JPH0626631B2 - Golf club head - Google Patents

Golf club head

Info

Publication number
JPH0626631B2
JPH0626631B2 JP62322083A JP32208387A JPH0626631B2 JP H0626631 B2 JPH0626631 B2 JP H0626631B2 JP 62322083 A JP62322083 A JP 62322083A JP 32208387 A JP32208387 A JP 32208387A JP H0626631 B2 JPH0626631 B2 JP H0626631B2
Authority
JP
Japan
Prior art keywords
club head
epoxy resin
head
outer shell
filler
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP62322083A
Other languages
Japanese (ja)
Other versions
JPH01160576A (en
Inventor
成幸 ▲高▼橋
泰三 藤岡
Original Assignee
株式会社青葉ゴルフ
積水化成品工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社青葉ゴルフ, 積水化成品工業株式会社 filed Critical 株式会社青葉ゴルフ
Priority to JP62322083A priority Critical patent/JPH0626631B2/en
Publication of JPH01160576A publication Critical patent/JPH01160576A/en
Publication of JPH0626631B2 publication Critical patent/JPH0626631B2/en
Anticipated expiration legal-status Critical
Application status is Expired - Lifetime legal-status Critical

Description

【発明の詳細な説明】 〔産業上の利用分野〕 本発明は、ゴルフクラブのクラブヘッドに関するものである。 Description of the Invention The present invention [relates], the present invention relates to a golf club of the club head.

〔従来の技術〕 [Prior art]

近年のゴルフクラブは、ゴルフボールの飛距離を延ばしてできるだけ遠くまで飛ばしたい(飛距離の延長)、 In recent years the golf club, want to skip as far as possible to extend the flying distance of the golf ball (an extension of the distance),
ゴルフボールを真っ直ぐに飛ばしたい(方向性の安定)、という二大要素が大きくクローズアップされている。 You want straight to skip the golf ball (in the direction of stability), the two major elements that have been largely close-up.

ボールの飛距離を延ばすには、クラブヘッドの速度を高めることが必要であり、そのためにはクラブヘッドを軽量化することが要求される。 To extend the flying distance of the ball, it is necessary to increase the speed of the club head, in order that it is required that the weight of the club head.

一方、ボールを真っ直ぐに飛ばすには、クラブヘッドのスイートスポットを大きく設定することが重要であり、 On the other hand, to fly the ball straight, it is important to set a large sweet spot of the club head,
そのためにはボールの当たる打撃面すなわちクラブヘッドのフェースを大きく形成する必要があり、これを実現するためにはクラブヘッドが必然的に大きくなり重量化してしまうことになる。 Therefore the need to form a large face of the striking surface or the club head strikes the ball, the club head is that result in increased and weight reduction inevitably in order to achieve this.

このように、ボールの飛距離を延ばすことと真っ直ぐに飛ばすこととは、クラブヘッドに対して相反する要求を生じるものであるが、これらの要求を共に満足させる、 Thus, to extend the flying distance of the ball and straight skip it and, although those which give conflicting demands with respect to the club head, both to satisfy these requirements,
すなわちクラブヘッドのフェースを大きく形成し且つ軽量化できるクラブヘッドの実現が待望されている。 That realization of the club head is awaited which can greatly formed and lighter the face of the club head.

そこで、近年では、ウッドクラブのクラブヘッドとして、柿の木、桜の木、米マツなどの天然木材に代えて、 Therefore, in recent years, as a club head of a wood club, persimmon, cherry tree, instead of the natural wood such as Douglas fir,
ステンレス製のシエルを有する中空のメタルヘッドや、 And a hollow metal head with a stainless steel shell,
炭素繊維などの繊維強化プラスチックからなるシエルを有する中空のカーボンヘッドなどが提案されている。 Such hollow carbon head having a shell made of a fiber-reinforced plastic such as carbon fiber are proposed. また、アイアンクラブのクラブヘッドについても中空状のものが知られている。 In addition, hollow things are also known for the club head of an iron club.

そして、例えばメタルヘッドについては、そのシエルの肉厚を0.7mm程度まで薄く形成して軽量化を図っている。 Then, the metal head, for example, is reduce the weight and thin wall thickness of the shell up to about 0.7 mm.

また、上記のクラブヘッドの中空部には充填材が充填されており、この充填材としては、例えば特開昭61−2 Further, the hollow portion of the club head may be filled with, as the filler, for example, JP-61-2
49485号公報に開示されているように硬質の発泡ウレタン樹脂が一般に用いられており、また近年においては、特開昭60−68873号公報に開示されているように多数のガラス微小中空球を混入した非発泡のエポキシ樹脂を用いたものもある。 Rigid urethane foam resin as disclosed in 49485 JP are commonly used, and in recent years, contamination many hollow glass microspheres as disclosed in JP-A-60-68873 also those using a non-foaming epoxy resin.

〔発明が解決しようとする問題点〕 [Problems to be Solved by the Invention]

ところが、中空クラブヘッドの充填材として硬質の発泡ウレタン樹脂を用いたものでは、発泡ウレタン樹脂の使用目的が打球時の消音効果のみを期待したものであって、強度面等を全く無視したものである。 However, one using a foamed urethane resin of rigid as a filler for hollow club heads, there is the intended use of the foamed urethane resin is expected only silencing effect at the time of hitting, the intensity surface or the like which was completely ignored is there. すなわち、この硬質発泡ウレタン樹脂は、衝撃音を吸収し且つ軽量であるという利点を有する反面、強度的に非常に弱く、且つ、ねばりに乏しく脆くて崩れやすい性質を有している。 That is, the rigid urethane foam resin, although having the advantage of being absorbed and lightweight impact noise, strength very weak, and has a property of readily collapsing poor brittle stickiness. それゆえ、クラブヘッドのフェースで打球したときの衝撃が加わったときに、上記の充填材が崩れてしまい、このクラブヘッドを繰り返し使用するうちに、クラブヘッドの外殻を形成するシエルやフェースなどに変形を生じる虞れがあり、しかも、この硬質発泡ウレタン樹脂の本来の使用目的とされている打球時の消音機能さえも徐々に低下してしまうという問題がある。 Therefore, when the impact is applied when the hitting in the face of the club head, will be above the filling material collapses, while the repeated use of the club head, such as shell or a face that forms the outer shell of the club head the there is a possibility that deformation occurs, moreover, mute function at the time of hitting, which is the original purpose of the hard urethane foam resin even there is a problem that even decreases gradually.

一方、中空クラブヘッドの充填材として、多数のガラス微小中空球を混入した非発泡のエポキシ樹脂を用いたものでは、ガラス微小中空球によって幾分軽量化はできるものの、非発泡のエポキシ樹脂を使用しているので全体としての重量が相当に大きくなり、したがってクラブヘッドのフェースをさほど大きく形成できない。 On the other hand, as a filler for hollow club head, the one using the non-foaming epoxy resin mixed with numerous glass microballoons, although it is somewhat lighter by hollow glass microspheres, use of non-foamed epoxy resin weight of the entire since the are to become considerably large, thus can not so large form face of the club head. また、上記の充填材は単体素材でないから、充填材自体の強度が低下する。 The above-mentioned filler do not unitary material, the strength of the filler itself is reduced. 特に、非発泡のエポキシ樹脂にガラス微小中空球が重量比で2.5%以上混入されていると、充填材自体の強度が著しく低下することになる。 In particular, the non-foaming epoxy resin to the glass microballoons are mixed to 2.5 percent by weight, so that the strength of the filling material itself is remarkably lowered. さらに、クラブヘッドの外殻を形成するシエルおよびフェースやソールなどの内面にガラス微小中空球が接した状態で充填されていると、それだけエポキシ樹脂による接着面積が減少するので、接着強度が著しく低減されることになり、 Further, when being filled, so much reduced adhesion area by epoxy resin, the adhesive strength is remarkably reduced in a state where the hollow glass microspheres is in contact with the inner surface of such shell and face and a sole forming the outer shell of the club head to be will be,
ガラス微小中空球の混入比が大きくなるほど、その傾向は強くなるなどの問題を有していた。 The larger the mixing ratio of the glass microballoons, the trend had problems such stronger.

このように、中空クラブヘッドに充填される上記の充填材では、その強度が弱いので、フェースやソールなどの内面に補強用のリブを形成している。 Thus, in the above filler is filled into the hollow club head, because its strength is weak, and forms a rib for reinforcing the inner surface of such a face or a sole. しかし、ヘッド中空部の外殻内面に補強リブを形成すると、それだけクラブヘッドの重量が増加して軽量化を充分に図ることができない。 However, by forming the reinforcing rib to the shell inner surface of the head hollow portion, it can not be fully attained in weight by much increasing the weight of the club head.

なお、中空クラブヘッドの充填材として発泡エポキシ樹脂を用いたものも提案されているが(特開昭58−20 Although there has been proposed one using a foaming epoxy resin as a filler for hollow club head (JP 58-20
3776号公報、特開昭59−101166号公報)、 3776 JP, Sho 59-101166 JP)
ここに示されている発泡エポキシ樹脂は、いずれも一般に使用される高発泡倍率(30倍〜40倍)のフォーム材であって、予め別型で成形されたものがクラブヘッドの中空部に充填されるようになっている。 Foamed epoxy resin shown here is a foam of a high expansion ratio both of which are commonly used (30 40 times), filling those molded in advance in a different type to the hollow portion of the club head It is adapted to be.

それゆえ、クラブヘッドの外殻を形成するシエル等と上記充填材との接着強度が殆ど得られず、しかも高発泡倍率を有しているので強度が著しく不足する結果となり、 Therefore, the adhesion strength between the shell or the like and the above filler material forming the outer shell of the club head can not be obtained mostly, yet results in the strength is insufficient significantly since they have a high expansion ratio,
打球時の衝撃を受けたときにフェース等の変形を生じたり上記充填材が欠けたり崩れたりする虞れがある。 There is a possibility that the filler or deformed such face is collapsed or chipped when impacted upon hitting. したがって、この種の充填材が使用されるとすれば、前記発泡ウレタン樹脂の場合と同様に、単に打球時の消音を目的とする場合に限られると考えられるが、コスト面や消音性能等を考慮すれば極めて実用性に乏しいものである。 Therefore, if the filler of this type is used, as in the case of the urethane foam resin, but simply considered to be limited to the case for the purpose of silencing of hitting, the cost and silencing performance, etc. those poor very practical considering. このような点に鑑み、上記公報に記載されている発泡エポキシ樹脂は単に着想段階のものに過ぎないと考えられるし、また事実、全く実用化されていなのが実情である。 In view of this point, to be considered as merely foamed epoxy resin simply idea stage as described in the above publication, also the fact, it is fact is not been at all practical.

〔問題点を解決するための手段〕 [Means for Solving the Problems]

本発明のゴルフクラブヘッドは、上記の問題点を解決するために、クラブヘッドをなす外殻にて形成されたヘッド中空部に、低発泡合成樹脂を内芯として充填したゴルフクラブヘッドにおいて、上記低発泡合成樹脂として、 The golf club head of the present invention, in order to solve the above problems, the head hollow portion formed in an outer shell forming a club head, the golf club head filled with low foaming synthetic resin inner core, said as low foaming synthetic resin,
2倍〜4倍の発泡倍率を有する低発泡エポキシ樹脂を用い、かつ、上記内芯と上記外殻の内表面とが、低発泡エポキシ樹脂の硬化に伴って接着されている構成を特徴としている。 Using low foaming epoxy resin having 2 to 4 times of expansion ratio, and the aforementioned inner core and the inner surface of the outer shell, and wherein the structure are bonded with the cured low-foaming epoxy resin . 上記のクラブヘッドをなす外殻は、ヘッドのトップ部、トー部、ヒール部、バック部などを含み、さらにフェースやソースなども含むものである。 Shell forming the above club head top portion of the head, toe portion, a heel portion, and the like back part, but also including such further face and sauces.

上記のゴルフクラブヘッドは、木製のウッドクラブ、メタル・ウッドクラブ、カーボン・ウッドクラブなどの全てに適用でき、さらにアイアンクラブにも適用することができる。 The above golf club head, wooden wood club, metal-wood club, can be applied to all, such as carbon-wood club, it can be further applied to iron club.

〔作用〕 [Action]

上記の構成により、低発泡エポキシ樹脂から成る内芯と外殻内表面との接着強度が大きく、かつ、内心は、素材に低発泡エポキシ樹脂を用いたことにより充分な強度を有していて耐衝撃性も保有している。 With the above configuration, the adhesive strength is large between the inner core and the outer shell inner surface made of a low foaming epoxy resin, and nisin have sufficient strength by using low foaming epoxy resin material resistant impact resistance are also held. したがって、ヘッド中空部の外殻内面に補強リブを形成する必要がなくなるとともに、クラブヘッドの肉厚をさらに薄く形成でき、しかも充填材自体が軽量性を有しているので、高い耐衝撃性と軽量性とを兼備したゴルフクラブヘッドが得られる。 Therefore, the need to form a reinforcing rib on the shell inner surface of the head hollow portion is eliminated, the thickness of the club head can further thinner, and since the filler itself has a light weight, high impact resistance and golf club head having both a light weight can be obtained.

また、クラブヘッドの重量が全体に著しく軽減されるので、クラブヘッドのフェースの面積を大きく形成してスイートスポットを拡大させることができる。 Further, since the weight of the club head is significantly reduced in the whole, it is possible to enlarge the sweet spot and larger area of ​​the face of the club head.

さらに、内芯と外殻内表面とが強固に接着していることにより、ゴルフクラブヘッドに衝撃が繰り返して加わっても、内芯は外殻から経時的に分離することがない。 Further, by the inner core and the outer shell inner surface is tightly adhered, even applied repeatedly impact the golf club head, the inner core never over time separated from the outer shell. この結果、ゴルフクラブヘッドの打撃面の変形や、打撃時の消音効果の経時的な低下等を回避でき、優れた性能を長期間保持することができる。 As a result, deformation of the striking face of the golf club head can be avoided over time such as reduction of silencing effect at the time of hitting can be maintained for a long time excellent performance.

〔実施例〕 〔Example〕

本発明の一実施例を第1図および第2図に基づいて説明すれば、以下の通りである。 To describe an embodiment of the present invention based on FIGS. 1 and 2 is as follows.

クラブヘッド1は、その外殻を形成するシエル2を有し、このシエル2は、ヘッドのトップ部2a、トー部2 Club head 1 has a shell 2 forming the outer shell, the shell 2, the top portion 2a of the head, toe portion 2
b、ヒール部2c、およびバック部2dから成っている。 b, it is made from the heel portion 2c, and the back part 2d. また、ボールの当たり面を形成しクラブヘッド1の正面部をなすフェース3と、クラブヘッド1の底面部をなすソール4についてもクラブヘッド1の外殻をなしており、さらに図示しないシャフトの先部を結合するネック部5を有している。 Further, a face 3 forming a front portion of the club head 1 to form a contact surface of the ball, the sole 4 forming the bottom portion of the club head 1 and forms an outer shell of the club head 1 also, the shaft to which the further unillustrated and a neck portion 5 for coupling the parts.

上記シエル2等にて形成されたヘッド中空部6には、発泡倍率が2倍〜4倍の低発泡エポキシ樹脂からなる充填材7が充填されている。 The head hollow portion 6 formed in the shell 2 and the like, the filling material 7 is filled with an expansion ratio of two to four times the low foaming epoxy resin. このように、エポキシ樹脂の発泡倍率を2倍〜4倍という低発泡に設定したのは、2倍未満の発泡倍率では充填材7としての重量が大きくなり過ぎてクラブヘッド1の軽量化を充分に図ることができない一方、発泡倍率が4倍を超えると、低発泡エポキシ樹脂の成形物に発泡状態の著しいばらつきを生じて強度的に不均一となり、これが打球の方向性等に悪影響を及ぼすことになるからである。 Thus, the set expansion ratio of the epoxy resin to the low foaming of 2 to 4 times is sufficient the weight of the club head 1 becomes too large weight of the filler 7 is less than twice the expansion ratio one that can not be achieved, when the expansion ratio is more than 4 times, the molded product of low foaming epoxy resin cause significant variations in the foamed state intensity to become nonuniform, which may adversely affect the direction or the like of hitting This is because become.

上記の低発泡エポキシ樹脂である充填材7は、上記ヘッド中空部6の外殻を成形型として直接充填すると同時に成形されるものであり、これによってヘッド中空部6の外殻と充填材7とが接着状態で充填されている。 Filler 7 is a low foaming epoxy resin described above are intended to be molded at the same time to fill directly the outer shell of the head hollow section 6 is used as a mold whereby the outer shell of the head hollow portion 6 and the filler 7 There has been filled with an adhesive state.

上記のゴルフクラブヘッドを製造する場合、クラブヘッド1の目立たない適当な箇所に充填口およびガス抜き孔を設けておき、上記充填口から液状のエポキシ樹脂を注入する。 If the production of the golf club head, may be provided a filling opening and a gas vent hole in a suitable position inconspicuous club head 1, to inject liquid epoxy resin from the filling port. このエポキシ樹脂は、主剤と、発泡剤を含む硬化剤とから成り、発泡倍率が2倍〜4倍となるように予め設定されている。 The epoxy resin is a main component, composed of a curing agent containing a foaming agent is previously set so that the expansion ratio becomes to 4 times 2 times. ヘッド中空部6に液状のエポキシ樹脂を注入して充填すると、このエポキシ樹脂はヘッド中空部6において自己発熱して2倍〜4倍に低発泡しながら硬化する。 When filled by injecting a liquid epoxy resin to the head hollow section 6, the epoxy resin is cured with low foaming in 2 to 4 times by self-heating in the head hollow section 6. 発泡時に発生したガスは、上記ガス抜き孔から外部に放出される。 Gas generated during foam is discharged to the outside from the degassing hole. ヘッド中空部6にエポキシ樹脂を充填したのち、上記充填口およびガス抜き孔を充填材7で面一状に加工成形するか、若しくは別部材で閉塞する。 After filling the epoxy resin in the head hollow portion 6, closes the filling opening and a gas venting hole or machining shaped to flush with a filling material 7, or a separate member.

このようにしてヘッド中空部6に充填された低発泡エポキシ樹脂は、ヘッド中空部6の外殻を成形型として成形されるので、優れた成形性を発揮してヘッド中空部6の外殻と低発泡エポキシ樹脂からなる充填材7とが一体的に接合され、且つ、エポキシ樹脂自体に強い接着性を有しているから、強力に接着された状態で充填される。 Low foaming epoxy resin filled in the head hollow section 6 in this way, since the molded outer shell of the head hollow section 6 is used as a mold outer shell of the head hollow portion 6 to exhibit excellent formability and a filler 7 made of a low foaming epoxy resin is integrally joined, and, because they have strong adhesion to the epoxy resin itself, is filled in a state of being strongly bonded. しかも、上記の低発泡エポキシ樹脂は、ねばりがあるので、強い接着強度を有しているばかりでなく、打球時の衝撃に対して充分な強度を保有しており、耐衝撃性にも優れている。 Moreover, the above-mentioned low foaming epoxy resin, there is a sticky, not only has a strong adhesive strength, holds sufficient strength against an impact upon hitting, also excellent in impact resistance there. したがって、かかるクラブヘッド1を繰り返し使用しても、上記充填材7が割れたり、欠けたり、 Therefore, even when repeatedly used such club head 1, or cracking the filler 7, or chipped,
或いは崩れたりしないので、クラブヘッド1のフェース3等に悪影響を及ぼさず、しかも打球時の消音機能を経時的に保持することができる。 Or does not or collapse, without adversely affecting the face 3 or the like of the club head 1, moreover it is possible to over time retaining the silencing function of the time of hitting the ball.

実験の結果によれば、ゴルフクラブヘッドをスイングしたときの支点(ゴルファーの喉元位置)からクラブヘッド1のトー部2bまでの長さが180cm、打球時のヘッドスピードが40m/s、クラブヘッド1の重さが50 According to the results of the experiment, the golf club head when the swing fulcrum of the (golfer's throat position) to the toe portion 2b of the club head 1 length 180cm, hitting head speed 40 m / s at the time, the club head 1 the weight of 50
0gとすると、クラブヘッド1に45.35kgfの運動エネルギーが発生するが、本発明のクラブヘッド1においては、ソール4の面積を25cm 2とすると500kgf When 0 g, but the kinetic energy of 45.35kgf the club head 1 is generated, in the club head 1 of the present invention, when the area of the sole 4 to 25 cm 2 500 kgf
の運動エネルギーに基づく衝撃にも耐えられ、また25 Also withstand impact based on the kinetic energy, also 25
0kg/cm 3の衝撃を受けても充填材7が割れたり崩れたりしないという結果が得られた。 It results that even when subjected to impact 0 kg / cm 3 not collapsed or cracked filling material 7 was obtained.

したがって、クラブヘッド1の強度が充分に確保されているので、フェース3やソール4の内面等に補強リブ等を形成する必要がなく、クラブヘッド1の軽量化を図ってクラブヘッド1のフェース3の面積を拡大してスイートスポットを大きく設定することが可能となる。 Thus, the strength of the club head 1 is sufficiently ensured, the face 3 and there is no need to form a reinforcing rib or the like on the inner surface or the like of the sole 4, the face 3 of the club head 1 reduce the weight of the club head 1 it is possible to set a large sweet spot to expand the area. また、 Also,
上記したクラブヘッド1の構造によれば、充填材7の成形性に優れていてヘッド中空部6の形状に左右されることがなく、エポキシ樹脂自体の接着効果をも伴うので、 According to the structure of the club head 1 described above, without being influenced by the shape of the head hollow portion 6 have excellent moldability of the filler 7, since also involves adhesion effect of the epoxy resin itself,
単にクラブヘッド1のヘッド中空部6に充填材7を充填したゴルフクラブヘッドというよりも、コンポジット化されたハイブリッドなクラブといえる。 Rather than just a golf club head filled with a filler 7 on the head hollow portion 6 of the club head 1, it can be said that the composite of the hybrid club.

本発明のクラブヘッド1の充填材7と、従来のクラブヘッドに充填される充填材としてガラス微小中空球を含む非発泡のエポキシ樹脂を使用した充填材(従来例1) And the filler 7 of the club head 1 of the present invention, the filling material using non-foaming epoxy resin containing glass microballoons as a filler to be filled in a conventional club head (Conventional Example 1)
と、従来より一般に採用されている柿の木の天然木材を加工してなるクラブヘッド(従来例2)との比較を示すと、次の通りである。 If, when a comparison of the made by processing the natural wood persimmon adopted more generally conventional club head (Conventional Example 2), is as follows.

以上のように、本発明のクラブヘッド1では、従来例1 As described above, in the club head 1 of the present invention, the conventional example 1
よりも更に軽量化され、また従来例2と比較すれば6割以上もの重量を軽減することが可能となる。 Further lighter, also it is possible to reduce the weight of even more than 60% in comparison with the conventional example 2 than.

なお、本発明のゴルフクラブヘッドは、木製のウッドクラブ、メタル・ウッドクラブ、カーボン・ウッドクラブなどの全てに適用でき、さらにアイアンクラブにも適用することができる。 It should be noted that the golf club head of the present invention, wooden wood club, metal-wood club, can be applied to all, such as carbon-wood club, it can be further applied to iron club.

〔発明の効果〕 〔Effect of the invention〕

本発明に係るゴルフクラブヘッドは、以上のように、クラブヘッドをなす外殻にて形成されたヘッド中空部に、 The golf club head according to the present invention, as described above, the head hollow portion formed in an outer shell forming a club head,
低発泡合成樹脂を内芯として充填したゴルフクラブヘッドにおいて、上記低発泡合成樹脂として、2倍〜4倍の発泡倍率を有する低発泡エポキシ樹脂を用い、かつ、上記内芯と上記外殻の内表面とが、低発泡エポキシ樹脂の硬化に伴って接着されている構成である。 A golf club head filled as the inner core of low foaming synthetic resin, as the low foaming synthetic resin, using a low-foaming epoxy resin having 2 to 4 times of expansion ratio, and, among the inner core and the outer shell and the surface is a configuration that is bonded with the cured low-foaming epoxy resin.

これにより、クラブヘッドの重量を著しく軽減できるので、それだけクラブヘッドのフェースの面積を大きく形成してスイートスポットを拡大させることができる。 Accordingly, since it significantly reduces the weight of the club head, it is possible to enlarge the sweet spot much larger forming area of ​​the face of the club head. すなわち、内芯の素材として、2倍〜4倍の発泡倍率を有する低発泡エポキシ樹脂が用いられており、かつ、この低発泡エポキシ樹脂はヘッド中空部の外殻にて成形され、硬化に伴って外殻内表面に強固に接着される。 That is, the inner core material, has low foaming epoxy resin is used having 2 to 4 times of expansion ratio, and the low foaming epoxy resin is molded at the outer shell of the head hollow portion, with the curing It is firmly bonded to the shell inner surface Te. しかも、硬化した低発泡エポキシ樹脂自体が、大きな強度を有していて耐衝撃性も保有している。 Moreover, cured low foaming epoxy resin itself possesses impact resistance have a high strength. したがって、ヘッド中空部の外殻内面に補強リブ等を形成する必要がなくなり、またクラブヘッドのシエル等をさらに薄肉に形成できるもので、低発泡エポキシ樹脂自体の軽量性と相まってクラブヘッドの重量を著しく軽減できることになる。 Therefore, it is not necessary to form the reinforcing ribs or the like to the shell inner surface of the head hollow portion, also as it can be formed into a further thin the shell, etc. of the club head, the weight of the combined club head and weight of low-foaming epoxy resin itself It would be significantly reduced.

さらに、内芯と外殻内表面との接着構造により、クラブヘッドに衝撃が繰り返し加わっても、内芯が外殻から経時的に分離することがない。 Further, by bonding structure of the inner core and the outer shell inner surface, even if an impact is repeatedly applied to the club head, it is not that the inner core with time separated from the outer shell. この結果、クラブヘッドの打撃面の変形や、内芯の損傷および打撃時の消音効果の経時的な低下を回避でき、優れた性能を長期間保持することができるという効果を併せて奏する。 As a result, deformation of the striking face of the club head, can avoid the temporal decrease in the silencing effect at the time of injury and the striking of the inner core, so together effect that it is possible to hold long-term excellent performance.

【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS

第1図は本発明の一実施例を示す斜視図、第2図はその縦断面図である。 Perspective view showing an embodiment of FIG. 1 according to the present invention, FIG. 2 is a longitudinal sectional view thereof. 1はクラブヘッド、2はシエル(外殻)、3はフェース(外殻)、4はソール(外殻)、6はヘッド中空部、7 1 club head, is 2 shell (outer shell), 3 denotes a face (outer shell), the sole (outer shell) 4, 6 head cavity, 7
は充填材(低発泡エポキシ樹脂)である。 Is filler (low foaming epoxy resin).

Claims (1)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】クラブヘッドをなす外殻にて形成されたヘッド中空部に、低発泡合成樹脂を内芯として充填したゴルフクラブヘッドにおいて、 上記低発泡合成樹脂として、2倍〜4倍の発泡倍率を有する低発泡エポキシ樹脂を用い、かつ、上記内芯と上記外殻の内表面とが、低発泡エポキシ樹脂の硬化に伴って接着されていることを特徴とするゴルフクラブヘッド。 To 1. A head hollow portion formed in an outer shell forming a club head, a golf club head which is filled as the inner core of low foaming synthetic resin, as the low foaming synthetic resin, 2 to 4 times the foam using low foaming epoxy resin having a magnification, and a golf club head and the inner core and the inner surface of the outer shell, characterized in that it is bonded with the cured low-foaming epoxy resin.
JP62322083A 1987-12-18 1987-12-18 Golf club head Expired - Lifetime JPH0626631B2 (en)