JPH07216328A - Light-diffusing pressure-sensitive adhesive composition - Google Patents

Light-diffusing pressure-sensitive adhesive composition

Info

Publication number
JPH07216328A
JPH07216328A JP4466994A JP4466994A JPH07216328A JP H07216328 A JPH07216328 A JP H07216328A JP 4466994 A JP4466994 A JP 4466994A JP 4466994 A JP4466994 A JP 4466994A JP H07216328 A JPH07216328 A JP H07216328A
Authority
JP
Grant status
Application
Patent type
Prior art keywords
resin
adhesive
agent
diffusing
pressure
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP4466994A
Other languages
Japanese (ja)
Other versions
JP3516976B2 (en )
Inventor
Takaaki Kato
Shuji Koda
孝昭 加藤
修二 甲田
Original Assignee
Kimoto & Co Ltd
株式会社きもと
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

PURPOSE: To obtain an adhesive composition which does not suffer from exudation of adhesive, has good adhesion to substrate, is easy in the work of uniformly mixing the constituent light diffusing agent and can give a surface illuminant of high luminance by mixing a pressure-sensitive adhesive resin with a crosslinking agent and resin particles as a light-diffusing agent.
CONSTITUTION: This composition is prepared by mixing a pressure-sensitive adhesive resin with a crosslinking agent and resin particles as a light diffusing agent. In a preferable example, 100 pts.wt. pressure-sensitive adhesive resin comprising an acrylic ester copolymer is mixed with 0.05-20 pts.wt. isocyanate and 5-300 pts.wt. crosslinked polystyrene resin particles.
COPYRIGHT: (C)1995,JPO

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【産業上の利用分野】本発明は、LEDや液晶用バックライトの光源を均一かつ平面的に発光させるために、フィルム等に塗布して使用される光拡散性粘着剤組成物に関する。 The present invention relates, in order to the source of the LED or LCD backlight uniformly and planarly emitted to an optical diffusing pressure-sensitive adhesive composition for use in coating the film or the like.

【0002】 [0002]

【従来の技術】従来、このような用途に使用されるものとしては、アクリル系粘着剤に無機質粒子を分散させたものが使用されていた。 Conventionally, as the ones used in such applications, those obtained by dispersing inorganic particles in the acrylic pressure-sensitive adhesive has been used. しかし、このようなものは均一な分散安定状態を得ることが困難であり、数分ないし数日の間に凝集しゲル化しやすくなる。 However, this stuff is difficult to obtain a uniform dispersion stable state, tends to gel aggregated for several minutes to several days. このため、3本ロール等の分散装置で粘着剤と無機質粒子を十分に混練した後、その分散を安定化するためにアミン系の分散安定剤を添加することが行われている(特開昭56−116 Therefore, three were sufficiently kneaded adhesive and inorganic particles dispersing apparatus such as a roll, (JP it has been practiced to add a dispersion stabilizer of amine to stabilize the dispersion 56-116
767号)。 No. 767).

【0003】一般に粘着剤は、通常のポリマーでは十分な凝集力、耐熱性などの性能が得られにくいことから、 [0003] In general adhesive, sufficient cohesive strength in the normal polymer, since the performance of the heat resistance is difficult to obtain,
イソシアネート架橋・エポキシ架橋等の架橋を行っている。 It is doing the cross-linking of such isocyanate crosslinking epoxy cross-linking. しかし、イソシアネート基やエポキシ基をもつ化合物を用いる粘着剤にアミン系の分散安定剤を添加すると、架橋硬化機構が阻害されるため、アミン系の分散安定剤は使用することができない。 However, the addition of amine-based dispersion stabilizer in the pressure-sensitive adhesive using a compound having an isocyanate group or an epoxy group, the crosslinking curing mechanism is inhibited, amine dispersion stabilizers can not be used. したがって、アミン系の分散安定剤を使用するためには、イソシアネート基およびエポキシ基をもたない非架橋型または一液架橋型の粘着剤を選択する必要があるが、このような粘着剤は架橋密度が低いため樹脂の凝集力が小さく粘着剤の滲みだし現象を起こしやすい。 Therefore, to use an amine of the dispersion stabilizer, it is necessary to select a non-crosslinked or one-pack crosslinking type pressure-sensitive adhesive no isocyanate group and an epoxy group, such adhesive crosslinked prone to bleeding out phenomenon of the resin cohesion is less adhesive for lower density. さらに、基材への密着性が劣り、被着体へ貼り合わせる際に位置ずれがあった場合に貼り直し作業をすると、粘着剤の糊残りを生じ部材の歩留まり低下を招いていた。 Furthermore, poor adhesion to a substrate, were invited when the working reattachment if there is a positional shift when bonding to the adherend, the yield reduction of the members caused the adhesive residue of the adhesive. 樹脂の凝集力及び基材への密着性を向上させるにはイソシアネート等の架橋剤を添加すれば良いのであるが、前述したとおりアミン系の分散安定剤と反応しゲル化を生ずるので樹脂の改質が行えなかった。 Although the improved adhesion to the resin of the cohesion and the substrate are than may be added a crosslinking agent such as isocyanate, Kai resin produce a reaction gel with a dispersion stabilizer of amine as described above the quality was not done.

【0004】一方、無機質粒子を分散するには、3本ロールなどの高価な分散設備を必要とし、さらに粘着性の高い樹脂を使用しているので工程替えの際の分散装置の清掃に多大な時間を必要とし、コスト高、生産性の低下を招いていた。 On the other hand, to disperse the inorganic particles, require expensive dispersion equipment such as a three-roll, considerable further cleaning of the dispersing device when the process replacement because it uses a highly adhesive resin time the need for, had invited high cost, a reduction in productivity. このため、分散工程の手間を少なくするために一回の分散液製造で多量の分散液を生産することにより生産性を向上させていたが、これにより多大な在庫を持つことになり、結果として長期にわたる保存性を考慮する必要に迫られていた。 Therefore, it had improved productivity by producing a large amount of dispersion in a single dispersion prepared in order to reduce the labor of dispersion process, thereby will have a tremendous inventory, as a result long-term had been faced with the need to consider the storage stability. また、無機質粒子は光拡散効果を発揮させるため樹脂に対して多量に充填する必要があり、そのため不要な隠蔽性が増大し、光源の輝度が低下して鮮明な表示が困難であった。 Further, the inorganic particles have a large amount of filling the resin in order to exhibit the light diffusion effect, therefore unnecessary concealing property is increased, the luminance of the light source was difficult clear display decreases.

【0005】 [0005]

【発明が解決しようとする課題】本発明は、これら一連の問題点を改善すべく、粘着剤の滲みだしがなく、基材への密着性が良好で、光拡散剤の均一な混合が容易な作業により行え、さらには高輝度な面光源を得ることができる光拡散性粘着剤組成物を提供することを目的とする。 SUMMARY OF THE INVENTION It is an object of the present invention, to improve the series of problems, no exudation of the adhesive, has good adhesion to a substrate, it facilitates uniform mixing of the light diffusing agent carried out by Do work, further an object to provide a light diffusing pressure-sensitive adhesive composition capable of providing a high-luminance surface light source.

【0006】 [0006]

【課題を解決するための手段】本発明の光拡散性粘着剤組成物は、粘着性樹脂中に、架橋剤および光拡散剤として樹脂粒子が添加されていることを特徴とするものである。 Means for Solving the Problems] light diffusing pressure sensitive adhesive composition of the present invention, in the adhesive resin, it is characterized in that the resin particles are added as a crosslinking agent and a light diffusing agent. すなわち、本発明は従来の無機質粒子にかえて樹脂粒子を使用することにより分散安定剤の添加や3本ロール等の設備を必要とせずに容易に均一混合が可能となること、樹脂粒子を使用することにより高い光拡散効果かつ高輝度の表示が可能となること、分散安定剤を使用する必要がないことから樹脂の架橋が容易に行えるため、 That is, the present invention is that it is possible to easily and uniformly mixed without the need for equipment additives and the like three rolls of a dispersion stabilizer by using resin particles instead of conventional inorganic particles, a resin particle high light diffusion effect and the display of high brightness is possible by, the crosslinking of the resin can be performed easily since there is no need to use a dispersion stabilizer,
粘着剤の滲みだしや糊残りを著しく減少させ、さらに基材への密着性を非常に向上させることができることを知見して完成されたものである。 Bleeding out and adhesive residue of the adhesive is significantly reduced, it has been completed by finding that it is possible to more highly enhance the adhesion to a substrate.

【0007】本発明に使用される粘着性樹脂としては、 [0007] As adhesive resin used in the present invention,
常温で粘着性を示すものであれば使用でき、例えば(メタ)アクリル系樹脂、ポリエステル系樹脂などがあげられ、必要に応じて可塑剤、タッキファイヤー等を添加して、粘弾性挙動や界面特性を調節することもできる。 At ordinary temperature can be used as long as it exhibits an adhesive property, for example (meth) acrylic resins, and polyester resins, and the like, a plasticizer, with the addition of tackifier, etc., viscoelastic behavior and interface properties It can also be adjusted. タッキファイヤーとしては、ロジン、変性ロジン、ロジンエステル、テルペン樹脂、テルペンフェノール樹脂等の天然物およびその誘導体、クマロン・インデン樹脂、スチレン系樹脂、フェノール樹脂、キシレン樹脂等の合成樹脂が使用可能である。 As the tackifier, rosin, modified rosin, rosin esters, natural products and their derivatives, coumarone-indene resin, styrene resin, phenol resin, synthetic resins such as xylene resin can be used such as a terpene resin, terpene phenol resin . 粘着性樹脂として特に好ましいものとしては、エチルアクリレート、ブチルアクリレート、2−エチルヘキシルアクリレートなどのモノマーからなるアクリル酸エステル共重合体があげられる。 Particularly preferable as the adhesive resin, ethyl acrylate, butyl acrylate, acrylic acid ester copolymer composed of monomers such as 2-ethylhexyl acrylate. これは、側鎖の炭素数や分岐が異なるアクリル酸エステルを所望の割合で共重合させることにより、タッキファイヤー等を添加せずとも所望の粘弾性挙動や界面特性が得られるものである。 This may be achieved by copolymerizing the number and branch carbon are different acrylic acid ester of the side chain in the desired proportions, in which the desired viscoelastic behavior and interface properties can be obtained even without the addition of tackifier or the like. また、アクリル酸エステルは架橋剤の添加により凝集力の調整が容易であるという特性も有する。 Also it has properties that acrylic acid ester is easy to adjust the cohesive force by addition of a crosslinking agent.

【0008】架橋剤としては、粘着性樹脂中の水酸基、 [0008] As the crosslinking agent, the hydroxyl group in the adhesive resin,
カルボキシル基、アミノ基などと反応してイソシアネート架橋するイソシアネート、粘着性樹脂中のカルボキシル基、アミノ基と反応してエポキシ架橋するエポキシ樹脂、粘着性樹脂中の水酸基、カルボキシル基などとメチロール基の縮合により架橋するメチロール化メラミン樹脂、メチロール化尿素樹脂、粘着性樹脂中のカルボキシル基と金属イオンが結合する金属塩、金属水酸化物などを使用することができる。 Isocyanates carboxyl group, reacts with an amino group to an isocyanate crosslinking, carboxyl group in the adhesive resin, epoxy resin epoxy crosslinking by reacting with an amino group, hydroxyl group in the adhesive resin, condensation such as with methylol group carboxyl group methylolated melamine resin crosslinking, methylolated urea resin, a carboxyl group and a metal metal salt ions are bound in the adhesive resin, metal hydroxide and the like can be used by.

【0009】架橋剤の中で特に好ましいものとしては、 [0009] as being particularly preferred in the cross-linking agent,
イソシアネートがあげられる。 Isocyanate, and the like. イソシアネートは、反応する官能基の種類が多いため種々の粘着性樹脂に使用でき、また、イソシアネートどうしが反応して高分子量化しても凝集力を向上させることができ、更に基材への密着性に優れている。 Isocyanates can be used in a variety of adhesive resins for the type of the functional group often reacts, also be high molecular weight isocyanate each other reacts it is possible to improve the cohesion, further adhesion to a substrate It has excellent. 架橋剤の添加量は、使用する粘着性樹脂、架橋剤の種類によって異なるが、粘着性樹脂としてポリエステル樹脂またはアクリル樹脂、架橋剤としてイソシアネートを使用した場合、通常、粘着性樹脂に対して0.05〜20%、好ましくは0.5〜10%である。 The amount of the crosslinking agent added, if adhesive resin to be used varies depending on the kind of the crosslinking agent, using a polyester resin or an acrylic resin as the adhesive resin, an isocyanate as a crosslinking agent, usually, 0 for adhesive resin. 05 to 20%, preferably from 0.5 to 10%. 0.05%以上とすることにより架橋密度が上がり樹脂の凝集力を向上させることができ、20%以下とすることにより過度の硬化を避け、適度な初期接着力及び粘着力を与えることができる。 It is possible to improve the cohesion of the cross-linking density is increased resin by 0.05% or more to avoid curing excessive by 20% or less, it is possible to provide an appropriate initial adhesive strength and adhesion . なお、本明細書において使用する「%」および「部」は、特記しない限り、重量%、重量部を表している。 Incidentally, "%" and "parts" as used herein, unless otherwise indicated, wt%, represent the parts by weight.

【0010】光拡散剤としては、使用する溶剤に対して耐溶剤性のある樹脂粒子であれば何れでも使用できるが、隠蔽性が少ないものが好適に使用される。 [0010] As the light diffusing agent can use any as long as it is a resin particle with a solvent resistance against solvents used, having less covering property is preferably used. このようなものとしては、例えばポリメチルメタクリレートを主成分とする架橋アクリル系樹脂粒子、架橋ポリスチレン系樹脂粒子、シリコーン系樹脂粒子などがあげられる。 Such examples include for instance crosslinked acrylic resin particles composed mainly of polymethyl methacrylate, crosslinked polystyrene resin particles, and silicone resin particles.
光拡散剤の中で特に好ましいものとしては、使用する樹脂の屈折率や架橋剤の種類により一概にはいえないが、 As particularly preferable in the light diffusing agent is not it may vary depending on the type of refractive index or a crosslinking agent for the resin to be used,
アクリル系樹脂に架橋剤としてイソシアネートを使用した場合には、架橋ポリスチレン樹脂粒子があげられる。 When using an isocyanate as a crosslinking agent to acrylic resin, crosslinked polystyrene resin particles.
光拡散剤の添加量は、必要とされる光拡散性、樹脂粒子の種類及び樹脂粒子の粒径により異なるが、通常、粘着性樹脂に対して5〜300%、好ましくは10〜100 The addition amount of the light diffusing agent, a light diffusing required varies depending particle diameter of the type of resin particles and resin particles, typically 5 to 300% with respect to tackifying resin, preferably 10 to 100
%である。 It is%. 5%以上としたのは適度な光拡散性を得るためであり、300%以下としたのは粘着力を低下させないためである。 Was set to 5% or more is for obtaining appropriate light diffusibility, was set at 300% or less is because not to lower the adhesive strength.

【0011】次に、これらの混合方法であるが、まず溶剤中に光拡散剤を混入し、この溶液と粘着性樹脂を分散混合した後、使用前に架橋剤を添加して使用する。 [0011] Next, a mixture of these methods, by mixing a light diffusing agent first in a solvent, was dispersed mixing the solution and the adhesive resin is used by adding a crosslinking agent prior to use. 混合してすぐに使用するのであれば、光拡散剤を混入した後、架橋剤を添加して、その後に粘着性樹脂と分散混合しても良い。 If mixed and of being used immediately, after mixing a light diffusing agent, and adding a crosslinking agent may be dispersed and mixed with adhesive resin thereafter.

【0012】 [0012]

【作用】このような構成とすることにより、簡易な攪拌により均一な分散が可能となるため、分散安定剤の添加や3本ロール等の分散装置などの分散手段の検討が不要となる。 With [act] this construction, it becomes possible to uniformly dispersed by simple stirring, examination of dispersion means such as a dispersing device added or such as a three-roll dispersion stabilizer is not necessary. また、樹脂粒子を使用しているため高い光拡散効果かつ高輝度の表示が可能となる。 Further, it is possible to display a high light diffusion effect and a high brightness due to the use of resin particles. 分散安定剤を使用する必要がないことから樹脂の架橋が容易に行え、粘着剤の滲みだしや糊残りを著しく減少させ、さらに基材への密着性を非常に向上させることができる。 Dispersion stabilizer crosslinking of the resin is easy to since it is not necessary to use, bleeding out and adhesive residue of the adhesive is significantly reduced, it is possible to more highly enhance the adhesion to a substrate.

【0013】 [0013]

【実施例】 【Example】

[実施例1] ・ポリエステル樹脂(NV:100%) 100部 (バイロンRV550:東洋紡績社) ・キシレン樹脂(タッキファイヤー、NV:80%) 100部 (ニカノールH80:三菱瓦斯化学社) ・シリコーン樹脂粒子 100部 (トスパール120:東芝シリコーン社) ・酢酸エチル 100部 ・酢酸ブチル 100部 ・イソシアネート(架橋剤、NV:75%) 10部 (タケネートA10:武田薬品工業社) Example 1 Polyester resin (NV: 100%) 100 parts (Byron RV550: Toyobo Co., Ltd.) and xylene resin (tackifier, NV: 80%) 100 parts (NIKANOL H80: Mitsubishi Gas Chemical Co., Ltd.) Silicone resin 100 parts particles (Tospearl 120: Toshiba silicone Co., Ltd.) ethyl acetate 100 parts butyl acetate 100 parts isocyanate (crosslinking agent, NV: 75%) 10 parts (Takenate A10: Takeda Chemical Industries)

【0014】[実施例2] ・アクリル酸エステル共重合樹脂(NV:40%) 100部 (SKダイン1102X:綜研化学社) ・架橋アクリル系樹脂粒子 56部 (MR−7HG:綜研化学社) ・酢酸エチル 50部 ・酢酸ブチル 50部 ・エポキシ樹脂(架橋剤) 0.6部 (SKダインE−AX:綜研化学社) [0014] [Example 2] Acrylic acid ester copolymer resin (NV: 40%) 100 parts (SK dyne 1102X: Soken Chemical & Engineering Co., Ltd.) crosslinked acrylic resin particles 56 parts (MR-7HG: Soken Chemical & Engineering Co., Ltd.) 50 parts of ethyl acetate butyl acetate 50 parts epoxy resin (crosslinking agent) 0.6 parts (SK dyne E-AX: Soken Chemical & Engineering Co., Ltd.)

【0015】[実施例3] ・アクリル酸エステル共重合樹脂(NV:40%) 100部 (リキダインAR−2120EA:リキダイン社) ・架橋ポリスチレン樹脂粒子 8部 (テクポリマーSBX−6:積水化成品工業社) ・酢酸エチル 50部 ・酢酸ブチル 50部 ・イソシアネート(架橋剤、NV:75%) 0.4部 (コロネートL:日本ポリウレタン工業社) [0015] [Example 3] Acrylic acid ester copolymer resin (NV: 40%) 100 parts (Rikidain AR-2120EA: Rikidain Inc.) crosslinked polystyrene resin particles 8 parts (Techpolymer SBX-6: manufactured by Sekisui Plastics Inc.) ethyl acetate 50 parts butyl acetate 50 parts isocyanate (crosslinking agent, NV: 75%) 0.4 parts (Coronate L: Nippon polyurethane industry Co., Ltd.)

【0016】[比較例1]実施例3の架橋ポリスチレン樹脂粒子にかえて、炭酸カルシウム(サンライトSL− [0016] [Comparative Example 1] instead of the crosslinked polystyrene resin particles of Example 3, calcium carbonate (Sunlight SL-
700:竹原化学工業社)を8部とした。 700: Takehara Kagaku Kogyo Co., Ltd.) was 8 parts.

【0017】[比較例2]実施例3の架橋ポリスチレン樹脂粒子にかえて、炭酸カルシウム(サンライトSL− [0017] [Comparative Example 2] in place of the crosslinked polystyrene resin particles of Example 3, calcium carbonate (Sunlight SL-
700:竹原化学工業社)を40部とした。 700: Takehara Kagaku Kogyo Co., Ltd.) was 40 parts.

【0018】[比較例3]実施例3の架橋ポリスチレン樹脂粒子にかえて、炭酸カルシウム(サンライトSL− [0018] [Comparative Example 3] instead of the crosslinked polystyrene resin particles of Example 3, calcium carbonate (Sunlight SL-
700:竹原化学工業社)を8部とし、更に架橋剤の添加を行わなかった。 700: Takehara and 8 parts Chemical Industry Co., Ltd.), was further carried out the addition of the crosslinking agent.

【0019】[比較例4]実施例3の架橋剤の添加を行わなかった。 [0019] was not added in Comparative Example 4 Example 3 of the crosslinking agent.

【0020】[比較例5]実施例3の架橋ポリスチレン樹脂粒子にかえて、炭酸カルシウム(サンライトSL− [0020] [Comparative Example 5] instead of the crosslinked polystyrene resin particles of Example 3, calcium carbonate (Sunlight SL-
700:竹原化学工業社)を8部とし、更に分散安定剤としてトリエチルアミンを3部添加した。 700: Takehara and 8 parts Chemical Industry Co., Ltd.) was further added 3 parts of triethylamine as a dispersion stabilizer.

【0021】[比較例6]実施例3の架橋ポリスチレン樹脂粒子にかえて、炭酸カルシウム(サンライトSL− [0021] [Comparative Example 6] in place of the crosslinked polystyrene resin particles of Example 3, calcium carbonate (Sunlight SL-
700:竹原化学工業社)を8部とし、分散安定剤としてトリエチルアミンを3部添加し、更に架橋剤の添加を行わなかった。 700: Takehara and Chemical Industry Co., Ltd.) 8 parts, were added 3 parts of triethylamine as a dispersion stabilizer, was further carried out the addition of a cross-linking agent.

【0022】上記実施例1〜3および比較例1〜6に記載の処方について、溶剤中に光拡散剤を混入し、これと粘着性樹脂を分散混合した後、架橋剤・分散安定剤の添加を要するものはこれを添加して光拡散性粘着剤を得た。 [0022] The formulations described in Examples 1-3 and Comparative Examples 1-6, by mixing a light diffusing agent in a solvent, which as after the adhesive resin dispersed mixture, addition of a crosslinking agent, a dispersion stabilizer shall be required were the addition of this to obtain a light diffusing adhesive. 上記実施例1〜3および比較例1〜6の光拡散性粘着剤について、以下に記載する試験を行い、その結果を表1に示す。 The light diffusing adhesive of Examples 1-3 and Comparative Examples 1-6, were tested as described below, and the results are shown in Table 1.

【0023】分散性:攪拌機(ディゾルバーMDH−V [0023] The dispersible: stirrer (dissolver MDH-V
−1型:井上製作所社)にて1000rpm、20分攪拌して均一混合されたものを「◎」、24時間攪拌して均一混合されたものを「○」、3本ロールを使用しなければ均一混合できないものを「×」とした。 -1 type: in Inoue Manufacturing Co., Ltd.) what was uniformly mixed by stirring 1000 rpm, 20 minutes "◎", "○" those are uniformly mixed by stirring for 24 hours, unless using the 3-roll the ones that can not be uniformly mixed was evaluated as "×".

【0024】光拡散性:透明な100μmのポリエステルフィルムに光拡散性粘着剤を乾燥膜厚30μmとなるよう塗工した後、LED表示板の表面に貼り合わせて表示をさせた場合に、個々の点光源が点光源として認識できるものを「×」、ほぼ認識できないものを「○」、完全に認識できないものを「◎」とした。 [0024] Light diffusing: After a light diffusing pressure-sensitive adhesive was coated so that a dry film thickness of 30μm polyester film of transparent 100 [mu] m, when obtained by the display by bonding a surface of the LED display board, the individual "×" what point light source can be recognized as a point light source, and the ones that can not be recognized almost as "○", "◎" what can not be fully recognized.

【0025】光線透過率:透明な100μmのポリエステルフィルムに光拡散性粘着剤を乾燥膜厚30μmとなるよう塗工したものを分光光度計で測定した。 The light transmittance: was what was the light diffusing pressure-sensitive adhesive was coated so that a dry film thickness of 30μm measured by a spectrophotometer polyester film transparent 100 [mu] m.

【0026】糊残り:透明な100μmのポリエステルフィルムに光拡散性粘着剤を塗工した後、ABS樹脂板に貼り合わせた後剥離して、ABS樹脂板に粘着剤が付着していなかったものを「○」、付着していたものを「×」とした。 The adhesive residue: After applying the light diffusing pressure-sensitive adhesive on a polyester film of a transparent 100 [mu] m, and peeled after bonding to ABS resin plate, those adhesive on ABS resin plate was not attached "○", it was what was adhered to as "×".

【0027】保存性:架橋剤を添加する前の光拡散性粘着剤を密閉して室温にて3カ月保存したものを、簡易な攪拌により使用可能なものを「○」、ゲル化して使用不可能のものを「×」とした。 The storage stability: those stored for 3 months at room temperature to seal the front of the light diffusing pressure-sensitive adhesive a crosslinking agent is added, "○" and those available by simple agitation, using gelled non possible of what was evaluated as "×".

【0028】 [0028]

【表1】 [Table 1]

【0029】実施例1〜3の光拡散性粘着剤は、すべての評価において良好な性能を有するものであった。 The light diffusing adhesive of Examples 1-3, had a good performance in all evaluations. 比較例1の光拡散性粘着剤は、無機質粒子を使用しているため、攪拌機で24時間攪拌しても均一混合はできず3本ロールを使用しなければ均一混合できなかった。 Light diffusing adhesive of Comparative Example 1, due to the use of inorganic particles, could not be uniformly mixed unless using three rolls can not be in even homogeneous mixture was stirred for 24 hours stirrer. また、 Also,
光拡散効果に乏しく、輝度も本実施例に比べて落ちていた。 Poor light diffusion effect, luminance had fallen compared to the embodiment. さらに、3カ月保存後においては、再度3本ロールで分散しなければ使用できなかった。 Furthermore, in the after storage 3 months, it could not be used unless dispersed on a three roll again.

【0030】比較例2は、比較例1の光拡散性粘着剤が光拡散効果に乏しかったため、光拡散効果が得られるまで無機質粒子の添加量を増やしたものであるが、輝度がかなり落ちてしまい、使用に堪えないものであった。 [0030] Comparative Example 2, since the light diffusing pressure-sensitive adhesive of Comparative Example 1 was poor in the light diffusion effect, but in which increasing the additive amount of the inorganic particles to the light diffusion effect is obtained, the luminance is considerably fallen sister were those not bear to use. 比較例3は、無機質粒子を使用して架橋剤の添加を行わなかったものであるが、すべての評価において劣っていた。 Comparative Example 3, but which was not performed the addition of a cross-linking agent using inorganic particles, were inferior in all evaluation. 比較例4は、樹脂粒子を使用して架橋剤を使用しなかったものであるが、樹脂粒子を使用しているために分散性、光拡散性は非常に良好であるが、粘着剤の凝集力が劣っているために糊残りを生じた。 Comparative Example 4, although those not used by using the resin particles crosslinking agent, dispersibility due to the use of the resin particles, the light diffusion property is very good, the aggregation of the adhesive resulted in a glue remaining in the force is inferior.

【0031】比較例5は、比較例1の光拡散性粘着剤の分散安定性を改良するために分散安定剤を添加したものであるが、ゲル化してしまい使用に堪えなかった。 [0031] Comparative Example 5 is obtained by adding a dispersion stabilizer in order to improve the dispersion stability of the light-diffusing adhesive of Comparative Example 1 did not bear the use will gelled. 比較例6は、比較例5のゲル化を防止するために架橋剤の添加を行わなかったものであるが、無機質粒子を使用しているために攪拌機で24時間攪拌しても均一混合はできず3本ロールを使用しなければ均一混合できなかった。 Comparative Example 6, although not to have made the addition of a crosslinking agent in order to prevent gelation of the Comparative Example 5, even uniform mixing can be stirred for 24 hours with a stirrer to using inorganic particles It could not be uniformly mixed unless using three rolls not.
また、光拡散効果に乏しく、輝度も本実施例に比べて落ちていた。 Also, poor light diffusion effect, luminance had fallen compared to the embodiment. さらに、架橋剤を添加していないため、粘着剤の凝集力が劣っており、糊残りを生じた。 Furthermore, since no addition of crosslinking agent, cohesive force of the pressure-sensitive adhesive has poor, resulting in adhesive remaining.

【0032】 [0032]

【発明の効果】以上の結果からも明らかなように、本発明の光拡散性粘着剤組成物は、光拡散剤として樹脂粒子を使用したことにより分散安定剤の添加や3本ロール等の設備を必要とせずに容易に均一混合が可能であり、また、樹脂粒子を使用しているため高い光拡散効果かつ高輝度な面光源を得ることができる。 These results, according to the present invention As is clear, light diffusing pressure sensitive adhesive composition of the present invention, equipment added and etc. 3-roll dispersion stabilizer by using resin particles as the light diffusing agent the it can be easily uniformly mixed without the need, also, it is possible to obtain a high light diffusion effect and a high luminance surface light source due to the use of resin particles. さらに、架橋剤を使用しているため粘着剤の凝集力が高く、粘着剤の滲みだしや糊残りを著しく減少させることができ、また基材への密着性を非常に向上させた光拡散性粘着剤組成物である。 Further, cohesive force of the adhesive due to the use of crosslinking agent is high, bleeding out and adhesive residue adhesive can be remarkably reduced, also the light diffusing with very improved adhesion to substrates a pressure-sensitive adhesive composition.

Claims (3)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 粘着性樹脂中に、架橋剤および光拡散剤として樹脂粒子が添加されていることを特徴とする光拡散性粘着剤組成物。 1. A in the pressure-sensitive resin, a crosslinking agent and a light diffusing pressure-sensitive adhesive composition, wherein the resin particles are added as a light diffusing agent.
  2. 【請求項2】 アクリル酸エステル共重合体からなる粘着性樹脂中に、イソシアネートおよび架橋ポリスチレン樹脂粒子が添加されていることを特徴とする請求項1記載の光拡散性粘着剤組成物。 Wherein in the pressure-sensitive resin consisting of acrylic acid ester copolymer, the isocyanate and the claims 1 light diffusing pressure-sensitive adhesive composition, wherein the crosslinked polystyrene resin particles have been added.
  3. 【請求項3】 アクリル酸エステル共重合体からなる粘着性樹脂100重量部中に、イソシアネート0.05〜 To 3. A tacky resin 100 parts by weight of acrylic acid ester copolymer, an isocyanate 0.05
    20重量部および架橋ポリスチレン樹脂粒子5〜300 20 parts by weight of crosslinked polystyrene resin particles 5 to 300
    重量部が添加されていることを特徴とする請求項2記載の光拡散性粘着剤組成物。 Light diffusing pressure-sensitive adhesive composition of claim 2, wherein the parts by weight is added.
JP4466994A 1994-02-04 1994-02-04 Surface light source Expired - Fee Related JP3516976B2 (en)