JPH0332472B2 - - Google Patents
Info
- Publication number
- JPH0332472B2 JPH0332472B2 JP58252061A JP25206183A JPH0332472B2 JP H0332472 B2 JPH0332472 B2 JP H0332472B2 JP 58252061 A JP58252061 A JP 58252061A JP 25206183 A JP25206183 A JP 25206183A JP H0332472 B2 JPH0332472 B2 JP H0332472B2
- Authority
- JP
- Japan
- Prior art keywords
- acid
- color
- present
- heat
- dibenzylbenzene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
本発明は感熱記録体に関するものである。更に
詳しくは一般にロイコ化合物といわれる無色また
は淡色の有機染料と、該ロイコ化合物と反応して
顕色するフエノール化合物などの有機酸とを主成
分とする、感熱記録体の改良に関するものであ
る。 さらに具体的に述べると、本発明は前記2成分
の発色反応物質を含む感熱記録体において、発色
促進剤としてジベンジルベンゼンを記録層中に含
有させて、該感熱記録体の発色特性を改良したこ
とを特徴とする新規な感熱記録体に関するもので
ある。 従来、ロイコ化合物および有機酸とを含む感熱
記録紙は、たとえば特公昭45−14039号などによ
つてすでに公知である。このような感熱記録紙は
熱エネルギーを記録層に与えて、ロイコ化合物、
有機酸および結着剤を軟化あるいは溶融し、それ
によつて両発色成分を接触させ、発色せしめると
いう原理に基づくものであり、近時各種プリンタ
ー、フアクシミリ等の分野で使用されている。 ところで、このような記録紙の記録特性はそれ
らの用途によつて当然異なつており、近年より高
度のものがこの種技術分野で要求されている。し
かして、たとえば記録速度を上げるためには、勿
論記録装置を改良すればよいのであるが、それと
共に使用する記録紙自身の発色性も同時に又は附
随的に促進することが要求されている。 ところで、この発色性を促進する方法として
は、通常低融点物質を感熱記録層中に含有させる
方法が行われている。 具体的に述べると低融点物質すなわち発色促進
剤または増感剤として、特公昭43−4160号では尿
素、無水フタル酸、アセトアニリドが;また特開
昭48−19231号ではパラフインろう、カルナバろ
う、密ろう、木ろう、高級脂肪酸、高級脂肪酸エ
ステルが;さらに特公昭49−17748号ではサリチ
ル酸、アニス酸、フタル酸モノフエニルエステ
ル、フタル酸モノベンジルエステルが;また近年
脂肪酸アミドを発色促進剤として使用することも
広く行なわれている。さらに特公昭51−27599号
には、パラフインまたはマイクロワツクスと脂肪
酸アミドとの組合せによる脂肪酸アミドの増感効
果が;特開昭54−139740号にはステアリン酸アミ
ド、オレイン酸アミドなどの脂肪酸アマイドの増
感効果が述べられている。 本発明者等は、これら公知の発色促進剤の効果
を確めるとともに、更に優れた特性を有する物質
を見出すべく鋭意研究を行なつた結果、ここに新
規な発色促進剤として有用な、ジベンジルベンゼ
ンを見出し、本発明に到達したのである。 すなわち、本発明はロイコ化合物と該ロイコ化
合物と反応して顕色する有機酸とを主成分とする
感熱記録体において、発色促進剤としてジベンジ
ルベンゼンを記録層中に含有せしめることを特徴
とする感熱記録体に関する。 以下、本発明に於て使用される物質につき説明
する。 (1) ジベンジルベンゼン 本発明において、有用かつ新規な発色促進剤
として働く化合物は、一般式 で表わされ、オルソー、メターおよびパラージ
ベンジルベンゼンが挙げられる。 これらの融点は、夫々パラジベンジルベンゼ
ンが87.8℃、オルソジベンジルベンゼンが83
℃、メタジベンジルベンゼンが58−9℃であ
る。 発色促進剤としては通常融点が約60〜約130°
のものが好ましいので、この範囲内であれば前
記ジベンジルベンゼンを単独では勿論のこと、
混合物としても用いることができる。 上記一般式で示される前述の化合物は、発色
促進の効果において優れており、更に感熱記録
紙に要求される各種特性、例えば地肌濃度、保
存後の地肌かぶり、退色等に於て、従来公知の
各種化合物と同等又はそれ以上の優れた効果を
有することが確認され満足に使用することがで
きるものである。 また、ジベンジルベンゼンは、例えばオルソ
ー、メター、パラ−キシリレンジクロライドと
ベンゼンとを塩化アルミニウム等のフリーデル
クラフツ触媒の存在下に反応させるか、または
1、2−、1、3−、1、4−ジベンゾイルベ
ンゼンのジヒドラゾンを苛性カリ等の苛性アル
カリの存在下に加熱分解することによつて合成
される。 本発明に於てジベンジルベンゼンの使用量
は、感熱記録層の全固形分の1〜40重量%の割
合とすることにより本発明の各種目的を達する
ことができる。 (2) ロイコ化合物 本発明に於て用いるロイコ化合物は無色ない
し淡色であつて、かつ有機酸と反応して発色す
る物質であれば総てのものが使用できる。例え
ばトリフエニルメタン系、トリフエニルメタン
フタリド系、フルオラン系、ロイコオーラミン
系、ジフエニルメタン系、フエノチアジン系、
フエノキサジン系、スピロピラン系、インドリ
ン系、インジゴ系などの各種融導体が挙げられ
る。更に具体的に述べると、例えば以下のもの
が例示できる(カツコ内は発色後の色)。 クリスタルバイオレツトラクトン(青色)、
3−ジエチルアミノ−6−メチル−7アニリノ
フルオラン(黒色)、3−(N−エチル−P−ト
ルイデイノ)−6−メチル−7−アニリノフル
オラン(黒色)、3−ジエチルアミノ−6−メ
チル−7−(オルト、パラ−ジメチルアニリノ)
フルオラン(黒色)、3−ピロリデイノ−6−
メチル−7−アニリノフルオラン(黒色)、3
−ピペリデイノ−6−メチル−7−アニリノフ
ルオラン(黒色)、3−(N−シクロヘキシル−
N−メチルアミノ)−6−メチル−7−アニリ
ノフルオラン(黒色)、3−ジエチルアミノ−
7−(オルト−クロロアニリノ)フルオラン
(黒色)、3−ジエチルアミノ−7−(メタ−ト
リフルオロメチルアニリノ)フルオラン(黒
色)、3−ジエチルアミノ−6−メチル−クロ
ロフルオラン(赤色)、3−ジエチルアミノ−
6−メチル−フルオラン(赤色)、3−シクロ
ヘキシルアミノ−6−クロロフルオラン(橙
色)、3−(N−イソアミル−N−エチルアミ
ノ)−6−メチル−7−アニリノフルオラン
(黒色)。 (3) 有機酸(またはそのエステル) 本発明に於て用いる有機酸は、常温で固体で
あり、加熱により溶融しロイコ化合物と接触し
て顕色剤となるような物質である。具体的には
各種フエノール性物質、脂肪酸、芳香族カルボ
ン酸などが挙げられる。 本発明において、有機酸の使用量は、感熱記
録層の全固形分の1〜40重量%の割合とするこ
とにより、本発明の各種目的を達成できる。 さらに具体的には次のようなものが用いられ
る。 没食子酸、サリチル酸、1−ヒドロキシ−2
−ナフトエ酸、o−ヒドロキシ安息香酸、m−
ヒドロキシ安息香酸、2−ヒドロキシ−p−ト
ルイル酸、3,5−キシレノール、チモール、
p−tert−ブチルフエノール、4−ヒドロキシ
フエノキシド、メチル−4−ヒドロキシベンゾ
エート、4−ヒドロキシアセトフエノン、α−
ナフトール、β−ナフトール、カテコール、レ
ゾルシン、ヒドロキノン、4−tert−オクチル
カテコール、4,4′−sec−ブチルデンフエノ
ール、2,2′−ジヒドロキシジフエニル、2,
2′−メチレンビス(4−メチル−6−tert−ブ
チルフエノール)、2,2−ビス(4′−ヒドロ
キシフエニル)プロパン(別名;ビスフエノー
ルA)、4,4′−イソプロピリデン−ビス(2
−tert−ブチルフエノール)、ピロガロール、
フロログルシン、フロログルシンカルボン酸。 P−メチルフエノール、P−ターシヤリーブ
チルフエノール、P−フエニルフエノール、
4,4′−シクロヘキシリデンジフエノール、
4,4′−(1−メチル−n−ヘキシリデン)ジ
フエノール、4,4′−イソプロピリデンジカテ
コール、4,4′−ベンジリデンジフエノール、
4,4′−イソプロピリデンビス(2−クロロフ
エノール)、3−フエニルサリチル酸、5−メ
チルサリチル酸、3,5−ジーターシヤリ−ブ
チルサリチル酸、1−オキシ−2−ナフトエ
酸、没食子酸エステル、サリチル酸エステル、
P−ヒドロキシ安息香酸エステル、4−ヒドロ
キシフタル酸エステル。 (4) 結着剤 本発明に於ては公知の結着剤を用いる。水溶
性のものを使用することが望ましい。 該結着剤は微粒子状に分散された発色剤を、
互いに隔離させて固着させるという働きをす
る。具体的にはポリビニルアルコール、メチル
セルロース、カルボキシメチルセルロース、ヒ
ドロキシエチルセルロース、ポリアクリル酸、
カゼイン、ゼラチン、でんぷんおよびそれらの
誘導体などが用いられる。 本発明において、結着剤の使用量は、感熱記
録層の全固形分の1〜30重量%の割合とするこ
とにより、本発明の各種目的を達成しうる。 (5) その他の添加剤 本発明の感熱記録体には必要に応じて感熱層
中に他の添加物質たとえばクレー、炭酸カルシ
ウム、水酸化アルミニウム、タルク、酸化チタ
ン、酸化亜鉛等の無機または有機顔料、ワツク
ス類、保存安定のための酸化防止剤、紫外線吸
収剤、ステイツク防止のための各種脂肪酸金属
塩、耐水性向上のための耐水化剤、フエノール
樹脂、界面活性剤等を添加してもよい。 また本発明による発色促進剤と組み合せてす
でにこの種技術分野に於て公知の発色促進剤を
添加してもよい。 (6) 基体 本発明に使用される基体としては、一般には
上質紙、中質紙、コート紙をはじめとする紙が
用いられるが、その他ガラス繊維シート、プラ
スチツクシート、フイルムラミネート紙なども
基体として使用することが出来る。 以下本発明の構成ならびに効果を実施例によ
り更に詳細に説明する。但し、本発明の技術的
範囲は、これらの実施例に限定されるものでは
ない。 実施例 1 a) 感熱記録体の製造 下記の組成のA液およびB液を各々別々にペ
イントシエーカー(東洋精機製)で10時間分散
させた。 A液: ロイコ染料PSD−150(新日曹化工) 5g パラジベンジルベンゼン 8g 水酸化アルミ 20g ステアリン酸亜鉛 5g ポリビニルアルコール12%液 35g 水 52g B液: ビスフエノールA 15g カオリン 20g ステアリン酸亜鉛 3g ポリビニルアルコール12%液 35g 水 52g 次にA液125g、B液125gとポリビニルアルコ
ール12%液50g、水40gを加えて混合撹拌し調整
して塗液をつくり、次にこの塗液を50g/m2の上
質紙の表面にマイヤバーを用いて乾燥後の塗布量
が8g/m2になるよう塗布乾燥し感熱記録紙を得
た。 実施例 2 実施例1で用いたA液の配合のうちロイコ染料
PSD−150(新日曹化工)のかわりにロイコ染料
S−205(山田化学)を用いた以外は実施例1と同
様にして感熱記録紙を得た。 比較例 1 実施例1で用いたA液の配合のうちパラジベン
ジルベンゼンは除いて他は実施例1と同様にして
感熱記録紙を得た。 比較例 2 実施例1で用いたA液の配合のうちパラジベン
ジルベンゼンのかわりにステアリン酸アマイドを
用いた以外は実施例1と同様にして感熱記録紙を
得た。 感熱記録体のテスト 以上の実施例および比較例で得た感熱記録紙を
記録面がベツク平滑度500秒になるようテストス
ーパーキヤレンダーで表面処理した。 次に表面処理して得られた感熱記録紙について
市販のGフアクシミリ装置FACOM FAX
621C(富士通(株)製)で記録電力0.96w/dot、通電
時間0.45msec、周期約5msec/lの条件下で印字
を行い、印字した時の画像濃度および地肌濃度を
マクベス濃度計を用いて測定した。保存性は乾燥
状態で60℃に保持した恒温室で24時間保存した後
の濃度を示した。実施例および比較例について表
の結果を得た。
詳しくは一般にロイコ化合物といわれる無色また
は淡色の有機染料と、該ロイコ化合物と反応して
顕色するフエノール化合物などの有機酸とを主成
分とする、感熱記録体の改良に関するものであ
る。 さらに具体的に述べると、本発明は前記2成分
の発色反応物質を含む感熱記録体において、発色
促進剤としてジベンジルベンゼンを記録層中に含
有させて、該感熱記録体の発色特性を改良したこ
とを特徴とする新規な感熱記録体に関するもので
ある。 従来、ロイコ化合物および有機酸とを含む感熱
記録紙は、たとえば特公昭45−14039号などによ
つてすでに公知である。このような感熱記録紙は
熱エネルギーを記録層に与えて、ロイコ化合物、
有機酸および結着剤を軟化あるいは溶融し、それ
によつて両発色成分を接触させ、発色せしめると
いう原理に基づくものであり、近時各種プリンタ
ー、フアクシミリ等の分野で使用されている。 ところで、このような記録紙の記録特性はそれ
らの用途によつて当然異なつており、近年より高
度のものがこの種技術分野で要求されている。し
かして、たとえば記録速度を上げるためには、勿
論記録装置を改良すればよいのであるが、それと
共に使用する記録紙自身の発色性も同時に又は附
随的に促進することが要求されている。 ところで、この発色性を促進する方法として
は、通常低融点物質を感熱記録層中に含有させる
方法が行われている。 具体的に述べると低融点物質すなわち発色促進
剤または増感剤として、特公昭43−4160号では尿
素、無水フタル酸、アセトアニリドが;また特開
昭48−19231号ではパラフインろう、カルナバろ
う、密ろう、木ろう、高級脂肪酸、高級脂肪酸エ
ステルが;さらに特公昭49−17748号ではサリチ
ル酸、アニス酸、フタル酸モノフエニルエステ
ル、フタル酸モノベンジルエステルが;また近年
脂肪酸アミドを発色促進剤として使用することも
広く行なわれている。さらに特公昭51−27599号
には、パラフインまたはマイクロワツクスと脂肪
酸アミドとの組合せによる脂肪酸アミドの増感効
果が;特開昭54−139740号にはステアリン酸アミ
ド、オレイン酸アミドなどの脂肪酸アマイドの増
感効果が述べられている。 本発明者等は、これら公知の発色促進剤の効果
を確めるとともに、更に優れた特性を有する物質
を見出すべく鋭意研究を行なつた結果、ここに新
規な発色促進剤として有用な、ジベンジルベンゼ
ンを見出し、本発明に到達したのである。 すなわち、本発明はロイコ化合物と該ロイコ化
合物と反応して顕色する有機酸とを主成分とする
感熱記録体において、発色促進剤としてジベンジ
ルベンゼンを記録層中に含有せしめることを特徴
とする感熱記録体に関する。 以下、本発明に於て使用される物質につき説明
する。 (1) ジベンジルベンゼン 本発明において、有用かつ新規な発色促進剤
として働く化合物は、一般式 で表わされ、オルソー、メターおよびパラージ
ベンジルベンゼンが挙げられる。 これらの融点は、夫々パラジベンジルベンゼ
ンが87.8℃、オルソジベンジルベンゼンが83
℃、メタジベンジルベンゼンが58−9℃であ
る。 発色促進剤としては通常融点が約60〜約130°
のものが好ましいので、この範囲内であれば前
記ジベンジルベンゼンを単独では勿論のこと、
混合物としても用いることができる。 上記一般式で示される前述の化合物は、発色
促進の効果において優れており、更に感熱記録
紙に要求される各種特性、例えば地肌濃度、保
存後の地肌かぶり、退色等に於て、従来公知の
各種化合物と同等又はそれ以上の優れた効果を
有することが確認され満足に使用することがで
きるものである。 また、ジベンジルベンゼンは、例えばオルソ
ー、メター、パラ−キシリレンジクロライドと
ベンゼンとを塩化アルミニウム等のフリーデル
クラフツ触媒の存在下に反応させるか、または
1、2−、1、3−、1、4−ジベンゾイルベ
ンゼンのジヒドラゾンを苛性カリ等の苛性アル
カリの存在下に加熱分解することによつて合成
される。 本発明に於てジベンジルベンゼンの使用量
は、感熱記録層の全固形分の1〜40重量%の割
合とすることにより本発明の各種目的を達する
ことができる。 (2) ロイコ化合物 本発明に於て用いるロイコ化合物は無色ない
し淡色であつて、かつ有機酸と反応して発色す
る物質であれば総てのものが使用できる。例え
ばトリフエニルメタン系、トリフエニルメタン
フタリド系、フルオラン系、ロイコオーラミン
系、ジフエニルメタン系、フエノチアジン系、
フエノキサジン系、スピロピラン系、インドリ
ン系、インジゴ系などの各種融導体が挙げられ
る。更に具体的に述べると、例えば以下のもの
が例示できる(カツコ内は発色後の色)。 クリスタルバイオレツトラクトン(青色)、
3−ジエチルアミノ−6−メチル−7アニリノ
フルオラン(黒色)、3−(N−エチル−P−ト
ルイデイノ)−6−メチル−7−アニリノフル
オラン(黒色)、3−ジエチルアミノ−6−メ
チル−7−(オルト、パラ−ジメチルアニリノ)
フルオラン(黒色)、3−ピロリデイノ−6−
メチル−7−アニリノフルオラン(黒色)、3
−ピペリデイノ−6−メチル−7−アニリノフ
ルオラン(黒色)、3−(N−シクロヘキシル−
N−メチルアミノ)−6−メチル−7−アニリ
ノフルオラン(黒色)、3−ジエチルアミノ−
7−(オルト−クロロアニリノ)フルオラン
(黒色)、3−ジエチルアミノ−7−(メタ−ト
リフルオロメチルアニリノ)フルオラン(黒
色)、3−ジエチルアミノ−6−メチル−クロ
ロフルオラン(赤色)、3−ジエチルアミノ−
6−メチル−フルオラン(赤色)、3−シクロ
ヘキシルアミノ−6−クロロフルオラン(橙
色)、3−(N−イソアミル−N−エチルアミ
ノ)−6−メチル−7−アニリノフルオラン
(黒色)。 (3) 有機酸(またはそのエステル) 本発明に於て用いる有機酸は、常温で固体で
あり、加熱により溶融しロイコ化合物と接触し
て顕色剤となるような物質である。具体的には
各種フエノール性物質、脂肪酸、芳香族カルボ
ン酸などが挙げられる。 本発明において、有機酸の使用量は、感熱記
録層の全固形分の1〜40重量%の割合とするこ
とにより、本発明の各種目的を達成できる。 さらに具体的には次のようなものが用いられ
る。 没食子酸、サリチル酸、1−ヒドロキシ−2
−ナフトエ酸、o−ヒドロキシ安息香酸、m−
ヒドロキシ安息香酸、2−ヒドロキシ−p−ト
ルイル酸、3,5−キシレノール、チモール、
p−tert−ブチルフエノール、4−ヒドロキシ
フエノキシド、メチル−4−ヒドロキシベンゾ
エート、4−ヒドロキシアセトフエノン、α−
ナフトール、β−ナフトール、カテコール、レ
ゾルシン、ヒドロキノン、4−tert−オクチル
カテコール、4,4′−sec−ブチルデンフエノ
ール、2,2′−ジヒドロキシジフエニル、2,
2′−メチレンビス(4−メチル−6−tert−ブ
チルフエノール)、2,2−ビス(4′−ヒドロ
キシフエニル)プロパン(別名;ビスフエノー
ルA)、4,4′−イソプロピリデン−ビス(2
−tert−ブチルフエノール)、ピロガロール、
フロログルシン、フロログルシンカルボン酸。 P−メチルフエノール、P−ターシヤリーブ
チルフエノール、P−フエニルフエノール、
4,4′−シクロヘキシリデンジフエノール、
4,4′−(1−メチル−n−ヘキシリデン)ジ
フエノール、4,4′−イソプロピリデンジカテ
コール、4,4′−ベンジリデンジフエノール、
4,4′−イソプロピリデンビス(2−クロロフ
エノール)、3−フエニルサリチル酸、5−メ
チルサリチル酸、3,5−ジーターシヤリ−ブ
チルサリチル酸、1−オキシ−2−ナフトエ
酸、没食子酸エステル、サリチル酸エステル、
P−ヒドロキシ安息香酸エステル、4−ヒドロ
キシフタル酸エステル。 (4) 結着剤 本発明に於ては公知の結着剤を用いる。水溶
性のものを使用することが望ましい。 該結着剤は微粒子状に分散された発色剤を、
互いに隔離させて固着させるという働きをす
る。具体的にはポリビニルアルコール、メチル
セルロース、カルボキシメチルセルロース、ヒ
ドロキシエチルセルロース、ポリアクリル酸、
カゼイン、ゼラチン、でんぷんおよびそれらの
誘導体などが用いられる。 本発明において、結着剤の使用量は、感熱記
録層の全固形分の1〜30重量%の割合とするこ
とにより、本発明の各種目的を達成しうる。 (5) その他の添加剤 本発明の感熱記録体には必要に応じて感熱層
中に他の添加物質たとえばクレー、炭酸カルシ
ウム、水酸化アルミニウム、タルク、酸化チタ
ン、酸化亜鉛等の無機または有機顔料、ワツク
ス類、保存安定のための酸化防止剤、紫外線吸
収剤、ステイツク防止のための各種脂肪酸金属
塩、耐水性向上のための耐水化剤、フエノール
樹脂、界面活性剤等を添加してもよい。 また本発明による発色促進剤と組み合せてす
でにこの種技術分野に於て公知の発色促進剤を
添加してもよい。 (6) 基体 本発明に使用される基体としては、一般には
上質紙、中質紙、コート紙をはじめとする紙が
用いられるが、その他ガラス繊維シート、プラ
スチツクシート、フイルムラミネート紙なども
基体として使用することが出来る。 以下本発明の構成ならびに効果を実施例によ
り更に詳細に説明する。但し、本発明の技術的
範囲は、これらの実施例に限定されるものでは
ない。 実施例 1 a) 感熱記録体の製造 下記の組成のA液およびB液を各々別々にペ
イントシエーカー(東洋精機製)で10時間分散
させた。 A液: ロイコ染料PSD−150(新日曹化工) 5g パラジベンジルベンゼン 8g 水酸化アルミ 20g ステアリン酸亜鉛 5g ポリビニルアルコール12%液 35g 水 52g B液: ビスフエノールA 15g カオリン 20g ステアリン酸亜鉛 3g ポリビニルアルコール12%液 35g 水 52g 次にA液125g、B液125gとポリビニルアルコ
ール12%液50g、水40gを加えて混合撹拌し調整
して塗液をつくり、次にこの塗液を50g/m2の上
質紙の表面にマイヤバーを用いて乾燥後の塗布量
が8g/m2になるよう塗布乾燥し感熱記録紙を得
た。 実施例 2 実施例1で用いたA液の配合のうちロイコ染料
PSD−150(新日曹化工)のかわりにロイコ染料
S−205(山田化学)を用いた以外は実施例1と同
様にして感熱記録紙を得た。 比較例 1 実施例1で用いたA液の配合のうちパラジベン
ジルベンゼンは除いて他は実施例1と同様にして
感熱記録紙を得た。 比較例 2 実施例1で用いたA液の配合のうちパラジベン
ジルベンゼンのかわりにステアリン酸アマイドを
用いた以外は実施例1と同様にして感熱記録紙を
得た。 感熱記録体のテスト 以上の実施例および比較例で得た感熱記録紙を
記録面がベツク平滑度500秒になるようテストス
ーパーキヤレンダーで表面処理した。 次に表面処理して得られた感熱記録紙について
市販のGフアクシミリ装置FACOM FAX
621C(富士通(株)製)で記録電力0.96w/dot、通電
時間0.45msec、周期約5msec/lの条件下で印字
を行い、印字した時の画像濃度および地肌濃度を
マクベス濃度計を用いて測定した。保存性は乾燥
状態で60℃に保持した恒温室で24時間保存した後
の濃度を示した。実施例および比較例について表
の結果を得た。
【表】
以上本発明の発色促進剤ジベンジルベンゼンが
すぐれた発色促進作用がありさらに保存安定性の
点でもすぐれた特性を有している事が実証され
た。
すぐれた発色促進作用がありさらに保存安定性の
点でもすぐれた特性を有している事が実証され
た。
Claims (1)
- 【特許請求の範囲】 1 ロイコ化合物と該ロイコ化合物と反応して顕
色する有機酸とを主成分とする感熱記録体におい
て、 発色促進材としてジベンジルベンゼンを記録層
中に含有せしめることを特徴とする感熱記録体。