JPH0833681B2 - Toner - composition - Google Patents

Toner - composition

Info

Publication number
JPH0833681B2
JPH0833681B2 JP61242601A JP24260186A JPH0833681B2 JP H0833681 B2 JPH0833681 B2 JP H0833681B2 JP 61242601 A JP61242601 A JP 61242601A JP 24260186 A JP24260186 A JP 24260186A JP H0833681 B2 JPH0833681 B2 JP H0833681B2
Authority
JP
Japan
Prior art keywords
toner
weight
parts
metal salt
photosensitive member
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP61242601A
Other languages
Japanese (ja)
Other versions
JPS6396664A (en
Inventor
和彦 山村
利一 松井
伸行 辻
和則 雪竹
Original Assignee
三田工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 三田工業株式会社 filed Critical 三田工業株式会社
Priority to JP61242601A priority Critical patent/JPH0833681B2/en
Publication of JPS6396664A publication Critical patent/JPS6396664A/en
Publication of JPH0833681B2 publication Critical patent/JPH0833681B2/en
Anticipated expiration legal-status Critical
Application status is Expired - Fee Related legal-status Critical

Description

【発明の詳細な説明】 〈産業上の利用分野〉 本発明は、トナー組成物に関し、より詳しくは、電子写真法、静電印刷法、静電記録法等において形成される静電荷像を現像するトナー組成物に関する。 DETAILED DESCRIPTION OF THE INVENTION The present invention <relates> is developing relates toner compositions, and more particularly, an electrophotographic method, an electrostatic printing method, an electrostatic image formed in electrophotography, electrostatic recording method, or the like the toner composition relates.

〈従来の技術〉 従来、電子写真法を利用した複写機等において、セレン、有機感光層等を有する感光体に形成された静電荷像を乾式現像法により可視化するため、着色剤、結着樹脂等を含有する種々のトナーが用いられている。 <Prior Art> Conventionally, in the copying machine or the like using an electrophotographic method, selenium, for visualization by a dry development method an electrostatic image formed on the photosensitive member having an organic photosensitive layer or the like, colorant, binder resin various toner is used which contains such.

上記乾式現像法では、帯電、露光により上記感光体上に形成された静電荷像を上記トナーで現像し、現像したトナー像を転写紙等の支持体に転写すると共に、加熱ローラまたは加圧ローラにより上記トナー像を支持体に定着させ、上記静電荷像を可視化している。 Above the dry developing method, charging, exposure by developing the electrostatic image formed on the photosensitive member in the toner, thereby transferring the toner image developed on a support such as a transfer sheet, the heating roller or pressure roller by then fusing the toner image to a support, and visualize the electrostatic latent image. また、上記トナー像を支持体に転写した後、感光体上に残留するトナーをクリーニングするため、クリーニングブレードにより感光体上の残留トナーを掻き取っている。 Further, after transferring the toner image to a support, for cleaning the toner remaining on the photosensitive member, and it scrapes the residual toner on the photosensitive member by the cleaning blade. このクリーニング工程が、繰返し行なわれると、上記感光体表面とクリーニングブレード間の摩擦熱等により、トナーが感光体に融着すると共に、徐々に成長する。 The cleaning process, when carried out repeatedly, by friction heat or the like between the photosensitive member surface and the cleaning blade, the toner is fused on the photosensitive member gradually grow. 特に、感光体が平滑でなかったり、感光体上に突起物や孔などが存在すると、感光体の損傷が大きくなることと、感光体表面にトナーがすじ上に融着し易くなることとが相まって、 Particularly, or not a photoreceptor smooth and like projections and holes are present on the photosensitive member, and the damage of the photosensitive member is increased, and the toner on the photosensitive member surface is liable to fuse to the stripes combined,
複写画像上にトナーのすじが生じ、複写画像の品質を低下させる等の問題がある。 Streaks of toner occurs on the copied image, there are problems such as lowering the quality of the copied image.

上記の問題を解決するため、上記トナーに、感光体を保護すると共にクリーニング性を向上させるための脂肪酸金属塩と、疎水性シリカ等の研磨物質を添加したものが知られている(特公昭54−16220号公報、特開昭58−1 To solve the above problems, in the toner, and a fatty acid metal salt for improving the cleaning property to protect the photoreceptor is known that the addition of abrasive material such as hydrophobic silica (JP-B-54 -16,220 JP, JP-A-58-1
25045号公報)。 25045 JP).

〈発明が解決しようとする問題点〉 しかしながら、上記脂肪酸金属塩の添加により、感光体を保護することはできるものの、特に、感光体が有機感光層を有するものである場合、上記脂肪酸金属塩と感光体との親和性が大きいため、上記感光体表面で脂肪酸金属塩がフィルミング化し易い。 <Problems to be Solved by the Invention> However, by adding the fatty acid metal salt, although it is possible to protect the photoreceptor, in particular, when the photosensitive body has an organic photosensitive layer, and the fatty acid metal salt since a large affinity with the photoconductor, easily fatty acid metal salt in the photosensitive member surface filming of. そして、脂肪酸金属塩がフィルミング化すると、フィルム化した脂肪酸金属塩が絶縁層として機能することと、上記有機感光層を有する感光体の表面電位が一般に低いことと相まって、複写画像等の品質が低下するという問題があった。 When the fatty acid metal salt is filming reduction, and that the fatty acid metal salt into a film functions as an insulating layer, together with the fact the surface potential of the photosensitive member having the organic photosensitive layer is generally low, the quality such as a copying image there is a problem that decreases. また、階調性等の画像特性をよくするため、上記脂肪酸金属塩を多量に添加すると、上記フィルミング化が生じるだけでなく、トナー、現像剤の電気抵抗が小さくなり、画像のうちベタ部近傍にトナーのニジミが生じ、複写画像等の品質が低下するという問題がある。 Further, in order to improve the image characteristics of the gradation and the like, when a large amount of addition of the fatty acid metal salt, not only the filming of results, toner, the electrical resistance of the developer is reduced, a solid portion of the image bleeding of the toner occurs in the vicinity, the quality of such copy image is lowered. さらには、上記感光体の有機感光層がセレン等の感光層に比べて軟質であるため、疎水性シリカ等の研磨物質が添加されたトナーを用いると、上記有機感光層が上記研磨物質により研磨されて、早期に使用に耐えなくなるという問題があった。 Further polishing, since the organic photosensitive layer of the photosensitive member is softer than the light-sensitive layer of selenium, the use of toner abrasive material such as hydrophobic silica is added, the organic photosensitive layer by the polishing material is, there is a problem that will not withstand the use at an early stage.

〈目的〉 本発明は上記問題点に鑑みてなされたものであり、感光体として有機感光層を有する感光体を用いる場合にあっても、感光体を保護すると共に、感光体表面でトナーがすじ状に融着するのを防止し、感光体の感光特性や、 <Object> The present invention has been made in view of the above problems, even in the case of using a photosensitive member having an organic photosensitive layer as the photosensitive member, to protect the photosensitive member, the toner streaks in the surface of the photosensitive member prevented from fusing to Jo, and the photosensitive characteristic of the photosensitive member,
トナー、現像剤の特性を劣化させることなくトナー、現像剤の電気抵抗を調整し、高品質の画像を形成することができるトナー組成物を提供することを目的とする。 Toner, toner without degrading the characteristics of the developer, by adjusting the electric resistance of the developer, and an object thereof is to provide a toner composition which can form a high quality image.

〈問題点を解決するための手段および作用〉 本発明は、結着樹脂、着色剤および他の添加剤を含有する粉体トナー100重量部に対して、その添加重量部x <Means and operation for solving the problems> present invention, a binder resin, a colorant and the powder 100 parts by weight of the toner containing other additives, the addition parts x
が下記関係式を充足する脂肪酸金属塩と、 0<x≦0.01(重量部) 上記粉体トナー100重量部に対して0.05〜0.3重量部の研磨物質と、上記粉体トナー100重量部に対して0.05〜0.3 There the fatty acid metal salt that satisfies the following relational expression, 0 <a polishing material 0.05 to 0.3 parts by weight with respect to x ≦ 0.01 (parts by weight) the powder toner 100 parts by weight, relative to the powder toner 100 parts by weight Te 0.05 to 0.3
重量部の電気抵抗調整剤とが添加されているトナー組成物により、上記従来の問題点を解決するものである。 The toner composition and the electric resistance adjusting agent parts by weight are added, and solves the above problems.

上記の構成からなる本発明のトナー組成物によれば、 According to the toner compositions of the present invention having the above structure,
脂肪酸金属塩の添加量が少量であり、感光体表面で脂肪酸金属塩のフィルミング化を抑制でき、万一、上記脂肪酸金属塩によるフィルミング化が生じても前記研磨物質により、脂肪酸金属塩のフィルムが研磨されて清浄化されるので、感光体を保護することができ、感光体のクリーニング時にも感光体表面でトナーがすじ状に融着するのを防止できる。 A minor amount of added fatty acid metal salt, the photosensitive member surface can be suppressed filming of fatty acid metal salt, any chance, by the abrasive material even when filming reduction by the fatty acid metal salt, the fatty acid metal salt since the film is cleaned and polished, it is possible to protect the photosensitive member, the toner can be prevented from fusing to the streak-like in the photosensitive member surface even when the cleaning of the photoreceptor. また、脂肪酸金属塩の添加量が少量であるため、トナー、現像剤の電気抵抗が殆ど低下せず、 Moreover, since the addition amount of the fatty acid metal salt is small, toner, the electrical resistance of the developing agent does not lower most,
トナーの特性、画像特性に悪影響を及ぼさない。 Properties of the toner, does not adversely affect the image characteristics. また、 Also,
研磨物質の添加により、トナーが流動性、ひいてはトナーの帯電特性、画像特性が改善されるだけでなく、電気抵抗調整剤の添加によりトナー、現像剤の電気抵抗を調整することができるので、画像特性が改良される。 The addition of abrasive material, the toner flowability, as well as thus charging characteristics of the toner, the image characteristics are improved, the toner by adding the electric resistance adjusting agent, it is possible to adjust the electric resistance of the developer, the image characteristics are improved.

以下に、本発明を詳細に説明する。 Hereinafter, the present invention will be described in detail.

本発明のトナー組成物は、結着樹脂、着色剤および他の添加剤を含有する粉体のトナーと、このトナーに添加される脂肪酸金属塩、研磨物質および電気抵抗調整剤とからなる。 The toner compositions of the present invention, a binder resin composed of a powder toner containing a coloring agent and other additives, fatty acid metal salt added to the toner, and abrasive materials and electric resistance adjusting agent.

上記結着樹脂としては、スチレン系重合体、アクリル系重合体、スチレン−アクリル系共重合体、ポリエチレン、塩素化ポリエチレン、ポリプロピレン、アイオノマー等のオレフィン系重合体、ポリ塩化ビニル、ポリエステル、ポリアミド、ポリウレタン、エポキシ樹脂、ジアリルフタレート樹脂、シリコーン樹脂、ケトン樹脂、ポリビニルブチラール樹脂、フェノール樹脂、ロジン変性フェノール樹脂、キシレン樹脂、ロジン変性マレイン酸樹脂、ロジンエステル、石油樹脂等、各種の重合体が例示できる。 As the binder resin, styrene polymer, acrylic polymer, styrene - acrylic copolymer, polyethylene, chlorinated polyethylene, polypropylene, olefin polymers such as ionomer, polyvinyl chloride, polyesters, polyamides, polyurethanes , epoxy resins, diallyl phthalate resins, silicone resins, ketone resins, polyvinyl butyral resins, phenol resins, rosin-modified phenolic resins, xylene resins, rosin-modified maleic acid resin, rosin ester, petroleum resin, various polymers can be exemplified.

上記重合体に用いられる不飽和単量体としては、スチレン、α−メチルスチレン、o−メチルスチレン、p− Examples of the unsaturated monomer used in the polymerization include styrene, alpha-methyl styrene, o- methyl styrene, p-
メチルスチレン、p−メトキシスチレン、p−クロロスチレン等のスチレン系単量体;アクリル酸、アクリル酸メチル、アクリル酸エチル、アクリル酸−n−ブチル、 Methylstyrene, p- methoxystyrene, styrene based monomers such as p- chlorostyrene, acrylic acid, methyl acrylate, ethyl acrylate,-n-butyl acrylate,
アクリル酸イソブチル、アクリル酸−n−オクチル、アクリル酸−2−エチルヘキシル、アクリル酸ドデシル、 Isobutyl acrylate, -n- octyl, 2-ethylhexyl acrylate, dodecyl acrylate,
アクリル酸ステアリル、アクリル酸シクロヘキシル、アクリル酸フェニル、アクリル酸−2−ヒドロキシエチル、アクリル酸−2−ヒドロキシプロピル、アクリル酸グリシジル、アクリル酸ジエチルアミノエチル、アクリルアミド、アクリロニトリル、メタクリル酸、メタクリル酸メチル、メタクリル酸エチル、メタクリル酸−n− Stearyl acrylate, cyclohexyl acrylate, phenyl acrylate, 2-hydroxyethyl acrylate, 2-hydroxypropyl, glycidyl acrylate, diethylaminoethyl acrylate, acrylamide, acrylonitrile, methacrylic acid, methyl methacrylate, ethyl, methacrylic acid -n-
ブチル、メタクリル酸イソブチル、メタクリル酸−n− Butyl, isobutyl methacrylate, -n-
オクチル、メタクリル酸−2−エチルヘキシル、メタクリル酸ドデシル、メタクリル酸ステアリル、メタクリル酸シクロヘキシル、ナタクリル酸フェニル、メタクリル酸グリシジル、メタクリル酸−2−ヒドロキシエチル、 Octyl, 2-ethylhexyl methacrylate, dodecyl methacrylate, stearyl methacrylate, cyclohexyl methacrylate, Natakuriru acid phenyl glycidyl methacrylate, 2-hydroxyethyl methacrylate,
メタクリル酸−2−ヒドロキシプロピル、メタクリル酸ジエチルアミノエチル等のアクリルまたはメタクリル系単量体;マレイン酸、フマル酸、クロトン酸、イタコン酸またはこれらのアルキルエステル等の不飽和二重結合を有するカルボン酸またはそのアルキルエステル;エチレン、プロピレン、ブタジエン等のオレフィン系単量体;酢酸ビニル;塩化ビニル;塩化ビニリデン;ビニルピロリドン;ビニルナフタレン等が例示できる。 Methacrylic acid-2-hydroxypropyl, acrylic or methacrylic monomers such as diethylaminoethyl methacrylate; maleic acid, fumaric acid, crotonic acid, carboxylic acids having an unsaturated double bond such as itaconic acid or their alkyl esters or alkyl esters thereof, ethylene, propylene, olefin monomer such as butadiene, vinyl acetate, vinyl chloride, vinylidene chloride; vinyl pyrrolidone; vinyl naphthalene and the like. 上記単量体は、一種または二種以上混合して使用される。 The monomer may be used independently or in combination.

上記重合体のうち、スチレン系重合体、アクリル系重合体、またはスチレン−アクリル共重合体等を主成分とするものが好ましい。 Among the above polymers, styrene polymer, acrylic polymer, or a styrene - those mainly containing acrylic copolymer or the like. これらの重合体は、重量平均分子量30,000〜200,000、特に、50,000〜150,000のものが好ましく、一種または二種以上混合して用いられる。 These polymers have a weight average molecular weight 30,000 to 200,000, particularly preferably has a 50,000 to 150,000, used independently or in combination.

なお、上記重合体のうち、ロジンエステル、ロジン変性フェノール樹脂、ロジンマレイン酸樹脂、エポキシ樹脂、ポリエステルや、繊維素系高分子、ポリエーテル樹脂等は、トナーの摩擦帯電特性等を改良する上で有用である。 Among the above polymers, rosin esters, rosin-modified phenolic resin, rosin-maleic acid resins, epoxy resins, or polyester, cellulose polymers, polyether resins, etc., in order to improve the frictional charging characteristics of the toner or the like it is useful.

また、トナーが熱定着トナーであるとき、上記重合体は、軟化点50〜200℃、好ましくは、軟化点70〜170℃を有するものが好ましい。 Further, when the toner is a heat fixing toner, the polymer has a softening point of 50 to 200 ° C., preferably, preference is given to those having a softening point 70 to 170 ° C..

また、トナーが圧力定着性トナーであるときは、ポリエチレン、ポリプロピレン等のオレフィン系ポリマー等、容易に塑性変形する重合体が主に用いられる。 Further, when the toner is a pressure fixing toner is polyethylene, olefin polymers such as polypropylene, easily polymer plastic deformation is mainly used. この重合体は、他の重合体、例えば、ポリ酢酸ビニル、エチレン−酢酸ヒニル共重合体、水素化ポリスチレン、水添ロジンエステル等の重合体、脂肪族系、脂環族系または芳香族系石油樹脂等を含有していてもよい。 The polymer may contain other polymers, e.g., polyvinyl acetate, ethylene - acetate Hiniru copolymers, hydrogenated polystyrene, polymers such as hydrogenated rosin esters, aliphatic, alicyclic or aromatic petroleum the resin may contain.

また、上記着色剤としては、例えば、カーボンブラック、ランプブラック(CINo.77266)、クロムイエロー(CINo.14090)、ハンザイエロー(CINo.11660、11 Further, as the coloring agent, for example, carbon black, lamp black (CINo.77266), chrome yellow (CINo.14090), Hansa Yellow (CINo.11660,11
680、等)、ベンジジンイエロー(CINo.21100等)、 680, etc.), benzidine yellow (CINo.21100, etc.),
スレンイエローG(CINo.70600)、キノリンイエロー(CINo.47005)、パーマネントオレンジGTR(CINo. Sleng yellow G (CINo.70600), quinoline yellow (CINo.47005), permanent orange GTR (CINo.
12305)、ピラゾロンオレンジ(CINo.21110)、バルカンオレンジ(CINo.21160)、ウオッチヤングレッド(CINo.15865)、パーマネントレッド(CINo.12310 12305), pyrazolone orange (CINo.21110), Balkan orange (CINo.21160), Watchung Red (CINo.15865), Permanent Red (CINo.12310
等)、ブリリアントカーミン3B(CINo.16105)、ブリリアントカーミン6B(CINo.15850)、デュポンオイルレッド(CINo.26105)、ピラゾロンレッド(CINo.2 Etc.), Brilliant Carmine 3B (CINo.16105), Brilliant Carmine 6B (CINo.15850), Du Pont Oil Red (CINo.26105), pyrazolone (CINo.2
1120)、リソールレッド(CINo.15630)、ローダミンBレーキ(CINo.45170)、レーキレッドC(CINo.1 1120), Li Saul Red (CINo.15630), Rhodamine B lake (CINo.45170), Lake Red C (CINo.1
5585)、ローズベンガル(CINo.45435)、アニリンブルー(CINo.50405)、ウルトラマリンブルー(CIN 5585), Rose Bengal (CINo.45435), aniline blue (CINo.50405), ultramarine blue (CIN
o.77103)、カルコオイルブルー(CINo.azoec Blue o.77103), Calco Oil Blue (CINo.azoec Blue
3)、メチレンブルークロライド(CINo.52015)、フタロシアニンブルー(CINo.74160)、フタロシアニングリーン(CINo.74260)、マラカイドグリーンオクサレート(CINo.42000)等、またはCISolvent Yellow 3), methylene blue chloride (CINo.52015), phthalocyanine blue (CINo.74160), phthalocyanine green (CINo.74260), Malachite green oxalate (CINo.42000) etc. or CI Solvent Yellow,
60、CISolvent Red 27、CISolvent Blue 35等の油溶性染料などが例示される。 60, such as CI Solvent Red 27, CI Solvent oil-soluble dye 35 such as Blue and the like. これらの着色剤は、一種または二種以上混合して用いられ、十分なトナー画像濃度が得られる量、例えば、1〜30重量%、好ましくは、2 These colorants amounts used independently or in combination, sufficient toner image density can be obtained, for example, 1 to 30 wt%, preferably, 2
〜20重量%用いられる。 20% by weight is used.

また、上記トナーが磁性トナーであるときは、上記着色剤と共に、または上記着色剤に代えて磁性体が用いられる。 Further, when the toner is a magnetic toner, together with the colorant or magnetic material in place of the coloring agent is used. 上記磁性体としては、磁性を示すか、磁化可能な材料であればよく、例えば、フェライト、マグネタイトを始めとする鉄、コバルト、ニッケル、マンガン等の強磁性を示す金属、合金、またはこれらの金属を含む化合物等が例示できる。 As the magnetic substance, either exhibiting magnetism, may be any magnetizable material, e.g., iron and ferrite, magnetite began, cobalt, nickel, a metal exhibiting ferromagnetism manganese, an alloy, or these metals, compounds can be exemplified which includes a. これらの磁性体は、平均粒径0.1〜 These magnetic materials have an average particle size of 0.1
1μmの大きさを有しており一種または二種以上混合して、通常20〜75重量%、好ましくは、40〜70重量%用いられる。 Independently or in combination has a size of 1 [mu] m, typically 20 to 75 wt%, preferably used 40-70 wt%.

なお、静電荷像現像用トナーの電荷を制御するため、 In order to control the charge of the toner for developing electrostatic images,
上記トナーは、他の添加剤として、電荷制御剤、例えば、ニグロシン染料(CINo.50415B)、オイルブラック(CINo.26150)、スピロンブラック等の油溶性染料や、ナフテン酸、サリチル酸、オクチル酸、後記脂肪酸、樹脂酸のマンガン、鉄、コバルト、鉛、亜鉛、セリウム、カルシウム、ニッケル等の金属塩である金属石鹸等あるいは含金属アゾ染料、ピリミジン化合物、アルキルサリチル酸金属キレート等を、前記結着樹脂当り0.1 The toner as other additives, a charge control agent, for example, nigrosine dye (CINo.50415B), Oil Black (CINo.26150), and oil-soluble dyes such as spiron black, naphthenic acid, salicylic acid, octyl acid, below fatty acids, resin acids manganese, iron, cobalt, lead, zinc, cerium, calcium, metal soaps or metal-containing azo dye is a metal salt such as nickel, pyrimidine compounds, alkyl salicylic acid metal chelate and the like, the binder resin per 0.1
〜5重量%含有しているものが好ましい。 Preferably one containing 5 wt%.

また、上記トナーは、前記定着ローラにトナーが付着するのを防止するため、オフセット防止剤、例えば、低分子量ポリプロピレン、低分子量ポリエチレン、パラフィンワックスなどの各種ワックス、炭素原子数4以上のオレフィン単量体の低分子量オレフィン重合体、脂肪酸アミド、シリコーンオイル等を、トナー当り0.5〜15重量%含有しているものが好ましい。 Further, the toner, the the toner to the fixing roller is prevented from adhering, offset inhibitor, for example, low molecular weight polypropylene, low molecular weight polyethylene, various waxes, having 4 or more olefin monomers of carbon atoms such as paraffin wax low molecular weight olefin polymer of the body, fatty amides, silicone oil or the like, it is preferable to contain 0.5 to 15% by weight per toner.

そして、上記粉体トナーには、感光体を保護すると共に、現像剤特性を劣化させることがなく、高品質の画像を得るため、脂肪酸金属塩が添加されている。 Then, the powder toner protects the photosensitive member, without deteriorating the developer properties, to obtain a high quality image, the fatty acid metal salt is added.

上記脂肪酸金属塩の脂肪酸としては、炭素数8〜36の飽和または不飽和脂肪酸、例えば、カプリル酸、カプリン酸、ウンデシル酸、ラウリン酸、トリデシル酸、ミリスチン酸、パルミチン酸、ステアリン酸、ベヘン酸、リグノセリン酸、セロチン酸、モンタン酸、オレイン酸、 The fatty acid of the fatty acid metal salt, saturated or unsaturated fatty acids having 8 to 36 carbon atoms, for example, caprylic acid, capric acid, undecyl acid, lauric acid, tridecyl acid, myristic acid, palmitic acid, stearic acid, behenic acid, lignoceric acid, cerotic acid, montanic acid, oleic acid,
エライジン酸、リノール酸、リノレン酸、エルカ酸、リシノレイン酸、ジヒドロキシステアリン酸、環状脂肪酸、二塩基性酸、あるいは上記不飽和脂肪酸の二量体であるダイマー酸等が例示される。 Elaidic acid, linoleic acid, linolenic acid, erucic acid, ricinoleic acid, dihydroxystearic acid, cyclic fatty acids, dibasic acids or dimer acid is a dimer of the unsaturated fatty acids, are exemplified. 上記脂肪酸のうち、飽和脂肪酸、特にステアリン酸が好ましい。 Among the fatty acids, saturated fatty acids, especially stearic acid.

また、上記脂肪酸金属塩の金属としては、亜鉛、鉛、 The metal of the fatty acid metal salt, zinc, lead,
鉄、銅、錫、カドミウム、アルミニウム、カルシウム、 Iron, copper, tin, cadmium, aluminum, calcium,
マグネシウム、ニッケル、コバルト、マンガン、リチウム、バリウム等各種の金属が例示できる。 Magnesium, nickel, cobalt, manganese, lithium, barium and various metals can be exemplified. 上記金属のうち、亜鉛が好ましい。 Of the above metals, zinc is preferred. 特に、脂肪族金属塩のうち、上記ステアリン酸亜鉛は、ステアリン酸アルミニウム等に比較して約5倍の効果を有するので好ましい。 In particular, among the aliphatic metal salts, the zinc stearate is preferred because has about 5 times more effective compared to aluminum stearate, and the like.

上記脂肪酸金属塩は、上記粉体トナー100重量部に対する脂肪酸金属塩の添加重量部をxとするとき、xが下記関係式を充足する量、 0<x≦0.01(重量部) 好ましくは、0.001〜0.01重量部添加される。 The fatty acid metal salt, when added parts by weight of the fatty acid metal salt to the powder toner 100 parts by weight x, the amount of x is satisfies the following relationships, 0 <x ≦ 0.01 (parts by weight) is preferably 0.001 0.01 is added parts. 脂肪酸金属塩が未添加であると、感光体を十分に保護することができず、感光体の表面でのトナーの融着に起因して複写画像等ですじが生じ画像品質が低下させる。 When the fatty acid metal salt is not added, it is impossible to sufficiently protect the photoconductor, image quality lowers occurs streaks in due to copy image such as fusion of the toner on the surface of the photosensitive member. また0.01重量部を越えると、感光体表面で前記脂肪酸金属塩がフィルミング化すると共に画像のニジミ等が発生し易くなり好ましくない。 Also it exceeds 0.01 part by weight, the fatty acid metal salt is not preferable because bleeding of the image is liable to occur while filming of the photosensitive member surface.

また、上記トナーには、研磨物質が添加されている。 Further, in the toner, the polishing material is added.
上記研磨物質としては、前記脂肪酸金属塩によるフィルムが生じた場合、このフィルムを研磨して感光体を清浄化すると共に、トナーの特性、感光体および画像に悪影響を及ぼさないものであれば、いかなるものも使用でき、例えば、タルク、カオリン、硫酸バリウム等であってもよいが、ケイ酸アルミニウム、表面処理したケイ酸アルミニウム、二酸化チタン、炭酸カルシウム、三酸化アンチモン、チタン酸バリウム、チタン酸カルシウム、 As the polishing material, if the film by the fatty acid metal salt occurs, thereby cleaning the photoreceptor by polishing the film, characteristics of the toner, as long as it does not adversely affect the photosensitive member and image, any can be used as, for example, talc, kaolin, it may be a barium sulfate, aluminum silicate, surface-treated aluminum silicate, titanium dioxide, calcium carbonate, antimony trioxide, barium titanate, calcium titanate,
チタン酸ストロンチウム、酸化マグネシウム、ケイ酸カルシウム、酸化亜鉛、酸化ジルコニウム等が好ましく、 Strontium titanate, magnesium oxide, calcium silicate, zinc oxide, zirconium oxide and the like are preferable,
特に、コロイド状シリカ、表面処理した疎水性シリカが好ましい。 In particular, colloidal silica, surface-treated hydrophobic silica is preferred. 上記研磨物質、特に、疎水性シリカの添加により、トナー、現像剤の流動性も良くなり、トナーの帯電特性、画像特性が改良される。 The polishing agent, in particular, the addition of hydrophobic silica, toner, even better fluidity of the developer, toner charging characteristics, image characteristics are improved. なお、上記研磨物質は、平均粒径5〜100mμ、特に、10〜30mμを有するものが好ましい。 Incidentally, the polishing agent has an average particle size 5~100Emumyu, particularly preferably has a 10~30Emumyu. 研磨物質の粒子径が上記範囲を外れると、上記の効果が低減し、好ましくない。 When the particle diameter of the abrasive material out of the above range, the above effect is reduced, which is not preferable.

上記研磨物質のうち好ましい具体例としては、日本アエロジル(株)製「アエロジルR972」(平均粒径16m Specific preferred examples of the polishing agent, Nippon Aerosil Co., Ltd. "Aerosil R972" (average particle size 16m
μ)等が例示できる。 mu) and the like.

上記研磨物質は、前記粉体トナー100重量部に対して、0.05〜0.3重量部に添加される。 The polishing material relative to the powder 100 parts by weight of the toner, is added to 0.05 to 0.3 parts by weight. 研磨物質の添加量が0.05重量部未満であると、トナーの流動性が劣り、また0.3重量部を越えると感光体が傷つき易くなる。 If the amount of the abrasive material is less than 0.05 part by weight, poor fluidity of the toner, the photoconductor is easily damaged addition amount exceeds 0.3 parts by weight.

また、上記粉体トナーには、トナー、現像剤の電気抵抗、ひていは階調性等の画像特性、濃度等を調整し、高品質の画像を得るため、電気抵抗調整剤が添加されている。 Further, in the powder toner, a toner, the electrical resistance, negative image characteristics of the gradation and the like of the developer, by adjusting the concentration and the like, to obtain a high quality image, the electrical resistance adjusting agent is added there.

上記電気抵抗調整剤としては、トナーの電気抵抗を調整しうると共に、トナーの特性、感光体および画像に悪影響を及さないものであればいかなるものでも使用でき、例えば、カーボンブラック等であってもよいが、電気抵抗を微調整できる酸化アルミニウムが好ましい。 As the electrical resistance adjusting agent, together may adjust the electric resistance of the toner, characteristics of toner, so long as it does not be 及 affect the photoreceptor and the image can be used of any type, for example, a carbon black, it may also be, but aluminum oxide can be finely adjusted electrical resistance is preferred.

上記電気抵抗調整剤は、前記研磨物質と同様の粒径を有するものが好ましく、例えば、日本アエロジル(株) The electrical resistance adjusting agent is preferably one having the same particle size and the abrasive material, for example, Nippon Aerosil Co.,
製「アルミニウムオキサイドC」(平均粒径20mμ)等が例示できる。 Ltd. "Aluminum Oxide C" (average particle size 20Emumyu) and the like.

上記電気抵抗調整剤は、前記粉体トナー100重量部に対して、0.05〜0.3重量部添加される。 The electrical resistance adjusting agent, to said powder to 100 parts by weight of the toner, is added 0.05 to 0.3 parts by weight. 電気抵抗調整剤の添加量が0.05重量部未満であると、電気抵抗の微調整が困難となる。 If the amount of the electric resistance adjusting agent is less than 0.05 part by weight, the fine adjustment of the electric resistance becomes difficult. また、0.3重量部を越えると画像のニジミが生じ易くなる。 Further, it is easy bleeding of an image is generated exceeds 0.3 parts by weight.

なお、トナーの流動性を改良するため、シランカップリング剤、シリコーンやフッ素化合物等の低表面張力を有する化合物でトナー表面を処理してもよい。 In order to improve the fluidity of the toner, silane coupling agents, may be treated with the toner surface with a compound having a low surface tension such as silicone or fluorine compound. さらには、上記の粉体トナーは、所望により、トナーの流動性をよくするため、熱処理することによりトナーの角部等を滑らかにしてもよい。 Further, the above powder toner is, if desired, in order to better the fluidity of the toner may be smoothed corners of the toner by heat treatment.

上記の粉体トナーは、粒径1〜30μm、好ましくは5 The above powder toner has a particle size 1 to 30 [mu] m, preferably 5
〜25μmを有している。 It has a ~25μm.

この発明のトナー組成物は、一成分系トナー、二成分系トナーの何れとしても有用である。 The toner composition of the present invention, one-component toner, it is useful as either a two-component toner. なお、一成分系トナーとして用いる場合には上記磁性体を含有するトナー単独で現像剤とし、二成分系トナーとして用いる場合には、鉄粉、ガラスビーズ等のキャリアと混合し、現像剤とする。 Incidentally, the developer with toner alone containing the magnetic substance in the case of using as one-component toner, when used as a two-component toner, iron powder, mixed with a carrier such as glass beads, and the developer . なお、上記キャリアとしては、ガラスビーズや、酸化または未酸化の鉄粉等の無被覆キャリア、または鉄、ニッケル、コバルト、フェライト等の磁性体をアクリル系重合体、フッ素重合体、ポリエステル等の重合体で被覆した被覆キャリアが用いられ、通常、50〜2000 As the above-mentioned carrier, and glass beads, uncoated carrier such as iron powder of oxide or unoxidized or iron, nickel, cobalt, acrylic polymer magnetic material such as ferrite, fluoropolymer, heavy polyester such as coated carrier is used which is coated with polymer, usually from 50 to 2,000
μmの粒径を有している。 It has a particle size of [mu] m. また、上記トナーとキャリアとからなる現像剤を用いる場合、トナーは、通常2〜15 In the case of using a developer comprising the above toner and a carrier, the toner is generally 2 to 15
重量%用いられる。 It used wt%.

なお、上記感光体としては、セレン、セレン−テルル、酸化亜鉛、硫化カドミウム、アモルファスシリコン等の感光体も使用できるが、有機感光体、例えば、セレン−ポリビニルカルバゾール(PVK)複合感光体、ポリビニルカルバゾールと、2,4,7−トリニトロフルオレノンまたはテトラシアノ−p−キノジメタン(TCNQ)とからなる感光体や、複素環、縮合環等を有する感光性有機化合物を重合体中に含有する感光体等の有機感光体を用いる場合、この発明のトナー組成物は、特に、好適である。 As the above-mentioned photosensitive member, selenium, selenium - tellurium, zinc oxide, cadmium sulfide, but photoconductor such as amorphous silicon can be used, organic photoconductor, for example, selenium - polyvinylcarbazole (PVK) complexes photoreceptor, polyvinylcarbazole If, 2,4,7-consisting Lennon or tetracyano -p- quinodimethane and (TCNQ) photosensitive member or heterocyclic, such as a photosensitive member containing a photosensitive organic compound having a condensed ring, in the polymer when using an organic photoconductor, the toner compositions of this invention is especially suitable.

上記トナー組成物は、従来公知の現像方法、例えば、 The toner composition, conventionally known developing methods, for example,
一成分トナーであるときは、毛ブラシ現像法、磁気ブラシ現像法、パウダークラウド現像法により、また二成分トナーであるときは、カスケード現像法、磁気ブラシ現像法等により現像される。 When a one-component toner, bristle brush development, magnetic brush development, the powder cloud development method, when also a two-component toner, the cascade developing method, is developed by the magnetic brush developing method or the like.

以下に、この発明のトナー組成物の一製造方法について簡単に説明する。 The following briefly describes an method for producing a toner composition of the present invention. まず、結着樹脂、着色剤等を含有する粉体トナーを製造する。 First, to produce a powder toner containing a binder resin, a colorant and the like. この粉体トナーは、従来公知の方法、例えば、前記結着樹脂と着色剤等を熱ロール、 The powder toner is a conventionally known method, for example, a hot roll the coloring agent and the binder resin,
エクストルーダー等の加熱混合器を用いて混合分散し、 It was mixed and dispersed using an extruder heated mixer, such as chromatography,
ハンマーミル、ジェットミル等の粉砕機により粉砕すると共に、分級機により分級して所定の粒径に揃える機械的粉砕法や、前記結着樹脂の溶液に前記着色剤等を分散させ、所定の粒径に噴霧乾燥する噴霧乾燥法等により製造することができる。 Hammer mill, the pulverized by a pulverizer such as a jet mill, and classified by a classifier or mechanical grinding method to align to a predetermined particle size, dispersing the coloring agent in a solution of the binder resin, predetermined particle it can be prepared by spray drying method or the like to spray drying in a radial. そして、上記トナーに、所定量の前記脂肪酸金属塩、研磨物質および電気抵抗調整剤を添加し、ボールミル、V型混合機等適宜の混合機を用いて均一に混合することにより、この発明のトナー組成物を製造することができる。 Then, the toner, a predetermined amount of said fatty acid metal salt was added abrasive material and the electrical resistance adjusting agent, a ball mill, by uniformly mixing using a V-type mixer such as a suitable mixer, the toner of the present invention it can be prepared composition.

〈実施例〉 以下に、実施例に基き、この発明をより詳細に説明する。 To <Example> Hereinafter, based on Examples, to explain this invention in greater detail.

実施例1 結着樹脂としてのスチレン−アクリル共重合体90重量%、着色剤としてのカーボンブラック7.5重量%、オフセット防止剤としてのポリプロピレン1.5重量%、電荷制御剤としてのニグロシン染料1.0重量%を用い、常法により、平均粒径5〜20μmを有する粉体トナーを作製した。 Using acrylic copolymer 90 wt%, carbon black 7.5 wt% as a colorant, polypropylene 1.5 wt% as an offset preventing agent, 1.0 wt% nigrosine dye as a charge control agent - styrene as in Example 1 Binder resin , by a conventional method to prepare a toner powder having an average particle size 5 to 20 [mu] m. このトナー100重量部に対して、ステアリン酸亜鉛を表1に示す割合で添加すると共に、疎水性シリカ(「アエロジルR972」、日本アエロジル(株)製)0.2 For this toner 100 parts by weight of zinc stearate with added in the proportions shown in Table 1, the hydrophobic silica ( "Aerosil R972", manufactured by Nippon Aerosil Co.) 0.2
重量部、酸化アルミニウム(「アルミニウムオキサイドC」、日本アエロジル(株)製」0.2重量部を添加して均一に混合し、トナー組成物を作製した。 Parts, aluminum oxide ( "Aluminum Oxide C" manufactured by Nippon Aerosil Co., Ltd. "and 0.2 part by weight of uniformly added and mixed to prepare a toner composition.

また、上記トナー組成物4.5重量%と、平均粒径50〜8 Further, the above-described toner composition 4.5 wt%, average particle diameter 50-8
0μmのフェライトキャリア95.5重量%とをボールミルにて均一に混合し、現像剤を作製した。 A ferrite carrier 95.5 wt% of 0μm uniformly mixed in a ball mill to prepare a developer.

そして、上記現像剤を用い、有機感光層を有する感光体を備えた複写機(三田工業(株)製DC−111型改造機)にて、現像特性を調べたところ、表1に示す結果を得た。 Then, using the developer, a copying machine having a photosensitive member having an organic photosensitive layer at (Mita Industrial Co., Ltd. DC-111 type modified machine), were examined development characteristics, the results shown in Table 1 Obtained.

表1の結果から明らかなように、ステアリン酸亜鉛が未添加であると感光体へのトナーの融着が生じ、また添加量が0.03重量部以上であると、感光体へのフィルミング化が生じる。 Table from 1 results evident, fusion of the toner occurs between the zinc stearate is not added to the photosensitive member, and when the addition amount is 0.03 parts by weight or more, the filming of the photosensitive member occur. これに対して、ステアリン酸亜鉛の添加量が0.01重量部以下であると、感光体へのトナーの融着、フィルミングおよび画像のニジミも生じないことが判明した。 In contrast, if the amount of zinc stearate is less than 0.01 part by weight, melt-adhesion of toner to the photosensitive member, that does not occur bleeding of filming and image were found. なお、感光体へトナーが融着したものは、融着したトナーに基づく黒すじが画像に見られた。 Incidentally, what the toner to the photosensitive member are fused, black streaks based on fused toner was observed on the image.

実施例2 上記実施例1の粉体トナー100重量部にステアリン酸亜鉛0.01重量部、および実施例1の酸化アルミニウム0. Aluminum oxide 0 Example 2 Example 1 above powder toner zinc stearate 0.01 parts by weight to 100 parts by weight, and Example 1.
2重量部を添加すると共に、上記実施例1の疎水性シリカを表2に示す割合でそれぞれ添加し、トナー組成物を作製した。 With the addition of 2 parts by weight, the hydrophobic silica of Example 1 was added each in a proportion shown in Table 2, to prepare a toner composition. そして、上記実施例1と同様にして画像特性を調べたところ、第2表に示す結果を得た。 Then, it was examined image characteristics in the same manner as in Example 1 to obtain the results shown in Table 2.

表2から明らかなように、疎水性シリカが未添加のものは、トナーの流動性が悪く、また、疎水性シリカをの添加量が0.4重量部以上であると感光体に傷がつき、感光体を保護することができなかった。 As is evident from Table 2, those hydrophobic silica is not added, the fluidity of the toner is poor, The amount of the hydrophobic silica is scratched photoconductor is 0.4 parts by weight or more, the photosensitive It was not able to protect the body. これに対して、疎水性シリカの添加量が0.05〜0.3重量部のものは、トナーの流動性がよく、感光体を保護することができると共に、感光体表面でのトナーの融着がなく、画像特性も優れていた。 In contrast, the addition amount of the hydrophobic silica include the 0.05 to 0.3 parts by weight, good fluidity of the toner, it is possible to protect the photosensitive member, there is no toner fusion on the photoreceptor surface, image characteristics were also excellent.

実施例3 上記実施例1の粉体トナー100重量部にステアリン酸亜鉛0.01重量部、および実施例1の疎水性シリカ0.2重量部を添加すると共に、上記実施例1の酸化アルミニウムを表3に示す割合でそれぞれ添加し、トナー組成物を作製した。 Example 3 Example 1 above powder toner 100 by weight 0.01 part by weight of zinc stearate in section, and the hydrophobic silica 0.2 parts by weight of the Example 1 with the addition, Table 3 shows the aluminum oxide of Example 1 respectively added at a ratio, to prepare a toner composition. そして、上記実施例1と同様にして画像特性を調べたところ、第3表に示す結果を得た。 Then, it was examined image characteristics in the same manner as in Example 1 to obtain the results shown in Table 3.

表3から明らかなように、酸化アルミニウムが未添加のものは、トナーの流動性が悪く、また、添加量が0.4 As is apparent from Table 3, those of aluminum oxide is not added, the fluidity of the toner is poor, also the amount of addition is 0.4
重量部以上であると、トナーの流動性が低下し、感光体に傷が付くと共に、画像のニジミも生じた。 If it is parts by weight or more, decrease the fluidity of the toner, along with scratched the photoreceptor, resulting also blurring of the image. これに対して、酸化アルミニウムの添加量が0.05〜0.3重量部のものは、いずれも、トナーの流動性がよく、感光体の傷つき、画像のニジミも生じることなく、階調性に優れた画像が得られた。 Image contrast, the addition amount of aluminum oxide that of 0.05-0.3 parts by weight, both the fluidity of the toner is good, damage of the photosensitive member, image bleeding even without producing, with excellent gradation was gotten. なお、酸化アルミニウムの添加量が増すにつれて、現像剤の電気抵抗値が低下し、酸化アルミニウムの添加量によりトナーの電気抵抗を調整できることが判明した。 Incidentally, as the additive amount of aluminum oxide is increased, it reduces the electric resistance of the developer, it can adjust the electrical resistance of the toner was found by the addition of aluminum oxide.

〈発明の効果〉 以上のように、この発明のトナー組成物によればれば、脂肪酸金属塩の添加量が少量であり、感光体表面で脂肪酸金属塩がフィルミング化し難く、また、万一、上記脂肪酸金属塩によるフィルミング化が生じても前記研磨物質により、脂肪酸金属塩のフィルムが研磨されて清浄化されるので、感光体を保護することができ、感光体のクリーニング時にも感光体表面でトナーがすじ状に融着するのを防止することができる。 As more <Effects of the Invention> In Re according to the toner compositions of the present invention, a minor amount of added fatty acid metal salts, fatty acid metal salt is less likely to filming of the photosensitive member surface, also unlikely by the abrasive material even when filming reduction by the fatty acid metal salt, the film of the fatty acid metal salt is cleaned and polished, it is possible to protect the photosensitive member, the photosensitive member surface even when the cleaning of the photosensitive member in the toner can be prevented from being fused to stripes. また、脂肪酸金属塩の添加量が少量であるため、トナー、現像剤の電気抵抗が殆ど低下せず、トナーの特性、画像特性に悪影響を及ぼさない。 Moreover, since the addition amount of the fatty acid metal salt is small, toner, the electric resistance of the developer does not drop almost does not adversely affect properties of the toner, the image characteristics. また、研磨物質の添加により、トナーの流動性、ひいてはトナーの帯電特性、画像特性が改善されるだけでなく、電気抵抗調整剤の添加によりトナー、現像剤の電気抵抗を調整することができるので、高品質の画像が得られるというこの発明特有の効果を奏する。 Further, the addition of abrasive material, the flowability of the toner, thus the toner charging characteristics, not only the image characteristics are improved by the addition of the electric resistance adjusting agent toner, it is possible to adjust the electric resistance of the developer achieves the present invention unique effect that a high quality image is obtained.

───────────────────────────────────────────────────── フロントページの続き (72)発明者 松井 利一 大阪府大阪市東区玉造1丁目2番28号 三 田工業株式会社内 (56)参考文献 特開 昭53−81127(JP,A) 特開 昭59−229567(JP,A) 特開 昭58−125046(JP,A) 特開 昭60−262172(JP,A) 特開 昭56−140356(JP,A) 特開 昭61−7846(JP,A) 特開 昭58−152257(JP,A) 特開 昭61−188546(JP,A) 特開 昭61−188549(JP,A) 特開 昭61−56353(JP,A) ────────────────────────────────────────────────── ─── of the front page continued (72) inventor Toshikazu Matsui Osaka, Osaka, Higashi-ku, Tamatukuri No. 1-chome No. 2 28 Mita industrial Co., Ltd. in the (56) reference Patent Sho 53-81127 (JP, a) JP open Akira 59-229567 (JP, A) JP Akira 58-125046 (JP, A) JP Akira 60-262172 (JP, A) JP Akira 56-140356 (JP, A) JP Akira 61-7846 ( JP, A) JP Akira 58-152257 (JP, A) JP Akira 61-188546 (JP, A) JP Akira 61-188549 (JP, A) JP Akira 61-56353 (JP, A)

Claims (4)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】結着樹脂、着色剤および他の添加剤を含有する粉体トナー100重量部に対して、その添加重量部x 1. A binder resin, a colorant and the powder 100 parts by weight of the toner containing other additives, the addition parts x
    が下記関係式を充足する脂肪酸金属塩と、 0<x≦0.01(重量部) 上記粉体トナー100重量部に対して0.05〜0.3重量部の研磨物質と、上記粉体トナー100重量部に対して0.05〜0.3 There the fatty acid metal salt that satisfies the following relational expression, 0 <a polishing material 0.05 to 0.3 parts by weight with respect to x ≦ 0.01 (parts by weight) the powder toner 100 parts by weight, relative to the powder toner 100 parts by weight Te 0.05 to 0.3
    重量部の電気抵抗調整剤とが添加されていることを特徴とするトナー組成物。 The toner composition, characterized in that the electrical resistance adjusting agent of the weight part is added.
  2. 【請求項2】脂肪酸金属塩が、ステアリン酸亜鉛である上記特許請求の範囲第1項記載のトナー組成物。 Wherein the fatty acid metal salt, the patent toner compositions ranging first claim of claim zinc stearate.
  3. 【請求項3】研磨物質が、シリカである上記特許請求の範囲第1項記載のトナー組成物。 Wherein the polishing material is above patent toner compositions ranging first claim of claim it is silica.
  4. 【請求項4】電気抵抗調整剤が、酸化アルミニウムである上記特許請求の範囲第1項記載のトナー組成物。 4. The electrical resistance adjusting agent, the above-mentioned patent toner compositions ranging first claim of claim aluminum oxide.
JP61242601A 1986-10-13 1986-10-13 Toner - composition Expired - Fee Related JPH0833681B2 (en)