JPH0699551A - Mold release sheet and manufacture thereof - Google Patents
Mold release sheet and manufacture thereofInfo
- Publication number
- JPH0699551A JPH0699551A JP27368492A JP27368492A JPH0699551A JP H0699551 A JPH0699551 A JP H0699551A JP 27368492 A JP27368492 A JP 27368492A JP 27368492 A JP27368492 A JP 27368492A JP H0699551 A JPH0699551 A JP H0699551A
- Authority
- JP
- Japan
- Prior art keywords
- release sheet
- layer
- ethylene
- release
- sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、例えば、粘着シートや
粘着テープ等の台紙、あるいは、高粘稠性成分を封入す
るための容器や袋の内周面層等としての用途を有する軽
剥離性の離型シート及び該離型シートの製造方法に関す
る。BACKGROUND OF THE INVENTION The present invention relates to a light release having a use as a mount such as an adhesive sheet or an adhesive tape, or as an inner peripheral surface layer of a container or bag for enclosing a highly viscous component. And a method for producing the release sheet.
【０００２】[0002]
【従来の技術】粘着シートや粘着テープ等の台紙に利用
される離型シートは、離型シート用支持基材に離型剤層
を積層させた積層シートからなる。2. Description of the Related Art A release sheet used as a mount such as an adhesive sheet or an adhesive tape is a laminated sheet in which a release agent layer is laminated on a support base material for a release sheet.
【０００３】かかる離型シートとしては、（１）例え
ば、離型シート用支持基材に対して、低密度ポリエチレ
ン樹脂層からなる離型剤層を、該低密度ポリエチレン樹
脂層における離型面の酸化を抑制しながら押し出し積層
した積層シート（特公昭５１−２０２０５号公報）、
（２）離型シート用支持基材に対して、低密度ポリエチ
レンとエチレン−プロピレン共重合体またはエチレン−
１・ブテンランダム共重合体との混合樹脂による離型剤
層を押し出し積層した積層シート（特公昭５７−４５７
９０号公報）、（３）離型シート用支持基材に対して低
密度ポリエチレンの押し出し樹脂層を形成した後に、こ
の低密度ポリエチレン樹脂層の表面にシリコーン樹脂を
塗工，硬化させた積層シート等が知られている。As such a release sheet, (1) For example, a release agent layer consisting of a low density polyethylene resin layer is formed on a support base material for a release sheet, and a release surface of the low density polyethylene resin layer Laminated sheets extruded and laminated while suppressing oxidation (Japanese Patent Publication No. 51-20205),
(2) Low density polyethylene and ethylene-propylene copolymer or ethylene-
Laminated sheet in which a release agent layer made of a mixed resin with 1-butene random copolymer is extruded and laminated (Japanese Patent Publication No. 57-457).
No. 90), (3) a laminated sheet in which an extruded resin layer of low-density polyethylene is formed on a support substrate for release sheet, and then a silicone resin is applied and cured on the surface of the low-density polyethylene resin layer. Etc. are known.
【０００４】なお、ロール巻きの状態で流通させる粘着
シートや粘着テープは、離型シート用支持基材に対して
離型剤層の反対側に粘着剤層を形成することによって得
られる。また、枚葉状状態で流通させる粘着シートや粘
着テープ、例えばラベルのような形態のものは、粘着剤
層を有する粘着シートの粘着剤層面と離型シートの離型
剤層面とが接当するようにして、粘着シートと離型シー
トとを積層させた状態で流通される。The pressure-sensitive adhesive sheet or pressure-sensitive adhesive tape which is circulated in a rolled state can be obtained by forming a pressure-sensitive adhesive layer on the side opposite to the release agent layer with respect to the release sheet supporting base material. Also, in the case of a pressure-sensitive adhesive sheet or pressure-sensitive adhesive tape that is distributed in a sheet-like state, for example, in the form of a label, the pressure-sensitive adhesive layer surface of the pressure-sensitive adhesive sheet having a pressure-sensitive adhesive layer and the release agent layer surface of the release sheet contact each other. Then, the pressure-sensitive adhesive sheet and the release sheet are distributed in a laminated state.
【０００５】[0005]
【発明が解決しようとする課題】前記した従来の離型シ
ートのうちの（１）項の低密度ポリエチレン樹脂層から
なる離型剤層を有するものは、高粘着性物質を剥離させ
る際の剥離が重く、離型性能が悪いために糊残りが発生
する。Among the above-mentioned conventional release sheets, those having a release agent layer consisting of the low-density polyethylene resin layer of the item (1) are peeled off at the time of peeling a highly adhesive substance. The adhesive is heavy and the release performance is poor, so adhesive residue occurs.
【０００６】また、（２）項の低密度ポリエチレンとエ
チレン−プロピレン共重合体またはエチレン−１・ブテ
ンランダム共重合体との混合樹脂による離型剤層を有す
るものは、高粘着性物質を剥離させる際の剥離が重く、
剥離工程がパルス状になって滑らかな剥離が行なえな
い。また、低密度ポリエチレンとエチレン−プロピレン
共重合体またはエチレン−１・ブテンランダム共重合体
との混合には自ら限界があり、エチレン−プロピレン共
重合体またはエチレン−１・ブテンランダム共重合体の
混合比率を高めると、製膜時にネックインが発生したり
モーター負荷が大きくなったりするため、安定した製膜
が行なえなく、軽剥離性の離型シートを得ることができ
ない。Further, in the item (2) having a release agent layer made of a mixed resin of low-density polyethylene and an ethylene-propylene copolymer or an ethylene-1-butene random copolymer, a highly adhesive substance is peeled off. When peeling, the peeling is heavy,
The peeling process becomes pulsed and smooth peeling cannot be performed. In addition, there is a limit to the mixing of low-density polyethylene with an ethylene-propylene copolymer or an ethylene-1.butene random copolymer, and a mixture of an ethylene-propylene copolymer or an ethylene-1.butene random copolymer. If the ratio is increased, neck-in will occur during film formation and the motor load will increase, so stable film formation cannot be performed, and a light-releasing release sheet cannot be obtained.
【０００７】さらに、（３）項のシリコーン樹脂の塗工
層による離型剤層を有するものは、離型剤層に遊離シリ
コーンが付着するため、該遊離シリコーンの離脱によっ
て粘着性物質の剥離力が低下する。このため、離型シー
トから粘着性物質を剥離する際の剥離力が低く、浮きが
発生する等の障害を起こす。Further, in the case of the release agent layer having the silicone resin coating layer of the item (3), since free silicone adheres to the release agent layer, the release force of the adhesive substance by the release of the free silicone. Is reduced. For this reason, the peeling force at the time of peeling the adhesive substance from the release sheet is low, which causes problems such as floating.
【０００８】これに対して本発明は、軽剥離性であっ
て、しかも、糊残りや浮きの発生等の無い均一な剥離を
行なえる離型シート、及び、該離型シートを的確に得る
方法を提供する。On the other hand, the present invention is a release sheet which is lightly peelable and can be uniformly peeled without causing adhesive residue or floating, and a method for accurately obtaining the release sheet. I will provide a.
【０００９】[0009]
【課題を解決するための手段】請求項１の発明は、離型
シート用支持基材に対してポリオレフィン樹脂層を介し
て離型剤層が形成されており、該離型剤層が、結晶化度
４０％以下のエチレン−α・オレフィン共重合体樹脂層
による離型シートからなる。According to a first aspect of the present invention, a release agent layer is formed on a support base material for a release sheet via a polyolefin resin layer, and the release agent layer is crystalline. The release sheet comprises an ethylene-α / olefin copolymer resin layer having a degree of conversion of 40% or less.
【００１０】請求項２の発明は、離型シート用支持基材
に対して、ポリオレフィン樹脂と、結晶化度４０％以下
のエチレン−α・オレフィン共重合体樹脂とを共押し出
し積層することにより、離型シート用支持基材に対して
ポリオレフィン樹脂層を介して結晶化度４０％以下のエ
チレン−α・オレフィン共重合体樹脂による離型剤層を
形成する離型シートの製造方法からなる。According to a second aspect of the present invention, a polyolefin resin and an ethylene-α-olefin copolymer resin having a crystallinity of 40% or less are co-extruded and laminated on a supporting base material for a release sheet, It comprises a method for producing a release sheet, in which a release agent layer made of an ethylene-α.olefin copolymer resin having a crystallinity of 40% or less is formed on a support base material for a release sheet via a polyolefin resin layer.
【００１１】請求項３の発明は、離型シート用支持基材
に対してポリオレフィン樹脂の押し出しコート層を形成
した後、該ポリオレフィン樹脂の押し出しコート層の上
に、結晶化度４０％以下のエチレン−α・オレフィン共
重合体樹脂によるコーティング剤を塗工，乾燥して離型
剤層を形成する離型シートの製造方法からなる。According to a third aspect of the present invention, an extrusion coating layer of a polyolefin resin is formed on a supporting base material for a release sheet, and ethylene having a crystallinity of 40% or less is formed on the extrusion coating layer of the polyolefin resin. -A method for producing a release sheet, which comprises applying a coating agent of an α-olefin copolymer resin and drying it to form a release agent layer.
【００１２】前記構成による本発明の離型シート及びそ
の製造方法において、離型シート用支持基材としては、
紙、熱可塑性ポリエステル，ナイロン，ポリプロピレ
ン，高密度ポリエチレン，ポリイミド等による２軸延伸
プラスチックフィルム、硬質ポリ塩化ビニルフィルム、
セロファン等によるこの種の離型シートにおける離型シ
ート用支持基材として公知のものを使用し得る。In the release sheet of the present invention having the above structure and the method for producing the same, the release sheet supporting base material is
Biaxially stretched plastic film made of paper, thermoplastic polyester, nylon, polypropylene, high density polyethylene, polyimide, etc., rigid polyvinyl chloride film,
Known materials can be used as a release sheet supporting base material in a release sheet of this type using cellophane or the like.
【００１３】離型シート用支持基材に対して形成される
ポリオレフィン樹脂層は、離型剤層の下引き層としての
機能を果たすものである。この下引き層としての機能を
果たすポリオレフィン樹脂層が形成される離型シート用
支持基材面には、離型シート用支持基材とポリオレフィ
ン樹脂層との間の接着強度を高めてこれらの両者の層間
の接着強度を安定化させるために、例えば、ポリエチレ
ンイミン，有機チタン，ウレタン系樹脂等によるアンカ
ーコート剤の処理や、オゾン酸化処理等の接着性改良処
理を予め行なって置くことが好ましい。The polyolefin resin layer formed on the release sheet supporting base material functions as an undercoat layer of the release agent layer. On the surface of the release sheet support base material on which the polyolefin resin layer that functions as the undercoat layer is formed, the adhesive strength between the release sheet support base material and the polyolefin resin layer is increased to enhance the adhesion strength between the release sheet support base material and the polyolefin resin layer. In order to stabilize the adhesive strength between the layers, it is preferable that the anchor coat agent is treated with, for example, polyethyleneimine, organic titanium, urethane resin or the like, or the adhesiveness-improving treatment such as ozone oxidation treatment is performed in advance.
【００１４】離型剤層の下引き層としての機能を果たす
ポリオレフィン樹脂層は、密度０．９１〜０．９７ｇ／
ｃｍ3 程度の低密度ポリエチレン，線状低密度ポリエチ
レン，ポリプロピレン等により、厚さ１０〜３０μ程度
に形成されることが好ましい。The polyolefin resin layer which functions as an undercoat layer for the release agent layer has a density of 0.91 to 0.97 g /
It is preferable that it is formed to have a thickness of about 10 to 30 μ by low density polyethylene, linear low density polyethylene, polypropylene or the like having a cm 3 level.
【００１５】離型シート用支持基材に対してポリオレフ
ィン樹脂層を介して形成される離型剤層は、結晶化度４
０％以下のエチレン−α・オレフィン共重合体樹脂によ
る厚さ１〜３０μ程度の層からなる。この離型剤層を形
成するエチレン−α・オレフィン共重合体樹脂として
は、密度０．８〜０．９５ｇ／ｃｍ3 ，ＡＳＴＭ Ｄ７
４６による脆化温度−７０℃以下，示差熱分析による融
点８０℃以下のエチレン−α・オレフィン共重合体の単
独または混合物を利用するのが好ましく、例えば、エチ
レン−１・ブテンランダム共重合体，エチレン−プロピ
レン共重合体，エチレン−１・ペンテン共重合体，エチ
レン−３・メチル・１ブテン共重合体，エチレン−４・
メチル・１・ペンテン共重合体、あるいはこれらのα・
オレフィンの３種以上の共重合体等を利用することがで
きる。なお、離型剤層を形成するエチレン−α・オレフ
ィン共重合体樹脂の結晶化度が４０％を超えるようにな
ると、軽剥離性でしかも安定した剥離性能を有する離型
シートが得られなくなる。The release agent layer formed on the release sheet supporting base material through the polyolefin resin layer has a crystallinity of 4
It is composed of a layer having a thickness of about 1 to 30 μm made of 0% or less of an ethylene-α-olefin copolymer resin. The ethylene-α / olefin copolymer resin forming the release agent layer has a density of 0.8 to 0.95 g / cm 3 , ASTM D7.
It is preferable to use an ethylene-α / olefin copolymer alone or in a mixture having an embrittlement temperature of −70 ° C. or less by 46 and a melting point of 80 ° C. or less by a differential thermal analysis, for example, an ethylene-1 · butene random copolymer, Ethylene-propylene copolymer, ethylene-1-pentene copolymer, ethylene-3-methyl / 1-butene copolymer, ethylene-4.
Methyl / 1-pentene copolymer, or α of these
Copolymers of three or more kinds of olefins can be used. When the crystallinity of the ethylene-α-olefin copolymer resin forming the release agent layer exceeds 40%, a release sheet having light release properties and stable release performance cannot be obtained.
【００１６】離型シート用支持基材に対してポリオレフ
ィン樹脂層を介して結晶化度４０％以下のエチレン−α
・オレフィン共重合体樹脂による離型剤層を形成する方
法として、ポリオレフィン樹脂と、結晶化度４０％以下
のエチレン−α・オレフィン共重合体樹脂との共押し出
しによる積層方法を利用する場合には、離型剤層側の樹
脂の押し出し温度を３００℃以下に抑制するのが好まし
い。Ethylene-α having a degree of crystallinity of 40% or less with respect to the supporting base material for the release sheet via the polyolefin resin layer.
As a method of forming a release agent layer of an olefin copolymer resin, when using a lamination method by coextrusion of a polyolefin resin and an ethylene-α / olefin copolymer resin having a crystallinity of 40% or less, It is preferable to suppress the extrusion temperature of the resin on the release agent layer side to 300 ° C. or lower.
【００１７】また、結晶化度４０％以下のエチレン−α
・オレフィン共重合体樹脂によるコーティング剤を塗
工，乾燥して離型剤層を形成する際には、結晶化度４０
％以下のエチレン−α・オレフィン共重合体樹脂を溶剤
中に溶解または分散させたコーティング剤を使用する。Further, ethylene-α having a crystallinity of 40% or less is used.
When the coating agent of olefin copolymer resin is applied and dried to form the release agent layer, the crystallinity is 40.
% Or less of an ethylene-α-olefin copolymer resin is used in a solvent to dissolve or disperse a coating agent.
【００１８】[0018]
【作用】本発明の離型シートは、軽剥離性でしかも安定
した離型性能を有しており、例えば、粘着シートや粘着
テープ等の台紙、あるいは、例えばゼリー，餡，ジャム
等の高粘稠性成分を封入するための容器や袋の内周面層
等としての用途において優れた作用を奏する。The release sheet of the present invention has a light releasability and a stable release performance. For example, a backing sheet such as an adhesive sheet or an adhesive tape, or a high-viscosity adhesive such as jelly, bean jam or jam. It exerts an excellent action in applications such as an inner peripheral surface layer of a container or bag for enclosing a viscous component.
【００１９】また、本発明の離型シートの製造方法によ
れば、軽剥離性でしかも安定した離型性能を有する離型
シートを的確に得られる。Further, according to the method for producing a release sheet of the present invention, a release sheet having light releasability and stable release performance can be accurately obtained.
【００２０】[0020]
【実施例】本発明の離型シート及びその製造方法の具体
的な構成を実施例を以って説明する。EXAMPLES The specific constitution of the release sheet and the method for producing the same according to the present invention will be described with reference to examples.
【００２１】「実施例１」晒クラフト紙「８０ｇ／ｍ
2 ：紀州製紙 (株) 」からなる離型シート用支持基材の
片面に、密度０．９１７ｇ／ｃｍ3 ，ＭＩ：７．２の低
密度ポリエチレン樹脂「三井石油化学工業 (株) ：Ｍ１
１Ｐ」と、結晶化度５％のエチレン−プロピレン共重合
体樹脂「三井石油化学工業 (株) ：タフマーＰ０２８
０」とを、低密度ポリエチレン樹脂層が離型シート用支
持基材面に接当するようにして共押し出し積層すること
により、厚さ３０μの低密度ポリエチレン樹脂層とエチ
レン−プロピレン共重合体樹脂による厚さ１５μの離型
剤層とを形成し、本発明の１実施例品である離型シート
（Ａ）を得た。"Example 1" Bleached kraft paper "80 g / m"
2 : A low-density polyethylene resin having a density of 0.917 g / cm 3 and MI: 7.2 on one side of a release sheet supporting substrate made of Kishu Paper Co., Ltd. “Mitsui Petrochemical Co., Ltd .: M1”
1P "and an ethylene-propylene copolymer resin having a crystallinity of 5%" Mitsui Petrochemical Industry Co., Ltd .: Tufmer P028 "
0 "and the low-density polyethylene resin layer are brought into contact with the surface of the supporting base material for the release sheet by co-extrusion to laminate to form a low-density polyethylene resin layer having a thickness of 30 µm and an ethylene-propylene copolymer resin. And a release agent layer having a thickness of 15 μm was formed to obtain a release sheet (A) which is an example of the present invention.
【００２２】「実施例２」実施例１による離型シート
（Ａ）の製造工程において、結晶化度５％のエチレン−
プロピレン共重合体樹脂「三井石油化学工業 (株) ：タ
フマーＰ０２８０」の代わりに、結晶化度１５％のエチ
レン−１・ブテンランダム共重合体樹脂「三井石油化学
工業 (株) ：Ａ４０８５」を利用することにより、本発
明の別の実施例品である離型シート（Ｂ）を得た。[Example 2] In the manufacturing process of the release sheet (A) according to Example 1, ethylene having a crystallinity of 5% was used.
Instead of propylene copolymer resin "Mitsui Petrochemical Industry Co., Ltd .: Toughmer P0280", ethylene-1 / butene random copolymer resin "Mitsui Petrochemical Industry Co., Ltd .: A4085" with a crystallinity of 15% was used. By doing so, a release sheet (B) which is another example of the present invention was obtained.
【００２３】「実施例３」実施例１による離型シート
（Ａ）の製造工程において、結晶化度５％のエチレン−
プロピレン共重合体樹脂「三井石油化学工業 (株) ：タ
フマーＰ０２８０」の代わりに、結晶化度２０％のエチ
レン−１・ブテンランダム共重合体樹脂「三井石油化学
工業 (株) ：Ａ−２００９０」を利用することにより、
本発明の別の実施例品である離型シート（Ｃ）を得た。[Example 3] In the manufacturing process of the release sheet (A) according to Example 1, ethylene having a crystallinity of 5% was used.
Instead of the propylene copolymer resin "Mitsui Petrochemical Industry Co., Ltd .: Toughmer P0280", an ethylene-1 / butene random copolymer resin having a crystallinity of 20% "Mitsui Petrochemical Industry Co., Ltd .: A-20090" By using
A release sheet (C) which is another example of the present invention was obtained.
【００２４】「比較例１〜６」実施例１による離型シー
ト（Ａ）の製造工程において、結晶化度５％のエチレン
−プロピレン共重合体樹脂「三井石油化学工業 (株) ：
タフマーＰ０２８０」の代わりに、［表１］の所定欄に
記載されている樹脂を利用することにより、比較のため
の離型シート（ａ）〜（ｆ）を得た。"Comparative Examples 1 to 6" In the manufacturing process of the release sheet (A) according to Example 1, an ethylene-propylene copolymer resin having a crystallinity of 5% "Mitsui Petrochemical Industry Co., Ltd .:
The release sheets (a) to (f) for comparison were obtained by using the resins described in the predetermined column of [Table 1] instead of "Toughmer P0280".
【００２５】[0025]
【表１】 (*1)・・三井石油化学工業 (株) ：Ｌ−８４０ (*2)・・三井石油化学工業 (株) ：Ｍ１１Ｐ，密度０．９
１７ｇ／ｍ3 (*3)・・三井石油化学工業 (株) ：ＵＺ２０８１，密度
０．９２０ｇ／ｍ3 (*4)・・三井石油化学工業 (株) ：１４０５，酢酸ヒ゛ニル
含有量；１４モル％ (*5)・・三井石油化学工業 (株) ：タフマーＰ０２８０[Table 1] (* 1) Mitsui Petrochemical Industry Co., Ltd .: L-840 (* 2) Mitsui Petrochemical Industry Co., Ltd .: M11P, density 0.9
17 g / m 3 (* 3) ··· Mitsui Petrochemical Industry Co., Ltd .: UZ2081, density 0.920 g / m 3 (* 4) ··· Mitsui Petrochemical Industry Co., Ltd .: 1405, vinyl acetate
Content: 14 mol% (* 5) ... Mitsui Petrochemical Industry Co., Ltd .: Tufmer P0280
【００２６】［実験］前記実施例及び比較例で得られた
各離型シートの離型剤層面を、ポリアクリル酸エステル
系感圧接着剤を主成分とする粘着剤層を有する粘着テー
プに圧接して積層シートとした後、該積層シートの離型
シートと粘着テープとを剥離した。このときの剥離強度
を測定すると共に、剥離工程での剥離状態を観察した。
結果を［表２］に示す。[Experiment] The release agent layer surface of each release sheet obtained in the above-mentioned Examples and Comparative Examples was pressure-bonded to the pressure-sensitive adhesive tape having the pressure-sensitive adhesive layer containing a polyacrylic ester pressure-sensitive adhesive as a main component. After forming a laminated sheet, the release sheet and the adhesive tape of the laminated sheet were peeled off. The peel strength at this time was measured, and the peeled state in the peeling step was observed.
The results are shown in [Table 2].
【００２７】[0027]
【表２】 [Table 2]
【００２８】[0028]
【効果】本発明の離型シートは、軽剥離性であって、し
かも、糊残りや浮きの発生等の無い均一な剥離を行なう
ことができ、特に粘着シートや粘着テープ等の台紙、あ
るいは、高粘稠性成分を封入するための容器や袋の内周
面層等としての用途において多大の効果を奏する。[Effect] The release sheet of the present invention is lightly peelable and can perform uniform peeling without generation of adhesive residue or floating. Particularly, a release sheet such as an adhesive sheet or an adhesive tape, or It exerts a great effect in applications such as an inner peripheral surface layer of a container or bag for enclosing a highly viscous component.
【００２９】また、本発明の離型シートの製造方法によ
れば、前記特性を有する離型シートを容易かつ的確に得
ることができる。Further, according to the method for producing a release sheet of the present invention, the release sheet having the above characteristics can be easily and accurately obtained.
Claims (3)
オレフィン樹脂層を介して、結晶化度４０％以下のエチ
レン−α・オレフィン共重合体樹脂による離型剤層が形
成されていることを特徴とする離型シート。1. A release agent layer made of an ethylene-α.olefin copolymer resin having a crystallinity of 40% or less is formed on a release sheet supporting base material via a polyolefin resin layer. Release sheet characterized by.
オレフィン樹脂と結晶化度４０％以下のエチレン−α・
オレフィン共重合体樹脂とを共押し出し積層することに
より、離型シート用支持基材に対してポリオレフィン樹
脂層を介して結晶化度４０％以下のエチレン−α・オレ
フィン共重合体樹脂による離型剤層を形成することを特
徴とする離型シートの製造方法。2. A polyolefin resin and ethylene-α.multidot.having a crystallinity of 40% or less with respect to a supporting base material for a release sheet.
A release agent made of an ethylene-α-olefin copolymer resin having a crystallinity of 40% or less through a polyolefin resin layer on a release sheet supporting base material by co-extruding and laminating an olefin copolymer resin A method for producing a release sheet, which comprises forming a layer.
レフィン樹脂の押し出しコート層を形成した後、該ポリ
オレフィン樹脂の押し出しコート層の上に、結晶化度４
０％以下のエチレン−α・オレフィン共重合体樹脂によ
るコーティング剤を塗工，乾燥して離型剤層を形成する
ことを特徴とする離型シートの製造方法。3. A polyolefin resin extrusion coating layer is formed on a release sheet supporting base material, and a crystallinity of 4 is formed on the polyolefin resin extrusion coating layer.
A method for producing a release sheet, which comprises applying a coating agent of 0% or less of an ethylene-α-olefin copolymer resin and drying it to form a release agent layer.