JPH05338358A - Heat mode thermal transfer recording material - Google Patents

Heat mode thermal transfer recording material

Info

Publication number
JPH05338358A
JPH05338358A JP14947292A JP14947292A JPH05338358A JP H05338358 A JPH05338358 A JP H05338358A JP 14947292 A JP14947292 A JP 14947292A JP 14947292 A JP14947292 A JP 14947292A JP H05338358 A JPH05338358 A JP H05338358A
Authority
JP
Grant status
Application
Patent type
Prior art keywords
layer
recording material
transfer recording
ink layer
heat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP14947292A
Other languages
Japanese (ja)
Other versions
JP3215988B2 (en )
Inventor
Sota Kawakami
Katsumi Maejima
Shinji Matsumoto
Atsushi Nakajima
厚志 仲島
勝己 前島
壮太 川上
晋治 松本
Original Assignee
Konica Corp
コニカ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

PURPOSE: To provide a heat mode thermal transfer recording material having sensitivity suitable for laser beam, imparting a transfer image free from color turbidity and obtaining an image excellent in color reproducibility.
CONSTITUTION: In a heat mode thermal transfer recording material characterized by that a photothermal conversion layer containing at least a solvent-soluble near infrared absorbing dye and a water-soluble ink layer are provided on a support, the solvent-soluble near infrared absorbing dye is dissolved in a solvent in an amount Of 0.1wt.% or more, the thickness of the photothermal conversion layer is 1.0μm or less, the absorbancy of the photothermal conversion layer at the max. absorption density of a wavelength of 700-1000nm is 0.3 or more, the ink layer contains a water-soluble binder, the thickness of the ink layer is 1.0μm or less and the transmissivity of a wavelength of 700nm or more at an absorption peak is 10% or less. The thickness of 1.0μm or less of the ink layer is a pref. mode because effect is more developed.
COPYRIGHT: (C)1993,JPO&Japio

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【産業上の利用分野】本発明はヒートモード熱転写記録材料に関し、特にレーザー等の光源により色再現性の良い転写画像が得られるヒートモード熱転写記録材料に関する。 The present invention relates to a heat mode transfer recording material BACKGROUND OF THE, more particularly a heat mode transfer recording material good transferred image color reproducibility can be obtained by a light source such as a laser.

【0002】 [0002]

【発明の背景】従来、熱転写記録方法としてはサーマルヘッドによる加圧加熱方式が実用化されてきたが、近年、より高解像度の画像を記録できる方式として、レーザービームを熱転写記録材料に照射し、この記録材料中でレーザービームを熱に変換して熱転写記録を行う方式が使用されるようになった。 BACKGROUND OF THE INVENTION Conventionally, a thermal transfer recording method as pressure heating method by a thermal head has been put into practical use, in recent years, as a method capable of recording image of higher resolution, the laser beam is irradiated to the thermal transfer recording material, the laser beam in the recording material has become a method of performing a thermal transfer recording is converted into heat is used. このレーザー熱転写記録方式(ヒートモード熱転写記録方式)は、エネルギー供給に用いられるレーザー光を数μm程度にまで集光できるので、サーマルヘッドで熱を供給する熱転写記録方法に比べて飛躍的に解像度の向上が可能となる。 The laser thermal transfer recording method (heat mode transfer recording system), since the laser light used for energy supply can condensing to about several [mu] m, dramatically resolution as compared to the thermal transfer recording method for supplying heat in a thermal head improvement is possible.

【0003】しかしながら、支持体上に光熱変換材を含有する光熱変換層とインク層の順に積層したヒートモード熱転写記録材料は、光熱変換層中の光熱変換材がインク層に溶け出したり、或いは転写時に光熱変換材が飛散して色濁りを生ずるなどの問題を有していた。 However, heat mode transfer recording material stacked in this order of the light-to-heat conversion layer and an ink layer containing a photothermal conversion material on a support, or light-to-heat conversion material of the photothermal conversion layer is dissolved into the ink layer, or a transfer It had problems such as causing color contamination during the light-to-heat conversion material is scattered.

【0004】 [0004]

【発明の目的】本発明の目的は、レーザー光等に適した感度を有し、転写像の色濁りがなく、従って色再現性に優れた画像が得られるヒートモード熱転写記録材料を提供することにある。 An object of the present invention is an object of the invention has a sensitivity suitable for laser beam or the like, no color turbidity of the transferred image, thus to provide a heat mode transfer recording material an image having excellent color reproducibility is obtained It is in.

【0005】 [0005]

【発明の構成】本発明の上記目的は、下記の構成により達成される。 The above object of the present invention DETAILED DESCRIPTION OF THE INVENTION is achieved by the following constitutions.

【0006】(1)支持体上に少なくとも溶剤溶解性近赤外吸収色素を含有する光熱変換層及び水溶性インク層を有することを特徴とするヒートモード熱転写記録材料。 [0006] (1) heat mode transfer recording material characterized by having at least a light-to-heat conversion layer and the water-soluble ink layer contains a solvent soluble near infrared absorbing dye on a support.

【0007】(2)溶剤溶解性近赤外吸収色素が溶剤に0. [0007] (2) 0 solvent-soluble near-infrared-absorbing dye in a solvent.
1重量%以上溶解する色素である(1)記載のヒートモード熱転写記録材料。 A dye which dissolves less than 1% by weight (1) a heat mode transfer recording material according.

【0008】(3)光熱変換層の厚みが1.0μm以下であり、かつ700nm〜1000nmの波長の最大吸収濃度での光熱変換層の吸光度が0.3以上である(1)記載のヒートモード熱転写記録材料。 [0008] (3) Thickness of the light-to-heat conversion layer has a 1.0μm or less, and the absorbance of the light-to-heat conversion layer at the maximum absorption density at a wavelength of 700nm~1000nm is 0.3 or more (1) heat mode thermal transfer recording material according .

【0009】(4)インク層が水溶性バインダーを含有する(1)記載のヒートモード熱転写記録材料。 [0009] (4) The ink layer contains a water-soluble binder (1) heat mode transfer recording material according.

【0010】(5)インク層がタッキファイアー樹脂の水エマルジョンを含有する(1)記載のヒートモード熱転写記録材料。 [0010] (5) The ink layer contains a water emulsion of tackifier Fire resin (1) heat mode transfer recording material according.

【0011】(6)インク層の厚みが1.0μm以下である [0011] (6) the thickness of the ink layer is 1.0μm or less
(1)記載のヒートモード熱転写記録材料。 (1) heat mode thermal transfer recording material according.

【0012】以下、本発明をより詳細に説明する。 [0012] In the following, the present invention will be described in more detail.

【0013】ヒートモード熱転写記録材料(以下、単に「記録材料」とも言う)は、基本的に支持体上に光熱変換材を含有する光熱変換層とインク層の順に積層したものである。 [0013] heat mode transfer recording material (hereinafter, simply referred to as "recording material") is formed by laminating in this order of the light-to-heat conversion layer and an ink layer containing a photothermal conversion material essentially on the support.

【0014】本発明においては、光熱変換作用を司る光熱変換材として溶剤溶解性の近赤外吸収色素を用いるので、該光熱変換材が上層(インク層)に溶け出し光熱変換色素の可視部の吸収が色濁りの原因となるのを、水系インク層により抑制するものである。 [0014] In the present invention uses the solvent solubility of the near infrared absorbing dye as a light-heat conversion material which governs the photothermal conversion effect, photothermal conversion material layer of the visible portion of the light-to-heat conversion dye dissolved into (ink layer) from absorption causes color turbidity, it is suppressed by water-based ink layer. この水系インクは、従来用いられて来た溶剤溶解性インクに比べ、環境汚染防止、安全衛生、省資源、省エネルギーの点からも好ましい。 The water-based ink, as compared to solvent solubility ink have been used conventionally, to prevent environmental pollution, the preferred safety and health, resource saving, in terms of energy saving.

【0015】上記近赤外吸収色素としては、シアニン系色素、スクアリウム系色素、クロコニウム系色素、アズレニウム系色素、フタロシアニン系色素、ナフタロシアニン系色素、ジチオール金属錯体系色素、アントラキノン系色素、インドアニリン金属錯体色素、分子間CT色素等が挙げられる。 [0015] Examples of the above-mentioned near-infrared-absorbing dyes, cyanine dyes, squarylium-based dyes, croconium dye, azulenium dyes, phthalocyanine dyes, naphthalocyanine dyes, dithiol metal complex dyes, anthraquinone dyes, indoaniline metal complex dye, intermolecular CT dyes.

【0016】本発明に好ましく用いられる近赤外吸収色素の代表的具体例を以下に挙げるが、これらに限定されない。 [0016] Typical examples of the near-infrared-absorbing dye preferably used in the present invention are set forth below, but not limited thereto.

【0017】 [0017]

【化1】 [Formula 1]

【0018】 [0018]

【化2】 ## STR2 ##

【0019】 [0019]

【化3】 [Formula 3]

【0020】 [0020]

【化4】 [Of 4]

【0021】上記色素の溶剤溶解性(室温におけるメチルエチルケトンへの溶解重量%)は以下の通りである。 The solvent solubility of the dye (dissolution wt% to methyl ethyl ketone at room temperature) is as follows.

【0022】(1)5%以上 (2)5%以上 (3)10%以上 (4)5%以上 (5)3%以上 (6)3%以上 (7)5%以上 (8)5%以上 (9)3% [0022] (1) 5% or more (2) more than 5% (3) 10% or more (4) more than 5% (5) 3% or more (6) 3% or more (7) 5% or more (8) 5% more (9) 3%
以上 (10)8%以上 (11)3%以上 (12)5%以上 (13)3%以上 これらの色素は勿論、公知の方法によって合成することができるが、下記のような市販品を用いることもできる。 Or (10) more than 8% (11) 3% or more (12) more than 5% (13) 3% or more of these dyes, of course, can be synthesized by known methods, using the commercially available products such as: it is also possible.

【0023】日本化薬:IR750(アントラキノン系);IR [0023] Nippon Kayaku: IR750 (anthraquinone); IR
002,IR003(アルミニウム系);IR820(ポリメチン系); 002, IR003 (aluminum type); IR820 (polymethine type);
IRG022,IRG033(ジインモニウム系);CY-2,CY-4,CY- IRG022, IRG033 (diimmonium); CY-2, CY-4, CY-
9,CY-20 三井東圧:KIR103,SIR103(フタロシアニン系);KIR10 9, CY-20 Mitsui Toatsu: KIR103, SIR103 (phthalocyanine); KIR10
1,SIR114(アントラキノン系);PA1001,PA1005,PA1006, 1, SIR114 (anthraquinone); PA1001, PA1005, PA1006,
SIR128(金属錯体系) 大日本インキ化学:Fastogen blue8120 みどり化学:M SIR128 (metal complex) Dainippon Ink and Chemicals: Fastogen blue8120 Green Chemistry: M
IR-101,1011,1021 その他、日本感光色素、住友化学、富士写真フイルム等の各社からも市販されている。 IR-101,1011,1021 other, Japan photosensitive dye, it is also commercially available from Sumitomo Chemical, each company of Fuji Photo Film, and the like.

【0024】これら光熱変換材は溶剤に溶解され、光熱変換層用塗布液が調製されるが、該溶剤としては光熱変換材を高濃度に溶解し、かつインク層の素材を溶解し難いものであれば特に制約されない。 [0024] These light-heat conversion material is dissolved in a solvent, although the light-to-heat conversion layer coating liquid is prepared, as is the solvent to dissolve the light-heat conversion material in a high concentration, and those difficult to dissolve the material of the ink layer It is not particularly limited, if any. 具体的には、アセトン、メチルエチルケトン、シクロヘキサノン等のケトン類;酢酸エチル、酢酸アミル、フタル酸ジメチル、安息香酸エチル等のエステル類;トルエン、キシレン、ベンゼン等の芳香族炭化水素;四塩化炭素、トリクロロエチレン、クロロベンゼン等のハロゲン化炭化水素;ジエチルエーテル、メチルセロソルブ、テトラヒドロフラン、 Specifically, acetone, methyl ethyl ketone, ketones such as cyclohexanone, ethyl acetate, amyl acetate, dimethyl phthalate, esters such as ethyl benzoate; toluene, xylene, aromatic hydrocarbons such as benzene, carbon tetrachloride, trichlorethylene halogenated hydrocarbons such as chlorobenzene; diethyl ether, methyl cellosolve, tetrahydrofuran,
ジオキサン等のエーテル類、その他、ジメチルホルムアミド、ジメチルスルホキシド、ベントキソン等が使用できる。 Ethers such as dioxane, etc., dimethylformamide, dimethyl sulfoxide, Bentokison like.

【0025】塗布液には、塗布性を向上させるために界面活性剤等を添加してもよく、更に光熱変換層と下層との接着を増すような物質や、上層のインク層との剥離性を良くするような物質を含有してもよい。 The coating liquid may be added a surfactant for improving the coating properties, materials and that further increase the adhesion between the light-to-heat conversion layer and the lower layer, peeling of the upper layer of the ink layer materials such as the well may contain.

【0026】光熱変換層中の光熱変換材量は、通常2〜 The light-heat conversion material of the photothermal conversion layer is usually 2 to
80重量%、好ましくは15〜60重量%であるが、700〜100 80 wt%, but preferably 15 to 60 wt%, from 700 to 100
0nmにおける最大吸収濃度での光熱変換層の吸光度が0.3 Absorbance of the light-to-heat conversion layer at a maximum absorption density at 0nm 0.3
以上になるように調整する。 Adjusted to be equal to or greater than. 尚、この光熱変換材は他の層にも添加できる。 Incidentally, the light-heat conversion material can be added to other layers.

【0027】本発明のインク層は、水溶性色材をバインダーと共に水に溶解あるいは分散して塗布液を調製する。 The ink layer of the present invention, to prepare a coating solution of a water-soluble colorant dissolved or dispersed in water together with a binder.

【0028】水溶性インクとしては、無機あるいは有機の顔料、染料で水溶性のものが用いられるが、例えばイエロー、マゼンタ、シアンの顔料系化合物が好ましい。 Examples of the water-soluble ink, inorganic or organic pigments, but water-soluble dye is used, for example, yellow, magenta, pigment-based compounds cyan are preferred.

【0029】無機顔料としては、二酸化チタン、カーボンブラック、酸化亜鉛、プルシアンブルー、硫化カドミウム、酸化鉄ならびに鉛、亜鉛、バリウム及びカルシウムのクロム酸塩などが挙げられる。 [0029] As the inorganic pigments include titanium dioxide, carbon black, zinc oxide, Prussian blue, cadmium sulfide, iron oxide and lead, zinc, chromium barium or calcium and the like. 有機顔料としては、 Examples of the organic pigment,
アゾ系、チオインジゴ系、アントラキノン系、アントアンスロン系、トリフェンジオキサジン系の顔料、バット染料顔料、フタロシアニン顔料(銅フタロシアニン及びその誘導体)、キナクリドン顔料などが挙げられる。 Azo, thioindigo, anthraquinone compounds, pigments triphendioxazine pigment, vat dye pigment, phthalocyanine pigment (copper phthalocyanine and its derivatives), such as quinacridone pigments.
又、有機染料としては、酸性染料、直接染料、分散染料などが挙げられる。 As the organic dyes, acid dyes, direct dyes, and the like disperse dyes.

【0030】インク層のバインダーとしては、ポリエステル、ポリ酢酸ビニル、ポリアクリルアミド、アイオノマー樹脂、オレフィン系樹脂、ロジン樹脂等の水エマルジョンが用いられるが、水に分散、溶解可能なものならば特に限定されない。 [0030] The binder of the ink layer, polyester, polyvinyl acetate, polyacrylamide, an ionomer resin, olefin resin, water emulsion, such as rosin resin is used, water in the dispersion is not particularly limited if it can dissolve .

【0031】又、水溶性バインダーとしては、ポリビニルピロリドン、ゼラチン、カゼイン、ヒドロキシエチルセルロース、カルボキシメチルセルロース、メチルセルロース、ヒドロキシエチル澱粉、アラビアゴム、サクローズオクタアセテート、アルギン酸アンモニウム、アルギン酸ナトリウム、ポリビニルアミン、ポリエチレンオキシド、ポリアクリル酸等が挙げられる。 [0031] Also, as the water-soluble binder is polyvinyl pyrrolidone, gelatin, casein, hydroxyethyl cellulose, carboxymethyl cellulose, methyl cellulose, hydroxyethyl starch, gum arabic, sucrose octacetate, ammonium alginate, sodium alginate, polyvinyl amine, polyethylene oxide, polyacrylic acid and the like.

【0032】タッキファイヤーとしては、ロジンあるいはロジン誘導体、テルペン系樹脂、石油系樹脂、フェノール系樹脂、キシレン系樹脂等があるが、特にロジンあるいはロジン誘導体は水系エマルジョンとして用い易い。 [0032] As the tackifier, rosin or rosin derivatives, terpene resins, petroleum resins, phenol resins, there are xylene resins, especially rosin or rosin derivative is easily used as an aqueous emulsion.

【0033】バインダーとインクとの重量比は1:10〜 The weight ratio of the binder and the ink is 1: 10
10:1が好ましく、2:8〜8:2が特に好ましい。 10: 1 are preferred, 2: 8 to 8: 2 is particularly preferred.

【0034】記録材料の支持体としては、寸法安定性が良く、画像形成時の熱に耐えるものなら何でもよく、具体的には特開昭63-193886号2頁左下欄12行〜18行に記載のフィルム又はシートを使用できる。 [0034] As the support of the recording material, good dimensional stability, whatever withstand the heat at the time of image forming well, on 63-193886 Patent 12 rows to 18 rows 2 page lower left column JP specifically the film or sheet according available. 支持体の厚さは特に制約はないが、通常2〜100μm、好ましくは25〜75μ The thickness of the support is not particularly limited, but usually 2 to 100 m, preferably 25~75μ
mである。 A m.

【0035】レーザー光を支持体側から照射して画像を形成するのであれば、支持体は透明であることが望ましい。 [0035] If images are formed by irradiating a laser beam from the support side, it is desirable that the support is transparent. 又、レーザー光が受像層側から照射するのであれば、支持体は特に透明である必要はない。 Further, if the laser beam is irradiated from the image receiving layer side, the support need not be particularly transparent.

【0036】光熱変換層及びインク層の膜厚は、薄い方が光熱変換層で得られた熱エネルギーがインク層と受像層との界面に到達する時間が短くて済み、又、光熱変換層の熱容量が小さくなるので、溶融温度に達するのに必要なエネルギーが小さくて済む。 The thickness of the light-to-heat conversion layer and an ink layer thinner is be short time to heat energy obtained in the light-to-heat conversion layer to reach the interface between the ink layer and the image receiving layer, and, the light-to-heat conversion layer since the heat capacity is small, only a small energy required to reach the melting temperature. 従って共に1.0um以下であることが好ましく、特に0.2〜0.8μmの範囲が望ましい。 Thus both is preferably 1.0um or less, in particular in the range of 0.2~0.8μm is desirable.

【0037】本発明においては、支持体と光熱変換層あるいは光熱変換層とインク層との間に中間層を介在させることができる。 [0037] In the present invention, it is possible to interpose an intermediate layer between the support and the light-heat conversion layer or the light-heat conversion layer and an ink layer. 中間層には様々の機能を持たせることができ、例えば、インク層中の熱拡散性色材が他層に拡散するのを防止するバリヤー層としての機能、記録材料と熱転写受像材料との密着を増すクッション層としての機能、画像形成時にインク層と光熱変換層との剥離を円滑にする剥離層としての機能などを付与できる。 The intermediate layer can have a variety of functions, for example, functions as a barrier layer thermally diffusing colorant in the ink layer is prevented from diffusing into other layers, adhesion to the recording material and the thermal transfer image receiving material functions as a cushion layer to increase, and functions as a release layer to facilitate separation of the ink layer and the light-heat conversion layer during image forming can be imparted. 支持体と光熱変換層の間にはクッション層があることが好ましく、光熱変換層とインク層の間には剥離層があってもよい。 Preferably there is a cushion layer between the support and the light-heat conversion layer, there may be a release layer between the light-to-heat conversion layer and an ink layer.

【0038】クッション性を付与するには、低弾性率を有する材料あるいはゴム弾性を有する材料を使用すればよい。 [0038] To impart cushioning property, it is sufficient to use a material having a material or rubber elasticity having a low modulus of elasticity. 具体的には、天然ゴム、アクリレートゴム、ブチルゴム、ニトリルゴム、ブタジエンゴム、イソプレンゴム、スチレン-ブタジエンゴム、クロロプレンゴム、ウレタンゴム、シリコーンゴム、アクリルゴム、弗素ゴム、ネオプレンゴム、クロロスルホン化ポリエチレン、 Specifically, natural rubber, acrylate rubber, butyl rubber, nitrile rubber, butadiene rubber, isoprene rubber, styrene - butadiene rubber, chloroprene rubber, urethane rubber, silicone rubber, acrylic rubber, fluorine rubber, neoprene rubber, chlorosulfonated polyethylene,
エピクロルヒドリン、EPDM(エチレン・プロピレン・ジエンゴム)、ウレタンエラストマー等のエラストマー、ポリエチレン、ポリプロピレン、ポリブタジエン、 Epichlorohydrin, EPDM (ethylene-propylene-diene rubber), elastomers such as urethane elastomer, polyethylene, polypropylene, polybutadiene,
ポリブテン、耐衝撃性ABS樹脂、ポリウレタン、AB Polybutene, impact resistance ABS resin, polyurethane, AB
S樹脂、アセテート、セルロースアセテート、アミド樹脂、ポリテトラフルオロエチレン、ニトロセルロース、 S resin, acetate, cellulose acetate, amide resin, polytetrafluoroethylene, nitrocellulose,
ポリスチレン、エポキシ樹脂、フェノール-ホルムアルデヒド樹脂、ポリエステル、耐衝撃性アクリル樹脂、スチレン-ブタジエン共重合体、エチレン-酢酸ビニル共重合体、アクリロニトリル-ブタジエン共重合体、塩化ビニル-酢酸ビニル共重合体、ポリ酢酸ビニル、可塑剤入り塩化ビニル樹脂、塩化ビニリデン樹脂、ポリ塩化ビニル、ポリ塩化ビニリデン等の内、弾性率の小さな樹脂が挙げられる。 Polystyrene, epoxy resin, phenol - formaldehyde resins, polyesters, impact-resistant acrylic resin, styrene - butadiene copolymer, ethylene - vinyl acetate copolymer, acrylonitrile - butadiene copolymer, vinyl chloride - vinyl acetate copolymer, poly vinyl acetate, vinyl chloride resins containing a plasticizer, a vinylidene chloride resin, polyvinyl chloride, of polyvinylidene chloride include a resin having a low modulus of elasticity.

【0039】又、これらの材料を支持体形成時に適用して、支持体自身にクッション性を持たせることもできる。 [0039] Also, by applying these materials when the support is formed, it is also possible to provide the cushioning support itself.

【0040】クッション層の厚みは使用する樹脂あるいはエラストマーの種類、記録材料-受像材料密着の際の吸引力、マット材の粒径、マット材の使用量など様々の因子により異なるので一概には決められないが、通常10 [0040] The thickness of the cushion layer is the type of resin or elastomer used, a recording material - suction force at the time of image-receiving material contact, the particle size of the mat member, unconditionally differs by a variety of factors such as the amount of the mat member decided is not, but usually 10
〜100μmの範囲である。 It is in the range of ~100μm.

【0041】クッション層の形成方法としては、前記素材を溶媒に溶解又はラテックス状に分散したものを、ブレードコーター、ロールコーター、バーコーター、カーテンコーター、グラビアコーター等の塗布法、ホットメルトでの押出しラミネーション法、クッション層フィルムの貼合せ法などを適用できる。 [0041] As a method of forming the cushion layer, extrusion of those of the material dispersed in dissolved or latex form in a solvent, a blade coater, a roll coater, a bar coater, a curtain coater, a coating method such as gravure coater, a hot melt lamination method, can be applied, such as lamination method of the cushion layer film.

【0042】次に、熱転写受像材料体(以下、「受像材料」と言う)について述べる。 Next, the thermal transfer image receiving material body (hereinafter referred to as "the image-receiving material") is described.

【0043】受像材料は、前記記録材料から像様に剥離した熱溶融性インク層を受容して画像を形成するものであり、基本的に支持体と受像層とから成るが、場合によっては支持体のみから形成されてもよいし、或は支持体と受像層の間にクッション層等の中間層を設けることもできる。 The image-receiving material is to receive the hot melt ink layer was peeled imagewise from said recording material is intended to form an image, consists basically support and the image receiving layer, the support optionally it may be formed from the body alone, or may be provided an intermediate layer of the cushion layer and the like between the support and the image receiving layer.

【0044】受像材料は熱により溶融した熱溶融性インク層が転写されるのであるから、適度の耐熱強度を有すると共に、画像が適正に形成されるよう寸法安定性に優れることが望ましい。 [0044] Since the image-receiving material is the heat-fusible ink layer which is melted by the heat is transferred, together with an appropriate heat resistance, it is desirable to excellent dimensional stability so that the image is properly formed.

【0045】受像材料は、画像形成時に記録材料と接する面が良好な平滑性を有するか、又は適度に粗面化してある。 The image-receiving material or surface in contact with the recording material during image formation has good smoothness, or are moderately roughened. 更に詳しくは、記録材料の熱溶融性インク層の表面がマット材等により粗面化されている時には、受像材料の熱溶融性インク層に接する面は良好な平滑性を有することが望ましく、又、熱溶融性インク層が粗面化されていない時には、受像材料の熱溶融性インク層に接する面はマット材により粗面化されているのが望ましい。 More specifically, when the surface of the heat-meltable ink layer of the recording material is roughened by the mat material or the like, the surface in contact with the heat-fusible ink layer of the image-receiving material it is desirable to have good smoothness, and , when the hot melt ink layer is not roughened, the surface in contact with the heat-fusible ink layer of the image receiving material is desirably is roughened by mat member.
又、熱溶融性インク層と受像材料の接触面が共に粗面化されていてもよい。 Further, the contact surface of the image-receiving material with hot melt ink layer may be roughened together.

【0046】受像層は、バインダーと必要に応じて添加される各種添加剤や、前記クッション性を付与するための物質とで形成することができる。 The image-receiving layer can be formed by various additives and which is optionally added a binder, a substance for imparting the cushioning.

【0047】受像層のバインダーとしては、エチレン- [0047] As the binder of the image-receiving layer, an ethylene -
塩化ビニル共重合体系接着剤、ポリ酢酸ビニルエマルジョン系接着剤、クロロプレン系接着剤、エポキシ樹脂系接着剤等の接着剤、天然ゴム、クロロプレン系ゴム、ブチルゴム系、ポリアクリル酸エステル系、ニトリルゴム系、ポリサルファイド系、シリコンゴム系、ロジン系樹脂、塩化ビニル系樹脂、石油系樹脂及びアイオノマー樹脂などの粘着剤、再生ゴム、SBR、ポリイソプレン、 Vinyl copolymer adhesives chloride, polyvinyl acetate emulsion adhesive, a chloroprene-based adhesive, an adhesive such as an epoxy resin adhesive, a natural rubber, chloroprene rubber, butyl rubber, polyacrylate, nitrile rubber , polysulfide, silicone rubber, rosin resin, adhesives such as vinyl chloride resin, petroleum resin and ionomer resins, reclaimed rubber, SBR, polyisoprene,
ポリビニルエーテル等を挙げることができる。 Polyvinyl ether, and the like.

【0048】支持体と受像層との間には、前記記録材料において説明したクッション層を設けることが好ましい。 [0048] Between the support and the image-receiving layer, it is preferable to provide a cushion layer described in the recording material.

【0049】なお、支持体とクッション層と受像層を有する受像材料における支持体の厚み、或は支持体だけで形成された受像材料における支持体の厚みについては特に制限はない。 [0049] Incidentally, no particular limitation is imposed on the thickness of the support in the image-receiving material which is formed the thickness of the support, or only the support of the image-receiving material having an image receiving layer and the support and the cushioning layer. 受像層の厚みは通常、0.1〜20μmであるが、クッション層を受像層として用いる場合はこの限りではない。 The thickness of the image-receiving layer is typically a 0.1 to 20 [mu] m, in the case of using a cushioning layer as the image-receiving layer is not limited thereto.

【0050】熱転写に用いる光源としては特に制約されないが、高解像度の画像形成のためにはレーザーが好ましく、安全、低価格、量産可能などの点から半導体レーザーの使用が特に好ましい。 [0050] Without being bound particularly as a light source for use in thermal transfer, preferably laser for high resolution imaging, safety, low cost, use of a semiconductor laser from the viewpoint of possible mass production is particularly preferred.

【0051】 [0051]

【実施例】以下、実施例を挙げて本発明を詳細に説明するが、本発明の態様はこれに限定されない。 EXAMPLES The following examples illustrate the present invention in detail, embodiments of the present invention is not limited thereto. 尚、各組成中の素材量は全て重量部で示す。 Incidentally, the material content in each composition is shown in all parts.

【0052】比較例1 インクシートの作成 <クッション層>100μm厚PET(ポリエチレンテレフタレート)支持体上に、下記組成の塗布液を調製し、ブレードコーターを用いて塗布・乾燥した。 [0052] on Comparative Example 1 Preparation of Ink Sheet <cushion layer> 100 [mu] m thick PET (polyethylene terephthalate) support, a coating solution having the following composition was prepared and coated and dried with a blade coater. 膜厚は約60μ The film thickness is about 60μ
m。 m.

【0053】 JSR0617(カルボキシ変性スチレン-ブタジエン樹脂 10部 :日本合成ゴム製) 水 90部 <光熱変換層>下記組成の塗布液を調製し、上記クッション層上にワイヤーバーを用いて塗布・乾燥した。 [0053] JSR0617 (carboxy modified styrene - 10 parts butadiene resins: Japan Synthetic Rubber Co.) 90 parts of water <photothermal conversion layer> to prepare a coating solution having the following composition was coated and dried with a wire bar on the cushion layer . なお、予め分光光度計で測定した光熱変換層の830nmでの透過濃度と、膜厚計で測定した膜厚の関係を求めておき、透過濃度を測定することにより膜厚を制御した。 Incidentally, to previously obtain a transmission density of at 830nm of the light-to-heat conversion layer measured in advance spectrophotometer, the relationship between the film thickness measured by the film thickness meter and the layer thickness by measuring the transmission density. 膜厚は0.35μmとした。 The film thickness was 0.35μm.

【0054】 IR-101 5部 S-2000(ポリカーボネート:三菱ガス製) 5部 MEK(メチルエチルケトン) 90部 <インク層>下記組成の塗布液を調製し、上記光熱変換層上にワイヤーバーを用いて塗布・乾燥した。 [0054] IR-101 5 parts S-2000 (polycarbonate Mitsubishi Gas Co.) 5 parts MEK (methyl ethyl ketone) 90 parts <Ink Layer> to prepare a coating solution having the following composition, using a wire bar on the light-heat conversion layer It was applied and dried. 膜厚は、 The film thickness,
予めインク層中のマゼンタ顔料の最大吸収波長570nmの透過濃度と膜厚の関係を調べておき、吸光度を測定することにより制御した。 Advance investigate the relationship between transmission density and thickness of the maximum absorption wavelength 570nm of magenta pigment in the ink layer was controlled by measuring the absorbance. 膜厚は0.70μmとした。 The film thickness was 0.70μm.

【0055】 EV40Y(エチレン-酢酸ビニル樹脂:三井デュポン製) 6.0部 MHI R527(マゼンタ顔料) 4.0部 MEK 90.0部受像体の作成 <受像層>100μm厚PET支持体上に、下記組成の塗布液をワイヤーバーを用いて塗布・乾燥した。 [0055] EV40Y -: creation (ethylene vinyl acetate resin Mitsui Du Pont Co.) 6.0 parts MHI R527 (magenta pigment) 4.0 parts MEK 90.0 parts image receptor <receiving layer> 100 [mu] m thick PET support on a coating solution having the following composition It was applied and dried using a wire bar. 膜厚は1.0 The thickness 1.0
μmとした。 It was μm.

【0056】 RB820(スチレン-ブタジエン樹脂) 10部 トルエン 90部 比較例2 比較例1のインクシートにおいて、光熱変換層中の光熱変換材をIR-102に代えた以外は同様にして光熱変換層を塗設した。 [0056] RB820 - the ink sheet (styrene-butadiene resin) 10 parts Toluene 90 parts Comparative Example 2 Comparative Example 1, except for changing the light-heat conversion material of the photothermal conversion layer to IR-102 in the same manner the light-heat conversion layer It was coated. クッション層は同じである。 Cushion layer is the same. 受像体の受像層も同じ構成とした。 Image-receiving layer of the image-receiving element was also the same configuration.

【0057】 [0057]

【化5】 [Of 5]

【0058】上記光熱変換材の溶剤溶解性(室温での重量%)は以下の通りである。 [0058] Solvent solubility of the light-heat conversion material (wt% at room temperature) is as follows.

【0059】 IR-101(MEK:5%以上,THF:3%以上) IR-102(MEK:5%以上,THF:5%以上) 実施例1 インクシートの作成 <クッション層>100μm厚PET支持体上に、下記組成の塗布液を調製し、ブレードコーターを用いて塗布・乾燥した。 [0059] IR-101 (MEK: 5% or more, THF: 3% or more) IR-102 (MEK: 5 % or more, THF: 5% or more) Example 1 ink creation of the seat <cushion layer> 100 [mu] m thick PET support on the body, a coating solution having the following composition was prepared and coated and dried with a blade coater. 膜厚は約60μm。 The film thickness is about 60μm.

【0060】 JSR0617(カルボキシ変性スチレン-ブタジエン樹脂) 10部 水 90部 <光熱変換層>下記組成の塗布液を調製し、上記クッション層(1及び2)上にワイヤーバーを用いて塗布・乾燥した。 [0060] JSR0617 (carboxy modified styrene - butadiene resin) 90 parts 10 parts Water <photothermal conversion layer> to prepare a coating solution having the following composition was coated and dried with a wire bar on the above cushion layer (1 and 2) . 膜厚制御は前記比較例1と同様に行った。 Thickness control was performed in the same manner as in Comparative Example 1. 膜厚は0.35μmとした。 The film thickness was 0.35μm.

【0061】 IR-101 5部 S-2000(ポリカーボネート:三菱ガス製) 5部 MEK 90部 <インク層>下記組成の塗布液を調製し、上記光熱変換層上にワイヤーバーを用いて塗布・乾燥した。 [0061] IR-101 5 parts S-2000 (polycarbonate Mitsubishi Gas Co.) 5 parts MEK 90 parts <Ink Layer> A coating solution having the following composition was prepared, coated and dried by using a wire bar on the light-heat conversion layer did. 膜厚制御は比較例1のインク層と同様である。 Thickness control is the same as the ink layer of Comparative Example 1. 膜厚0.70μm。 The film thickness 0.70μm.

【0062】 <インク層> DS-70E(ロジン変性合成樹脂:播磨化成製) 5.0部 G1-346(ワックス:ボンドワックス製) 0.5部 AD37P295(EVA:東洋モートン製) 5.5部 マゼンタ顔料(HIミクロンKピンク:御国色素製) 4.0部 水 90.0部 実施例2 インクシートのクッション層、光熱変換層は実施例1と同じだが、インク層のみ下記のように変更した。 [0062] <ink layer> DS-70E (rosin-modified synthetic resin: Harima Kasei) 5.0 parts G1-346 (Wax: Bond Ltd. Wax) 0.5 parts AD37P295 (EVA: manufactured by Toyo Morton) 5.5 parts Magenta pigment (HI microns K pink: Mikuni Color Ltd.) 4.0 parts water 90.0 parts example 2 ink sheet cushion layer, although the light-to-heat conversion layer the same as in example 1 was changed as follows only the ink layer.

【0063】<インク層>下記組成の塗布液を調製し、 [0063] prepare a coating solution of <ink layer> the following composition,
光熱変換層上にワイヤーバーを用いて塗布・乾燥した。 It was coated and dried with a wire bar in the light-to-heat conversion layer.
膜厚0.70μm。 The film thickness 0.70μm.

【0064】 G1-346(ワックス) 0.5部 AD37P295(EVA) 5.5部 マゼンタ顔料(HIミクロンKピンク) 4.0部 MEK 90.0部 実施例3 インクシートのクッション層、インク層は実施例1と同じだが、光熱変換層のみを下記のように変更した。 [0064] G1-346 (wax) 0.5 parts AD37P295 (EVA) 5.5 parts Magenta pigment (HI microns K pink) 4.0 parts MEK 90.0 parts Example 3 ink sheet cushion layer, the ink layer is the same as in Example 1, photothermal you change the only conversion layer, as described below.

【0065】<光熱変換層>下記組成の塗布液を調製し、上記クッション層上にワイヤーバーを用いて塗布・ [0065] was prepared <photothermal conversion layer> the coating solution having the following composition, coating and with a wire bar on the cushion layer
乾燥した。 Dry. 膜厚制御は前記比較例1と同様に行い、0.35 Thickness control is performed in the same manner as in Comparative Example 1, 0.35
μmとした。 It was μm.

【0066】 IR-102 5部 S-2000(ポリカーボネート:三菱ガス製) 5部 MEK 90部 実施例4 インクシートのクッション層、光熱変換層は実施例3と同じだが、インク層のみを下記の処方に変更した。 [0066] IR-102 5 parts S-2000 (polycarbonate: Mitsubishi Gas) 5 parts MEK 90 parts Example 4 ink sheet cushion layer, the photothermal conversion layer is the same as in Example 3, formulation only ink layer having the following It was changed to. インク層の膜厚は0.70μmとした。 The film thickness of the ink layer was 0.70 .mu.m.

【0067】 G1-346(ワックス) 0.5部 AD37P295(EVA) 5.5部 マゼンタ顔料(HIミクロンKピンク) 4.0部 MEK 90.0部 実施例5 インクシートの光熱変換層、インク層は実施例1と同じだが、クッション層及び支持体のみを下記の処方に変更した。 [0067] G1-346 (wax) 0.5 parts AD37P295 (EVA) 5.5 parts Magenta pigment (HI microns K pink) 4.0 parts MEK 90.0 parts Example 5 ink sheet photothermal conversion layer, the ink layer is the same as in Example 1, change only the cushion layer and the support to the following formulation.

【0068】<クッション層>75μm厚PET支持体上に、P1407C(酢酸ビニル14%のEVA:三井デュポンケミカル製)を押出しラミネートすることによりクッション層を設けた。 [0068] in <cushion layer> 75 [mu] m thick PET support on, P1407C (vinyl acetate 14% EVA: Mitsui DuPont Chemical) a cushion layer is provided by extrusion laminating the. 膜厚は約30μmで、Ra(表面粗さ)値は0.3以下にした。 The film thickness is about 30 [mu] m, Ra (surface roughness) value was 0.3 or less.

【0069】実施例6 インクシートの光熱変換層、インク層は実施例2と同じだが、クッション層及び支持体のみを実施例5と同じ処方で作成した。 [0069] Example 6 ink sheet photothermal conversion layer, the ink layer is the same as in Example 2, but creates only cushion layer and the support in the same formulation as in Example 5.

【0070】実施例7 インクシートの光熱変換層、インク層は実施例3と同じだが、クッション層及び支持体のみを実施例5と同じ処方で作成した。 [0070] photothermal conversion layer of Example 7 ink sheet, the ink layer is the same as in Example 3, but creates only cushion layer and the support in the same formulation as in Example 5.

【0071】実施例8 インクシートの光熱変換層、インク層は実施例4と同じだが、クッション層及び支持体のみを実施例5と同じ処方で作成した。 [0071] Example 8 ink sheet photothermal conversion layer, the ink layer is the same as in Example 4, but creates only cushion layer and the support in the same formulation as in Example 5.

【0072】(熱転写による画像形成)ドラム上に、前記インクシートのインク層と受像体の受像層側が接するようにインクシートを上にして重ね合わせた。 [0072] on the drum (image formation by thermal transfer), and the ink sheet superposed in the upper as the image receiving layer side of the ink layer and the image receiving material of the ink sheet is in contact. 次いで、 Then,
両者の密着性を増すために真空ポンプを用いて減圧し、 Under reduced pressure using a vacuum pump to increase the adhesion between them,
インクシートと受像体間の空気を取り除いた。 Removing the air between the ink sheet and the image receiving member. 又、この際、スクィーズを掛けることにより更に密着性を増した。 Also, this time, was increased further adhesion by applying a squeeze.

【0073】半導体レーザー(830nm)でインクシート支持体側から照射し、ドラムの回転数を変化させた時の転写像を観察し、感度、色再現性、ドット再現性を評価した。 [0073] irradiated from the ink sheet support side with the semiconductor laser (830 nm), to observe the transfer image at the time of changing the rotation speed of the drum was evaluated sensitivity, color reproducibility, dot reproducibility. 感度はドラムの回転数から計算した単位面積当たりのエネルギー(mJ/mm 2 )で表した。 The sensitivity was expressed as energy per unit area was calculated from the rotation speed of the drum (mJ / mm 2). 結果を以下に示す。 The results are shown below.

【0074】 光 熱 クッション インク層 感度 色再現性 ドツト 変換層 層 (mJ/mm 2 ) 再現性 実施例1 IR-101 JSR0617 DS-70E 0.50 色濁り無 良好 実施例2 IR-101 JSR0617 AD37P295 0.40 色濁り無 良好 実施例3 IR-102 JSR0617 DS-70E 0.60 色濁り無 良好 実施例4 IR-102 JSR0617 AD37P295 0.50 色濁り無 良好 実施例5 IR-101 EVA DS-70E 0.50 色濁り無 良好 実施例6 IR-101 EVA AD37P295 0.40 色濁り無 良好 実施例7 IR-102 EVA DS-70E 0.60 色濁り無 良好 実施例8 IR-102 EVA AD37P295 0.50 色濁り無 良好 比較例1 IR-101 JSR0617 EV-40Y 0.85 色濁り大 悪い 比較例2 IR-102 JSR0617 EV-40Y 0.85 色濁り大 悪い 実施例9 インクシートの光熱変換層(光熱変換材はIR-101、バインダーはS-2000)の膜厚を0.1〜0.8μmの範囲で変化させた(インク層の膜厚は0.7μm)。 [0074] Light heat cushion ink layer sensitive color reproducibility dots conversion layer layer (mJ / mm 2) Reproducibility Example 1 IR-101 JSR0617 DS-70E 0.50 color turbidity no good Example 2 IR-101 JSR0617 AD37P295 0.40 color turbidity No good example 3 IR-102 JSR0617 DS-70E 0.60 color turbidity no good example 4 IR-102 JSR0617 AD37P295 0.50 color turbidity no good example 5 IR-101 EVA DS-70E 0.50 color turbidity no good example 6 IR- 101 EVA AD37P295 0.40 color turbidity no good example 7 IR-102 EVA DS-70E 0.60 color turbidity no good example 8 IR-102 EVA AD37P295 0.50 color turbidity No good Comparative example 1 IR-101 JSR0617 EV-40Y 0.85 color turbidity Univ bad Comparative example 2 IR-102 JSR0617 EV-40Y 0.85 color turbidity large bad example 9 ink sheet photothermal conversion layer (light-heat conversion material is IR-101, the binder S-2000) range 0.1~0.8μm the thickness of in varying (thickness of the ink layer 0.7 [mu] m). ただし、光熱変換層の膜厚は830nmの吸光度の測定から求めた。 However, the thickness of the light-to-heat conversion layer was determined from measurements of absorbance at 830 nm.

【0075】光熱変換層の膜厚と感度の関係を以下に示す。 [0075] The relationship between the film thickness and the sensitivity of the light-to-heat conversion layer is shown below.

【0076】 光熱変換層膜厚(μm) インク層膜厚(μm) 感度(mJ/mm 2 ) 0.10 0.70 0.50 0.20 0.70 0.50 0.25 0.70 0.50 0.30 0.70 0.60 0.35 0.70 0.60 0.40 0.70 0.70 0.60 0.70 0.85 0.80 0.70 1.20 比較例3 光熱変換層の膜厚を1.1〜3.0μmの範囲で変化させた他は実施例9と同様に実施した。 [0076] photothermal conversion layer thickness ([mu] m) ink layer thickness ([mu] m) Sensitivity (mJ / mm 2) 0.10 0.70 0.50 0.20 0.70 0.50 0.25 0.70 0.50 0.30 0.70 0.60 0.35 0.70 0.60 0.40 0.70 0.70 0.60 0.70 0.85 0.80 0.70 1.20 Comparative example 3 except that the thickness of the light-heat conversion layer varied from 1.1~3.0μm was carried out in the same manner as in example 9. 結果は以下の通り。 The results are as follows.

【0077】 1.10 0.70 3.00 1.50 0.70 3.50 2.00 0.70 4.00 3.00 0.70 4.00 実施例10 インクシートのインク層(マゼンタ顔料はHIミクロンK [0077] 1.10 0.70 3.00 1.50 0.70 3.50 2.00 0.70 4.00 3.00 0.70 4.00 Example 10 an ink sheet ink layer (magenta pigment HI microns K
ピンク、バインダーはDS-70E)の膜厚を0.3〜0.9μmの範囲で変化させた(光熱変換層の膜厚は0.35μm)。 Pink, binder was changed in the range of 0.3~0.9μm the thickness of the DS-70E) (0.35 .mu.m film thickness of the light-to-heat conversion layer). ただし、インク層の膜厚は570nmの吸光度の測定から求めた。 However, the thickness of the ink layer was determined from measurements of absorbance at 570 nm.

【0078】インク層の膜厚と感度の関係を以下に示す。 [0078] The relationship between the thickness and sensitivity of the ink layer are shown below.

【0079】 0.35 0.30 0.65 0.35 0.40 0.65 0.35 0.60 0.65 0.35 0.90 0.75 比較例4 インク層の膜厚を1.1〜2.0μmの範囲で変化させた他は実施例10と同様に実施した。 [0079] 0.35 0.30 0.65 0.35 0.40 0.65 0.35 0.60 0.65 0.35 0.90 0.75 other with varying thickness of Comparative Example 4 Ink layer in the range of 1.1~2.0μm was carried out in the same manner as Example 10. 結果は以下の通り。 The results are as follows.

【0080】 0.35 1.10 1.50 0.35 1.50 1.50 0.35 2.00 1.75 [0080] 0.35 1.10 1.50 0.35 1.50 1.50 0.35 2.00 1.75

【0081】 [0081]

【表1】 [Table 1]

【0082】 [0082]

【発明の効果】本発明のヒートモード熱転写記録材料により、レーザー光走査を用いて色濁りのない色再現性に優れる転写画像が得られる。 The heat mode transfer recording material of the present invention, a transfer image having excellent free color reproduction color turbidity using a laser beam scanning can be obtained.

───────────────────────────────────────────────────── フロントページの続き (72)発明者 前島 勝己 東京都日野市さくら町1番地コニカ株式会 社内 ────────────────────────────────────────────────── ─── front page of the continuation (72) inventor Katsumi Maejima Hino City, Tokyo Sakura-cho, address 1 Konica shares meeting house

Claims (6)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】 支持体上に少なくとも溶剤溶解性近赤外吸収色素を含有する光熱変換層及び水溶性インク層を有することを特徴とするヒートモード熱転写記録材料。 1. A heat mode transfer recording material characterized by having at least a light-to-heat conversion layer and the water-soluble ink layer contains a solvent soluble near infrared absorbing dye on a support.
  2. 【請求項2】 溶剤溶解性近赤外吸収色素が溶剤に0.1 2. A 0.1 solvent solubility near infrared absorbing dye in a solvent
    重量%以上溶解する色素であることを特徴とする請求項1記載のヒートモード熱転写記録材料。 Heat mode transfer recording material of claim 1, wherein it is a dye that dissolves% by weight or more.
  3. 【請求項3】 光熱変換層の厚みが1.0μm以下であり、 Wherein the thickness of the light-to-heat conversion layer has a 1.0μm or less,
    かつ700nm〜1000nmの波長の最大吸収濃度での光熱変換層の吸光度が0.3以上であることを特徴とする請求項1 And claim 1, the absorbance of the light-to-heat conversion layer at the maximum absorption density at a wavelength of 700nm~1000nm is equal to or less than 0.3
    記載のヒートモード熱転写記録材料。 Heat mode thermal transfer recording material according.
  4. 【請求項4】 インク層が水溶性バインダーを含有することを特徴とする請求項1記載のヒートモード熱転写記録材料。 4. A heat mode transfer recording material of claim 1, wherein the ink layer is characterized by containing a water-soluble binder.
  5. 【請求項5】 インク層がタッキファイアー樹脂の水エマルジョンを含有することを特徴とする請求項1記載のヒートモード熱転写記録材料。 5. A heat mode transfer recording material of claim 1, wherein the ink layer is characterized by containing a water emulsion of tackifier Fire resin.
  6. 【請求項6】 インク層の厚みが1.0μm以下であることを特徴とする請求項1記載のヒートモード熱転写記録材料。 Heat mode transfer recording material of claim 1, wherein the thickness of 6. The ink layer is 1.0μm or less.
JP14947292A 1992-06-09 1992-06-09 Heat mode thermal transfer recording material Expired - Fee Related JP3215988B2 (en)