JPH0538795A - Multilayer oriented film and manufacture thereof - Google Patents

Multilayer oriented film and manufacture thereof

Info

Publication number
JPH0538795A
JPH0538795A JP19629991A JP19629991A JPH0538795A JP H0538795 A JPH0538795 A JP H0538795A JP 19629991 A JP19629991 A JP 19629991A JP 19629991 A JP19629991 A JP 19629991A JP H0538795 A JPH0538795 A JP H0538795A
Authority
JP
Grant status
Application
Patent type
Prior art keywords
film
resin layer
layer
nylon
method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP19629991A
Other languages
Japanese (ja)
Other versions
JP3016917B2 (en )
Inventor
Ichiro Matsui
一郎 松居
Original Assignee
Sumitomo Bakelite Co Ltd
住友ベークライト株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

PURPOSE:To provide a multilayer oriented film suitable as a raw fabric for the laminate of a film for packaging foods and others, excellent in successive biaxial orientation aptitude, and superior in transparency, mechanical strength, pinhole resistance, gas barrier properties, laminate aptitude, printability, etc., and manufacture thereof. CONSTITUTION:In a multilayer oriented film, in which a polyamide resin layer (A), an ethylene-vinyl acetate copolymer saponified substance resin layer (B) and a modified polyolefin bonding resin layer (C) are laminated in the order of A-B-C-B-A, a layer composed of the blend of amorphous nylon and another nylon is used as the polyamide resin layer (A) and the manufacture of the multilayer oriented film is provided.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【産業上の利用分野】本発明は低密度ポリエチレン、リニア低密度ポリエチレン、ポリプロピレン、エチレン− The present invention is low density polyethylene BACKGROUND OF linear low density polyethylene, polypropylene, ethylene -
酢酸ビニル共重合体、アイオノマー等の樹脂あるいはフィルムと、ドライラミネートや押出ラミネート等の方法により積層することにより、食品、雑貨等の袋包装用フィルム、レトルト用コンテナー、深絞り包装等の蓋材用フィルム等に用いる、透明性、機械的強度、耐ピンホール性、ガスバリヤー性、ラミネート適性、及び印刷適性等が優れた多層延伸フィルム及びその製造方法に関するものである。 Vinyl acetate copolymer, and a resin or a film of ionomers, by laminating by a method such as dry lamination or extrusion lamination, a food, a bag packaging films, such as goods, lid material such as retort containers, deep draw packaging used in the film such as transparency, mechanical strength, pinhole resistance, gas barrier properties, to a laminate suitability, and multilayer stretched film and a manufacturing method thereof printability etc. excellent.

【0002】 [0002]

【従来の技術】食品や雑貨等の包装について、近年、各メーカーにおいては、生産工程上、人員・設備両面から合理化を計る動きがあり、包装機械においては高速化、 For packaging, etc. BACKGROUND OF THE INVENTION food and miscellaneous goods, in recent years, in each of the manufacturer, on the production process, there is a movement to measure the rationalization from personnel and equipment both sides, speeding in the packaging machine,
自動化を目的としてピロー型包装機等の製袋充填包装機が多く用いられるようになってきた。 Automation has come to be used in many cases pillow packaging machine or the like bag-making filling and packaging machine for the purpose. このような包装機にはOPP/PEのようなヒートシール可能なものが通常用いられている。 Such packaging machines are heat-sealable ones are usually used, such as OPP / PE. ところが、内容物や流通方法によっては、これらのフィルムに要求される特性として機械的強度やガスバリヤー性など複数の機能を満足していることが必要であり、フィルムを何層かの積層構造にし、各層に種々の機能を分散させ、総合的に多くの機能を有するものとすることが考えられる。 However, depending on the content and distribution methods, it is necessary to satisfy the plurality of functions, such as mechanical strength and gas barrier properties as properties required for these films, the film several layers of the laminate structure , each layer by dispersing various functions, it is conceivable to as having a total number of features.

【0003】例えば、食品業界においては、流通過程における温度、水分、酸素、光線等や、細菌、カビなどの微生物によって形、色、味、香気の損失などの多種多様の変質により品質低下をおこしやすく、消費者の口に入るまで品質の劣化をおこさせることなく保存する方法として、従来は保存料や酸化防止材などの添加剤を直接食品に添加する方法がとられてきた。 For example, in the food industry, causing the temperature in the distribution process, moisture, oxygen, or light, etc., bacteria, forms by microorganisms such as molds, color, taste, quality degradation by a variety of alteration, such loss of aroma easier, as a method for saving without causing deterioration of quality before entering the consumer's mouth, the conventional way of adding to the food additives such as preservatives and antioxidant material directly it has been taken. ところが近年、食品加工業界、取分け畜肉加工、魚肉加工分野においては食品への添加剤規制が厳しくなり、添加剤の使用量を減少するか或は、ほとんど使用しなくなりつつあり、内容物の長期保存性、新鮮度を確保するために、包装材料に酸素ガスバリヤー性や水蒸気バリヤー性等の機能性を付与したフィルムの開発が必要である。 However, in recent years, the food processing industry, especially processed meat, additive regulations to food is severely in the fish processing sector, or to reduce the use of the additive, or are becoming, and almost never used, long-term storage of the contents gender, in order to ensure the freshness, it is necessary to develop a granted the functionality of the oxygen gas barrier property and water vapor barrier property, etc. in the packaging material film. また、食品流通過程における輸送段階において、輸送方法によってはピンホールが発生するなどの問題があり、耐ピンホール性及び機械的強度の優れたフィルムが必要である。 Further, in the transportation stage in the food distribution process, the transportation method has problems such as pinholes, it is necessary excellent film of pinhole resistance and mechanical strength.

【0004】以上のような点から用いられるフィルムの構成としては、機械的強度付与層/バリヤー層/シーラント層等の構造が必要であり、例えば、機械的強度付与層としては、OPPフィルム、ONyフィルム、PET As a structure of a film to be used from a point as described above, requires a structure such as mechanical strength imparting layer / barrier layer / sealant layer, for example, as a mechanical strength imparting layer, OPP film, ONy film, PET
フィルム等が、酸素ガスバリヤー層としては延伸EVO Films and the like, stretching EVO as oxygen gas barrier layer
Hフィルム等が、水蒸気バリヤー層としては、PVDC H film or the like is, as the moisture vapor barrier layer, PVDC
コートフィルム、アルミ蒸着フィルム等が、また、シーラント層としては、CPPフィルム、LLDPEフィルム、EVA等が従来から用いられてきた。 Coated film, aluminum-deposited films and the like, also, as the sealant layer, CPP film, LLDPE film, EVA or the like has been used conventionally. これらの積層方法としては、ドライラミネート、押出ラミネート、コーティング、蒸着等が用いられるが、これらの方法だと一層々々積層を行わなければならないため、層数が増えて構成が複雑になればなるほど製造工程が増え、コストがかかるという欠点があった。 As a method of these lamination, dry lamination, extrusion lamination, coating, and vapor deposition or the like is used, since not have to more people people perform lamination that's these methods, The more complicated configuration increases the number of layers increase in the manufacturing process, the cost there has been a drawback that it takes. また各層のフィルムの最低厚みに限界があるため多層でかつ極薄のフィルムの製造は不可能である。 The production of films in the multilayer a and ultra-thin because there is a limit to a minimum thickness of each layer of the film is impossible.

【0005】フィルムの二軸延伸方法としてテンター方式による逐次二軸延伸法、及び同時二軸延伸法が知られている。 [0005] successive biaxial stretching method using a tenter method as biaxially stretching method of the film, and simultaneous biaxial stretching method are known. これら両方法を比較すると逐次二軸延伸法は、 The sequential biaxial stretching method Comparing these two methods,
装置の構造が簡単な上、生産性も同時二軸延伸法よりも優れている。 On the structure of the apparatus is simple, it is superior productivity of simultaneous biaxial stretching method. ところが、従来より用いられているナイロン6やナイロン6−6に代表される脂肪族ポリアミド樹脂は逐次二軸延伸における縦延伸において分子間水素結合が横延伸の方向に配向するため横延伸が極めて困難である。 However, aliphatic polyamide resins represented by nylon 6 and nylon 6-6 which are conventionally used are very difficult transverse stretching for intermolecular hydrogen bonds in the longitudinal stretching in sequential biaxial stretching is oriented in the direction of the transverse stretching it is. これらを解決する方法として、脂肪族ポリアミドに、メタキシリレン基を含有するポリアミドをブレンドする方法が、特公昭51−29193号公報等に記載されている。 As a method for solving these, aliphatic polyamides, a method of blending a polyamide containing a m-xylylene group is described in JP-B-51-29193 Publication. 本公報に記載されているのはポリアミドの単層フイルムについてであり、この方法から得られるフィルムは透明性が不十分であり、包装用フィルムとしての要求を満足出来ているものではない。 What is described in this publication is a for a single layer film of the polyamide, films resulting from this method is insufficient transparency, it does not have can satisfy the requirements as packaging film.

【0006】ポリアミド層として非晶性ナイロンを含有する多層延伸フィルムに関しては、特開昭64−717 [0006] With respect to the multilayer stretched film containing the amorphous nylon as the polyamide layer, JP 64-717
49公報に記載されているが、ここでは非晶性ナイロンを用いる目的がバリヤー性向上のためだけであり、延伸方法も、インフレーション法(チューブラー法)によって行われている。 It is described in 49 publications, where the purpose of using the amorphous nylon is only for barrier properties improve, stretching method is also performed by an inflation method (tubular method). また、同時二軸延伸法の一つとしてインフレーション法も知られているが本発明のような複雑な構成を有するフィルムの延伸には不向きである。 Moreover, also known inflation method as one of the simultaneous biaxial stretching method is not suitable for stretching a film having a complicated structure as in the present invention.

【0007】以上の欠点を解決するため、本発明者は特願平02−295388で、ポリアミド樹脂層(A)、 [0007] To solve the above drawbacks, the present inventor in Japanese Patent Application No. 02-295388, a polyamide resin layer (A),
エチレン−酢酸ビニル共重合体けん化物樹脂層(B)、 Ethylene - vinyl acetate copolymer saponified resin layer (B),
変性ポリオレフィン接着用樹脂層(C)を用い、 A− Modified polyolefin adhesive resin layer (C) used, A-
B−A、 A−C−B−C−A、 A−C−B−Aなる層構成の多層延伸フィルムを出願している。 B-A, A-C-B-C-A, has filed a multilayer stretched film of the A-C-B-A comprising a layer structure. ところがこれらのフィルムは水蒸気バリヤー性が劣っていること、 However, of these films that have poor water vapor barrier properties,
ポリアミド樹脂層(A)とエチレン−酢酸ビニル共重合体けん化物樹脂層(B)との異なった樹脂を積層し良好な接着強度が得られる接着用樹脂(C)が少ないこと、 Polyamide resin layer (A) and the ethylene - that vinyl copolymer saponified resin layer acetate (B) and different resin was laminated good adhesive strength can be obtained adhesive resin (C) is small,
又層構成が対称形でないためカールが生じること、等の欠点があった。 The curling occurs due Mataso configuration is not symmetrical, there is a problem and the like.

【0008】 [0008]

【発明が解決しようとする課題】本発明は、これらの欠点を解決するため、本発明者らは鋭意研究を重ねた結果、ポリアミド層として非晶性ナイロンとその他のナイロンとのブレンド物からなる層を用いることにより、逐次二軸延伸性が良好で、さらに耐ピンホール性、透明性、ガスバリヤー性、機械的強度等の優れたの多層延伸フィルム及びその製造方法を得ることが出来た。 The present invention 0005] In order to solve these drawbacks, the present inventors have results of extensive studies, it consists of blends of amorphous nylon and other nylon as the polyamide layer by using a layer, sequential biaxial stretchability is good, further pinhole resistance, transparency, it was possible to obtain a gas barrier property, an excellent multi-layer stretched film and a method of manufacturing such mechanical strength. 本発明の目的とするところは、逐次二軸延伸適性に優れ、また透明性、機械的強度、耐ピンホール性、ガスバリヤー性、ラミネート適性、及び印刷適性等が優れた多層延伸フィルム及びその製造方法を提供することにある。 It is an object of the present invention is excellent in sequential biaxial stretchability, also transparency, mechanical strength, pinhole resistance, the multilayer stretched film and its manufacturing gas barrier laminate suitability, and printability and the like excellent It is to provide a method.

【0009】 [0009]

【課題を解決するための手段】本発明は、ポリアミド樹脂層(A)、エチレン−酢酸ビニル共重合体けん化物樹脂層(B)、変性ポリオレフィン接着用樹脂層(C) The present invention SUMMARY OF], the polyamide resin layer (A), ethylene - vinyl copolymer saponified resin layer acetate (B), modified polyolefin adhesive resin layer (C)
が、A−B−C−B−Aの順で積層された多層延伸フィルムにおいて、ポリアミド樹脂層(A)が、非晶性ナイロンとその他のナイロンとのブレンド物からなる層を用いることを特徴とする多層延伸フィルム、及びその製造方法に関するものである。 Characterized but the multilayer stretched film laminated in the order of A-B-C-B-A, the polyamide resin layer (A), the use of a layer comprising a blend of amorphous nylon and other nylon it relates multilayer stretched film, and a manufacturing method thereof according to. 即ち機械的強度付与層としてポリアミド樹脂層、酸素ガスバリヤー性付与層としてエチレン−酢酸ビニル共重合体けん化物樹脂層を用い、さらに水蒸気バリヤー性を付与するため変性ポリオレフィン接着用樹脂を、層間接着強度とフィルム層構成の対称形を損なわない形で用いて、共押出法により積層構造にしたフィルムを逐次二軸延伸したものである。 That polyamide resin layer as a mechanical strength imparting layer, ethylene as oxygen gas barrier property-imparting layer - using vinyl acetate copolymer saponified resin layer, further a modified polyolefin adhesive resin for imparting water vapor barrier properties, interlayer adhesion strength and used in a form that does not impair the symmetrical film layer structure is obtained by film sequential biaxial stretching in which a laminated structure by a coextrusion method.

【0010】本発明において用いられるポリアミド(以下、PAと略記する。)樹脂(A)は、非晶性ナイロンとその他のナイロンとブレンド物からなる層である。 [0010] Polyamide used in the present invention (hereinafter abbreviated as PA.) Resin (A) is a layer composed of amorphous nylon and other nylon and blends. 非晶性ナイロンとしては、原料としてジカルボン酸、ジアミン、ラクタム、ジイソシアネート等を用い加圧溶融縮重合、脱炭酸縮合反応等により得られる。 The amorphous nylon, dicarboxylic acid as raw materials, diamines, lactams, pressurized melt polycondensation with diisocyanate obtained by decarboxylation condensation reaction or the like. ジカルボン酸としては、アジピン酸、スベリン酸、アゼライン酸、テレフタル酸、イソフタル酸等があげられる。 Examples of the dicarboxylic acid, adipic acid, suberic acid, azelaic acid, terephthalic acid, and isophthalic acid. ジアミンとしては、ヘキサメチレンジアミン、トリメチルヘキサメチレンジアミン、イソホロンジアミン、ビス−p−(アミノシクロヘキシル)メタン、ビス−p−(アミノシクロヘキシル)プロパン等が用いられる。 Examples of the diamine, hexamethylene diamine, trimethyl hexamethylene diamine, isophorone diamine, bis-p-(aminocyclohexyl) methane, bis-p-like (aminocyclohexyl) propane is used. ラクタムとしては、カプロラクタム、ラウロラクタム等があげられる。 As the lactam, caprolactam, laurolactam, and the like.
ジイソシアネートとしては、ジフェニルメタンジイソシアネート、トリレンジイソシアネート等がもちいられる。 The diisocyanate, diphenylmethane diisocyanate, tolylene diisocyanate or the like is used. ブレンドされるその他のナイロンとしては、ω−アミノカルボキシ酸の重縮合反応や、二塩基性酸とジジカルボン酸アミンの重縮合反応等により製造される、ナイロン6、ナイロン12、ナイロン11、ナイロン6− Other nylons are blended, polycondensation reaction or the ω- amino carboxy acid, dibasic acid and is prepared by polycondensation reaction of Jijikarubon acid amine, nylon 6, nylon 12, nylon 11, nylon 6
6、ナイロン6−10、ナイロン6−12、およびこれらの共重合体、またはブレンド物等が用いられる。 6, nylon 6-10, nylon 6-12, and copolymers thereof, or blends thereof or the like is used.

【0011】エチレン−酢酸ビニル共重合体けん化物樹脂(EVOH)層(B)は、軟化温度(フローテスタ− [0011] Ethylene - vinyl acetate copolymer saponified resin (EVOH) layer (B), softening temperature (Flow Tester -
法)が、150℃〜175℃で、エチレン含有率が25 Law) is, at 0.99 ° C. to 175 ° C., ethylene content 25
〜75モル%、共重合体中の酢酸ビニルに対するけん化度が90%以上のものがよい。 75 mol%, saponification degree for vinyl acetate in the copolymer is better of 90% or more.

【0012】変性ポリオレフィン接着用樹脂層(C) [0012] modified polyolefin adhesive resin layer (C)
は、エチレン−酢酸ビニル共重合体、またはエチレン− An ethylene - vinyl acetate copolymer, or ethylene -
プロピレンエラストーに、アクリル酸、メタクリル酸などの一塩基性不飽和脂肪酸、あるいはマレイン酸、フマル酸、イタコン酸などの二塩基性不飽和脂肪酸の無水物、すなわち無水マレイン酸等を、化学的に結合させて得られる酸変性オレフィン系樹脂が用いられる。 Propylene elastography chromatography, acrylic acid, monobasic unsaturated fatty acids, such as methacrylic acid or maleic acid, fumaric acid, anhydrides of dibasic unsaturated fatty acids such as itaconic acid, i.e. maleic acid and the like, chemically acid-modified olefin resin obtained coupled to form is used.

【0013】本発明の多層延伸フイルムの総厚みは、特に限定しないが、他のフイルムや樹脂と積層して食品包装等の用途に用いる場合は、10〜30μm位の厚さが最適である。 [0013] The total thickness of the multilayer stretched film of the present invention is not particularly limited, when using laminated with other film or resin for use food packaging, such as, the thickness of the position 10~30μm is optimal.

【0014】本発明の多層延伸フィルムの外層となるP [0014] P which is the outer layer of the multilayer stretched film of the present invention
A樹脂層(A)には印刷機、ラミネート機、および包装機等との機械適性を上げるため適当な滑剤を適量添加してもよい。 A resin layer printing machine (A), the may be added in an appropriate amount of suitable lubricants to increase the machinability of a laminating machine, and packaging machines.

【0015】フィルムの製造方法としては、複数の押出機による共押出方法にて積層ダイから溶融押出しを行い、冷却固化を行う方法が最適である。 [0015] As a method for producing the film, was melt-extruded from stacked die in a coextrusion method by a plurality of extruders, a method of performing cooling and solidification is optimal. 延伸方法としてはテンター方式による逐次二軸延伸方法により行い、その延伸温度としては50℃〜200℃、延伸倍率としては2〜6倍の範囲内の条件が適している。 Carried out by successive biaxial stretching method by a tenter method as the stretching method, the 50 ° C. to 200 DEG ° C. As the stretching temperature, the conditions in the range of 2-6 times are suitable as draw ratio. さらに延伸の後続けて、延伸温度よりも5℃以上高い温度でヒートセットを行う。 Further continued after stretching, performing heat setting at 5 ° C. or higher temperature higher than the stretching temperature. あるいは、ヒートセットを行わず、熱収縮性フィルムとすることもできる。 Alternatively, without performing the heat setting, it may be a heat-shrinkable film.

【0016】 [0016]

【実施例】Tダイ押出し法により、多層共押出ダイから溶融押出しし、PA/EVOH/接着性樹脂/EVOH The EXAMPLES T-die extrusion method, and melt-extruded from a multilayer co-extrusion die, PA / EVOH / adhesive resin / EVOH
/PAの層構成のフィルム(厚み170μm)を作製した。 / Film of the layer structure of PA (thickness 170 [mu] m) were produced. 各層の厚み比率は27/10/26/10/27% Thickness ratio of each layer is 27/10/26/10/27%
とした。 And the. 各層構成樹脂の原料としては、 PA 三井テ゛ュホ゜ンホ゜リケミカル製 シ―ラPA3426 The raw material of each layer constituting the resin, PA Mitsui de Yuponpo Rikemikaru made sheet - la PA3426
(非晶性ナイロン)と、 宇部興産製 1030B(6-Ny)とのブレンド物 EVOH クラレ製 エバールEP−F And (amorphous nylon), EVAL blend EVOH produced by Kuraray Co. and manufactured by Ube Industries 1030B (6-Ny) EP-F
101 接着性樹脂層 三井石油化学製 アドマーNF−5 101 adhesive resin layer made by Mitsui Petrochemical Admer NF-5
00 を用いた。 00 was used. 得られた多層フィルムを、テンター方式逐次二軸延伸製造装置にかけ、下記条件で延伸を行い、厚さ15μmのフィルムを作製した。 The resulting multilayer film was subjected to tenter method successive biaxial stretching manufacturing apparatus performs a stretching under the following conditions to prepare a film having a thickness of 15 [mu] m. 延伸温度 縦 85℃ 横 100℃ 延伸倍率 縦 3.2倍 横 3.4倍 ヒートセット温度 190℃ ライン速度 100M/分 表1にPA層のブレンド比率を変えた場合の逐次二軸延伸適性を示した。 Stretching temperature Vertical 85 ° C. Horizontal 100 ° C. stretch ratio lengthwise 3.2 times transverse 3.4 times heat set temperature 190 ° C. The line speed 100M / in min Table 1 shows the sequential biaxial stretchability when changing the blending ratio of the PA layers It was.

【0017】 [0017]

【表1】 [Table 1]

【0018】比較例1、2に示すように非晶性Ny、6 [0018] Amorphous As shown in Comparative Examples 1, 2 Ny, 6
−Ny単独のものについては、横延伸時にフィルムの破断や延伸斑が生じ良好なフィルムは得られなかった。 For -Ny single ones, good film occurs breakage or stretching unevenness of the film during the transverse stretching was not obtained. これに対し本発明による実施例1、2のフィルムについては特に問題なく延伸でき、非晶性ナイロンをブレンドしたことによる6−Nyの延伸性改良の効果が得られた。 Contrast can stretch without any particular problem for the films of Examples 1 and 2 according to the present invention, the effect of stretching improving the 6-Ny due to a blend of amorphous nylon were obtained.

【0019】実施例1のフィルムと、比較例3として、 [0019] and the film of Example 1, Comparative Example 3,
PA/EVOH/PAの層構成のフィルム(厚み170 PA / EVOH / film of the layer structure of PA (thickness 170
μm、各層厚み比率40/20/40%、原材料と延伸条件は実施例1と同じ)の物性を表2に示した。 [mu] m, each layer thickness ratio 40/20/40% raw materials and stretching conditions showed the physical properties of the same) as in Example 1 in Table 2.

【0020】 [0020]

【表2】 [Table 2]

【0021】表2に示すように、本発明による実施例1 As shown in Table 2, Example 1 according to the present invention
のフィルムの機械的強度や透明性は、上市されている延伸ナイロン(ONy)フィルム(15μm)とほぼ同等である。 Mechanical strength and transparency of the film is substantially the same as nylon stretched as it is marketed (ONy) film (15 [mu] m). そのうえ、酸素ガスバリア性が非常に優れている。 In addition, oxygen gas barrier properties are very good. これらの特性を合わせ持つフィルムを、ONyフィルムと延伸EVOHフィルム(クラレ 製エバールEF A film having both these characteristics, ONy film and stretched EVOH film (manufactured by KURARAY EVAL EF
−XL)とのドライラミネートにより得ようとしても、 As well as trying to obtain by dry lamination of the -XL),
各フィルムの厚みに限界があるため、本発明の様に15 Since the thickness of each film is limited, as in the present invention 15
μm厚のフィルムを得ることは不可能である。 It is impossible to obtain μm thick film. また、比較例3のフィルムは透湿度が49g/m2・day と大きいが、実施例1のフィルムは約5倍、バリヤー性が良くなっている。 The film of Comparative Example 3 is the moisture permeability is large and 49g / m2 · day, the film of Example 1 was about 5-fold, it has better barrier properties. 実施例1のフィルムの片面をコロナ処理し、 One side of the film in Example 1 was corona treated,
図柄を印刷し、さらに厚み50μmのリニア低密度ポリエチレン(LLDPE)フィルムをウレタン系接着剤を介してドライラミネート法で貼合わせ厚み65μmのフィルムを作製した。 Print the pattern, to form a film of lamination thickness 65μm with dry lamination method further via a urethane adhesive linear low density polyethylene (LLDPE) film having a thickness of 50 [mu] m. コロナ処理、印刷、ドライラミネートの各工程での機械適性等の問題は特になかった。 Corona treatment, printing, such as mechanical suitability in the process of dry lamination problem was not specified. このフィルムを用いて、3方シール製袋機、横ピロー包装機で適当な大きさの袋を作製し、外観、破袋強度等の試験を行ったが特に問題は無かった。 Using this film, edge sealed bag-making machine, the horizontal pillow type packaging machine to produce bags of appropriate size, appearance, and were tested such as bag breakage strength particular problem was not.

【0022】 [0022]

【発明の効果】本発明による多層延伸フィルムは、逐次二軸延伸適性が優れている上、透明性、機械的強度、耐ピンホール性、ガスバリヤー性、ラミネート適性、及び印刷適性等が優れており、食品、その他の包装用フィルムのラミネート用原反として好適である。 The multilayer stretched film according to the present invention exhibits, on its excellent sequential biaxial stretchability, transparency, mechanical strength, pinhole resistance, gas barrier property, lamination aptitude, and printability and the like excellent cage, food, is suitable as a laminate original sheet for other packaging films.

───────────────────────────────────────────────────── ────────────────────────────────────────────────── ───

【手続補正書】 [Procedure amendment]

【提出日】平成4年10月12日 [Filing date] 1992 October 12,

【手続補正1】 [Amendment 1]

【補正対象書類名】明細書 [Correction target document name] specification

【補正対象項目名】0012 [Correction target item name] 0012

【補正方法】変更 [Correction method] change

【補正内容】 [Correction contents]

【0012】変性ポリオレフィン接着用樹脂層(C) [0012] modified polyolefin adhesive resin layer (C)
は、エチレン−酢酸ビニル共重合体、またはエチレン− An ethylene - vinyl acetate copolymer, or ethylene -
プロピレンエラストーに、アクリル酸、メタクリル酸などの一塩基性不飽和脂肪酸、あるいはマレイン酸、フマル酸、イタコン酸などの二塩基性不飽和脂肪酸の無水物、すなわち無水マレイン酸等を、化学的に結合させて得られる酸変性オレフィン系樹脂が用いられる。 Propylene elastography M a, acrylic acid, monobasic unsaturated fatty acids, such as methacrylic acid or maleic acid, fumaric acid, anhydrides of dibasic unsaturated fatty acids such as itaconic acid, i.e. maleic acid and the like, chemical acid-modified olefin resin obtained by binding to is used.

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl. 5識別記号 庁内整理番号 FI 技術表示箇所 B29K 55:00 77:00 B29L 7:00 4F 9:00 4F ────────────────────────────────────────────────── ─── front page continued (51) Int.Cl. 5 identification symbol Agency in Docket No. FI art display portion B29K 55:00 77:00 B29L 7:00 4F 9:00 4F

Claims (2)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 ポリアミド樹脂層(A)、エチレン−酢酸ビニル共重合体けん化物樹脂層(B)、変性ポリオレフィン接着用樹脂層(C)が、A−B−C−B−Aの順で積層された多層延伸フィルムにおいて、ポリアミド樹脂層(A)が、非晶性ナイロンとその他のナイロンとのブレンド物からなる層を用いることを特徴とする多層延伸フィルム。 1. A polyamide resin layer (A), ethylene - vinyl copolymer saponified resin layer acetate (B), modified polyolefin adhesive resin layer (C) is in the order of A-B-C-B-A in laminated multilayer stretched film, multilayer stretched film polyamide resin layer (a), is characterized by using a layer made of a blend of amorphous nylon and other nylon.
  2. 【請求項2】 延伸温度が50〜200℃、延伸倍率が2〜6倍の範囲で逐次二軸延伸を行うことを特徴とする請求項記載1の多層延伸フィルムの製造方法。 2. A method for producing a multilayer stretched film of the claimed 1 stretching temperature is 50 to 200 ° C., the draw ratio and performs the sequential biaxial stretching in the range of 2-6 times.
JP19629991A 1991-08-06 1991-08-06 Multi-layer stretched film and a method of manufacturing the same Expired - Fee Related JP3016917B2 (en)