JPH08253665A - 帯電防止性のポリ乳酸組成物及びその成型品 - Google Patents
帯電防止性のポリ乳酸組成物及びその成型品Info
- Publication number
- JPH08253665A JPH08253665A JP7058893A JP5889395A JPH08253665A JP H08253665 A JPH08253665 A JP H08253665A JP 7058893 A JP7058893 A JP 7058893A JP 5889395 A JP5889395 A JP 5889395A JP H08253665 A JPH08253665 A JP H08253665A
- Authority
- JP
- Japan
- Prior art keywords
- polylactic acid
- block copolymer
- polyalkylene ether
- composition according
- polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
的少量の混合で優れた制電性が得られる、改良された新
しいポリ乳酸組成物を提供する。 【構成】 乳酸を主成分とする重合体(A)の中に、ポ
リ乳酸とポリアルキレンエーテルのブロック共重合体
(B)を混入する。制電性(B)中のポリアルキレンエ
ーテル成分が優れた制電性を発揮すると共に、ポリ乳酸
成分が母体ポリマー(A)との親和性を高めるので、制
電性(B)は母体ポリマー(A)中に微細に分散され
て、制電性、透明性、光沢などに優れた成型品が得られ
る。
Description
及びその成型品に関する。
リマーが、環境保護の見地から注目されている。特にポ
リ乳酸は、農産物を原料とするため、資源的にも有利
で、更に溶融成型性や耐熱性に優れるために最も期待さ
れている。しかし、未変性のポリ乳酸は、結晶性が高く
吸水性も低いために、摩擦やはく離によって容易に帯電
し、色々の静電気トラブルを発生する。このため帯電防
止性に優れたポリ乳酸が求められている。
成樹脂に、ポリエーテル、特にポリエチレングリコール
又はその変性体を混合し、帯電防止性(以下制電性と記
す)を付与することは周知である。しかしポリエチレン
グリコールをポリ乳酸に混合すると、両者の親和性が小
さいために、ポリエチレングリコールは比較的大きい粒
子状に混合され、充分な制電性を得るにはかなり多量に
混合しなくてはならず、又成型品の透明度や光沢が損な
われるという問題が生じる。
品の透明性や光沢の低下を抑え、且つ比較的少量の混合
率で優れた制電性が得られる、改良された新しいポリ乳
酸組成物を提供するにある。
的は、乳酸を主成分とする重合体(A)と、ポリアルキ
レンエーテルとポリ乳酸とのブロック共重合体(B)と
を含む混合組成物のうち、前記ブロック共重合体(B)
を重量比率が0.3〜50%の範囲で混合することによ
り達成される。
リL−乳酸、ポリD−乳酸、ポリL/D−乳酸などのポ
リ乳酸ホモポリマー、及びそれらにエステル結合形成性
の重合材料を共重合した共重合ポリ乳酸で、重合体中の
乳酸由来の成分が50重量%以上のものを言う。
オキシド)は、エーテル結合によって電気伝導性がある
が、制電剤としてはポリエチレングリコール、ポリプロ
ピレングリコール及びそれらの共重合物が制電性に優れ
ており、特にポリエチレングリコール及びその変性体が
最も優れた制電性を持っている。
乳酸とポリアルキレンエーテルのブロック共重合体
(B)を用いることにある。このブロック共重合体は、
ポリ乳酸セグメント(L)とポリアルキレンエーテルセ
グメント(E)とが1対1でL・Eの型に結合したもの
でもよく、2:1又は1:2でL・E・L,E・L・E
のような型に結合してもよく、同じくL・E・L・E・
L・Eなどのように多数のセグメント(ブロック)が結
合されていてもよい。又、両者の間に第3成分が継手と
して入っていてもよく、更にこれら以外の副次成分が加
わっていてもよい。しかし主たる成分(50重量%以
上)はポリアルキレンエーテルとポリ乳酸である。
きは、制電剤(B)と母体(マトリクス)ポリマーであ
るポリ乳酸(A)との親和性を高めるものである。両者
の親和性が高いほど、制電剤は母体ポリマー中に微細に
分散され、制電性、透明性、光沢などに優れた成型品が
得られる。しかし、制電剤中のポリ乳酸セグメントが多
過ぎると、ポリエーテルセグメントが減少し制電性が劣
るようになる。このため制電剤(B)中のポリアルキレ
ンエーテル成分の重量分率は、50〜97%が好まし
く、70〜95%が特に好ましい。すなわち制電剤
(B)中のポリ乳酸成分の重量分率は、3〜50%、特
に5〜30%が好ましい。
が、或程度大きいことが好ましく、例えば分子量1,0
00以上、特に3,000以上が好ましく、5,000
以上が更に好ましく10,000〜200,000が最
も広く用いられる。
較的容易である。例えば1方の末端を封鎖し、片末端に
水酸基を持つポリエチレングリコールをラクチドの重合
開始剤としてラクチドを重合すれば、L・E型のブロッ
ク共重合体が得られ、両末端に水酸基を持つポリエチレ
ングリコールを重合開始剤にすれば、L・E・L型のブ
ロック共重合体が得られる。同じく片末端又は両末端に
水酸基を持つポリエチレングリコールとポリ乳酸に、ジ
カルボン酸無水物、ジカルボン酸塩化物、ジイソシアネ
ートなどの2官能性化合物を反応させて、両者を連結す
ることが出来る。更に末端に水酸基を有するポリ乳酸に
アルキレンオキシド、例えばエチレンオキシドを付加重
合させてポリエチレングリコール鎖を形成し、ブロック
共重合体とすることが出来る。これらの反応において、
ポリアルキレンエーテルブロックの分子量、ポリ乳酸ブ
ロックの分子量を制御するのも比較的容易である。例え
ば、分子量8,000のポリエチレングリコール80部
と、ラクチド20部とが完全且つ均一に反応(重合)す
れば、分子量8,000のポリエチレングリコールの両
末端に重合度10のポリ乳酸(オリゴマー)が結合した
L・E・L型のブロック共重合体が得られる筈である。
実際には、平均値としてはそうなるが、かなりバラツキ
が生じ、各種の化合物の混合物が得られるが、その混合
物の主成分は、ポリエチレングリコールとポリ乳酸との
ブロック共重合物であり、混合物をそのまま制電剤とし
て用いて一向に差支えない。
キシル基などの官能基は、そのままでもよいが、単官能
基性化合物と反応させて鎖鎖して安定化すると更に好ま
しい。
い。一般にポリエチレングリコールの体積抵抗率は1×
109 オーム・cm程度(25℃,40%RH,直流1k
V以下で測定)であり、ポリ乳酸と共重合すると1×1
010オーム・cm程度に増大する。しかしこれらに電離し
易い化合物、例えばアルキルベンゼンスルホン酸ナトリ
ウムなどを2〜20%程度混合して、体積抵抗率を1×
10 8〜9 オーム・cm程度以下としたものが好適であ
る。本発明の組成物及び成型品の体積抵抗率は1×10
12オーム・cm以下、特に1×1011オーム・cmが好まし
い。制電剤(B)には、副次的添加剤として、ヒンダー
トフェノールなどの酸化防止剤、各種安定剤、紫外線吸
収剤、その他の添加剤を加えることが出来る。
合は、機械的撹拌、静止混合器の応用、両者の併用など
任意である。混合は母体ポリマー(A)の重合後に行な
うのが一般的である。重合原料や重合工程中に添加する
と相互に反応して共重合し、制電性が失われたり、低下
することがある。優れた制電性は、制電剤が母体ポリマ
ー中に分散した微細粒子、微細繊維、網状構造、薄層状
などの形態で独立して存在する必要がある。共重合によ
ってポリアルキレンエーテルブロックが母体ポリマー分
子に組込まれると、かなり多量のポリアルキレンエーテ
ルを用いる必要があり、物性の劣化を招き好ましくな
い。
クリュー押出機、2軸混練機、ニーダー、ギヤポンプな
どを利用して行なうことが出来る。一方静止混合器を用
い、流れの分割と接合(複合)の繰返しによって静的に
混合すると、制電剤(B)を母体ポリマー(A)中に薄
層状、微細繊維状など、連続する構造で微細に分散する
ことが出来る。静止混合器の例としては、本発明者ら特
公昭47−15526、同47−15527、同47−
15528、同47−15533,などで開示したも
の、及び特開昭47−34166に開示されたものなど
があげられる。機械的撹拌と静止混合器を併用すること
も出来る。例えば静止混合器で多層混合後、ギヤポンプ
で計量送液すると、ポンプ部分で機械的に撹拌され、制
電剤は微細な粒子状に分散される。勿論制電性は、連続
構造の方が格段に優れ、粒状(不連続)構造の1/5〜
1/10の制電剤の混合率で、同等の制電性が得られる
ことが多い。
は、制電剤の導電性、制電剤の組成や体積抵抗率によっ
て異なるが、多くの場合0.3〜50重量%、特に0.
5〜30%の範囲が好適である。前述のように、制電剤
が繊維状、網状、薄膜状などの連続構造で分散・混合さ
れていると電気伝導性に優れ、比較的少量の混合率、例
えば0.3〜10%、特に0.5〜5%で優れた制電性
が得られる。一方、制電剤が粒子状、細長い粒子状、針
状などの非連続構造で分散・混合されていると、比較的
多くの制電剤を必要とし、例えば3〜50%,特に5〜
30%の混合率が好適である。非連続と連続との混合構
造、例えば粒状と繊維状とが混在する構造では、両者の
中間の混合率が好適である。
重合体(A)及び制電剤(B)の他に、副次的に他の成
分を添加してもよい。副次的添加剤の例としては、安定
剤、酸化防止剤、紫外線吸収剤、顔料、着色剤、各種無
機粒子、各種フィラー、撥水剤、親水剤、離型剤、可塑
剤、生理活性物質、防腐剤、抗菌剤、発泡剤その他類似
のものがあげられる。
は、特記しない限り重量比、重量分率で示す。乳酸を主
成分とする重合体の分子量は、試料のクロロホルム 0.1
%溶液のGPC分析で、分子量 500以下を除く、高分子
物の分散の、重量平均値である。
コール80部、光学純度99%以上のL−ラクチド20
部に対し、重合触媒としてオクチル酸錫0.1%,酸化
防止剤としてチバガイギー社イルガノックス1010を0.
1%を混合し、窒素雰囲気中180℃で45分間反応さ
せて得たポリエチレングリコールとポリ乳酸のブロック
共重合物(体積抵抗率3×109 オーム・cm)を制電
剤AS1とする。
し、オクチル酸錫0.03%、直径0.05μmの酸化
チタン粒子(結晶核剤)を混合し、2本のスクリュウが
互いに噛み合う2軸連続混合送液機を用い、窒素雰囲気
中180℃で連続的に、平均30分間反応させ、次にオ
クチル酸錫を0.1%添加し、互いに噛み合うスクリュ
ウ群と、互いに噛み合う長円形(2フライト型)の撹拌
素子群からなる2軸混練機を用い、190℃で17分間
重合し、最終ベント孔より、溶融し水分量5ppm以下
とした制電剤AS1を、重合系に対し7%添加、混合
し、更にケニックス社スタティックミキサー60素子を
組入んだ円筒を通過させて混合した後、口金より押出
し、水で冷却、固化、切断してチップC1を得た。
熱処理し、更に140℃で48時間熱処理(固相重合)
してチップC2を得た。チップC2の平均分子量は15
2,000、残存モノマー(ラクチド)量は0.3%で
あった。
で溶融し、孔径0.2mm,温度195℃のオリフィス
より紡出し、空気中で冷却後オイリングして800m/
minの速度で巻取り、次に延伸温度80℃で3.7倍
に延伸し、緊張下120℃で熱処理して繊度75デニー
ル/24フィラメントの延伸糸Y1を得た。
S1を添加しないで得た延伸糸をY2とする。
型丸編機を用いチューブ編物K1を得た。編物K1をJ
IS L 1094−1988に従って家庭用洗剤及び
家庭用電気洗濯機を用いて3回洗濯し、水流中で充分す
すいだ後、80℃の熱風乾燥機で2時間乾燥後、25
℃,33%RHの恒温室中に24時間放置した後、その
摩擦帯電性を測定した。
JIS L 1094−1988に参考法「摩擦帯電放
電曲線測定法」として規定されており、繊維機械学会誌
vol.40,No.4,p181−188(198
7)及び特公昭62−11303に開示した方法によっ
た。すなわち、洗濯した試料を長さ12cm,幅12c
mに切断し、直径7cmの孔のある金属板に取付け、木
製台で試験片と同様に洗濯、乾燥、調湿した羊毛織物を
摩擦布とし、手動で10回摩擦した後、台より引離し電
位検出器の前に移動し、摩擦帯電圧とその減衰曲線を記
録計で自記記録する。
用いて得た編物K2の摩擦帯電性を測定した。更に比較
のため、分子量20,000のポリエチレングリコール
を制電剤として7%混合し、以下編物K1と同様にして
得た編物K3の帯電性を測定した。
圧及び摩擦1分後の帯電圧を表1に示す。表1に見るよ
うに本発明による編物K1は、比較例K2及びK3に較
べて帯電圧(特に1分後)の絶縁値が低く、制電性に優
れていた。
アジペート15部と光学純度99%以上のL−ラクチド
85部を180℃で45分間、溶融共重合して得たポリ
乳酸とポリブチレンアジペートのブロック共重合物をポ
リマーP3とする。ポリマーP3の分子量は163,0
00で、これを温度200℃のスクリュウ押出機で溶融
紡糸した。紡糸時に、別に溶融脱水した制電剤AS2を
静止混合機を内臓した紡糸口金内で0.7%混合して紡
糸した。制電剤AS2は、実施例1のAS1に、ドデシ
ルベンゼンスルホン酸ナトリウムを15%混合し、体積
抵抗率を1×108 まで低下せしめたものである。静止
混合器は、本発明者等が特公昭57−20842に開示
したもので、混合素子を12個直列に接続したものであ
る。静止混合機で多層状(薄層状)に混合された制電剤
は、オリフィス直前の最終フィルターで分断され、繊維
横断面では多点状に分散し、長さ方向には実質的に連続
する微細繊維状(線状)の形態となる。(米国ケニック
ス社のスタティックミキサーの混合素子を10〜12個
直列にしたものを用いても、ほぼ同様なものが得られ
る)。紡糸した繊維を、実施例1の延伸糸Y1、編物K
1と同様にして延伸、熱処理、編立、洗濯、乾燥、調湿
した編物K4の摩擦帯電性を測定し、表2の結果を得
た。表2に見るように、制電剤中に電離性の化合物を混
合し、又制電剤が母体ポリマー中に連続微細繊維状に混
合されることにより、極く少量の制電剤の混合で、高い
制電性が得られる。なお、編物の光沢及び透明感につい
ては、本発明による編物K1、K4が優れ、比較例の編
物K2,K3は光沢、透明感が劣っていた。(この相異
は、フィルムや肉厚の成型品では更に大きくなる)。
に優れた各種成形品が容易に得られる。例えば、繊維、
編物、織物、不織布、紙、綱、網、ロープ、フィルム、
シ−ト、板、棒、各種容器、チューブ、各種部品、その
他各種の成型品があげられる。本発明による制電性組成
物により、各種成型品の帯電による障害、すなわちゴ
ミ、細菌の付着による汚染、スカートやズボン、下着な
どのまとわりつき、火花放電による可燃物の引火、爆
発、火花放電による電子機器の誤動作、故障などが低減
又は防止され、更に光沢や透明度の高い優れた繊維、フ
ィルム、成型品が得られる。また、本発明制電剤(B)
は、弾性率が小さく衝撃吸収性に優れるため、本発明組
成物及び成型品は、副次的効果として、柔軟性や耐衝撃
性が改良される。
Claims (9)
- 【請求項1】 乳酸を主成分とする重合体(A)と、ポ
リアルキレンエーテルとポリ乳酸とのブロック共重合体
(B)とを含む混合組成物であって、前記ブロック共重
合体(B)の重量比率が0.3〜50%の範囲であるこ
とを特徴とする、帯電防止性のポリ乳酸組成物。 - 【請求項2】 ポリアルキレンエーテルが、「ポリエチ
レングリコール、ポリプロピレングリコール及びそれら
の共重合体」の群より選ばれた少なくとも1種のもので
ある、請求項1記載の組成物。 - 【請求項3】 ポリアルキレンエーテルとポリ乳酸との
ブロック共重合体(B)を構成するポリアルキレンエー
テルの重量分率が70〜95%である、請求項1〜2記
載の組成物。 - 【請求項4】 ポリアルキレンエーテルとポリ乳酸との
ブロック共重合体(B)の体積抵抗率が1×1010オーム
・cm以下である、請求項1〜3記載の組成物。 - 【請求項5】 ポリアルキレンエーテルとポリ乳酸との
ブロック共重合体(B)の混合比率が0.5〜30重量
%である、請求項1〜4記載の組成物。 - 【請求項6】 ポリアルキレンエーテルとポリ乳酸との
ブロック共重合体(B)の分子量が10,000以上で
ある、請求項1〜5記載の組成物。 - 【請求項7】 ポリアルキレンエーテルとポリ乳酸との
ブロック共重合体(B)が、微細な粒子状又は/及び針
状の形態で、母体である乳酸を主成分とする重合体
(A)の中に分散している、請求項1〜6記載の組成
物。 - 【請求項8】 ポリアルキレンエーテルとポリ乳酸との
ブロック共重合体(B)が、微細な繊維状、線状、網状
又は/及び薄層状で、母体である乳酸を主成分とする重
合体(A)の中に分散している、請求項1〜7記載の組
成物。 - 【請求項9】 請求項1〜8記載の組成物よりなる繊
維、編物、織物、不織布、紙、フェルト、網、ロープ、
フィルム、シート、板、棒、チューブ、容器、各種部品
及びその他の成型品。