JPH08127111A - Decorative sheet - Google Patents

Decorative sheet

Info

Publication number
JPH08127111A
JPH08127111A JP29045594A JP29045594A JPH08127111A JP H08127111 A JPH08127111 A JP H08127111A JP 29045594 A JP29045594 A JP 29045594A JP 29045594 A JP29045594 A JP 29045594A JP H08127111 A JPH08127111 A JP H08127111A
Authority
JP
Japan
Prior art keywords
layer
resin
pattern
sheet
decorative sheet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP29045594A
Other languages
Japanese (ja)
Inventor
Eiji Hinishi
英二 日西
Katsunori Nishijima
克典 西島
Ryotaro Sato
亮太郎 佐藤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toppan Printing Co Ltd
Original Assignee
Toppan Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toppan Printing Co Ltd filed Critical Toppan Printing Co Ltd
Priority to JP29045594A priority Critical patent/JPH08127111A/en
Publication of JPH08127111A publication Critical patent/JPH08127111A/en
Pending legal-status Critical Current

Abstract

PURPOSE: To provide a decorative sheet having a design feeling very similar to natural wood by expressing the movement of a glossy feeling by the change in the reflecting direction of light due to a looking angle. CONSTITUTION: In a decorative sheet, a layer 2 having an uneven shape is formed on the surface of a base material sheet 1 and brilliant parts 3 are formed by filling the recessed parts of the layer 2 with a resin containing a brilliant material and a picture pattern printing layer 4 and a topcoat layer 5 are successively formed on the brilliant parts 3.

Description

【発明の詳細な説明】Detailed Description of the Invention

【0001】[0001]

【産業上の利用分野】本発明は、家具、住宅内装壁面、
天井、住宅部材などに使用される化粧シートに関するも
のであり、さらに詳しくは、見る方向により木目絵柄模
様等の底部での照り感が移動するように見えるような光
輝層を形成することにより、極めて天然木に酷似した意
匠感が得られる化粧シートに関するものである。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to furniture, interior wall surfaces of houses,
The present invention relates to a decorative sheet used for a ceiling, a housing member, and the like, and more specifically, by forming a glitter layer that makes it appear that the feeling of light at the bottom of a woodgrain pattern or the like moves depending on the viewing direction, The present invention relates to a decorative sheet that gives a design feeling very similar to natural wood.

【0002】[0002]

【従来の技術】従来より天然木に酷似した照り感を表現
しようとして、輝度感を持つ木目絵柄模様の化粧シート
を製造する方法は広く行われている。
2. Description of the Related Art Conventionally, a method for producing a decorative sheet having a wood grain pattern having a brightness feeling has been widely used in order to express a feeling of luster much like natural wood.

【0003】最も代表的な手段としては、絵柄模様の底
部に光輝性材料による輝度感のある層を形成するもので
あり、その具体的な方法としては、基材シートに光輝性
材料を練り込んで光輝層とする方法や、基材シートに全
面ベタもしくは絵柄模様にて光輝性材料を含むインキで
印刷して光輝層を形成する方法などが用いられ、その上
に所望の絵柄模様を印刷して化粧シートを得ようとする
ものである。
[0003] The most typical means is to form a layer having a feeling of brightness by a glittering material on the bottom of a picture pattern, and a concrete method thereof is to knead the glittering material into a base sheet. Method to form a glitter layer, or a method of forming a glitter layer by printing with ink containing a glittering material on the entire surface of a base material sheet or in a pattern pattern is used, and a desired pattern pattern is printed on it. To obtain a decorative sheet.

【0004】[0004]

【発明が解決しようとする課題】しかしながら、上記印
刷によって光輝層を形成する方法においては、形成した
光輝層の印刷面の凹凸の差が少ないと、単に輝度感はあ
っても、見る角度により光の反射方向が変化して照り感
が移動するような意匠効果はほとんどない。また、基材
シートに光輝性材料を練り込む方法でも光輝層の凹凸の
差はほとんどないので、意匠効果の点では印刷による場
合と同等である。
However, in the method for forming the glitter layer by the printing described above, if the difference in the unevenness of the printing surface of the formed glitter layer is small, the brightness may vary depending on the viewing angle, even if the brightness is simply sensed. There is almost no design effect in which the direction of reflection changes and the feeling of light moves. Further, even when the glittering material is kneaded into the base material sheet, there is almost no difference in the unevenness of the glittering layer, and therefore the design effect is the same as in the case of printing.

【0005】一方、光輝層を盛り上げ印刷などによって
凹凸の差をつけることも可能であるが、その上に絵柄模
様を印刷しようとすると凹部はほとんどインキが着肉さ
れずに絵柄抜けになってしまい、化粧シートとしての役
目を果たさない。
On the other hand, it is possible to make unevenness by printing the glitter layer by printing and the like, but if a pattern is printed on it, almost no ink will be inked in the recesses, resulting in a missing pattern. , Does not serve as a decorative sheet.

【0006】また、他の手段として、基材シート上に絵
柄模様の印刷を行い、その上に光輝性材料を含むインキ
で印刷する方法も行われているが、光輝層は最も上にあ
るので輝度感は十分に得られるが、光輝層の下に絵柄模
様があるため絵柄模様の底部での照り感の移動といった
意匠感が表現されず天然木の材質感は得られない。
[0006] As another means, a method of printing a pattern on a base material sheet and then printing with an ink containing a glitter material is also used, but since the glitter layer is on the top. A sufficient brightness can be obtained, but since there is a pattern under the glitter layer, a design feeling such as a shift of the shiny feeling at the bottom of the pattern cannot be expressed, and the feeling of the natural wood cannot be obtained.

【0007】すなわち、上述したような従来の方法で
は、輝度感はあっても、天然木の持っているような見る
方向によって照り感が移動するような材質感のある木目
模様柄の化粧シートは得られていない。
In other words, according to the conventional method as described above, a decorative sheet having a wood grain pattern, which has a feeling of brightness, but has a feeling of material in which the feeling of light moves depending on the viewing direction of natural wood, Not obtained.

【0008】本発明は、上記従来の問題に鑑み為された
ものであり、その目的とするところは、見る角度によっ
て光の反射方向が変化することにより照り感の移動を表
現して、極めて天然木に酷似した意匠感を有する化粧シ
ートを提供することにある。
The present invention has been made in view of the above-mentioned conventional problems, and an object thereof is to express a movement of a feeling of light by changing a reflection direction of light depending on a viewing angle, and to realize a very natural feeling. An object of the present invention is to provide a decorative sheet having a design feeling very similar to wood.

【0009】[0009]

【課題を解決するための手段】上記目的を達成するため
に、本発明の化粧シートは、基材シートに凹凸形状を形
成し、その凹部に光輝性材料を含む樹脂を充填した光輝
部を形成し、さらにその上に所望の絵柄模様層を設けて
なることを特徴としている。
In order to achieve the above object, the decorative sheet of the present invention has a base sheet having an uneven shape, and the concave portion is provided with a glitter portion filled with a resin containing a glitter material. In addition, a desired pattern layer is further provided thereon.

【0010】また、本発明の化粧シートは、前記基材シ
ート上に電離放射線硬化型樹脂を塗布し、その樹脂面を
エンボスロールに圧着し、前記基材シートの裏面より電
離放射線を照射して前記樹脂を硬化させることにより前
記凹凸形状が形成されていることを特徴としている。
In the decorative sheet of the present invention, an ionizing radiation curable resin is applied onto the base sheet, the resin surface is pressure-bonded to an embossing roll, and the back surface of the base sheet is irradiated with ionizing radiation. The uneven shape is formed by curing the resin.

【0011】以下、本発明の構成をさらに詳しく説明す
る。
The structure of the present invention will be described in more detail below.

【0012】図1は本発明の化粧シートの一構成例を示
す断面図である。これによると、基材シート1の表面に
凹凸形状の層2が形成されており、その凹部に光輝性材
料を含む樹脂を充填した光輝部3が形成され、その上に
絵柄模様印刷層4、さらにその上にトップコート層5が
それぞれ形成されている。
FIG. 1 is a sectional view showing an example of the constitution of the decorative sheet of the present invention. According to this, the uneven layer 2 is formed on the surface of the base material sheet 1, the glitter portion 3 filled with the resin containing the glitter material is formed in the recess, and the pattern printed layer 4, Further, a top coat layer 5 is formed on each of them.

【0013】上記基材シート1としては、紙、塩化ビニ
ル樹脂フィルムなどのプラスチックフィルムなどが使用
可能であるが、特に限定はされない。
The base sheet 1 may be paper, plastic film such as vinyl chloride resin film, or the like, but is not particularly limited.

【0014】上記基材シート1の表面に凹凸を形成する
方法として、一般には加熱加圧エンボスによる方法や盛
り上げ印刷による方法があるが、いずれの方法もエンボ
スロールや盛り上げ印刷版の形状をそのまま100%凹
凸形状として再現することは困難であり、本発明者等の
実験したところでは概ね70%程度しか再現することが
出来なかった。
As a method for forming irregularities on the surface of the substrate sheet 1, generally, there are a method by heat and pressure embossing and a method by raised printing. In either method, the shape of the embossing roll or the raised printing plate is kept as it is. % It is difficult to reproduce as a concavo-convex shape, and in experiments conducted by the present inventors, it was possible to reproduce only about 70%.

【0015】そこで本発明では、最も好適な方法とし
て、基材シート1の表面に電離放射線硬化型樹脂を塗布
し、その樹脂面を凹凸形状を形成したエンボスロールに
圧着し、基材シート1の裏面より電離放射線を照射して
上記樹脂を硬化させた後、エンボスロールから基材シー
ト1を離型させて凹凸形状の層2を基材シート1の表面
に形成する方法を選択することにより、エンボスロール
の凹凸形状をほぼ100%再現させることが出来て、凹
凸差のある凹凸形状を容易に形成することが出来る。
Therefore, in the present invention, as the most suitable method, the surface of the base material sheet 1 is coated with an ionizing radiation curable resin, and the resin surface is pressure-bonded to an embossing roll having an uneven shape to form a base material sheet 1 By irradiating ionizing radiation from the back surface to cure the resin, the base sheet 1 is released from the embossing roll, and a method for forming the uneven layer 2 on the surface of the base sheet 1 is selected. Almost 100% of the uneven shape of the embossing roll can be reproduced, and the uneven shape having unevenness can be easily formed.

【0016】ところで、凹凸形状の層2は基材シート1
が木目絵柄模様の下地色に着色されている場合は透明も
しくは半透明であることが望ましいが、基材シート1の
隠ぺい性が低い場合は木目絵柄模様の下地色などの着色
層としても構わない。また、この凹凸形状は均一な柄に
形成しても良いし、あるいは、上に設ける絵柄模様(例
えば木目絵柄模様)と同調するような柄に形成しても良
い。
By the way, the uneven layer 2 is the base sheet 1
Is preferably transparent or semi-transparent when the base color of the wood grain pattern is colored, but may be used as a colored layer for the base color of the wood pattern when the hiding property of the base sheet 1 is low. . Further, the uneven shape may be formed in a uniform pattern, or may be formed in a pattern that is in synchronization with a pattern pattern (for example, a wood grain pattern pattern) provided on the pattern.

【0017】ここで、電離放射線硬化型樹脂としては、
一般に、X線硬化型樹脂、電子線硬化型樹脂、紫外線硬
化型樹脂などが挙げられるが、照射装置のコスト等を考
えると、電子線硬化型樹脂、紫外線硬化型樹脂を使用す
るのが適当である。なお、照射線源として紫外線を用い
る場合は、上記基材シート1は紫外線を透過する透明性
のある材質でなければならない。
Here, as the ionizing radiation curable resin,
Generally, an X-ray curable resin, an electron beam curable resin, an ultraviolet curable resin, etc. are mentioned. However, considering the cost of the irradiation device, it is appropriate to use the electron beam curable resin or the ultraviolet curable resin. is there. When ultraviolet rays are used as the radiation source, the base material sheet 1 must be made of a transparent material that transmits ultraviolet rays.

【0018】ここで、電子線硬化型樹脂としては、例え
ばポリエステルアクリレート、エポキシアクリレート、
ウレタンアクリレートなどのアクリル酸エステルオリゴ
マーに粘度や硬化性などを調整するための単官能もしく
は多官能のモノマーを配合したものを主体とし、これに
着色顔料やシリカなどの体質顔料、その他添加剤を配合
して、粘度を数100〜数1000cpsに調整した固
形分がほぼ100%の電子線硬化型樹脂が好ましい。
Here, examples of the electron beam curable resin include polyester acrylate, epoxy acrylate,
Mainly composed of acrylic acid ester oligomers such as urethane acrylate mixed with monofunctional or polyfunctional monomers for adjusting viscosity and curability, etc., and mixed with extender pigments such as coloring pigments and silica, and other additives. Then, an electron beam curable resin having a solid content of almost 100% whose viscosity is adjusted to several hundred to several thousand cps is preferable.

【0019】電離放射線硬化型樹脂の塗布方法として
は、通常用いられる例えばグラビアコート法、グラビア
オフセットコート法、グラビアリバースコート法、ロー
ルコート法などを適宜選択することができる。
As a method for applying the ionizing radiation curable resin, a commonly used method such as a gravure coating method, a gravure offset coating method, a gravure reverse coating method and a roll coating method can be appropriately selected.

【0020】基材シート1上に塗布した電離放射線硬化
型樹脂の樹脂面を凹凸形状が形成されたエンボスロール
に圧着した状態で基材シート1の裏面より電離放射線を
照射して上記樹脂を硬化させるが、上記樹脂の硬化後、
エンボスロールと樹脂との離型性を良くするために、エ
ンボスロールの表面には予めクロムメッキなどが施され
ていることが望ましい。また、例えば電子線照射により
樹脂を硬化させる場合、電子線の加速電圧は150〜2
50kv、照射量は2〜10Mrad程度が好適であ
る。
Ionizing radiation is applied from the back surface of the base material sheet 1 in a state where the resin surface of the ionizing radiation curable resin applied on the base material sheet 1 is pressure-bonded to an embossing roll having an uneven shape to cure the resin. However, after curing the resin,
In order to improve the releasability between the embossing roll and the resin, it is desirable that the surface of the embossing roll is previously plated with chromium or the like. Further, for example, when the resin is cured by electron beam irradiation, the acceleration voltage of the electron beam is 150 to 2
50 kv, and the irradiation amount is preferably about 2 to 10 Mrad.

【0021】このようにして形成した凹凸形状の層2の
凹部に光輝性材料を含む樹脂を充填して光輝部3を形成
する。光輝部3に使用する樹脂としては、熱硬化、紫外
線硬化、電子線硬化といった硬化の形態や、溶剤、水な
どの希釈溶媒などには特に限定されないが、固形分が5
0%以上の樹脂(もしくはインキ)を使用することが望
ましい。固形分が50%未満であると、希釈溶媒の乾燥
による容積減少により、充填した凹部の平滑が得られな
くなる。但し、このように凹部の平滑に支障がでてきた
場合は、その上に透明のベタの樹脂層を形成して全面を
平滑にすることも可能である。光輝部3に使用する光輝
性材料としては、アルミニウム、銅、錫などの金属粉末
やパール顔料などが使用できる。このような光輝性材料
の使用量は特に限定されるものではないが、得られる輝
度感、凹凸形状の層2との固形分の密着性を考えると、
光輝性材料を固形分に対し10〜40%程度の範囲で含
有させて使用するのが望ましい。
A resin containing a glittering material is filled in the recesses of the uneven layer 2 thus formed to form a glittering portion 3. The resin used for the bright portion 3 is not particularly limited to a curing form such as heat curing, ultraviolet curing, electron beam curing, a solvent, a diluting solvent such as water, etc., but the solid content is 5
It is desirable to use 0% or more of resin (or ink). When the solid content is less than 50%, the volume of the diluted solvent is reduced by drying, and the filled concave portions cannot be smoothed. However, in the case where the smoothness of the concave portion is impaired in this way, it is possible to form a transparent solid resin layer on the concave portion to smooth the entire surface. As the glitter material used for the glitter portion 3, metal powder such as aluminum, copper, tin or the like, pearl pigment and the like can be used. The amount of such a glittering material used is not particularly limited, but considering the obtained brightness feeling and the adhesion of the solid content to the uneven layer 2,
It is desirable to use the glittering material in the range of about 10 to 40% based on the solid content.

【0022】ところで、凹凸形状の層2の凹部に光輝性
材料を含む樹脂を充填する方法としては、例えば、凹凸
形状の層2上の全面に上記樹脂をベタで塗工した後、凸
部の樹脂をドクターブレードもしくはドクターロールな
どで掻き落とす方法を選択することにより、巻き取り状
で連続して行うことが出来、効率も良く、好適である。
By the way, as a method of filling the concave portion of the uneven layer 2 with the resin containing the glittering material, for example, the above resin is solidly coated on the entire surface of the uneven layer 2 and then the convex portion is formed. By selecting a method of scraping off the resin with a doctor blade, a doctor roll or the like, it is possible to carry out the resin continuously in a wound state, which is efficient and suitable.

【0023】なお、上記の凹凸形状の層2の凹凸の差、
つまり凹部の深さは、本発明の効果が十分に発揮される
ためには、20〜100μm程度の範囲の深さであるこ
とが望ましい。
The difference in the unevenness of the uneven layer 2 is as follows.
That is, the depth of the recess is preferably in the range of about 20 to 100 μm so that the effect of the present invention can be sufficiently exerted.

【0024】光輝部3の上に形成する絵柄模様印刷層4
は、例えばグラビア印刷などの公知の印刷手段を用いて
形成することができる。絵柄模様としては、通常木目模
様が用いられるが、この他に例えば石目模様などを用い
ても良い。ここで、柄抜けが生じないように、光輝部3
の上面は全体にほぼ平滑であることが望ましい。
A picture pattern printing layer 4 formed on the glitter portion 3.
Can be formed using a known printing means such as gravure printing. As the picture pattern, a wood grain pattern is usually used, but other than this, for example, a stone grain pattern or the like may be used. Here, the glitter portion 3 is formed so that the pattern is not omitted.
It is desirable that the upper surface of is entirely smooth.

【0025】絵柄模様印刷層4の上には、図1に示すよ
うに、インキ面を保護するためのトップコート層5を設
けることが望ましい。トップコート層5の塗工方法は、
通常用いられる例えばグラビアコート法、グラビアオフ
セットコート法、グラビアリバースコート法、ロールコ
ート法などの方法を適宜選択して用い、使用するトップ
コート樹脂や硬化方法についても適当なものを適宜選択
することが出来る。
It is desirable to provide a top coat layer 5 for protecting the ink surface on the pattern print layer 4, as shown in FIG. The coating method of the top coat layer 5 is
Normally used methods such as gravure coating method, gravure offset coating method, gravure reverse coating method, and roll coating method can be appropriately selected and used, and the top coat resin to be used and the curing method can also be appropriately selected. I can.

【0026】本発明の化粧シートは、上述したように、
基材シート1の上に凹凸を形成する方法として、基材シ
ート上に塗工した電離放射線硬化型樹脂をエンボスロー
ルに圧着して樹脂を硬化させる方法を選択し、さらに形
成した凹部に光輝性材料含有樹脂を塗工、掻き取ること
による光輝部3の形成、絵柄模様印刷層4の形成、トッ
プコート層5の形成を一連のオンラインで行うことによ
り、巻き取り状態で連続的に製造することが可能であ
り、非常に効率的で安価な製造が行える。
The decorative sheet of the present invention, as described above,
As a method of forming irregularities on the base material sheet 1, a method of press-bonding an ionizing radiation curable resin coated on the base material sheet to an embossing roll to cure the resin is selected, and the formed recesses have a glitter property. Continuous production in a wound state by applying a material-containing resin and forming a bright portion 3 by scraping, forming a pattern printing layer 4, and forming a top coat layer 5 in a series of online. Is possible, and very efficient and inexpensive manufacturing can be performed.

【0027】[0027]

【作用】本発明の化粧シートは、基材シートの上に凹凸
形状の層を形成し、その凹部に光輝性材料を含む樹脂を
充填してほぼ平滑な面とすることにより凹凸の差のある
光輝部を形成し、その上に木目模様等の絵柄模様印刷層
を形成したものである。これによって、見る角度によっ
て光の反射方向が変化して、絵柄模様の底部での照り感
が移動するような意匠感を表現でき、極めて天然木に酷
似した材質感が得られる。
The decorative sheet of the present invention has unevenness by forming an uneven layer on the base material sheet and filling the concave portion with a resin containing a glittering material to form a substantially smooth surface. A bright portion is formed, and a picture pattern printing layer such as a wood grain pattern is formed thereon. As a result, the direction of light reflection changes depending on the viewing angle, and it is possible to express a design feeling in which the shining feeling at the bottom of the pattern moves, and a material feeling that is extremely similar to natural wood can be obtained.

【0028】[0028]

【実施例】以下、実施例により本発明をさらに具体的に
説明する。
EXAMPLES The present invention will be described in more detail below with reference to examples.

【0029】坪量60g/m2 のうす茶色着色化粧紙用
原紙に、粘度800cpsに調整した透明の電子線硬化
型樹脂(ダイセル・ユーシービー(株)製:エベクリル
600/HDODA/富士デヴィソン化学(株)製:サ
イロイド244)をグラビアコート法により25g/m
2 塗布し、深度20μmのヘアーライン状模様の凹凸形
状が形成されたエンボスロールに上記樹脂の塗布面を圧
着したままで上記原紙の裏面より加速電圧200kv、
照射量4Mradの電子線を照射して、上記樹脂を硬化
させた後、エンボスロールより離型してヘヤーライン状
模様の凹凸形状が形成されたシートを得た。
[0029] pale brown colored decorative paper base paper for a basis weight of 60 g / m 2, manufactured by electron beam curing resin in the transparent adjusted to a viscosity 800 cps (manufactured by Daicel UCB Co., Ltd .: EBECRYL 600 / HDODA / Fuji-Davison Chemical ( Co., Ltd .: Cyloid 244) 25g / m by gravure coating method
2 coating, and the accelerating voltage of 200 kv from the back surface of the base paper with the resin-coated surface being pressure bonded to an embossing roll having a hairline-like pattern with a depth of 20 μm.
After the resin was cured by irradiating it with an electron beam of a dose of 4 Mrad, it was released from the embossing roll to obtain a sheet having an uneven shape of a hairline pattern.

【0030】次に、パール顔料(日本光研工業(株)
製:SME−70)を10部、アクリル系樹脂を60
部、水性溶剤を40部で配合した塗料を、上記で得られ
たシートの全面にグラビア印刷法にて塗工した後、ドク
ターブレードにて凸部の樹脂を掻き取ってシート表面の
凹部に光輝部を形成した。
Next, a pearl pigment (Nihon Koken Kogyo Co., Ltd.)
Made: SME-70) 10 parts, acrylic resin 60
Part, a coating solution containing 40 parts of an aqueous solvent is applied to the entire surface of the sheet obtained above by the gravure printing method, and then the resin on the convex portion is scraped off with a doctor blade to shine on the concave portion of the sheet surface. Parts were formed.

【0031】続いて、3色柄の木目絵柄模様を印刷し、
その上にウレタン系トップコート樹脂を乾燥後塗布量が
10g/m2 になるように塗工することにより、本発明
の化粧シートを得た。
Subsequently, a three-color pattern wood grain pattern is printed,
A urethane-based topcoat resin was dried on the coated layer so that the coating amount was 10 g / m 2 to obtain a decorative sheet of the present invention.

【0032】得られた化粧シートは、見る角度によって
光の反射方向が変化して木目絵柄模様の底部での照り感
が移動し、極めて天然木に酷似した材質感が感じられる
ものであった。
The obtained decorative sheet was such that the reflection direction of light changed depending on the viewing angle, and the feeling of shining at the bottom of the woodgrain pattern moved, giving a feeling of material that closely resembled natural wood.

【0033】[0033]

【発明の効果】以上詳細に説明したように、本発明によ
れば、基材シートの上に凹凸形状の層を形成し、その凹
部に光輝性材料を含む樹脂を充填してほぼ平滑な面とす
ることにより凹凸の差のある光輝部を形成し、その上に
木目模様等の絵柄模様印刷層を形成したので、見る角度
によって光の反射方向が変化して、絵柄模様の底部での
照り感が移動するような意匠感を表現でき、極めて天然
木に酷似した材質感のある化粧シートが得られるという
優れた効果を奏する。
As described in detail above, according to the present invention, an uneven layer is formed on a base sheet, and the recess is filled with a resin containing a glittering material to form a substantially smooth surface. By forming a bright part with unevenness by forming a pattern printing layer such as a wood grain pattern on it, the reflection direction of light changes depending on the viewing angle, and the shining at the bottom of the pattern It has an excellent effect that a decorative sheet having a feeling of movement can be expressed, and a decorative sheet having a material feeling extremely similar to natural wood can be obtained.

【0034】また、本発明の化粧シートによれば、凹凸
形状の層の形成、光輝部の形成、絵柄模様印刷層の形
成、トップコート層の形成といった一連の工程をオンラ
インで行うことができ、巻き取り状態で連続的に製造す
ることが可能であり、非常に効率的で安価な化粧シート
の製造が行える。
Further, according to the decorative sheet of the present invention, it is possible to carry out a series of steps on-line, such as forming a layer having an uneven shape, forming a bright portion, forming a pattern printing layer, and forming a top coat layer, It is possible to manufacture continuously in a wound state, and it is possible to manufacture a very efficient and inexpensive decorative sheet.

【図面の簡単な説明】[Brief description of drawings]

【図1】本発明の化粧シートの一構成例を示す断面図で
ある。
FIG. 1 is a cross-sectional view showing one structural example of a decorative sheet of the present invention.

【符号の説明】[Explanation of symbols]

1 基材シート 2 凹凸形状の層 3 光輝部 4 絵柄模様印刷層 5 トップコート層 1 Base Material Sheet 2 Layer with Concavo-convex Shape 3 Bright Part 4 Pattern Print Layer 5 Top Coat Layer

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 FI 技術表示箇所 D21H 27/02 ─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 6 Identification code Internal reference number FI technical display location D21H 27/02

Claims (2)

【特許請求の範囲】[Claims] 【請求項1】 基材シートに凹凸形状を形成し、その凹
部に光輝性材料を含む樹脂を充填した光輝部を形成し、
さらにその上に所望の絵柄模様層を設けてなることを特
徴とする化粧シート。
1. An uneven shape is formed on a base material sheet, and a bright portion filled with a resin containing a bright material is formed in the concave portion,
A decorative sheet, further comprising a desired pattern layer provided thereon.
【請求項2】 前記基材シート上に電離放射線硬化型樹
脂を塗布し、その樹脂面をエンボスロールに圧着し、前
記基材シートの裏面より電離放射線を照射して前記樹脂
を硬化させることにより前記凹凸形状が形成されている
ことを特徴とする請求項1記載の化粧シート。
2. An ionizing radiation-curable resin is applied onto the base sheet, the resin surface is pressure-bonded to an embossing roll, and the resin is cured by irradiating ionizing radiation from the back surface of the base sheet. The decorative sheet according to claim 1, wherein the uneven shape is formed.
JP29045594A 1994-10-31 1994-10-31 Decorative sheet Pending JPH08127111A (en)