JPH10225532A - Golf ball - Google Patents
Golf ballInfo
- Publication number
- JPH10225532A JPH10225532A JP9029373A JP2937397A JPH10225532A JP H10225532 A JPH10225532 A JP H10225532A JP 9029373 A JP9029373 A JP 9029373A JP 2937397 A JP2937397 A JP 2937397A JP H10225532 A JPH10225532 A JP H10225532A
- Authority
- JP
- Japan
- Prior art keywords
- golf ball
- cover
- borate whisker
- ionomer resin
- aluminum borate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、アイオノマー樹脂
を主材とする樹脂材料にホウ酸アルミニウムウィスカー
を配合したカバーを有するゴルフボールに関する。The present invention relates to a golf ball having a cover in which an aluminum borate whisker is blended with a resin material mainly composed of an ionomer resin.
【0002】[0002]
【従来の技術】ゴルフボールのカバー材料として、良好
な反発性、耐衝撃性、耐摩耗性等を付与することのでき
るアイオノマー樹脂が広く使用されている。特に、ソリ
ッドゴルフボールでは、アイオノマー樹脂カバーが大部
分となっている。2. Description of the Related Art As a cover material for a golf ball, an ionomer resin capable of imparting good resilience, impact resistance, abrasion resistance and the like is widely used. In particular, ionomer resin covers are the majority of solid golf balls.
【0003】このアイオノマー樹脂カバーを有するソリ
ッドゴルフボールにおいて、近年、ソフト化することで
硬い打球感を改善しようとしたものが開発されている。
例えば、コアを非常に軟らかくしたものがある。しかし
ながら、このソリッドゴルフボールは、打球時の変形が
大きいため、耐久性に問題がある。従って、カバーの耐
久性をさらに向上させることが要望されている。[0003] In recent years, a solid golf ball having an ionomer resin cover has been developed to improve a hard hit feeling by softening the golf ball.
For example, some cores are very soft. However, since the solid golf ball is greatly deformed when hit, there is a problem in durability. Therefore, there is a demand for further improving the durability of the cover.
【0004】例えば、特公平4−39866号公報に
は、高強度、高反発性を有するゴルフボール用被覆組成
物を得るために、アイオノマー樹脂等に繊維状チタン酸
アルカリ金属を配合するようにした技術が開示されてい
る。しかしながら、繊維状チタン酸アルカリ金属は、化
学的に不安定であるため、カバーの性能を長期的に維持
することができないという問題を有している。[0004] For example, Japanese Patent Publication No. 4-39866 discloses that a fibrous alkali metal titanate is mixed with an ionomer resin or the like in order to obtain a golf ball coating composition having high strength and high resilience. Techniques are disclosed. However, the fibrous alkali metal titanate has a problem that the performance of the cover cannot be maintained for a long time because it is chemically unstable.
【0005】[0005]
【発明が解決しようとする課題】そこで、本発明は、反
発性、打球感を低下させることなく、優れた耐久性を得
ることができるゴルフボールを提供することを目的とす
る。SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to provide a golf ball capable of obtaining excellent durability without deteriorating resilience and shot feeling.
【0006】[0006]
【課題を解決するための手段】本発明におけるアイオノ
マー樹脂は、エチレン・不飽和カルボン酸共重合体、例
えば、エチレン・(メタ)アクリル酸共重合体を金属イ
オンで中和して得られる樹脂もしくはその2種以上の混
合物であり、これらにエチレン・不飽和カルボン酸・不
飽和カルボン酸エステル三元共重合体、例えば、エチレ
ン・(メタ)アクリル酸・(メタ)アクリル酸エステル
三元共重合体を金属イオンで中和して得られるソフトア
イオノマー樹脂を混合することもできる。The ionomer resin according to the present invention is a resin obtained by neutralizing an ethylene / unsaturated carboxylic acid copolymer, for example, an ethylene / (meth) acrylic acid copolymer with metal ions. A mixture of two or more thereof, and a terpolymer of ethylene / unsaturated carboxylic acid / unsaturated carboxylic acid ester, for example, a terpolymer of ethylene / (meth) acrylic acid / (meth) acrylate ester Can be mixed with a soft ionomer resin obtained by neutralizing with a metal ion.
【0007】エチレン・不飽和カルボン酸共重合体およ
びエチレン・不飽和カルボン酸・不飽和カルボン酸エス
テル三元共重合体を中和する金属イオンとしては、リチ
ウム、ナトリウム、カリウム、マグネシウム、カルシウ
ム、亜鉛、アルミニウム等のイオンを例示することがで
きる。また、エチレン・不飽和カルボン酸・不飽和カル
ボン酸エステル三元共重合体における不飽和カルボン酸
エステルとしては、メチル、エチル、n−ブチル、イソ
ブチル等のエステルを例示することができる。The metal ions for neutralizing the ethylene / unsaturated carboxylic acid copolymer and the ethylene / unsaturated carboxylic acid / unsaturated carboxylic acid ester terpolymer include lithium, sodium, potassium, magnesium, calcium, and zinc. , Aluminum and the like. Examples of the unsaturated carboxylic acid ester in the ethylene / unsaturated carboxylic acid / unsaturated carboxylic acid ester terpolymer include esters such as methyl, ethyl, n-butyl and isobutyl.
【0008】このようなアイオノマー樹脂は、1種のも
のを用いる場合よりも、反発性が相乗的に増大すること
を考慮すると、中和する金属イオンが異なる2種以上の
アイオノマー樹脂の混合物、特に、リチウム、ナトリウ
ム、カリウム等の1価金属イオンで中和された少なくと
も1種のアイオノマー樹脂と、マグネシウム、カルシウ
ム、亜鉛等の2価金属イオンで中和された少なくとも1
種のアイオノマー樹脂との混合物を使用するのが好まし
く、リチウム/マグネシウム、リチウム/亜鉛、ナトリ
ウム/マグネシウム、ナトリウム/亜鉛、カリウム/マ
グネシウム、カリウム/亜鉛、リチウム/ナトリウム/
亜鉛等の金属イオンの組み合わせを例示することができ
る。In view of the fact that such an ionomer resin has a synergistic increase in resilience as compared with the case of using only one kind, a mixture of two or more kinds of ionomer resins having different metal ions to be neutralized, in particular, At least one ionomer resin neutralized with a monovalent metal ion such as lithium, sodium, and potassium; and at least one ionomer resin neutralized with a divalent metal ion such as magnesium, calcium, and zinc
It is preferred to use mixtures with different ionomer resins, lithium / magnesium, lithium / zinc, sodium / magnesium, sodium / zinc, potassium / magnesium, potassium / zinc, lithium / sodium /
A combination of metal ions such as zinc can be exemplified.
【0009】アイオノマー樹脂としては、米国デュポン
社製の「サーリン(SURLYN)」(商品名)、三井
デュポンポリケミカル株式会社製の「ハイミラン(HI
MILAN)」(商品名)、エクソン社製の「イオテッ
ク(IOTEK)」(商品名)が市販されており、「サ
ーリン」および「ハイミラン」は、エチレン・メタクリ
ル酸共重合体ベースのアイオノマー樹脂であり、「イオ
テック」は、エチレン・アクリル酸共重合体ベースのア
イオノマー樹脂である。Examples of the ionomer resin include "SURLYN" (trade name) manufactured by DuPont in the United States and "HIMILAN (HI)" manufactured by DuPont-Mitsui Polychemicals.
"MILAN)" (trade name) and "IOTEK" (trade name) manufactured by Exxon are marketed, and "Surlyn" and "Himilan" are ionomer resins based on ethylene-methacrylic acid copolymer. "Iotek" is an ionomer resin based on an ethylene-acrylic acid copolymer.
【0010】ホウ酸アルミニウムウィスカーは、一般的
に化学式nAl2 O3 ・mB2 O3で表され、9Al2
O3 ・2B2 O3 、2Al2 O3 ・B2 O3 等の化合物
を例示することができ、0.05〜5μmの繊維径、2
〜50μmの繊維長および10〜100のアスペクト比
であるものが好ましい。このようなホウ酸アルミニウム
ウィスカーについては、その製造方法と併せて特公平4
−21640号公報、特公平4−22880号公報等に
詳しく記載されている。[0010] aluminum borate whiskers is generally expressed by the chemical formula nAl 2 O 3 · mB 2 O 3, 9Al 2
Compounds such as O 3 · 2B 2 O 3 and 2Al 2 O 3 · B 2 O 3 can be exemplified, and have a fiber diameter of 0.05 to 5 μm.
Those having a fiber length of 5050 μm and an aspect ratio of 10-100 are preferred. Such aluminum borate whiskers are described in Japanese Patent Publication No.
These are described in detail in JP-A-21640, JP-B-4-22880 and the like.
【0011】本発明において、ホウ酸アルミニウムウィ
スカーは、アイオノマー樹脂との強い結合性を得るため
に、カップリング剤で表面処理したものを使用すること
ができ、カップリング剤としては、シリコン系、チタン
系、アルミニウム系、ジルコニウム系等のカップリング
剤を例示することができる。ホウ酸アルミニウムウィス
カーの未処理品および処理品としては、四国化成工業株
式会社製の「アルボレックス」(商品名)が市販されて
いる。In the present invention, aluminum borate whiskers can be used which have been surface-treated with a coupling agent in order to obtain a strong bond with an ionomer resin. Examples thereof include coupling agents such as a series, an aluminum series, and a zirconium series. As untreated and treated aluminum borate whiskers, “Albolex” (trade name) manufactured by Shikoku Chemicals Co., Ltd. is commercially available.
【0012】ホウ酸アルミニウムウィスカーは、特公平
4−39866号公報で好適な材料とされているチタン
酸カリウムウィスカーよりも強度、弾性率が高い。この
ことにより、ホウ酸アルミニウムウィスカーを配合した
アイオノマー樹脂組成物から形成するカバーについて、
反発性を損なうことなく耐久性を向上させることができ
る。さらに、ホウ酸アルミニウムウィスカーは、化学的
にほぼ中性であることから、カバー性能を長期的に安定
させることができる。Aluminum borate whiskers have higher strength and elastic modulus than potassium titanate whiskers, which are preferred materials in Japanese Patent Publication No. 4-39866. Thereby, for the cover formed from the ionomer resin composition containing the aluminum borate whisker,
The durability can be improved without impairing the resilience. Furthermore, since aluminum borate whiskers are chemically almost neutral, the cover performance can be stabilized for a long time.
【0013】本発明において、カバーを構成する樹脂組
成物中におけるホウ酸アルミニウムウィスカーの配合割
合は、3〜35重量%の範囲であることが好ましい。ホ
ウ酸アルミニウムウィスカーの配合割合が3重量%より
少ないと、耐久性を向上させる効果が得られ難くなる。
一方、35重量%より多いと、反発性が低下し、また、
ホウ酸アルミニウムウィスカーの分散が悪くなるおそれ
があるので好ましくない。In the present invention, the mixing ratio of aluminum borate whiskers in the resin composition constituting the cover is preferably in the range of 3 to 35% by weight. If the mixing ratio of the aluminum borate whisker is less than 3% by weight, it is difficult to obtain the effect of improving the durability.
On the other hand, if it is more than 35% by weight, the resilience decreases, and
It is not preferable because the dispersion of the aluminum borate whisker may be deteriorated.
【0014】カバー用樹脂組成物は、公知の方法、例え
ば熱可塑性樹脂用のバンバリーミキサー、スクリュー押
出機等を使用してブレンドすることにより得られ、カバ
ー用樹脂組成物には、通常用いられる添加剤、例えば、
顔料、蛍光増白剤、酸化防止剤、紫外線吸収剤、紫外線
安定剤、分散剤等を配合してもよい。また、アイオノマ
ー樹脂以外に他の樹脂を混合することもできる。The cover resin composition can be obtained by blending using a known method, for example, using a Banbury mixer or a screw extruder for a thermoplastic resin. Agent, for example,
A pigment, a fluorescent whitening agent, an antioxidant, an ultraviolet absorber, an ultraviolet stabilizer, a dispersant, and the like may be added. Further, other resins besides the ionomer resin can be mixed.
【0015】本発明のゴルフボールは、公知の方法によ
りブレンドされるカバー用樹脂組成物を用いてコアを被
覆してカバーを形成して製造される。ゴルフボールのコ
アは、ソリッドコアおよび糸巻きコアのいずれでもよ
く、カバーの成形方法としては、公知の射出成形法等を
使用することができる。The golf ball of the present invention is manufactured by coating a core with a cover resin composition blended by a known method to form a cover. The core of the golf ball may be either a solid core or a wound core, and a known injection molding method or the like can be used as a molding method of the cover.
【0016】[0016]
【実施例および比較例】表1の配合によるカバー用樹脂
組成物を用いて、直径38.3mmの単層構造のソリッ
ドコアを被覆してカバーを射出成形により形成し、研
磨、塗装を施して直径42.7mmのツーピースソリッ
ドゴルフボールを作製した。ゴルフボールの重量は、規
格内の45.9g以下であった。EXAMPLES AND COMPARATIVE EXAMPLES Using a resin composition for a cover having the composition shown in Table 1, a solid core having a single-layered structure having a diameter of 38.3 mm was coated, and a cover was formed by injection molding, followed by polishing and painting. A two-piece solid golf ball having a diameter of 42.7 mm was produced. The weight of the golf ball was 45.9 g or less within the standard.
【0017】作製したゴルフボールにつき、耐衝撃性、
耐摩耗性、反発性を測定、評価して表1に示した。The resulting golf ball has impact resistance,
The abrasion resistance and resilience were measured and evaluated and are shown in Table 1.
【0018】この場合、比較例1に対して、ホウ酸アル
ミニウムウィスカーを配合した各実施例1〜6におい
て、高い耐衝撃性を得ることができた。また、ゴルフボ
ールの反発性は、比較例1と実施例1〜6とでは殆ど差
異がなく、従って、ホウ酸アルミニウムウィスカーを配
合することによるゴルフボール自体のソフト感の低下は
生じていない。この結果、打球感が低下することはな
い。In this case, high impact resistance was obtained in each of Examples 1 to 6 in which aluminum borate whiskers were added to Comparative Example 1. In addition, the resilience of the golf ball is almost the same between Comparative Example 1 and Examples 1 to 6, and therefore, the softness of the golf ball itself does not decrease due to the addition of the aluminum borate whisker. As a result, the shot feeling does not decrease.
【0019】[0019]
【表1】 [Table 1]
【0020】*1(ハイミラン1605):商品名、三
井デュポンポリケミカル株式会社製のエチレン・メタリ
クル酸共重合体のナトリウムイオン中和のアイオノマー
樹脂。* 1 (Himilan 1605): trade name, ionomer resin of sodium ion neutralization of ethylene / methacrylic acid copolymer manufactured by Du Pont-Mitsui Polychemicals, Inc.
【0021】*2(ハイミラン1706):商品名、三
井デュポンポリケミカル株式会社のエチレン・メタリク
ル酸共重合体の亜鉛イオン中和のアイオノマー樹脂。* 2 (Himilan 1706): trade name, Mitsui DuPont Polychemical Co., Ltd. ethylene / metallic acid copolymer zinc ion neutralized ionomer resin.
【0022】*3(アルボレックスY):商品名、四国
化成工業株式会社製のホウ酸アルミニウムウィスカー
(未処理品)。* 3 (Albolex Y): trade name, aluminum borate whisker manufactured by Shikoku Chemicals Corporation (untreated product).
【0023】*4(アルボレックスYS4):商品名、
四国化成工業株式会社製のホウ酸アルミニウムウィスカ
ー(シリコン系カップリング剤処理品)。* 4 (Arbolex YS4): trade name
Aluminum borate whisker manufactured by Shikoku Chemical Industry Co., Ltd. (silicon-based coupling agent treated product).
【0024】*5(耐衝撃性):スイングロボット装置
を使用して、ウッド1番クラブにより繰り返し打ったと
きの割れ発生までの打球回数で、比較例1を100とす
る指数。* 5 (impact resistance): The number of hits until cracking occurs when repeatedly hit with the No. 1 wood club using a swing robot device.
【0025】*6(耐摩耗性):スイングロボット装置
を使用して、ピッチングウェッジクラブにより打ったと
きの傷つき程度。各ゴルフボール5個ずつについて行
い、◎→ほとんど傷がつかない、○→わずかに傷がつく
が、気にならない、とした。* 6 (wear resistance): Degree of damage when hit with a pitching wedge club using a swing robot device. The evaluation was performed for each of five golf balls, and →→ slightly scarred, ○ → slightly scratched, but not bothersome.
【0026】*7(反発性):スイングロボット装置を
使用して、ウッド1番クラブによりヘッドスピード40
m/secで打ったときのゴルフボールの初速度で、比
較例1を100とする指数。* 7 (Resilience): Using a swing robot device, the head speed was set to 40 using a Wood No. 1 club.
Index of the initial velocity of the golf ball when hit at m / sec.
【0027】[0027]
【発明の効果】本発明によれば、アイオノマー樹脂にホ
ウ酸アルミニウムウィスカーを配合してカバーを形成す
ることにより、反発性、打球感を低下させることなく、
耐久性に優れたゴルフボールを提供することができる。According to the present invention, by forming an aluminum borate whisker into an ionomer resin to form a cover, the resilience and shot feeling can be reduced.
A golf ball excellent in durability can be provided.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 FI C08L 33/02 C08L 33/02 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 6 Identification code FI C08L 33/02 C08L 33/02
Claims (4)
において、 カバーがアイオノマー樹脂を主材とする樹脂材料にホウ
酸アルミニウムウィスカーを配合した樹脂組成物から形
成されることを特徴とするゴルフボール。1. A golf ball having a core covered with a cover, wherein the cover is formed from a resin composition in which an aluminum borate whisker is blended with a resin material mainly composed of an ionomer resin. .
ーの配合割合が3〜35重量%の範囲であることを特徴
とするゴルフボール。2. The golf ball according to claim 1, wherein the mixing ratio of the aluminum borate whisker in the resin composition is in a range of 3 to 35% by weight.
5〜5μm、繊維長が2〜50μm、アスペクト比が1
0〜100であることを特徴とするゴルフボール。3. The golf ball according to claim 1, wherein the aluminum borate whisker has a fiber diameter of 0.0.
5-5 μm, fiber length 2-50 μm, aspect ratio 1
A golf ball characterized by being 0 to 100.
により表面処理されていることを特徴とするゴルフボー
ル。4. The golf ball according to claim 1, wherein the aluminum borate whiskers are surface-treated with a coupling agent.