支持体フィルム(5A)を巻取る支持体フィルム巻取ロール(9)、フィルムBを供給する第2 (3) laminating roll films having a laminated onto a substrate (7) (10), feed rolls sending support film (5A) (12), wound support film (5A) support film takeup roll (9), second supplying film B
    の供給ロール(2)、カバーフィルム(6B)を巻取るカバーフィルム巻取ロール(8)、支持体フィルム(5 Of the supply roll (2), the cover film take-up roll (8) for winding the cover film (6B), the support film (5
    B)及び熱可塑性樹脂層B(4)を有するフィルムを送る送りロール(12)、基板(7)上に積層された熱可塑性樹脂層A(3)の上に、支持体フィルム(5B)及び熱可塑性樹脂層B(4)を有するフィルムを積層する積層ロール(10)を設けた請求項8、9又は10記載の積層装置。 B) and the feed roll to send a film having a thermoplastic resin layer B (4) (12), on a substrate (7) laminated on the thermoplastic resin layer A (3), the support film (5B) and the thermoplastic resin layer B (4) laminating apparatus according to claim 8, 9 or 10, wherein is provided a laminating roll for laminating (10) a film having a.
  12. 【請求項12】 基板(7)を送る搬送ロール(1 12. A transport roll Send substrate (7) (1
    1)、フィルムAを供給する第1の供給ロール(1)、 1), the first supply roll supplying a film A (1),
    フィルムAを送る送りロール(12)、カバーフィルム(6A)を巻取るカバーフィルム巻取ロール(8)、支持体フィルム(5A)及び熱可塑性樹脂層A(3)を有するフィルムを送る送りロール(12)、フィルムBを供給する第2の供給ロール(2)、フィルムBを送る送りロール(12)、カバーフィルム(6B)を巻取るカバーフィルム巻取ロール(8)、支持体フィルム(5 Feed Send film A roll (12), cover film take-up roll (8) for winding the cover film (6A), the support film (5A) and feed roll to send a film having a thermoplastic resin layer A (3) ( 12), the film B second supply roll for supplying (2), feed rolls (12 to send the film B), a cover film take-up roll (8 winding the cover film (6B)), the support film (5
    B)及び熱可塑性樹脂層B(4)を有するフィルムを送る送りロール(12)、支持体フィルム(5A)及び熱可塑性樹脂層A(3)を有するフィルムと支持体フィルム(5B)及び熱可塑性樹脂層B(4)を有するフィルムを貼り合わせる合わせロール(13)、支持体フィルム(5A)を送る送りロール(12)、支持体フィルム(5A)を巻取る支持体フィルム巻取ロール(9)、熱可塑性樹脂層A(3)、熱可塑性樹脂層B(4)及び支持体フィルム(5B)を有するフィルムを送る送りロール(12)、熱可塑性樹脂層A(3)、熱可塑性樹脂層B(4)及び支持体フィルム(5B)を有するフィルムを基板(7)上に積層する積層ロール(10)を設けた請求項8、9又は10記載の積層装置。 B) and the feed roll to send a film having a thermoplastic resin layer B (4) (12), the support film (5A) and the thermoplastic resin layer A (3) film and the support film (5B having a) and thermoplastic combined bonding a film having a resin layer B (4) roll (13), feed rolls sending support film (5A) (12), the support film (5A) of the winding takes support film winding roll (9) , the thermoplastic resin layer a (3), feed rolls (12) to send the film having the thermoplastic resin layer B (4) and the support film (5B), the thermoplastic resin layer a (3), the thermoplastic resin layer B (4) and the support film (5B) laminating apparatus according to claim 8, 9 or 10, wherein the film provided with the substrate (7) laminating roll to be stacked (10) having a.
  13. 【請求項13】 (I)凹凸を有する基板の凹凸表面上に、請求項1記載の積層方法により蛍光体を含有する感光性樹脂組成物層である熱可塑性樹脂層Aを有するフィルムA及び熱可塑性樹脂層Bを有するフィルムBを積層して熱可塑性樹脂層A及び熱可塑性樹脂層Bを形成する工程、(II)活性光線を像的に照射する工程、(III) To 13. (I) on the uneven surface of the substrate having unevenness, the film A and the thermal having a thermoplastic resin layer A is a photosensitive resin composition layer containing a phosphor by the method of laminating according to claim 1, wherein forming a thermoplastic resin layer a and the thermoplastic resin layer B are laminated film B having a thermoplastic resin layer B, the step of irradiating (II) active light rays imagewise, (III)
    現像により不要部を除去する工程及び(IV)焼成により不要分を除去する工程を含む蛍光体パターンの製造法。 Preparation of a phosphor pattern including the step of removing the unnecessary components by the process and (IV) calcining to remove unnecessary portion by development.
  14. 【請求項14】 請求項13記載の蛍光体パターンの製造法により製造された蛍光体パターン。 14. phosphor pattern produced by the production method of the phosphor pattern according to claim 13, wherein.
  15. 【請求項15】 プラズマディスプレイパネル用基板上に請求項14記載の蛍光体パターンを備えてなるプラズマディスプレイパネル用背面板。 15. become comprises a phosphor pattern according to claim 14, wherein the plasma display panel on the substrate for a plasma display panel back plate.
JP13945597A 1996-05-30 1997-05-29 Lamination method, lamination apparatus, method for producing the phosphor pattern, a phosphor pattern and a back panel for a plasma display panel Expired - Fee Related JP3925749B2 (en)