JPH0957113A - Photocatalyst, incadescent electric bulb, discharge lamp and luminaire - Google Patents

Photocatalyst, incadescent electric bulb, discharge lamp and luminaire

Info

Publication number
JPH0957113A
JPH0957113A JP33543295A JP33543295A JPH0957113A JP H0957113 A JPH0957113 A JP H0957113A JP 33543295 A JP33543295 A JP 33543295A JP 33543295 A JP33543295 A JP 33543295A JP H0957113 A JPH0957113 A JP H0957113A
Authority
JP
Grant status
Application
Patent type
Prior art keywords
photocatalytic
action
particles
surface
based
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP33543295A
Other languages
Japanese (ja)
Inventor
Hisashi Honda
Hiroshi Kamata
久司 本田
博士 鎌田
Original Assignee
Toshiba Lighting & Technol Corp
東芝ライテック株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

PROBLEM TO BE SOLVED: To obtain a photocatalyst element good in photocatalytic action and also high in membrane strength by specifying a wavelength of light and the thickness of a catalyst membrane when a photocatalytic membrane wherein fine particles of TiO2 having photocatalytic action are dispersed in a phase based on metal oxide having photocatalytic action is formed on the film forming surface of a light permeable substrate. SOLUTION: A substrate 1 pervious to light with a wavelength of 410nm or less and a photocatalytic membrane 2 with a thickness of 0.01-0.3μm formed from fine particles 2a based on at least one of crystalline TiO2 and ZnO having photocatalytic action and ultrafine particles 2b based on metal oxide having an average particle size smaller than that of the fine particles 2a and having photocatalytic action are provided on the film forming surface integrally provided on the outer peripheral surface of a discharge lamp. If necessary, a layer based on SiO2 is interposed between the film forming surface of the substrate 1 and the photocatalyst layer 2. This photocatalyst element shows excellent purifying function to environmental pollution caused by tar of tobacco and is effective for eliminating a malodor of a toilet.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は光触媒作用をを備えた光触媒体,白熱電球,放電ランプ,蛍光ランプおよび照明器具に関する。 The present invention is a photocatalyst having a photocatalytic activity BACKGROUND OF THE INVENTION, an incandescent lamp, a discharge lamp, to a fluorescent lamp and lighting equipment.

【0002】 [0002]

【従来の技術】放電によって紫外線を放射する水銀などを封有する放電ランプの外周面(外表面)に、光触媒作用を有する物質(たとえば TiO 2 …酸化チタン)から成る光触媒膜を一体的に設けた放電ランプが知られている(特開平1-169866号公報)。 The outer peripheral surface of the Related Art discharge lamp having sealing and mercury emits ultraviolet by discharge (outer surface), the photocatalytic film made of material (e.g., TiO 2 ... titanium oxide) having a photocatalytic action provided integrally discharge lamps are known (JP-A-1-169866). この種の放電ランプは、バルブの外周面に設けた光触媒膜が放電ランプ内部から放出される紫外線を受けると表面が活性化し、酸化力を有するようになり、付着もしくは接触した有機物を酸化・ This type of discharge lamp, the surface is activated when receiving the ultraviolet photocatalytic film provided on the outer peripheral surface of the valve is released from the internal discharge lamp, it takes on the oxidizing power, and oxidation adhesion or contact organics
分解して、脱臭や防汚などの作用を呈する。 Decomposition to exhibit the effects such as deodorizing and anti-fouling. つまり、前記放電ランプを設置した雰囲気では、その周囲の脱臭もしくは消臭、雰囲気中の有機成分の分解などが行われる。 That is, in the atmosphere established the discharge lamp, deodorant or deodorizing the surrounding, such as decomposition of the organic component in the atmosphere is performed.

【0003】ところで、光触媒反応を示す照射光の波長は、光触媒膜を形成する物質のエネルギーバンドギャップに依存する。 Meanwhile, the wavelength of the irradiated light showing the photocatalytic reaction depends on the energy band gap of the material forming the photocatalyst film. たとえば TiO 2のエネルギーバンドギャップは 3eVであり、 400nmの光エネルギーに相当する。 For example the energy band gap of TiO 2 is 3 eV, corresponding to the light energy of 400 nm.
したがって、この値よりも大きなエネルギーを持つ短波長の光は、 TiO 2に吸収されて光触媒作用を示す。 Thus, short-wavelength light having energy greater than this value shows a photocatalysis is absorbed by the TiO 2. そして、光触媒膜を形成する物質によっては、このエネルギーバンドギャップの値が小さくなったりする。 Then, the material forming the photocatalyst film, the value of the energy band gap may become smaller. また、不純物によってもエネルギーバンドギャップの値は変動するので、光触媒作用は紫外線照射に限定されない。 Further, since the value of the energy band gap by impurities varies, photocatalysis is not limited to UV irradiation.

【0004】上記光触媒膜は、光触媒作用を有する金属酸化物の微粒子から成る粉体を水もしくはエタノールなどの適当なバインダー成分に分散させて、バルブの外周面に塗布後、焼成して形成している。 [0004] The above photocatalyst film, a powder consisting of fine particles of a metal oxide having a photocatalytic action is dispersed in a suitable binder components, such as water or ethanol, after application to the outer surface of the bulb, and formed by firing there. また、光触媒作用を有する金属酸化物の微粒子を、アルコキシド法で塗布後、高温焼成して光触媒膜を形成することも知られている。 Further, fine particles of metal oxide having a photocatalytic action, after coating with the alkoxide method, it is also known to form a photocatalytic film by high temperature firing.

【0005】一方、白熱電球においては、その外周面に On the other hand, in the incandescent lamp, on the outer peripheral surface
TiO 2 )およびFe 2 O 3の混合体から成る高屈折率層と And the high refractive index layer made of a mixture of TiO 2) and Fe 2 O 3
SiO 2 (シリカ)を主体とした低屈折率層を重ねて成る紫外線カットフィルター膜を設けた構成も知られている。 Structure in which a UV-cut filter film formed by overlapping SiO 2 low refractive index layer composed mainly of (silica) are also known. すなわち、白熱電球の外周面に紫外線カットフィルター膜を設けることにより、紫外線の悪影響を除去することも知られている(特開昭61−253763号公報)。 That is, by providing the ultraviolet cut filter membrane to the outer peripheral surface of the incandescent lamp, it is also known to remove the adverse effects of ultraviolet (JP 61-253763 JP).

【0006】さらに、事務機用光源として使用されるハロゲン電球においても、前記 SiO 2を主体として成る低屈折率層およびチタニウを主体として成る高屈折率層を交互に多層化した光干渉膜を、石英ガラスバルブ内壁面や外周面に設けた構成が知られている。 Furthermore, even in the halogen bulb to be used as office machines light source, an optical interference film multilayered alternately high refractive index layer formed of a low refractive index layer and Chitaniu made the SiO 2 as a main component mainly, structure in which the quartz glass bulb inner wall and the outer peripheral surface are known. つまり、発光用フィラメントから放射された光のうち、可視光は光干渉膜を透過して石英ガラスバルブ外に放射させ、赤外線は光干渉膜での反射によって発光用フィラメントに帰還させ、発光用フィラメントを加熱する構成としている。 That is, of the light emitted from the light emitting filament, the visible light is transmitted through the optical interference film is emitted to the outside of the quartz glass bulb, infrared is fed back to the light emitting filament by reflection by the light interference film, light-emitting filament It has a configuration for heating the. そして、このような構成を採ることによって、赤外線の外部放射が低減され、その赤外線による熱が発光用フィラメントの熱保持に利用されるので、ランプ効率の向上を図ることも知られている(特開昭61−225756号公報)。 Then, by adopting such a configuration, the reduced infrared external radiation, the heat due to the infrared rays is used for heat retention of the light emitting filament, it is also known to improve the lamp efficiency (Japanese HirakiAkira 61-225756 JP).

【0007】 [0007]

【発明が解決しようとする課題】上記説明したように、 The object of the invention is to be Solved As described above,
光触媒作用(光触媒機能)を備えた放電ランプは知られ、また、その応用もいろいろ試みられているが、なお、次のようなな問題があった。 Photocatalysis discharge lamp having a (photocatalytic function) is known, also, although its application has been variously attempted also noted, there are the following problems. 第1には、光触媒作用を有する金属酸化物から成る光触媒膜の膜厚は、数〜 The first, the film thickness of the photocatalyst film made of a metal oxide having a photocatalytic action, several to
数十μm 程度で実用化が検討されており、数μm 以下においては十分な光触媒作用は生じないと考えられており、検討されていなかった。 Are commercialized discussed several tens μm or so, it is believed that no sufficient photocatalytic activity in several μm or less, has not been studied. すなわち、膜厚数μm 以下の場合は、脱臭もしくは消臭、雰囲気中の有機成分の分解などの光触媒作反応が十分に行われないと考えられていた。 That is, in the case of less thickness number [mu] m, deodorant or deodorizing, photocatalytic sensitization reaction such as decomposition of the organic components in the atmosphere has been considered not to take sufficiently.

【0008】第2には、光触媒作用を有する金属酸化物の微粒子を、水やエタノールなどのバインダー成分に分散させ、これを塗布焼き付けて形成した光触媒膜は、一般的に膜の強度が劣り剥離し易いので、耐久性に問題がある。 [0008] The second, fine particles of metal oxide having a photocatalytic action, is dispersed in a binder component, such as water, ethanol, a photocatalyst film formed by baking the paste is applied to is generally inferior in strength of film separation so easy, there is a problem in durability. そこで、光触媒膜の強度を向上させるために、 S Therefore, in order to improve the strength of the photocatalyst film, S
iO 2粉末をエタノールなどに分散させたものを併用することが試みられている。 It is used in combination as the iO 2 powder was dispersed like ethanol has been tried. しかし、このような手段を採った場合は、結果的に光触媒作用を有する金属酸化物が外表面に露出する割合が低減するので、光触媒作用の低下を招来することになる。 However, if adopted such a means, the proportion of metal oxide having a resultant photocatalytic action is exposed to the outer surface so reduced, will lead to decrease in the photocatalytic activity. しかも、金属酸化物の微粒子に対する SiO 2の馴染み性も劣るため、成膜(膜の形成) Moreover, since inferior conformability of SiO 2 to fine particles of a metal oxide, film formation (film formation)
に支障が生じ易く、かつ成膜後において膜の劣化を招来し易いという問題がある。 There are likely to occur trouble, and of easily lead to deterioration of the film after the film formation problem.

【0009】一方、アルコキシド法で形成した光触媒膜の場合は、膜自体の強度は比較的強固であるが、表面が平坦面化して表面積が低減するので、光触媒作用が低下するという問題がある。 On the other hand, in the case of photocatalytic film formed by the alkoxide method, the strength of the film itself is relatively rigid, the surface is reduced surface area flat grained, photocatalysis is lowered. さらに、たとえばソーダライムガラス面などに光触媒膜を形成した場合、ソーダライムガラス中のNa成分が光触媒膜中に析出し、汚損を生じたり、光の透過率を低減化など招来する恐れも懸念される。 Furthermore, for example, when the photocatalyst film formed on soda-lime glass surface, Na component in the soda-lime glass is deposited in the photocatalyst film may give rise to fouling, fear is feared that Shorai like reducing the transmittance of light that.

【0010】本発明は、上記問題を解決するものであって、光触媒作用が良好で、かつ膜強度も強固な光触媒体、白熱電球、放電ランプ、蛍光ランプおよび照明器具の提供を目的とする。 [0010] The present invention has been made to solve the above problems, the photocatalytic activity is good, and the film strength strong photocatalyst, an incandescent lamp, a discharge lamp, and an object thereof is to provide a fluorescent lamp and lighting equipment.

【0011】 [0011]

【課題を解決するための手段】請求項1の発明は、膜形成面を有し、少なくとも 410nm以下の波長の光が透過可能な基体と;前記膜形成面に設けられた光触媒作用を有する金属酸化物を主体とした相、およびこの相に分散された光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1種を主体とした微粒子で形成された膜厚0.01 [Means for Solving the Problems] of claim 1 invention has a film forming surface, light and permeable substrate of at least 410nm or less wavelength; metal having a photocatalytic action provided on the film forming surface phase consisting mainly of oxides, and the thickness of at least one of which is formed of a fine particle mainly composed of crystalline TiO 2, ZnO having a photocatalytic activity which is dispersed in this phase 0.01
〜 0.3μm の光触媒膜とを備えた光触媒体である。 A photocatalyst and a photocatalyst film of ~ 0.3 [mu] m.

【0012】請求項2の発明は、膜形成面を有し、少なくとも 410nm以下の波長の光が透過可能な基体と;前記膜形成面に設けられた光触媒作用を有する結晶性 Ti [0012] The invention according to claim 2, having a film forming surface, light and permeable substrate of at least 410nm wavelength below; crystalline Ti having a photocatalytic action provided on the film forming surface
O 2 , ZnOのうちの少なくとも1種を主体とした第1の微粒子、および平均粒径が前記第1の微粒子の平均粒径よりも小さい光触媒作用を有する金属酸化物を主体とした第2の超微粒子で形成された膜厚0.01〜 0.3μm の光触媒膜とを備えた光触媒体である。 O 2, the first fine particles containing mainly at least one of ZnO, and the average particle size of the second consisting mainly of metal oxide having a small light catalysis than the average particle diameter of the first particles a photocatalyst having a photocatalytic film having a thickness of 0.01 to 0.3 [mu] m formed by the ultrafine particles.

【0013】請求項3の発明は、請求項1もしくは請求項2記載の光触媒体において、基体と光触媒膜との間に [0013] A third aspect of the present invention, in the photocatalyst of claim 1 or claim 2, wherein, between the substrate and the photocatalyst film
SiO 2を主体とした層(下地層)を介挿させた光触媒体である。 A photocatalyst was interposed a layer in which the SiO 2 as a main component (base layer).

【0014】光触媒膜を支持する基体としては、少なくとも 410nm以下の波長の光を透過し、かつ支持機能を有すれば特に限定されないが、その使用態様によって、ガラスやセラミックスなどの非金属無機質系材料,アルミニウムなどの金属系無機質材料,有機質系材料を素材とした成形体が挙げられる。 [0014] As the substrate for supporting the photocatalyst film transmits light of at least 410nm or less wavelength and is not particularly limited if it has a supporting function, its use aspects, non-metallic inorganic based, such as glass or ceramic material , metallic inorganic material such as aluminum, molded body a material of the organic-based material. ここで、基体について、少なくとも 410nm以下の波長の光透過性を有することを必要とするのは、少なくとも 410nm以下の波長の紫外線を含む光を透過すれば、基体形状や光触媒膜の形成面拘らずに、所要の防臭,防汚,殺菌などの作用効果が得られるからである。 Here, the substrate, the need to have a light transmission of at least 410nm wavelength below, if transmit light containing the ultraviolet at least 410nm or less wavelength, forming surface of the substrate shape and the photocatalyst film regardless in, because the required deodorizing, antifouling, actions and effects such as disinfection is obtained.

【0015】また、光触媒膜の膜厚と吸着物質が分解される作用について、本発明者らが検討した結果、次のような傾向が確認された。 Further, the effect of film thickness and the adsorption material of the photocatalyst film is degraded, the present inventors have studied, trends such as the following was confirmed. すなわち、石英ガラス板の一主面に、厚さを変えて TiO 2系の光触媒膜を形成し、この光触媒膜面にそれぞれ一定濃度のタバコの煙を暴露し、 That is, on one main surface of the quartz glass plate, by changing the thickness to form a photocatalytic film of TiO 2 system, each exposing the smoke constant concentration of tobacco to the photocatalyst film surface,
ヤニを付着させ、波長約 550nm の透過率を測定して、 Depositing a tar, by measuring the transmittance at a wavelength of about 550 nm,
光触媒作用を評価したところ、膜厚0.01〜 0.3μm で良好な光触媒作用を呈することを確認した。 Evaluation of the photocatalytic action, it was confirmed that exhibits good light catalytic action at a film thickness of 0.01~ 0.3μm. ここで、膜厚が厚くなると紫外線によって励起・生成される光触媒膜の正孔は、膜形成面付近だけに限られ、ヤニなどの吸着面まで正孔が拡散されずに、膜内部での再結合率が増加して分解力が低下すると推定される。 The hole of the photocatalyst film to be excited and generated by the ultraviolet When the film thickness is increased is limited to the vicinity of the film formation surface, without being diffused holes to the suction surface, such as tar, re inside film resolving power coupling ratio is increased is estimated to decrease. 一方、膜厚0.01μ On the other hand, the film thickness 0.01μ
m 未満では、光触媒膜内の金属酸化物の結晶が均一に形成されず、十分な光触媒作用を呈する程活性化されないためと推定される。 Is less than m, not crystals uniformly formed of a metal oxide in the photocatalyst film, it is estimated that since the extent not activated exhibit sufficient photocatalytic activity.

【0016】さらに、 SiO 2を主体とした層(下地層) [0016] In addition, a layer composed mainly of SiO 2 (the base layer)
を、たとえばソーダライムガラス面との間に介挿させた場合は、前記光触媒膜の構成,性状(微粒子の分散した連続膜性)による高い光触媒作用と、ソーダライムガラス中のNa成分の光触媒膜側への析出防止(抑制)と相俟って、光触媒作用の低下や光透過率の低減なども効果的に防止される。 , For example if was inserted between the soda lime glass surface, arrangement of the photocatalyst film, Properties and photocatalysis higher by (dispersed continuous film of fine particles), the photocatalytic film of the Na component in the soda-lime glass preventing precipitation to the side and (suppression) I coupled with, such as reduction and a decrease in the light transmittance of the photocatalytic action is also effectively prevented. すなわち、光触媒膜の強度および光触媒の活性を図るために、チタンアルコレート溶液中に、結晶化した TiO 2微粒子を分散させた液をディップ法などでソーダライムガラスに塗布し、焼成することにより形成した光触媒膜を検討してみたところ、膜強度も良好で、活性の高い光触媒膜として機能する。 That is, in order to achieve the strength and activity of the photocatalyst of the photocatalyst film, formed by a titanium alcoholate solution, was dispersed the TiO 2 fine particles crystallized liquid was coated on a soda lime glass or the like dipping, baking When we examined the photocatalyst film, the film strength is good, and function as a high photocatalytic film active. この点について、本発明者らはさらに検討を進めた結果、上記光触媒作用を有する金属酸化物の連続層に光触媒作用を有する金属酸化物の微粒子を分散させた構成の光触媒膜に対し、前記下地層を介挿することによって、光触媒膜の薄膜化および高活性化が容易になり、前記薄膜化などに伴って、干渉色を回避しながら透過率も向上,改善されることを確認した。 In this regard, with respect to the present invention have further a result of our study, the photocatalytic film of the structure in which fine particles are dispersed in the metal oxide having a continuous layer on the photocatalytic action of the metal oxide having the photocatalytic activity, the lower by interposing the formation, it facilitates the thinning and high activation of the photocatalyst film, along with such a thinning, also improved transmittance while avoiding interference color was confirmed to be improved.

【0017】請求項4の発明は、膜形成面を有し、少なくとも 410nm以下の波長の光が透過可能な光透過性を有するバルブと;前記バルブ内に封装された発光フィラメントと;前記バルブ内の発光フィラメントの両端にへそれぞれ一端が接続されるとともに他端がバルブ外に気密に導出された電気導入手段と;前記バルブ外周面に設けられた光触媒作用を有する金属酸化物を主体とした相、 [0017] The invention of claim 4 has a film forming surface, valve and having at least 410nm or less of the light-transmissive light that is capable of transmitting a wavelength; and a light-emitting filaments is FuSo within said valve; said valve phase consisting mainly of a metal oxide having a photocatalytic action provided in the valve outer circumferential surface; the other end respectively with one end connected to both ends of the light emitting filament electric introducing means and derived hermetically out valve ,
およびこの相に分散された光触媒作用を有する結晶性 T And crystalline T having photocatalyst activity dispersed in this phase
iO 2 , ZnOのうちの少なくとも1種を主体とした微粒子で形成された膜厚0.01〜 0.3μm の光触媒膜とを具備していることを特徴とする白熱電球である。 a incandescent lamp which is characterized in that it comprises a iO 2, at least one thickness 0.01 to 0.3 [mu] m of the photocatalyst film formed of a fine particle mainly composed of one of ZnO.

【0018】請求項5の発明は、膜形成面を有し、少なくとも 410nm以下の波長の光が透過可能な光透過性を有するバルブと;前記バルブ内に封装された発光フィラメントと;前記バルブ内の発光フィラメントの両端にへそれぞれ一端が接続されるとともに他端がバルブ外に気密に導出された電気導入手段と;前記バルブ外周面に設けられた光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1種を主体とした第1の微粒子、および平均粒径が前記第1の微粒子の平均粒径よりも小さい光触媒作用を有する金属酸化物を主体とした第2の超微粒子で形成された膜厚0.01〜 0.3μm の光触媒膜とを具備していることを特徴とする白熱電球である。 [0018] The invention of claim 5 has a film forming surface, valve and having at least 410nm or less of the light-transmissive light that is capable of transmitting a wavelength; and a light-emitting filaments is FuSo within said valve; said valve to both ends of the light emitting filament and an electric introducing means whose other end is led to the air-tight to the outside of the valve one end each is connected; of crystalline TiO 2, ZnO having a photocatalytic action provided in the valve outer circumferential surface formed by second ultrafine particles first microparticles, and the average particle size mainly of metal oxide having a small light catalysis than the average particle diameter of the first fine particle mainly containing at least one a incandescent lamp which is characterized in that it comprises a photocatalyst film having a thickness of 0.01 to 0.3 [mu] m. 請求項6の発明は、請求項4もしくは請求項5記載の白熱電球において、バルブ外周面と光触媒膜との間に SiO 2を主体とする層を介挿させたことを特徴とする。 The invention of claim 6 is the light source device according to claim 4 or claim 5, characterized in that was interposed a layer made mainly of SiO 2 between the valve outer circumferential surface and the photocatalyst film.

【0019】請求項7の発明は、内部に放電ガスが封入され、かつ少なくとも 410nm以下の波長の光が透過可能な透光性気密容器と;前記透光性気密容器内に放電を発生させる電極手段と;前記透光性気密容器の外周面に設けられた光触媒作用を有する金属酸化物を主体とした相、およびこの相に分散された光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1種を主体とした微粒子で形成された膜厚0.01〜 0.3μm の光触媒膜とを具備していることを特徴とする放電ランプである。 [0019] The invention of claim 7, inside the discharge gas is sealed, and at least 410nm or less of the light is capable of transmitting light-transmissive airtight envelope wavelengths; electrodes for generating a discharge in the transparent airtight container means and; the light-transmissive airtight envelope phase was a metal oxide having a photocatalytic activity provided on the outer peripheral surface mainly of, and at least one of crystalline TiO 2, ZnO having a photocatalytic action that is dispersed in the phase it is the discharge lamp, characterized in that comprises one or a mainly the photocatalyst film having a thickness of 0.01 to 0.3 [mu] m formed of fine particles. 請求項8の発明は、内部に放電ガスが封入され、かつ少なくとも 410nm以下の波長の光が透過可能な透光性気密容器と;前記透光性気密容器内に放電を発生させる電極手段と;前記透光性気密容器の外周面に設けられた光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1種を主体とした第1の微粒子、および平均粒径が前記第1 The invention of claim 8 is encapsulated inside the discharge gas, and at least 410nm or less in wavelength light and capable of transmitting light-transmissive airtight envelope; and electrode means for generating a discharge in the transparent airtight container; the light-transmissive airtight envelope first particles mainly composed of at least one of crystalline TiO 2, ZnO having a photocatalytic action provided on the outer peripheral surface, and an average particle size of the first
の微粒子の平均粒径よりも小さい光触媒作用を有する金属酸化物を主体とした第2の超微粒子で形成された膜厚 Second thickness formed of ultrafine particles of metal oxide having a small light catalysis than the average particle diameter of the fine particles mainly
0.01〜 0.3μm の光触媒膜とを具備していることを特徴とする放電ランプである。 It is the discharge lamp, characterized in that and a photocatalyst film of 0.01 to 0.3 [mu] m.

【0020】請求項9の発明は、内部に放電ガスが封入され、かつ少なくとも 410nm以下の波長の光が透過可能な透光性気密容器と;前記透光性気密容器の外周面に設けられた光触媒作用を有する金属酸化物を主体とした相、およびこの相に分散された光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1種を主体とした微粒子で形成された膜厚0.01〜 0.3μm の光触媒膜とを具備していることを特徴とする無電極放電ランプである。 [0020] The invention of claim 9 is encapsulated inside the discharge gas, and at least 410nm or less in wavelength light and capable of transmitting light-transmissive airtight envelope; provided on an outer peripheral surface of the light-transmissive airtight envelope phase consisting mainly of metal oxide having a photocatalytic activity, and thickness 0.01 formed of a fine particle mainly composed of at least one of crystalline TiO 2, ZnO having a photocatalytic activity which is dispersed in this phase 0.3 it is an electrodeless discharge lamp, characterized in that and a photocatalyst film of [mu] m.

【0021】請求項10の発明は、内部に放電ガスが封入され、かつ少なくとも 410nm以下の波長の光が透過可能な透光性気密容器と;前記透光性気密容器の外周面側に設けられた光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1種を主体とした第1の微粒子、および平均粒径が前記第1の微粒子の平均粒径よりも小さい光触媒作用を有する金属酸化物を主体とした第2の超微粒子で形成された膜厚0.01〜 0.3μm の光触媒膜とを具備していることを特徴とする無電極放電ランプである。 [0021] The invention of claim 10 is encapsulated inside the discharge gas, and at least 410nm or less in wavelength light and capable of transmitting light-transmissive airtight envelope; provided on the outer peripheral surface side of the light-transmissive airtight envelope first microparticles, and the average particle size of the metal oxide having a small light catalysis than the average particle diameter of the first fine particle mainly containing at least one of crystalline TiO 2, ZnO having a photocatalytic activity was which is the electrodeless discharge lamp, characterized in that it comprises a photocatalyst film of a second thickness 0.01 to 0.3 [mu] m formed by the ultrafine particles mainly.

【0022】請求項11の発明は、請求項7ないし請求項 [0022] The invention of claim 11, claims 7 to
10いずれか一記載の放電ランプにおいて、透光性気密容器外周面と光触媒膜との間に SiO 2を主体とする層を介挿させたことを特徴とする。 In 10 the discharge lamp of any one described, characterized in that was interposed a layer made mainly of SiO 2 between the light-transmissive airtight envelope outer peripheral surface and the photocatalyst film.

【0023】ここで、無電極放電ランプは、一般的に分離されている高周波コイルと組み合わされて、透光性気密容器内に放電を発生させ、発光源として機能する。 [0023] Here, the electrodeless discharge lamp is combined with the high frequency coil which is generally separated, a discharge is generated in the light-transmitting airtight container, functions as a light emitting source.

【0024】請求項12の発明は、内部に放電ガスが封入された透光性気密容器と;前記透光性気密容器内に放電を発生させる電極手段と;前記透光性気密容器の面に設けられ、かつ放電によって生じる紫外線に励起されて発光する蛍光体層と;前記透光性気密容器の外周面に設けられた光触媒作用を有する金属酸化物を主体とした相、 The invention of claim 12, inside the discharge gas encapsulated light-transmissive airtight envelope and; on the surface of the translucent airtight container; and electrode means for generating a discharge in the transparent airtight container provided, and is excited in the ultraviolet generated by discharge to emit light phosphor layer and; phase consisting mainly of a metal oxide having a photocatalytic action provided on the outer circumferential surface of the light-transmissive airtight envelope,
およびこの相に分散された膜厚0.01〜 0.3μm の光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1 And at least one of crystalline TiO 2, ZnO having a photocatalytic activity of the dispersed film thickness 0.01 to 0.3 [mu] m in this phase
種を主体とした微粒子で形成された光触媒膜とを具備していることを特徴とする蛍光ランプである。 A fluorescent lamp, characterized in that it comprises a photocatalyst film formed by fine particles consisting mainly of seed.

【0025】請求項13の発明は、内部に放電ガスが封入され、かつ少なくとも 410nm以下の波長の光が透過可能な透光性気密容器と;前記透光性気密容器内に放電を発生させる電極手段と;前記透光性気密容器の面に設けられ、かつ放電によって生じる紫外線に励起されて発光する蛍光体層と;前記透光性気密容器の外周面側に設けられた光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1種を主体とした第1の微粒子、および平均粒径が前記第1の微粒子の平均粒径よりも小さい光触媒作用を有する金属酸化物を主体とした第2の超微粒子で形成された膜厚0.01〜 0.3μm の光触媒膜とを具備していることを特徴とする蛍光ランプである。 The invention of claim 13, inside the discharge gas is sealed, and at least 410nm or less of the light is capable of transmitting light-transmissive airtight envelope wavelengths; electrodes for generating a discharge in the transparent airtight container means and; the a surface on the light-transmissive airtight envelope, and a phosphor layer which emits light when excited in the ultraviolet generated by discharge; having photocatalyst activity provided on the outer peripheral surface side of the light-transmissive airtight envelope crystals the first fine particles containing mainly at least one of sex TiO 2, ZnO, and the average particle size mainly of metal oxide having a small light catalysis than the average particle diameter of the first fine particle 2 it is a fluorescent lamp, characterized in that the are and a photocatalyst film having a thickness of 0.01 to 0.3 [mu] m formed by the ultrafine particles. 請求項14の発明は、請求項12もしくは請求項13記載の蛍光ランプにおいて、透光性気密容器外周面と光触媒膜との間に SiO 2を主体とする層を介挿させたことを特徴とする。 The invention of claim 14, and characterized in that the fluorescent lamp of claim 12 or claim 13, was interposed a layer made mainly of SiO 2 between the light-transmissive airtight envelope outer peripheral surface and the photocatalyst film to.

【0026】なお、上記蛍光ランプの電極手段は、放電容器内に設けられたもの、もしくは放電容器外に設けられた無電極形のどちらでもよい。 [0026] The electrode means of the fluorescent lamp, which is provided in the discharge vessel, or may be either of an electrodeless type provided outside the discharge vessel. また、放電ガスに水銀および希ガスを混合したものを用いることができるが、 Further, it is possible to use a mixture of mercury and a rare gas in the discharge gas,
放電によって紫外線を発生するものであればこれらに限らない。 Not limited to as long as it generates ultraviolet rays by discharge.

【0027】請求項15の発明は、請求項4ないし請求項 The invention of claim 15, claim 4 or claim
14いずれか一記載の光源と;前記光源を装着する器具本体とを具備していることを特徴とする照明器具である。 14 and a light source of any one described; a lighting fixture, characterized in that it comprises a fixture body for mounting the light source.

【0028】請求項16の発明は、光源と;前記光源に対向して配設された制光体と;前記光源からの光が到達する制光体の対向面および反対向面の少なくともいずか一方の面に形成された光触媒作用を有する金属酸化物を主体とした相、およびこの相に分散された光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1種を主体とした微粒子で形成された膜厚0.01〜 0.3μm の光触媒膜とを具備していることを特徴とする照明器具である。 The claimed invention in claim 16, the light source and; Sukunakutomoizu the facing surface and the non-opposing face of Seihikaritai that light reaches from the light source; a control light body that is disposed opposite to the light source or one surface which is formed in a phase consisting mainly of metal oxide having a photocatalytic activity, and a fine particle mainly composed of at least one of crystalline TiO 2, ZnO having a photocatalytic action that is dispersed in the phase a lighting fixture, characterized in that it comprises a photocatalyst film of the formed film thickness 0.01 to 0.3 [mu] m.

【0029】請求項17の発明は、光源と;前記光源に対向して配設された制光体と;前記光源からの光が到達する制光体の対向面および反対向面の少なくともいずか一方の面に形成された光触媒作用を有する結晶性 TiO 2 The claimed invention in claim 17, light source and; Sukunakutomoizu the facing surface and the non-opposing face of Seihikaritai that light reaches from the light source; a control light body that is disposed opposite to the light source or crystalline TiO 2 having photocatalytic activity which is formed on one surface,
ZnOのうちの少なくとも1種を主体とした第1の微粒子、および平均粒径が前記第1の微粒子の平均粒径よりも小さい光触媒作用を有する金属酸化物を主体とした第2の超微粒子で形成された膜厚0.01〜 0.3μm の光触媒膜とを具備していることを特徴とする照明器具である。 In the second ultrafine particles first microparticles, and the average particle size mainly of metal oxide having a small light catalysis than the average particle diameter of the first fine particle mainly containing at least one of ZnO a lighting fixture, characterized in that it comprises a photocatalyst film of the formed film thickness 0.01 to 0.3 [mu] m.

【0030】前記制光体とは、たとえば反射鏡やレンズなど例示されるが、これらに限定されるものでなく、また、少なくともいずれか一方の面とは、一般的には光源側の面(対向面)であるが、石英など紫外線が透過する材質製の場合は光源側と反対の面(反対向面)でもよいことを意味する。 [0030] and the system optical body, for example, is exemplified such as a reflective mirror or a lens, not limited to, also, the at least one surface, typically the light source-side surface ( is a facing surface), if made of materials that ultraviolet quartz passes means that may be a surface opposite to the light source side (non-opposing surface).

【0031】請求項18の発明は、光源と;前記光源を包囲する包囲体と;前記光源からの光が到達する包囲体の内壁面および外壁面の少なくともいずか一方の面に形成された光触媒作用を有する金属酸化物を主体とした相、 The invention of claim 18 comprises a light source and; formed on one surface or not a Sukunakutomoi the inner wall surface and outer wall surface of the enclosure light reaches from the light source; enclosure and surrounding said light source phase consisting mainly of metal oxide having a photocatalytic action,
およびこの相に分散された光触媒作用を有する結晶性 T And crystalline T having photocatalyst activity dispersed in this phase
iO 2 , ZnOのうちの少なくとも1種を主体とした微粒子で形成された膜厚0.01〜 0.3μm の光触媒膜とを具備していることを特徴とする照明器具である。 a lighting fixture, characterized in that it comprises iO 2, a thickness of 0.01 to 0.3 [mu] m formed of fine particles mainly composed of at least one of ZnO and the photocatalyst film.

【0032】請求項19の発明は、光源と;前記光源を包囲する包囲体と;前記光源からの光が到達する包囲体の内壁面および外壁面の少なくともいずか一方の面に形成された光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1種を主体とした第1の微粒子、および平均粒径が前記第1の微粒子の平均粒径よりも小さい光触媒作用を有する金属酸化物を主体とした第2の超微粒子で形成された膜厚0.01〜0.3μm の光触媒膜とを具備していることを特徴とする照明器具である。 The invention of claim 19, light source and; formed on one surface or not a Sukunakutomoi the inner wall surface and outer wall surface of the enclosure light reaches from the light source; enclosure and surrounding said light source the metal oxides having a first fine particle, and small photocatalysis than the average particle diameter of the average particle diameter of the first fine particle mainly containing at least one of crystalline TiO 2, ZnO having a photocatalytic action a lighting fixture, characterized in that it comprises a photocatalyst film of a second thickness 0.01~0.3μm formed of ultrafine particles mainly.

【0033】前記包囲体とは、反射鏡,器具全面の透光レンズやガラス板などを指し、制光体として機能するものを含んでもよい。 [0033] The the enclosure, reflector, refers to such light-transmitting lens or a glass plate of the instrument entirely, may include those that function as Seihikaritai.

【0034】請求項20の発明は、請求項16ないし請求項 The invention of claim 20, claim 16 or claim
19いずれか一記載の照明器具において、光触媒膜の下地層として SiO 2を主体とする層を介挿させたことを特徴とする。 19 In the luminaire of any one described, characterized in that was interposed a layer of SiO 2 as a main component as an underlying layer of the photocatalyst film.

【0035】本発明に係る光触媒膜は、上記のように光触媒作用を有する金属酸化物を主体としたものと、光触媒作用を有する結晶性 TiO 2 , ZnOの少なくとも1種を主体としたものとを必須の成分としている。 The photocatalyst film according to the present invention, as those mainly composed of metal oxide having a photocatalytic action as described above, crystalline TiO 2, ZnO having a photocatalytic activity and those mainly composed of at least one It is an essential component. ここで、光触媒作用を有する金属酸化物としては、前記 TiO 2の外、たとえばWO 3 , LaRhO 3 , FeTiO 3 ,Fe 2 O 3 ,Cd Examples of the metal oxide having a photocatalytic action, outside of the TiO 2, for example WO 3, LaRhO 3, FeTiO 3 , Fe 2 O 3, Cd
Fe 2 O 4 ,SrTiO 3 ,CdSe,GaAs, GaP, RuO 2などの微粒子、もしくは2種以上の微粒子混合系が挙げられる。 Fe 2 O 4, SrTiO 3, CdSe, GaAs, GaP, fine particles such as RuO 2, or 2 or more kinds of fine particles mixed systems. また、前記金属酸化物を主体とした相(連続膜)もしくは超微粒子中に、分散される結晶性 TiO 2 , ZnOの少なくとも1種を主体とした微粒子(もしくは第1の微粒子)は、たとえば平均粒径 5〜70nm程度のものが選ばれる。 Also, the metal oxide phases formed mainly through the (continuous film) or fine particles, particles composed mainly of at least one crystalline TiO 2, ZnO dispersed (or the first particles), for example the average those having a particle size of about 5~70nm is selected.

【0036】前記光触媒膜は、次のようにして容易に形成できる。 [0036] The photocatalytic film can be easily formed as follows. たとえば平均粒径 5nm未満の TiO 2などの光触媒作用を有する金属酸化物微粒子と、平均粒径 5〜70 For example, a metal oxide fine particles having a photocatalytic activity, such as TiO 2 having an average particle size of less than 5 nm, the average particle diameter of 5 to 70
nmのTiO 2などの光触媒作用を有する金属酸化物微粒子とを、たとえばテトライソプロピルチタネートモノマーもしくはテトライソプロピルチタネートポリマーなどのアルコキシチタネート系化合物の溶液に、添加分散させて調製した懸濁・分散液を支持基体面に塗布焼付けることによって、所要の光触媒体を形成できる。 a metal oxide fine particles having a photocatalytic activity, such as TiO 2 of nm, for example, a solution of an alkoxy titanate compounds such as tetraisopropyl titanate monomer or tetraisopropyl titanate polymer, supporting the suspension-dispersion prepared by adding dispersing by baking it applied to the substrate surface to form a desired photocatalyst. さらに詳しくは、たとえばチタンのアルコキシド溶液に平均粒径 5 The average particle size of 5 More particularly, for example, the alkoxide solution of titanium
〜10nm程度のアナターゼ型結晶の TiO 2微粒子を懸濁・ Suspension of TiO 2 particles of ~10nm about anatase-
分散液を支持基体面に塗布し、焼成によってチタンアルコキシド成分から平均粒径 5nm未満の TiO 2を結晶化させた場合、チタンアルコキシド成分で形成される光学系膜と同程度の硬度,強度と、平均粒径 5〜70nmの TiO 2 The dispersion was coated on the support substrate surface, if the TiO 2 having an average particle size of less than 5nm titanium alkoxide component was crystallized by firing, optics film about the same hardness, which is formed by a titanium alkoxide component, and strength, TiO having an average particle diameter of 5 to 70 nm 2
微粒子のみで形成される光触媒膜と同程度の光触媒作用を備えた光触媒体を形成できる。 The photocatalyst can be formed with only the photocatalytic action of the same extent as the photocatalytic film formed by fine particles.

【0037】なお、前記結晶性 TiO 2 , ZnO系微粒子(もしくは第1の微粒子)を分散させる金属酸化物相は、一部もしくはすべてが非晶質性あるいは多孔質性であってもよい。 [0037] The metal oxide phase dispersing the crystalline TiO 2, ZnO-based particles (or the first fine particles), a portion or all may be amorphous or porous. ここで金属酸化物は、アナターゼ型結晶を主成分としたものが望ましく、また、前記 TiO 2などの超微粒子(平均粒径 5nm未満程度)、および結晶性 T Wherein the metal oxide is desirably those composed mainly of anatase, also ultrafine particles (about average particle size of less than 5 nm), such as the TiO 2, and crystalline T
iO 2微粒子(平均粒径 5〜70nm程度)の混合組成比は、 mixing composition ratio of iO 2 particles (average particle size of about 5 to 70 nm) is
特に限定されないが、一般的に質量比で 1: 4〜 4: 1 Is not particularly limited, in general, the weight ratio 1: 4 4: 1
程度がよい。 Degree is good.

【0038】本発明に係る白熱電球,放電ランプ,無電極放電ランプおよび蛍光ランプにおいて、バルブ外周面への光触媒膜の形成は、前記光触媒膜の形成手段に準じて行われる。 The incandescent lamp according to the present invention, a discharge lamp, in electrodeless discharge lamps and fluorescent lamps, formed of a photocatalytic film to the valve outer circumferential surface is carried out according to the forming means of the photocatalyst film. そして、この光触媒膜の厚さは、一般的に、白熱電球や蛍光ランプから放出される波長 300〜 3 The thickness of the photocatalyst film is typically, wavelength 300-3 emitted from an incandescent bulb or a fluorescent lamp
70nmの紫外線分光エネルギーの透過率が10%以上、さらに好ましくは50%以上であるように選択・設定すればよい。 70nm transmittance of ultraviolet spectral energy more than 10%, even more preferably may be selected and set to be 50% or more. さらに具体的には、光触媒膜の厚さは 0.1〜 100n More specifically, the thickness of the photocatalytic film is 0.1 to 100n
m,好ましくは 0.5〜30nm、さらに好ましくは 1〜15nm m, preferably 0.5 to 30 nm, more preferably 1~15nm
である。 It is. ここで、前記波長 300〜 370nmの紫外線分光エネルギーの透過率が10%以上、さらには50%以上に膜厚を設定したときは、光触媒膜表面の紫外線照射が大きくなるので、光触媒作用がさらに向上する。 Here, the wavelength 300 ultraviolet spectral energy transmittance of 370nm is 10% or more, further that where an thickness at least 50%, the ultraviolet irradiation of the photocatalyst film surface is increased, further improving the photocatalytic activity to. なお、波長 3 The wavelength 3
00〜 370nmの領域を基準としたのは、一般的に波長 300 00~ 370 nm region was referenced to the generally Wavelength 300
nm未満の放射エネルギーは相対的に少なく無視できること、また波長 370nmを超える紫外線は、光触媒作用が急激に低減することによる。 Radiant energy below nm may be negligible relatively small, also ultraviolet wavelengths above 370nm is by photocatalytic action is rapidly reduced. 請求項1の発明では、基体面の光触媒膜が、光触媒作用を有する金属酸化物相に、結晶性 TiO 2などの微粒子を分散させた構成を採っている。 In the invention of claim 1, the photocatalyst film of the substrate surface, the metal oxide phase having a photocatalytic action, adopts a configuration in which fine particles are dispersed, such as crystalline TiO 2. すなわち、同種の光触媒作用を有する金属酸化物で全体的に形成されているので、全体的に馴染みがよくすぐれた耐久性を呈する。 That is, since it is entirely formed of a metal oxide having a photocatalytic activity of the same type, exhibits a generally familiar well excellent durability. また、実質的に粒子径の異なる組み合わせ系であるために、硬度,強度が高くて表面積の大きい膜となって、光触媒作用も向上する。 Further, in order to be substantially different combinations based particle diameters, hardness, strength becomes larger film surface area is high, thereby improving photocatalytic activity.

【0039】請求項2の発明では、光触媒作用を有する膜が、結晶性の TiO 2微粒子などと、光触媒作用を有する金属酸化物超微粒子の混合系膜としたことにより、すぐれた光触媒作用を呈する一方、支持基体に対する接着強度(耐剥離性)も良好で脱離・損傷なども回避され、 [0039] In the second aspect of the present invention, a film having a photocatalytic action, exhibits such a crystalline TiO 2 particles, by which a mixed system film of metal oxide ultrafine particles having a photocatalytic activity, superior photocatalytic activity On the other hand, the adhesive strength to the support base (peel resistance), etc. also good release and damaging also be avoided,
硬度の高さと相俟って長期間に亘って安定した光触媒機能を保持発揮する。 It exerts maintain a stable photocatalytic function for a long period of time I height coupled with the hardness.

【0040】請求項3の発明では、下地層を介挿したことにより、基体を構成する成分の一部が光触媒膜側に析出して悪影響を及ぼす恐れが解消し、活性度が高くて干渉色のない光触媒膜として機能する。 [0040] In the present invention of claim 3, by which interposed an underlying layer, a part of the components constituting the base is precipitated in the photocatalyst film side eliminated have adverse effects, interference colors high activity functions as no photocatalyst film.

【0041】請求項4の発明では、一般的な光源などしての使用において、前記のようなすぐれた耐久性および良好な光触媒作用など呈するだけでなく、屈折率の相違に起因する乱反射なども回避され、光学的特性も損なわれないので、高品質な白熱電球として機能しながらその周辺部の清浄化なども行うことができる。 [0041] In a fourth aspect of the present invention, in the use of the like conventional light source, not only exhibits such the like excellent durability and good photocatalysis, also including irregular reflection due to the difference in refractive index it is avoided, because it is not also impair the optical properties, while functioning as a high-quality incandescent bulbs may also be performed, such as cleaning of the peripheral portion thereof.

【0042】請求項5の発明では、一般的な光源などしての使用において、前記のようなすぐれた耐久性および光触媒作用を呈するだけでなく、屈折率の相違に起因する乱反射なども回避され、光学的特性も損なわれないので、高品質な白熱電球として機能しながらその周辺部の清浄化なども行うことができる。 [0042] In the invention of claim 5 is the use of in such a conventional light source, not only exhibits durability and photocatalytic action superior as described above, are also avoided, such as irregular reflection due to the difference in refractive index since not even impair optical properties, while functioning as a high-quality incandescent bulbs may also be performed, such as cleaning of the peripheral portion thereof.

【0043】請求項6の発明では、下地層の保護膜的な機能と相俟って、上記高品質な白熱電球として、より効果的に作用しながら、その周辺部の清浄化なども行うことができる。 [0043] In the present invention of claim 6, I protective film functions coupled with the underlying layer, as the high quality incandescent bulbs, while working effectively, be carried out such as cleaning of the peripheral portion can.

【0044】請求項7の発明では、前記すぐれた光触媒作用などを有する放電ランプであるため、照明用光源としての使用で、消臭,殺菌(減菌)なども併せて行うことができる。 [0044] In the present invention of claim 7, since a discharge lamp having such the excellent photocatalytic activity, the use of a light source for illumination, can be also performs deodorant, sterilization (sterilization).

【0045】請求項8の発明では、光源などしての使用において、前記のようなすぐれた耐久性および良好な光触媒作用など呈するだけでなく、屈折率の相違に起因する乱反射なども回避され、光学的特性も損なわれないので、高品質な放電ランプとして機能しながら、その周辺部の清浄化なども行うことができる。 [0045] In the invention of claim 8 is the use of in such a light source, not only exhibits such the like excellent durability and good photocatalysis also be avoided, such as irregular reflection due to the difference in refractive index, since not even impair optical properties, while functioning as a high-quality discharge lamp can also be performed, such as cleaning of the peripheral portion thereof.

【0046】請求項9の発明では、光源などしての使用において、前記のようなすぐれた耐久性および良好な光触媒作用など呈するだけでなく、屈折率の相違に起因する乱反射なども回避され、光学的特性も損なわれないので、高品質な無電極放電ランプとして機能しながら、その周辺部の清浄化なども行うことができる。 [0046] In the invention of claim 9 is the use of in such a light source, not only exhibits such the like excellent durability and good photocatalysis also be avoided, such as irregular reflection due to the difference in refractive index, since not even impair optical properties, while functioning as a high-quality electrodeless discharge lamp can also be performed, such as cleaning of the peripheral portion thereof.

【0047】請求項10の発明では、光源などしての使用において、前記のようなすぐれた耐久性および良好な光触媒作用など呈するだけでなく、屈折率の相違に起因する乱反射なども回避され、光学的特性も損なわれないので、高品質な無電極放電ランプとして機能しながら、その周辺部の清浄化なども行うことができる。 [0047] In the invention of claim 10, as used with such a light source, not only exhibits such the like excellent durability and good photocatalysis also be avoided, such as irregular reflection due to the difference in refractive index, since not even impair optical properties, while functioning as a high-quality electrodeless discharge lamp can also be performed, such as cleaning of the peripheral portion thereof.

【0048】請求項11の発明では、下地層の保護膜的な機能と相俟って、上記高品質な放電ランプもしくは無電極放電ランプとして、より効果的に作用しながら、その周辺部の清浄化なども行うことができる。 [0048] In the present invention of claim 11, I protective film functions coupled with the underlying layer, as the high-quality discharge lamp or an electrodeless discharge lamp, while acting more effectively clean the periphery it can also be carried out such as the reduction.

【0049】請求項12の発明では、光源などしての使用において、前記のようなすぐれた耐久性および良好な光触媒作用など呈するだけでなく、屈折率の相違に起因する乱反射なども回避され、光学的特性も損なわれないので、高品質な蛍光ランプとして機能しながら、その周辺部の清浄化なども行うことができる。 [0049] In the invention of claim 12, as used with such a light source, not only exhibits such the like excellent durability and good photocatalysis also be avoided, such as irregular reflection due to the difference in refractive index, since not even impair optical properties, while functioning as a high quality fluorescent lamps can also be performed, such as cleaning of the peripheral portion thereof.

【0050】請求項13の発明は、光源などしての使用において、前記のようなすぐれた耐久性および良好な光触媒作用など呈するだけでなく、屈折率の相違に起因する乱反射なども回避され、光学的特性も損なわれないので、高品質な蛍光ランプとして機能しながら、その周辺部の清浄化なども行うことができる。 The invention of claim 13, as used with such a light source, not only exhibits such the like excellent durability and good photocatalysis also be avoided, such as irregular reflection due to the difference in refractive index, since not even impair optical properties, while functioning as a high quality fluorescent lamps can also be performed, such as cleaning of the peripheral portion thereof.

【0051】請求項14の発明では、下地層の保護膜的な機能と相俟って、上記高品質な蛍光ランプとして、より効果的に作用しながら、その周辺部の清浄化なども行うことができる。 [0051] In the present invention of claim 14, I protective film functions coupled with the underlying layer, as the high-quality fluorescent lamps, while working effectively, be carried out such as cleaning of the peripheral portion can.

【0052】請求項15の発明では、前記のようなすぐれた耐久性および良好な光触媒作用など呈するだけでなく、屈折率の相違に起因する乱反射なども回避され、光学的特性も損なわれない高品質な光源を備えたことにより、照明用光源として機能しながら、その周辺部の清浄化なども行うことができる。 [0052] In the present invention of claim 15, not only exhibits such the like excellent durability and good photocatalysis, such irregular reflection due to the difference in refractive index is also avoided, higher not be impaired optical properties by having a quality light, while functions as an illumination light source can also be performed, such as cleaning of the peripheral portion thereof.

【0053】請求項16の発明では、前記のようなすぐれた耐久性および良好な光触媒作用など呈するだけでなく、屈折率の相違に起因する乱反射なども回避され、光学的特性も損なわれない制光体を備えたことにより、照明器具として機能しながら、その周辺部の清浄化なども行うことができる。 [0053] In the present invention of claim 16, not only exhibits such the like excellent durability and good photocatalysis, such irregular reflection due to the difference in refractive index is also avoided, not even impaired optical properties braking by having a light body, while functioning as a lighting fixture it can also be performed, such as cleaning of the peripheral portion thereof.

【0054】請求項17の発明は、前記のようなすぐれた耐久性および良好な光触媒作用など呈するだけでなく、 [0054] The invention of claim 17, not only exhibits such the like excellent durability and good photocatalysis,
屈折率の相違に起因する乱反射なども回避され、光学的特性も損なわれない制光体を備えたことにより、照明器具として機能しながら、その周辺部の清浄化なども行うことができる。 Such irregular reflection due to the difference in refractive index is also avoided, by having a system optical member which is not also impair the optical properties, while functioning as a lighting fixture can also be performed, such as cleaning of the peripheral portion thereof.

【0055】請求項18の発明では、前記のようなすぐれた耐久性および良好な光触媒作用など呈するだけでなく、屈折率の相違に起因する乱反射なども回避され、光学的特性も損なわれない包囲体を備えたことにより、照明器具として機能しながら、その周辺部の清浄化なども行うことができる。 [0055] In the present invention of claim 18, not only exhibits such the like excellent durability and good photocatalysis, such irregular reflection due to the difference in refractive index is also avoided, not even impair optical characteristics surrounded by having the body, while functioning as a lighting fixture it can also be performed, such as cleaning of the peripheral portion thereof.

【0056】請求項19の発明では、前記のようなすぐれた耐久性および良好な光触媒作用など呈するだけでなく、屈折率の相違に起因する乱反射なども回避され、光学的特性も損なわれない包囲体を備えたことにより、照明器具として機能しながら、その周辺部の清浄化なども行うことができる。 [0056] In the present invention of claim 19, not only exhibits such the like excellent durability and good photocatalysis, such irregular reflection due to the difference in refractive index is also avoided, not even impair optical characteristics surrounded by having the body, while functioning as a lighting fixture it can also be performed, such as cleaning of the peripheral portion thereof.

【0057】請求項20の発明では、下地層の保護膜的な機能と相俟って、より効果的に照明器具として機能しながら、その周辺部の清浄化なども行うことができる。 [0057] In the invention of claim 20, I protective film functions coupled with the underlying layer, while functions as a more effective luminaire can also be performed, such as cleaning of the peripheral portion thereof.

【0058】 [0058]

【発明の実施の形態】以下図1〜図11を参照して実施形態を説明する。 It will be described by referring to embodiments below FIGS. 1-11 PREFERRED EMBODIMENTS.

【0059】実施例1 図1は、光触媒体の構成例を断面的に示したもので、1 [0059] Example 1 FIG. 1 is a configuration example of a photocatalyst which was shown sectionally, 1
は支持基板(たとえばガラス板…波長 410nm以下の光を透過する)、2は光触媒膜であり、この光触媒膜2は結晶性微粒子(第1の TiO 2微粒子)2a,および結晶性微粒子2aを分散・担持する光触媒作用を有する金属酸化物相(第2の TiO 2超微粒子領域)2bで形成されている。 Supporting substrate (for example, transmits light below the glass plate ... wavelength 410 nm), 2 is a photocatalyst film, the photocatalyst film 2 is dispersed crystalline particles (first TiO 2 particles) 2a, and crystalline particles 2a · supported metal oxide phase having a photocatalytic activity are formed in the (second TiO 2 ultrafine particles region) 2b.

【0060】次に、前記光触媒膜2の形成方法を説明する。 [0060] Next, a method for forming the photocatalyst film 2. 先ず、テトライソプロピルチタネートモノマーをグリセリンおよびアセチルアセトンでキレート化したもの、ガラス質形成剤( P 2 O 5 )を、酢酸エチル−エタノール系混合溶媒に加えて溶液化した後、この混合溶液中に、平均粒径 7nm,比表面積300m 2 /g のアナターゼ結晶型の TiO 2超微粒子(第1の TiO 2微粒子)を分散・懸濁させて、懸濁液を調製する。 First, those chelated with glycerine and acetylacetone tetraisopropyl titanate monomers, vitreous formers (P 2 O 5), ethyl acetate - After the solution by addition of ethanol-based mixed solvent, to this mixed solution, the average particle size 7 nm, and a specific surface area of 300 meters 2 / g of anatase crystalline form of TiO 2 ultrafine particles (first TiO 2 fine particles) are dispersed or suspended to prepare a suspension. この懸濁液を、予め用意しておいた厚さ 1mmのソーダライムガラス片(30× The suspension, soda lime glass piece having a thickness of 1mm which had been prepared beforehand (30 ×
30mm)に塗布し、 500℃×10時間焼成処理を施して、アナターゼ結晶型のTiO 2微粒子(第1の TiO 2微粒子) Was applied to 30 mm), subjected to 500 ° C. × 10 hours calcination treatment, anatase crystalline form of TiO 2 fine particles (first TiO 2 fine particles)
および TiO 2相(第2の TiO 2超微粒子の領域)を主体とする膜厚 0.2〜 0.3μm の光触媒膜を作成する。 And creating a photocatalytic film having a thickness of 0.2 to 0.3 [mu] m to TiO 2 phase (the region of the second TiO 2 ultrafine particles) mainly.

【0061】また、比較のため、前記平均粒径 7nm,比表面積300m 2 /g のアナターゼ結晶型の TiO 2微粒子(第1の TiO 2微粒子)を分散・懸濁させた懸濁液(比較例1)、テトライソプロピルチタネートモノマーのキレート化物を、ガラス質形成剤( P 2 O 5 )とともに酢酸エチル−エタノール系混合溶媒に加えて溶液化した溶液(比較例2)を、それぞれ前記実施例の場合と同様の条件でソーダライムガラス片に、塗布・焼成して光触媒体を作成した。 [0061] For comparison, the average particle size 7 nm, specific surface area 300 meters 2 / g of anatase crystalline form of TiO 2 fine particles (first TiO 2 particles) was dispersed and suspended in (Comparative Example 1), a chelate compound of tetraisopropyl titanate monomers, vitreous formers (P 2 O 5) with ethyl acetate - in addition to the ethanol-based mixed solvent solution of solution (Comparative example 2), in each case example soda lime glass pieces under the same conditions as to prepare a photocatalyst by coating and firing.

【0062】これらの光触媒膜面におけるタバコのヤニの吸着力(剥がれ易さ)%、紫外線放電ランプからの紫外線照射(波長 365nm,0.16mW/cm 2 )によるヤニの分解力%、ヤニの分解率(分解/吸着)%および光触媒膜の硬さをそれぞれ評価した結果を表1に示す。 [0062] suction force of the tar of tobacco in these photocatalyst film surface (peeling easiness)%, ultraviolet radiation from the ultraviolet discharge lamp (wavelength 365nm, 0.16mW / cm 2) decomposition activity% of tar by, decomposition rate of tar Table 1 shows the results of evaluation (decomposed / adsorption)% and the photocatalyst film hardness, respectively. なお、吸着力および分解力は、透過率の変化で行って実施例の場合を基準値として評価し、また硬さは鉛筆硬度で行った。 Incidentally, the suction force and resolving power is carried out in the change of the transmittance evaluated in Example as the reference value, also the hardness was conducted by pencil hardness.

【0063】 [0063] 上記特性例の評価からも分かるように、本発明の光触媒体は、タバコのヤニによる外界汚染に対してすぐれた清浄化機能を呈するだけでなく、他の有機物、たとえばトイレの臭気の解消などにも有効であった。 As can be seen from the evaluation of the characteristic example, photocatalyst of the present invention not only exhibits a cleaning ability superior against external contamination with tar of tobacco, other organic matter, for example, such as elimination of toilet odor also it was effective.

【0064】このように本実施例の光触媒体の場合は、 [0064] In such the photocatalyst of this embodiment,
TiO 2微粒子の塗布,焼き付けで形成した焼結型の光触媒膜(比較例1相当)と少なくとも同程度の光触媒作用を有する一方、チタンアルコキシドの熱分解で生成・形成した光学系型の光触媒膜(比較例2相当)と同程度の硬度を保持しており、耐久性などすぐれた光触媒膜として機能する。 Coating of TiO 2 fine particles, while having a photocatalytic activity of at least the same extent as sintering type photocatalyst film (corresponding Comparative Example 1) formed by baking, the optical system type generated, formed by thermal decomposition of a titanium alkoxide photocatalyst film ( Comparative example 2 corresponds) and holds the same degree of hardness, which functions as a photocatalyst film excellent durability.

【0065】また、本実施例の光触媒体においては、ソーダライムガラス片に SiO 2層などのアンダーコートを設けずとも、良好な光触媒作用を呈することが分かった。 [0065] In the photocatalyst of the present embodiment, without providing an undercoat such as a SiO 2 layer on soda lime glass piece, it exhibits a good photocatalysis. これは、ソーダライムガラス片から析出されるナトリウム(Na)などの支持基板1からの不純物が、主にアルコレート金属酸化物層(第2の TiO 2超微粒子領域)2b This impurity from the supporting substrate 1 such as sodium (Na) is deposited from a soda lime glass pieces, mainly alcoholates metal oxide layer (second TiO 2 ultrafine particles region) 2b
に拡散されるためであり、光触媒作用がすぐれている結晶性微粒子(第1の TiO 2微粒子)2aがこの不純物の影響を受けにくくなる。 In is because the diffused, crystalline microparticles (first TiO 2 particles) 2a of photocatalysis is excellent is not easily affected by the impurity. すなわち、支持基体側からの悪影響も回避されることは、光学系型および焼結型の両 TiO That is, it is also avoided adverse effects from the support base side, both TiO optics type and sintered type
2微粒子の混成によって成されていると考えられる。 It is considered to have been made by a mixture of 2 fine particles.

【0066】さらに、本実施例の光触媒膜2は、ディップ方式など簡単な成膜手段により、短時間で所要の膜厚に形成することができる。 [0066] Further, the photocatalyst film 2 of the present embodiment, by simple deposition means such as a dipping method, can be formed into a required thickness in a short time. これは、アルコレート懸濁液が結晶性微粒子(第1の TiO 2微粒子)2aの周囲を覆いながら、支持基板1の表面に拡散していくためである。 This is because the alcoholate suspension while covering the periphery of crystalline particles (first TiO 2 particles) 2a, it diffuses to the surface of the supporting substrate 1.
このように、結晶性微粒子2aを核として、アルコレート溶液のみを塗布する場合に比べて、1回の塗布工程で膜厚の光触媒膜2を形成することができる。 Thus, the crystalline particles 2a as nuclei, as compared with the case of applying only the alcoholate solution, it is possible to form a film thickness of the photocatalyst film 2 in one coating step. またさらに、 Furthermore,
光触媒膜2の膜厚が厚くなると、結晶性微粒子2aは、支持基板1からの不純物の影響が一層受けにくくなる。 When the thickness of the photocatalytic film 2 is increased, the crystalline particles 2a is the influence of impurities from the supporting substrate 1 is hardly more received.

【0067】実施例2 図2は、光触媒体の構成例を断面的に示したもので、1 [0067] EXAMPLE 2 FIG. 2 is a configuration example of a photocatalyst which was shown sectionally, 1
はソーダライムガラス片、2は光触媒膜であり、この光触媒膜2は結晶性微粒子(第1の TiO 2微粒子)2a,および結晶性微粒子2aを分散・担持する光触媒作用を有する金属酸化物相(第2の TiO 2超微粒子領域)2bで形成されている。 Soda-lime glass piece, 2 is a photocatalyst film, a metal oxide phase photocatalytic film 2 having a photocatalytic effect of dispersing and carrying the crystalline particles (first TiO 2 particles) 2a and crystalline particles 2a, ( are formed in the second TiO 2 ultrafine particles region) 2b. また、3は前記ソーダライムガラス片1と光触媒膜2との間に介挿された SiO 2層である。 Also, 3 is a SiO 2 layer interposed between the soda-lime glass piece 1 and the photocatalyst film 2.

【0068】次に、前記光触媒体の形成方法を説明する。 [0068] Next, a method for forming the photocatalyst. 先ず、厚さ 5mmのソーダライムガラス片を用意し、 First, a soda-lime glass piece having a thickness of 5 mm,
このガラス片をアルコキシシリコーン系化合物の溶液(商品名, NSi-500,日曹KK製)に浸漬した後、30mm/ The solution of the glass pieces alkoxy silicone compound (trade name, NSi-500, Nisso Ltd. KK) after immersion in, 30 mm /
minの速度で引上げてから、 550℃の温度で10 min焼成して、厚さ約20nmの SiO 2層を形成した。 After pulling at a min rate of, and 10 min calcined at a temperature of 550 ° C., to form the SiO 2 layer having a thickness of about 20 nm.

【0069】その後、予め調製,用意しておいた TiO 2 [0069] Then, TiO 2, which previously prepared, which had been prepared
超微粒子を分散含有させたチタネート系溶液(分散液) Titanate solution is dispersed contains ultrafine particles (dispersion liquid)
に、前記 SiO 2層を設けたガラス片を浸漬し、 300mm/ To, dipping the glass piece provided the SiO 2 layer, 300 mm /
minの速度で引上げてから、 550℃の温度で10 min焼成して、 TiO 2相(連続膜)中に結晶化 TiO 2微粒子が分散した厚さ約 0.1μm の TiO 2系光触媒膜を形成した。 After pulling at a min rate of, and 10 min calcined at a temperature of 550 ° C., crystallized TiO 2 particles to form TiO 2 based photocatalyst film with a thickness of about 0.1μm dispersed in TiO 2 phase (continuous film) .
ここで、チタネート系分散液は、テトライソプロピルチタネート系溶液(商品名, NTiO 92,日曹KK製)を酢酸ブチルで3倍に希釈し、この希釈液に平均粒径nm,比表面積300m 2 /g のアナターゼ結晶型の TiO 2超微粒子(商品名,STS-01,石原産業KK製)を、前記テトライソプロピルチタネート系溶液に対して、重量比で 5%加え分散させて調製したものである。 Here, titanate dispersions, tetraisopropyl titanate-based solution (trade name, NTIO 92, Nisso Ltd. KK) was diluted 3-fold with butyl acetate, the average particle size nm in this dilution, a specific surface area of 300 meters 2 / g of anatase crystalline form of TiO 2 ultrafine particles (trade name, STS-01, manufactured by Ishihara Sangyo Kaisha, KK) and, with respect to the tetraisopropyl titanate-based solution, in which was prepared by 5% added dispersed at a weight ratio.

【0070】また、比較例3として、テトライソプロピルチタネート系溶液(商品名, NTiO 92,日曹KK製)の酢酸ブチルによる3倍希釈液に、前記 SiO 2層を設けたガラス片を浸漬し、 300mm/ minの速度で引上げてから、 550℃の温度で10 min焼成して、厚さ約 5μm の T [0070] As a comparative example 3, tetraisopropyl titanate-based solution (trade name, NTIO 92, Nisso Ltd. KK) in 3-fold dilutions by butyl acetate, by dipping the glass piece provided the SiO 2 layer, after pulling at a speed of 300 mm / min, and 10 min calcined at a temperature of 550 ° C., a thickness of about 5 [mu] m T
iO 2系光触媒膜( TiO 2相のみの連続膜)を形成した。 It was formed iO 2 based photocatalyst film (continuous film of only TiO 2 phases).
これら光触媒体の光触媒膜面に、サラダオイル 1mgを載置(被着)した後、紫外線放電ランプからの紫外線(波長 360nm,強度20mW/cm 2 )を 2時間照射して、重量の変化から光触媒活性を評価する一方、 JIS(K5400)に準拠した鉛筆硬度法で膜の硬さ(膜強度)をそれぞれ評価した結果を表2に示す。 The photocatalyst film surface of photocatalyst, after the salad oil 1mg placed (deposited), ultraviolet rays from the ultraviolet discharge lamp (wavelength 360 nm, intensity 20 mW / cm 2) was irradiated for 2 hours, the photocatalyst from the change in weight while evaluating the activity, indicating JIS (K5400) to the hardness of the film in the pencil hardness method in conformity with the results of evaluating each (film strength) in Table 2. なお、光触媒活性の評価は、サラダオイルの残量比(%)で示した。 The evaluation of photocatalytic activity was expressed by the remaining ratio of the salad oil (%).

【0071】 [0071] 上記の試験・評価から分かるように、実施例2の光触媒体は、 TiO 2相に分散含有された結晶化 TiO 2微粒子が主活性種として作用する一方、 TiO 2相は活性を保持しながらバインダーとして作用する。 As can be seen from the above testing and evaluation, photocatalyst of Example 2, while the crystallization TiO 2 particles dispersed contained in TiO 2 phase acts as the primary active species, the TiO 2 phase binder while retaining activity to act as. しかも、支持体として機能するガラス片と光触媒体との間には SiO 2から成るアンダーコートが介挿されているので、前記 TiO 2相の結晶化が侵されることも解消し、光触媒活性が高められている。 Moreover, between the glass pieces and photocatalyst that functions as a support because the undercoat made of SiO 2 is interposed, and also eliminates the crystallization of the TiO 2 phase is affected, photocatalytic activity increased It is. ここで、光触媒活性が高められることは、光触媒膜の厚さを薄くでき、かつ TiO 2相に分散含有される結晶化 TiO 2微粒子の量を低減できることになり、さらには、光触媒膜の強度も向上する。 Here, the photocatalytic activity is enhanced can reduce the thickness of the photocatalyst film, and will be able to reduce the amount of crystallinity TiO 2 particles dispersed and contained in the TiO 2 phase, and further, the strength of the photocatalyst film improves. すなわち、この構成においては、光触媒活性,膜強度および高い透過率(干渉色のない)を備えていた。 That is, in this arrangement was equipped with photocatalytic activity, film strength and high transmittance (without interference color).

【0072】実施例3 先ず、図3に一部切り欠き断面的に示すハロゲン電球を用意した。 [0072] Example 3 was first prepared partially cutaway halogen bulb shown sectionally in FIG. 図3において、4は石英ガラスから成るバルブ、5は前記バルブ4の圧潰封止部、5a,5bは前記圧潰封止部5に気密に埋設された一対の導入リード線(電気導入手段)、6a,6bは前記導入リード線5a,5bに一端が接続する内導体、7は前記内導体6a,6b間に装架されたタングステンコイルフィラメント、8は前記導入リード線5a,5bに電気的に接続しながら圧潰封止部5に装着された口金である。 3, the valve made of quartz glass 4, 5 crush seal portion of the valve 4, 5a, 5b of the pair of introduction lead in hermetically to the pinch sealing portion 5 (electric introducing means), 6a, inner conductors 6b is to be connected at one end to the introduction lead wire 5a, 5b, 7 is the inner conductor 6a, mounted tungsten coil filament between 6b, 8 is the introduction lead wire 5a, electrically to 5b a mouthpiece attached to the pinch seal portion 5 while connected.

【0073】一方、テトライソプロピルチタネートを有機溶媒に溶解させ、テトライソプロピルチタネート含有量 2〜10質量%、粘度約2.0 cps の溶液を調製した。 [0073] On the other hand, tetraisopropyl titanate is dissolved in an organic solvent, tetraisopropyl titanate content 2-10 wt%, to prepare a solution having a viscosity of about 2.0 cps. さらに、前記テトライソプロピルチタネート溶液に、平均粒径 5nmの TiO 2超微粉末(特にアナターゼを主成分としたものが好ましい)を添加・懸濁液化した。 Furthermore, the tetraisopropyl titanate solution was added, the suspension of the average particle diameter 5 nm TiO 2 ultrafine powder (especially preferably those composed mainly of anatase).

【0074】次に、前記ハロゲン電球を、前記溶液・懸濁液に浸漬してから所定速度で引上げ、乾燥後、空気中,約 700℃で 5分間焼成して、前記石英バルブ3の外表(外周)面に、厚さ 0.2μm 程度の TiO 2膜(光触媒膜)9を形成した。 Next, the halogen bulb, said pulling at a predetermined speed after immersion in the solution-suspension, after drying, was calcined in an air at about 700 ° C. 5 min, external surface of the quartz bulb 3 ( on the outer circumferential) surface, to form a TiO 2 film (photocatalytic film) 9 having a thickness of about 0.2 [mu] m. このようにして、石英バルブ4の外表(外周)面に設けた厚さ 0.2μm 程度の TiO 2膜9 In this way, the quartz tube external surface 4 (outer peripheral) having a thickness of about 0.2μm provided on surfaces of the TiO 2 film 9
は、前記ハロゲン電球内で生じ、石英バルブ4壁を透過して外表(外周)面に到達した紫外線の約70%を透過しており、この紫外線や光の透過によって、前記 TiO 2膜9は光触媒として活性な機能・作用を呈することが確認された。 Is caused within the halogen bulb is transmitted through the quartz tube 4 walls have been transmitted through about 70% of ultraviolet rays reaching the external surface (outer peripheral) surface, the transmission of this ultraviolet radiation or light, the TiO 2 film 9 to exhibit activity functions and act as a photocatalyst was confirmed. すなわち、有機ガストしてアセトアルテヒド濃度(1300 ppm)の雰囲気下で、前記ハロゲンラ電球を点灯し、点灯時間の経過に伴うアセトアルテヒド濃度の変化・低減を測定したところ、前記実施例1の場合と同様にすぐれた光触媒作用が認められた。 That is, in an atmosphere of acetoacetic Arte hydrate concentration in the organic gust (1300 ppm), the Harogenra bulb lights, were measured change and reduction of acetoacetic Arte hydrate concentration with the elapse of the lighting time of the Example 1 photocatalytic effect excellent as in the case were observed. また、このハロゲン電球は、前記 TiO 2膜(光触媒膜)が光学膜を成しており、良好な帯電防止性を有しているため、雰囲気中の細かい塵埃などの付着も回避され、表面が清浄さを維持していた。 Further, the halogen bulb, said has a TiO 2 film (photocatalytic film) forms an optical film, because it has a good antistatic property, adhesion of such fine dust in the atmosphere is also prevented, the surface I had to maintain the cleanliness.

【0075】なお、前記構成において、石英バルブ4の外表(外周)面と TiO 2膜(光触媒膜)9との間に SiO [0075] In the above configuration, SiO between the quartz external surface of the valve 4 (the outer circumference) surface and TiO 2 film (photocatalytic film) 9
2を介在させた場合は、光触媒活性,膜強度および高い透過率(干渉色のない)を兼備した光触媒膜を有するハロゲン電球として機能することを確認した。 If is interposed 2, it was confirmed to function as a halogen bulb having photocatalytic activity, film strength and high transmittance photocatalytic film having both (without interference color).

【0076】実施例4 図4に断面的に示す管形ハロゲン電球を用意した。 [0076] was prepared tubular halogen bulb shown sectionally in Example 4 FIG. 図4 Figure 4
において、10は石英ガラスから成る管形バルブ、11は前記管形バルブ10の圧潰封止部、 12a, 12bは前記圧潰封止部11に気密に埋設された一対の導入リード線(電気導入手段)、13は前記導入リード線 12a, 12b間に装架されたフィラメントである。 In, tubular valve made of quartz glass 10, 11 pinch sealed portion of the tubular valve 10, 12a, 12b are a pair of introducing lead in hermetically to the pinch seal portion 11 (electrically introduction means ), 13 is a filament which is mounted between the introduction leads 12a, 12b. ここで、フィラメント13は発光部 13aおよび非発光部 13bで構成され、サポーター 1 Here, the filament 13 is constituted by the light emitting portion 13a and the non-light emitting portion 13b, supporter 1
3cによって管形バルブ10内壁面に非接触に支持されている。 It is supported by a non-contact manner tubular valve 10 in the wall by 3c. また、14は接点 14aを有するベース部で、前記圧潰封止部11に気密に埋設されたモリブデン箔 12a′, 12 Further, 14 is a base portion having a contact 14a, the pinch seal portions 11 hermetically to molybdenum foils 12a ', 12
b′を介して、導入リード線 12a, 12bに電気的に接続されている。 Through b ', introducing lead 12a, and is electrically connected to 12b.

【0077】一方、前記実施例3の場合と同一組成のテトライソプロピルチタネートおよびTiO 2超粉末の溶液・懸濁液を用意し、この溶液・懸濁液に、前記ハロゲン電球を浸漬してから所定速度で引上げ、乾燥後、空気中,約 700℃で 5分間焼成して、前記石英バルブ10の外表(外周)面に厚さ0.25μm 程度の TiO 2膜14を形成した。 [0077] On the other hand, providing a solution-suspension of tetraisopropyl titanate and TiO 2 super powder of the same composition as in Example 3, the solution-suspension, given after immersing the halogen bulb pulling at a rate, after drying, it was calcined in an air at about 700 ° C. 5 minutes to form a TiO 2 film 14 having a thickness of about 0.25μm to external surface (outer peripheral) surface of the quartz bulb 10. このようにして、石英バルブ10の外表(外周)面に設けた厚さ0.25μm 程度の TiO 2膜15は、前記ハロゲン電球内で生じ、石英バルブ10壁を透過して外表(外周) In this way, the external surface (outer peripheral) thick is provided on the surface 0.25μm approximately TiO 2 film 15 of the quartz bulb 10 is caused in the halogen lamp, the outer table is transmitted through the quartz bulb 10 wall (outer circumference)
面に到達した紫外線の約70%を透過しており、この紫外線や光の透過によって、前記 TiO 2膜15は光触媒として活性な機能・作用を呈することが確認された。 And transmits about 70% of ultraviolet rays reaching the surface, the transmission of this ultraviolet radiation or light, the TiO 2 film 15 to exhibit the active functions and act as a photocatalyst was confirmed. すなわち、有機ガストしてアセトアルテヒド濃度(1300 ppm) That is, aceto Alte hydrate concentration in the organic gust (1300 ppm)
の雰囲気下で、前記ハロゲンラ電球を点灯し、点灯時間の経過に伴うアセトアルテヒド濃度の変化・低減を測定したところ、前記実施例1の場合と同様に、すぐれた光触媒作用が認められた。 Under the atmosphere, lights the Harogenra bulb, were measured change and reduction of acetoacetic Arte hydrate concentration with the elapse of the lighting time, as in the case of Example 1, excellent photocatalytic activity was observed.

【0078】また、この管形のハロゲン電球16は、前記 [0078] In addition, halogen bulbs 16 of the tubular, the
TiO 2膜(光触媒膜)15が光学系の膜を成しており、良好な帯電防止性を有しているため、雰囲気中の細かい塵埃などの付着も回避され、表面が清浄さを維持していた。 And TiO 2 film (photocatalytic film) 15 forms a film of the optical system, because it has a good antistatic property, is avoided adhesion of such fine dust in the atmosphere, the surface maintains a of cleanliness which was.

【0079】さらに、上記構成の管形ハロゲン電球16 [0079] Further, tubular halogen bulb 16 having the above structure
を、両端側に電気的な接続装着部を備えたリフレクター And with an electrical connection mounting portion on both ends reflector
17に組み込み、図5に断面的に示すような、複写機用の読取り光源部17を作成した。 Built in 17, as shown in cross section in Figure 5, to create a reading light source section 17 of the copying machine. そして、この複写機用の読取り光源部17を、図6に要部構成の概略を断面的に示すごとく、複写機の原稿読取り部に装着し、複写機としての機能評価を行った。 Then, the reading light source section 17 for the copying machine, as shown schematically in main configuration in FIG. 6 in cross section, attached to the document reading unit of the copying machine were functional evaluation as a copier. 図6において、18は露光用ユニットで、前記読取り光源部17、原稿台ガラス19, 反射鏡20 6, 18 in the exposure unit, the reading light source unit 17, the platen glass 19, the reflecting mirror 20
など構成されている。 It is configured such. また、21は前記反射鏡20で反射導光される光を集光する指定レンズユニット、22は指定レンズユニット21からの光を受ける受光器、23は指定レンズユニット21および受光器22を内装する暗室である。 Further, designated lens unit for focusing light reflected guided by the reflection mirror 20 is 21, 22 is the light receiver 23 for receiving light from the designated lens unit 21 to interior designated lens unit 21 and the light receiver 22 is a dark room.

【0080】前記複写機について、繰り返し所要の複写操作を行ったところ、前記露光ユニット18の管形ハロゲン電球16表面は、清浄さが保持されており、信頼性の高い露光光源として機能することが確認された。 [0080] For the copying machine was subjected to repeated required copying operations, tubular halogen bulb 16 surface of the exposure unit 18, cleanliness is held, to function as a reliable exposure source confirmed. これは、 this is,
露光ユニット18部における雰囲気に浮遊する汚染などの原因となる有機物が、管形ハロゲン電球16表面の光り触媒膜15に接触することによって、容易に酸化・分解して除去されるためである。 Organic matter causing pollution floating in the atmosphere in the exposure unit 18 parts of, by contacting the catalyst film 15 light of tubular halogen bulb 16 surface is to be removed easily oxidized and decomposed. 上記実施例では、管形ハロゲン電球16を露光ユニット18の光源として組み込んだ複写機について説明したが、トナー像を記録紙などに転写した後の、定着用ユニットの熱定着光源として組み込んでも、同様の作用・効果が認められる。 In the above embodiment has been described incorporating copier tubular halogen lamp 16 as a light source of the exposure unit 18, after transferring the toner image such as a recording paper, be incorporated as a thermal fixing the light source of the fixing unit, the same action and effect of is observed.

【0081】前記構成において、管形ハロゲン電球16の外表(外周)面と TiO 2膜(光触媒膜)15との間に SiO [0081] SiO in the structure, between the external surface (outer peripheral) surface and TiO 2 film (photocatalytic film) 15 of the tubular halogen bulb 16
2を介在させた場合は、光触媒活性,膜強度および高い透過率(干渉色のない)を兼備した光触媒膜を有する管形ハロゲン電球として機能することを確認した。 If is interposed 2, was confirmed to function as a tubular halogen bulb having photocatalytic activity, the photocatalyst film having both film strength and high transmittance (without interference color).

【0082】なお、本発明は前記実施例に限定されるものでなく、発明の趣旨を逸脱しない範囲でいろいろの変形を採り得る。 [0082] The present invention is not limited to the above embodiments, it can take a variety of modifications without departing from the spirit of the invention. たとえば、上記では白熱電球として、一般的なハロゲン電球、事務機用などの管形ハロゲンランプを例示したが、車輛前照灯用のハロゲン電球、照明装置などであってもよい。 For example, the incandescent light bulb in the above, typical halogen bulb, is exemplified tubular halogen lamps, such as for office equipment, vehicle headlights halogen bulbs, may be a lighting device.

【0083】実施例5 この実施例は3波長発光形の直管形蛍光ランプの場合であり、図7 (a)は直管形蛍光ランプの斜視図、図7 (b) [0083] Example 5 This example is the case of the straight tube fluorescent lamp of three-wavelength emission type, 7 (a) is a perspective view of a straight tube fluorescent lamp, and FIG. 7 (b)
は一部を拡大した断面図、図8は直管形蛍光ランプを用いた照明器具の概略構成を示す側面図である。 Enlarged sectional view of a part, FIG. 8 is a side view showing a schematic configuration of an illumination fixture using a straight tube fluorescent lamp.

【0084】蛍光ランプ本体は、 JIS規格でFL40SSと表示される定格電力37 Wの低圧水銀蒸気放電ランプであり、24は直管形を成す透光性気密容器としての発光管であって、この発光管24は、バルブ外径が28mm、管長1198 [0084] Fluorescent lamp body is a low-pressure mercury vapor discharge lamp having a rated power of 37 W, which is displayed FL40SS in JIS standard, 24 is a light emitting tube of the light-transmissive airtight envelope forming a straight tube, the light emitting tube 24, the valve outer diameter of 28mm, tube length 1198
mm程度の大きさをなし、 300nm以上の紫外線を透過するガラス、たとえばソーダライムガラスにて形成されている。 None of the order of magnitude of mm, are formed by glass which transmits more UV 300 nm, for example soda-lime glass. そして, この発光管24の両端部はステム25,25により封止されており、これらステム25,25にはリード線2 Then, both ends of the arc tube 24 is sealed with stems 25, 25, leads to these stems 25, 25 2
6,26が気密に貫通されている。 6 and 26 have been through in an air-tight. また、前記リード線2 In addition, the lead wire 2
6,26には、タングステンワイヤなどにより2重コイルに形成された電極手段としてのフィラメント電極27,27 The 6 and 26, the filament electrodes of the electrode means formed on the double coil due tungsten wire 27 and 27
が取付けられており、図示しないエミッタが塗布されている。 It is attached, an emitter (not shown) is applied.

【0085】さらに、前記発光管24の外周面(外表面) [0085] Further, the outer peripheral surface of the arc tube 24 (outer surface)
には全面に亘り光触媒膜28が形成されている。 Photocatalytic film 28 over the entire surface is formed in the. ここで、 here,
光触媒膜28は、たとえば平均粒径 5〜 7nmのアナターゼ型結晶 TiO 2微粒子 28aおよび平均粒径 5nm未満の TiO Photocatalyst film 28, for example, an average particle diameter. 5 to 7 nm of anatase TiO 2 particles 28a and the average particle size less than 5nm of TiO
2超微粒子 28bの混合系で形成されている(超微粒子相 2 is formed of a mixed system of ultrafine particles 28b (ultrafine particle phase
28bに結晶性微粒子 28aが分散した状態)。 A state in which crystal particles 28a are dispersed in 28b). つまり、前記実施例1の場合と同様の条件で調製した溶液・懸濁液に、前記蛍光ランプを浸漬して外周面(外表面)に塗布し、乾燥( 150℃で約 5分間保持)させることによって、耐剥離性が良好な平均 0.2μm 厚み光触媒膜27を発光管24の外表面に形成する。 That is, wherein when a solution-suspension prepared under the same conditions as in Example 1, the fluorescent lamp was immersed was applied to the outer peripheral surface (outer surface), causing dried (0.99 ° C. for about 5 minutes hold) it allows the peeling resistance that forms a favorable average 0.2μm thickness photocatalytic film 27 on the outside surface of the arc tube 24.

【0086】また、この実施例では、水銀から放出された紫外線により励起されて可視光に変換する蛍光体層29 [0086] The phosphor layer 29 is converted into visible light in this embodiment, it is excited by ultraviolet rays emitted from a mercury
を、たとえば3波長発光形蛍光体、および水銀から放出された紫外線により励起されて 300nm〜 400nmの紫外線を発する蛍光体の混合体で構成した。 , For example 3-wavelength luminescent type phosphors, and was composed of a mixture of phosphors that emit ultraviolet excited by 300nm to 400 nm by the emitted UV mercury. ここで、3波長発光形蛍光体はしては、たとえば 610nm付近にピーク波長を有する赤系蛍光体として Y 2 O 3 :Eu、 540nm付近にピーク波長を有する緑系蛍光体として(La,Ce,Tb)P Here, 3 are wavelength emission type fluorescent material, for example Y 2 O 3 as the red-based phosphor having a peak wavelength around 610 nm: Eu, as a green phosphor having a peak wavelength around 540 nm (La, Ce , Tb) P
O 4 、 450nm付近にピーク波長を有する青系蛍光体としてBaMg 2 Al 16 O 27 :Euが用いられている。 O 4, 450 nm BaMg as blue phosphor having a peak wavelength around 2 Al 16 O 27: Eu is used. 紫外線発光蛍光体としては、ユーロピウム付活アルカリ土類金属硼酸塩、鉛付活珪酸塩、ユーロピウム付活アルカリ土類金属アルミン酸塩、またはこれらにハロゲンが添加された蛍光体の少なくとも1種類以上が用いられている。 The ultraviolet light emitting phosphor, europium-activated alkaline earth metal borates, Namarizukekatsu silicate, europium-activated alkaline earth metal aluminate or at least one or more of these phosphors halogen is added, It has been used. ユーロピウム付活アルカリ土類金属硼酸塩としては、たとえば The europium-activated alkaline earth metal borate salt, for example,
368nmにピーク波長をもつSr,B 4 ,O 7 :Eu 2+が有効であり、鉛付活珪酸塩としては 370nmにピーク波長をもつ(Ba,Sr,Mg) 3 Si 2 O 7 :Pb 2+や350nmにピーク波長をもつBaSi 2 O 5 :Pb 2+などが好適である。 Sr having a peak wavelength in 368nm, B 4, O 7: Eu 2+ is valid, the Namarizukekatsu silicate having a peak wavelength of 370nm (Ba, Sr, Mg) 3 Si 2 O 7: Pb 2 + and BaSi having a peak wavelength in the 350 nm 2 O 5: like Pb 2+ are preferred. この実施例では、紫外線発光蛍光体としては、Sr,B 4 ,O 7 :Eu 2+を用いており、その混合比は蛍光体層28の 1〜10質量%の割合である。 In this embodiment, the ultraviolet light emitting phosphor, Sr, B 4, O 7 : uses a Eu 2+, the mixing ratio is the ratio of 1 to 10 wt% of the phosphor layer 28.

【0087】さらに、前記発光管24内には所定量の水銀とアルゴンガスなどの不活性ガスが封入されており、また、発光管24の端部には口金ピン30を突設させた口金31 [0087] Furthermore, the the light emitting tube 24 and an inert gas, such as a predetermined amount of mercury and argon gas is sealed, also, die 31 is projected the base pins 30 at the ends of the arc tube 24
が被着されている。 There has been deposited. そして、前記口金ピン30は前記リード線26,26を介してフィラメント電極(放電電極)27に接続されている。 Then, the base pins 30 are connected to the filament electrode (discharge electrode) 27 through the lead wires 26, 26.

【0088】前記構成の蛍光ランプ32を、たとえば図8 [0088] The fluorescent lamp 32 of the arrangement, for example, FIG. 8
に示すような照明器具本体に取り付けて照明器具を構成することができる。 It is possible to construct a lighting fixture mounted in the luminaire main body, as shown in. すなわち、図8において33は天井直付け形照明器具の本体であり、この照明器具本体33の長手方向両端にはランプソケット34,34が相互に対向して配置されている。 That is, 33 in FIG. 8 is a main body of the headlining luminaires, the lamp socket 34, 34 are arranged opposite each other at both ends in the longitudinal direction of the luminaire body 33. これらソケット34,34間に、前記蛍光ランプ32を、その口金31,31の口金ピン30を係合させて取り付けられ、照明器具を構成している。 Between these sockets 34 and 34, wherein the fluorescent lamp 32, mounted by engaging the base pins 30 of the cap 31, constitutes a lighting fixture. なお、照明器具本体33には、蛍光ランプ32を点灯させるための安定器 Note that the luminaire body 33, ballast for lighting the fluorescent lamp 32
35を含む点灯回路が収容されており、前記蛍光ランプ32 Lighting circuit comprising 35 have been accommodated, the fluorescent lamp 32
は安定器35を介して点灯される。 It is turned through the ballast 35.

【0089】次に、前記構成の蛍光ランプおよび照明器具の作用を説明する。 [0089] Next, the operation of the fluorescent lamp and lighting equipment of the configuration.

【0090】蛍光ランプ32を点灯すると電極27,27間のアーク放電により水銀蒸気が水銀特有の 185nmおよび 2 [0090] When the fluorescent lamp 32 by arc discharge between the electrodes 27, 27 mercury vapor mercury specific 185nm and 2
54nmの紫外線を放出し、この紫外線は蛍光体層29を励起する。 Ultraviolet release of 54 nm, the ultraviolet light excites the phosphor layer 29. この場合、蛍光体層29は3波長発光形蛍光体および 300nm〜 400nmの紫外線を発する蛍光体を混合体で形成されていので、3波長発光形蛍光体が3波長域にピーク波長を有する可視光を発するとともに、紫外線発光蛍光体が 300nm〜 400nmの紫外線を発する。 In this case, since the phosphor layer 29 is formed of a phosphor mixture that emits ultraviolet 3 wavelength light emitting fluorescent substance and 300nm to 400 nm, a visible light three-wavelength emission type fluorescent material having a peak wavelength in three-wavelength together emit ultraviolet light emitting phosphor emits ultraviolet 300nm to 400 nm. そして、3波長発光形蛍光体によって発せられた可視光は発光管24の壁を透過し、 TiO 2混合膜28を透過して外部に放出され、所定の可視光量が得られので、所定の明るさに照らすことができる。 Then, 3 visible light emitted by the wavelength-emitting fluorescent substance is transmitted through the wall of the arc tube 24, passes through the TiO 2 mixed film 28 is released to the outside, than the predetermined visible amount of light is obtained, predetermined brightness it can be illuminated to be.

【0091】一方、紫外線発光蛍光体が 300nm〜 400nm [0091] On the other hand, the ultraviolet light emitting phosphor 300nm~ 400nm
の紫外線を発するので、この紫外線は発光管24の壁を透過し、 TiO 2を主成分とする光触媒膜28に達する。 Since emits UV, the UV light passes through the wall of the arc tube 24, reaches the photocatalyst film 28 composed mainly of TiO 2. このためTiO 2は紫外線を吸収し、光触媒作用で TiO 2の内部に電子とホールを生させるとともに、このホールを移動させて表面において電子移動反応を起こし、このホールがほぼバンドギャップ(3.0 eV)分のエネルギーだけ電子を引き抜く力、すなわち酸化力をもち、表面に付着した物質を酸化させる。 Therefore TiO 2 absorbs ultraviolet, causes produce electrons and holes in the interior of the TiO 2 in the photocatalytic action, cause electron transfer reaction at the surface by moving the hole, the hole is approximately the band gap (3.0 eV) min energy only extract electrons force, i.e. having oxidizing power to oxidize the substance adhering to the surface. したがって、環境を汚染している臭気,有機物などを、より効率的に酸化・分解するように機能した。 Thus, odors which pollute the environment, organics, etc., and functions to oxidize and decomposed more efficiently. たとえば、臭気(アセトアルデヒド濃度 For example, the odor (acetaldehyde concentration
1300 ppm)を有する密閉型の雰囲気下で、前記照明装置を点灯して、点灯時間とアセトアルデヒド濃度の変化を測定したところ、 1時間後 300 ppm,24時間後 5 ppm程度とすぐれた触媒機能を呈することかせ確認された。 Under an atmosphere of sealed with 1300 ppm), lit the illumination device was measured for changes in lighting time and acetaldehyde concentration, 1 hour after 300 ppm, 24 hours after 5 ppm about the excellent catalytic function was either to confirm that the exhibit.

【0092】上記のように、結晶性 TiO 2超微粒子混合系を主成分とした光触媒膜28は、表面に付着した物質を効率よく酸化・分解させることができため、たとえばメチルメルカプタン、硫化水素などの硫黄化合物、アンモニアなどの含窒素化合物、アルデヒド類などの分解が促され、臭気物質の分解による消臭作用も容易に奏する。 [0092] As described above, the photocatalyst film 28 composed mainly of crystalline TiO 2 ultrafine particles mixed system, since it is possible to efficiently oxidized and decomposed the substance adhering to the surface, such as methyl mercaptan, such as hydrogen sulfide sulfur compounds, nitrogen-containing compounds such as ammonia, the decomposition of such aldehydes is accelerated, also easily Kanade deodorizing effect due to decomposition of odorous substances.
また、同じく強い酸化作用により、細菌を含む雑菌の殺菌作用、汚れなどの浄化、たとえば煙草のヤニを分解するなどの作用も容易に生じる。 Also, similarly by a strong oxidizing action, bactericidal action of bacteria, including bacteria, purification of dirt, also occurs easily effect, e.g. decomposing tar cigarette. つまり、前記蛍光ランプ In other words, the fluorescent lamp
10によれば、照明用光源として多量の可視光を発するとともに、表面に塗布した TiO 2膜28に対する紫外線発生源としても機能する。 According to 10, together with the emit large quantities of visible light as the illuminating light source, also serves as an ultraviolet source for the TiO 2 film 28 coated on the surface. したがって、住宅やオフィスなどの居住空間の照明および空気浄化を単一の蛍光ランプで実現できることになり、快適な居住環境を得ることができる。 Accordingly, in the lighting and air purification of residential space, such as homes and offices can be realized with a single fluorescent lamp can be obtained a comfortable living environment.

【0093】また、蛍光ランプの外表面に、ほこりや, [0093] In addition, the outer surface of the fluorescent lamp, and dust,
煙草のヤニ,油脂成分などが堆積しようとしても、 TiO Tobacco tar, even if an attempt such as oil and fat component is deposited, TiO
2微粒子混合系膜28の酸化分解作用によりこれら物質の付着を防止するから、蛍光ランプの光束低下を防止することができ、蛍光ランプを拭くなどの掃除が不要であり、メンテナンスも容易になる。 Since to prevent adhesion of these substances by oxidative decomposing action of the 2-particulate admixture based film 28, it is possible to prevent a brightness decrease of the fluorescent lamp, to clean such wiping fluorescent lamp is unnecessary, it is easy maintenance.

【0094】前記蛍光ランプの構成において、発光管24 [0094] In the configuration of the fluorescent lamp, the arc tube 24
の外表(外周)面と TiO 2膜(光触媒膜)28との間に S S between the external surface (outer peripheral) surface of the a TiO 2 film (photocatalytic film) 28
iO 2を介在させた場合は、光触媒活性,膜強度および高い透過率(干渉色のない)を兼備した光触媒膜を有する蛍光ランプとして機能することを確認した。 If the iO 2 is interposed, was confirmed to function as a fluorescent lamp having photocatalytic activity, the film strength and high transmittance (without interference color) photocatalyst film having both.

【0095】実施例6 曲成,排気,封止までの工程を経た環状の蛍光ランプを用意し、この環状の蛍光ランプを封止部を上方として、 [0095] Example 6 the bent, exhaust, prepared fluorescent lamp annular manufactured through the preceding steps seal, a seal as above the annular fluorescent lamp,
イソプロピルチタネート溶液に、平均粒径 5〜7nmの結晶型 TiO 2超微粒子を分散させた分散液に浸漬,取り出してから、前記封止部を下方に反転させた状態で、 150 Isopropyl titanate solution, immersed in a dispersion prepared by dispersing the crystal form TiO 2 ultrafine particles having an average particle diameter of 5 to 7 nm, the removed, in an inverted state of the said sealing portion downward, 150
℃で約 5分間保持して環状の蛍光ランプ外周面に結晶型の TiO 2微粒子混合系の光触媒膜を形成した。 ℃ for about 5 minute hold to the formation of the photocatalytic film of the annular fluorescent lamp outer peripheral surface TiO 2 particles mixed system of crystalline form.

【0096】この環状蛍光ランプの外周面に設けた光触媒膜の厚さは、曲成部の外周側表面での平均値 0.2μm [0096] The thickness of the photocatalyst film formed on the outer peripheral surface of the annular fluorescent lamp, the average value 0.2μm on the outer peripheral side surface of the curved portion
,曲成部の内周側表面での平均値 0.1μm ,封止部側での平均値 0.1μm であった。 , The average value 0.1μm on the inner circumferential surface of the curved portion, and an average value 0.1μm at the sealing portion.

【0097】次に、前記光触媒膜を発光管外周面に設けた環状蛍光ランプを、対応する照明器具に組み込み、実施例1の場合と同様に脱臭効果を検討したところ、実施例1の場合と同様な作用効果が認められた。 Next, an annular fluorescent lamp provided with the photocatalyst layer to the light emitting tube outer peripheral surface, embedded in a corresponding luminaire, was examined in the same manner as in deodorizing effect in Example 1, in the case of Example 1 same effect was observed.

【0098】また、前記環状蛍光ランプ外周面の光触媒膜に、一定量の煙草のヤニを全面的に塗布し、無色になる間での時間で光触媒作用を比較したところ、熱の影響を受け易い封止部(電極近傍)における光触媒作用は、 [0098] Further, the photocatalyst film of said annular fluorescent lamp outer peripheral surface, entirely coated with tar certain amount of tobacco, were compared photocatalysis in time while the colorless, susceptible to heat photocatalysis in the sealing portion (the vicinity of the electrodes) is
他の領域の約 2倍であった。 Was approximately twice that of the other regions. 上記では、環状蛍光ランプの場合を説明したが、図9 (a)に平面的に示すようなU In the above description, the case of annular fluorescent lamp, as shown in a plan view in FIG. 9 (a) U
字型蛍光ランプ,図9 (b)もしくは図9 (c)に斜視的に示すようなW−U字型蛍光ランプの発光管外周面に、前記に準じてそれぞれ光触媒膜を形成・具備させた場合も同様の作用効果が認められた。 Shaped fluorescent lamp, the arc tube outer peripheral surface of the W-U-shaped fluorescent lamp shown in perspective in FIG. 9 (b) or FIG. 9 (c), the respectively according to the to form, comprising a photocatalyst film If it observed the same effect as well.

【0099】なお、本発明は上記実施例の構造に制約されるものではない。 [0099] The present invention is not to be restricted to the structure of the above embodiment. たとえば、上記実施例では可視光を発する蛍光体として3波長発光形蛍光体を用いたが、本発明はこれに限らず、ハロりん酸カルシウム蛍光体や、 For example, in the above embodiment, using a three-wavelength emission type fluorescent material as a phosphor which emits visible light, the present invention is not limited to this, and halo calcium phosphate phosphor,
その他蛍光ランプに使用されている通常の蛍光体であってもよい。 It may be a conventional phosphor used in other fluorescent lamps. また、蛍光ランプは直管形蛍光ランプ、環形蛍光ランプ、U字型、W字型に限らず、H字、鞍形などのような屈曲形蛍光ランプなどであってもよい。 The fluorescent lamp straight tube fluorescent lamps, circular fluorescent lamps, U-shaped, not limited to the W-shape, H-shape, it may be a bent fluorescent lamp, such as saddle-shaped.

【0100】実施例7 図10は、紫外線を放出する光源、たとえば高圧水銀蒸気放電灯に制光体(もしくは包囲体)を組み合わせた照明器具の概略構成を示す断面図である。 [0100] Example 7 FIG. 10 is a sectional view showing a light source, for example, a schematic configuration of a lighting apparatus that combines Seihikaritai (or enclosure) to the high-pressure mercury vapor discharge lamp which emits ultraviolet light. 図10において、36 10, 36
は電源側に一端が接続する外部リード部37およびソケット部38などを装着した器具本体である。 Is a fixture main body equipped with an external lead portion 37 and the socket portion 38 at one end to the power supply side are connected. また、39は前記器具本体36のソケット部38に装着された高圧水銀蒸気放電灯、40は前記高圧水銀蒸気放電灯39に沿って配置内装された反射板であり、この反射板40は前記器具本体36に取り付けられた支持枠41によって支持・固定されている。 Further, 39 high-pressure mercury vapor discharge lamp mounted in the socket portion 38 of the instrument body 36, 40 is a reflective plate disposed interior along the high-pressure mercury vapor discharge lamp 39, the reflector 40 is the instrument It is supported and fixed by a supporting frame 41 which is attached to the body 36. さらに、42は前記器具本体36と組み合わせられて包囲体を形成する紫外線透過性のグローブ、たとえば石英ガラス製のグローブであり、この外表面に光触媒膜43が設けられている。 Further, 42 the instrument body 36 and combined UV permeable forming an enclosure with the glove, for example, a quartz glass globe, the photocatalytic film 43 is provided on the outer surface. ここで、前記光触媒膜43は、実施例3 Here, the photocatalyst film 43, Example 3
の場合と同一組成のテトライソプロピルチタネートおよび TiO 2超粉末の溶液・懸濁液液を、前記石英ガラス製グローブ42の側外表面に塗布,乾燥後、空気中,約 700 Tetraisopropyl titanate and TiO 2 super powder solution-suspension liquid of the same composition as in, coated on the side outside surface of the quartz glass globe 42, after drying in air, about 700
℃で 5分間焼成して、厚さ 0.3μm 程度の膜厚に形成されている。 ℃ and calcined 5 minutes, and is formed to a thickness of about thickness 0.3 [mu] m.

【0101】このように構成された照明器具は、高圧水銀蒸気放電灯39の点灯で、高圧水銀蒸気放電灯39から放出された紫外線が石英ガラス製グローブ42を透過し、外表(外周)面に到達して前記光触媒膜43は、光触媒として活性な機能・作用を呈することが確認された。 [0102] configured luminaire in this way, by lighting the high-pressure mercury vapor discharge lamp 39, the ultraviolet light emitted from the high-pressure mercury vapor discharge lamp 39 is transmitted through the quartz glass globe 42, the outer table (outer peripheral) surface the photocatalyst film 43 is reached, to exhibit activity functions and act as a photocatalyst was confirmed. すなわち、有機ガストしてアセトアルテヒド濃度(1300 ppm) That is, aceto Alte hydrate concentration in the organic gust (1300 ppm)
の雰囲気下で、前記照明器具を点灯し、点灯時間の経過に伴うアセトアルテヒド濃度の変化・低減を測定したところ、すぐれた光触媒作用が認められた。 Under the atmosphere, it lights the lighting fixture, the measured change and reduction of acetoacetic Arte hydrate concentration over the course of a lighting time, excellent photocatalytic activity was observed.

【0102】前記照明器具の構成において、石英ガラス製グローブ42の外表(外周)面と TiO 2膜(光触媒膜) [0102] In the configuration of the luminaire, external surface of a quartz glass globe 42 (outer circumferential) plane and TiO 2 film (photocatalytic film)
43との間に SiO 2を介在させた場合は、光触媒活性,膜強度および高い透過率(干渉色のない)を兼備した光触媒膜を有する高圧水銀蒸気放電灯として機能することを確認した。 If are interposed SiO 2 between 43 and was confirmed to function as a high-pressure mercury vapor discharge lamp having photocatalytic activity, the film strength and high transmittance (without interference color) photocatalyst film having both.

【0103】また、図11に透視的に示すごとく、反射膜 [0103] Further, as shown in phantom in FIG. 11, the reflective film
44付きのレフランプのバルブ45の頂面に、前記手法に準じて光触媒膜46を形成して、照明器具に装着して点灯評価を行ったところ、光触媒活性,膜強度および高い透過率を兼備した光触媒膜を有するレフランプとして機能することを確認した。 The top surface of the valve 45 of Refuranpu with 44, to form a photocatalytic film 46 in accordance with the above method, was subjected to lighting evaluated by mounting the lighting fixtures, and combines the photocatalytic activity, film strength and high transmittance It was confirmed to function as a Refuranpu having photocatalytic film. なお、図11において、46は E型口金、47はフィラメントをそれぞれ示す。 In FIG. 11, 46 indicates an E-type cap, 47 filaments each.

【0104】 [0104]

【発明の効果】請求項1および請求項2の発明によれば、構成を簡略化しながら、光触媒膜の活性および硬度が高く、かつ支持基体に対する密着力もしくは接着力も高くて、耐剥離性などすぐれているため、長期間に亘って所要の光触媒作用を呈する外界清浄化用の触媒膜が提供される。 Effects of the Invention According to the invention of claim 1 and claim 2, while simplifying the structure, high activity and hardness of the photocatalyst film, and with higher adhesion or adhesion to the supporting substrate, good like peeling resistance and for that, the catalyst layer for external cleaning exhibiting the required photocatalysis for a long time is provided.

【0105】請求項3の発明によれば、光触媒膜の薄膜化および良好な透過性化を図りながら、一方では、光触媒膜の活性および硬度が高く、かつ支持基体に対する密着力もしくは接着力も高くて、耐剥離性などすぐれているため、長期間に亘って所要の光触媒作用を呈する外界清浄化用の触媒膜が提供される。 [0105] According to the invention of claim 3, while achieving thinning and good permeability of the photocatalyst film, on the one hand, the activity and the hardness of the photocatalyst film is high and with higher adhesion or adhesion to the supporting base , since the good like peeling resistance, the catalyst layer for external cleaning exhibiting the required photocatalysis for a long time is provided.

【0106】請求項4,請求項5および請求項6の発明によれば、白熱電球が光学的特性の良好な光源として機能しながら、一方では、点灯・使用雰囲気中の有機成分などを、長期間に亘って、安定的かつ容易に酸化・分解除去し得るので、殺菌もしくは減菌、臭気の除去(脱臭)などが要望される居住空間、たとえば病院用光源として有効な光源の提供が可能である。 [0106] Claim 4, according to the invention of claims 5 and 6, while an incandescent lamp functions as a good source of optical properties, on the one hand, the organic component in the lighting-use atmosphere, long over a period, so may stably and easily oxidized and decomposed and removed, the living space of sterilization or sterilization, removal of odor (deodorant), etc. is desired, for example is possible to provide a valid source as hospital source is there.

【0107】請求項7,請求項8,請求項9,請求項1 [0107] Claim 7, Claim 8, Claim 9, Claim 1
0,および請求項11の発明によれば、放電ランプが光学的特性の良好な光源として機能しながら、一方では、点灯・使用雰囲気中の有機成分などを長期間に亘って安定的、かつ容易に酸化・分解除去し得るので、殺菌もしくは減菌、臭気の除去(脱臭)などが要望される居住空間、たとえば病院用光源として有効な光源の提供が可能である。 0, and according to the invention of claim 11, while the discharge lamp acts as a good source of optical properties, on the one hand, stable over organic components in the lighting-use atmosphere a long time, and easy since capable of oxidizing, decomposing and removing, the living space of sterilization or sterilization, removal of odor (deodorant), etc. is desired, it is possible to provide effective light source, for example, as a hospital source.

【0108】請求項12,請求項13および請求項14の発明によれば、蛍光ランプが光学的特性の良好な光源として機能しながら、一方では、光触媒膜は剥離する恐れもないので、長期間に亘って殺菌、臭気の除去(脱臭)、有機物の酸化,分解など容易に行うことができる光源の提供が可能となる。 [0108] 12. According to the invention of claims 13 and 14, while function as a good source of the fluorescent lamp optical properties, on the one hand, since the photocatalytic film is also no risk of peeling, long term sterilization over the removal of odor (deodorant), the oxidation of organic matter, it is possible to provide a light source that can be carried like easily decomposed.

【0109】請求項15の発明によれば、一般照明用として機能しながら、前記請求項11〜12の発明で見られるような作用・効果を呈するので、その実用性がさらに助長される。 [0109] According to the invention of claim 15, with functions for general lighting, since exhibits operations and effects as found in the invention of claim 11 to 12, its utility is further promoted.

【0110】請求項16,請求項17,請求項18,請求項19 [0110] 16, 17, claim 18, claim 19
および請求項20の発明によれば、照明器具に装着した光源が紫外線放射源として有効に機能する一方、点灯・使用雰囲気中の有機成分など長期間に亘って安定的、かつ容易に酸化・分解除去し得るので、殺菌もしくは減菌、 And According to the invention of claim 20, whereas a light source mounted on the luminaire to function effectively as a UV radiation source, stable, and easily oxidized and decomposed over a long period of time, such as an organic component in the lighting and use Atmosphere so can be removed, disinfection or sterilization,
臭気の除去(脱臭)などが要望される居住空間、たとえば病院用光源として有効な照明器具の提供が可能である。 Living space such as the removal of odor (deodorant) is desired, it is possible to for example provide effective luminaire as hospital source.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

【図1】本発明の光触媒体の一実施例を示す要部断面図。 Cross sectional view showing an embodiment of a photocatalyst of the present invention; FIG.

【図2】本発明の光触媒体の他の実施例を示す要部断面図。 Fragmentary cross-sectional view showing another embodiment of a photocatalyst of the present invention; FIG.

【図3】本発明の白熱電球の一実施例の構造を示す一部切り欠き断面図。 Figure 3 is a cross-sectional view partially cutaway showing the structure of an embodiment of the incandescent lamp of the present invention.

【図4】本発明の管型白熱電球の一実施例の構造を示す断面図。 Cross-sectional view showing the structure of an embodiment of a tubular incandescent lamp of the present invention; FIG.

【図5】本発明に係る照明器具の一実施例の構造を示す断面図。 Cross-sectional view showing the structure of an embodiment of a luminaire according to the present invention; FIG.

【図6】本発明に係る照明器具の応用例である複写機の要部構造を示す断面図。 Cross-sectional view showing the essential structure of a copying machine which is an application example of a lighting fixture according to the present invention; FIG.

【図7】(a)は本発明の蛍光ランプの一実施例の構造を示す一部切り欠き断面図、 (b)は一部拡大断面図。 7 (a) is a cross sectional view partially cutaway showing the structure of an embodiment of a fluorescent lamp of the present invention, (b) is a partially enlarged cross-sectional view.

【図8】本発明に係る照明器具の他の実施例の構造を示す側面図。 Figure 8 is a side view showing the structure of another embodiment of the luminaire according to the present invention.

【図9】(a), (b), (c)は本発明の蛍光ランプの他の変形例の構造を示す斜視図。 9 (a), (b), (c) is a perspective view showing a structure of another modification of the fluorescent lamp of the present invention.

【図10】本発明に係る照明器具のさらに他の実施例の概略構造を示す断面図。 Sectional view further showing the schematic structure of another embodiment of the luminaire according to the invention; FIG.

【図11】本発明に係る白熱電球の他の実施例の構造を示す透視図。 [11] a perspective view showing the structure of another embodiment of an incandescent lamp according to the present invention.

【符号の説明】 DESCRIPTION OF SYMBOLS

1……支持用の基体 2,9,15,28,43……光触媒膜 2a, 28a……光触媒作用を有する金属酸化物の結晶性微粒子(第1の微粒子) 2b, 28b……光触媒作用を有する金属酸化物相(第2の超微粒子領域) 3……支持用の基体と光触媒膜都の間に介挿した SiO 2 1 ...... supporting substrate 2,9,15,28,43 ...... photocatalyst film 2a, 28a crystalline particles (first particles) of ...... light metal oxides having a catalytic action 2b, and 28b ...... photocatalytic activity metal oxide phase SiO 2 having interposed a (second ultrafine particles region) 3 ...... between the substrate and the photocatalyst film Prefecture for support with
層 4,10,24……透光性気密容器(発光管,ガラスバルブ) 33……照明器具本体 40……紫外線を放出する光源 42……包囲体 Layers 4,10,24 ...... light-transmissive airtight envelope (arc tube glass bulb) 33 ...... luminaire body 40 ...... emits ultraviolet light source 42 ...... enclosure

フロントページの続き (51)Int.Cl. 6識別記号 庁内整理番号 FI 技術表示箇所 H01K 1/32 H01K 1/32 Z Front page continued (51) Int.Cl. 6 identification symbol Agency Docket No. FI art display portion H01K 1/32 H01K 1/32 Z

Claims (20)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 膜形成面を有し、少なくとも 410nm以下の波長の光が透過可能な基体と;前記膜形成面に設けられた光触媒作用を有する金属酸化物を主体とした相、およびこの相に分散された光触媒作用を有する結晶性 TiO 1. A having a film forming surface, at least 410nm and less light available transmissive substrates wavelength; phase consisting mainly of a metal oxide having a photocatalytic action provided on the film forming surface, and this phase crystalline TiO having photocatalyst activity dispersed in
    2 , ZnOのうちの少なくとも1種を主体とした微粒子で形成された膜厚0.01〜 0.3μm の光触媒膜と;を備えた光触媒体。 Photocatalyst having a; 2, at least one photocatalyst film having a thickness of 0.01 to 0.3 [mu] m formed of fine particles mainly composed of one of ZnO.
  2. 【請求項2】 膜形成面を有し、少なくとも 410nm以下の波長の光が透過可能な基体と;前記膜形成面に設けられた光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1種を主体とした第1の微粒子、および平均粒径が前記第1の微粒子の平均粒径よりも小さい光触媒作用を有する金属酸化物を主体とした第2の超微粒子で形成された膜厚0.01〜 0.3μm の光触媒膜と;を備えた光触媒体。 2. A having a film forming surface, at least 410nm and less light transmissible substrate having a wavelength; crystalline TiO 2, at least one of ZnO having a photocatalytic action provided on the film forming surface first microparticles, and the average particle diameter second thickness 0.01 formed of ultrafine particles consisting mainly of metal oxide having a small photocatalytic activity than the average particle diameter of the first fine particle mainly containing photocatalyst film and 0.3 [mu] m; photocatalyst having a.
  3. 【請求項3】 基体の膜形成面と光触媒膜との間に SiO Wherein SiO between the base of the film forming surface and the photocatalyst film
    2を主体とする層を介挿させたことを特徴とする請求項1もしくは請求項2記載の光触媒体。 Claim 1 or claim 2 photocatalyst according to, characterized in that 2 was interposed a layer mainly composed of.
  4. 【請求項4】 膜形成面を有し、少なくとも 410nm以下の波長の光が透過可能な光透過性を有するバルブと;前記バルブ内に封装された発光フィラメントと;前記バルブ内の発光フィラメントの両端にそれぞれ一端が接続されるとともに他端がバルブ外に気密に導出された電気導入手段と;前記バルブ外周面に設けられた光触媒作用を有する金属酸化物を主体とした相、およびこの相に分散された光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1種を主体とした微粒子で形成された膜厚0. Has a 4. A film forming surface, valve and having at least 410nm or less of the light-transmissive light that is capable of transmitting a wavelength; and a light-emitting filaments is FuSo within said valve; across the two ends of the light emitting filaments in the bulb dispersed phase mainly composed of metal oxide having a photocatalytic activity that is provided on the valve outer circumferential surface, and in this phase; the other end is electrically introduction means and derived hermetically outside the valve with one end each of which is connected It is crystalline TiO 2, film thickness formed by particles consisting mainly of at least one of ZnO 0 having photocatalyst activity.
    01〜 0.3μm の光触媒膜と;を具備していることを特徴とする白熱電球。 Incandescent lamp, characterized in that it comprises a; and the photocatalyst film. 01 to 0.3 [mu] m.
  5. 【請求項5】 膜形成面を有し、少なくとも 410nm以下の波長の光が透過可能な光透過性を有するバルブと;前記バルブ内に封装された発光フィラメントと;前記バルブ内の発光フィラメントの両端にへそれぞれ一端が接続されるとともに他端がバルブ外に気密に導出された電気導入手段と;前記バルブ外周面に設けられた光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1種を主体とした第1の微粒子、および平均粒径が前記第1の微粒子の平均粒径よりも小さい光触媒作用を有する金属酸化物を主体とした第2の超微粒子で形成された膜厚0. Has 5. A film forming surface, valve and having at least 410nm or less of the light-transmissive light that is capable of transmitting a wavelength; and a light-emitting filaments is FuSo within said valve; across the two ends of the light emitting filaments in the bulb each electrical introducing means whose other end is led to the air-tight to the outside of the valve with one end connected to the; at least one of crystalline TiO 2, ZnO having a photocatalytic action provided in the valve outer circumferential surface first microparticles, and thickness of the average particle diameter is formed in the second ultrafine particles consisting mainly of metal oxide having a small light catalysis than the average particle diameter of the first fine particles containing mainly 0.
    01〜 0.3μm の光触媒膜と;を具備していることを特徴とする白熱電球。 Incandescent lamp, characterized in that it comprises a; and the photocatalyst film. 01 to 0.3 [mu] m.
  6. 【請求項6】 バルブ外周面と光触媒膜との間に SiO 2 6. SiO 2 between the valve outer circumferential surface and the photocatalyst film
    を主体とする層を介挿させたことを特徴とする請求項4 Claim, characterized in that was interposed a layer made mainly of 4
    もしくは請求項5記載の白熱電球。 Or claim 5 light source device according.
  7. 【請求項7】 内部に放電ガスが封入され、かつ少なくとも 410nm以下の波長の光が透過可能な透光性気密容器と;前記透光性気密容器内に放電を発生させる電極手段と;前記透光性気密容器の外周面に設けられた光触媒作用を有する金属酸化物を主体とした相、およびこの相に分散された光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1種を主体とした微粒子で形成された膜厚0.01〜 0.3μm の光触媒膜と;を具備していることを特徴とする放電ランプ。 And electrode means for generating a discharge in the transparent airtight container; 7. inside the discharge gas is enclosed, and at least 410nm or less in wavelength light permeable light-transmissive airtight envelope and said Toru a principal phase consisting mainly of a metal oxide having a photocatalytic action provided on the outer peripheral surface of the optical hermetic vessel, and at least one of crystalline TiO 2, ZnO having a photocatalytic action that is dispersed in the phase discharge lamp, characterized in that it comprises a; the photocatalyst film having a thickness of 0.01 to 0.3 [mu] m formed of fine particles.
  8. 【請求項8】 内部に放電ガスが封入され、かつ少なくとも 410nm以下の波長の光が透過可能な透光性気密容器と;前記透光性気密容器内に放電を発生させる電極手段と;前記透光性気密容器の外周面に設けられた光触媒作用を有する結晶性 TiO 2 ,ZnOのうちの少なくとも1種を主体とした第1の微粒子、および平均粒径が前記第1 And electrode means for generating a discharge in the transparent airtight container; is 8. encapsulation inside the discharge gas, and at least 410nm or less in wavelength light permeable light-transmissive airtight envelope and said Toru first particles mainly composed of at least one of crystalline TiO 2, ZnO having a photocatalytic action provided on the outer peripheral surface of the optical hermetic vessel, and the average particle diameter is the first
    の微粒子の平均粒径よりも小さい光触媒作用を有する金属酸化物を主体とした第2の超微粒子で形成された膜厚 Second thickness formed of ultrafine particles of metal oxide having a small light catalysis than the average particle diameter of the fine particles mainly
    0.01〜 0.3μm の光触媒膜と;を具備していることを特徴とする放電ランプ。 Discharge lamp, characterized in that it comprises a; and the photocatalyst film of 0.01 to 0.3 [mu] m.
  9. 【請求項9】 内部に放電ガスが封入され、かつ少なくとも 410nm以下の波長の光が透過可能な透光性気密容器と;前記透光性気密容器の外周面に設けられた光触媒作用を有する金属酸化物を主体とした相、およびこの相に分散された光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1種を主体とした微粒子で形成された膜厚0.01〜 0.3μm の光触媒膜と;を具備していることを特徴とする無電極放電ランプ。 Metal having a photocatalytic action provided on the outer circumferential surface of the light-transmissive airtight envelope; 9. inside the discharge gas is enclosed, and at least 410nm or less of the light is capable of transmitting light-transmissive airtight envelope wavelength mainly of oxides phases, and a photocatalyst film of at least one form of a fine particle mainly composed of a thickness 0.01 to 0.3 [mu] m of crystalline TiO 2, ZnO having a photocatalytic action that is dispersed in the phase electrodeless discharge lamp, characterized in that it comprises a;.
  10. 【請求項10】 内部に放電ガスが封入され、かつ少なくとも 410nm以下の波長の光が透過可能な透光性気密容器と;前記透光性気密容器の外周面側に設けられた光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1種を主体とした第1の微粒子、および平均粒径が前記第1の微粒子の平均粒径よりも小さい光触媒作用を有する金属酸化物を主体とした第2の超微粒子で形成された膜厚0.01〜 0.3μm の光触媒膜と;を具備していることを特徴とする無電極放電ランプ。 Having photocatalyst activity provided on the outer peripheral surface side of the light-transmissive airtight envelope; 10. Internal to the discharge gas is enclosed, and at least 410nm or less of the light is capable of transmitting light-transmissive airtight envelope wavelength the first fine particles containing mainly at least one of crystalline TiO 2, ZnO, and the average particle size mainly of metal oxide having a small light catalysis than the average particle diameter of the first particles electrodeless discharge lamp, characterized in that it comprises a; 2 of a photocatalyst film having a thickness of 0.01 to 0.3 [mu] m formed by the ultrafine particles.
  11. 【請求項11】 透光性気密容器外周面と光触媒膜との間に SiO 2を主体とする層を介挿させたことを特徴とする請求項7ないし請求項10いずれか一記載の無電極放電ランプ。 11. An electrodeless of any one claim 7 to claim 10, characterized in that was interposed a layer made mainly of SiO 2 between the light-transmissive airtight envelope outer peripheral surface and the photocatalyst film discharge lamp.
  12. 【請求項12】 内部に放電ガスが封入され、かつ少なくとも 410nm以下の波長の光が透過可能な透光性気密容器と;前記透光性気密容器内に放電を発生させる電極手段と;前記透光性気密容器の面に設けられ、かつ放電によって生じる紫外線に励起されて発光する蛍光体層と; And electrode means for generating a discharge in the transparent airtight container; 12. Internal to the discharge gas is enclosed, and at least 410nm or less in wavelength light permeable light-transmissive airtight envelope and said Toru a surface on the light-airtight container, and a phosphor layer which emits light when excited in the ultraviolet generated by discharge;
    前記透光性気密容器の外周面に設けられた光触媒作用を有する金属酸化物を主体とした相、およびこの相に分散された光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1種を主体とした微粒子で形成された膜厚0. The light-transmissive airtight envelope phase consisting mainly of a metal oxide having a photocatalytic action provided on the outer peripheral surface, and at least one of crystalline TiO 2, ZnO having a photocatalytic action that is dispersed in the phase thickness formed by mainly the microparticles 0.
    01〜 0.3μm の光触媒膜と;を具備していることを特徴とする蛍光ランプ。 Fluorescent lamps, characterized in that it comprises a; and the photocatalyst film. 01 to 0.3 [mu] m.
  13. 【請求項13】 内部に放電ガスが封入され、かつ少なくとも 410nm以下の波長の光が透過可能な透光性気密容器と;前記透光性気密容器内に放電を発生させる電極手段と;前記透光性気密容器の面に設けられ、かつ放電によって生じる紫外線に励起されて発光する蛍光体層と; And electrode means for generating a discharge in the transparent airtight container; 13. Internal to the discharge gas is enclosed, and at least 410nm or less in wavelength light permeable light-transmissive airtight envelope and said Toru a surface on the light-airtight container, and a phosphor layer which emits light when excited in the ultraviolet generated by discharge;
    前記透光性気密容器の外周面側に設けられた光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1種を主体とした第1の微粒子、および平均粒径が前記第1の微粒子の平均粒径よりも小さい光触媒作用を有する金属酸化物を主体とした第2の超微粒子で形成された膜厚0. The first consisting mainly of at least one of crystalline TiO 2, ZnO having a photocatalytic action provided on the outer peripheral surface side of the light-transmissive airtight envelope particles, and average particle size of the first particles second thickness formed of ultrafine particles consisting mainly of metal oxide having a small light catalysis than the average particle diameter of 0.
    01〜 0.3μm の光触媒膜と;を具備していることを特徴とする蛍光ランプ。 Fluorescent lamps, characterized in that it comprises a; and the photocatalyst film. 01 to 0.3 [mu] m.
  14. 【請求項14】 透光性気密容器外周面と光触媒膜との間に SiO 2を主体とする層を介挿させたことを特徴とする請求項12もしくは請求項13記載の蛍光ランプ。 14. light-transmissive airtight envelope outer peripheral surface according to claim 12 or claim 13 fluorescent lamp according to, characterized in that was interposed a layer made mainly of SiO 2 between the photocatalyst film.
  15. 【請求項15】 請求項4ないし請求項14いずれか一記載の光源と;前記光源を装着する器具本体と;を具備していることを特徴とする照明器具。 Luminaire, characterized in that it comprises a; 15. A light source according to claim 4 to claim 14 any one described; and the instrument body for attaching the light source.
  16. 【請求項16】 光源と;前記光源に対向して配設された制光体と;前記光源からの光が到達する制光体の対向面および反対向面の少なくともいずか一方の面に形成された光触媒作用を有する金属酸化物を主体とした相、およびこの相に分散された光触媒作用を有する結晶性 TiO 16. A light source; has been the control light body disposed opposite to the light source; a facing surface and one surface or not a Sukunakutomoi the non-opposing face of Seihikaritai that light reaches from the light source formed phase mainly composed of metal oxide having a photocatalytic activity, and crystalline TiO having photocatalyst activity dispersed in this phase
    2 , ZnOのうちの少なくとも1種を主体とした微粒子で形成された膜厚0.01〜 0.3μm の光触媒膜と;を具備していることを特徴とする照明器具。 Luminaire, characterized in that it comprises a; 2, a photocatalyst film having a thickness of 0.01 to 0.3 [mu] m formed of fine particles mainly composed of at least one of ZnO.
  17. 【請求項17】 光源と;前記光源に対向して配設された制光体と;前記光源からの光が到達する制光体の対向面および反対向面の少なくともいずか一方の面に形成された光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1種を主体とした第1の微粒子、および平均粒径が前記第1の微粒子の平均粒径よりも小さい光触媒作用を有する金属酸化物を主体とした第2の超微粒子で形成された膜厚0.01〜 0.3μm の光触媒膜と;を具備していることを特徴とする照明器具。 17. A light source; has been the control light body disposed opposite to the light source; a facing surface and one surface or not a Sukunakutomoi the non-opposing face of Seihikaritai that light reaches from the light source metal having a first fine particle, and small photocatalysis than the average particle diameter of the average particle diameter of the first fine particle mainly containing at least one of crystalline TiO 2, ZnO having the formed photocatalytic action luminaire, characterized in that it comprises a; mainly of oxides was the second photocatalyst film having a thickness of 0.01 to 0.3 [mu] m formed by the ultrafine particles.
  18. 【請求項18】 光源と;前記光源を包囲する包囲体と;前記光源からの光が到達する包囲体の内壁面および外壁面の少なくともいずか一方の面に形成された光触媒作用を有する金属酸化物を主体とした相、およびこの相に分散された光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1種を主体とした微粒子で形成された膜厚0.01〜 0.3μm の光触媒膜と;を具備していることを特徴とする照明器具。 18. The light source and; metal having photocatalyst activity light is formed on one surface or not a Sukunakutomoi the inner wall surface and outer wall surface of the enclosure to reach from the light source; enclosure and surrounding said light source mainly of oxides phases, and a photocatalyst film of at least one form of a fine particle mainly composed of a thickness 0.01 to 0.3 [mu] m of crystalline TiO 2, ZnO having a photocatalytic action that is dispersed in the phase luminaire, characterized in that it comprises a;.
  19. 【請求項19】 光源と;前記光源を包囲する包囲体と;前記光源からの光が到達する包囲体の内壁面および外壁面の少なくともいずか一方の面に形成された光触媒作用を有する結晶性 TiO 2 , ZnOのうちの少なくとも1 19. A light source; and an enclosure surrounding said light source; crystals having a photocatalytic effect light is formed on one surface or not a Sukunakutomoi the inner wall surface and outer wall surface of the enclosure to reach from the light source At least one of the sex TiO 2, ZnO
    種を主体とした第1の微粒子、および平均粒径が前記第1の微粒子の平均粒径よりも小さい光触媒作用を有する金属酸化物を主体とした第2の超微粒子で形成された膜厚0.01〜 0.3μm の光触媒膜と;を具備していることを特徴とする照明器具。 First microparticles thickness, and the average particle size is formed in the second ultrafine particles consisting mainly of metal oxide having a small light catalysis than the average particle diameter of the first fine particle mainly containing seeds 0.01 luminaire, characterized in that it comprises a; and the photocatalyst film of ~ 0.3 [mu] m.
  20. 【請求項20】 光触媒膜の下地層として SiO 2を主体とする層を介挿させたことを特徴とする請求項16ないし請求項19いずれか一記載の照明器具。 20. photocatalyst film of the luminaire of any one claim 16 to claim 19, characterized in that the SiO 2 was interposed a layer mainly as a base layer.
JP33543295A 1995-06-15 1995-12-22 Photocatalyst, incadescent electric bulb, discharge lamp and luminaire Pending JPH0957113A (en)